U.S. patent application number 15/069453 was filed with the patent office on 2017-09-14 for cold pressure fix toners comprising crystalline co-polyester-co-poly(alkylsiloxane).
The applicant listed for this patent is XEROX CORPORATION. Invention is credited to KIMBERLY D. NOSELLA, GUERINO G. SACRIPANTE.
Application Number | 20170260337 15/069453 |
Document ID | / |
Family ID | 59581417 |
Filed Date | 2017-09-14 |
United States Patent
Application |
20170260337 |
Kind Code |
A1 |
SACRIPANTE; GUERINO G. ; et
al. |
September 14, 2017 |
COLD PRESSURE FIX TONERS COMPRISING CRYSTALLINE
CO-POLYESTER-CO-POLY(ALKYLSILOXANE)
Abstract
A block copolymer includes a crystalline polyester block and an
amorphous polyalkylsiloxane block, the block copolymer exhibiting
baroplastic behavior. The block copolymer is used in a cold
pressure fix toner. A method of making a block copolymer including
a crystalline polyester block and an amorphous polyalkylsiloxane
block includes heating a mixture of a diacid, a diol, and a
carbinol-terminated poly(alkylsiloxane).
Inventors: |
SACRIPANTE; GUERINO G.;
(OAKVILLE, CA) ; NOSELLA; KIMBERLY D.;
(MISSISSAUGA, CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
XEROX CORPORATION |
NORWALK |
CT |
US |
|
|
Family ID: |
59581417 |
Appl. No.: |
15/069453 |
Filed: |
March 14, 2016 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
G03G 9/08782 20130101;
G03G 9/087 20130101; G03G 9/08773 20130101; G03G 9/08795 20130101;
C08G 77/445 20130101; G03G 9/08797 20130101; C08L 83/10 20130101;
G03G 9/08755 20130101; G03G 9/093 20130101; G03G 9/09328 20130101;
G03G 9/08788 20130101 |
International
Class: |
C08G 77/445 20060101
C08G077/445; G03G 9/093 20060101 G03G009/093 |
Claims
1. (canceled)
2. A block copolymer comprising: a crystalline polyester block; and
an amorphous poly(alkylsiloxane) block, wherein the block copolymer
exhibits baroplastic behavior and the block copolymer has a
structure of Formula (I): ##STR00006## wherein R.sup.1 and R.sup.2
are independently a C.sub.1 to C.sub.4 alkyl group; a is an integer
from 1 to 1000; b is an integer from 1 to 100; m is an integer from
1 to 12; n is an integer from 0 to 10; and p is an integer from 5
to 1000.
3. The block copolymer of claim 2, wherein R.sup.1 and R.sup.2 are
methyl.
4. The block copolymer of claim 2, wherein n is 4.
5. The block copolymer of claim 2, wherein m is 8.
6. The block copolymer of claim 2, wherein the block copolymer has
a number average molecular weight (M.sub.n) from about 2,000
Daltons to about 50,000 Daltons.
7. The block copolymer of claim 2, wherein the block copolymer has
an average molecular weight (M.sub.w) from about 5,000 Daltons to
about 100,000 Daltons.
8. The block copolymer of claim 2, wherein the baroplastic behavior
results in a temperature shift in a range from about 5.degree. C.
to about 40.degree. C. when viscosity is measured at 10 kg/cm.sup.2
versus 100 kg/cm.sup.2.
9. (canceled)
10. A cold pressure fix (CPF) toner comprising: a colorant; an
optionally a wax; and a block copolymer, wherein the block
copolymer comprising a crystalline polyester block, an amorphous
poly(alkylsiloxane) block; further wherein the block copolymer has
a structure of Formula (I): ##STR00007## wherein R.sup.1 and
R.sup.2 are independently a C.sub.1 to C.sub.4 alkyl group; a is an
integer from 1 to 1000; b is an integer from 1 to 100; m is an
integer from 1 to 12; n is an integer from 0 to 10; and p is an
integer from 5 to 1000.
11. The CPF toner of claim 10, wherein R.sup.1 and R.sup.2 are
methyl.
12. The CPF toner of claim 10, wherein n is 4.
13. The CPF toner of claim 10, wherein m is 8.
14. The CPF toner of claim 10, wherein block copolymer has a
molecular weight from about 1,000 Daltons to about 100,00
Daltons.
15. The CPF toner of claim 10, wherein the block copolymer has a
molecular weight from about 4,000 Daltons to about 30,000
Daltons.
16. The CPF toner of claim 10, further comprising one or more agent
selected from the group consisting of an antioxidant, a defoamer, a
slip agent, a leveling agent, a clarifier, a viscosity modifier, an
adhesive, a plasticizer, and combinations thereof.
17. The CPF toner of claim 10, wherein a wax is selected as a
polyethylene or polypropylene.
18. The CPF toner of claim 10, further comprising a shell, wherein
the shell comprises an amorphous polyester resin selected as a
terpoly-(propoxylated bisphenol A terephthalate)
terpoly-(propoxylated bisphenol A-dodecenylsuccinate)
terpoly-(propoxylated bisphenol A-fumarate), a
terpoly-(propoxylated bisphenol A-terephthalate)
terpoly-(propoxylated bisphenol
A-dodecenylsuccinate)-terpoly-(ethoxylated bisphenol A
terephthalate) terpoly-(ethoxylated bisphenol
A-dodecenylsuccinate)-terpoly-(propoxylated bisphenol
A-trimellitate)-terpoly-(ethoxylated bisphenol A-trimellitate),
poly(ethoxylated bisphenol co-fumarate), poly(butyloxylated
bisphenol co-fumarate), poly(co-propoxylated bisphenol
co-ethoxylated bisphenol co-fumarate), and poly(1,2-propylene
fumarate).
19. (canceled)
20. A method of making a block copolymer comprising a crystalline
polyester block and an amorphous poly(alkylsiloxane) block, the
method comprising contacting a carbinol-terminated
poly(alkylsiloxane) with a diacid and a diol, further wherein the
block copolymer has a structure of Formula (I): ##STR00008##
wherein R.sup.1 and R.sup.2 are independently a C.sub.1 to C.sub.4
alkyl group; a is an integer from 1 to 1000; b is an integer from 1
to 100; m is an integer from 1 to 12; n is an integer from 0 to 10;
and p is an integer from 5 to 1000.
