U.S. patent application number 15/450362 was filed with the patent office on 2017-10-26 for process for manufacturing medium and high molecular weight polyesters.
This patent application is currently assigned to Valspar Sourcing, Inc.. The applicant listed for this patent is Valspar Sourcing, Inc.. Invention is credited to Larry B. Brandenburger, Thomas J. Melnyk.
Application Number | 20170306086 15/450362 |
Document ID | / |
Family ID | 40932336 |
Filed Date | 2017-10-26 |
United States Patent
Application |
20170306086 |
Kind Code |
A1 |
Brandenburger; Larry B. ; et
al. |
October 26, 2017 |
Process for Manufacturing Medium and High Molecular Weight
Polyesters
Abstract
Medium and high molecular weight polyester polymers are prepared
in syrup form from an ester oligomer. The oligomer is converted to
the polymer by polycondensation at elevated pressure and elevated
temperature in a nonreactive carrier capable of forming an
azeotrope with water. The ester oligomerization or polycondensation
reactions desirably are monitored using a non-viscometric
technique. The process has a rapid cycle time. The syrup contains
the polymer and nonreactive carrier, and may more conveniently be
used to make initially non-solid products such as polyester
coatings than is the case when employing pelletized solid polyester
resins.
Inventors: |
Brandenburger; Larry B.;
(Circle Pines, MN) ; Melnyk; Thomas J.;
(Greenfield, MN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Valspar Sourcing, Inc. |
Minneapolis |
MN |
US |
|
|
Assignee: |
Valspar Sourcing, Inc.
Minneapolis
MN
|
Family ID: |
40932336 |
Appl. No.: |
15/450362 |
Filed: |
March 6, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12027233 |
Feb 6, 2008 |
9624342 |
|
|
15450362 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C08G 63/81 20130101 |
International
Class: |
C08G 63/81 20060101
C08G063/81 |
Claims
1-20. (canceled)
21. A polyester syrup comprising a nonreactive carrier and a linear
polyester derived from an ester oligomer, wherein the hydroxyl:acid
or hydroxyl;ester ratio is from about 0.98:1 to about 1.1:1, and
wherein the linear polyester has a number average molecular weight
of 6,000 to 20,000 amu and a hydroxyl number of 5 to 20, the
polymer having a backbone free of or substantially free of ethylene
oxide or propylene oxide groups and the syrup being free of or
substantially free of alcohols, glycols or esters that react with
the polymer at polycondensation temperatures.
22. A polyester syrup according to claim 21 wherein the polymer has
a number average molecular weight of 8,000 to 15,000 amu, the
nonreactive carrier comprises an alkane, aromatic hydrocarbon,
petroleum solvent, plant-derived solvent, ketone or mixture
thereof, and the nonreactive carrier has a boiling point of about
140 to about 300.degree. C.
23. A packaged polyester product comprising a container suitable
for interstate or export shipment within which is stored a
polyester syrup comprising a solution of high molecular weight
polyester polymer derived from an ester oligomer wherein the
hydroxyl:acid or hydroxyl;ester ratio is from about 0.98:1 to about
1.1:1 in a nonreactive carrier capable of forming an azeotrope with
water, the solution being free of or substantially free of
alcohols, glycols or esters that react with the polymer at
polycondensation temperatures and containing at least about 5% or
more of nonreactive carrier.
24. A packaged polyester product according to claim 23 wherein the
container is a shipping drum, tote, trailer tank car or rail tank
car.
25. A packaged polyester product according to claim 23 wherein the
polymer has a number average molecular weight of 7,001 to 30,000
amu, the nonreactive carrier comprises an alkane, aromatic
hydrocarbon, petroleum solvent, plant-derived solvent, ketone or
mixture thereof, and the nonreactive carrier has a boiling point of
about 140 to about 300.degree. C.
26. A packaged polyester product according to claim 23 wherein the
polymer has a number average molecular weight of 8,000 to 15,000
amu, the nonreactive carrier comprises an alkane, aromatic
hydrocarbon, petroleum solvent, plant-derived solvent, ketone or
mixture thereof, and the nonreactive carrier has a boiling point of
about 140 to about 300.degree. C.
27. (canceled)
Description
FIELD
[0001] This invention relates to polyester manufacturing.
BACKGROUND
[0002] Linear polyesters typically are prepared from oligomers made
by reacting together one or more dicarboxylic acids and one or more
diols via direct esterification, by reacting together one or more
dimethyl esters and one or more diols via transesterification, or
by carrying out both direct esterification and transesterification
in a single reaction mixture. Water evolves from the reaction
mixture in the case of direct esterification, and methanol evolves
from the reaction mixture in the case of transesterification. The
resulting oligomers may be converted to higher molecular weight
polyester polymers via polycondensation. Branched polyesters may be
made by introducing tri- or higher-functional reactants in place of
some of the dicarboxylic acids, diols or dimethyl esters.
[0003] Low molecular weight polyesters normally are prepared in a
single stage reaction that accomplishes both direct esterification
and polycondensation. The reaction typically is carried out at
atmospheric pressure and at temperatures near the normal boiling
point for the diol (e.g., at temperatures of about 170-210.degree.
C. for reactions using ethylene glycol). A large diol excess
normally is employed. A small quantity (e.g., about 3%) of xylenes
may be added near the end of the reaction to assist in distilling
water from the reaction mixture. The end product is a low molecular
weight polyester which after cooling to room temperature may be a
liquid or in some cases an amorphous solid.
