U.S. patent application number 15/637709 was filed with the patent office on 2017-10-19 for water repellent film and component for vehicle including the film.
This patent application is currently assigned to NISSAN MOTOR CO., LTD.. The applicant listed for this patent is NISSAN MOTOR CO., LTD.. Invention is credited to Takayuki FUKUI, Motohiko KURODA, Yuji NOGUCHI, Isao YAMAMOTO.
Application Number | 20170297293 15/637709 |
Document ID | / |
Family ID | 45066284 |
Filed Date | 2017-10-19 |
United States Patent
Application |
20170297293 |
Kind Code |
A1 |
KURODA; Motohiko ; et
al. |
October 19, 2017 |
WATER REPELLENT FILM AND COMPONENT FOR VEHICLE INCLUDING THE
FILM
Abstract
A water repellent film (200) according to the present invention
includes a first layer (10) having a plurality of fine protrusions
(100) on the surface thereof, a second layer (20) covering the fine
protrusions (100) and having a water repellent property, and a
third layer (30) provided on the surface of the first layer (10) on
the opposite side of the fine protrusions (100). When a modulus of
elasticity of the first layer (10) is defined as E1, a modulus of
elasticity of the second layer (20) is defined as E2, and a modulus
of elasticity of the third layer (30) is defined as E3, a
definition of E2>E1>E3 is fulfilled. Accordingly, the water
repellent film having excellent resistance to abrasion in which a
fine structure is not easily abraded and damaged by an external
friction force or the like can be obtained.
Inventors: |
KURODA; Motohiko; (Kanagawa,
JP) ; NOGUCHI; Yuji; (Kanagawa, JP) ;
YAMAMOTO; Isao; (Kanagawa, JP) ; FUKUI; Takayuki;
(Kanagawa, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
NISSAN MOTOR CO., LTD. |
Yokohama-shi |
|
JP |
|
|
Assignee: |
NISSAN MOTOR CO., LTD.
Yokohama-shi
JP
|
Family ID: |
45066284 |
Appl. No.: |
15/637709 |
Filed: |
June 29, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13202853 |
Aug 23, 2011 |
9724892 |
|
|
PCT/JP2010/059222 |
May 31, 2010 |
|
|
|
15637709 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B32B 2307/54 20130101;
B32B 2307/40 20130101; B32B 27/08 20130101; B32B 2590/00 20130101;
Y10T 428/24355 20150115; B32B 2307/554 20130101; B32B 7/02
20130101; B32B 27/308 20130101; B32B 2605/006 20130101; B32B
2605/00 20130101; B32B 2307/73 20130101; B32B 27/36 20130101; B32B
2255/26 20130101; B32B 3/30 20130101; B32B 2457/20 20130101; B32B
2255/20 20130101; B32B 25/08 20130101; B32B 2255/205 20130101; B32B
2255/10 20130101 |
International
Class: |
B32B 3/30 20060101
B32B003/30; B32B 27/36 20060101 B32B027/36; B32B 27/08 20060101
B32B027/08; B32B 27/30 20060101 B32B027/30; B32B 7/02 20060101
B32B007/02; B32B 25/08 20060101 B32B025/08 |
Claims
1. A water repellent film, comprising: a first layer having a
plurality of fine protrusions on a surface thereof; a second layer
covering the fine protrusions and having a water repellent
property; and a third layer provided on a surface of the first
layer on an opposite side of the fine protrusions, wherein when a
modulus of elasticity of the first layer is defined as El, a
modulus of elasticity of the second layer is defined as E2, and a
modulus of elasticity of the third layer is defined as E3, a
definition of E2>E1>E3 is fulfilled.
2. The water repellent film according to claim 1, wherein a pitch
of the fine protrusions is 380 nm or less.
3. The water repellent film according to claim 1, wherein a height
of the fine protrusions is 100 nm or more.
4. The water repellent film according to claim 1, wherein a pitch
of the fine protrusions is 150 nm or less.
5. The water repellent film according to claim 1, wherein a height
of the fine protrusions is 600 nm or less.
6. The water repellent film according to claim 1, wherein a
thickness of the third layer is larger than a thickness of the
first layer.
7. The water repellent film according to claim 1, wherein a
thickness T3 of the third layer is 20 .mu.m<T3<250 .mu.m.
8. The water repellent film according to claim 1, wherein an
elongation at break E.sub.max of the third layer is 50% or
more.
9. The water repellent film according to claim 1, wherein the
modulus of elasticity of the first layer is between 0.1 GPa and 5
GPa, and the modulus of elasticity of the second layer is between
50 GPa and 210 GPa.
10. The water repellent film according to claim 1, wherein the fine
protrusions are formed into a cone or pyramid shape, or a frustum
shape.
11. The water repellent film according to claim 1, wherein the
thickness of the first layer is between 1 .mu.m and 30 .mu.m, and a
thickness of the second layer is between 1 nm and 30 nm.
12. A component for a vehicle comprising the water repellent film
according to claim 1.
13. The water repellent film according to claim 1, wherein the
first layer includes a material selected from the group consisting
of a thermoplastic resin, a styrene elastomer, a urethane
elastomer, a silicone elastomer, and gel material, and wherein the
thermoplastic resin includes a material selected from the group
consisting of a non-cross-linked acrylic resin, a cross-linked
acrylic resin, a cross-linked acrylic-urethane copolymer, a
cross-linked acrylic-elastomer copolymer, a silicone elastomer,
cross-linked polyvinyl alcohol, polyvinylidene chloride,
polyethylene terephthalate, polyvinyl chloride, polycarbonate,
modified polyphenylene ether, polyphenylene sulfide, polyether
ether ketone, a liquid crystal polymer, fluororesin, polyarylate,
polysulfone, polyether sulfone, thermoplastic polyimide, polyamide
imide and polyether imide.
14. The water repellent film according to claim 1, wherein the
second layer includes a material selected from the group consisting
of a transparent inorganic and a ceramic material, wherein the
transparent inorganic includes a material selected from the group
consisting of glass, silicon oxide, and aluminum oxide, and wherein
the ceramic material includes a material selected from the group
consisting of silicon nitride, magnesium oxide, titanium oxide,
indium oxide, niobium oxide, zirconium oxide, zinc oxide, ITO,
barium titanate, and hafnia.
15. The water repellent film according to claim 1, wherein the
third layer includes a material selected from the group consisting
of a methacrylic film, a polyolefin film, a polycarbonate film, a
polyester film, a vinyl chloride film, a silicone film, a polyvinyl
alcohol (PVA) film, an ethylene vinyl acetate copolymer (EVA) film,
a cellulose film, and an amide film, wherein the polyolefin film
includes any one of polyethylene and polypropylene, and wherein the
polyester film includes a material selected from the group
consisting of polyethylene terephthalate (PET), polyethylene
naphthalate (PEN), and fluorene derivatives.
Description
CROSS REFERENCE TO RELATED APPLICATION
[0001] This application is a divisional of U.S. application Ser.
