U.S. patent application number 14/941961 was filed with the patent office on 2016-03-10 for method of producing an insulated exhaust device.
The applicant listed for this patent is Tenneco Automotive Operating Company Inc.. Invention is credited to William Alcini, Steven Freis, Ruth Latham.
Application Number | 20160069246 14/941961 |
Document ID | / |
Family ID | 48134746 |
Filed Date | 2016-03-10 |
United States Patent
Application |
20160069246 |
Kind Code |
A1 |
Latham; Ruth ; et
al. |
March 10, 2016 |
METHOD OF PRODUCING AN INSULATED EXHAUST DEVICE
Abstract
A method for producing an exhaust gas aftertreatment or acoustic
device (20) having a maximum operating temperature T.sub.MAX. The
method includes the steps of (a) providing a blanket (40) of silica
fiber insulation material having a weight percentage of SiO.sub.2
greater than 65%; (b) calcining the insulating material by heating
the blanket (40) so that all of silica fiber insulation material is
raised to a temperature T greater than T.sub.MAX (where T is less
than the melting temperature of the silica fibers of the blanket);
and (c) securing the blanket (40) on the device (20) after the
calcining step. The blanket is encapsulated in a covering (50)
prior to the calcining step whereby the blanket is batting in the
covering, with the covering between the blanket and the device
being a selected one of wire mesh or siliconized fiber glass.
Inventors: |
Latham; Ruth; (Ann Arbor,
MI) ; Alcini; William; (Ann Arbor, MI) ;
Freis; Steven; (Ann Arbor, MI) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Tenneco Automotive Operating Company Inc. |
Lake Forest |
IL |
US |
|
|
Family ID: |
48134746 |
Appl. No.: |
14/941961 |
Filed: |
November 16, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13277663 |
Oct 20, 2011 |
9217357 |
|
|
14941961 |
|
|
|
|
Current U.S.
Class: |
29/890.08 |
Current CPC
Class: |
F01N 13/14 20130101;
F01N 2310/02 20130101; Y10T 29/49826 20150115; F01N 13/148
20130101; F01N 13/18 20130101 |
International
Class: |
F01N 13/18 20060101
F01N013/18 |
Claims
1. A method of providing external insulation for an exhaust gas
aftertreatment or acoustic device having a maximum operating
temperature T.sub.MAX, the method comprising: providing a blanket
of silica fiber insulation material having a weight percentage of
SiO.sub.2 of greater than 65%; calcining the blanket by heating all
of the silica fiber insulation material to a temperature T greater
than T.sub.MAX, wherein T is less than a melting temperature of the
silica fibers of the blanket; encapsulating said blanket in a
covering before the calcining step whereby said blanket is batting
in said covering; and securing the blanket around an outermost
surface of the exhaust gas aftertreatment or acoustic device after
the calcining step; wherein said covering between said blanket and
said exhaust gas aftertreatment or acoustic device is a selected
one of wire mesh or high temperature textile.
2. The method of claim 1 wherein T is at least
1.05.times.T.sub.MAX.
3. The method of claim 1, wherein said high temperature textile is
a selected one of siliconized fiber glass or straight woven glass
fiber.
4. The method of claim 1 wherein during the calcining step the
blanket is in an uncompressed state.
5. The method of claim 1 wherein T.sub.MAX is within a range of
300.degree. C. to 1100.degree. C.
6. The method of claim 1, wherein the securing step comprises
installing the blanket so that the blanket encircles a core of the
device through which the exhaust gas passes.
7. A method of providing external insulation for an exhaust gas
aftertreatment or acoustic device having a maximum operating
temperature T.sub.MAX, the method comprising: providing a blanket
of silica fiber insulation material having a weight percentage of
SiO.sub.2 of greater than 95%; calcining the blanket by heating all
of the silica fiber insulation material to a temperature T greater
than T.sub.MAX, wherein T is less than a melting temperature of the
silica fibers of the blanket; encapsulating said blanket in a
covering before the calcining step whereby said blanket is batting
in said covering; and securing the blanket around an outermost
surface of the exhaust gas aftertreatment or acoustic device after
the calcining step; wherein said covering between said blanket and
said exhaust gas aftertreatment or acoustic device is a selected
one of wire mesh or high temperature textile.
