U.S. patent application number 15/298395 was filed with the patent office on 2017-05-18 for manufacturing method of press-molded article and press molding apparatus.
This patent application is currently assigned to Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.). The applicant listed for this patent is Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.). Invention is credited to Kensuke FUNADA, Yasuhiro HAYASHIDA, Jiro IWAYA, Takayuki KIMURA, Junya NAITOU, Kazuki SAKAMOTO, Kenichi WATANABE.
Application Number | 20170136521 15/298395 |
Document ID | / |
Family ID | 57288102 |
Filed Date | 2017-05-18 |
United States Patent
Application |
20170136521 |
Kind Code |
A1 |
SAKAMOTO; Kazuki ; et
al. |
May 18, 2017 |
MANUFACTURING METHOD OF PRESS-MOLDED ARTICLE AND PRESS MOLDING
APPARATUS
Abstract
A manufacturing method of press-molded article of the present
invention comprises a step of placing a member to be pressed in a
press molding apparatus and a step of pressing a flat plate portion
of the member to be pressed by bringing a first press portion and a
second press portion closer to each other. A first opposing surface
and a second opposing surface, while facing to each other, keep in
contact with the flat plate portion during pressing. In the press
step, a thick part is formed on the flat plate portion by allowing
a part of a material of the flat plate portion to flow, in a press
direction, into a thickened portion-forming section formed on the
first opposing surface. The second opposing surface is moved to the
press direction as the flat plate portion is pressed by the first
press portion and the second press portion.
Inventors: |
SAKAMOTO; Kazuki; (Kobe-shi,
JP) ; HAYASHIDA; Yasuhiro; (Kobe-shi, JP) ;
WATANABE; Kenichi; (Kobe-shi, JP) ; NAITOU;
Junya; (Kobe-shi, JP) ; FUNADA; Kensuke;
(Kobe-shi, JP) ; KIMURA; Takayuki; (Kobe-shi,
JP) ; IWAYA; Jiro; (Nagoya-shi, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) |
Hyogo |
|
JP |
|
|
Assignee: |
Kabushiki Kaisha Kobe Seiko Sho
(Kobe Steel, Ltd.)
Hyogo
JP
|
Family ID: |
57288102 |
Appl. No.: |
15/298395 |
Filed: |
October 20, 2016 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B21J 13/08 20130101;
B21D 35/006 20130101; B21J 9/022 20130101; B21J 9/06 20130101; B21D
49/00 20130101; B21J 13/025 20130101; B21D 22/02 20130101; B21J
5/08 20130101 |
International
Class: |
B21J 9/02 20060101
B21J009/02; B21J 13/08 20060101 B21J013/08 |
Foreign Application Data
Date |
Code |
Application Number |
Nov 18, 2015 |
JP |
2015-225995 |
Claims
1. A manufacturing method of press-molded article by molding a
member to be pressed including a flat plate portion, the method
comprising: a step of placing the member to be pressed in a press
molding apparatus in a manner such that a first main surface of the
flat plate portion is opposed to a first opposing surface and a
second main surface of the flat plate portion, directing opposite
to the first main surface, is opposed to a second opposing surface;
and a step of pressing the flat plate portion by bringing a first
press portion opposing to a first end portion of the flat plate
portion and a second press portion opposing to a second end portion
of the flat plate portion, the second end portion being located on
an opposite side of the first end portion, closer to each other,
wherein: the first opposing surface and the second opposing
surface, while facing to each other, keep in contact with the flat
plate portion during pressing; and in the press step: a thick part
is formed on the flat plate portion by allowing a part of a
material of the flat plate portion to flow, in a press direction,
into a thickened portion-forming section formed on at least one of
the first opposing surface and the second opposing surface; and at
least one of the first opposing surface and the second opposing
surface is moved to the press direction as the flat plate portion
is pressed by the first press portion and the second press
portion.
2. The manufacturing method of press-molded article according to
claim 1, wherein, in the step of placing the member to be pressed,
the flat plate portion is placed between a die provided with the
first press portion and the first opposing surface and a die
provided with the second press portion and the second opposing
surface.
3. The manufacturing method of press-molded article according to
claim 1, wherein: the die provided with the first opposing surface
includes a first divided portion and a second divided portion
formed separately from the first divided portion; the first press
portion is formed in the first divided portion; the second press
portion is formed in the second divided portion; and in the press
step, the first divided portion is moved to the press direction of
the first press portion as the flat plate portion is pressed by the
first press portion, and the second divided portion is moved to the
press direction of the second press portion as the flat plate
portion is pressed by the second press portion.
4. The manufacturing method of press-molded article according to
claim 3, wherein: the first divided portion and the second divided
portion have a comb-teeth shape so as to mesh with each other; and
in the press step, the first divided portion and the second divided
portion come close to each other in such a manner that the both
comb teeth mesh with each other.
5. The manufacturing method of press-molded article according to
claim 1, wherein, in the step of placing the member to be pressed,
the member to be pressed is placed so as to arrange the first main
surface and the second main surface of the flat plate portion along
a perpendicular direction.
6. The manufacturing method of press-molded article according to
claim 5, wherein, in the step of placing the member to be pressed,
positions of the first main surface and the second main surface are
maintained along the perpendicular direction by supporting the flat
plate portion using a temporarily supporting member.
7. The manufacturing method of press-molded article according to
claim 1, wherein, in the press step, pressing force is applied to
the material of the flat plate portion flowing into the thickened
portion-forming section.
8. The manufacturing method of press-molded article according to
claim 1, wherein the member to be pressed is molded by a hot
press.
9. A press molding apparatus for molding a member to be pressed
including a flat plate portion, comprising: a first press portion
opposing to a first end portion of the flat plate portion; a second
press portion opposing to a second end portion of the flat plate
portion, the second end portion being located on an opposite side
of the first end portion; a first opposing surface opposing to a
first main surface of the flat plate portion; a second opposing
surface opposing to a second main surface of the flat plate
portion, the second main surface directing opposite to the first
main surface; and a driving section for bringing the first press
portion and the second press portion closer to each other to press
the flat plate portion, wherein: a thickened portion-forming
section is formed on at least one of the first opposing surface and
the second opposing surface for forming a thick part on the flat
plate portion by allowing a part of a material of the flat plate
portion to flow into the thickened portion-forming section; the
first opposing surface and the second opposing surface, while
facing to each other, keep in contact with the flat plate portion
during pressing; and at least one of the first opposing surface and
the second opposing surface is moved to the press direction as the
flat plate portion is pressed by the first press portion and the
second press portion.
10. The press molding apparatus according to claim 9, wherein: the
first press portion and the first opposing surface are provided in
a same die; and the second press portion and the second opposing
surface are provided in a same die.
11. The press molding apparatus according to claim 9, wherein: the
die provided with the first opposing surface includes a first
divided portion and a second divided portion formed separately from
the first divided portion; the first press portion is formed in the
first divided portion; and the second press portion is formed in
the second divided portion.
12. The press molding apparatus according to claim 11, wherein the
first divided portion and the second divided portion have a
comb-teeth shape so as to mesh with each other.
13. The press molding apparatus according to claim 9, wherein the
first opposing surface and the second opposing surface are arranged
along a perpendicular direction.
14. The press molding apparatus according to claim 13, comprising a
temporarily supporting member for supporting the flat plate portion
to maintain positions of the first main surface and the second main
surface along the perpendicular direction.
15. The press molding apparatus according to claim 9, comprising a
back-pressure applicator for applying pressure force to the
material of flat plate portion flowing into the thickened
portion-forming section.
Description
BACKGROUND OF THE INVENTION
[0001] Field of the Invention
[0002] The present invention relates to a manufacturing method of
press-molded article and a press molding apparatus.
[0003] Description of the Related Art
[0004] There has been conventionally known a technique of
manufacturing a metal plate used in a vehicle skeleton part of
automobile and the like by press molding. In the above uses, there
are growing demands on not only a metal plate having a fixed
thickness, but also a metal plate having a thickness difference by
partially forming a thickened portion. A manufacturing apparatus
and method of the metal plate having such a thickened portion by
press molding are disclosed in the following patent documents, JP
2014-166645 A, JP 2007-14978 A, and JP 2008-296252 A.
[0005] In the press molding apparatuses disclosed in JP 2014-166645
A and JP 2007-14978 A, both main surfaces of a metal plate are held
by a top and bottom pair of dies and the metal plate is pressed in
a direction parallel to the main surfaces while maintaining this
condition. By this operation, a material of the metal plate flows
into a concave portion provided on a part of a holding surface of
the die to form a thickened portion. Further, in JP 2008-296252 A,
a metal plate folded into a U-shape has an extension portion in one
part thereof in a longitudinal direction and a thickened portion is
formed on the part in the longitudinal direction when the extension
portion is pressed.
[0006] In the press molding apparatuses disclosed in the above
patent documents, JP 2014-166645 A and JP 2007-14978 A, the both
main surfaces of the metal plate are held by the top and bottom
pair of dies and the metal plate is pressed in a direction parallel
to the main surfaces under a condition where positions of the dies
are fixed. In this configuration, friction force generated by
sliding between the dies and the metal plate increases and pressing
force, which is required for pressing, increases excessively. On
the other hand, in the press molding apparatus disclosed in the
above patent document, JP 2008-296252 A, there is a large gap
between the dies and the metal plate, thereby sometimes causing
folding of the metal plate during pressing. When the folding occurs
to the metal plate, a flow direction of the material of the metal
plate becomes out of control, thus making it difficult to form the
thickened portion having a desired shape.
[0007] The present invention has been made in view of the foregoing
problems, and an object thereof is to provide a manufacturing
method of press-molded article and a press molding apparatus,
capable of forming a thickened portion having a desired shape while
reducing pressing force.