Description
BACKGROUND
[0001] The present disclosure relates to toner compositions for use
in xerography. In particular, the present disclosure relates to
cold pressure fix toner compositions.
[0002] Cold pressure fix (CPF) toners normally operate in a system
employing a pair of high-pressure rollers to fix toner to paper
without heating. Among the advantages of such systems are the use
of low power and little paper heating. One example of a cold
pressure fix toner comprises predominantly wax an ethylene-vinyl
acetate copolymer with softening point of 99.degree. C., and a
120.degree. C. softening point polyamide thermoplastic polymer. An
example of this approach is shown in U.S. Pat. No. 4,935,324, which
is incorporated herein by reference. Another example of a cold
pressure fix toner is comprised of a copolymer of styrene with
1-tertiary-butyl-2-ethenyl benzene and a polyolefin wax exemplified
for example as Xerox 4060 cold pressure fix toner. Other cold fix
toners have been based on a long chain acrylate core produced by
suspension polymerization, such as lauryl acrylate. Examples of
such compositions are disclosed in U.S. Pat. Nos. 5,013,630 and
5,023,159 which are incorporated herein by reference. Such systems
are designed to have a core with a T.sub.g less than room
temperature. A hard shell, such as polyurethane prepared by an
interfacial polymerization, is disposed about the core in order to
keep the liquid content in the core in the toner particle.
[0003] Performance issues in designs with high wax content include
that they work only at high pressure, such as about 2,000 psi or
even 4,000 psi, which are respectively, 140 kgf/cm.sup.2 and 280
kgf/cm.sup.2 and even then image robustness can be poor. In the
case of long chain acrylate core designs the shell needs to be very
thin to break under pressure, but it can be very challenging to
prevent the capsules from leaking because the core is typically a
liquid at room temperature.
[0004] Other material approaches for CPF toner applications employ
baroplastics that are nano-phase polymeric materials comprised of
two components that can become miscible under pressure thereby
facilitating flow. Block copolymers have been employed in which the
baroplastic resin comprises of a low T.sub.g and a high T.sub.g
component that nano-phase separate (U.S. Pat. No. 8,273,516). The
CPF toners made by this strategy have provided moderate cold
pressure fix performance. Nonetheless, there still exists a need
for materials for cold pressure fix applications.
SUMMARY
[0005] In some aspects, embodiments herein relate to block
copolymers comprising a crystalline polyester block; and an
amorphous poly(alkylsiloxane) block, wherein the block copolymer
exhibits baroplastic behavior.
[0006] In some aspects, embodiments herein relate to cold pressure
fix (CPF) toners comprising a block copolymer, the block copolymer
comprising a crystalline polyester block and an amorphous
poly(alkylsiloxane) block, a colorant, and optionally a wax.
[0007] In some aspects, embodiments herein relate to methods of
making a block copolymers comprising a crystalline polyester block
and an amorphous poly(alkylsiloxane) block, the method comprising
heating a mixture of a diacid, a diol, and a carbinol-terminated
poly(alkylsiloxane).
BRIEF DESCRIPTION OF DRAWINGS
[0008] Various embodiments of the present disclosure will be
described herein below with reference to the figures wherein:
[0009] FIG. 1 shows a plot of viscosity versus temperature for
Comparative Example 1, a polyester control lacking a
poly(alkylsiloxane) block, obtained using a CFT-500D
Flowtester.TM..
[0010] FIG. 2 shows a plot of viscosity versus temperature for
Example 4, an exemplary co-polyester co-poly(alkylsiloxane) block
copolymer, obtained using a CFT-500D Flowtester.TM..
[0011] FIG. 3 shows a plot of viscosity versus temperature for
Example 7, a further exemplary co-polyester co-poly(alkylsiloxane)
block copolymer, obtained using a CFT-500D Flowtester.TM..
[0012] FIG. 4 shows a plot of viscosity versus temperature for
Example 10, a still further exemplary co-polyester
co-poly(alkylsiloxane) block copolymer, obtained using a CFT-500D
Flowtester.TM..
DETAILED DESCRIPTION
[0013] Embodiments herein provide cold pressure fix toners based on
crystalline co-polyester-co-poly(alkylsiloxane) resins. The toners
optionally have an amorphous small molecule ester or polymer resin
as a shell component, to provide a material that undergoes a phase
change from solid to liquid under pressure.
[0014] As used herein, "cold pressure fix toner" or "CPF toner"
refers to a toner material designed for application to a substrate
and which is affixed to the substrate primarily by application of
pressure. While heating may be optionally employed to assist in
fixing a CPF toner, one benefit of the compositions disclosed
herein is the ability to use reduced heating, or in embodiments, no
applied heating. Affixing by application of pressure may be
achieved utilizing a Shimadzu Flowtester.TM. in a broad range of
pressures, such as from about 50 kgf/cm.sup.2 to about 100
kgf/cm.sup.2 or to about 200 kgf/cm.sup.2. If necessary it is
possible to use higher pressures up to about 400 kgf/cm.sup.2,
however, generally such higher pressures are undesirable, causing
calendaring and even wrinkling of the paper which distorts the look
and feel of the paper, and requires more robust pressure fix rolls
and spring assemblies.
[0015] As used herein, the term "baroplastic," used in connection
with block copolymers disclosed herein, refers to the copolymer
property of undergoing a phase change from solid to liquid under
pressure. Baroplastic materials typically comprise a low T.sub.g
and a high T.sub.g component that nano-phase separate. Embodiments
herein achieve this by providing copolymers comprising a
crystalline hydrocarbon resin block with high T.sub.m, such as from
about 55.degree. C. to about 100.degree. C., and in other
embodiments, from about 60.degree. C. to 80.degree. C., and a block
of a low T.sub.g of amorphous poly(alkylsiloxane), such as from
about -30 t to about 50.degree. C., and in other embodiments, from
about -20.degree. C. to 25.degree. C. Inexpensive carbinol
terminated polydimethylsiloxanes, in particular, are commercially
available with various molecular weights. Reacting these with
crystalline resin components such as diacid and diols can generate
block copolymers of amorphous co-polydimethylsiloxane resin with
crystalline co-polyester according to Scheme I below:
##STR00001##
wherein R.sup.1 and R.sup.2 are independently a C.sub.1 to C.sub.4
alkyl group; a is an integer from 1 to 1000; b is an integer from 1
to 100; m is an integer from 2 to 12; n is an integer from 2 to 12;
and p is an integer from 5 to 10,000. The resultant crystalline
co-polyester and amorphous co-poly(alkylsiloxane) block resin can
provide the requisite nano-phase separation of the block
co-poly(alkylsiloxane) from the crystalline co-polyesters.