8. The method of claim 7 wherein T is at least
1.05.times.T.sub.MAX.
9. The method of claim 7, wherein said high temperature textile is
a selected one of siliconized fiber glass or straight woven glass
fiber.
10. The method of claim 7 wherein during the calcining step the
blanket is in an uncompressed state.
11. The method of claim 7 wherein T.sub.MAX is within a range of
300.degree. C. to 1100.degree. C.
12. The method of claim 7, wherein the securing step comprises
installing the blanket so that the blanket encircles a core of the
device through which the exhaust gas passes.
13. A method of providing external insulation for an exhaust gas
aftertreatment or acoustic device having a maximum operating
temperature T.sub.MAX, the method comprising: providing a blanket
of silica fiber insulation material having a weight percentage of
SiO.sub.2 of greater than 65%; calcining the blanket in an
uncompressed state by heating all of the silica fiber insulation
material to a temperature T greater than T.sub.MAX, wherein T is
less than a melting temperature of the silica fibers of the blanket
and is at least 1.05.times.T.sub.MAX and T.sub.MAX is within a
range of 300.degree. C. to 1100.degree. C.; encapsulating said
blanket in a covering before the calcining step whereby said
blanket is batting in said covering; and securing the blanket
around an outermost surface of the exhaust gas aftertreatment or
acoustic device after the encapsulating step; wherein said covering
between said blanket and said exhaust gas aftertreatment or
acoustic device is a selected one of wire mesh or high temperature
textile.
18. The method of claim 17, wherein said high temperature textile
is a selected one of siliconized fiber glass or straight woven
glass fiber.
19. The method of claim 17, wherein the securing step comprises
installing the blanket so that the blanket encircles a core of the
device through which the exhaust gas passes.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a divisional of Ser. No. 13/277,663,
filed Oct. 20, 2011, the disclosure of which is hereby incorporated
by reference.
FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT
[0002] Not Applicable.
MICROFICHE/COPYRIGHT REFERENCE
[0003] Not Applicable.
FIELD OF THE INVENTION
[0004] This invention relates to exhaust gas aftertreatment and/or
acoustic systems and the devices used therein that utilize external
insulation blankets.
BACKGROUND OF THE INVENTION
[0005] Heat insulating batts and blankets are utilized in exhaust
gas systems in order to provide heat insulation for acoustic and
aftertreatment devices of the system to control the heat exchange
to and from the devices. It is known, for example, to place heat
insulating blankets between adjacent wall surfaces of such devices
with the material of the heat insulation blanket being compressed
to provide a desired installed density for the material to help
maintain the heat insulating blanket in its mounted position via
frictional forces between the blanket and the adjacent wall
surfaces. Such a structure is shown in U.S. Ser. No. 12/696,347,
filed Jan. 29, 2010 by Keith Olivier et al., entitled "Method of
Producing an Insulated Exhaust Device", the disclosure of which is
hereby incorporated by reference.
[0006] It is also known to provide heat insulation blankets around
the exterior of such exhaust gas system devices. However, such
blankets have been found to encounter a variety of failure modes,
including damage and cracking when removing and replacing
insulation, damage due to exposure to vibration, damage due to
loose or otherwise inappropriate fit due to thermal set, loss of
insulation properties due to loose or otherwise inappropriate fit,
and/or loss of insulation material.
[0007] The present invention is directed to overcoming one or more
of the problems set forth above.
SUMMARY OF THE INVENTION
[0008] In one aspect of the invention, a method of providing
external insulation for an exhaust gas aftertreatment or acoustic
device having a maximum operating temperature T.sub.MAX is
provided, where the method includes (a) providing a blanket of
silica fiber insulation material having a weight percentage of
SiO.sub.2 of greater than 65%, (b) calcining the blanket by heating
all of the silica fiber insulation material to a temperature T
greater than T.sub.MAX, wherein T is less than a melting
temperature of the silica fibers of the blanket, (c) encapsulating
the blanket in a covering before the calcining step whereby the
blanket is batting in the covering, and (d) securing the blanket
around an outermost surface of the exhaust gas aftertreatment or
acoustic device after the calcining step, wherein the covering
between the blanket and the exhaust gas aftertreatment or acoustic
device is a selected one of wire mesh or high temperature
textile.