No. 13/202,853, filed on Aug. 23, 2011, which is the National Stage
of Application No. PCT/JP2010/059222; filed on May 31, 2010, the
entire contents of all of which are incorporated herein by
reference.
TECHNICAL FIELD
[0002] The present invention relates to a film having a water
repellent function. More particularly, the present invention
relates to a water repellent film capable of preventing abrasions
and damages due to an external friction force caused to fine
protrusions formed on the surface of the film, and relates to a
component for a vehicle including the film.
BACKGROUND ART
[0003] A fine structure has fine protrusions formed on the surface
thereof, and has a water repellent/hydrophilic function and an
antireflection function depending on a material and a dimensional
configuration of the fine structure. Therefore, surfaces of various
substrates applied with such a fine structure can have an
antireflection function with respect to light and a water repellent
function to prevent adhesion of liquid, such as water in
particular. For example, in order to provide such an antireflection
function, a fine structure is favorably used for optical elements
such as lenses for mechanical equipment (for example, refer to
Patent Literature 1).
CITATION LIST
Patent Literature
[0004] Patent Literature 1: Japanese Patent Unexamined Publication
No. 2005-31538
SUMMARY OF INVENTION
[0005] However, in the case where the fine structure described in
Patent Literature 1 is applied to a member such as a window panel
of a vehicle that is subjected to various environmental conditions,
when dirt adhered to the surface of the member because of rain or
the like is removed with a cloth, the fine structure is easily
abraded and damaged. Thus, there is a problem with a water
repellent property of the fine structure that is impaired in a
short period of time.
[0006] The present invention has been made in view of such a
conventional problem. It is an object of the present invention to
provide a water repellent film having excellent resistance to
abrasion, in which a fine structure is not easily abraded and
damaged by an external friction force such as a removal of dirt
with a cloth on a surface thereof, and a component for a vehicle
including the film.
[0007] A water repellent film according to the embodiment of the
present invention includes: a first layer having a plurality of
fine protrusions on a surface thereof; a second layer covering the
fine protrusions and having a water repellent property; and a third
layer provided on a surface of the first layer on an opposite side
of the fine protrusions. When a modulus of elasticity of the first
layer is defined as E1, a modulus of elasticity of the second layer
is defined as E2, and a modulus of elasticity of the third layer is
defined as E3, a definition of E2>E1>E3 is fulfilled.
BRIEF DESCRIPTION OF DRAWINGS
[0008] FIG. 1 is a partial cross-sectional view showing one example
of a water repellent film according to the embodiment of the
present invention.
[0009] FIG. 2 is a schematic view showing a configuration example
of fine protrusions in a water repellent film according to the
embodiment of the present invention.
[0010] FIG. 3 is a schematic view showing a structural example of
fine protrusions in a water repellent film according to the
embodiment of the present invention.
[0011] FIG. 4 is a schematic view explaining input conditions in a
compressive direction and in a shear direction with respect to fine
protrusions in a water repellent film according to the embodiment
of the present invention.
[0012] FIG. 5 is a schematic view showing a mechanism of a water
repellent property in a water repellent film according to the
embodiment of the present invention.
[0013] FIG. 6 is a schematic view showing elongation behavior of
each layer in a case in which a water repellent film according to
the embodiment of the present invention is attached to a
three-dimensional curved surface.
DESCRIPTION OF EMBODIMENTS
[0014] A description will be made below in detail of a water
repellent film and a component for a vehicle including the film
according to the present invention with reference to the drawings.
Note that, the dimensional ratios in the drawings are exaggerated
for convenience of explanation, and may be different from the
actual ratios. In the present description, "%" with regard to
concentrations, contents and the like represents a mass percentage
unless otherwise specified.
[0015] [Water Repellent Film]
[0016] A water repellent film 200 according to the embodiment of
the present invention includes a first layer 10 having a plurality
of fine protrusions 100 on the surface thereof, and a second layer
20 covering the surfaces of the fine protrusions 100 and having a
water repellent property. In addition, a third layer 30 is provided
on the surface of the first layer 10 on the opposite side of the
surface provided with the fine protrusions 100. When a modulus of
elasticity of the first layer 10 is defined as E1, a modulus of
elasticity of the second layer 20 is defined as E2, and a modulus
of elasticity of the third layer 30 is defined as E3, the
definition of E2>E1>E3 is fulfilled.
[0017] FIG. 1 shows the water repellent film 200 according to the
embodiment of the present invention. The water repellent film 200
has the fine protrusions 100 formed into a frustum shape. Examples
of the configuration of the fine protrusions 100 to be favorably
used include a frustum shape such as a circular truncated cone and
a truncated pyramid, and a cone or pyramid shape. In addition,
other configurations such as a deformed cone shape such as a bell
shape and an acorn shape, a deformed pyramid shape having curved
side surfaces, a round-tipped shape, and a shape inclined from a
center line, may be applied to the fine protrusions 100. FIG. 2
shows examples of the cross-sectional configuration that the fine
protrusions 100 may employ in the water repellent film according to
the embodiment of the present invention.
[0018] Examples of a bottom surface configuration of the fine
protrusions 100 to be favorably used include a polygonal shape and
a substantially circular shape. In addition, other shapes such as a
star shape and an oval shape may be used. The water repellent film
of the present invention may include concave portions 101 between
the fine protrusions 100 as long as the fine protrusions 100 are
two-dimensionally aligned with a predetermined pitch, as shown in
FIG. 3. In the present description, as shown in FIG. 3(a), when it
is assumed that there is a surface B' passing through bottoms 102
of the respective concave portions 101, each section on the surface
B' sectioned by the bottoms 102 of the concave portions 101
surrounding the fine protrusions 100 is defined as a bottom surface
of the respective fine protrusions 100. Similarly, in the case
where base portions 103 of the fine protrusions 100 have curved
surfaces as shown in FIG. 3(b), when it is assumed that there is
the surface B' passing through bottoms 104 between the respective
base portions 103 of the fine protrusions 100, each section on the
surface B' sectioned by the bottoms 104 between the base portions
103 surrounding the fine protrusions 100 is defined as a bottom
surface of the respective fine protrusions 100.
[0019] A pitch A of the respective fine protrusions 100 is
preferably 50 .mu.m or less. When the pitch A between the fine
protrusions 100 adjacent to each other is more than 50 .mu.m, an
effective water repellent property of various window panels using
such a water repellent film is not easily exerted. Namely, since
water droplets of a drizzly rain have a size of approximately 50
.mu.m, water droplets are infiltrated in gaps between the fine
protrusions, and the water droplets are not easily removed from the
surface of the water repellent film. However, when the surface of
the second layer 20 formed on the fine protrusions 100 is subjected
to water repellent treatment using a water repellent material as
described below, the water repellent film may have a high water
repellent property even when the pitch A is more than 50 .mu.m.
Note that, in the present description, the pitch A of the
respective fine protrusions 100 represents a distance between each
barycenter in the bottom surfaces of the fine protrusions 100
adjacent to each other.