[0016] In embodiments, there are provided block copolymers
comprising a crystalline polyester block; and an amorphous
poly(alkylsiloxane) block. In embodiments, the block copolymers
have a structure of Formula (I):
##STR00002##
wherein R.sup.1 and R.sup.2 are independently a C.sub.1 to C.sub.4
alkyl group; a is an integer from 1 to 1000; b is an integer from 1
to 100; m is an integer from 2 to 12; n is an integer from 0 to 12;
and p is an integer from 5 to 1000. In embodiments, R.sup.1 and
R.sup.2 are methyl. In preferred embodiments, n is 4 to 10. In
embodiments m is 6 to 10.
[0017] In embodiments, block copolymer has a number average
molecular weight (M.sub.n) from about 2,000 Daltons to about 50,000
Daltons, or in other embodiments, about 4,000 Daltons to about
10,000 Daltons. In embodiments, the block copolymer has an average
molecular weight (M.sub.w) from about 5,000 Daltons to about
100,000 Daltons, or in other embodiments, about 10,000 Daltons to
about 50,000 Daltons.
[0018] In embodiments, there provided cold pressure fix (CPF)
toners comprising a block copolymer, the block copolymer comprising
a crystalline polyester block, and an amorphous poly(alkylsiloxane)
block.
[0019] In embodiments, the CPF toners comprise a block copolymer
having a structure of Formula (I):
##STR00003##
wherein R.sup.1 and R.sup.2 are independently a C.sub.1 to C.sub.4
alkyl group; a is an integer from 1 to 1000; b is an integer from 1
to 100; m is an integer from 2 to 12; n is an integer from 0 to 10;
and p is an integer from 5 to 1000. In some such embodiments,
R.sup.1 and R.sup.2 are methyl. In some such embodiments, n is 4 to
12. In some such embodiments, m is 6 to 10.
[0020] In embodiments, CPF toners may further comprise a colorant.
In embodiments, CPF toners may further comprise one or more agent
selected from the group consisting of an antioxidant, a defoamer, a
slip agent, a leveling agent, a clarifier, a viscosity modifier, an
adhesive, a plasticizer, and combinations thereof.
[0021] Numerous suitable waxes may be selected for the toners
illustrated herein, and which waxes can be included in the CPF
toner.
[0022] Examples of optional waxes included polyolefins, such as
polypropylenes, polyethylenes, and the like, such as those
commercially available from Allied Chemical and Baker Petrolite
Corporation; wax emulsions available from Michaelman Inc. and the
Daniels Products Company; EPOLENE N-15.TM. commercially available
from Eastman Chemical Products, Inc.; VISCOL 550-P.TM. a low weight
average molecular weight polypropylene available from Sanyo Kasei
K.K.; OMNOVA D1509.RTM., available from IGI Chemicals as a wax
dispersion and similar materials. Examples of functionalized waxes
that can be selected for the disclosed toners include amines, and
amides of, for example, AQUA SUPERSLIP 6550.TM., SUPERSLIP 6530.TM.
available from Micro Powder Inc.; fluorinated waxes, for example,
POLYFLUO 190.TM., POLYFLUO 200.TM., POLYFLUO 523XF.TM., AQUA
POLYFLUO 411.TM., AQUA POLYSILK 19.TM., POLYSILK 14.TM. available
from Micro Powder Inc.; mixed fluorinated, amide waxes, for
example, MICROSPERSION 19.TM. also available from Micro Powder
Inc.; imides, esters, quaternary amines, carboxylic acids or
acrylic polymer emulsion of, for example, JONCRYL 74.TM., 89.TM.,
130.TM., 537.TM., and 538.TM., all available from SC Johnson Wax;
chlorinated polypropylenes and polyethylenes available from Allied
Chemical, Petrolite Corporation, and from SC Johnson Wax. A number
of these disclosed waxes can optionally be fractionated or
distilled to provide specific cuts or portions that meet viscosity
and/or temperature criteria wherein the viscosity is, for example,
about 10,000 cps, and the temperature is about 100.degree. C. In
embodiments, the wax is selected from the group consisting of
polyethylene, polypropylene, and mixtures thereof. In embodiments,
the wax has a melting range of from about 70 to about 120.degree.
C., or from about 80 to about 100.degree. C., or from about 85 to
about 95.degree. C.
[0023] In embodiments, the wax is in the form of a dispersion
comprising, for example, a wax having a particle diameter of from
about 100 nanometers to about 500 nanometers, or from about 100
nanometers to about 300 nanometers, water, and an anionic
surfactant or a polymeric stabilizer, and optionally a nonionic
surfactant. In embodiments, the wax comprises polyethylene wax
particles, such as POLYWAX.RTM. 655, or POLYWAX.RTM. 725,
POLYWAX.RTM. 850, POLYWAX.RTM. 500 (the POLYWAX.RTM. waxes being
commercially available from Baker Petrolite) and, for example,
fractionated/distilled waxes, which are distilled parts of
commercial POLYWAX.RTM. 655 designated as X1214, X1240, X1242,
X1244, and the like, but are not limited to POLYWAX.RTM. 655 cuts.
Waxes providing a specific cut that meet the viscosity/temperature
criteria, wherein the upper limit of viscosity is about 10,000 cps
and the temperature upper limit is about 100.degree. C., can be
used. These waxes can have a particle diameter in the range of from
about 100 to about 500 nanometers, although not limited to these
diameters or sizes. Other wax examples include FT-100 waxes
available from Shell (SMDA), and FNP0092 available from Nippon
Seiro.