[0009] In one form of this aspect of the invention, T is at least
1.05.times.T.sub.MAX.
[0010] In another form of this aspect of the invention, the high
temperature textile is a selected one of siliconized fiber glass or
straight woven glass fiber.
[0011] In yet another form of this aspect of the present invention,
during the calcining step the blanket is an uncompressed state.
[0012] In another form of this aspect of the present invention,
T.sub.MAX is within the range of 300.degree. C. to 1100.degree.
C.
[0013] In still another form, the securing step comprises
installing the blanket so that the blanket encircles a core of the
device through which the exhaust gas passes.
[0014] In another aspect of the invention, a method of providing
external insulation for an exhaust gas aftertreatment or acoustic
device having a maximum operating temperature T.sub.MAX is
provided, where the method includes (a) providing a blanket of
silica fiber insulation material having a weight percentage of
SiO.sub.2 of greater than 95%, (b) calcining the blanket by heating
all of the silica fiber insulation material to a temperature T
greater than T.sub.MAX, wherein T is less than a melting
temperature of the silica fibers of the blanket, (c) encapsulating
the blanket in a covering before the calcining step whereby the
blanket is batting in the covering, and (d) securing the blanket
around an outermost surface of the exhaust gas aftertreatment or
acoustic device after the calcining step, wherein the covering
between the blanket and the exhaust gas aftertreatment or acoustic
device is a selected one of wire mesh or high temperature
textile.
[0015] In one form of this aspect of the invention, T is at least
1.05.times.T.sub.MAX.
[0016] In another form of this aspect of the invention, the high
temperature textile is a selected one of siliconized fiber glass or
straight woven glass fiber.
[0017] In yet another form of this aspect of the present invention,
during the calcining step the blanket is an uncompressed state.
[0018] In another form of this aspect of the present invention,
T.sub.MAX is within the range of 300.degree. C. to 1100.degree.
C.
[0019] In still another form, the securing step comprises
installing the blanket so that the blanket encircles a core of the
device through which the exhaust gas passes.
[0020] In still another aspect of the invention, a method of
providing external insulation for an exhaust gas aftertreatment or
acoustic device having a maximum operating temperature T.sub.MAX is
provided, where the method includes (a) providing a blanket of
silica fiber insulation material having a weight percentage of
SiO.sub.2 of greater than 65%, (b) calcining the blanket in an
uncompressed state by heating all of the silica fiber insulation
material to a temperature T greater than T.sub.MAX, wherein T is
less than a melting temperature of the silica fibers of the blanket
and is at least 1.05.times.T.sub.MAX and T.sub.MAX is within a
range of 300.degree. C. to 1100.degree. C., (c) encapsulating the
blanket in a covering before the calcining step whereby the blanket
is batting in the covering, and (d) securing the blanket around an
outermost surface of the exhaust gas aftertreatment or acoustic
device after the encapsulating step, wherein the covering between
the blanket and the exhaust gas aftertreatment or acoustic device
is a selected one of wire mesh or high temperature textile.
[0021] In one form of this aspect of the invention, the high
temperature textile is a selected one of siliconized fiber glass or
straight woven glass fiber.
[0022] In another form, the securing step comprises installing the
blanket so that the blanket encircles a core of the device through
which the exhaust gas passes.
[0023] Other objects, features, and advantages of the invention
will become apparent from a review of the entire specification,
including the appended claims and drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0024] FIG. 1 is a section view of an exhaust system component
employing the invention; and
[0025] FIG. 2 is a section view of a portion of the external
blanket of the present invention encapsulated in a covering.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
[0026] The present invention may be used, for example, in an
exhaust gas system such as a diesel exhaust gas aftertreatment
system to treat the exhaust from a diesel combustion process (e.g.,
a diesel compression engine). The exhaust will typically contain
oxides of nitrogen (NO.sub.x) such as nitric oxide (NO) and
nitrogen dioxide (NO.sub.2) among others, particulate matter (PM),
hydrocarbons, carbon monoxide (CO), and other combustion
by-products. The system may include one or more exhaust gas
acoustic and/or aftertreatment devices or components. Examples of
such devices include catalytic converters, diesel oxidation
catalysts, diesel particulate filters, gas particulate filters,
lean NO.sub.x traps, selective catalytic reduction monoliths,
burners, manifolds, connecting pipes, mufflers, resonators, tail
pipes, emission control system enclosure boxes, insulation rings,
insulated end cones, insulated end caps, insulated inlet pipes, and
insulated outlet pipes, all of any cross-sectional geometry, many
of which are known.