SUMMARY OF THE INVENTION
[0008] (1) A manufacturing method of press-molded article according
to one embodiment of the present invention is a method for
manufacturing a press-molded article by molding a member to be
pressed including a flat plate portion. The method comprises:
[0009] a step of placing the member to be pressed in a press
molding apparatus in a manner such that a first main surface of the
flat plate portion is opposed to a first opposing surface and a
second main surface of the flat plate portion, directing opposite
to the first main surface, is opposed to a second opposing surface;
and
[0010] a step of pressing the flat plate portion by bringing a
first press portion opposing to a first end portion of the flat
plate portion and a second press portion opposing to a second end
portion of the flat plate portion, the second end portion being
located on an opposite side of the first end portion, closer to
each other. The first opposing surface and the second opposing
surface, while facing to each other, keep in contact with the flat
plate portion during pressing. In the press step, a thick portion
is formed on the flat plate portion by allowing a part of a
material of the flat plate portion to flow, in a press direction,
into a thickened portion-forming section formed on at least one of
the first opposing surface and the second opposing surface, and at
least one of the first opposing surface and the second opposing
surface is moved to the press direction as the flat plate portion
is pressed by the first press portion and the second press
portion.
[0011] In the above method, when the flat plate portion is pressed
by bringing the first press portion and the second press portion
closer to each other, the opposing surface opposing to the main
surface of the flat plate portion is moved to the press direction.
Thus, as compared to a conventional case where the press is
performed while the opposing surface is fixed without moving,
friction force generated by sliding between the main surface of the
flat plate portion and the opposing surface can be further reduced.
As a result, necessary pressing force can be further reduced.
[0012] Further, in the above method, the thick portion, of which a
thickness is increased, can be formed on the flat plate portion by
pressing the flat plate portion using the first press portion and
the second press portion and allowing a part of the material of the
flat plate portion to flow, in the press direction, into the
thickened portion-forming section. During this process, the first
opposing surface and the second opposing surface, while facing to
each other, keep in contact with the flat plate portion during
pressing, thus enabling to prevent an occurrence of folding to the
flat plate portion during pressing and suppress the non-uniformity
of a flow direction of the material. As a result, the material of
the flat plate portion can be reliably flown into the thickened
portion-forming section to form the thickened portion having a
desired shape.
[0013] The term "first end portion and second end portion" herein
refers to both ends of the flat plate portion in the press
direction.
[0014] (2) In the above manufacturing method of press-molded
article, in the step of placing the member to be pressed, the flat
plate portion may be placed between a die provided with the first
press portion and the first opposing surface and a die provided
with the second press portion and the second opposing surface.
[0015] Having such a configuration can further simplify an
apparatus structure in comparison with a case where the first press
portion and the first opposing surface are provided in separate
members and the second press portion and the second opposing
surface are provided in separate members.
[0016] (3) In the above manufacturing method of press-molded
article, the die provided with the first opposing surface may
include a first divided portion and a second divided portion formed
separately from the first divided portion. The first press portion
may be formed in the first divided portion and the second press
portion may be formed in the second divided portion. In the press
step, the first divided portion may be moved to the press direction
of the first press portion as the flat plate portion is pressed by
the first press portion, and the second divided portion is moved to
the press direction of the second press portion as the flat plate
portion is pressed by the second press portion.
[0017] In this configuration, the first and second end portions of
the flat plate portion can be pressed by the first and second press
portions, respectively, by bringing the first divided portion and
the second divided portion closer to each other. Thus, the first
opposing surfaces can be moved to the press directions of the first
and second press portions accordingly and friction force generated
between the main surface of the flat plate portion and the opposing
surfaces can be further effectively reduced. As a result, pressing
force can be further reduced.
[0018] (4) In the above manufacturing method of press-molded
article, the first divided portion and the second divided portion
may have a comb-teeth shape so as to mesh with each other. In the
press step, the first divided portion and the second divided
portion may come close to each other in such a manner that the both
comb teeth mesh with each other.
[0019] In this configuration, the flat plate portion can be
press-molded in a state of being further stably supported.
[0020] (5) In the above manufacturing method of press-molded
article, in the step of placing the member to be pressed, the
member to be pressed may be placed so as to arrange the first main
surface and the second main surface of the flat plate portion along
a perpendicular direction.
[0021] Having such a configuration can reduce an installation area
of the press molding apparatus, thereby saving a space, in
comparison with a case where the first main surface and the second
main surface are arranged along a horizontal direction.
[0022] (6) In the above manufacturing method of press-molded
article, in the step of placing the member to be pressed, positions
of the first main surface and the second main surface may be
maintained along the perpendicular direction by supporting the flat
plate portion using a temporarily supporting member.
[0023] Having such a configuration can stably support the flat
plate portion to prevent it from falling when the first main
surface and the second main surface of the flat plate portion are
vertically arranged along the perpendicular direction.
[0024] (7) In the above manufacturing method of press-molded
article, in the press step, pressing force may be applied to the
material of the flat plate portion flowing into the thickened
portion-forming section.
[0025] Having such a configuration can further effectively prevent
an occurrence of folding to the flat plate portion in the process
of forming a thick part by allowing the material of the flat plate
portion to flow into the thickened portion-forming section.
[0026] (8) In the above manufacturing method of press-molded
article, the member to be pressed may be molded by a hot press.
[0027] The above method enables to press the flat plate portion
without causing folding as described above, thus a flow direction
of the material can be further reliably controlled even when the
hot press is used.
[0028] (9) A press molding apparatus according to another
embodiment of the present invention is a press molding apparatus
for molding a member to be pressed including a flat plate portion.
The press molding apparatus comprises: a first press portion
opposing to a first end portion of the flat plate portion; a second
press portion opposing to a second end portion of the flat plate
portion, the second end portion being located on an opposite side
of the first end portion; a first opposing surface opposing to a
first main surface of the flat plate portion; a second opposing
surface opposing to a second main surface of the flat plate
portion, the second main surface directing opposite to the first
main surface; and a driving section for bringing the first press
portion and the second press portion closer to each other to press
the flat plate portion. A thickened portion-forming section is
formed on at least one of the first opposing surface and the second
opposing surface for forming a thick part on the flat plate portion
by allowing a part of a material of the flat plate portion to flow
into the thickened portion-forming section. The first opposing
surface and the second opposing surface are, while facing to each
other, configured to keep in contact with the flat plate portion
during pressing. At least one of the first opposing surface and the
second opposing surface is configured to move to a press direction
as the flat plate portion is pressed by the first press portion and
the second press portion.
[0029] In the above press molding apparatus, the opposing surface
opposing to the main surface of the flat plate portion can be moved
to the press direction as the flat plate portion is pressed by
bringing the first press portion and the second press portion
closer to each other. Thus, as compared to a conventional case
where the press is performed while the opposing surface is fixed
without moving, friction force generated by sliding between the
main surface of the flat plate portion and the opposing surface can
be further reduced. As a result, necessary pressing force can be
further reduced.
[0030] Further, in the above press molding apparatus, the thickened
portion, of which a thickness is increased, can be formed on the
flat plate portion by pressing the flat plate portion using the
first press portion and the second press portion and allowing a
part of the material of the flat plate portion to flow, in the
press direction, into the thickened portion-forming section. During
this process, the first opposing surface and the second opposing
surface, while facing to each other, keep in contact with the flat
plate portion during pressing, thus the flat plate portion can be
prevented from being folded during pressing and a flow direction of
the material can be suppressed from becoming non-uniform. As a
result, the material of the flat plate portion can be reliably
flown into the thickened portion-forming section to form the
thickened portion having a desired shape.
[0031] (10) In the above press molding apparatus, the first press
portion and the first opposing surface may be provided in a same
die. The second press portion and the second opposing surface may
be provided in a same die.
[0032] Having such a configuration can further simplify a structure
of press molding apparatus in comparison with a case where the
first press portion and the first opposing surface are provided in
separate members and the second press portion and the second
opposing surface are provided in separate members.
[0033] (11) In the above press molding apparatus, the die provided
with the first opposing surface may include a first divided portion
and a second divided portion formed separately from the first
divided portion. The first press portion may be formed in the first
divided portion and the second press portion may be formed in the
second divided portion.
[0034] In this configuration, the first and second end portions of
the flat plate portion can be pressed by the first and second press
portions, respectively, by bringing the first divided portion and
the second divided portion closer to each other. Thus, the first
opposing surfaces can be moved to the press directions of the first
and second press portions accordingly and friction force generated
between the main surface of the flat plate portion and the opposing
surfaces can be further effectively reduced. As a result, pressing
force can be further reduced.
[0035] (12) In the above press molding apparatus, the first divided
portion and the second divided portion may have a comb-teeth shape
so as to mesh with each other.
[0036] In this configuration, the flat plate portion can be
press-molded in a state of being further stably supported.
[0037] (13) In the above press molding apparatus, the first
opposing surface and the second opposing surface may be arranged
along a perpendicular direction.
[0038] Having such a configuration can reduce an installation area
of the press molding apparatus, thereby saving a space, in
comparison with a case where the first and second opposing surfaces
are arranged along a horizontal direction.
[0039] (14) The above press molding apparatus may comprise a
temporarily supporting member for supporting the flat plate portion
to maintain positions of the first main surface and the second main
surface along the perpendicular direction.
[0040] Having such a configuration can stably support the flat
plate portion to prevent it from falling even when the first main
surface and the second main surface are vertically arranged along
the perpendicular direction.
[0041] (15) The above press molding apparatus may comprise a
back-pressure applicator for applying pressure force to the
material of flat plate portion flowing into the thickened
portion-forming section.