[0004] Medium and high molecular weight polyesters typically are
made via a two stage process. The first stage typically is a direct
esterification or transesterification reaction to form a liquid low
molecular weight oligomer and the second stage typically is a
polycondensation reaction to convert the oligomer to a polymer with
a targeted molecular weight. Considerable time may be required to
complete the two stages. The first stage esterification reaction
may for example be carried out using conditions similar to the low
molecular weight polyester direct esterification reaction
conditions described above. The second stage polycondensation
reaction typically is performed using melt or solid state
polymerization, together with vacuum (e.g., about 0.1-1 mm
pressure) and high temperature (e.g., temperatures above ambient
temperature such as about 270-290.degree. C. for polyesters derived
from ethylene glycol). The vacuum and heat aid in removal of the
excess diol. The reaction mixture typically has sufficiently high
viscosity so that it would be unduly difficult to stir it during
the polycondensation reaction. The end product is a medium or high
molecular weight polyester which after cooling is a solid. The
solid product typically is pelletized prior to shipment to an end
user. The end user may in turn melt the pellets using an extruder
or other suitable device and form the melt into a film or mold it
into solid objects. For example, containers (e.g., bottles in the
case of polyethylene terephthalate resins) represent a very high
volume use for pelletized polyester resins.
SUMMARY OF THE INVENTION
[0005] We have found a process for preparing medium or high
molecular weight polyester syrups, which process comprises: [0006]
a) providing or forming an ester oligomer; [0007] b) converting the
oligomer to a polyester polymer by stirring at elevated pressure
and elevated temperature a solution of the oligomer in a
nonreactive carrier capable of forming an azeotrope with water; and
[0008] c) removing water from the mixture via azeotropic reflux to
provide a syrup comprising a medium or high molecular weight
polyester polymer in the nonreactive carrier.
[0009] The invention provides in another aspect novel polyester
syrups comprising a nonreactive carrier and a linear polyester
polymer having a number average molecular weight (Mn) of 6,000 to
20,000 amu and a hydroxyl number of 5 to 20, the polymer having a
backbone free of or substantially free of ethylene oxide or
propylene oxide groups and the syrup being free of or substantially
free of alcohols, glycols or esters that react with the polymer at
polycondensation temperatures.
[0010] The invention provides in another aspect a packaged
polyester product comprising a container suitable for interstate or
export shipment within which is stored a polyester syrup comprising
a solution of high molecular weight polyester polymer in a
nonreactive carrier capable of forming an azeotrope with water, the
solution being free of or substantially free of alcohols, glycols
or esters that react with the polymer at polycondensation
temperatures and containing at least about 5% or more of
nonreactive carrier.
[0011] The invention provides in another aspect a packaged
polyester product comprising a container suitable for interstate or
export shipment within which is stored a polyester syrup consisting
essentially of a solution of high molecular weight polyester
polymer in a nonreactive carrier for the polymer capable of forming
an azeotrope with water.
[0012] The disclosed process offers rapid reaction completion and
may enable greater flexibility in the choice of reactants. The
resulting liquid polyester product can more conveniently be used to
manufacture polyester coatings and other liquid polyester products
than is the case when using pelletized solid polyester starting
materials.
BRIEF DESCRIPTION OF THE DRAWING
[0013] FIG. 1 is a schematic view of one embodiment of the
disclosed process.
[0014] FIG. 2 is a schematic view of another embodiment of the
disclosed process.
[0015] FIG. 3 is a perspective cutaway view of a shipping container
filled with the disclosed polyester syrup.
[0016] Like reference symbols in the various figures of the drawing
indicate like elements. The elements in the drawing are not to
scale.
DETAILED DESCRIPTION
[0017] Unless the context indicates otherwise the following terms
shall have the following meaning and shall be applicable to the
singular and plural:
[0018] The terms "a," "an," "the," "at least one," and "one or
more" are used interchangeably. Thus, for example, a coating
composition that contains "an" additive means that the coating
composition may include "one or more" additives.
[0019] The term "azeotrope" means a mixture of two or more pure
compounds which form a constant boiling point mixture.
[0020] The term "elevated temperature" means a temperature of at
least 120.degree. C.
[0021] The term "esterification" refers to direct esterification or
transesterification.
[0022] When used with respect to a polymer, the term "low molecular
weight" means a polymer whose Mn is less than 4,000 amu, "medium
molecular weight" means a polymer whose Mn is 4,000 up to 7,000 amu
and "high molecular weight" means a polymer whose Mn is greater
than 7,000 amu.
[0023] The term "nonreactive carrier" means a solvent or other
carrier which can dissolve, disperse or otherwise solubilize a
medium or high molecular weight polyester to form the disclosed
polyester syrup, which is not a reactant (e.g., not a glycol) from
which the polyester is formed, and which will not react with the
polyester (e.g., will not transesterify with the polyester) at
polycondensation temperatures.
[0024] The term "non-viscometric technique" means a method for
monitoring the progress of a polymer-forming reaction without
requiring a viscosity measurement.
[0025] The term "polycondensation temperatures" means temperatures
of at least 200.degree. C.
[0026] The term "polyester" refers to linear and branched
polyesters.
[0027] The term "polyester syrup" means a liquid which is readily
pourable at room temperature and which contains a medium molecular
weight or high molecular weight polyester polymer in a nonreactive
carrier.
[0028] The terms "preferred" and "preferably" refer to embodiments
of the invention that may afford certain benefits, under certain
circumstances. However, other embodiments may also be preferred,
under the same or other circumstances. Furthermore, the recitation
of one or more preferred embodiments does not imply that other
embodiments are not useful, and is not intended to exclude other
embodiments from the scope of the invention.
[0029] When used with respect to a component which may be found in
a mixture, the term "substantially free of" means containing less
than about 5 wt. % of the component based on the mixture
weight.
