U.S. patent application number 15/588087 was filed with the patent office on 2017-08-17 for ophthalmic spectacle lenses, materials and method.
The applicant listed for this patent is OptimEyes4u, Inc.. Invention is credited to Charles P. Larson.
Application Number | 20170235160 15/588087 |
Document ID | / |
Family ID | 56417554 |
Filed Date | 2017-08-17 |
United States Patent
Application |
20170235160 |
Kind Code |
A1 |
Larson; Charles P. |
August 17, 2017 |
OPHTHALMIC SPECTACLE LENSES, MATERIALS AND METHOD
Abstract
An ophthalmic spectacle lens having transmittance properties
that block UV and violet light and partially block certain cyan
wavelengths to enhance contrast between blue versus green and
partially block certain yellow wavelengths to enhance contrast
between green versus red, and keep in accordance with the
tristimulus values. Adding wavelength-selective organic dyes
provides the entire functional attributes of the current invention
or improves the contrast-enhancing attributes provided by a glass
wafer having functional rare-earth oxides, either of which improve
multi-band spectrum that is balanced in blocking UV light, and
adding contrast between the primary colors to optimize
color-enhancing functions. When using organic dyes for all
functional attributes it is possible to integrate these dyes into
plastic ophthalmic materials. Some lenses are polarized. Unlike
other color-enhancing sunglass lenses, this invention may help
protect the eyes from over-exposure to some high-energy visible
blue light, which may lead to age-related macular degeneration
(AMD).
Inventors: |
Larson; Charles P.;
(Redmond, OR) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
OptimEyes4u, Inc. |
Redmond |
OR |
US |
|
|
Family ID: |
56417554 |
Appl. No.: |
15/588087 |
Filed: |
May 5, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15515589 |
|
|
|
|
PCT/US2015/047997 |
Sep 1, 2015 |
|
|
|
15588087 |
|
|
|
|
62146558 |
Apr 13, 2015 |
|
|
|
62105202 |
Jan 19, 2015 |
|
|
|
Current U.S.
Class: |
351/45 |
Current CPC
Class: |
G02C 7/102 20130101;
G02C 7/12 20130101; G02B 5/223 20130101; G02C 7/104 20130101; G02B
5/208 20130101; G02C 2202/06 20130101 |
International
Class: |
G02C 7/10 20060101
G02C007/10; G02C 7/12 20060101 G02C007/12 |
Claims
1. An ophthalmic color-enhancing lens that provides transmittance
properties which blocks UV light and some visible light, enhances
blue colors, and provides enhanced perceived contrast between blue
light and green light and provides enhanced perceived contrast
between green light and red light, wherein, when assembled, the
lens has a luminous transmission value that is defined by ANSI
Z80.3-2009 4.6.3.2, the lens comprising: one or more
color-absorbing materials that together provide: a first
reduced-light-transmittance zone for a first range of wavelengths
that extends from 300 nm to 399 nm, wherein light transmission at
any wavelength in the first range is no more than 1% of the
luminous transmission of the lens; a second
reduced-light-transmittance zone for a second range of wavelengths
that extends from 400 nm to 409 nm, wherein light transmission at
any wavelength in the second range is no more than 10% of the
luminous transmission of the lens; a third
reduced-light-transmittance zone for a third range of wavelengths
that extends from 410 nm to 420 nm, wherein light transmission at
any wavelength in the third range is no more than 15% of the
luminous transmission of the lens; and a fourth
reduced-light-transmittance zone for a fourth range of wavelengths
that extends from 420 nm to 430 nm, wherein light transmission at
any wavelength in the third range is no more than 20% of the
luminous transmission of the lens; and a plurality of
maximum-light-transmittance zones including three
maximum-light-transmittance zones, one for each respective
wavelength ranges of 440 to 460 nm, 540 to 560 nm, 600 to 630 nm,
with each said maximum-transmittance-zone having at least one
wavelength that is 40% to 150%, inclusive, of the luminous
transmission of the lens, and two
contrast-enhancing-light-transmittance zones coordinately found
between the three maximum-transmittance-zones and specifically
found in the wavelength ranges of 480 nm to 510 nm and 570 nm to
590 nm, wherein each contrast-enhancing-light-transmittance zone
has at least one wavelength having a light-transmittance value
between 20% and 90%, inclusive, of the luminous transmission of the
lens.
2. The lens according to claim 1, wherein the assembled lens
includes at least one light absorber selected from the group
consisting of copper halide, copper indium, titanium dioxide,
neodymium oxide, praseodymium, erbium oxide, and organic dyes.
3. The lens of claim 1, wherein the assembled lens is made using a
two-wafer system including a front glass wafer and a rear glass
wafer with each wafer being about 1 mm in thickness, wherein the
one or more color-absorbing materials include wavelength-selective
light-absorbing oxides in the rear wafer, wherein the front glass
wafer and the rear glass wafer are adhered together with a light
polarizing filter in between the front glass wafer and the rear
glass wafer.
4. The lens of claim 1, wherein the assembled lens is made using a
two-wafer system including a front wafer and a rear wafer with each
wafer being about 1 mm in thickness, wherein the one or more
color-absorbing materials include wavelength-selective
light-absorbing oxides in the front wafer, wherein the front wafer
and the rear wafer are adhered together with a light polarizing
filter in between the front wafer and the rear wafer.
5. The lens of claim 1, wherein the assembled lens includes two
glass wafers that are adhered together using an adhesive with a
light polarizing filter in between the two glass wafers, wherein
the one or more color-absorbing materials are included in at least
one selected from the group consisting of the adhesive and the
light polarizing filter.
6. The lens of claim 1, wherein the assembled lens includes two
glass wafers that are adhered together using an adhesive with a
light polarizing layer in between the two glass wafers, and wherein
the one or more color-absorbing materials are included in at least
one selected from the group consisting of one of the glass wafers,
the adhesive, and the light polarizing layer.
7. The lens of claim 1, wherein the lens includes a fifth
reduced-light-transmittance zone that extends from 430 nm to 450 nm
such that a value of the light transmission at any wavelength in
the fifth reduced-light-transmittance zone is less than 10% of the
luminous transmission value of the assembled lens system.
8. The lens of claim 1, wherein the lens includes additional
organic dyes to increase attenuation from 700 nm to 780 nm such
that a reduced infrared light transmittance zone that extends from
700 nm to 780 nm has a value of the light transmission at any
wavelength in the reduced infrared light transmittance zone that is
not greater than 300% of the luminous transmission value of the
assembled lens system.
9. The lens of claim 1, wherein the assembled lens includes two
wafers including a front wafer and a rear wafer, wherein the front
wafer includes a mirror coating.
10. The lens of claim 1, wherein the assembled lens includes two
wafers including a front wafer and a rear wafer, wherein the rear
wafer includes a concave surface that has an anti-reflection
coating.
11. The lens of claim 1, wherein the lens meets all spectral
requirements found in ANSI Z80.3-2009 and ISO 12312-1 2013.
12. The lens of claim 1, wherein the transmittance properties are
created by using at least one material selected from the group
consisting of class dopants, plastic additives, dyes, stains, a
material that changes on exposure to heat, a material that changes
on exposure to ultraviolet light, a material that changes on
exposure to chemical baths, a material that forms a
semi-transparent mirror coating, and a material that forms a
semi-transparent color coating.
13. The lens of claim 1, wherein the lens is an ophthalmic plastic
lens.
14. The lens of claim 13, wherein the one or more color-absorbing
materials includes at least one selected from the group consisting
of narrowband absorbing dyes, sharp cut absorbing dyes, and
optical-interference coatings.
15. The lens of claim 13, wherein the lens includes a light
polarizing filter.
16. The lens of claim 1, wherein the lens includes a front glass
wafer, a rear glass lens and an adhesive, located between the front
lens and the rear lens, that adheres the front lens to the rear
lens and that contains the one or more color-absorbing
materials.
17. The lens of claim 1, wherein the lens includes a front glass
wafer, a rear glass lens and an adhesive, located between the front
lens and the rear lens, that adheres the front lens to the rear
lens and that contains the one or more color-absorbing materials,
and wherein the lens is polarizing.
18. The lens of claim 1, wherein the lens is adhesiveless but
includes a polymer and at least one organic dye, wherein the lens
has no adhesive layers and has substantially no rare-earth
oxides.
19. The lens of claim 18, wherein the polymer includes a
polycarbonate.
20. The lens of claim 18, wherein the polymer includes a
polyurethane.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of U.S. patent
application Ser. No. 15/515,589, filed Mar. 29, 2017 by Charles P.
Larson and titled "Ophthalmic spectacle lenses, materials and
method," which is a national-stage entry of PCT Application No.
PCT/US2015/047997, filed Sep. 1, 2015 by Charles P. Larson and
titled "Ophthalmic spectacle lenses, materials and method," which
claims priority benefit, including under 35 U.S.C. .sctn.119(e), of
U.S. Provisional Patent Application No. 62/105,202, filed Jan. 19,
2015 by Charles P. Larson, titled "Apparatus and method for
ophthalmic spectacle lenses," and U.S. Provisional Patent
Application No. 62/146,558, filed Apr. 13, 2015 by Charles P.
Larson, titled "Apparatus and method for ophthalmic spectacle
lenses," each of which is incorporated herein by reference in its
entirety.
FIELD OF THE INVENTION
[0002] The present invention relates to methods and devices for
ophthalmic spectacle lenses, and in particular to lens system that
reduces transmission of wavelengths around 500 nm, optionally
including one or more wavelength-selective light-absorbing species
within an adhesive layer of multi-layer-lens versions, optionally
with, and optionally without, significant additional reduction of
transmission of wavelengths around 580 nm, and optionally including
a polarizing filter layer, wherein the lens system optimizes light
transmittance and absorbance characteristics of the tri-stimulus
values.
BACKGROUND OF THE INVENTION
[0003] High-quality sunglasses enhance certain wavelengths of light
and block other wavelengths. A number of U.S. patents attempt to
achieve improved sunglasses and/or enhanced perception of color in
various ways, including the following U.S. patents.
[0004] Each of the patents and patent application publications
referred to in this specification and its accompanying Figures is
incorporated herein by reference in its entirety for all
purposes.
[0005] U.S. Pat. No. 3,300,436 to Marks et al. issued Jan. 24, 1967
with the title "CASTING COMPOSITION FOR LIGHT POLARIZING FILM".
U.S. Pat. No. 3,300,436 describes casting compositions initially
forming an amorphous polymer-complex which are transformable upon
extension into a continuous crystalline film capable of strongly
polarizing transmitted light.
[0006] U.S. Pat. No. 4,549,894 to Araujo, et al. issued on Oct. 29,
1985 with the title "Ultraviolet absorbing photochromic glass of
low silver content". U.S. Pat. No. 4,549,894 describes a method of
producing a photochromic glass having a reduced transmittance for
ultraviolet radiation while having substantially unimpaired
photochromic properties. The method comprises providing a
combination of 0.1-1.0% CeO.sub.2 and 0.1-1.5% Sb.sub.2O.sub.3
and/or As.sub.2O.sub.3 as part of the glass composition. In an
embodiment utilizing minimal silver content, the glass article in
thicknesses of 1.3 to 2.0 mm can be chemically strengthened to
surpass the impact specification imposed by the Federal Food and
Drug Administration for eyewear, will transmit less than 0.2% of
radiation having wavelengths between 290 nm-315 nm, and will
demonstrate a darkened luminous transmittance at
20.degree.-25.degree. C. below 35% and a fading rate such that
after five minutes the luminous transmittance will be at least 1.75
times that of the darkened transmittance.
[0007] U.S. Pat. No. 4,979,976 to Havens, et al. issued Dec. 25,
1990 with the title "Making colored photochromic glasses". U.S.
Pat. No. 4,979,976 describes a method for making tinted
photochromic glass articles having an integral reduced surface
layer exhibiting color, the glass utilizing silver halide crystals
as the photochromic agent. The method generally comprises heat
treating the glass article in a heating chamber in an atmosphere of
flowing hydrogen at temperatures below 500.degree. C. The specific
steps of the inventive method comprise: (a) initially flowing
hydrogen gas into said heat treating chamber at a sufficiently
rapid rate to essentially instantaneously fill said chamber with
the gas; (b) immediately thereafter decreasing the flow of said the
hydrogen gas to permit careful control of the rate at which
reduction takes place in the glass surface; and (c) continuing that
gas flow for a sufficient length of time to produce an integral
reduced surface layer on both front and back surfaces of the
article having a combined depth effective to exhibit a color, but
not of such individual depth as to prevent the passage of
ultraviolet radiation through the front surface of the article.
[0008] U.S. Pat. No. 5,646,781 issued Jul. 8, 1997 to Robert L.
Johnson, Jr. with the title "Optical filters for forming enhanced
images". U.S. Pat. No. 5,646,781 describes an optical filter for
providing an enhanced image. The filter may comprise at least one
substrate, layers of a low refractive index material and layers of
a high refractive index material. The layers are stacked so that
the filter blocks passbands at 490 nm and 590 nm as well as other
image-confusing radiation. Light which is transmitted by the filter
provides an enhanced image for viewing by the human eye as well as
nonhuman detectors.
[0009] U.S. Pat. No. 6,113,811 to Kausch, et al. issued on Sep. 5,
2000 with the title "Dichroic polarizing film and optical polarizer
containing the film". U.S. Pat. No. 6,113,811 describes a dichroic
polarizing film made, for example, by first combining polyvinyl
alcohol and a second polymer, such as, polyvinyl pyrrolidone or a
sulfonated polyester, in a solvent. The ratio of polyvinyl alcohol
to second polymer is between about 5:1 to 100:1 by weight. The film
is coated on a substrate, dried, and then stretched to orient at
least a portion of the film. The film incorporates a dichroic dye
material, such as iodine, to form a dichroic polarizer. This
polarizer may be used in conjunction with a multilayer optical
film, such as a reflective polarizer, to form an optical polarizer.
The multilayer optical film may contain two or more sets of
polyester films, where at least one of the sets is birefringent and
orientable by stretching. The polyvinyl alcohol/second polymer film
and the multilayer optical film may be simultaneously stretched to
orient both polymer films.
[0010] U.S. Pat. No. 6,145,984 to Farwig issued Nov. 14, 2000 with
the title "Color-enhancing polarized lens". U.S. Pat. No. 6,145,984
describes a color-enhancing polarized lens is constructed having
substantially trichroic spectral-transmission. A lens so
constructed may have an overall transmitted tint which is a
virtually colorless gray to the eye. A lens so constructed and
tint-neutralized delivers unexpectedly dramatic improvements in the
areas of color saturation, chromatic and luminous contrast, clarity
of detail, depth perception, haze penetration, and overall
impact.
[0011] U.S. Pat. No. 6,334,680 issued to Larson (the inventor of
the present invention) on Jan. 1, 2002 with the title "Polarized
lens with oxide additive". U.S. Pat. No. 6,334,680 describes lens
for reducing glare and improving color discrimination includes a
lens wafer containing a rare-earth oxide such as neodymium that
provides relatively high light transmittancy at 450 nm, 540 nm, and
610 nm, and relatively low light transmittancy at 500 nm and at 580
nm. A polarized filter is included to reduce glare, and an
anti-reflective layer minimizes ghost images, haze, and loss of
contrast.
[0012] U.S. Pat. No. 6,604,824 to Larson (the inventor of the
present invention) issued Aug. 12, 2003 with the title "Polarized
lens with oxide additive". U.S. Pat. No. 6,604,824 describes a lens
for reducing glare and improving color discrimination includes a
lens wafer containing a rare earth oxide such as neodymium that
provides progressively higher transmittance at 540 nm than at 500
nm and at 450 nm, and average transmittance at 540 nm and 610 nm
that is greater than the transmittance at 580 nm. An ultra-violet
absorber, a polarized filter and anti-reflective layer may be
included to reduce UV light, glare and improve contrast and
vision.
[0013] U.S. Pat. No. 6,773,816 to Tsutsumi issued Aug. 10, 2004
with the title "Driving glasses". U.S. Pat. No. 6,773,816 describes
driving glasses in which a thermic ray reflection layer made of a
metal or an organic substance is provided on the outer surface of a
glass matrix, and an anti-reflection layer 3 is provided on the
inner surface thereof, wherein the glass matrix contains neodymium
oxide Nd.sub.2O.sub.3 through 12% by weight and praseodymium oxide
Pr.sub.6O.sub.11 of 0.5 through 8% by weight, and forms an
absorption peak of light transmittance at a wavelength of 510 nm
through 540 nm and a wavelength of 570 nm through 590 nm.
[0014] U.S. Pat. No. 7,029,118 to Ishak issued on Apr. 18, 2006
with the title "Waterman's sunglass lens". U.S. Pat. No. 7,029,118
describes an improved ten-layer performance polarized lens for
sunglasses. The lens design maximizes visual acuity while
minimizing blue-light transmission using a multi-layer dielectric
mirror to reduces glare and overall light transmission, two layers
of high-contrast blue-blocking amber CR-39 plastic or
polycarbonate, sandwiching a polarizing layer. An outer hydrophobic
overcoat is also provided to protect against haze, delamination,
and smudging. The foregoing layers are arranged to provide a
balanced light transmission profile optimum for use on the water in
which 100% of UV-A & B light is absorbed to at least 400 nm.
The resulting dielectric-mirrored sunglass lens reduces both
overall light transmission and ocular photochemical damage.
[0015] U.S. Pat. No. 7,044,599 to Kumar, et al. issued May 16, 2006
with the title "Polarizing devices and methods of making the same".
U.S. Pat. No. 7,044,599 describes ophthalmic elements and devices
comprising an at least partial coating adapted to polarize at least
transmitted radiation on at least a portion of at least one
exterior surface of an ophthalmic element or substrate. Further,
according to certain non-limiting embodiments, the at least partial
coating adapted to polarize at least transmitted radiation
comprises at least one at least partially aligned dichroic
material. Other non-limiting embodiments of the disclosure provide
methods of making ophthalmic elements and devices comprising
forming an at least partial coating adapted to polarize at least
transmitted radiation on at least a portion of at least one
exterior surface of the ophthalmic element or substrate. Optical
elements and devices and method of making the same are also
disclosed.
[0016] U.S. Pat. No. 7,372,640 to Fung issued May 13, 2008 with the
title "Enhanced color contrast". U.S. Pat. No. 7,372,640 describes
a color contrast enhancing lens made from adhering two different
lenses and a membrane together. It includes a color enhancing lens
whose specific component will selectively absorb the yellow light
in the visible spectrum, which enhances the user vision by
enhancing the distinction between red and green. It also includes
an ultraviolet blocking lens whose special compounds will absorb
the majority of violet light and a part of blue light. It also
includes a light polarization membrane whose special structure can
reduce strong light. It can also absorb the majority of violet
light and keep a low transmission rate of blue light, thus reduced
the retina injury caused by overexposure to blue light. It can also
block the invisible ultraviolet and reduce strong light. So while
the users' eyes are protected, they can also enjoy their view.
[0017] U.S. Pat. No. 7,506,977 to Aiiso issued Mar. 24, 2009 with
the title "Plastic spectacles lens". U.S. Pat. No. 7,506,977
describes plastic spectacles lens containing an organic dye instead
of a neodymium compound and having an optical transmission
equivalent to a plastic spectacles lens containing a neodymium
compound is provided. The plastic spectacles lens comprises a
plastic lens wafer formed from a thermosetting or thermoplastic
resin, or the plastic lens wafer and one, or two or more component
layers formed on at least one side of the plastic lens wafer, and
an organic dye satisfying the specific conditions.
[0018] U.S. Pat. No. 7,597,441 to Farwig issued on Oct. 6, 2009
with the title "Polarized contrast enhancing sunglass lens". U.S.
Pat. No. 7,597,441 describes a polarized sunglass lens that
utilizes a multiband contrast enhancer comprised of three
rare-earth oxides to provide relatively high peak transmittance in
portions of the red and green spectrum, relatively lower
transmittance for the blue spectrum, and very low transmittance for
the UV spectrum. The lens provides enhanced perception of colors,
heightened contrast, and improved visual acuity. The inclusion of
vanadium pentoxide in the lens provides attenuation of the UV
spectrum, thus protecting the user's eyes and the internal layers
and colorants from UV-induced damage. The front lens element can be
either the multiband contrast enhancer or a photochromic lens
element.
[0019] U.S. Pat. No. 8,210,678 to Farwig issued Jul. 3, 2012 with
the title "Multiband contrast-enhancing light filter and polarized
sunglass lens comprising same". U.S. Pat. No. 8,210,678 describes a
polarized sunglass lens that comprises a multiband contrast
enhancer to provide relatively high light transmittance for
portions of the red, green, and blue spectra, while blocking UV and
visible violet wavelengths, and optionally blocking deep-red
wavelengths, in a single lens layer which when positioned as the
front lens layer also protects the internal lens layers from
UV-induced degradation. The multiband contrast enhancer comprises a
combination of a copper halide or copper indium compound with
rare-earth oxides in a heat-treated glass composition, or a
combination of narrowband and sharp-cut absorbing dyes in a plastic
composition, and provides attenuation of the UV and violet
spectrum, thus protecting the user's eyes and the internal layers
and colorants from UV-induced damage while providing enhanced
optical contrast, color saturation, and visual acuity for the
wearer.
[0020] U.S. Pat. No. 8,733,929 to Chiou et al. (hereinafter, "Chiou
et al.") titled "Color contrast enhancing sunglass lens", issued
May 27, 2014. Chiou et al. describe a color contrast enhancing
sunglass lens that includes a lens body and a multi-layer coating
disposed on the lens body. The multi-layer coating includes a set
of alternating layers formed of materials having different
refractive indices and confines the transmission of visible light
to a predetermined spectral profile having at least three high
transmission bands that include blue, green and red bands and that
have a maximum of spectral transmittance no less than 60%, three
low transmission bands that include purple, cyan and yellow bands
and that have a minimum of spectral transmittance no greater than
40%, and no spectral transmittance being less than 15% between 475
nm and 650 nm. The thicknesses of the layers in the multiple-layer
lens coatings determine which wavelengths are reflected and which
wavelengths are passed. The color contrast enhancing sunglass lens
as disclosed meets the ANSI specification Z80.3-2009 section
4.6.3.3.