[0042] Having such a configuration can further effectively prevent
an occurrence of folding to the flat plate portion in the process
of forming the thick part by allowing the material of the flat
plate portion to flow into the thickened portion-forming
section.
[0043] The above press molding apparatus enables to press the flat
plate portion without causing folding as described above, thus a
flow direction of the material can be further reliably controlled
even when a hot press is used.
[0044] The present invention can provide the manufacturing method
of press-molded article and the press molding apparatus, capable of
forming the thickened portion having a desired shape while reducing
pressing force.
BRIEF DESCRIPTION OF THE DRAWINGS
[0045] FIG. 1 is a schematic view of a configuration of a press
molding apparatus according to a first embodiment of the present
invention.
[0046] FIG. 2 is an enlarged view around a thickened
portion-forming section of the above press molding apparatus.
[0047] FIG. 3 is a flowchart showing procedures of a manufacturing
method of press-molded article according to the first embodiment of
the present invention.
[0048] FIG. 4 is a diagram showing how a member to be pressed is
heated by an electric furnace.
[0049] FIG. 5 is a diagram showing how a flat plate portion is
pressed to form a thickened portion.
[0050] FIG. 6 is a schematic view of a press-molded article.
[0051] FIG. 7 is a graph showing measured results of a molding load
and a pressing load.
[0052] FIG. 8 is a schematic view of a configuration of a press
molding apparatus according to a first modification of the above
first embodiment.
[0053] FIG. 9 is a diagram showing how a flat plate portion is
pressed to form a thickened portion in the above first
modification.
[0054] FIG. 10 is a schematic view of a configuration of a press
molding apparatus according to a second embodiment of the present
invention.
[0055] FIG. 11 is a diagram showing how a flat plate portion is
pressed in the above second embodiment.
[0056] FIG. 12 is a diagram showing how the flat plate portion is
pressed to form a thickened portion in the above second
embodiment.
[0057] FIG. 13 is a schematic view of a configuration of a press
molding apparatus according to a first modification of the above
second embodiment.
[0058] FIG. 14 is a schematic view of the configuration of the
press molding apparatus according to the first modification of the
above second embodiment.
[0059] FIG. 15 is a schematic view of a configuration of a press
molding apparatus according to a second modification of the above
second embodiment.
[0060] FIG. 16 is a diagram showing how a flat plate portion is
pressed to form a thickened portion in the second modification of
the above second embodiment.
[0061] FIG. 17A and FIG. 17B are schematic views of a configuration
of a press molding apparatus according to a third embodiment of the
present invention.
[0062] FIG. 18A and FIG. 18B are diagrams showing how a flat plate
portion is arranged between dies in the above third embodiment.
[0063] FIG. 19A and FIG. 19B are diagrams showing how the flat
plate portion is pressed to form a thickened portion in the above
third embodiment.
[0064] FIG. 20A and FIG. 20B are schematic views of a configuration
of a press molding apparatus according to a first modification of
the above third embodiment.
[0065] FIG. 21A and FIG. 21B are diagrams showing how a flat plate
portion is arranged between dies in the first modification of the
above third embodiment.
[0066] FIG. 22A and FIG. 22B are diagrams showing how the flat
plate portion is pressed to form a thickened portion in the first
modification of the above third embodiment.
[0067] FIG. 23A and FIG. 23B are schematic views of a configuration
of a press molding apparatus according to a second modification of
the above third embodiment.
[0068] FIG. 24A and FIG. 24B are diagrams showing how a flat plate
portion is pressed to form a thickened portion in the second
modification of the above third embodiment.
[0069] FIG. 25A and FIG. 25B are schematic views of a configuration
of a press molding apparatus according to a third modification of
the above third embodiment.
[0070] FIG. 26A and FIG. 26B are diagrams showing how a flat plate
portion is pressed to form a thickened portion in the third
modification of the above third embodiment.
[0071] FIG. 27A and FIG. 27B are schematic views of a configuration
of a press molding apparatus according to a fourth modification of
the above third embodiment.
[0072] FIG. 28A and FIG. 28B are diagrams showing how a flat plate
portion is pressed to form a thickened portion in the fourth
modification of the above third embodiment.
[0073] FIG. 29 is a diagram showing a configuration of divided
portions in another modification of the above third embodiment.
[0074] FIG. 30 is a schematic view of a configuration of a press
molding apparatus according to a fourth embodiment of the present
invention.
[0075] FIG. 31 is a diagram showing how a flat plate portion is
pressed in the above fourth embodiment.
[0076] FIG. 32 is a diagram showing how the flat plate portion is
pressed to form a thickened portion in the above fourth
embodiment.
[0077] FIG. 33 is a schematic view of a configuration of a press
molding apparatus according to a first modification of the above
fourth embodiment.
[0078] FIG. 34 is a diagram showing how a flat plate portion is
pressed in the first modification of the above fourth
embodiment.
[0079] FIG. 35 is a diagram showing how the flat plate portion is
pressed to form a thickened portion in the first modification of
the above fourth embodiment.
[0080] FIG. 36 is a schematic view of a configuration of a press
molding apparatus according to another embodiment of the present
invention.
[0081] FIG. 37 is a diagrammatic illustration for describing
partial electric heating.
[0082] FIG. 38 is a diagrammatic illustration for describing
press-molding of a flat plate portion subjected to the partial
electric heating.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0083] Hereinafter, embodiments of the present invention will be
described in detail with reference to the drawings.
First Embodiment
[0084] [Configuration of Press Molding Apparatus]
[0085] First of all, a configuration of a press molding apparatus 1
according to a first embodiment of the present invention will be
described by mainly referring to FIG. 1.
[0086] The press molding apparatus 1 is an apparatus for
press-molding a member to be pressed including a flat plate portion
10, such as a metal plate having a fixed thickness, so as to
partially form a thick part (thickened portion) on the flat plate
portion 10. The press molding apparatus 1 comprises a first die 11,
a second die 12, a supporting member 13, a press member 18, and a
drive section 18B.
[0087] The member to be pressed is, for example, a metal plate made
of a material, such as hard steel, soft steel, or aluminum. In an
example shown in the drawing, the whole member to be pressed is
constituted by the flat plate portion 10.
[0088] It is noted that, in the present invention, the whole member
to be pressed is not necessary to be constituted by the flat plate
portion 10, and the member to be pressed may include the flat plate
portion 10 at one part. The flat plate portion 10 comprises a first
main surface 10C, a second main surface 10D, directing opposite to
the first main surface 10C, a first end portion 10A, and a second
end portion 10B, which is located on an opposite side of the first
end portion 10A.
[0089] The first die 11 is fixed on a mount surface 13A of the
supporting member 13 by a fixing member such as a bolt B. The first
die 11 comprises an opposing portion 11C opposing to the flat plate
portion 10, and a guide portion 11D for guiding a movement of the
second die 12, arranged with an interval from the opposing portion
11C.
[0090] The opposing portion 11C comprises a first opposing surface
11B opposing to the first main surface 10C and a first press
portion 11A opposing to the first end portion 10A. In this
configuration, the first press portion 11A and the first opposing
surface 11B are provided in the same first die 11. The first
opposing surface 11B is connected to an upper surface 11F at its
upper end and vertically arranged along a perpendicular direction
(parallel to perpendicular direction). The first press portion 11A
is connected to a lower end of the first opposing surface 11B and
formed flatly along a horizontal direction (parallel to horizontal
direction).
[0091] A thickened portion-forming section 15 as a concave groove
is formed near a center of the first opposing surface 11B. The
thickened portion-forming section 15 is provided to form a
thickened portion, of which a thickness is increased, on the flat
plate portion 10 by allowing a part of a material of the flat plate
portion 10 in a press direction during press-molding. The thickened
portion-forming section 15 is surrounded by a pair of horizontal
sidewall surfaces, stretching horizontally, and a bottom wall
surface connecting between inner side end portions of the pair of
sidewall surfaces, and recessed in a direction away from the flat
plate portion 10. The thickened portion-forming section 15 is
formed on one part of the first opposing surface 11B in the press
direction.
[0092] It is noted that a shape of the thickened portion-forming
section 15 is not limited thereto and can be appropriately changed
according to a shape of the thickened portion formed on the flat
plate portion 10. For example, the shape may have a semi-circular
cross section, a triangular cross section, and the like. Further,
the first opposing surface 11B may include a plurality of the
thickened portion-forming sections 15. Further, the thickened
portion-forming section 15 needs not be formed in the center.
[0093] A plurality of guide rollers 17 are arranged on an inner
surface of the guide portion 11D. The second die 12 has its lower
end part between the guide portion 11D and the opposing portion 11C
and moves to the perpendicular direction according to contraction
of a spring 16. During this process, the guide rollers 17 comes
into contact with a side surface of the second die 12, thereby
guiding a movement of the second die 12 in the perpendicular
direction.
[0094] The second die 12 is connected to an upper end of the spring
16 at its lower surface and has its lower end part between the
opposing portion 11C and the guide portion 11D. Before the
press-molding is started (FIG. 1), an upper surface 12C of the
second die 12 is located higher than an upper surface 11F of the
first die 11.
[0095] The second die 12 comprises a second opposing surface 12B
opposing to the second main surface 10D and a second press portion
12A opposing to the second end portion 10B. In this configuration,
the second press portion 12A and the second opposing surface 12B
are provided in the same second die 12. The second opposing surface
12B is connected to the second press portion 12A at its upper end
and vertically arranged along the perpendicular direction (parallel
to perpendicular direction). The second press portion 12A is formed
flatly along the horizontal direction (parallel to horizontal
direction).
[0096] The second die 12 is arranged in a manner such that the
second opposing surface 12B is opposed to the first opposing
surface 11B in the horizontal direction across the flat plate
portion 10 and the second press portion 12A is opposed to the first
press portion 11A in the perpendicular direction across the flat
plate portion 10. In this configuration, the flat plate portion 10
can be arranged between the first die 11 and the second die 12.
