U.S. patent application number 14/973099 was filed with the patent office on 2016-04-14 for fluid activatable adhesive for glue-free, liner-free, labels for glass and plastic substrates and methods of use thereof.
The applicant listed for this patent is NuLabel Technologies, Inc.. Invention is credited to Daniel Cho, Benjamin Lux, Heidi Munnelly.
Application Number | 20160104396 14/973099 |
Document ID | / |
Family ID | 53762299 |
Filed Date | 2016-04-14 |
United States Patent
Application |
20160104396 |
Kind Code |
A1 |
Cho; Daniel ; et
al. |
April 14, 2016 |
Fluid Activatable Adhesive for Glue-Free, Liner-Free, Labels for
Glass and Plastic Substrates and Methods of Use Thereof
Abstract
Methods for applying a liner-free, or liner-less label, to a
substrate, particularly glass or plastic (e.g., polyethylene
terephthalate) substrates, are described herein. The method
includes applying an adhesive composition, such as a polymeric
coating, to a label face sheet, activating the adhesive composition
with an activating fluid, and contacting the label to the
substrate. The activating fluid is preferably a mixture of water
and one or more organic solvents, such as low molecular weight
alcohols.
Inventors: |
Cho; Daniel; (Seattle,
WA) ; Munnelly; Heidi; (Cumberland, RI) ; Lux;
Benjamin; (Providence, RI) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
NuLabel Technologies, Inc. |
East Providence |
RI |
US |
|
|
Family ID: |
53762299 |
Appl. No.: |
14/973099 |
Filed: |
December 17, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14310913 |
Jun 20, 2014 |
9254936 |
|
|
14973099 |
|
|
|
|
Current U.S.
Class: |
428/211.1 ;
428/195.1; 428/355EN; 428/441; 428/483 |
Current CPC
Class: |
C09J 7/21 20180101; C09D
135/06 20130101; C09J 7/22 20180101; C09J 2425/00 20130101; G09F
2003/023 20130101; B32B 37/0038 20130101; C09J 7/30 20180101; G09F
3/02 20130101; G09F 2003/025 20130101; C09J 5/02 20130101; C09D
133/02 20130101; C09J 2301/306 20200801; C09J 7/20 20180101; C09J
2203/334 20130101; C09D 125/08 20130101; C09J 7/32 20180101; C09J
2400/283 20130101; B65C 3/08 20130101; G09F 2003/0257 20130101 |
International
Class: |
G09F 3/02 20060101
G09F003/02; C09J 7/04 20060101 C09J007/04 |
Claims
1. A liner-free label comprising a non-tacky polymeric coating on a
face sheet, wherein the polymeric coating comprises one or more
alkaline soluble polymers selected from the group consisting of
styrene-maleic anhydride resins, esters of styrene-maleic anhydride
resins, styrene-maleic anhydride amic acid resins, styrene-maleic
anhydride imide resins, ammonium and alkali metal salts of
styrene-maleic anhydride resins, and combinations thereof and one
or more emulsion polymers, wherein the one or more alkaline soluble
polymers are water-insoluble at neutral pH.
2. The liner-free label of claim 1, wherein the emulsion polymer
comprises a styrene acrylic polymer.
3. The liner-free label of claim 1, wherein the face sheet is
printed or printable paper.
4. The liner-free label of claim 1, wherein the face sheet is a
printed or printable polymeric film.
5. The liner-free label of claim 1, wherein the alkaline soluble
polymer comprises styrene-maleic anhydride resins.
6. The liner-free label of claim 1, wherein the face sheet has a
moisture vapor transmission rate of at least about 160 g/m.sup.2/24
hr.
7. The liner-free label of claim 1, wherein the label exhibits no
blocking after 90 seconds at 60 psi and 120-122.degree. F.
8. The liner-free label of claim 1, wherein the polymer coating
further comprises a hygroscopic particulate filler selected from
the group consisting of alumina, alumina gel, boehmite,
pseudoboehmite, clay, calcium carbonate, chalk, magnesium
carbonate, kaolin, calcined clay, pyropylate, bentonite, zeolite,
talc, silica, silica gel, synthetic aluminum silicates, synthetic
calcium silicates, diatomatious earth, anhydrous silicic acid
powder, aluminum hydroxide, barite, barium sulfate, gypsum, calcium
sulfate, polyamides, polyvinyl alcohol, polyvinylpyrrolidone,
polyvinylpyrrolidone vinyl acetate, and combinations thereof.
9. A liner-free label attached to a polyethylene terephthalate or
glass substrate, wherein the liner-free label comprises a polymeric
coating on a face sheet, wherein the polymeric coating comprises
one or more alkaline soluble polymers selected from the group
consisting of styrene-maleic anhydride resins, esters of
styrene-maleic anhydride resins, styrene-maleic anhydride amic acid
resins, styrene-maleic anhydride imide resins, ammonium and alkali
metal salts of styrene-maleic anhydride resins, and combinations
thereof and one or more emulsion polymers, wherein the one or more
alkaline soluble polymers are water-insoluble at neutral pH, and
wherein the polymeric coating serves as an adhesive composition
that attaches the label to the polyethylene terephthalate or glass
substrate.
10. The liner-free label of claim 9, wherein the face sheet is
printed or printable paper.
11. The liner-free label of claim 9, wherein the face sheet is a
printed or printable polymeric film.
12. The liner-free label of claim 10, wherein the label has greater
than 50% fiber tear after 2 minutes.
13. The liner-free label of claim 10, wherein the label has greater
than 75% fiber tear after 2 minutes.
14. The liner-free label of claim 9, wherein the label exhibits no
label drop-off after 72 hours immersed in ice water.
15. The liner-free label of claim 14, wherein the label has
complete label drop-off after soaking in 0.5% to 5% sodium
hydroxide solution at 65.degree. C. to 75.degree. C. for less than
5 minutes.
16. The liner-free label of claim 9, wherein prior to contact with
the substrate, the polymeric coating is activated by an activating
fluid to form the adhesive composition.
17. The liner-free label of claim 16, wherein the activation fluid
comprises water and one or more organic solvents.
18. The liner-free label of claim 17, wherein activation fluid
composition comprises 5% to 70% by weight of one or more low
boiling alcohol(s).
19. The liner free-label of claim 18, wherein the activation fluid
composition comprises 10 to 30% by weight of one or more low
boiling alcohol(s).
20. The liner-free label of claim 18, wherein at least one low
boiling alcohol is n-propanol or isopropanol.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a divisional of U.S. Ser. No.
14/310,913, filed Jun. 20, 2014, the disclosure of which is
incorporated herein in its entirety by reference.
FIELD OF THE INVENTION
[0002] This invention is in the field of automated labeling systems
for glass and plastic substrates, such as food and beverage
containers and containers for pharmaceuticals.
BACKGROUND OF THE INVENTION
[0003] Plastic and glass containers or bottles are prevalent in a
wide variety of shapes and sizes for holding many different types
of materials such as detergents, chemicals, motor oil, beverages,
etc. These containers are glass or plastic (mono or multi layers)
of polyethylene, polypropylene, polyester or vinyl along with other
specialty blends for specific barrier and product resistance
performance. These containers are typically provided with a label
which designates the trade name of the product and may contain
other information.
[0004] Labels designed to adhere to glass and/or polyethylene
terephthalate (PET) are typically applied using a cold or hot glue
application processes. During the automated bottle labeling, glue
(high viscosity, tacky liquid) is directly applied to the
preprinted label and then applied to the bottle. The use of glues,
however, requires extensive cleaning as the glue dries and
accumulates on the bottling line equipment. In some cases, the glue
must be heated prior to application, which requires additional
heating equipment and increases energy costs.
[0005] In addition to cold- and hot-glue applied labeling methods,
preprinted pressure sensitive adhesive (PSA) labels are also used.
These labels utilize a release liner to protect the preprinted
label face from interacting with the tacky PSA. The use of
traditional PSA labels results in several million pounds of liner
waste per year in the bottling industry. PSAs also lack
removability properties desirable in downstream recycling and
bottle reusing facilities.
[0006] Attempts to overcome these limitations have been described
in the literature. U.S. Pat. Nos. 6,306,242; 6,517,664; and
6,663,746 to Dronzek describe a labeling system for applying labels
to plastic and glass bottles. The labeling system includes applying
a layer of a hydrophilic solid material to a polymeric label to
form a hydrophilic layer on the polymeric label; applying water,
water containing a cross-linking agent or a water based adhesive
over the hydrophilic layer to form a fastenable polymeric label;
fastening the fastenable polymeric label to a glass, plastic or
metal container or surface; and curing the polymeric label on the
glass, plastic or metal surface or container.
