U.S. patent application number 15/214658 was filed with the patent office on 2017-06-15 for polymer blend, method for making the same and roofing membrane containing the same.
The applicant listed for this patent is ExxonMobil Chemical Patents Inc.. Invention is credited to Narayanaswami Dharmarajan, Jan Kalfus, Liang Li, Felix M. Zacarias.
Application Number | 20170166736 15/214658 |
Document ID | / |
Family ID | 59018360 |
Filed Date | 2017-06-15 |
United States Patent
Application |
20170166736 |
Kind Code |
A1 |
Kalfus; Jan ; et
al. |
June 15, 2017 |
POLYMER BLEND, METHOD FOR MAKING THE SAME AND ROOFING MEMBRANE
CONTAINING THE SAME
Abstract
A polymer blend comprising 10 to 90 parts by weight of a
propylene-based polymer component having a weight average molecular
weight of at least 200 kgmol.sup.-1; and 20 to 80 parts by weight
of a propylene-based elastomer component comprising structural
units derived from propylene and at least one of ethylene and
C4-C12 alpha-olefins having a weight average molecular weight in
the range from 5 to 50 kgmol.sup.-1, method for making a membrane
comprising the same and roofing membrane comprising the same. The
polymer blend is particularly suitable for making roofing membrane
due to advantageous elastic modulus in broad temperature
ranges.
Inventors: |
Kalfus; Jan; (Spring,
TX) ; Li; Liang; (Shanghai, CN) ; Dharmarajan;
Narayanaswami; (Houston, TX) ; Zacarias; Felix
M.; (Houston, TX) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
ExxonMobil Chemical Patents Inc. |
Baytown |
TX |
US |
|
|
Family ID: |
59018360 |
Appl. No.: |
15/214658 |
Filed: |
July 20, 2016 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
62266994 |
Dec 14, 2015 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C08J 5/18 20130101; C08L
23/12 20130101; C08J 2323/12 20130101; C08L 2314/02 20130101; E04D
5/06 20130101; C08L 2314/06 20130101; C08L 23/16 20130101; C08L
23/12 20130101; C08J 2423/12 20130101 |
International
Class: |
C08L 23/12 20060101
C08L023/12; E04D 5/06 20060101 E04D005/06; C08J 5/00 20060101
C08J005/00 |
Foreign Application Data
Date |
Code |
Application Number |
Mar 8, 2016 |
EP |
16159066.6 |
Claims
1. A polymer blend comprising: 40 to 65 parts by weight of a
propylene-based polymer component having a weight average molecular
weight of at least 200 kgmol.sup.-1, having at least 95 wt %
propylene-derived units, and a melting temperature of at least
120.degree. C.; and 35 to 60 parts by weight of a propylene-based
elastomer component comprising structural units derived from
propylene and ethylene, having an ethylene content in a range from
8 to 16 wt %, based on the total weight of the propylene-based
elastomer component, and having a weight average molecular weight
in the range from 5 to 50 kgmol.sup.-1.
2. (canceled)
3. The polymer blend of claim 1, wherein the propylene-based
elastomer component consists of structural units derived from
propylene and structural units derived from ethylene.
4. The polymer blend of claim 1, wherein the propylene-based
polymer has a melting temperature of at least 130.degree. C.
5. The polymer blend of claim 1, comprising 45 to 55 parts by
weight of the propylene-based polymer component; and 45 to 55 parts
by weight of the propylene-based elastomer component.
6. The polymer blend of claim 1, wherein the propylene-based
elastomer component has a weight average molecular weight in the
range from 6 to 20 kgmol.sup.-1.
7. The polymer blend of claim 1, wherein the propylene-based
polymer component has a weight average molecular weight of at most
800 kgmol.sup.-1.
8. The polymer blend of claim 7, wherein the propylene-based
polymer component has a weight average molecular weight of at most
600 kgmol.sup.-1.
9. A membrane having a thickness of from 0.1 to 5 mm comprising the
polymer blend of claim 1.
10. The polymer blend of claim 1, wherein the propylene-based
elastomer component has an ethylene content in the range from 10 to
15 wt %, based on the total weight of the propylene-based elastomer
component.
11. The polymer of claim 1, wherein the propylene-based elastomer
component is produced by using a metallocene catalyst.
12. The polymer blend of claim 1, wherein the propylene-based
polymer component is produced by using a Ziegler-Natta
catalyst.
13. The polymer blend of claim 1, further comprising at least one
of: a filler; a UV stabilizer; and an oxidization inhibitor.
14. A method for making a membrane, the method comprising: (i)
providing a propylene-based elastomer component comprising
structural units derived from propylene and ethylene, having an
ethylene content in a range from 8 to 16 wt %, based on the total
weight of the propylene-based elastomer component, and having a
weight average molecular weight in the range from 5 to 50
kgmol.sup.-1; (ii) providing a propylene-based polymer component
having a weight average molecular weight of at least 200
kgmol.sup.-1 and having at least 95 wt % propylene-derived units,
and a melting temperature of at least 120.degree. C.; (iii) mixing
the propylene-ethylene component and the propylene-based polymer
component to obtain a polymer blend material comprising 40 to 65
parts by weight of the propylene-based elastomer component; and 35
to 60 parts by weight of the propylene-based polymer component; and
(iv) forming a membrane from the polymer blend material.
15. The method of claim 14, wherein the propylene-based polymer has
a melting temperature of at least 130.degree. C.
16. The method of claim 14, wherein in step (iii), the blend
material comprises 45 to 55 parts by weight of the propylene-based
polymer component; and 45 to 55 parts by weight of the
propylene-based elastomer component.
17. (canceled)
18. The method of claim 14, wherein the propylene-based elastomer
consists of structure units derived from propylene and
ethylene.
19. The method of claim 14, wherein the propylene-based elastomer
component has a weight average molecular weight in the range from 6
to 20 kgmol.sup.-1.
20. The method of claim 14, wherein the propylene-based polymer
component has a weight average molecular weight of at most 800
kgmol.sup.-1.
21. The method of claim 20, wherein the propylene-based polymer
component has a weight average molecular weight of at most 600
kgmol.sup.-1.
22. The method of claim 14, the membrane having a thickness of from
0.1 to 5 mm.
23. The method of claim 14, wherein the propylene-based elastomer
component has an ethylene content in the range from 10 to 15 wt %,
based on the total weight of the propylene-based elastomer
component.
24. The method of claim 14, wherein in step (iii), the
propylene-based elastomer component and the propylene-based polymer
component are further mixed with at least one of: a filler; a UV
stabilizer; and an oxidization inhibitor.
25. A method for insulating a roof top, comprising (A) applying at
least one layer of a membrane comprising a polymer blend according
to claim 1.
26. The polymer blend of claim 1, wherein in the range from
-15.degree. C. to about 50.degree. C. the blend has a consistent
elastic modulus.
27. The method of claim 14, wherein in the range from -15.degree.
C. to about 50.degree. C. the blend has a consistent elastic
modulus.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application claims priority to and the benefit of U.S.
Provisional Application No. 62/266,994, filed Dec. 14, 2015, and
European Application No. 16159066.6, filed Mar. 8, 2016, all of
which are incorporated by reference in their entireties.
[0002] The present application is related to U.S. Provisional
Application Serial No. 62/121,230, filed on Feb. 26, 2015 and
entitled "Roofing Compositions Comprising Propylene-Based
Elastomers," the contents of which are incorporated herein by
reference in its entirety.