[0021] U.S. Pat. No. 8,770,749 to McCabe, et al. issued Jul. 8,
2014 with the title "Eyewear with chroma enhancement". U.S. Pat.
No. 8,770,749 describes a lens including a lens body and an optical
filter configured to attenuate visible light in a plurality of
spectral bands. Each of the plurality of spectral bands can include
an absorptance peak with a spectral bandwidth, a maximum
absorptance, and an integrated absorptance peak area within the
spectral bandwidth. An attenuation factor obtained by dividing the
integrated absorptance peak area within the spectral bandwidth by
the spectral bandwidth of the absorptance peak can be greater than
or equal to about 0.8 for the absorptance peak in each of the
plurality of spectral bands.
[0022] German patent application number DE 102005052812 A1 by Asmus
was published Dec. 28, 2006 with the title "Getonte UV-Haftfolie
fur optische Brillenglaser" (roughly, "Tinted UV-adhesive-film for
optical lenses"). This application describes a self-adhesive tinted
UV-blocking tinted film that provides UV-protection against glaring
light, e.g., of sun and snow, in the anti-glaring category 3, that
is, having 8- to 18-percent transmission. The film is made up of
PVC (polyvinylchloride) of thickness 0.1 mm coated with an
adhesive.
[0023] U.S. Pat. No. 3,684,641 to Murphy issued Aug. 15, 1972 with
the title "LAMINATED PRODUCT BONDED WITH COLORED ADHESIVE". U.S.
Pat. No. 3,684,641 describes multi-ply creped tissue paper
containing printing between the plies of tissue to create a pattern
of muted and aesthetically pleasing coloration visible on the
exterior surface of the plies and the method of making the product
which involves the use of water-based adhesives as the printing
media. Such a product is unsuited for making ophthalmic spectacle
lenses.
[0024] U.S. Pat. No. 8,746,879 to Jiang et al issued Jun. 10, 2014
with the title "Adhesive system for a laminated lens and method for
applying same". U.S. Pat. No. 8,746,879 describes a method for
laminating a functional film on to an optical base element and a
tri-layer adhesive system for use in the method. The tri-layer
adhesive includes a first latex adhesive layer disposed on the
functional film and a second latex adhesive layer disposed on the
optical base element. A hot-melt adhesive (HMA) layer is disposed
in between the latex layers to form a tri-layer adhesive to
permanently retain the functionalized film on the optical base
element. The method includes first coating a latex adhesive on the
functional film and second coating a latex adhesive on the optical
base element. An HMA is then coated on to one of the dried latex
adhesive layers. The film is hot pressed on to the optical base
element with the HMA sandwiched in between the latex layers to form
a laminated optical device.
[0025] U.S. Pat. No. 8,916,233 to Mosse et al. issued Dec. 23,
2014, with the title "Methods for coating lenses curved surfaces
with a polarizing liquid". U.S. Pat. No. 8,916,233 describes
methods and apparatus for coating at least a portion of a curved
surface of a lens with a polarizing liquid. For example, there is
provided a method of providing a lens having a curved surface, and
applying a polarizing liquid to at least a portion of the curved
surface by shear flow with a flexible apparatus. Apparatus include
ophthalmic lenses having polarized coatings formed according to the
disclosed methods.
[0026] U.S. Pat. No. 5,793,467 to Bailey issued Aug. 11 1998 with
the title "Semi-permanent reading lenses for sunglasses". U.S. Pat.
No. 5,793,467 describes a plastic reading lens using a
microstructure to provide reading correction can be
semi-permanently attached to a non-prescription sunglass using a
water-soluble adhesive. The lens may be removed from the sunglass
using an adhesive remover which is non-damaging to plastic or
glass. The microstructure lens may also be applied to the
sunglasses using a non-adhesive molecular attraction mechanism.
[0027] U.S. Patent Application Publication 2014/0233105 of Schmeder
et al. published Aug. 21, 2014 with the title "Multi-band color
vision filters and method by LP-optimization". Patent Application
Publication 2014/0233105 describes optical filters that provide
regulation and/or enhancement of chromatic and luminous aspects of
the color appearance of light to human vision, generally to
applications of such optical filters, to therapeutic applications
of such optical filters, to industrial and safety applications of
such optical filters when incorporated, for example, in
radiation-protective eyewear, to methods of designing such optical
filters, to methods of manufacturing such optical filters, and to
designs and methods of incorporating such optical filters into
apparatus including, for example, eyewear and illuminants.
[0028] Accordingly, there is a need for improved ophthalmic
spectacle lenses.
SUMMARY OF THE INVENTION
[0029] In some embodiments, the present invention includes a
color-enhancing ophthalmic spectacle lens whose spectral values
conform to those of the tri-stimulus values. In some embodiments,
the color-enhancing ophthalmic spectacle lens absorbs more
high-frequency visible light than other inventions in its field,
while maintaining or increasing color definition with the use of
transitional metal oxides, rare-earth metal oxides, and/or organic
dyes. In embodiments that include a polarizing filter, this
invention becomes particularly beneficial in providing the wearer
with increased color definition, visual and depth perception, and
acuity.
[0030] In some embodiments, the present invention includes one or
more wavelength-selective light-absorbing species within an
adhesive layer, wherein this adhesive layer itself, when combined
with the wavelength-selective light-absorbing species, is
wavelength-selective transparent (i.e., that allows light to pass
through with substantially no diffusion (but that allows more of
certain wavelengths than other wavelengths) so that objects behind
can be distinctly seen, such as by analogy "transparent blue
water," in contrast to translucent (allowing light, but not
detailed images, to pass through), opaque, or semi-opaque
materials) in the final assembled lens system. In some embodiments,
the adhesive component that contains the wavelength-selective
light-absorbing species includes one or more layers that include a
hot-melt adhesive, a latex adhesive, a polyurethane adhesive, an
acrylic adhesive, a silicone adhesive, an epoxy adhesive, or any
other suitable adhesive layer. The adhesive layer also provides a
mechanical function of adhering other lens components to one
another. In some embodiments, the present invention uses a
water-activated adhesive, for example, the adhesive sold under the
brand name Acrylic Adhesive No. 467 available from the 3M
Corporation of Saint Paul, Minn., USA (3M Corporation). In some
embodiments, a medium viscosity, two component epoxy system with
high performance bonding qualities is preferred. In some
embodiments, the preferred adhesive should be readily cured at room
temperature and/or more rapidly cured at elevated temperatures
relative to room temperature, making the assembled parts available
for handling in a production environment in a shorter time
allotment. In some embodiments, the preferred adhesive should also
be reactive with high physical-strength properties and optical
clarity. Known epoxy resins that are used in some embodiments of
the present invention include those made from epichlorohydrin,
bisphenol A, bisphenol F, and/or other aliphatic polyols such as
glycerol. Such materials can be characterized by a glycidyl ether
structure and are commonly cured with a variety of amines and/or
amides. The result of the combination of the components is a resin
based on the reactivity of such epoxide groups. In some
embodiments, the present invention includes any of the above
adhesives or other suitable adhesive and also includes one or more
wavelength-selective light-absorbing species within the adhesive in
order that the adhesive can be used as the adhering layer between
other lens components (such as ophthalmic-grade glass wafers,
polarizing layers and the like) in sunglasses. In some embodiments,
the present invention includes such sunglasses that include the
adhesive and its one or more wavelength-selective light-absorbing
species as one interior layer (for convenience, referred to as the
first adhesive layer, wherein there is optionally one or more
further adhesive layers) in the lenses. In some embodiments, the
first adhesive layer in the sunglasses includes one or more
wavelength-selective light-absorbing species that reduce
transmission of wavelengths around 500 nm more than the average of
the reduction of transmission of wavelengths around 480 nm and the
reduction of transmission of wavelengths around 520 nm, and the
sunglasses do not substantially reduce wavelengths around 580 nm
more than the average reduction of transmission of wavelengths
around 550 nm and wavelengths around 610 nm. In some embodiments,
the first adhesive layer in the sunglasses includes one or more
wavelength-selective light-absorbing species that reduce
transmission of wavelengths around 500 nm more than the average of
the reduction of transmission of wavelengths around 480 nm and the
reduction of transmission of wavelengths around 520 nm, and the
first adhesive layer also includes one or more wavelength-selective
light-absorbing species that do reduce wavelengths around 580 nm
more than the average of the reduction of transmission of
wavelengths around 560 nm and the reduction of transmission of
wavelengths around 600 nm. In some embodiments, the first adhesive
layer (for example, the layer that holds a first outer glass layer
to a central polarizing layer) in the sunglasses includes one or
more wavelength-selective light-absorbing species that reduce
transmission of wavelengths around 500 nm more than the average of
the reduction of transmission of wavelengths around 480 nm and the
reduction of transmission of wavelengths around 520 nm, and a
second adhesive layer (for example, the layer that holds a second
outer glass layer to the central polarizing layer) includes one or
more wavelength-selective light-absorbing species that reduce
transmission of wavelengths around 580 nm more than the average of
the reduction of transmission of wavelengths around 560 nm and the
reduction of transmission of wavelengths around 600 nm.
[0031] Generally speaking, in accordance with some embodiments of
the invention, an epoxy adhesive composition and one or more
organic dyes are used, in which a base formulation of epoxy with
optical clarity is combined with one or more wavelength-selective
light-absorbing dyes from one or more sources to provide a colored
epoxy adhesive having an enhanced perceived contrast between blue
light and green light due to a blue-versus-green partial-absorbance
band specifically found between 480 nm and 510 nm, and/or having an
enhanced perceived contrast between green light and red light due
to a green-versus-red partial-absorbance band between 570 nm and
590 nm. In some embodiments, by partial-absorbance it is meant that
the band passes at least a certain amount of light in the
wavelengths of the band for safety reasons (e.g., in some
embodiments, an amount of light that is at least 20% of the average
transmittance of the lens over the wavelength range of 400 nm to
700 nm). For example, a lens passing at least this certain amount
of light in the 570 nm to 590 nm partial-absorbance band would help
automobile drivers to notice an amber traffic light that might not
be visible if less light in this band were passed. Similarly,
having the lens pass at least a certain amount of light in the
blue-versus-green partial-absorbance band would help automobile
drivers to notice a cyan or blue-green traffic light that might not
be visible if less light in this band were passed. In some
embodiments, the blue-versus-green partial-absorbance band is
primarily between 480 nm and 490 nm. In some embodiments, the
blue-versus-green partial-absorbance band is primarily between 490
nm and 500 nm. In some preferred embodiments, the blue-versus-green
partial-absorbance band is primarily between 500 nm and 510 nm. In
some other preferred embodiments, the blue-versus-green
partial-absorbance band is primarily between 495 nm and 515 nm.
Some embodiments further include a violet-blocking absorbance band
for wavelengths from 400 to 420 nm when in an assembled lens. In
some embodiments, the violet-blocking absorbance band is for
wavelengths from 400 to 430 nm when in an assembled lens. In some
embodiments, the violet-blocking absorbance band is for wavelengths
from 400 to 440 nm when in an assembled lens. In some embodiments,
the violet-blocking absorbance band is for wavelengths from 400 to
450 nm when in an assembled lens. In some embodiments, the
assembled lens includes two glass wafers and a polymer layer that
is cured between the two wafers in a two-wafer lens system. In some
embodiments, the base compositions include an uncured epoxy resin
with transparent optical clarity. In some embodiments, the dye
pigments are advantageously added to the resin, preferably using
wetting agents and other additives. To this, the dye pigments are
added as needed to provide the desired spectral composition in
conformance to the tri-stimulus values discussed herein. In some
embodiments, the invention accordingly includes compositions
possessing the characteristics, properties and the relations of
components, as well as a system and method involving these
compositions.
[0032] Some embodiments include one or more wavelength-selective
light-absorbing species within a non-adhesive layer that is
deposited on a lens component of the lens system. This non-adhesive
layer itself, when combined with the wavelength-selective
light-absorbing species, is wavelength-selective transparent (i.e.,
that allows light to pass through with substantially no diffusion
(but that allows more of certain wavelengths than other
wavelengths) so that objects behind can be distinctly seen, such as
by analogy "transparent blue water," in contrast to translucent
(allowing light, but not detailed images, to pass through), opaque,
or semi-opaque materials) in the final assembled lens system. In
some embodiments, the non-adhesive deposited layer(s) that contains
the wavelength-selective light-absorbing species is applied to lens
components as a polarizing liquid that provides a light-polarizing
function, such as described in U.S. Pat. No. 8,916,233, as well as
a color-enhancing function obtained from the wavelength-selective
light-absorbing species. In some embodiments, the one or more
wavelength-selective light-absorbing species are added to the
polarizing liquid described in U.S. Pat. No. 8,916,233 along with
an adhesive species such that the resulting liquid is treated as
described in U.S. Pat. No. 8,916,233 to provide its polarization
functionality and is also treated to activate its adhesive function
of holding two other lens components to one another. In some
embodiments, the adhesive component includes a polyurethane that is
water activated.
[0033] In some embodiments, the one or more wavelength-selective
light-absorbing species are applied as a layer by themselves using
vacuum-deposition, sputtering, ion-assisted deposition, applying
when the wavelength-selective light-absorbing species are dissolved
in a solvent that is later evaporated away, or other suitable
techniques. In some such embodiments, an adhesive layer is
deposited on top of such a deposited surface layer of
wavelength-selective light-absorbing species to hold the substrate
having the wavelength-selective absorbing layer to another lens
wafer.
[0034] In some embodiments, the present invention uses one or more
wavelength-selective light-absorbing species to provide
wavelength-selective attenuation of wavelengths around 500 nm
without providing wavelength-selective attenuation of wavelengths
around 580 nm, such that the completed lens system enhances color
separation between blue and green colors (by blocking cyan at 500
nm) without blocking yellow colors of around 580 nm. These lenses
thus allow users of sunglasses and other color-enhancing ophthalmic
spectacle lenses performing certain activities to see certain
desired wavelengths, such as all wavelengths in the visible
spectrum between green and yellow (e.g., in some embodiments,
wavelengths between about 520 nm and about 600 nm are passed to
about equal amounts; in other embodiments, each wavelength between
about 520 nm and about 600 nm is transmitted at a level at least
80% of the average transmission of all wavelengths between about
520 nm and about 600 nm; and in some such embodiments, each
wavelength between about 520 nm and about 600 nm is transmitted at
a level at least 90% of the average transmission of all wavelengths
between about 520 nm and about 600 nm), as well as blue wavelengths
(e.g., in some embodiments, wavelengths between about 440 nm and
about 480 nm are passed to about equal amounts). In some
embodiments, this wavelength-selectivity that attenuates cyan
colors (wavelengths around 500 nm), optionally combined with
polarization in the lens, provides enhanced visibility for people
fishing for, for example, yellow and blue fish, which might not be
as visible to a person wearing other sunglasses that also attenuate
yellow colors (wavelengths around 580 nm). In some embodiments, the
wavelength-selective function attenuates at least some wavelengths
between 490 nm and 510 nm to pass an amount of such light at a
level that is no greater than 75% of the average amount of blue
light (between 440 nm and 480 nm) passed, and also no greater than
75% of the average amount of green and yellow light (between 520 nm
and 590 nm) passed; and at the same time, passes all wavelengths
between 520 nm and 590 nm in an amount of at least 80% of the
average amount of light passed having wavelengths between 520 nm
and 590 nm. In some embodiments, the wavelength-selective function
attenuates at least some wavelengths between 490 nm and 510 nm to
pass an amount of such light at a level that is no greater than 50%
of the average amount of blue light (between 440 nm and 480 nm)
passed, and also no greater than 50% of the average amount of green
and yellow light (between 520 nm and 590 nm) passed; and at the
same time, passes all wavelengths between 520 nm and 590 nm in an
amount of at least 80% of the average amount of light passed having
wavelengths between 520 nm and 590 nm.
[0035] Absorbing ultraviolet (UV) light at wavelengths shorter than
400 nm is important in protecting the eyes from overexposure to UV,
which can cause cataracts. Other lenses in this field attempt to
address this concern, but the effects of extended exposure to
high-frequency visible light has been researched extensively and
there is increasing evidence that not only ultraviolet (UV) light
but also high-frequency visible light may have potentially damaging
effects on our eyes. Cataracts can form from over-exposure to UV
light. Over-exposure to high-frequency visible light may increase
Age Related Macular Degeneration (AMD). Studies such as "The Role
of Oxidative Stress in the Pathogenesis of Age-Related Macular
Degeneration" published in the SURVEY OF OPHTHALMOLOGY, VOLUME 45,
NUMBER 2, pages 115-134, September-October 2000, West S K,
Rosenthal F S, Bressler N M, et al. "Exposure to sunlight and other
risk factors for age-related macular degeneration." Arch.
Ophthalmol. 1989; 107(6):875-9 (hereinafter, the "Maryland Watermen
Study"), plus Klein R, Klein B E, Jensen S C, et al. "The five-year
incidence and progression of age-related maculopathy: The Beaver
Dam Eye Study." Ophthalmol 1997; 104(1):7-21 (hereinafter the
"Beaver Dam Eye Study"), which are all incorporated herein by
reference) all point to a probability that over exposure to blue
light may lead to AMD. In the Maryland Watermen Study, findings are
that AMD was more common in men exposed to increased levels of blue
light, but not in those with increased levels of ultraviolet
exposure. Similarly, the Beaver Dam Eye Study found that exposure
to visible light was associated with AMD in men.
[0036] In some embodiments, the device of the present invention
absorbs more potentially harmful visible light than other lenses in
this field, i.e., nearly 100% of the high-frequency visible light
between 400 nm and 420 nm (or optionally from 400 nm to 430 nm, or
optionally from 400 to 440, or optionally from 400 to 450), while
balancing the visible color spectrum. It is known that when a lens
absorbs light to a degree of 50% of the luminous transmittance of
the lens between 430 nm and 450 nm, the perception of the color
blue starts to deteriorate. Human eyes contain three types of
color-sensitive cones. The first type of cone in the human eye
responds to blue light and is most sensitive at about 450 nm, the
second type of cone is stimulated by green light and is most
sensitive at about 550 nm, and the third type of cone is stimulated
by red light and is most sensitive at about 600 nm. The "green" and
"red" cones are mostly packed into the fovea centralis. By
population, about 64% of the cones are red-sensitive, about 32% are
green sensitive, and about 2% are blue sensitive. The "blue" cones
have the highest sensitivity and are mostly found outside the
fovea. The present invention defines an absorption band one for
visible wavelengths shorter than wavelengths in the "blue" pass
band (i.e., wavelengths of 430 nm or shorter), an absorption band
two for wavelengths longer than wavelengths in the "blue" pass band
but shorter than wavelengths in "green" pass band, an absorption
band three for wavelengths longer than wavelengths in the "green"
pass band but shorter than wavelengths in "red" pass band, and an
absorption band four for wavelengths longer than wavelengths in the
"red" pass band. The mixture of energy responses signaled by the
three types of cones in the human eye defines the total color
perception that a person views. Additionally, chromatic response of
the human eye falls to near zero in the absorption band two (about
500 nm) and absorption band three (about 580 nm), as well as in
violet and ultraviolet of absorption band one (including
wavelengths shorter than about 400 nm) and in deep red of
absorption band four (including wavelengths longer than about 700
nm).
[0037] Lenses that absorb light from 400 nm to 420 nm may increase
protection for a person's eyes due to over exposure of
high-frequency visible light. At the same time, lenses that absorb
light having wavelengths from 400 nm to 420 nm or optionally from
400 to 430 nm will decrease glare and increase distance-vision
acuity. In some embodiments, the present invention can at least
partially achieve one preferred embodiment by adding copper oxides
and/or titanium oxides into an ophthalmic-grade glass wafer, heat
treating this wafer to create a chemical reaction allowing the
absorbance of light to nearly 100% through the range of 415 nm to
425 nm. In some embodiments, adding an organic dye that has a peak
absorbance near 420 nm, or 430 nm, or 440 nm increases the total
absorbance from 400 nm to 420 nm, or 400 nm to 430 nm to nearly
100%. Alternatively, some embodiments use two (2) glass wafers,
with no copper oxides or titanium oxides used, and achieve the
desired absorbance by adding organic dyes (with the functional
attributes to absorb light having wavelengths in the 400 nm to 420
nm or to 430 nm range) to one or more of the adhesive layers, to
the polarizing filter layer, or to both the polarizing filter and
one or more of the adhesive layers. Alternatively, some embodiments
use ophthalmic-grade plastic polymers such as polycarbonate or
polyurethane for the lenses (instead of or in addition to one or
both of the glass wafers used in other embodiments), and have
organic dyes dispersed into or onto the polymer material to cause
the desired spectral curve (such as spectral curve 330 of FIG. 3C
and FIG. 4, or spectral curve 930 of FIG. 9, or the spectral
blocking bands, reducing bands and passing bands shown
schematically in spectral schematic 1030 shown in FIG. 10A) as it
relates to the tristimulus values. Human eyes are most sensitive to
blue light having a wavelength of about 450 nm, so by allowing the
spectral transmittance cut-on between 430 nm and 450 nm allows for
continued blue color perception, without distortion. Human eyes are
most sensitive to green light having a wavelength of about 550 nm.