[0020] When an antireflection function is applied to the water
repellent film 200, the pitch A of the respective fine protrusions
100 is preferably 380 nm or less. Namely, the pitch A of the fine
protrusions 100 is preferably equal to or less than a wavelength of
visible light which is not more than 380 nm to 750 nm. When the
pitch A exceeds 380 nm, the visible light is partially diffused or
diffracted by the fine protrusions 100, and accordingly, a
reflectance of the light may become large. The pitch A of the
respective fine protrusions 100 is more preferably 150 nm or less.
When the pitch A is 150 nm or less, the surface roughness of the
water repellent film is not more than an average surface roughness
of human nails. Therefore, performance of abrasion resistance to
scratch of nails is effectively exerted on various window panels
using the water repellent film. As described below, a high water
repellent property is exerted on the water repellent film when the
fine protrusions 100 are formed on the surface of the water
repellent film so as to increase a surface area, and when gaps for
trapping air are formed between the fine protrusions 100 adjacent
to each other. Consequently, the pitch A of the fine protrusions
100 is preferably 50 nm or more.
[0021] In the first layer 10, a height H of the fine protrusions
100 is preferably 100 nm or more. When the height H of the fine
protrusions 100 is less than 100 nm, an antireflection effect may
be decreased. In addition, when the height H of the fine protrusion
100 is too low, it is hard to trap air between the fine protrusions
100, which may cause a decrease of a water repellent property. On
the other hand, when the height H of the fine protrusions 100 is
too high, the fine protrusions 100 are easily fractured and at the
same time moldability may be decreased. Thus, the height of the
fine protrusions 100 is preferably 600 nm or less. It is to be
noted that, when the surface of the second layer 20 is subjected to
water repellent treatment as described above, a high water
repellent property may be exerted even when the height H is less
than 100 nm. The height of the fine protrusions 100 is a distance
between each bottom 104 of the fine protrusions 100 and each tip of
the fine protrusions 100 in the perpendicular direction to the
bottom surface B'. When the concave portions 101 are provided
between the respective fine protrusions 100, the height as
indicated by the reference symbol H in FIG. 3 is a distance each
bottom (the deepest part) 102 of the concave portions 101 and each
tip of the fine protrusions 100 in the perpendicular direction to
the bottom surface B'.
[0022] In the water repellent film 200, when the fine protrusions
100 are formed into a cone or pyramid shape, or a truncated cone or
truncated pyramid shape (tapered shape), and two-dimensionally
aligned with the pitch A of 380 nm or less, a dimension of the fine
asperity on the surface cannot be recognized by visible light. As a
result, coloration due to interference of light disappears, and
therefore, the water repellent film can be used as a transparent
material. Moreover, since reflection of surrounding scenery on the
film can be decreased due to an antireflection effect, the water
repellent film can be favorably used for window panels for
vehicles, ships and vessels, and aircraft. Further, since the gaps
between the fine protrusions 100 are elongated, and water
infiltration because of impact of water droplets is prevented, the
water repellent film exerts a superhydrophobic property with no
adhesion of water droplets such as rain, depending on the materials
to be selected.
[0023] The dimension of the fine protrusions 100 in the water
repellent film of the present invention is a nanometer order as
described above. Thus, the configuration and pitch of the fine
protrusions 100 do not have a complete geometric configuration, but
vary to some extent because of a manufacturing restriction.
However, the there is no limitation in scope of the present
invention even if variations of the configuration and pitch of the
fine protrusions are caused.
[0024] As described above, the water repellent film 200 according
to the present embodiment includes the first layer 10 having a
plurality of the fine protrusions 100, the second layer 20 covering
the entire surface of the fine protrusions 100 and having a water
repellent property, and the third layer 30 provided on the surface
of the first layer 10 on the opposite side of the fine protrusions
100. In addition, when the modulus of elasticity of the first layer
10 is defined as E1, the modulus of elasticity of the second layer
20 is defined as E2, and the modulus of elasticity of the third
layer 30 is defined as E3, the definition of E2>E1>E3 is
fulfilled. Due to such a configuration, destruction of the fine
protrusions 100, that is, abrasions and damages can be
prevented.
[0025] The external input such as a removal of dirt with a cloth
may be broadly divided into an input in a shear direction
substantially along the surface of the first layer 10, and an input
in a compressive direction substantially perpendicular to the
surface of the first layer. With regard to the input in the shear
direction, the second layer 20 has the modulus of elasticity E2
higher than that of the first layer 10, so as not to be easily
abraded. Further, the input of shear force transmitted to the first
layer 10 is absorbed and dispersed. In addition, since the first
layer 10 has the modulus of elasticity E1 lower than that of the
second layer 20, the input of shear force to the fine protrusions
100 is flexibly absorbed.
[0026] With regard to the input in the compressive direction, the
third layer 30 having the modulus of elasticity E3 lower than that
of the first layer 10 mainly receives the input so as to be
deformed elastically, thereby preventing destruction of the fine
protrusions 100. The first layer 10 is required to have a
predetermined level of the modulus of elasticity E1 in view of
enhancing a dimensional accuracy at the time of the formation of
the fine protrusions 100 and preventing the fine protrusions 100
from scratches of nails. However, when the first layer 10 is only
provided with the second layer 20 covering the first layer and
having the higher modulus of elasticity E2, the first layer 10 is
mainly subjected to elastic deformation due to the input in the
compressive direction; on the other hand, the second layer 20 is
not elastically deformed very much. In such a case, since the
amount of elastic deformation of the first layer 10 relatively
becomes large, it is hard to ensure resistance to abrasion.
However, when the third layer 30 having the modulus of elasticity
E3 lower than that of the first layer 10 is provided on the surface
of the first layer 10 on the opposite side of the fine protrusions
100, the third layer 30 is subjected to elastic deformation.
Accordingly, the amount of elastic deformation of the first layer
10 or the second layer 20 can be decreased.
[0027] The influence of the inputs in the compressive direction and
the shear direction with respect to the fine protrusions will be
further explained. FIGS. 4(a) to 4(c) show water repellent films
not provided with the second layer. In particular, in FIG. 4(b),
the modulus of elasticity E3 of the third layer 30 and the modulus
of elasticity E1 of the first layer 10 have a relationship of
E3>E1. In FIG. 4(c), the modulus of elasticity E3 of the third
layer 30 and the modulus of elasticity E1 of the first layer 10
have a relationship of E1>E3. As shown in FIG. 4(b), when a load
W is applied in the compressive direction, the first layer 10 is
mainly deformed and the third layer 30 is not easily deformed since
the modulus of elasticity E3 of the third layer 30 is higher than
the modulus of elasticity E1 of the first layer 10. As a result,
the load W is concentrated on the fine protrusions 100, so that the
fine protrusions 100 are crushed by the load W (refer to the
reference symbol C). On the other hand, as shown in FIG. 4(c), when
the modulus of elasticity E3 of the third layer 30 is lower than
the modulus of elasticity E1 of the first layer 10, not only the
first layer 10 but also the third layer 30 are deformed, and the
load W applied to the fine protrusions 100 is dispersed.