[0030] The recitation of a numerical range using endpoints includes
all numbers subsumed within that range (e.g., 1 to 5 includes 1,
1.5, 2, 2.75, 3, 3.80, 4, 5, etc.).
[0031] FIG. 1 shows an exemplary schematic view of one embodiment
of the disclosed process in which a two-stage reaction is
performed. Apparatus 10 includes an esterification reactor 12 for
forming an ester oligomer by direct esterification or
transesterification. Reactor 12 is equipped with an impeller 14
mounted on shaft 16 and driven by a motor 18. Fractional
distillation column 20 enables removal of water through outlet 22.
Inert gas supply 24 is regulated by valve 26 and fed to reactor 12
through conduit 28. A carboxylic acid reactant stored in vessel 30
(typically in solid form) may be melted using extruder 32 and fed
to reactor 12 through conduit 34. Extruder 32 may be omitted for
reactants (e.g., isophthalic or terephthalic acid) that may be
degraded in an extruder and which may simply be added in solid form
to reactor 12. Extruder 32 may also be omitted for reactants (e.g.,
phthalic anhydride) whose melting behavior is such that they may be
melted in vessel 30 and fed directly to reactor 12 through conduit
34. A glycol reactant stored in vessel 36 (usually in liquid form)
is regulated by valve 38 and fed to reactor 12 through conduit 40.
A catalyst solution stored in vessel 42 is regulated by valve 44
and fed to reactor 12 through conduit 46. At the completion of the
esterification reaction, an oligomer or low molecular weight
polyester product 50 is removed from reactor 12 by opening valve 52
and fed through conduit 54 to polycondensation reactor 60.
[0032] Reactor 60 is a pressurizable vessel equipped with an
impeller 62 mounted on shaft 64 and driven by motor 66. Reflux
distillation column 68 removes reaction byproducts and evaporated
nonreactive carrier from reactor 60 and passes them through conduit
70 to condenser 72. Condensed nonreactive carrier 73 is collected
in the bottom of condenser 72 and reaction byproducts are removed
via port 74. Drain conduit 76, pump 78 and return conduit 80 enable
condensed nonreactive carrier 73 to be returned to column 68.
Nonreactive carrier stored in vessel 84 is regulated by valve 86
and fed to reactor 60 through conduit 88. A catalyst solution
stored in vessel 90 is regulated by valve 92 and fed to reactor 60
through conduit 94. The polycondensation reaction is performed
under pressure and its progress may be monitored in a variety of
ways, e.g., by withdrawing samples at sampling port 96 when valve
98 is opened. When the polycondensation reaction is judged to be
complete, the polycondensation reaction product syrup 100 is
removed from reactor 60 by opening valve 102 and feeding the
reaction product 100 through conduit 104 to shipping drum 106.
[0033] The esterification and polycondensation reactions outlined
in FIG. 1 may be referred to as first and second stages
respectively involving oligomerization and polymer foimation. It
will be appreciated by persons having ordinary skill in the art
that the dividing line between oligomerization and polymerization
may be somewhat hard to draw, and that some polymer formation may
take place in reactor 50 and some oligomerization may take place in
reactor 60.
[0034] The reactions outlined in FIG. 1 may be performed in a
single pressurizable reactor. FIG. 2 shows an exemplary schematic
view of a single reactor embodiment of the disclosed process.
Apparatus 200 includes a pressurizable reactor 202 equipped with an
impeller 204 mounted on shaft 206 and driven by a motor 208.
Fractional distillation column 210 enables removal of water through
outlet 212. Inert gas supply 214 is regulated by valve 216 and fed
to reactor 202 through conduit 218. Reflux distillation column 220
removes reaction byproducts and evaporated nonreactive carrier from
reactor 202 and passes them through conduit 222 to condenser 224.
Condensed nonreactive carrier 225 is collected in the bottom of
condenser 224 and reaction byproducts are removed via port 226.
Drain conduit 228, pump 230 and return conduit 232 enable condensed
nonreactive carrier 225 to be returned to column 220. A carboxylic
acid reactant stored in vessel 240 is melted using extruder 242 and
fed to reactor 202 through conduit 244. As is the case for the FIG.
1 embodiment, extruder 242 may be omitted for carboxylic reactants
that can be added in solid form directly to reactor 202 or melted
in vessel 240. A glycol reactant stored in vessel 246 is regulated
by valve 248 and fed to reactor 202 through conduit 250. An
esterification catalyst solution stored in vessel 252 is regulated
by valve 254 and fed to reactor 202 through conduit 256. At the
completion of the esterification reaction, an oligomer or low
molecular weight polyester product is obtained and is further
reacted to form a polyester syrup. Nonreactive carrier stored in
vessel 258 is regulated by valve 260 and fed to reactor 202 through
conduit 262. A polycondensation catalyst solution stored in vessel
264 is regulated by valve 266 and fed to reactor 202 through
conduit 268. The polycondensation reaction is carried out under
pressure and its progress may be monitored by withdrawing samples
at sampling port 270 when valve 272 is opened. The polycondensation
reaction product syrup 274 is removed from reactor 202 by opening
valve 276 and feeding the reaction product 274 through conduit 278
to shipping tote 280.
[0035] FIG. 3 shows another exemplary shipping container 300 for
transporting the disclosed polyester syrup. Rail tank car 302
contains polyester syrup 304 as a solution of the polyester in
nonreactive carrier. Syrup 304 may conveniently be used as is to
fonu polyester coatings and other initially non-solid products, or
readily combined (using for example a stirrer or static mixer) with
other suitable liquid or solid ingredients without first having to
be melted or combined with a carrier.