FIELD
[0003] The present invention relates to polymer blends based on
propylene-based polymer and propylene-based elastomer and membranes
based on such blends. In particular, the present invention relates
to polymer blends based on high molecular weight polypropylene and
propylene-based elastomers and membranes based on such blends. The
present invention is useful, e.g., in making thermoplastic roofing
membranes.
BACKGROUND
[0004] Membrane roofing is commonly used on flat or nearly flat
roofs in North America, especially in commercial building
structures with large roof surfaces, to prevent moisture
penetration and move water off the roof. Common roof membrane
materials include synthetic rubbers, thermoplastic plastics,
asphalt, and modified bitumen. Roofing membranes can be custom-made
to the precise sizes of the specific building roof surface in
rolled transportable sheets, shipped to the construction site and
then readily applied. The roofing membrane sheets can be made at a
given width such as 10 feet (3 meters) or greater.
[0005] Compositions and membranes comprising thermoplastic olefin
(TPO) polymers have recently found widespread use in the roofing
industry for commercial buildings. TPO membranes are often
fabricated as a composite structure including a reflective membrane
(e.g., 1.0 to 1.5 millimeters thick) as an upper layer, a
reinforcing polyester scrim fabric layer (e.g., 0.025 to 0.050
millimeter thick) as an intermediate layer, and a pigmented layer
(e.g., 1.0 to 1.5 millimeters thick) as the lower layer. When the
membrane is applied to the roof the reflective upper layer is
typically exposed to sunlight while the pigmented lower layer is
attached to the roof insulation material.
[0006] During transport the rolls can be exposed to extreme heat
conditions, such as from 40.degree. C. to 100.degree. C., which can
lead to blocking of the rolls during installation. After
installation, the membranes can be exposed during service to a wide
range of conditions that may deteriorate or destroy the integrity
of the membrane. As such, a membrane is desired that can withstand
a wide variety of service temperatures, such as from -40.degree. C.
to 40.degree. C.
[0007] PCT Application Publication No. WO 2010/115079A1 is directed
to roofing membranes that contain compositions of Formula I that
comprise (a) 30 to 50 wt % of a propylene-based elastomer, (b) 9 to
20 wt % of a plastomer, (c) from 7 to 20 wt % of an impact
propylene-based elastomer, (d) 20 to 35 wt % of magnesium
hydroxide, (e) 5 to 10 wt % of titanium dioxide, and (f) 1 to 2 wt
% of additives; or compositions of Formula II that comprise (a) 32
to 48 wt % of a propylene-based elastomer, (h) 9 to 18 wt % of a
plastomer, (c) 7 to 20 wt % of an impact propylene-based elastomer,
(d) 25 to 35 wt % of magnesium hydroxide, (e) 4 to 6 wt % of
titanium dioxide, (F) 0.75 to 1,5 wt % of UV inhibitor, (g) 0.2 to
0.45 wt % of antioxidant/stabilizer, (h) 0.15 to 0.4 wt % of
thermal stabilizer, and (i) 0.1 to 0.2 is wt % of lubricant. The
propylene-based elastomer used in WO 2010/115079A1 was
Vistamaxx.TM. 6102 Performance Polymer and the lubricant used was
Asahi AX71 which is a mono or di-stearyl acid phosphate. The
roofing membrane in WO 2010/115079A1 is formed around a scrim
having reinforcing polyester threads.
[0008] PCT Application Publication No. WO 2014/001224A1 is directed
to compositions comprising 40 to 75 wt % of at least one
polypropylene-based elastomer and around 25 to 60 wt % of at least
one random copolymer of polypropylene. The polypropylene-based
elastomers used in WO 2014/001224A1 were Vistamaxx.TM. 3980, 6102,
and 6202 Performance Polymers.
[0009] PCT Publication No. WO 2014/040914A1 is directed to
thermoplastic mixtures that comprise at least one impact-resistant
polypropylene copolymer and at least one ethylene-1-octene
copolymer, where the weight ratio of impact-resistant polypropylene
copolymer to ethylene-l-octene copolymer is in the range of 35:65
to 65:35.
[0010] U.S. Patent Application Serial No, 2010/0255739 A1 discloses
roofing membrane with a composition having a polypropylene based
elastomer, a plastomer, and an impact propylene-based elastomer.
The total weight percent of propylene-based elastomer present in
the composition may range from about 7 to 20 percent. It is
disclosed therein that rolled sheets of such membrane can be
supplied to the roofer and installed onsite using fasteners,
adhesives and other means of fixation.
[0011] Additional background references include U.S. Patent
Application Nos. 2006/0046084; 2007/208139; and 2010/197844; U.S.
Pat. Nos. 6,743,864; 6,953,828; 6,750,284; 7,666,491; 7,927,595;
and 8,769,903; and PCT Publication No. WO 2014/105809.
[0012] While such roofing membranes provide the workability for
many applications, substitutes thereof with lower modulus at low
temperature (e.g., temperature lower than -50.degree. C.) and
higher modulus at high temperature (e.g., temperature higher than
75.degree. C.) are desired.
SUMMARY
[0013] It has been found that a polymer blend comprising a high
molecular weight propylene-based polymer and a low molecular weight
propylene-based elastomer can provide the desired combination of
low-temperature modulus, ambient-temperature modulus, and
high-temperature modulus, rendering it an excellent candidate
material for roofing membrane.
[0014] Accordingly, a first aspect of the present invention
provides a composition suitable for roofing membrane comprising 10
to 90 parts by weight of a propylene-based polymer component having
a weight average molecular weight of at least 200 kgmol.sup.-1; and
20 to 80 parts by weight of a propylene-based elastomer copolymer
component comprising structural units derived from propylene and at
least one of ethylene and C4-C12 olefins having a weight average
molecular weight in the range from 5 to 50 kgmol.sup.-1.
[0015] A second aspect of the present invention relates to a method
for making a membrane, the method comprising: (i) providing a
propylene-based elastomer component having a weight average
molecular weight in the range from 5 to 50 kgmol.sup.-1; (ii)
providing a propylene-based polymer component having a weight
average molecular weight of at least 200 kgmol; (iii) mixing the
propylene-ethylene component and the propylene-based polymer
component to obtain a polymer blend material comprising from 10 to
90 parts by weight of the propylene-based elastomer component and
from 20 to 80 parts by weight of the propylene-based polymer
component; and (iv) forming a membrane from the polymer blend
material.
[0016] A third aspect of the present invention relates to a method
for insulating a roof top, comprising applying at least one layer
of a membrane comprising a polymer blend over the roof top, wherein
the polymer blend has a composition according to the first aspect
of the present invention described summarily above and in greater
detail below.
BRIEF DESCRIPTION OF THE DRAWINGS
[0017] FIG. 1 is a graph comparing the in-phase elastic modulus of
a blend of a propylene-based polymer and a propylene-based
elastomer blend of the present invention as a function of
temperature to that of a prior art roofing membrane material.
[0018] FIG. 2 is a diagram comparing elastic modulus at 23.degree.
C. of two blends of propylene-based polymers and propylene-based
elastomers and a prior art roofing membrane material.
DETAILED DESCRIPTION
[0019] The invention is based on the concept that using low
molecular weight propylene-based elastomers to deliver desired
softness (e,g., softness in terms of elastic modulus in the range
80 to 120 MPa in the temperature range of 10.degree. C. to
30.degree. C.), of polypropylene based thermoplastic polyolefin
blends. Metallocene catalyst can be used to synthesize
propylene-based elastomers in broad range of molecular weights and
ethylene contents, in a solution process. Propylene-based
elastomers low in molecular weight and ethylene content, suitable
for adhesives application, can be used as a softening agent for
polypropylene that provides a convenient combination of mechanical
properties and processability.
