U.S. patent application number 14/977938 was filed with the patent office on 2016-06-09 for three-dimensional objects produced from materials having multiple mechanisms of hardening.
The applicant listed for this patent is Carbon3D, Inc.. Invention is credited to Kai Chen, Joseph M. DeSimone, James Goodrich, Robert Pinschmidt, Justin Poelma, Lloyd M. Robeson, Jason P. Rolland.
Application Number | 20160160077 14/977938 |
Document ID | / |
Family ID | 54938697 |
Filed Date | 2016-06-09 |
United States Patent
Application |
20160160077 |
Kind Code |
A1 |
Rolland; Jason P. ; et
al. |
June 9, 2016 |
THREE-DIMENSIONAL OBJECTS PRODUCED FROM MATERIALS HAVING MULTIPLE
MECHANISMS OF HARDENING
Abstract
A three dimensional object includes (a) a light polymerized
first component; and (b) a second solidified component different
from the first component. The object is preferably of a polymer
blend formed from the first component and the second component,
with the polymer blend as an interpenetrating polymer network, a
semi-interpenetrating polymer network, or a sequential
interpenetrating polymer network. In some preferred embodiments,
the second component does not contain a cationic polymerization
photoinitiator. In some preferred embodiments, the three
dimensional object is produced by the process of continuous liquid
interface production.
Inventors: |
Rolland; Jason P.; (San
Carlos, CA) ; Chen; Kai; (Sunnyvale, CA) ;
Poelma; Justin; (Goleta, CA) ; Goodrich; James;
(Phoenix, AZ) ; Pinschmidt; Robert; (Carrboro,
NC) ; DeSimone; Joseph M.; (Los Gatos, CA) ;
Robeson; Lloyd M.; (Macungie, PA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Carbon3D, Inc. |
Redwood City |
CA |
US |
|
|
Family ID: |
54938697 |
Appl. No.: |
14/977938 |
Filed: |
December 22, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
PCT/US2015/036924 |
Jun 22, 2015 |
|
|
|
14977938 |
|
|
|
|
62133642 |
Mar 16, 2015 |
|
|
|
62129187 |
Mar 6, 2015 |
|
|
|
62111961 |
Feb 4, 2015 |
|
|
|
62101671 |
Jan 9, 2015 |
|
|
|
62036161 |
Aug 12, 2014 |
|
|
|
62015780 |
Jun 23, 2014 |
|
|
|
Current U.S.
Class: |
428/36.9 ;
264/401; 428/36.92; 521/134; 525/123; 525/124 |
Current CPC
Class: |
B29C 2033/0005 20130101;
C08G 18/4825 20130101; C08K 5/0008 20130101; C08L 75/04 20130101;
B29C 64/106 20170801; B29C 71/0009 20130101; B33Y 10/00 20141201;
C08G 18/8175 20130101; C09D 175/04 20130101; B29D 11/00663
20130101; G03F 7/027 20130101; B29K 2105/043 20130101; B29K 2105/16
20130101; C08G 18/42 20130101; B33Y 50/02 20141201; C08F 283/006
20130101; B29C 35/0805 20130101; C08K 3/01 20180101; C08K 3/013
20180101; G03F 7/00 20130101; G03F 7/38 20130101; B29L 2011/0075
20130101; C08G 18/40 20130101; B33Y 30/00 20141201; B29C 64/129
20170801; C08G 18/4854 20130101; G03F 7/0757 20130101; B29C 64/386
20170801; C08G 18/81 20130101; C08G 18/244 20130101; C09D 175/08
20130101; B29C 64/135 20170801; B29K 2995/0026 20130101; B29K
2105/0002 20130101; C08G 18/755 20130101; B29C 64/165 20170801;
C09D 135/02 20130101; B29K 2075/02 20130101; C08J 5/00 20130101;
B29C 2035/0855 20130101; C08G 18/7671 20130101; G03F 7/0037
20130101; B29L 2011/0016 20130101; C08L 75/14 20130101; B29D
11/00009 20130101; C08G 18/10 20130101; B29L 2011/00 20130101; B29C
64/124 20170801; B29L 2031/001 20130101; B33Y 80/00 20141201; G03F
7/038 20130101; B29K 2075/00 20130101; B29C 64/255 20170801; B29K
2509/00 20130101; B33Y 70/00 20141201; C08F 290/067 20130101; C08J
2375/14 20130101; B29C 64/40 20170801; B29C 71/02 20130101; C08G
18/73 20130101; C08K 5/0041 20130101; B29K 2105/0058 20130101; C08G
18/758 20130101; C08F 220/34 20130101; B29C 2035/0827 20130101;
B29L 2031/10 20130101; C08G 18/69 20130101; C08F 283/006 20130101;
C08F 222/102 20200201; C08F 222/1063 20200201; C08F 290/067
20130101; C08F 222/102 20200201; C08F 222/1063 20200201; C08F
220/1808 20200201; C08F 290/067 20130101; C08F 222/102 20200201;
C08F 220/1811 20200201; C08G 18/672 20130101; C08G 18/48 20130101;
C08F 290/067 20130101; C08G 18/672 20130101; C08F 222/102 20200201;
C08G 18/48 20130101; C08F 222/1063 20200201; C08F 283/006 20130101;
C08F 222/102 20200201; C08F 222/1063 20200201 |
International
Class: |
C09D 175/08 20060101
C09D175/08; C09D 135/02 20060101 C09D135/02; B29C 67/00 20060101
B29C067/00; C09D 175/04 20060101 C09D175/04 |
Claims
1. A three dimensional object comprised of: (a) a light polymerized
first component; and (b) a second solidified component different
from said first component; said object comprising a polymer blend
formed from said first component and said second component, with
said polymer blend comprising an interpenetrating polymer network,
a semi-interpenetrating polymer network, or a sequential
interpenetrating polymer network; subject to the proviso that: (i)
said second component does not contain a cationic polymerization
photoinitiator, and/or (ii) said three dimensional object is
produced by the process of continuous liquid interface
production.
2. The object of claim 1, wherein said second component is
solidified (or further reacted, polymerized, or chain extended) on
contacting to heat, water, water vapor, light at a different
wavelength than that at which said first component is polymerized,
catalysts, evaporation of a solvent from the polymerizable liquid,
exposure to microwave irradiation, or combinations thereof.
3. The object of claim 1, wherein: (i) said first component
comprises the polymerization product of monomers and/or prepolymers
polymerized by exposure to actinic radiation or light, said
monomers and/or prepolymers comprising reactive end groups selected
from the group consisting of acrylates, methacrylates,
.alpha.-olefins, N-vinyls, acrylamides, methacrylamides, styrenics,
epoxides, thiols, 1,3-dienes, vinyl halides, acrylonitriles, vinyl
esters, maleimides, and vinyl ethers.
4. The object of claim 3, wherein: (ii) said second component
comprises the solidified product of the polymerization of monomers
and/or prepolymers comprising reactive end groups, said reactive
end groups selected from the group consisting of: epoxy/amine,
epoxy/hydroxyl, oxetane/amine, oxetane/alcohol,
isocyanate/hydroxyl, isocyanate/amine, isocyanate/carboxylic acid,
cyanate ester, anhydride/amine, amine/carboxylic acid, amine/ester,
hydroxyl/carboxylic acid, hydroxyl/acid chloride, amine/acid
chloride, vinyl/Si--H, Si--Cl/hydroxyl, Si--Cl/amine,
hydroxyl/aldehyde, amine/aldehyde, hydroxymethyl or alkoxymethyl
amide/alcohol, aminoplast, alkyne/azide, click chemistry reactive
groups, alkene/sulfur, alkene/thiol, alkyne/thiol, hydroxyl/halide,
isocyanate/water, Si--OH/hydroxyl, Si--OH/water, Si--OH/Si--H,
Si--OH/Si--OH, perfluorovinyl, diene/dienophiles, olefin metathesis
polymerization groups, olefin polymerization groups for
Ziegler-Natta catalysis, and ring-opening polymerization groups,
and mixtures thereof.
5. The object of claim 1, wherein said second solidified component
comprises a thermoset polymer.
6. The object of claim 5, wherein said second solidified component
comprises a polyurethane, polyurea, or copolymer thereof.
7. The object of claim 1, wherein said second solidified component
comprises a thermoplastic polymer.
8. The object of claim 7, wherein said second solidified component
comprises a polyurethane, polyurea, or copolymer thereof.
9. The object of claim 1, further comprising: (a) a third
solidified component different from said first and second
component, with said object having at least a first structural
segment and a second structural segment covalently coupled to one
another, said first structural segment comprised of said second
solidified component, said second structural segment comprised of
said third solidified component; and both said first and second
structural segments comprised of the same or different light
polymerized first component.
10. The object of claim 1, subject to the proviso that: (i) said
second component does not contain a cationic polymerization
photoinitiator.
11. The object of claim 1, subject to the proviso that: (ii) said
three dimensional object is produced by the process of continuous
liquid interface production.
12. The object of claim 1, wherein said object comprises a sol-gel
composition, a hydrophobic-hydrophilic polymer network, a phenolic
resin, a polyimide, a conductive polymer, a natural product polymer
network, a polyolefin, or a combination thereof.
13. The object of claim 1, wherein said object further comprises
reacted photoinitator fragments, and/or unreacted
photoinitiator.
14. The object of claim 1, wherein said object is rigid, is
comprised of polyurethane, polyurea, or copolymer thereof, has a
Young's modulus of 800 to 3500 megapascals, has a tensile strength
of 30 to 100 megapascals, and has a percent elongation at break of
from 1 to 100.
15. The object of claim 14, wherein said object is a fastener, an
electronic device housing, a gear, propeller, or impeller, a wheel,
a mechanical device housing, or a tool.
16. The object of claim 1, wherein said object is rigid and
flexible, is comprised of polyurethane, polyurea, or copolymer
thereof, has a Young's modulus of 300 to 2500 megapascals, has a
tensile strength of from 20 to 70 megapascals, and has a percent
elongation at break of from 40 to 300 or 600.
17. The object of claim 16, wherein said object is a structural
element, a hinge, a boat or watercraft hull or deck, a wheel, a
bottle, jar or other container, a pipe, a liquid tube, or a
connector.
18. The object of claim 1, wherein said object is elastomeric, is
comprised of polyurethane, polyurea, or copolymer thereof, has a
Young's modulus of 0.5 to 40 megapascals, has a tensile strength of
from 0.5 to 30 megapascals, and has a percent elongation at break
of from 50 to 1000.
19. The object of claim 18, wherein said object is a foot-ware
sole, heel, innersole or midsole; a bushing or gasket; a cushion,
or an electronic device housing.
20. The object of claim 1, produced by the process comprising: (a)
providing a carrier and an optically transparent member having a
build surface, said carrier and said build surface defining a build
region therebetween; (b) filling said build region with a
polymerizable liquid, said polymerizable liquid comprising a
mixture of (i) a light polymerizable liquid first component, and
(ii) a second solidifiable component different from said first
component; (c) irradiating said build region with light through
said optically transparent member to form a solid polymer scaffold
from said first component and also advancing said carrier away from
said build surface to form a three-dimensional intermediate having
the same shape as, or a shape to be imparted to, said
three-dimensional object and containing said second solidifiable
component carried in said scaffold in unsolidified and/or uncured
form; and (d) concurrently with or subsequent to said irradiating
step, solidifying and/or curing said second solidifiable component
in said three-dimensional intermediate to form said
three-dimensional object.
21. The object of claim 20, wherein said irradiating and/or said
advancing steps are carried out while also concurrently: (i)
continuously maintaining a dead zone of polymerizable liquid in
contact with said build surface, and (ii) continuously maintaining
a gradient of polymerization zone between said dead zone and said
solid polymer and in contact with each thereof, said gradient of
polymerization zone comprising said first component in partially
cured form.
22. The object of claim 1, wherein said object has a shape that
cannot be formed by injection molding or casting.
23. The object of claim 1, wherein said object comprises: (i)
enclosed cavities, partially open cavities, repeating unit cells,
open cell foams, closed cell foams, or combinations thereof; (ii) a
waveguide, prism, lens, or combination thereof; and/or (iii) a
wall, strut, beam, tie, or combination thereof.
Description
RELATED APPLICATIONS
[0001] This application is a continuation-in-part under 35 U.S.C.
111(a) of PCT Application PCT/US2015/036924 (Attorney Docket No.
1151-16CWO), filed Jun. 22, 2015, which in turn claims the benefit
of U.S. Provisional Patent Application Ser. Nos. 62/133,642 filed
Mar. 16, 2015, 62/129,187 filed Mar. 6, 2015, 62/111,961 filed Feb.
4, 2015, 62/101,671 filed Jan. 9, 2015, 62/036,161 filed Aug. 12,
2014, and 62/015,780 filed Jun. 23, 2014, the disclosure of each
which is incorporated by reference herein in its entirety.
FIELD OF THE INVENTION
[0002] The present invention concerns materials, methods and
apparatus for the fabrication of solid three-dimensional objects
from liquid materials, and objects so produced.
BACKGROUND OF THE INVENTION
[0003] In conventional additive or three-dimensional fabrication
techniques, construction of a three-dimensional object is performed
in a step-wise or layer-by-layer manner. In particular, layer
formation is performed through solidification of photo curable
resin under the action of visible or UV light irradiation. Two
techniques are known: one in which new layers are formed at the top
surface of the growing object; the other in which new layers are
formed at the bottom surface of the growing object.
[0004] If new layers are formed at the top surface of the growing
object, then after each irradiation step the object under
construction is lowered into the resin "pool," a new layer of resin
is coated on top, and a new irradiation step takes place. An early
example of such a technique is given in Hull, U.S. Pat. No.
5,236,637, at FIG. 3. A disadvantage of such "top down" techniques
is the need to submerge the growing object in a (potentially deep)
pool of liquid resin and reconstitute a precise overlayer of liquid
resin.
[0005] If new layers are formed at the bottom of the growing
object, then after each irradiation step the object under
construction must be separated from the bottom plate in the
fabrication well. An early example of such a technique is given in
Hull, U.S. Pat. No. 5,236,637, at FIG. 4. While such "bottom up"
techniques hold the potential to eliminate the need for a deep well
in which the object is submerged by instead lifting the object out
of a relatively shallow well or pool, a problem with such "bottom
up" fabrication techniques, as commercially implemented, is that
extreme care must be taken, and additional mechanical elements
employed, when separating the solidified layer from the bottom
plate due to physical and chemical interactions therebetween. For
example, in U.S. Pat. No. 7,438,846, an elastic separation layer is
used to achieve "non-destructive" separation of solidified material
at the bottom construction plane. Other approaches, such as the
B9Creator.TM. 3-dimensional printer marketed by B9Creations of
Deadwood, S. Dak., USA, employ a sliding build plate. See, e.g., M.
Joyce, US Patent App. 2013/0292862 and Y. Chen et al., US Patent
App. 2013/0295212 (both Nov. 7, 2013); see also Y. Pan et al., J.
Manufacturing Sci. and Eng. 134, 051011-1 (October 2012). Such
approaches introduce a mechanical step that may complicate the
apparatus, slow the method, and/or potentially distort the end
product.
[0006] Continuous processes for producing a three-dimensional
object are suggested at some length with respect to "top down"
techniques in U.S. Pat. No. 7,892,474, but this reference does not
explain how they may be implemented in "bottom up" systems in a
manner non-destructive to the article being produced, which limits
the materials which can be used in the process, and in turn limits
the structural properties of the objects so produced.
[0007] Southwell, Xu et al., US Patent Application Publication No.
2012/0251841, describe liquid radiation curable resins for additive
fabrication, but these comprise a cationic photoinitiator (and
hence are limited in the materials which may be used) and are
suggested only for layer by layer fabrication.
[0008] Velankar, Pazos, and Cooper, Journal of Applied Polymer
Science 162, 1361 (1996), describe UV-curable urethane acrylates
formed by a deblocking chemistry, but they are not suggested for
additive manufacturing, and no suggestion is made on how those
materials may be adapted to additive manufacturing.
[0009] Accordingly, there is a need for new materials and methods
for producing three-dimensional objects by additive manufacturing
that have satisfactory structural properties.
SUMMARY OF THE INVENTION
[0010] Described herein are methods, systems and apparatus
(including associated control methods, systems and apparatus), for
the production of a three-dimensional object by additive
manufacturing. In preferred (but not necessarily limiting)
embodiments, the method is carried out continuously. In preferred
(but not necessarily limiting) embodiments, the three-dimensional
object is produced from a liquid interface. Hence they are
sometimes referred to, for convenience and not for purposes of
limitation, as "continuous liquid interface production,"
"continuous liquid interphase printing," or the like (i.e.,
"CLIP"). A schematic representation of an embodiment thereof is
given in FIG. 1 herein.
[0011] The present invention provides a method of forming a
three-dimensional object, comprising: (a) (i) providing a carrier
and an optically transparent member having a build surface, the
carrier and the build surface defining a build region therebetween,
or (ii) providing a carrier in a polymerizable liquid reservoir,
the reservoir having a fill level, the carrier and the fill level
defining a build region therebetween; (b) filling the build region
with a polymerizable liquid, the polymerizable liquid comprising a
mixture of: (i) a light polymerizable liquid first component, and
(ii) a second solidifiable (or second reactive) component different
from the first component; (c) irradiating the build region with
light (through the optically transparent member when present) to
form a solid polymer scaffold from the first component and
advancing (e.g., advancing concurrently--that is, simultaneously,
or sequentially in an alternating fashion with irradiating steps)
the carrier away from the build surface to form a three-dimensional
intermediate having the same shape as, or a shape to be imparted
to, the three-dimensional object and containing the second
solidifiable component carried in the scaffold in unsolidified or
uncured form; and (d) concurrently with or subsequent to the
irradiating step, solidifying and/or curing (e.g., further
reacting, polymerizing, or chain extending) the second solidifiable
or reactive component in the three-dimensional intermediate to form
the three-dimensional object.
[0012] Optionally, a wash step may be included between formation of
the three-dimensional intermediate and the subsequent solidifying
and/or curing step (d) which by which the three-dimensional object
is formed. Any suitable wash liquid may be employed (e.g.,
BIO-SOLV.TM. solvent replacement; PURPLE POWER.TM.
degreaser/cleaner; SIMPLE GREEN.RTM. all purpose cleaner; a 50:50
volume:volume mixture of water and isopropanol, etc. See also, U.S.
Pat. No. 5,248,456).
[0013] In some embodiments, the second component comprises: (i) a
polymerizable liquid solubilized in or suspended in the first
component; (ii) a polymerizable solid solubilized in the first
component; or (iii) a polymer solubilized in the first component.
In other embodiments, the second component comprises: (i) a
polymerizable solid suspended in the first component; or (ii) solid
thermoplastic or thermoset polymer particles suspended in the first
component.
[0014] In some embodiments, the first component comprises a blocked
or reactive blocked prepolymer and (optionally but in some
embodiments preferably) a reactive diluent, and the second
component comprises a chain extender. The first components react
together to form a blocked polymer scaffold during the irradiating
step, which is unblocked by heating or microwave irradiating during
the second step to in turn react with the chain extender. In some
embodiments, the reactive blocked component comprises a reactive
blocked diisocyanate and/or chain extender, alone or in combination
with a reactive blocked prepolymer, and other unblocked
constituents (e.g., polyisocyanate oligomer, diisocyanate, reactive
diluents, and/or chain extender).
[0015] In some embodiments, reactive blocked prepolymers,
diisocyanates, and/or chain extenders are blocked by reaction of
(i.e., are the reaction product of a reaction between) a
polyisocyanate oligomer, a diisocyanate, and/or a chain extender
with an amine(meth)acrylate, alcohol(meth)acrylate, maleimide, or
n-vinylformamide monomer blocking agent.
[0016] In some embodiments, the three-dimensional intermediate is
collapsible or compressible (e.g., elastic).
[0017] In some embodiments, the scaffold is continuous; in other
embodiments, the scaffold is discontinuous (e.g., an open or closed
cell foam, which foam may be regular (e.g., geometric, such as a
lattice) or irregular).
[0018] In some embodiments, the three-dimensional object comprises
a polymer blend (e.g., an interpenetrating polymer network, a
semi-interpenetrating polymer network, a sequential
interpenetrating polymer network) formed from the first component
and the second component.
[0019] In some embodiments, the polymerizable liquid comprises from
1, 2 or 5 percent by weight to 20, 30, 40, 90 or 99 percent by
weight of the first component; and from 1, 10, 60, 70 or 80 percent
by weight to 95, 98 or 99 percent by weight of the second component
(optionally including one or more additional components). In other
embodiments, the polymerizable liquid comprises from 1, 2 or 5
percent by weight to 20, 30, 40, 90 or 99 percent by weight of the
second component; and from 1, 10, 60, 70 or 80 percent by weight to
95, 98 or 99 percent by weight of the first component (optionally
including one or more additional components).
[0020] In some embodiments, the solidifying and/or curing step (d)
is carried out concurrently with the irradiating step (c) and: (i)
the solidifying and/or curing step is carried out by precipitation;
(ii) the irradiating step generates heat from the polymerization of
the first component in an amount sufficient to thermally solidify
or polymerize the second component (e.g., to a temperature of 50 or
80 to 100.degree. C., for polymerizing polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)); and (iii) the second
component (e.g., a light or ultraviolet light curable epoxy resin)
is solidified by the same light as is the first component in the
irradiating step.
[0021] In some embodiments, the solidifying and/or curing step (d)
is carried out subsequent to the irradiating step (c) and is
carried out by: (i) heating or microwave irradiating the second
solidifiable component; (ii) irradiating the second solidifiable
component with light at a wavelength different from that of the
light in the irradiating step (c); (iii) contacting the second
polymerizable component to water; or (iv) contacting the second
polymerizable component to a catalyst.
[0022] In some embodiments, the second component comprises
precursors to a polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), a silicone resin, or natural rubber, and the
solidifying and/or curing step is carried out by heating or
microwave irradiating.
[0023] In some embodiments, the second component comprises a
cationically cured resin (e.g., an epoxy resin or a vinyl ether)
and the solidifying and/or curing step is carried out by
irradiating the second solidifiable component with light at a
wavelength different from that of the light in the irradiating step
(c).
[0024] In some embodiments, the second component comprises a
precursor to a polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), and the solidifying and/or curing step is
carried out by contacting the second component to water (e.g., in
liquid, gas, or aerosol form). Suitable examples of such precursors
include, but are not limited to, those described in B. Baumbach,
Silane Terminated Polyurethanes (Bayer MaterialScience 2013).
[0025] In some embodiments, the second component comprises a
precursor to a polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), a silicone resin, a ring-opening metathesis
polymerization resin, or a click chemistry resin (alkyne monomers
in combination with compound plus an azide monomers), and the
solidifying and/or curing step is carried out by contacting the
second component to a polymerization catalyst (e.g., a metal
catalyst such as a tin catalyst, and/or an amine catalyst, for
polyurethane/polyurea resins; platinum or tin catalysts for
silicone resins; ruthenium catalysts for ring-opening metathesis
polymerization resins; copper catalyst for click chemistry resins;
etc., which catalyst is contacted to the article as a liquid
aerosol, by immersion, etc.), or an aminoplast containing resin,
such as one containing N-(alkoxymethyl)acrylamide, hydroxyl groups,
and a blocked acid catalyst.
[0026] In some embodiments, the irradiating step and/or advancing
step is carried out while also concurrently:
[0027] (i) continuously maintaining a dead zone (or persistent or
stable liquid interface) of polymerizable liquid in contact with
the build surface, and
[0028] (ii) continuously maintaining a gradient of polymerization
zone (e.g., an active surface) between the dead zone and the solid
polymer and in contact with each thereof, the gradient of
polymerization zone comprising the first component in partially
cured form.
[0029] In some embodiments, the first component comprises a free
radical polymerizable liquid and the inhibitor comprises oxygen; or
the first component comprises an acid-catalyzed or cationically
polymerizable liquid, and the inhibitor comprises a base.
[0030] In some embodiments, the gradient of polymerization zone and
the dead zone together have a thickness of from 1 to 1000
microns.
[0031] In some embodiments, the gradient of polymerization zone is
maintained for a time of at least 5, 10, 20 or 30 seconds, or at
least 1 or 2 minutes.
[0032] In some embodiments, the advancing is carried out at a
cumulative rate of at least 0.1, 1, 10, 100 or 1000 microns per
second.
[0033] In some embodiments, the build surface is substantially
fixed or stationary in the lateral and/or vertical dimensions.
[0034] In some embodiments the method further comprises vertically
reciprocating the carrier with respect to the build surface to
enhance or speed the refilling of the build region with the
polymerizable liquid.
[0035] A further aspect of the invention is a polymerizable liquid
substantially as described herein above and below, and/or for use
in carrying out a method as described herein.
[0036] In some embodiments of the methods and compositions
described above and below, the polymerizable liquid (or "dual cure
resin") has a viscosity of 100, 200, 500 or 1,000 centipoise or
more at room temperature and/or under the operating conditions of
the method, up to a viscosity of 10,000, 20,000, or 50,000
centipoise or more, at room temperature and/or under the operating
conditions of the method.
[0037] One particular embodiment of the inventions disclosed herein
is a method of forming a three-dimensional object comprised of
polyurethane, polyurea, or copolymer thereof, the method
comprising: (a) providing a carrier and an optically transparent
member having a build surface, the carrier and the build surface
defining a build region therebetween; (b) filling the build region
with a polymerizable liquid, the polymerizable liquid comprising at
least one of: (i) a blocked or reactive blocked prepolymer, (ii) a
blocked or reactive blocked diisocyanate, or (iii) a blocked or
reactive blocked diisocyanate chain extender; (c) irradiating the
build region with light through the optically transparent member to
form a solid blocked polymer scaffold and advancing the carrier
away from the build surface to form a three-dimensional
intermediate having the same shape as, or a shape to be imparted
to, the three-dimensional object, with the intermediate containing
the chain extender; and then (d) heating or microwave irradiating
the three-dimensional intermediate sufficiently to form from the
three-dimensional intermediate the three-dimensional object
comprised of polyurethane, polyurea, or copolymer thereof.
[0038] In some embodiments, the solidifiable or polymerizable
liquid is changed at least once during the method with a subsequent
solidifiable or polymerizable liquid; optionally where the
subsequent solidifiable or polymerizable liquid is cross-reactive
with each previous solidifiable or polymerizable liquid during the
subsequent curing, to form an object having a plurality of
structural segments covalently coupled to one another, each
structural segment having different structural (e.g., tensile)
properties.
[0039] A further aspect of the inventions disclosed herein is a
polymerizable liquid useful for the production of a
three-dimensional object comprised of polyurethane, polyurea, or a
copolymer thereof by additive manufacturing, the polymerizable
liquid comprising a mixture of: [0040] (a) at least one
constitutent selected from the group consisting of (i) a blocked or
reactive blocked prepolymer, (ii) a blocked or reactive blocked
diisocyanate, and (iii) a blocked or reactive blocked diisocyanate
chain extender, [0041] (b) optionally at least one additional chain
extender, [0042] (c) a photoinitiator, [0043] (d) optionally a
polyol and/or a polyamine, [0044] (e) optionally a reactive
diluent, [0045] (f) optionally a non-reactive (i.e., non-reaction
initiating) light absorbing, particularly a ultraviolet
light-absorbing, pigment or dye which when present is included in
an amount of from 0.001 or 0.01 to 10 percent by weight, and [0046]
(g) optionally a filler (e.g. silica, a toughener such as a
core-shell rubber, etc., including combinations thereof.); [0047]
optionally, but in some embodiments preferably, subject to the
proviso that the non-reactive light absorbing pigment or dye is
present when the at least one constituent is only the blocked or
reactive blocked prepolymer.
[0048] In some embodiments, polymerizable liquids used in the
present invention include a non-reactive pigment or dye. Examples
include, but are not limited to, (i) titanium dioxide (e.g., in an
amount of from 0.05 or 0.1 to 1 or 5 percent by weight), (ii)
carbon black (e.g., included in an amount of from 0.05 or 0.1 to 1
or 5 percent by weight), and/or (iii) an organic ultraviolet light
absorber such as a hydroxybenzophenone, hydroxyphenylbenzotriazole,
oxanilide, benzophenone, thioxanthone, hydroxyphenyltriazine,
and/or benzotriazole ultraviolet light absorber (e.g. in an amount
of 0.001 or 0.005 to 1, 2 or 4 percent by weight).
[0049] In some embodiments, a Lewis acid or an oxidizable tin salt
is included in the polymerizable liquid (e.g., in an amount of from
0.01 or 0.1 to 1 or 2 percent by weight, or more) in an amount
effective to accelerate the formation of the three-dimensional
intermediate object during the production thereof.
[0050] A further aspect of the inventions disclosed herein is a
three dimensional object comprised of: (a) a light polymerized
first component; and (b) a second solidified component (e.g., a
further reacted, polymerized or chain extended component) different
from the first component; optionally but in some embodiments
preferably subject to the proviso that: (i) the second component
does not contain a cationic polymerization photoinitiator, and/or
(ii) the three dimensional object is produced by the process of
continuous liquid interface production.
[0051] In some embodiments, the object further comprises: (c) a
third solidified (or further reacted, polymerized, or chain
extended) component different from the first and second component,
with the object having at least a first structural segment and a
second structural segment covalently coupled to one another, the
first structural segment comprised of the second solidified
component, the second structural segment comprised of the third
solidified component; and both the first and second structural
segments comprised of the same or different light polymerized first
component.
[0052] In some embodiments, the object comprises a polymer blend
formed from the first component and the second component.
[0053] The object may be one that has a shape that cannot be formed
by injection molding or casting.
[0054] Non-limiting examples and specific embodiments of the
present invention are explained in greater detail in the drawings
herein and the specification set forth below. The disclosures of
all United States Patent references cited herein are to be
incorporated herein by reference in their entirety.
BRIEF DESCRIPTION OF THE DRAWINGS
[0055] FIG. 1 is a schematic illustration of one embodiment of a
method of the present invention.
[0056] FIG. 2 is a perspective view of one embodiment of an
apparatus of the present invention.
[0057] FIG. 3 is a first flow chart illustrating control systems
and methods for carrying out the present invention.
[0058] FIG. 4 is a second flow chart illustrating control systems
and methods for carrying out the present invention.
[0059] FIG. 5 is a third flow chart illustrating control systems
and methods for carrying out the present invention.
[0060] FIG. 6 is a top view of a 3 inch by 16 inch "high aspect"
rectangular build plate (or "window") assembly of the present
invention, where the film dimensions are 3.5 inch by 17 inch.
[0061] FIG. 7 is an exploded view of the build plate of FIG. 6,
showing the tension ring and tension ring spring plate.
[0062] FIG. 8 is a side sectional view of the build plates of FIGS.
6-9, showing how the tension member tensions and rigidifies the
polymer film.
[0063] FIG. 9 is a top view of a 2.88 inch diameter round build
plate of the invention, where the film dimension may be 4 inches in
diameter.
[0064] FIG. 10 is an exploded view of the build plate of FIG.
8.
[0065] FIG. 11 shows various alternate embodiments of the build
plates of FIGS. 7-10.
[0066] FIG. 12 is a front perspective view of an apparatus
according to an exemplary embodiment of the invention.
[0067] FIG. 13 is a side view of the apparatus of FIG. 12.
[0068] FIG. 14 is a rear perspective view of the apparatus of FIG.
12.
[0069] FIG. 15 is a perspective view of a light engine assembly
used with the apparatus of FIG. 12.
[0070] FIG. 16 is a front perspective view of an apparatus
according to another exemplary embodiment of the invention.
[0071] FIG. 17A is a schematic diagram illustrating tiled
images.
[0072] FIG. 17B is a second schematic diagram illustrating tiled
images.
[0073] FIG. 17C is a third schematic diagram illustrating tiled
images.
[0074] FIG. 18 is a front perspective view of an apparatus
according to another exemplary embodiment of the invention.
[0075] FIG. 19 is a side view of the apparatus of FIG. 18.
[0076] FIG. 20 is a perspective view of a light engine assembly
used with the apparatus of FIG. 18.
[0077] FIG. 21 is a graphic illustration of a process of the
invention indicating the position of the carrier in relation to the
build surface or plate, where both advancing of the carrier and
irradiation of the build region is carried out continuously.
Advancing of the carrier is illustrated on the vertical axis, and
time is illustrated on the horizontal axis.
[0078] FIG. 22 is a graphic illustration of another process of the
invention indicating the position of the carrier in relation to the
build surface or plate, where both advancing of the carrier and
irradiation of the build region is carried out stepwise, yet the
dead zone and gradient of polymerization are maintained. Advancing
of the carrier is again illustrated on the vertical axis, and time
is illustrated on the horizontal axis.