Accordingly, the crush of the fine protrusions 100 can be
prevented.
[0028] It is to be noted that, when the second layer is not formed
in the water repellent film, and particularly when the first layer
10 is made of a material such as a resin material as described
later having the modulus of elasticity E1, the fine protrusions are
easily subjected to abrasion from the tips thereof due to
continuous inputs in the shear direction. In view of this, the
water repellent film according to the present invention is provided
with the second layer having a high modulus of elasticity and
rigidity in order to improve resistance to abrasion. However, even
if the second layer 20 is formed in the film, the fine protrusions
100 are easily fractured when the modulus of elasticity E3 of the
third layer 30 is higher than the modulus of elasticity E1 of the
first layer 10, or when the third layer is not provided, as shown
in FIG. 4(d). In other words, since the surface of the second layer
is rigid, moment is concentrated on a portion D of a ridge line of
the fine protrusions 100 due to the input in the shear direction
(horizontal direction), and therefore, the fine protrusions 100 are
easily fractured. When the load W is applied in a sliding direction
while evenly coming in contact with the surface of the second
layer, the second layer is not easily fractured since the surface
thereof is rigid. On the other hand, when the load W is applied in
a sliding direction not evenly coming in contact with the surface
of the second layer, the input locally becomes large, and as a
result, the fine protrusions 100 are fractured because of
brittleness of the second layer 20. However, as described above,
when the modulus of elasticity E3 of the third layer 30 is lower
than the modulus of elasticity El of the first layer 10, the third
layer 30 is deformed, so that the load W applied to the fine
protrusions 100 is dispersed. Accordingly, moment concentrated on
the fine protrusions 100 can be prevented, and therefore, the fine
protrusions 100 are not easily fractured.
[0029] As described above, since the first layer 10, the second
layer 20 and the third layer 30 share the function with respect to
an external input such as a removal of dirt with a cloth, the
fracture of the fine protrusions 100 can be suppressed.
[0030] The modulus of elasticity E1 of the first layer 10 is
particularly preferably between 0.1 GPa and 5 GPa, and the modulus
of elasticity E2 of the second layer 20 is preferably between 50
GPa and 210 GPa. When the modulus of elasticity E1 of the first
layer 10 is within the above-mentioned range, the second layer 20
can sufficiently exert the effect of dispersing an external input
in a shear direction without being inhibited by the first layer. In
addition, when the modulus of elasticity of the second layer 20 is
50 GPa or more, abrasions of the second layer 20 and plastic
deformation or fracture of the first layer 10 can be surely
suppressed. Moreover, when the modulus of elasticity of the second
layer 20 is 210 GPa or less, brittle damages of the second layer 20
due to an external input in a shear direction can be more surely
suppressed.
[0031] A thickness T1 of the first layer 10 is preferably between 1
.mu.m and 30 .mu.m. When the thickness of the first layer 10 is 1
.mu.m or more, an occurrence of brittle damages (cracks) of the
first layer 10 can be prevented even when the third layer 30 is
deformed due to an input in a compressive direction. In addition,
when the thickness of the first layer 10 is 30 .mu.m or less, a
curved surface compliance property can be easily ensured when the
water repellent film 200 is applied to a molded product having a
three-dimensional curved surface. Further, moldability can be
easily ensured when an active energy beam curable resin is used as
a material of the first layer 10.
[0032] A film thickness T2 of the second layer 20 is preferably
between 1 nm and 30 nm, more preferably between 3 nm and 20 nm.
With regard to the structure of the fine protrusions 100 having the
pitch A of 380 nm or less, the film thickness T2 of the second
layer 20 is preferably between 3 nm and 10 nm. When the film
thickness of the second layer 20 is within 30 nm, brittle damages
of the second layer 20 can be prevented. In addition, when the film
thickness is 1 nm or more, the entire fine protrusions 100 can be
evenly covered with the second layer 20.
[0033] Examples of the material of the first layer 10 include:
thermoplastic resins such as a non-cross-linked acrylic resin, a
cross-linked acrylic resin, a cross-linked acrylic-urethane
copolymer, a cross-linked acrylic-elastomer copolymer, a silicone
elastomer, polyethylene, polypropylene, cross-linked polyvinyl
alcohol, polyvinylidene chloride, polyethylene terephthalate,
polyvinyl chloride, polycarbonate, modified polyphenylene ether,
polyphenylene sulfide, polyether ether ketone, a liquid crystal
polymer, fluororesin, polyarylate, polysulfone, polyether sulfone,
polyamide imide, polyether imide, and thermoplastic polyimide;
styrene elastomers such as polystyrene; urethane elastomers;
silicone elastomers; and various gel materials.
[0034] Examples of the material of the second layer 20 include:
transparent inorganic materials such as glass, silicon oxide, and
aluminum oxide; and ceramic materials such as silicon nitride,
magnesium oxide, titanium oxide, indium oxide, niobium oxide,
zirconium oxide, zinc oxide, ITO (indium tin oxide), and barium
titanate. In particular, hafnia (hafnium oxide, HfO.sub.2) has a
contact angle of 90 degrees or more. Therefore, a high water
repellent property can be exerted even if the surface of the second
layer is not subjected to chemical treatment in order to have a
water repellent property.
[0035] When a contact angle of the material of the second layer 20
with respect to water droplets is 90 degrees or more, a
superhydrophobic state that far exceeds the contact angle of the
material itself of the second layer 20 is obtained (Cassie theory)
because of an increase of the surface area of the water repellent
film and an effect of trapping air in gaps 22 between the fine
protrusions 100 adjacent to each other, as shown in FIG. 5. In
order to further effectively exert the superhydrophobic state, the
contact angle of the material itself of the second layer 20 with
respect to water droplets is preferably 100 degrees or more, more
preferably 110 degrees or more. Especially when the material having
the contact angle of 110 degrees or more is used for the second
layer of the fine protrusions 100, the contact angle is amplified
by the fine protrusions 100 so that the contact angle becomes 140
degrees or more, thereby improving a water repellent property to
such a degree that water droplets are hardly adhered to the surface
of the second layer 20.
[0036] In order to achieve such a water repellent effect, the
contact angle may be controlled by selecting the material of the
second layer 20 itself. As a method of controlling the contact
angle more simply, a method of allowing a water repellent material
having reactivity with the material of the second layer to
chemically adhere to or react with a surface 21 of the second layer
20 may be used. The method of controlling the contact angle is not
particularly limited as long as a plurality of the fine protrusions
100 are not blocked by the water repellent material. When the
method of applying the water repellent material diluted with a
solvent to the surface 21 of the second layer 20 is used, the water
repellent material can be fixed to the surface 21 of the second
layer 20.