The BG crossover 214 (see FIG. 2) wavelength-sensitivity curves of
the blue cones and green cones of the human eye occurs at about 500
nm, so by creating an absorption peak near 500 nm, the present
invention will better separate the distinction between blue and
green, increasing contrast and/or improving the pleasurable
perception of the two colors blue and green. In some embodiments,
adding to the lens an organic dye whose peak absorbance is near 500
nm creates the functional absorbance peak desired in the present
invention. The GR crossover 215 (see FIG. 2) of the
wavelength-sensitivity curves of the green cones and red cones of
the human eye occurs at about 580 nm. Creating an absorption peak
in this wavelength region is particularly beneficial in helping the
eye resolve the differences between green and red, thereby
increasing contrast and/or improving the pleasurable perception of
these two colors. Neodymium oxide, a rare-earth oxide, has an
absorption peak at about 585 nm and helps obtain this functional
absorption for some embodiments of the present invention.
Alternatively or additionally, some embodiments of the present
invention use an organic dye (as discussed in U.S. Pat. No.
7,506,977) with an absorbance peak of about 580 nm to replace or
supplement the absorption provided by neodymium. In some
embodiments, neodymium is added to the lens system of the present
invention containing the copper oxides and titanium oxides and/or
to the lens system of the present invention containing the
organic-dye cocktail (e.g., the lens system that includes organic
dyes in the polarizing filter layer and/or one or more adhesive
layers to absorb light having wavelengths from 400 nm to 420 nm or,
430 nm) designed to mimic the absorption characteristics of copper
oxides and titanium oxides.
[0038] In some embodiments, combining the precise ratios of the
embodiments allows the present invention to maintain ANSI
Z80.3-2009 4.6.3.2 and ISO 12312-1 2013 5.3.2.2 and 5.3.2.3
standards for sunglass filters' traffic-signal recognition. In some
embodiments, it is important for the present invention to meet
these standards, as this invention is particularly beneficial for
daytime driving. In some embodiments, the ratios of metal oxides
formulated in a glass wafer are adjusted to compensate for the
thickness of the wafer, which can have various values for thickness
from 1 mm or greater, thus requiring different ratios of oxides in
order to meet the above-described standards for passing a given
minimum amount of light having the wavelengths used for green (or
cyan) and amber signal lights. In some embodiments, the glass wafer
having the metal oxides is used as either the front wafer, rear
wafer, or both in the multi-layered lens embodiments of the present
invention. In some embodiments, the organic dye is added to either
the polarized filter layer or the adhesive layer, or both. In some
embodiments, the metal oxide(s) restrict light transmittance from
400 nm to 415 nm and 585 nm, while the organic dye(s) restrict
light transmittance from 415 nm to 420 nm, or 415 nm to 430 and 490
nm to 510 nm, resulting in at least three transmittance peaks (pass
bands) at about 450 nm, 550 nm, and 600 nm and at least two
absorption peaks (absorption bands) at about 500 nm and 585 nm.
[0039] In some embodiments that include a polarizing filter, the
polarizing filter is applied by one of two technologies well known
in the art: the first would be using a film between two
approximately 1-mm-thick glass wafers, wherein one of the two
wafers contains absorption species of some of the embodiments of
this invention that use one or more of the group consisting of
copper halides, copper oxides, titanium oxides, praseodymium
oxides, and/or erbium oxides, and wherein the second wafer is clear
glass without any particularly unusual spectral transmittance, or
is a photochromic glass wafer (i.e., a glass wafer that darkens
(reduces light transmittance) in bright sunlight). In some
embodiments, the wafers are laminated together with an adhesive
and, in some embodiments, this adhesive contains the organic dyes
used to achieve one or more of the reduced-transmission spectral
bands). Herein, this is called a two-wafer system.
[0040] In other embodiments, the polarizing-filter technology
includes a single glass wafer that contains the absorption species
of some of embodiments that use one or more of the group consisting
of copper halides, copper oxides, titanium oxides, praseodymium
oxides, and/or erbium oxides, wherein the glass wafer is about 2-mm
thick, and wherein the polarizing filter is applied to the concave
surface of the wafer using a vacuum-coating process that is well
known in the art of ion-assisted deposition. Herein, this is called
a single-wafer system.
[0041] In some embodiments, the present invention also includes
mirror coatings and/or anti-reflection coatings. If a mirror
coating is desirable, the use of a two-wafer system is particularly
beneficial. In some embodiments, the mirror coating is applied to
the concave surface of the front wafer, which provides protection
to the mirror coating from scratching or abrasion, and protects the
mirror coating from separating from the lens surface. With an
internal mirror coating such as this, in some embodiments, it is
desirable to include an anti-reflection coating on the concave
surface of the rear wafer to minimize internal reflections induced
by the mirror coating. In some embodiments, the mirror coating
includes a metal film. In other embodiments, the mirror coating
includes a plurality of dielectric layers. In still other
embodiments, the mirror coating includes both a metal film and a
plurality of dielectric layers. In some embodiments, the
thicknesses of the dielectric layers are chosen to reflect (and
thus help block) one or more of the wavelengths in one or more of
the reduced-transmittance wavelength bands.
BRIEF DESCRIPTION OF THE FIGURES
[0042] FIG. 1A is a set of spectral graphs 1110 comparing the
spectral light-transmission curves 110, 120, and 130 at various
wavelengths of three embodiments of the present invention to
light-transmission curves 88 and 99 at various wavelengths of a
lens according to U.S. Pat. No. 8,770,749 (Prizm Daily) and
according to a conventional 580-blocking-only polarized embodiment
(e.g., such as described in U.S. Pat. No. 7,506,977),
respectively.
[0043] FIG. 1A1 is a set of spectral graphs 1111 comparing spectral
light-transmission curves 110, 120, and 130 at various wavelengths
to various averages of the light-transmission curves 119, 129, and
139 across the various wavelengths.
[0044] FIG. 1A2 is a set of spectral graphs 1112 comparing spectral
light-transmission curves 114, 124, and 134 at various wavelengths
to various averages of the light-transmission curves 117, 127, and
137 across the various wavelengths.
[0045] FIG. 1A3 is a cross-sectional schematic of a lens 11 that
represents one embodiment of the 500 & 580 Brown Polarized lens
that exhibits the spectral curve 110 as shown in FIG. 1A1 according
to some embodiments of the present invention.
[0046] FIG. 1A4 is a cross-sectional schematic of a lens 12 which
represents one embodiment of the 500 & 580 No Polarization lens
that exhibits the spectral curve 120 of FIG. 1A1 according to the
present invention.
[0047] FIG. 1A5 is a cross-sectional schematic of a lens 13 which
represents one embodiment of the 500 & 580 Gray Polarized lens
that exhibits the spectral curve 130 of FIG. 1A1 according to the
present invention.
[0048] FIG. 1B is a spectral graph 1120 that illustrates
light-transmission curve 88 at various wavelengths.
[0049] FIG. 1C1 is a spectral graph 1131 that illustrates
light-transmission curve 99 at various wavelengths of a lens
according to a conventional or current 580-only blocking
embodiment.
[0050] FIG. 1C2 is a set of spectral graphs 1132 that illustrate
details of the spectral graphs set forth in FIG. 1A1.
[0051] FIG. 1C3 is a set of spectral graphs 1133 that illustrate
details of the spectral graphs set forth in FIG. 1A2.
[0052] FIG. 1D1 is a spectral graph 1141 that illustrates the
spectral light-transmission curve 130 at various wavelengths of one
embodiment of the present invention.
[0053] FIG. 1D2 is a set of spectral graphs 1142 comparing the
spectral light-transmission curve 130 at various wavelengths to
various averages of the spectral light-transmission curve 130
across the various wavelengths.
[0054] FIG. 1D3 is a set of spectral graphs 1143 comparing the
spectral light-transmission curve 134 at various wavelengths to
various averages of the spectral light-transmission curve 134
across the various wavelengths.
[0055] FIG. 1E1 is a spectral graph 1151 that illustrates the
spectral light-transmission curve 120 at various wavelengths of one
embodiment of the present invention.
[0056] FIG. 1E2 is a set of spectral graphs 1152 comparing the
spectral light-transmission curve 120 at various wavelengths to
various averages of the spectral light-transmission curve 120
across the various wavelengths.
[0057] FIG. 1E3 is a set of spectral graphs 1153 comparing the
spectral light-transmission curve 124 at various wavelengths to
various averages of the spectral light-transmission curve 124
across the various wavelengths.
[0058] FIG. 1F1 is a spectral graph 1161 that illustrates the
spectral light-transmission curve 110 at various wavelengths of one
embodiment of the present invention.
[0059] FIG. 1F2 is a set of spectral graphs 1162 comparing the
spectral light-transmission curve 110 at various wavelengths to
various averages of the spectral light-transmission curve 110
across the various wavelengths.
[0060] FIG. 1F3 is a set of spectral graphs 1163 comparing the
spectral light-transmission curve 114 at various wavelengths to
various averages of the spectral light-transmission curve 114
across the various wavelengths.
[0061] FIG. 1G (Assembled Lens Drawing) is a cross section view of
a two-wafer system 1170 according to some embodiments of the
present invention.
[0062] FIG. 2 is a graph 200 of spectral sensitivity versus
wavelength (called the tristimulus curve) detailing the peak
sensitivity curves for color vision. Blue sensitivity is designated
as zone B, green sensitivity is designated as zone G, and red
sensitivity is designated as zone R.
[0063] FIG. 3A is a set of spectral graphs 301 comparing the
spectral light-transmission curve 360 and 370 at various
wavelengths of two embodiments of the present invention to
tristimulus curves 211, 212 and 213.
[0064] FIG. 3B is a set of spectral graphs 302 comparing the
spectral light-transmission curves 340 and 350 at various
wavelengths of two embodiments of the present invention to light
transmission 310 at various wavelengths of a "clear" lens.
[0065] FIG. 3C is a set of spectral graphs 303 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 321 at
various wavelengths of a lens according to Farwig's U.S. Pat. No.
7,597,441.
[0066] FIG. 4 is a set of spectral graphs 400 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 421 at
various wavelengths of a lens according to Tsutsumi's U.S. Pat. No.
6,773,816.
[0067] FIG. 5 is a set of spectral graphs 500 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 521 at
various wavelengths of a lens according to Larson's U.S. Pat. No.
6,604,824.
[0068] FIG. 6 is the set of spectral graphs 600 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 621 at
various wavelengths of a lens according to Fung's U.S. Pat. No.
7,372,640.
[0069] FIG. 7 is the set of spectral graphs 700 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 721 at
various wavelengths of a lens according to U.S. Pat. No. 6,145,984
describes three maximum transmittal peaks and two minimum
transmittal peaks.
[0070] FIG. 8 is the set of spectral graphs 800 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 821 at
various wavelengths of a lens according to a typical sunglass
lens.
[0071] FIG. 9 is the set of spectral graphs 900 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 930 at
various wavelengths of a sunglass lens according to another
embodiment of the present invention.
[0072] FIG. 10A is a set of graphs 1001 that compare the absorption
and transmittance bands of various embodiments of the current
invention to both the tristimulus values 1010 and to the absorption
and transmittance bands 1021 of U.S. Pat. No. 6,145,984.
[0073] FIG. 10B is a set of graphs 1002 that compare the sets 1036,
1037, 1038, 1039, and 1040 of absorption and transmittance bands of
various embodiments of the current invention to the tristimulus
values 1010.
[0074] FIG. 10C is a set of graphs 1003 that compare various
optional absorption subbands of various embodiments of the current
invention to the tristimulus values 1010.
[0075] FIG. 10D is a set of graphs 1004 that compare various
optional absorption subbands of various embodiments of the current
invention to the tristimulus values 1010.
[0076] FIG. 11 is a set of graphs 1100 that compares the absorption
and transmittance bands 1030 of the current invention to the
tristimulus values 1010 and to the absorption and transmittance
bands 1121 of U.S. Pat. No. 6,773,816.
[0077] FIG. 12 is a set of graphs 1200 that compares the absorption
and transmittance bands 1030 of the current invention to the
tristimulus values 1010 and to the absorption and transmittance
bands 1221 of U.S. Pat. No. 7,597,640.
[0078] FIG. 13 is a set of graphs 1300 that compares the absorption
and transmittance bands 1030 of the current invention to the
tristimulus values 1010 and to the absorption and transmittance
bands 1321 of U.S. Pat. No. 7,597,441.
[0079] FIG. 14 is a set of graphs 1400 that compares the absorption
and transmittance bands 1030 of the current invention to the
tristimulus values 1010 and to the absorption and transmittance
bands 1421 of U.S. Pat. No. 8,210,678.
[0080] FIG. 15A is a set of graphs 1501 that compares the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the absorption and transmittance
bands 1521 of U.S. Pat. No. 7,506,977.
[0081] FIG. 15B is a set of graphs 1502 that compares the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the absorption and transmittance
bands 1522 of U.S. Pat. No. 8,770,749.
[0082] FIG. 15C is a set of graphs 1503 that compares the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the absorption and transmittance
bands 1523 of U.S. Pat. No. 8,733,929.
[0083] FIG. 15D is a set of graphs 1504 that compares the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the absorption and transmittance
bands 1524 of U.S. Pat. No. 6,604,824.
[0084] FIG. 15E is a set of graphs 1505 that compares the
absorption and transmittance bands 1031 of the current invention to
the tristimulus values 1010 and to the absorption and transmittance
bands 1525 of U.S. Patent Application Publication 2013/0141693.
[0085] FIG. 16 is a schematic of a lens 1600 having a plurality of
layers, some of which are optionally omitted, according to some
embodiments of the present invention.
DETAILED DESCRIPTION OF THE INVENTION
[0086] Although the following detailed description contains many
specifics for the purpose of illustration, a person of ordinary
skill in the art will appreciate that many variations and
alterations to the following details are within the scope of the
invention. Specific examples are used to illustrate particular
embodiments; however, the invention described in the claims is not
intended to be limited to only these examples, but rather includes
the full scope of the attached claims. Accordingly, the following
preferred embodiments of the invention are set forth without any
loss of generality to, and without imposing limitations upon the
claimed invention. Further, in the following detailed description
of the preferred embodiments, reference is made to the accompanying
drawings that form a part hereof, and in which are shown by way of
illustration specific embodiments in which the invention may be
practiced. It is understood that other embodiments may be utilized
and structural changes may be made without departing from the scope
of the present invention.
[0087] It is specifically contemplated that the present invention
includes embodiments having combinations and subcombinations of the
various embodiments and features that are individually described
herein (i.e., rather than listing every combinatorial of the
elements, this specification includes descriptions of
representative embodiments and contemplates embodiments that
include some of the features from one embodiment combined with some
of the features of another embodiment, including embodiments that
include some of the features from one embodiment combined with some
of the features of embodiments described in the patents and
application publications incorporated by reference in the present
application). Further, some embodiments include fewer than all the
components described as part of any one of the embodiments
described herein.
[0088] The leading digit(s) of reference numbers appearing in the
Figures generally corresponds to the Figure number in which that
component is first introduced, such that the same reference number
is used throughout to refer to an identical component which appears
in multiple Figures. Signals and connections may be referred to by
the same reference number or label, and the actual meaning will be
clear from its use in the context of the description.
[0089] It is well known in the art of color-enhancing polarized
lenses that using a glass lens wafer within a multiple-layered lens
system is useful to include light-absorbing oxides to create a
filter that selectively transmits, absorbs and reflects light in
specific bands of the visible-light spectrum, which preferably
would correlate with the tristimulus values. The tristimulus values
are a guideline for those who want to improve the art of
color-enhancing ophthalmic lenses. In some embodiments, an
alternative to using a glass wafer containing one or more
light-absorbing oxides is to use organic dyes with
specific-wavelength absorbent characteristics and add these dyes to
either the adhesive layers or to an ophthalmic plastic substrate
such as the plastic lens material itself or a polarizing
filter.
[0090] The human eye has three kinds of cone cells that sense
light, with spectral-sensitivity peaks in short, middle, and long
wavelengths. These cone cells underlie human color perception under
medium- and high-brightness conditions (in very dim light, color
vision diminishes, and the low-brightness, monochromatic
"night-vision" receptors, called rod cells, take over). Studies
conducted in the connection of the manufacture of artificial
lighting have found that human color vision may be characterized
chromatically by three channels. Chromatic response falls to near
zero in the blue green wavelengths near 500 nm and in the yellow
wavelengths near 580 nm, as well as in violet wavelengths near 400
nm and in deep red wavelengths beyond 700 nm. The minima may be
related to the fact that the red-green blind protanope sees no hue
at all near 500 nm and the tritanope sees no hue near 580 nm. These
wavelengths impair proper identification of chromaticities of color
objects. The eye uses wavelengths near 450 nm, 550 nm, and 600 nm
most effectively. Thus, the importance to have higher transmittance
at 450 nm (blue light), 550 nm (green light), and 600 nm (red
light), while having lower transmittance values near 500 nm
(transitional band of wavelengths between blue and green) and 580
nm (transitional band of wavelengths between green and red).
[0091] It is well known in the art of color-enhancing glass lenses
that neodymium oxide creates an absorption peak between 570 nm and
590 nm. More recently, the art has adopted the use of organic dyes
in plastic substrates to replicate some of what the glass
substrates have achieved. There are organic dyes being produced
today that have specific absorption peaks to cover all bands in the
visible spectrum of this present invention, including dyes with
absorption peaks near 400 nm, 409 nm, 419 nm, 425 nm, 430 nm, 439
nm and 584 nm, and others. The first color-enhancing glass
polarized lenses provided one or more absorption peaks between 570
nm and 590 nm but did not address the rest of the tristimulus
values. In fact, U.S. Pat. Nos. 6,145,984, 6,334,680, 6,604,824,
6,773,816, 7,372,640, 7,597,441, 8,210,678 and plastic-lens U.S.
Pat. Nos. 7,506,977, and 8,770,749 only cover sections of the
tristimulus values.
[0092] In some embodiments, the present invention addresses all
five bands, and further addresses a sixth band of wavelengths the
area of the visible spectrum between 400 nm and 450 nm. This sixth
band includes ultra-violet (about 300 nm to about 400 nm,
inclusive), violet (about 400 nm to about 420 nm, inclusive) and
blue light (about 420 nm to about 490 nm, inclusive). This actually
creates a sixth zone or range of wavelengths that includes
wavelengths that herein will be called absorption band one. Only
U.S. Pat. No. 8,210,678 addresses the need to reduce light in the
sixth zone of violet-blue (VB). Light in absorption band one
(including high-frequency visible light, e.g., 400 nm-420 nm or 400
nm-430 nm) can potentially cause "Age Related Macular Degeneration"
(AMD) and light in absorption band one can also reduce
distant-vision acuity. The present invention absorbs significant
portions of the high-frequency visible light and balances color
perception.
[0093] Color-enhancing technology in polarized sunglasses has
become readily available on the market place but ophthalmic lenses
with color-enhancing functions without a polarizing filter are less
common. Most patents fail to address the absorption of
high-frequency visible light while at the same time using known
technology for better, more balanced color enhancement and
definition. Color enhancement visually enhances the difference in
colors giving the wearer increased perception and color saturation
of objects being viewed. The shortcoming of other spectacle lenses
in this field is twofold, first most fail to absorb the
highest-frequency light found in the visible spectrum of absorption
band one, between 400 nm and 430 nm. This high-frequency light
tends to be scattered and thus will cause glare and restricts
visual perception. Atmospheric contaminants increase the
reflections of high frequency visible light which in turn will
increase glare and the loss of vision and visual perception,
diminishing the effects of the color enhancing benefits.
Eliminating or greatly reducing light between 400 nm and 420 nm
increases contrast, allowing the wearer noticeable increased
clarity, and more so when reducing light to 430 nm. Second, no
other spectacle lens in the art addresses the bisecting band of
light between blue and green, near 500 nm. In the art of color
enhancing this is a very important band to attenuate light to
complete the tristimulus values.
[0094] Ultra-violet light (UV) is defined as electromagnetic
radiation in the spectral region between 180 and 400 nanometers
(nm). The visible spectrum is found between about 400 nm and 700
nm. High frequency visible light can be found in the range of about
400 nm to about 475 nm. Other inventions in this field are asserted
to protect the wearer from only UV light. Farwig U.S. Pat. No.
6,145,984 does not address the transmittance of light from 400 nm
to 420 nm, Farwig U.S. Pat. No. 7,597,441 describes its light
transmittance at 400 nm to be between 50% and 100% of the value of
the luminous transmittance of the lens, and transmittance between
420 nm and 460 nm is 125% of the value of the luminous
transmittance of the lens. Tsutsumi U.S. Pat. No. 6,773,816 shows
0% transmittance at 400 nm but does not address the transmittance
between 400 nm and 420 nm. Larson U.S. Pat. No. 6,334,680 does not
address the transmittance of light between 400 nm and 420 nm.
Larson U.S. Pat. No. 6,604,824 does not address the transmittance
of light between 400 nm and 420 nm. Fung U.S. Pat. No. 7,372,640
shows nearly 100% absorption of light to 415 nm in a lens that is
2.0 mm thick, with the absorbing species evenly dispersed through
the thickness of the lens and a 1-mm thickness is required to
produce the assembled lens, using a 1-mm thick wafer, the Fung lens
can only absorb nearly 100% of light to 410 nm. Hopnic U.S. Pat.
No. 7,506,977 only describes a substantial absorbance peak found
between 565 nm and 605 nm with no description of any absorbance at
about 500 nm. Oakley U.S. Pat. No. 8,770,749 by McCabe et al. only
describes absorption peaks in two bands, one being between 445 nm
and 480 nm and the other between 560 nm and 580 nm. The current
invention specifically addresses the transmittance of light between
400 nm and 430 nm, and absorbs nearly 100% of this high-frequency
visible light, regardless of lens thickness. None of the
above-mentioned patents have any absorbance peak in the band
including 500 nm, nor any absorbance peak to 420 nm or 430 nm. Only
Farwig U.S. Pat. No. 8,210,678 has addressed the spectral
wavelengths from 400 nm to 450 nm, but it does not address all
tristimulus values in the manner of the present invention,
specifically absorption band two including 500 nm. In contrast, the
Ishak U.S. Pat. No. 7,029,118 (titled "Waterman's sunglass lens")
absorbs nearly 100% of the visible light found between 400 nm and
500 nm, this type of transmittance distorts the colors of objects
the viewer sees and will not allow the wearer to perceive the color
blue. This can also reduce visibility of blue-green or cyan traffic
signals at wavelength of 500 nm, which is a hazard for vehicle
drivers.