[0079] FIG. 23 is a graphic illustration of still another process
of the invention indicating the position of the carrier in relation
to the build surface or plate, where both advancing of the carrier
and irradiation of the build region is carried out stepwise, the
dead zone and gradient of polymerization are maintained, and a
reciprocating step is introduced between irradiation steps to
enhance the flow of polymerizable liquid into the build region.
Advancing of the carrier is again illustrated on the vertical axis,
and time is illustrated on the horizontal axis.
[0080] FIG. 24 is a detailed illustration of an reciprocation step
of FIG. 23, showing a period of acceleration occurring during the
upstroke (i.e., a gradual start of the upstroke) and a period of
deceleration occurring during the downstroke (i.e., a gradual end
to the downstroke).
[0081] FIG. 25A depicts a dual cure system employing a thermally
cleavable end group. I. Crosslinked blocked diisocyanate prepolymer
containing unreacted chain extender. II. Polymer blend of: i)
linear ethylenically unsaturated blocking monomer copolymerized
with reactive diluent and ii) linear thermoplastic
polyurethane.
[0082] FIG. 25B depicts a method of the present invention carried
out with (meth)acrylate blocked diisocyanates (ABDIs). I.
Crosslinked blocked diisocyanate containing unreacted soft segment
and chain extender. II. Polymer blend of: i) linear ethylenically
unsaturated blocking monomer copolymerized with reactive diluent
and ii) linear thermoplastic polyurethane.
[0083] FIG. 25C depicts a method of the present invention carried
out with (meth)acrylate blocked chain extenders (ABCEs). I.
Crosslinked blocked diisocyanate containing chain extender
containing unreacted soft segment and chain extender. II. Polymer
blend of: i) linear ethylenically unsaturated blocking monomer
copolymerized with reactive diluent and ii) linear thermoplastic
polyurethane.
DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS
[0084] The present invention is now described more fully
hereinafter with reference to the accompanying drawings, in which
embodiments of the invention are shown. This invention may,
however, be embodied in many different forms and should not be
construed as limited to the embodiments set forth herein; rather
these embodiments are provided so that this disclosure will be
thorough and complete and will fully convey the scope of the
invention to those skilled in the art.
[0085] Like numbers refer to like elements throughout. In the
figures, the thickness of certain lines, layers, components,
elements or features may be exaggerated for clarity. Where used,
broken lines illustrate optional features or operations unless
specified otherwise.
[0086] The terminology used herein is for the purpose of describing
particular embodiments only and is not intended to be limiting of
the invention. As used herein, the singular forms "a," "an" and
"the" are intended to include plural forms as well, unless the
context clearly indicates otherwise. It will be further understood
that the terms "comprises" or "comprising," when used in this
specification, specify the presence of stated features, integers,
steps, operations, elements components and/or groups or
combinations thereof, but do not preclude the presence or addition
of one or more other features, integers, steps, operations,
elements, components and/or groups or combinations thereof.
[0087] As used herein, the term "and/or" includes any and all
possible combinations or one or more of the associated listed
items, as well as the lack of combinations when interpreted in the
alternative ("or").
[0088] Unless otherwise defined, all terms (including technical and
scientific terms) used herein have the same meaning as commonly
understood by one of ordinary skill in the art to which this
invention belongs. It will be further understood that terms, such
as those defined in commonly used dictionaries, should be
interpreted as having a meaning that is consistent with their
meaning in the context of the specification and claims and should
not be interpreted in an idealized or overly formal sense unless
expressly so defined herein. Well-known functions or constructions
may not be described in detail for brevity and/or clarity.
[0089] It will be understood that when an element is referred to as
being "on," "attached" to, "connected" to, "coupled" with,
"contacting," etc., another element, it can be directly on,
attached to, connected to, coupled with and/or contacting the other
element or intervening elements can also be present. In contrast,
when an element is referred to as being, for example, "directly
on," "directly attached" to, "directly connected" to, "directly
coupled" with or "directly contacting" another element, there are
no intervening elements present. It will also be appreciated by
those of skill in the art that references to a structure or feature
that is disposed "adjacent" another feature can have portions that
overlap or underlie the adjacent feature.
[0090] Spatially relative terms, such as "under," "below," "lower,"
"over," "upper" and the like, may be used herein for ease of
description to describe an element's or feature's relationship to
another element(s) or feature(s) as illustrated in the figures. It
will be understood that the spatially relative terms are intended
to encompass different orientations of the device in use or
operation in addition to the orientation depicted in the figures.
For example, if the device in the figures is inverted, elements
described as "under" or "beneath" other elements or features would
then be oriented "over" the other elements or features. Thus the
exemplary term "under" can encompass both an orientation of over
and under. The device may otherwise be oriented (rotated 90 degrees
or at other orientations) and the spatially relative descriptors
used herein interpreted accordingly. Similarly, the terms
"upwardly," "downwardly," "vertical," "horizontal" and the like are
used herein for the purpose of explanation only, unless
specifically indicated otherwise.
[0091] It will be understood that, although the terms first,
second, etc., may be used herein to describe various elements,
components, regions, layers and/or sections, these elements,
components, regions, layers and/or sections should not be limited
by these terms. Rather, these terms are only used to distinguish
one element, component, region, layer and/or section, from another
element, component, region, layer and/or section. Thus, a first
element, component, region, layer or section discussed herein could
be termed a second element, component, region, layer or section
without departing from the teachings of the present invention. The
sequence of operations (or steps) is not limited to the order
presented in the claims or figures unless specifically indicated
otherwise.
[0092] "Shape to be imparted to" refers to the case where the shape
of the intermediate object slightly changes between formation
thereof and forming the subsequent three-dimensional product,
typically by shrinkage (e.g., up to 1, 2 or 4 percent by volume),
expansion (e.g., up to 1, 2 or 4 percent by volume), removal of
support structures, or by intervening forming steps (e.g.,
intentional bending, stretching, drilling, grinding, cutting,
polishing, or other intentional forming after formation of the
intermediate product, but before formation of the subsequent
three-dimensional product). As noted above, the three dimensional
intermediate may also be washed, if desired, before further curing,
and/or before, during, or after any intervening forming steps.
[0093] "Hydrocarbyl" as used herein refers to a bifunctional
hydrocarbon group, which hydrocarbon may be aliphatic, aromatic, or
mixed aliphatic and aromatic, and optionally containing one or more
(e.g. 1, 2, 3, or 4) heteroatoms (typically selected from N, O, and
S). Such hydrocarbyl groups may be optionally substituted and may
contain from 1, 2, or 3 carbon atoms, up to 6, 8 or 10 carbon atoms
or more, and up to 40, 80, or 100 carbon atoms or more.
[0094] Heating may be active heating (e.g., in an oven, such as an
electric, gas, or solar oven), or passive heating (e.g., at ambient
temperature). Active heating will generally be more rapid than
passive heating and in some embodiments is preferred, but passive
heating--such as simply maintaining the intermediate at ambient
temperature for a sufficient time to effect further cure--is in
some embodiments preferred.
[0095] "Diisocyanate" and "polyisocyanate" are used interchangeably
herein and refer to aliphatic, cycloaliphatic, and aromatic
isocyanates that have at least 2, or in some embodiments more than
2, isocyanate (NCO) groups per molecule, on average. In some
embodiments, the isocyanates have, on average, 3 to 6, 8 or 10 or
more isocyanate groups per molecule. In some embodiments, the
isocyanates may be a hyperbranched or dendrimeric isocyanate (e.g.,
containing more than 10 isocyanate groups per molecule, on
average). Common examples of suitable isocyanates include, but are
not limited to, methylene diphenyl diisocyanate (MDI), toluene
diisocyanate (TDI)), para-phenyl diisocyanate (PPDI),
4,4'-dicyclohexylmethane-diisocyanate (HMDI), hexamethylene
diisocyanate (HDI), isophorone diisocyanate (IPDI),
triphenylmethane-4,4'4''-triisocyanate, toluene-2,4,6-triyl
triisocyanate, 1,3,5-triazine-2,4,6-triisocyanate, ethyl ester
L-lysine triisocyanate, etc., including combinations thereof.
Numerous additional examples are known and are described in, for
example, U.S. Pat. Nos. 9,200,108; 8,378,053; 7,144,955; 4,075,151,
3,932,342, and in US Patent Application Publication Nos. US
20040067318 and US 20140371406, the disclosures of all of which are
incorporated by reference herein in their entirety.
[0096] Oxidizable tin salts useful for carrying out the present
invention include, but are not limited to, stannous butanoate,
stannous octoate, stannous hexanoate, stannous heptanoate, stannous
linoleate, stannous phenyl butanoate, stannous phenyl stearate,
stannous phenyl oleate, stannous nonanoate, stannous decanoate,
stannous undecanoate, stannous dodecanoate, stannous stearate,
stannous oleate stannous undecenoate, stannous 2-ethylhexoate,
dibutyl tin dilaurate, dibutyl tin dioleate, dibutyl tin
distearate, dipropyl tin dilaurate, dipropyl tin dioleate, dipropyl
tin distearate, dibutyl tin dihexanoate, and combinations thereof.
See also U.S. Pat. Nos. 5,298,532; 4,421,822; and 4,389,514, the
disclosures of which are incorporated herein by reference. In
addition to the foregoing oxidizable tin salts, Lewis acids such as
those described in Chu et al. in Macromolecular Symposia, Volume
95, Issue 1, pages 233-242, June 1995 are known to enhance the
polymerization rates of free-radical polymerizations and are
included herein by reference.
[0097] Any suitable filler may be used in connection with the
present invention, depending on the properties desired in the part
or object to be made. Thus, fillers may be solid or liquid, organic
or inorganic, and may include reactive and non-reactive rubbers:
siloxanes, acrylonitrile-butadiene rubbers; reactive and
non-reactive thermoplastics (including but not limited to:
poly(ether imides), maleimide-styrene terpolymers, polyarylates,
polysulfones and polyethersulfones, etc.) inorganic fillers such as
silicates (such as talc, clays, silica, mica), glass, carbon
nanotubes, graphene, cellulose nanocrystals, etc., including
combinations of all of the foregoing. Suitable fillers include
tougheners, such as core-shell rubbers, as discussed below.
[0098] Tougheners.
[0099] One or more polymeric and/or inorganic tougheners can be
used as a filler in the present invention. See generally US Patent
Application Publication No. 20150215430. The toughener may be
uniformly distributed in the form of particles in the cured
product. The particles could be less than 5 microns (um) in
diameter. Such tougheners include, but are not limited to, those
formed from elastomers, branched polymers, hyperbranched polymers,
dendrimers, rubbery polymers, rubbery copolymers, block copolymers,
core-shell particles, oxides or inorganic materials such as clay,
polyhedral oligomeric silsesquioxanes (POSS), carbonaceous
materials (e.g., carbon black, carbon nanotubes, carbon nanofibers,
fullerenes), ceramics and silicon carbides, with or without surface
modification or functionalization. Examples of block copolymers
include the copolymers whose composition is described in U.S. Pat.
No. 6,894,113 (Court et al., Atofina, 2005) and include
"NANOSTRENTH.RTM..TM." SBM
(polystyrene-polybutadiene-polymethacrylate), and AMA
(polymethacrylate-polybutylacrylate-polymethacrylate), both
produced by Arkema. Other suitable block copolymers include
FORTEGRA.RTM..TM. and the amphiphilic block copolymers described in
U.S. Pat. No. 7,820,760B2, assigned to Dow Chemical. Examples of
known core-shell particles include the core-shell (dendrimer)
particles whose compositions are described in US20100280151A1
(Nguyen et al., Toray Industries, Inc., 2010) for an amine branched
polymer as a shell grafted to a core polymer polymerized from
polymerizable monomers containing unsaturated carbon-carbon bonds,
core-shell rubber particles whose compositions are described in EP
1632533A1 and EP 2123711A1 by Kaneka Corporation, and the "KaneAce
MX" product line of such particle/epoxy blends whose particles have
a polymeric core polymerized from polymerizable monomers such as
butadiene, styrene, other unsaturated carbon-carbon bond monomer,
or their combinations, and a polymeric shell compatible with the
epoxy, typically polymethylmethacrylate, polyglycidylmethacrylate,
polyacrylonitrile or similar polymers, as discussed further below.
Also suitable as block copolymers in the present invention are the
"JSR SX" series of carboxylated polystyrene/polydivinylbenzenes
produced by JSR Corporation; "Kureha Paraloid" EXL-2655 (produced
by Kureha Chemical Industry Co., Ltd.), which is a butadiene alkyl
methacrylate styrene copolymer; "Stafiloid" AC-3355 and TR-2122
(both produced by Takeda Chemical Industries, Ltd.), each of which
are acrylate methacrylate copolymers; and "PARALOID" EXL-2611 and
EXL-3387 (both produced by Rohm & Haas), each of which are
butyl acrylate methyl methacrylate copolymers. Examples of suitable
oxide particles include NANOPDX.RTM..TM. produced by nanoresins AG.
This is a master blend of functionalized nanosilica particles and
an epoxy.
[0100] Core-Shell Rubbers.
[0101] Core-shell rubbers are particulate materials (particles)
having a rubbery core. Such materials are known and described in,
for example, US Patent Application Publication No. 20150184039, as
well as US Patent Application Publication No. 20150240113, and U.S.
Pat. Nos. 6,861,475, 7,625,977, 7,642,316, 8,088,245, and
elsewhere.
[0102] In some embodiments, the core-shell rubber particles are
nanoparticles (i.e., having an average particle size of less than
1000 nanometers (nm)). Generally, the average particle size of the
core-shell rubber nanoparticles is less than 500 nm, e.g., less
than 300 nm, less than 200 nm, less than 100 nm, or even less than
50 nm. Typically, such particles are spherical, so the particle
size is the diameter; however, if the particles are not spherical,
the particle size is defined as the longest dimension of the
particle.
[0103] In some embodiments, the rubbery core can have a Tg of less
than -25.degree. C., more preferably less than -50.degree. C., and
even more preferably less than -70.degree. C. The Tg of the rubbery
core may be well below -100.degree. C. The core-shell rubber also
has at least one shell portion that preferably has a Tg of at least
50.degree. C. By "core," it is meant an internal portion of the
core-shell rubber. The core may form the center of the core-shell
particle, or an internal shell or domain of the core-shell rubber.
A shell is a portion of the core-shell rubber that is exterior to
the rubbery core. The shell portion (or portions) typically forms
the outermost portion of the core-shell rubber particle. The shell
material can be grafted onto the core or is cross-linked. The
rubbery core may constitute from 50 to 95%, or from 60 to 90%, of
the weight of the core-shell rubber particle.
[0104] The core of the core-shell rubber may be a polymer or
copolymer of a conjugated diene such as butadiene, or a lower alkyl
acrylate such as n-butyl-, ethyl-, isobutyl- or
2-ethylhexylacrylate. The core polymer may in addition contain up
to 20% by weight of other copolymerized mono-unsaturated monomers
such as styrene, vinyl acetate, vinyl chloride, methyl
methacrylate, and the like. The core polymer is optionally
cross-linked. The core polymer optionally contains up to 5% of a
copolymerized graft-linking monomer having two or more sites of
unsaturation of unequal reactivity, such as diallyl maleate,
monoallyl fumarate, allyl methacrylate, and the like, at least one
of the reactive sites being non-conjugated.
[0105] The core polymer may also be a silicone rubber. These
materials often have glass transition temperatures below
-100.degree. C. Core-shell rubbers having a silicone rubber core
include those commercially available from Wacker Chemie, Munich,
Germany, under the trade name Genioperl.
[0106] The shell polymer, which is optionally chemically grafted or
cross-linked to the rubber core, can be polymerized from at least
one lower alkyl methacrylate such as methyl methacrylate, ethyl
methacrylate or t-butyl methacrylate. Homopolymers of such
methacrylate monomers can be used. Further, up to 40% by weight of
the shell polymer can be formed from other monovinylidene monomers
such as styrene, vinyl acetate, vinyl chloride, methyl acrylate,
ethyl acrylate, butyl acrylate, and the like. The molecular weight
of the grafted shell polymer can be between 20,000 and 500,000.
[0107] One suitable type of core-shell rubber has reactive groups
in the shell polymer which can react with an epoxy resin or an
epoxy resin hardener. Glycidyl groups are suitable. These can be
provided by monomers such as glycidyl methacrylate.
[0108] One example of a suitable core-shell rubber is of the type
described in US Patent Application Publication No. 2007/0027233 (EP
1 632 533 A1). Core-shell rubber particles as described therein
include a cross-linked rubber core, in most cases being a
cross-linked copolymer of butadiene, and a shell which is
preferably a copolymer of styrene, methyl methacrylate, glycidyl
methacrylate and optionally acrylonitrile. The core-shell rubber is
preferably dispersed in a polymer or an epoxy resin, also as
described in the document.
[0109] Suitable core-shell rubbers include, but are not limited to,
those sold by Kaneka Corporation under the designation Kaneka Kane
Ace, including the Kaneka Kane Ace 15 and 120 series of products,
including Kanaka Kance Ace MX 120, Kaneka Kane Ace MX 153, Kaneka
Kane Ace MX 154, Kaneka Kane Ace MX 156, Kaneka Kane Ace MX170, and
Kaneka Kane Ace MX 257 and Kaneka Kane Ace MX 120 core-shell rubber
dispersions, and mixtures thereof.
I. Polymerizable Liquids: Part A.
[0110] Dual cure systems as described herein may include a first
curable system (sometimes referred to as "Part A" or herein) that
is curable by actinic radiation, typically light, and in some
embodiments ultraviolet (UV) light). Any suitable polymerizable
liquid can be used as the first component. The liquid (sometimes
also referred to as "liquid resin" "ink," or simply "resin" herein)
can include a monomer, particularly photopolymerizable and/or free
radical polymerizable monomers, and a suitable initiator such as a
free radical initiator, and combinations thereof. Examples include,
but are not limited to, acrylics, methacrylics, acrylamides,
styrenics, olefins, halogenated olefins, cyclic alkenes, maleic
anhydride, alkenes, alkynes, carbon monoxide, functionalized
oligomers, multifunctional cute site monomers, functionalized PEGs,
etc., including combinations thereof. Examples of liquid resins,
monomers and initiators include but are not limited to those set
forth in U.S. Pat. Nos. 8,232,043; 8,119,214; 7,935,476; 7,767,728;
7,649,029; WO 2012129968 A1; CN 102715751 A; JP 2012210408 A.
[0111] Acid Catalyzed Polymerizable Liquids.
[0112] While in some embodiments as noted above the polymerizable
liquid comprises a free radical polymerizable liquid (in which case
an inhibitor may be oxygen as described below), in other
embodiments the polymerizable liquid comprises an acid catalyzed,
or cationically polymerized, polymerizable liquid. In such
embodiments the polymerizable liquid comprises monomers contain
groups suitable for acid catalysis, such as epoxide groups, vinyl
ether groups, etc. Thus suitable monomers include olefins such as
methoxyethene, 4-methoxystyrene, styrene, 2-methylprop-1-ene,
1,3-butadiene, etc.; heterocyclic monomers (including lactones,
lactams, and cyclic amines) such as oxirane, thietane,
tetrahydrofuran, oxazoline, 1,3, dioxepane, oxetan-2-one, etc., and
combinations thereof. A suitable (generally ionic or non-ionic)
photoacid generator (PAG) is included in the acid catalyzed
polymerizable liquid, examples of which include, but are not
limited to onium salts, sulfonium and iodonium salts, etc., such as
diphenyl iodide hexafluorophosphate, diphenyl iodide
hexafluoroarsenate, diphenyl iodide hexafluoroantimonate, diphenyl
p-methoxyphenyl triflate, diphenyl p-toluenyl triflate, diphenyl
p-isobutylphenyl triflate, diphenyl p-tert-butylphenyl triflate,
triphenylsulfonium hexafluorophosphate, triphenylsulfonium
hexafluoroarsenate, triphenylsulfonium hexafluoroantimonate,
triphenylsulfonium triflate, dibutylnaphthylsulfonium triflate,
etc., including mixtures thereof. See, e.g., U.S. Pat. Nos.
7,824,839; 7,550,246; 7,534,844; 6,692,891; 5,374,500; and
5,017,461; see also Photoacid Generator Selection Guide for the
electronics industry and energy curable coatings (BASF 2010).
[0113] Hydrogels.
[0114] In some embodiments suitable resins includes photocurable
hydrogels like poly(ethylene glycols) (PEG) and gelatins. PEG
hydrogels have been used to deliver a variety of biologicals,
including Growth factors; however, a great challenge facing PEG
hydrogels crosslinked by chain growth polymerizations is the
potential for irreversible protein damage. Conditions to maximize
release of the biologicals from photopolymerized PEG diacrylate
hydrogels can be enhanced by inclusion of affinity binding peptide
sequences in the monomer resin solutions, prior to
photopolymerization allowing sustained delivery. Gelatin is a
biopolymer frequently used in food, cosmetic, pharmaceutical and
photographic industries. It is obtained by thermal denaturation or
chemical and physical degradation of collagen. There are three
kinds of gelatin, including those found in animals, fish and
humans. Gelatin from the skin of cold water fish is considered safe
to use in pharmaceutical applications. UV or visible light can be
used to crosslink appropriately modified gelatin. Methods for
crosslinking gelatin include cure derivatives from dyes such as
Rose Bengal.
[0115] Photocurable Silicone Resins.
[0116] A suitable resin includes photocurable silicones. UV cure
silicone rubber, such as Siliopren.TM. UV Cure Silicone Rubber can
be used as can LOCTITE.TM. Cure Silicone adhesives sealants.
Applications include optical instruments, medical and surgical
equipment, exterior lighting and enclosures, electrical
connectors/sensors, fiber optics, gaskets, and molds.
[0117] Biodegradable Resins.
[0118] Biodegradable resins are particularly important for
implantable devices to deliver drugs or for temporary performance
applications, like biodegradable screws and stents (U.S. Pat. Nos.
7,919,162; 6,932,930). Biodegradable copolymers of lactic acid and
glycolic acid (PLGA) can be dissolved in PEG di(meth)acrylate to
yield a transparent resin suitable for use. Polycaprolactone and
PLGA oligomers can be functionalized with acrylic or methacrylic
groups to allow them to be effective resins for use.
[0119] Photocurable Polyurethanes.
[0120] A particularly useful resin is photocurable polyurethanes
(including, polyureas, and copolymers of polyurethanes and
polyureas (e.g., poly(urethane-urea)). A photopolymerizable
polyurethane/polyurea composition comprising (1) a polyurethane
based on an aliphatic diisocyanate, poly(hexamethylene isophthalate
glycol) and, optionally, 1,4-butanediol; (2) a polyfunctional
acrylic ester; (3) a photoinitiator; and (4) an anti-oxidant, can
be formulated so that it provides a hard, abrasion-resistant, and
stain-resistant material (U.S. Pat. No. 4,337,130). Photocurable
thermoplastic polyurethane elastomers incorporate photoreactive
diacetylene diols as chain extenders.
[0121] High Performance Resins.
[0122] In some embodiments, high performance resins are used. Such
high performance resins may sometimes require the use of heating to
melt and/or reduce the viscosity thereof, as noted above and
discussed further below. Examples of such resins include, but are
not limited to, resins for those materials sometimes referred to as
liquid crystalline polymers of esters, ester-imide, and ester-amide
oligomers, as described in U.S. Pat. Nos. 7,507,784; 6,939,940.
Since such resins are sometimes employed as high-temperature
thermoset resins, in the present invention they further comprise a
suitable photoinitiator such as benzophenone, anthraquinone, and
fluorenone initiators (including derivatives thereof), to initiate
cross-linking on irradiation, as discussed further below.
[0123] Additional Example Resins.
[0124] Particularly useful resins for dental applications include
EnvisionTEC's Clear Guide, EnvisionTEC's E-Denstone Material.
Particularly useful resins for hearing aid industries include
EnvisionTEC's e-Shell 300 Series of resins. Particularly useful
resins include EnvisionTEC's HTM140IV High Temperature Mold
Material for use directly with vulcanized rubber in molding/casting
applications. A particularly useful material for making tough and
stiff parts includes EnvisionTEC's RC31 resin. Particularly useful
resin for investment casting applications include EnvisionTEC's
Easy Cast EC500 resin and MadeSolid FireCast resin.
[0125] Additional Resin Ingredients.
[0126] The liquid resin or polymerizable material can have solid
particles suspended or dispersed therein. Any suitable solid
particle can be used, depending upon the end product being
fabricated. The particles can be metallic, organic/polymeric,
inorganic, or composites or mixtures thereof. The particles can be
nonconductive, semi-conductive, or conductive (including metallic
and non-metallic or polymer conductors); and the particles can be
magnetic, ferromagnetic, paramagnetic, or nonmagnetic. The
particles can be of any suitable shape, including spherical,
elliptical, cylindrical, etc. The particles can be of any suitable
size (for example, ranging from 1 nm to 20 um average
diameter).
[0127] The particles can comprise an active agent or detectable
compound as described below, though these may also be provided
dissolved solubilized in the liquid resin as also discussed below.
For example, magnetic or paramagnetic particles or nanoparticles
can be employed.
[0128] The liquid resin can have additional ingredients solubilized
therein, including pigments, dyes, active compounds or
pharmaceutical compounds, detectable compounds (e.g., fluorescent,
phosphorescent, radioactive), etc., again depending upon the
particular purpose of the product being fabricated. Examples of
such additional ingredients include, but are not limited to,
proteins, peptides, nucleic acids (DNA, RNA) such as siRNA, sugars,
small organic compounds (drugs and drug-like compounds), etc.,
including combinations thereof.
[0129] Non-Reactive Light Absorbers.
[0130] In some embodiments, polymerizable liquids for carrying out
the present invention include a non-reactive pigment or dye that
absorbs light, particularly UV light. Suitable examples of such
light absorbers include, but are not limited to: (i) titanium
dioxide (e.g., included in an amount of from 0.05 or 0.1 to 1 or 5
percent by weight), (ii) carbon black (e.g., included in an amount
of from 0.05 or 0.1 to 1 or 5 percent by weight), and/or (iii) an
organic ultraviolet light absorber such as a hydroxybenzophenone,
hydroxyphenylbenzotriazole, oxanilide, benzophenone, thioxanthone,
hydroxyphenyltriazine, and/or benzotriazole ultraviolet light
absorber (e.g., Mayzo BLS1326) (e.g., included in an amount of
0.001 or 0.005 to 1, 2 or 4 percent by weight). Examples of
suitable organic ultraviolet light absorbers include, but are not
limited to, those described in U.S. Pat. Nos. 3,213,058; 6,916,867;
7,157,586; and 7,695, 643, the disclosures of which are
incorporated herein by reference.
[0131] Inhibitors of Polymerization.
[0132] Inhibitors or polymerization inhibitors for use in the
present invention may be in the form of a liquid or a gas. In some
embodiments, gas inhibitors are preferred. In some embodiments,
liquid inhibitors such as oils or lubricants (e.g., fluorinated
oils such as perfluoropolyethers) may be employed, as inhibitors
(or as release layers that maintain a liquid interface)). The
specific inhibitor will depend upon the monomer being polymerized
and the polymerization reaction. For free radical polymerization
monomers, the inhibitor can conveniently be oxygen, which can be
provided in the form of a gas such as air, a gas enriched in oxygen
(optionally but in some embodiments preferably containing
additional inert gases to reduce combustibility thereof), or in
some embodiments pure oxygen gas. In alternate embodiments, such as
where the monomer is polymerized by photoacid generator initiator,
the inhibitor can be a base such as ammonia, trace amines (e.g.
methyl amine, ethyl amine, di and trialkyl amines such as dimethyl
amine, diethyl amine, trimethyl amine, triethyl amine, etc.), or
carbon dioxide, including mixtures or combinations thereof.
[0133] Polymerizable Liquids Carrying Live Cells.
[0134] In some embodiments, the polymerizable liquid may carry live
cells as "particles" therein. Such polymerizable liquids are
generally aqueous, and may be oxygenated, and may be considered as
"emulsions" where the live cells are the discrete phase. Suitable
live cells may be plant cells (e.g., monocot, dicot), animal cells
(e.g., mammalian, avian, amphibian, reptile cells), microbial cells
(e.g., prokaryote, eukaryote, protozoal, etc.), etc. The cells may
be of differentiated cells from or corresponding to any type of
tissue (e.g., blood, cartilage, bone, muscle, endocrine gland,
exocrine gland, epithelial, endothelial, etc.), or may be
undifferentiated cells such as stem cells or progenitor cells. In
such embodiments the polymerizable liquid can be one that forms a
hydrogel, including but not limited to those described in U.S. Pat.
Nos. 7,651,683; 7,651,682; 7,556,490; 6,602,975; 5,836,313;
etc.
II. Apparatus.
[0135] A non-limiting embodiment of an apparatus of the invention
is shown in FIG. 2. It comprises a radiation source 11 such as a
digital light processor (DLP) providing electromagnetic radiation
12 which though reflective mirror 13 illuminates a build chamber
defined by wall 14 and a rigid or flexible build plate 15 forming
the bottom of the build chamber, which build chamber is filled with
liquid resin 16. The bottom of the chamber 15 is constructed of a
build plate comprising a rigid or flexible semipermeable member as
discussed further below. The top of the object under construction
17 is attached to a carrier 18. The carrier is driven in the
vertical direction by linear stage 19, although alternate
structures can be used as discussed below.
[0136] A liquid resin reservoir, tubing, pumps liquid level sensors
and/or valves can be included to replenish the pool of liquid resin
in the build chamber (not shown for clarity) though in some
embodiments a simple gravity feed may be employed. Drives/actuators
for the carrier or linear stage, along with associated wiring, can
be included in accordance with known techniques (again not shown
for clarity). The drives/actuators, radiation source, and in some
embodiments pumps and liquid level sensors can all be operatively
associated with a suitable controller, again in accordance with
known techniques.
[0137] Build plates 15 used to carry out the present invention
generally comprise or consist of a (typically rigid or solid,
stationary, and/or fixed, although in some embodiments flexible)
semipermeable (or gas permeable) member, alone or in combination
with one or more additional supporting substrates (e.g., clamps and
tensioning members to tension and stabilize an otherwise flexible
semipermeable material). The semipermeable member can be made of
any suitable material that is optically transparent at the relevant
wavelengths (or otherwise transparent to the radiation source,
whether or not it is visually transparent as perceived by the human
eye--i.e., an optically transparent window may in some embodiments
be visually opaque), including but not limited to porous or
microporous glass, and the rigid gas permeable polymers used for
the manufacture of rigid gas permeable contact lenses. See, e.g.,
Norman G. Gaylord, U.S. Pat. No. RE31,406; see also U.S. Pat. Nos.
7,862,176; 7,344,731; 7,097,302; 5,349,394; 5,310,571; 5,162,469;
5,141,665; 5,070,170; 4,923,906; and 4,845,089. In some embodiments
such materials are characterized as glassy and/or amorphous
polymers and/or substantially crosslinked that they are essentially
non-swellable. Preferably the semipermeable member is formed of a
material that does not swell when contacted to the liquid resin or
material to be polymerized (i.e., is "non-swellable"). Suitable
materials for the semipermeable member include amorphous
fluoropolymers, such as those described in U.S. Pat. Nos. 5,308,685
and 5,051,115. For example, such fluoropolymers are particularly
useful over silicones that would potentially swell when used in
conjunction with organic liquid resin inks to be polymerized. For
some liquid resin inks, such as more aqueous-based monomeric
systems and/or some polymeric resin ink systems that have low
swelling tendencies, silicone based window materials maybe
suitable. The solubility or permeability of organic liquid resin
inks can be dramatically decreased by a number of known parameters
including increasing the crosslink density of the window material
or increasing the molecular weight of the liquid resin ink. In some
embodiments the build plate may be formed from a thin film or sheet
of material which is flexible when separated from the apparatus of
the invention, but which is clamped and tensioned when installed in
the apparatus (e.g., with a tensioning ring) so that it is
tensioned and stabilized in the apparatus. Particular materials
include TEFLON AF.RTM. fluoropolymers, commercially available from
DuPont. Additional materials include perfluoropolyether polymers
such as described in U.S. Pat. Nos. 8,268,446; 8,263,129;
8,158,728; and 7,435,495.
[0138] It will be appreciated that essentially all solid materials,
and most of those described above, have some inherent "flex" even
though they may be considered "rigid," depending on factors such as
the shape and thickness thereof and environmental factors such as
the pressure and temperature to which they are subjected. In
addition, the terms "stationary" or "fixed" with respect to the
build plate is intended to mean that no mechanical interruption of
the process occurs, or no mechanism or structure for mechanical
interruption of the process (as in a layer-by-layer method or
apparatus) is provided, even if a mechanism for incremental
adjustment of the build plate (for example, adjustment that does
not lead to or cause collapse of the gradient of polymerization
zone) is provided).