[0037] Examples of the water repellent material applied to the
surface 21 of the second layer 20 include silicone compounds such
as
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2OCH.sub.3
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--SiCH.sub.3(OCH.sub.3).sub.2
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(OCH.sub.3).sub.3
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(OC.sub.2H.sub.5).sub.3
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2(CH.sub.2).sub-
.3OCH.sub.2CH(OH)CH.sub.2NH(CH.sub.2).sub.3Si(OCH.sub.3).sub.3
(n>13; contact angle of 95 to 105 degrees),
(CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2(CH.sub.2).su-
b.3OCH.sub.2CH(OH)CH.sub.2).sub.2N(CH.sub.2).sub.3Si(OCH.sub.3).sub.3
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(OH).sub.3 (n>13;
contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2Cl
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2(CH.sub.2).sub-
.2SiCH.sub.3Cl.sub.2 (n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--SiCl.sub.3 (n>13;
contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(OCOCH.sub.3).sub.3
(n>13; contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(NCO).sub.3 (n>13;
contact angle of 95 to 105 degrees),
CH.sub.3--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2(CH.sub.2).sub-
.3O(CH.sub.2).sub.3OCONHSi(NCO).sub.3 (n>13; contact angle of 95
to 105 degrees),
Rf-(CH.sub.2).sub.2--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3-
).sub.2(CH.sub.2).sub.3OCH.sub.2CH(OH)CH.sub.2NHSi(OCH.sub.3).sub.3
(n>13; contact angle of 95 to 115 degrees), and
(Rf-(CH.sub.2).sub.2--(Si(CH.sub.3).sub.2--O).sub.n--Si(CH.sub.3).sub.2(C-
H.sub.2).sub.3OCH.sub.2CH(OH)CH.sub.2).sub.2N(CH.sub.2).sub.3Si(OCH.sub.3)-
.sub.3 (n>13; contact angle of 95 to 115 degrees) (Rf is
CF.sub.3--(CF.sub.3).sub.m--, or CF.sub.3--(OCF.sub.2).sub.m: m=1
to 20). In addition, a material obtained by changing a substituent
group such as Teflon (registered trademark) and the above-mentioned
silane compound to isocyanate may also be used.
[0038] When the water repellent film according to the present
invention is used in applications in contact with liquid other than
water, such as an observation window panel of a reactor vessel or a
distillation column in various types of plant equipment, and a lens
surface of an endoscope, a contact angle with respect to contacting
liquid is preferably set at 90 degrees or more by surface treatment
or the like depending on the applications.
[0039] As shown in FIG. 1, the water repellent film 200 according
to the present invention includes the third layer 30 in contact
with the first layer 10 on the opposite side of the fine
protrusions 100. In addition, the third layer 30 may be provided
with an adhesive agent on the opposite side of the first layer 10
according to the applications of the water repellent film. When a
water repellent film is used for an antireflection application,
both surfaces of a transparent material are required to be provided
with fine protrusions. In the present invention, both surfaces of
the third layer 30 made of a transparent material are provided with
the first layer 10 and the second layer 20 symmetrically, so that
an antireflection effect can be obtained.
[0040] The modulus of elasticity E3 of the third layer 30 is
required to be lower than the modulus of elasticity E1 of the first
layer 10. Examples of the material used for the third layer 30
include general-purpose resin films and engineering plastic films.
More specific examples of the material to be used include
methacrylic films; polyolefin films such as polyethylene and
polypropylene; polycarbonate films; polyester films such as
polyethylene terephthalate (PET), polyethylene naphthalate (PEN),
and fluorene derivatives; vinyl chloride films; silicone films;
polyvinyl alcohol (PVA) films; ethylene vinyl acetate copolymer
(EVA) films; cellulose films; and amide films. When the water
repellent film is used in a portion in which further transparency
is required, a transparent third layer is selected. A material of
the transparent third layer is preferably methacrylic films,
polycarbonate films, or PET films, more preferably methacrylic
films or PET films.
[0041] When the first layer 10 has a thickness barely able to
prevent brittleness, the third layer 30 functions to support
rigidity and film intensity of the first layer 10. In addition,
when the modulus of elasticity of the third layer is controlled to
be lower than that of the first layer, the third layer is more
easily deformed due to an external input in a compressive direction
compared to the first layer. Therefore, an input to the fine
protrusions 100 can be absorbed.
[0042] A thickness T3 of the third layer 30 is not particularly
limited as long as the third layer is thick sufficient to comply
with a three-dimensional curved surface or sufficient to be molded.
However, the thickness T3 of the third layer 30 is preferably
thicker than the thickness of the first layer 10. Due to such a
thickness, the third layer 30 is more easily deformed than the
first layer, and an input to the fine protrusions 100 in a
compressive direction can be absorbed. When considering
processability of molding and adhesion in addition to such an
action, the thickness T3 of the third layer 30 is preferably
approximately between 20 .mu.m and 250 .mu.m, more preferably
between 25 .mu.m and 200 .mu.m, most preferably between 25 .mu.m
and 70 .mu.m. When the thickness T3 of the third layer 30 is within
the range of 20 .mu.m to 200 .mu.m, the deformation amount of the
third layer 30 is appropriately decreased when a load in a
compressed direction is input to the water repellent film 200.
Accordingly, an uneven contact of friction elements at the time of
friction input is not caused, a load is uniformly dispersed, and
therefore, the fine protrusions 100 are not easily abraded.
[0043] The modulus of elasticity E3 of the third layer 30 is at
most 6 GPa when considering the type of the material described
above. Therefore, with regard to deformation, a variation of the
thickness of the third layer 30 is more influential than the first
layer 10. In addition, in view of handling of a stacked film such
as the water repellent film 200 according to the present invention,
and in view of damages of the third layer at the time of
compressive deformation, an elongation at break .epsilon..sub.max
of the third layer 30 is preferably 50% or more. Note that, the
upper limit of the elongation at break .epsilon..sub.max of the
third layer 30 is not particularly limited; however, the upper
limit may be 500% or less.
[0044] [Method for Manufacturing Water Repellent Film]
[0045] Hereinafter, a method for manufacturing the water repellent
film according to the present invention will be explained. In the
water repellent film according to the present invention, a film to
be the third layer 30 is prepared first. Then, the film is provided
with the fine protrusions 100 so as to form the first layer 10. A
method of providing the fine protrusions 100 on the first layer 10
is not particularly limited. For example, a method of forming the
fine protrusions 100 directly on the first layer is used. Further,
a method of pressing a concave-convex molding die having a fine
protrusion pattern to a thin film obtained by applying a material
easily molded to the film prepared first so as to transfer the fine
protrusion pattern to the thin film is used. As a result, the fine
protrusions 100 are formed.
[0046] More specifically, a film composed of materials of the first
layer and the third layer produced by a known method is prepared.
Then, a molding die to form numerous fine protrusions is prepared,
and the molding die and the film composed of materials of the first
layer and the third layer are pressed relatively while heating one
of or both of the molding die and the film. Therefore, the fine
protrusions 100 can be formed on the surface of the first
layer.
[0047] In addition, an active energy beam curable resin is applied
on the film to be the third layer. Then, a portion between the
molding die and the film to be the third layer is irradiated with
an active energy beam while interposing the active energy beam
curable resin, so that the resin is cured. An example of the active
energy beam curable resin may be an ultraviolet beam curable
resin.