[0007] U.S. Pat. No. 7,943,714 to Schneiders describes a labeling
system containing a blend of two or more polymers having different
hydrophilicities or using a polymer with repeat units having
carboxylic, sulfonic or phosphonic acid groups and/or their
salts.
[0008] Dronzek and Schneiders require the use of non-porous or
relatively non-porous face sheets, such as polypropylene, high/low
density polyethylene, polyethylene terephthalate, polystyrene,
polycarbonate, vinyl and compatibilized blends. Face sheets
prepared from these materials typically have a moisture vapor
transmission rate of less than about 150 g/m.sup.2/24 hr as
measured using the TAPPI T448 om-09 standard protocol. In fact,
Schneiders discloses that the use of porous face sheets, i.e.,
those having high moisture vapor transmission rates (MVTR) values,
with pressure sensitive adhesives is undesirable because the
finished labels exhibit poor wet tack and swimming. Similar
disadvantages are described in Dronzek.
[0009] There exists a need for a clean, liner-free labeling
solution for glass and polyethylene terephthalate (PET) automated
bottle labeling applications that provides long term label to
bottle adhesion when dry and long term adhesion when exposed to ice
water condition for extended time periods, particularly for
substrates having high MVTR values.
[0010] Therefore, it is an object of the invention to provide
improved liner-free labels that provide long-term adhesion to a
desired substrate, but can be readily removed when needed, such as
in standard recycling or reuse facilities.
[0011] It is yet a further object of the invention to provide
improved methods for applying a liner-free label to a
substrate.
[0012] It is a further object of the invention to provide a clean,
glue-free, liner-free labeling solution for glass and polyethylene
terephthalate (PET) automated bottle labeling applications that
provides long term label to bottle adhesion when dry and long term
adhesion when exposed to ice water conditions for extended time
periods.
[0013] It is also an object of the invention to provide a clean,
glue-free, liner-free labeling solution for glass and polyethylene
terephthalate (PET) automated bottle labeling applications that
provides long term label to bottle adhesion when dry and long term
adhesion when exposed to ice water conditions for extended time
periods wherein the labels can be readily removed when necessary
using methods readily available in bottle recycling and reuse
facilities.
SUMMARY OF THE INVENTION
[0014] Methods for applying a liner-free, or liner-less label, to a
substrate, particularly glass or plastic (e.g., PET) substrates are
described herein. The method includes applying an adhesive
composition, such as a polymeric coating, to a label face sheet,
activating the adhesive composition with an activating fluid, and
contacting the label to the substrate. The activating fluid is
preferably a mixture of water and one or more organic solvents,
such as low molecular weight alcohols. In some embodiments, the
face sheet has an MVTR value of at least about 160, 170, 175, 180,
185, 190, 195, or 200 g/m.sup.2/24 hr.
[0015] In some embodiments, the adhesive composition contains a
blend or mixture of polymers, such as homopolymers, copolymers,
terpolymers, etc., and combinations thereof. In particular
embodiments, the blend or mixture contains a non-blocking resin in
a continuous film that provides a non-blocking surface and an
emulsion/dispersion polymer which provides adhesion to the
substrate. The blend of the emulsion/dispersion polymer into the
non-blocking resin disrupts the polymer film and allows for
improved activation of the film by the activation spray.
[0016] Volatile-base neutralized resin solutions are used to
prepare aqueous solutions of the resin that dries to form a
water-insoluble film due to the evaporation of the base. The resin
provides the desired ice water resistance. The use of a
non-volatile base that remains in the polymeric film results in a
loss of ice water resistance. The sensitivity of the resin to base
allows for caustic removability of the label due to the dissolution
of the polymer in the base, which is important for recycling and
removal applications.
[0017] The moderate to high acid number of the resin provides the
base solubility needed to allow for the use of a water-based
solution combined with the caustic removability. The higher acid
number allows for ice water resistance as well. Lower acid number
resins typically have less resistance to ice water, especially over
longer durations, such as 24-72 hours or longer.
[0018] In other embodiments, the adhesive composition contains a
copolymer containing at least two monomers with different
hydrophilicities. The more hydrophilic monomer is referred to as
"the hydrophilic monomer" and the more hydrophobic monomer is
referred to as "the hydrophobic monomer". The hydrophilic and
hydrophobic monomers are selected to allow the at least one
hydrophilic monomer to have a characteristic of quick tack when
exposed to a hydrophilic solvent, such as water or other aqueous
solvent, while the at least one hydrophobic monomer has a
characteristic which enables strong adhesion to a paper or
polymeric substrate. Alternatively, independent polymers with
hydrophilic and hydrophobic functionality can be blended in various
ratios yielding polymeric mixtures with hydrophobic and hydrophilic
functionality.
[0019] The adhesive composition may contain hygroscopic particulate
fillers which enable fast exhaustion of the activation fluid out of
the adhesive when applied to a substrate. This allows the
hydrophobic monomers of the adhesive composition to achieve a
strong adhesive bond between the face sheet and substrate. The
particulate fillers may also provide fast absorption of the
activation fluid composition into the full thickness of the
adhesive composition and rapid swelling of not only the hydrophilic
part, but also the hydrophobic part, of the adhesive composition.
The particulate fillers may also function as anti-blocking agents
when liner-free label media are tightly wound in a roll or
stacked.
[0020] The compositions described herein can quickly go from a
non-tacky to a tacky state enabling the use of solvent-activated
glue-free, liner-free labels for label printing and labeling that
require both quick tack and strong adhesion. The activating fluid
is non-tacky, dries clean, and requires no additional maintenance
or clean up, e.g., to remove glue from the labeling machinery. The
ability of the non-tacky adhesive layer to be applied before,
during, or after label printing allows for flexibility in the work
flow and customization of the system. Further, applying the
adhesive layer as a coating during the printing of the label
provides manufacturing efficiencies resulting in waste and cost
reduction. In certain embodiments, the adhesive is engineered to be
compatible with application methods that are typically used to
print labels. This includes, but is not limited to, flexographic,
gravure, and offset printing methods. The resulting system allows a
standard printing press to be able to both print colors and coat
adhesive onto a web or sheet label in a single pass.
[0021] The adhesive compositions described herein may be used not
only on paper, cardboard, particle board, medium density
fiberboard, wood, manufactured wood products, and metal substrates,
but also on glass and plastics commonly used in commercial
applications including, but not limited to, polyethylene
terephthalate (PETE, PET, PETG), polyethylene (PE), polystyrene
(PS), low-density polyethylene (LDPE), linear low-density
polyethylene (LLDPE), high density polyethylene (HDPE),
polypropylene (PP), polyester, polyvinyl chloride (PVC) and
polyvinyl chloride films, and TYVEK.RTM., as well as other low
energy and thermoplastic substrates.
[0022] The performance of the adhesive can be evaluated using a
variety of assays including block resistance, peel strength and
percent fiber tear at 2 and 10 minutes, and tunneling and/or
swimming when immersed in an ice bath for 24 hours to 72 hours. The
performance of the adhesive in the peel strength and immersion
assays can vary depending on the activating fluid used to activate
the adhesive.
[0023] In some embodiments, the composition provides fair, good, or
excellent, preferably good or excellent, heat seal blocking
resistance and/or pressure blocking resistance; fair, good, or
excellent, preferably good or excellent peel strength on PET and/or
glass when activated by a cosolvent and/or water; and resists
swimming, tunneling, and/or edge lifting for at least 20 minutes, 1
hour, or two hours when immersed in an ice water bath.
[0024] The assays described herein qualitatively or quantitatively
describe the performance characteristics of the adhesive
compositions. For example, in some embodiments, the peel strength
of the adhesive on PET and/or glass when activated by an activating
fluid, such as 30% n-propanol (nPA), 30% isopropanol (IPA), or 10%
nPA is greater than about 100 grams/inch within about 5 minutes of
application to a substrate, preferably greater than about 200
grams/inch within about 2 minutes of application to a substrate,
more preferably greater than about 200 grams/inch within about 1
minute of application to a substrate. The activating fluid then
distributes into the hydrophobic regions resulting in their
swelling and ultimate adhesion to the substrate. This adhesion to
the substrate results in average peel test values in the range from
about 100 grams/inch to about 1,000 grams/inch, preferably from
about 200 grams/inch to about 1,000 grams/inch, more preferably
from about 400 grams/inch to about 1,000 grams/inch.
[0025] Alternatively, the adhesive can be evaluated using the fiber
tear test. In some embodiment, the labels exhibit a paper tear
greater than about 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95% after
one, two, three, four, five, six, seven, eight, nine, or 10 minutes
or longer. In particular embodiments, the labels exhibits a paper
tear greater than 60, 65, 70, 75, 80, 85, 90, or 95% after two
minutes and 10 minutes. These tear strengths can be achieved using
paper-based or polymer or synthetic based face sheets. However,
these tear strengths are often unnecessarily high for polymer and
synthetic based face sheets.