[0020] Various specific embodiments and versions of the present
invention will now be described, including preferred embodiments
and definitions that are adopted herein. While the following
detailed description gives specific preferred embodiments, those
skilled in the art will appreciate that these embodiments are
exemplary only, and that the present invention can be practiced in
other ways. Any reference to the "invention" may refer to one or
more, but not necessarily all, of the embodiments defined by the
claims. The use of headings is for purposes of convenience only and
does not limit the scope of the present invention.
[0021] All numerical values within the detailed description and the
claims herein are modified by "about" or "approximately" the
indicated value, and take into account experimental error and
variations that would be expected by a person having ordinary skill
in the art.
[0022] As used herein, the term "copolymer" is meant to include
polymers having two or more monomers, optionally, with other
monomers, and may refer to interpolymers, terpolymers, etc. The
term "polymer" as used herein includes, but is not limited to,
homopolymers, copolymers, terpolymers, etc., and alloys and blends
thereof. The term "polymer" as used herein also includes impact,
block, graft, random, and alternating copolymers. The term
"polymer" shall further include all possible geometrical
configurations unless otherwise specifically stated. Such
configurations may include isotactic, syndiotactic and random
symmetries. The term "blend" as used herein refers to a mixture of
two or more polymers. The term "elastomer" shall mean any polymer
exhibiting some degree of elasticity, where elasticity is the
ability of a material that has been deformed by a force (such as by
stretching) to return at least partially to its original dimensions
once the force has been removed.
[0023] The term "monomer" or "comonomer," as used herein, can refer
to the monomer used to form the polymer, i.e., the unreacted
chemical compound in the form prior to polymerization, and can also
refer to the monomer after it has been incorporated into the to
polymer, also referred to herein as a "[monomer]-derived unit".
Different monomers are discussed herein, including propylene
monomers, ethylene monomers, and diene monomers.
[0024] "Reactor grade," as used herein, means a polymer that has
not been chemically or mechanically treated or blended after
polymerization in an effort to alter the polymer's average
molecular weight, molecular weight distribution, or viscosity.
Particularly excluded from those polymers described as reactor
grade are those that have been visbroken or otherwise treated or
coated with peroxide or other agents that facilitate degradation.
For the purpose of this disclosure, however, reactor grade polymers
include those polymers that are reactor blends.
[0025] "Reactor blend," as used herein, means a highly dispersed
and mechanically inseparable blend of two or more polymers produced
in situ as the result of sequential or parallel polymerization of
one or more monomers with the formation of one polymer in the
presence of another, or by solution blending polymers made
separately in parallel reactors. Reactor blends may be produced in
a single reactor, a series of reactors, or parallel reactors and
are reactor grade blends. Reactor blends may be produced by any
polymerization method, including batch, semi-continuous, or
continuous systems. Particularly excluded from "reactor blend"
polymers are blends of two or more polymers in which the polymers
are blended ex situ, such as by physically or mechanically blending
in a mixer, extruder, or other similar device.
The Propylene-Based Polymer (PBP) Component
[0026] The PBP component in the polymer blend of the present
invention useful for roofing membrane desirably has a high
molecular weight of at least 200 kgmol.sup.-1 (weight average) in
order to keep tensile strength and puncture resistance of the
membrane made therefrom at an acceptable level. Preferably, the PBP
component has a weight average molecular weight in the range from
MW(PBP)1 kgmol.sup.-1 to MW(PBP)2 kgmol.sup.-1, where MW(PBP)1 and
MW(PBP)2 can be, independently, 200, 210, 220, 230, 240, 250, 260,
270, 280, 290, 300, 350, 400, 450, 500, 550, 600, 650, 700, 750,
800, as long as MW(PBP)1 MW(PBP)2. If the weight average molecular
weight of the PBP component is lower than 200 kgmol.sup.-1, the
tensile strength of the membrane can be too low, resulting in an
unacceptably low puncture resistance thereof. If the weight average
molecular weight of the PBP component is higher than 800
kgmol.sup.-1, extrusion of sheet during fabrication will be an
issue.
[0027] The term "polypropylene-based polymer" as used herein
broadly means any to polymer that is considered a "polypropylene"
by persons skilled in the art and includes homo, impact, and random
copolymers of propylene. Preferably, the polypropylene used in the
compositions described herein has a melting point above 110.degree.
C. and includes at least 90 wt % propylene-derived units. The
polypropylene may also include isotactic, atactic or syndiotactic
sequences, and preferably includes isotactic sequences. The
polypropylene can either derive exclusively from propylene monomers
(i.e., having only propylene-derived units) or comprises at least
90 wt %, or at least 93 wt %, or at least 95 wt %, or at least 97
wt %, or at least 98 wt %, or at least 99 wt % propylene-derived
units with the remainder derived from olefins, such as ethylene,
and/or C4-C10 alpha-olefins.
[0028] The PBP may have a melting temperature of from at last
110.degree. C., or at least 120.degree. C., or at least 130.degree.
C., and may range from 110.degree. C. to 170.degree. C. or higher
as measured by DSC.
[0029] The PBP may have a melt flow rate ("MFR") as measured by
ASTM D1238 at 230.degree. C. and 2.16 kg weight of from about 0.1
to 20 g/10 min. For example, the PBP may have a fractional MFR of
less than about 2 g/10 min, or less than about 1.5 g/10 min, or
less than about 1 g/10 min. For example, the PBP may have a MFR of
from a low of about 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9,
1.0, 1.2, 1.4, 1.5, 1.6, 1.8, 2.0 or g/10 min to a high of about
5.5, 6.0, 6.5, 7.0, 7.5, 8.0, 8.5, 9.0, 9.5, 10, 11, 12, 13, 14,
15, 16, 17, 18, 19, or 20 g/10 min, where desirable ranges may
include ranges from any lower limit to any upper limit. For
example, the PBP may have a MFR of from a low of about 0.5, 1.0,
1.5, 2.0, 2.5 g/10 min to a high of about 5.0, 5.5, 6.0, 6.5, 7.0,
7.5, 8.0, 8.5, 9.0, 10, 11, 12, 13, 14, or 15 g/10 min.
[0030] The PBP component can be a propylene homopolymer made by
using a Ziegler-Natta catalyst. Suitable polypropylene homopolymers
are various grades thereof supplied from ExxonMobil Chemical
Company, Houston, Tex., U.S.A., for example, grades PP5341, PP3155,
and the like.
The Propylene-Based Elastomer ("PBE") Component
[0031] The PBE component in the composition and membrane of the
present invention advantageously is an elastomer comprising
structural units derived from propylene, at least one of ethylene
and C4-C12 alpha-olefin monomer(s), and optionally one or more
dienes. Preferably, the PBE component consists essentially of
propylene and ethylene derived structural units (e.g., with total
contents of propylene and ethylene-derived structural units of at
least 95 wt %, 96 wt %, 97 wt %, 98 wt %, 99 wt %, based on the
total weight of the PBE component), or consists only of propylene
and ethylene derived units.
[0032] The PBE component may include structural units derived from
ethylene at a quantity in the range from al wt % to a2 wt %, based
upon the total weight of the PBE component, where a1 and a2 can be,
independently, 8, 9, 10, 11, 12, 13, 14, 15, or 16, as long as
a1<a2. The PBE may include up to about 30 wt %, up to about 25
wt %, up to about 22 wt %, up to about 20 wt %, up to about 19 wt
%, up to about 18 wt %, or up to about 17 wt %, ethylene- or C4-C12
alpha-olefin-derived units, based upon the total weight
thereof.