[0036] A variety of dicarboxylic acids or their anhydrides or
esters may be used in the disclosed process. Representative
dicarboxylic acids for use in direct esterification reactions
include but are not limited to saturated carboxylic acids,
unsaturated carboxylic acids, their anhydrides, and combinations
thereof, and the eventual polyester may be a saturated or
unsaturated polyester. The dicarboxylic acids may be aromatic,
aliphatic or cycloaliphatic. Exemplary dicarboxylic acids include
but are not limited to maleic acid, chloromaleic acid, fumaric
acid, itaconic acid, citraconic acid, mesaconic acid, malic acid,
succinic acid, glutaric acid, d-methylglutaric acid, adipic acid,
sebacic acid, pimelic acid, o-phthalic acid, isophthalic acid
(IPA), terephthalic acid (TPA), dihydrophthalic acid,
tetrahydrophthalic acid, hexahydrophthalic acid,
tetrachlorophthalic acid, chlorendic acid, dodecanedicarboxylic
acid, cis-5-norbornene-2,3-dicarboxylic acid, 2, 6-naphthalene
dicarboxylic acid, dimethyl-2,6-naphthenic dicarboxylic acid,
1,4-cyclohexane dicarboxylic acid and their anhydrides. Preferred
dicarboxylic acids include terephthalic acid, isophthalic acid,
o-phthalic acid, glutaric acid, adipic acid, 1,4-cyclohexane
dicarboxylic acid, 2, 6-naphthalene dicarboxylic acid,
hexahydrophthalic acid, adipic acid and their anhydrides and
esters. Esters (e.g., methyl esters) of any of the above
dicarboxylic acids may be employed in transesterification
reactions. The reaction mixture may if desired contain minor
amounts of monocarboxylic acids or esters or minor amounts of tri-
or higher carboxylic acids or esters, including but not limited to
for example, ethylhexanoic acid, propionic acid, trimellitic acid,
benzoic acid, 4-methylbenzoic acid, 1,2,4-benzenetricarboxylic
acid, 1,2,4,5-benzenetetracarboxylic acid, and their anhydrides or
esters.
[0037] A variety of glycols may be used in the disclosed process.
Representative glycols for use in direct esterification reactions
include but are not limited to linear, cyclic, and branched
aliphatic diols having 2 or more (e.g., 2 to about 8) carbon atoms;
aliphatic and aromatic ether glycols having 4 or more (e.g., 4 to
about 20, or 4 to about 10) carbon atoms; and combinations thereof.
Exemplary glycols include but are not limited to ethylene glycol
(also referred to as EG, B.P. 195.degree. C. at atmospheric
pressure), 1,2-propanediol (propylene glycol or PG, B.P.
188.degree. C.), 1,3-propanediol (B.P. 214.degree. C.),
2-methyl-1,3-propanediol (MPDiol, B.P. 212.degree. C.),
2,2-dimethyl-1,3-propanediol (neopentyl glycol or NPG, B.P.
208.degree. C.), 2,2,4-trimethyl-1,3-pentanediol (TMPD Glycol,
initial B.P. 220.degree. C.), 2-butyl-2-ethyl-1,3-propanediol
(BEPG, B.P. 103-106.degree. C.), 3-hydroxy-2,2-dimethylpropyl
3-hydroxy-2,2-dimethyl propanate, 1,3-butylene glycol (B.P.
204.degree. C.), 1,4-butanediol (B.P. 230.degree. C.),
3-methyl-1,5-pentanediol (MPD, B.P. 249.degree. C.), 1,6-hexanediol
(B.P. 250.degree. C.), 1,2-cyclohexanediol (B.P. 118-120.degree. C.
at 10 mm Hg), 1,4-cyclohexanediol (B.P. 150.degree. C. at 50 mm
Hg), 1,4-bis(hydroxymethyl)cyclohexane (cyclohexanedimethanol or
CHDM, B.P. 283.degree. C.), 2,2-dimethyl heptanediol, 2,2-dimethyl
octanediol, diethylene glycol (DEG, B.P. 245.degree. C.),
triethylene glycol (TEG, B.P. 285.degree. C.), dipropylene glycol
(B.P. 229-232.degree. C.), tripropylene glycol (B.P. 273.degree.
C.), polyethylene glycol (PEG), hydroquinone
bis(2-hydroxyethyl)ether, diethylene ether glycol (B.P. 197.degree.
C.), poly(ethylene ether) glycol,
2,2-bis-(p-hydroxycyclohexyl)-propane, 5-norbornene-2,2-dimethylol,
and 2,3-norbornene diol. The reaction mixture may be prepared
without or substantially without the use of EG or PG and instead
prepared using higher boiling point glycol(s) which in conventional
polyester polymer syntheses might normally not be employed alone.
For example, the reaction mixture may be prepared using only
glycols having atmospheric pressure boiling points of at least
about 196.degree. C., at least about 200.degree. C., at least about
204.degree. C. or at least about 208.degree. C. This may enable the
synthesis of novel polyester polymers having especially desirable
physical properties (e.g., altered crystallinity, glass transition
temperature, softening point or melt flow rate) not available or
not readily available in polyester polymers derived from EG or PG.
Preferred glycols include 2-methyl-1,3-propanediol,
2,2-dimethyl-1,3-propanediol, 1,3-butylene glycol, 1,4-butanediol
and 1,6-hexanediol. The reaction mixture may if desired contain
minor amounts of monofunctional alcohols or minor amounts of tri-
or higher-functional alcohols, including but not limited to
2-ethylhexyl alcohol, 2-cyclohexyl ethanol,
2,2-dimethyl-1-propanol, lauryl alcohol, benzyl alcohol,
cyclohexanol, glycerol, trimethylol propane, trimethylol ethane,
di-trimethylol propane, pentaerythritol, dipentaerythritol and
tripentaerythritol.