[0024] The surfactant used to disperse the wax can be an anionic
surfactant, such as, for example, NEOGEN RK.RTM. commercially
available from Daiichi Kogyo Seiyaku or TAYCAPOWER.RTM. BN2060
commercially available from Tayca Corporation, or DOWFAX.RTM.
available from DuPont.
[0025] In embodiments, wax can be present in the toner in any
suitable or desired amount. In the present embodiments, the wax may
be present in the toner in a lower amount than previously required,
such as from 2 to about 15, or from about 2 to about 13, or from
about 4 to about 10, or from about 4 to about 6 percent by weight
based on the total weight of the toner solids. In a specific
embodiment, the wax is present in the toner in an amount of from
about 4 to about 6 percent by weight, based on the total weight of
toner solids. The toner wax amount can in embodiments be, for
example, from about 0.1 to about 20 weight percent or percent by
weight, from about 0.5 to about 15 weight percent, from about 1 to
about 12 weight percent, from about 1 to about 10 weight percent,
from about 2 to about 8 weight percent, from about 4 to about 9
weight percent, from about 1 to about 5 weight percent, from about
1 to about 4 weight percent, or from about 1 to about 3 weight
percent based on the toner solids. In embodiments, the wax is
present in an amount of from about 2 to about 13 percent by weight,
based on the total weight of the toner. In a specific embodiment,
the wax is present in an amount of from about 4 to about 5 weight
percent based on the total weight of the toner.
[0026] In embodiments, the CPF toners may further comprise a shell.
In embodiments, the shell comprises an amorphous small molecule
ester or a polymer resin. Examples of amorphous polyesters,
selected as a replacement for the prior art resin mixtures of a
first resin of, for example, a terpoly-(propoxylated bisphenol A
terephthalate) terpoly-(propoxylated bisphenol
A-dodecenylsuccinate) terpoly-(propoxylated bisphenol A-fumarate)
(Comparative Example A), a terpoly-(propoxylated bisphenol
A-terephthalate) terpoly-(propoxylated bisphenol
A-dodecenylsuccinate)-terpoly-(ethoxylated bisphenol A
terephthalate) terpoly-(ethoxylated bisphenol
A-dodecenylsuccinate)-terpoly-(propoxylated bisphenol
A-trimellitate)-terpoly-(ethoxylated bisphenol A-trimellitate),
poly(ethoxylated bisphenol co-fumarate), poly(butyloxylated
bisphenol co-fumarate), poly(co-propoxylated bisphenol
co-ethoxylated bisphenol co-fumarate), poly(1,2-propylene
fumarate), poly(propoxylated bisphenol co-maleate),
poly(ethoxylated bisphenol co-maleate), poly(butyloxylated
bisphenol co-maleate), poly(co-propoxylated bisphenol
co-ethoxylated bisphenol co-maleate), poly(1,2-propylene maleate),
poly(propoxylated bisphenol co-itaconate), poly(ethoxylated
bisphenol co-itaconate), poly(butyloxylated bisphenol
co-itaconate), poly(co-propoxylated bisphenol co-ethoxylated
bisphenol co-itaconate), and terpoly(propoxylated bisphenol
A-terephthalate)-terpoly(propoxylated bisphenol
A-dodecenylsuccinate)-terpoly(propoxylated bisphenol A-fumarate),
mixtures thereof, and the like.
[0027] The amorphous polyester resins can possess, for example, a
number average molecular weight (Mn), as measured by gel permeation
chromatography (GPC) of, for example, from about 5,000 to about
100,000, from about 10,000 to about 75,000, or from about 5,000 to
about 50,000. The weight average molecular weight (Mw) of the
amorphous polyester resins can be, for example, from about 2,000 to
about 100,000, from about 15,000 to about 85,000, or from about
5,000 to about 80,000, as determined by GPC using polystyrene
standards. The broad molecular weight distribution (Mw/Mn) or
polydispersity of the amorphous polyester resin is, for example,
from about 2 to about 8, from about 2 to about 6, and from about 3
to about 5.
[0028] In embodiments, there are provided methods of making a block
copolymer comprising a crystalline polyester block and an amorphous
polyalkylsiloxane block, the method comprising heating a mixture of
a diacid, a diol, and a carbinol-terminated poly(alkylsiloxane). In
particular embodiments, methods may be used to make the block
copolymer having a structure of Formula (I):
##STR00004##
wherein R.sup.1 and R.sup.2 are independently a C.sub.1 to C.sub.4
alkyl group; a is an integer from 1 to 1000; b is an integer from 1
to 100; m is an integer from 1 to 12; n is an integer from 0 to 10;
and p is an integer from 5 to 1000.
[0029] In embodiments, if a heating step is performed along with
pressure application to fix the toner a temperature may be in a
range from about 25.degree. C. to about 130.degree. C., at a
heating rate of from about 1.degree. C. to about 20.degree. C. per
minute.
[0030] In embodiments, the crystalline component of the copolymer
is a polyester. Crystalline polyester can be prepared from a diacid
and a diol. Examples of organic diols selected for the preparation
of crystalline polyester resins include aliphatic diols with from
about 2 to about 36 carbon atoms, such as 1,2-ethanediol,
1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol,
1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, 1,10-decanediol,
1,12-dodecanediol, and the like. The aliphatic diol is, for
example, selected in an amount of from about 45 to about 55 mole
percent of the resin.
[0031] Examples of organic diacids or diesters selected for the
preparation of the crystalline polyester resins include oxalic
acid, succinic acid, glutaric acid, adipic acid, suberic acid,
azelaic acid, sebacic acid, dodecanedioic acid, phthalic acid,
isophthalic acid, terephthalic acid, napthalene-2,6-dicarboxylic
acid, naphthalene-2,7-dicarboxylic acid, cyclohexane dicarboxylic
acid, malonic acid and mesaconic acid, a diester or anhydride
thereof. The organic diacid may be selected in an amount of, for
example, from about 45 to about 55 mole percent of the resin.