[0026] Kits containing the adhesive formulations are also described
herein. The kit can contain only the adhesive formulation. The kits
can contain the adhesive formulation and uncoated labels. The kits
can contain paper or synthetic (polymeric film) labels which have
been coated with the adhesive formulation and the activating fluid.
The kits can contain coated labels, activating fluid, and an
activation apparatus used to apply the activating fluid to the
solvent-sensitive adhesive layer.
[0027] The compositions, methods, and kits described herein offer
significant ecological benefits compared to the prior art as well
as products currently commercialized in particular markets. For
example, the compositions, methods, and kits described herein
eliminate the liner backing which is a waste byproduct of
liner-backed pressure sensitive adhesive labels. This reduces
landfill waste and eliminates the energy and carbon emissions from
the production of liner backing and the shipment of the material to
suppliers and customers.
[0028] In addition, the compositions, methods, and kits described
herein eliminate the silicone release layer which is either
disposed of on the liner backing in liner-backed pressure sensitive
adhesive labels or on the top of the printed layer of liner-less
pressure sensitive adhesive labels. In either existing art, the
silicone presents an energy intensive manufacturing process and the
addition of a petrochemical derivative product that is unnecessary
and eliminated by the compositions, methods, and kits described
herein, thereby reducing the carbon footprint of the label and the
requirement for silicone to be utilized in the label manufacturing
process. The system described herein also eliminates the need for
wet or hot glue application processes as described above, which
avoids the necessary extensive cleaning as the glue dries and
accumulates on the bottling line equipment.
[0029] The labeling system described herein provides labels which
exhibit sufficient peel strength to glass and/or plastics, such as
PET, and removability properties which are desirable in downstream
recycling and bottle reusing facilities.
DETAILED DESCRIPTION OF THE INVENTION
I. Definitions
[0030] "Hydrophilic", as used herein, refers to one or more
monomers or polymers (e.g., homopolymers or copolymer) in the
adhesive composition or mixture having a greater affinity for water
than one or more other monomers or polymers (e.g., homopolymers or
copolymer) in the adhesive composition or mixture. Hydrophilicity
can be quantified by measuring its partition coefficient between
water (or a buffered aqueous solution) and a water-immiscible
organic solvent, such as octanol, methylene chloride, or methyl
tert-butyl ether. If after equilibration a greater concentration of
the compound is attained in water than in the organic solvent, then
the compound is considered hydrophilic. Hydrophilicity can also be
evaluated using water contact angle. Generally, hydrophilic
surfaces exhibit a water contact angle of less than about
90.degree..
[0031] "Hydrophobic", as used herein, refers to one or more
monomers or polymers (e.g., homopolymers or copolymer) in the
adhesive composition or mixture having less affinity for water than
one or more other monomers or polymers (e.g., homopolymers or
copolymer) in the adhesive composition or mixture. Hydrophobicity
can be quantified by measuring its partition coefficient between
water (or a buffered aqueous solution) and a water-immiscible
organic solvent, such as octanol, methylene chloride, or methyl
tert-butyl ether. If after equilibration a greater concentration of
the compound is attained in the organic solvent than in water, the
compound is considered hydrophobic. Hydrophobicity can also be
evaluated using water contact angle. Generally, hydrophobic
surfaces exhibit a water contact angle of greater than about 90,
95, 100, 105, or 110.degree..
[0032] "Tack" or "quick tack", as used herein, refers to
instantaneous or nearly instantaneous formation of a bond between
an adhesive and surface when brought into light contact for a very
short period, e.g., less than five second. Tack properties are
dependent, at least in part, on the viscoelastic flow
characteristics of the polymer adhesive system. In a system where a
volatile solvent-based activation method is being employed, it is
possible for the system to possess initial tack when the adhesive
is in a moist state and no tack (but still be well adhered to a
substrate through adhesive bonding) once the moisture has
evaporated or been removed. Tack is particularly relevant where
bonds must immediately sustain forces after assembly. Tack forces
are particularly significant in maintaining bond strength to low
surface energy substrates when chemical or mechanical bonding
processes do not readily occur. Tack measurement methods are
typically application specific, however the Standard Test Method
for Tack of Pressure-Sensitive Adhesives by Rolling Ball (D3121-06)
as developed by the American Society for Testing and Materials
(ASTM) provides a reliable measurement method. In this method a
ball of a fixed size is rolled down a ramp of a fixed height and
propelled onto a tacky label. The distance the ball travels across
the label provides a measure of tack. "No tack" or "non-tacky"
means that there is no such instant contact bond or adhesion
between the adhesive and the substrate.
[0033] "Blocking" refers to the formation of a bond between the
adhesive layer of the label and the face of an adjacent label when
the label is in roll or stacked form.
[0034] "Adhesion" or "adhesive bonding", as used herein, refers to
the longer term bond between the adhesive and the substrate and/or
another adhesive. Adhesion, unlike tack, focuses on the bond
created between a surface and a substrate (which can also be
another adhesive) that is not dependent upon the viscoelastic flow
characteristics of the adhesive.
[0035] Good adhesive tack (the combination between adhesion and
tack) is achieved when the adhesive strength is greater than the
cohesive strength of the adhesive system. A bond of adequate
strength can be formed and maintained using adhesive forces, tack
forces, or a combination of the two; however, bond formation is not
limited by these forces. Peel strength is a force measure of both
tack and adhesive forces. ASTM Standard D3330 (Standard Test Method
for Peel Adhesion of Pressure-Sensitive Tape) provides an accurate
measure of peel strength. For a particular substrate, average peel
test values range from about 100 grams/inch to about 1,000
grams/inch, preferably from about 200 grams/inch to about 1,000
grams/inch, more preferably about 400 grams/inch to about 1,000
grams/inch to achieve adequate adhesion.
[0036] "Open time" as used herein, refers to the amount of time
between the activation of the adhesive and the application of the
label to a substrate.
[0037] "Resin", as used herein, generally refers to polymeric
solutions that consist of a single phase, as in a solution of the
polymer dissolved in a solvent. When cast into a film, these
materials can form a continuous phase as the solvent
evaporates.
[0038] "Emulsion/dispersion polymer", as used herein, generally
refers to liquids consisting of a continuous aqueous phase in which
polymeric particles are distributed. The term "emulsion" is used to
refer to such solutions where the polymer is dispersed as a liquid
or in a high flow/soft state. In contrast, dispersions refer to
such solutions in which the polymer is dispersed as a hard solid.
When the film is cast, the polymeric particles can coalesce to form
a continuous film or remain as discreet particles.
[0039] "Non-blocking", as used herein, generally refers to the
property of a polymeric film to show no tendency to form a bond
between the adhesive layer of the label and the top of an adjacent
label when the label is in roll or stacked form.
[0040] "Acid number", as used herein, refers to the mass of
potassium hydroxide (KOH) in milligrams that is required to
neutralize one gram of the polymer or polymers. The acid number is
a measure of the amount of carboxylic acid groups in the
polymer(s). In a typical procedure, a known amount of sample is
dissolved in organic solvent and titrated with a solution of
potassium hydroxide of known concentration and containing a color
indicator.
II. Methods for Applying Glue-Free, Liner-Free Labels to Glass or
Plastic Substrates
[0041] Methods for applying a liner-free, or liner-less label, to a
substrate, particularly glass or plastic (e.g., PET) substrates are
described herein. The method includes applying an adhesive
composition, such as a polymeric coating, to a label face sheet,
activating the adhesive composition with an activating fluid, and
contacting the label to the substrate. The activating fluid is
preferably a mixture of water and one or more organic solvents,
such as low molecular weight alcohols.
[0042] A. Face Sheets
[0043] Unlike other water and solvent activated labels and adhesive
systems, the adhesive compositions described herein can be applied
to a variety of face sheets, with a variety of MVTR of the face
sheet. In particular embodiments, the MVTR of the face sheet is at
least about 160, 170, 175, 180, 185, 190, 195, or 200, 210, 220,
225, 230, 240, 250, 260, 270, 275, 280, 290, 300, 325, 350, 400,
425, 450, 475, 500, 525, 550, 575, or 600 g/m.sup.2/24 hr as
measured using TAPPI T448 om-09 standard protocol. MTVR for
uncoated paper is reported at 620-670 g/m.sup.2/24 hr.