[0033] The PBE component may include structural units derived from
propylene at a quantity in the range from b l wt % to b2 wt %,
based on the total weight of the PBE component, where b1 and b2 can
be, independently, 70, 72, 74, 75, 76, 78, 80, 82, 84, 85, 86, 88,
90, 92, as long as b1<b2.
[0034] The PBE component of can be characterized by a melting point
(Tm), which can be determined by differential scanning calorimetry
(DSC). Using the DSC test method described herein, the melting
point is the temperature recorded corresponding to the greatest
heat absorption within the range of melting temperature of the
sample. When a single melting peak is observed, that peak is deemed
to be the "melting point." When multiple peaks are observed (e.g.,
principle and secondary peaks), then the melting point is deemed to
be the highest of those peaks. It is noted that due to the
low-crystallinity of many of the PBE components, the melting point
peak may be at a low temperature and be relatively flat, making it
difficult to determine the precise peak location. A "peak" in this
context is defined as a change in the general slope of the DSC
curve (heat flow versus temperature) from positive to negative,
forming a maximum without a shift in the baseline where the DSC
curve is plotted so that an endothermic reaction would be shown
with a positive peak.
[0035] The Tm of the PBE component (as determined by DSC) may be
less than about 120.degree. C., less than about 115.degree. C.,
less than about 110.degree. C., less than about 105.degree. C.,
less than about 100.degree. C., less than about 90.degree. C., less
than about 80.degree. C., less than about 70.degree. C., less than
about 65.degree. C., or less than about 60.degree. C. For example,
the PBE component may have a Tm of from about 20 to about
110.degree. C., from about 30 to about 110.degree. C., from about
40 to about 110.degree. C., or from about 50 to about 105.degree.
C., where desirable ranges may include ranges from any lower limit
to any upper limit. For example, the PBE component may have a Tin
of from about 40 to about 70.degree. C., or from about 45 to about
65.degree. C., or from about 50 to about 60.degree. C., where
desirable ranges may include ranges from any lower limit to any
upper limit. For example, the PBE component may have a Tm of from
about 80 to about 110.degree. C., or from about 85 to about
110.degree. C., or from about 90 to about 105.degree. C., where
desirable ranges may include ranges from any lower limit to any
upper limit.
[0036] The PBE component can be characterized by its heat of fusion
(Hf), as determined by DSC. The PBE component may have an Hf that
is at least about 0.5 J/g, at least about 1.0 J/g, at least about
1.5 J/g, at least about 3.0 J/g, at least about 5.0 J/g, at least
about 7.0 J/g, at least about 10.0 J/g, or at least about 12 J/g.
The component may be characterized by an Hf of less than about 75
J/g, less than about 65 J/g, less than about 60 J/g, less than
about 55 J/g, less than about 50 J/g, less than about 40 J/g, less
than about 35 J/g, less than about 30 J/g, less than about 25 J/g,
less than about 20 J/g, less than about 17 J/g, or less than 15
J/g. For example, the PBE component may have a Hf of from about 1.0
to about 40 J/g, from about 3.0 to about 30 J/g, or from about 5.0
to about 20 J/g, where desirable ranges may include ranges from any
lower limit to any upper limit. For example, the PBE component may
have a Hf of from about 1.0 to about 15 J/g or from about 3.0 to
about 10 J/g, where desirable ranges may include ranges from any
lower limit to any upper limit. For example, the PBE component may
have a Hf of from 5.0 to about 30 J/g, from about 7.0 to about 25
J/g, or from about 12 to about 20 J/g, where desirable ranges may
include ranges from any lower limit to any upper limit.
[0037] As used herein, DSC procedures for determining Tm and Hf are
as follows. The polymer is pressed at a temperature of from about
200.degree. C. to about 230.degree. C. in a heated press, and the
resulting polymer sheet is hung, under ambient conditions, in the
air to cool. About 6 to 10 mg of the polymer sheet is removed with
a punch die. This 6 to 10 mg sample is annealed at room temperature
for about 80 to 100 hours. At the end of this period, the sample is
placed in a DSC (Perkin Elmer Pyris One Thermal Analysis System)
and cooled to about -30.degree. C. to about -50.degree. C. and held
for 10 minutes at that temperature. The sample is then heated at
10.degree. C./rain to attain a final temperature of about
200.degree. C. The sample is kept at 200.degree. C. for 5 minutes.
Then a second cool-heat cycle is performed, where the sample is
cooled to about -30.degree. C. to about -50.degree. C. and held for
10 minutes at that temperature, and then re-heated at10.degree.
C/min to a final temperature of about 200.degree. C. Events from
both cycles are recorded. The thermal output is recorded as the
area under the melting peak of the sample, which typically occurs
between about 0.degree. C. and about 200.degree. C. It is measured
in Joules and is a measure of the HI of the polymer.
[0038] Preferably, the PBE component has crystalline regions
interrupted by non-crystalline regions. The non-crystalline regions
can result from regions of non-crystallizable propylene segments,
the inclusion of comonomer units, or both. In one or more
embodiments, the PBE component has a propylene-derived
crystallinity that is isotactic, syndiotactic, or a to combination
thereof. In a preferred embodiment, the PBE component has isotactic
sequences. The presence of isotactic sequences can be determined by
NMR measurements showing two or more propylene derived units
arranged isotactically. Such isotactic sequences can, in some cases
be interrupted by propylene units that are not isotactically
arranged or by other monomers that otherwise disturb the
crystallinity derived from the isotactic sequences.
[0039] The PBE component can have a triad tacticity of three
propylene units (mmm tacticity), as measured by 13C NMR, of 75% or
greater, 80% or greater, 85% or greater, 90% or greater, 92% or
greater, 95% or greater, or 97% or greater. In one or more
embodiments, the triad tacticity may range from about 75 to about
99%, from about 80 to about 99%, from about 85 to about 99%, from
about 90 to about 99%, from about 90 to about 97%, or from about 80
to about 97%. Triad tacticity is determined by the methods
described in U.S. Pat. No. 7,232,871.
[0040] The PBE component may have a tacticity index m/r ranging
from a lower limit of 4 or 6 to an upper limit of 8 or 10 or 12.
The tacticity index, expressed herein as "m/r", is determined by
.sup.13C nuclear magnetic resonance ("NMR"). The tacticity index,
m/r, is calculated as defined by H. N. Cheng in Vol. 17,
MACROMOLECULES, pp. 1950-1955 (1984), incorporated herein by
reference. The designation "m" or "r" describes the stereochemistry
of pairs of contiguous propylene groups, "m" referring to meso and
"r" to racemic. An m/r ratio of 1.0 generally describes a
syndiotactic polymer, and an m/r ratio of 2.0 describes an atactic
material. An isotactic material theoretically may have a ratio
approaching infinity, and many by-product atactic polymers have
sufficient isotactic content to result in ratios of greater than
50.
[0041] The PBE component may have a percent crystallinity of from
about 0.5% to about 40%, from about 1% to about 30%, or from about
5% to about 25%, determined according to DSC procedures, where
desirable ranges may include ranges from any lower limit to any
upper limit. Crystallinity may be determined by dividing the Hf of
a sample by the Hf of a 100% crystalline polymer, which is assumed
to be 189 J/g for isotactic polypropylene.
