U.S. patent application number 15/241193 was filed with the patent office on 2016-12-08 for two sided multi-ply tissue product.
The applicant listed for this patent is Kimberly-Clark Worldwide, Inc.. Invention is credited to Elizabeth Oriel Bradley, Geoffrey Fenn Carlow, Mike Thomas Goulet.
Application Number | 20160355986 15/241193 |
Document ID | / |
Family ID | 53681788 |
Filed Date | 2016-12-08 |
United States Patent
Application |
20160355986 |
Kind Code |
A1 |
Goulet; Mike Thomas ; et
al. |
December 8, 2016 |
TWO SIDED MULTI-PLY TISSUE PRODUCT
Abstract
The invention provides a multi-ply tissue product having
different surface characteristics on each side of the product. The
multi-ply tissue product may be formed from two or more plies where
one surface is formed by a substantially smooth creped ply and the
other surface is formed by a textured through-air dried ply. In
this manner the tissue product may be used for both personal care,
which requires a soft and smooth surface, and general household
wiping, which requires a rough, durable surface.
Inventors: |
Goulet; Mike Thomas;
(Neenah, WI) ; Bradley; Elizabeth Oriel; (Neenah,
WI) ; Carlow; Geoffrey Fenn; (Neenah, WI) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Kimberly-Clark Worldwide, Inc. |
Neenah |
WI |
US |
|
|
Family ID: |
53681788 |
Appl. No.: |
15/241193 |
Filed: |
August 19, 2016 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14401429 |
Nov 14, 2014 |
9447546 |
|
|
PCT/US2014/012856 |
Jan 24, 2014 |
|
|
|
15241193 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
D21H 27/30 20130101;
D21H 27/005 20130101; D21H 11/04 20130101; D21H 27/40 20130101 |
International
Class: |
D21H 27/00 20060101
D21H027/00; D21H 11/04 20060101 D21H011/04; D21H 27/40 20060101
D21H027/40; D21H 27/30 20060101 D21H027/30 |
Claims
1. A multi-ply tissue product comprising at least two fibrous
plies, each ply consisting essentially of hardwood kraft pulp
fibers and softwood kraft pulp fibers, the tissue product having a
top and a bottom surface and a Surface Smoothness Ratio greater
than about 1.4.
2. The multi-ply tissue product of claim 1 having a GMT from about
500 to about 1,200 g/3''.
3. The multi-ply tissue product of claim 1 having a sheet bulk from
about 8 to about 20 cc/g.
4. The multi-ply tissue product of claim 1 having a basis weight
from about 40 to about 60 gsm.
5. The multi-ply tissue product of claim 1 further comprising a
third tissue ply comprising hardwood kraft pulp fibers and softwood
kraft pulp fibers.
6. The multi-ply tissue product of claim 5 wherein the first and
the second tissue ply are substantially smooth creped tissue plies
and the third ply is a through-air dried ply.
7. The multi-ply tissue product of claim 1 wherein the Surface
Smoothness Ratio is from about 1.5 to about 2.2.
8. The multi-ply tissue product of claim 1 wherein the Surface
Smoothness Ratio is from about 1.5 to about 2.2 and the tissue
product has a sheet bulk greater than about 9 cc/g and a geometric
mean tensile (GMT) greater than about 1,000 g/3''.
9. The multi-ply tissue product of claim 1 wherein the Surface
Smoothness Ratio is from about 1.5 to about 2.2 and the tissue
product has a sheet caliper greater than about 500 .mu.m and a
geometric mean tensile (GMT) greater than about 1,000 g/3''.
10. The multi-ply tissue product of claim 1 wherein the first
surface has a Surface Smoothness of about 0.006 or less and the
second surface has a Surface Smoothness of about 0.009 or
greater.
11. The multi-ply tissue product of claim 1 wherein each ply
comprises at least about 30 percent, by weight of the ply, softwood
kraft pulp fibers.
Description
RELATED APPLICATIONS
[0001] The present application is a continuation application of
U.S. application Ser. No. 14/401429, filed on Nov. 14, 2014, which
is a national-phase entry, under 35 U.S.C. .sctn.371, of PCT Patent
Application No. PCT/US2014/012856, filed on Jan. 24, 2014, all of
which are incorporated herein by reference in a manner consistent
with the instant application.