[0139] The semipermeable member typically comprises a top surface
portion, a bottom surface portion, and an edge surface portion. The
build surface is on the top surface portion; and the feed surface
may be on one, two, or all three of the top surface portion, the
bottom surface portion, and/or the edge surface portion. In the
embodiment illustrated in FIG. 2 the feed surface is on the bottom
surface portion, but alternate configurations where the feed
surface is provided on an edge, and/or on the top surface portion
(close to but separate or spaced away from the build surface) can
be implemented with routine skill.
[0140] The semipermeable member has, in some embodiments, a
thickness of from 0.01, 0.1 or 1 millimeters to 10 or 100
millimeters, or more (depending upon the size of the item being
fabricated, whether or not it is laminated to or in contact with an
additional supporting plate such as glass, etc., as discussed
further below.
[0141] The permeability of the semipermeable member to the
polymerization inhibitor will depend upon conditions such as the
pressure of the atmosphere and/or inhibitor, the choice of
inhibitor, the rate or speed of fabrication, etc. In general, when
the inhibitor is oxygen, the permeability of the semipermeable
member to oxygen may be from 10 or 20 Barrers, up to 1000 or 2000
Barrers, or more. For example, a semipermeable member with a
permeability of 10 Barrers used with a pure oxygen, or highly
enriched oxygen, atmosphere under a pressure of 150 PSI may perform
substantially the same as a semipermeable member with a
permeability of 500 Barrers when the oxygen is supplied from the
ambient atmosphere under atmospheric conditions.
[0142] Thus, the semipermeable member may comprise a flexible
polymer film (having any suitable thickness, e.g., from 0.001,
0.01, 0.05, 0.1 or 1 millimeters to 1, 5, 10, or 100 millimeters,
or more), and the build plate may further comprise a tensioning
member (e.g., a peripheral clamp and an operatively associated
strain member or stretching member, as in a "drum head"; a
plurality of peripheral clamps, etc., including combinations
thereof) connected to the polymer film and to fix and tension,
stabilize or rigidify the film (e.g., at least sufficiently so that
the film does not stick to the object as the object is advanced and
resiliently or elastically rebound therefrom). The film has a top
surface and a bottom surface, with the build surface on the top
surface and the feed surface preferably on the bottom surface. In
other embodiments, the semipermeable member comprises: (i) a
polymer film layer (having any suitable thickness, e.g., from
0.001, 0.01, 0.1 or 1 millimeters to 5, 10 or 100 millimeters, or
more), having a top surface positioned for contacting the
polymerizable liquid and a bottom surface, and (ii) a gas
permeable, optically transparent supporting member (having any
suitable thickness, e.g., from 0.01, 0.1 or 1 millimeters to 10,
100, or 200 millimeters, or more), contacting the film layer bottom
surface. The supporting member has a top surface contacting the
film layer bottom surface, and the supporting member has a bottom
surface which may serve as the feed surface for the polymerization
inhibitor. Any suitable materials that are semipermeable (that is,
permeable to the polymerization inhibitor) may be used. For
example, the polymer film or polymer film layer may, for example,
be a fluoropolymer film, such as an amorphous thermoplastic
fluoropolymer like TEFLON AF 1600.TM. or TEFLON AF 2400.TM.
fluoropolymer films, or perfluoropolyether (PFPE), particularly a
crosslinked PFPE film, or a crosslinked silicone polymer film. The
supporting member comprises a silicone or crosslinked silicone
polymer member such as a polydimethylsiloxane polydmiethylxiloxane
member, a gas permeable polymer member, or a porous or microporous
glass member. Films can be laminated or clamped directly to the
rigid supporting member without adhesive (e.g., using PFPE and PDMS
materials), or silane coupling agents that react with the upper
surface of a PDMS layer can be utilized to adhere to the first
polymer film layer. UV-curable, acrylate-functional silicones can
also be used as a tie layer between UV-curable PFPEs and rigid PDMS
supporting layers.
[0143] When configured for placement in the apparatus, the carrier
defines a "build region" on the build surface, within the total
area of the build surface. Because lateral "throw" (e.g., in the X
and/or Y directions) is not required in the present invention to
break adhesion between successive layers, as in the Joyce and Chen
devices noted previously, the area of the build region within the
build surface may be maximized (or conversely, the area of the
build surface not devoted to the build region may be minimized).
Hence in some embodiments, the total surface area of the build
region can occupy at least fifty, sixty, seventy, eighty, or ninety
percent of the total surface area of the build surface.
[0144] As shown in FIG. 2, the various components are mounted on a
support or frame assembly 20. While the particular design of the
support or frame assembly is not critical and can assume numerous
configurations, in the illustrated embodiment it is comprised of a
base 21 to which the radiation source 11 is securely or rigidly
attached, a vertical member 22 to which the linear stage is
operatively associated, and a horizontal table 23 to which wall 14
is removably or securely attached (or on which the wall is placed),
and with the build plate fixed, either permanently or removably, to
form the build chamber as described above.
[0145] As noted above, the build plate can consist of a single
unitary and integral piece of a semipermeable member, or can
comprise additional materials. For example, a porous or microporous
glass can be laminated or fixed to a semipermeable material. Or, a
semipermeable member as an upper portion can be fixed to a
transparent lower member having purging channels formed therein for
feeding gas carrying the polymerization inhibitor to the
semipermeable member (through which it passes to the build surface
to facilitate the formation of a release layer of unpolymerized
liquid material, as noted above and below). Such purge channels may
extend fully or partially through the base plate: For example, the
purge channels may extend partially into the base plate, but then
end in the region directly underlying the build surface to avoid
introduction of distortion. Specific geometries will depend upon
whether the feed surface for the inhibitor into the semipermeable
member is located on the same side or opposite side as the build
surface, on an edge portion thereof, or a combination of several
thereof.
[0146] Any suitable radiation source (or combination of sources)
can be used, depending upon the particular resin employed,
including electron beam and ionizing radiation sources. In a
preferred embodiment the radiation source is an actinic radiation
source, such as one or more light sources, and in particular one or
more ultraviolet light sources. Any suitable light source can be
used, such as incandescent lights, fluorescent lights,
phosphorescent or luminescent lights, a laser, light-emitting
diode, etc., including arrays thereof. The light source preferably
includes a pattern-forming element operatively associated with a
controller, as noted above. In some embodiments, the light source
or pattern forming element comprises a digital (or deformable)
micromirror device (DMD) with digital light processing (DLP), a
spatial modulator (SLM), or a microelectromechanical system (MEMS)
mirror array, a liquid crystal display (LCD) panel, a mask (aka a
reticle), a silhouette, or a combination thereof. See, U.S. Pat.
No. 7,902,526. Preferably the light source comprises a spatial
light modulation array such as a liquid crystal light valve array
or micromirror array or DMD (e.g., with an operatively associated
digital light processor, typically in turn under the control of a
suitable controller), configured to carry out exposure or
irradiation of the polymerizable liquid without a mask, e.g., by
maskless photolithography. See, e.g., U.S. Pat. Nos. 6,312,134;
6,248,509; 6,238,852; and 5,691,541.
[0147] In some embodiments, as discussed further below, there may
be movement in the X and/or Y directions concurrently with movement
in the Z direction, with the movement in the X and/or Y direction
hence occurring during polymerization of the polymerizable liquid
(this is in contrast to the movement described in Y. Chen et al.,
or M. Joyce, supra, which is movement between prior and subsequent
polymerization steps for the purpose of replenishing polymerizable
liquid). In the present invention such movement may be carried out
for purposes such as reducing "burn in" or fouling in a particular
zone of the build surface.
[0148] Because an advantage of some embodiments of the present
invention is that the size of the build surface on the
semipermeable member (i.e., the build plate or window) may be
reduced due to the absence of a requirement for extensive lateral
"throw" as in the Joyce or Chen devices noted above, in the
methods, systems and apparatus of the present invention lateral
movement (including movement in the X and/or Y direction or
combination thereof) of the carrier and object (if such lateral
movement is present) is preferably not more than, or less than, 80,
70, 60, 50, 40, 30, 20, or even 10 percent of the width (in the
direction of that lateral movement) of the build region.
[0149] While in some embodiments the carrier is mounted on an
elevator to advance up and away from a stationary build plate, on
other embodiments the converse arrangement may be used: That is,
the carrier may be fixed and the build plate lowered to thereby
advance the carrier away therefrom. Numerous different mechanical
configurations will be apparent to those skilled in the art to
achieve the same result.
[0150] Depending on the choice of material from which the carrier
is fabricated, and the choice of polymer or resin from which the
article is made, adhesion of the article to the carrier may
sometimes be insufficient to retain the article on the carrier
through to completion of the finished article or "build." For
example, an aluminum carrier may have lower adhesion than a
poly(vinyl chloride) (or "PVC") carrier. Hence one solution is to
employ a carrier comprising a PVC on the surface to which the
article being fabricated is polymerized. If this promotes too great
an adhesion to conveniently separate the finished part from the
carrier, then any of a variety of techniques can be used to further
secure the article to a less adhesive carrier, including but not
limited to the application of adhesive tape such as "Greener
Masking Tape for Basic Painting #2025 High adhesion" to further
secure the article to the carrier during fabrication.
III. Controller and Process Control.
[0151] The methods and apparatus of the invention can include
process steps and apparatus features to implement process control,
including feedback and feed-forward control, to, for example,
enhance the speed and/or reliability of the method.
[0152] A controller for use in carrying out the present invention
may be implemented as hardware circuitry, software, or a
combination thereof. In one embodiment, the controller is a general
purpose computer that runs software, operatively associated with
monitors, drives, pumps, and other components through suitable
interface hardware and/or software. Suitable software for the
control of a three-dimensional printing or fabrication method and
apparatus as described herein includes, but is not limited to, the
ReplicatorG open source 3d printing program, 3DPrint.TM. controller
software from 3D systems, Slic3r, Skeinforge, KISSlicer,
Repetier-Host, PrintRun, Cura, etc., including combinations
thereof.
[0153] Process parameters to directly or indirectly monitor,
continuously or intermittently, during the process (e.g., during
one, some or all of the filling, irradiating and advancing steps)
include, but are not limited to, irradiation intensity, temperature
of carrier, polymerizable liquid in the build zone, temperature of
growing product, temperature of build plate, pressure, speed of
advance, pressure, force (e.g., exerted on the build plate through
the carrier and product being fabricated), strain (e.g., exerted on
the carrier by the growing product being fabricated), thickness of
release layer, etc.
[0154] Known parameters that may be used in feedback and/or
feed-forward control systems include, but are not limited to,
expected consumption of polymerizable liquid (e.g., from the known
geometry or volume of the article being fabricated), degradation
temperature of the polymer being formed from the polymerizable
liquid, etc.
[0155] Process conditions to directly or indirectly control,
continuously or step-wise, in response to a monitored parameter,
and/or known parameters (e.g., during any or all of the process
steps noted above), include, but are not limited to, rate of supply
of polymerizable liquid, temperature, pressure, rate or speed of
advance of carrier, intensity of irradiation, duration of
irradiation (e.g. for each "slice"), etc.
[0156] For example, the temperature of the polymerizable liquid in
the build zone, or the temperature of the build plate, can be
monitored, directly or indirectly with an appropriate thermocouple,
non-contact temperature sensor (e.g., an infrared temperature
sensor), or other suitable temperature sensor, to determine whether
the temperature exceeds the degradation temperature of the
polymerized product. If so, a process parameter may be adjusted
through a controller to reduce the temperature in the build zone
and/or of the build plate. Suitable process parameters for such
adjustment may include: decreasing temperature with a cooler,
decreasing the rate of advance of the carrier, decreasing intensity
of the irradiation, decreasing duration of radiation exposure,
etc.
[0157] In addition, the intensity of the irradiation source (e.g.,
an ultraviolet light source such as a mercury lamp) may be
monitored with a photodetector to detect a decrease of intensity
from the irradiation source (e.g., through routine degradation
thereof during use). If detected, a process parameter may be
adjusted through a controller to accommodate the loss of intensity.
Suitable process parameters for such adjustment may include:
increasing temperature with a heater, decreasing the rate of
advance of the carrier, increasing power to the light source,
etc.
[0158] As another example, control of temperature and/or pressure
to enhance fabrication time may be achieved with heaters and
coolers (individually, or in combination with one another and
separately responsive to a controller), and/or with a pressure
supply (e.g., pump, pressure vessel, valves and combinations
thereof) and/or a pressure release mechanism such as a controllable
valve (individually, or in combination with one another and
separately responsive to a controller).
[0159] In some embodiments the controller is configured to maintain
the gradient of polymerization zone described herein (see, e.g.,
FIG. 1) throughout the fabrication of some or all of the final
product. The specific configuration (e.g., times, rate or speed of
advancing, radiation intensity, temperature, etc.) will depend upon
factors such as the nature of the specific polymerizable liquid and
the product being created. Configuration to maintain the gradient
of polymerization zone may be carried out empirically, by entering
a set of process parameters or instructions previously determined,
or determined through a series of test runs or "trial and error";
configuration may be provided through pre-determined instructions;
configuration may be achieved by suitable monitoring and feedback
(as discussed above), combinations thereof, or in any other
suitable manner.
[0160] In some embodiments, a method and apparatus as described
above may be controlled by a software program running in a general
purpose computer with suitable interface hardware between that
computer and the apparatus described above. Numerous alternatives
are commercially available. Non-limiting examples of one
combination of components is shown in FIGS. 3 to 5, where
"Microcontroller" is Parallax Propeller, the Stepper Motor Driver
is Sparkfun EasyDriver, the LED Driver is a Luxeon Single LED
Driver, the USB to Serial is a Parallax USB to Serial converter,
and the DLP System is a Texas Instruments LightCrafter system.
IV. General Methods.
[0161] The three dimensional intermediate is preferably formed from
resins as described above by additive manufacturing, typically
bottom-up or top-down additive manufacturing.
[0162] In general, top-down three-dimensional fabrication is
carried out by:
[0163] (a) providing a polymerizable liquid reservoir having a
polymerizable liquid fill level and a carrier positioned in the
reservoir, the carrier and the fill level defining a build region
therebetween;
[0164] (b) filling the build region with a polymerizable liquid
(i.e., the resin), said polymerizable liquid comprising a mixture
of (i) a light (typically ultraviolet light) polymerizable liquid
first component, and (ii) a second solidifiable component of the
dual cure system; and then
[0165] (c) irradiating the build region with light to form a solid
polymer scaffold from the first component and also advancing
(typically lowering) the carrier away from the build surface to
form a three-dimensional intermediate having the same shape as, or
a shape to be imparted to, the three-dimensional object and
containing said second solidifiable component (e.g., a second
reactive component) carried in the scaffold in unsolidified and/or
uncured form.
[0166] A wiper blade, doctor blade, or optically transparent (rigid
or flexible) window, may optionally be provided at the fill level
to facilitate leveling of the polymerizable liquid, in accordance
with known techniques. In the case of an optically transparent
window, the window provides a build surface against which the three
dimensional intermediate is formed, analogous to the build surface
in bottom-up three dimensional fabrication as discussed below.
[0167] In general, bottom-up three dimensional fabrication is
carried out by:
[0168] (a) providing a carrier and an optically transparent member
having a build surface, the carrier and the build surface defining
a build region therebetween;
[0169] (b) filling the build region with a polymerizable liquid
(i.e., the resin), said polymerizable liquid comprising a mixture
of (i) a light (typically ultraviolet light) polymerizable liquid
first component, and (ii) a second solidifiable component of the
dual cure system; and then
[0170] (c) irradiating the build region with light through said
optically transparent member to form a solid polymer scaffold from
the first component and also advancing (typically raising) the
carrier away from the build surface to form a three-dimensional
intermediate having the same shape as, or a shape to be imparted
to, the three-dimensional object and containing said second
solidifiable component (e.g., a second reactive component) carried
in the scaffold in unsolidified and/or uncured form.
[0171] In some embodiments of bottom up or top down three
dimensional fabrication as implemented in the context of the
present invention, the build surface is stationary during the
formation of the three dimensional intermediate; in other
embodiments of bottom-up three dimensional fabrication as
implemented in the context of the present invention, the build
surface is tilted, slid, flexed and/or peeled, and/or otherwise
translocated or released from the growing three dimensional
intermediate, usually repeatedly, during formation of the three
dimensional intermediate.
[0172] In some embodiments of bottom up or top down three
dimensional fabrication as carried out in the context of the
present invention, the polymerizable liquid (or resin) is
maintained in liquid contact with both the growing three
dimensional intermediate and the build surface during both the
filling and irradiating steps, during fabrication of some of, a
major portion of, or all of the three dimensional intermediate.
[0173] In some embodiments of bottom-up or top down three
dimensional fabrication as carried out in the context of the
present invention, the growing three dimensional intermediate is
fabricated in a layerless manner (e.g., through multiple exposures
or "slices" of patterned actinic radiation or light) during at
least a portion of the formation of the three dimensional
intermediate.
[0174] In some embodiments of bottom up or top down three
dimensional fabrication as carried out in the context of the
present invention, the growing three dimensional intermediate is
fabricated in a layer-by-layer manner (e.g., through multiple
exposures or "slices" of patterned actinic radiation or light),
during at least a portion of the formation of the three dimensional
intermediate.
[0175] In some embodiments of bottom up or top down three
dimensional fabrication employing a rigid or flexible optically
transparent window, a lubricant or immiscible liquid may be
provided between the window and the polymerizable liquid (e.g., a
fluorinated fluid or oil such as a perfluoropolyether oil).
[0176] From the foregoing it will be appreciated that, in some
embodiments of bottom-up or top down three dimensional fabrication
as carried out in the context of the present invention, the growing
three dimensional intermediate is fabricated in a layerless manner
during the formation of at least one portion thereof, and that same
growing three dimensional intermediate is fabricated in a
layer-by-layer manner during the formation of at least one other
portion thereof. Thus, operating mode may be changed once, or on
multiple occasions, between layerless fabrication and
layer-by-layer fabrication, as desired by operating conditions such
as part geometry.
[0177] In some embodiments, the intermediate is formed by
continuous liquid interface production (CLIP), as discussed further
below.
[0178] As noted above, the present invention provides (in some
embodiments) a method of forming a three-dimensional object,
comprising the steps of: (a) providing a carrier and a build plate,
the build plate comprising a semipermeable member, the
semipermeable member comprising a build surface and a feed surface
separate from the build surface, with the build surface and the
carrier defining a build region therebetween, and with the feed
surface in fluid contact with a polymerization inhibitor; then
(concurrently and/or sequentially) (b) filing the build region with
a polymerizable liquid, the polymerizable liquid contacting the
build segment, (c) irradiating the build region through the build
plate to produce a solid polymerized region in the build region,
with a liquid film release layer comprised of the polymerizable
liquid formed between the solid polymerized region and the build
surface, the polymerization of which liquid film is inhibited by
the polymerization inhibitor; and (d) advancing the carrier with
the polymerized region adhered thereto away from the build surface
on the stationary build plate to create a subsequent build region
between the polymerized region and the top zone. In general the
method includes (e) continuing and/or repeating steps (b) through
(d) to produce a subsequent polymerized region adhered to a
previous polymerized region until the continued or repeated
deposition of polymerized regions adhered to one another forms the
three-dimensional object.
[0179] Since no mechanical release of a release layer is required,
or no mechanical movement of a build surface to replenish oxygen or
other inhibitor is required, the method can be carried out in a
continuous fashion, though it will be appreciated that the
individual steps noted above may be carried out sequentially,
concurrently, or a combination thereof. Indeed, the rate of steps
can be varied over time depending upon factors such as the density
and/or complexity of the region under fabrication.
[0180] Also, since mechanical release from a window or from a
release layer generally requires that the carrier be advanced a
greater distance from the build plate than desired for the next
irradiation step, which enables the window to be recoated, and then
return of the carrier back closer to the build plate (e.g., a "two
steps forward one step back" operation), the present invention in
some embodiments permits elimination of this "back-up" step and
allows the carrier to be advanced unidirectionally, or in a single
direction, without intervening movement of the window for
re-coating, or "snapping" of a pre-formed elastic release-layer.
However, in other embodiments of the invention, reciprocation is
utilized not for the purpose of obtaining release, but for the
purpose of more rapidly filling or pumping polymerizable liquid
into the build region.
[0181] While the dead zone and the gradient of polymerization zone
do not have a strict boundary therebetween (in those locations
where the two meet), the thickness of the gradient of
polymerization zone is in some embodiments at least as great as the
thickness of the dead zone. Thus, in some embodiments, the dead
zone has a thickness of from 0.01, 0.1, 1, 2, or 10 microns up to
100, 200 or 400 microns, or more, and/or the gradient of
polymerization zone and the dead zone together have a thickness of
from 1 or 2 microns up to 400, 600, or 1000 microns, or more. Thus
the gradient of polymerization zone may be thick or thin depending
on the particular process conditions at that time. Where the
gradient of polymerization zone is thin, it may also be described
as an active surface on the bottom of the growing three-dimensional
object, with which monomers can react and continue to form growing
polymer chains therewith. In some embodiments, the gradient of
polymerization zone, or active surface, is maintained (while
polymerizing steps continue) for a time of at least 5, 10, 15, 20
or 30 seconds, up to 5, 10, 15 or 20 minutes or more, or until
completion of the three-dimensional product.
[0182] The method may further comprise the step of disrupting the
gradient of polymerization zone for a time sufficient to form a
cleavage line in the three-dimensional object (e.g., at a
predetermined desired location for intentional cleavage, or at a
location in the object where prevention of cleavage or reduction of
cleavage is non-critical), and then reinstating the gradient of
polymerization zone (e.g. by pausing, and resuming, the advancing
step, increasing, then decreasing, the intensity of irradiation,
and combinations thereof).
[0183] In some embodiments, the advancing step is carried out
sequentially in uniform increments (e.g., of from 0.1 or 1 microns,
up to 10 or 100 microns, or more) for each step or increment. In
some embodiments, the advancing step is carried out sequentially in
variable increments (e.g., each increment ranging from 0.1 or 1
microns, up to 10 or 100 microns, or more) for each step or
increment. The size of the increment, along with the rate of
advancing, will depend in part upon factors such as temperature,
pressure, structure of the article being produced (e.g., size,
density, complexity, configuration, etc.)
[0184] In other embodiments of the invention, the advancing step is
carried out continuously, at a uniform or variable rate.
[0185] In some embodiments, the rate of advance (whether carried
out sequentially or continuously) is from about 0.1 1, or 10
microns per second, up to about to 100, 1,000, or 10,000 microns
per second, again depending again depending on factors such as
temperature, pressure, structure of the article being produced,
intensity of radiation, etc
[0186] As described further below, in some embodiments the filling
step is carried out by forcing the polymerizable liquid into the
build region under pressure. In such a case, the advancing step or
steps may be carried out at a rate or cumulative or average rate of
at least 0.1, 1, 10, 50, 100, 500 or 1000 microns per second, or
more. In general, the pressure may be whatever is sufficient to
increase the rate of the advancing step(s) at least 2, 4, 6, 8 or
10 times as compared to the maximum rate of repetition of the
advancing steps in the absence of the pressure. Where the pressure
is provided by enclosing an apparatus such as described above in a
pressure vessel and carrying the process out in a pressurized
atmosphere (e.g., of air, air enriched with oxygen, a blend of
gasses, pure oxygen, etc.) a pressure of 10, 20, 30 or 40 pounds
per square inch (PSI) up to, 200, 300, 400 or 500 PSI or more, may
be used. For fabrication of large irregular objects higher
pressures may be less preferred as compared to slower fabrication
times due to the cost of a large high pressure vessel. In such an
embodiment, both the feed surface and the polymerizable liquid can
be are in fluid contact with the same compressed gas (e.g., one
comprising from 20 to 95 percent by volume of oxygen, the oxygen
serving as the polymerization inhibitor.
[0187] On the other hand, when smaller items are fabricated, or a
rod or fiber is fabricated that can be removed or exited from the
pressure vessel as it is produced through a port or orifice
therein, then the size of the pressure vessel can be kept smaller
relative to the size of the product being fabricated and higher
pressures can (if desired) be more readily utilized.
[0188] As noted above, the irradiating step is in some embodiments
carried out with patterned irradiation. The patterned irradiation
may be a fixed pattern or may be a variable pattern created by a
pattern generator (e.g., a DLP) as discussed above, depending upon
the particular item being fabricated.
[0189] When the patterned irradiation is a variable pattern rather
than a pattern that is held constant over time, then each
irradiating step may be any suitable time or duration depending on
factors such as the intensity of the irradiation, the presence or
absence of dyes in the polymerizable material, the rate of growth,
etc. Thus in some embodiments each irradiating step can be from
0.001, 0.01, 0.1, 1 or 10 microseconds, up to 1, 10, or 100
minutes, or more, in duration. The interval between each
irradiating step is in some embodiments preferably as brief as
possible, e.g., from 0.001, 0.01, 0.1, or 1 microseconds up to 0.1,
1, or 10 seconds. In example embodiments, the pattern may vary
hundreds, thousands or millions of times to impart shape changes on
the three-dimensional object being formed. In addition, in example
embodiments, the pattern generator may have high resolution with
millions of pixel elements that can be varied to change the shape
that is imparted. For example, the pattern generator may be a DLP
with more than 1,000 or 2,000 or 3,000 or more rows and/or more
than 1,000 or 2,000 or 3,000 or more columns of micromirrors, or
pixels in a liquid crystal display panel, that can be used to vary
the shape. In example embodiments, the three-dimensional object may
be formed through the gradient of polymerization allowing the shape
changes to be imparted while continuously printing. In example
embodiments, this allows complex three-dimensional objects to be
formed at high speed with a substantially continuous surface
without cleavage lines or seams. In some examples, thousands or
millions of shape variations may be imparted on the
three-dimensional object being formed without cleavage lines or
seams across a length of the object being formed of more than 1 mm,
1 cm, 10 cm or more or across the entire length of the formed
object. In example embodiments, the object may be continuously
formed through the gradient of polymerization at a rate of more
than 1, 10, 100, 1000, 10000 or more microns per second.
[0190] In some embodiments the build surface is flat; in other the
build surface is irregular such as convexly or concavely curved, or
has walls or trenches formed therein. In either case the build
surface may be smooth or textured.
[0191] Curved and/or irregular build plates or build surfaces can
be used in fiber or rod formation, to provide different materials
to a single object being fabricated (that is, different
polymerizable liquids to the same build surface through channels or
trenches formed in the build surface, each associated with a
separate liquid supply, etc.
[0192] Carrier Feed Channels for Polymerizable Liquid.
[0193] While polymerizable liquid may be provided directly to the
build plate from a liquid conduit and reservoir system, in some
embodiments the carrier include one or more feed channels therein.
The carrier feed channels are in fluid communication with the
polymerizable liquid supply, for example a reservoir and associated
pump. Different carrier feed channels may be in fluid communication
with the same supply and operate simultaneously with one another,
or different carrier feed channels may be separately controllable
from one another (for example, through the provision of a pump
and/or valve for each). Separately controllable feed channels may
be in fluid communication with a reservoir containing the same
polymerizable liquid, or may be in fluid communication with a
reservoir containing different polymerizable liquids. Through the
use of valve assemblies, different polymerizable liquids may in
some embodiments be alternately fed through the same feed channel,
if desired.
V. Reciprocal Feed of Polymerizable Liquid.
[0194] In an embodiment of the present invention, the carrier is
vertically reciprocated with respect to the build surface to
enhance or speed the refilling of the build region with the
polymerizable liquid.
[0195] In some embodiments, the vertically reciprocating step,
which comprises an upstroke and a downstroke, is carried out with
the distance of travel of the upstroke being greater than the
distance of travel of the downstroke, to thereby concurrently carry
out the advancing step (that is, driving the carrier away from the
build plate in the Z dimension) in part or in whole.
[0196] In some embodiments, the speed of the upstroke gradually
accelerates (that is, there is provided a gradual start and/or
gradual acceleration of the upstroke, over a period of at least 20,
30, 40, or 50 percent of the total time of the upstroke, until the
conclusion of the upstroke, or the change of direction which
represents the beginning of the downstroke. Stated differently, the
upstroke begins, or starts, gently or gradually.
[0197] In some embodiments, the speed of the downstroke gradually
decelerates (that is, there is provided a gradual termination
and/or gradual deceleration of the downstroke, over a period of at
least 20, 30, 40, or 50 percent of the total time of the
downstroke. Stated differently, the downstroke concludes, or ends,
gently or gradually.
[0198] While in some embodiments there is an abrupt end, or abrupt
deceleration, of the upstroke, and an abrupt beginning or
deceleration of the downstroke (e.g., a rapid change in vector or
direction of travel from upstroke to downstroke), it will be
appreciated that gradual transitions may be introduced here as well
(e.g., through introduction of a "plateau" or pause in travel
between the upstroke and downstroke). It will also be appreciated
that, while the reciprocating step may be a single upstroke and
downstroke, the reciprocations may occur in linked groups thereof,
of the same or different amplitude and frequency.
[0199] In some embodiments, the vertically reciprocating step is
carried out over a total time of from 0.01 or 0.1 seconds up to 1
or 10 seconds (e.g., per cycle of an upstroke and a
downstroke).
[0200] In some embodiments, the upstroke distance of travel is from
0.02 or 0.2 millimeters (or 20 or 200 microns) to 1 or 10
millimeters (or 1000 to 10,000 microns). The distance of travel of
the downstroke may be the same as, or less than, the distance of
travel of the upstroke, where a lesser distance of travel for the
downstroke serves to achieve the advancing of the carrier away from
the build surface as the three-dimensional object is gradually
formed.
[0201] Preferably the vertically reciprocating step, and
particularly the upstroke thereof, does not cause the formation of
gas bubbles or a gas pocket in the build region, but instead the
build region remains filled with the polymerizable liquid
throughout the reciprocation steps, and the gradient of
polymerization zone or region remains in contact with the "dead
zone" and with the growing object being fabricated throughout the
reciprocation steps. As will be appreciated, a purpose of the
reciprocation is to speed or enhance the refilling of the build
region, particularly where larger build regions are to be refilled
with polymerizable liquid, as compared to the speed at which the
build region could be refilled without the reciprocation step.
[0202] In some embodiments, the advancing step is carried out
intermittently at a rate of 1, 2, 5 or 10 individual advances per
minute up to 300, 600, or 1000 individual advances per minute, each
followed by a pause during which an irradiating step is carried
out. It will be appreciated that one or more reciprocation steps
(e.g., upstroke plus downstroke) may be carried out within each
advancing step. Stated differently, the reciprocating steps may be
nested within the advancing steps.
[0203] In some embodiments, the individual advances are carried out
over an average distance of travel for each advance of from 10 or
50 microns to 100 or 200 microns (optionally including the total
distance of travel for each vertically reciprocating step, e.g.,
the sum of the upstroke distance minus the downstroke
distance).
[0204] Apparatus for carrying out the invention in which the
reciprocation steps described herein are implemented substantially
as described above, with the drive associated with the carrier,
and/or with an additional drive operatively associated with the
transparent member, and with the controller operatively associated
with either or both thereof and configured to reciprocate the
carrier and transparent member with respect to one another as
described above.
VI. Increased Speed of Fabrication by Increased Light
Intensity.
[0205] In general, it has been observed that speed of fabrication
can increase with increased light intensity. In some embodiments,
the light is concentrated or "focused" at the build region to
increase the speed of fabrication. This may be accomplished using
an optical device such as an objective lens.
[0206] The speed of fabrication may be generally proportional to
the light intensity. For example, the build speed in millimeters
per hour may be calculated by multiplying the light intensity in
milliWatts per square centimeter and a multiplier. The multiplier
may depend on a variety of factors, including those discussed
below. A range of multipliers, from low to high, may be employed.
On the low end of the range, the multiplier may be about 10, 15, 20
or 30. On the high end of the multiplier range, the multiplier may
be about 150, 300, 400 or more.
[0207] The relationships described above are, in general,
contemplated for light intensities of from 1, 5 or 10 milliWatts
per square centimeter, up to 20 or 50 milliWatts per square
centimeter.
[0208] Certain optical characteristics of the light may be selected
to facilitate increased speed of fabrication. By way of example, a
band pass filter may be used with a mercury bulb light source to
provide 365.+-.10 nm light measured at Full Width Half Maximum
(FWHM). By way of further example, a band pass filter may be used
with an LED light source to provide 375.+-.15 nm light measured at
FWHM.