[0042] The comonomer content and sequence distribution of the
polymers can be measured using .sup.13C nuclear magnetic resonance
(NMR) by methods well known to those skilled in the art. Comonomer
content of discrete molecular weight ranges can be measured using
methods well known to those skilled in the art, including Fourier
Transform Infrared Spectroscopy (FTIR) in conjunction with samples
by GPC, as described in Wheeler and Willis, Applied Spectroscopy,
1993, Vol. 47, pp. 1128-1130. For a propylene ethylene copolymer
containing greater than 75 wt % propylene, the comonomer content
(ethylene content) of such a polymer can be measured as follows: A
thin homogeneous film is pressed at a temperature of about
150.degree. C. or greater, and mounted on a Perkin Elmer PE 1760
infrared spectrophotometer. A full spectrum of the sample from 600
cm.sup.-1 to 4000 cm.sup.-1 is recorded and the monomer weight
percent of ethylene can be calculated according to the following
equation: Ethylene wt %=82.585-111.987+30.045X2, where Xis the
ratio of the peak height at 1155 cm.sup.-1 and peak height at
either 722 cm.sup.-1 or 732 cm.sup.-1, whichever is higher. For
propylene ethylene copolymers having 75 wt % or less propylene
content, the comonomer (ethylene) content can be measured using the
procedure described in Wheeler and Willis. Reference is made to
U.S. Pat. No. 6,525,157 which contains more details on GPC
measurements, the determination of ethylene content by NAIR and the
DSC measurements.
[0043] The PRE component may have a density of from about 0.84
g/cm.sup.3 to about 0.92 g/cm.sup.3, from about 0.85 g./cm.sup.3 to
about 0.90 g/cm.sup.3, or from about 0.85 g/cm.sup.3 to about 0.87
g/cm.sup.3 at room temperature, as measured per the ASTM D-1505
test method, where desirable ranges may include ranges from any
lower limit to any upper limit.
[0044] The PBE component may have a g' index value of 0.95 or
greater, or at least 0.97, or at least 0.99, wherein g' is measured
at the Mw of the polymer using the intrinsic viscosity of isotactic
polypropylene as the baseline. For use herein, the g' index is
defined as:
g ' = .eta. b .eta. l ##EQU00001##
where .eta.b is the intrinsic viscosity of the polymer and .eta.1
is the intrinsic viscosity of a linear polymer of the same
viscosity-averaged molecular weight (Mv) as the polymer.
.eta.1=KMv.alpha., K and .alpha. are measured values for linear
polymers and should be obtained on the same instrument as the one
used for the g' index measurement.
[0045] The PBE component has a weight average molecular weight in
the range from MW(PEP)1 kgmol.sup.-1 to MW(PEP)2 kgmol.sup.-1,
where MW(PEP)1 and MW(PEP)2 can be, independently, 5.0, 6.0, 7,0,
8.0, 9.0, 10, 15, 20, 25, 30, 35, 40, 45, and 50, as long as
MW(PEP)1 <MW(PEP)2. If the weight average molecular weight of
the PBE component is lower than 5 kgmol.sup.-1, the membrane
produced from the blend can be too soft, resulting in an
unacceptably low puncture resistance thereof. If the weight average
molecular weight of the PBE component is higher than 50
kgmol.sup.-1, the membrane produced from the blend can be too
stiff, especially at low temperature such as below 0.degree. C.,
resulting in difficulty of installation.
[0046] The molecular weight distribution (MWD equal to Nw/Mn) of
the PBE component may be from about 0.5 to about 10, from about
0.75 to about 5, from about 1.0 to about 5, from about 1.5 to about
4, or from about 1.8 to about 3, where desirable ranges may include
ranges from any lower limit to any upper limit.
[0047] The PBE component may have a Shore D hardness (ASTM D2240)
less than about 50, less than about 45, less than about 40, less
than about 35, or less than about 20.
[0048] The PBE component may have a Shore A hardness (ASTM D2240)
of less than about 100, less than about 95, less than about 90,
less than about 85, less than about 80, less than about 75, or less
than 70. For example, the PBE component may have a Shore A hardness
of from about 10 to about 100, from about 15 to about 90, from
about 20 to about 80, or from about 30 to about 70, where desirable
ranges may include ranges from any lower limit to any upper
limit.
[0049] For example, the PBE component is a propylene-based
elastomer that has at least four, or at least five, or at least
six, or at least seven, or at least eight, or all nine of the
following properties (i) from about 10 to about 25 wt %, or from
about 12 to about 20 wt %, or from about 16 wt % to about 17 wt %
ethylene-derived units, based on the weight of the PBE component;
(ii) a Tm of from 80 to about 110.degree. C., or from about 85 to
about 110.degree. C., or from about 90 to about 105.degree. C.;
(iii) a Hf of less than about 75 J/g, or less than 50 J/g, or less
than 30 J/g, or from about 1.0 to about 15 J/g or from about 3.0 to
about 10 J/g; (iv) a Mw of from about 5 to about 50 kgmol.sup.-1,
or from about 6 to about 40 kgmol.sup.-1, or from about 7 to about
30 kgmol.sup.-1, or from about 8 to about 20 kgmol.sup.-1, (v) a Mn
of from about 3 to about 40 kgmol.sup.-1, or from about 4 to about
30 kgmol.sup.-1, or from about 5 to about 20 kgmol.sup.-1; (vi) MWD
of from about 1,0 to about 5, or from about 1.5 to about 4, or from
about 1.8 to about 3; and/or (vii) a Shore D hardness of less than
30, or less than 25, or less than 20. For example, such PBE
component is a reactor-blended PBE component as described
herein.
[0050] Optionally, the PBE component may also include one or more
dienes. The term "diene" is defined as a hydrocarbon compound that
has two unsaturation sites, i.e., a compound having two double
bonds connecting carbon atoms. Depending on the context, the term
"diene" as used herein refers broadly to either a diene monomer
prior to polymerization, e.g., forming part of the polymerization
medium, or a diene monomer after polymerization has begun (also
referred to as a diene monomer unit or a diene-derived unit). For
example, the diene may be selected from 5-ethylidene-2-norbornene
(ENB); 1,4-hexadiene; 5-methylene-2-norbornene (MNB);
1,6-octadiene; 5-methyl-1,4-hexadiene; 3,7-dimethyl-1,6-octadiene;
1,3-cyclopentadiene; 1,4-cyclohexadiene; vinyl norbornene VNB);
dicyclopentadiene (DCPD), and combinations thereof. In embodiments
where the PBE component comprises a diene, the diene may be present
at from 0.05 wt % to about 6 wt %, from about 0.1 wt % to about 5.0
wt %, from about 0.25 wt % to about 3.0 wt %, or from about 0.5 wt
% to about 1.5 wt %, diene-derived units, based upon the total
weight of the PBE component.
[0051] Optionally, PBE component may be grafted (i.e.,
"functionalized") using one or more grafting monomers. As used
herein, the term "grafting" denotes covalent bonding of the
grafting monomer to a polymer chain of the l'13E. The grafting
monomer can be or include at least one ethylenically unsaturated
carboxylic acid or acid derivative, such as an acid anhydride,
ester, salt, amide, imide, acrylates or the like. Illustrative
grafting monomers include, but are not limited to, acrylic acid,
methacrylic acid, maleic acid, fumaric acid, itaconic acid,
citraconic acid, mesaconic acid, maleic anhydride, 4-methyl
cyclohexene-1,2-dicarboxylic acid anhydride,
bicyclo(2.2.2)octene-2,3-dicarboxylic acid anhydride,
1,2,3,4,5,8,9,10-octahydronaphthalene-2,3-dicarboxylic acid
anhydride, 2-oxa-1,3-diketospiro(4.4)nonene,
bicyclo(2.2.1)heptene-2,3-dicarboxylic acid anhydride, maleopimaric
acid, tetrahydrophthalic anhydride, norbornene-2,3-dicarboxylic
acid anhydride, nadic anhydride, methyl nadic anhydride, himic
anhydride, methyl himic anhydride, and
5-methylbicyclo(2.2.1)heptene-2,3- dicarboxylic acid anhydride.
