U.S. patent application number 15/362381 was filed with the patent office on 2017-08-17 for use of no-bake mold process to manufacture side frame and bolster for a railway truck.
The applicant listed for this patent is Nevis Industries LLC. Invention is credited to Jason C. Bryant, Arthur A. Gibeaut, Erik L. Gotlund, Jon R. Jeambey, William A. Kurtzhals, Vaughn Makary, Roshan N. Manibharathi, F. Andrew Nibouar, James A. Pike, Ronald P. Sellberg, Jerry R. Smerecky, Jonathan A. Stull, Maureen Werner.
Application Number | 20170232503 15/362381 |
Document ID | / |
Family ID | 59560114 |
Filed Date | 2017-08-17 |
United States Patent
Application |
20170232503 |
Kind Code |
A1 |
Nibouar; F. Andrew ; et
al. |
August 17, 2017 |
USE OF NO-BAKE MOLD PROCESS TO MANUFACTURE SIDE FRAME AND BOLSTER
FOR A RAILWAY TRUCK
Abstract
A method for casting a railroad component such as a component of
a railway car truck. The component of the railway car truck may be,
e.g., a side frame or a bolster of the railway car truck. The
method includes manufacturing the railroad component made of steel
in a no-bake manufacturing process including use of a
chemically-bonded sand system that results in a sand mold from
which the railroad component is cast. The railroad component
resulting from the no-bake manufacturing process has a surface
finish less than 750 micro-inches RMS, resulting in increased
fatigue life compared to a railroad component manufactured by a
green sand process.
Inventors: |
Nibouar; F. Andrew;
(Chicago, IL) ; Smerecky; Jerry R.; (South
Barrington, IL) ; Sellberg; Ronald P.; (Naperville,
IL) ; Gibeaut; Arthur A.; (Erie, IL) ;
Gotlund; Erik L.; (Green Oaks, IL) ; Werner;
Maureen; (Bolingbrook, IL) ; Makary; Vaughn;
(Muskegon, MI) ; Jeambey; Jon R.; (Naperville,
IL) ; Pike; James A.; (Fairview, PA) ; Bryant;
Jason C.; (Erie, PA) ; Stull; Jonathan A.;
(Erie, PA) ; Kurtzhals; William A.; (Erie, PA)
; Manibharathi; Roshan N.; (Des Plaines, IL) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Nevis Industries LLC |
Wilmington |
DE |
US |
|
|
Family ID: |
59560114 |
Appl. No.: |
15/362381 |
Filed: |
November 28, 2016 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14943269 |
Nov 17, 2015 |
|
|
|
15362381 |
|
|
|
|
13109843 |
May 17, 2011 |
9216450 |
|
|
14943269 |
|
|
|
|
14739857 |
Jun 15, 2015 |
9505418 |
|
|
13109843 |
|
|
|
|
14337722 |
Jul 22, 2014 |
9079590 |
|
|
14739857 |
|
|
|
|
13916114 |
Jun 12, 2013 |
8783481 |
|
|
14337722 |
|
|
|
|
12685346 |
Jan 11, 2010 |
8485371 |
|
|
13916114 |
|
|
|
|
15152860 |
May 12, 2016 |
9637143 |
|
|
12685346 |
|
|
|
|
Current U.S.
Class: |
164/138 |
Current CPC
Class: |
B22C 9/10 20130101; B22C
9/02 20130101; B22C 1/00 20130101; B22C 9/103 20130101; B22C 9/108
20130101; B22C 9/24 20130101; B61F 5/52 20130101; B22D 25/02
20130101; B61G 3/06 20130101 |
International
Class: |
B22C 9/02 20060101
B22C009/02; B22D 25/02 20060101 B22D025/02; B22C 9/24 20060101
B22C009/24; B61F 5/52 20060101 B61F005/52; B22C 1/00 20060101
B22C001/00 |
Claims
1. A method for casting a bolster of a railway car truck, the
method comprising: manufacturing a bolster made of steel in a
no-bake manufacturing process including use of a chemically-bonded
sand system that results in a sand mold from which the bolster is
cast, the bolster that results having a surface finish less than
750 micro-inches RMS, resulting in increased fatigue life compared
to a bolster manufactured by a green sand process.
2. The method of claim 1, wherein the bolster resulting from the
no-bake manufacturing process includes draft angles comprising 1.0
(one) degree or less for a plurality of typical features of the
bolster.
3. The method of claim 1, wherein the bolster resulting from the
no-bake manufacturing process includes a pair of shoe pockets at
respective ends configured to be inserted into bolster openings of
respective side frames, and wherein a surface finish of the pair of
shoe pockets is less than 500 micro-inches RMS.
4. The method of claim 3, wherein a shoe pocket side wall draft
angle of the bolster is no more than about 3/4 degrees.
5. The method of claim 3, wherein a margin of error in shoe pocket
angles is within about .+-.0.5 degrees.
6. The method of claim 1, wherein the bolster resulting from the
no-bake manufacturing process includes inner and outer gibs, and
wherein a margin of error in a spacing between respective inner and
outer gibs of the bolster is within about .+-.0.063 inches.
7. The method of claim 6, wherein respective inner and outer gib
draft angles are not more than about 3/4 degrees.
8. A method of manufacturing a side frame of a railway car truck,
the method comprising: manufacturing a side frame made of steel in
a no-bake manufacturing process including use of a
chemically-bonded sand system that results in a sand mold from
which the side frame is cast, the side frame that results having a
surface finish less than 750 micro-inches RMS, resulting in
increased fatigue life compared to a side frame manufactured by a
green sand process.
9. The method of claim 8, wherein the side frame resulting from the
no-bake manufacturing process includes draft angles comprising 1.0
(one) degree or less for a plurality of typical features of the
side frame.
10. The method of claim 8, wherein the side frame resulting from
the no-bake manufacturing process includes a pair of pedestals
defining a pedestal jaw into which a wheel assembly of a wheel set
of the railway car truck is mounted, and wherein a surface finish
of the pair of pedestals is less than 500 micro-inches RMS.
11. The method of claim 10, wherein a pedestal roof draft angle of
the side frame is no more than about 3/4 degrees.
12. The method of claim 10, wherein tolerances between centers of
the pair of pedestals is within about .+-.0.038 inches.
13. A method for casting a railway car truck assembly including a
side frame and a bolster, the side frame including a pair of
pedestals defining a pedestal jaw into which a wheel assembly of a
wheel set of the railway car truck is mounted, the bolster
including inner and outer gibs and a pair of shoe pockets at
respective ends configured to be inserted into bolster openings of
the side frame, the method comprising: manufacturing a side frame
and bolster made of steel in a no-bake manufacturing process
including use of a chemically-bonded sand system that results in at
least one sand mold from which the side frame and the bolster are
cast, the side frame and the bolster that results having a surface
finish less than 750 micro-inches RMS, resulting in increased
fatigue life compared to a side frame and a bolster manufactured by
a green sand process.
14. The method of claim 13, wherein the side frame and bolster
resulting from the no-bake manufacturing process includes draft
angles comprising 1.0 (one) degree or less for a plurality of
typical features of the side frame and bolster.
15. The method of claim 13, wherein a surface finish of at least
one of: the pair of shoe pockets of the bolster, and the pair of
pedestals of the side frame, is less than 500 micro-inches RMS.
16. The method of claim 13, wherein a shoe pocket side wall draft
angle of the bolster is no more than about 3/4 degrees.
17. The method of claim 13, wherein a margin of error in shoe
pocket angles is within about .+-.0.5 degrees.
18. The method of claim 13, wherein a margin of error in a spacing
between respective inner and outer gibs of the bolster is within
about .+-.0.063 inches.
19. The method of claim 13, wherein respective inner and outer gib
draft angles are not more than about 3/4 degrees.
20. The method of claim 13, wherein a pedestal roof draft angle of
the side frame is no more than about 3/4 degrees.
21. The method of claim 13, wherein tolerances between centers of
the pair of pedestals of the side frame is within about .+-.0.038
inches.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation-in-part of U.S. patent
application Ser. No. 14/739,857, filed Jun. 15, 2015, which is a
continuation of U.S. patent application Ser. No. 14/337,722, filed
Jul. 22, 2014, issued as U.S. Pat. No. 9,079,590; which is a
continuation of U.S. patent application Ser. No. 13/916,114, filed
Jun. 12, 2013, issued as U.S. Pat. No. 8,783,481; which is a
continuation of U.S. patent application Ser. No. 12/685,346, filed
Jan. 11, 2010, issued as U.S. Pat. No. 8,485,371. This application
is also a continuation-in-part of U.S. patent application Ser. No.
14/943,269, which is a continuation of U.S. patent application Ser.
No. 13/109,843, filed May 17, 2011, issued as U.S. Pat. No.
9,216,450. This application is also a continuation-in-part of U.S.
patent application Ser. No. 15/152,860, filed May 12, 2016. The
disclosures of the foregoing applications are herein incorporated
by reference in their entirety.
TECHNICAL FIELD
[0002] The present disclosure relates generally to the field of
railcar components, and more specifically, to the manufacturing of
railcar components through the use of no-bake or air-set casting or
the like.
BACKGROUND
[0003] Sand casting is one of the earliest forms of casting. Its
popular use is due to its low cost and the simplicity of materials
involved. A sand casting or a sand molded casting is a cast part
produced through the following process: (1) placing a pattern in
sand to create a mold, which incorporates a gating system; (2)
removing the pattern; (3) filling the mold cavity with molten
metal; (4) allowing the metal to cool; (5) breaking away the sand
mold and removing the casting; and (6) finishing the casting, which
may include weld repair, grinding, machining, and/or heat treatment
operations. This process is now explained in more detail.
[0004] In sand casting, the primary piece of equipment is the mold,
which contains several components. The mold is divided into two
halves--the cope (upper half) and the drag (bottom half), which
meet along a parting line. The sand mixture is packed around a
master "pattern" forming a mold cavity, which is an impression of
the shape being cast. The sand is usually housed in what casters
refer to as flasks, which are boxes without a bottom or lid, used
to contain the sand. The sand mixture can be tamped down as it is
added and/or the final mold assembly is sometimes vibrated to
compact the sand and fill any unwanted voids in the mold. The sand
can be packed by hand, but machines that use pressure or impact
ensure even packing of the sand and require far less time, thus
increasing the production rate. The pattern is removed, leaving the
mold cavity. Cores are added as required, and the cope is placed on
top of the drag.