[0044] Suitable face sheets include, but are not limited to, paper,
coated one side paper, coated two side paper, top-coated and
non-top-coated grades of direct thermal paper, thermal transfer
paper, polymer films, woven and non-woven synthetic materials,
wood, manufacture wood products, metal films, composite films,
plastics (i.e. polyester, polypropylene, or polyethylene),
metalized paper, and mylar. In some embodiments, the faces sheet is
a laminate, such as used to apply to furniture. The face sheet for
furniture lamination can be formed from any suitable laminate
material, including but not limited to, wood, manufacture wood, and
synthetic materials. In some embodiments, the face sheets can be
printed on with a suitable printing device. In other embodiments,
the adhesive side of the label can receive dye/ink/pigment from a
printing device, for example, printer registration marks. In
particular embodiments, the face sheet is printed or printable
paper or printed or printable polymeric film.
[0045] B. Substrates
[0046] The adhesive compositions described herein can be used to
adhere coated labels to a variety of substrates. Suitable
substrates include, but are not limited to, paper, cardboard,
particle board, medium density fiberboard, wood, manufacture wood
products, and metal, glass and plastics commonly used in commercial
applications including, but not limited to, polyethylene
terephthalate (PETE, PET, PETG), polyethylene (PE), polystyrene
(PS), low-density polyethylene (LDPE), linear low-density
polyethylene (LLDPE), high density polyethylene (HDPE),
polypropylene (PP), polyester, polyvinyl chloride (PVC) and
polyvinyl chloride films, and TYVEK.RTM., as well as other low
energy and thermoplastic substrates. Other substrates include
porous substrates, such as natural or synthetic textiles and
cellulosic fiber-based substrates. In particular embodiments, the
substrate is glass or plastic, particularly PET.
[0047] In some embodiments, the adhesives are designed to adhere to
a single specific substrate but do not adhere to other substrates.
In one embodiment, the adhesive can be designed to have a specific
strength of adhesion and/or mode of failure. For example, the
adhesive bond has a lower failure point than the construct of the
face sheet. In other embodiments, the adhesive is designed to
adhere to a variety of substrates with little or no modification of
the adhesive formulation.
[0048] The adhesive composition (or blend) can be applied to the
above-listed face sheets utilizing typical web coating methods
including, but not limited to, knife over roll, gravure,
reverse-gravure, metering rod, slot die, and air knife coating
methods.
[0049] The coat weight of the adhesive composition on the face
sheet is largely dependent upon the end use application of the
solvent sensitive adhesive label. To reduce cost, coat weights of 3
dry grams of adhesive per square meter are typically used. However,
coat weights up to 25 dry grams per square meter may be also be
used. Preferred coat weight ranges between 6 dry grams of adhesive
per square meter to 12 dry grams of adhesive per square meter.
[0050] After the application of the adhesive composition to the
face sheet web, the remaining water and solvent is extracted from
the adhesive composition. This may be accomplished using
conventional methods including, but not limited to, air flotation
oven, roller supported web oven, and energy cure methods (for
example, infrared heaters and dryers).
[0051] Optionally, it may be desirable to coat thermally activated
paper and films. Care must be taken in adhesive selection to ensure
that the components formulating the adhesive composition do not
contain certain chemistries or solvents that negatively interact
with the embedded thermal dye. In addition, during the drying (or
solvent removal) process, the heat or energy from the process
should not activate the thermal paper (a processes known as
imaging).
[0052] Sometimes the coating of a web with an adhesive can induce a
phenomenon known as a shape memory or curling. As it is often
important for end applications that labels have lay flat
properties, a number of additives can be added to the adhesive
formulation to prevent curl, as described earlier. Suitable curl
preventing additives include, but are not limited to glycerol,
ethylene glycol, propylene glycol, or polyethylene glycol
(molecular weight range from 150 to 10,000). In addition,
mechanical methods can be employed to reduce curl, such as a
bending bar or mechanical embossing. Also, the addition of
vaporized water (or other liquid vapors) to the non-adhesive coated
side of the label can have dramatic effects in reducing curl.
[0053] C. Coated Labels
[0054] In one embodiment, the final product is a label having three
layers: a first layer which is printable, a second layer of face
stock material, and then a third layer of adhesive composition
described herein, e.g., coated on one surface of the face stock.
Preferably, there is a continuous phase composed of a homogenous
mix of all adhesive polymers with a uniform dispersion of the
filler. In some embodiments, the filler particles are localized to
the surface of the film; in others, they are localized to the
interface between the paper and the adhesive or distributed
uniformly in the z-axis. In all embodiments, the adhesive portion
of the liner-free label is in a non-tacky state prior to activation
by the activating solution.
[0055] Adhesive compositions containing one or more of the
copolymers described herein exhibit higher peel strengths,
particularly on glass and plastic substrates, such as PET, than
materials containing one or more hydrophilic or one or more
hydrophobic materials alone.
[0056] D. Adhesive Compositions
[0057] The adhesive compositions described herein can contain a
single polymer (e.g., homopolymers, copolymer, terpolymer, etc.) or
a mixture of polymers, such as homopolymers, copolymers,
terpolymers, etc., and combinations thereof. Additives, such as
hygroscopic particulate fillers, can be incorporated into the
adhesive composition for the generation of both quick tack and
longer term adhesion upon activation by an aqueous or solvent-based
solution for adhesion to a variety of substrates, such as paper,
cardboard, metal, as well as glass and plastics, particularly glass
and polyethylene terephthalate substrates, such as bottles.
[0058] Hygroscopic agents (e.g., particulate fillers) in the
adhesive formulations can modulate the kinetics of the distribution
of water and/or the activation fluid throughout the adhesion
composition to achieve the desired adhesive behavior and
performance of the glue-free, liner-free label. Kinetics may also
be modified by the degree of hydrophilicity and hydrophobicity of
the polymers in the adhesive layer.
[0059] 1. Polymer Blends/Mixtures
[0060] In one embodiment, the adhesive composition contains a blend
or mixture of a polymeric resin and an emulsion/dispersion polymer.
The polymers can be homopolymers, copolymers, terpolymers, etc.,
and combinations thereof. In particular embodiments, the blend or
mixture contains a non-blocking resin in a continuous film that
provides a non-blocking surface and an emulsion/dispersion polymer
which provides adhesion to the substrate. The blend of the
emulsion/dispersion polymer into the non-blocking resin disrupts
the polymer film and allows for improved activation of the film by
the activation spray.
[0061] a. Polymeric Resin
[0062] The blends typically contain a continuous phase,
film-forming polymeric resin. The resin should be non-blocking. The
film-forming polymeric resin can be water-soluble or insoluble,
alkali soluble, or combinations thereof. In particular embodiments,
the resin is water-insoluble which provides resistance to label
removal when immersed in a cold water bath but is alkali soluble
which allows for removal of the label facilitating recycling of the
substrate (e.g., glass or plastic container, such as a bottle).
[0063] The resin polymer should form a continuous phase in which
the other components of the adhesive composition (e.g., emulsion or
dispersion polymer, etc.) will be dispersed when dried. This
arrangement allows for any tack found in the emulsion/dispersion
polymers to be hidden from the surface of the film by the
continuous phase polymer, which will prevent blocking. These
polymers should be non-tacky and either fully or partially soluble
in the activation spray.
[0064] For increased humidity resistance, resin polymer or polymers
that are soluble in alkaline or acidic aqueous environments, but
insoluble in aqueous environment at neutral pH, and have some
sensitivity to solvent is preferred since environmental moisture
will have no effect on their physical properties. The pH-dependent
solubility of the resin polymers improves coating stability and
sensitivity to solvent facilitates activation.
[0065] Suitable resins include, but are not limited to,
styrene-maleic anhydride resins, esters of styrene-maleic anhydride
resin, styrene-maleic anhydride amic acid resin, styrene-maleic
anhydride imide resin, ammonium and alkali metal salts of
styrene-maleic anhydride resin, polymers based on polyvinyl
acetate, copolymers of polyvinyl pyrrolidone, and acrylic
copolymers of styrene and acrylic acid. In particular embodiments,
the resin is or includes styrene-maleic anhydride.
[0066] Suitable solvent choices for solubilizing the alkaline
soluble resin include, but are not limited to, aqueous solutions of
sodium hydroxide, potassium hydroxide, ammonium hydroxide,
monoethanolamine, diethanolamine, triethanolamine, primary amino
alcohols, for example; 2-amino-2-methyl-1-propanol,
2-amino-1-butanol, Tris(hydroxymethyl)-aminomethane, and
2-amino-2-ethyl-1,3-propanediol, and additionally, ethylamine and
propylamine.
[0067] The concentration of the resin can vary depending on the
adhesion and tack of the emulsion/dispersion polymer and the
continuous phase formation of the resin polymer. If the emulsion
polymer is relatively non-tacky/blocky, then less resin polymer can
be used. In contrast, if the emulsion polymer is very tacky, more
resin polymer is likely needed. The other required properties of
the label also need to be considered (e.g., caustic resolubility,
ice water resistance, manufacturability, etc.). In some
embodiments, the resin polymer is present in an amount of about 75%
or less by weight of the adhesive composition, such as about 10% to
about 70% by weight, preferably 25% to about 65%, preferably 30% to
about 60% by weight. The concentration of the resin can be less
than 10% or greater than 75% in view of the requirements/properties
discussed above.