[0097] In FIG. 2, a thickness of the flat plate portion 10 is
represented by T1, a distance between the first and second opposing
surfaces 11B and 12B is represented by D1, and a distance between a
bottom wall surface 15A of the thickened portion-forming section 15
and the second opposing surface 12B is represented by D2. In the
press molding apparatus 1, the distance D1 is adjusted according to
the thickness T1, so that a ratio of distance D1 (mm)/thickness T1
(mm) becomes 1.1 or lower. For example, when the flat plate portion
10 having the thickness T1 of 1.4 mm is pressed, the distance D1 is
adjusted to 1.6 mm. Further, the distance D2 is adjusted to 2.2
mm.
[0098] As shown in FIG. 2, before the pressing is started (i.e.,
before the flat plate portion 10 is pressed by the first and second
press portions 11A and 12A), a gap between the flat plate portion
10, and the first opposing surface 11B and second opposing surface
12B may be formed unless the gap causes folding during pressing. In
another words, the first opposing surface 11B and the second
opposing surface 12B are opposed to each other with the distance D1
sufficient to avoid the folding of the flat plate portion 10 during
pressing. The term "folding of the flat plate portion 10" herein
refers to a condition where the flat plate portion 10 is folded to
such a degree that a flow of the material of the flat plate portion
10 caused by pressing is disturbed, and does not include a minute
swell of the flat plate portion 10 caused during pressing unless it
affects the flow of the material.
[0099] Then, during pressing, the first opposing surface 11B and
the second opposing surface 12B, while facing to each other, keep
in contact with the flat plate portion 10. However, the flat plate
portion 10 needs not always contact with the first opposing surface
11B or the second opposing surface 12B during pressing. Further,
the whole flat plate portion 10 needs not contact with the first
opposing surface 11B or the second opposing surface 12B.
[0100] As shown in FIG. 1, the supporting member 13 is a metallic
member having a rectangular parallelepiped shape and comprises the
flat mount surface 13A on which a lower surface of the first die 11
is placed. The mount surface 13A of the supporting member 13 is
laterally arranged along the horizontal direction and fixed on the
first die 11 by a fixing member such as the bolt B.
[0101] A press member 18 is a member that presses the upper surface
12C of the second die 12 to move the second die 12 downward in the
perpendicular direction. The press member 18 having a press surface
18A is moved downward in the perpendicular direction by operating a
driving section 18B. Then, the upper surface 12C of the second die
12 is pressed by the press surface 18A, so that the second die 12
can move downward in the perpendicular direction.
[0102] The driving section 18B is arranged in contact with an upper
surface 18C of the press member 18. The driving section 18B
comprises, for example, a hydraulic or electric piston and presses
the upper surface 18C to move the press member 18 downward in the
perpendicular direction.
[0103] In the above press molding apparatus 1, first of all, the
press member 18 is lowered by operating the driving section 18B, so
that the press surface 18A is brought into contact with the upper
surface 12C of the second die 12. The press member 18 is further
lowered to move the second die 12 downward in the perpendicular
direction while maintaining this state, so that the second press
portion 12A is brought closer to the first press portion 11A. Then,
the flat plate portion 10 is pressed by the first press portion 11A
and the second press portion 12A from the both end portions 10A and
10B in a direction parallel to the main surfaces 10C and 10D (FIG.
5). By this operation, a part of the material of the flat plate 10
is flown, in the press direction, into the thickened
portion-forming section 15 to form the thickened portion.
[0104] In this configuration in the above press molding apparatus
1, the second opposing surface 12B is moved to the press direction
as the pressing is performed by the first and second press portions
11A and 12A. That is, the second opposing surface 12B is slid
toward the same direction as the press direction of the flat plate
portion 10. Thus, friction force generated by sliding between the
second main surface 10D and the second opposing surface 12B can be
reduced and pressing force required for molding the flat plate
portion 10 can be reduced.
[0105] [Manufacturing Method of Press-Molded Article]
[0106] Next, a manufacturing method of press-molded article using
the above press molding apparatus 1, according to the present
embodiment, will be described along a flowchart shown in FIG. 3.
First of all, a member to be pressed is prepared in a step S10. In
the step S10, the member to be pressed including the flat plate
portion 10, such as a metal plate having a fixed thickness, is
prepared and heated with a predetermined temperature by an electric
furnace F (FIG. 4). By this operation, the whole flat plate portion
10 becomes softened. In the present embodiment, a press-molded
article is manufactured by a hot press, in which the whole flat
plate portion 10 is heated to be softened and then molded. It is
noted that the present invention is not limited to the case where
the hot press is performed, and may adopt a cold working without
performing the step S10.
[0107] Next, the member to be pressed is placed in a step S20. In
the step S20, the flat plate portion 10 softened in the above step
S10 is placed between the first die 11 and the second die 12 (FIG.
1). More specifically, the flat plate portion 10 is placed in such
a manner that the first main surface 10C is opposed to the first
opposing surface 11B along the perpendicular direction and the
second main surface 10D is opposed to the second opposing surface
12B along the perpendicular direction. During this process, the
first opposing surface 11B and the second opposing surface 12B,
while facing to each other, keep in contact with the flat plate
portion 10 during pressing to prevent an occurrence of folding to
the flat plate portion 10 in a following press step S30.
[0108] Next, the member to be pressed is pressed in a step S30. In
the step S30, first of all, the press member 18 is lowered by
operating the driving section 18B, so that the press surface 18A is
brought into contact with the upper surface 12C of the second die
12. Then, the press member 18 is further lowered to press the upper
surface 12C of the second die 12, so that the second die 12 is
moved downward and the second press portion 12A is brought closer
to the first press portion 11A. By this operation, the flat plate
portion 10 is pressed by the first press portion 11A and the second
press portion 12A from the both end portions 10A and 10B in the
direction parallel to the main surfaces 10C and 10D. Then, a part
of the material of the flat plate portion 10 is flown into the
thickened portion-forming section 15 in the press direction (arrows
in FIG. 5) to form the thickened portion, of which a thickness is
increased, on the flat plate portion 10. Subsequently, the
operation of the driving section 18B is stopped at the time when
the press surface 18A comes into contact with the upper surface 11F
of the first die 11.
[0109] In the step S30, the second opposing surface 12B is moved
(slid) toward the press direction as the flat plate portion 10 is
pressed by the first press portion 11A and the second press portion
12A. That is, the second opposing surface 12B is moved to the same
direction as the press direction of the flat plate portion 10.
Thus, friction force generated by sliding between the second main
surface 10D and the second opposing surface 12B can be reduced
during pressing and the flat plate portion 10 can be molded with
less pressing force.
[0110] Further, the first and second opposing surfaces 11B and 12B,
while facing to each other, keep in contact with the flat plate
portion 10 during pressing. This can prevent the flat plate portion
10 from being folded during pressing, thereby suppressing the
non-uniformity of the flow direction of the material. Thus, the
material of the flat plate portion 10 can be reliably flown into
the thickened portion-forming section 15 from the both end portions
10A and 10B. As a result, the thickened portion can be formed in a
desired shape in accordance with the shape of the thickened
portion-forming section 15.
[0111] Finally, the press-molded article is taken out in a step
S40. In the step S40, the press member 18 is moved up by operating
the driving section 18B after completing the press-molding of the
flat plate portion 10 in the step S30. Then, a press-molded article
100 having a thickened portion 100A formed thereon (FIG. 6) is
taken out. Through the above steps S10 to S40, the manufacturing
method of press-molded article according to the present embodiment
is completed.
ADVANTAGEOUS EFFECTS
[0112] Next, representative configurations and advantageous effects
of the above press molding apparatus 1 will be described.
[0113] The above press molding apparatus 1 comprises the first
press portion 11A, the second press portion 12A, the first opposing
surface 11B, the second opposing surface 12B, and the driving
section 18B that brings the first press portion 11A and the second
press portion 12A closer to each other. The first opposing surface
11B includes the thickened portion-forming section 15 for forming
the thick part on the flat plate portion 10. The first opposing
surface 11B and the second opposing surface 12B, while facing to
each other, keep in contact with the flat plate portion 10 during
pressing. The thickened portion-forming section 15 is configured in
such a manner that the part of the material of the flat plate
portion 10 is flown, in the press direction, into the thickened
portion-forming section 15 as the flat plate portion 10 is pressed
by the first press portion 11A and the second press portion 12A.
The second opposing surface 12B is configured to move to the press
direction as the flat plate portion 10 is pressed by the first
press portion 11A and the second press portion 12A.
[0114] In the above press molding apparatus 1, the second opposing
surface 12B can be moved to the press direction as the first press
portion 11A and the second press portion 12A come closer to each
other to press the flat plate portion 10. Thus, as compared to a
conventional case where the pressing is performed while the
opposing surface is fixed without moving, friction force generated
by sliding between the second main surface 10D and the second
opposing surface 12B can be further reduced. As a result, necessary
pressing force can be further reduced.
[0115] A graph in FIG. 7 shows an effect of load reduction achieved
in the present embodiment, in which the pressing is performed while
moving the opposing surface. In the graph in FIG. 7, columns 1 and
2 show values of a molding load and a pressing load in a case where
the pressing is performed without moving the opposing surface and a
case where the pressing is performed while moving the opposing
surface, respectively. The term "molding load" refers to a load
required for press-molding the flat plate portion 10, while the
term "pressing load" refers to a load required for fixing a
clearance between the dies. As is evident from the graph, the
molding load is significantly reduced (reduced up to about
one-tenth) when the pressing is performed while moving the opposing
surface as compared to the case where the pressing is performed
without moving the opposing surface.