[0048] After the first layer having the fine protrusions 100 is
formed by the above-described methods, the second layer 20 is
formed by a conventionally known method. Examples of the method of
producing the second layer 20 include a Langmuir-Blodgett method
(LB method), a physical vapor deposition method (PVD method), a
chemical vapor deposition method (CVD method), a self-organization
method, a sputtering method, a vapor polymerization method, and an
evaporation method.
[0049] Further, as described above, when a water repellent material
is fixed to the second layer, the water repellent material that is
diluted with a solvent is applied on the second layer and then
dried. In order to promote the reaction of the second layer with
the water repellent material after the application of the water
repellent material, heat treatment may be carried out as
necessary.
[0050] [Molded Product Including Water Repellent Film]
[0051] A molded product (component) including the water repellent
film according to the present invention may be preferably used for
a display device that is required to have an antireflection
function on the front surface thereof and is subjected to water
such as rain and greasy dirt. Examples of the molded product
include meter panels and window panels for vehicles and motor
cycles, mobile devices such as a mobile phone and an electronic
organizer, signs, and watches. A type of the display device is not
particularly limited, and a system in which a mechanical display
and lighting are combined such as an analog meter may be included.
Moreover, a system, such as a digital meter and a monitor, using a
back light and a light-emitting surface such as a liquid crystal,
light-emitting diode (LED) and electroluminescence (EL), and a
system using a reflective liquid crystal such as a mobile device
may also be included.
[0052] Such a molded product is mainly used in places to be
subjected to light. Therefore, an ultraviolet absorbing agent, an
antioxidant, a radical scavenger, and the like may be added to the
first layer and the third layer in order to prevent deterioration
by light. In addition, a blueing agent and a fluorescent pigment
for offsetting yellowing caused by resin deterioration may also be
used.
[0053] A method for manufacturing the molded product including the
water repellent film is not particularly limited as long as the
film can be attached to the surface of the molded product. A method
of attaching the film by hands while applying heat on a curved
surface may be used. In addition, a laminator and the like may be
used when the molded product does not have a curved surface.
Further, the water repellent film according to the present
invention may be attached to the molded product by use of an
adhesive agent as necessary.
[0054] When the water repellent film according to the present
invention is incorporated in a display device, the provision of the
film on the front surface of the display device is most effective.
In addition, a conventional antireflection means may be applied to
the surface of the third layer on the opposite side of the first
layer in the water repellent film according to the present
invention. Examples of the conventional antireflection means
include a means of applying an antireflection structure only
provided with fine protrusions with a pitch not more than a
wavelength of light, and a means of allowing reflected light from
the surface of the thin film in which the thickness of the
antireflection layer is controlled and reflected light from the
attachment surface of the third layer to interfere with each other,
so as to decrease reflection.
[0055] When it is assumed that the water repellent film according
to the present invention is attached to a three-dimensional curved
surface, the properties required for the third layer and the first
layer are determined according to a radius of curvature of the
three-dimensional curved surface. In particular, the important
property in molding and processing of the film for the
three-dimensional curved surface is a maximum value of elongation
at break B. That is, as shown in FIG. 6, it is assumed that the
thickness of the first layer 10 is T1, the thickness of the third
layer 30 is T3, and the thickness of an adhesion layer 40 applied
on the surface of the third layer 30 on the opposite side of the
first layer 10 is T4. When the water repellent film 200 is attached
to a convex surface of a radius of curvature R of a component 50,
the water repellent film 200 is curved on the basis of an adhesion
surface 41 of the adhesion layer 40. Then, one-dimensional
elongation of the uppermost surface of the first layer 10 that is
the most elongated layer with respect to a distance R (radius of
curvature) from the center O of curvature to the adhesion surface
41 is calculated. Thus, the maximum value of elongation at break B
can be calculated according to the formula 1. Therefore, at least
the material of the first layer 10 is required to have an
elongation at break higher than the maximum value of elongation at
break B.
B = ( R + T 1 + T 3 + T 4 ) 2 R 2 = R + T 1 + T 3 + T 4 R [ Math 1
] ##EQU00001##
[0056] On the other hand, when the water repellent film 200 is
attached to a concave surface of the component 50, the adhesion
layer 40 is to be elongated on the basis of the uppermost surface
of the first layer 10 since the first layer 10 has the higher
modulus of elasticity than the third layer 30 or the adhesion layer
40. However, the adhesion layer 40 is not fractured since the
elongation at break of the adhesion layer 40 is much larger than
that of the first layer 10.
[0057] As described above, the water repellent film according to
the present invention includes the first layer, the second layer
and the third layer having the above-described characteristics.
Therefore, the water repellent film has an excellent resistance to
abrasion while ensuring a high water repellent property. Further,
since the pitch between the fine protrusions is controlled to be
380 nm or less, reflection of visible light can be decreased to an
extremely low level. Accordingly, when the water repellent film is
applied to a component for a vehicle and other applications, such
as a meter cover and a windshield, reflection of surrounding
sceneries or interiors on the film can be prevented while ensuring
a water repellent property.
[0058] When the water repellent film according to the present
invention is used for window glass or an analog meter, all of the
first layer, the second layer and the third layer included in the
water repellent film are preferably transparent. On the other hand,
when the water repellent film is used for a digital meter or a
screen of a car navigation system, the first layer and the third
layer may have opaque areas for the purpose of adding an anti-glare
function and a depolarization function.
EXAMPLES
[0059] Hereinafter, the present invention will be further explained
in detail with reference to examples. However, the scope of the
present invention is not limited to those examples.
Examples 1 to 19
[0060] First, a film to be the third layer and an ultraviolet
curable monomer for forming the first layer were prepared for
respective Examples 1 to 3 and 8 to 19, as shown in Table 1. Note
that, "flexible acrylic resin" in Table 1 is ACRYPLEN (registered
trademark) manufactured by Mitsubishi Rayon Co., Ltd. Next, the
ultraviolet curable monomer was applied to one surface of the film
to be the third layer. Then, a metal mold for forming fine
protrusions having dimensions described in Table 2 was pressed
against the monomer, followed by irradiation of ultraviolet from
the film to be the third layer, so that the monomer was cured.
Subsequently, the film was separated from the metal mold, so as to
prepare the film provided with the fine protrusions on the first
layer for the respective examples. Thereafter, the second layer
described in Table 1 was applied to the film of the respective
examples by use of a sputtering method.
[0061] With regard to Example 4, a film to be the third layer and a
urethane gel (product name: PANDEX (registered trademark)
<two-component curable type>, manufactured by DIC
Corporation) for forming the first layer were prepared, as shown in
Table 1. Next, the gel solution was applied to a metal mold for
forming fine protrusions having dimensions described in Table 2,
and the metal mold was pressed against the film to be the third
layer, followed by curing at 100.degree. C. for one hour. Then, the
film was separated from the metal mold, so as to prepare the film
provided with the fine protrusions on the first layer. Thereafter,
the second layer described in Table 1 was applied to the film by
use of a sputtering method.
