U.S. patent application number 14/849630 was filed with the patent office on 2016-03-10 for nonwoven web.
The applicant listed for this patent is The Procter & Gamble Company. Invention is credited to Kelyn Anne Arora, Rajeev Chhabra, Dean Larry DuVal, John Lee Hammons, Stephanie Michelle Niezgoda.
Application Number | 20160067118 14/849630 |
Document ID | / |
Family ID | 54238538 |
Filed Date | 2016-03-10 |
United States Patent
Application |
20160067118 |
Kind Code |
A1 |
Hammons; John Lee ; et
al. |
March 10, 2016 |
Nonwoven Web
Abstract
Nonwoven webs for use in absorbent articles are disclosed. A
nonwoven web can have a first nonwoven layer and a second nonwoven
layer. The first nonwoven layer has a first plurality of fibers, a
first side and a second side opposed to the first side, and a first
plurality of apertures extending through the first nonwoven layer
from the first side to the second side. The first nonwoven layer
also has an additive which is disposed, at least in part, on at
least a portion of the first plurality of fibers. The second
nonwoven layer has a second plurality of fibers, a first side and a
second side opposed to the first side. The second nonwoven layer is
attached to the first nonwoven layer such that at least a portion
of the second plurality of fibers is in liquid communication with
the first plurality of apertures.
Inventors: |
Hammons; John Lee;
(Hamilton, OH) ; Arora; Kelyn Anne; (Cincinnati,
OH) ; DuVal; Dean Larry; (Lebanon, OH) ;
Niezgoda; Stephanie Michelle; (Cincinnati, OH) ;
Chhabra; Rajeev; (Mason, OH) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
The Procter & Gamble Company |
Cincinnati |
OH |
US |
|
|
Family ID: |
54238538 |
Appl. No.: |
14/849630 |
Filed: |
September 10, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
62048316 |
Sep 10, 2014 |
|
|
|
Current U.S.
Class: |
428/137 |
Current CPC
Class: |
A61F 13/512 20130101;
A61F 13/5125 20130101; A61F 2013/51338 20130101; A61F 2013/51178
20130101; A61F 2013/8432 20130101; A61F 13/51113 20130101; A61F
13/5116 20130101; A61F 2013/51366 20130101; D04H 1/4374 20130101;
A61F 13/5123 20130101; D04H 11/08 20130101; A61F 13/8405
20130101 |
International
Class: |
A61F 13/511 20060101
A61F013/511; A61F 13/512 20060101 A61F013/512 |
Claims
1. A nonwoven web for use in an absorbent article, the nonwoven web
comprising: a first nonwoven layer comprising a first plurality of
fibers, a first side and a second side opposed to the first side, a
first plurality of apertures extending through the first nonwoven
layer from the first side to the second side, wherein the first
nonwoven layer comprises an additive which is disposed, at least in
part, on at least a portion of the first plurality of fibers; and a
second nonwoven layer comprising a second plurality of fibers, a
first side and a second side opposed to the first side, the second
nonwoven layer being attached to the first nonwoven layer such at
least a portion of the second plurality of fibers are in liquid
communication with the first plurality of apertures, wherein the
first nonwoven layer is hydrophobic and wherein the second nonwoven
layer is hydrophilic.
2. The nonwoven web of claim 1, wherein the second nonwoven layer
comprises a second plurality of apertures which are substantially
aligned with the apertures of the first nonwoven layer.
3. The nonwoven web of claim 1, wherein the additive comprises a
hydrophobic material with HLB value between 0 and 4.
4. The nonwoven web of claim 3, wherein the additive has a melting
point in the range of about 40 degrees C. to about 80 degrees
C.
5. The nonwoven web of claim 4, wherein the additive comprises
glycerol tristearate.
6. The nonwoven web of claim 2, wherein the first nonwoven layer
and the second nonwoven layer are attached about at least a portion
of a periphery of each aperture.
7. The nonwoven web of claim 1, wherein the first plurality of
fibers comprises bi-component fibers.
8. The nonwoven web of claim 1, wherein the additive is present in
the first nonwoven layer at from between about 0.5 percent to about
15 percent by weight.
9. The nonwoven web of claim 1, wherein the first plurality of
fibers comprises bi-component fibers comprising polyethylene and
polypropylene arranged in a sheath/core configuration.
10. The nonwoven web of claim 9, wherein the additive is applied to
the first nonwoven layer at from between about 0.1 gsm to about 10
gsm.
11. The nonwoven web of claim 9, wherein the additive is provided
at different levels in each component of the bi-component
fiber.
12. The nonwoven web of claim 1, wherein the first plurality of
fibers comprises bi-component fibers comprising a first
polypropylene and a second polypropylene arranged in a side by side
configuration.
13. The nonwoven web of claim 1 further comprising a plurality of
tufts extending above the first side of the first nonwoven
layer.