BACKGROUND
[0002] Tissue products such as facial tissue, bath tissue, paper
towels, industrial wipers, and the like are designed to provide
several important properties. For example, the products should have
good bulk characteristics and a soft feel. The products should be
highly absorbent to fluids, including bodily fluids. In many cases,
the products need good strength even after they become wet. Some
products require a high resistance to tearing. Small changes in the
structure or manufacturing processes of such products can provide a
profound impact on the ultimate sensation to the user. Attempts
have been made in the past to enhance and increase the physical
characteristics of multi-ply tissue products.
[0003] Traditionally multi-ply tissue products employ plies that
are structurally similar and manufactured using similar papermaking
techniques. In certain instances, however, attempts have been made
to form multi-ply products from heterogeneous plies. Generally
these products are formed using a ply that while providing some
beneficial property, is not suitable for contact with the user and
therefore must be disposed in the center of a three ply product.
For example, U.S. Pat. No. 4,738,847 to Rothe et al. discloses a
multi-ply tissue product where the middle ply of a three ply
product comprises a virucidal. The virucidal containing ply is
disposed in the middle ply, away from the surface, to avoid contact
with the user's skin. Similarly, U.S. Pat. No. 7,497,923 to Ward et
al. discloses a multi-ply tissue product where the middle ply of a
three ply product comprises an uncreped through-air dried ply
disposed between two smoother creped plies. In this manner, the
uncreped ply provides bulk but does not compromise the softness of
the product because it is not brought into contact with the user in
use. While these products provide certain benefits to the user,
they lack differing surface textures, which limits their
usefulness.
[0004] In other instances, the prior art has attempted to improve
tissue product absorbency by providing a multi-ply tissue product
with an absorbent core in the center, such as provided in U.S. Pat.
No. 5,919,556 to Barnholtz. The stated goal of such tissues is
increased absorbency by providing a three ply tissue product in
which the center ply comprises a more dense, thinner ply. While
such products generally have improved absorbency, the dense, thin
middle layers compromise softness and fail to provide the user with
differing surface textures for different applications.
[0005] Thus, there remains a need in the art for a tissue product
having two different surface characteristics. More specifically
there is a need in the art for a multi-ply tissue product having a
substantially smooth first surface for contact with a user's skin
and a second textured surface for wiping and scrubbing
applications.
SUMMARY
[0006] It has now been surprisingly discovered that the most
effective and efficient means of forming a tissue product having
different surface characteristics is to combine one substantially
smooth tissue ply, such as a creped tissue ply, and one textured
tissue ply, such as a through-air dried ply. In this manner the
resulting tissue product has two surfaces with different textures
and may be used for both personal care, which requires a soft and
smooth surface, and general household wiping, which requires a
textured, durable surface.
[0007] Accordingly, in one embodiment the present invention
provides a multi-ply tissue product having a top and a bottom
surface wherein the Surface Smoothness Ratio is greater than about
1.4.
[0008] In another embodiment the present invention provides a
multi-ply tissue product having a top and a bottom surface wherein
the Surface Smoothness Ratio is greater than about 1.4 and the
tissue product has a sheet bulk greater than about 9 cc/g and a
geometric mean tensile (GMT) greater than about 1,000 g/3''.
[0009] In yet another embodiment the present invention provides a
multi-ply tissue product having a top and a bottom surface wherein
the Surface Smoothness Ratio is greater than about 1.4 and the
tissue product has a sheet caliper greater than about 500 .mu.m and
a geometric mean tensile (GMT) greater than about 1,000 g/3''.
[0010] In still another embodiment the present invention provides a
three ply tissue product having a top and a bottom surface
comprising a first creped ply, a second creped ply and a
through-air dried ply, wherein the second creped ply is disposed
between the first creped ply and the through-air dried ply and
wherein the Surface Smoothness Ratio is greater than about 1.4.
[0011] In yet another embodiment the present invention provides a
three ply tissue product comprising a first, a second and a third
ply, where the first ply forms a first surface of the tissue
product and the third ply forms a second surface of the tissue
product, wherein the first surface has a Surface Smoothness of
about 0.006 or less and the second surface has a Surface Smoothness
of about 0.009 or greater.
DESCRIPTION OF THE DRAWINGS
[0012] FIG. 1 illustrates one embodiment of the invention
comprising a three ply tissue product.