[0068] b. Emulsion/Dispersion Polymer
[0069] The blend or mixture also contains an emulsion or dispersion
polymer. This polymer forms a discrete phase dispersed in the
continuous phase polymeric resin. The emulsion or dispersion
polymer provides the adhesion of the label to the substrate. The
film-forming resin encapsulates the emulsion/dispersion polymer to
provide a non-tacky surface which allows for storage of the labels
as rolls or stacks. However, the blend of the emulsion/dispersion
polymer into the non-blocking resin disrupts the continuous polymer
film and allows for improved activation of the film by the
activation spray to provide the necessary adhesion to affix the
label to the substrate. The emulsion or dispersion polymer is
generally hydrophobic or more hydrophobic than the resin polymer.
The emulsion or dispersion polymer can adhere to the surface
through a variety of interactions/mechanisms, including, but not
limited to, hydrogen bonding or other intermolecular forces, such
as hydrophobic interactions.
[0070] Suitable emulsion polymers include, but are not limited to,
styrene acrylic emulsion polymers, natural and reclaimed rubbers,
polyurethanes, non-carboxylated and carboxylated styrene-butadiene
rubbers, polyacrylates based on the polymerization of monomers of
methacrylates, methyl acrylate, ethyl acrylate, 2-chloroethyl vinyl
ether, 2-ethylhexyl acrylate, hydroxyethyl methacrylate, butyl
acrylate, butyl methacrylate or combinations of the previous,
polyamides, polyesters, polyolefins, polyolefins containing maleic
anhydride, polystyrenes, polyvinyl esters, polyvinyl ketones,
polydiene elastomers, polyisobutylenes, poly butadienes,
polychloroprenes, as well as combinations of the above materials.
Other material(s) having the desired long-term adherence
characteristic may also be used. In particular embodiments, the
emulsion or dispersion polymer is or includes styrene acrylic
emulsion polymers.
[0071] The concentration of the emulsion/dispersion polymer can
vary depending on the adhesion and tack of the emulsion/dispersion
polymer and the continuous phase formation of the of the resin
polymer. In some embodiments, the emulsion or dispersion polymer is
present in an amount of about 40% or greater by weight of the
adhesive composition, such as about 50% to about 90% by weight,
preferably 50% to about 80%, preferably 60% to about 80% by weight.
The concentration of the resin can be less than 40% or greater than
90% in view of the requirements/properties discussed above for the
resin and the emulsion/dispersion polymer. The concentration of the
resin and/or emulsion dispersion polymer can be varied due to the
presence of additives which modify the properties of the adhesive
composition.
[0072] c. Polymer Properties
[0073] The resin, emulsion/dispersion property, and/or copolymer
can vary in terms of molecular weight, acid number, and/or glass
transition temperature based on the monomers use to form the
polymers. In some embodiments, the weight average molecular weight
of the resin and/or emulsion/dispersion polymer is from about 5,000
Daltons to 1,000,000 Dalton, preferably from about 5,000 Daltons to
about 500,000 Daltons, more preferably from about 5,000 Daltons to
about 250,000 Daltons. In some embodiments, the weight average
molecular weight is from about 5,000 Dalton to about 30,000
Daltons. In other embodiments, the weight average molecular weight
is greater than about 200,000 Daltons. In particular embodiments,
the polymer is a styrene-acrylic copolymer having a weight average
molecular weight from about 5,000 Dalton to about 25,000 Daltons or
greater.
[0074] For those copolymers containing acidic functional groups,
such as acrylic acid monomers, the acidity of the polymer can be
measured by determining the acid number. In those embodiments where
the adhesive composition contains an alkaline soluble resin and an
emulsion or dispersion polymer, the resin has an acid number from
about 75 mg KOH/g polymer to about 500 mg KOH/g polymer, preferably
from about 100 mg KOH/g polymer to about 250 mg KOH/g polymer and
the emulsion/dispersion polymer has an acid number from about 0 mg
KOH/g polymer to about 70 mg KOH/g polymer, preferably from about
40 mg KOH/g polymer to about 60 mg KOH/g polymer.
[0075] The glass transition temperature of the polymer typically
varies from about -50.degree. C. to about 200.degree. C. In some
embodiments, the glass transition temperature is from about
-50.degree. C. to about -15.degree. C., from 0.degree. C. to about
10.degree. C., from about 40.degree. C. to about 90.degree. C. or
from about 200.degree. C. to about 225.degree. C. In those
embodiments where the adhesive composition contains an alkaline
soluble resin and an emulsion or dispersion polymer, the resin has
a Tg from about 40.degree. C. to about 160.degree. C., preferably
from about 100.degree. C. to about 130.degree. C. and the emulsion
polymer has a Tg from about +10.degree. C. to about -80.degree. C.,
preferably from about -10.degree. C. to about -60.degree. C., more
preferably from about -15.degree. C. to about -50.degree. C. In
general, higher Tg polymers will have better heat-seal blocking
resistance but the use of lower Tg emulsion polymers is suitable if
the emulsion polymer is entrapped within a continuous phase of a
higher Tg alkaline soluble resin.
[0076] E. Hygroscopic Particulate Fillers
[0077] Hygroscopic particulate fillers can be added to the
composition to enhance the adhesive performance of the hydrophobic
and hydrophilic materials. The use of such hygroscopic agents is
beneficial as a means to enhance the penetration of water into the
adhesive layer on a label as well as to control the kinetics of
adhesive activation based on the distribution and redistribution of
the activation fluid (or solvent) into both the hydrophilic and
hydrophobic regions of the adhesive. In order for the adhesives to
transition from their non-tacky to tacky state, they require a
certain amount of water and/or solvent moisture to be present
within the material. The retention of this moisture can be utilized
as a mechanism to preserve viscoelastic flow of the polymer layer
and in turn create a tacky label. However, excessive moisture can
prevent the contact of the adhesive with the substrate by acting as
a physical barrier to the generation of adhesive interactions
resulting in the migration of the label from the desired
application area on a substrate during down-stream processing. An
added benefit of the use of hygroscopic agents is their ability to
reduce the phenomena of `blocking` in self-wound rolls of labels
having a surface coated with the adhesive composition described
herein.
[0078] These hygroscopic particulate filler materials are typically
available as colloidal suspensions in a variety of solvents or as
solids and are incorporated into the final adhesive composition at
the desired concentrations. Concentrations of the suspensions are
typically in the range of 10% to 90% solids (weight of solids in
the suspension to volume of liquid phase of suspension) in either
an aqueous or solvent based suspension and present in the final dry
film in a ratio from 1% to 25% (weight of dry solids in film as a
ratio of other components dry weight in film). However,
concentrations below or above this range are possible depending on
the composition and/or the desired application.
[0079] Care should be taken to prevent the flocculation of these
hygroscopic agents during adhesive preparation and storage since
these agents are often micro- and nanoparticles, which are prone to
aggregation due to their high surface area to volume ratios.
Generally, particles within the particulate fillers may have the
largest particle dimension between 0.005 .mu.m (micrometers) and 15
.mu.m, more preferably between 0.005 .mu.m and 10 .mu.m, and most
preferably between 0.005 .mu.m and 5 .mu.m. As used herein, the
term "largest particle dimension" refers to the longest linear
dimension between two points on the particle.
[0080] Methods to ensure the homogenous distribution of these
agents in suspension can include the use of agitation, surfactants,
temperature and/or pH. The pre-saturation or treatment of the
hygroscopic agents using solvents, water, and/or adhesive
components is also possible to alter their affinity for different
components of the activating solution.
[0081] Suitable hygroscopic particulate fillers include, but are
not limited to, alumina, alumina gel, boehmite, pseudoboehmite,
clay, calcium carbonate, chalk, magnesium carbonate, kaolin,
calcined clay, pyropylate, bentonite, zeolite, talc, silica, silica
gel, synthetic aluminum silicates, synthetic calcium silicates,
diatomatious earth, anhydrous silicic acid powder, aluminum
hydroxide, barite, barium sulfate, gypsum, calcium sulfate, and
organic particles, such as hydrophilic and/or hydrophobic polymeric
beads including but not limited to polyamides, polyvinyl alcohol,
polyvinylpyrrolidone, polyvinylpyrrolidone vinyl acetate and other
similar materials as well as combinations of the above
materials.