[0005] Cores are additional pieces that form the internal openings,
recesses, and passages of the casting. Cores are typically
comprised of sand so that they can be shaken out of the casting,
rather than requiring the necessary geometry to slide out. As a
result, sand cores allow for the creation of many complex internal
features. Each core is positioned in the mold before the molten
metal is poured. Recesses in the pattern called core prints anchor
each core in place. The core may still shift, however, due to poor
fit up between core and core prints, the flow of the metal around
the core, or due to buoyancy in the molten metal.
[0006] Small metal pieces called chaplets are fastened between the
cores and the cavity surface to provide further support for the
cores. Chaplets are small metal pieces that are fastened between
the core and the cavity surface. Chaplets consist of a metal with a
higher melting temperature than that of the metal being cast in
order to maintain their structure to support the core. After
solidification, the chaplets are cast inside the casting and the
excess material of the chaplets that protrudes is cut off.
[0007] In addition to the external and internal features of the
casting, other features must be incorporated into the mold to
accommodate the flow of molten metal. The molten metal is poured
into a pouring basin, which is a large depression in the top of the
sand mold. The molten metal funnels out of the bottom of this basin
and down the main channel, called the sprue. The sprue connects to
a series of channels, called runners that carry the molten metal
into the cavity. At the end of each runner, the molten metal enters
the cavity through a gate that controls the flow rate and minimizes
turbulence.
[0008] Chambers called risers that fill with molten metal are often
connected to the runner system. Risers provide an additional source
of metal during solidification. When the casting cools, the molten
metal shrinks and the additional material in the gate and risers
acts to back fill into the cavities as needed. Open risers also aid
in reducing shrinkage. When open risers are utilized, the first
material to enter the cavity is allowed to pass completely through
the cavity and enter the open riser. This strategy prevents early
solidification of the molten metal and provides a source of
material to compensate for shrinkage. Lastly, small channels are
included running from the cavity to the exterior of the mold. These
channels act as venting holes to allow gases to escape the cavity.
The porosity of the sand also allows some air to escape, but
additional vents are sometimes needed. The molten metal that flows
through all of the channels (sprue, runners, and risers) will
solidify attached to the casting and must be separated from the
part after it is removed. Molten metal is poured into the mold
cavity, and after it cools and solidifies, the casting is separated
from the sand mold.
[0009] The accuracy of the casting is limited by the type of sand
and the molding process. Sand castings made from coarse green sand
impart a rough texture on the surface of the casting, making them
easy to distinguish from castings made by other processes. Air-set,
or no-bake, molds can produce castings with much smoother surfaces.
The benefit to providing a smoother surface is discussed in more
detail below but is not insignificant in improving the performance
of castings made utilizing the air-set casting process. After
molding, the casting is covered in a residue of oxides, silicates,
and other compounds. This residue can be removed by various means,
such as grinding or shot blasting. Several other surface condition
benefits result from the use of the air-set process compared to the
green sand process. These include benefits with regards to surface
inclusions, surface porosity, laps, and scabs. Details of a
comparison between required surface conditions and what can be
obtained using the air-set process are provided below.
[0010] During casting, some of the components of the sand mixture
are lost in the thermal casting process. Green sand can be reused
after adjusting its composition to replenish the lost moisture and
additives. The pattern itself can be reused indefinitely to produce
new sand molds. The sand molding process has been used for many
centuries to produce castings manually. Since 1950,
partially-automated casting processes have been developed for
production lines, some including hydraulics to compact the
sand.
[0011] Green sand is an aggregate of sand (about 90%), bentonite
clay or binder (about 7%), which includes pulverized coal, and
water (about 3%). It is termed "green" because like a green tree
branch, it contains water. The largest portion of the aggregate is
always sand, which can be either silica or olivine. There are many
recipes for the proportion of clay, but they all strike different
balances between moldability, surface finish, and ability of the
hot molten metal to degas. The coal, typically referred to in
foundries as sea-coal, is present at a ratio of less than 5% and
partially combusts in the presence of the molten metal leading to
off-gassing of organic vapors. Also, the presence of 2-3% water
results in increased occurrence of gas defects in the casting after
reacting with the molten steel. Rough surface discontinuities can
form as a result of the off gassing or vapors and can result in
lower fatigue life for couplers and coupler parts. Given the cyclic
loading which coupler assemblies are subjected, it is important to
provide as long a fatigue life as possible.
[0012] Another type of mold is a skin-dried mold. A skin-dried mold
begins like a green sand mold, but additional bonding materials are
added and the cavity surface is dried by a torch or heating lamp to
increase mold strength. This improves the dimensional accuracy and
surface finish, but lowers the collapsibility. Dry skin molds are
more expensive and require more time, thus lowering the production
rate.
[0013] Another type of sand that may be used in sand casting is dry
sand. In a dry sand mold, sometimes called a cold box mold, the
sand is mixed only with an organic binder. The mold is strengthened
by baking it in an oven. The resulting mold has a high dimensional
accuracy, but is expensive and results in a lower production
rate.
[0014] The casting process for the manufacture of couplers has
historically employed the green sand process. While this process
has served the railroad industry well, there are disadvantages
associated with the green sand process, such as poor material
strength, porosity, and poor surface finish, resulting in shorter
fatigue life, large tolerance variation, and secondary
grinding/machining is often required after the casting process.
Additionally, a large number of weld repairs may be required at
finishing time to fix either surface or subsurface defects.
Production rates are also low and include high finishing labor
costs. For reasons that will become more apparent below, these
disadvantages can require earlier replacement of railcar
components, and create additional manufacturing costs that can be
avoided. It would be beneficial, therefore, to use another casting
process in the manufacture of railcar components to overcome, or at
least ameliorate, these disadvantages.
[0015] These casting processes are used to form many railcar
components including, e.g., couplers, knuckles, side frames,
bolsters, and the like.
[0016] For example, railway cars typically consist of a rail car
that rests upon a pair of truck assemblies. The truck assemblies
include a pair of side frames and wheelsets connected together via
a bolster and damping system. The car rests upon the center bowl of
the bolster, which acts as a point of rotation for the truck
system. The car body movements are reacted through the springs and
friction wedge dampers, which connect the bolster and side frames.
The side frames include pedestals that each defines a jaw into
which a wheel assembly of a wheel set is positioned using a roller
bearing adapter.
[0017] The side frames and bolsters may be formed via various
casting techniques. The most common technique for producing these
components is through sand casting, as discussed. Traditionally,
side frames and bolsters have been created using the green sand
process, due to the lower cost associated with the molding
materials. While this method has been effective at producing these
components for many years, there are disadvantages to this
process.
[0018] Side frames and bolsters produced via the green sand
operation above have several problems. First, relatively large
draft angles required in the patterns result in corresponding draft
angles in the cast items. In areas where flat sections are
required, such as the pedestal area on the side frames, and
friction shoe pockets on the bolster, cores must be used to create
these features. These cores have a tendency to shift and float
during pouring. This movement can result in inconsistent final
product dimensions, increased finishing time, or scrapping of the
component if outside specified dimensions. Other problems with
these casting operations will become apparent upon reading the
description below.
BRIEF SUMMARY OF SELECTED INVENTIVE ASPECTS
[0019] This Summary provides an introduction to some general
concepts relating to this invention in a simplified form that is
further described below in the Detailed Description.
[0020] Aspects of the invention include a method for casting a
railroad component such as a component of a railway car truck. The
component of the railway car truck may be, e.g., a side frame or a
bolster. The method includes manufacturing the railroad component
made of steel in a no-bake manufacturing process including use of a
chemically-bonded sand system that results in a sand mold from
which the railroad component is cast. The railroad component
resulting from the no-bake manufacturing process has a surface
finish less than 750 micro-inches RMS, resulting in increased
fatigue life compared to a railroad component manufactured by a
green sand process.
[0021] According to some aspects, the method may result in reduced
draft angles for typical features of the railroad component
compared to a railroad component manufactured by a green sand
process. For example, the side frame or bolster resulting from the
no-bake manufacturing process may include draft angles comprising
1.0 (one) degree or less for a plurality of typical features of the
side frame and bolster. In some embodiments, a draft angle of a
shoe pocket side wall of the bolster may be no more than about 3/4
degrees. In other embodiments, a draft angle for a pedestal rood of
the side frame may be no more than about 3/4 degrees.
[0022] According to other aspects, a surface finish and/or margin
of error in dimensions may be improved from certain aspects of the
railroad component compared to a railroad component manufactured by
a green sand process. For example, in some embodiments a surface
finish of shoe pockets of the bolster and/or a pair of pedestals of
the side frame may be less than 500 micro-inches RMS. In other
embodiments, a margin of error in a spacing between respective
inner and outer gibs of the bolster may be within about plus or
minus 0.063 inches. In still other embodiments, a tolerance between
centers of the pair of pedestals of the side frame may be within
about plus or minus 0.038 inches. In still other embodiments, a
margin of error of shoe pocket angles of the bolster may be about
plus or minus 0.5 degrees.
BRIEF DESCRIPTION OF THE DRAWINGS
[0023] The system may be better understood with reference to the
following drawings and description. The components in the figures
are not necessarily to scale, emphasis instead being placed upon
illustrating the principles of the invention. Moreover, in the
figures, like-referenced numerals designate corresponding parts
throughout the different views.
[0024] FIG. 1 is a perspective view of a railroad coupler
manufactured by a no-bake, or air-set, process.
[0025] FIG. 2 is a perspective, exploded view of a coupler assembly
used to form the railroad coupler of FIG. 1.
[0026] FIG. 3 is a top perspective view of the coupler body of FIG.
2.
[0027] FIG. 4 is a side, cross section view along line 4-4 of the
coupler body of FIG. 2.
[0028] FIGS. 5A and 5B are two perspective views of the coupler
body of FIG. 2, showing the location of the coupler buffing
shoulders relative to the coupler pin hole.
[0029] FIG. 6 is a perspective view of the railroad coupler of FIG.
2, showing the location of the pin protector bosses relative to the
coupler pin hole.
[0030] FIG. 7 is a side perspective view of the coupler body of
FIG. 2.
[0031] FIG. 8 is a cross section view along line 8-8 of the coupler
body of FIG. 7.
[0032] FIG. 9 is a side perspective view of the coupler body of
FIG. 2.