[0062] With regard to Example 5, a film to be the third layer and a
silicone gel (product name: KE-1051, manufactured by Shin-Etsu
Chemical Co., Ltd.) for forming the first layer were prepared, as
shown in Table 1. Next, the silicone gel solution was applied to a
metal mold for forming fine protrusions having dimensions described
in Table 2, and the metal mold was pressed against the film to be
the third layer, followed by curing at 100.degree. C. for one hour.
Then, the film was separated from the metal mold, so as to prepare
the film provided with the fine protrusions on the first layer.
Thereafter, the second layer described in Table 1 was applied to
the film by use of a sputtering method.
[0063] With regard to Examples 6 and 7, a film to be the third
layer was prepared. In addition, for the formation of the first
layer, a mixture solution of 5% of polycaprolactone (product name:
PCL-220, manufactured by Daicel Chemical Industries, Ltd.) and 95%
of 4,4'-diphenylmethane diisocyanate (product name: Millionate MT,
manufactured by Nippon Polyurethane Industry Co., Ltd.) was
prepared. Next, the mixture solution was applied to a metal mold
for forming fine protrusions having dimensions described in Table
2, and the metal mold was pressed against the film to be the third
layer, followed by curing at 130.degree. C. for one hour. Then, the
film was separated from the metal mold, so as to prepare the film
provided with the fine protrusions on the first layer for the
respective examples. Thereafter, the second layer described in
Table 1 was applied to the film for the respective examples by use
of a sputtering method.
[0064] With regard to Examples 1 to 8 and 15 to 19, the surface of
the second layer was subjected to surface treatment using
perfluoroethertrimethoxysilane as a water repellent material. More
specifically, a solution obtained by diluting
perfluoroethertrimethoxysilane with hydrofluoroether (product name:
HFE-7100, manufactured by Sumitomo 3M Limited) by 0.1% was
prepared. Next, the film provided with the second layer for the
respective examples was impregnated with this solution, and pulled
up at a pull-up rate of 10 mm/sec, so as to apply the solution to
the surface of the second layer. Thereafter, the film applied with
the solution was dried at 100.degree. C. for one hour, followed by
fixing water repellent groups to the surface of the second layer
provided on fine protrusions, thereby obtaining the water repellent
film for the respective examples. Note that,
perfluoroethertrimethoxysilane is indicated by a reference symbol
"a" in Table 2.
[0065] With regard to Examples 9, 11 and 13, the second layer was
subjected to the same surface treatment using
(heptadecafluoro-1,1,2,2-tetrahydrodecyl) trimethoxysilane
(manufactured by AZmax Co., Ltd.). Note that,
(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane is
indicated by a reference symbol "b" in Table 2.
[0066] With regard to Examples 10 and 14, the second layer was
subjected to the same surface treatment using
(heptafluorooctyl)trimethoxysilane (manufactured by AZmax Co.,
Ltd.). Note that, (heptafluorooctyl)trimethoxysilane is indicated
by a reference symbol "c" in Table 2. With regard to Example 12,
the second layer made of hafnia was not subjected to surface
treatment.
Comparative Example 1
[0067] First, a fine protrusion pattern was transferred to PVA, so
as to prepare a replica mold of fine protrusions having dimensions
described in Table 2. Next, polysiloxane was poured into the
replica mold. Then, the third layer subjected to corona treatment
was pressed against the polysiloxane, and heated at 100.degree. C.
for 24 hours, followed by keeping at constant temperature and
humidity at 100.degree. C. and at 60% humidity for 24 hours,
thereby forming a film composed of the first layer having the fine
protrusions and the third layer. In this comparative example, the
film was not provided with the second layer.
Comparative Example 2
[0068] A film composed of the first layer and the third layer was
prepared in the same manner as Example 3. However, the film was not
provided with the second layer in this example.
[0069] The materials, properties and thicknesses of the first layer
to third layer for the respective examples and comparative examples
are shown in Table 1. The respective values of each modulus of
elasticity in Table 1 were measured according to the method
described in JIS K 6911 of Japanese Industrial Standard. The
elongation at break was measured according to the method described
in JIS K 7161 (ISO 527). In addition, the thicknesses of the
respective layers, and the pitches, heights and tip diameters of
the fine protrusions were measured using a scanning electron
microscope (SEM), respectively.
TABLE-US-00001 TABLE 1 Third Layer First Layer Second Layer Modulus
of Elongation Modulus of Modulus of Contact Elasticity Thickness at
Break Elasticity Thickness Elasticity Thickness Angle Material
(GPa) (.mu.m) (%) Material (GPa) (.mu.m) Material (GPa) (.mu.m)
(.degree.) Example 1 PET 3.5 25 150 Cross- 3.8 8 Silicon 70 10 21
linked Oxide PMMA Example 2 PET 3.5 50 150 Cross- 4 5 Zirconium 210
15 25 linked Oxide PMMA Example 3 PET 3.5 100 150 Cross- 5 5
Zirconium 210 30 25 linked Oxide PMMA Example 4 Silicone 0.05 100
300 Urethane 0.1 30 Silicon 50 10 21 Gel Oxide Example 5 Silicone
0.1 100 250 Silicone 0.3 30 Silicon 60 10 21 Gel Oxide Example 6
Silicone 0.3 200 200 Urethane 0.7 30 Silicon 70 10 21 Elastomer
Oxide Example 7 Siheone 0.3 200 200 Urethane 0.7 30 Silicon 80 10
21 Elastomer Oxide Example 8 Flexible 2 50 50 Cross- 2.8 15 Silicon
70 10 21 Acrylic linked Oxide Resin PMMA Example 9 Flexible 1.2 50
50 Cross- 4 10 Aluminum 70 5 21 Acrylic linked Oxide Resin PMMA
Example 10 Flexible 1.3 100 50 Cross- 4 10 Aluminum 65 5 21 Acrylic
linked Oxide Resin PMMA Example 11 Flexible 0.9 100 50 Cross- 4.5
10 Aluminum 70 10 21 Acrylic linked Oxide Resin PMMA Example 12
Flexible 0.9 100 50 Cross- 4.5 10 Hafnia 70 5 90 Acrylic linked
Resin PMMA Example 13 Acrylic 2.8 200 40 Cross- 5 8 Zirconium 210
15 25 Resin linked Oxide PMMA Example 14 Acrylic 3 200 40 Cross- 5
1 Zirconium 210 30 25 Resin linked Oxide PMMA Example 15 Flexible 2
100 50 Cross- 3.8 6 Silicon 70 5 15 Acrylic linked Oxide Resin PMMA
Example 16 Flexible 2 100 50 Cross- 2.8 8 Silicon 70 5 15 Acrylic
linked Oxide Resin PMMA Example 17 Flexible 1.9 200 50 Cross- 2.8
10 Silicon 70 5 15 Acrylic linked Oxide Resin PMMA Example 18
Flexible 1.9 250 50 Cross- 2.8 10 Silicon 70 5 15 Acrylic linked
Oxide Resin PMMA Example 19 Flexible 1.9 250 50 Cross- 2.8 10
Silicon 70 5 15 Acrylic linked Oxide Resin PMMA Comparative PET 3.5