Other suitable grafting monomers include methyl acrylate and higher
alkyl acrylates, methyl methacrylate and higher alkyl
methacrylates, acrylic acid, methacrylic acid, hydroxy-methyl
methacrylate, hydroxyl-ethylmethacrylate and higher hydroxy-alkyl
methacrylates and glycidyl methacrylate. Maleic anhydride is a
preferred grafting monomer. In embodiments wherein the graft
monomer is maleic anhydride, the maleic anhydride concentration in
the grafted polymer is preferably in the range of about 1 wt % to
about 6 wt %, at least about 0.5 wt %, or at least about 1.5 wt
%.
[0052] In preferred embodiments, the PBE component is a reactor
grade or reactor blended polymer, as defined above. That is, in
preferred embodiments, the PBE component is a reactor blend of a
first polymer component and a second polymer component. Thus, the
comonomer content of the PBE component can be adjusted by adjusting
the comonomer content of the first polymer component, adjusting the
comonomer content of second polymer component, and/or adjusting the
ratio of the first polymer component to the second polymer
component present in the PBE component.
[0053] In embodiments where the PBE component is a reactor blended
polymer, the alpha-olefin content of the first polymer component
("R.sub.1") may be greater than 5 wt %, greater than 7 wt %,
greater than 10 wt %, greater than 12 wt %, greater than 15 wt %,
or greater than 17 wt %, based upon the total weight of the first
polymer component. The alpha-olefin content of the first polymer
component may be less than 30 wt %, less than 27 wt %, less than 25
wt %, less than 22 wt %, less than 20 wt %, or less than 19 wt %,
based upon the total weight of the first polymer component. For
example, the alpha-olefin content of the first polymer component
may range from 5 wt(,)/, to 30 wt %, from 7 wt % to 27 wt %, from
10 wt % to 25 wt %, from 12 wt % to 22 wt %, from 15 wt % to 20 wt
%, or from 17 wt % to 19 wt %. Preferably, the first polymer
component comprises propylene and ethylene derived units, or
consists essentially of propylene and ethylene derived units.
[0054] In embodiments where the PBE component is a reactor blended
polymer, the alpha-olefin content of the second polymer component
("R.sub.2") may be greater than 1.0 wt %, greater than 1.5 wt %,
greater than 2.0 wt %, greater than 2.5 wt %, greater than 2.75 wt
%, or greater than 3.0 wt % alpha-olefin, based upon the total
weight of the second polymer component. The alpha-olefin content of
the second polymer component may be less than 10 wt'%.COPYRGT.,
less than 9 wt %, less than 8 wt'%.COPYRGT., less than 7
wt'%.COPYRGT., less than 6 wt %, or less than 5 wt %, based upon
the total weight of the second polymer component. For example, the
alpha-olefin content of the second polymer component may range from
1.0 wt % to 10 wt %, or from 1.5 wt % to 9 wt %, or from 2.0 wt %
to 8 wt %, or from 2.5 wt % to 7 wt %, or from 2.75 wt % to 6 wt %,
or from 3 wt % to 5 wt %. Preferably, the second polymer component
comprises propylene and ethylene derived units, or consists
essentially of propylene and ethylene derived units.
[0055] In embodiments where the PBE component is a reactor blended
polymer, the PBE component may comprise from 1 to 25 wt % of the
second polymer component, from 3 to 20 wt % of the second polymer
component, from 5 to 18 wt % of the second polymer component, from
7 to 15 wt % of the second polymer component, or from 8 to 12 wt %
of the second polymer component, based on the weight of the PBE
component, where desirable ranges may include ranges from any lower
limit to any upper limit. The PBE component may comprise from 75 to
99 wt % of the first polymer component, from 80 to 97 wt % of the
first polymer component, from 85 to 93 wt % of the first polymer
component, or from 82 to 92 wt % of the first polymer component,
based on the weight of the PBE component, where desirable ranges
may include ranges from any lower limit to any upper limit.
[0056] The PBE component is preferably prepared using homogeneous
conditions, such as a continuous solution polymerization process.
For example, the PBE component is prepared in parallel solution
polymerization reactors, such that the first reactor component is
prepared in a first reactor and the second reactor component is
prepared in a second reactor, and the reactor effluent from the
first and second reactors are combined and blended to form a single
reactor effluent from which the final the PBE component is
separated. Exemplary methods for the preparation of the PBE
components may be found in U.S. Pat. Nos. 6,881,800; 7,803,876;
8,013,069; and 8,026,323 and PCT Publications WO 2011/087729; WO
2011/087730; and WO 2011/087731,
The Blend Composition
[0057] The blend advantageously comprises from c1 to c2 parts by
weight of the PBP component, and c3 to c4 parts by weight of the
PBE component, where c1 and c2 can be, independently, 10, 15, 20,
25, 30, 35, 36, 38, 40, 42, 44, 45, 46, 48, 50, 52, 54, 55, 56, 58,
60, 62, 64, 65, 70, 75, 80, 85, 90, as long as c1<c2, and c3 and
c4 can be, independently, 20, 25, 30, 35, 36, 38, 40, 42, 44, 45,
46, 48, 50, 52, 54, 55, 56, 58, 60, 62, 64, 65, 70, 75, 80, as long
as c3<c4. Preferably, c1=40, c2=65, c3=35, and c4=60. More
preferably, c1=45, c2=55, c3=45, and c4=55.
[0058] Additionally or alternatively, the blend advantageously
comprises from d1 to d2 wt % of the PBP component, and d3 to d4 wt
% of the PBE component, based on the total weight of the PBP
component and the PBE component, where d1 and d2 can be,
independently, 10, 15, 20, 25, 30, 35, 36, 38, 40, 42, 44, 45, 46,
48, 50, 52, 54, 55, 56, 58, 60, 62, 64, 65, 70, 75, 80, 85, 90, as
long as d1<d2, and d3 and d4 can be, independently, 20, 25, 30,
35, 36, 38, 40, 42, 44, 45, 46, 48, 50, 52, 54, 55, 56, 58, 60, 62,
64, 65, 70, 75, 80, as long as d3<d4. If the PBP component
constitutes less than 10 wt % of the total weight of the PBP
component and the PBE component, the membrane thus produced can
have insufficient strength. If the PBP component constitutes more
than 90 wt % of the total weight of these two components, the
membrane produced from it can have an overly high elastic modulus
resulting in unacceptable stiffness, making installation of the
membrane made from the blend difficult to implement. Preferably,
d1=40, d2=65, d3=35, and d4=60. More preferably, d1=45, d2=55,
d3=45, and d4=55.
[0059] The blend described herein may have a Shore A hardness, as
determined by ASTM-D2240 in the range of from 10 to 200, or from 20
to 150, or from 30 to 100, or from 40 to 75, or from 45 to 65.