[0027] As those skilled in the art will appreciate, some of the
foregoing devices may be strictly metallic components with a
central core through which the exhaust flows, and other of the
devices may include a core in the form of a ceramic monolithic
structure and/or a woven metal structure through which the exhaust
flows. These devices are conventionally used in motor vehicles
(diesel or gasoline), construction equipment, locomotive engine
applications (diesel or gasoline), marine engine applications
(diesel or gasoline), small internal combustion engines (diesel or
gasoline), and stationary power generation (diesel or
gasoline).
[0028] FIG. 1 shows one example of such a device for use in a
system such as described above, in the form of a catalytic unit 20
such as shown in Olivier et al. U.S. Ser. No. 12/696,347, the
disclosure of which was heretofore incorporated by reference.
[0029] The catalytic unit 20 has a catalytic core 22, a mount mat
24, a cylindrical inner housing or can 26, and heat insulating
blanket or batt 28, and a cylindrical outer housing or jacket
30.
[0030] The core 22 may typically be a ceramic substrate having a
monolithic structure with a catalyst coated thereon and will
typically have an oval or circular cross section.
[0031] The mounting mat 24 is sandwiched between the core 22 and
the can 26 to help protect the core 22 from shock and vibrational
forces that can be transmitted from the can 26 to the core 22.
Typically the mounting mat 24 is made of a heat resistant and shock
absorbing-type material, such as a mat of glass fibers or rock wool
and is compressed between the can and the carrier in order to
generate a desired holding force.
[0032] The heat insulating blanket 28 located inside the catalytic
unit outer housing 30 may be made of a silica fiber insulation
material having a weight percentage of SiO.sub.2 of greater than
65%, and in preferred embodiments greater than 95%, and in highly
preferred embodiments greater than 98%. Such material is known and
commercially available, with one suitable example being supplied by
BGF Industries, Inc. under the trade name SilcoSoft.RTM., and
another suitable example being supplied by ASGLAWO technofibre GmbH
under the trade name Asglasil.RTM.. Such material is typically
supplied in rolls, with the individual blankets 28 being die cut to
the appropriate length and width for the corresponding device 18
after the material has been taken from the roll.
[0033] In accordance with the present invention, an external
blanket 40 is wrapped around the unit outer housing 30 so as to
substantially encapsulate the housing 30.
[0034] In one embodiment, the external blanket 40 may be
advantageously made of a silica fiber insulation material having a
weight percentage of SiO.sub.2 of greater than 65%, and in
preferred embodiments greater than 95%, and in highly preferred
embodiments greater than 98%. Such material is known and
commercially available, with one suitable example being supplied by
BGF Industries, Inc. under the trade name SilcoSoft.RTM., and
another suitable example being supplied by ASGLAWO technofibre GmbH
under the trade name Asglasil.RTM.. Such material is typically
supplied in rolls, with the individual blankets 40 being die cut to
the appropriate length and width for the corresponding device 20
after the material has been taken from the roll. In one preferred
form, the blanket 40 may have an average installed density of 0.18
grams/cubic centimeter to 0.30 grams/cubic centimeter of the silica
fiber insulation material of the blanket 40.
[0035] According to the invention, before the blanket 40 is
installed into the device 18, the blanket 28 is heat treated to
achieve calcination of the silica fiber insulation material. In
this regard, the blanket 40 is heated so that all of the silica
fiber insulation material in the blanket 28 is raised to a
temperature T greater than the maximum operating temperature
T.sub.MAX of the device 20. This heat treatment improves the
resiliency and erosion resistance of the silica fiber insulation
material and also eliminates the potential for a "thermoset"
failure mode that can result if the silica fiber material were
calcinated in-situ in the device 20 during operation of the system.