[0095] It is further believed in the art of spectacle
color-enhancing lenses that there is no oxide that effectively
attenuates light in visible-light absorption band two, which is
near 500 nm. Conventional devices have an increase in transmittance
or a transmittance peak in wavelengths around 500 nm. In some
embodiments, the present invention provides an absorption peak in
this absorption band two by adding an organic dye. As for
absorption band three, it is well known in the art that the oxide
neodymium has an absorption peak at about 585 nm and is used in
some current devices.
[0096] FIG. 1A is a set of spectral graphs 1110 comparing the
spectral light-transmission curves 110, 120, and 130 at various
wavelengths of three embodiments of the present invention to
light-transmission curves 88 and 99 at various wavelengths of a
lens according to U.S. Pat. No. 8,770,749 (Oakley Prizm Daily) and
a modified lens similar to a conventional 580-blocking-only
polarized embodiment (e.g., such as described in U.S. Pat. No.
7,506,977), respectively. The numbers along the X axis of each of
the graphs herein represent light wavelengths in nanometers (nm),
and the numbers along the Y axis represent light transmission
through the respective lenses expressed as a percentage of the
incoming light. In some embodiments, curve 130 represents the
spectral transmission of a lens embodiment of the present invention
that includes enhanced narrowband absorption at 500 and 580
nanometers, has a perceived gray tint (due to relatively similar
amounts of light transmission in the red, green and blue
passbands), and is polarized (also referred to herein as "500 &
580 Gray Polarized" lens 13 or "500 & 580 Blocking Gray
Polarized" lens 13). In some embodiments, curve 120 represents the
spectral transmission of a lens embodiment of the present invention
that includes enhanced narrowband absorption at 500 and 580
nanometers and is not polarized (also referred to herein as "500
& 580 No Polarization" lens 12 or "500 & 580 Blocking No
Polarization" lens 12). In some embodiments, curve 110 represents
the spectral transmission of a lens embodiment of the present
invention that includes absorption at 500 and 580 nanometers, has a
perceived brown tint (due to relatively higher amounts of light
transmission in the red passband, relatively lower amounts of light
transmission in the blue passband), and is polarized (also referred
to herein as "500 & 580 Brown Polarized" lens 11). For
comparison, curve 88 represents a lens according to U.S. Pat. No.
8,770,749 (also referred to as Prizm Daily). In some embodiments,
curve 99 is somewhat similar to a lens according to U.S. Pat. No.
7,506,977 (a conventional 580-blocking-only polarized lens that has
an absorption band at 580 nm), except that the spectral curve of
the lens 99 has been modified relative to the description in U.S.
Pat. No. 7,506,977 to increase absorption in wavelengths from 400
nanometers to 430 nanometers.
[0097] FIG. 1A1 is a set of spectral graphs 1111 comparing spectral
light-transmission curves 110, 120, and 130 (each of which exhibit
enhanced narrowband absorption at 500 nm and at 580 nm) at various
wavelengths to various narrowband averages (graph horizontal lines
111, 112, 113, 121, 122, 123, 131, 132 and 133) and wideband
averages (graph horizontal lines 119, 129 and 139) of the
light-transmission curves 110, 120, and 130 across the various
wavelengths.
[0098] FIG. 1A2 is a set of spectral graphs 1112 comparing spectral
light-transmission curves 114, 124, and 134 (each of which exhibit
enhanced narrowband absorption at 500 nm but not at 580 nm) at
various wavelengths to various narrowband averages (graph
horizontal lines 111, 112, 113, 121, 122, 123, 131, 132 and 133)
and wideband averages (graph horizontal lines 117, 127 and 137) of
the light-transmission curves 114, 124, and 134 across the various
wavelengths.
[0099] FIG. 1A3 is a cross-sectional schematic of a lens 11 that
represents one embodiment of the 500 & 580 Brown Polarized lens
that exhibits the spectral curve 110 as shown in FIG. 1A1 according
to some embodiments of the present invention. In other embodiments,
lens 11 represents one embodiment of the 500-block-only Brown
Polarized lens that exhibits the spectral curve 114 as shown in
FIG. 1A2 according to some embodiments of the present invention. In
some embodiments, lens 11 includes a polarization layer 103
sandwiched between front glass wafer 101 and rear glass wafer 102
using rear adhesive layer 104 and front adhesive layer 105. In some
embodiments, one or both of rear adhesive layer 104 and front
adhesive layer 105 include one or more wavelength-selective
absorbing materials (e.g., in some embodiments, one or more organic
dyes) that preferentially absorb a relatively narrow absorption
band (e.g., in some embodiments, a range of about 20 nm) of
wavelengths around 500 nm. In addition, in some embodiments, one or
both of rear adhesive layer 104 and front adhesive layer 105
include one or more wavelength-selective absorbing materials (e.g.,
in some embodiments, one or more organic dyes) that preferentially
absorb a relatively narrow absorption band (e.g., in some
embodiments, a range of about 20 nm) of wavelengths around 580 nm.
In some embodiments, one or more additional lens layers or coatings
are also applied to lens 11, as set forth below in the description
of FIG. 1G.
[0100] In other embodiments, the 500 & 580 Brown Polarized lens
11 is implemented as a single-layer polymer lens that has
polarization properties and that also includes one or more
wavelength-selective absorbing materials (e.g., in some
embodiments, one or more organic dyes) that preferentially absorb a
relatively narrow absorption band (e.g., in some embodiments, a
range of about 20 nm) of wavelengths around 500 nm. In some such
embodiments, 500 & 580 Brown Polarized lens 11 includes one or
more wavelength-selective absorbing materials (e.g., in some
embodiments, one or more organic dyes) that preferentially absorb a
relatively narrow absorption band (e.g., in some embodiments, a
range of about 20 nm) of wavelengths around 580 nm. In other
embodiments, lens 11 is implemented as a single-layer polymer lens
(in some embodiments, with polarization and in other embodiments,
without polarization) that includes one or more
wavelength-selective absorbing organic dyes that preferentially
absorb a relatively narrow absorption band of wavelengths around
500 nm, but which does not have additives that preferentially
absorb a relatively narrow absorption band of wavelengths around
580 nm.
[0101] FIG. 1A4 is a cross-sectional schematic of a lens 12 which
represents one embodiment of the 500 & 580 No Polarization lens
that exhibits the spectral curve 120 of FIG. 1A1 according to the
present invention. In other embodiments, lens 12 represents one
embodiment of the 500-block-only No Polarization lens that exhibits
the spectral curve 124 as shown in FIG. 1A2. In some embodiments,
lens 12 includes a single adhesive layer 104 sandwiched between
front glass wafer 101 and rear glass wafer 102. In some
embodiments, adhesive layer 104 includes one or more
wavelength-selective absorbing materials (e.g., in some
embodiments, one or more organic dyes) that preferentially absorb a
relatively narrow absorption band (e.g., in some embodiments, a
range of about 20 nm) of wavelengths around 500 nm. In addition, in
some embodiments, adhesive layer 104 includes one or more
wavelength-selective absorbing materials (e.g., in some
embodiments, one or more organic dyes) that preferentially absorb a
relatively narrow absorption band (e.g., in some embodiments, a
range of about 20 nm) of wavelengths around 580 nm. In some
embodiments, one or more additional lens layers or coatings are
also applied to lens 12, as set forth below in the description of
FIG. 1G.
[0102] In other embodiments, the 500 & 580 No Polarization lens
12 is implemented as a single-layer polymer lens that has no
polarization properties and that also includes one or more
wavelength-selective absorbing materials (e.g., in some
embodiments, one or more organic dyes) that preferentially absorb a
relatively narrow absorption band (e.g., in some embodiments, a
range of about 20 nm) of wavelengths around 500 nm. In some such
embodiments, lens 12 includes one or more wavelength-selective
absorbing materials (e.g., in some embodiments, one or more organic
dyes) that preferentially absorb a relatively narrow absorption
band (e.g., in some embodiments, a range of about 20 nm) of
wavelengths around 580 nm. In other embodiments, lens 12 is
implemented as a single-layer polymer lens without polarization
that includes one or more wavelength-selective absorbing organic
dyes that preferentially absorb a relatively narrow absorption band
of wavelengths around 500 nm, but which does not have additives
that preferentially absorb a relatively narrow absorption band of
wavelengths around 580 nm.
[0103] FIG. 1A5 is a cross-sectional schematic of a lens 13 which
represents one embodiment of the 500 & 580 Gray Polarized lens
that exhibits the spectral curve 130 of FIG. 1A1 according to the
present invention. In other embodiments, lens 13 represents one
embodiment of the 500-block-only No Polarization lens that exhibits
the spectral curve 134 as shown in FIG. 1A2. The descriptions of
components of lens 11 also apply to the like-numbered components of
lens 13; however, 500 & 580 Gray Polarized lens 13 transmits
relatively similar average amounts of light in the red, green and
blue passbands (in some embodiments, about 19, 15% and 17% in red,
green and blue respectively) in contrast to 500 & 580 Brown
Polarized lens 11, which passes relatively more red and less blue
(in some embodiments, about 25%, 15% and 9% in red, green and blue
respectively).
[0104] In other embodiments, the 500 & 580 Gray Polarized lens
13 is implemented as a single-layer polymer lens that has
polarization properties and that also includes one or more
wavelength-selective absorbing materials (e.g., in some
embodiments, one or more organic dyes) that preferentially absorb a
relatively narrow absorption band (e.g., in some embodiments, a
range of about 20 nm) of wavelengths around 500 nm. In some such
embodiments, lens 13 includes one or more wavelength-selective
absorbing materials (e.g., in some embodiments, one or more organic
dyes) that preferentially absorb a relatively narrow absorption
band (e.g., in some embodiments, a range of about 20 nm) of
wavelengths around 580 nm. In other embodiments, lens 13 (in some
embodiments, with polarization and in other embodiments, without
polarization) is implemented as a single-layer polymer lens that
includes one or more wavelength-selective absorbing organic dyes
that preferentially absorb a relatively narrow absorption band of
wavelengths around 500 nm, but which does not have additives that
preferentially absorb a relatively narrow absorption band of
wavelengths around 580 nm.
[0105] Referring again to FIG. 1A1, in some embodiments, graphs
1111 include horizontal lines 121, 122, and 123 that illustrate
average-passband-transmission percentages at red, green, and blue
(RGB), respectively, for one embodiment of 500 & 580 No
Polarization lens 12 of the present invention (also referred to as
the Present Invention No Polarization (PINP) lens 12) represented
by plotted transmission curve 120. In some embodiments, as shown on
graphs 1111, the RGB passband-averages for PINP lens 12 are 36%
(the average transmission 121 of red wavelengths in the range of
600 nm to 640 nm, inclusive, hereinafter referred to as the
"primary red passband"), 26% (the average transmission 122 of green
wavelengths in the range of 520 nm to 560 nm, inclusive,
hereinafter referred to as the "primary green passband"), and 22%
(the average transmission 123 of blue wavelengths in the range of
440 nm to 480 nm, inclusive, hereinafter referred to as the
"primary blue passband").
[0106] In some embodiments, graphs 1111 include horizontal lines
111, 112, and 113 that illustrate RGB average-passband-transmission
percentages for the 500 & 580 Brown Polarized lens 11
embodiment of the present invention represented by plotted
transmission curve 110. In some embodiments, as shown on graphs
1111, the RGB passband-averages for 500 & 580 Brown Polarized
are 25% (primary red passband average transmission 111), 15%
(primary green passband average transmission 112), and 9% (primary
blue passband average transmission 113).
[0107] In some embodiments, graphs 1111 include horizontal lines
131, 132, and 133 that illustrate RGB average-passband-transmission
percentages for the 500 & 580 Gray Polarized lens 13 embodiment
of the present invention. In some embodiments, as shown on graphs
1111, the RGB averages for 500 & 580 Gray Polarized are 19%
(primary red passband average transmission 131), 15% (primary green
passband average transmission 132), and 17% (primary blue passband
average transmission 133).
[0108] In some embodiments, graphs 1111 include horizontal line
129, which illustrates the average transmission percentage of PINP
lens 12 across a wavelength range of 400 to 700 nanometers (i.e.,
27% average transmission across the wideband visible-light range
400 nm to 700 nm, inclusive). In some embodiments, graphs 1111
include horizontal line 119, which illustrates the average
transmission percentage of 500 & 580 Brown Polarized 11 across
a wavelength range of 400 to 700 nanometers (i.e., 17% average
transmission across the range 400 nm to 700 nm, inclusive). In some
embodiments, graphs 1111 include horizontal line 139, which
illustrates the average transmission percentage of 500 & 580
Gray Polarized lens 13 across a wavelength range of 400 to 700
nanometers (i.e., 16% average transmission across the range 400 nm
to 700 nm, inclusive).
[0109] FIG. 1A2 is a set of spectral graphs 1112 comparing spectral
light-transmission curves 114, 124, and 134 at various wavelengths
to various averages of the light-transmission curves 114, 124, and
134 across the various wavelengths. In some embodiments, curves
114, 124, and 134 of FIG. 1A2 are similar to curves 110, 120, and
130 of FIG. 1A1, except that curves 114, 124, and 134 omit the
yellow absorption band at 580 nm. In some embodiments, curve 134
represents the spectral transmission of a lens 13 embodiment of the
present invention that includes absorption at 500 nanometers, has a
gray tint, and is polarized (also referred to herein as
"500-block-only Gray Polarized"). In some embodiments, curve 124
represents the spectral transmission of a lens 12 embodiment of the
present invention that includes absorption at 500 nanometers and is
not polarized (also referred to herein as "500-block-only No
Polarization"). In some embodiments, curve 114 represents the
spectral transmission of a lens 11 embodiment of the present
invention that includes absorption at 500 nanometers, has a brown
tint, and is polarized (also referred to herein as "500-block-only
Brown Polarized"). In some embodiments, graphs 1112 include
horizontal lines 121, 122, and 123 that illustrate RGB
average-transmission percentages (of the primary red passband, the
primary green passband, and the primary blue passband,
respectively) for the 500-block-only No Polarization lens 12
embodiment of the present invention. In some embodiments, as shown
on graphs 1112, the RGB transmission averages for 500-block-only No
Polarization lens 12 are 36% (primary red passband), 26% (primary
green passband), and 22% (primary blue passband). In some
embodiments, graphs 1112 include curves 111, 112, and 113 that
illustrate RGB average-transmission percentages (of the primary red
passband, the primary green passband, and the primary blue
passband, respectively) for the 500-block-only Brown Polarized lens
11 embodiment of the present invention. In some embodiments, as
shown on graphs 1112, the RGB transmission averages for
500-block-only Brown Polarized are 25% (primary red passband), 15%
(primary green passband), and 9% (primary blue passband). In some
embodiments, graphs 1112 include curves 131, 132, and 133 that
illustrate RGB average-transmission percentages for the
500-block-only Gray Polarized embodiment of the present invention.
In some embodiments, as shown on graphs 1112, the RGB transmission
averages for 500-block-only Gray Polarized are 19% (primary red
passband), 15% (primary green passband), and 17% (primary blue
passband). Horizontal line 117 represents the average transmission
of all wavelengths of light in the range 400 nm to 700 nm through
one embodiment of a brown lens 11 of the present invention (about
18%), horizontal line 127 represents the average transmission of
all wavelengths of light in the range 400 nm to 700 nm through one
embodiment of a PINP lens 12 of the present invention (about 29%),
and horizontal line 137 represents the average transmission of all
wavelengths of light in the range 400 nm to 700 nm through one
embodiment of a gray lens 13 of the present invention (about 17%).
Horizontal line 116 represents 20% times the value of horizontal
line 117 of a brown lens 11, horizontal line 126 represents 20%
times the value of horizontal line 127 of a PINP lens 12, and
horizontal line 136 represents 20% times the value of horizontal
line 137 of a gray lens 13.
[0110] In some embodiments, graphs 1112 include curve 127, which
illustrates the average transmission percentage of 500-block-only
No Polarization across a wavelength range of 400 to 700 nanometers
(i.e., 29%). In some embodiments, graphs 1112 include curve 117,
which illustrates the average transmission percentage of
500-block-only Brown Polarized across a wavelength range of 400 to
700 nanometers (i.e., 18%). In some embodiments, graphs 1112
include curve 137, which illustrates the average transmission
percentage of 500-block-only Gray Polarized across a wavelength
range of 400 to 700 nanometers (i.e., 17%).
[0111] FIG. 1B is a spectral graph 1120 that illustrates
light-transmission curve 88 at various wavelengths. Note here that
there is no cyan absorption band that has a local minimum in the
range of 490 nm to 510 nm; rather there is a severe absorption band
at about 475 nm that block substantial amounts of blue light
between 460 nm and 490 nm. The lens has a wideband transmission
average of about 24% across the range of wavelengths from 380 nm to
700 nm.
[0112] FIG. 1C1 is a spectral graph 1131 that illustrates
light-transmission curve 99 at various wavelengths of a lens
according to a conventional or current 580-only blocking
embodiment. Note here too that there is no cyan absorption band
that has a local minimum in the range of 490 nm to 510 nm. The
yellow enhanced absorption band has a minimum transmission of 3.2%,
and the lens has a wideband transmission average of about 15%
across the range of wavelengths from 380 nm to 700 nm.
[0113] FIG. 1C2 is a set of spectral graphs 1132 that illustrate
details of the spectral graphs set forth in FIG. 1A1. In some
embodiments, the y-axis of graphs 1132 is magnified (compared to
graphs 1111 of FIG. 1A1) to a range of zero (0) to fifty (50)
percent transmission. The horizontal line 128 represents a level of
20% of the value of horizontal line 129 that indicates the average
transmission from 400 nm to 700 nm of lens 12. In some embodiments,
the present invention provides a lens that transmits the
wavelengths in the cyan absorption band of 490 nm to 510 nm at a
level of at least 20% of the average transmission from 400 nm to
700 nm of that lens, and that transmit the wavelengths in the
yellow absorption band of 570 nm to 590 nm at a level of at least
20% of the average transmission from 400 nm to 700 nm of that lens.
In some embodiments, this enhances safety for persons wearing such
sunglasses while driving vehicles because the lens passes enough of
the cyan wavelengths of 490 nm to 510 nm so the user can easily see
"green" traffic signals that use cyan LEDs for illumination, and
the lens passes enough of the yellow wavelengths of 570 nm to 590
nm so the user can easily see amber/yellow traffic signals that use
yellow LEDs for illumination. The various reference numbers in FIG.
1C2 correspond to those same numbers in the description of FIG.
1A1.
[0114] FIG. 1C3 is a set of spectral graphs 1133 that illustrate
details of the spectral graphs set forth in FIG. 1A2. In some
embodiments, the y-axis of graphs 1133 is magnified (compared to
graphs 1112 of FIG. 1A2) to a range of zero (0) to fifty (50)
percent transmission. The various reference numbers in FIG. 1C3
correspond to those same numbers in the description of FIG.
1A2.
[0115] FIG. 1D1 is a spectral graph 1141 that illustrates the
spectral light-transmission curve 130 at various wavelengths in the
range of 380 nm to 780 nm of one embodiment of lens 13 of the
present invention. The various reference numbers in FIG. 1D1
correspond to those same numbers in the description of FIG. 1A1.
Note that the wideband average transmission 169 of lens 13 on this
graph is computed on the wavelength range of 380 nm to 700 nm,
which results in a lower average transmission (15%) as compared to
the FIG. 1A1 and FIG. 1D2 wideband average transmission (16%),
which is computed on the wavelength range of 400 nm to 700 nm.
[0116] Note that transmission curve 130 has a cyan minimum 165 (of
8.5% transmission) in the range 150 of wavelengths from 490 nm to
510 nm, a blue maximum 163 (of 19% transmission) in the 50 nm-wide
range of blue wavelengths from 440 nm to 490 nm, a green maximum
162 (of 16% transmission) in the 50 nm-wide range of green
wavelengths from 520 nm to 570 nm, and that for this embodiment,
the cyan minimum 165 of 8.5% is about 55% of the green maximum 162
(of 16%), which is the smaller of the blue maximum 163 and the
green maximum 162. In other embodiments, the cyan minimum 165 is no
more than (i.e., less than or equal to) 80% of the smaller of the
blue maximum 163 and the green maximum 162. In other embodiments,
the cyan minimum 165 is no more than (i.e., less than or equal to)
70% of the smaller of the blue maximum 163 and the green maximum
162. In other embodiments, the cyan minimum 165 is no more than
(i.e., less than or equal to) 60% of the smaller of the blue
maximum 163 and the green maximum 162. In other embodiments, the
cyan minimum 165 is no more than (i.e., less than or equal to) 50%
of the smaller of the blue maximum 163 and the green maximum 162.
In other embodiments, the cyan minimum 165 is no more than (i.e.,
less than or equal to) 40% of the smaller of the blue maximum 163
and the green maximum 162. In other embodiments, the cyan minimum
165 is no more than (i.e., less than or equal to) 30% of the
smaller of the blue maximum 163 and the green maximum 162. In some
embodiments, the cyan minimum 165 is no less than (i.e., greater
than or equal to) 20% of the 380 nm to 700 nm wideband average
transmission 169 of lens 13.