[0033] FIG. 10 is a cross section view along line 10-10 of the
coupler body of FIG. 9.
[0034] FIG. 11 is a top view of the coupler knuckle of FIG. 2.
[0035] FIG. 12 is the cross section view along line 12-12 of the
knuckle of FIG. 11.
[0036] FIGS. 13A and 13B are two perspective views of the knuckle
of the railroad coupler of FIG. 11, showing the location of the
knuckle pulling lugs relative to the knuckle pin hole.
[0037] FIGS. 14A and 14B are two perspective views of the knuckle
of the railroad coupler of FIG. 11, showing the location of the
knuckle buffing shoulders relative to the knuckle pin hole.
[0038] FIGS. 15A and 15B are two perspective views of the knuckle
of the railroad coupler of FIG. 11, showing the location of the
knuckle pin protector bosses relative to the knuckle pin hole.
[0039] FIG. 16 is a top view of the coupler knuckle of FIG. 2,
indicating the approximate dimension between the center of the
knuckle pin hole and the knuckle buffing shoulder as about 31/2
inches and between the center of the knuckle pin hole and the
knuckle pulling lug as about 57/8 inches.
[0040] FIG. 17 is a bottom view of the coupler knuckle of FIG. 2,
indicating the approximate dimension between the center of the
knuckle pin hole and the knuckle buffing shoulder as about 31/2
inches and between the center of the knuckle pin hole and the
knuckle pulling lug as about 53/4 inches.
[0041] FIGS. 18A and 18B illustrate a perspective and side views,
respectively, of an exemplary side frame of a railway car
truck.
[0042] FIGS. 19A and 19B illustrate an inner surface of an
exemplary side frame column that includes a pair of column
stiffeners.
[0043] FIG. 20 illustrates an exemplary pedestal jaw of a cast side
frame.
[0044] FIG. 21 illustrates exemplary operations for manufacturing a
side frame.
[0045] FIG. 22A illustrates exemplary drag and cope portions of a
mold for forming a side frame.
[0046] FIG. 22B illustrates exemplary risers and gating system for
the side frame.
[0047] FIG. 23 illustrates exemplary cores that may be utilized
with the mold.
[0048] FIG. 24 illustrates an exemplary bolster that may be
utilized in combination with the side frame above.
[0049] FIG. 25 illustrates risers and gating system for forming the
bolster.
[0050] FIG. 26A illustrates an exemplary mold for forming a
bolster.
[0051] FIG. 26B illustrates an exemplary bolster formed in the mold
of FIG. 26A.
[0052] FIG. 26C illustrates an exemplary cross-section of a bolster
mold and core within the bolster mold.
[0053] FIG. 27A illustrates a cross-section of a bolster in a brake
window region.
[0054] FIG. 27B illustrates a cross-section of a friction shoe
pocket of a bolster.
[0055] FIG. 28 illustrates a core assembly that may be utilized in
conjunction with a mold for forming a bolster.
DETAILED DESCRIPTION
[0056] In the following description of various example structures
according to the invention, reference is made to the accompanying
drawings, which form a part hereof, and in which are shown by way
of illustration various example devices, systems, and environments
in which aspects of the invention may be practiced. It is to be
understood that other specific arrangements of parts, example
devices, systems, and environments may be utilized and structural
and functional modifications may be made without departing from the
scope of the present invention. Also, while the terms "top,"
"bottom," "front," "back," "side," "rear," and the like may be used
in this specification to describe various example features and
elements of the invention, these terms are used herein as a matter
of convenience, e.g., based on the example orientations shown in
the figures or the orientation during typical use. Additionally,
the term "plurality," as used herein, indicates any number greater
than one, either disjunctively or conjunctively, as necessary, up
to an infinite number. Nothing in this specification should be
construed as requiring a specific three dimensional orientation of
structures in order to fall within the scope of this invention.
Also, the reader is advised that the attached drawings are not
necessarily drawn to scale.
[0057] Many of the disadvantages of using the green sand process
discussed above can be overcome, or at least ameliorated, by using
a no-bake, or air-set, casting process. "No bake" and "air-set"
refer to the same type of process and are considered
interchangeable throughout this disclosure. The Association of
American Railroads (AAR) coupler 100, shown in FIG. 1, is an
assembly of parts, all of which are required to interact in a
precise manner for the coupler assembly to operate properly and to
have optimum part life. Operating positions include locked,
unlocked, and lockset. Since coupler parts are often replaced
during the service life of a coupler, the interchange of parts must
maintain the proper interfacing dimensions for proper operation.
Therefore, control of the dimensional characteristics of coupler
parts is important to ensure proper operation.
[0058] The coupler also transmits the longitudinal forces pulling
and pushing a railcar in service operations. These forces can be of
significant magnitude--often many hundreds of thousands of
pounds--and require that the load path of force through the coupler
assembly be precisely controlled. Design loads per the AAR
Specification M-211 reach 650,000 pounds for the knuckle and
900,000 pounds for the coupler body. Uniform loading helps ensure
uniform wear patterns and in turn more uniform load distribution.
Finally, the strength of the coupler and its fatigue life is
important in order to prevent premature failure of parts, which is
directly influenced by dimensional consistency and consequently the
level of uniform load distribution.
[0059] Surface finish or texture of the coupler has a definite
effect in maintaining the required coupler strength and fatigue
life. The no-bake casting process provides better dimensional
control, improved load path for operating forces, more uniform wear
patterns, castings with fewer weld repairs, and improved surface
texture for improved strength and fatigue life compared to the
green sand process.
[0060] In no-bake mold casting, molten metal is poured into a
non-reusable mold made from a mixture of sand, quick-setting resin,
and catalyst, and the mold is held together until solidification
occurs. No-bake sand molding produces a sand mold of considerable
strength, which can be free standing without the need for a
traditional, steel flask and therefore unlimited in size and shape.
The traditional flask is heavy and rigid, which limits green sand
operations by the molding efficiencies that result from the
limitations of metal flasks.
[0061] The no-bake casting process involves the use of
chemically-bonded sand systems. The use of the chemical bonding
agents typically makes the no-bake process somewhat more expensive
than the green sand process. As part of the no-bake casting
process, a resin and catalyst are mixed together. Examples of gas
catalysts used for curing include sodium silicate (CO2), amine,
SO2, and ester cured phenolic systems. Examples of a liquid
catalyst can include the air-set system. Through a chemical
reaction, the resin hardens into a very strong bond. Sometimes an
accelerator may be added to speed the hardening process. The
no-bake casting process can also be less sensitive to the air
temperature and moisture as compared to green sand operations.
[0062] The no-bake process uses graded kiln dried sand, which is
mechanically mixed with a resin (or binder) to bind the sand
together. Most binder systems are variations on a few basic
chemicals, such as furan, phenolic urethane, and sodium silicate.
Usually the no-bake method of forming the mold is accomplished at
room temperature. Therefore, unlike the green sand process that
requires curing the sand, water, and clay mixture at elevated
temperature, the no-bake process derives its name by eliminating
the baking process required when using the green sand method.
[0063] A chemical hardener is then added to the sand mix, which
reacts with the binder and begins to set the sand into a solid
form. At this point, the fluid sand is poured into a mold around a
pattern or multiple patterns. Once poured, the sand is left to set.
The binder causes the sand particles to bond together forming a
very stable and accurate shape for the cavity that will be used to
pour the final casting. Setting time depends on the type of
hardener used. The sand sets into a solid block from which the
pattern equipment is drawn. Cores are then added to the mold and
the mold is closed and ready for casting.
[0064] Refractory coatings can be applied to resin-bonded cores and
molds. These coatings are sometimes referred to as a wash. Coatings
can be used for several reasons, including: (1) to improve surface
finish; (2) to control the heat transfer characteristics and
microstructure in the steel casting; (3) improve venting of a core;
and (4) to prevent certain types of defects in the casting.
[0065] In contrast to the green sand process, as discussed, this
hardened mold does not require the use of a traditional fabricated
metal flask. Flask size limitations can be a detriment for the
green sand process by preventing the manufacturer from varying the
number of multiple parts in a single flask or by limiting the size
of a single casting that can fit in a given flask because of the
pre-existing fabricated metal flask sizes. Heavy, steel flasks
cannot be cost-effectively modified to accommodate new customer
parts sizes, if different than presently-used flasks. Purchasing
various single flasks can become costly. Typical sizes can range up
to four feet wide, six feet long, and depths from 18-24 inches deep
for both cope and drag. Accordingly, an air-set mold is well-suited
to larger, heavier castings as the mold strength allows casting of
greater weights of metal. A solid sand structure allows a mold to
be formed of various sizes, producing the best yields available for
each solid sand structure. Also, sand use for a mold can be kept to
a minimum without compromising quality so production costs are
reduced. The chemical bonding of the sand particles for the no-bake
process provides for a better surface condition compared to the
green sand process where water and clay are used as the bonding
agents.
[0066] State-of-the-art foundry equipment on modem-day air-set
lines allows up to 100% reclamation of the primary raw material,
sand. This reclaimed sand is broken down, cooled and filtered, to
be used repeatedly. To maintain sand quality and mold strength, the
reclaimed sand is mixed with new sand at a ratio of 75%:25%. This
process keeps production costs to a minimum without compromising
quality. Note that the new sand to reclaim sand ratio varies
depending on the typical casting geometry and weight; the ratio of
75%:25% is only a typical value. Industry values range from 95%:5%
to 40%:60%.
[0067] Some characteristics and advantages that distinguish the
no-bake mold process from that of other sand molding processes,
such as the green sand process, include: molds are chemically cured
at room temperature; the process produces precise and repeatable
dimensions; and finishing labor costs and scrap are reduced while
obtaining high casting yields.
[0068] As a measure of the dimensional stability of the no-bake
process compared to the green sand process, the Steel Founders'
Society of America publishes values for dimensional tolerances in
Supplement 3 of their Steel Casting Handbook. Base tolerances for
castings made by the no-bake process are listed as plus or minus
0.020 inches compared to plus or minus 0.030 inches for castings
made by the green sand process. While these are both small
dimensions, the ability to have tolerances with a reduction in
range of one third is significant when it comes to assuring proper
load paths and operational characteristics of coupler assemblies as
explained above. The tolerances of the coupler parts depends on
casting weight and dimension as will be discussed below, so the
tolerance achievable with the no-bake process when compared to the
green sand process varies across different parts and dimensions of
the railroad coupler. In all cases, however, the tolerances
achievable with the no-bake process are smaller than the tolerances
required by the AAR Specification M-211.