[0082] F. Polymer Solvents
[0083] Solvent(s) can be added to the composition as means for
formulating the copolymer. For example, solvent(s) can be added to
mirror the composition of the solution of the activating fluid to
enhance the rapid swelling of the label and quick tack adhesion
forces following the exposure of the adhesive layer to the
activating fluid. By including the chemistry of the activating
solution during the deposition process, the surface of the adhesive
can be modified to promote the penetration of the activating
solution into the adhesive layer for activation. Furthermore, the
incorporation of solvents, particularly those that are less viscous
and/or have higher vapor pressures, allows for the deposition of
more consistent and uniform adhesive films on the labels.
Furthermore, some solvents may be able to prevent any adverse
effects of the adhesive layer deposition process on the front side
of the label, which must remain pristine for optimal label print
quality.
[0084] Care must be taken to insure that the solvent selected does
not damage or deform the substrate being coated. In one embodiment,
thermally activated paper is coated with a water based solvent
system as primary alcohol, glycols, and acetates tend to damage or
activate the thermal ink. Solvents may include, but are not limited
to, water, ethanol, isopropanol, n-propanol, methyl ethyl ketone,
toluene, methylene chloride, and/or coalescing agents including
polyethylene glycol, glycol ethers, and fatty alcohols. In some
embodiments, the copolymer is formulated as a water-based emulsion
or dispersion.
[0085] G. Activating Fluids
[0086] The activating fluid composition provides optimal activation
of the adhesive component(s) of the layer of adhesive composition
of the liner-free label. The activating fluid composition must
penetrate into the adhesive layer to moisten the hydrophilic and
hydrophobic adhesive monomers without over-wetting the adhesive
surface of the label, which can compromise adhesive performance. In
addition, the activating fluid composition needs to be compatible
with mechanisms for applying activating fluids onto a liner-free
label, such as in stand-alone systems, label printers, labeling
lines, or other apparatuses. The activating fluid composition
should also be safe, non-toxic and comply with the guidelines
established by regulatory boards for their intended purpose.
[0087] The purpose of the activating fluid (or solution) is to
introduce moisture into the adhesive layer to allow for the
conversion of the adhesive from its non-tacky to tacky state.
However, given the selection of both hydrophilic and hydrophobic
adhesive monomers, one must account for the chemistries of the two
or more polymers and the solvent used in the deposition process for
enabling optimal activation. As described previously, the
activating fluid needs to penetrate into the hydrophilic regions of
the adhesive layer to generate quick tack then redistribute and
remain in the hydrophobic regions to maintain ultimate tack and
long-term adhesion.
[0088] Suitable solvents include, but are not limited to, water;
acetone; acetonitrile; lower alcohols (i.e., having from 1-10
carbons) including, but not limited to, methanol, ethanol,
isopropyl alcohol, n-propanol, n-butanol, 2-butanol, isobutanol,
2-methy-2-butanol, n-pentanol, n-hexanol, 2-hexanol, cyclohexanol,
n-heptanol, n-octanol, n-nonanol, n-decanol; glycols including, but
not limited to, propylene glycol, ethylene glycol, and butylene
glycol; fatty alcohols (i.e., having more than 10 carbons)
including, but not limited to, undecanol, dodecanol,
1-tetradecanol, arachidyl alcohol, docosanol, tetracosanol,
hexacosanol, octanosol, triacontanol, cetyl alcohol, stearyl
alcohol, and polycosinol; ketones, such as methyl ethyl ketone;
esters, such as lower (i.e., having from 1-10 carbons) acetates
including, but not limited to, methyl acetate, ethyl acetate,
n-propyl acetate, isopropyl acetate, isobutyl acetate, sec-Butyl
acetate, tert-Butyl acetate, 3-methyl-1-butyl acetate; mineral
spirits; oils, such as linseed oil and vegetable oil; citrus based
solvents, such as limonene, other primary, secondary, and tertiary
alcohols, and combinations thereof.
[0089] Low volatile solvents, such as ethylene glycol and propylene
glycol, are particularly useful in extending the latency
period.
[0090] Low surface energy solvents, such as isopropyl alcohol are
particularly effective in increasing wet out on hydrophobic and/or
low surface energy substrates.
[0091] The polymer selection for the adhesive formulation can be
such that the activation solvent required to activate the label is
water. However, selecting polymers that only require water to
rapidly transition from non-tacky to active may not be desirable as
the finished labels are highly vulnerable to blocking due to
absorption of atmospheric moisture, causing a transition from the
non-tacky state to the tacky state.
[0092] Therefore, in one embodiment, the activating fluid contains
at least two or more solvents. The first solvent or component is
water or an aqueous solution which allows for rapid wetting and
swelling of the hydrophilic regions of the adhesive to generate the
quick tack responsible for the initial adhesion of the label to the
substrate. However, as the water is drawn into the hygroscopic
filler, quick tack is lost and must be replaced by ultimate or
long-term tack, derived from the hydrophobic regions, which exhibit
some swelling behavior in water. Thus, a second solvent or
component is a non-aqueous (non-water) solvent containing
hydrophobic chemical moieties which enhances the activation of the
hydrophobic regions by increasing the permeability of the
activating fluid into these regions. In a particular embodiment,
the non-aqueous solvent is partly miscible or fully miscible with
water. By using a mixture of solvents, the swelling of the
hydrophilic regions can increase the surface area of the
hydrophobic regions exposed for solvent penetration, resulting in
the more rapid generation of ultimate tack. An optional third
solvent or component, which preferably is a volatile material, may
be used to aid in the removal of excess moisture from the adhesive
layer to promote stronger adhesion.
[0093] In one embodiment, the solvent contains between about 1% and
about 70%, preferably about 5% to about 70%, more preferably from
about 10% to about 60%, most preferably about 10% to about 50% by
weight of a non-toxic organic solvent in an aqueous solution. Care
should be taken to match the polymer adhesive layer with suitable
solvents that will activate the layer within the parameters
discussed above. In a particular embodiment, the activation
composition is a mixed solvent system with 5-70% w/w alcohol in
water, preferably 10-50%, more preferably 20-40%, most preferably
about 30% w/w mix of an alcohol in water. However, any polar
solvent with some water miscibility containing hydrophobic chemical
moieties may also be used. In particular embodiments, the solvent
is a mixture of water and n-propanol, isopropanol, or combinations
thereof. The concentration of the alcohol(s) can be about 1%, 2%,
5%, 10%, 15%, 20%, 25%, 30%, 35%, or 40% by weight of the
fluid.
[0094] The solvent system can be varied for a particular adhesive
composition in order to vary the properties of the adhesive
composition. For example, the examples below show that the
activating solvent can be varied to correlate with the selected
hydrophilic and/or hydrophobic materials to achieve the desired
performance. Generally, a solvent is a liquid fluid that either
solubilizes or swells polymeric components of a solvent sensitive
film. A non-solvent is a liquid fluid that does not solubilize or
swell the polymeric components of a solvent sensitive film. In one
embodiment, non-solvent can be incorporated into the activation
fluid to reduce the overall average peel adhesion of the label. In
another embodiment, solvent with a vapor pressure greater than that
of water at a given temperature can be incorporated into the
activation fluid to lower the amount of time required to achieve
acceptable ultimate adhesion values.
[0095] To decrease surface tension, enhance solvent spreading on
the adhesive film surface, and/or promote activating solvent
penetration, surfactants may be added to the activating fluid.
Surfactants may also help in the delivery of the activating fluid
by allowing for the creation of finer mists with smaller particle
sizes during atomization (when used to apply the activating fluid
to the adhesive layer of a label) which can promote adhesive
activation by increasing the surface area for the interaction
between the activating solution and the adhesive layer. Classes of
surfactants that can be used include anionic, cationic, non-ionic
and amphoteric surfactants. Specific examples include lecithin,
Span.TM.-60, Span.TM.-80, Span.TM.-65, Tween.TM.-20, Tween.TM.-40,
Tween.TM.-60, Dynol.TM. 604 (Air Products), Surfynol.TM. (Air
Products), Pluronics.TM. (BASF, Germany), Polysorbates.TM.
(Tween.TM.), Sodium dodecyl sulfate (sodium lauryl sulfate), Lauryl
dimethyl amine oxide, Cetyltrimethylammonium bromide (CTAB),
Polyethoxylated alcohols, Polyoxyethylene sorbitan, Octoxynol.TM.
(Triton X100.TM.), N, N-dimethyl-dodecylamine-N-oxide,
Hexadecyl-trimethylammonium bromide (HTAB), Polyoxyl 10 lauryl
ether, Brij.TM. 721 .TM., Bile salts (sodium deoxycholate, sodium
cholate), Polyoxyl castor oil (Cremophor.TM.), Nonylphenol
ethoxylate (Tergitol.TM.), Cyclodextrins, Lecithin, or
Methylbenzethonium chloride (Hyamine.TM.).
[0096] H. Other Additives
[0097] Additives may incorporated into activating fluid, such as
acids, bases, buffers, antimicrobial agents, stabilizers,
emulsifiers, and/or defoaming agents, as needed for the particular
application.