[0117] In the embodiment shown in FIG. 1D1, the cyan absorption
band dip has a full-width half-minimum 167 (FWHM'; as distinguished
from a full-width half-maximum, or FWHM, of a passband) that is
measured at a level of half way between the cyan minimum 165 and
the smaller of the blue maximum 163 and the green maximum 162. In
this embodiment, the cyan absorption band dip FWHM' 167 is about 22
nm. In some embodiments, the cyan absorption band dip FWHM' 167 is
in a range of about 10 nm to 30 nm; preferably in a range of about
15 nm to 25 nm, more preferably in a range of about 17 nm to 23 nm,
and yet more preferably in a range of about 18 nm to 22 nm.
[0118] Note also that transmission curve 130 has a yellow minimum
164 (of 5.4% transmission) in the range 140 of yellow wavelengths
from 570 nm to 590 nm, a red maximum 166 (of 23% transmission) in
the 50 nm-wide range of blue wavelengths from 600 nm to 650 nm, and
that for this embodiment, the yellow minimum of 5.4% is about 35%
of the green maximum 162 (of 16%), which is the smaller of the red
maximum 166 and the green maximum 162. In other embodiments, the
yellow minimum 164 is no more than (i.e., less than or equal to)
80% of the smaller of the blue maximum 163 and the green maximum
162. In other embodiments, the yellow minimum 164 is no more than
(i.e., less than or equal to) 70% of the smaller of the blue
maximum 163 and the green maximum 162. In other embodiments, the
yellow minimum 164 is no more than (i.e., less than or equal to)
60% of the smaller of the blue maximum 163 and the green maximum
162. In other embodiments, the yellow minimum 164 is no more than
(i.e., less than or equal to) 50% of the smaller of the blue
maximum 163 and the green maximum 162. In other embodiments, the
yellow minimum 164 is no more than (i.e., less than or equal to)
40% of the smaller of the blue maximum 163 and the green maximum
162. In other embodiments, the yellow minimum 164 is no more than
(i.e., less than or equal to) 30% of the smaller of the blue
maximum 163 and the green maximum 162. In some embodiments, the
yellow minimum 164 is no less than (i.e., greater than or equal to)
20% of the 380 nm to 700 nm wideband average transmission 169 of
lens 13.
[0119] In the embodiment shown in FIG. 1D1, the yellow absorption
band dip has a full-width half-minimum 168 (FWHM' 168) that is
measured at a level of half way between the yellow minimum 164 and
the smaller of the red maximum 166 and the green maximum 162. In
this embodiment, the yellow absorption band dip FWHM' 168 is about
18 nm. In some embodiments, the yellow absorption band dip FWHM'
168 is in a range of about 10 nm to 30 nm; preferably in a range of
about 15 nm to 25 nm, more preferably in a range of about 17 nm to
23 nm, and yet more preferably in a range of about 18 nm to 22
nm.
[0120] FIG. 1D2 is a set of spectral graphs 1142 comparing the
spectral light-transmission curve 130 of a gray polarized lens 13
at various wavelengths to various narrowband and wideband averages
of the spectral light-transmission curve 130 across the various
wavelengths. In some embodiments, transmission curve 130 has a blue
passband average transmission 133 (in this case about 17%) for
wavelengths in the 40 nm-wide range 440 nm to 480 nm, a green
passband average transmission 132 (in this case about 15%) for
wavelengths in the 40 nm-wide range 520 nm to 560 nm, and a red
passband average transmission 131 (in this case about 19%) for
wavelengths in the 40 nm-wide range 600 nm to 640 nm. The wideband
average transmission horizontal line 139 (in this case, about 16%)
is measured over the range of wavelengths 400 nm to 700 nm, and the
horizontal line 138 represents 20% of the value 139 (in this case,
about 3.2%).
[0121] In contrast to the absorption-band-width definitions set
forth for FIG. 1D1, FIG. 1D2 provides slightly different
definitions that utilize formulae based on the average passband
transmission values measured over 40-nm-wide passbands that are on
either side of the cyan and yellow absorption bands. In the
embodiment shown in FIG. 1D2, the cyan absorption band dip has a
full-width half-dip 177 (FWHD; as distinguished from FWHM'
described above) that is measured at a level of half way between
the cyan minimum 165, and the smaller of the blue passband average
133 and the green passband average 132. In this embodiment, the
cyan absorption band dip FWHD 167 is about 21 nm. In some
embodiments, the cyan absorption band dip FWHD 177 is in a range of
about 10 nm to 30 nm; preferably in a range of about 15 nm to 25
nm, more preferably in a range of about 17 nm to 23 nm, and yet
more preferably in a range of about 18 nm to 22 nm. In the
embodiment shown in FIG. 1D1, the yellow absorption band dip has a
FWHM' 168 that is measured at a level of half way between the
yellow minimum 164 and the smaller of the red passband average 131
and the green passband average 132. In this embodiment, the yellow
absorption band dip FWHD 178 is about 17 nm. In some embodiments,
the yellow absorption band dip FWHD 168 is in a range of about 10
nm to 30 nm; preferably in a range of about 15 nm to 25 nm, more
preferably in a range of about 17 nm to 23 nm, and yet more
preferably in a range of about 18 nm to 22 nm.
[0122] FIG. 1D3 is a set of spectral graphs 1143 comparing the
spectral light-transmission curve 134 of a gray 500 nm-only lens 13
at various wavelengths to various averages of the spectral
light-transmission curve 134 across the various wavelengths. Curve
134 represents a gray sunglass lens that has a cyan absorption band
but substantially no yellow absorption band (i.e., the light
transmission for any wavelengths in the range of 570 nm to 590 nm
is no less than 90% of the average of the green passband average
transmission 132 for wavelengths in the range 520 nm to 560 nm and
the red passband average transmission 131 for wavelengths in the
range 600 nm to 640 nm. Other than the lack of a yellow absorption
band, curve 134 for gray 500 nm-only lens 13 is substantially the
same as set forth in the description of FIG. 1D2.
[0123] FIG. 1E1 is a spectral graph 1151 that illustrates the
spectral light-transmission curve 120 of a no-polarization lens 12
at various wavelengths according to one embodiment of the present
invention. The various reference numbers in FIG. 1E1 correspond to
those same numbers in the description of FIG. 1A1. Note that the
wideband average transmission 179 of lens 12 on this graph is
computed on the wavelength range of 380 nm to 780 nm, which results
in a higher average transmission (35%) as compared to the FIG. 1A1
and FIG. 1E2 wideband average transmission 129 (27%), which is
computed on the wavelength range of 400 nm to 700 nm.
[0124] Note that transmission curve 120 has a cyan minimum 175 (of
5.7% transmission) in the range 150 of wavelengths from 490 nm to
510 nm, a blue maximum 173 (of .about.30% transmission) in the 50
nm-wide range of blue wavelengths from 440 nm to 490 nm, a green
maximum 172 (of .about.31% transmission) in the 50 nm-wide range of
green wavelengths from 520 nm to 570 nm, and that for this
embodiment, the cyan minimum 175 of 5.7% is about 19% of the green
maximum 172 (of .about.31%), which is the smaller of the blue
maximum 173 and the green maximum 172. In other embodiments, the
cyan minimum 175 is no more than (i.e., less than or equal to) 80%
of the smaller of the blue maximum 173 and the green maximum 172.
In other embodiments, the cyan minimum 175 is no more than (i.e.,
less than or equal to) 70% of the smaller of the blue maximum 173
and the green maximum 172. In other embodiments, the cyan minimum
175 is no more than (i.e., less than or equal to) 60% of the
smaller of the blue maximum 173 and the green maximum 172. In other
embodiments, the cyan minimum 175 is no more than (i.e., less than
or equal to) 50% of the smaller of the blue maximum 173 and the
green maximum 172. In other embodiments, the cyan minimum 175 is no
more than (i.e., less than or equal to) 40% of the smaller of the
blue maximum 173 and the green maximum 172. In other embodiments,
the cyan minimum 175 is no more than (i.e., less than or equal to)
30% of the smaller of the blue maximum 173 and the green maximum
172. In some embodiments, the cyan minimum 175 is no less than
(i.e., greater than or equal to) 20% of the 400 nm to 700 nm
wideband average transmission 129 of lens 12.
[0125] In the embodiment shown in FIG. 1E1, the cyan absorption
band dip FWHD 177 that is measured at a level of half way between
the cyan minimum 165 and the smaller of the blue average 123 and
the green average 122. In this embodiment, the cyan absorption band
dip FWHD 177 is about 27 nm. In some embodiments, the cyan
absorption band dip FWHD 177 is in a range of about 10 nm to 30 nm;
preferably in a range of about 15 nm to 25 nm, more preferably in a
range of about 17 nm to 23 nm, and yet more preferably in a range
of about 18 nm to 22 nm.
[0126] Note also that transmission curve 120 has a yellow minimum
174 (of 4.1% transmission) in the range 140 of yellow wavelengths
from 570 nm to 590 nm, a red maximum 171 (of 47% transmission) in
the 50 nm-wide range of blue wavelengths from 600 nm to 650 nm, and
that for this embodiment, the yellow minimum 174 of 4.1% is about
13% of the green maximum 172 (of .about.31%), which is the smaller
of the red maximum 171 and the green maximum 172. In other
embodiments, the yellow minimum 174 is no more than (i.e., less
than or equal to) 80% of the smaller of the blue maximum 173 and
the green maximum 172. In other embodiments, the yellow minimum 174
is no more than (i.e., less than or equal to) 70% of the smaller of
the blue maximum 173 and the green maximum 172. In other
embodiments, the yellow minimum 174 is no more than (i.e., less
than or equal to) 60% of the smaller of the blue maximum 173 and
the green maximum 172. In other embodiments, the yellow minimum 174
is no more than (i.e., less than or equal to) 50% of the smaller of
the blue maximum 173 and the green maximum 172. In other
embodiments, the yellow minimum 174 is no more than (i.e., less
than or equal to) 40% of the smaller of the blue maximum 173 and
the green maximum 172. In other embodiments, the yellow minimum 174
is no more than (i.e., less than or equal to) 30% of the smaller of
the blue maximum 173 and the green maximum 172. In some
embodiments, the yellow minimum 174 is no less than (i.e., greater
than or equal to) 20% of the 400 nm to 700 nm wideband average
transmission 129 of lens 12.
[0127] In the embodiment shown in FIG. 1E1, the yellow absorption
band FWHD 178 that is measured at a level of half way between the
yellow minimum 174 and the smaller of the red average 121 and the
green average 122. In this embodiment, the yellow absorption band
dip FWHD 178 is about 20 nm. In some embodiments, the yellow
absorption band dip FWHD 178 is in a range of about 10 nm to 30 nm;
preferably in a range of about 15 nm to 25 nm, more preferably in a
range of about 17 nm to 23 nm, and yet more preferably in a range
of about 18 nm to 22 nm.
[0128] FIG. 1E2 is a set of spectral graphs 1152 comparing the
spectral light-transmission curve 120 of a 500 & 580 PINP lens
12 at various wavelengths to various averages of the spectral
light-transmission curve 120 across the various wavelengths. The
various reference numbers in FIG. 1E2 correspond to those same
numbers in the description of FIG. 1A1 and FIG. 1E1. Curve 120
represents a lens 12 that passes more blue and green light than a
polarized lens such as represented by curves 130 and 110 of FIG.
1A1. In some embodiments, the primary red passband average 121 is
about 36% over the red wavelength range 600 nm to 640 nm, the
primary green passband average 122 is about 26% over the green
wavelength range 520 nm to 560 nm, and the primary blue passband
average 123 is about 22% over the blue wavelength range 600 nm to
640 nm. The wideband transmission average 129 (about 27%) is
measured over the visible-light wavelength range 400 nm to 700 nm,
and the horizontal line 128 (at about 5.4%) is 20% times the value
of wideband transmission average 129. In some embodiments, (not
shown here), both the cyan minimum 175 and the yellow minimum 174
are no less than the value 128 (20% times wideband transmission
average 129).
[0129] FIG. 1E3 is a set of spectral graphs 1153 comparing the
spectral light-transmission curve 124 of a 500-block-only PINP lens
12 at various wavelengths to various averages of the spectral
light-transmission curve 124 across the various wavelengths. Curve
124 represents a non-polarized sunglass lens that has a cyan
absorption band but substantially no yellow absorption band (i.e.,
the light transmission for any wavelengths in the range of 570 nm
to 590 nm is no less than 90% of the average of the green passband
average transmission 122 for wavelengths in the range 520 nm to 560
nm and the red passband average transmission 121 for wavelengths in
the range 600 nm to 640 nm. Other than the lack of a yellow
absorption band, curve 124 for PINP 500 nm-only lens 12 is
substantially the same as set forth in the description of FIG.
1E2.
[0130] FIG. 1F1 is a spectral graph 1161 that illustrates the
spectral light-transmission curve 110 for a brown-tint polarized
lens 11 at various wavelengths, according to some embodiments of
the present invention. The various reference numbers in FIG. 1F1
correspond to those same numbers in the description of FIG. 1A1.
Note that the wideband average transmission 189 of lens 11 on this
graph is computed on the wavelength range of 380 nm to 700 nm,
which results in an average transmission (about 16%), which is
lower than the wideband average transmission 119 (about 17%) of
lens 11 on FIG. 1E2 that is computed on the wavelength range of 400
nm to 700 nm.
[0131] Note that transmission curve 110 has a cyan minimum 185 (of
5.9% transmission) in the range 150 of wavelengths from 490 nm to
510 nm, a blue maximum 183 (of .about.10% transmission) in the 50
nm-wide range of blue wavelengths from 440 nm to 490 nm, a green
maximum 182 (of .about.17% transmission) in the 50 nm-wide range of
green wavelengths from 520 nm to 570 nm, and that for this
embodiment, the cyan minimum 185 of 5.9% is about 60% of the blue
maximum 183 (of .about.10%), which is the smaller of the blue
maximum 183 and the green maximum 182. In other embodiments, the
cyan minimum 185 is no more than (i.e., less than or equal to) 80%
of the smaller of the blue maximum 183 and the green maximum 182.
In other embodiments, the cyan minimum 185 is no more than (i.e.,
less than or equal to) 70% of the smaller of the blue maximum 183
and the green maximum 182. In other embodiments, the cyan minimum
185 is no more than (i.e., less than or equal to) 60% of the
smaller of the blue maximum 183 and the green maximum 182. In other
embodiments, the cyan minimum 185 is no more than (i.e., less than
or equal to) 50% of the smaller of the blue maximum 183 and the
green maximum 182. In other embodiments, the cyan minimum 185 is no
more than (i.e., less than or equal to) 40% of the smaller of the
blue maximum 183 and the green maximum 182. In other embodiments,
the cyan minimum 185 is no more than (i.e., less than or equal to)
30% of the smaller of the blue maximum 183 and the green maximum
182. In some embodiments, the cyan minimum 185 is no less than
(i.e., greater than or equal to) 20% of the 400 nm to 700 nm
wideband average transmission 119 of lens 11. In the embodiment
shown in FIG. 1E1, the cyan absorption band dip FWHM' 187 that is
measured at a level of half way between the cyan minimum 165 and
the smaller of the blue average 113 and the green average 112. In
this embodiment, the cyan absorption band dip FWHM' 187 is about 19
nm. In some embodiments, the cyan absorption band dip FWHM' 187 is
in a range of about 10 nm to 30 nm; preferably in a range of about
15 nm to 25 nm, more preferably in a range of about 17 nm to 23 nm,
and yet more preferably in a range of about 18 nm to 22 nm.
[0132] Note also that transmission curve 110 has a yellow minimum
184 (of 7.1% transmission) in the range 140 of yellow wavelengths
from 570 nm to 590 nm, a red maximum 181 (of .about.30%
transmission) in the 50 nm-wide range of blue wavelengths from 600
nm to 650 nm, and that for this embodiment, the yellow minimum 184
of 7.1% is about 42% of the green maximum 182 (of .about.17%),
which is the smaller of the red maximum 181 and the green maximum
182. In other embodiments, the yellow minimum 184 is no more than
(i.e., less than or equal to) 80% of the smaller of the blue
maximum 183 and the green maximum 182. In other embodiments, the
yellow minimum 184 is no more than (i.e., less than or equal to)
70% of the smaller of the blue maximum 183 and the green maximum
182. In other embodiments, the yellow minimum 184 is no more than
(i.e., less than or equal to) 60% of the smaller of the blue
maximum 183 and the green maximum 182. In other embodiments, the
yellow minimum 184 is no more than (i.e., less than or equal to)
50% of the smaller of the blue maximum 183 and the green maximum
182. In other embodiments, the yellow minimum 184 is no more than
(i.e., less than or equal to) 40% of the smaller of the blue
maximum 183 and the green maximum 182. In other embodiments, the
yellow minimum 184 is no more than (i.e., less than or equal to)
30% of the smaller of the blue maximum 183 and the green maximum
182. In some embodiments, the yellow minimum 184 is no less than
(i.e., greater than or equal to) 20% of the 400 nm to 700 nm
wideband average transmission 119 of lens 11.
[0133] In the embodiment shown in FIG. 1F1, the yellow absorption
band FWHM' 188 that is measured at a level of half way between the
yellow minimum 184 and the smaller of the red average 181 and the
green average 182. In this embodiment, the yellow absorption band
dip FWHD 188 is about 18 nm. In some embodiments, the yellow
absorption band dip FWHM' 188 is in a range of about 10 nm to 30
nm; preferably in a range of about 15 nm to 25 nm, more preferably
in a range of about 17 nm to 23 nm, and yet more preferably in a
range of about 18 nm to 22 nm.
[0134] FIG. 1F2 is a set of spectral graphs 1162 comparing the
spectral light-transmission curve 110 at various wavelengths to
various averages of the spectral light-transmission curve 110
across the various wavelengths. The various reference numbers in
FIG. 1F2 correspond to those same numbers in the description of
FIG. 1A1 and FIG. 1F1. Curve 110 represents a brown-tinted lens 11
that passes less blue and more red light than a polarized
gray-tinted lens such as represented by curves 130 of FIG. 1A1. In
some embodiments, the primary red passband average 111 is about 25%
over the red wavelength range 600 nm to 640 nm, the primary green
passband average 112 is about 15% over the green wavelength range
520 nm to 560 nm, and the primary blue passband average 113 is
about 9% over the blue wavelength range 600 nm to 640 nm. The
wideband transmission average 119 (about 17%) is measured over the
visible-light wavelength range 400 nm to 700 nm, and the horizontal
line 118 (at about 3.4%) is 20% times the value of wideband
transmission average 119. In some embodiments, both the cyan
minimum 185 and the yellow minimum 184 are no less than the value
118 (20% times wideband transmission average 119).
[0135] FIG. 1F3 is a set of spectral graphs 1163 comparing the
spectral light-transmission curve 114 of a 500-block-only Brown
lens 11 at various wavelengths to various averages of the spectral
light-transmission curve 114 across the various wavelengths. Curve
114 represents a non-polarized sunglass lens that has a cyan
absorption band but substantially no yellow absorption band (i.e.,
the light transmission for any wavelengths in the range of 570 nm
to 590 nm is no less than 90% of the average of the green passband
average transmission 112 for wavelengths in the range 520 nm to 560
nm and the red passband average transmission 111 for wavelengths in
the range 600 nm to 640 nm. Other than the lack of a yellow
absorption band, curve 114 for 500-block-only Brown lens 11 is
substantially the same as set forth in the description of FIG.
1F2.
[0136] FIG. 1G (representing an assembled lens drawing) is a cross
section view of a two-wafer system 1170 according to some
embodiments of the present invention. In some embodiments, front
wafer 101 and rear wafer 102 are laminated to each face of
polarized film 103 with adhesive layer 104 and adhesive layer 105.
In some embodiments, the concave or convex surface of front wafer
101 includes a mirror coating 106. In some embodiments, the concave
surface of rear wafer 102 includes an optional anti-reflection
coating. Some preferred embodiments include hydrophobic coatings on
the outer surfaces of the assembled lens system. In some
embodiments, it is preferred that the wafer that includes added
oxides to manage the transmittance and absorption of visible light
is used as the rear wafer 102 of the lens system (designated in
FIG. 1A3, FIG. 1A4, FIG. 1A5, and FIG. 1G as rear wafer 102).
[0137] FIG. 2 (showing what is called herein as the tristimulus
curve 210) is a graph 200 of spectral sensitivity versus wavelength
detailing the peak sensitivity curves for color vision. Blue
sensitivity is designated as zone B, green sensitivity is
designated as zone G, and red sensitivity is designated as zone R.
The BG crossover 214 of wavelength-sensitivity curves of the blue
cones and green cones of the human eye occurs at about 500 nm, so
by creating an absorption peak near 500 nm, the present invention
will better separate the distinction between blue and green,
increasing contrast and/or improving the pleasurable perception of
the two colors blue and green. In some embodiments, adding to the
lens an organic dye whose peak absorbance is near 500 nm creates
the functional absorbance peak desired in the present invention.
The GR crossover 215 of wavelength-sensitivity curves of the green
cones and red cones of the human eye occurs at about 580 nm, so by
creating an absorption peak near 580 nm, the present invention will
better separate the distinction between green and red, increasing
contrast and/or improving the pleasurable perception of the two
colors green and red.