14. A nonwoven web for use in an absorbent article, the nonwoven
web comprising: a first nonwoven layer comprising a first plurality
of fibers, a first side and a second side opposed to the first
side, wherein second side comprises a plurality of discontinuities,
wherein the first nonwoven layer comprises an additive which is
disposed, at least in part, on at least a portion of the first
plurality of fibers; and a second nonwoven layer comprising a
second plurality of fibers, a first surface and a second surface
opposed to the first surface and a plurality of tufts extending
through at least a portion of the discontinuities in the first
nonwoven layer, wherein the second nonwoven layer is attached to
the first nonwoven layer such that at least a portion of the second
plurality of fibers are in liquid communication with the first
nonwoven layer, wherein the first nonwoven layer is hydrophobic and
the second nonwoven layer is hydrophilic.
15. The nonwoven web of claim 14, wherein the first nonwoven layer
comprises a first plurality of apertures, and wherein the second
nonwoven layer comprises a second plurality of apertures which are
substantially aligned with the first plurality of apertures of the
first nonwoven layer.
16. The nonwoven web of claim 14, wherein the additive comprises a
hydrophobic material with HLB value between 0 and 4.
17. The nonwoven web of claim 16, wherein the additive has a
melting point in the range of about 40 degrees C. to about 80
degrees C.
18. The nonwoven web of claim 17, wherein the additive comprises
glycerol tristearate.
19. The nonwoven web of claim 14, wherein the first plurality of
fibers comprises bi-component fibers.
20. The nonwoven web of claim 19, wherein the additive is present
in the first nonwoven layer at from between about 1 percent to
about 15 percent by weight.
21. The nonwoven web of claim 14, wherein the first plurality of
fibers comprises bi-component fibers comprise a first polypropylene
and a second polypropylene arranged in a side by side configuration
and are crimped.
22. The nonwoven web of claim 21, wherein the additive is applied
to the first nonwoven layer at from between about 0.1 gsm to about
10 gsm.
23. The nonwoven web of claim 22, wherein the additive is provided
at different levels in each component.
24. The nonwoven web of claim 14, wherein the first nonwoven layer
further comprises a plurality of caps, wherein each of the
plurality of caps is positioned above the first surface of the
first nonwoven layer and each of the plurality of caps at least
partially overlies an opening of the plurality of
discontinuities.
25. The nonwoven web of claim 14, wherein the first plurality of
fibers comprises bi-component fibers comprising polyethylene and
polypropylene arranged in a sheath/core configuration.
Description
FIELD OF THE INVENTION
[0001] The disclosure herein relates generally to a nonwoven web
and an article incorporating the nonwoven web.
BACKGROUND OF THE INVENTION
[0002] Topsheets of disposable absorbent articles perform a
valuable function. Topsheets are typically the interface between
the disposable absorbent article and the user. As such, topsheets
should be tactilely appealing to the user. Additionally,
particularly in the context of hygiene articles, topsheets should
blur/mask staining caused by menses and/or urine. If the topsheet
does not successfully blur/mask the staining caused by
menses/urine, the user may be left with the impression that the
disposable absorbent article did not perform well.
[0003] There are a variety of topsheets known in the art. For
example, in some conventional feminine hygiene articles, topsheets
may comprise a film. Films are typically desirable because they
provide good blurring/masking benefits regarding menses/urine
staining. However, films are generally not considered to be soft
without additional processing. Additionally, even with the
additional processing, some users describe the film topsheet as
having a "plastic feel". And, films can sometimes leave residual
liquid, e.g. menses and/or urine, in contact with the skin of the
wearer which can create an unpleasant feel as well as create an
"unclean" perception in the mind of the user.
[0004] Other conventional feminine hygiene articles comprise
nonwoven topsheets. Nonwoven topsheets can provide a soft feel to
the user; however, nonwoven topsheets typically do not have good
blurring/masking capability with regard to menses/urine stains.
[0005] Based on the foregoing, there is a need for a topsheet which
can provide a soft feel to the user while also providing good
masking of menses/urine stains.
SUMMARY OF THE INVENTION
[0006] Disclosed herein is a nonwoven web which can be used as a
topsheet of a disposable absorbent article. The nonwoven web of the
present invention, when utilized as a topsheet of a feminine
hygiene article, can provide a soft feel to the user and can
provide good blurring/masking benefits regarding menses stains and
in some embodiments urine stains.