[0116] Further, in the above press molding apparatus 1, the
thickened portion 100A, of which a thickness is increased, can be
formed on the flat plate portion 10 by pressing the flat plate
portion 10 by the first press portion 11A and the second press
portion 12A and allowing the part of the material of the flat plate
portion 10 to flow into the thickened portion-forming section 15 in
the press direction. During this process, the first opposing
surface 11B and the second opposing surface 12B, while facing to
each other, keep in contact with the flat plate portion 10 during
pressing. This can prevent the non-uniformity of the flow direction
of the material caused by folding generated in the flat plate
portion 10 during pressing. That is, it becomes possible to control
the flow of the material. Thus, the material of the flat plate
portion 10 can be reliably flown into the thickened portion-forming
section 15, thereby enabling to form the thickened portion 100A
having a desired shape.
[0117] In the above press molding apparatus 1, the first press
portion 11A and the first opposing surface 11B are provided in the
same first die 11, and the second press portion 12A and the second
opposing surface 12B are provided in the same second die 12. This
can further simplify a structure of the press molding apparatus 1
in comparison with a case where the first press portion 11A and the
first opposing surface 11B are provided in separate members and the
second press portion 12A and the second opposing surface 12B are
provided in separate members.
[0118] In the above press molding apparatus 1, the first opposing
surface 11B and the second opposing surface 12B are arranged along
the perpendicular direction. This can reduce an installation area
of the press molding apparatus 1, thereby saving a space, in
comparison with a case where the first opposing surface 11B and the
second opposing surface 12B are arranged along the horizontal
direction.
First Modification
[0119] Next, a press molding apparatus 1A according to a first
modification of the above first embodiment will be described with
reference to FIG. 8 and FIG. 9. In the press molding apparatus 1A
according to the first modification, the opposing portion 11C of
the first die 11 and the guide portion 11D are provided separately
from each other. Further, the press member 18 comprises a main body
portion 18D, which has the upper surface 18C in contact with the
driving section 18B, and a press portion 18E fixed on a lower
surface 18G of the main body portion 18D. The press portion 18E is
made from a shape in which a press portion main body 18H, fixed on
the lower surface 18G by a fixing member such as a bolt B, is
connected to a first supporting portion 18F and a second supporting
portion 18I. The press portion 18E is formed in an upside down
U-shape in a cross sectional view.
[0120] The press portion main body 18H comprises a press surface
18J that presses the upper surface 12C of the second die 12. The
first supporting portion 18F and the second supporting portion 18I
extend downward in the perpendicular direction from both end
portions of the press portion main body 18H in the horizontal
direction.
[0121] A first inner surface 18K is formed inside the first
supporting portion 18F and a second inner surface 18L is formed
inside the second supporting portion 18I. A horizontal distance
between the first inner surface 18K and the second inner surface
18L is made slightly larger than that between side surfaces of the
first die 11 (opposing portion 11C) and the second die 12. In this
configuration, when the press member 18 is lowered to press the
flat plate portion 10 as shown in FIG. 9, the first die 11
(opposing portion 11C) and the second die 12 can be placed between
the first and second supporting portions 18F and 18I. This can
further reliably prevent displacement of the first and second dies
11 and 12 during pressing.
Second Embodiment
[0122] Next, a press molding apparatus 2 and a manufacturing method
of press-molded article according to a second embodiment of the
present invention will be described with reference to FIG. 10 to
FIG. 12. It is noted that only the parts in which the second
embodiment differs from the above first embodiment will be
described in detail.
[0123] [Configuration of Press Molding Apparatus]
[0124] The press molding apparatus 2 comprises a first die 21, a
second die 22, a supporting member 26, and a driving section 28B.
The first die 21 is formed in an approximately rectangular
parallelepiped shape and comprises a first opposing surface 21B
opposing to the first main surface 10C, a first side surface 21C
directing opposite to the first opposing surface 21B, and a first
press portion 21A opposing to the first end portion 10A. In this
configuration, the first press portion 21A and the first opposing
surface 21B are provided in the same first die 21. The first side
surface 21C of the first die 21 is fixed on a fixed surface 26A of
the supporting member 26 by a fixing member such as a bolt B.
[0125] The first opposing surface 21B is connected to an upper
surface 21F at its upper end and arranged along the perpendicular
direction. The first press portion 21A is connected to a lower end
of the first opposing surface 21B so as to form an acute angle at
the point of intersection. A thickened portion-forming section 25
as a concave groove is formed near a center of the first opposing
surface 21B and used for forming a thickened portion by allowing a
part of the material of the flat plate portion 10 to flow into the
thickened portion-forming section 25 during pressing.
[0126] The second die 22 comprises a second die main body 28 and a
die fixing member 29 connected to an upper surface of the second
die main body 28. The second die main body 28 is formed in a
rectangular parallelepiped shape, having a size capable of being
inserted into a die space 26B formed in the supporting member 26.
The second die main body 28 comprises a second opposing surface 22B
opposing to the second main surface 10D, a second side surface 22C
directing opposite to the second opposing surface 22B, and a second
press portion 22A opposing to the second end portion 10B. In this
configuration, the second press portion 22A and the second opposing
surface 22B are provided in the same second die 22. The second
opposing surface 22B is connected to the second press portion 22A
at its upper end and arranged along the perpendicular direction.
The second press portion 22A intersects with the second opposing
surface 22B so as to form an acute angle. The die fixing member 29
has the approximately same width as the supporting member 26 and
fixed to the upper surface of the second die main body 28 by the
bolt B.
[0127] The second die main body 28 is inserted into the die space
26B (FIG. 11), so that the second opposing surface 22B is arranged
to be opposed to the first opposing surface 21B across the flat
plate portion 10 in the horizontal direction and the second press
portion 22A is arranged to be opposed to the first press portion
21A across the flat plate portion 10 in the perpendicular
direction. Thus, the flat plate portion 10 can be placed between
the first die 21 and the second die 22. In this configuration, the
first opposing surface 21B and the second opposing surface 22B,
while facing to each other, keep in contact with the flat plate
portion 10 during pressing. Further, the second side surface 22 C
comes into contact with guide rollers 27, thereby guiding a
movement of the second die main body 28 in the perpendicular
direction.
[0128] The supporting member 26 is a metallic member and includes
the die space 26B having a concave shape, to which the second die
main body 28 is inserted. The supporting member 26 comprises the
fixed surface 26A to which the first die 21 is fixed, a bottom
surface 26C opposing to a lower surface 22D of the second die main
body 28, and a guide surface 26D on which a plurality of the guide
rollers 27 are arranged.
[0129] The driving section 28B is arranged in contact with an upper
surface 29A of the die fixing member 29. The driving section 28B
comprises, as in the above first embodiment, a hydraulic or
electric piston and moves the second die 22 downward in the
perpendicular direction by pressing the upper surface 29A.
[0130] [Manufacturing Method of Press-Molded Article]
[0131] Next, explanation is given to a manufacturing method of
press-molded article using the above press molding apparatus 2.
First of all, a member to be pressed including the flat plate
portion 10 is softened by heating to be prepared (FIG. 3: S10).
Next, the flat plate portion 10 is placed in the first die 21 while
the second die 22 is positioned above the first die 21 (FIG. 10).
Then, the second die 22 is lowered by operating the driving section
28B, so that the second die main body 28 is inserted into the die
space 26B, and the second press portion 22A is brought into contact
with the second end portion 10B (FIG. 11). By this operation, the
member to be pressed is placed in a manner such that the first main
surface 10C is opposed to the first opposing surface 21B and the
second main surface 10D is opposed to the second opposing surface
22B (FIG. 3: S20). During this process, the first and second main
surfaces 10C and 10D are arranged along the perpendicular
direction. Further, the first opposing surface 21B and the second
opposing surface 22B, while facing to each other, keep in contact
with the flat plate portion 10 during pressing.
[0132] Next, the second die 22 is further lowered by operating the
driving section 28B, so that the second press portion 22A is
brought closer to the first press portion 21A. By this operation,
the flat plate portion 10 is pressed by the first press portion 21A
and the second press portion 22A in a direction parallel to the
main surfaces 10C and 10D, and a part of the material of the flat
plate portion 10 is flown into the thickened portion-forming
section 25 (FIG. 12). By this operation, the thickened portion, of
which a thickness is increased, is formed on one part of the flat
plate portion 10 (FIG. 3: S30). During this process, as in the
above first embodiment, the second opposing surface 22B is moved
toward the press direction as the flat plate portion 10 is pressed
by the first press portion 21A and the second press portion 22A.
Then, after the press of the flat plate portion 10 is completed,
the second die 22 is moved up by operating the driving section 28B
and a press-molded article is taken out (FIG. 3: S40).
[0133] In the above second embodiment, as in the above first
embodiment, the second opposing surface 22B is moved toward the
press direction as the flat plate portion 10 is pressed by the
first press portion 21A and the second press portion 22A in the
perpendicular direction. Thus, friction force generated by sliding
between the second main surface 10D and the second opposing surface
22B can be reduced during pressing and the flat plate portion 10
can be molded with less pressing force. Further, the first opposing
surface 21B and the second opposing surface 22B, while facing to
each other, keep in contact with the flat plate portion 10 during
pressing. This can prevent the non-uniformity of the flow direction
of the material of the flat plate portion 10 caused by folding
generated during pressing, thus the material of the flat plate
portion 10 can be reliably flown into the thickened portion-forming
section 25. Further, in the configuration of the above second
embodiment, the first side surface 21C of the first die 21 is fixed
to the supporting member 26 and the second die 22 (second die main
body 28) is inserted into the die space 26B of the supporting
member 26, thus displacement of the first and second dies 21 and 22
can be further reliably prevented during pressing.