[0032] For cold pressure fixable toner it may be desirable to have
the toner material flow near room temperature under the applied
pressure of the cold pressure fixing system, to enable the toner to
flow over the substrate surface and into pores or fibers in the
substrate, as well as to enable the toner particles to flow into
each other, thus providing a smooth continuous toner layer that is
effectively adhered to the substrate. The flow can be measured
utilizing the CFT-500D Flowtester.TM., available from Shimadzu
Corporation. It may be desirable that the pressure applied be
relatively low compared to the prior art, such as about 100
kgf/cm.sup.2. However, in embodiments the pressure can be higher,
up to about 400 kgf/cm.sup.2, or lower, as little as 5
kgf/cm.sup.2, provided that the above described conditions for
onset of toner flow and flow viscosity can be met. In embodiments,
some heat may be applied to preheat the toner or the paper prior to
entry to the cold pressure fixing system, which can enable cold
pressure fix for temperatures somewhat above room temperature.
[0033] In embodiments, it may be desirable for cold pressure fix
that under low pressures, such as about 10 kgf/cm.sup.2 applied
pressure the cold pressure fix toner does not flow significantly
such that the toner particles stick together, for example in the
toner cartridge, or in the printer, including in the developer
housing, or on the imaging surfaces such as the photoreceptor, or
in embodiments the intermediate transfer belt. In shipping or in
the printer the temperature may rise to as much as 50.degree. C.,
thus in embodiments it may be desirable that the toner does not
flow significantly to allow the particles stick together up to
50.degree. C. at about 10 kgf/cm.sup.2. Thus, in embodiments the
temperature for the viscosity of the material to be reduced to a
value of about 10,000 Pa-s, for the cold pressure fix toner at a
lower pressure of about 10 kgf/cm.sup.2 applied pressure, is from
about 50.degree. C. to about 70.degree. C., in embodiments about
55.degree. C. to about 70.degree. C., in embodiments about
60.degree. C. to about 90.degree. C., or in further embodiments at
about 20 kgf/cm.sup.2 to about 40 kgf/cm.sup.2.
[0034] Thus it may be desirable to have a high temperature for
material flow at low pressures representative of storage and usage
in the printer, and a low temperature for material at the desired
higher cold pressure fix pressure. In embodiments there is a
temperature shift calculated in the range from about 10.degree. C.
to about 60.degree. C. where the flow viscosity of the cold
pressure fix composition equal to about 10,000 pascal-seconds, when
the applied pressure on the cold pressure fix composition is
increased from 10 to 100 Kgf/cm.sup.2. In such embodiments, the
temperature shift can be calculated as:
.DELTA.T.sub..eta.=10000=T.sub..eta.=10000(10
kgf/cm2)-T.sub..eta.=10000(100 kgf/cm2)
where T.sub..eta.=10000(10 kgf/cm.sup.2) is the temperature for
flow viscosity .eta. of 10000 Pa-s at 10 kgf/cm.sup.2 applied
pressure and T.sub..eta.=10000(100 kgf/cm.sup.2) is the temperature
for flow viscosity .eta. of 10000 Pa-s at 100 kgf/cm.sup.2. In
other embodiments the low pressure for storage and printer usage
applied can be in the range of about 10 kgf/cm.sup.2 to about 40
kgf/cm.sup.2, and the high pressure for applied for cold pressure
fix can be in the range of about 25 kgf/cm.sup.2 to about 400
kgf/cm.sup.2.
[0035] Toners can be prepared from the block copolymers disclosed
herein by any means, including conventional extrusion and grinding,
suspension, SPSS (Spherical Polyester Toner by Suspension of
Polymer/Pigment Solution and Solvent Removal Method., as described
in Journal of the Imaging Society of Japan, Vol. 43, 1, 48-53,
2004), incorporated in an N-Cap toner, (encapsulated toner, as
described for example in U.S. Pat. No. 5,283,153 and incorporated
in an emulsion aggregation toner, optionally with a shell. Where
needed for toner applications, latexes can be made incorporating
the crystalline and/or amorphous mixtures, prepared by solvent
flash, by phase inversion emulsification, including by solvent free
methods.
[0036] Other additives may be present in the CPF toners disclosed
here. The CPF toner compositions of the present embodiments may
further optionally include one or more conventional additives to
take advantage of the known functionality associated with such
conventional additives. Such additives may include, for example,
colorants, antioxidants, defoamer, slip and leveling agents,
clarifier, viscosity modifier, adhesive, plasticizer and the like.
When present, the optional additives may each, or in combination,
be present in the CPF toner in any desired or effective amount,
such as from about 1% to about 10%, from about 5% to about 10%, or
from about 3% to about 5% by weight of the CPF toner.
[0037] In a typical CPF toner composition antioxidants are added
for preventing discoloration of the small molecule composition. In
embodiments, the antioxidant material can include IRGANOX.RTM.
1010; and NAUGARD.RTM. 76, NAUGARD.RTM. 445, NAUGARD.RTM. 512, and
NAUGARD.RTM. 524. In embodiments, the antioxidant is NAUGARD.RTM.
445. In other embodiments the antioxidant material can include
MAYZO.RTM. BNX.RTM. 1425 a calcium salt of phosphonic acid, and
MAYZO.RTM. BNX.RTM. 358 a thiophenol both available commercially
from MAYZO.RTM., and ETHANOX.RTM. 323A a nonylphenol disulfide
available commercially from SI Group.
[0038] In embodiments, CPF toners disclosed herein may further
comprise a plasticizer. Exemplary plasticizers may include Uniplex
250 (commercially available from Unitex), the phthalate ester
plasticizers commercially available from Ferro under the trade name
SANTICIZER.RTM., such as dioctyl phthalate, diundecyl phthalate,
alkylbenzyl phthalate (SANTICIZER.RTM. 278), triphenyl phosphate
(commercially available from Ferro), KP-140, a tributoxyethyl
phosphate (commercially available from Great Lakes Chemical
Corporation), MORFLEX.RTM. 150, a dicyclohexyl phthalate
(commercially available from Morflex Chemical Company Inc.),
trioctyl trimellitate (commercially available from Sigma Aldrich
Co.), and the like. Plasticizers may be present in an amount from
about 0.01 to about 30 percent, from about 0.1 to about 25 percent,
from about 1 to about 20 percent by weight of the CPF toner.