DEFINITIONS
[0013] As used herein, the term "tissue product" refers to products
made from tissue webs and includes, bath tissues, facial tissues,
paper towels, industrial wipers, foodservice wipers, napkins,
medical pads, and other similar products.
[0014] As used herein, the terms "tissue web" and "tissue sheet"
refer to a fibrous sheet material suitable for forming a tissue
product.
[0015] As used herein the term "ply" refers to a discrete product
element. Individual plies may be arranged in juxtaposition to each
other. The term may refer to a plurality of web-like components
such as in a multi-ply facial tissue, bath tissue, paper towel,
wipe, or napkin.
[0016] As used herein, the term "basis weight" generally refers to
the bone dry weight per unit area of a tissue and is generally
expressed as grams per square meter (gsm). Basis weight is measured
using TAPPI test method T-220.
[0017] As used herein, the term "geometric mean tensile" (GMT)
refers to the square root of the product of the machine direction
tensile and the cross-machine direction tensile of the web, which
are determined as described in the Test Method section.
[0018] As used herein, the term "caliper" is the representative
thickness of a single sheet (caliper of tissue products comprising
two or more plies is the thickness of a single sheet of tissue
product comprising all plies) measured in accordance with TAPPI
test method T402 using an EMVECO 200-A Microgage automated
micrometer (EMVECO, Inc., Newberg, Oreg.). The micrometer has an
anvil diameter of 2.22 inches (56.4 mm) and an anvil pressure of
132 grams per square inch (per 6.45 square centimeters) (2.0
kPa).
[0019] As used herein, the term "sheet bulk" refers to the quotient
of the caliper (.mu.m) divided by the bone dry basis weight (gsm).
The resulting sheet bulk is expressed in cubic centimeters per gram
(cc/g).
[0020] As used herein, the term "slope" refers to slope of the line
resulting from plotting tensile versus stretch and is an output of
the MTS TestWorks.TM. in the course of determining tensile strength
as described in the Test Methods section. Slope is reported in the
units of kilograms (kg) per unit of sample width (inches) and is
measured as the gradient of the least-squares line fitted to the
load-corrected strain points falling between a specimen-generated
force of 70 to 157 grams (0.687 to 1.540 N) divided by the specimen
width. Slopes are generally reported herein as having units of
kg/3''.
[0021] As used herein, the term "geometric mean slope" (GM Slope)
generally refers to the square root of the product of machine
direction slope and cross-machine direction slope. GM Slope
generally is expressed in units of kg/3'' or g/3''.
[0022] As used herein, the term "Stiffness Index" refers to the
quotient of the geometric mean slope (having units of g/3'')
divided by the geometric mean tensile strength (having units of
g/3'').
[0023] As used herein, the term "Surface Smoothness" refers to
square root of the product of machine direction mean deviation of
MIU (MMD) and cross direction MMD, measured as described in the
Test Methods section below.
[0024] As used herein, the term "Surface Smoothness Ratio" refers
to Surface Smoothness of the second surface of a tissue product,
the tissue surface having the highest Surface Smoothness of the two
tissue surfaces, divided by the Surface Smoothness of the first
surface of the tissue product, the tissue surface having the lowest
Surface Smoothness of the two tissue surfaces.
DETAILED DESCRIPTION
[0025] The two sided multi-ply tissue product of the present
invention comprises at least two plies having different surface
characteristics such as one ply that is substantially smooth and
another ply that is textured. In a particularly preferred
embodiment the two sided multi-ply tissue product of the present
invention comprises a substantially smooth ply, such as a creped
tissue ply, forming a first surface of the tissue product and a
textured tissue ply, such as a through-air dried ply, forming the
second surface of the tissue product. In this manner the first
surface of the tissue product has a Surface Smoothness of about
0.006 or less and the second surface of the tissue product has a
Surface Smoothness of about 0.009 or greater. The dual texture
provides a tissue product that may be used in several different
applications.
[0026] In one particularly preferred embodiment the two sided
tissue product of the present invention comprises at least three
plies, where one of the plies is a through-air dried ply and at
least one ply is a creped ply, where the through-air dried ply
forms one of the outer surfaces of the product and the creped ply
forms the other.
[0027] Referring now to FIG. 1, one embodiment of a tissue product
10 comprising a first 20, second 30 and third 40 ply is
illustrated. The second ply 30 is disposed between the first 20 and
third 40 plies. The first ply 20 has a top surface which forms the
first surface 12 of the tissue product 10. The second outer ply 40
has a bottom surface which forms the second surface 14 of the
tissue product.