[0209] As noted above, polymerizable liquids used in such processes
are, in general, free radical polymerizable liquids with oxygen as
the inhibitor, or acid-catalyzed or cationically polymerizable
liquids with a base as the inhibitor. Some specific polymerizable
liquids will of course cure more rapidly or efficiently than others
and hence be more amenable to higher speeds, though this may be
offset at least in part by further increasing light intensity.
[0210] At higher light intensities and speeds, the "dead zone" may
become thinner as inhibitor is consumed. If the dead zone is lost
then the process will be disrupted. In such case, the supply of
inhibitor may be enhanced by any suitable means, including
providing an enriched and/or pressurized atmosphere of inhibitor, a
more porous semipermeable member, a stronger or more powerful
inhibitor (particularly where a base is employed), etc.
[0211] In general, lower viscosity polymerizable liquids are more
amenable to higher speeds, particularly for fabrication of articles
with a large and/or dense cross section (although this can be
offset at least in part by increasing light intensity).
Polymerizable liquids with viscosities in the range of 50 or 100
centipoise, up to 600, 800 or 1000 centipoise or more (as measured
at room temperature and atmospheric pressure with a suitable device
such as a HYDRAMOTION REACTAVISC.TM. Viscometer (available from
Hydramotion Ltd, 1 York Road Business Park, Malton, York YO17 6YA
England). In some embodiments, where necessary, the viscosity of
the polymerizable liquid can advantageously be reduced by heating
the polymerizable liquid, as described above.
[0212] In some embodiments, such as fabrication of articles with a
large and/or dense cross-section, speed of fabrication can be
enhanced by introducing reciprocation to "pump" the polymerizable
liquid, as described above, and/or the use of feeding the
polymerizable liquid through the carrier, as also described above,
and/or heating and/or pressurizing the polymerizable liquid, as
also described above.
VII. Tiling.
[0213] It may be desirable to use more than one light engine to
preserve resolution and light intensity for larger build sizes.
Each light engine may be configured to project an image (e.g., an
array of pixels) into the build region such that a plurality of
"tiled" images are projected into the build region. As used herein,
the term "light engine" can mean an assembly including a light
source, a DLP device such as a digital micromirror or LCD device
and an optical device such as an objective lens. The "light engine"
may also include electronics such as a controller that is
operatively associated with one or more of the other
components.
[0214] This is shown schematically in FIGS. 17A-17C. The light
engine assemblies 130A, 130B produce adjacent or "tiled" images
140A, 140B. In FIG. 17A, the images are slightly misaligned; that
is, there is a gap between them. In FIG. 17B, the images are
aligned; there is no gap and no overlap between them. In FIG. 17C,
there is a slight overlap of the images 140A and 140B.
[0215] In some embodiments, the configuration with the overlapped
images shown in FIG. 17C is employed with some form of "blending"
or "smoothing" of the overlapped regions as generally discussed in,
for example, U.S. Pat. Nos. 7,292,207, 8,102,332, 8,427,391,
8,446,431 and U.S. Patent Application Publication Nos.
2013/0269882, 2013/0278840 and 2013/0321475, the disclosures of
which are incorporated herein in their entireties.
[0216] The tiled images can allow for larger build areas without
sacrificing light intensity, and therefore can facilitate faster
build speeds for larger objects. It will be understood that more
than two light engine assemblies (and corresponding tiled images)
may be employed. Various embodiments of the invention employ at
least 4, 8, 16, 32, 64, 128 or more tiled images.
VIII. Dual Hardening Polymerizable Liquids: Part B.
[0217] As noted above, in some embodiments of the invention, the
polymerizable liquid comprises a first light polymerizable
component (sometimes referred to as "Part A" herein) and a second
component that solidifies by another mechanism, or in a different
manner from, the first component (sometimes referred to as "Part B"
herein), typically by further reacting, polymerizing, or chain
extending. Numerous embodiments thereof may be carried out. In the
following, note that, where particular acrylates such as
methacrylates are described, other acrylates may also be used.
[0218] Part A Chemistry.
[0219] As noted above, in some embodiments of the present
invention, a resin will have a first component, termed "Part A."
Part A comprises or consists of a mix of monomers and/or
prepolymers that can be polymerized by exposure to actinic
radiation or light. This resin can have a functionality of 2 or
higher (though a resin with a functionality of 1 can also be used
when the polymer does not dissolve in its monomer). A purpose of
Part A is to "lock" the shape of the object being formed or create
a scaffold for the one or more additional components (e.g., Part
B). Importantly, Part A is present at or above the minimum quantity
needed to maintain the shape of the object being formed after the
initial solidification. In some embodiments, this amount
corresponds to less than ten, twenty, or thirty percent by weight
of the total resin (polymerizable liquid) composition.
[0220] In some embodiments, Part A can react to form a cross-linked
polymer network or a solid homopolymer.
[0221] Examples of suitable reactive end groups suitable for Part A
constituents, monomers, or prepolymers include, but are not limited
to: acrylates, methacrylates, .alpha.-olefins, N-vinyls,
acrylamides, methacrylamides, styrenics, epoxides, thiols,
1,3-dienes, vinyl halides, acrylonitriles, vinyl esters,
maleimides, and vinyl ethers.
[0222] An aspect of the solidification of Part A is that it
provides a scaffold in which a second reactive resin component,
termed "Part B," can solidify during a second step (which may occur
concurrently with or following the solidification of Part A). This
secondary reaction preferably occurs without significantly
distorting the original shape defined during the solidification of
Part A. Alternative approaches would lead to a distortion in the
original shape in a desired manner.
[0223] In particular embodiments, when used in the methods and
apparatus described herein, the solidification of Part A is
continuously inhibited during printing within a certain region, by
oxygen or amines or other reactive species, to form a liquid
interface between the solidified part and an inhibitor-permeable
film or window (e.g., is carried out by continuous liquid
interphase/interface printing).
[0224] Part B Chemistry.
[0225] Part B may comprise, consist of or consist essentially of a
mix of monomers and/or prepolymers that possess reactive end groups
that participate in a second solidification reaction after the Part
A solidification reaction. In some embodiments, Part B could be
added simultaneously to Part A so it is present during the exposure
to actinide radiation, or Part B could be infused into the object
made during the 3D printing process in a subsequent step. Examples
of methods used to solidify Part B include, but are not limited to,
contacting the object or scaffold to heat, water or water vapor,
light at a different wavelength than that at which Part A is cured,
catalysts, (with or without additional heat), evaporation of a
solvent from the polymerizable liquid (e.g., using heat, vacuum, or
a combination thereof), microwave irradiation, etc., including
combinations thereof.
[0226] Examples of suitable reactive end group pairs suitable for
Part B constituents, monomers or prepolymers include, but are not
limited to: epoxy/amine, epoxy/hydroxyl, oxetane/amine,
oxetane/alcohol, isocyanate*/hydroxyl, Isocyanate*/amine,
isocyanate/carboxylic acid, anhydride/amine, amine/carboxylic acid,
amine/ester, hydroxyl/carboxylic acid, hydroxyl/acid chloride,
amine/acid chloride, vinyl/Si--H (hydrosilylation),
Si--Cl/hydroxyl, Si--Cl/amine, hydroxyl/aldehyde, amine/aldehyde,
hydroxymethyl or alkoxymethyl amide/alcohol, aminoplast,
alkyne/Azide (also known as one embodiment of "Click Chemistry,"
along with additional reactions including thiolene, Michael
additions, Diels-Alder reactions, nucleophilic substitution
reactions, etc.), alkene/Sulfur (polybutadiene vulcanization),
alkene/peroxide, alkene/thiol, alkyne/thiol, hydroxyl/halide,
isocyanate*/water (polyurethane foams), Si--OH/hydroxyl,
Si--OH/water, Si--OH/Si--H (tin catalyzed silicone), Si--OH/Si--OH
(tin catalyzed silicone), Perfluorovinyl (coupling to form
perfluorocyclobutane), etc., where *Isocyanates include protected
isocyanates (e.g. oximes)), diene/dienophiles for Diels-Alder
reactions, olefin metathesis polymerization, olefin polymerization
using Ziegler-Natta catalysis, ring-opening polymerization
(including ring-opening olefin metathesis polymerization, lactams,
lactones, Siloxanes, epoxides, cyclic ethers, imines, cyclic
acetals, etc.), etc.
[0227] Other reactive chemistries suitable for Part B will be
recognizable by those skilled in the art. Part B components useful
for the formation of polymers described in "Concise Polymeric
Materials Encyclopedia" and the "Encyclopedia of Polymer Science
and Technology" are hereby incorporated by reference.
[0228] Organic Peroxides.
[0229] In some embodiments, an organic peroxide may be included in
the polymerizable liquid or resin, for example to facilitate the
reaction of potentially unreacted double bonds during heat and/or
microwave irradiation curing. Such organic peroxides may be
included in the resin or polymerizable liquid in any suitable
amount, such as from 0.001 or 0.01 or 0.1 percent by weight, up to
1, 2, or 3 percent by weight. Examples of suitable organic
peroxides include, but are not limited to,
2,5-bis(tert-butylperoxy)-2,5-dimethylhexane (e.g., LUPEROX
101.TM.), dilauroyl peroxide (e.g. LUPEROX LP.TM.) benzoyl peroxide
(e.g., LUPEROX A98.TM.), and bis(tert-butyldioxyisopropyl)benzene
(e.g., VulCUP R.TM.), etc., including combinations thereof. Such
organic peroxides are available from a variety of sources,
including but not limited to Arkema (420 rue d'Estienne d'Orves,
92705 Colombes Cedex, France).
[0230] Elastomers.
[0231] A particularly useful embodiment for implementing the
invention is for the formation of elastomers. Tough,
high-elongation elastomers are difficult to achieve using only
liquid UV-curable precursors. However, there exist many thermally
cured materials (polyurethanes, silicones, natural rubber) that
result in tough, high-elongation elastomers after curing. These
thermally curable elastomers on their own are generally
incompatible with most 3D printing techniques.
[0232] In embodiments of the current invention, small amounts
(e.g., less than 20 percent by weight) of a low-viscosity UV
curable material (Part A) are blended with thermally-curable
precursors to form (preferably tough) elastomers (e.g.
polyurethanes, polyureas, or copolymers thereof (e.g.,
poly(urethane-urea)), and silicones) (Part B). The UV curable
component is used to solidify an object into the desired shape
using 3D printing as described herein and a scaffold for the
elastomer precursors in the polymerizable liquid. The object can
then be heated after printing, thereby activating the second
component, resulting in an object comprising the elastomer.
[0233] Adhesion of Formed Objects.
[0234] In some embodiments, it may be useful to define the shapes
of multiple objects using the solidification of Part A, align those
objects in a particular configuration, such that there is a
hermetic seal between the objects, then activate the secondary
solidification of Part B. In this manner, strong adhesion between
parts can be achieved during production. A particularly useful
example may be in the formation and adhesion of sneaker
components.
[0235] Fusion of Particles as Part B.
[0236] In some embodiments, "Part B" may simply consist of small
particles of a pre-formed polymer. After the solidification of Part
A, the object may be heated above the glass transition temperature
of Part B in order to fuse the entrapped polymeric particles.
[0237] Evaporation of Solvent as Part B.
[0238] In some embodiments, "Part B" may consist of a pre-formed
polymer dissolved in a solvent. After the solidification of Part A
into the desired object, the object is subjected to a process (e.g.
heat+vacuum) that allows for evaporation of the solvent for Part B,
thereby solidifying Part B.
[0239] Thermally Cleavable End Groups.
[0240] In some embodiments, the reactive chemistries in Part A can
be thermally cleaved to generate a new reactive species after the
solidification of Part A. The newly formed reactive species can
further react with Part B in a secondary solidification. An
exemplary system is described by Velankar, Pezos and Cooper,
Journal of Applied Polymer Science, 62, 1361-1376 (1996). Here,
after UV-curing, the acrylate/methacrylate groups in the formed
object are thermally cleaved to generated diisocyanate prepolymers
that further react with blended chain-extender to give high
molecular weight polyurethanes/polyureas within the original cured
material or scaffold. Such systems are, in general, dual-hardening
systems that employ blocked or reactive blocked prepolymers, as
discussed in greater detail below. It may be noted that later work
indicates that the thermal cleavage above is actually a
displacement reaction of the chain extender (usually a diamine)
with the hindered urea, giving the final polyurethanes/polyureas
without generating isocyanate intermediates.
[0241] Methods of Mixing Components.
[0242] In some embodiments, the components may be mixed in a
continuous manner prior to being introduced to the printer build
plate. This may be done using multi-barrel syringes and mixing
nozzles. For example, Part A may comprise or consist of a
UV-curable di(meth)acrylate resin, Part B may comprise or consist
of a diisocyanate prepolymer and a polyol mixture. The polyol can
be blended together in one barrel with Part A and remain unreacted.
A second syringe barrel would contain the diisocyanate of Part B.
In this manner, the material can be stored without worry of "Part
B" solidifying prematurely. Additionally, when the resin is
introduced to the printer in this fashion, a constant time is
defined between mixing of all components and solidification of Part
A.
[0243] Other Additive Manufacturing Techniques.
[0244] It will be clear to those skilled in the art that the
materials described in the current invention will be useful in
other additive manufacturing techniques including fused deposition
modeling (FDM), solid laser sintering (SLS), and Ink-jet methods.
For example, a melt-processed acrylonitrile-butadiene-styrene resin
may be formulated with a second UV-curable component that can be
activated after the object is formed by FDM. New mechanical
properties could be achieved in this manner. In another
alternative, melt-processed unvulcanized rubber is mixed with a
vulcanizing agent such as sulfur or peroxide, and the shape set
through FDM, then followed by a continuation of vulcanization.
IX. Dual Hardening Polymerizable Liquids Employing Blocked
Constituents and Thermally Cleavable Blocking Groups.
[0245] In some embodiments, where the solidifying and/or curing
step (d) is carried out subsequent to the irradiating step (e.g.,
by heating or microwave irradiating); the solidifying and/or curing
step (d) is carried out under conditions in which the solid polymer
scaffold degrades and forms a constituent necessary for the
polymerization of the second component (e.g., a constituent such as
(i) a prepolymer, (ii) a diisocyanate or polyisocyanate, and/or
(iii) a polyol and/or diol, where the second component comprises
precursors to a polyurethane/polyurea resin). Such methods may
involve the use of reactive or non-reactive blocking groups on or
coupled to a constituent of the first component, such that the
constituent participates in the first hardening or solidifying
event, and when de-protected (yielding free constituent and free
blocking groups or blocking agents) generates a free constituent
that can participate in the second solidifying and/or curing event.
Non-limiting examples of such methods are described further
below.
A. Dual Hardening Polymerizable Liquids Employing Blocked
Prepolymers and Thermally Cleavable Blocking Groups.
[0246] Some "dual cure" embodiments of the present invention are,
in general, a method of forming a three-dimensional object,
comprising:
[0247] (a) providing a carrier and an optically transparent member
having a build surface, the carrier and the build surface defining
a build region therebetween;
[0248] (b) filling the build region with a polymerizable liquid,
the polymerizable liquid comprising a mixture of a blocked or
reactive blocked prepolymer, optionally but in some embodiments
preferably a reactive diluent, a chain extender, and a
photoinitiator;
[0249] (c) irradiating the build region with light through the
optically transparent member to form a (rigid, compressible,
collapsible, flexible or elastic) solid blocked polymer scaffold
from the blocked prepolymer and optionally the reactive diluent
while concurrently advancing the carrier away from the build
surface to form a three-dimensional intermediate having the same
shape as, or a shape to be imparted to, the three-dimensional
object, with the intermediate containing the chain extender; and
then
[0250] (d) heating or microwave irradiating the three-dimensional
intermediate sufficiently to form the three-dimensional product
from the three-dimensional intermediate (without wishing to be
bound to any particular mechanism, the heating or microwave
irradiating may cause the chain extender to react with the blocked
or reactive blocked prepolymer or an unblocked product
thereof).
[0251] In some embodiments, the blocked or reactive blocked
prepolymer comprises a polyisocyanate.
[0252] In some embodiments, the blocked or reactive blocked
prepolymer is a compound of the formula A-X-A, where X is a
hydrocarbyl group and each A is an independently selected
substituent of Formula X:
##STR00001##
where R is a hydrocarbyl group, R' is O or NH, and Z is a blocking
group, the blocking group optionally having a reactive terminal
group (e.g., a polymerizable end group such as an epoxy, alkene,
alkyne, or thiol end group, for example an ethylenically
unsaturated end group such as a vinyl ether).). In a particular
example, each A is an independently selected substituent of Formula
(XI):
##STR00002##
where R and R' are as given above.
[0253] In some embodiments, the blocked or reactive blocked
prepolymer comprises a polyisocyanate oligomer produced by the
reaction of at least one diisocyanate (e.g., a diisocyanate such as
hexamethylene diisocyanate (HDI),
bis-(4-isocyanatocyclohexyl)methane (HMDI), isophorone diisocyanate
(IPDI), etc., a triisocyanate, etc.) with at least one polyol
(e.g., a polyether or polyester or polybutadiene diol).
[0254] In some embodiments, the reactive blocked prepolymer is
blocked by reaction of a polyisocyanate with an amine(meth)acrylate
monomer blocking agent (e.g., tertiary-butylaminoethyl methacrylate
(TBAEMA), tertiary pentylaminoethyl methacrylate (TPAEMA), tertiary
hexylaminoethyl methacrylate (THAEMA), tertiary-butylaminopropyl
methacrylate (TBAPMA), acrylate analogs thereof, and mixtures
thereof (see, e.g., US Patent Application Publication No.
20130202392). Note that all of these can be used as diluents as
well.
[0255] There are many blocking agents for isocyanate. In preferred
embodiments of the current invention, the blocking agent (e.g.,
TBAEMA), cures (e.g., from the actinic radiation or light) into the
system. Those skilled in the art can couple (meth)acrylate groups
to known blocking agents to create additional blocking agents that
can be used to carry out the present invention. Still further,
those skilled in the art can use maleimide, or substitute maleimide
on other known blocking agents, for use in the present
invention.
[0256] Examples of known blocking agents which can be substituted
on or covalently coupled to (meth)acrylate or maleimide for use in
the present invention include, but are not limited to, phenol type
blocking agents (e.g. phenol, cresol, xylenol, nitrophenol,
chlorophenol, ethyl phenol, t-butylphenol, hydroxy benzoic acid,
hydroxy benzoic acid esters, 2,5-di-t-butyl-4-hydroxy toluene,
etc.), lactam type blocking agents (e.g. .epsilon.-caprolactam,
.delta.-valerolactam, .gamma.-butyrolactam, .beta.-propiolactam,
etc.), active methylene type blocking agents (e.g. diethyl
malonate, dimethyl malonate, ethyl acetoacetate, methyl
acetoacetate, acetyl acetone, etc.), alcohol type blocking agents
(e.g. methanol, ethanol, n-propanol, isopropanol, n-butanol,
isobutanol, t-butanol, n-amyl alcohol, t-amyl alcohol, lauryl
alcohol, ethylene glycol monomethyl ether, ethylene glycol
monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol
monomethyl ether, diethylene glycol monoethyl ether, propylene
glycol monomethyl ether, methoxyethanol, glycolic acid, glycolic
acid esters, lactic acid, lactic acid ester, methylol urea,
methylol melamine, diacetone alcohol, ethylene chlorohydrine,
ethylene bromhydrine, 1,3-dichloro-2-propanol,
.omega.-hydroperfluoro alcohol, acetocyanhydrine, etc.), mercaptan
type blocking agents (e.g. butyl mercaptan, hexyl mercaptan,
t-butyl mercaptan, t-dodecyl mercaptan, 2-mercapto-benzothiazole,
thiophenol, methyl thiophenol, ethyl thiophenyl, etc.), acid amide
type blocking agents (e.g. acetoanilide, acetoanisidine amide,
acrylamide, methacrylamide, acetic amide, stearic amide, benzamide,
etc.), imide type blocking agents (e.g. succinimide, phthalimide,
maleimide, etc.), amine type blocking agents (e.g. diphenylamine,
phenylnaphthylamine, xylidine, N-phenyl xylidine, carbazole,
aniline, naphthylamine, butylamine, dibutylamine, butyl
phenylamine, etc.), imidazole type blocking agents (e.g. imidazole,
2-ethylimidazole, etc.), urea type blocking agents (e.g. urea,
thiourea, ethylene urea, ethylene thiourea, 1,3-diphenyl urea,
etc.), carbamate type blocking agents (e.g. N-phenyl carbamic acid
phenyl ester, 2-oxazolidone, etc.), imine type blocking agents
(e.g. ethylene imine, etc.), oxime type blocking agents (e.g.
formaldoxime, acetaldoximine, acetoxime, methylethyl ketoxime,
diacetylomonoxime, benzophenoxime, cyclohexanonoxime, etc.) and
sulfurous acid salt type blocking agents (e.g. sodium bisulfite,
potassium bisulfite, etc.). Of these, use is preferably made of the
phenol type, the lactam type, the active methylene type and the
oxime type blocking agents (see, e.g., U.S. Pat. No.
3,947,426).
[0257] In some embodiments, the diisocyanate or
isocyanate-functional oligomer or prepolymer is blocked with an
aldehyde blocking agent, such as a formyl blocking agent. Examples
include but are not limited to 2-formyloxyethyl(meth)acrylate
(FEMA) (or other aldehyde-containing acrylate or methacrylate) with
a diisocyanate or isocyanate functional oligomer or polymer. See,
e.g., X. Tassel et al., A New Blocking Agent of isocyanates,
European Polymer Journal 36(9), 1745-1751 (2000); T. Haig, P.
Badyrka et al., U.S. Pat. No. 8,524,816; and M. Sullivan and D.
Bulpett, U.S. Pat. Appl. Pub. No. US20120080824 The reaction
product of such an aldehyde blocking agent and an isocyanate can in
some embodiments possess an advantage over TBAEMA blocked ABPUs by
reducing hydrogen bonding due to urea formation, in turn (in some
embodiments) resulting in lower viscosity blocked isocyanates. In
addition, in some embodiments, a second advantage is eliminating
free amines within the final product (a product of the deblocking
of TBAEMA from the ABPU) which might oxidize and cause yellowness
or lead to degradation.
[0258] In some embodiments, the reactive diluent comprises an
acrylate, a methacrylate, a styrene, an acrylic acid, a vinylamide,
a vinyl ether, a vinyl ester (including derivatives thereof),
polymers containing any one or more of the foregoing, and
combinations of two or more of the foregoing. (e.g., acrylonitrile,
styrene, divinyl benzene, vinyl toluene, methyl acrylate, ethyl
acrylate, butyl acrylate, methyl(meth)acrylate,
amine(meth)acrylates as described above, and mixtures of any two or
more of these) (see, e.g., US Patent Application Publication No.
20140072806).
[0259] In some embodiments, the chain extender comprises at least
one diol, diamine or dithiol chain extender (e.g., ethylene glycol,
1,3-propanediol, 1,2-propanediol, 1,4-butanediol, 1,5-pentanediol,
1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol,
1,10-decanediol, 1,11-undecanediol, 1,12-dodecanediol,
1,2-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, the
corresponding diamine and dithiol analogs thereof, lysine ethyl
ester, arginine ethyl ester, p-alanine-based diamine, and random or
block copolymers made from at least one diisocyanate and at least
one diol, diamine or dithiol chain extender; see, e.g., US Patent
Application Publication No. 20140010858). Note also that, when
dicarboxylic acid is used as the chain extender, polyesters (or
carbamate-carboxylic acid anhydrides) are made.
[0260] In some embodiments, the polymerizable liquid comprises:
[0261] from 5 or 20 or 40 percent by weight to 60 or 80 or 90
percent by weight of the blocked or reactive blocked
prepolymer;
[0262] from 10 or 20 percent by weight to 30 or 40 or 50 percent by
weight of the reactive diluent;
[0263] from 5 or 10 percent by weight to 20 or 30 percent by weight
of the chain extender; and
[0264] from 0.1 or 0.2 percent by weight to 1, 2 or 4 percent by
weight of the photoinitiator. Optional additional ingredients, such
as dyes, fillers (e.g., silica), surfactants, etc., may also be
included, as discussed in greater detail above.
[0265] An advantage of some embodiments of the invention is that,
because these polymerizable liquids do not rapidly polymerize upon
mixing, they may be formulated in advance, and the filling step
carried out by feeding or supplying the polymerizable liquid to the
build region from a single source (e.g., a single reservoir
containing the polymerizable liquid in pre-mixed form), thus
obviating the need to modify the apparatus to provide separate
reservoirs and mixing capability.
[0266] Three dimensional objects made by the process are, in some
embodiments, collapsible or compressible (that is, elastic (e.g.,
has a Young's modulus at room temperature of from about 0.001, 0.01
or 0.1 gigapascals to about 1, 2 or 4 gigapascals, and/or a tensile
strength at maximum load at room temperature of about 0.01, 0.1, or
1 to about 50, 100, or 500 megapascals, and/or a percent elongation
at break at room temperature of about 10, 20 50 or 100 percent to
1000, 2000, or 5000 percent, or more).
[0267] An additional example of the preparation of a blocked
reactive prepolymer is shown in the Scheme below:
##STR00003##
[0268] One can use similar chemistry to that described above to
form a reactive blocked diioscyanate, a reactive blocked chain
extender, or a reactive blocked prepolymer.
[0269] A non-limiting example of a dual cure system employing a
thermally cleavable end group is shown in the FIG. 25A and the
Scheme below:
##STR00004##
Without wishing to be bound to any underlying mechanism, in some
embodiments, during thermal cure, blocking agent is cleaved and
diisocyanate prepolymer is re-formed and quickly reacts with chain
extenders or additional soft segment to form thermoplastic or
thermoset polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), as follows:
##STR00005##
Alternative mechanisms such as those described in section B below
may also be implemented or involved.
[0270] In the scheme above, the dual cure resin is comprised of a
UV-curable (meth)acrylate blocked polyurethane (ABPU), a reactive
diluent, a photoinitiator, and a chain extender(s). The reactive
diluent (10-50 wt %) is an acrylate or methacrylate that helps to
reduce the viscosity of ABPU and will be copolymerized with the
ABPU under UV irradiation. The photoinitiator (generally about 1 wt
%) can be one of those commonly used UV initiators, examples of
which include but are not limited to such as acetophenones
(diethoxyacetophenone for example), phosphine oxides
diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide,
phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide (PPO), Irgacure
369, etc.
[0271] After UV curing to form a intermediate shaped product having
blocked polyurethane oligomers as a scaffold, and carrying the
chain extender, the ABPU resin is subjected to a thermal cure,
during which a high molecular weight polyurethane/polyurea is
formed by a spontaneous reaction between the polyurethane/polyurea
oligomers and the chain extender(s). The polyurethane/polyurea
oligomer can react with proper chain extenders through substitution
of TBAEMA, N-vinylformamide (NVF) or the like by proper chain
extenders, either by deblocking or displacement. The thermal cure
time needed can vary depending on the temperature, size, shape, and
density of the product, but is typically between 1 to 6 hours
depending on the specific ABPU systems, chain extenders and
temperature.
[0272] One advantageous aspect of the foregoing is using a tertiary
amine-containing (meth)acrylate (e.g., t-butylaminoethyl
methacrylate, TBAEMA) to terminate synthesized
polyurethane/polyurea oligomers with isocyanate at both ends. Using
acrylate or methacrylate containing hydroxyl groups to terminate
polyurethane/polyurea oligomers with isocyanate ends is used in UV
curing resins in the coating field. The formed urethane bonds
between the isocyanate and hydroxyl groups are generally stable
even at high temperatures. In embodiments of the present invention,
the urea bond formed between the tertiary amine of TBAEMA and
isocyanate of the oligomer becomes labile when heated to suitable
temperature (for example, about 100.degree. C.), regenerating the
isocyanate groups that will react with the chain extender(s) during
thermal-cure to form high molecular weight polyurethane (PU). While
it is possible to synthesize other (meth)acrylate containing
isocyanate blocking functionality as generally used (such as
N-vinylformamide, .epsilon.-caprolactam, 1,2,3-triazole, methyl
ethyl ketoxime, diethyl malonate, etc.), the illustrative
embodiment uses TBAEMA that is commercially available. The used
chain extenders can be diols, diamines, triols, triamines or their
combinations or others. Ethylene glycol, 1,4-butanediol, methylene
dicyclohexylamine (H12MDA; or PACM as the commercial name from Air
Products), hydroquinone bis(2-Hydroxyethyl) Ether (HQEE),
4,4'-Methylenebis(3-Chloro-2,6-Diethylaniline) (MCDEA),
4,4'-methylene-bis-(2,6 diethylaniline)(MDEA),
4,4'-Methylenebis(2-chloroaniline) (MOCA) are the preferred chain
extenders.
[0273] To produce an ABPU, TBAEMA may be used to terminate the
isocyanate end groups of the prepolymer, which is derived from
isocyanate tipped polyols. The polyols (preferably with hydroxyl
functionality of 2) used can be polyethers [especially
polytetramethylene oxide (PTMO), polypropylene glycol (PPG)],
polyesters [polycaprolactone (PCL), polycarbonate, etc.],
polybutadiene and block copolymers such as PCL and PTMO block
copolymer (Capa 7201A of Perstop, Inc.). The molecular weight of
these polyols can be 500 to 6000 Da, and 500-2000 Da are preferred.
In the presence of a catalyst (e.g., stannous octoate with 0.1-0.3
wt % to the weight of polyol; other tin catalysts or amine
catalysts), diisocyanate (e.g., toluene diisocyanate (TDI),
methylene diphenyl diisocyanate (MDI), hexamethylene diisocyanate
(HDI), isophorone diisocyanate (IPDI), hydrogenated MDI (HMDI),
para-phenyl diisocyanate (PPDI) etc.) is added to the polyol (or
the reverse order; preferably the polyol being added to the
isocyanate) with certain molar ratio (larger than 1:1; preferably,
no less than 2:1 and 2:1 is mostly preferred) to make a prepolymer
with residual isocyanate groups (50.about.100.degree. C.). TBAEMA
is then added to the reaction [Note:
moles(TBAEMA)*2+moles(OH)=moles(isocyanate)] to cap the remaining
isocyanate groups, resulting in ABPU (under 40-70.degree. C.).
Radical inhibitors such as hydroquinone (100-500 ppm) can be used
to inhibit polymerization of (meth)acrylate during the
reaction.
[0274] In general, a three-dimensional product of the foregoing
methods comprises (i) a linear thermoplastic polyurethane,
polyurea, or copolymer thereof (e.g., poly(urethane-urea)), (ii) a
cross-linked thermoset polyurethane, polyurea, or copolymer thereof
(e.g., poly(urethane-urea)), or (iii) combinations thereof
(optionally blended with de-blocked blocking group which is
copolymerized with the reactive diluents(s), for example as an
interpenetrating polymer network, a semi-interpenetrating polymer
network, or as a sequential interpenetrating polymer network).). In
some example embodiments, the three-dimensional product may also
include unreacted photoinitiator remaining in the three-dimensional
formed object. For example, in some embodiments, from 0.1 or 0.2
percent by weight to 1, 2 or 4 percent by weight of the
photoinitiator may remain in the three-dimensional formed object or
the photoinitiator may be present in lower amounts or only a trace
amount. In some example embodiments, the three-dimensional product
may also include reacted photoinitiator fragments. For example, in
some embodiments, the reacted photoinitiator fragments may be
remnants of the first cure forming the intermediate product. For
example, from 0.1 or 0.2 percent by weight to 1, 2 or 4 percent by
weight of reacted photoinitiator fragments may remain in the
three-dimensional formed object or the reacted photoinitiator
fragments may be present in lower amounts or only a trace amount.
In example embodiments, a three-dimensional product may comprise,
consist of or consist essentially of all or any combination of a
linear thermoplastic polyurethane, a cross-linked thermoset
polyurethane, unreacted photoinitiator and reacted photoinitiator
materials.
[0275] While this embodiment has been described above primarily
with respect to reactive blocking groups, it will be appreciated
that unreactive blocking groups may be employed as well.
[0276] In addition, while less preferred, it will be appreciated
that processes as described above may also be carried out without a
blocking agent, while still providing dual cure methods and
products of the present invention.
[0277] In addition, while this embodiment has been described
primarily with diol and diamine chain extenders, it will be
appreciated that chain extenders with more than two reactive groups
(polyol and polyamine chain extenders such as triols and triamine
chain extenders) may be used to three dimensional objects comprised
of a crosslinked thermoset polyurethane, polyurea, or copolymer
thereof (e.g., poly(urethane-urea)).
[0278] These materials may be used in bottom-up additive
manufacturing techniques such as the continuous liquid interface
printing techniques described herein, or other additive
manufacturing techniques as noted above and below.