[0039] In embodiments, the cold pressure fix toner compositions
described herein also include a colorant. Any desired or effective
colorant can be employed in the cold pressure fix toner
compositions, including dyes, pigments, mixtures thereof. Any dye
or pigment may be chosen, provided that it is capable of being
dispersed or dissolved in the CPF toner and is compatible with the
other CPF toner components. Any conventional cold pressure fix
toner colorant materials, such as Color Index (C.I.) Solvent Dyes,
Disperse Dyes, modified Acid and Direct Dyes, Basic Dyes, Sulphur
Dyes, Vat Dyes, fluorescent dyes and the like. Examples of suitable
dyes include NEOZAPON.RTM. Red 492 (BASF); ORASOL.RTM. Red G (Pylam
Products); Direct Brilliant Pink B (Oriental Giant Dyes); Direct
Red 3BL (Classic Dyestuffs); SUPRANOL.RTM. Brilliant Red 3BW (Bayer
AG); Lemon Yellow 6G (United Chemie); Light Fast Yellow 3G
(Shaanxi); Aizen Spilon Yellow C-GNH (Hodogaya Chemical);
Bemachrome Yellow GD Sub (Classic Dyestuffs); CARTASOL.RTM.
Brilliant Yellow 4GF (Clariant); Cibanone Yellow 2G (Classic
Dyestuffs); ORASOL.RTM. Black RLI (BASF); ORASOL.RTM. Black CN
(Pylam Products); Savinyl Black RLSN (Clariant); Pyrazol Black BG
(Clariant); MORFAST.RTM. Black 101 (Rohm & Haas); Diaazol Black
RN (ICI); THERMOPLAST.RTM. Blue 670 (BASF); ORASOL.RTM. Blue GN
(Pylam Products); Savinyl Blue GLS (Clariant); LUXOL.RTM. Fast Blue
MBSN (Pylam Products); Sevron Blue 5GMF (Classic Dyestuffs);
BASACID.RTM. Blue 750 (BASF); KEYPLAST.RTM. Blue (Keystone Aniline
Corporation); NEOZAPON.RTM. Black X51 (BASF); Classic Solvent Black
7 (Classic Dyestuffs); SUDAN.RTM. Blue 670 (C.I. 61554) (BASF);
SUDAN.RTM. Yellow 146 (C.I. 12700) (BASF); SUDAN.RTM. Red 462 (C.I.
26050) (BASF); C.I. Disperse Yellow 238; Neptune Red Base NB543
(BASF, C.I. Solvent Red 49); Neopen Blue FF-4012 (BASF); Fatsol
Black BR (C.I. Solvent Black 35) (Chemische Fabriek Triade BV);
Morton Morplas Magenta 36 (C.I. Solvent Red 172); metal
phthalocyanine colorants such as those disclosed in U.S. Pat. No.
6,221,137, the disclosure of which is totally incorporated herein
by reference, and the like. Polymeric dyes can also be used, such
as those disclosed in, for example, U.S. Pat. No. 5,621,022 and
U.S. Pat. No. 5,231,135, the disclosures of each of which are
herein entirely incorporated herein by reference, and commercially
available from, for example, Milliken & Company as Milliken Ink
Yellow 869, Milliken Ink Blue 92, Milliken Ink Red 357, Milliken
Ink Yellow 1800, Milliken Ink Black 8915-67, uncut Reactint Orange
X-38, uncut Reactint Blue X-17, Solvent Yellow 162, Acid Red 52,
Solvent Blue 44, and uncut Reactint Violet X-80.
[0040] Pigments are also suitable colorants for the cold pressure
fix toners. Examples of suitable pigments include PALIOGEN.RTM.
Violet 5100 (BASF); PALIOGEN.RTM. Violet 5890 (BASF); HELIOGEN.RTM.
Green L8730 (BASF); LITHOL.RTM. Scarlet D3700 (BASE); SUNFAST.RTM.
Blue 15:4 (Sun Chemical); HOSTAPERM.RTM. Blue B2G-D (Clariant);
HOSTAPERM.RTM. Blue B4G (Clariant); Permanent Red P-F7RK;
HOSTAPERM.RTM. Violet BL (Clariant); LITHOL.RTM. Scarlet 4440
(BASF); Bon Red C (Dominion Color Company); ORACET.RTM. Pink RF
(BASF); PALIOGEN.RTM. Red 3871 K (BASF); SUNFAST.RTM. Blue 15:3
(Sun Chemical); PALIOGEN.RTM. Red 3340 (BASF); SUNFAST.RTM.
Carbazole Violet 23 (Sun Chemical); LITHOL.RTM. Fast Scarlet L4300
(BASF); SUNBRITE.RTM. Yellow 17 (Sun Chemical); HELIOGEN.RTM. Blue
L6900, L7020 (BASF); SUNBRITE.RTM. Yellow 74 (Sun Chemical);
SPECTRA PAC C Orange 16 (Sun Chemical); HELIOGEN.RTM. Blue K6902,
K6910 (BASF); SUNFAST.RTM. Magenta 122 (Sun Chemical);
HELIOGEN.RTM. Blue D6840, D7080 (BASF); SUDAN.RTM. Blue OS (BASF);
NEOPEN Blue FF4012 (BASF); PV Fast Blue B2GO1 (Clariant); IRGALITE
Blue GLO (BASF); PALIOGEN.RTM. Blue 6470 (BASF); SUDAN.RTM. Orange
G (Aldrich); SUDAN.RTM. Orange 220 (BASF); PALIOGEN.RTM. Orange
3040 (BASF); PALIOGEN.RTM. Yellow 152, 1560 (BASF); LITHOL.RTM.
Fast Yellow 0991 K (BASF); PALIOTOL Yellow 1840 (BASF); NOVOPERM
Yellow FGL (Clariant); Ink Jet Yellow 4G VP2532 (Clariant); Toner
Yellow HG (Clariant); Lumogen Yellow D0790 (BASF); Suco-Yellow
L1250 (BASF); Suco-Yellow D1355 (BASF); Suco Fast Yellow D1355,
D1351 (BASF); HOSTAPERM Pink E 02 (Clariant); Hansa Brilliant
Yellow 5GX03 (Clariant); Permanent Yellow GRL 02 (Clariant);
Permanent Rubine L6B 05 (Clariant); FANAL Pink D4830 (BASF);
CINQUASIA.RTM. Magenta (DU PONT); PALIOGEN.RTM. Black L0084 (BASF);
Pigment Black K801 (BASF); and carbon blacks such as REGAL 330.TM.