[0028] In the illustrated embodiment the first outer ply 20
comprises a tissue ply that is substantially smooth. Generally,
when a tissue ply is referred to herein as being substantially
smooth, the tissue ply has at least one surface having a Surface
Smoothness less than about 0.006 and more preferably less than
about 0.0055. In a preferred embodiment the first outer ply is a
creped tissue ply. The second ply 30 also comprises a tissue ply
that is substantially smooth and in a preferred embodiment is also
a creped tissue ply and is substantially similar to the first ply
20. Unlike the first 20 and second 30 plies, the third ply 40 is a
textured tissue ply. In a particularly preferred embodiment the
third ply 40 is a through-air dried tissue ply and in a
particularly preferred embodiment an uncreped through-air dried
tissue ply.
[0029] Constructing a multi-ply tissue product in this manner
provides a tissue that has two different surface characteristics as
well as good bulk, tensile strength and low stiffness. The
combination of these properties is not found in the prior art, as
summarized below.
TABLE-US-00001 TABLE 1 Surface Sheet GM No. Smoothness Bulk GMT
Slope Stiffness Tissue Product Plies Ratio (cc/g) (g/3'') (kg/3'')
Index U.S. Pat. No. 7,497,923 Prior Art 3 1.05 10.5 1024 13.84
13.52 U.S. Pat. No. 6,649,025 Prior Art 2 1.33 8.1 992 12.23 12.33
Quilted Northern Ultra Soft & Strong 2 1.01 11.6 884 6.87 7.76
Charmin Ultra Strong Bath Tissue 2 1.14 13.8 1161 9.66 8.32
Inventive 3 1.96 9.0 1063 14.98 14.09 Inventive 3 1.90 10.1 1080
13.84 12.82 Inventive 3 1.45 8.8 1261 13.55 10.75 Inventive 3 1.51
9.7 980 13.09 13.36
[0030] The instant multi-ply tissue product may be constructed from
two or more plies that are manufactured using the same or different
tissue making techniques. In a particularly preferred embodiment
the multi-ply tissue product comprises three plies where the first
and second plies are manufactured by the same tissue manufacturing
process, such as creped wet pressed, and the third ply is
manufactured using a different process, such as creped through-air
dried (CTAD) or uncreped through-air dried (UCTAD).
[0031] In a particularly preferred embodiment the tissue product
comprises one or more substantially smooth tissue plies, which may
be produced using one of the creped tissue making processes known
in the art. For example, creped tissue webs may be formed using
either a wet pressed or modified wet pressed process such as those
disclosed in U.S. Pat. Nos. 3,953,638, 5,324,575 and 6,080,279, the
disclosures of which are incorporated herein in a manner consistent
with the instant application. In these processes the embryonic
tissue web is transferred to a Yankee dryer, which completes the
drying process, and then creped from the Yankee surface using a
doctor blade or other suitable device.
[0032] In addition to a substantially smooth ply the tissue product
comprises a textured tissue ply. The textured tissue ply may be a
creped through-air dried (CTAD) tissue; uncreped through-air dried
(UCTAD) tissue; a textured tissue, made using a process including
the step of using pressure, vacuum, or air flow through the wet web
(or a combination of these) to conform the wet web into a shaped
fabric and subsequently drying the shaped sheet using a Yankee
dryer, or series of steam heated dryers, or some other means,
including but not limited to tissue made using the ATMOS process
developed by Voith or the NTT process developed by Metso; or fabric
creped tissue, made using a process including the step of
transferring the wet web from a carrying surface (belt, fabric,
felt, or roll) moving at one speed to a fabric moving at a slower
speed (at least 5% slower) and subsequently drying the sheet. Those
skilled in the art will recognize that these processes are not
mutually exclusive, e.g., an uncreped TAD process may include a
fabric crepe step in the process.
[0033] Particularly preferred textured tissue plies are formed by
through-air dried process known in the art. In such processes the
embryonic web is noncompressive dried. For example, textured tissue
plies may be formed by either creped or uncreped through-air dried
processes. Particularly preferred are uncreped through-air dried
webs, such as those described in U.S. Pat. No. 5,779,860, the
contents of which are incorporated herein in a manner consistent
with the present disclosure.