[0038] A variety of catalysts may be employed for esterification
and will be familiar to persons having ordinary skill in the art.
Exemplary catalysts include but are not limited to inorganic and
organic compounds of titanium, tin, lanthanum, zinc, copper,
magnesium, calcium, manganese, iron and cobalt, including oxides,
carbonates and phosphorus compounds, alkyl compounds, aryl
compounds and aryl derivatives, as well as combinations of two or
more thereof. Representative catalysts include but are not limited
to titanium catalysts (e.g., tetraisopropyl titanate and
tetraisobutyl titanate); mixed titanium/zirconium catalysts;
lanthanum acetylacetonate; cobalt acetate; organic titanium and
organic zirconium compounds such as those disclosed in U.S. Pat.
Nos. 3,056,818, 3,326,965, 5,981,690 and 6,043,335; and tin
catalysts including n-butylstannoic acid, octylstannoic acid and
others as described in U.S. Pat. Nos. 6,281,325 and 6,887,953. The
catalyst may be employed in an amount sufficient to promote the
desired direct esterification or transesterification reaction, for
example about 5 to about 10,000 ppm catalyst based on the polyester
weight.
[0039] The hydroxyl:acid mole ratio for a direct esterification
reaction (or the hydroxyl:ester ratio for a transesterification
reaction) may for example be from about 0.5:1 up to about 2:1, and
preferably between about 0.5:1 and about 1.5:1, between about 0.8:1
and about 1.2:1, between about 0.9:1 and about 1.1:1, between about
0.95:1 and about 1.05:1 or between about 0.98:1 and about 1.02:1.
Preferably an excess of hydroxyl is employed, and preferably the
hydroxyl:acid or hydroxyl:ester mole ratio is between about 1:1 and
about 2:1, between about 1:1 and about 1.5:1, between about 1:1 and
about 1.2:1, between about 1:1 and about 1.1:1, between about 1:1
and about 1.05:1 or between about 1:1 and about 1.02:1. The desired
ratio may be well below the ratios normally used for direct
esterification where a substantial excess of glycol typically is
employed. The disclosed process thus permits a reduction in the
amount of glycol employed at the start of the esterification
reaction, and permits the reaction to be performed using glycols
with boiling points above the 196.degree. C. boiling point of
ethylene glycol. This may speed the reaction rate, alter the number
of side reactions or make it easier to attain a targeted number
average molecular weight for the ester oligomer or for the final
polyester. For example, approximately a 1.025:1 hydroxyl:acid ratio
may provide an approximately 10,000 amu final polyester product,
and approximately a 1.01:1 hydroxyl:acid ratio may provide an
approximately 20,000 amu final polyester product. The end product
number average molecular weight will increase sharply as the
hydroxyl:acid or hydroxyl:ester mole ratio approaches 1:1, and thus
careful monitoring of the ratio during the course of the
esterification reaction will help avoid overshooting a targeted
number average molecular weight.
[0040] Esterification may be performed using a batch or continuous
reaction process. Heating may be employed prior to feeding, during
feeding, during mixing, or combinations thereof. The temperature
may be held at a constant value or may be varied during the course
of esterification. The reactants desirably are maintained at a
temperature sufficient to promote rapid reaction and evolution of
water, methanol or other byproducts while avoiding decomposition of
the oligomer. For polyesters derived from ethylene glycol, reaction
temperatures of about 210-235.degree. C. are recommended. The
esterification reaction conveniently may be performed at
atmospheric or elevated pressure, for example at gauge pressures
from about 34 KPa (5 psi) up to about 100 KPa (15 psi), up to about
200 KPa (29 psi) or up to about 300 KPa (44 psi). The use of
elevated pressure may provide an increased reaction rate, and the
use of elevated pressure together with temperatures lower than
those employed in the absence of pressure may limit the number of
side reactions. The esterification reaction preferably forms a
hydroxyl-functional and optionally acid-functional oligomer having
a greater hydroxyl number than acid number. Unlike typical practice
for making solid polyester products, the disclosed esterification
reaction may be performed using a carrier whose presence in the
final product would not be objectionable. Adding a carrier during
oligomerization would also make it difficult to use
typically-employed intrinsic viscosity measurement techniques to
monitor the reaction progress. However, by employing a
non-viscometric measurement technique (discussed in more detail
below) to monitor one or both of the oligomerization and
polycondensation reactions, monitoring may be carried out despite
the presence of carriers which alter the reaction mixture
viscosity.
[0041] A variety of carriers may be used, including the nonreactive
carriers discussed in more detail below. Fractional distillation
may be used to remove water, methanol and other byproducts from the
esterification reactor and to return glycol (and if employed,
nonreactive carrier) to the reactor. In a production setting, the
esterification reaction may for example be carried out in less than
about 8, less than about 7 or less than about 6 hours including
time required to heat the reactants but not including time to cool
the product. The resulting oligomeric product may immediately be
converted to higher molecular weight polyester while still hot, or
may be cooled or stored in any convenient fashion as desired and
later converted.