[0069] The no-bake process also allows for smaller draft angles
than the green sand process. A draft angle refers to the small
slope included for the vertical surfaces of the casting pattern, as
oriented in the mold box, so that the pattern can be drawn away
from the mold. The draft angle must be included both in the top of
the cope and the drag portions of the patterns. Where the green
sand process requires a draft angle of 1.5 degrees or more for
typical shapes, the no-bake process requires only a 1.0 degree
draft angle. Where the green sand (manual) process requires a draft
angle of 2.0 degrees or more for deep pockets, the no-bake process
requires only a 1.5 degree draft angle for deep pockets. The
required draft angle of the green sand process results in a
significantly greater deviation from the nominal dimension at cast
points that are farther from the pointing line of the entire
casting than a casting produced by the no-bake process. Smaller
draft angles can promote better part loading and increase bearing
area. This small difference is significant when accounting for the
interfacing of the complicated shapes that make up the parts in a
coupler assembly, and when combined with the reduced tolerance
range.
[0070] FIG. 2 displays the major parts of a railroad coupler
assembly 200, including a body 204, a knuckle 208, a knuckle pin
212, a thrower 216, a lock 220, and a locklift 224. Of these major
parts, the knuckle 208 and the body 204 are usually produced using
the green sand casting process. Due to their small sizes, the lock
220, the thrower 216, and the locklift 224 assembly can be produced
by various methods. The thrower 216 can also be produced by the
green sand casting process or by the forging process. The present
disclosure contemplates forming the body and knuckle utilizing the
no-bake or air-casting process for all of the above-discussed
reasons.
[0071] During the locking and unlocking operations, the knuckle 208
rotates about the axis of the knuckle pin 212. The knuckle tail 228
must pass under the knuckle shelf seat 232 on the lock 220 during
the locking and unlocking operations. The lock must also move
downward and upward in a lock chamber 236 of the body 204 during
the locking and unlocking operations. Also, during lockset, the
lock 220 must move upward in the lock chamber 236 of the body such
that a lockset seat 240 on a lock leg 244 sits with precision on a
leg-lock seat 248 of the thrower 216.
[0072] The parts of the coupler assembly 200 should have accurate
dimensional characteristics to ensure successful operation. The
better the dimensional characteristics, the smoother the operation.
The larger the dimensional variation, the rougher the operation,
and if large enough, the parts will jam and the coupler may become
inoperable. Smooth surface finishes also aid in successful
operation, which will be discussed in more detail below. If the
tolerances of the parts are too large, interference can occur when
the knuckle 208 is rotating relative to the body 204 and the lock
220. This interference can result in sticking conditions making
difficult the operations of locking and unlocking the coupler. In
some cases, extremes of tolerances in relative part dimensions have
resulted in coupler inoperability and/or an inability to
interchange parts.
[0073] The coupler load path for draft (pull) and buff (push)
forces generated during train operations is also dependent on
precise control of dimensional tolerances of the coupler parts. For
draft forces, the coupler is designed to receive the pulling forces
at the pulling faces 252 of the knuckles 208 (shown in FIGS. 14A,
14B) between two mating couplers. This pulling force is transmitted
through the knuckle 208 to pulling lugs 258 at the knuckle tail
228. At that point, the pulling force is transmitted by the pulling
lugs 278 of the coupler body 204 as best seen in FIG. 4. Finally,
the pulling forces are transmitted through the coupler body 204
through a key slot 279 or the butt 280 of the coupler 204 to the
draft system of the freight car and on through the car body to the
other end of the car. If the tolerances of the coupler parts do not
provide for the load path as described above, the pulling forces
can be transmitted through the knuckle 208 to pin protector bosses
256 of the coupler body 204, to the knuckle pin 212, and/or
unevenly between the top and bottom pulling lugs 258, 278, which
results in uneven and expedited wear on these parts. Additionally,
loads can be transmitted unevenly between mating coupler parts
resulting in unequal loading. When the intended load path changes
or there is unequal loading between the top and bottom pulling lugs
278, premature failure or reduced part life can occur in the
coupler body 204, the knuckle pin 212, and/or the knuckle 208.
[0074] Buff forces are maxed during switching operations when
freight cars impact each other. The coupler assembly is designed to
react to the buff forces at the buffing shoulders 260 of the
coupler body 204 and at the buffing shoulders 261 of the knuckle
208. If tolerances of the coupler parts are not controlled
accurately, buffing forces can be transmitted at the pin protector
bosses 256, 286 (see FIGS. 6, 15A, 15B), the knuckle pin 212, or
unequally between the top and bottom buffing shoulders 260, 261 of
the body 204 and the knuckle 208, respectively. Damage can thus
occur, and result in the premature failure of the knuckle 208, the
knuckle pin 212, and/or the coupler body 204. Therefore, it is
advantageous to minimize dimensional tolerances so that proper load
paths are maintained throughout the coupler assembly. These proper
load paths promote uniform wear patterns.
[0075] While the green sand casting process has been used
successfully for many years to produce coupler parts, the no-bake
casting process results in a better surface finish and therefore
can reduce cracking and associated issues that are created when
surface conditions are less than optimal. The normally higher costs
associated with the no-bake process have been minimized or offset
by: reducing casting finishing (gauging) time, spending less
capital investment on items such as special flasks that are not
required, requiring less casting defect weld repair, reducing
processing time, and yielding more dimensionally-consistent and
higher-quality parts with improved part life.
[0076] The creation of good surface finish or texture has been
established as a priority by the American Association of Railroads
(AAR) through action taken by their Coupling Systems and Truck
Castings Committee. In the past, certain surface conditions, such
as sand inclusions and seams, have been found in critical areas of
coupler parts. In some cases, surface conditions can result in
cracks which result in reduced fatigue life of the coupler or
knuckle. For instance, a radius area 281 between the coupler horn
264 and the shank 268 has received the attention of the Federal
Railroad Administration. See Code of Federal Regulations, Title 49,
215.123. Cracks in this area now require replacement of the
coupler. Furthermore, a smoother surface achievable through use of
the no-bake process adds to tighter tolerances, which will be
further discussed below. A part made with tighter tolerances has
better fit and functions better with their mating parts, which also
increases fatigue life.
[0077] In the effort to make sure surface conditions do not result
in premature coupler failure, the Coupling Systems and Truck
Castings Committee has included specific surface finish criteria as
a part of the AAR Specification M-211. Foundry and Product Approval
Requirements for the Manufacture of Couplers, Coupler Yokes,
Knuckles, Follower Blocks, and Coupler Parts, Specification M-211,
Last Adopted October 2009. Section 11.2 of the AAR Specification
M-211 reviews specific surface acceptance levels, which are defined
utilizing Steel Castings Research and Trade Association (SCRATA)
Comparators for the Definition of Surface Quality of Steel
Castings. The SCRATA comparators are nine categories, each with
five quality levels, decreasing from 1 to 5, in which level 1 is
the highest quality and level 5 is the poorest:
[0078] A. Surface Roughness--the natural surface of the casting
after shot blasting.
[0079] B. Surface Inclusions--non-metallic material trapped on the
casting surface.
[0080] C. Gas Porosity--indications of gas at the casting
surface.
[0081] D. Laps and Cold Shuts--surface irregularities giving a
wrinkled appearance.
[0082] E. Scabs--slightly raised surface irregularities.
[0083] F. Chaplets--indications of chaplets or internal chills.
[0084] G. Surface Finish--Thermal Dressing--surface remaining after
using oxy-gas or air-carbon arc processes for metal removal.
[0085] H. Surface Finish--Mechanical Dressing--surface remaining
after using a mechanical means of dressing a cast surface or a
previously thermally dressed surface.
[0086] J. Welds--indications of welds fully or partially removed by
thermal or mechanical dressing.
[0087] The following Tables 1 and 2 are comparison charts
respectively for the coupler 204 and knuckle 208 that show the
minimum surface conditions required by the AAR Specification M-211
and the improved surface conditions achievable using the no-bake
process. Fig. A.11 referred to in Table 1 is a three-page figures
shown in Appendix A of the AAR Specification M-211 in which the
shaded areas are the critical areas and the non-shaded areas are
the non-critical areas. One of ordinary skill in railroad couplers
would know to refer to Fig. A.11 to determine which areas are
currently considered critical as distinguished from non-critical
areas by the AAR. In general, however, the critical areas are those
areas that take on more load force with regards to the draft and
buff forces discussed above and also those areas that interface or
wear with other parts.
TABLE-US-00001 TABLE 1 COUPLER BODY Critical Area With Non-Critical
Area With Category (FIG. A.11) No-Bake (FIG. A.11) No-Bake A)
Surface A3 Al A3 Al Roughness B) Surface B2 B2 B4 B3 Inclusions C)
Gas C2 C2 C3 C2 Porosity D) Laps Dl Dl D4 Dl E) Scabs E2 El E2 El
F) Chaplets F2 Fl F4 Fl G) Thermal G2 Gl G3 Gl Dressing H)
Mechanical H3 Hl H4 Hl Dressing J) Welds J2 Jl J3 Jl
[0088] The data in Table 1 was obtained through visual comparison
of a number of coupler bodies 204 produced by the no-bake process
with SCRATA plates representing 1 through 5 in each of the above
categories. With reference to categories D through J in Table 1, no
laps, scabs, chaplets, or welding were observed. Also, surface
conditions of Thermal Dressing and Mechanical Dressing do not
depend on the casting process, but result from an individual
performing surface conditioning after the casting process has been
completed. The frequency with which Thermal and Mechanical Dressing
operations must be performed is, however, a result of the casting
process, so a comparison with the green sand process is still
helpful. As indicated, the surface quality of a coupler produced by
the no-bake process is superior in just about every category, and
at least equal to the minimum requirements under the AAR
Specification M-211.
TABLE-US-00002 TABLE 2 KNUCKLE Critical Area With Non-Critical Area
With Category (FIG. A.11) No-Bake (FIG. A.11) No-Bake A) Surface A3
A1 A3 A1 Roughness B) Surface B2 B2 B4 B3 Inclusions C) Gas C2 C2
C3 C2 Porosity D) Laps Dl Dl D4 Dl E) Scabs E2 El E2 El F) Chaplets
F2 Fl F4 Fl G) Thermal G2 Gl G3 Gl Dressing H) Mechanical H3 H2 H4
H2 Dressing J) Welds J2 Jl J3 Jl
[0089] The data in Table 2 was obtained through visual comparison
of a number of knuckles 208 produced by the no-bake process with
SCRATA plates representing 1 through 5 in each of the above
categories. With reference to categories D through J in Table 1, no
laps, scabs, chaplets, or welding were observed. As with the
coupler, the surface quality of the knuckles was superior in almost
every category, or at least equal to the minimum requirements under
the AAR Specification M-211.