[0098] Other additives may be added into the adhesive composition
to modulate the performance of the liner-free labels. These
additives may be selected for a variety of purposes, such as
enhancing water penetration, reducing blocking, increasing quick
tack and/or long-term adhesion as well as improving latency (the
time between label activation and application). Potential classes
of additives include, but are not limited to, colorants, both dye
and pigment based, salts, sugars, other carbohydrates,
polyelectrolytes, proteins, dry and liquid surfactants, resins,
wetting agents, additive that provide desired lay flat properties
of the labels, such as humectants, polyethylene glycol, and/or
salts, other similar materials as well as combinations thereof.
These additives can be incorporated into one or both of the polymer
components, the polymer solvent, the activating fluid, or
combinations thereof.
[0099] In particular, the use of non-volatile solvents,
plasticizers, coalescents, oligomers, and/or polymers in the
activation may extend the open time of a given adhesive
composition. The additives in the activation spray should not clog
the applicator used to apply the activation spray and should not
require excessive cleanup.
[0100] I. Adhesive Performance
[0101] The performance of the adhesive can be evaluated using a
variety of assays including block resistance, peel strength,
percent fiber tear and label edge peel, tunneling, and/or swimming
when immersed in an ice bath. The performance of the adhesive in
the peel strength, percent fiber tear and immersion assays can vary
depending on the activating fluid used to activate the adhesive.
Results of these assays on a variety of adhesive compositions are
shown in Table 1 in the examples.
[0102] The labels coated with the adhesive compositions described
herein exhibit
[0103] (1) peel ratings of good or excellent, preferably excellent,
at two minutes;
[0104] (2) percent fiber tear from about 50% to about 100%,
preferably greater than about 75%, at two minutes;
[0105] (3) heat seal blocking of good or excellent, preferably
excellent, which indicates no interaction of the face sheet with
the non-tacky adhesive applied to the backside of the sheet. The
block test is predictive of how the non-tacky adhesive coating will
behave following the coating production step when face sheets stock
is kept in roll form prior to converting to sheet form. Ratings of
excellent provide for face sheet rolls with no blocking and unwind
easily with no damage to face sheet or adhesive coatings.
[0106] (4) a rating of pass for the 72 hour ice bucket test for
edge lifting, tunneling, and swimming. The label must remain fully
adhered and intact after 72 hr treatment; preferably, moderate to
strong force must be applied in order to remove the wet label
immediately following the ice bucket test. Labels that easily
remove, swim, have tunneling and edge lifting receive ratings of
fail and are not acceptable;
[0107] (5) a rating of pass for the caustic bath test. Labels that
receive a pass rating fall off completely while labels that remain
adhered after 2 min receive a fail rating. Caustic bath test
ratings of pass are preferred with label drop of preferred between
15 sec and 2 min and most preferred between 30 sec and 90 sec. Any
adhesive remaining on the glass bottle after the caustic bath test
is not acceptable. It is preferred to have not adhesive remaining
on the glass following the caustic bath test;
[0108] (6) or combinations thereof.
III. Kits
[0109] Kits containing the adhesive composition or the components
to prepare the adhesive compositions are described herein. In one
embodiment, the kit contains, premixed, the copolymer and alkaline
soluble resin, as well as any additives. The mixture can be in the
form of a solution or suspension in a suitable solvent or an
emulsion. Alternatively, the mixture can be a solid, which is
formulated into a solution, suspension, or emulsion by the user. In
these embodiments, the kit can contain one or more solvents for
formulating the adhesive composition. The copolymer, additives,
and/or solvents can be provided in appropriate containers, such as
drums or totes. The kit may also contain instructions for preparing
the adhesive composition as well as instructions for applying it to
labels. The kit can also contain the activating solution, which is
packaged in a separate container, such as a drum or tote. The
activating solution may contain one or more additives solubilized
or dispersed in the activating solution. Alternatively, the
additives can be added to the activating solution prior to use. In
other embodiments, the kit contains the adhesive composition,
optionally any additives, and the activating fluid, wherein the
adhesive composition and the activating fluid are packaged and/or
delivered separately but are used in combination to prepare
liner-less labels.
[0110] In some embodiments, the adhesive composition and the
activating solution are sold to an entity that applies the adhesive
composition to labels and sells the treated labels and the
activating solution to the final end user. The entity that sells
the treated labels and the activating solution to the final end
user can package the labels and activating solution with a
printing/labeling device, fitted with an aftermarket device to
activate the labels, used to print the labels and/or apply them to
commercial products. In another embodiment, finished labels,
wherein the adhesive composition has been applied prior to
packaging of the labels, are provided to the final customer.
[0111] In specific embodiments, kits are sold to label
coaters/manufacturers. The kits can contain one or more of the
following: (1) drums, pails, totes, or other bulk containers
containing adhesive to be coated onto a face sheet using a large
format web-based coater or printing press or sheet fed printing
press; (2) drums, pails, totes, or other bulk containers containing
activation fluid to be repackaged into refill stations, reusable
containers, or disposable cartridges; (3) refill stations, reusable
containers, or disposable cartridges containing activation fluid;
(4) wide format rolls or stacks of liner-free labels; and
combinations thereof. The elements of the kit can be sold to a
single coater/manufacturer or to multiple
coaters/manufacturers.
[0112] The KRONES Manual of Labeling Technology (Hermann Kronseder
Maschinenfabrik, 1978) lists various automated labeling methods
that have become increasingly ubiquitous within industry since its
publishing. These glue-free, liner-free labels are engineered to be
compatible with these methods as well as more modern methods known
to one of ordinary skill in the art. In particular, these labels
would be compatible with existing cut and stack glue applied
labeling machines with simple retrofits to the machinery.
IV. Methods of Making Adhesive Compositions
[0113] The copolymer can be packaged individually, along with one
or more solvents, and mixed together at a later time.
Alternatively, the polymer can be mixed together to form a blend
and dissolved or suspended in a solvent in the form of an emulsion,
suspension, or solution. Prior to the preparation of the final
adhesive composition, all formulations can be diluted to the
desired concentrations with distilled water or appropriate organic
solvent.
[0114] The desired coating concentration of the formulations is
from about 20% wt solids to about 70% wt solids, preferably from
about 20% wt solids to about 60% wt solids, more preferably from
about or between 25% wt solids and 55% wt solids. Depending on the
particular combination of components in the adhesive compositions,
the polymer(s) and any additives are mixed together in the
appropriate ratios. For example, if the hygroscopic particulate
filler to be added is in the form of a colloidal suspension, the
copolymer can be mixed into this suspension; if the hygroscopic
agent is a solid, it can be added to the copolymer.
V. Methods of Using Adhesive Compositions
[0115] The adhesive compositions described herein can be used to
adhere glue-free, liner-free labels to a variety of substrates,
particularly glass and plastic, such as polyethylene terephthalate.
In particular embodiments, the adhesive composition is applied to a
printed or printable paper or polymeric film for application to
glass or plastic, such as food and beverage bottles and containers,
containers for pharmaceutical products, or other storage or
consumer containers made from or of glass or plastics.
[0116] The labels provides long term label to bottle adhesion when
dry and long term adhesion when exposed to ice water condition for
extended time periods, particular for substrates having high MVTR
values. This is particular important for food and beverage bottles
and containers which are stored in ice, such as in coolers. The
labels, however, are easily removable in a caustic bath which
allows for straightforward label removal and recycling of the glass
or plastic container.
EXAMPLES
Examples 1-7
Preparation of Non-Tacky, Label Samples for Block Testing, Adhesive
Peel Testing and Coefficient of Friction Testing
[0117] Alkaline-soluble resins and emulsion polymers used for
Examples 1 to 7 are listed in Table 1. Non-tacky, label sample
films were prepared at the blend ratios described in Table 2. All
label sample films were coated on the backside of wet strength 70
gsm paper stock with a wire wound rod to achieve a coating film
weight of approximately 8 g/m.sup.2 and dried for 5 min at
approximately 110.degree. F.
[0118] Blocking Test
[0119] Label sample strips, cut to 1.5'' by 6'', were placed in a
Precision Bench Heat Seal Press (Packworld USA, Nazareth, Pa.) with
the non-tacky, adhesive layer oriented down on top of the face
sheet of a 2'' by 6'' sample strip. The label samples were treated
for 90 sec at 120-122.degree. F. and 60 psi. After testing, the
cooled samples were peeled apart. Sample evaluation was based on
the level of cling (or interaction) the adhesive coating had for
the face stock of the paper label. Samples with no cling received a
rating of Excellent. Samples with low level of cling received a
rating of Good, while samples with high level of cling resulting in
visible damage to the label face stock coating received a rating of
Fair. Samples with the greatest amount of cling, resulting in paper
tear of the label, received a rating of Poor.