[0042] The polycondensation reaction may be carried out in a
different reactor from the reactor used for esterification (e.g.,
as in FIG. 1), or in the same reactor used to perform
esterification (e.g., as in FIG. 2). The oligomer is combined with
a suitable catalyst and nonreactive carrier at elevated pressure
and elevated temperature. Water and glycol are removed via
azeotropic reflux with the nonreactive carrier. The end product
preferably is a syrup rather than a solid. By avoiding production
of a solid end product, a wider array of diol reactants may be
employed, including higher-boiling diols whose unreacted residuum
might otherwise be difficult to remove using vacuum and heat. For
example, the disclosed process enables use of diols whose boiling
points approach or exceed temperatures at which the polyester
product might decompose. The end product typically contains
appreciable quantities (e.g., 5 wt. % or more) of nonreactive
carrier. Adding a carrier would be undesirable in the conventional
approach for manufacturing medium or high molecular weight
polyester resins, since the added carrier would have to be removed
to obtain the normally-desired solid end product. Adding a
viscosity-reducing carrier during polycondensation would also make
it difficult to use intrinsic viscosity measurement techniques to
monitor the polymer-forming reaction. However, by employing a
non-viscometric measurement technique, monitoring may be carried
out despite the presence of carriers which alter the reaction
mixture viscosity. The targeted number average molecular weight for
a medium molecular weight polyester may for example be 4,000 to
7,000 amu, 5,000 to 7,000 amu, 5,000 to 6,000 amu or 6,000 to 7,000
amu. The targeted number average molecular weight for a high
molecular weight polyester may for example be more than 7,000 amu
(e.g., at least 7,001 emu), 7,001 to 30,000 amu, 7,001 to 25,000
amu, 7,001 to 20,000 amu, 8,000 to 30,000 amu, 8,000 to 25,000 amu,
8,000 to 20,000 amu, 10,000 to 25,000 amu, 10,000 to 20,000 amu,
10,000 to 18,000 amu or 10,000 to 16,000 amu.
[0043] As noted above it may be desirable to employ hydroxyl:acid
or hydroxyl:ester mole ratios approaching 1:1. Under such
circumstances the polymer number average molecular weight can
increase rapidly. When forming high molecular weight polyesters or
when using viscometric measuring techniques to monitor the reaction
progress, and may be all too easy to overshoot the desired reaction
endpoint. Alternative monitoring methods such as the use of gel
permeation chromatography to determine number average molecular
weight, or titrations to determine hydroxyl number may likewise be
too time consuming when the polymer-forming reaction is underway.
Progression or completion of one or both of the disclosed ester
oligomerization and polycondensation reactions preferably employs a
non-viscometric monitoring technique. A variety of such techniques
may be employed, with the main criteria being rapid availability of
measurement results and accuracy as good as or preferably better
than the accuracy obtainable using intrinsic viscosity
measurements. The use of near-IR analysis to monitor the
disappearance of hydroxyl and acid groups is an especially
preferred technique. Nuclear magnetic resonance as described in
U.S. Pat. No. 6,887,953 B2 may also be employed. The measurement
results may be used to determine whether additional starting
material (e.g. additional diacid or glycol) should be added to the
reactor during the ester oligomerization or polycondensation
reactions in order to correct the reaction mixture and assist in
reaching a targeted number average molecular weight.
Non-viscometric techniques may also be combined with viscometric
techniques (such as the measurement of intrinsic viscosity or the
monitoring of stirrer torque) to monitor the ester oligomerization
and polycondensation reactions.
[0044] The polyester polymer may be formulated to obtain targeted
properties other than molecular weight, or to obtain properties at
a given number average molecular weight that are not available in
commercially-supplied polyester polymers. One preferred subclass of
polyester polymers contains linear polyester polymers having a
number average molecular weight (Mn) of 6,000 to 20,000 amu and a
hydroxyl number of 5 to 20, the polymer backbone being free of or
substantially free of ethylene oxide or propylene oxide groups.
Linear polyester polymers within such subclass and having a number
average molecular weight greater than 6000 amu, or less than 15,000
amu, or less than 12,000 amu, are also preferred. Another preferred
subclass of polyester polymers has a Tg greater than 20 and less
than 40.degree. C. and a number average molecular weight of 7,001
to 20,000 amu. Polyester polymers within such subclass having a Tg
greater than 25 and less than 35.degree. C. are also preferred. For
example, the Tg may be chosen so as to provide a polyester polymer
that is non-tacky at room temperature but which is sufficiently
flexible so that a coating made using the polymer resists cracking
or crazing when bent. Yet another preferred subclass of polyester
polymers is derived from at least some aromatic dicarboxylic acid,
anhydride or ester.
[0045] A variety of catalysts may be employed in the
polycondensation reaction and will be familiar to persons having
ordinary skill in the art. Exemplary catalysts include but are not
limited to those mentioned above in connection with the
esterification reaction, used in amounts sufficient to promote the
polycondensation reaction, for example about 5 to about 10,000 ppm
catalyst based on the polyester weight.
[0046] A variety of nonreactive carriers may be employed.
Representative nonreactive carriers include but are not limited to
hydrocarbons, fluorocarbons, ketones and mixtures thereof. The
chosen nonreactive carrier may be selected based on a variety of
parameters including its azeotropic boiling point characteristics
when mixed with water, any contemplated later processing steps or
storage considerations, volatile organic compound (VOC)
considerations, or the intended end uses for products which may be
made from the disclosed polyester syrup. The nonreactive carrier
may for example have a boiling point greater than the highest
expected temperature at which the polyester syrup may be stored
(e.g., at least about 60.degree. C.) up to temperatures as high as
or even exceeding temperatures at which the polyester product might
decompose (e.g., up to or in excess of 250.degree. C., 260.degree.
C., 275.degree. C. or 300.degree. C.). For example, the nonreactive
carrier may have a boiling point of about 60 to about 300.degree.