[0034] Suitable textured tissue webs may also include embossed,
microembossed, and microstrained tissue webs. Suitable techniques
for embossing tissues are well known in the art such as those
disclosed in U.S. Pat. Nos. 5,409,572 and 5,693,406, the contents
of which are incorporated herein in a manner consistent with the
present disclosure.
[0035] Regardless of the tissue making process used to produce the
individual plies, the resulting multi-ply tissue product has a
first surface that is substantially smooth and a second surface
that is textured such that the Surface Smoothness Ratio is greater
than about 1.4, such as from about 1.4 to about 2.2, and more
preferably from about 1.6 to about 2.0.
[0036] When forming the multi-ply tissue products of the present
invention substantially smooth plies, such as the first ply,
generally have a basis weight less than about 40 gsm, such as from
about 10 to about 30 gsm, and more preferably from about 14 to
about 20 gsm. Further, the first outer ply and middle ply generally
have a sheet bulk greater than about 5 cc/g, such as from about 5
to about 15 cc/g, and more preferably from about 7 to about 10
cc/g.
[0037] In addition to having the foregoing basis weights and sheet
bulks, the substantially smooth plies have a geometric mean tensile
(GMT) greater than about 500 g/3'', such as from about 500 to about
1,000 g/3'', and more preferably from about 600 to about 800 g/3''.
At these tensile strengths the substantially smooth plies have
relatively low geometric mean modulus, expressed as GM Slope, so as
to not overly stiffen the tissue product. Accordingly, in certain
embodiments the substantially smooth plies have GM Slope less than
about 18 kg/3'', such as from about 10 to about 18 kg/3'', and more
preferably from about 12 to about 15 kg/3''.
[0038] The textured tissue ply generally has a basis weight less
than about 60 gsm, such as from about 20 to about 60 gsm, and more
preferably from about 30 to about 50 gsm. The textured tissue ply
generally has a sheet bulk greater than about 8 cc/g, such as from
about 8 to about 20 cc/g, and more preferably from about 10 to
about 18 cc/g.
[0039] In addition to having the foregoing basis weights and sheet
bulks, the textured tissue ply generally has a GMT greater than
about 500 g/3'', such as from about 500 to about 1,200 g/3'', and
more preferably from about 700 to about 1,000 g/3''. At these
tensile strengths the textured tissue ply generally has a GM Slope
less than about 12 kg/3'', such as from about 6 to about 12 kg/3'',
and more preferably from about 8 to about 10 kg/3''.
[0040] Generally the foregoing individual plies are joined together
using any ply attachment means known in the art, such as mechanical
crimping, adhesive, or embossing. Crimping is particularly
preferred ply attachment means as it avoids the over stiffening of
the tissue product often associated with adhesive ply attachment
and does not impart any additional texture to the product as is
often the case with embossing.
[0041] When plies having differing texture are joined together the
resulting multi-ply tissue product generally has a basis weight
greater than about 40 gsm, such as from about 40 to about 80 gsm,
and more preferably from about 50 to about 60 gsm. At these basis
weights the tissue products generally have calipers greater than
about 400 .mu.m, such as from about 400 to about 600 .mu.m, and
more preferably from about 450 to about 550 .mu.m. The tissue
products further have sheet bulks greater than about 7.0 cc/g, such
as from about 8.0 to about 20.0 cc/g, and more preferably from
about 10.0 to about 18.0 cc/g.
[0042] While being bulky and substantive enough to have multiple
applications the tissue products are also strong enough to
withstand use, but have relatively low modulus so as not to be
overly stiff. For example, in certain embodiments the tissue
products have GMT greater than about 800 g/3'', such as from about
800 to about 1200 g/3'', and more preferably from about 900 to
about 1100 g/3''. At these tensile strengths the tissue products
generally have GM Slopes less than about 15.0 kg/3'', such as from
about 10.0 to about 15.0 kg/3'', and more preferably from about
12.0 to about 14.0 kg/3''.
[0043] As noted previously, regardless of the tissue making process
used to form the various plies, it is preferred that the composite
multi-ply tissue product have a first surface that is substantially
smooth and second surface that is textured. For example, in certain
embodiments the first surface has a Surface Smoothness less than
about 0.0070, such as from about 0.0050 to about 0.0070, and more
preferably from about 0.0055 to about 0.0065. Meanwhile the second
surface has a Surface Smoothness greater than about 0.0075, such as
from about 0.0075 to about 0.0120, and more preferably from about
0.0080 to about 0.0110. In this manner the tissue product of the
present invention has a Surface Smoothness Ratio greater than about
1.4, such as from about 1.4 to about 2.0, and more preferably from
about 1.5 to about 1.8. Thus, compared to multi-ply tissue products
of the prior art the instant two sided tissue products have
markedly different surface properties on the first and the second
sides, as illustrated in Table 2, below.