[0060] The blend described herein may have a MFR, as measured
according to ASTM D-1238 (2.16 kg weight @ 230.degree. C.), greater
than about 0.5 g/10 min, greater than about 1.0 g/10 min, greater
than about 1.5 g/10 min, greater than about 2.0 g/10 min, or
greater than about 2.5 g/10 nun, or greater than about 3 g/10 min,
or greater than about 3.5 g/10 min, or greater than about 4 g/10
min. The blend composition may have an MFR less than about 100 g/10
min, less than about 50 g/10 min, less than about 25 g/10 min, less
than about 15 g/10 min, less than about 10 g/10 min, less than
about 7 g/10 min. For example, the blend composition may have an
MFR from about 0.5 to about 15 g/10 min, from about 1.0 to about 10
g/10 min, or from about 3 to about 7 g/10 min.
[0061] The blend may have a Vicat softening point, as measured
according to ASTM D-1525 (200 g), of from about 10 to 100.degree.
C., or from about 20 to about 75.degree. C., or from about 30 to
about 60.degree. C., or from about 35 to 50.degree. C.
Process for Making the Blend
[0062] The blend can be made by various means. In one process, the
polypropylene component and the propylene-ethylene component are
separately and independently fabricated. The pre-fabricated
polypropylene resin and the propylene-based elastomer components
are then intimately mixed, and processed into the blend. Such
mixing can be dry mixing in extrusion compounding, mixing with the
aid of additional components such as a solvent, example being
toluene, and the like. Additives, such as anti-oxidants, UV
absorbers, inorganic fillers, and the like, may be added when
blending the two polymer components together.
[0063] In an alternative process, ethylene and propylene are
injected into a polymerization reactor and allowed to polymerize in
the presence of a catalyst such as a metallocene catalyst, and the
like, to form the propylene-ethylene component. The polypropylene
component is added in a post-reaction step through a finishing
extruder to form the mixture. The thus formed propylene-ethylene
component is mixed intimately with the polypropylene material fed
into the reaction vessel. The polymerization of ethylene with
propylene in the reaction vessel can takes place mainly in
solution.
[0064] For example, the blend of the present invention is prepared
by combining the PBE component and PBP component and then
pelletizing the blend compositions. Without being bound by theory,
it is believed that, by pelletizing the blend composition before
forming a fabricated article or before blending with other
components can allow for a more homogeneous mixing between the PBE
component and the PBP component is achieved. Therefore, for
example, the roofing compositions described herein may be prepared
by a method comprising the steps of: (a) combining (i) a
propylene-based elastomer comprising at least about 60 wt %
propylene-derived units and about 5 to about 25 wt %
ethylene-derived units, based on total weight of the
propylene-based elastomer and (ii) a PBP resin to form a blend; (b)
pelletizing the blend to form a pellet composition; and (c)
blending the pellet composition with other components to form a
roofing membrane composition.
[0065] For example, the method of blending the PBP component and
the PBE component may be to melt blend the components in an
extruder, such as a single-screw extruder or a twin-screw extruder.
Extrusion technology for polymer blends is well known in the art,
and is described in more detail in, for example, PLASTICS EXTRUSION
TECHNOLOGY, F. Hensen, Ed, (Hanser, 1988), pp. 26-37, and in
POLYPROPYLENE HANDBOOK, E. P. Moore, Jr. Ed. (Hanser, 1996), pp.
304-348. Other blending methods may utilize a double-cone blender,
ribbon blender, or a Farrel Continuous Mixer (FCM.TM.).
Roofing Membrane Compositions
[0066] A roofing composition described herein may comprise, in
addition to the blend composition described above, a variety of
additives. The additives may include reinforcing and
non-reinforcing fillers, antioxidants, stabilizers, processing
oils, compatibilizing agents, lubricants (e.g., oleamide),
antiblocking agents, antistatic agents, waxes, coupling agents for
the fillers and/or pigment, pigments, flame retardants,
antioxidants, and other processing aids known to the art. For
example, the additives may comprise up to about 65 wt %, or up to
about 60 wt %, or up to about 55 wt %, or up to about 50 wt % of
the roofing composition. For example, the additives may comprise at
least 5 wt %, or at least 10 wt %, or at least 15 wt %, or at least
20 wt'%.COPYRGT., or at least 25 wt %, or at least 30 wt %, or at
least 35 wt %, or at least 40 wt % of the roofing composition.
[0067] For example, the roofing composition may include fillers and
coloring agents. Exemplary materials include inorganic fillers such
as calcium carbonate, clays, silica, talc, titanium dioxide or
carbon black. Any type of carbon black can be used, such as channel
blacks, furnace blacks, thermal blacks, acetylene black, lamp black
and the like.
[0068] For example, the roofing composition may include flame
retardants, such as calcium carbonate, inorganic clays containing
water of hydration such as aluminum trihydroxides ("ATH") or
Magnesium Hydroxide. For example, the calcium carbonate or
magnesium hydroxide may be pre-blended into a masterbatch with a
thermoplastic resin, such as polypropylene, or a polyethylene, such
as linear low density polyethylene. For example, the flame
retardant may be pre-blended with a polypropylene, an impact
propylene-based elastomer, or polyethylene, where the masterbatch
comprises at least 40 wt %, or at least 45 wt %, or at least 50 wt
%, or at least 55 wt'%.COPYRGT., or at least 60 wt %, or at least
65 wt %, or at least 70 wt %, or at least 75 wt %, of flame
retardant, based on the weight of the masterbatch. The flame
retardant masterbatch may then form at least 5 wt %, or at least 10
wt %, or at least 15 wt %, or at least 20 wt %, or at least 25 wt
%, of the roofing composition. For example, the roofing composition
comprises from 5 wt % to 40 wt %, or from 10 wt % to 35 wt %, or
from 15 wt % to 30 wt % flame retardant masterbatch, where
desirable ranges may include ranges from any lower limit to any
upper limit.
[0069] For example, the roofing composition may include UV
stabilizers, such as titanium dioxide or Tinuvin.RTM. XT-850. The
UV stabilizers may be introduced into the roofing composition as
part of a masterbatch. For example, UV stabilizer may be
pre-blended into a masterbatch with the PBP or other polymer
materials, where the masterbatch comprises at least 5 wt %, or at
least 7 wt %, or at least 10 wt %, or at least 12 wt'%.COPYRGT., or
at least 15 wt %, of UV stabilizer, based on the weight of the
masterbatch. The UV stabilizer masterbatch may then form at least 5
wt %, or at least 7 wt %, or at least 10 wt %, or at least 15 wt %,
of the roofing composition. For example, the roofing composition
comprises from 5 wt % to 30 we.)/, or from 7 we.)/, to 25 wt %, or
from 10 wt % to 20 wt % flame retardant masterbatch, where
desirable ranges may include ranges from any lower limit to any
upper limit.
[0070] Still other additives may include antioxidant and/or thermal
stabilizers. In an exemplary embodiment, processing and/or field
thermal stabilizers may include 1RGANOX.RTM. B-225 and/or
IRGANOX.RTM. 1010 available from BASF.
RoofingMembrane
[0071] Membrane can be made comprising the
polypropylene/propylene-based elastomer blend of the present
invention. Machines and processes known in the art for making
polymer films, such as extrusion compounding and calendaring are
typically adopted.