(Cabot), Nipex 150 (Evonik) Carbon Black 5250 and Carbon Black 5750
(Columbia Chemical), and the like, as well as mixtures thereof.
[0041] Pigment dispersions in the CPF toner may be stabilized by
synergists and dispersants. Generally, suitable pigments may be
organic materials or inorganic. Magnetic material-based pigments
are also suitable, for example, for the fabrication of robust
Magnetic Ink Character Recognition (MICR) inks. Magnetic pigments
include magnetic nanoparticles, such as for example, ferromagnetic
nanoparticles.
[0042] Also suitable are the colorants disclosed in U.S. Pat. No.
6,472,523, U.S. Pat. No. 6,726,755, U.S. Pat. No. 6,476,219, U.S.
Pat. No. 6,576,747, U.S. Pat. No. 6,713,614, U.S. Pat. No.
6,663,703, U.S. Pat. No. 6,755,902, U.S. Pat. No. 6,590,082, U.S.
Pat. No. 6,696,552, U.S. Pat. No. 6,576,748, U.S. Pat. No.
6,646,111, U.S. Pat. No. 6,673,139, U.S. Pat. No. 6,958,406, U.S.
Pat. No. 6,821,327, U.S. Pat. No. 7,053,227, U.S. Pat. No.
7,381,831 and U.S. Pat. No. 7,427,323, the disclosures of each of
which are incorporated herein by reference in their entirety.
[0043] In embodiments, solvent dyes are employed. An example of a
solvent dye suitable for use herein may include spirit soluble dyes
because of their compatibility with the CPF toner carriers
disclosed herein. Examples of suitable spirit solvent dyes include
NEOZAPON.RTM. Red 492 (BASF); ORASOL.RTM. Red G (Pylam Products);
Direct Brilliant Pink B (Global Colors); Aizen Spilon Red C-BH
(Hodogaya Chemical); Kayanol Red 3BL (Nippon Kayaku); Spirit Fast
Yellow 3G; Aizen Spilon Yellow C-GNH (Hodogaya Chemical);
CARTASOL.RTM. Brilliant Yellow 4GF (Clariant); PERGASOL.RTM. Yellow
5RA EX (Classic Dyestuffs); ORASOL.RTM. Black RLI (BASF);
ORASOL.RTM. Blue GN (Pylam Products); Savinyl Black RLS (Clariant);
MORFAST.RTM. Black 101 (Rohm and Haas); THERMOPLAST.RTM. Blue 670
(BASF); Savinyl Blue GLS (Sandoz); LUXOL.RTM. Fast Blue MBSN
(Pylam); Sevron Blue 5GMF (Classic Dyestuffs); BASACID.RTM. Blue
750 (BASF); KEYPLAST.RTM. Blue (Keystone Aniline Corporation);
NEOZAPON.RTM. Black X51 (C.I. Solvent Black, C.I. 12195) (BASF);
SUDAN.RTM. Blue 670 (C.I. 61554) (BASF); SUDAN.RTM. Yellow 146
(C.I. 12700) (BASF); SUDAN.RTM. Red 462 (C.I. 260501) (BASF),
mixtures thereof and the like.
[0044] The colorant may be present in the cold pressure fix toner
in any desired or effective amount to obtain the desired color or
hue such as, for example, at least from about 0.1 percent by weight
of the CPF toner to about 50 percent by weight of the CPF toner, at
least from about 0.2 percent by weight of the CPF toner to about 20
percent by weight of the CPF toner, and at least from about 0.5
percent by weight of the CPF toner to about 10 percent by weight of
the CPF toner. The colorant may be included in the CPF toner in an
amount of from, for example, about 0.1 to about 15% by weight of
the CPF toner, or from about 0.5 to about 6% by weight of the CPF
toner.
EXAMPLES
[0045] The following Examples are being submitted to illustrate
embodiments of the present disclosure. These Examples are intended
to be illustrative only and are not intended to limit the scope of
the present disclosure. Also, parts and percentages are by weight
unless otherwise indicated. As used herein, "room temperature"
refers to a temperature of from about 20.degree. C. to about
25.degree. C.
Comparative Example 1
[0046] This Example describes the synthesis of a crystalline
polyester derived from dodecanedioic acid and nonane-diol glycol
(m=10, n=7) without any polydimethylsiloxane.
[0047] A 2-L buchi reactor was charged with 632 g of dodecanedioic
acid, 540 g of nonanediol and 3 grams of FASCAT 4100 available from
Elf Atochem. The mixture was slowly heated to 225.degree. C., over
a three hour period and then maintained at 225.degree. C. for seven
additional hours. The resin was then discharged through and left to
cool to room temperature.
Example 2
[0048] This Example describes the synthesis of a crystalline
co-polyester-co-poly(dimethylsiloxane) (95% by weight of
co-polyester-derived from dodecanedioic acid and ethylene glycol
(m=10, n=0) with 5% by weight of co-polydimethylsiloxane.
[0049] A 2-L buchi reactor was charged with 624 g of dodecanedioic
acid, 337 g of ethylene glycol and 50 grams of carbinol terminated
polydimethylsiloxane available from Gelest, Inc. with a viscosity
of about 50 to about 60 poise, and 3 grams of FASCAT 4100 available
from Elf Atochem. The mixture was slowly heated to 225.degree. C.,
over a three hour period, and then maintained at 225.degree. C. for
additional five hours. The co-polyester-co-polydimethylsiloxane was
comprised of about 95% crystalline co-polyester and about 5%
co-polydimethylsiloxane (PDMS):
##STR00005##
wherein m=10 and n=0, R.sup.1 and R.sup.2 are methyl.
Example 3 to 10
[0050] A series of co-Polyester-co-polydimethylsiloxane were
prepared with varying co-polyester and co-polydimethylsiloxane
ratio by the procedure of Example 1. The thermal and analytical
results are listed in Table 1. The acid value was obtained using
tetrahydrofuran as the solvent and potassium methoxide as the
titrant and using phenolphthalein as the indicator. The viscosity
was obtained using the CAP 2000+Viscometer available from
Brookfield at 100.degree. C. The melting point, re-crystallization
temperature and heat of fusion were obtained by Differential
Scanning calorimetry at a heating and cooling rate of 10 t/minute.