[0138] FIG. 3A is a set of spectral graphs 301 comparing the
spectral light-transmission curve 360 and 370 at various
wavelengths of two embodiments of the present invention to
tristimulus curves 211, 212 and 213. In some embodiments, the
embodiment represented by curve 370 allows more shorter-wavelength
blue light at wavelengths 430 nm to 450 nm to pass than the
embodiment of curve 360, but reduces light transmittance at the red
wavelengths 610 nm-700 nm and the IR wavelengths from 700 nm-780
nm. In this and in later figures, the small shaded box below 450 nm
to 460 nm represents the approximate range of peak blue sensitivity
of the human eye, the small shaded box below 550 nm to 560 nm
represents the approximate range of peak green sensitivity of the
human eye, and the small shaded box below 600 nm to 610 nm
represents the approximate range of peak red sensitivity of the
human eye
[0139] FIG. 3B is a set of spectral graphs 302 comparing the
spectral light-transmission curves 340 and 350 at various
wavelengths of two embodiments of the present invention to light
transmission 310 at various wavelengths of a "clear" lens. In some
embodiments, the embodiment represented by curve 340 does not
include a polarizing film and allows much more blue light at
wavelengths 430 nm to 460 nm, much more green light at wavelengths
530 nm to 560 nm and much more red light at wavelengths 600 nm to
700 nm to pass than the embodiment of curve 350 which does include
a polarizing film, but reduces light in the IR wavelengths from 740
nm-770 nm.
[0140] FIG. 3C is a set of spectral graphs 303 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 321 at
various wavelengths of a lens according to Farwig's U.S. Pat. No.
7,597,441. The Farwig lens has a sharp cut on at about 380 nm and
jumps to about 42% transmission at 400 nm, as detailed by the
rectangular box 322, while at 430 nm the transmission 323 further
jumps to 64%. These two spectral data points are significantly
higher than the embodiment of the current invention set forth by
spectral light-transmission curve 330. This U.S. Pat. No. 7,597,441
utilizes praseodymium to control the spectral transmission between
420 nm and 460 nm, while this embodiment of the current invention
set forth by spectral light-transmission curve 330 does not require
this praseodymium to create a continued increase of light
transmission from about 430 nm to about 460 nm.
[0141] In some embodiments, the present invention provides nearly
complete blocking of light having wavelengths in the range 400
nm-420 nm, inclusive (e.g., in some embodiments, the average
transmittance of wavelengths in the range 400 nm-420 nm shown by
box 332 is less than 10% of the average visible transmittance of
the assembled lens (i.e., average transmittance over wavelengths
400 nm-700 nm)). In some embodiments, the present invention
provides substantial blocking of light having wavelengths in the
range 420 nm-430 nm, inclusive (e.g., in some embodiments, the
average transmittance of wavelengths in the range 420 nm-430 nm
shown by box 333 is less than 20% of the average visible
transmittance of the assembled lens (i.e., average transmittance
over wavelengths 400 nm-700 nm)). In some embodiments, the present
invention provides a partial reduction of transmission of light
having wavelengths in the range 480 nm-510 nm, inclusive (e.g., in
some embodiments, the average transmittance of wavelengths in the
range 480 nm-510 nm shown by box 335 is less than the average
transmittance of wavelengths in the range 450 nm-470 nm shown by
box 334 and between 10% and 85% of the average visible
transmittance of the assembled lens (i.e., average transmittance
over wavelengths 400 nm-700 nm)). In some other embodiments, the
average transmittance of wavelengths in the range 480 nm-510 nm
shown by box 335 is less than the average transmittance of
wavelengths in the range 440 nm-470 nm (a larger range of
wavelengths than shown by box 334) and between 20% and 85% of the
average visible transmittance of the assembled lens (i.e., average
transmittance over wavelengths 400 nm-700 nm). In some other
embodiments, the average transmittance of wavelengths in the range
490 nm-510 nm (a smaller range of wavelengths than shown by box
335) is less than the average transmittance of wavelengths in the
range 440 nm-470 nm (a larger range of wavelengths than shown by
box 334) and between 10% and 85% of the average visible
transmittance of the assembled lens (i.e., average transmittance
over wavelengths 400 nm-700 nm). In some embodiments, the present
invention provides a partial reduction of transmission of light
having wavelengths in the range 570 nm-590 nm, inclusive (e.g., in
some embodiments, the average transmittance of wavelengths in the
range 570 nm-590 nm shown by box 337 is less than the average
transmittance of wavelengths in the range 530 nm-560 nm shown by
box 336 and between 10% and 85% of the average visible
transmittance of the assembled lens (i.e., average transmittance
over wavelengths 400 nm-700 nm)).
[0142] FIG. 4 is a set of spectral graphs 400 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 421 at
various wavelengths of a lens according to Tsutsumi's U.S. Pat. No.
6,773,816. The set of spectral graphs 400 detail in particular the
disparity of spectral readings between 380 nm and 525 nm. The
Tsutsumi graph 421 details light transmission of a lens of 2.2-mm
thickness and 1.5-mm thickness. The 2.2-mm-thick lens has a
spectral reading of about 0% at 400 nm but when reducing the
thickness of this lens to 1.5 mm, the transmission jumps to 70%. At
a wavelength of 430 nm, the lens according to Tsutsumi U.S. Pat.
No. 6,773,816 is 1.5-mm-thick lens that has 23% transmission while
the 2.2 mm thick lens has a transmission of 2.5%. The Tsutsumi lens
does not address zone BG (the absorption band at about 500 nm
between blue and green according to the present invention) and has
no absorption peak as required by the tristimulus values for some
embodiments of the present invention.
[0143] FIG. 5 is a set of spectral graphs 500 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 521 at
various wavelengths of a lens according to Larson's U.S. Pat. No.
6,604,824. The two improvements of this embodiment 330 of current
invention over Larson U.S. Pat. No. 6,604,824 include the optional
increased absorption from 410 nm through 440 nm. In Larson U.S.
Pat. No. 6,604,824 there is no discussion addressing wavelengths in
this region. Further, the second improvement in the present
invention illustrated by curve 330 is an absorption peak found
between 480 and 510 nm. This improvement creates a lower
transmittance at 500 nm than at 450 nm, which is contrary to the
teaching of Larson '824. In some embodiments, the way this is
achieved is by adding organic dyes to either the polarized film or
the adhesive or both. Two such dyes used in some embodiments are
Exciton ABS 419 (a narrow-band visible light absorber available
from Exiton, P.O. Box 31126, Dayton, Ohio, 45437 USA, or at
www.exciton.com) or Orcosolve Chinoline (a light absorber available
from Orco, 65 Valley Street, East Providence, R.I., 02914 USA or at
www.organicdye.com/dyes/solvent-dyes). The second improvement in
the present invention is the absorption peak created between 470 nm
and 510 nm, (see the rectangle box 532 of FIGS. 5 and 532 and 1032
of FIG. 10A outlining the spectral section). Box 533 shows the
absorption band centered at about 580 nm according to some
embodiments of the present invention that matches that of Larson
U.S. Pat. No. 6,604,824. In some embodiments, by adding an organic
dye such as Exciton's P491 to the adhesive, this absorption peak is
achieved.
[0144] FIG. 6 is the set of spectral graphs 600 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 621 at
various wavelengths of a lens according to Fung's U.S. Pat. No.
7,372,640. Fung U.S. Pat. No. 7,372,640 describes similar or the
same oxides in one of its wafers as this current invention's glass
wafer. Both wafers will absorb light at short wavelengths from less
than 400 nm and up to 415 nm. In some embodiments, the current
invention adds an organic dye to increase absorbance in the range
from 400 nm to 440 nm, which is not described by Fung. The second
difference between Fung U.S. Pat. No. 7,372,640 and this current
invention is the absorbance peak in the present invention between
470 nm and 510 nm (i.e., wavelengths in the range shown by box 532
of FIG. 5). Fung's U.S. Pat. No. 7,372,640 is not concerned with
this spectral range and in fact when viewing FIG. 6, the
transmittance a lens according to of Fung's U.S. Pat. No.
7,372,640, the transmittance of Fung's lens system and embodiments
of present invention are reversed between 480 nm and 510 nm.
[0145] FIG. 7 is the set of spectral graphs 700 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 721 at
various wavelengths of a lens according to U.S. Pat. No. 6,145,984
describes three maximum transmittal peaks and two minimum
transmittal peaks. The specific zones for the three maximum peaks
are said to be between 420 nm and 460 nm, 480 nm and 520 nm, 610 nm
and 650 nm. The minimum transmittal peak zones are said to be
between 460 nm and 480 nm, 520 nm and 610 nm. The wavelength range
from 300 nm to 420 nm is not addressed. The obvious difference
between the current invention and MJ 984 is the current inventions
from 480 nm to 510 nm have a minimum transmittance between 20% and
90% of the luminous transmission of the assembled lens system. U.S.
Pat. No. 6,145,984 shows a maximum peak transmission in this same
zone of at least 125% of the luminous transmission of the assembled
lens system.
[0146] FIG. 8 is the set of spectral graphs 800 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 821 at
various wavelengths of a lens according to a typical sunglass lens.
This embodiment 330 of the current invention has three specific
zones of reduced transmission (depression) as compared to the
typical sunglass lens: the first is for wavelengths between 400 nm
and 430 nm, the second is for wavelengths at about 500 nm, and the
third is for wavelengths at about 580 nm.
[0147] FIG. 9 is the set of spectral graphs 900 comparing the
spectral light-transmission curve 330 at various wavelengths of one
embodiment of the present invention to light transmission 930 at
various wavelengths of a sunglass lens according to a sunglass lens
according to another embodiment of the present invention details
the corresponding transmittance peaks and absorbance peaks between
the tristimulus values and this current invention.
[0148] FIG. 10A is a set of graphs 1001 that compares the sets of
absorption and transmittance bands of various embodiments of the
current invention, including sets 1031, 1032, 1033, 1034, and 1035,
to the tristimulus values 1010 and to the absorption and
transmittance bands 1021 of U.S. Pat. No. 6,145,984.
[0149] In some embodiments, each of these sets 1031, 1032, 1033,
1034, and 1035 of absorption and transmittance bands include an
optional stop band 1099, shown in lighter shading) that blocks some
or all of the light having infrared wavelengths between 700 nm and
800 nm (i.e., in some embodiments, optional stop band 1099 has a
shortest-wavelength cut-on wavelength between about 700 nm and 800
nm and a longest-blocked wavelength that is longer than the
shortest-wavelength cut-on wavelength).
[0150] In some embodiments, each of the cyan reduction bands (1040
or 1044) of FIG. 10A transmits substantially all wavelengths
between 480 nm and 515 nm, in an amount of at least about 10% of
the average transmittance of the lens at all wavelengths between
400 nm and 700 nm, and each of the yellow reduction bands (1050 or
1054) of FIG. 10A transmits substantially all wavelengths between
570 nm and 590 nm, in an amount of at least about 10% of the
average transmittance of the lens at all wavelengths between 400 nm
and 700 nm. In some embodiments, the set 1031 of absorption and
transmittance bands includes a violet-stop band 1022 that blocks at
least 95% of all wavelengths between 400 nm and 420 nm (relative to
the average lens transmission of wavelengths between 400 nm and 700
nm), a cyan-reduction band 1040 that blocks at least 50% but less
than 75% of all wavelengths between 480 nm and 515 nm (relative to
the average lens transmission of wavelengths between 400 nm and 700
nm), and a yellow-reduction band 1050 that blocks at least 75% but
less than 95% of all wavelengths between 570 nm and 590 nm
(relative to the average lens transmission of wavelengths between
400 nm and 700 nm). (In the following paragraphs describing the
absorption bands shown in FIG. 10A, FIG. 10B, FIG. 10C, and FIG.
10D, the description of the percentage blocked in each subband is a
percentage relative to the average lens transmission of all
wavelengths between 400 nm and 700 nm.)
[0151] In some embodiments, the set 1032 of absorption and
transmittance bands includes a violet-stop band 1022 that blocks at
least 95% of all wavelengths between 400 nm and 430 nm, a
cyan-reduction band 1040 that blocks at least 50% but less than 75%
of all wavelengths between 480 nm and 515 nm, and a
yellow-reduction band 1050 that blocks at least 75% but less than
95% of all wavelengths between 570 nm and 590 nm.
[0152] In some embodiments, the set 1033 of absorption and
transmittance bands includes a violet-stop band 1023 that blocks at
least 95% of all wavelengths between 400 nm and 440 nm, a
cyan-reduction band 1040 that blocks at least 50% but less than 75%
of all wavelengths between 480 nm and 515 nm, and a
yellow-reduction band 1050 that blocks at least 75% but less than
95% of all wavelengths between 570 nm and 590 nm.
[0153] In some embodiments, the set 1034 of absorption and
transmittance bands includes a violet-stop-and-reduction band 1024
that blocks at least 95% of all wavelengths between 400 nm and 420
nm, at least 75% but less than 95% of all wavelengths between 420
nm and 430 nm, at least 50% but less than 75% of all wavelengths
between 430 nm and 440 nm, and at least 25% but less than 50% of
all wavelengths between 440 nm and 450 nm, a cyan-reduction band
1044 that blocks at least 75% but less than 95% of all wavelengths
between 490 nm and 510 nm and at least 25% but less than 50% of all
wavelengths between 480 nm and 515 nm, and a yellow-reduction band
1054 that blocks at least 75% but less than 95% of all wavelengths
between 580 nm and 590 nm and at least 25% but less than 50% of all
wavelengths between 570 nm and 600 nm.
[0154] In some embodiments, the set 1035 of absorption and
transmittance bands includes a violet-stop-and-reduction band 1025
that blocks at least 95% of all wavelengths between 400 nm and 425
nm, at least 75% but less than 95% of all wavelengths between 425
nm and 435 nm, at least 50% but less than 75% of all wavelengths
between 435 nm and 440 nm, and at least 25% but less than 50% of
all wavelengths between 440 nm and 450 nm, a cyan-reduction band
1044 that blocks at least 75% but less than 95% of all wavelengths
between 490 nm and 510 nm and at least 25% but less than 50% of all
wavelengths between 480 nm and 515 nm, and a yellow-reduction band
1054 that blocks at least 75% but less than 95% of all wavelengths
between 580 nm and 590 nm and at least 25% but less than 50% of all
wavelengths between 570 nm and 600 nm.
[0155] FIG. 10B is a set of graphs 1002 that compare the sets 1036,
1037, 1038, 1039, and 1040 of absorption and transmittance bands of
various embodiments of the current invention to the tristimulus
values 1010.
[0156] In some embodiments, the set 1036 of absorption and
transmittance bands includes a cyan-reduction band 1044 that blocks
at least 75% but less than 95% of all wavelengths between 490 nm
and 510 nm and at least 25% but less than 50% of all wavelengths
between 480 nm and 515 nm, and a yellow-reduction band 1054 that
blocks at least 75% but less than 95% of all wavelengths between
570 nm and 590 nm and at least 25% but less than 50% of all
wavelengths between 570 nm and 600 nm (this embodiment omits the
violet-stop-and/or-reduction band).
[0157] In some embodiments, the set 1037 of absorption and
transmittance bands includes a violet-stop band 1026 that blocks at
least 95% of all wavelengths between 400 nm and 440 nm, a
cyan-reduction band 1045 that blocks at least 75% but less than 95%
of all wavelengths between 490 nm and 510 nm, at least 50% but less
than 75% of all wavelengths between 480 nm and 490 nm, and at least
25% but less than 50% of all wavelengths between 510 nm and 515 nm,
and a yellow-reduction band 1054 that blocks at least 75% but less
than 95% of all wavelengths between 580 nm and 590 nm and at least
25% but less than 50% of all wavelengths between 570 nm and 600
nm.
[0158] In some embodiments, the set 1038 of absorption and
transmittance bands includes a violet-stop-and-reduction band 1027
that blocks at least 95% of all wavelengths between 400 nm and 420
nm, at least 75% but less than 95% of all wavelengths between 420
nm and 430 nm, at least 50% but less than 75% of all wavelengths
between 430 nm and 440 nm, and at least 25% but less than 50% of
all wavelengths between 440 nm and 450 nm, a cyan-reduction band
1046 that blocks at least 75% but less than 95% of all wavelengths
between 490 nm and 510 nm, and at least 25% but less than 50% of
all wavelengths between 480 nm and 515 nm, and a yellow-reduction
band 1054 that blocks at least 75% of all wavelengths between 580
nm and 590 nm and at least 25% but less than 50% of all wavelengths
between 570 nm and 600 nm.
[0159] In some embodiments, the set 1039 of absorption and
transmittance bands includes a violet-stop-and-reduction band 1027
that blocks at least 95% of all wavelengths between 400 nm and 425
nm, at least 75% but less than 95% of all wavelengths between 425
nm and 435 nm, at least 50% but less than 75% of all wavelengths
between 435 nm and 440 nm, and at least 25% but less than 50% of
all wavelengths between 440 nm and 450 nm, a cyan-reduction band
1046 that blocks at least 75% but less than 95% of all wavelengths
between 490 nm and 510 nm, and at least 25% but less than 50% of
all wavelengths between 480 nm and 515 nm, and a yellow-reduction
band 1054 that blocks at least 75% but less than 95% of all
wavelengths between 580 nm and 590 nm and at least 25% but less
than 50% of all wavelengths between 570 nm and 600 nm.
[0160] In some embodiments, the set 1040 of absorption and
transmittance bands includes a violet-stop-and-reduction band 1027
that blocks at least 95% of all wavelengths between 400 nm and 430
nm, at least 75% but less than 95% of all wavelengths between 430
nm and 440 nm, and at least 25% but less than 50% of all
wavelengths between 440 nm and 450 nm, a cyan-reduction band 1046
that blocks at least 75% but less than 95% of all wavelengths
between 490 nm and 510 nm, and at least 25% but less than 50% of
all wavelengths between 480 nm and 515 nm, and a yellow-reduction
band 1047 that blocks at least 75% but less than 95% of all
wavelengths between 580 nm and 590 nm.
[0161] FIG. 10C is a set of graphs 1003 that compare various
optional absorption subbands of various embodiments of the current
invention to the tristimulus values 1010.
[0162] FIG. 10D is a set of graphs 1004 that compare various
optional absorption subbands of various embodiments of the current
invention to the tristimulus values 1010.
[0163] For the various optional absorption subbands shown in FIGS.
10C and 10D, some embodiments choose one variation from each of the
four columns, and thus use: [0164] one of the
violet-stop-and-reduction bands (1011, 1012, 1013, 1014, or 1015 of
FIG. 10C, or 1010 (i.e., an embodiment that does not substantially
block (i.e., less than 25% blockage) light having wavelengths
between 400 nm and 450 nm), 1016, 1017, 1018, or 1019 of FIG. 10D);
[0165] one of the cyan-reduction bands (1061, 1062, 1063, 1064, or
1065 of FIG. 10C, or 1060 (i.e., an embodiment that does not
substantially block (i.e., less than 25% blockage) light having
wavelengths between 480 nm and 520 nm), 1066, 1067, 1068, or 1069
of FIG. 10D); [0166] one of the yellow-reduction bands (1071, 1072,
1073, 1074, or 1075 of FIG. 10C, or 1070 (i.e., an embodiment that
does not substantially block (i.e., less than 25% blockage) light
having wavelengths between 560 nm and 600 nm), 1076, 1077, 1078, or
1079 of FIG. 10D); and [0167] one of the
long-wavelength-red-reduction-or-blocking bands (1081, 1082, 1083,
1084, or 1085 of FIG. 10C, or 1080 (i.e., an embodiment that does
not substantially block (i.e., less than 25% blockage) light having
wavelengths between 640 nm and 700 nm), 1086, 1087, 1088, or 1089
of FIG. 10D).
[0168] In some embodiments (see FIG. 10C), violet-stop band 1011
blocks at least 95% of light having wavelengths between 390 nm and
400 nm; violet-stop band 1012 blocks at least 95% of light having
wavelengths between 390 nm and 410 nm; violet-stop band 1013 blocks
at least 95% of light having wavelengths between 390 nm and 420 nm;
violet-stop-and-reduction band 1014 blocks at least 95% of light
having wavelengths between 390 nm and 420 nm and at least 75% but
less than 95% of light having wavelengths between 420 nm and 430
nm; and violet-stop-and-reduction band 1015 blocks at least 95% of
light having wavelengths between 390 nm and 420 nm and at least 75%
but less than 95% of light having wavelengths between 420 nm and
440 nm.
[0169] In some embodiments (see FIG. 10D), violet-passing band 1010
is an embodiment that does not substantially block (i.e., less than
25% blockage) light having wavelengths between 400 nm and 450 nm);
violet-stop-and-reduction band 1016 blocks at least 95% of light
having wavelengths between 390 nm and 410 nm and at least 75% but
less than 95% of light having wavelengths between 410 nm and 420 nm
and at least 50% but less than 75% of light having wavelengths
between 420 nm and 430 nm; violet-stop-and-reduction band 1017
blocks at least 95% of light having wavelengths between 390 nm and
410 nm and at least 75% but less than 95% of light having
wavelengths between 410 nm and 420 nm and at least 50% but less
than 75% of light having wavelengths between 420 nm and 425 nm and
at least 25% but less than 50% of light having wavelengths between
425 nm and 435 nm; violet-stop-and-reduction band 1018 blocks at
least 95% of light having wavelengths between 390 nm and 410 nm and
at least 50% but less than 75% of light having wavelengths between
410 nm and 420 nm and at least 25% but less than 50% of light
having wavelengths between 420 nm and 430 nm; and
violet-stop-and-reduction band 1019 blocks at least 95% of light
having wavelengths between 390 nm and 420 nm and at least 25% but
less than 50% of light having wavelengths between 420 nm and 430
nm.
[0170] In some embodiments (see FIG. 10C), cyan-reduction band 1061
blocks at least 75% but less than 95% of light having wavelengths
between 485 nm and 505 nm, cyan-reduction band 1062 blocks at least
75% but less than 95% of light having wavelengths between 490 nm
and 510 nm, cyan-reduction band 1063 blocks at least 75% but less
than 95% of light having wavelengths between 495 nm and 515 nm,
cyan-reduction band 1064 blocks at least 75% but less than 95% of
light having wavelengths between 500 nm and 520 nm, and
cyan-reduction band 1065 blocks at least 75% but less than 95% of
light having wavelengths between 495 nm and 510 nm.