First Modification
[0134] Next, a press molding apparatus 2A according to a first
modification of the above second embodiment will be described with
reference to FIG. 13 and FIG. 14. The press molding apparatus 2A
according to the first modification further comprises a temporarily
supporting member 26E, which prevents the flat plate portion 10
from falling.
[0135] The press molding apparatus 2A comprises a pair of the
temporarily supporting members 26E each having a thin plate shape.
As shown in FIG. 14, each temporarily supporting member 26E is
provided outside of an insertion region of the second die 22. Each
temporarily supporting member 26E is formed in an elongate shape
extending from a lower end to an upper end, and the upper end is
bent in a direction away from the flat plate portion 10 while the
lower end is attached to the supporting member 26 by a fixture 26F.
The temporarily supporting members 26E contact with both end parts
of the second main surface 10D of the flat plate portion 10,
thereby supporting the flat plate portion 10 so as to maintain the
first main surface 10C and the second main surface 10D along the
perpendicular direction.
[0136] In the above press molding apparatus 2A, first of all, the
flat plate portion 10 is placed between the first die 21 and the
temporarily supporting members 26E. During this process, the flat
plate portion 10 is supported by the temporarily supporting members
26E and thus maintained in a vertical condition where the first and
second main surfaces 10C and 10D are arranged along the
perpendicular direction. Subsequently, the second die 22 (second
die main body 28) is inserted into the die space 26B and the flat
plate portion 10 is arranged between the first die 21 and the
second die 22. In this manner, before the flat plate portion 10 is
arranged between the first die 21 and the second die 22, the
temporarily supporting members 26E can stably support the flat
plate portion 10 and prevent it from falling.
Second Modification
[0137] Next, a press molding apparatus 2B according to a second
modification of the above second embodiment will be described with
reference to FIG. 15 and FIG. 16. The press molding apparatus 2B
according to the second modification comprises a back-pressure
applicator 25E that applies pressure force to the material of the
flat plate portion 10 flowing into a thickened portion-forming
section 25A.
[0138] The thickened portion-forming section 25A is formed as a
hole that penetrates in the horizontal direction at a substantially
center of the first die 21. A through hole 26G is formed in the
supporting member 26 and communicates with the thickened
portion-forming section 25A.
[0139] The back-pressure applicator 25E comprises a pad portion
25B, an elastic member 25C, and a supporting portion 25D. The pad
portion 25B is formed in a convex shape and arranged inside the
thickened portion-forming section 25A. The elastic member 25C is
constituted by a spring that energizes the pad portion 25B and
arranged inside the through hole 26G. The elastic member 25C is
arranged between the pad portion 25B and the supporting portion
25D. Both ends of the elastic member 25C may or may not be
connected to the pad portion 25B and the supporting portion 25D.
The supporting portion 25D is integrally fixed to the supporting
member 26.
[0140] When the flat plate portion 10 is pressed by the first press
portion 21A and the second press portion 22A, the material of the
flat plate portion 10 flows into the thickened portion-forming
section 25A while pushing the pad portion 25B and thereby causing
compression of the elastic member 25C. During this process,
restoring force of the elastic member 25C is imparted, via the pad
portion 25B, to the material flowing into the thickened
portion-forming section 25A. That is, the material of the flat
plate portion 10 flows into the thickened portion-forming section
25A while the pressure force is applied to the material by the
back-pressure applicator 25E. In this manner, an occurrence of
folding to the flat plate portion 10 can be further effectively
prevented in the process of flowing the material into the thickened
portion-forming section 25A by pressing the flat plate portion
10.
Third Embodiment
[0141] Next, a press molding apparatus 3 and a manufacturing method
of press-molded article according to a third embodiment of the
present invention will be described with reference to FIG. 17A to
FIG. 19B. It is noted that only the parts in which the third
embodiment differs from the above first embodiment will be
described in detail.
[0142] [Configuration of Press Molding Apparatus]
[0143] The press molding apparatus 3 comprises a first die 33, a
second die 34 arranged above the first die 33, a supporting member
39 on which the first die 33 is placed, a press member 38, and a
driving section 38B. The first die 33 is constituted of a first
divided portion 31 and a second divided portion 32 formed
separately from the first divided portion 31. The first divided
portion 31 and the second divided portion 32 are arranged to be
opposed to each other in the horizontal direction.
[0144] The first divided portion 31 comprises a first portion 31D
to be pressed, which is pressed by the press member 38, a first
press portion 31E for pressing the flat plate portion 10, and a
first mount portion 31F on which the flat plate portion 10 is
placed. A first surface 31C to be pressed, formed on an upper part
of the first portion 31D to be pressed, is pressed by a first press
surface 38F. A first press portion 31A, formed on a side part of
the first press portion 31E, is opposed to the first end portion
10A of the flat plate portion 10. A first opposing surface 31B,
formed on an upper part of the first mount portion 31F, is opposed
to the first main surface 10C of the flat plate portion 10.
[0145] The second divided portion 32 has a symmetrical shape to the
first divided portion 31. That is, the second divided portion 32
comprises a second portion 32D to be pressed, which is pressed by
the press member 38, a second press portion 32E for pressing the
flat plate portion 10, and a second mount portion 32F on which the
flat plate portion 10 is placed. A second surface 32C to be
pressed, formed on an upper part of the second portion 32D to be
pressed, is pressed by a second press surface 38G. A second press
portion 32A, formed on a side part of the second press portion 32E,
is opposed to the second end portion 10B of the flat plate portion
10. A first opposing surface 32B, formed on an upper part of the
second mount portion 32F, is opposed to the first main surface 10C
of the flat plate portion 10. Further, the first opposing surfaces
31B and 32B are laterally arranged along the horizontal direction
(parallel to horizontal direction).
[0146] The first and second mount portions 31F and 32F have a
comb-teeth shape so as to mesh with each other. Specifically, as
shown by arrows in FIG. 17B, the comb teeth of the first mount
portion 31F are inserted into gaps between the comb teeth of the
second mount portion 32F, and vice versa, as the first and second
mount portions 31F and 32 are brought closer to each other.
[0147] The second die 34 is formed in an approximately rectangular
parallelepiped shape and comprises a second opposing surface 34B
opposing to the second main surface 10D of the flat plate portion
10. The second opposing surface 34B is laterally arranged along the
horizontal direction (parallel to horizontal direction). A
thickened portion-forming section 35 is formed as a concave groove
near a center of the second opposing surface 34B, so that a
thickened portion, of which a thickness is increased, can be formed
on the flat plate portion 10 by allowing a part of the material of
the flat plate portion 10 to flow into the thickened
portion-forming section 35 during pressing. Further, when the flat
plate portion 10 is arranged between the first and second dies 33
and 34 (FIG. 18A), the first opposing surfaces 31B and 32B, and the
second opposing surface 34B, while facing to each other, keep in
contact with the flat plate portion 10 during pressing.
[0148] The supporting member 39 is a member made of metal, formed
in a rectangular parallelepiped shape, and used for mounting the
first die 33. A plurality of guide rollers 37 are arranged on an
upper surface of the supporting member 39, and allows the first and
second divided portions 31 and 32 to slide in the horizontal
direction.
[0149] The press member 38 presses the first and second divided
portions 31 and 32, thereby sliding them in the horizontal
direction. The press member 38 comprises a main body portion 38A in
contact with the driving section 38H and a press portion 38B fixed
on a lower surface of the main body portion 38A. The press portion
38B is made from a shape in which a press portion main body 38C,
fixed on the lower surface of the main body portion 38A by the bolt
B, is connected to a first extension portion 38D and a second
extension portion 38E. A cross section of the press portion 38B cut
with a plane including a width direction (right/left direction in
FIG. 17B) of the flat plate portion 10 and the perpendicular
direction has an upside down U-shape. A lower surface of the press
portion main body 38C is connected to an upper surface of the
second die 34 by a plurality of (two) springs. The first press
surface 38F for pressing the first divided portion 31 is formed at
a tip of the first extension portion 38D, while the second press
surface 38G for pressing the second divided portion 32 is formed at
a tip of the second extension portion 38E.
[0150] The driving section 38H is arranged in contact with the
upper surface of the press member 38 (main body portion 38A). The
driving section 38H comprises, as in the above first embodiment, a
hydraulic or electric piston, and moves the press member 38
downward in the perpendicular direction by pressing.
[0151] [Manufacturing Method of Press-Molded Article]
[0152] Next, explanation is given to a manufacturing method of
press-molded article using the above press molding apparatus 3.
First of all, a member to be pressed including the flat plate
portion 10 is softened by heating to be prepared (FIG. 3: S10).
[0153] Next, the flat plate portion 10 is placed on the first and
second divided portions 31 and 32 with the first main surface 10C
turned downward (FIG. 17A), while the second die 34 is positioned
above them (FIG. 17A). Next, the press member 38 is lowered by
operating the driving section 38H, so that the second die 34 fixed
to the press member 38 is also lowered. By this operation, as shown
in FIG. 18A, the flat plate portion 10 is placed in a manner such
that the first main surface 10C is opposed to the first opposing
surfaces 31B and 32B, and the second main surface 10D is opposed to
the second opposing surface 34B (FIG. 3: S20). During this process,
the first opposing surfaces 31B and 32B, and the second opposing
surface 34B, while facing to each other, keep in contact with the
flat plate portion 10 during pressing.
[0154] Next, the press member 38 is further lowered by operating
the driving section 38H, so that the first and second press
surfaces 38F and 38G are brought into contact with the first and
second surfaces 31C and 32C to be pressed, respectively (FIG. 19A).