The molecular weight average (M.sub.w) and weight number (M.sub.e)
was obtained by Gel Permeation chromatography using polystyrene
standards.
TABLE-US-00001 TABLE 1 Resin Properties Molecular Acid Melting
Crystallization Heat of Weight A B Value Viscosity Point
Temperature Fusion g/mole Resin % n:m % mg/KOH g Poise .degree. C.
.degree. C. joules/g Mn Mw Comparative 0 10:7 100 10.5 47 76 60 140
10,400 22,100 Example 1 Example 2 5 10:0 95 3.8 7.1 83.5 62.9 72.1
5,066 12,091 Example 3 10 10:0 90 2.41 7.7 82.9 60.7 98.9 5,554
12,556 Example 4 15 10:0 85 3.14 11.3 81.3 59.1 83.5 7,232 16,421
Example 5 5 10:7 95 19.3 10.7 71.9 58.8 131.6 8.085 15,202 Example
6 10 10:7 90 12.4 29.2 70.3 57.3 125.3 10,063 21,210 Example 7 15
10:7 85 10.4 18.1 68.9 55.7 117.7 8,220 18,623 Example 8 5 8:4 95
9.7 19.8 64.8 49.6 113.5 7,159 16,305 Example 9 10 8:4 90 14.7 19.4
63.9 51.2 111.9 6,895 16,117 Example 10 15 8:4 85 13.4 16.4 62.6
46.6 98.01 6,570 15,812 A = Co-Polydimethylsiloxane; B =
Co-Polyester (n:m are integers from Formula (I))
[0051] From the above resins, Comparative Example 1, and Examples
4, 7 and 10, were evaluated utilizing the CFT-500D Flowtester.TM.
at both 10 and 100 Kg/cm.sup.2 pressure at a temperature range from
20.degree. C. to 100.degree. C. The results are shown in FIGS. 1 to
4. FIG. 1, which characterizes the crystalline resin of comparative
example 1, shows no baroplastic effect as the temperature
difference between 10 and 100 Kg/cm.sup.2 pressure does not show
any difference in viscosity versus temperature behavior. This is
expected, as the resin of Comparative Example 1, does not comprise
co-blocks of polyester with polydimethylsiloxane. The copolymers of
Examples 4, 7 and 10 comprised of selected
co-polyester-co-polydimethylsiloxane are illustrated in FIGS. 2, 3
and 4, respectively. In each of these latter resins, a difference
of 10.degree. C. to about 20.degree. C. drop in viscosity versus
temperature can be seen when these resins are subjected from 10 to
100 Kg/cm.sup.2 pressure, demonstrating that they are all
baroplastic materials.
Example 11
[0052] This Example describes the synthesis of a CPF toner from the
block copolymer of Example 5 (94% by weight) and Cyan Pigment (6%
by weight).
[0053] A latex was first generated by a Phase Inversion Process: In
a 1 Liter Buchi reactor, equipped with a mechanical anchor blade,
and distillation apparatus, was added 200 grams of the block
copolymer of Example 5, 120 grams of methyl ethyl ketone, and 6 g
of isopropanol. The mixture was heated to 65.degree. C. and after
dissolution of the resin, 12 grams of 10% ammonium hydroxide was
added. To this mixture was then added 300 grams of water dropwise
at a rate of 1 gram per minute. A latex resulted, and the organic
solvent (methyl ethyl ketone and isopropanol) was distilled off.
The latex was then screened through a 20 micron sieve. The particle
size was measured to be 141.4 nm with a solids content of 42% by
weight.
[0054] In a 1 L glass kettle, equipped with a mechanical anchor
blade, was charged with 223 grams of the above latex, 18.1 grams of
cyan pigment dispersion (33% by weight) available from Sun
Chemicals, 3 grams of sodium dodecyl benzene sulfonate surfactant,
and 76 grams of water. The resulting mixture was adjusted to a pH
of 4.5 using 0.3M aqueous nitric acid solution. Then 2.1 grams of
aluminum sulphate mixed with 9.4 grams of water was added to the
mixture under homogenization at 3000 to 4000 revolution per minute
(rpm). The reactor agitator was set to 230 rpm and heated to
40.degree. C. to aggregate the resin and pigment particles. When
the toner particle size reached 6.5 microns, the pH of the slurry
was adjusted to 9.0 using a 4% NaOH solution and the agitator was
decreased to 160 rpm. The reactor was then heated to 50.degree. C.,
and the pH was maintained at 8.5 for 2 hours, during which the
toner aggregates coalesced to form the toner particle. The mixture
was then discharged into a container of cold water (1 Liter). The
toner was then filtered off, washed repeatedly with water and
freeze dried. The final particle size was 6.4 microns.
Example 12 to 14
[0055] A series of CPF Toners were then prepared following the
above procedure with block copolymer resins and colorants. The
properties are listed in Table 2.
TABLE-US-00002 TABLE 2 Block Copolymer Colorant Particle Size Toner
(94%) (6%) microns Example 11 Example 5 Cyan 6.4 Example 12 Example
6 Cyan 7.2 Example 13 Example 7 Black 5.8 Example 14 Example 10
Black 6.0
Cold Pressure Fixture
[0056] A cold pressure fixture was utilized with a process speed of
243 mm/s, a variable nip pressure load area of 1000 PSI (6.9 MPa)
and 1500 PSI (10.3 MPa) and a with a roll contact length of 70 mm.
The pressure was maintained at a constant pressure of 5 Kg/cm.sup.2
(82 lb/inch.sup.2). Toner Images on paper were generated using the
Xerox 800 printer with the fusing fixture disabled. The unfused
prints were then subjected to the above cold pressure fixture.
Imabe permanence was then evaluated using the Taber Linear Abraser
(Model 5700), with a Crock cloth attachment. The images were rubbed
10 cycles, 60 cycles per minute. All of the above toners displayed
excellent toner fix to paper and none to minimal removal of toner
image onto the Crock cloth during the Taber test.
* * * * *