C., about 140 to about 300.degree. C., about 150 to about
300.degree. C. or about 175 to about 300.degree. C. Preferably the
nonreactive carrier has a boiling point greater than or equal to
that of xylenes (140.degree. C.) and more preferably greater than
or equal to that of kerosene (150.degree. C.). Exemplary
nonreactive carriers include alkanes such as heptane (B.P.
98.degree. C.), octane (B.P. 126.degree. C.), mineral spirits (B.P.
140-300.degree. C.) and mixtures thereof; aromatic hydrocarbons
including toluene (B.P. 110.degree. C.), xylene (B.P. 140.degree.
C.), ligroin (B.P. 60-90.degree. C.), commercially-available
materials such as the "AROMATIC" series fluids (e.g., AROMATIC 150
and AROMATIC 200) from ExxonMobil Corp. and the SHELLSOL.TM. series
fluids (e.g., SHELLSOL A100 and SHELLSOL A150) from Shell Chemical
Co, and mixtures thereof; petroleum solvents including petroleum
naphtha, VM&P naphtha, Stoddard solvent, kerosene (B.P.
150.degree. C.) and mixtures thereof, plant-derived solvents
including turpentine (B.P. 150-180.degree. C.); ketones including
methyl ethyl ketone (B.P. 80.degree. C.), methyl isobutyl ketone
(B.P. 117.degree. C.), methyl isoamyl ketone (B.P. 144.degree. C.),
methyl amyl ketone (B.P. 150.degree. C.), cyclohexanone (B.P.
156.degree. C.), isobutyl ketone (B.P. 168.degree. C.), methyl
hexyl ketone (B.P. 173.degree. C.), methyl heptyl ketone (B.P.
192.degree. C.) and mixtures thereof; and mixtures of different
such classes of nonreactive carriers. Aromatic hydrocarbons are
preferred nonreactive carriers. Sufficient nonreactive carrier
should be employed to provide a stirrable reaction mixture and to
provide a final product in the form of a polyester syrup. The
nonreactive carrier may be used in a relatively high proportion
(e.g., in amounts corresponding to about 5% or more, about 10% or
more, about 15% or more, about 20% or more, about 30% or more,
about 40% or more or about 50% or more of the final polyester syrup
weight). The nonreactive carrier may for example be as much as
about 95%, about 90%, about 85%, about 80%, about 70%, about 60% or
about 50% of the final polyester syrup weight. Large amounts of
nonreactive carrier generally help increase the polycondensation
reaction rate, shorten the polycondensation reaction cycle time or
reduce the required stirring torque.
[0047] The polycondensation reaction may be performed at any
convenient elevated temperature so long as the polymer forms at a
suitable rate and does not undesirably degrade. The reaction
temperature may for example be about 200 to about 260.degree. C.,
about 215 to about 250.degree. C. or about 225 to about 235.degree.
C. (as determined by measuring the temperature of the reactants
themselves rather than the headspace above the reactants). The
reaction may be performed at pressures above atmospheric pressure,
for example at gauge pressures from about 34 KPa (5 psi) up to
about 100 KPa (15 psi), up to about 200 KPa (29 psi), up to about
300 KPa (44 psi), up to about 400 KPa (58 psi) or up to about 500
KPa (73 psi). The polycondensation reaction proceeds more rapidly
at higher temperatures. Temperatures of about 210 to about
250.degree. C. and more preferably about 210 to about 235.degree.
C., and pressures of about 200 to about 350 KPa are preferred for
polyesters derived from ethylene glycol. In a production setting,
the polycondensation reaction may for example be carried out in
less than about 8, less than about 7 or less than about 6 hours not
counting time to heat the reactants or cool the product. These
times are considerably shorter than the times that have been
required for conventional solid state polyester
polycondensation.
[0048] Since the final product preferably will be a polyester syrup
rather than a solid (e.g., pelletized) polyester, there are few
penalties and in fact several advantages associated with the
disclosed process. For example, as noted above the disclosed
polyester syrup may be much more conveniently used to manufacture
polyester coatings than is the case when starting from a pelletized
solid. By conducting the polycondensation reaction under pressure
rather than under vacuum, the polycondensation reaction rate may
increase or the cycle time may shorten. The polycondensation
reaction mixture may be stirred, thus further shortening cycle
times. The polycondensation reaction may be performed at reduced
temperatures compared to a conventional polycondensation reaction,
thus limiting the occurrence of side reactions. The use of pressure
rather than vacuum during the polycondensation reaction may also
reduce overall capital or operating costs, as vacuum reactors can
be more expensive to build or more difficult to operate than
pressurized reactors. It should be noted however that preparation
of high molecular weight polyesters using the disclosed process may
(in comparison to medium molecular weight polyester preparation)
require use of an enlarged polycondensation reaction kettle
stirring motor, a longer or higher temperature reaction cycle time,
an increased flow of nitrogen or other purging gas through the
reactor, quicker measurement of polycondensation reaction progress,
or a combination of these measures.
[0049] The resulting polyester syrup may for example contain about
5 to about 95 wt. % polyester solids and about 95 to about 5 wt. %
nonreactive carrier, with the desired amounts of polyester and
nonreactive carrier normally depending somewhat on the polyester
number average molecular weight. A medium molecular weight
polyester syrup might for example contain about 40 to about 95 wt.