[0090] The no-bake process may be used to manufacture the coupler
body 204, the knuckle 208, the lock 220, the thrower 216, and the
locklift 224 in such a way that better (smaller) tolerances for
various relative dimensions are achieved due to the no-bake
process. As discussed above, tolerances for the no-bake process is
plus or minus 0.020 inches and the draft angle is about one (1.0)
degree or less for typical features. Actual tolerances, however,
vary with weight and dimension of the casted parts according to the
Steel Founder's Society of America (SFSA) Tolerance Tables. Table 3
below shows the T3 tolerances used for the no-bake process used by
the manufacturers. For comparison, Table 4 shows the T5 tolerances
that correspond to the green sand process typical of conventional
railroad couplers.
TABLE-US-00003 TABLE 3 NO-BAKE TOLERANCES Tolerances (.+-.inches)
for Tolerance Grade T3 CASTING WEIGHT - LBS L* 2 5 10 20 50 75 100
150 200 250 500 750 1000 1250 1500 2000 3000 4000 5000 .5 .024 .026
.028 .031 .036 .039 .041 .044 .047 .049 .057 .063 .068 .071 .075
.081 .090 .097 .103 1.0 .028 .031 .033 .036 .041 .043 .045 .049
.051 .054 .062 .068 .072 .076 .079 .085 .094 .101 .108 2.0 .034
.036 .039 .041 .046 .049 .051 .054 .057 .059 .068 .073 .078 .082
.085 .091 .100 .107 .113 4.0 .041 .044 .046 .049 .054 .056 .058
.062 .064 .067 .075 .081 .085 .089 .092 .098 .107 .114 .121 6.0
.046 .049 .051 .054 .059 .061 .063 .067 .069 .072 .080 .086 .090
.094 .097 .103 .112 .120 .126 8.0 .050 .053 .055 .058 .063 .065
.067 .071 .073 .076 .084 .090 .094 .098 .101 .107 .116 .124 .130
10.0 .054 .056 .058 .061 .066 .069 .071 .074 .077 .079 .087 .093
.098 .101 .105 .111 .120 .127 .133 15.0 .061 .063 .065 .068 .073
.o76 .078 .081 .084 .086 .094 .100 .105 .108 .112 .117 .127 .134
.140 20.0 .066 .069 .071 .074 .078 .081 .083 .087 .089 .091 .100
.105 .110 .114 .117 .123 .132 .139 .145 30.0 .075 .077 .079 .082
.087 .090 .092 .095 .098 .100 .108 .114 .119 .123 .126 .132 .141
.148 .154 40.0 .082 .084 .086 .089 .094 .097 .099 .102 .105 .107
.115 .121 .126 .129 .133 .139 .148 .155 .161 50.0 .088 .090 .092
.095 .100 .103 .105 .108 .111 .113 .121 .127 .131 .135 .139 .144
.154 .161 .167 60.0 .093 .095 .097 .100 .105 .108 .110 .113 .116
.118 .126 .132 .137 .140 .144 .150 .159 .166 .172 *Dimension Length
in Inches
TABLE-US-00004 TABLE 4 GREEN SAND TOLERANCES Tolerances
(.+-.inches) for Tolerance Grade T5 CASTING WEIGHT - LBS L* 2 5 10
20 50 75 100 150 200 250 500 750 1000 1250 1500 2000 3000 4000 5000
.5 .038 .045 .052 .061 .076 .085 .092 .103 .111 .118 .145 .163 .178
.190 .201 .219 .248 1.0 .042 .049 .057 .066 .081 .090 .096 .107
.116 .123 .149 .167 .182 .194 .205 .224 .253 .276 .296 2.0 .048
.055 .062 .071 .087 .095 .102 .113 .121 .129 .155 .173 .188 .200
.211 .229 .259 .282 .301 4.0 .055 .062 .070 .079 .094 .103 .109
.120 .129 .136 .162 .180 .195 .207 .218 .237 .266 .289 .309 6.0
.060 .068 .075 .084 .099 .108 .114 .125 .134 .141 .167 .186 .200
.213 .223 .242 .271 .294 .314 8.0 .064 .072 .079 .088 .103 .112
.118 .129 .138 .145 .171 .190 .204 .217 .227 .246 .275 .298 .318
10.0 .068 .075 .082 .091 .107 .115 .122 .133 .141 .148 .175 .193
.208 .220 .231 .249 .278 .302 .321 15.0 .075 .082 .089 .098 .113
.122 .129 .140 .148 .155 .181 .200 .215 .227 .238 .256 .285 .308
.328 20.0 .080 .087 .094 .103 .119 .127 .134 .145 .154 .161 .187
.205 .220 .232 .243 .262 .291 .314 .334 30.0 .089 .096 .103 .112
.128 .136 .143 .154 .162 .169 .196 .214 .229 .241 .252 .270 .299
.323 .342 40.0 .096 .103 .110 .119 .135 .143 .150 .161 .169 .176
.203 .221 .236 .248 .259 .277 .306 .330 .349 50.0 .102 .109 .116
.125 .140 .149 .156 .166 .175 .182 .208 .227 .241 .254 .265 .283
.312 .335 .355 60.0 .107 .114 .121 .130 .145 .154 .161 .172 .180
.187 .214 .232 .247 .259 .270 .288 .317 .341 .360 *Dimension Length
in Inches
[0091] By way of a simple example, suppose a casted part is made by
both the no-bake and the green sand processes, both that weigh
about 100 pounds. Suppose a dimension of interest is about 2.0
inches. The tolerance achievable by the no-bake process is about
0.051 inches while the tolerance of the part made by the green sand
process is about 0.102, which is about twice that achievable by the
no-bake process.
[0092] FIG. 3 is a top perspective view of the coupler body 204 of
FIG. 2. FIG. 4 illustrates a side, cross section view along line
4-4 of the coupler body 204 of FIG. 2, including coupler pin holes
272 through which the knuckle pin 212 is inserted, and pulling lugs
278 of the coupler body 204 that correspond to the pulling lugs 258
of the knuckle 208. The balanced loading achievable through the
no-bake process results in more even wearing at the pulling lugs
278 of the coupler body, thus extending the fatigue life of the
coupler body. The tolerances achievable, discussed below, using the
no-bake process for dimensions define the location of the body
pulling lugs 278 relative to the coupler pin holes 272.
[0093] FIGS. 5A and 5B are two perspective views of the coupler
body 204 of FIG. 2, showing the location of the coupler buffing
shoulders 260 relative to the coupler pin hole 272 achievable with
the no-bake process. FIG. 6 is a perspective view of the railroad
coupler of FIG. 2, showing the location of the pin protector bosses
256 relative to the coupler pin hole 272 achievable with the
no-bake process.
[0094] FIG. 7 is a side perspective view of the coupler body 204 of
FIG. 2. FIG. 8 is a cross section view alone line 8-8 of the
coupler body of FIG. 7. FIG. 9 is a side perspective view of the
coupler body 204 of FIG. 2. FIG. 10 is a cross section view alone
line 10-10 of the coupler body 204 of FIG. 9, thus showing the
cross section from the other side of the coupler body 204 from the
line 8-8 view shown in FIG. 8. The dimension of 31h inches in both
FIGS. 8 and 10 is the approximate distance between the center of
the coupler pin holes 272 and the coupler buffing shoulders 260,
achievable with the no-bake process. Based on an approximate weight
of 378 pounds, the tolerance of this dimension is approximately
plus or minus 0.075 inches using Table 3. The tolerance that
results from the green sand process results in about plus or minus
0.162 inches using Table 4. Accordingly, the tolerance achievable
with the no-bake process is less than half that achievable using
the green sand process.
[0095] Because one must round the weight up to 500 pounds and the
length up to 4 inches in the example of FIG. 8 to use the AAR
tables, the cited tolerances are but estimates and probably
somewhat greater than reality in this case. For instance, the 31/2
inch dimension yields a tolerance closer to plus or minus 0.070
inches. Also, because of the draft angles discussed above, and due
to angled surfaces designed with some features, the dimension
changes some throughout the measured features. Accordingly, the
dimensions themselves vary to some degree and showing a specific
length, or reciting a specific tolerance, should not be taken as
exact values but as close approximations. Therefore, the difference
between approximate tolerances between the no-bake and the green
sand processes more accurately describes the improvement of using
the no-bake process in terms of dimensional tolerances.
[0096] FIGS. 8 and 10 also show additional dimensions: 11/2 inches
between the center of the coupler pin holes 272 and the pin
protector bosses 256 and 5% inches between the center of the
coupler pin holes 272 and the pulling lugs 278 of the coupler body
204. Using the same 500 pound estimate, and rounding to 2 inches,
the 11/2 inch dimension in Table 3 indicates a tolerance of about
plus or minus 0.068 inches, although in reality it is probably
somewhat less, such as plus or minus 0.062 inches for the reasons
discussed above. The corresponding tolerance from Table 4, using
the green sand process, is approximately plus or minus 0.155
inches, which is more than twice that achievable from the no-bake
process.
[0097] Using the same 500 pound estimate, and rounding to 6 inches,
the 5% inch dimension in Table 3 indicates a tolerance of about
plus or minus 0.080 inches. Because of rounding, this tolerance is
probably closer to plus or minus 0.075 inches. The corresponding
tolerance from Table 4 using the green sand process is about plus
or minus 0.167 inches, again about twice that which is achievable
using the no-bake process.
[0098] FIG. 11 is a top view of the coupler knuckle of FIG. 2. FIG.
12 is the cross section view along line 12-12 of the knuckle of
FIG. 11. FIGS. 11 and 12 show the knuckle pin hole 282 in relation
to the knuckle buffing shoulders 261 and to the knuckle pulling
lugs 258.
[0099] FIGS. 13A and 13B are two perspective views of the knuckle
of the railroad coupler of FIG. 11, showing the location of the
knuckle pulling lugs 258 relative to the knuckle pin hole 282 when
formed by the no-bake process. FIGS. 14A and 14B are two
perspective views of the knuckle of the railroad coupler of FIG.