TABLE-US-00002 TABLE 2 First Second Surface No. Surface Surface
Smoothness Tissue Product Plies Smoothness Smoothness Ratio U.S.
Pat. No. 7,497,923 3 0.0066 0.0069 1.05 Prior Art U.S. Pat. No.
6,649,025 2 0.0067 0.0089 1.33 Prior Art Bounty Towels 2 0.0191
0.0203 1.06 Bounty Extra Soft Towels 2 0.0093 0.0114 1.23 Charmin
Ultra Strong 2 0.0098 0.0112 1.14 Bath Tissue Quilted Northern 2
0.0090 0.0091 1.01 Ultra Soft & Strong Inventive 3 0.0062
0.0118 1.90 Inventive 3 0.0058 0.0099 1.71 Inventive 3 0.0059
0.0115 1.95
TEST METHODS
Surface Smoothness
[0044] The surface properties of samples were measured on KES
Surface Tester (Model KE-SE, Kato Tech Co., Ltd., Kyoto, Japan).
For each sample the surface smoothness was measured according to
the Kawabata Test Procedures with samples tested along MD and CD
and on both sides for five repeats with a sample size of 10
cm.times.10 cm. Care was taken to avoid folding, wrinkling,
stressing, or otherwise handling the samples in a way that would
deform the sample. Samples were tested using a multi-wire probe of
10 mm.times.10 mm consisting of 20 piano wires of 0.5 mm in
diameter each with a contact force of 25 grams. The test speed was
set at 1 mm/s. The sensor was set at "H" and FRIC was set at "DT".
The data was acquired using KES-FB System Measurement Program
KES-FB System Ver 7.09 E for Win98/2000/XP by Kato Tech Co., Ltd.,
Kyoto, Japan. The selection in the program was "KES-SE Friction
Measurement".
[0045] KES Surface Tester determined the coefficient of friction
(MIU) and mean deviation of MIU (MMD), where higher values of MIU
indicate more drag on the sample surface and higher values of MMD
indicate more variation or less uniformity on the sample
surface.
[0046] The values MIU and MMD are defined by:
MIU(.mu.)=1/X.intg..sub.0.sup.x.mu.dx
MMD=1/X.intg..sub.0.sup.x|.mu.-.mu.|dx
where [0047] .mu.=friction force divided by compression force
[0048] .mu.=mean value of .mu. [0049] x=displacement of the probe
on the surface of specimen, cm [0050] X=maximum travel used in the
calculation, 2 cm
[0051] The cross machine (CD) and machine direction (MD) MMD values
of the top and bottom surface of each tissue product sample was
tested five times. The results of five sample measurements were
averaged and reported as the MMD-CD and MMD-MD. The square root of
the product of MMD-CD and MMD-MD was reported as Surface
Smoothness.
Tensile
[0052] Samples for tensile strength testing are prepared by cutting
a 3'' (76.2 mm).times.5'' (127 mm) long strip in either the machine
direction (MD) or cross-machine direction (CD) orientation using a
JDC Precision Sample Cutter (Thwing-Albert Instrument Company,
Philadelphia, Pa., Model No. JDC 3-10, Ser. No. 37333). The
instrument used for measuring tensile strengths is an MTS Systems
Sintech 11S, Serial No. 6233. The data acquisition software is MTS
TestWorks.TM. for Windows Ver. 4 (MTS Systems Corp., Research
Triangle Park, N.C.). The load cell is selected from either a 50 or
100 Newton maximum, depending on the strength of the sample being
tested, such that the majority of peak load values fall between 10
and 90 percent of the load cell's full scale value. The gauge
length between jaws is 4.+-.0.04 inches. The jaws are operated
using pneumatic-action and are rubber coated. The minimum grip face
width is 3'' (76.2 mm), and the approximate height of a jaw is 0.5
inches (12.7 mm). The crosshead speed is 10.+-.0.4 inches/min
(254.+-.1 mm/min), and the break sensitivity is set at 65 percent.