[0171] In some embodiments (see FIG. 10D), cyan-passing band 1060
is an embodiment that does not substantially block (i.e., less than
25% blockage) light having wavelengths between 480 nm and 520 nm);
cyan-reduction band 1066 blocks at least 75% but less than 95% of
light having wavelengths between 485 nm and 505 nm and at least 25%
but less than 50% of light having wavelengths between 480 nm and
510 nm; cyan-reduction band 1067 blocks at least 75% but less than
95% of light having wavelengths between 490 nm and 510 nm and at
least 25% but less than 50% of light having wavelengths between 485
nm and 515 nm; cyan-reduction band 1068 blocks at least 75% but
less than 95% of light having wavelengths between 495 nm and 515 nm
and at least 25% but less than 50% of light having wavelengths
between 490 nm and 520 nm; and cyan-reduction band 1069 blocks at
least 75% but less than 95% of light having wavelengths between 495
nm and 510 nm and at least 25% but less than 50% of light having
wavelengths between 490 nm and 515 nm.
[0172] In some embodiments (see FIG. 10C), yellow-reduction band
1071 blocks at least 75% but less than 95% of light having
wavelengths between 565 nm and 585 nm; yellow-reduction band 1072
blocks at least 75% but less than 95% of light having wavelengths
between 570 nm and 590 nm; yellow-reduction band 1073 blocks at
least 75% but less than 95% of light having wavelengths between 575
nm and 595 nm; yellow-reduction band 1074 blocks at least 75% but
less than 95% of light having wavelengths between 580 nm and 600
nm; and yellow-reduction band 1075 blocks at least 75% but less
than 95% of light having wavelengths between 575 nm and 590 nm.
[0173] In some embodiments (see FIG. 10D), yellow-passing band 1070
is an embodiment that does not substantially block (i.e., less than
25% blockage) light having wavelengths between 560 nm and 600 nm;
yellow-reduction band 1076 blocks at least 75% but less than 95% of
light having wavelengths between 565 nm and 585 nm and at least 25%
but less than 50% of light having wavelengths between 560 nm and
590 nm; yellow-reduction band 1077 blocks at least 75% but less
than 95% of light having wavelengths between 570 nm and 590 nm and
at least 25% but less than 50% of light having wavelengths between
565 nm and 595 nm; yellow-reduction band 1078 blocks at least 75%
but less than 95% of light having wavelengths between 575 nm and
595 nm and at least 25% but less than 50% of light having
wavelengths between 570 nm and 600 nm; and yellow-reduction band
1079 blocks at least 75% but less than 95% of light having
wavelengths between 575 nm and 590 nm and at least 25% but less
than 50% of light having wavelengths between 570 nm and 595 nm.
[0174] In some embodiments (see FIG. 10C),
long-wavelength-red-blocking band 1081 blocks at least 95% of light
having wavelengths between 700 nm and 800 nm;
long-wavelength-red-blocking band 1082 blocks at least 95% of light
having wavelengths between 690 nm and 800 nm;
long-wavelength-red-blocking band 1083 blocks at least 95% of light
having wavelengths between 680 nm and 800 nm;
long-wavelength-red-blocking-and-reduction band 1084 blocks at
least 95% of light having wavelengths between 680 nm and 800 nm and
at least 75% but less than 95% of light having wavelengths between
670 nm and 680 nm; and long-wavelength-red-blocking-and-reduction
band 1085 blocks at least 95% of light having wavelengths between
680 nm and 800 nm and at least 75% but less than 95% of light
having wavelengths between 660 nm and 680 nm.
[0175] In some embodiments (see FIG. 10D),
long-wavelength-red-passing band 1080 is an embodiment that does
not substantially block (i.e., less than 25% blockage) light having
wavelengths between 640 nm and 705 nm);
long-wavelength-red-blocking-and-reduction band 1086 blocks at
least 95% of light having wavelengths between 690 nm and 800 nm and
at least 75% but less than 95% of light having wavelengths between
680 nm and 690 nm and at least 50% but less than 75% of light
having wavelengths between 670 nm and 680 nm;
long-wavelength-red-blocking-and-reduction band 1087 blocks at
least 95% of light having wavelengths between 680 nm and 800 nm and
at least 75% but less than 95% of light having wavelengths between
670 nm and 680 nm and at least 50% but less than 75% of light
having wavelengths between 665 nm and 670 nm and at least 25% but
less than 50% of light having wavelengths between 655 nm and 660
nm; long-wavelength-red-blocking-and-reduction band 1088 blocks at
least 95% of light having wavelengths between 680 nm and 800 nm and
at least 50% but less than 75% of light having wavelengths between
665 nm and 680 nm; and long-wavelength-red-blocking-and-reduction
band 1089 blocks at least 95% of light having wavelengths between
685 nm and 800 nm and at least 25% but less than 50% of light
having wavelengths between 670 nm and 685 nm.
[0176] FIG. 11 is a set of graphs 1100 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1121 of U.S. Pat. No.
6,773,816.
[0177] FIG. 12 is a set of graphs 1200 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1221 of U.S. Pat. No.
7,597,640.
[0178] FIG. 13 is a set of graphs 1300 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1321 of U.S. Pat. No.
7,597,441.
[0179] FIG. 14 is a set of graphs 1400 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1421 of U.S. Pat. No.
8,210,678.
[0180] FIG. 15A is a set of graphs 1501 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1521 of U.S. Pat. No.
7,506,977.
[0181] FIG. 15B is a set of graphs 1502 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1522 of U.S. Pat. No.
8,770,749.
[0182] FIG. 15C is a set of graphs 1503 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1523 of U.S. Pat. No.
8,733,929.
[0183] FIG. 15D is a set of graphs 1504 that compares both the
absorption and transmittance bands 1030 of the current invention to
the tristimulus values 1010 and to the bands 1524 of U.S. Pat. No.
6,604,824.
[0184] FIG. 15E is a set of graphs 1506 that compares both the
absorption and transmittance bands 1031 of the current invention to
the tristimulus values 1010 and to the bands 1525 of U.S. Patent
Application Publication 2013/0141693.
[0185] In some embodiments, the present invention includes a
multi-layered sunglass lens 1170 as detailed by the cross-sectional
view of FIG. 1G. The two glass wafers, referred to as front wafer
101 and back, or rear, wafer 102, are laminated together with a
polarizing filter layer 103 in between. In some embodiments, the
lamination is secured by adhesive layers 104 and 105. In other
embodiments (not shown here) the lamination is achieved by fusing
the polarizing filter layer 103 directly to the glass wafer using,
for example, heat and a vacuum. One preferred embodiment has the
option of a mirror coating 106 placed on either the convex (outer)
surface of front wafer 101 or the concave (inner) surface of front
wafer 101. Additionally, one preferred embodiment has an
anti-reflection coating 107 with a top hydrophobic layer 109. In
some embodiments, a top hydrophobic layer 108 is applied to the
convex surface of optional mirror coating 106, or if no mirror
coating 106 is used on the convex (outer) surface of front wafer
101, then to the convex surface of front wafer 101.
[0186] The luminous transmittance of this lens is preferred to be
12%, but some embodiments have transmission in a range of 8% to
35%. When discussing spectral transmittance of lenses, this
specification refers to the standards provided by ANSI Z80.3-2009
4.6.3.2 and ISO 12312-1 2013 5.3.2.2 and 5.3.2.3. In some
embodiments, the measurements are made in accordance to CIE
illuminant D65. As used herein, "average visible transmittance of a
lens" is defined as the average light transmittance of the lens to
all wavelengths in the range of 400 nm to 700 nm, inclusive.
[0187] The lens system found in FIG. 1 includes two glass wafers of
preferred thicknesses between 0.8 mm and 1.0 mm. One preferred
embodiment of the lens system shown in FIG. 1 uses ophthalmic-grade
glass wafers and is assembled by well-known processes and
specifications found in the sunglass market. The two-wafer system
is preferred as the rear wafer 102 can have varied thicknesses to
induce prism on the horizontal axis in order to off-set the optical
center of the lens. In the sunglass industry this is typically
known as de-centering the lens. The typical thickness variance
within rear wafer 102 is about 0.8 mm to 1.2 mm. In some
embodiments, the front wafer 101 has an even thickness, which is
typically about 1.0 mm thick. The preferred luminous transmittance
of the embodiments of rear wafer 102 that use oxide additives is
about 65%. In some embodiments, it is preferred that the
wavelength-selective light-absorbing oxide additives are in rear
wafer 102. Both the Farwig U.S. Pat. No. 7,597,441 and Tsutsumi
U.S. Pat. No. 6,773,816 include a lanthanide oxide called
praseodymium for coloration and wavelength-selective attenuation
between 420 nm and 440 nm. Farwig U.S. Pat. No. 7,597,441 describes
0.25 to 1.75 mole percent praseodymium, while Tsutsumi U.S. Pat.
No. 6,773,816 describes a range of 3:1 to 1:1 ratio of neodymium to
praseodymium, and Fung patent describes 3% praseodymium. In some
embodiments, the current invention uses less than 0.0005%
praseodymium by mole and over 2% neodymium by mole which gives a
ratio of neodymium to praseodymium far more than 3:1; the ratio of
neodymium to praseodymium in this embodiment of the present
invention will be in the range of about 2000:1, which is far
greater than the Tsutsumi U.S. Pat. No. 6,773,816 describes.
[0188] In one preferred embodiment, glass rear wafer 102 includes
the following functional oxides: copper oxide at about 0.50% by
mole, titanium oxides at about 0.16% by mole, praseodymium oxide at
about 0.0004% by mole, and neodymium oxide at about 2.15% by mole.
In some embodiments, the fusion of oxides and in addition to other
oxides that are typically used in making ophthalmic glass lenses
have a luminous transmission of about 65%, but in other
embodiments, the present invention provides a luminous transmission
in a range of 50% to 80%.
[0189] The functional oxides of the preferred embodiment do not
complete the desired spectral curve 330 as shown in FIG. 8. In some
embodiments, organic dyes are added in order to create the desired
spectral curve. In some embodiments, organic dyes are added to the
adhesive layer(s), to the polarizing film layer, or to both the
adhesive layer(s) and the polarizing film layer. Organic dyes are
typically available in a powder form and, in some embodiments, are
diluted by 20 ppm in glycol ether. In some embodiments, an organic
dye such as Exciton ABS 549 or Orco's Chinoline and Exciton's P 491
is used. In some embodiments, the quantity needed for ABS 549 is
about 0.1 milligram per lens, and for P 491, about 0.05 milligram
per lens. In some embodiments, the luminous transmittance of the
organic dye mixture is about 95%, but in other embodiments, is in
the range from 90% to 99%, inclusive.
[0190] Polyvinyl alcohol (PVA) is the sunglass-industry standard in
material used to produce polarizing film for sunglasses. In some
embodiments, the PVA film used for making polarized film for
sunglasses of the present invention is quite thin and has a high
transmission to visible light, ideally about 45% for some
embodiments of the present invention. In some embodiments, dyeing
PVA film requires rolling it into a dye tank to dye the polymers
within the film. The most commonly used dyes are iodine and
dichroic dyes. The density of dye is important to the polarization
co-efficiency of the film. Once the PVA film is dyed it is
stretched at least five-fold (5-fold) for polarization. In some
embodiments, before stretching, the PVA polymers are oriented in a
random way within the film. Once stretched, the PVA polymers are
aligned in a single direction. In some embodiments, the organic
dyes used for some embodiments of this current invention are added
to the dye bath. To do this, the required dyes are mixed in their
powder form, diluted, and added to the dye bath to a ratio
appropriate to accommodate the desired spectral curve. There is
considerable prior art for this process, including but not limited
to U.S. Pat. Nos. 3,300,436 and 6,113,811. In some embodiments, the
luminous transmittance of the polarized fill for the present
invention is about 45%, but in other embodiments, can have a range
of between 30% and 60%, inclusive.
[0191] When referencing "polarized filter coatings" that can be
used on this current invention, some embodiments of the present
invention use a process such as that detailed in U.S. Pat. No.
7,044,599.
[0192] In some embodiments, the present invention uses plastic
lenses that include organic narrow-band absorbing dyes to block UV
and certain specific bands of visible light in order to replicate
the transmittance properties of the rare-earth oxides used in glass
embodiments of the present invention. In some embodiments, organic
dyes are used in molded thermoplastic polyurethane lenses of the
present invention, while in other embodiments, other narrow-band
dyes are used for molded thermoplastic polycarbonate lenses of the
present invention. Adding dyes to plastic materials can be achieved
through several options, including but not limited to:
[0193] 1. Adding the functional dyes to the thermoplastic material
before injection or casting;
[0194] 2. Using a two-lens system and including the dyes in the
adhesive layer that bonds the two lenses together;
[0195] 3. Imbibing, which is the process of using heat to draw the
organic dyes into the lens itself; and/or
[0196] 4. Trans-Bonding.TM. to put the dyes on the lens
surface.
[0197] Typical conventional polarized sunglass lenses have
relatively flat spectral curves as seen in FIG. 8. In such
conventional polarized sunglass lenses, there is no relationship to
the tristimulus values. In some embodiments, the current invention
adds functional oxides and/or organic dyes, while other embodiments
optionally use only organic dyes that absorb specific wavelengths
of light and structure the spectral curve to more closely simulate
the tristimulus values.
[0198] 1. Some embodiments of the present invention reduce spectral
transmittance at certain wavelengths by creating an absorption peak
before the peak sensitivity of the cones used for seeing the color
blue at about 450 nm (i.e., absorption in wavelengths shorter than
about 450 nm). In one preferred embodiment, rear glass wafer 102 is
used for the preferred functional oxides. In some embodiments, this
results in very low light transmittance (in some embodiments, a
transmittance of about less than 1% of the luminous transmittance
of the assembled lens of this current invention) for wavelengths in
a range of about 300 nm to about 420 nm. In some embodiments, the
desired cut-on wavelength of transmittance is about 430 nm, so to
increase the absorbance between 420 nm and 430 nm, some embodiments
add Exciton ABS 549 or Orco's Chinoline (Orco, Rhode Island
Division, 65 Valley Street, East Providence, R.I. 02914, USA)
organic dyes to either the adhesive or polarizing film or both to
accomplish this. [0199] a. Some embodiments of the present
invention omit the functional oxides and instead use one or more
organic dyes with absorbance peaks between 380 nm and 430 nm to
result in the same spectral curve shift as embodiments of the
current invention that include glass wafers. [0200] b. Some
embodiments of the present invention add further organic dyes that
have an absorbance peak near 440 nm to increase the absorbance of
blue light, but this can also affect how one perceives the color
blue.
[0201] 2. Some embodiments of the present invention further reduce
spectral transmittance in the transitional zone between the colors
blue and green at about 500 nm by using a narrow-band absorbent
having a wavelength-absorption band of about 20 nm. In all present
art an absorption-band peak between 490 and 510 nm is not described
(note that U.S. Pat. No. 8,733,929 to Chiou et al. uses multi-layer
coatings to reflect light in some wavelengths in this band). In
some embodiments, an organic dye such as, or similar to, Exciton's
P 491 (Exciton, P.O. Box 31126, Dayton, Ohio 45437) in a quantity
of about 0.1 milligram per lens is used. In some embodiments, the
absorbent peak desired for the present invention at about 500 nm is
not as deep as the absorbance peaks found at about 430 nm and 580
nm. In some embodiments, this helps to maintains transmittance
properties as found in ANSI Z80.3-2009 and ISO 12312-1 2013.
[0202] 3. Some embodiments of the present invention further reduce
the spectral transmittance by adding a narrow-band absorbent for
wavelengths in the transitional zone between the colors green and
red at about 580 nm. In some embodiments, a fairly steep and narrow
absorbance peak is wanted. One preferred embodiment uses neodymium
oxide with an amount of about 2.15 mole %. [0203] a. Some
embodiments optionally omit the neodymium oxide, and instead use a
narrow-band organic dye with an absorbance peak at about 580 nm.
Some embodiments use the organic dye Exciton ABS 584 in a quantity
of about 0.1 milligram per lens. In other embodiments, the amount
of neodymium oxide is reduced and an organic dye such as Exciton
ABS 584 is used to supplement absorption at wavelengths of about
580 nm.
[0204] 4. Some embodiments optionally add additional organic dyes
to attenuate the transmission of light between 700 nm and 780
nm.
[0205] Adding absorbance peaks as detailed in steps 1. through 3.
in the paragraph immediately above creates the preferred spectral
characteristics of some embodiments of this current invention.
There are four distinct bands within the visible spectrum as
detailed below.
[0206] Photochromic lenses refer to any lens whose luminous
transmission adjusts through the introduction of energy. The
adjustment occurs typically from a chemical reaction activated by
UV exposure. Once the lens is exposed to increased levels of UV
light a chemical reaction occurs within the lens, turning the lens
darker. Prior art exists in this field and, for example, is
detailed in Corning U.S. Pat. Nos. 4,549,894 and 4,979,976. In some
embodiments, the assembled lens system of the present invention
includes a photochromic lens. When included in this invention it
would be preferred to use the photochromic lens as the front-side
wafer 101 so that UV, which activates the photochromic-darkening
function, would not be filtered out by a front-side glass such as
described for other embodiments within this specification.
Optionally this current invention could be used when front glass
wafer 101 is photochromic, being directly exposed to the sun's rays
allow the photochromic wafer to function appropriately. When wafer
101 is implemented as a photochromic wafer and has a variable
luminous light transmittance from about 20% to about 40%, then
increasing the luminous light transmittance of the polarizing
filter from about 45% to about 60% would be most preferred. This
would be necessary for complying with ANSI Z80.3-2009 transmittance
standards.
[0207] Placing the optional mirror coating 106 on the concave
surface of wafer 101 protects the mirror coating 106 from damage
such as scratches, salt water, or peeling. The coating is deposited
on the lens by an evaporation process conducted under a vacuum. The
density of the coated lens depends on the thickness of the metallic
oxide coating. Because the index of refraction of the metallic
oxides is higher than the index of refraction of the underlying
lens, the amount of light reflected from the absorptive coating is
greater than the amount reflected uncoated surface of the
glass.
[0208] FIG. 16 is a schematic diagram of an ophthalmic spectacle
lens 1600, according to some embodiments of the present invention.
In FIG. 16, the top hydrophobic layer 1605 represents the front
layer of lens 1600, and the bottom hydrophobic layer 1615
represents the back layer of lens 1600. In some embodiments, lens
1600 includes (from front to back): a first hydrophobic layer 1605,
a first mirror layer 1606, a first ophthalmic-grade glass wafer
1607, a second mirror layer 1608 (in some embodiments, second
mirror layer 1608 and third mirror layer 1612 are alternatives to
first mirror layer 1606, so only one or the other is used, or in
some embodiments, all mirror layers are omitted), a first adhesive
layer 1609, a polarizing layer 1610, a second adhesive layer 1611,
a third mirror layer 1612 deposited on a second ophthalmic-grade
glass wafer 1613, an anti-reflective layer 1614, and a second
hydrophobic layer 1615. In some embodiments, one or more layers of
lens 1600 are omitted. In some embodiments, one or more of the
mirror layers 1606, 1608, and/or 1612 includes a metal film. In
other embodiments, one or more of the mirror layers 1606, 1608,
and/or 1612 includes a plurality of dielectric layers such that the
mirror layer(s) is/are wavelength-selective. (In some embodiments,
using wavelength-selective mirror-reflectors produces undesirable
reflections (i.e., for users who do not want mirror-type lenses),
so using wavelength selective organic dyes or oxides is preferred
to provide the absorbance at 400 nm-430 nm, 500 nm and 580 nm
bands. In some embodiments, the 400 nm-430 nm absorbance band has
zero or nearly zero transmittance from 400 nm to 420 nm, and a
transmittance of 5% luminous or less.) In some embodiments, one or
more of glass wafer 1613, adhesive layers 1609 and 1611, and/or
polarizing layer 1610 includes transitional metal oxides,
rare-earth metal oxides, and/or organic dyes. In various
embodiments of the present invention, one or more of the layers
shown in FIG. 16 are omitted. In some embodiments, a substitute
element (such as a polymer layer substituted for one or more of the
glass layers) is used for one or more of the layers shown in FIG.
16. In some embodiments, one or more additional layers (such as
additional coatings) are provided. Note that while three mirror or
reflective layers are shown as optional, in practice, only one
reflective layer is implemented in most embodiments, and the other
two reflective layers shown are omitted.
[0209] In some embodiments, the present invention provides an
assembled lens that has a predetermined or given average visible
light transmittance for wavelengths in the range of 400 nm-700 nm
(Tv; also called the average transmission for all wavelengths
between 400 nm and 700 nm inclusive).
[0210] In some embodiments, the transmittance of the lens for
wavelengths between 400 nm and 409 nm inclusive is less than or
equal to (i.e., no more than) 10% of Tv; the transmittance of the
lens for wavelengths between 410 nm and 419 nm inclusive is no more
than 15% of Tv, the transmittance of the lens for wavelengths
between 420 nm and 429 nm inclusive is no more than 20% of Tv, the
transmittance of the lens for wavelengths between 430 nm and 439 nm
inclusive is no more than 30% of Tv, and the transmittance of the
lens for wavelengths between 440 nm and 449 nm inclusive is no more
than 40% of Tv.
[0211] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 400 nm-420 nm that is
less than 1% of the average visible light transmittance of the
assembled lens. Some embodiments have an average transmittance for
wavelengths in the range of 400 nm-420 nm that is less than 3% of
the average visible light transmittance of the assembled lens. Some
embodiments have an average transmittance for wavelengths in the
range of 400 nm-420 nm that is less than 5% of the average visible
light transmittance of the assembled lens.
[0212] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 420 nm-430 nm that is
less than 1% of the average visible light transmittance of the
assembled lens. Some embodiments have an average transmittance for
wavelengths in the range of 420 nm-430 nm that is less than 5% of
the average visible light transmittance of the assembled lens. Some
embodiments have an average transmittance for wavelengths in the
range of 420 nm-430 nm that is less than 10% of the average visible
light transmittance of the assembled lens.