B. Dual Hardening Polymerizable Liquids Employing Blocked
Diisocyanates and Thermally Cleavable Blocking Groups.
[0279] Another embodiment provides a method of forming a
three-dimensional object comprised of polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)), the method
comprising:
[0280] (a) providing a carrier and an optically transparent member
having a build surface, the carrier and the build surface defining
a build region therebetween;
[0281] (b) filling the build region with a polymerizable liquid,
the polymerizable liquid comprising a mixture of (i) a blocked or
reactive blocked diisocyanate, (ii) a polyol and/or polyamine,
(iii) a chain extender, (iv) a photoinitiator, and (v) optionally
but in some embodiments preferably a reactive diluent (vi)
optionally but in some embodiments preferably a pigment or dye,
(vii) optionally but in some embodiments preferably a filler (e.g.
silica),
[0282] (c) irradiating the build region with light through the
optically transparent member to form a solid blocked diisocyanate
scaffold from the blocked diisocyanate, and optionally the reactive
diluent and advancing the carrier away from the build surface to
form a three-dimensional intermediate having the same shape as, or
a shape to be imparted to, the three-dimensional object, with the
intermediate containing the chain extender and polyol and/or
polyamine; and then
[0283] (d) heating or microwave irradiating the three-dimensional
intermediate sufficiently (e.g., sufficiently to de-block the
blocked diisocyanate and form an unblocked diisocyanate that in
turn polymerizes with the chain extender and polyol and/or
polyamine) to form the three-dimensional product comprised of
polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), from the three-dimensional intermediate.
[0284] In some embodiments, the blocked or reactive blocked
diisocyanate is a compound of the formula A'-X'-A', where X' is a
hydrocarbyl group and each A' is an independently selected
substituent of Formula (X'):
##STR00006##
where Z is a blocking group, the blocking group optionally having a
reactive terminal group (e.g., a polymerizable end group such as an
epoxy, alkene, alkyne, or thiol end group, for example an
ethylenically unsaturated end group such as a vinyl ether). In a
particular example, each A' is an independently selected
substituent of Formula (XI'):
##STR00007##
[0285] Other constituents and steps of these methods are carried
out in like manner as described in section 9a above.
[0286] In a non-limiting example, a blocked diisocyanate is
prepared as shown in the Scheme below. Such blocked diisocyanates
may be used in methods as shown in FIG. 25B.
##STR00008##
Without wishing to be bound by any particular underlying mechanism,
in some embodiments, during thermal cure, the blocking agent is
cleaved and the chain extender reacts to form thermoplastic or
thermoset polyurethane, polyurea, or a copolymer thereof (e.g.,
poly(urethane-urea)), for example as shown below:
##STR00009##
[0287] In an alternative mechanism, the chain extender reacts with
the blocked diisocyanate, eliminates the blocking agent, in the
process forming thermoplastic or thermoset polyurethane, polyurea,
or a copolymer thereof (e.g., poly(urethane-urea)).
[0288] In general, a three-dimensional product of the foregoing
methods comprises (i) a linear thermoplastic polyurethane,
polyurea, or copolymer thereof (e.g., poly(urethane-urea)), a(ii)
cross-linked thermoset polyurethane, polyurea, or copolymer thereof
(e.g., poly(urethane-urea)), or (iii) combinations thereof
(optionally blended with de-blocked blocking group which is
copolymerized with the reactive diluents(s), for example as an
interpenetrating polymer network, a semi-interpenetrating polymer
network, or as a sequential interpenetrating polymer network). In
some example embodiments, the three-dimensional product may also
include unreacted photoinitiator remaining in the three-dimensional
formed object. For example, in some embodiments, from 0.1 or 0.2
percent by weight to 1, 2 or 4 percent by weight of the
photoinitiator may remain in the three-dimensional formed object or
the photoinitiator may be present in lower amounts or only a trace
amount. In some example embodiments, the three-dimensional product
may also include reacted photoinitiator fragments. For example, in
some embodiments, the reacted photoinitiator fragments may be
remnants of the first cure forming the intermediate product. For
example, from 0.1 or 0.2 percent by weight to 1, 2 or 4 percent by
weight of reacted photoinitiator fragments may remain in the
three-dimensional formed object or the reacted photoinitiator
fragments may be present in lower amounts or only a trace amount.
In example embodiments, a three-dimensional product may comprise,
consist of or consist essentially of all or any combination of a
linear thermoplastic polyurethane, a cross-linked thermoset
polyurethane, unreacted photoinitiator and reacted photoinitiator
materials.
[0289] While this embodiment has been described above primarily
with respect to reactive blocking groups, it will be appreciated
that unreactive blocking groups may be employed as well.
[0290] In addition, while less preferred, it will be appreciated
that processes as described above may also be carried out without a
blocking agent, while still providing dual cure methods and
products of the present invention.
[0291] In addition, while this embodiment has been described
primarily with diol and diamine chain extenders, it will be
appreciated that chain extenders with more than two reactive groups
(polyol and polyamine chain extenders such as triols and triamine
chain extenders) may be used to three dimensional objects comprised
of a crosslinked thermoset polyurethane, polyurea, or copolymer
thereof (e.g., poly(urethane-urea)).
[0292] These materials may be used in bottom-up additive
manufacturing techniques such as the continuous liquid interface
printing techniques described herein, or other additive
manufacturing techniques as noted above and below.
C. Dual Hardening Polymerizable Liquids Employing Blocked Chain
Extenders and Thermally Cleavable Blocking Groups.
[0293] Another embodiment provides a method of forming a
three-dimensional object comprised of polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)), the method
comprising:
[0294] (a) providing a carrier and an optically transparent member
having a build surface, the carrier and the build surface defining
a build region therebetween;
[0295] (b) filling the build region with a polymerizable liquid,
the polymerizable liquid comprising a mixture of (i) a polyol
and/or polyamine, (ii) a blocked or reactive blocked diisocyanate
chain extender, (iii) optionally one or more additional chain
extenders, (iv) a photoinitiator, and (v) optionally but in some
embodiments preferably a reactive diluent (vi) optionally but in
some embodiments preferably a pigment or dye, (vii) optionally but
in some embodiments preferably a filler (e.g. silica);
[0296] (c) irradiating the build region with light through the
optically transparent member to form a solid blocked chain
diisocyanate chain extender scaffold from the blocked or reactive
blocked diisocyanate chain extender and optionally the reactive
diluent and advancing the carrier away from the build surface to
form a three-dimensional intermediate having the same shape as, or
a shape to be imparted to, the three-dimensional object, with the
intermediate containing the polyol and/or polyamine and optionally
one or more additional chain extenders; and then
[0297] (d) heating or microwave irradiating the three-dimensional
intermediate sufficiently to form the three-dimensional product
comprised of polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), from the three-dimensional intermediate
(e.g., heating or microwave irradiating sufficiently to de-block
the blocked diisocyanate chain extender to form an unblocked
diisocyanate chain extender that in turn polymerizes with the
polyol and/or polyamine and optionally one or more additional chain
extenders).
[0298] In some embodiments, the blocked or reactive blocked
diisocyanate chain extender is a compound of the formula
A''-X''-A'', where X'' is a hydrocarbyl group, and each A'' is an
independently selected substituent of Formula (X''):
##STR00010##
where R is a hydrocarbyl group, R' is O or NH, and Z is a blocking
group, the blocking group optionally having a reactive terminal
group (e.g., a polymerizable end group such as an epoxy, alkene,
alkyne, or thiol end group, for example an ethylenically
unsaturated end group such as a vinyl ether). In a particular
example, each A'' is an independently selected substituent of
Formula (XI''):
##STR00011##
where R and R' are as given above.
[0299] Other constituents and steps employed in carrying out these
methods may be the same as described in section 9A above.
[0300] An example of the preparation of a blocked diol chain
extender is shown in the Scheme below.
##STR00012##
[0301] An example of the preparation of a blocked diamine chain
extender is shown in the Scheme below:
##STR00013##
An example of method of the present invention carried out with the
materials above is given in the FIG. 25C.
[0302] Without wishing to be bound to any underlying mechanism of
the invention, in some embodiments, during thermal cure, (a) the
blocked isocyanate-capped chain extender reacts either directly
with soft segment and/or chain extender amine or alcohol groups,
displacing the blocking agent; or (b) the blocked isocyanate-capped
chain extender is cleaved and diisocyanate-capped chain extender is
re-formed and reacts with soft segments and additional chain
extender if necessary to yield thermoplastic or thermoset
polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), such as follows:
##STR00014##
An alternative mechanism analogous to that described in section B
above may also be implemented or employed.
[0303] In general, a three-dimensional product of the foregoing
methods comprises (i) a linear thermoplastic polyurethane,
polyurea, or copolymer thereof (e.g., poly(urethane-urea)), (ii) a
cross-linked thermoset polyurethane, polyurea, or copolymer thereof
(e.g., poly(urethane-urea)), or (iii) combinations thereof
(optionally blended with de-blocked blocking group which is
copolymerized with the reactive diluents(s), for example as an
interpenetrating polymer network, a semi-interpenetrating polymer
network, or as a sequential interpenetrating polymer network). In
some example embodiments, the three-dimensional product may also
include unreacted photoinitiator remaining in the three-dimensional
formed object. For example, in some embodiments, from 0.1 or 0.2
percent by weight to 1, 2 or 4 percent by weight of the
photoinitiator may remain in the three-dimensional formed object or
the photoinitiator may be present in lower amounts or only a trace
amount. In some example embodiments, the three-dimensional product
may also include reacted photoinitiator fragments. For example, in
some embodiments, the reacted photoinitiator fragments may be
remnants of the first cure forming the intermediate product. For
example, from 0.1 or 0.2 percent by weight to 1, 2 or 4 percent by
weight of reacted photoinitiator fragments may remain in the
three-dimensional formed object or the reacted photoinitiator
fragments may be present in lower amounts or only a trace amount.
In example embodiments, a three-dimensional product may comprise,
consist of or consist essentially of all or any combination of a
linear thermoplastic polyurethane, a cross-linked thermoset
polyurethane, unreacted photoinitiator and reacted photoinitiator
materials.
[0304] While this embodiment has been described above primarily
with respect to reactive blocking groups (that is, blocking groups
containing polymerizable moieties), it will be appreciated that
unreactive blocking groups may be employed as well.
[0305] In addition, while less preferred, it will be appreciated
that processes as described above may also be carried out without a
blocking agent, while still providing dual cure methods and
products of the present invention.
[0306] In addition, while this embodiment has been described
primarily with diol and diamine chain extenders, it will be
appreciated that chain extenders with more than two reactive groups
(polyol and polyamine chain extenders such as triols and triamine
chain extenders) may be used to form three dimensional objects
comprised of a crosslinked thermoset polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)).
[0307] These materials may be used in bottom-up additive
manufacturing techniques such as the continuous liquid interface
printing techniques described herein, or other additive
manufacturing techniques as noted above and below.
[0308] Those skilled in the art will appreciate that systems as
described in Ying and Cheng, Hydrolyzable Polyureas Bearing
Hindered Urea Bonds, JACS 136, 16974 (2014), may be used in
carrying out the methods described herein.
X. Articles Comprised of Interpenetrating Polymer Networks (IPNs)
Formed from Dual Hardening Polymerizable Liquids.
[0309] In some embodiments, polymerizable liquids comprising dual
hardening systems such as described above are useful in forming
three-dimensional articles that in turn comprise interpenetrating
polymer networks. This area has been noted by Sperling at Lehigh
University and K. C. Frisch at the University of Detroit, and
others.
[0310] In non-limiting examples, the polymerizable liquid and
method steps are selected so that the three-dimensional object
comprises the following:
[0311] Sol-Gel Compositions.
[0312] This may be carried out with an amine (ammonia) permeable
window or semipermeable member. In the system discussed here,
tetraethyl orthosilicate (TEOS), epoxy (diglycidyl ether of
Bisphenol A), and 4-amino propyl triethoxysilane are be added to a
free radical crosslinker and in the process the free radical
crosslinker polymerizes and contain the noted reactants which are
then reacted in another step or stage. Reaction requires the
presence of water and acid. Photoacid generators (PAGs) could
optionally be added to the mixture described above to promote the
reaction of the silica based network. Note that if only TEOS is
included one will end up with a silica (glass) network. One could
then increase the temperature to remove the organic phase and be
left with a silica structure that would be difficult to prepare by
more conventional methods. Many variations (different polymeric
structures) can be prepared by this process in addition to epoxies
including urethanes, functionalized polyols, silicone rubber
etc.)
[0313] Hydrophobic-Hydrophilic IPNs.
[0314] Prior IPN research contained a number of examples for
hydrophobic-hydrophilic networks for improved blood compatibility
as well as tissue compatibility for biomedical parts.
Poly(hydroxyethyl(meth)acrylate) is a typical example of a
hydrophilic component. Another option is to added poly(ethylene
oxide)polyols or polyamines with a diisocyanate to produce
polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)), incorporated in the reactive system.
[0315] Phenolic Resins (Resoles).
[0316] Precursors to phenolic resins involve either phenolic
resoles (formaldehyde terminal liquid oligomers) or phenolic
novolacs (phenol terminal solid oligomers crosslinkable with
hexamethyltetraamine). For the present process phenolic resoles can
be considered. The viscosity thereof may be high but dilution with
alcohols (methanol or ethanol) may be employed. Combination of the
phenolic resole with the crosslinkable monomer can then provide a
product formed from an IPN. Reaction of the phenolic resole to a
phenolic resin can occur above 100.degree. in a short time range.
One variation of this chemistry would be to carbonize the resultant
structure to carbon or graphite. Carbon or graphite foam is
typically produced from phenolic foam and used for thermal
insulation at high temperatures.
[0317] Polyimides.
[0318] Polyimides based on dianhydrides and diamines are amenable
to the present process. In this case the polyimide monomers
incorporated into the reactive crosslinkable monomer are reacted to
yield an IPN structure. Most of the dianhydrides employed for
polyimides may be crystalline at room temperature but modest
amounts of a volatile solvent can allow a liquid phase. Reaction at
modest temperatures (e.g., in the range of about 100.degree. C.) is
possible to permit polyimide formation after the network is
polymerized.
[0319] Conductive Polymers.
[0320] The incorporation of aniline and ammonium persulfate into
the polymerizable liquid is used to produce a conductive part.
After the reactive system is polymerized and a post treatment with
acid (such as HCl vapor), polymerization to polyaniline can then
commence.
[0321] Natural Product Based IPNs.
[0322] Numerous of natural product based IPNs are known based on
triglyceride oils such as castor oil. These can be incorporated
into the polymerizable liquid along with a diisocyanate. Upon
completion of the part the triglycerides can then be reacted with
the diisocyanate to form a crosslinked polyurethane. Glycerol can
of course also be used.
[0323] Sequential IPNs.
[0324] In this case, the molded crosslinked network are swollen
with a monomer and free radical catalyst (peroxide) and optionally
crosslinker followed by polymerization. The crosslinked triacylate
system should imbide large amounts of styrene, acrylate and/or
methacrylate monomers allowing a sequential IPN to be produced.
[0325] Polyolefin Polymerization.
[0326] Polyolefin catalysts (e.g. metallocenes) can be added to the
crosslinkable reactive system. Upon exposure of the part to
pressurized ethylene (or propylene) or a combination (to produce
EPR rubber) and temperature in the range of 100.degree. C.) the
part can then contain a moderate to substantial amount of the
polyolefin. Ethylene, propylene and alpha olefin monomers should
easily diffuse into the part to react with the catalyst at this
temperature and as polymerization proceeds more olefin will diffuse
to the catalyst site. A large number of parts can be
post-polymerized at the same time.
XI. Fabrication Products.
A. Example Three-Dimensional (3D) Objects.
[0327] Three-dimensional products produced by the methods and
processes of the present invention may be final, finished or
substantially finished products, or may be intermediate products
subject to further manufacturing steps such as surface treatment,
laser cutting, electric discharge machining, etc., is intended.
Intermediate products include products for which further additive
manufacturing, in the same or a different apparatus, may be carried
out). For example, a fault or cleavage line may be introduced
deliberately into an ongoing "build" by disrupting, and then
reinstating, the gradient of polymerization zone, to terminate one
region of the finished product, or simply because a particular
region of the finished product or "build" is less fragile than
others.
[0328] Numerous different products can be made by the methods and
apparatus of the present invention, including both large-scale
models or prototypes, small custom products, miniature or
microminiature products or devices, etc. Examples include, but are
not limited to, medical devices and implantable medical devices
such as stents, drug delivery depots, functional structures,
microneedle arrays, fibers and rods such as waveguides,
micromechanical devices, microfluidic devices, etc.
[0329] Thus in some embodiments the product can have a height of
from 0.1 or 1 millimeters up to 10 or 100 millimeters, or more,
and/or a maximum width of from 0.1 or 1 millimeters up to 10 or 100
millimeters, or more. In other embodiments, the product can have a
height of from 10 or 100 nanometers up to 10 or 100 microns, or
more, and/or a maximum width of from 10 or 100 nanometers up to 10
or 100 microns, or more. These are examples only: Maximum size and
width depends on the architecture of the particular device and the
resolution of the light source and can be adjusted depending upon
the particular goal of the embodiment or article being
fabricated.
[0330] In some embodiments, the ratio of height to width of the
product is at least 2:1, 10:1, 50:1, or 100:1, or more, or a width
to height ratio of 1:1, 10:1, 50:1, or 100:1, or more.
[0331] In some embodiments, the product has at least one, or a
plurality of, pores or channels formed therein, as discussed
further below.
[0332] The processes described herein can produce products with a
variety of different properties. Hence in some embodiments the
products are rigid; in other embodiments the products are flexible
or resilient. In some embodiments, the products are a solid; in
other embodiments, the products are a gel such as a hydrogel. In
some embodiments, the products have a shape memory (that is, return
substantially to a previous shape after being deformed, so long as
they are not deformed to the point of structural failure). In some
embodiments, the products are unitary (that is, formed of a single
polymerizable liquid); in some embodiments, the products are
composites (that is, formed of two or more different polymerizable
liquids). Particular properties will be determined by factors such
as the choice of polymerizable liquid(s) employed.
[0333] In some embodiments, the product or article made has at
least one overhanging feature (or "overhang"), such as a bridging
element between two supporting bodies, or a cantilevered element
projecting from one substantially vertical support body. Because of
the unidirectional, continuous nature of some embodiments of the
present processes, the problem of fault or cleavage lines that form
between layers when each layer is polymerized to substantial
completion and a substantial time interval occurs before the next
pattern is exposed, is substantially reduced. Hence, in some
embodiments the methods are particularly advantageous in reducing,
or eliminating, the number of support structures for such overhangs
that are fabricated concurrently with the article.
B. Example Structures and Geometries of 3D Objects.
[0334] In example embodiments, the three-dimensional (3D) object
may be formed with thousands or millions of shape variations
imparted on the three-dimensional object while being formed. In
example embodiments, the pattern generator generates different
patterns of light to activate photoinitiator in the region of the
gradient of polymerization to impart different shapes as the object
is extracted through the gradient of polymerization. In example
embodiments, the pattern generator may have high resolution with
millions of pixel elements that can be varied to change the shape
that is imparted. For example, the pattern generator may be a DLP
with more than 1,000 or 2,000 or 3,000 or more rows and/or more
than 1,000 or 2,000 or 3,000 or more columns of micromirrors, or
pixels in an LCD panel, that can be used to vary the shape. As a
result, very fine variations or gradations may be imparted on the
object along its length. In example embodiments, this allows
complex three-dimensional objects to be formed at high speed with a
substantially continuous surface without cleavage lines or seams.
In some examples, more than a hundred, thousand, ten thousand,
hundred thousand or million shape variations may be imparted on the
three-dimensional object being formed without cleavage lines or
seams across a length of the object being formed of more than 1 mm,
1 cm, 10 cm or more or across the entire length of the formed
object. In example embodiments, the object may be continuously
formed through the gradient of polymerization at a rate of more
than 1, 10, 100, 1000, 10000 or more microns per second.
[0335] In example embodiments, this allows complex
three-dimensional (3D) objects to be formed. In some example
embodiments, the 3D formed objects have complex non-injection
moldable shapes. The shapes may not be capable of being readily
formed using injection molding or casting. For example, the shapes
may not be capable of being formed by discrete mold elements that
are mated to form a cavity in which fill material is injected and
cured, such as a conventional two-part mold. For example, in some
embodiments, the 3D formed objects may include enclosed cavities or
partially open cavities, repeating unit cells, or open-cell or
closed-cell foam structures that are not amenable to injection
molding and may including hundreds, thousands or millions of these
structures or interconnected networks of these structures. However,
in example embodiments, these shapes may be 3D formed using the
methods described in the present application with a wide range of
properties, including a wide range of elastomeric properties,
tensile strength and elongation at break through the use of dual
cure materials and/or interpenetrating polymer networks to form
these structures. In example embodiments, the 3D objects may be
formed without cleavage lines, parting lines, seams, sprue, gate
marks or ejector pin marks that may be present with injection
molding or other conventional techniques. In some embodiments, the
3D formed objects may have continuous surface texture (whether
smooth, patterned or rough) that is free from molding or other
printing artifacts (such as cleavage lines, parting lines, seams,
sprue, gate marks or ejector pin marks) across more than 1 mm, 1
cm, 10 cm or more or across the entire length of the formed object.
In example embodiments, complex 3D objects may be formed with no
discrete layers visible or readily detectable from the printing
process in the finished 3D object across more than 1 mm, 1 cm, 10
cm or more or across the entire length of the formed object. For
example, the varying shapes imparted during the course of printing
by the pattern generator may not be visible or detectable as
different layers in the finished 3D object since the printing
occurs through the gradient of polymerization zone (from which the
3D object is extracted as it is exposed by varying patterns
projected from the pattern generator). While the 3D objects
resulting from this process may be referred to as 3D printed
objects, the 3D objects may be formed through continuous liquid
interphase printing without the discrete layers or cleavage lines
associated with some 3D printing processes.
[0336] In some embodiments, the 3D formed object may include one or
more repeating structural elements to form the 3D objects,
including, for example, structures that are (or substantially
correspond to) enclosed cavities, partially-enclosed cavities,
repeating unit cells or networks of unit cells, foam cell, Kelvin
foam cell or other open-cell or closed-cell foam structures,
crisscross structures, overhang structures, cantilevers,
microneedles, fibers, paddles, protrusions, pins, dimples, rings,
tunnels, tubes, shells, panels, beams (including I-beams, U-beams,
W-beams and cylindrical beams), struts, ties, channels (whether
open, closed or partially enclosed), waveguides, triangular
structures, tetrahedron or other pyramid shape, cube, octahedron,
octagon prism, icosidodecahedron, rhombic triacontahedron or other
polyhedral shapes or modules (including Kelvin minimal surface
tetrakaidecahedra, prisms or other polyhedral shapes), pentagon,
hexagonal, octagon and other polygon structures or prisms, polygon
mesh or other three-dimensional structure. In some embodiments, a
3D formed object may include combinations of any of these
structures or interconnected networks of these structures. In an
example embodiments, all or a portion of the structure of the 3D
formed object may correspond (or substantially correspond) to one
or more Bravais lattice or unit cell structures, including cubic
(including simple, body-centered or face-centered), tetragonal
(including simple or body-centered), monoclinic (including simple
or end-centered), orthorhombic (including simple, body-centered,
face-centered or end-centered), rhombohedral, hexagonal and
triclinic structures. In example embodiments, the 3D formed object
may include shapes or surfaces that correspond (or substantially
correspond) to a catenoid, helicoid, gyroid or lidinoid, other
triply periodic minimal surface (TPMS), or other geometry from the
associate family (or Bonnet family) or Schwarz P ("Primitive") or
Schwarz D ("Diamond"), Schwarz H ("Hexagonal") or Schwarz CLP
("Crossed layers of parallels") surfaces, argyle or diamond
patterns, lattice or other pattern or structure.
[0337] In example embodiments, the pattern generator may be
programmed to vary rapidly during printing to impart different
shapes into the gradient of polymerization with high resolution. As
a result, any of the above structural elements may be formed with a
wide range of dimensions and properties and may be repeated or
combined with other structural elements to form the 3D object. In
example embodiments, the 3D formed object may include a single
three-dimensional structure or may include more than 1, 10, 100,
1000, 10000, 100000, 1000000 or more of these structural elements.
The structural elements may be repeated structural elements of
similar shapes or combinations of different structural elements and
can be any of those described above or other regular or irregular
shapes. In example embodiments, each of these structural elements
may have a dimension across the structure of at least 10
nanometers, 100 nanometers, 10 microns, 100 microns, 1 mm, 1 cm, 10
cm, 50 cm or more or may have a dimension across the structure of
less than 50 cm, 10 cm, 1 cm, 1 mm, 100 microns, 10 microns, 100
nanometers or 10 nanometers or less. In example embodiments, a
height, width or other dimension across the structure may be in the
range of from about 10 nanometers to about 50 cm or more or any
range subsumed therein. As used herein, "any range subsumed
therein" means any range that is within the stated range. For
example, the following are all subsumed within the range of about
10 nanometers to about 50 square cm and are included herein: 10
nanometers to 1 micron; 1 micron to 1 millimeter; 1 millimeter to 1
centimeter; and 1 centimeter to 50 cm or any other range or set of
ranges within the stated range. In example embodiments, each of the
structural elements may form a volume of the 3D object in the range
of from about 10 square nanometers to about 50 square cm or more or
any range subsumed therein. In example embodiments, each of the
structural elements may form a cavity or hollow region or gap
between surfaces of the structural element having a dimension
across the cavity or hollow region or gap in the range of from
about 10 nanometers to about 50 cm or more or any range subsumed
therein or may define a volume within the expanse of the 3D formed
object in the range of from about 10 square nanometers to about 50
square cm or more or any range subsumed therein.
[0338] The structural elements may be about the same size or the
size may vary throughout the volume of the 3D formed object. The
sizes may increase or decrease from one side of the 3D formed
object to another side (gradually or step-wise) or elements of
different shapes may be intermixed in regular or irregular patterns
(for example, a 3D elastomeric foam with varying sizes of open-cell
and/or closed-cell cavities intermixed throughout the foam).
[0339] In some embodiments, the 3D formed objects may have
irregular shapes with overhangs, bridging elements or asymmetries
or may otherwise have an offset center of gravity in the direction
being formed. For example, the 3D formed object may be asymmetric.
In example embodiments, the 3D formed object may not have
rotational symmetry around any axis or may have rotational symmetry
only around a single axis. In example embodiments, the 3D formed
object may not have reflectional symmetry around any plane through
the 3D formed object or may have reflectional symmetry only around
a single plane. In example embodiments, the 3D object may have an
offset center of gravity. For example, the center of gravity of the
3D formed object may not be at the positional center of the object.
In some examples, the center of gravity may not be located along
any central axis of the object. For example, the 3D formed object
may be a shoe sole or insert that generally follows the contour of
a foot. The shoe sole or insert may tilt to the right or left and
have different widths for the heel and toes. As a result, the 3D
formed object in this example will not have reflectional symmetry
from side to side or front to back. However, it may have
reflectional symmetry from bottom to top if it is a uniformly flat
shoe sole or insert. In other examples, the shoe sole or insert may
be flat on one side and be contoured to receive the arch of a foot
on the other side and, as a result, will not have reflectional
symmetry from bottom to top either. Other 3D formed objects for
wearable, prosthetic or anatomical shapes or devices may have
similar asymmetries and/or offset center of gravity. For example, a
3D formed object for a dental mold or dental implant may
substantially conform to the shape of a tooth and may not have
reflectional symmetry about any plane. In another example, a 3D
formed component for a wearable device may substantially conform to
the shape of a body party and have corresponding asymmetries, such
as athletic wear such as a right or left contoured shin guard or
foam padding or insert for use between a hard shin guard or a
helmet or other wearable component and the human body. These are
examples only and any number of 3D formed objects may be asymmetric
and/or have an offset center of gravity. In example embodiments,
where there are significant asymmetries or protruding elements
(such as arms, bridging elements, cantilevers, brush fibers or the
like) and the desired structural elements will be elastomeric,
there is a potential for deformation during 3D printing or
subsequent curing. For example, if a large amount of non-UV curable
elastomeric resin material is included, gravity may cause
deformation before final curing. While the scaffold formed from
UV-curable material during 3D printing (from the initial cure in a
dual cure process) helps lock-in the shape, some elastomeric
compositions with highly asymmetric or protruding shapes may be
susceptible to deformation. In some example embodiments, the UV
curable material in the composition may be adjusted to form a more
rigid scaffold to avoid deformation. In other example embodiments,
objects with asymmetric shapes and/or offset center of gravity may
be formed in pairs (or in other combinations) with connectors that
are later removed, particularly if the 3D formed objects or
protruding elements are relatively long. In an example, an
elastomeric 3D object may be formed along a length, and have an
asymmetry, center of gravity offset and/or protruding element
transverse to the length that is more than 10%, 20%, 30%, 40%, 50%
or more of the length. For example, the 3D formed object may have a
length of about 1 cm to 50 cm or more or any range subsumed therein
and may have a transverse or lateral asymmetry or protruding
element of about 1 cm to 50 cm or more or any range subsumed
therein. In an example embodiment, two or more of these objects may
be formed together in a way that provides support for the
transverse or protruding elements until the elastomeric material is
cured and the objects are separated. For example, two shoe soles
may be formed (e.g., when formed in the direction of their length)
as a pair (for example, with rotated and inverted shoe soles formed
together with small removable connectors between them) such that
the soles provide support to one another while being formed. In
other example embodiments, other support structures may be formed
and removed after curing of the elastomeric material.
C. Example Materials and Compositions of 3D Objects.
[0340] In example embodiments, 3D formed objects may have any of
the above shapes or structures and may comprise or consist of or
consist essentially of: (i) a linear thermoplastic polyurethane,
polyurea, or copolymer thereof (e.g., poly(urethane-urea)), (ii) a
cross-linked thermoset polyurethane, polyurea, or copolymer thereof
(e.g., poly(urethane-urea)), and/or (iii) combinations thereof
(optionally blended with de-blocked blocking group which is
copolymerized with the reactive diluents(s), for example as an
interpenetrating polymer network, a semi-interpenetrating polymer
network, or as a sequential interpenetrating polymer network),
and/or (iv) photoinitiator, including unreacted photoinitiator
and/or reacted photoinitiator fragments.
[0341] In some example embodiments, a silicone rubber 3D object may
be formed.
[0342] 1. Silicone Polyurethanes, Polyureas, or
Poly(Urethane-Ureas).
[0343] In any of the preceding polyurethane examples, silicone or
poly(dimethylsiloxane) (PDMS) may be used as soft segment in the
formation of these materials. For example, a
(meth)acrylate-functional ABPU could be formed by first reacting an
oligomeric PDMS diol or diamine with two equivalents of
diisocyanate to form a PDMS urethane prepolymer. This material can
be further reacted with TBAEMA or other reactive blocking agents
described herein to form a reactive blocked PDMS prepolymer which
could be blended with chain extenders and reactive diluents as
described in the examples above.
[0344] 2. Silicone Interpenetrating Polymer Networks.
[0345] In some embodiments, the material may comprise, consists of
or consist essentially of a UV-curable PDMS oligomer that is
blended with a two-part thermally curable PDMS oligomer system.
[0346] In example embodiments, 3D formed objects may have any of
the above shapes or structures and may comprise or consist of or
consist essentially of: [0347] (i) A thermoset silicone or PDMS
network cured by platinum-catalyzed hydrosilation, tin-catalyzed
condensation chemistry, or peroxide initiated chemistry. [0348]
(ii) A UV-curable reactive diluent that is miscible with silicone
thermoset oligomers prior to curing. Example: an
acrylate-functional PDMS oligomer. [0349] (iii) combinations
thereof (optionally blended with reactive diluents(s), for example
as an interpenetrating polymer network, a semi-interpenetrating
polymer network, or as a sequential interpenetrating polymer
network), and/or [0350] (iv) photoinitiator, including unreacted
photoinitiator and/or reacted photoinitiator fragments.
[0351] In an example embodiment, Phenylbis(2 4
6-trimethylbenzoyl)phosphine oxide (PPO) is dissolved in isobornyl
acrylate (IBA) with a THINKY.TM. mixer. Methacryloxypropyl
terminated polydimethylsiloxane (DMS-R31; Gelest Inc.) is added to
the solution, followed by addition of Sylgard Part A and Part B
(Corning PDMS precursors), and then further mixed with a THINKY.TM.
mixer to produce a homogeneous solution. The solution is loaded
into an apparatus as described above and a three-dimensional
intermediate is produced by ultraviolet curing as described above.