[0072] The roofing membrane advantageously has a multi-layer
structure comprising at least one layer made of the blend according
to the present invention. For example, the membrane can have three
layers: a top layer, desirably with a light color such as white,
made from a roofing composition described above, a bottom layer,
desirably with a dark color such as black, made from another
roofing composition described above, and an intermediate layer,
desirably made from a material that reinforces the overall
mechanical structure of the membrane. The intermediate layer can be
any type of scrim including, but not limited to, polyester,
fiberglass, fiberglass reinforced polyester, polypropylene, woven
or non-woven fabrics (e.g. Nylon) or combinations thereof Preferred
scrims are fiberglass and/or polyester.
[0073] For example, a surface layer of the top and/or bottom of the
membrane may be textured with various patterns. Texture increases
the surface area of the membrane, reduces glare and makes the
membrane surface less slippery. Examples of texture designs
include, but are not limited to, a polyhedron with a polygonal base
and triangular faces meeting in a common vertex.sub.; such as a
pyramidal base; a cone configuration having a circular or
ellipsoidal configurations; and random pattern configurations.
[0074] Useful roofing membranes may have a thickness of from 0.1 to
5 mm, or from 0.5 to 4 mm.
Application of Membrane
[0075] The membrane of the present invention is particularly
advantageously used in roofing applications, especially in the roof
structures of commercial buildings with relatively small sloping
grade. The membrane functions to block liquid water and moisture
from entering the building from the roof. The membrane may be
designed to have a reflective top layer, which can reflect the
sunlight thereby resulting in cooler buildings with substantial
energy savings or the reduced need of thermal insulation below the
membrane.
[0076] The membrane of the present invention can be made into rolls
and/or sheets with specific dimensions (width, thickness, and
length) predetermined according to the dimensions and shape of the
roof intended to be covered by the membrane. The rolls and/or
sheets can be shipped from the membrane manufacturer to the
construction site and applied in-situ. Alternatively, rolls and/or
sheets of the membrane of the present invention with standard
dimensions may be cut into specific sizes and then applied at the
job site. Due to the advantaged properties of the membrane of the
present invention, especially the desired modulus at higher
temperature and lower temperature, the membrane of the present
application can be conveniently applied in a large range of
temperature with relative ease, without the need of worry about its
being too soft or propensity to puncture.
[0077] The roofing membranes may be fixed over the base roofing by
any means known in the art such as via adhesive material, ballasted
material, spot bonding, or mechanical spot fastening. For example,
the membranes may be installed using mechanical fasteners and
plates placed along the edge sheet and fastened through the
membrane and into the roof to decking. Adjoining sheets of the
flexible membranes are overlapped, covering the fasteners and
plates, and preferably joined together, for example with a hot air
weld. The membrane may also be fully adhered or self-adhered to an
insulation or deck material using an adhesive. Insulation is
typically secured to the deck with mechanical fasteners and the
flexible membrane is adhered to the insulation.
[0078] The present invention is further illustrated by the
following non-limiting examples.
EXAMPLES
[0079] A high molecular weight polypropylene from ExxonMobil
Chemical Company (PP5341E1) made by using a Ziegler-Matta catalyst,
and a low-molecular weight propylene-based elastomer with an
ethylene content of 12 wt % and Brookfield viscosity at 200.degree.
C. of 1012 centipoise, made by using solution polymerization in the
presence of a metallocene catalyst were used as the polypropylene
component and the propylene-based elastomer components,
respectively.
[0080] Blends of polymers were prepared by melt blending in
Brabender Plasticorder mixer at 150.degree. C. The mixer had a
chamber size of 50 cm.sup.3 and roller-type mixer blades (Cast 304
stainless steel roller). Prior to each melt mixing, 40 grams of dry
blend were prepared and homogenized in a plastic bag by shaking for
about 30 seconds. The dry blend was then introduced into the mixing
chamber at a roller velocity of 20 rpm. After filling the chamber
and melting the components (1 minute), the rotor speed was
increased to 50 rpm and the blend was mixed for 4-5 minutes. After
this time the torque stabilized indicating homogenization of the
components. The blend was collected after opening the hot mixer
using a brass spatula. The mixer was carefully cleaned prior to
each mixing.
[0081] The blends were characterized by the dynamic-mechanical
thermal analysis (DMTA, RSA-G2 by TA Instruments). All samples were
compression molded at 180.degree. C. in a hot press for 3 minutes
and quenched in a cold press for 2 minutes. The thickness of
compression molded films was 0.35 millimeter. A strip of the film
with dimensions 5 millimeters by 40 millimeters was cut with a
sharp razor blade and the DMTA measurement was carried out at a
single frequency of 1 Hz in uniaxial extension (amplitude of 0.05%,
linear viscoelastic regime) in the temperature range from
-60.degree. C. to 120.degree. C. at a heating rate of
2.degree.C/minute.
[0082] FIG. 1 shows the elastic modulus of as a function of
temperature of a first blend of the present invention (101) made by
the process described above versus a comparative material (103,
which is Catalloy.TM. Hifax CA10A resin available from Lyondell
Chemical to Company, Carrollton, Tex., U.S.A.). The comparative
material, a polymer blend made by gas phase polymerization of
propylene/ethylene mixture in a porous matrix of polypropylene, is
widely used in roofing membranes due to its good combination of
flexibility and strength at the application and use temperatures.
The inventive first blend 101 consists of 45 wt % of a propylene
homopolymer ExxotiMobil PP5431E1) and 55% of a propylene-based
elastomer. Compositions of the materials are provided in TABLE I
below. As can be seen, the first inventive blend 101 provides a
combination of properties that is desirable for roofing membranes:
a low temperature flexibility (easy installation even at low
temperatures) and a high temperature stiffness (reduced blocking
during installation). In fact, compared to the comparative
material, the first inventive blend show both (i) appreciably lower
elastic modulus at temperature below -30.degree. C. and (ii)
appreciably higher elastic modulus at temperatures higher than
75.degree. C. Moreover, in the range from -15.degree. C. to about
50.degree. C., where outdoors installation of roofing membrane is
most likely to occur, the blend of the present invention
demonstrated more consistent elastic modulus in the most desirable
range of modulus.
[0083] FIG. 2 shows the elastic modulus at 23.degree. C. of three
materials: Catalloy.TM. Hifax CA10A resin (201); a second inventive
blend according to the present invention (203) which is made by
using the same method as described above; and a second comparative
blend (205). Compositions are provided in TABLE I below. Material
205 is a comparative material because of the high weight average
molecular weight of the PBE component therein (221 kgmol.sup.-1).
From FIG. 2, it can be seen that at 23.degree. C., the inventive
material 203 has comparable elastic modulus to material 201; while
material 205 showed unacceptably high elastic modulus. Such high
room temperature elastic modulus of material 205 renders it
unsuitable for roofing membrane applications because of
insufficient flexibility.
TABLE-US-00001 TABLE I Material Components PBP PBE Content in
Ethylene Content in Mw Mn blend Monomer(s) content in PBE Mw Mn
blend Example Trade Name Monomer(s) (kg mol.sup.-1) (wt %) (wt %)
(wt %) (kg mol.sup.-1) (wt %) 101 Inventive ExxonMobil Propylene
457 131 45 Propylene; 12 26.6 11.9 55 PP5341E1 ethylene 103/201
Comparative Catalloy .TM. Hifax Propylene N/D N/D N/D Propylene;
N/D >100 N/D N/D CA10A ethylene 203 Inventive ExxonMobil
Propylene 457 131 50 Propylene; 12 26.6 11.9 50 PP5341E1 ethylene
205 Comparative ExxonMobil Propylene 180 64 50 Propylene; 16 221
114 50 PP3155 ethylene N/D: Not Determined
* * * * *