11, showing the location of the knuckle buffing shoulders 261
relative to the knuckle pin hole 282 when formed by the no-bake
process. FIGS. 15A and 15B are two perspective views of the knuckle
of the railroad coupler of FIG. 11, showing the location of the
knuckle pin protector bosses 286 relative to the knuckle pin hole
282 when formed by the no-bake process.
[0100] FIG. 16 is a top view of the coupler knuckle of FIG. 2,
indicating the approximate dimension between the center of the
knuckle pin hole 282 and the knuckle buffing shoulder 261 as about
31/2 inches; between the center of the knuckle pin hole 282 and the
knuckle pulling lug 258 as about 57/8 inches; and between the
center of the pin hole 282 and the pin protector bosses 286 as
about 15/8 inches. With an approximate weight of the knuckle of
about 86 pounds, the 31/2 inch dimension would have a tolerance of
about plus or minus 0.056 inches using the no-bake process compared
to about plus or minus 0.103 inches for the green sand process. (In
this case, the rounding causes the cited tolerances to be somewhat
less than reality, but again these are close approximations.) The
relative tolerances again indicate a nearly two-fold improvement in
tolerance when using the no-bake process.
[0101] The 57/8 inch dimension between the knuckle pulling lug 258
and the knuckle pin hole 282 results in a tolerance of about plus
or minus 0.061 inches for the no-bake process compared to about
plus or minus 0.108 inches for the green sand process, not quite a
two-fold improvement. The 15/8 inch dimension between the knuckle
pin hole 282 and the pin protector bosses 286 results in a
tolerance of about plus or minus 0.049 inches for the no-bake
process compared to about plus or minus 0.095 inches for the green
sand process, again about a two-fold improvement.
[0102] FIG. 17 is a bottom view of the coupler knuckle of FIG. 2,
indicating the approximate dimension between the center of the
knuckle pin hole 282 and the knuckle buffing shoulder 261 as about
31/2 inches; between the center of the knuckle pin hole 282 and the
knuckle pulling lug 258 as about 5% inches; and between the knuckle
pin hole 282 and the pin protector bosses 286 of about 15/8 inches.
The only dimension that differs from those shown in FIG. 16 is the
5% inch dimension between the knuckle pin hole 282 and the knuckle
pulling lug 258, which still results in a tolerance of about plus
or minus 0.061 inches for the no-bake process compared to about
plus or minus 0.108 for the green sand process, not a quite a
two-fold improvement.
[0103] According to some aspects of the disclosure, the no-bake
process can be used to manufacture other railcar components such
as, e.g., side frames and bolsters.
[0104] FIG. 18A illustrates a perspective view of a side frame 1100
of a railway car truck. The railway car may correspond to a freight
car, such as those utilized in the United States for carrying cargo
in excess of 220,000 lbs. Gross Rail Load. The side frame 1100
includes bolster opening 1110 and a pair of pedestals 1105.
[0105] The bolster opening 1110 is defined by a pair of side frame
columns 1120, a compression member 1125, and a spring seat 1127.
The bolster opening 1110 is sized to receive an outboard end
section 1705 (FIG. 24) of a bolster 1700 (FIG. 24). A group of
springs (not shown) is positioned between the outboard end sections
1705 of the bolster 1700 and the spring seat 1127 and resiliently
couple the bolster 1700 to the side frame 1100.
[0106] A pair of wear plates 1135 are positioned between shoe
pockets 1710 of the outboard end sections 1705 of the bolster 1700
and the side frame columns 1120. A single exemplary wear plate 1135
is illustrated in FIG. 18A in a detached mode for illustrative
purposes. The wear plates 1135 and friction wedges (not shown)
function as shock absorbers that prevent sustained oscillation
between the side frame 1100 and the bolster 1700. Each wear plate
1135 may be made of metal. The wear plates 1135 are configured to
be attached to a side of the side frame column 1120 that faces the
bolster 1700 (i.e., the bolster side of the side frame column
1120). The wear plates 1135 may be attached via fasteners, such as
a bolt or bolt and nut assembly that enables removal of the wear
plates 1135.
[0107] In operation, pressure is produced against the wear plates
1135 by the movement of the bolster 1700 within the bolster opening
1110. In known side frames, the side frame columns 1120 tend to
elastically deform under these wedge pressures. As a result, the
fasteners securing the wear plates 1135 to the side frame columns
1120 become loose. To overcome these problems, an embodiment of the
side frame 1100 of the application includes column stiffeners 1205
(FIG. 19) in the form of ribs 1205 positioned on the side frame
columns 1120.
[0108] FIGS. 19A and 19B illustrate an inner surface 1130 of an
exemplary side frame column 1120 including a pair of column
stiffeners 1205. The column stiffeners 1205 are positioned on the
inner surface of the side frame column 1120 and extend between
sides of the side frame 1100. For example, the column stiffeners
1205 extend between the drag and cope portions 1102 and 1103 of the
side frame 1100. The column stiffeners 1205 may be centered within
openings 1210 formed in the side frame columns 1120 for the
fasteners described above. The thickness T 1203 of the side frame
columns 1120 in the region of the column stiffeners 1205 may be
about 1.125'', as opposed to 0.625'' thick as used in known side
frame columns, which do not include column stiffeners. The column
stiffeners 1205 provide increased support to the side frame columns
1120 to prevent the side frame columns 1120 from deforming under
the pressures described above. Moreover, the column stiffeners 1205
increase the length over which the fasteners are tensioned. In
other words, the tensioned portion of the fastener is longer than
that of known side frames. This enables the fastener to have a
longer stretch during fastening, creating a greater clamp force,
extending the fatigue life of the bolted joint.
[0109] Returning to FIG. 18A, each pedestal 1105 defines a pedestal
jaw 1140 into which a wheel assembly from a wheel set of the truck
is mounted. In particular, each pedestal jaw 1140 includes a
pedestal roof 1116, an outboard vertical jaw 1117, an inboard
vertical jaw 1118, and inboard and outboard contact surfaces 1115
known as thrust lugs that are in direct contact with complementary
surfaces of the adapter and wheel assemblies. The contact surfaces
1115 determine the alignment of the wheel assemblies within the
pedestal jaws 1140. To provide correct alignment, the contact
surfaces 1115 are cleaned during a finishing process to remove
imperfections left over from the casting process.
[0110] FIG. 20 illustrates an exemplary pedestal jaw 1140 of the
side frame 1100 after the side frame has been removed from a mold
1500 (FIG. 22A), but prior to finishing. In this state, the contact
surfaces 1115 are not planar. Rather, the contact surfaces 1115 are
tapered by a draft angle amount D 1305 that corresponds to a draft
angle of a mold for manufacturing the side frame 1100, as described
below. The draft angle D 1305 may be about 1.degree. or less, which
is less than draft angles of known cast side frames, which may be
3.degree. or more. In one embodiment, the draft angle is about
3/4.degree.. Other portions may have smaller draft angles as well.
For example, the pedestal roof 1116 may have a draft angle of less
than about 3/4.degree.. Jaw 1117 and 1118 draft angles may be less
than about 3/4.degree.. The smaller the draft angle, the less
finishing required to form the planar surface. Accordingly, the
contact surfaces 1115 of the side frame 1100 require less finishing
time than those of known cast side frames, because there are no
core seams in the pedestal area.
[0111] FIG. 21 illustrates exemplary operations for manufacturing
the side frame 1100 described above. The operations are better
understood with reference to FIGS. 22 and 23.
[0112] At block 1400, a mold 1500 for manufacturing the side frame
1100 may be formed. Referring to FIG. 22A, the mold 1500 may
include a drag portion 1505 and a cope portion 1510. The drag
portion 1505 of the mold 1500 includes a cavity formed in the shape
of the drag side 1102 of the side frame 1100. The cope portion 1510
includes a cavity formed in the shape of the cope side 1103 of the
side frame 1100.
[0113] The respective portions may be formed by first providing
first and second patterns (not shown) that define an outside
perimeter of the drag side 1102 and cope side 1103, respectively,
of the side frame 1100. The patterns may partially define one or
more feed paths 1540 for distribution of molten material within the
mold 1500. The one or more feed paths 1540 are advantageously
positioned in a center region of the mold 1500, which results in an
even distribution of the molten material throughout the mold 1500.
For example, the feed paths 1540 may be positioned in an area of
the mold 1500 that defines the bolster opening 1110 of the side
frame 1100.
[0114] The patterns (not shown) also define a pedestal jaw portion
1520 that defines the pedestal jaw 1140 of the side frame 1100. In
known forming methods, the patterns do not define the details of
the pedestal jaw 1140. Instead, a core having the general shape of
the inner area of the pedestal jaw 1140 is inserted into the mold
prior to casting. The cores tend to move during the casting process
resulting in inaccurate dimensions, large core seams that have to
be removed.
[0115] The pattern above and a group of risers 1535 may then be
inserted into respective flasks 1525 and 1526 for holding a molding
material 1527. The risers 1535 may inserted in the cope portion
1510. The risers 1535 correspond to hollow cylindrical structures
into which molten material fills during casting operations. The
risers 1535 are positioned at areas of the mold that correspond to
thicker areas of the side frame that cool more slowly than other
areas of the side frame. The risers 1535 function as reservoirs of
molten material that compensate for contraction that occurs in the
molten material as the molten material cools, and thus prevent
shrinkage, or hot tearing of the cast side frame in the thicker
areas that might otherwise occur. Exemplary risers 1550 for the
side frame 1100 are illustrated in FIG. 22B.
[0116] In known casting operations, the precise locations requiring
accurate feeding are not generally known. Therefore, relatively
large risers (e.g., 6 inches or more) that cover larger areas are
utilized. By contrast, in the disclosed embodiments, the precise
locations requiring accurate feeding have been determined via
various analytical techniques, as described below. As a result,
risers 1435 that are considerably smaller in diameter (e.g., about
4 inches or smaller) may be utilized, which improve the yield of
the casting. The riser heights may be between about 4 and 6 inches.
In one embodiment, less than 10% of the gross weight of the casting
material poured into the mold ends up in the risers. This leads to
more efficient use of the casting material.