The sample is placed in the jaws of the instrument, centered both
vertically and horizontally. The test is then started and ends when
the specimen breaks. The peak load is recorded as either the "MD
tensile strength" or the "CD tensile strength" of the specimen
depending on the sample being tested. At least six representative
specimens are tested for each product, taken "as is," and the
arithmetic average of all individual specimen tests is either the
MD or CD tensile strength for the product.
EXAMPLES
[0053] Two and three ply tissue products were made from various
tissue webs, prepared as described below. The tissue products were
formed by plying various webs together, calendering and crimping
the plied products. Both inventive and prior art tissue products
were produced to assess surface smoothness and physical properties.
Prior art tissue products consisted of two-ply tissue products (one
ply CTEC and one ply UCTAD) prepared as described in U.S. Pat. No.
6,649,025 and three-ply tissue products (one ply UCTAD disposed
between two plies CTEC) as described in U.S. Pat. No.
7,497,923.
Creped Tissue Webs
[0054] Creped tissue webs were made using a conventional wet
pressed tissue-making process on a pilot scale tissue machine.
Initially, northern softwood kraft (NSWK) pulp was dispersed in a
pulper for 30 minutes at about 4 percent consistency at about
100.degree. F. The NSWK pulp was then transferred to a dump chest
and subsequently diluted with water to approximately 2 percent
consistency. Softwood fibers were then pumped to a machine chest.
Generally the softwood fibers were added to the middle layer in the
3-layer tissue structure.
[0055] Eucalyptus hardwood kraft (EHWK) pulp was dispersed in a
pulper for 30 minutes at about 4 percent consistency at about
100.degree. F. The EHWK pulp was then transferred to a dump chest
and diluted to about 2 percent consistency. The EHWK pulp was then
pumped to a machine chest. Generally the EHWK fibers were added to
the dryer and felt layers of the 3-layer sheet structure.
[0056] The pulp fibers from the machine chests were pumped to the
headbox at a consistency of about 0.1 percent. Pulp fibers from
each machine chest were sent through separate manifolds in the
headbox to create a 3-layered tissue structure having a furnish
split of 44 wt % EHWK/32 wt % NBSK/24 wt % EHWK. The fibers were
deposited onto a felt using a Crescent Former.
[0057] The wet sheet, about 10 to 20 percent consistency, was
adhered to a Yankee dryer via a pressure roll. The consistency of
the wet sheet after the pressure roll nip (post-pressure roll
consistency or PPRC) was approximately 40 percent. The wet sheet is
adhered to the Yankee dryer due to the additive composition that is
applied to the dryer surface. A spray boom situated underneath the
Yankee dryer sprayed the creping composition, described in the
present disclosure, onto the dryer surface at addition levels of
about 10 mg/m.sup.2. The creping composition comprised 71 percent
Crepetrol A9915 and 29 percent Rezosol 6601 (both available from
Ashland, Inc., Wilmington Del.).
Uncreped Through-Air Dried Webs
[0058] Tissue webs for use on the outer ply of a multi-ply tissue
product were produced using a through-air dried papermaking process
commonly referred to as "uncreped through-air dried" ("UCTAD") and
generally described in U.S. Pat. No. 5,607,551, the contents of
which are incorporated herein in a manner consistent with the
present disclosure. Base sheets with a target bone dry basis weight
of about 44 grams per square meter (gsm) were produced. The base
sheets were then converted and spirally wound into rolled tissue
products.
[0059] In all cases the base sheets were produced from a furnish
comprising northern softwood kraft and eucalyptus kraft using a
layered headbox fed by three stock chests such that the webs having
three layers (two outer layers and a middle layer) were formed. The
two outer layers comprised eucalyptus and the middle layer
comprised softwood. The 3-layered tissue structure had a furnish
split of 33 wt % EHWK/34 wt % NBSK/33 wt % EHWK.
[0060] The tissue web was formed on a Voith Fabrics TissueForm V
forming fabric, vacuum dewatered to approximately 25 percent
consistency and then subjected to rush transfer (approximately 35
percent) when transferred to the transfer fabric. The transfer
fabric was the fabric described as "Fred" in U.S. Pat. No.
7,611,607 (commercially available from Voith Fabrics, Appleton,
Wis.).
[0061] The web was then transferred to a through-air drying fabric.