The three-dimensional intermediate is then thermally cured at
100.degree. C. for 12 hours to produce the final silicone rubber
product.
[0352] 3. Epoxy Interpenetrating Networks.
[0353] In some example embodiments, an epoxy 3D object may be
formed. In example embodiments, 3D formed objects may have any of
the above shapes or structures and may comprise or consist of or
consist essentially of: [0354] (i) A thermoset epoxy network cured
by the reaction of a diepoxide with a diamine. Optionally,
co-reactants may also be included for example: co-reactants
including polyfunctional amines, acids (and acid anhydrides),
phenols, alcohols, and thiols; [0355] (ii) A UV-curable reactive
diluent that is miscible with the epoxy thermoset precursors prior
to curing; [0356] (iii) (combinations thereof (optionally blended
with the reactive diluents(s), for example as an interpenetrating
polymer network, a semi-interpenetrating polymer network, or as a
sequential interpenetrating polymer network), and/or [0357] (iv)
photoinitiator, including unreacted photoinitiator and/or reacted
photoinitiator fragments.
[0358] In an example embodiment: 10.018 g EpoxAcast 690 resin part
A and 3.040 g part B is mixed on a THINKY.TM. mixer. 3.484 g is
then mixed with 3.013 g of RKP5-78-1, a 65/22/13 mix of Sartomer
CN9782/N-vinylpyrrolidone/diethyleneglycol diacrylate to give a
clear blend which is cured under a Dymax ultraviolet lamp to
produce an elastic 3D object.
[0359] In a second example embodiment, RKP11-10-1 containing 3.517
g of the above epoxy and 3.508 g of RKP5-90-3 and 65/33/2/0.25
blend of Sartomer CN2920/N-vinylcaprolactam/N-vinylpyrrolidone/PPO
initiator is cured similarly to form a flexible 3D object.
[0360] In some example embodiments, the 3D formed object may
include sol-gel compositions, hydrophobic or hydrophilic
compositions, phenolic resoles, cyanate esters, polyimides,
conductive polymers, natural product based IPNs, sequential IPNs
and polyolefin as described above.
[0361] In example embodiments, 3D formed objects may have any of
the shapes or structures described above and may comprise or
consist of or consist essentially of a plurality of different
materials in different regions of the 3D formed object with
different tensile strength or other varying properties. In example
embodiments, the differing materials may be selected from any of
those describe above. In some example embodiments, the process of
fabricating the product may be paused or interrupted one or more
times, to change the polymerizable liquid. In example embodiments,
3D formed objects may include multiple materials (which may, for
example, be a thermoplastic or thermoset polyurethane, polyurea, or
copolymer thereof or silicone rubber or epoxy or combination of the
foregoing) with different tensile strengths as described further
below. While a fault line or plane may be formed in the
intermediate by the interruption, if the subsequent polymerizable
liquid is, in its second cure material, reactive with that of the
first, then the two distinct segments of the intermediate will
cross-react and covalently couple to one another during the second
cure (e.g., by heating or microwave irradiation). Thus, for
example, any of the materials described herein may be sequentially
changed to form a product having multiple distinct segments with
different tensile properties, while still being a unitary product
with the different segments covalently coupled to one another.
[0362] In example embodiments, the polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) or silicone rubber or
epoxy or combination of the foregoing may comprise a majority of
the 3D formed object by weight and may comprise more than 50%, 60%,
70%, 80% or 90% of the 3D formed object by weight. In example
embodiments, the polyurethane, polyurea, or copolymer thereof
(e.g., poly(urethane-urea)) or silicone rubber or epoxy or
combination of the foregoing may comprise or consist of or consist
essentially of an interpenetrating network, a semi-interpenetrating
polymer network, or as a sequential interpenetrating polymer
network.
[0363] (i) Examples of Thermoplastic or Thermoset Polyurethane,
Polyurea, or Copolymer Thereof (e.g., Poly(Urethane-Urea)).
[0364] In example embodiments, the polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) may comprise a
majority of the 3D formed object by weight and may comprise more
than 50%, 60%, 70%, 80% or 90% of the 3D formed object by
weight.
[0365] In example embodiments, the polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) may comprise or
consist of or consist essentially of linear thermoplastic or
thermoset polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)). In example embodiments, the linear
thermoplastic or cross-linked thermoset polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) may comprise a
majority of the 3D formed object by weight and may comprise more
than 50%, 60%, 70%, 80% or 90% of the 3D formed object by
weight.
[0366] In example embodiments, the polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) may comprise or
consist of or consist essentially of a polymer blend of (i) linear
ethylenically unsaturated blocking monomer copolymerized with
reactive diluent and (ii) linear thermoplastic or cross-linked
thermoset polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)). In example embodiments, the polymer blend may
comprise a majority of the 3D formed object by weight and may
comprise more than 50%, 60%, 70%, 80% or 90% of the 3D formed
object by weight. In example embodiments, the linear thermoplastic
or cross-linked polyurethane, polyurea, or copolymer thereof (e.g.,
poly(urethane-urea)) may comprise or consist of or consist
essentially of linear poly(meth)acrylate.
[0367] In example embodiments, the polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) may comprise or
consist of or consist essentially of an interpenetrating network, a
semi-interpenetrating polymer network, or as a sequential
interpenetrating polymer network of ethylenically unsaturated
monomer and crosslinked or linear polyurethane. In example
embodiments, the network of ethylenically unsaturated monomer and
crosslinked polyurethane may comprise a majority of the 3D formed
object by weight and may comprise more than 50%, 60%, 70%, 80% or
90% of the 3D formed object by weight. In example embodiments, the
linear thermoplastic or cross-linked thermoset polyurethane,
polyurea, or copolymer thereof (e.g., poly(urethane-urea)) may
comprise or consist of or consist essentially of crosslinked
poly(meth)acrylate.
[0368] In example embodiments, the polyurethane, polyurea, or
copolymer thereof (e.g., poly(urethane-urea)) may comprise or
consist of or consist essentially of an interpenetrating network, a
semi-interpenetrating polymer network, or as a sequential
interpenetrating polymer network of ethylenically unsaturated
monomer and linear thermoplastic or cross-linked thermoset
polyurethane. In example embodiments, the network of ethylenically
unsaturated monomer and linear thermoplastic or crosslinked
thermoset polyurethane may comprise a majority of the 3D formed
object by weight and may comprise more than 50%, 60%, 70%, 80% or
90% of the 3D formed object by weight. In example embodiments, the
linear thermoplastic or cross-linked thermoset polyurethane,
polyurea, or copolymer thereof (e.g., poly(urethane-urea)) may
comprise or consist of or consist essentially of linear
poly(meth)acrylate.
[0369] In some example embodiments, the 3D formed object may
include sol-gel compositions, hydrophobic or hydrophilic
compositions, phenolic resoles, cyanate esters, polyimides,
conductive polymers, natural product based IPNs, sequential IPNs
and polyolefin as described above.
[0370] (ii) Example Photoinitiator and Photoinitiator
Fragments.
[0371] In example embodiments, the 3D formed object may include
unreacted photoinitiator remaining in the 3D formed object. For
example, in some embodiments, from 0.1 or 0.2 percent by weight to
1, 2 or 4 percent by weight of the photoinitiator may remain in the
three-dimensional formed object or the photoinitiator may be
present in lower amounts or only a trace amount. In some example
embodiments, the three-dimensional product may also include reacted
photoinitiator fragments. For example, in some embodiments, the
reacted photoinitiator fragments may be remnants of the first cure
forming the intermediate product. For example, from 0.1 or 0.2
percent by weight to 1, 2 or 4 percent by weight of reacted
photoinitiator fragments may remain in the three-dimensional formed
object or the reacted photoinitiator fragments may be present in
lower amounts or only a trace amount.
[0372] In example embodiments, because the systems, in part,
consist of monomers and oligomers capable of being polymerized by
exposure to UV light, the end products will contain residual
photoinitiator molecules and photoiniator fragments.
[0373] In some embodiments, a photopolymerization will undergo the
transformation outlined below. In the first step, initiation, UV
light cleaves the initiator into active radical fragments. These
active radical fragments will go on to react with monomer group
"M." During the propagation step, the active monomer will react
with additional monomers that attach to the growing polymer chain.
Finally, termination can occur either by recombination or by
disproportionation.
[0374] Initiation [0375] Initiator+h.sub.v.fwdarw.R' [0376]
R'+M.fwdarw.RM'
[0377] Propagation [0378] RM'+M.sub.n.fwdarw.RM.sub.n+1'
[0379] Termination [0380] combination [0381]
RM.sub.n'+'M.sub.mR.fwdarw.RM.sub.nM.sub.mR [0382]
disproportionation [0383]
RM.sub.n'+'M.sub.mR.fwdarw.RM.sub.n+M.sub.mR
[0384] In example embodiments, 3D formed objects generated by the
processes outlined herein may contain the following chemical
products after the object is created: [0385] (1) Latent unreacted
photoinitiator--photoinitiator is rarely 100% consumed during
photopolymerization, therefore the product will typically contain
unreacted photoinitiators embedded throughout the solid object:
[0386] (2) Photoinitiator by-products covalently attached to the
polymer network.
[0387] In example embodiments, photoinitiators may include the
following:
[0388] (a) Benzoyl-Chromophore Based:
[0389] These systems take the form
##STR00015##
where "R" is any number of other atoms, including H, O, C, N, S.
These initiators cleave to form:
##STR00016##
Where represents a free radical. Either of these components may go
on to initiate polymerization and will therefore be covalently
bound to the polymer network.
##STR00017##
An example of such an initiator is shown below
##STR00018##
[0390] (b) Morpholino and Amino Ketones.
[0391] These systems take the form:
##STR00019##
where "R" is any number of other atoms including H, 0, C, N, S.
These initiators cleave to form
##STR00020##
Where represents a free radical. Either of these components may go
on to initiate polymerization and will therefore be covalently
bound to the polymer network.
##STR00021##
An example of such an initiator is shown below
##STR00022##
[0392] (c) Benzoyl Phosphine Oxide.
[0393] These systems take the form
##STR00023##
where "R" is any number of other atoms including H, O, C, N, S.
These initiators cleave to form
##STR00024##
Where represents a free radical. Either of these components may go
on to initiate polymerization and will therefore be covalently
bound to the polymer network.
##STR00025##
An example of such an initiator is shown below
##STR00026##
[0394] (d) Amines.
[0395] Many photoinitiators may be used in combination with amines.
Here the photoinitiators in the excited state serve to abstract a
hydrogen atom from the amine, thus generating an active radical.
This radical can go on to initiator polymerization and will
therefore become incorporated into the formed polymer network. This
process is outlined below:
##STR00027##
Either of these active species can go on to form an active polymer
chain resulting in the structures below:
##STR00028##
[0396] (e) Other Systems.
[0397] Other types of photoinitiators that may be used to generate
such materials and therefore will generate fragments which are
covalently attached to the formed polymer network include:
triazines, ketones, peroxides, diketones, azides, azo derivatives,
disulfide derivatives, disilane derivatives, thiol derivatives,
diselenide derivatives, diphenylditelluride derivatives, digermane
derivatives, distannane derivatives, carob-germanium compounds,
carbon-silicon derivatives, sulfur-carbon derivatives,
sulfur-silicon derivatives, peresters, Barton's ester derivatives,
hydroxamic and thiohydroxamic acids and esters, organoborates,
organometallic compounds, titanocenes, chromium complexes, alumate
complexes, carbon-sulfur or sulfur-sulfur iniferter compounds,
oxyamines, aldehydes, acetals, silanes, phosphorous-containing
compounds, borane complexes, thioxanthone derivatives, coumarins,
anthraquinones, fluorenones, ferrocenium salts.
[0398] (f) Detection.
[0399] Detection of the unique chemical fingerprint of
photoinitiator fragments in a cured polymer object can be
accomplished by a number of spectroscopic techniques. Particular
techniques useful alone or in combination include: UV-Vis
spectroscopy, fluorescence spectroscopy, infrared spectroscopy,
nuclear magnetic resonance spectroscopy, mass spectrometry, atomic
absorption spectroscopy, raman spectroscopy, and X-Ray
photoelectron spectroscopy.
D. Example Properties of 3D Objects.
[0400] The structural properties of the 3D formed object may be
selected together with the properties of the materials from which
the 3D object is formed to provide a wide range of properties for
the 3D object. Dual cure materials and methods described above in
the present application may be used to form complex shapes with
desired materials properties to form a wide range of 3D
objects.
[0401] In some embodiments, 3D formed objects may be rigid and
have, for example, a Young's modulus (MPa) in the range of about
800 to 3500 or any range subsumed therein, a Tensile Strength (MPa)
in the range of about 30 to 100 or any range subsumed therein,
and/or a percent elongation at break in the range of about 1 to 100
or any range subsumed therein. Non-limiting examples of such rigid
3D formed objects may include fasteners; electronic device
housings; gears, propellers, and impellers; wheels, mechanical
device housings; tools and other rigid 3D objects.
[0402] In some embodiments, 3D formed objects may be semi-rigid and
have, for example, a Young's modulus (MPa) in the range of about
300-2500 or any range subsumed therein, a Tensile Strength (MPa) in
the range of about 20-70 or any range subsumed therein, and/or a
percent elongation at break in the range of about 40 to 300 or 600
or any range subsumed therein. Non-limiting examples of such rigid
3D formed objects may include structural elements; hinges including
living hinges; boat and watercraft hulls and decks; wheels;
bottles, jars and other containers; pipes, liquid tubes and
connectors and other semi-rigid 3D objects.
[0403] In some embodiments, 3D formed objects may be elastomeric
and have, for example, a Young's modulus (MPa) in the range of
about 0.5-40 or any range subsumed therein, a Tensile Strength
(MPa) in the range of about 0.5-30 or any range subsumed therein,
and/or a percent elongation at break in the range of about 50-1000
or any range subsumed therein. Non-limiting examples of such rigid
3D formed objects may include foot-wear soles, heels, innersoles
and midsoles; bushings and gaskets; cushions; electronic device
housings and other elastomeric 3D objects.
[0404] In examples 18-61 are given materials for the formation of
polyurethane products having a variety of different tensile
properties, ranging from elastomeric, to semi-rigid, to flexible,
as described above.
[0405] In some example embodiments, the process of fabricating the
product may be paused or interrupted one or more times, to change
the polymerizable liquid. In example embodiments, 3D formed objects
may include multiple materials (which may, for example, be a
thermoplastic or thermoset polyurethane, polyurea, or copolymer
thereof) with different tensile strengths. While a fault line or
plane may be formed in the intermediate by the interruption, if the
subsequent polymerizable liquid is, in its second cure material,
reactive with that of the first, then the two distinct segments of
the intermediate will cross-react and covalently couple to one
another during the second cure (e.g., by heating or microwave
irradiation). Thus, for example, any of the materials described
herein may be sequentially changed to form a product having
multiple distinct segments with different tensile properties, while
still being a unitary product with the different segments
covalently coupled to one another. In some embodiments, a 3D object
may be formed with a plurality of regions with different materials
and properties. For example, a 3D formed object could have one or
more regions formed from a first material or first group of one or
more materials having a Tensile Strength (MPa) in the range of
about 30-100 or any range subsumed therein, and/or one or more
regions formed from a second material or second group of one or
more materials having a Tensile Strength (MPa) in the range of
about 20-70 or any range subsumed therein and/or one or more
regions formed from a third material or third group of one or more
materials having a Tensile Strength (MPa) in the range of about
0.5-30 or any range subsumed therein or any combination of the
foregoing. For example, the 3D object could have from 1-10 or more
different regions (or any range subsumed therein) with varying
tensile strength selected from any of the materials and tensile
strengths described above. For example, a hinge can be formed, with
the hinge comprising a rigid segment, coupled to a second elastic
segment, coupled to a third rigid segment, by sequentially changing
polymerizable liquids (e.g., from among those described in examples
19-60 above) during the formation of the three-dimensional
intermediate. A shock absorber or vibration dampener can be formed
in like manner, with the second segment being either elastic or
semi-rigid. A unitary rigid funnel and flexible hose assembly can
be formed in like manner.
E. Additional Examples of 3D Objects.
[0406] The above methods, structures, materials, compositions and
properties may be used to 3D print a virtually unlimited number of
products. Examples include, but are not limited to, medical devices
and implantable medical devices such as stents, drug delivery
depots, catheters, bladder, breast implants, testicle implants,
pectoral implants, eye implants, contact lenses, dental aligners,
microfluidics, seals, shrouds, and other applications requiring
high biocompatibility, functional structures, microneedle arrays,
fibers, rods, waveguides, micromechanical devices, microfluidic
devices; fasteners; electronic device housings; gears, propellers,
and impellers; wheels, mechanical device housings; tools;
structural elements; hinges including living hinges; boat and
watercraft hulls and decks; wheels; bottles, jars and other
containers; pipes, liquid tubes and connectors; foot-ware soles,
heels, innersoles and midsoles; bushings, o-rings and gaskets;
shock absorbers, funnel/hose assembly, cushions; electronic device
housings; shin guards, athletic cups, knee pads, elbow pads, foam
liners, padding or inserts, helmets, helmet straps, head gear, shoe
cleats, gloves, other wearable or athletic equipment, brushes,
combs, rings, jewelry, buttons, snaps, fasteners, watch bands or
watch housings, mobile phone or tablet casings or housings,
computer keyboards or keyboard buttons or components, remote
control buttons or components, auto dashboard components, buttons,
dials, auto body parts, paneling, other automotive, aircraft or
boat parts, cookware, bakeware, kitchen utensils, steamers and any
number of other 3D objects. The universe of useful 3D products that
may be formed is greatly expanded by the ability to impart a wide
range of shapes and properties, including elastomeric properties,
through the use of multiple methods of hardening such as dual cure
where a shape can be locked-in using continuous liquid interphase
printing and subsequent thermal or other curing can be used to
provide elastomeric or other desired properties. Any of the above
described structures, materials and properties can be combined to
form 3D objects including the 3D formed products described above.
These are examples only and any number of other 3D objects can be
formed using the methods and materials described herein.
XII. Alternate Methods and Apparatus.
[0407] While the present invention is preferably carried out by
continuous liquid interphase/interface polymerization, as described
in detail above and in further detail below, in some embodiments
alternate methods and apparatus for bottom-up or top down
three-dimension fabrication may be used, including layer-by-layer
fabrication. Examples of such methods and apparatus include, but
are not limited to, those described in U.S. Pat. No. 5,236,637 to
Hull, U.S. Pat. Nos. 5,391,072 and 5,529,473 to Lawton, U.S. Pat.
No. 7,438,846 to John, U.S. Pat. No. 7,892,474 to Shkolnik, U.S.
Pat. No. 8,110,135 to El-Siblani, U.S. Patent Application
Publication Nos. 2013/0292862 to Joyce and 2013/0295212 to Chen et
al., and PCT Application Publication No. WO 2015/164234 to Robeson
et al. The disclosures of these patents and applications are
incorporated by reference herein in their entirety.
[0408] Elements and features that may be used in carrying out the
present invention are explained in PCT Applications Nos.
PCT/US2014/015486 (published as U.S. Pat. No. 9,211,678 on Dec. 15,
2015); PCT/US2014/015506 (also published as U.S. Pat. No. 9,205,601
on Dec. 8, 2015), PCT/US2014/015497 (also published as US
2015/0097316, and to publish as U.S. Pat. No. 9,216,546 on Dec. 22,
2015), and in J. Tumbleston, D. Shirvanyants, N. Ermoshkin et al.,
Continuous liquid interface production of 3D Objects, Science 347,
1349-1352 (published online 16 Mar. 2015).
[0409] Embodiments of the present invention are explained in
greater detail in the following non-limiting examples.
Example 1
High Aspect Ratio Adjustable Tension Build Plate Assembly
[0410] FIG. 6 is a top view and FIG. 7 is an exploded view of a 3
inch by 16 inch "high aspect" rectangular build plate (or "window")
assembly of the present invention, where the film dimensions are
3.5 inches by 17 inches. The greater size of the film itself as
compared to the internal diameter of vat ring and film base
provides a peripheral or circumferential flange portion in the film
that is clamped between the vat ring and the film base, as shown in
side-sectional view in FIG. 8. One or more registration holes (not
shown) may be provided in the polymer film in the peripheral or
circumferential flange portion to aid in aligning the polymer film
between the vat ring and film base, which are fastened to one
another with a plurality of screws (not shown) extending from one
to the other (some or all passing through holes in the peripheral
edge of the polymer film) in a manner that securely clamps the
polymer film therebetween.
[0411] As shown in FIGS. 7-8 a tension ring is provided that abuts
the polymer film and stretches the film to tension, stabilize or
rigidify the film. The tension ring may be provided as a pre-set
member, or may be an adjustable member. Adjustment may be achieved
by providing a spring plate facing the tension ring, with one or
more compressible elements such as polymer cushions or springs
(e.g., flat springs, coil springs, wave springs etc.) therebetween,
and with adjustable fasteners such as screw fasteners or the like
passing from the spring plate through (or around) the tension ring
to the film base.
[0412] Polymer films are preferably fluoropolymer films, such as an
amorphous thermoplastic fluoropolymer, in a thickness of 0.01 or
0.05 millimeters to 0.1 or 1 millimeters, or more. In some
embodiments we use Biogeneral Teflon AF 2400 polymer film, which is
0.0035 inches (0.09 millimeters) thick, and Random Technologies
Teflon AF 2400 polymer film, which is 0.004 inches (0.1
millimeters) thick.
[0413] Tension on the film is preferably adjusted with the tension
ring to about 10 to 100 pounds, depending on operating conditions
such as fabrication speed.
[0414] The vat ring, film base, tension ring, and tension ring
spring plate may be fabricated of any suitable, preferably rigid,
material, including metals (e.g., stainless steel, aluminum and
aluminum alloys), carbon fiber, polymers, and composites
thereof.
[0415] Registration posts and corresponding sockets may be provided
in any of the vat ring, film base, tension ring and/or spring
plate, as desired.
Example 2
Round Adjustable Tension Round Build Plate Assembly
[0416] FIG. 9 is a top view and FIG. 10 is an exploded view of a
2.88 inch diameter round build plate of the invention, where the
film dimension may be 4 inches in diameter. Construction is in like
manner to that given in Example 1 above, with a circumferential
wave spring assembly shown in place. Tension on the film preferably
adjusted to a like tension as given in Example 1 above (again
depending on other operating conditions such as fabrication
speed).
[0417] FIG. 10 is an exploded view of the build plate of FIG.
8.
Example 3
Additional Embodiments of Adjustable Build Plates
[0418] FIG. 11 shows various alternate embodiments of the build
plates of FIGS. 7-10. Materials and tensions may be in like manner
as described above.
Example 4
Example Embodiment of an Apparatus
[0419] FIG. 12 is a front perspective view, FIG. 13 is a side view
and FIG. 14 is a rear perspective view of an apparatus 100
according to an exemplary embodiment of the invention. The
apparatus 100 includes a frame 102 and an enclosure 104. Much of
the enclosure 104 is removed or shown transparent in FIGS.
12-14.
[0420] The apparatus 100 includes several of the same or similar
components and features as the apparatus described above in
reference to FIG. 2. Referring to FIG. 12, a build chamber 106 is
provided on a base plate 108 that is connected to the frame 102.
The build chamber 106 is defined by a wall or vat ring 110 and a
build plate or "window" such as one of the windows described above
in reference to FIGS. 2 and 6-11.
[0421] Turning to FIG. 13, a carrier 112 is driven in a vertical
direction along a rail 114 by a motor 116. The motor may be any
suitable type of motor, such as a servo motor. An exemplary
suitable motor is the NXM45A motor available from Oriental Motor of
Tokyo, Japan.
[0422] A liquid reservoir 118 is in fluid communication with the
build chamber 106 to replenish the build chamber 106 with liquid
resin. For example, tubing may run from the liquid reservoir 118 to
the build chamber 106. A valve 120 controls the flow of liquid
resin from the liquid reservoir 118 to the build chamber 106. An
exemplary suitable valve is a pinch-style aluminum solenoid valve
for tubing available from McMaster-Carr of Atlanta, Ga.
[0423] The frame 102 includes rails 122 or other some other
mounting feature on which a light engine assembly 130 (FIG. 15) is
held or mounted. A light source 124 is coupled to the light engine
assembly 130 using a light guide entrance cable 126. The light
source 124 may be any suitable light source such as a BlueWave.RTM.
200 system available from Dymax Corporation of Torrington,
Conn.
[0424] Turning to FIG. 15, the light engine or light engine
assembly 130 includes condenser lens assembly 132 and a digital
light processing (DLP) system including a digital micromirror
device (DMD) 134 and an optical or projection lens assembly 136
(which may include an objective lens). A suitable DLP system is the
DLP Discovery.TM. 4100 system available from Texas Instruments,
Inc. of Dallas, Tex. Light from the DLP system is reflected off a
mirror 138 and illuminates the build chamber 106. Specifically, an
"image" 140 is projected at the build surface or window.
[0425] Referring to FIG. 14, an electronic component plate or
breadboard 150 is connected to the frame 102. A plurality of
electrical or electronic components are mounted on the breadboard
150. A controller or processor 152 is operatively associated with
various components such as the motor 116, the valve 120, the light
source 124 and the light engine assembly 130 described above. A
suitable controller is the Propeller Proto Board available from
Parallax, Inc. of Rocklin, Calif.
[0426] Other electrical or electronic components operatively
associated with the controller 152 include a power supply 154 and a
motor driver 158 for controlling the motor 116. In some
embodiments, an LED light source controlled by pulse width
modulation (PWM) driver 156 is used instead of a mercury lamp
(e.g., the Dymax light source described above).
[0427] A suitable power supply is a 24 Volt, 2.5 A, 60 W, switching
power supply (e.g., part number PS1-60W-24 (HF60W-SL-24) available
from Marlin P. Jones & Assoc, Inc. of Lake Park, Fla.). If an
LED light source is used, a suitable LED driver is a 24 Volt, 1.4 A
LED driver (e.g., part number 788-1041-ND available from Digi-Key
of Thief River Falls, Minn.). A suitable motor driver is the
NXD20-A motor driver available from Oriental Motor of Tokyo,
Japan.
[0428] The apparatus of FIGS. 12-15 has been used to produce an
"image size" of about 75 mm by 100 mm with light intensity of about
5 mW/cm.sup.2. The apparatus of FIGS. 12-15 has been used to build
objects at speeds of about 100 to 500 mm/hr. The build speed is
dependent on light intensity and the geometry of the object.
Example 5
Another Example Embodiment of an Apparatus
[0429] FIG. 16 is a front perspective view of an apparatus 200
according to another exemplary embodiment of the invention. The
apparatus 200 includes the same components and features of the
apparatus 100 with the following differences.
[0430] The apparatus 200 includes a frame 202 including rails 222
or other mounting feature at which two of the light engine
assemblies 130 shown in FIG. 15 may be mounted in a side-by-side
relationship. The light engine assemblies 130 are configured to
provide a pair of "tiled" images at the build station 206. The use
of multiple light engines to provide tiled images is described in
more detail above.
[0431] The apparatus of FIG. 16 has been used to provide a tiled
"image size" of about 150 mm by 200 mm with light intensity of
about 1 mW/cm.sup.2. The apparatus of FIG. 16 has been used to
build objects at speeds of about 50 to 100 mm/hr. The build speed
is dependent on light intensity and the geometry of the object.
Example 6
Another Example Embodiment of an Apparatus
[0432] FIG. 18 is a front perspective view and FIG. 19 is a side
view of an apparatus 300 according to another exemplary embodiment
of the invention. The apparatus 300 includes the same components
and features of the apparatus 100 with the following
differences.
[0433] The apparatus 300 includes a frame 302 including rails 322
or other mounting feature at which a light engine assembly 330
shown in FIG. 20 may be mounted in a different orientation than the
light assembly 130 of the apparatus 100. Referring to FIGS. 19 and
20, the light engine assembly 330 includes a condenser lens
assembly 332 and a digital light processing (DLP) system including
a digital micromirror device (DMD) 334 and an optical or projection
lens assembly 336 (which may include an objective lens). A suitable
DLP system is the DLP Discovery.TM. 4100 system available from
Texas Instruments, Inc. of Dallas, Tex. Light from the DLP system
illuminates the build chamber 306. Specifically, an "image" 340 is
projected at the build surface or window. In contrast to the
apparatus 100, a reflective mirror is not used with the apparatus
300.
[0434] The apparatus of FIGS. 18-20 has been used to provide "image
sizes" of about 10.5 mm by 14 mm and about 24 mm by 32 mm with
light intensity of about 200 mW/cm.sup.2 and 40 mW/cm.sup.2 The
apparatus of FIGS. 18-20 has been used to build objects at speeds
of about 10,000 and 4,000 mm/hr. The build speed is dependent on
light intensity and the geometry of the object.
Example 7
Control Program with Lua Scripting
[0435] Current printer technology requires low level control in
order to ensure quality part fabrication. Physical parameters such
as light intensity, exposure time and the motion of the carrier
should all be optimized to ensure the quality of a part. Utilizing
a scripting interface to a controller such as the Parallax
PROPELLER.TM. microcontroller using the programming language "Lua"
provides the user with control over all aspects of the printer on a
low level. See generally R. Ierusalimschy, Programming in Lua
(2013) (ISBN-10: 859037985X; ISBN-13: 978-8590379850).
[0436] This Example illustrates the control of a method and
apparatus of the invention with an example program written
utilizing Lua scripting. Program code corresponding to such
instructions, or variations thereof that will be apparent to those
skilled in the art, is written in accordance with known techniques
based upon the particular microcontroller used.
[0437] Concepts.
[0438] A part consists of slices of polymer which are formed
continuously. The shape of each slice is defined by the frame that
is being displayed by the light engine.
[0439] Frame.
[0440] The frame represents the final output for a slice. The frame
is what manifests as the physical geometry of the part. The data in
the frame is what is projected by the printer to cure the
polymer.
[0441] Slice.
[0442] All the 2D geometry that will be outputted to a frame should
be combined in a Slice. Slices can consist of procedural geometry,
Slices of a 3D model or any combination of the two. The slice
generating process allows the user to have direct control over the
composition of any frame.
[0443] Slice of a 3D Model.
[0444] A slice is a special type of 2D geometry derived from a 3D
model of a part. It represents the geometry that intersects a plane
that is parallel to the window. Parts are usually constructed by
taking 3D models and slicing them at very small intervals. Each
slice is then interpreted in succession by the printer and used to
cure the polymer at the proper height.
[0445] Procedural Geometry.
[0446] Procedurally generated geometry can also be added to a
slice. This is accomplished by invoking shape generation functions,
such as "addcircle", "addrectangle", and others. Each function
allows projection of the corresponding shape onto the printing
window. A produced part appears as a vertically extruded shape or
combination of shapes.
[0447] Coordinate Spaces: Stage.
[0448] The coordinate system that the stage uses is usually
calibrated such that the origin is 1-20 microns above the
window.
[0449] Coordinate Spaces: Slice.
[0450] Coordinate system of the projected slice is such that origin
is located at the center of the print window.
Quick Start.
[0451] The following is the most basic method of printing a part
from a sliced 3D model. Printing a sliced model consists of 4 main
parts: Loading the data, preparing the printer, printing, and
shutdown.
[0452] Loading Data.
[0453] In this section of the code the sliced model data is loaded
into memory. The file path to the model is defined in the Constants
section of the code. See the full code below for details.
TABLE-US-00001 --Loading Model modelFilePath = "Chess King.svg"
numSlices = loadslices(modelFilePath)
Preparing the printer it is important to do two things before
printing. You must first turn on the light engine with the relay
function, and if applicable, the desired fluid height should be
set.
TABLE-US-00002 --Prepare Printer relay(true)--turn light on
showframe(-1) --ensure nothing is exposed durring setup
setlevels(.55, .6)--if available, printer set fluid pump to
maintain about 55% fill
[0454] Printing.
[0455] The first step of the printing process is to calibrate the
system and set the stage to its starting position by calling
gotostart. Next we begin a for loop in which we print each slice.
The first line of the for loop uses the infoline command to display
the current slice index in the sidebar. Next we determine the
height at which the next slice should be cured. That value is
stored to nextHeight. Following this we move the stage to the
height at which the next slice needs to be cured. To ensure a clean
print it can sometimes be necessary to wait for oxygen to diffuse
into the resin. Therefore we call sleep for a half second (the
exact time for preExposureTime is defined in the constants section
as well). After this it's time to actually cure the resin so we
call showframe and pass it the index of the slice we want to print,
which is stored in sliceIndex by the for loop. We sleep again after
this for exposureTime seconds in order to let the resin cure.
Before moving on to the next frame, we call showframe(-1) in order
to prevent the light engine from curing any resin while the stage
is moving to the next height.