Preferably, this heat treatment takes place with the blanket 40 in
an uncompressed or free state wherein there are no compressive
forces being applied to the silica fiber insulation material of the
blanket 40. The temperature T preferably has some margin of safety
above the maximum operating temperature T.sub.MAX of the device 18,
with one preferred margin of safety being 1.05.times.T.sub.MAX.
[0036] This heat treatment improves the resiliency and erosion
resistance of the silica fiber insulation material and also
eliminates the potential for a "thermoset" failure mode that could
result if the silica fiber material were to be calcinated in-situ
on the device during operation of the system. Preferably, such heat
treatment takes place with the external blanket 40 in an
uncompressed or free state wherein there are no compressive forces
being applied to the silica fiber insulation material of the
external blanket 40. The temperature T preferably has some margin
of safety above the maximum operating temperature T.sub.MAX of the
device 18, with one preferred margin of safety being
1.05.times.T.sub.MAX.
[0037] By heat treating the silica fiber heat insulation material
to the temperature T greater than T.sub.MAX before the external
blanket 40 is installed on the device, the heat treated blanket can
maintain suitable frictional engagement with the unit outer housing
30 over the desired life of the device because the silica fiber
insulation material of the blanket 40 maintains its resiliency and
does not take on a "thermoset" from the max operation temperature
T.sub.MAX of the device.
[0038] The heat treatment may advantageously be accomplished using
an in-line oven wherein the silica fiber heat insulation material
is unrolled from a supply roll of the material and passed fiat
through an oven on a conveyor so that the external blanket 40 is
planar during the heat treatment to reduce or prevent differential
heating of the material of the blanket 40 and variation in
thickness of the material in the blanket 40. After heat treatment,
individual blankets 40 can be die cut to the desired length and
width before installing on a device. Alternatively, however, a
complete supply roll of the silica fiber heat insulation material
can be heat treated, with or without rotation of the roll in an
oven, whereby individual blankets 40 can be die cut to the desired
length and width after heat treatment and before installing on the
device. As yet an another alternative, the silica fiber insulation
material can be die cut before heat treatment, with the blanket
being slightly oversized in length and width to account for
shrinkage during heat treatment, and with the die cut blankets then
heat treated in an oven while laying flat on a planar surface.
[0039] In accordance with a second embodiment, the external blanket
40 may also advantageously be a high alumina blanket. In one
embodiment, the external blanket 40 may be advantageously made of
an alumina insulation material having a weight percentage of
Al.sub.2O.sub.3 of greater than 65%, and in preferred embodiments
greater than 95%, and in highly preferred embodiments greater than
98%. Such blankets are known and commercially available, with one
suitable example being supplied by Sell Ltd. of Cheshire, U.K.
under the LDM trade name, and another suitable example being
supplied by Mitsubishi under the MLS-2 trade name. In accordance
with the present invention, these high alumina blankets 40 are also
heat treated to achieve calcination prior to placement on the
device 20.
[0040] The calcined external blanket 40 of either embodiment is
advantageously used as batting encapsulated in a covering 50 prior
to placement on the device 20, as illustrated in FIG. 2.
Calcination of the blanket 40 may be accomplished before
encapsulating the blanket 40 in the covering 50. However,
calcination may also be accomplished in the covering 50 where the
covering 50 will not be adversely impacted by the temperatures used
in the calcinations. When installed on the device 20, the side of
the covering facing the heat side (e.g., the device 20) may
advantageously be foil, wire mesh or a high temperature textile,
such as siliconized fiber glass or straight woven glass fiber.
[0041] It should be appreciated that devices in exhaust gas systems
having external blankets according to the present invention
substantially reduce damage and cracking when removing and
replacing insulation, damage due to exposure to vibration, damage
due to loose or otherwise inappropriate fit due to thermal set,
and/or loss of insulation properties due to loose or otherwise
inappropriate fit, and/or loss of insulation material.
[0042] It should also be appreciated that while the invention has
been described herein in connection with a diesel combustion
process in the form of, for example, a diesel compression engine,
the invention may find use in devices that are utilized in exhaust
gas systems for other types of combustion processes, including
other types of internal combustion engines, including, for example,
internal combustion engines that use gasoline or other alternative
fuels.
* * * * *