The through-air drying fabric was T-605-1 (commercially available
from Voith Fabrics, Appleton, Wis.); T-1205-2 described previously
in U.S. Pat. No. 8,500,955; or a silicone printed fabric described
previously in co-pending PCT Appl. No. US2013/072220 (referred to
herein as "Fozzie"). Transfer to the through-drying fabric was done
using vacuum levels of greater than 10 inches of mercury at the
transfer. The web was then dried to approximately 98 percent solids
before winding.
Creped Through-Air Dried Webs
[0062] For tissue webs produced by CTAD, the web was formed on a
TissueForm V forming fabric, transferred to a Voith 2164 fabric and
vacuum dewatered to roughly 25 percent consistency. The web was
then transferred to a t-807-1 TAD fabric (illustrated in FIG. 2,
Voith Fabrics, Appleton, Wis.). No rush transfer was utilized at
the transfer to the t-807-1 TAD fabric. After the web was
transferred to the t-807-1 TAD fabric, the web was dried, however
the consistency was maintained low enough to allow significant
molding when the web was transferred using high vacuum to the
impression fabric described as "Fred" in U.S. Pat. No. 7,611,607,
which is incorporated herein in a manner consistent with the
present disclosure. A vacuum level of at least 10 inches of mercury
was used for the transfer to the impression fabric in order to mold
the web as much as possible into the fabric. The web was then
transferred to a Yankee dryer and creped. Minimum pressure was used
at the web transfer to minimize compaction of the web during the
transfer to the Yankee dryer so as to maintain maximum web
caliper.
[0063] An adhesive formulation of polyvinyl alcohol, PAE resin and
non-oil based release agent was used for creping. The adhesive
composition and add on rates were typical for standard creped
throughdried tissue. The sheet was dried to a very high level (less
than about 2 percent moisture) on the Yankee dryer to maximize bulk
in the creping process. High web tension between the Yankee and the
reel was maintained to prevent sheet wrinkling.
Multi-ply Tissue Products
[0064] Various two and three ply tissue products were prepared from
the tissue webs prepared as described above. The composition of the
various tissue products is summarized in Table 3, below. To produce
the multi-ply tissue products, tissue web soft rolls were rewound,
calendared between two steel rolls and plied together. Mechanical
crimping on the edges of the structure held the plies together. The
plied sheet was then slit on the edges to a standard width of
approximately 8.5 inches, folded, and cut to facial tissue length.
Tissue samples were conditioned and tested. The results of the
testing are summarized in Tables 4 and 5, below.
TABLE-US-00003 TABLE 3 UCTAD CTAD CTEC Tissue Product UCTAD BW BW
BW Calender Sample Plies Structure Fabric (gsm) (gsm) (gsm) (ph) 1
3 CTEC/UCTAD/CTEC T-605-1 30.0 -- 14.2 135 2 2 CTEC/UCTAD T-605-1
45.0 -- 14.2 135 3 3 CTEC/CTEC/UCTAD T1205-2 30.0 -- 14.2 135 4 3
CTEC/CTEC/UCTAD T1205-2 22.0 -- 14.5 135 5 3 CTEC/CTEC/UCTAD
T-605-1 45.0 -- 17.5 170 6 3 CTEC/CTEC/TAD -- -- 29.4 14.2 135 7 3
CTEC/CTEC/UCTAD Fozzie 30.0 -- 14.2 40
TABLE-US-00004 TABLE 4 Sheet GM BW Caliper Bulk GMT Slope Stiffness
Sample (gsm) (.mu.m) (cc/g) (g/3'') (kg/3'') Index 1 52.3 551 10.5
1024 13.84 13.52 2 55.4 447 8.1 992 12.23 12.33 3 53.7 467 8.1 1058
14.79 13.98 4 46.6 448 9.0 1063 14.98 14.09 5 53.2 538 10.1 1080
13.84 12.82 6 52.6 461 8.8 1261 13.55 10.75 7 50.5 488 9.7 980
13.09 13.36
TABLE-US-00005 TABLE 5 Top Bottom Surface Surface Surface
Smoothness Sample Smoothness Smoothness Ratio 1 0.0066 0.0069 1.05
2 0.0067 0.0089 1.33 3 0.0058 0.0099 1.69 4 0.0059 0.0115 1.96 5
0.0062 0.0118 1.90 6 0.0058 0.0084 1.45 7 0.0061 0.0091 1.51
* * * * *