TABLE-US-00003 --Execute Print gotostart( )--move stage to starting
position for sliceIndex =0,numSlices-1 do infoline(5,
string.format("Current Slice: %d", sliceIndex)) nextHeight =
sliceheight(sliceIndex)--calculate the height that the stage should
be at to expose this frame moveto(nextHeight, stageSpeed)--move to
nextHeight sleep(preExposureTime)--wait a given amount of time for
oxygen to diffuse into resin , prepExposureTime is predefined in
the Constants section showframe(sliceIndex)--show frame to expose
sleep(exposureTime)--wait while frame exposes, exposureTime is
predefined in the Constants section showframe(-1)-- show nothing to
ensure no exposure while stage is moving to next position end
Shutdown.
[0456] The final step in the printing process is to shut down the
printer. Call relay(false) to turn the light engine off. If you are
using fluid control, call setlevels(0,0) to ensure the valve is
shut off. Finally it is a good idea to move the stage up a bit
after printing to allow for easy removal of the part.
TABLE-US-00004 --Shutdown relay(false) setlevels(0,0) --Lift stage
to remove part moveby(25, 16000)
Fully completed code implementing instructions based on the above
is set forth below.
TABLE-US-00005 --Constants exposureTime = 1.5-- in seconds
preExposureTime = 0.5 -- in seconds stageSpeed = 300 --in mm/hour
--Loading Model modelFilePath = "Chess King.svg" numSlices =
loadslices(modelFilePath) --calculating parameters maxPrintHeight =
sliceheight(numSlices-1)--find the highest point in the print, this
is the same as the height of the last slice. Slices are 0 indexed,
hence the -1. infoline(1, "Current Print Info:") infoline(2,
string.format("Calculated Max Print Height: %dmm", maxPrintHeight))
infoline(3, string.format("Calculated Est. Time: %dmin",
(maxPrintHeight/stageSpeed)*60 +
(preExposureTime+exposureTime)*numSlices/60)) infoline(4,
string.format("Number of Slices: %d", numSlices)) --Prepare Printer
relay(true)--turn light on showframe(-1) --ensure nothing is
exposed durring setup setlevels(.55, .6)--if available, printer set
fluid pump to maintain about 55% fill --Execute Print gotostart(
)--move stage to starting position for sliceIndex =0,numSlices-1 do
infoline(5, string.format("Current Slice: %d", sliceIndex))
nextHeight = sliceheight(sliceIndex)--calculate the height that the
stage should be at to expose this frame moveto(nextHeight,
stageSpeed)--move to nextHeight sleep(preExposureTime)--wait a
given amount of time for oxygen to diffuse into resin ,
prepExposureTime is predefined in the Constants section
showframe(sliceIndex)--show frame to expose
sleep(exposureTime)--wait while frame exposes, exposureTime is
predefined in the Constants section showframe(-1)-- show nothing to
ensure no exposure while stage is moving to next position end
--Shutdown relay(false) setlevels(0,0) --Lift stage to remove part
moveby(25, 16000)
[0457] Gotostart.
[0458] The main purpose of gotostart is to calibrate the stage.
This function resets the coordinate system to have the origin at
the lowest point, where the limit switch is activated. Calling this
command will move the stage down until the limit switch in the
printer is activated; this should occur when the stage is at the
absolute minimum height.
gotostart( ) moves stage to start at the maximum speed which varies
from printer to printer. gotostart( )--moving to origin at default
speed gotostart(number speed) moves stage to start at speed given
in millimeters/hour. gotostart(15000)--moving stage to origin at
15000 mm/hr
[0459] speed: speed, in mm/hour, at which the stage will move to
the start position.
Moveto
[0460] moveto allows the user to direct the stage to a desired
height at a given speed. Safe upper and lower limits to speed and
acceleration are ensured internally.
moveto(number targetHeight, number speed) moveto(25, 15000)--moving
to 25 mm at 15,000 mm/hr moveto(number targetHeight, number speed,
number acceleration) This version of the function allows an
acceleration to be defined as well as speed. The stage starts
moving at initial speed and then increases by acceleration. [0461]
moveto(25, 20000, 1e7)--moving the stage to 25 mm at 20,000 mm/hr
while accelerating at 1 million mm/hr 2 moveto(number targetHeight,
number speed, table controlPoints, function callback) This function
behaves similar to the basic version of the function. It starts at
its initial speed and position and moves to the highest point on
the control point table. callback is called when the stage passes
each control point.
TABLE-US-00006 [0461] function myCallbackFunction(index)--defining
the callback function print("hello") end moveto(25, 20000,
slicecontrolpoints( ), myCallbackFunction)-- moving the stage to
25mm at 20,000mm/hr while calling myCallbackFunction at the control
points generated by slicecontrolpoints( )
[0462] moveto(number targetHeight, number speed, number
acceleration, table controlPoints, function callback) This function
is the same as above except the user can pass an acceleration. The
stage accelerates from its initial position continuously until it
reaches the last control point.
TABLE-US-00007 [0462] function myCallbackFunction(index)--defining
the callback function print("hello") end moveto(25, 20000, 0.5e7,
slicecontrolpoints( ), myCallbackFunction)-- moving the stage to
25mm at 20,000mm/hr while accelerating at 0.5 million
mm/hr{circumflex over ( )}2 and also calling myCallbackFunction at
the control points generated by slicecontrolpoints( )
[0463] targetHeight: height, in mm from the origin, that the stage
will move to. [0464] initialSpeed: initial speed, in mm/hour, that
the stage will start moving at. [0465] acceleration: rate, in
mm/hour.sup.2, that the speed of the stage will increase from
initial speed. [0466] controlPoints: a table of target heights in
millimeters. After the stage reaches a target height, it calls the
function callback. [0467] callback: pointer to a function that will
be called when the stage reaches a control point. The callback
function should take one argument which is the index of the control
point the stage has reached.
Moveby
[0468] moveby allows the user to change the height of the stage by
a desired amount at a given speed. Safe upper and lower limits to
speed and acceleration are ensured internally. moveby(number
dHeight, number initalSpeed) [0469] 1 moveby(-2, 15000)--moving
down 2 mm at 15,000 mm/hr [0470] moveby(number dHeight, number
initialSpeed, number acceleration) This version of the function
allows an acceleration to be defined as well as speed. The stage
starts moving at initial speed and then increases by acceleration
until it reaches its destination. [0471] 1 moveby(25, 15000,
1e7)--moving up 25 mm at 15,000 mm/hr while accelerating 1e7 mm/hr
2 [0472] moveby(number dHeight, number initialSpeed, table
controlPoints, function callback) This function usage allows the
user to pass the function a table of absolute height coordinates.
After the stage reaches one of these target heights, it calls the
function `callback.` Callback should take one argument which is the
index of the control point it has reached.
TABLE-US-00008 [0472] function myCallbackFunction(index)--defining
the callback function print("hello") end moveby(25, 20000,
slicecontrolpoints( ), myCallbackFunction)--moving the stage up
25mm at 20,000mm/hr while calling myCallbackFunction at the control
points generated by slicecontrolpoints( )
[0473] moveby(number dHeight, number initialSpeed, number
acceleration, table controlPoints, function callback) This function
is the same as above except the user can pass an acceleration. The
stage accelerates from its initial position continuously until it
reaches the last control point.
TABLE-US-00009 [0473] function myCallbackFunction(index)--defining
the callback function print("hello") end moveby(25, 20000,
1e7,slicecontrolpoints( ), myCallbackFunction)--moving the stage up
25mm at 20,000mm/hr while calling myCallbackFunction at the control
points generated by slicecontrolpoints( ) and accelerating at
1e7mm/hr{circumflex over ( )}2
[0474] dHeight: desired change in height, in millimeters, of the
stage. [0475] initialSpeed: initial speed, in mm/hour, at which the
stage moves. [0476] acceleration: rate, in mm/hour.sup.2, that the
speed of the stage will increase from initial speed. [0477]
controlPoints: a table of target heights in millimeters. After the
stage reaches a target height, it calls the function callback.
[0478] callback: pointer to a function that will be called when the
stage reaches a control point. The callback function should take
one argument which is the index of the control point the stage has
reached.
Light Engine Control
Light
[0478] [0479] relay is used to turn the light engine on or off in
the printer. The light engine must be on in order to print. Make
sure the relay is set to off at the end of the script.
relay(boolean lightOn) [0480] relay(true)--turning light on [0481]
lightOn: false turns the light engine off, true turns the light
engine on.
Adding Procedural Geometry
[0482] Functions in this section exist to project shapes without
using a sliced part file. Every function in this section has an
optional number value called figureIndex. Each figure in a slice
has its own index. The figures reside one on top of another.
Figures are drawn so that the figure with the highest index is `on
top` and will therefore not be occluded by anything below it. By
default indexes are assigned in the order that they are created so
the last figure created will be rendered on top. One can, however,
change the index by passing the desired index into figureIndex.
[0483] Every function in this section requires a sliceIndex
argument. This value is the index of the slice that the figure will
be added to.
[0484] Note that generating this procedural geometry does not
guarantee that it will be visible or printable. One must use one of
the functions such as fillmask or linemask outlined below.
Addcircle
[0485] addcircle(number x, number y, number radius, number
sliceIndex) addcircle draws a circle in the specified slice.
addCircle(0,0, 5, 0)--creating a circle at the origin of the first
slice with a radius of 5 mm [0486] x: is the horizontal distance,
in millimeters, from the center of the circle to the origin. [0487]
y: is the vertical distance, in millimeters, from the center of the
circle to the origin. [0488] radius: is the radius of the circle
measured in millimeters. [0489] sliceIndex: index of the slice to
which the figure will be added. [0490] Returns: figure index of the
figure. addrectangle [0491] addrectangle(number x, number y, number
width, number height number sliceIndex) addrectangle draws a
rectangle in the specified slice. addrectangle(0,0, 5,5,
0)--creating a 5 mm.times.5 mm square with its top left corner at
the origin. [0492] x: horizontal coordinate, in millimeters, of the
top left corner of the rectangle. [0493] y: vertical coordinate, in
millimeters, of the top left corner of the rectangle. [0494] width:
width of the rectangle in millimeters. [0495] height: height of the
rectangle in millimeters. [0496] sliceIndex: index of the slice to
which the figure will be added. [0497] Returns: figure index of the
figure.
Addline
[0497] [0498] addline(number x0, number y0, number x1, number y1,
number sliceIndex) addline draws a line segment. addLine(0,0,
20,20, 0)--creating a line from the origin to 20 mm along the x and
y axis on the first slice. [0499] x0: horizontal coordinate of the
first point in the segment, measured in millimeters. [0500] y0:
vertical coordinate of the first point in the segment, measured in
millimeters. [0501] x1: horizontal coordinate of the second point
in the segment, measured in millimeters. [0502] y2: vertical
coordinate of the second point in the segment, measured in
millimeters. [0503] sliceIndex: index of the slice to which the
figure will be added. Returns: figure index of the figure.
Addtext
[0504] text(number x, number y, number scale, string text, number
sliceIndex) addtext draws text on the specified slice starting at
position `x, y` with letters of size `scale`.
addtext(0,0, 20, "Hello world", 0)--writing Hello World at the
origin of the first slice [0505] x: horizontal coordinate, measured
in millimeters, of the top left corner of the bounding box around
the text. [0506] y: vertical coordinate, measured in millimeters,
of the top left corner of the bounding box around the text. [0507]
scale: letter size in millimeters, interpretation may vary
depending on the underlying operating system (Windows, OSX, Linux,
etc). [0508] text: the actual text that will be drawn on the slice.
[0509] sliceIndex: index of the slice to which the figure will be
added. Returns: figure index of the figure.
Fill and Line Control
Fillmask
[0509] [0510] fillmask(number color, number sliceIndex, number
figureIndex) fillmask is used to control how the procedural
geometry is drawn. fillmask tells the figure in question to fill
the entirety of its interior with color. [0511] color: can be any
number on the range 0 to 255. Where 0 is black and 255 is white,
any value in between is a shade of grey interpolated linearly
between black and white based on the color value. Any value less
than 0 will produce a transparent color. [0512]
myCircle=addCircle(0,0,5,0)--creating the circle to fill [0513]
fillmask(255, 0, myCircle)--Creating a white filled circle [0514]
sliceIndex: the index of the slice that should be modified. [0515]
figureIndex: the is used to determine which figure on the slice
should be filled. Each figure has its own unique index. If no
figureIndex is passed, the fill applies to all figures in the
slice.
Linemask
[0515] [0516] linemask(number color, number sliceIndex, number
figureIndex) linemask is used to control how the procedural
geometry is drawn. linemask tells a figure to draw its outline in a
specific color. The width of the outline is defined by the function
linewidth. [0517] myCircle=addCircle(0,0,20,0)--creating the circle
to fill [0518] linemask(255, 0, myCircle)--setting the outline of
the circle to be white [0519] fillmask(150,0, myCircle)--setting
the fill of the circle to be grey [0520] color: can be any number
on the range 0 to 255. Where 0 is black and 255 is white, any value
in between is a shade of grey interpolated linearly between black
and white based on the color value. Any value less than 0 will
produce a transparent color. [0521] sliceIndex: the index of the
slice that should be modified. [0522] figureIndex: is used to
determine which figure on the slice should be filled. Each figure
has its own unique index. If no figureIndex is passed, the fill
applies to all figures in the slice.
Linewidth
[0522] [0523] linewidth(number width, number sliceIndex, number
figureIndex) linewidth is used to set the width of the line that
linemask will use to outline the figure. [0524]
linewidth(2,0)--setting the line width for every figure on the
first slice to 2 mm [0525] sliceIndex: the index of the slice that
should be modified. [0526] figureIndex: is used to determine which
figure on the slice should have its outline changed. Each figure
has its own unique index, see section 2.3 (Pg. 10) for more
details. If no figureIndex is passed, the fill applies to all
figures in the slice.
Loadmask
[0526] [0527] loadmask(string filepath) loadmask allows for
advanced fill control. It enables the user to load a texture from a
bitmap file and use it to fill the entirety of a figure with the
texture. [0528] texture=loadmask("voronoi_noise.png")--loading
texture. voronoi_noise.png is in the same directory as the script.
[0529] myCircle=addCircle(0,0,20,0)--creating the circle to fill
[0530] fillmask(texture, 0, myCircle)--filling the circle with
voronoi noise [0531] filepath: file path to image file [0532]
Returns: a special data type which can be passed into a fillmask or
linemask function as the color argument.
Frames
Showframe
[0532] [0533] showframe(number sliceIndex) showframe is essential
to the printing process. This function sends the data from a slice
to the printer. Call showframes on a frame that doesn't exist to
render a black frame e.g. showframe(-1). [0534]
showframe(2)--showing the 3rd slice [0535] sliceIndex: the index of
the slice to send to the printer.
Framegradient
[0535] [0536] framegradient(number slope) framegradient is designed
to compensate for differences in light intensity.
Calcframe
[0536] [0537] calcframe( ) [0538] calcframe is designed to analyze
the construction of a slice calculates the last frame shown. [0539]
showframe(0) [0540] calcframe( ) [0541] Returns: the maximum
possible distance between any point in the figure and the edge.
[0542] 2.5.4 loadframe [0543] loadframe(string filepath) [0544]
loadframe is used to load a single slice from a supported bitmap
file. [0545] loadframe("slice.png")--slice.png is in the same
directory as the script [0546] filepath: file path to slice
image.
Slices
[0546] [0547] addslice [0548] addslice(number sliceHeight) addslice
creates a new slice at a given height at the end of the slice
stack. [0549] addslice(0.05)--adding a slice at 0.05 mm [0550]
addslice(number sliceHeight, number sliceIndex) [0551]
addslice(0.05, 2)--adding a slice at 0.05 mm and at index 2. this
pushes all layers 2 and higher up an index. [0552] addslice creates
a new slice at a given height and slice index. [0553] sliceHeight:
height, in millimeters, of the slice. [0554] sliceIndex: index at
which the slice should be added. Returns: slice index. [0555]
loadslices [0556] loadslices(string filepath) loadslices is used to
load all the slices from a 2D slice file. [0557] loadslices("Chess
King.svg")--loading all the slices from the Chess King.svg file
[0558] filepath: file path to the sliced model. Acceptable formats
are .cli and .svg. Returns: number of slices.
Sliceheight
[0558] [0559] sliceheight(number sliceIndex) sliceheight is used to
find the height of a slice in mm off the base. [0560]
addslice(0.05,0)--setting the first slice to 0.05 mm [0561]
sliceheight(0)--checking the height of slice 0, in this example it
should return 0.05 [0562] sliceIndex: index of the slice to check.
Returns: slice height in mm.2.6.4 slicecontrolpoints [0563]
slicecontrolpoints( ) slicecontrolpoints is a helper function which
creates a control point for each slice of a model. These control
points can be passed to the moveto or moveby function to set it to
callback when the stage reaches the height of each slice. Make sure
loadslices has been called prior to calling this function.
loadslices("Chess King.svg") controlPoints=slicecontrolpoints( )
[0564] Returns: Lua table of control points.
Timing
Sleep
[0564] [0565] sleep(number seconds) sleep allows the user to pause
the execution of the program for a set number of seconds. [0566]
sleep(0.5)--sleeping for a half second [0567] seconds: number of
seconds to pause script execution.
Clock
[0567] [0568] clock( ) clock returns the current time in seconds.
It is accurate at least up to the millisecond and should therefore
be used instead of Lua's built in clock functionality. clock should
be used as a means to measure differences in time as the start time
for the second count varies from system to system. [0569] t1=clock(
) [0570] loadslices("Chess King.svg") [0571] deltaTime=clock( )-t1
[0572] Returns: system time in seconds.
Fluid Control
[0573] This set of functions can be used with printer models that
support fluid control. Before the script finishes executing,
setlevels(0,0) should be called to ensure that the pump stops
pumping fluid into the vat.
Getcurrentlevel
[0574] getcurrentlevel( ) getcurrentlevel returns the percentage of
the vat that is full. [0575] print(string.format("Vat is % d
percent full.", getcurrentlevel( )*100)) [0576] Returns: a floating
point number on the range 0 to 1 that represents the percentage of
the vat that is full. setlevels [0577] setlevels(number min, number
max) setlevels allows the user to define how much fluid should be
in the vat. The fluid height will be automatically regulated by a
pump. The difference between min and max should be greater than
0.05 to ensure that the valve is not constantly opening and
closing. [0578] setlevels(0.7,0.75)--keeping vat about 75 percent
full [0579] min: the minim percentage of the vat that should be
full. Entered as a floating point number from 0 to 1. [0580] max:
the max percentage of the vat that should be full. Entered as a
floating point number from 0 to 1.
User Feedback
[0580] [0581] infoline [0582] infoline(int lineIndex, string text)
infoline allows the user to display up to 5 lines of text in a
constant position on the sidebar of the Programmable Printer
Platform. This function is often used to allow the user to monitor
several changing variables at once. [0583] infoline(1,
string.format("Vat is % d percent full.", getcurrentlevel( )*100))
[0584] lineIndex: the index of the line. Indexes should be in the
range 1 to 5, 1 being the upper most line. [0585] text: text to be
displayed at line index.
Global Configuration Table.
[0586] Before a print script is executed, all global variables are
loaded into a configuration table called cfg. Most of the data in
this table has already been read by the Programmable Printer
Platform by the time the users script executes, therefore, changing
them will have no effect. However, writing to the xscale, yscale,
zscale, xorig and yorig fields of the cfg, will effect all the
loadslices and addlayer calls that are made afterwards. If the
users script is designed to be run at a specific scale and/or
position, it is good practice to override the cfg with the correct
settings to ensure the scale and position can't be accidentally
changed by the Programmable Printer Platform.
cfg.xscale=3--overriding global settings to set scale on the x axis
to 3 cfg.yscale=2--overriding global settings to set scale on the y
axis to 2 cfg.zscale=1--overriding global settings to set scale on
the z axis to 1 cfg.xorig=-2.0--overriding global settings to set
the origin on the x axis 2 mm left cfg.yorig=0.25--overriding
global settings to set the origin on the y axis 0.25 mm in the
positive direction
Fields in cfg:
[0587] serial port: name of serial port (changing this variable
wont effect code) [0588] xscale: x scale [0589] yscale: y scale
[0590] zscale: z scale [0591] xorig: x origin [0592] yorig: y
origin [0593] hw xscale: pixel resolution in x direction (changing
this variable won't effect code) [0594] hw yscale: pixel resolution
in y direction (changing this variable won't effect code)
Useful Lua Standard Libraries.
[0595] The math standard library contains several different
functions that are useful in calculating geometry. The string
object is most useful in printing for manipulating info strings.
For details contact LabLua at Departamento de Informatica, PUC-Rio,
Rua Marqu s de Sao Vicente, 225; 22451-900 Rio de Janeiro, RJ,
Brazil
Example 8
Lua Script Program for Continuous Print
[0596] This example shows a Lua script program corresponding to
Example 7 above for continuous three dimension printing.
TABLE-US-00010 --Constants sliceDepth = .05--in millimeters
exposureTime = .225-- in seconds --Loading Model modelFilePath =
"Chess King.svg" numSlices = loadslices(modelFilePath)
controlPoints = slicecontrolpoints( )--Generate Control Points
--calculating parameters exposureTime =
exposureTime/(60*60)--converted to hours stageSpeed =
sliceDepth/exposureTime--required distance/required time
maxPrintHeight = sliceheight(numSlices-1)--find the highest point
in the print, this is the same as the height of the last slice.
Slices are 0 indexed, hence the -1. infoline(1, "Current Print
Info:") infoline(2, string.format("Calulated Stage Speed:
%dmm/hr\n", stageSpeed)) infoline(3, string.format("Calculated Max
Print Height: %dmm", maxPrintHeight)) infoline(4,
string.format("Calculated Est. Time: %dmin",
(maxPrintHeight/stageSpeed)*60)) --Create Callback Function for use
with moveto function movetoCallback(controlPointIndex)
showframe(controlPointIndex) end --Prepare Printer
relay(true)--turn light on setlevels(.55, .6)--if available,
printer set fluid pump to maintain about 50% fill --Execute Print
gotostart( )--move stage to starting position
moveto(maxPrintHeight, stageSpeed, controlPoints, movetoCallback)
--Shutdown relay(false) setlevels(0,0) --Lift stage to remove part
moveby(25, 160000)
Example 9
Lua Script Program for Cylinder and Buckle
[0597] This example shows a Lua script program for two fitted parts
that use procedural geometry.
[0598] Cylinder:
TABLE-US-00011 --Constants exposureTime = 1.5-- in seconds
preExposureTime = 1 -- in seconds stageSpeed = 300 --in mm/hour
sliceDepth = .05 numSlices = 700 --Generating Model radius = 11
thickness = 4 smallCircleRad = 1.4 for sliceIndex = 0,numSlices-1
do addlayer(sliceDepth*(sliceIndex+1), sliceIndex)--the depth of a
slice*its index = height of slice largeCircle =
addcircle(0,0,radius, sliceIndex) linewidth(thickness, sliceIndex,
largeCircle) linemask(255, sliceIndex, largeCircle) for
i=0,2*math.pi, 2*math.pi/8 do addcircle(math.cos(i)*radius,
math.sin(i)*radius, smallCircleRad, sliceIndex) end
fillmask(0,sliceIndex) end --calculating parameters maxPrintHeight
= sliceheight(numSlices-1)--find the highest point in the print,
this is the same as the height of the last slice. Slices are 0
indexed, hence the -1. infoline(1, "Current Print Info:")
infoline(2, string.format("Calculated Max Print Height: %dmm",
maxPrintHeight)) infoline(3, string.format("Calculated Est. Time:
%dmin", (maxPrintHeight/stageSpeed)*60 +
(preExposureTime+exposureTime)*numSlices/60)) infoline(4,
string.format("Number of Slices: %d", numSlices)) --Prepare Printer
relay(true)--turn light on showframe(-1) --ensure nothing is
exposed durring setup setlevels(.55, .6)--if available, printer set
fluid pump to maintain about 55% fill --Execute Print gotostart(
)--move stage to starting position for sliceIndex =0,numSlices-1 do
infoline(5, string.format("Current Slice: %d", sliceIndex))
nextHeight = sliceheight(sliceIndex)--calculate the height that the
stage should be at to expose this frame moveto(nextHeight,
stageSpeed)--move to nextHeight sleep(preExposureTime)--wait a
given amount of time for oxygen to diffuse into resin ,
prepExposureTime is predefined in the Constants section
showframe(sliceIndex)--show frame to expose sleep(1.5)--wait while
frame exposes, exposureTime is predefined in the Constants section
showframe(-1)-- show nothing to ensure no exposure while stage is
moving to next position end --Shutdown relay(false) setlevels(0,0)
--Lift stage to remove part moveby(25, 160000)
Buckle:
TABLE-US-00012 [0599] --Constants exposureTime = 1.5-- in seconds
preExposureTime = 0.5 -- in seconds stageSpeed = 300 --in mm/hour
sliceDepth = .05 numSlices = 900 --Generating Model baseRadius = 11
thickness = 3 innerCircleRad = 7.5 for sliceIndex = 0,numSlices-1
do addlayer(sliceDepth*(sliceIndex+1))--the depth of a slice*its
index = height of slice if(sliceIndex < 100) then --base
addcircle(0,0, baseRadius, sliceIndex) fillmask(255, sliceIndex)
else -- inner circle innerCircle = addcircle(0,0, innerCircleRad,
sliceIndex) linewidth(thickness, sliceIndex, innerCircle)
linemask(255, sliceIndex, innerCircle) for i = 0,4*2*math.pi/8,
2*math.pi/8 do x = math.cos(i)*(innerCircleRad+thickness) y =
math.sin(i)*(innerCircleRad+thickness) cutLine = addline(x,y,
-x,-y, sliceIndex) linewidth(3, sliceIndex, cutLine) linemask(0,
sliceIndex, cutLine) end if (sliceIndex > 800) then --tips r0 =
innerCircleRad +2 if(sliceIndex < 850) then r0 = innerCircleRad
+ (sliceIndex-800)*(2/50) end for i = 0,4*2*math.pi/8, 2*math.pi/8
do ang = i + (2*math.pi/8)/2 x = math.cos(ang)*(r0) y =
math.sin(ang)*(r0) nubLine = addline(x,y, -x,-y, sliceIndex)
linewidth(2, sliceIndex, nubLine) linemask(255, sliceIndex,
nubLine) end fillmask(0,sliceIndex, addcircle(0,0,
innerCircleRad-(thickness/2), sliceIndex)) end end
showframe(sliceIndex) sleep(.02) end --calculating parameters
maxPrintHeight = sliceheight(numSlices-1)--find the highest point
in the print, this is the same as the height of the last slice.
Slices are 0 indexed, hence the -1. infoline(1, "Current Print
Info:") infoline(2, string.format("Calculated Max Print Height:
%dmm", maxPrintHeight)) infoline(3, string.format("Calculated Est.
Time: %dmin", (maxPrintHeight/stageSpeed)*60 +
(preExposureTime+exposureTime)*numSlices/60)) infoline(4,
string.format("Number of Slices: %d", numSlices)) --Prepare Printer
relay(true)--turn light on showframe(-1) --ensure nothing is
exposed durring setup setlevels(.55, .6)--if available, printer set
fluid pump to maintain about 55% fill --Execute Print gotostart(
)--move stage to starting position for sliceIndex =0,numSlices-1 do
infoline(5, string.format("Current Slice: %d", sliceIndex))
nextHeight = sliceheight(sliceIndex)--calculate the height that the
stage should be at to expose this frame moveto(nextHeight,
stageSpeed)--move to nextHeight sleep(preExposureTime)--wait a
given amount of time for oxygen to diffuse into resin,
prepExposureTime is predefined in the Constants section
showframe(sliceIndex)--show frame to expose sleep(1.5)--wait while
frame exposes, exposureTime is predefined in the Constants section
showframe(-1)-- show nothing to ensure no exposure while stage is
moving to next position end --Shutdown relay(false) setlevels(0,0)
--Lift stage to remove part moveby(25, 160000)
Example 10
Continuous Fabrication with Intermittent Irradiation and
Advancing
[0600] A process of the present invention is illustrated in FIG.
21, where the vertical axis illustrates the movement of the carrier
away from the build surface. In this embodiment, the vertical
movement or advancing step (which can be achieved by driving either
the carrier or the build surface, preferably the carrier), is
continuous and unidirectional, and the irradiating step is carried
out continuously. Polymerization of the article being fabricated
occurs from a gradient of polymerization, and hence creation of
"layer by layer" fault lines within the article is minimized.
[0601] An alternate embodiment of the present invention is
illustrated in FIG. 22. In this embodiment, the advancing step is
carried out in a step-by-step manner, with pauses introduced
between active advancing of the carrier and build surface away from
one another. In addition, the irradiating step is carried out
intermittently, in this case during the pauses in the advancing
step. We find that, as long as the inhibitor of polymerization is
supplied to the dead zone in an amount sufficient to maintain the
dead zone and the adjacent gradient of polymerization during the
pauses in irradiation and/or advancing, the gradient of
polymerization is maintained, and the formation of layers within
the article of manufacture is minimized or avoided. Stated
differently, the polymerization is continuous, even though the
irradiating and advancing steps are not. Sufficient inhibitor can
be supplied by any of a variety of techniques, including but not
limited to: utilizing a transparent member that is sufficiently
permeable to the inhibitor, enriching the inhibitor (e.g., feeding
the inhibitor from an inhibitor-enriched and/or pressurized
atmosphere), etc. In general, the more rapid the fabrication of the
three-dimensional object (that is, the more rapid the cumulative
rate of advancing), the more inhibitor will be required to maintain
the dead zone and the adjacent gradient of polymerization.
Example 11
Continuous Fabrication with Reciprocation During Advancing to
Enhance Filling of Build Region with Polymerizable Liquid
[0602] A still further embodiment of the present invention is
illustrated in FIG. 23. As in Example 10 above, this embodiment,
the advancing step is carried out in a step-by-step manner, with
pauses introduced between active advancing of the carrier and build
surface away from one another. Also as in Example 10 above, the
irradiating step is carried out intermittently, again during the
pauses in the advancing step. In this example, however, the ability
to maintain the dead zone and gradient of polymerization during the
pauses in advancing and irradiating is taken advantage of by
introducing a vertical reciprocation during the pauses in
irradiation.
[0603] We find that vertical reciprocation (driving the carrier and
build surface away from and then back towards one another),
particularly during pauses in irradiation, can serve to enhance the
filling of the build region with the polymerizable liquid,
apparently by pulling polymerizable liquid into the build region.
This is advantageous when larger areas are irradiated or larger
parts are fabricated, and filling the central portion of the build
region may be rate-limiting to an otherwise rapid fabrication.
[0604] Reciprocation in the vertical or Z axis can be carried out
at any suitable speed in both directions (and the speed need not be
the same in both directions), although it is preferred that the
speed when reciprocating away is insufficient to cause the
formation of gas bubbles in the build region.
[0605] While a single cycle of reciprocation is shown during each
pause in irradiation in FIG. 23, it will be appreciated that
multiple cycles (which may be the same as or different from one
another) may be introduced during each pause.
[0606] As in Example 10 above, as long as the inhibitor of
polymerization is supplied to the dead zone in an amount sufficient
to maintain the dead zone and the adjacent gradient of
polymerization during the reciprocation, the gradient of
polymerization is maintained, the formation of layers within the
article of manufacture is minimized or avoided, and the
polymerization/fabrication remains continuous, even though the
irradiating and advancing steps are not.
Example 12
Acceleration During Reciprocation Upstroke and Deceleration During
Reciprocation Downstroke to Enhance Part Quality
[0607] We observe that there is a limiting speed of upstroke, and
corresponding downstroke, which if exceeded causes a deterioration
of quality of the part or object being fabricated (possibly due to
degradation of soft regions within the gradient of polymerization
caused by lateral shear forces a resin flow). To reduce these shear
forces and/or enhance the quality of the part being fabricated, we
introduce variable rates within the upstroke and downstroke, with
gradual acceleration occurring during the upstroke and gradual
deceleration occurring during the downstroke, as schematically
illustrated in FIG. 24.