% polyester solids and about 60 to about 5 wt. % nonreactive
carrier, or about 50 to about 80 wt. % polyester solids and about
50 to about 20 wt. % nonreactive carrier. A high molecular weight
polyester syrup might for example contain about 5 to about 80 wt. %
polyester solids and about 95 to about 20 wt. % nonreactive
carrier, about 10 to about 70 wt. % polyester solids and about 90
to about 30 wt. % nonreactive carrier or about 20 to about 60 wt. %
polyester solids and about 80 to about 40 wt. % nonreactive
carrier. If desired, additional carriers (including nonreactive
carriers) may be added to the polyester syrup after completion of
the polycondensation reaction. For example, reactive carriers
(e.g., esters) may be added once the syrup has cooled sufficiently
so as to discourage reactions with the polyester. However, in one
preferred embodiment the syrup is substantially free of alcohols,
glycols or esters that could react with the polyester at
polycondensation temperatures (e.g., at the actual temperature or
temperatures at which the polycondensation reaction occurred).
[0050] The syrup may be used as is to form products or stored or
shipped for use at another time or in another place. A variety of
shipping containers may be used, including drums such as the drum
106 shown in FIG. 1, totes such as the tote 280 shown in FIG. 2,
rail tank cars such as the tank car 300 shown in FIG. 3, truck tank
trailers, trucks, bottles, cans, sachets and other shipping
containers that will be or will become familiar to persons having
ordinary skill in the art. The chosen shipping container desirably
will meet applicable requirements for interstate shipment and
applicable fire codes for storage.
[0051] Products which may be formed from the polyester syrup
include but are not limited to initially non-solid products such as
paints and primers (e.g., corrosion-resistant primers containing
high molecular weight polyesters), coil coatings, sheet coatings,
packaging coatings, sealants and adhesives. Additives including
coating formation carriers, coalescing agents, pigments, dyes,
fillers, thickeners, dispersing aids, flow modifiers, viscosity
modifiers, antifoam agents, UV absorbers, inhibitors, binders,
crosslinking agents and initiators (including photoinitiators) may
be combined with the polyester syrup. The amounts and types of such
additives will be or will become familiar to persons having
ordinary skill in the art.
[0052] The invention is further described in the following
Examples, in which all parts and percentages are by weight unless
otherwise indicated.
Example 1
Preparation of a High Molecular Weight Polyester Resin
[0053] A mixing vessel equipped with an agitator, distillation
column, condenser, thermometer, and inert gas inlet was charged
with 3.2 moles 2-methyl 1,3-propanediol, 3.06 moles 1,3-benzene
dicarboxylic acid and 0.8 grams FASTCAT.TM. 4201 dibutyltin oxide
catalyst (from Arkema Inc.). The reactants had a 1.046:1
hydroxyl:acid ratio and did not include EG or PG. The reactor was
flushed with inert gas and heated to 235.degree. C. over 4 hours
while removing water. The batch temperature was held at 235.degree.
C. until an acid number of 18-25 was achieved, as determined by
adding AROMATIC 150 fluid (from ExxonMobil Corp.) to dilute and
cool the sample, followed by titration with 0.1 N methanolic KOH
solution to a pH 12 endpoint. The batch hydroxyl number was also
determined in under 30 minutes, by adding AROMATIC 150 fluid to
dilute and cool a further sample, reacting the OH groups with
excess anhydride to convert them to acid groups, followed by
titration with 0.1 N methanolic KOH to a pH 12 endpoint. The
reaction temperature was lowered to 180.degree. C. and additional
1,3-benzene dicarboxylic acid was added to adjust the hydroxyl:acid
ratio to 1.03:1. Polycondensation was started using azeotropic
distillation and sufficient AROMATIC 150 fluid (as nonreactive
carrier) to provide 17% aromatic hydrocarbon and 83% nonvolatile
reactor contents in the distillation mixture. The reaction
temperature was increased to 235.degree. C. and the reaction vessel
pressure was allowed to rise to 100 KPa (15 psi). The batch
temperature was maintained at 215.degree. C. until an acid number
less than 3.0 was achieved. The final acid number was 2.9 and the
final hydroxyl number was 8.0. The color as measured on the Gardner
scale was 1 and the resin was free from haze. The product number
average molecular weight was Mn=9,087 as determined by Gel
Permeation Chromatography.
Example 2
Preparation of a Medium Molecular Weight Polyester Resin
[0054] A mixing vessel equipped with an agitator, distillation
column, condenser, thermometer, and inert gas inlet is charged with
3.2 moles 2-methyl 1,3-propanediol, 3.06 moles 1,3-benzene
dicarboxylic acid and 0.8 grams FASTCAT 4201 dibutyltin oxide
catalyst. The reactants have a 1.046:1 hydroxyl:acid ratio and do
not include EG or PG. The reactor is flushed with inert gas and
heated to 235.degree. C. over 4 hours while removing water. The
batch temperature is held at 235.degree. C. until an acid number of
18-25 is achieved. The reaction temperature is lowered to
180.degree. C. and additional 1,3-benzene dicarboxylic acid are
added to adjust the hydroxyl:acid ratio to 1.04:1.0.
Polycondensation is started using azeotropic distillation and
sufficient AROMATIC 150 fluid to provide 17% aromatic hydrocarbon
and 83% nonvolatile reactor contents in the distillation mixture.
The reaction temperature is increased to 235.degree. C. and the
reaction vessel pressure is allowed to rise to 100 KPa (15 psi).
The batch temperature is maintained at 215.degree. C. until an acid
number less than 3.0 and a targeted molecular number average
molecular weight of 5,500 amu are achieved.
[0055] Having thus described the preferred embodiments of the
present invention, those of skill in the art will readily
appreciate that the teachings found herein may be applied to yet
other embodiments within the scope of the claims hereto attached.
The complete disclosure of all patents, patent documents, and
publications are incorporated herein by reference as if
individually incorporated.
* * * * *