[0117] The flasks 1525 and 1527 are generally sized to follow the
shape of the pattern, which is different than flasks utilized in
known casting operations. These flasks are generally sized to
accommodate the largest cast item in a casting operation. For
example, in known casting operations, the flask may be sized to
accommodate a bolster or an even larger item. By contrast, as
illustrated in FIG. 22A, the flasks 1525 and 1527 according to
disclosed embodiments have a shape that follows the general shape
of the item being cast. For example, the flasks 1525 and 1526 in
FIG. 22A have the general shape of the side frame 1100. The maximum
distance L 1530 between an edge of the respective flasks 1525 and
1527 and a closest portion of the pattern to the edge of the flask
may be less than 2 inches. Such flasks 1525 and 1527 minimize the
amount of molding sand needed for forming the mold 1500. For
example, the ratio of the molding sand to the molten material
poured into the mold in subsequent operations may be less than 5:1.
This is an important consideration given that the mold 1500 may
only be used a single time when casting.
[0118] A molding material 1527 is then packed into the flask 1525
and over and around the pattern until the flasks 1525 are filled.
The molding material 1527 is then screeded or leveled off with the
flask, and then cured to harden the molding material 1527. The
patterns are removed once the molding material 1527 cures.
[0119] The molding material 1527 may correspond to a chemical or
resin binder material such as phenolic urethane, rather than
green-sand products utilized in known casting operations. The
chemical binder material product enables forming molds with greater
precision and finer details.
[0120] To facilitate removal of the patterns (not shown), sides of
the respective cavities in the drag and cope portions of the mold
1500 are formed with a draft angle D 1515 of 1.degree.,
3/4.degree., or even less to prevent damage to the mold 1500 when
removing the pattern. The draft angle of the mold forms a
corresponding draft angle D 1305 along sides of the side frame
1100. The draft angle formed on most surfaces of the side frame
1100 may be of little consequence. However, in certain regions,
such as the contact surfaces 1115 of the pedestal jaws 1140 draft
angles of greater than 1.degree. may not be tolerated. The chemical
or resin binder material such as phenolic urethane facilitates
forming sides with draft angles of 1.degree. or less versus
green-sand products, for which draft angles of 3.degree. or greater
are required to prevent damaging the mold. In the pedestal jaws
1140 green-sand products require additional cores to create these
features to maintain flatness requirements. These cores create
large seams and dimensional variation among castings.
[0121] At block 1405, a core assembly 1545 that defines the
interior region of the side frame 1100 is formed. Referring to FIG.
23, the core assembly 1545 may include one or more portions. For
example, the core assembly 1545 may include a pair of pedestal
& window cores 1605, a bolster core 1610, a spring seat core
1615, a lower tension member core 1620, and a pair of inner jaw
cores 1625. Each pedestal core 1605 defines an interior of a
pedestal of a side frame from an end 1101 (FIG. 18A) of the side
frame to an inside end of the side frame column 1120 (FIG. 18A) of
the side frame. The pedestal core 1605 may define one or more core
prints that form openings in the cast side frame. For example, a
first set of core prints 1630 may form openings at the ends of the
pedestal that correspond to ends of the side frame. A second core
print 1632 may form openings in the diagonal tension members 1141
(FIG. 18A) of the side frame. A third core print 1634 may form
column windows 1142 (FIG. 18A) in the side frame.
[0122] For example, a mold that includes a cope and drag portion
that defines a given core may be formed. Molding sand may be
inserted into the core box and cured. The core box is then removed
to reveal the cured core. The respective cores may be formed
individually, integrally, or in some combination thereof. The
respective cores may be-formed as two portions. For example, each
core (i.e., pedestal core, bolster core, etc.) may include a cope
portion and a drag portion formed separately in separate core boxes
(i.e., a cope mold and drag mold). After curing, the formed
portions may be attached. For example, the cope and drag portions
of a given core may be glued together to form the core.
[0123] At block 1410, the core assembly 1545 is inserted in the
mold and the side frame 1100 is cast. For example, the core
assembly 1545 may be inserted into the drag portion 1505 of the
mold 1500. The cope portion 1510 may be placed over the drag
portion 1505 and secured to the drag portion 1505 via clamps,
straps, and the like. In this regard, locating features may be
formed in the drag portion 1505 and the cope portion 1510 to ensure
precise alignment of the respective portions.
[0124] After securing the respective portions, molten material,
such as molten steel, is poured into the mold 1500 via an opening
in the cope portion 1510. The molten material then flows through
the gating 1540 and throughout the mold 1500 in the space between
the mold 1500 and the core assembly 1545.
[0125] At block 1415, the mold 1500 is removed from the side frame
1100 and the side frame 1100 is finished. For example, the contact
surfaces 1115 are machined to remove portions of the residual draft
angle D 1305 produced as a result of the draft angle D 1515 of the
mold. Other material may be removed. For example, riser material
formed in the risers 1535 is removed. In some implementations, the
mold 1500 is configured so that a wedge or recess is formed in
riser material just beyond the side of the side frame 1100. The
wedge or recess enables hammering the riser material off, rather
than more time consuming flame cutting utilized in known casting
operations.
[0126] As shown by the various operations, the side frames 1100 may
be produced with a minimum of wasted material and time. For
example, the flask configurations minimize the amount of casting
material needed to form the mold 1500. Smaller risers result in the
removal of less material (i.e., solidified steel) during finishing.
The precision of the mold enables, for example, producing
dimensionally accurate pedestal jaws. These improvements result in
removal of less than 10% of the material during finishing.
[0127] In addition to these advantages, other advantages are
realized. For example, as noted above, the flasks 1525 and 1526 are
not required when casting the side frame 1100. Therefore, the
flasks 1525 and 1526 may be utilized to form new molds while a
given side frame 1100 is being cast.
[0128] As noted above, various analytic techniques may be utilized
to precisely determine various dimensions. To achieve tolerances
narrower than normally achievable for green sand, or chemical or
resin binder material such as phenolic urethane molding, an
iterative process of casting and three-dimensional scanning to
measure critical dimensions and variability is utilized. This
approach may be utilized throughout the manufacturing of the core
boxes, patterns, manufacturing cores, manufacturing cope and drag
mold portions, and casting the final part. By accurately measuring
each step of the process, the exact shrink rates are known in all
three directions (i.e., vertical, longitudinal, lateral) as well as
how well the cores and mold collapse during solidification.
[0129] In one implementation, the scanning may be performed with a
30 point cloud scanner, such as a Z Scanner, Faro Laser Scanner, or
a similar device. 30 point cloud data may be analyzed in software
such as Geomagic.RTM., Cam2.RTM., and Solidworks.RTM. to measure
and compare the tooling, cores, and final parts. These comparisons
may be utilized to calculate actual casting shrink, which is
usually expressed as a percentage. For example, typical pattern
maker shrink allowance for a carbon steel casting may be about
1.56%. This typical shrink allowance is not exact, and varies
depending on the complexity of the shape being cast. In some cases,
shrink allowance may be as much as 2%. For large castings, such as
a side frame or bolster, this range of shrink allowance may create
casting differences of up to 0.5'', and therefore out of tolerance.
In the described embodiments, the actual shrinkage rates in
vertical, longitudinal, and lateral directions were determined
using this process, and is reflected in the tooling dimensions.
[0130] In addition to calculating the shrink of the casting as it
cools, it is important to understand how the cores and mold
collapse during solidification. Controlling the collapsibility of
the cores and mold can control the range of tolerances achieved.
This can be achieved through a combination of molding materials,
and geometry of the core and mold. For critical side frame
dimensions, such as column spacing A 1170 (FIG. 18B), pedestal
spacing B 1175 (FIG. 18B), and column wear plate bolt spacing C
1270 (FIG. 19A), lightener openings 1550 (FIG. 22A) formed in the
cores and mold may be utilized to control the contraction of the
casting. By creating the pedestals in the mold, rather than
external cores, tolerances of .+-.0.038'' are achieved between
centers of the pedestals, as shown. By adding a pair of symmetric
core lightener openings 1550 in the bolster opening core 1610 (FIG.
23), centered at a distance of about 10.6'' above the spring seat,
and about 2'' away from the column faces, columns within
.+-.0.038'' spacing was achieved. That is, dimensions A 1170 and B
1175 may be constrained to within .+-.0.038'' so that the margin of
error in these dimensions is .+-.0.038''. In addition, the bolt
hole openings spacing C 1270 (FIG. 19A) may be uniform among all
parts, and allows parts to be produced within .+-.0.020'' of one
another between column bolt openings 1210. That is, dimension C 270
may be constrained to within .+-.0.020''. This accuracy of opening
1210 placement facilitates the use of smaller cores to create the
openings 1210 0.050'' larger than the fasteners, for a tighter
fitting bolted joint.
[0131] In addition to determining the range of manufacturing
variance achieved of the molds and cores for calculating shrink and
collapse, core print sizes may be reduced. Reducing the clearance
between the interface between the core print in the mold and core
protrusion reduces core movement during pouring. Less core movement
creates more accurate wall thicknesses and part tolerances. In
addition to the accuracy of the mold and tooling tolerances, a
controlled amount of mold wash has been achieved to minimize the
variance of core print dimensions. The clearance used in this
process was 0.030'', wherein the mold was 0.030'' larger than the
inserting protrusion created in the core, as illustrated by
dimension F 1561, which illustrates a cross section taken along
section 1555 (FIG. 22A). That is, the space F 1561 between the edge
of the core print 1630 and the portion of the mold closest to the
core print 1630 is about 0.030''. This translates to an achievable
wall thickness tolerance E 1560 (FIG. 22A) on the final part of
.+-.0.020''. That is, the wall thickness E 1560 may be constrained
to .+-.0.020''.
[0132] Another advantage of these operations is that the surface
finish of the cast side frame is smoother than in known casting
operations. The smoother the surface, the greater the fatigue life
of the part. The operations above facilitate manufacturing side
frames with a surface finish less than about 750 micro-inches RMS,
and with a pedestal surface finish that is less than about 500
micro-inches RMS.
[0133] FIG. 24 illustrates an exemplary bolster 1700 that may be
utilized in combination with the side frame 1100 as part of a truck
for a railway car. The bolster 1700 includes a main body section
1715 and first and second outboard end sections 1705. The main body
section 1715 defines a bowl section 1707 upon which a rail car
rests. A pair of brake window openings 1725 and lightener windows
1720 are defined on a longitudinal side of the bolster 1700. The
brake window openings 1725 and lightener windows 1720 are
configured to be substantially centered with a parting line that
separates drag and cope portions of a mold for forming a bolster,
as described below. The first and second outboard end sections 1705
are configured to be coupled to a pair of side frames 1100.