Example 13
Dual Cure with PEGDA+EGDA+Polyurethane (HMDI Based)
[0608] 5 g of the following mixture was mixed for 3 minutes in a
high-shear mixer. [0609] 1 g of poly(ethylene glycol)diacrylate
(Mn=700 g/mol) containing 12 wt % of
diphenyl(2-(6-trimethylbenzoyl)phosphine oxide (DPO). [0610] 1 g of
diethyleneglycol diacrylate containing 12 wt % DPO [0611] 1 g of
"Part A" polyurethane resin (Methylene bis(4-Cyclohexylisocyanate)
based: "ClearFlex 50" sold by Smooth-On.RTM. inc. [0612] 2 g of
"Part B" polyurethane resin (polyol mixture): "ClearFlex 50" sold
by Smooth-On.RTM. inc. [0613] 0.005 g of amorphous carbon black
powder
[0614] After mixing, the resin was 3D formed using an apparatus as
described herein. A "honeycomb" object was formed at a speed of 160
mm/hr using a light intensity setting of 1.2 mV (when measured
using a volt meter equipped with a optical sensor). Total printing
time was approximately 10 minutes.
[0615] After printing, the part was removed from the print stage,
rinsed with hexanes, and placed into an oven set at 110.degree. C.
for 12 hours.
[0616] After heating, the part maintained its original shape
generated during the initial printing, and it had transformed into
a tough, durable, elastomer having an elongation at break around
200%
Example 14
Dual Cure with EGDA+Polyurethane (TDI Based)
[0617] 5 g of the following mixture was mixed for 3 minutes in a
high-shear mixer. [0618] 1 g of diethyleneglycol diacrylate
containing 12 wt % DPO [0619] 2 g of "Part A" polyurethane resin
(toluene diisocyanate) based: "VytaFlex 30" sold by Smooth-On.RTM.
inc. [0620] 2 g of "Part B" polyurethane resin (polyol mixture):
"Vytaflex 30" sold by Smooth-On.RTM. inc.
[0621] After mixing, the resin was 3D formed using an apparatus as
described herein. The cylindrical object was formed at a speed of
50 mm/hr using a light intensity setting of 1.2 mV (when measured
using a volt meter equipped with an optical sensor). Total printing
time was approximately 15 minutes.
[0622] After printing, the part was removed from the print stage,
rinsed with hexanes, and placed into an oven set at 110.degree. C.
for 12 hours.
[0623] After heating, the part maintained its original shape
generated during the initial printing, and it had transformed into
a tough, durable, elastomer having an elongation at break around
400%
Example 15
Synthesis of a Reactive Blocked Polyurethane Prepolymer for Dual
Cure
[0624] Add 200 g of melted anhydrous 2000 Da, polytetramethylene
oxide (PTMO2k) into a 500 mL 3-neck flask charged with an overhead
stirrer, nitrogen purge and a thermometer. Then 44.46 g IPDI is
added to the flask and stirred to homogeneous solution with the
PTMO for 10 min, followed by addition of 140 uL Tin(II) catalyst
stannous octoate. Raise the temperature to 70.degree. C., and keep
reaction for 3 h. After 3 h, gradually lower the temperature to
40.degree. C., and gradually add 37.5 g TBAEMA using an additional
funnel within 20 min. Then set the temperature to 50.degree. C. and
add 100 ppm hydroquinone. Keep the reaction going on for 14 h. Pour
out the final liquid as the product.
Example 16
Synthesis of a Second Reactive Blocked Polyurethane Prepolymer for
Dual Cure
[0625] Add 150 g dried 1000 Da, polytetramethylene oxide (PTMO1k)
into a 500 mL 3-neck flask charged with an overhead stirrer,
nitrogen purge and a thermometer. Then 50.5 g HDI is added to the
flask and stirred to homogeneous solution with the PTMO for 10 min,
followed by addition of 100 uL Tin(II) catalyst stannous octoate.
Raise the temperature to 70.degree. C., and keep reaction for 3 h.
After 3 h, gradually lower the temperature to 40.degree. C., and
gradually add 56 g TBAEMA using an additional funnel within 20 min.
Then set the temperature to 50.degree. C. and add 100 ppm
hydroquinone. Keep the reaction going on for 14 h. Pour out the
final liquid as the product.
[0626] In the above examples, the PTMO can be replaced by
polypropylene glycol (PPG, such as 1000 Da PPG (PPG1k)) or other
polyesters or polybuadiene diols. IPDI or HDI can be replaced by
other diisocyanates. The molar stoichiometry of the
polyol:diisocyanate:TBAEMA is preferably 1:2:2. Preferably use
0.1-0.3 wt % stannous octoate to the weight of the polyol.
Example 17
Printing and Thermal Curing with a Reactive Blocked Polyurethane
Prepolymers
[0627] ABPU resins can be formed (optionally but preferably by
continuous liquid interphase/interface printing) at up to 100 mm/hr
using the formulations in Table 1 to generate elastomers with low
hysteresis after thermally cured at 100.degree. C. for 2 to 6
hours, depending on the diisocyanates used in ABPU and the chain
extender(s).
TABLE-US-00013 TABLE 1 Parts by weight ABPU 320 Reactive Diluent
40-80 Ethylene glycol 8-20 H12MDA 8-20 PPO 1-4
[0628] Dog-bone-shaped specimens were formed by continuous liquid
interface printing with different ABPUs (varying the diisocyanate
and polyol used for the synthesis) and reactive diluents. Table 2
shows the mechanical properties of some of the thermally cured
dog-bone samples at room temperature.
TABLE-US-00014 TABLE 2 Tensile stress ABPU Reactive at maximum %
elongation Diisocyanate Polyol diluent load (MPa) at break IPDI
PTMO2k Methyl 25 650 methacrylate IPDI PPG1k Cyclohexane 7.5 368
methacrylate MDI PTMO2k TBAEMA 13.4 745 HDI PTMO1k TBAEMA 13 490
HMDI PTMO1k TBAEMA 13.6 334
Examples 18-61
Additional Polyurethane Dual Cure Materials, Testing and Tensile
Properties
[0629] The following abbreviations are used in the Examples below:
"DEGMA" means di(ethylene glycol)methyl ether methacrylate; "IBMA"
means isoboronyl methacrylate; "PACM" means
4,4'-Diaminodicyclohexyl methane; "BDO" means 1,4-butanediol; "PPO"
means Phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide; "MDEA"
means 4,4'-methylene-bis-(2,6-diethylaniline); "2-EHMA" means
2-ethylhexyl methacrylate; and "PEGDMA" means poly(ethylene
glycol)dimethacrylate (MW=700 Da).
Example 18
Testing of Tensile Properties
[0630] In the examples above and below, tensile properties were
tested in accordance with ASTM standard D638-10, Standard Test
Methods for Tensile Properties of Plastics (ASTM International, 100
Barr Harbor Drive, PO Box C700, West Conshohocken, Pa., 19428-2959
USA).
[0631] Briefly, tensile specimens (sometimes referred to as
"dog-bone samples" in reference to their shape), were loaded onto
an Instron 5964 testing apparatus with Instron BLUEHILL3
measurement software (Instron, 825 University Ave, Norwood, Mass.,
02062-2643, USA). The samples are oriented vertically and parallel
to the direction of testing. Cast and flood cured samples were
fully cured using a DNMAX 5000 EC-Series enclosed UV flood lamp
(225 mW/cm.sup.2) for from thirty to ninety seconds of exposure.
Table 3 below summarizes the types of tensile specimens tested,
general material property (rigid or non-rigid), and the associated
strain rate.
TABLE-US-00015 TABLE 3 Strain Rate Dogbone Type MaterialType
(mm/min) IV Rigid 5 V Rigid 1 IV Non-rigid 50 V Non-rigid 10
Dogbone type IV is used to test elastomeric samples.
[0632] The samples were tested at a rate such that the sample
ruptures at a time between 30 seconds to 5 minutes to ensure that
sample strain rate is slow enough to capture plastic deformation in
the samples.
[0633] Measured dogbone samples that do not rupture in the middle
rectangular section are excluded. Samples that break in the grips
or prior to testing are not representative of the anticipated
failure modes and are excluded from the data.
[0634] Persuant to ASTM D-638, measure the Young's modulus (modulus
of elasticity) (slope of the stress-strain plot between 5-10%
elongation), tensile strength at break, tensile strength at yield,
percent elongation at break, percent elongation at yield.
[0635] A strain rate is chosen such that the part with the lowest
strain-at-break (%) will fail within 5 minutes. This often means
that a slower strain rate will be necessary for rigid samples.
Example 19
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0636] Components as shown in Table 4, except PACM, were added to a
container and thoroughly mixed (either by an overhead stirrer or a
centrifugation mixer such as THINKY.TM. mixer) to obtain a
homogeneous resin. Then PACM was added to the resin and mixed for
another 2-30 min depending on the volume and viscosity of resin.
The resin was formed by CLIP as described above into D638 Type IV
dog-bone-shaped specimens followed by thermal curing at 125.degree.
C. for 2 h. The cured elastomer specimens were tested following
ASTM standard D638-10 on an Instron apparatus for mechanical
properties as described above, which properties are also summarized
in Table 4.
TABLE-US-00016 TABLE 4 Parts by weight ABPU(PTMO1k + HDI + TBAEMA)
697 DEGMA 82 IBMA 123 PACM 83 PPO 5 Tensile Strength (MPa) 13.1 %
Elongation at Break 395
Example 20
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0637] Cured elastomer specimens were prepared in the same manner
as in Example 19 but using the formulation in Table 5. The cured
specimens were tested following ASTM standard on an Instron
apparatus for mechanical properties as described above, which
properties are summarized in Table 5.
TABLE-US-00017 TABLE 5 Parts by weight ABPU(PTMO2k + IPDI + TBAEMA)
721 DEGMA 84 IBMA 126 PACM 54 PPO 5 Tensile Strength (MPa) 26.8 %
Elongation at Break 515
Example 21
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0638] Cured elastomer specimens were prepared in the same manner
as in Example 19 but using the formulation in Table 6. The cured
specimens were tested following ASTM standard on an Instron
apparatus for mechanical properties as described above, which
properties are summarized in Table 6.
TABLE-US-00018 TABLE 6 Parts by weight ABPU(PTMO2k + HMDI + TBAEMA)
728 DEGMA 86 IBMA 128 PACM 53 PPO 5 Tensile Strength (MPa) 23.1 %
Elongation at Break 456
Example 22
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0639] Components as shown in Table 7 were added to a container and
thoroughly mixed (either by an overhead stirrer or a centrifugation
mixer such as THINKY.TM. mixer) to obtain a homogeneous resin. The
resin was casted into a square mold (with dimensions of
100.times.100.times.4 mm), and UV flood cured for 1 min, followed
by thermal curing at 125.degree. C. for 2 h. The obtained elastomer
sheet was die-cut into rectangular bars with dimensions of
100.times.20.times.4 mm. The elastomer specimens were tested
following ASTM standard D638-10 on an Instron apparatus for
mechanical properties as described above, which properties are
summarized in Table 7.
TABLE-US-00019 TABLE 7 Parts by weight ABPU(PTMO1k + HDI + TBAEMA)
666 2-EHMA 131 IBMA 66 MDEA 123 PPO 10 Tensile Strength (MPa) 14.4
% Elongation at Break 370
Example 23
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0640] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 8. The
elastomer specimens were tested following ASTM standard D638-10 an
Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 8.
TABLE-US-00020 TABLE 8 Parts by weight ABPU(PTMO1k + HDI + TBAEMA)
692 DEGMA 102 2-EHMA 102 PEGDMA 14 PACM 80 PPO 10 Tensile Strength
(MPa) 6.42 % Elongation at Break 388
Example 24
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0641] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 9. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 9.
TABLE-US-00021 TABLE 9 Parts by weight ABPU(PTMO1k + IPDI + TBAEMA)
700 DEGMA 206 PEGDMA 10 PACM 74 PPO 10 Tensile Strength (MPa) 11.26
% Elongation at Break 366
Example 25
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0642] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 10. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 10.
TABLE-US-00022 TABLE 10 Parts by weight ABPU(PTMO1k + MDI + TBAEMA)
672 2-EHMA 248 PEGDMA 10 PACM 60 PPO 10 Tensile Strength (MPa)
24.93 % Elongation at Break 320
Example 26
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0643] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 11. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 11.
TABLE-US-00023 TABLE 11 Parts by weight ABPU(PTMO1k + MDI + TBAEMA)
698 DEGMA 208 PEGDMA 10 PACM 74 PPO 10 Tensile Strength (MPa) 20.14
% Elongation at Break 355
Example 27
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0644] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 12. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 12.
TABLE-US-00024 TABLE 12 Parts by weight ABPU(PTMO2k + HMDI +
TBAEMA) 2000 DEGMA 400 2-EHMA 200 PEGDMA 66 PACM 145 PPO 14 Tensile
Strength (MPa) 16.7 % Elongation at Break 476
Example 28
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0645] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 13. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 13.
TABLE-US-00025 TABLE 13 Parts by weight ABPU(PTMO2k + HMDI +
TBAEMA) 2000 DEGMA 400 2-EHMA 200 PACM 145 PPO 14 Tensile Strength
(MPa) 16.9 % Elongation at Break 499
Example 29
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0646] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 14 by mixing
all the components together. The elastomer specimens were tested
following ASTM standard D638-10 on an Instron apparatus for
mechanical properties as described above, which properties are
summarized in Table 14.
TABLE-US-00026 TABLE 14 Parts by weight ABPU(PTMO2k + HMDI +
TBAEMA) 2000 DEGMA 400 2-EHMA 200 PEGDMA 66 BDO 62 PPO 14 Tensile
Strength (MPa) 2.14 % Elongation at Break 188
Example 30
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0647] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 15. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 15.
TABLE-US-00027 TABLE 15 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2000 DEGMA 420 2-EHMA 180 PEGDMA 67 PACM 149 PPO 14 Tensile
Strength (MPa) 8.37 % Elongation at Break 386
Example 31
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0648] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 16. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 16.
TABLE-US-00028 TABLE 16 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2400 2-EHMA 700 PACM 179 PPO 16 Tensile Strength (MPa) 17.2
% Elongation at Break 557
Example 32
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0649] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 17. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 17.
TABLE-US-00029 TABLE 17 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2400 2-EHMA 630 PEGDMA 70 PACM 179 PPO 16 Tensile Strength
(MPa) 13.4 % Elongation at Break 520
Example 33
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0650] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 18. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 18.
TABLE-US-00030 TABLE 18 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2000 DEGMA 400 2-EHMA 200 PACM 149 PPO 14 Tensile Strength
(MPa) 13.6 % Elongation at Break 529
Example 34
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0651] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 19. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 19.
TABLE-US-00031 TABLE 19 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2,000 DEGMA 500 2-EHMA 500 PACM 149 PPO 14 Tensile Strength
(MPa) 9.32 % Elongation at Break 485
Example 35
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0652] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 20. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 20.
TABLE-US-00032 TABLE 17 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2000 DEGMA 650 2-EHMA 750 PACM 149 PPO 14 Tensile Strength
(MPa) 5.14 % Elongation at Break 440
Example 36
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0653] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 21. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 21.
TABLE-US-00033 TABLE 21 Parts by weight ABPU(PTMO1k + HDI + TBAEMA)
2000 DEGMA 580 PACM 246 PPO 14 Tensile Strength (MPa) 6.48 %
Elongation at Break 399
Example 37
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0654] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 22. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 22.
TABLE-US-00034 TABLE 22 Parts by weight ABPU(PTMO1k + HDI + TBAEMA)
2000 DEGMA 580 PEGDMA 60 PACM 246 PPO 14 Tensile Strength (MPa)
6.49 % Elongation at Break 353
Example 38
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0655] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 23. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 23.
TABLE-US-00035 TABLE 23 Parts by weight ABPU(PTMO1k + HDI + TBAEMA)
2000 DEGMA 620 2-EHMA 180 PACM 246 PPO 14 Tensile Strength (MPa)
6.83 % Elongation at Break 415
Example 39
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0656] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 24. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 24.
TABLE-US-00036 TABLE 24 Parts by weight ABPU(PTMO2k + HMDI +
TBAEMA) 2000 DEGMA 400 2-EHMA 200 PEGDMA 66 PACM 145 PPO 14 Tensile
Strength (MPa) 15.6 % Elongation at Break 523
Example 40
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0657] Cured elastomer specimens were prepared in the same manner
as in Example 22 but using the formulation in Table 25. The
elastomer specimens were tested following ASTM standard D638-10 on
an Instron apparatus for mechanical properties as described above,
which properties are summarized in Table 25.
TABLE-US-00037 TABLE 25 Parts by weight ABPU(PTMO2k + IPDI +
TBAEMA) 2000 DEGMA 420 2-EHMA 180 PEGDMA 67 PACM 149 PPO 14 Tensile
Strength (MPa) 13.2 % Elongation at Break 480
Example 41
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0658] Components as shown in Table 26, except PACM, were added to
a container and thoroughly mixed (either by an overhead stirrer or
THINKY.TM. mixer) to obtain a homogeneous resin. Then PACM was
added to the resin and mixed for another 30 min. The resin was cast
into dog-bone-shaped specimens by UV flood cure for 60 seconds
followed by thermal curing at 125.degree. C. for 4 h. The cured
specimens were tested following ASTM standard on an Instron
apparatus for mechanical properties as described above, which
properties are also summarized in Table 26.
TABLE-US-00038 TABLE 26 Component Weight % ABPU ABPU-1K-MDI 61.78
Reactive Diluent IBMA 30.89 Chain Extender PACM 6.56 Initiator PPO
0.77 Tensile Strength (MPa) 31.7 Modulus (MPa) 680 Elongation (%)
273
Example 42
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0659] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 27. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 27.
TABLE-US-00039 TABLE 27 Component Weight % ABPU ABPU-1K-MDI 53.51
Reactive Diluent IBMA 40.13 Chain Extender PACM 5.69 Initiator PPO
0.67 Tensile Strength (MPa) 26.2 Modulus (MPa) 1020 Elongation (%)
176
Example 43
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0660] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 28. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 28.
TABLE-US-00040 TABLE 28 Component Weight % ABPU ABPU-1K-MDI 47.2
Reactive Diluent IBMA 47.2 Chain Extender PACM 5.01 Initiator PPO
0.59 Tensile Strength (MPa) 29.5 Modulus (MPa) 1270 Elongation (%)
3.21
Example 44
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0661] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 29. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 29.
TABLE-US-00041 TABLE 29 Component Weight % ABPU ABPU-1K-MDI 42.22
Reactive Diluent IBMA 52.77 Chain Extender PACM 4.49 Initiator PPO
0.53 Tensile Strength (MPa) 19.3 Modulus (MPa) 1490 Elongation (%)
1.42
Example 45
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0662] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 30. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 30.
TABLE-US-00042 TABLE 30 Component Weight % ABPU ABPU-1K-MDI 61.13
Reactive Diluent IBMA 30.57 Chain Extender PACM 7.54 Initiator PPO
0.76 Tensile Strength (MPa) 19.3 Modulus (MPa) 1490 Elongation (%)
1.42
Example 36
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0663] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 31. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 31.
TABLE-US-00043 TABLE 31 Component Weight % ABPU ABPU-1K-MDI 61.55
Reactive Diluent IBMA 30.78 Chain Extender PACM 6.9 Initiator PPO
0.77 Tensile Strength (MPa) 34.1 Modulus (MPa) 713 Elongation (%)
269
Example 47
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0664] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 32. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 32.
TABLE-US-00044 TABLE 32 Component Weight % ABPU ABPU-1K-MDI 61.98
Reactive Diluent IBMA 30.99 Chain Extender PACM 6.25 Initiator PPO
0.77 Tensile Strength (MPa) 39.7 Modulus (MPa) 664 Elongation (%)
277
Example 48
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0665] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 33. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 33.
TABLE-US-00045 TABLE 33 Component Weight % ABPU ABPU-1K-MDI 63.75
Reactive Diluent IBMA 31.87 Chain Extender PACM 3.59 Initiator PPO
0.8 Tensile Strength (MPa) 21.3 Modulus (MPa) 265 Elongation (%)
207
Example 49
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0666] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 34. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 34.
TABLE-US-00046 TABLE 35 Component Weight % ABPU ABPU-1K-MDI 63.75
Reactive Diluent IBMA 31.87 Chain Extender PACM 5.02 Initiator PPO
0.8 Tensile Strength (MPa) 22.7 Modulus (MPa) 312 Elongation (%)
211
Example 50
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0667] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 36. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 36.
TABLE-US-00047 TABLE 36 Component Weight % ABPU ABPU-1K-MDI 63.75
Reactive Diluent IBMA 31.87 Chain Extender PACM 5.71 Initiator PPO
0.8 Tensile Strength (MPa) 28.4 Modulus (MPa) 407 Elongation (%)
222
Example 51
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0668] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 37. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 37.
TABLE-US-00048 TABLE 37 Component Weight % ABPU ABPU-1K-MDI 63.03
Reactive Diluent IBMA 31.51 Chain Extender BAMN 4.67 Initiator PPO
0.79 Tensile Strength (MPa) 25.1 Modulus (MPa) 155 Elongation (%)
297
Example 52
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0669] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 38. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 38.
TABLE-US-00049 TABLE 38 Component Weight % ABPU ABPU-1K-MDI 63.03
Reactive Diluent IBMA 31.35 Chain Extender BAMN 5.2 Initiator PPO
0.79 Tensile Strength (MPa) 21.7 Modulus (MPa) 214 Elongation (%)
291
Example 53
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0670] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 39. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 39.
TABLE-US-00050 TABLE 39 Component Weight % ABPU ABPU-650- 52.62
HMDI Reactive Diluent IBMA 39.47 Chain Extender PACM 7.26 Initiator
PPO 0.66 Tensile Strength (MPa) 31.7 Modulus (MPa) 1460 Elongation
(%) 3.65
Example 54
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0671] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 40. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 40.
TABLE-US-00051 TABLE 40 Component Weight % ABPU ABPU-650- 60.6 HMDI
Reactive Diluent IBMA 30.29 Chain Extender PACM 8.36 Initiator PPO
0.76 Tensile Strength (MPa) 29.4 Modulus (MPa) 864 Elongation (%)
191
Example 55
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0672] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 41. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 41.
TABLE-US-00052 TABLE 41 Component Weight % ABPU ABPU-650- 30.53
HMDI ABPU ABPU-1K-MDI 30.53 Reactive Diluent IBMA 30.53 Chain
Extender PACM 7.63 Initiator PPO 0.76 Tensile Strength (MPa) 29.1
Modulus (MPa) 492 Elongation (%) 220
Example 56
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0673] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 42. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 42.
TABLE-US-00053 TABLE 42 Component Weight % ABPU ABPU-650- 54.6 HMDI
Reactive Diluent IBMA 27.6 Crosslinker DUDMA 9.9 Chain Extender
PACM 7.1 Initiator PPO 0.8 Tensile Strength (MPa) 59.3 Modulus
(MPa) 1880 Elongation (%) 91
Example 57
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0674] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 43. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 43.
TABLE-US-00054 TABLE 43 Component Weight % ABPU ABPU-650- 54.6 HMDI
Reactive Diluent IBMA 18.8 Reactive Diluent PEMA 18.8 Chain
Extender PACM 7.1 Initiator PPO 0.8 Tensile Strength (MPa) 32.5
Modulus (MPa) 1050 Elongation (%) 178
Example 58
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0675] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 44. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 44.
TABLE-US-00055 TABLE 44 Component Weight % ABPU PTMO-1K-MDI 53.6
Reactive Diluent IB MA 23.1 Reactive Diluent PEMA 7.1 Crosslinker
DUDMA 9.7 Chain Extender PACM 5.7 Initiator PPO 0.8 Tensile
Strength (MPa) 43.8 Modulus (MPa) 1030 Elongation (%) 135
Example 59
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0676] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 45. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 45.
TABLE-US-00056 TABLE 45 Component Weight % ABPU PTMO-650- 55.1 HMDI
Reactive Diluent IBMA 33.1 Crosslinker BPADMA 3.7 Chain Extender
PACM 7.2 Initiator PPO 0.9 Tensile Strength (MPa) 33 Modulus (MPa)
1390 Elongation (%) 57
Example 60
Dual-Cure Material from Reactive Blocked Polyurethane
Prepolymer
[0677] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 30. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 30.
TABLE-US-00057 TABLE 30 Component Weight % ABPU PTMO-650- 52.6 HMDI
Reactive Diluent IBMA 14.9 Reactive Diluent PEMA 5.0 Crosslinker
SR239 19.9 Chain Extender PACM 6.9 Initiator PPO 0.8 Tensile
Strength (MPa) 44.5 Modulus (MPa) 1520 Elongation (%) 12.4
[0678] Cured specimens were prepared in the same manner as in
Example 41 but using the formulation in Table 30. The specimens
were tested following ASTM standard D638-10 on an Instron apparatus
for mechanical properties as described above, which properties are
summarized in Table 30.
Example 61
Elastomer from a Reactive Blocked Polyurethane Prepolymer
[0679] Cured elastomer specimens are prepared in the same manner as
in Example 20 but using the formulation in Table 31 below. The cure
specimens give elastomeric properties similar to those disclosed
above.
TABLE-US-00058 TABLE 31 Parts by weight ABPU(PTMO2k + IPDI + NVF)
721 DEGMA 84 Isobornyl acrylate 126 PACM 54 PPO 5
Example 62
Representative Polyurethane Products Produced from Dual-Cure
Materials
[0680] Polymerizable materials as described in the examples, or
detailed description, above (or variations thereof that will be
apparent to those skilled in the art) provide products with a range
of different elastic properties. Examples of those ranges of
properties, from rigid, through semi-rigid (rigid and flexible), to
elastomeric. Particular types of products that can be made from
such materials include but are not limited to those given in Table
32 below. The products may contain reacted photoinitiator fragments
(remnants of the first cure forming the intermediate product) when
produced by some embodiments of methods as described above. It will
be appreciated that the properties may be further adjusted by
inclusion of additional materials such as fillers and/or dyes, as
discussed above.
TABLE-US-00059 TABLE 32 Polyurethane Products by Properties and
Example Products.sup.1 Rigid and Flexible Rigid (Semi-Rigid)
Elastomeric Young's 800-3500 300-2500 0.5-40 Modulus (MPa) Tensile
30-100 20-70 0.5-30 Strength (MPa) % 1-100 40-300 or 600 50-1000
Elongation at Break Non- Fasteners; Structural elements; Foot-ware
soles, limiting electronic hinges including heels, innersoles
Example device housings; living hinges; boat and midsoles; Products
gears, propellers, and watercraft bushings and impellers; hulls and
decks; and gaskets; wheels, wheels; bottles, cushions; mechanical
jars and other electronic device device containers; pipes,
housings, etc. housings; tools, liquid tubes and etc. connectors,
etc. .sup.1In the table above, the following general terms and
phrases include the following non-limiting specific examples:
"Fastener" includes, but is not limited to, nuts, bolts, screws,
expansion fasteners, clips, buckles, etc, "Electronic device
housing" includes, but is not limited to, partial and complete cell
phone housings, tablet computer housings, personal computer
housings, electronic recorder and storage media housings, video
monitor housings, keyboard housings, etc., "Mechanical device
housing" includes, but is not limited to, partial and complete gear
housings, pump housings, motor housings, etc. "Structural elements"
as used herein includes, but is not limited to, shells, panels,
rods, beams (e.g., I-beams, U-beams, W-beams, cylindrical beams,
channels, etc), struts, ties, etc., for applications including
architectural and building, civil engineering, automotive and other
transportation (e.g., automotive body panel, hood, chassis, frame,
roof, bumper, etc.), etc. "Tools" includes, but is not limited to,
impact tools such as hammers, drive tools such as screwdrivers,
grasping tools such as pliers, etc., including component parts
thereof (e.g., drive heads, jaws, and impact heads).
Example 63
Polyurethane Products Having Multiple Structural Segments and/or
Multiple Tensile Properties
[0681] In examples 18-61 are given materials for the formation of
polyurethane products having a variety of different tensile
properties, ranging from elastomeric, to semi-rigid, to flexible,
as described in Example 62 above.
[0682] Because the polyurethane polymer is formed by curing the
intermediate product (e.g., by heating or microwave irradiating),
the process of fabricating the product may be paused or interrupted
one or more times, to change the polymerizable liquid. While a
fault line or plane may be formed in the intermediate by the
interruption, if the subsequent polymerizable liquid is, in its
second cure material, reactive with that of the first, then the two
distinct structural segments of the intermediate will cross-react
and covalently couple to one another during the second cure (e.g.,
by heating or microwave irradiation). Thus, for example, any of the
materials described in examples 19-60 above may be sequentially
changed to form a product having multiple distinct structural
segments with different tensile properties, while still being a
unitary product with the different segments covalently coupled to
one another.
[0683] For example, a hinge can be formed, with the hinge
comprising a rigid segment, coupled to a second elastic segment,
coupled to a third rigid segment, by sequentially changing
polymerizable liquids (e.g., from among those described in examples
19-60 above) during the formation of the three-dimensional
intermediate.
[0684] A shock absorber or vibration dampener can be formed in like
manner, with the second segment being either elastic or
semi-rigid.
[0685] A unitary rigid funnel and flexible hose assembly can be
formed in like manner.
[0686] Sequential changing of the polymerizable liquid can be
carried out with a multi-port, feed-through carrier, system, such
as described in PCT Application Publication No. WO 2015/126834, or,
where the polymerizable liquid is supplied in a reservoir
positioned above the build surface, providing the reservoir and
build surface as interchangeable cartridges that can be changed out
or swapped during a pause in fabrication.
Example 64
Silicone Rubber Product
[0687] Phenylbis(2-(6-trimethylbenzoyl)phosphine oxide (PPO) is
dissolved in isobornyl acrylate (IBA) with a THINKY.TM. mixer.
Methacryloxypropyl terminated polydimethylsiloxane (DMS-R31; Gelest
Inc.) is added to the solution, followed by addition of Sylgard
Part A and Part B (Corning PDMS precursors), and then further mixed
with a THINKY.TM. mixer to produce a homogeneous solution. The
solution is loaded into an apparatus as described above and a
three-dimensional intermediate is produced by ultraviolet curing as
described above. The three-dimensional intermediate is then
thermally cured at 100.degree. C. for 12 hours to produce the final
silicone rubber product. Parts by weight and tensile properties are
given in Table 33 below.
TABLE-US-00060 TABLE 33 Parts by weight DMS -R31 40 IBA 20 Sylgard
184Part A 40 Sylgard 184 Part B 4 PPO 1 Tensile Strength (MPa) 1.3
% Elongation at Break 130
Example 65
Epoxy Dual Cure Product
[0688] 10.018 g EpoxAcast 690 resin part A and 3.040 g part B were
mixed on a THINKY.TM. mixer. 3.484 g was then mixed with 3.013 g of
RKP5-78-1, a 65/22/13 mix of Sartomer
CN9782/N-vinylpyrrolidone/diethyleneglycol diacrylate to give a
clear blend which was cured in a "dog bone" shaped sample mold (for
tensile strength testing) for 2 minutes under a Dymax ultraviolet
lamp to give a very elastic but weak dog bone sample.
[0689] A second sample, RKP11-10-1 contained 3.517 g of the above
epoxy and 3.508 g of RKP5-90-3 and 65/33/2/0.25 blend of Sartomer
CN2920/N-vinylcaprolactam/N-vinylpyrrolidone/PPO initiator cured
similarly to give a very flexible dog bone. A third 1:1 sample made
with RKP5-84-8 50/20/30/0.25 CN2920/CN9031/NVF/PPO did not cure
completely and was discarded.
[0690] Later, first samples of an epoxy/acrylate dual cure resins
were made, as follows: [0691] Smooth-On EpoxAcure 690 is an EEW 190
epoxy (probably the diglycidyl ether of bisphenol A) sold with a
diaminopropyleneglycol oligomer curing agent and offering a 5 hr
open time/24 hr room temperature cure. [0692] This was blended 1:1
with three print formulations. Two samples were good homogeneous
blends that gave highly elastic, but very weak dog bone samples on
standard 2 minute UV cure. [0693] Subsequent thermal cure of the
samples at 84.degree. C. for 5 hrs gave reasonably strong and
stiff, but flexible samples, in one case with tenacious adhesion to
the polystyrene petri dish on which it was cured. Tensiles were in
the modest 5-8 MPa range, less than the base acrylate resins.
[0694] Later, RKP1-17-2D a 66/33/1 mix of CN2920/NVC/DPO initiator
was blended with EpoxAcure 690 in a 1:1 ratio and 2:1 ratio
[0695] The 1:1 epoxy/acrylate dual cure formulation previously
prepared failed to print in a CLIP apparatus as described above, at
100 or 60 mm/hr, but a 1:2 ratio gave a decent argyle pattern at 60
mm/hr. The Smooth-On EpoxAcure 690/CN2920/NVC argyle was post-cured
at room temperature to a clear, flexible, if tacky, sample. Dog
bones were also prepared.
[0696] The foregoing is illustrative of the present invention, and
is not to be construed as limiting thereof. The invention is
defined by the following claims, with equivalents of the claims to
be included therein.
* * * * *