When the press member 38 is further lowered while maintaining this
state, the first press surface 38F, while sliding on the first
surface 31C to be pressed, makes the first divided portion 31 slide
to a side of the second divided portion 32, and the second press
surface 38G, while sliding on the second surface 32C to be pressed,
makes the second divided portion 32 slide to a side of the first
divided portion 31. By this operation, the first and second divided
portions 31 and 32 approach each other so as to cause tips of the
comb teeth of one divided portion to abut gaps between the comb
teeth of the other divided portion (FIG. 19B). In this manner, when
the first and second divided portions 31 and 32 approach each
other, the first and second press portions 31A and 32a also come
close to each other and the flat plate portion 10 is pressed from
the both sides of the end portions 10A and 10B in the horizontal
direction. During this process, a part of the material of the flat
plate portion 10 is flown into the thickened portion-forming
section 35 in the press direction, thereby forming a thickened
portion, of which a thickness is increased, on the flat plate
portion 10.
[0155] In the press step, the first divided portion 31 moves to the
press direction of the first press portion 31A (direction from left
to right in drawing) as the first press portion 31A presses the
flat plate portion 10. Further, the second divided portion 32 moves
to the press direction of the second press portion 32A (direction
from right to left in drawing) as the second press portion 32A
presses the flat plate portion 10. Thus, the first opposing surface
31B is moved to the press direction of the first press portion 31A
as the flat plate portion 10 is being pressed, and the second
opposing surface 32B is moved to the press direction of the second
press portion 32A as the flat plate portion 10 is being pressed.
Then, after the press of the flat plate portion 10 is completed,
the press member 38 and the second die 34 are moved up by operating
the driving section 38H and a press-molded article is taken out
(FIG. 3: S40).
[0156] In the above third embodiment, the first die 33 is divided
into the first divided portion 31 and the second divided portion
32. By bringing them closer to each other, the first and second end
portions 10A and 10B of the flat plate portion 10 can be pressed by
the first and second press portions 31A and 32A, respectively. In
this configuration, the first opposing surface 31B and the first
opposing surface 32B can be moved in the opposite directions to
each other according to the press directions of the first and
second press portions 31A and 32A. As a result, friction force
generated between the first main surface 10C, and the first
opposing surfaces 31B and 32B can be further effectively reduced
and pressing force can be further reduced. Further, the first and
second divided portions 31 and 32 are formed in the comb-teeth
shape so as to mesh with each other, thus the flat plate portion 10
can be press-molded while being stably supported.
First Modification
[0157] Next, a first modification of the above third embodiment
will be described with reference to FIG. 20A to FIG. 22B. In a
press molding apparatus 3A according to the first modification, a
plurality of (two) thickened portion-forming sections 35 are formed
at intervals from each other on the second opposing surface 34B. In
this configuration, by pressing the flat plate portion 10 using the
first and second press portions 31A and 32A, the material of the
flat plate portion 10 can be flown into each of the plurality of
the thickened portion-forming sections 35 (FIG. 22A), thereby
enabling to manufacture a press-molded article having a more
complicated shape.
[0158] It is noted that a shape and size of each thickened
portion-forming section 35 may be the same or different from each
other. Further the intervals between the thickened portion-forming
sections 35 can be appropriately designed according to a shape of
the press-molded article.
Second Modification
[0159] Next, a second modification of the above third embodiment
will be described with reference to FIG. 23A and FIG. 24B. A press
molding apparatus 3B according to the second modification
comprises, as described in the second modification of the above
second embodiment, a back-pressure applicator 35D that applies
pressure force to the material of the flat plate portion 10 flowing
into a thickened portion-forming section 35A.
[0160] The thickened portion-forming section 35A having a hole
shape is formed near a center of the second opposing surface 34B.
The back-pressure applicator 35D comprises a pad portion 35B and an
elastic member 35C. The pad portion 35B is formed in a convex shape
and arranged inside the thickened portion-forming section 35A. The
elastic member 35C is constituted by a spring that energizes the
pad portion 35B, and one end of the elastic member 35C is connected
to the pad portion 35B and the other end is connected to a hole
wall surface of the second die 34.
[0161] As shown in FIG. 24A, when the flat plate portion 10 is
pressed by the first and second press portions 31A and 32A, the
material of the flat plate portion 10 presses the pad portion 35B
while flowing into the thickened portion-forming section 35A.
During this process, restoring force of the elastic member 35C is
imparted to the material flowing into the thickened portion-forming
section 35A via the pad portion 35B. That is, the material of the
flat plate portion 10 flows into the thickened portion-forming
section 35A, while pressure force is applied to the material by the
back-pressure applicator 35D. In this manner, an occurrence of
folding to the flat plate portion 10 can be further effectively
prevented in the process of flowing the material of the flat plate
portion 10 into the thickened portion-forming section 35A.
Third Modification
[0162] Next, a third modification of the above third embodiment
will be described with reference to FIG. 25A and FIG. 26B. In a
press molding apparatus 3C according to the third modification, the
first divided portion 31 and the second divided portion 32 are
connected to each other by a spring 33A.
[0163] The first divided portion 31 comprises a first mount portion
31G of a quadrangular shape in a plan view (FIG. 25B) and a first
protrusion 31H projected from a side surface of the first mount
portion 31G. A first opposing surface 31B is formed on an upper
part of the first mount portion 31G. The first protrusion 31H is
provided to the first mount portion 31G with a difference in
height, so that an upper surface of the first protrusion 31H is
located lower than the first opposing surface 31B (FIG. 25A).
[0164] The second divided portion 32 comprises a second mount
portion 32G of a quadrangular shape, of which an area is smaller
than that of the first mount portion 31G, in a plan view (FIG.
25B). A first opposing surface 32B is formed on an upper part of
the second mount portion 32G. Further the second divided portion 32
is provided with a hollow portion 32H, in which the first
protrusion 31H can be inserted. That is, the hollow portion 32H is
formed to be larger than the first protrusion 31H. The flat plate
portion 10 is placed on the first opposing surfaces 31B and 32B so
as to cross over the first and second divided portions 31 and 32
(FIG. 25A).
[0165] In this configuration, the first and second divided portions
31 and 32 are connected to each other by the spring 33A, thus a
positional relation between the first and second divided portions
31 and 32 can be further reliably maintained. Further, in this
configuration, the first protrusion 31H can be inserted into the
hollow portion 32H, thereby enabling to guide the movement of the
first and second divided portions 31 and 32 in horizontal direction
during pressing.
Fourth Modification
[0166] Next, a fourth modification of the above third embodiment
will be described with reference to FIG. 27A and FIG. 28B. In a
press molding apparatus 3D according to the fourth modification,
the first divided portion 31 comprises a first mount portion 31I of
an approximately right-angled triangle shape in a plan view (FIG.
27B). The first opposing surface 31B is formed on an upper part of
the first mount portion 31I. Further, the second divided portion 32
comprises a second mount portion 32I of an approximately
right-angled triangle shape, symmetric to that of the first mount
portion 31I, in a plan view (FIG. 27B). The first opposing surface
32B is formed on an upper part of the second mount portion 32I. By
bringing the first and second mount portions 31I and 32I closer to
each other, slopes 31J and 32J of the right-angled triangles come
in contact with each other to form a mount surface having a
quadrangular shape in a plan view (FIG. 28B). Also in this
modification, as is the case using the comb-teeth shape described
in the above third embodiment, the flat plate portion 10 can be
pressed while being stably supported.
[0167] It is noted that the shapes of the first and second divided
portions 31 and 32 are not limited to the comb-teeth shape and the
right-angled triangle shape as described above. Specifically,
various shapes of the first and second divided portions 31 and 32
can be adopted as long as such a shape allows the first and second
divided portions 31 and 32 to overlap each other, at least
partially, in the press direction at a time point when the
thickened portion is formed on the flat plate portion 10 by
pressing.
[0168] Further, when the comb-teeth shape is adopted, both comb
teeth need not be completely inserted to each other at the time of
completion of the pressing, as shown in FIG. 19B. For example, as
shown in FIG. 29, in a region R, to which a pair of meshing
portions are externally contacting at the time of completion of the
pressing, there may be gaps S of size not causing an inflow of the
material or folding during press-molding.
Fourth Embodiment
[0169] Next, a press molding apparatus 4 and a manufacturing method
of press-molded article according to a fourth embodiment of the
present invention will be described with reference to FIG. 30 to
FIG. 32. It is noted that only the parts in which the fourth
embodiment differs from the above first embodiment will be
described in detail.
[0170] [Configuration of Press Molding Apparatus]
[0171] The press molding apparatus 4 comprises a first die 41, a
second die 42, a die opening prevention portion 43, a press member
48, and a driving section 48B.
[0172] The first die 41 comprises a first portion 41D to be
pressed, which is pressed by the press member 48, a first press
portion 41E for pressing the flat plate portion 10, and a first
mount portion 41F, on which the flat plate portion 10 is placed. A
first surface 41C to be pressed, formed on an upper part of the
first portion 41D to be pressed, is pressed by a first press
surface 48F. Further, the first portion 41D to be pressed is
provided at each end located at a front side and a rear side of the
drawing. A first press portion 41A, formed on a side part of the
first press portion 41E, is opposed to the first end portion 10A of
the flat plate portion 10. A first opposing surface 41B, formed on
an upper part of the first mount portion 41F, is opposed to the
first main surface 10C of the flat plate portion 10. In this
manner, the first press portion 41A and the first opposing surface
41B are provided in the same first die 41. The first opposing
surface 41B is laterally arranged along the horizontal direction,
and the first press portion 41A is connected to an end part of the
first opposing surface 41B so as to make an acute angle with the
first opposing surface 41B. Further, a thickened portion-forming
section 45 as a concave groove is formed on the first opposing
surface 41B and used for forming a thick part on the flat plate
portion 10 by allowing a part of the material of the flat plate
portion 10 to flow into the thickened portion-forming section 45
during pressing.