[0120] The emulsion polymer in Example 1 received a blocking rating
of good. This rating improved to Excellent with the blending of the
non-tacky resins as demonstrated in Examples 4 to 7. On their own,
resins B and E have Excellent blocking ratings (Examples 2 and
3).
[0121] Adhesive Peel Test
[0122] The non-tacky, adhesive sides of coated label samples, cut
to 1'' by 6'' rectangles, were sprayed with approximately 6
mg/in.sup.2 of activation spray. Activated samples were immediately
placed, adhesive side down, on a glass slide or bottle and applied
smooth and flat with moderate pressure by a rubber roller. Samples
were allowed to sit undisturbed for 2 min or for 10 min after which
time the sample strips were peeled from the substrate surface. The
2 min time point is considered to be representative of quick tack
performance. Label samples with a high percentage of fiber tear 2
min after application are considered to have a faster quick tack
time than label samples that generate a high percentage of fiber
tear 10 min after application. Fast quick tack is an important
property of beverage labels as the typical time required for labels
to generate sufficient tack on a typical bottling line can be on
the order of 100-300 msec.
[0123] Samples were evaluated based on the failure mode of the
sample strip upon peeling. If the applied label sample showed no
adhesion to the substrate and peeled off with no interaction, the
sample received a rating of Poor. If the applied label sample
remained intact but required low amount of effort to remove it from
the substrate, the sample received a rating of Fair. If the applied
label sample remained intact but required strong effort to remove
it from the substrate, the sample received a rating of Good. If the
sample exhibited tearing or face stock delamination, the sample
received a rating of Excellent.
[0124] The percent fiber tear is evaluated for samples that achieve
a peel rating of Excellent. It is determined by visually inspecting
and estimating the percent of the surface area of the label that
remains adhered to the substrate following the removal of the label
in a single smooth peel. This assay may be more appropriate since
for adhesive labels having an "excellent" rating, the label often
tears prior to the adhesive failing.
[0125] Label samples allowed to sit for 2 min after application
achieved percent fiber tear of 60% to 100% for formulations
containing the styrene-maleic anhydride alkaline soluble resin
(Examples 4 to 7). Samples without the resin, as in Example 1, did
not achieve sufficient adhesion or percent fiber tear 2 min after
application. The alkaline soluble resin alone, as in Examples 2 and
3, did not generate enough adhesion, even after 10 min
post-application.
[0126] Ice Bucket Test
[0127] The non-tacky, adhesive sides of coated label samples, cut
to 1'' by 6'' rectangles, were sprayed with approximately 6
mg/in.sup.2 of activation spray. The activated samples were
immediately placed, adhesive side down, on the glass bottle and
with moderate pressure, labels were smoothed and rubbed flat by
hand. The samples were allowed to sit undisturbed for 24 hours at
room temperature, after which time the bottle was filled with cold
water and placed in an ice bath. Following treatment in the ice
bath for 72 hours, the sample strips were evaluated based on the
failure mode of the label sample. The label samples were evaluated
for edge lifting (E), tunneling (T), swimming (S), and complete
separation (Fail) from the bottle.
[0128] Sample labels composed of emulsion polymer only, as in
Example 1, pass the 72 hour ice bucket test. Resin only samples,
Examples 2 and 3, were not tested for ice bucket resistance as
these samples did not generate enough adhesion as indicated by the
Adhesive Peel test results. When the emulsion polymer was blended
with the styrene-maleic anhydride ammonium salt resins (Examples 4
and 7), label samples pass the 72 hour ice bucket test. When the
emulsion polymer was blended with the styrene-maleic anhydride
sodium salt resin (Example 5), label samples did not pass the ice
bucket test due to swimming. Blending the emulsion polymer with the
pH neutral styrene-maleic anhydride amic acid resin resulted in
label sample failure of the ice bucket test due to swimming. When
non-volatile resin solutions were used (Polymer C and D), the
adhered adhesive film was soluble in the ice water allowing for
labels to swim and eventually detach from the glass bottles. When
volatile base resin solutions are used (Polymer B and E), the
adhered adhesive film is insoluble in the ice water due to the
evolution of ammonia during drying of the non-tacky adhesive
film.
[0129] Caustic Bath Test
[0130] The non-tacky, adhesive sides of coated label samples, cut
to 1'' by 6'', were sprayed with approximately 6 mg/in.sup.2 of
activation spray. Activated samples were immediately placed,
adhesive side down, on a glass bottle applied smooth and flat with
moderate pressure by hand. Samples were allowed to sit undisturbed
for a minimum of 24 hours after activation to allow for the
adhesive to set. The glass bottles were immersed in a bath of 4.5%
NaOH at .about.65-75.degree. C. for 2 minutes during which time the
bath was agitated by stir bar. The glass bottles were removed from
the caustic bath and each label was evaluated for release from the
glass substrates. Samples that fell off from the glass or were
easily removed without leaving residue by light shear force applied
by one finger were considered to pass the test (pass). The amount
of time required for label to drop off the glass bottle during
immersion was recorded. Preferred drop off times are 2 min or less.
Samples that remained adhered to the glass did not pass the test
(fail).
[0131] All sample labels passed the caustic drop test (Examples 1,
4 to 7). Samples prepared from resin only were not tested as these
samples did not pass the Adhesion Peel Test. For Example 1,
however, following the caustic drop test a thin film of emulsion
polymer was observed, permanently adhered to the glass. The caustic
solution allowed for complete removal of the paper label but the
emulsion polymeric film was not soluble in the caustic solution and
it remained on the glass bottle. Blending the alkaline soluble
resin with the emulsion polymer resulted in complete label drop off
and no polymeric residue left on the glass bottle.
TABLE-US-00001 TABLE 1 List of Polymeric Emulsion and Alkaline
Soluble Resins Used in Examples 1 to 7 % wt Acid solids Number
Polymer (as Tg (mg.sub.KOH/ ID Polymer Description supplied)
(.degree. C.) g.sub.polymer) pH A Rovene Emulsion Polymer: 48 -45
50 8.1-8.8 6104 .sup.1 Styrene acrylic copolymer B SMA Alkaline
Soluble Resin: 39 +155 465-495 8.5-9.5 1000H .sup.2 Styrene maleic
anhydride ammonium salt C SMA Alkaline Soluble Resin: 40 +155
465-495 8.0-11.0 1000HNa .sup.2 Styrene maleic anhydride sodium
salt D SMA Alkaline Soluble Resin: 31 +155 465-495 6.8 1000MA
.sup.2 Styrene maleic anhydride resin amic acid (pH neutral) E SMA
Alkaline Soluble Resin: 25 +255-285 125 8.0-9.5 17352H .sup.2
Styrene maleic anhydride ammonium salt Footnotes: .sup.1 Rovene
6104 was supplied by Mallard Creek Polymers. .sup.2 SMA 1000H, SMA
1000HNa, SMA 1000MA and SMA 17352 were supplied by Total
Petrochemicals & Refining Inc.
TABLE-US-00002 TABLE 2 Adhesive compositions and performance test
results for Examples 1 to 7 Peel Rating Peel Rating Polymer Polymer
and % and % Ice Bucket 1 2 fiber tear fiber tear Heat Seal Test (72
Caustic Example (% comp) (% comp) at 2 min at 10 min Blocking hour)
Drop 1 100% A -- Fair and 0% Excellent Good Pass/ Pass* and
90%-100% Strong (65 sec) adhesion 2 100% B -- Poor and 0% Poor and
0% Excellent -- -- 3 100% E .sup. -- Poor and 0% Poor and 0%
Excellent -- -- 4 45% A 55% B Excellent Excellent Excellent Pass/
Pass and 100% and 100% Moderate (50 sec) adhesion 5 45% A 55% C
Excellent Excellent Excellent Fail/swim Pass and 60%-70% and 100%
(40 sec) 6 45% A 55% D Excellent Excellent Excellent Fail/swim Pass
and 70%-80% and 100% (40 sec) 7 45% A 55% E Excellent Excellent
Excellent Pass/ Pass and 90%-100% and 100% Moderate- (45 sec)
strong adhesion *While this label composition passed the caustic
drop test, a film of emulsion polymer, also called ghosting,
remained adhered to the glass bottle following the test.
[0132] Unless defined otherwise, all technical and scientific terms
used herein have the same meanings as commonly understood by one of
skill in the art to which the disclosed invention belongs.
Publications cited herein and the materials for which they are
cited are specifically incorporated by reference.
[0133] Those skilled in the art will recognize, or be able to
ascertain using no more than routine experimentation, many
equivalents to the specific embodiments of the invention described
herein. Such equivalents are intended to be encompassed by the
following claims.
* * * * *