25 150 SiOx 65 10 -- -- -- -- Example 1 Comparative PET 3.5 50 150
PMMA 2 5 -- -- -- -- Example 2
TABLE-US-00002 TABLE 2 Fine Protrusions Surface Treatment Tip
Contact Pitch Height Diameter Angle Configuration (nm) (nm) (nm)
Material (.degree.) Example 1 Circular Truncated 100 200 5 a 115
Cone Example 2 Circular Truncated 380 500 30 a 115 Cone Example 3
Circular Truncated 5000 5000 200 a 115 Cone Example 4 Circular
Truncated 250 250 15 a 115 Cone Example 5 Circular Truncated 250
500 10 a 115 Cone Example 6 Circular Truncated 300 380 20 a 115
Cone Example 7 Circular Truncated 300 300 10 a 115 Cone Example 8
Circular Truncated 100 100 5 a 115 Cone Example 9 Circular
Truncated 100 200 7 b 110 Cone Example 10 Circular Truncated 100
200 5 c 108 Cone Example 11 Circular Truncated 200 200 5 b 110 Cone
Example 12 Circular Truncated 200 200 5 -- -- Cone Example 13
Hemisphere 2000 2000 0 b 110 Example 14 Truncated 5000 3000 100 c
108 Square Pyramid Example 15 Bell Shape 100 200 -- a 115 Example
16 Bell Shape 100 200 -- a 115 Example 17 Bell Shape 100 200 -- a
115 Example 18 Bell Shape 100 200 -- a 115 Example 19 Frustum Shape
100 200 -- a 115 Comparative Circular Truncated 100 200 5 -- --
Example 1 Cone Comparative Circular Truncated 300 600 15 -- --
Example 2 Cone
[0070] The fine films of Examples 1 to 19 and Comparative Examples
1 to 2 manufactured as described above were used for the
evaluations of an abrasion resistance, an antireflection property
and a water repellent property according to the following
evaluation methods.
[0071] [Test Method for Evaluation of Abrasion Resistance]
[0072] The respective films were reciprocated 200 times using a
traverse abrasion testing machine under the following conditions,
followed by visually confirming damages of the films. In Table 3,
the case in which no damage was visually confirmed is indicated by
"circle", the case in which some damages were visually confirmed
but acceptable is indicated by "triangle", and the case in which
apparent damages were confirmed and an white-colored appearance was
observed is indicated by "cross".
[0073] Friction cloth: Canvas cloth (JIS L 3102)
[0074] Load: 9.8 kPa
[0075] Stroke length: 100 mm
[0076] Friction rate: 30 reciprocation/minute
[0077] [Test Method for Evaluation of Antireflection Property]
[0078] The examples having the pitches of the fine protrusions of
380 nm or less were used to measure the visible light reflectance
at 0 degree using a goniophoto meter (manufactured by Otsuka
Electronics Co., Ltd.). In table 3, the case in which an arithmetic
average value of the visible light reflectance is 0.5% or less is
indicated by "circle", the case in which the arithmetic average
value is more than 0.5% to 1% or less is indicated by "triangle",
and the case in which the arithmetic average value is more than 1%
is indicated by "cross". In this test method, since reflection was
caused from the rear surface of the water repellent film of the
respective examples, the rear surface was blacked out so as to
measure the reflectance.
[0079] [Test Method for Evaluation of Water Repellent Property]
[0080] After the test for the evaluation of the abrasion
resistance, the water repellent property was evaluated on a scale
of 1 to 5 based on the following criteria according to the method
specified by JIS L 1092 using a spray tester (manufactured by Toyo
Seiki Seisaku-sho, Ltd.).
[0081] 1: Get entire surface wet
[0082] 2: Get surface wet without maintaining spherical droplet
shape on surface
[0083] 3: Have spherical droplets adhering to surface
[0084] 4: Have fine spherical droplets slightly adhering to
surface
[0085] 5: Have no spherical droplet
[0086] The respective evaluation results are shown in Table 3.
According to the results, it was confirmed that the abrasion
resistance of the fine protrusions was improved by increasing the
modulus of elasticity of the second layer more than the first
layer. In addition, it was also confirmed that the abrasion
resistance was improved by decreasing the modulus of elasticity of
the third layer less than the first layer. Further, according to
the examples, it was confirmed that a particularly excellent water
repellent property was exerted when the contact angle in the fine
protrusions of the surface of the second layer or the contact angle
after surface treatment of the second layer was high.
TABLE-US-00003 TABLE 3 Anti- Water Abrasion reflection Repellent
Resistance Property Property Note Example 1 .largecircle.
.largecircle. 5 Surface Treatment Example 2 .largecircle.
.largecircle. 5 Surface Treatment Example 3 .largecircle. -- 5
Surface Treatment Example 4 .largecircle. .largecircle. 5 Surface
Treatment Example 5 .largecircle. .largecircle. 5 Surface Treatment
Example 6 .largecircle. .largecircle. 5 Surface Treatment Example 7
.largecircle. .largecircle. 5 Surface Treatment Example 8
.largecircle. .largecircle. 5 Surface Treatment Example 9
.largecircle. .largecircle. 5 Surface Treatment Example 10
.largecircle. .largecircle. 5 Surface Treatment Example 11
.largecircle. .largecircle. 5 Surface Treatment Example 12
.largecircle. .largecircle. 5 No Surface Treatment Example 13
.largecircle. -- 5 Surface Treatment Example 14 .largecircle. -- 5
Surface Treatment Example 15 .largecircle. .largecircle. 5 Surface
Treatment Example 16 .largecircle. .largecircle. 5 Surface
Treatment Example 17 .largecircle. .largecircle. 5 Surface
Treatment Example 18 .largecircle. .largecircle. 5 Surface
Treatment Example 19 .largecircle. .largecircle. 5 Surface
Treatment Comparative X -- -- -- Example 1 Comparative X -- 1 --
Example 2
[0087] Although the present invention has been described above by
reference to the embodiment and the examples, the present invention
is not limited to those, and it will be apparent to these skilled
in the art that various modifications and improvements can be
made.
INDUSTRIAL APPLICABILITY
[0088] In the water repellent film according to the present
invention, the relationships among the modulus of elasticity E1 of
the first layer, the modulus of elasticity E2 of the second layer,
and the modulus of elasticity E3 of the third layer are defined as
E2>E1>E3. Therefore, a water repellent film having excellent
resistance to abrasion, in which a fine structure is not easily
abraded and damaged by an external friction force such as a rain
impact and a removal of dirt with a cloth on the surface of the
film, and a component for a vehicle including the film can be
provided.
REFERENCE SIGNS LIST
[0089] A Pitch
[0090] 10 First layer
[0091] 20 Second layer
[0092] 30 Third layer
[0093] 100 Fine protrusions
[0094] 200 Water repellent film
* * * * *