[0173] The second die 42, arranged above the first die 41, has a
structure approximately symmetrical to the first die 41. That is,
the second die 42 comprises a second portion 42D to be pressed,
which is pressed by the press member 48, a second press portion 42E
for pressing the flat plate portion 10, and a second opposing
portion 42F opposing to the flat plate portion 10. A second surface
42C to be pressed, formed on the second portion 42D to be pressed,
is pressed by a second press surface 48G. Further, the second
portion 42D to be pressed is provided at each end located at a
front side and a rear side of the drawing. A second press portion
42A, formed on a side part of the second press portion 42E, is
opposed to the second end portion 10B of the flat plate portion 10.
A second opposing surface 42B, formed on a lower part of the second
opposing portion 42F, is opposed to the second main surface 10D of
the flat plate portion 10. In this manner, the second press portion
42A and the second opposing surface 42B are provided in the same
second die 42. The second opposing surface 42B is laterally
arranged along the horizontal direction, and the second press
portion 42A is connected to an end part of the second opposing
surface 42B so as to make an acute angle with the second opposing
surface 42B.
[0174] The first opposing surface 41B and the second opposing
surface 42B, while facing to each other, keep in contact with the
flat plate portion 10 during pressing. Further, a plurality of
guide rollers 47 are arranged on a lower part of the second die 42,
so that the second die 42 can slide on the first die 41 in the
horizontal direction.
[0175] The die opening prevention portion 43 is a member that
prevents die opening of the first die 41 and the second die 42 and
is formed a rectangular shape enclosing the first die 41 and the
second die 42. The die opening prevention portion 43 comprises a
part positioned on an upper side of the second die 42 and a part
positioned on a lower side of the first die 41, and prevents the
die opening of the first die 41 and the second die 42 by vertically
clamping them. Further, the die opening prevention portion 43
comprises an inside upper surface 43A and an inside lower surface
43B, which are provided with a plurality of upper guide rollers 47A
and a plurality of lower guide rollers 47B, respectively. An upper
surface 41G and a lower surface 41H of the first die 41 are brought
into contact with the upper guide rollers 47A and the lower guide
rollers 47B, respectively, thereby enabling to slide the first die
41 in the horizontal direction. Further, an upper surface 42G and
the guide rollers 47 of the second die 42 are brought into contact
with the upper guide rollers 47A and the first die 41,
respectively, thereby enabling to slide the second die 42 in the
horizontal direction in a similar manner.
[0176] The press member 48 presses the first and second dies 41 and
42, thereby sliding them in the horizontal direction. The press
member 48 comprises a main body portion 48A in contact with a
driving section 48H and a press portion 48B fixed to a lower
surface of the main body portion 48A. The press portion 48B is made
from a shape in which a press portion main body 48C, fixed on the
lower surface of the main body portion 48A by the bolt B, is
connected to a first extension portion 48D and a second extension
portion 48E. The press portion 48B is formed in an upside down
U-shape in a cross sectional view. The first press surface 48F for
pressing the first die 41 is formed at a tip of the first extension
portion 48D, while the second press surface 48G for pressing the
second die 42 is formed at a tip of the second extension portion
48E. Further, both the first and second extension portions 48D and
48E are provided at each end located at a front side and a rear
side of the drawing.
[0177] The driving section 48H is arranged in contact with an upper
surface of the press member 48 (main body portion 48A). The driving
section 48H comprises, as in the above first embodiment, a
hydraulic or electric piston and moves the press member 48 downward
in the perpendicular direction by pressing.
[0178] [Manufacturing Method of Press-Molded Article]
[0179] Next, explanation is given to a manufacturing method of
press-molded article using the above press molding apparatus 4.
First of all, a member to be pressed including the flat plate
portion 10 is softened by heating to be prepared (FIG. 3: S10).
Next, the flat plate portion 10 is placed between the first die 41
and the second die 42. By this operation, as shown in FIG. 30, the
member to be pressed is placed in a manner such that the first main
surface 10C is opposed to the first opposing surface 41B and the
second main surface 10D is opposed to the second opposing surface
42B (FIG. 3: S20). During this process, the first opposing surface
41B and the second opposing surface 42B, while facing to each
other, keep in contact with the flat plate portion 10 during
pressing.
[0180] Next, the press member 48 is lowered by operating the
driving section 48H, so that the first and second press surfaces
48F and 48G are brought into contact with the first and second
surfaces 41C and 42C to be pressed, respectively (FIG. 31). When
the press member 48 is further lowered while maintaining this
state, the first press surface 48F, while sliding on the first
surface 41C to be pressed, makes the first die 41 slide in the
horizontal direction, and the second press surface 48G, while
sliding on the second surface 42C to be pressed, makes the second
die 42 slide in the horizontal direction. By this operation, the
first and second press portions 41A and 42A approach each other and
the flat plate portion 10 is pressed from the both sides of the end
portions 10A and 10B in the horizontal direction. During this
process, a part of the material of the flat plate portion 10 is
flown into the thickened portion-forming section 45 in the press
direction, thereby enabling to form a thickened portion, of which a
thickness is increased, on the flat plate portion 10 (FIG. 3:
S30).
[0181] In the press step, the first opposing surface 41B is moved
to the press direction as the flat plate portion 10 is pressed by
the first press portion 41A and the second opposing surface 42B is
moved to the press direction as the flat plate portion 10 is
pressed by the second press portion 42A. That is, both the first
and second opposing surfaces 41B and 42B are moved to the press
directions as the flat plate portion 10 is being pressed. In this
manner, both friction force generated by sliding between the first
main surface 10C and the first opposing surface 41B and friction
force generated by sliding between the second main surface 10D and
the second opposing surface 42B can be reduced. Thus, pressing
force required for molding the flat plate portion 10 can be further
reduced. Then, after the press of the flat plate portion 10 is
completed, the press member 48 is moved up by operating the driving
section 48H and a press-molded article is taken out (FIG. 3:
S40).
First Modification
[0182] Next, a first modification of the above fourth embodiment
will be described with reference to FIG. 33 to FIG. 35. As shown in
FIG. 33, in a press molding apparatus 4A according to the first
modification, the thickened portion-forming section 45 is formed on
the second opposing surface 42B, instead of the first opposing
surface 41B. In this configuration, as shown in FIG. 34 and FIG.
35, a press-molded article having a thickened portion formed on the
second main surface 10D side can be manufactured by pressing the
flat plate portion 10 with the first and second press portions 41A
and 42A and allowing the material of the flat plate portion 10 to
flow into the thickened portion-forming section 45. Further, when
the thickened portions are formed both on the first main surface
10C and the second main surface 10D, the thickened portion-forming
sections 45 may be formed both on the first opposing surface 41B
and the second opposing surface 42B.
Other Embodiments
[0183] Finally, other embodiments of the present invention will be
described. The present invention can be applied not only to a
member to be pressed, in which the whole member to be pressed is
constituted with a single flat plate portion, as described above,
but also to a member to be pressed including the flat plate portion
in one part thereof. For example, as shown in FIG. 36, the present
invention can be applied to a member 10E to be pressed of a bent
shape, having a plurality of (two) flat plate portions 10F.
[0184] More specifically, a press molding apparatus 7 comprises an
upper die 71 including first and second upper dies 71A and 71B and
a lower die 72 including first and second lower dies 72A and 72B.
The member 10E to be pressed is placed between the upper die 71 and
the lower die 72. A first press portion 71C opposing to the first
end portion 10A of the flat plate portion 10F is formed on the
first upper die 71A, and a first opposing surface 71D opposing to
the first main surface 10C of the flat plate portion 10F is formed
on the second upper die 71B. Further, a second opposing surface 72D
opposing to the second main surface 10D of the flat plate portion
10F is formed on the first lower die 72A, and a second press
portion 72C opposing to the second end portion 10B of the flat
plate portion 10F is formed on the second lower die 72B.
[0185] As shown by arrows in FIG. 36, by lowering the first upper
die 71A, the flat plate portion 10F is pressed by the first press
portion 71C and the second press portion 72C in the direction
parallel to the main surfaces 10C and 10D, and a material of the
flat plate portion 10F is flown into a thickened portion-forming
section 75 to form a thickened portion. During this process, when
the first lower die 72A is pressed by the first upper die 71A and
lowered, the second opposing surface 72D is moved to the press
direction. Thus, friction force generated by sliding between the
second main surface 10D and the second opposing surface 72D can be
reduced and, as in the cases for the above first to fourth
embodiments, pressing force required for molding the flat plate
portion 10F can be reduced.
[0186] Further, the present invention is not limited to the case
where the whole flat plate portion 10 is heated by the electric
furnace F (FIG. 4). As shown in FIG. 37, a plurality of electrodes
101 may be arranged at intervals from each other on the main
surface of the flat plate portion 10 and a temperature rising
portion 102 by heating is partially formed on the flat plate
portion 10 by supplying electric current to the plurality of
electrodes 101 (partial electrical heating). Then, as shown in FIG.
38, a thickened portion may be formed by pressing the flat plate
portion 10 in a state of being arranged between dies 91 and 92 and
allowing a material located at the temperature rising portion 102
by heating to flow into a thickened portion-forming section 95. In
this manner, remaining parts of the flat plate portion 10 other
than the temperature rising portion 102 by heating are kept at a
low temperature without being heated, thus such low-temperature
parts are not softened and retain high strength. This enables to
further reduce a friction coefficient between the dies 91 and 92,
and the flat plate portion 10 during pressing. Further, instead of
performing the partial electrical heating, the whole flat plate
portion 10 may be subjected to electrical heating.
* * * * *