Specifically, each outboard end section 1705 is positioned within
the bolster opening 1110 of a side frame 1100 and defines a pair of
side bearing pads 1706 that are positioned below a bearing surface
of a rail car. A group of springs is positioned within the bolster
opening 1110 below the outboard end sections 1705.
[0134] Each outboard end section 1705 includes a pair of friction
shoe pockets 1710. The surfaces of the respective shoe pockets 1710
are known to be a critical area of the bolster 1700 from a
finishing perspective as the shoe pockets 1705 are configured to
abut the wear plates 1135 and cooperate with the wear plates 1135
to function as shock absorbers, as described above. There are
wedges which are assembled into the shoe pockets, and the wedges
wear against the column guide wear plates.
[0135] As described above, the main body section 1715 of the
bolster 1700 defines a pair of brake window openings 1725
configured to enable the use of brake rigging. These windows also
act as core prints to support the main body core in the mold.
[0136] The bolster 1700 may be formed in a manner similar to that
of the side frame 1100. For example, cope and drag sections of a
mold may be formed from a casting material, such as a chemical or
resin binder material such as phenolic urethane. Patterns that
define the exterior of the respective cope and drag sections of the
bolster 1700 may be utilized to form respective cavities in the
cope and drag sections of the mold. The draft angles of the sides
of the patterns may be 1.degree. or less. As in the side frame,
flasks for forming the mold may be sized to follow the shape of a
pattern that defines the bolster. A flask configured in this manner
minimizes the amount of molding material needed to cast a bolster.
For example, in some embodiments, the ratio of the molding sand to
the molten material poured into the mold in subsequent operations
may be less than 3:1. This is an important consideration given that
the mold may only be used a single time when casting.
[0137] Risers 1805 (FIG. 25) may be positioned at strategic
locations and optimized in size to provide an optimal amount of
feeding material during solidification to prevent the formation of
shrinkage voids and hot tears in critical areas of the bolster
1700. One or more feed paths 1810 for distributing molten material
throughout the mold may be formed in the mold in a region of the
mold that extends along a longitudinal side of the bolster 1700.
For example, the uniformly lengthed feed paths 1810 may be formed
in an area of the mold for forming the brake windows 1720 and
inboard of the inboard gibs 1708 the bolster 1700, as shown. The
feed paths 1810 are advantageously positioned in a center region of
the mold, which results in an even distribution of the molten
material throughout the bolster 1700 during casting. By contrast,
in known bolster casting operations, molten material is poured into
the bolster mold at an outboard end region 1701. This result in
uneven cooling of the material along the longitudinal plane of the
bolster. For example, if the molten material is poured into the
bolster mold at a first end 1701 of the bolster mold, the metal at
the opposite end of the bolster mold will cool more quickly than
the metal at the first end 1701. The flasks in which the drag and
cope portions are formed may be removed once the respective
portions are cured.
[0138] FIG. 26A illustrates exemplary closed cope 1903 and drag
1902 portions of a bolster mold 1900. As shown, a parting line 1905
that separates the respective portions does not follow a straight
line parallel to the edges of the cope 1903 and drag 1902 portions
as is the case in known bolster molds, as illustrated by the dashed
line 1901 in FIG. 26A. FIG. 26B illustrates the relationship
between the parting line 1905 and a bolster 1700 cast in the
bolster mold 1900. In the main body 1715 section of the mold, the
parting line 1905 is generally centered between portions of the
mold that define the brake window openings 1720. The parting line
1905 generally follows a path that is centered within the top and
bottom of the bolster 1700. However, at the shoe pockets 1710 of
the end sections 1705, the parting line 1905 is configured so that
the shoe pockets 1705 are substantially defined within the drag
section of the mold. In other words, the parting line 1905 does not
pass through the shoe pockets 1710.
[0139] In known casting operations, the entire parting line forms a
plane that cuts through the bolster. For example, the parting line
may extend between the end .cndot. sections and may be centered
within the end sections such that the parting line bisects the shoe
pockets and passes through the upper portions of the brake windows.
In green sand, pockets are created with cores, because the
operation cannot create this shape.
[0140] Configuring the parting line according to the disclosed
embodiments has several advantages over known parting line
configurations. For example, the upper and lower portions of the
respective brake windows are known to be regions of high stress.
Placement of the parting line near such locations, as is the case
in known configurations, renders the bolster more susceptible to
higher stresses. By contrast, in the disclosed embodiments, the
parting line 1905 is positioned in the middle of the brake window
openings 1720 where the stress is lower. The parting line of the
mold is also in the same location as the parting line of the cores.
This allows for uniform wall thicknesses of the side walls, thereby
promoting even cooling of the casting.
[0141] No finishing of the shoe pockets 1710 is required because
the parting line does not pass through the shoe pockets 1710. In
known parting line configurations, the parting line may be a
straight line that bi-sects the bolster and passes through a middle
region of the shoe pockets. This may necessitate finishing of the
core seams surrounding the shoe pockets. However, the disclosed
parting line is configured to be above the shoe pockets 1710. That
is, the shoe pockets 1710 are formed entirely in either the cope or
the drag portion of the mold. As noted earlier, the shoe pockets
1710 are a more critical region of the bolster 1700. Therefore,
elimination of a finishing operation is advantageous.
[0142] The cross-sectional thickness of the bolster is more
symmetrical about the parting line 1905. As noted above, patterns
are utilized to form cavities in the drag and cope portions of the
mold. The patterns are formed with draft angles to enable removal
of the patterns from the mold. Core boxes are used to create the
cores defining the inside of the bolster. The two halves of the
core boxes meet at a parting line, from which draft angles also
extend to allow the removal of the core. Where the parting lines of
a core, and parting line of a mold do not match, non-uniform wall
thicknesses occur. Placing the parting line towards the top of the
bolster, as is the case in known parting line configurations,
results in a non-uniform thickness in the cross-section of the
bolster. The non-uniform thickness results in the utilization of
excess material in casting the bolster. This non-uniform thickness
also prevents uniform cooling, and may allow shrinkage and voids to
be present. To prevent shrinkage and voids from occurring, large
risers to feed the critical sections must be used. By contrast,
positioning the parting line 1905 as disclosed enables the
formation of a bolster 1700 with a symmetrical side wall thickness
about the parting line 1905 as illustrated by thicknesses T1 11005
and T2 11010 in FIG. 27A. This, in turn, minimizes the amount of
material needed in casting the bolster 1700 and allows for uniform
cooling throughout the casting. In some implementations, less than
15% of the casting material is removed from the cast bolster to
form a finished bolster. The uniform cooling rate throughout the
casting allows for substantially smaller risers to be used.
[0143] Another advantage of the disclosed parting line 1905
configuration is that it enables easy alignment of the drag and
cope portions of the mold. In known molding operations, locating
features, such as pins and openings, are arranged within the drag
and cope flask portions to align the two portions. Any amount of
misalignment in the locating features results in misalignment
between the drag portion and cope portion of the bolsters. The
described parting line 1405, however, is keyed by virtue of the
geometry of the parting line 1405 and the drag portion and cope
portion essentially interlock with one another in such a manner
that the two portions self-align. As a result, pins and bushings
known in art are not necessary to maintain alignment of the drag
and cope portions.
[0144] After forming the drag and cope portions, one or more cores
11100 that define an interior of the bolster 1700 are formed.
Referring to FIG. 28, the cores 11100 may be formed as described
above at block 1405. The cores 11100 may include a drag portion and
cope portion that together define the interior of substantially the
entire interior of the bolster 1700. For example, one or more main
body cores 11105 may include a drag portion 11105a and a cope
portion 11105b that together define the entire interior region of
the bolster 1700. In other implementations, each of the main body
cores 11105a and 11105b may define a respective half of the entire
interior region from the center of the bolster (i.e., a central
transverse planes that bisect the bolster) towards inward gibs 1709
(FIG. 24) positioned at outboard end sections 1705 of the bolster
1700. The main body cores 11105a and 11105b may partially define
the interior region between the inward gibs 1709 and the ends of
the bolster 1700. Each of the main body cores 11105a and 11105b may
define first and second core prints 11120 and 11115. Separate end
cores 11110 may define the interior region at the outboard end
sections 1705 of the bolster 1700 that is not defined by the main
body cores 11105a and 11105b. The end cores 11110 may be formed
independently of the main body cores 11105a and 11105b. The end
cores 11110 may by attached to the main body cores 11105a and
11105b in subsequent operations via, for example, an adhesive.
[0145] The techniques described above with respect to a side frame
for constraining the tolerance of various dimensions may be applied
to the bolster. For critical bolster dimensions such as shoe pocket
angles N 11020 (FIG. 27B), shoe pocket widths M 11025 (FIG. 27B),
and inner and outer gib spacing G 1750 (FIG. 26B), similar
approaches may be utilized to accurately measure the actual
collapse amount of the cores and molds. By accounting for this
amount in the tooling, shoe pocket angles N 11020 of
.+-.0.5.degree. tolerance, and shoe pocket widths M 11025 of
.+-.0.063'' tolerance were achieved on the final parts. In
addition, the inner and outer gibs 1708 and 1709 (FIG. 26B) may be
created in the bolster molds, thereby constraining their spacing G
1750 to .+-.0.063'' tolerance.
[0146] The distance H 1950 (FIG. 26C) between respective core
prints of the cores for manufacturing the bolster, and those
portions of the cope and drag portions that are closest to the
surface of the core prints can be set to about 0.030''.
[0147] Another advantage of these operations is that the surface
finish of the cast bolster is smoother than in known casting
operations. The smoother the surface, the greater the fatigue life
of the part. The operations above facilitate manufacturing bolsters
with a surface finish less than about 750 micro-inches RMS, and
with shoe pockets with a surface finish less than about 500
micro-inches RMS.
[0148] The terms and descriptions used herein are set forth by way
of illustration only and are not meant as limitations. Those
skilled in the art will recognize that many variations can be made
to the details of the above-described embodiments without departing
from the underlying principles of the disclosed embodiments. For
example, the steps of the methods need not be executed in a certain
order, unless specified, although they may have been presented in
that order in the disclosure. The scope of the invention should,
therefore, be determined only by the following claims (and their
equivalents) in which all terms are to be understood in their