[0213] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 480 nm-510 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 450 nm-460
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 480 nm-510 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 440 nm-470
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 480 nm-510 nm that is
less than 85% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 480 nm-510 nm
that is less than 75% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 480 nm-510 nm
that is less than 65% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 480 nm-510 nm
that is less than 50% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 480 nm-510 nm
that is less than 40% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 480 nm-510 nm
that is more than 20% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 480 nm-510 nm
that is more than 30% of the average visible light transmittance of
the assembled lens.
[0214] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 490 nm-510 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 450 nm-460
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 490 nm-510 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 440 nm-470
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 490 nm-510 nm that is
less than 85% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-510 nm
that is less than 75% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-510 nm
that is less than 65% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-510 nm
that is less than 50% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-510 nm
that is less than 40% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-510 nm
that is more than 20% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-510 nm
that is more than 30% of the average visible light transmittance of
the assembled lens.
[0215] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 490 nm-500 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 450 nm-460
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 490 nm-500 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 440 nm-470
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 490 nm-500 nm that is
less than 85% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-500 nm
that is less than 75% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-500 nm
that is less than 65% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-500 nm
that is less than 50% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-500 nm
that is less than 40% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-500 nm
that is more than 20% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 490 nm-500 nm
that is more than 30% of the average visible light transmittance of
the assembled lens.
[0216] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 570 nm-590 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 540 nm-560
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 570 nm-590 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 520 nm-560
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 570 nm-590 nm that is
less than 85% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 570 nm-590 nm
that is less than 75% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 570 nm-590 nm
that is less than 65% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 570 nm-590 nm
that is less than 50% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 570 nm-590 nm
that is less than 40% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 570 nm-590 nm
that is more than 20% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 570 nm-590 nm
that is more than 30% of the average visible light transmittance of
the assembled lens.
[0217] Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 580 nm-590 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 540 nm-560
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 580 nm-590 nm that is
less than 85% but more than 20% of the average visible light
transmittance of the assembled lens and that is less than the
average transmittance for wavelengths in the range of 520 nm-560
nm. Some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 580 nm-590 nm that is
less than 85% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 580 nm-590 nm
that is less than 75% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 580 nm-590 nm
that is less than 65% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 580 nm-590 nm
that is less than 50% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 580 nm-590 nm
that is less than 40% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 580 nm-590 nm
that is more than 20% of the average visible light transmittance of
the assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 580 nm-590 nm
that is more than 30% of the average visible light transmittance of
the assembled lens.
[0218] Regarding infrared (IR) blocking, some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 700 nm-780 nm that is less than 20% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 700 nm-780 nm that is less than 10% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 700 nm-780 nm that is less than 5% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 700 nm-780 nm that is less than 2% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 700 nm-780 nm that is less than 1% of the average visible
light transmittance of the assembled lens. On the other hand, some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 700 nm-780 nm that is less than 300% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 700 nm-780 nm that is less than 200% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 700 nm-780 nm that is less than 150% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 700 nm-780 nm that is less than 100% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 700 nm-780 nm that is less than 50% of
the average visible light transmittance of the assembled lens.
[0219] Further regarding infrared (IR) blocking, some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 700 nm-750 nm that is less than 20% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 700 nm-750 nm that is less than 10% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 700 nm-750 nm that is less than 5% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 700 nm-750 nm that is less than 2% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 700 nm-750 nm that is less than 1% of the average
visible light transmittance of the assembled lens. On the other
hand, some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 700 nm-750 nm that is
less than 300% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 700 nm-750 nm
that is less than 200% of the average visible light transmittance
of the assembled lens. Some embodiments of the assembled lens have
an average transmittance for wavelengths in the range of 700 nm-750
nm that is less than 150% of the average visible light
transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 700 nm-750 nm that is less than 100% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 700 nm-750 nm that is less than 50% of the average
visible light transmittance of the assembled lens.
[0220] Further regarding infrared (IR) blocking, some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 730 nm-780 nm that is less than 20% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 730 nm-780 nm that is less than 10% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 730 nm-780 nm that is less than 5% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 730 nm-780 nm that is less than 2% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 730 nm-780 nm that is less than 1% of the average
visible light transmittance of the assembled lens. On the other
hand, some embodiments of the assembled lens have an average
transmittance for wavelengths in the range of 730 nm-780 nm that is
less than 300% of the average visible light transmittance of the
assembled lens. Some embodiments of the assembled lens have an
average transmittance for wavelengths in the range of 730 nm-780 nm
that is less than 200% of the average visible light transmittance
of the assembled lens. Some embodiments of the assembled lens have
an average transmittance for wavelengths in the range of 730 nm-780
nm that is less than 150% of the average visible light
transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 730 nm-780 nm that is less than 100% of the average
visible light transmittance of the assembled lens. Some embodiments
of the assembled lens have an average transmittance for wavelengths
in the range of 730 nm-780 nm that is less than 50% of the average
visible light transmittance of the assembled lens.
[0221] Regarding ultraviolet (UV) blocking, some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 300 nm-400 nm that is less than 20% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 300 nm-400 nm that is less than 10% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 300 nm-400 nm that is less than 5% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 300 nm-400 nm that is less than 2% of the average visible
light transmittance of the assembled lens. Some embodiments of the
assembled lens have an average transmittance for wavelengths in the
range of 300 nm-400 nm that is less than 1% of the average visible
light transmittance of the assembled lens.
[0222] Further regarding ultraviolet (UV) blocking, some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 350 nm-400 nm that is less than 20% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 350 nm-400 nm that is less than 10% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 350 nm-400 nm that is less than 5% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 350 nm-400 nm that is less than 2% of
the average visible light transmittance of the assembled lens. Some
embodiments of the assembled lens have an average transmittance for
wavelengths in the range of 350 nm-400 nm that is less than 1% of
the average visible light transmittance of the assembled lens.
[0223] In some embodiments, the present invention provides an
ophthalmic color-enhancing lens that provides transmittance
properties which blocks UV light and some visible light, enhances
blue colors, and provides greater contrast between blue green and
green red wavelengths. Some embodiments include a lens assembly
that has: a first zone, a second zone, a third zone, a fourth zone,
a fifth zone, a sixth zone, a seventh zone and an eighth zone,
wherein (a.) the first zone is a reduced-light-transmittance zone
having a range of wavelengths that extends from 300 nm to 399 nm,
inclusive, so that the value of the light transmission at any one
"point" (e.g., wherein the point has a wavelength range of plus or
minus 5 nm from a first-zone wavelength) in the first zone is less
than 1% of the luminous transmission of the assembled lens system;
wherein (b.) the second zone is a reduced-light-transmittance zone
found between 400 nm-409 nm so that the value of the light
transmission at any one point (e.g., wherein the point has a
wavelength range of plus or minus 2 nm from a wavelength between
400 nm-409 nm) is less than 5% of the luminous transmission of the
assembled lens system; wherein (c.) the third zone is a
minimum-light-transmittance zone found between 410 nm-430 nm so
that the value of the light transmission at any one point (e.g.,
wherein the point has a wavelength range of plus or minus 2 nm from
a wavelength between 410 nm-430 nm) is less than 10% of the
luminous transmission of the assembled lens system; wherein (d.)
the lens system provides at least three higher-transmittance zones
including the fourth zone having wavelengths in the range of 440 nm
to 460 nm, the fifth zone having wavelengths in the range of 540 nm
to 560 nm, and the sixth zone having wavelengths in the range of
600 nm to 630 nm, with each of the higher-transmittance zones
having at least one wavelength that has a transmittance of 75% to
150% of the luminous transmission of the assembled lens system, and
wherein (e.) the lens system provides at least two
reduced-transmittance zones having wavelengths between the three
higher-transmittance zones, and specifically including the seventh
zone having wavelengths in the range of 485 nm to 510 nm and the
eighth zone having wavelengths in the range of 570 nm to 590 nm and
wherein the seventh zone and the eighth zone each has at least one
wavelength within their respective wavelength ranges that has a
light transmittance of between 20% and 90% of the luminous
transmission of the assembled lens system.
[0224] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye, a copper oxide, a titanium oxide, and a
neodymium oxide.
[0225] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye, a copper halide, a titanium oxide, and a
neodymium oxide.
[0226] In some embodiments, the ophthalmic color-enhancing lens
includes at least one light absorber selected from the group
consisting of a copper halide, a copper oxide, a copper indium
compound, a titanium dioxide, a neodymium oxide, praseodymium, an
erbium oxide and an organic dye.
[0227] In some embodiments, the ophthalmic color-enhancing lens
includes at least two light absorbers selected from the group
consisting of a copper halide, a copper oxide, a copper indium
compound, a titanium dioxide, a neodymium oxide, praseodymium, an
erbium oxide and an organic dye.
[0228] In some embodiments, the ophthalmic color-enhancing lens
includes at least three light absorbers selected from the group
consisting of a copper halide, a copper oxide, a copper indium
compound, a titanium dioxide, a neodymium oxide, praseodymium, an
erbium oxide and an organic dye.
[0229] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye and at least one element selected from the
group consisting of copper, indium, titanium, neodymium,
praseodymium, erbium and a halide.
[0230] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye and at least one oxide selected from the
group consisting of copper oxide, indium oxide, titanium oxide,
neodymium oxide, praseodymium oxide, and erbium oxide.
[0231] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye and at least two oxides selected from the
group consisting of copper oxide, indium oxide, titanium oxide,
neodymium oxide, praseodymium oxide, and erbium oxide.
[0232] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye and at least three oxides selected from the
group consisting of copper oxide, indium oxide, titanium oxide,
neodymium oxide, praseodymium oxide, and erbium oxide.
[0233] In some embodiments, the ophthalmic color-enhancing lens
includes an organic dye and at least four oxides selected from the
group consisting of copper oxide, indium oxide, titanium oxide,
neodymium oxide, praseodymium oxide, and erbium oxide.
[0234] In some embodiments, the ophthalmic color-enhancing lens
includes at least two light absorbers selected from the group
consisting of copper oxide, indium oxide, titanium oxide, neodymium
oxide, praseodymium oxide, erbium oxide, and an organic dye.
[0235] In some embodiments, the ophthalmic color-enhancing lens
includes at least three light absorbers selected from the group
consisting of copper oxide, indium oxide, titanium oxide, neodymium
oxide, praseodymium oxide, erbium oxide, and an organic dye.
[0236] In some embodiments, the ophthalmic color-enhancing lens is
made using a two-wafer system with each wafer being about 1 mm in
thickness and wherein the rear wafer contains wavelength-selective
light-absorbing oxides, and wherein the two wafers are adhered
together with a light-polarizing filter in between.
[0237] In some embodiments, the ophthalmic color-enhancing lens is
made using a two-wafer system, wherein the two wafers are adhered
together using an adhesive with a light-polarizing filter in
between.
[0238] In some embodiments, the ophthalmic color-enhancing lens is
made using a two-wafer system, wherein the two wafers are adhered
together without an adhesive but with a light-polarizing filter in
between. In some such embodiments, the two wafers are heat-fused to
the two opposite faces of the polarizing filter. In some such
embodiments, the heat fusing is done in a vacuum.
[0239] In some embodiments, the ophthalmic color-enhancing lens is
made using a two-wafer system with each wafer being about 1 mm in
thickness and the preferred wavelength-selective absorbing material
embodiment containing oxides is positioned as the front wafer
adhered together with a light polarizing filter in between.
[0240] In some embodiments, the two glass wafers are adhered
together with a polarizing filter in between and all
wavelength-selective absorbing material embodiments are included in
either the adhesive or light polarizing filter.
[0241] In some embodiments, the wavelength-selective absorbing
materials are included in the one of the glass wafers and in the
adhesive or light polarizing layer.
[0242] In some embodiments, the ophthalmic color-enhancing lens
includes a minimum light transmittance zone found between 430
nm-450 nm so that the value of the light transmission at any one
point is less than 10% of the luminous transmission of the
assembled lens system.
[0243] In some embodiments, the ophthalmic color-enhancing lens
includes additional organic dyes to increase attenuation from 700
nm to 780 nm so that a minimum light transmittance zone found
between 700 nm-780 nm has a value of the light transmittance at any
one point that is not greater than 300% of the luminous
transmittance of the assembled lens system. In some embodiments,
the ophthalmic color-enhancing lens has a minimum light
transmittance zone found between 700 nm-780 nm has a value of the
light transmittance at any one point that is not greater than 200%
of the luminous transmittance of the assembled lens system. In some
embodiments, the ophthalmic color-enhancing lens has a minimum
light transmittance zone found between 700 nm-780 nm has a value of
the light transmittance at any one point that is not greater than
150% of the luminous transmittance of the assembled lens system. In
some embodiments, the ophthalmic color-enhancing lens has a minimum
light transmittance zone found between 700 nm-780 nm has a value of
the light transmittance at any one point that is not greater than
100% of the luminous transmittance of the assembled lens
system.
[0244] In some embodiments, the ophthalmic color-enhancing lens
includes a mirror coating on either the convex or concave
surface.
[0245] In some embodiments, the ophthalmic color-enhancing lens has
the concave surface of the rear wafer having an anti-reflection
coating.
[0246] In some embodiments, the ophthalmic color-enhancing lens
adheres to all spectral requirements as found in ANSI Z80.3-2009
and ISO 12312-1 2013.
[0247] In some embodiments, the ophthalmic color-enhancing lens
includes photochromic properties in the front wafer.
[0248] In some embodiments, the rear wafer is thicker in order to
accommodate prescription surfacing.
[0249] In some embodiments, the spectral absorbents are selected
from the group consisting of class dopants, plastic additives,
dyes, stains, heat treatments, exposure to ultraviolet light,
chemical baths, semi-transparent mirror coatings, and
semi-transparent color coatings.
[0250] In some embodiments, the lens is an ophthalmic plastic
lens.
[0251] In some embodiments, the spectral absorbents are selected
from a list including but not limited to narrowband absorbing dyes,
sharp-cut absorbing dyes, and optical-interference coatings.
[0252] Some embodiments include a light polarizing filter.
[0253] Some embodiments include a mirror coating.
[0254] Some embodiments include wavelength-selective
multi-layer-dielectric reflective coating.
[0255] Some embodiments include wavelength-selective
multi-layer-dielectric reflective coating for only one of four
wavelength-absorption bands, and include an organic dye.
[0256] Some embodiments include an anti-reflection coating.
[0257] In some embodiments, the rear portion of the lens is thicker
to allow for prescription surfacing.
[0258] In some embodiments, the rear wafer of the two-wafer lens is
thicker than the front wafer to allow for prescription
surfacing.
[0259] In some embodiments, the present invention provides an
ophthalmic color-enhancing lens that provides transmittance
properties which blocks UV light and some visible light, enhances
blue colors, and provides enhanced perceived contrast between blue
light and green light and provides enhanced perceived contrast
between green light and red light, wherein, when assembled, the
lens has a luminous transmission value that is defined by ANSI
Z80.3-2009 4.6.3.2, the lens including: one or more color-absorbing
materials that together provide: a first
reduced-light-transmittance zone for a first range of wavelengths
that extends from 300 nm to 399 nm, wherein light transmission at
any wavelength in the first range is no more than 1% of the
luminous transmission of the lens; a second
reduced-light-transmittance zone for a second range of wavelengths
that extends from 400 nm to 409 nm, wherein light transmission at
any wavelength in the second range is no more than 5% of the
luminous transmission of the lens; a third
reduced-light-transmittance zone for a third range of wavelengths
that extends from 410 nm to 430 nm, wherein light transmission at
any wavelength in the third range is no more than 10% of the
luminous transmission of the lens; and a plurality of
light-transmittance zones for respective wavelength ranges of 440
to 460 nm, 540 to 560 nm, 600 to 630 nm with each said maximum
transmittance zone having at least one wavelength that is 75% to
150%, inclusive, of the luminous transmission of the lens
contrast-enhancing-light-transmittance zones coordinately found
between the three maximum transmittance zones and specifically
found in the wavelength ranges of 480 nm to 510 nm and 570 nm to
590 nm and each contrast-enhancing-light-transmittance zone having
at least one wavelength having a light-transmittance value between
20% and 90%, inclusive, of the luminous transmission of the
lens.
[0260] An ophthalmic color-enhancing lens that provides
transmittance properties which blocks UV light and some visible
light, enhances blue colors, and provides enhanced perceived
contrast between blue light and green light and provides enhanced
perceived contrast between green light and red light, wherein, when
assembled, the lens has a luminous transmission value that is
defined by ANSI Z80.3-2009 4.6.3.2, the lens including: one or more
color-absorbing materials that together provide: a first
reduced-light-transmittance zone for a first range of wavelengths
that extends from 300 nm to 399 nm, wherein light transmission at
any wavelength in the first range is no more than 1% of the
luminous transmission of the lens; a second
reduced-light-transmittance zone for a second range of wavelengths
that extends from 400 nm to 409 nm, wherein light transmission at
any wavelength in the second range is no more than 10% of the
luminous transmission of the lens; a third
reduced-light-transmittance zone for a third range of wavelengths
that extends from 410 nm to 420 nm, wherein light transmission at
any wavelength in the third range is no more than 15% of the
luminous transmission of the lens; and a fourth
reduced-light-transmittance zone for a fourth range of wavelengths
that extends from 420 nm to 430 nm, wherein light transmission at
any wavelength in the third range is no more than 20% of the
luminous transmission of the lens; and a plurality of
light-transmittance zones for respective wavelength ranges of 440
to 460 nm, 540 to 560 nm, 600 to 630 nm with each said maximum
transmittance zone having at least one wavelength that is 40% to
150%, inclusive, of the luminous transmission of the lens
contrast-enhancing-light-transmittance zones coordinately found
between the three maximum transmittance zones and specifically
found in the wavelength ranges of 480 nm to 510 nm and 570 nm to
590 nm and each contrast-enhancing-light-transmittance zone having
at least one wavelength having a light-transmittance value between
20% and 90%, inclusive, of the luminous transmission of the
lens.
[0261] In some embodiments, the assembled lens comprises all of or
part of and not limited to copper halide, copper indium, and
titanium dioxide, neodymium oxide, praseodymium, erbium oxide and
organic dyes.
[0262] In some embodiments, the assembled lens is made using a
two-wafer system including a front glass wafer and a rear glass
wafer with each wafer being about 1 mm in thickness and the glass
wafer containing wavelength-selective light-absorbing oxides is
positioned as the rear wafer adhered together with a light
polarizing filter in between.
[0263] In some embodiments, the assembled lens is made using a
two-wafer system with each wafer being about 1 mm in thickness and
the preferred embodiment containing oxides is positioned as the
front wafer adhered together with a light polarizing filter in
between.
[0264] In some embodiments, the assembled lens includes two glass
wafers that are adhered together with a polarizing filter in
between and all embodiments are included in either the adhesive or
light polarizing filter.
[0265] In some embodiments, the wavelength-selective
light-absorbing materials are included in the one of the glass
wafers and in the adhesive or light polarizing layer.
[0266] In some embodiments, a minimum light transmittance zone is
created between 430 nm-450 nm so that the value of the light
transmission at any one point is less than 10% of the luminous
transmission of the assembled lens system.
[0267] Some embodiments further include additional organic dyes to
increase attenuation from 700 nm to 780 nm so that a minimum light
transmittance zone found between 700 nm-780 nm has a value of the
light transmittance at any one point that is not greater than 300%
of the luminous transmittance of the assembled lens system.
[0268] Some embodiments further include a mirror coating on either
the convex or concave surface or both.
[0269] In some embodiments, the concave surface of the rear wafer
has an anti-reflection coating.
[0270] In some embodiments, the lens is adhesiveless (i.e., made
without the use of adhesive within or between layers of the lens)
but includes a polycarbonate polymer, and the wavelength blocking
in the violet absorbance band, the cyan partial-absorbance band and
the yellow absorbance band is provided only by at least one organic
dye (i.e., wherein the lens has no adhesive layers and has
substantially no wavelength-blocking rare-earth oxides).
[0271] In some embodiments, the lens is made such that it meets all
spectral requirements as found in ANSI Z80.3-2009 and ISO 12312-1
2013.
[0272] In some embodiments, the front wafer is photochromic. In
some embodiments, the rear wafer is thicker than the front wafer in
order to accommodate prescription surfacing.
[0273] In some embodiments, said spectral characteristics are
created by using materials selected from the group consisting of
class dopants, plastic additives, dyes, stains, heat treatments,
exposure to ultraviolet light, chemical baths, semi-transparent
mirror coatings, and semi-transparent color coatings.
[0274] In some embodiments, the lens is an ophthalmic plastic lens.
In some such embodiments, the wavelength-selective light-absorbing
materials are selected from a list including but not limited to
narrowband absorbing dyes, sharp cut absorbing dyes, and optical
interference coatings. Some such embodiments further include a
light polarizing filter. Some such embodiments further include a
mirror coating. Some such embodiments further include
anti-reflection coatings. In some such embodiments, the rear
portion of the lens is thicker to allow for prescription
surfacing.
[0275] It is to be understood that the above description is
intended to be illustrative, and not restrictive. Although numerous
characteristics and advantages of various embodiments as described
herein have been set forth in the foregoing description, together
with details of the structure and function of various embodiments,
many other embodiments and changes to details will be apparent to
those of skill in the art upon reviewing the above description. The
scope of the invention should be, therefore, determined with
reference to the appended claims, along with the full scope of
equivalents to which such claims are entitled. In the appended
claims, the terms "including" and "in which" are used as the
plain-English equivalents of the respective terms "comprising" and
"wherein," respectively. Moreover, the terms "first," "second," and
"third," etc., are used merely as labels, and are not intended to
impose numerical requirements on their objects.
* * * * *