[0007] In one embodiment, a nonwoven web for use in an absorbent
article comprises a first nonwoven layer and a second nonwoven
layer. The first nonwoven layer comprises a first plurality of
fibers, a first surface and a second surface opposed to the first
surface. The first nonwoven layer also comprises a first plurality
of apertures extending through the first nonwoven layer from the
first surface to the second surface, wherein the first nonwoven
layer comprises an additive which is disposed, at least in part, of
at least a portion of the first plurality of fibers. The second
nonwoven layer comprises a second plurality of fibers, a first
surface and a second surface opposed to the first surface. And, the
second nonwoven layer is attached to the first nonwoven layer such
that at least a portion of the second plurality of fibers are in
liquid communication with the first plurality of apertures.
[0008] In another embodiment, a nonwoven web for use in an
absorbent article comprises a first nonwoven layer and a second
nonwoven layer. The first nonwoven layer comprises a first
plurality of fibers, a first surface and a second surface opposed
to the first surface--the second surface comprising a plurality of
discontinuities. And, the first nonwoven layer comprises an
additive which is disposed, at least in part, on at least a portion
of the first plurality of fibers.
[0009] The second nonwoven layer comprises a second plurality of
fibers, a first surface and a second surface opposed to the first
surface and a plurality of tufts extending through at least a
portion of the discontinuities in the first nonwoven layer, wherein
the second nonwoven layer is attached to the first nonwoven layer
such that at least a portion of the second plurality of fibers are
in liquid communication with the first nonwoven layer.
[0010] In yet another embodiment, a nonwoven web for use in an
absorbent article comprises a first nonwoven layer and a second
nonwoven layer. The first nonwoven layer comprises a first
plurality of fibers, a first surface and a second surface opposed
to the first surface--the second surface comprising a plurality of
tufts. The first nonwoven layer comprises an additive which is
disposed, at least in part, on at least a portion of the first
plurality of fibers.
[0011] The second nonwoven layer comprises a second plurality of
fibers, a first surface and a second surface opposed to the first
surface. The second surface comprises a plurality of
discontinuities, wherein at least a portion of the tufts of the
first nonwoven layer extend through the discontinuities in the
second nonwoven layer. The second nonwoven layer is attached to the
first nonwoven layer such at least a portion of the second
plurality of fibers are in liquid communication with the first
nonwoven layer.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] While the specification concludes with claims particularly
pointing out and distinctly claiming the subject matter of the
present invention, it is believed that the invention can be more
readily understood from the following description taken in
connection with the accompanying drawings, in which:
[0013] FIG. 1A is an exploded view of a nonwoven web of the present
invention;
[0014] FIG. 1B is an exploded view of another embodiment of a
nonwoven web of the present invention;
[0015] FIG. 2A is a side view of another embodiment of a nonwoven
web of the present invention;
[0016] FIG. 2B is a side view of another embodiment of a nonwoven
web of the present invention;
[0017] FIG. 2C is a side view of another embodiment of a nonwoven
web of the present invention;
[0018] FIG. 3 is a close up view of a tuft and cap of the
embodiments of FIGS. 2A-2C;
[0019] FIG. 4 is a cross sectional view showing the tuft and cap of
FIG. 3 and taken along line 4-4 of FIG. 3;
[0020] FIG. 5 is a plan view of the tuft and cap shown in FIG.
3;
[0021] FIG. 6 is a plan view of the tuft and cap shown in FIG.
3;
[0022] FIG. 7 is a side view of another embodiment of a nonwoven
web of the present invention;
[0023] FIG. 8 is a side view of another embodiment of a nonwoven
web of the present invention;
[0024] FIG. 9 is a side view of another embodiment of a nonwoven
web of the present invention;
[0025] FIG. 10 is a perspective view showing an apparatus for
producing some of the nonwoven webs of the present invention;
[0026] FIG. 11 is a scanning electron micrograph ("SEM") photo
showing a nonwoven fiber with additive that has bloomed on the
surface of the fiber;
[0027] FIG. 12 is an SEM photo showing another nonwoven fiber with
additive that has bloomed on the surface of the fiber;
[0028] FIG. 13 is an SEM photo showing another nonwoven fiber with
additive that has bloomed on the surface of the fiber;
[0029] FIG. 14 is an SEM photo showing another nonwoven fiber with
additive that has bloomed on the surface of the fiber;
[0030] FIG. 15 is an SEM photo showing another nonwoven fiber with
additive that has bloomed on the surface of the fiber;
[0031] FIG. 16 is an SEM photo showing other nonwoven fibers with
additive that has been applied to the fibers;
[0032] FIG. 17 is an SEM photo showing nonwoven fibers with
additive that has formed a film on the surface of the fibers;
[0033] FIG. 18 is an SEM photo showing nonwoven fibers with
additive that has formed a film and fibrils on the surface of the
fibers;
[0034] FIGS. 19A-19C are SEM photos showing crimped fiber nonwovens
comprising melt additives; and
[0035] FIGS. 20A-20C are SEM photos showing a sprayed on topical
hydrophobic treatment at varying basis weights.
DETAILED DESCRIPTION OF THE INVENTION
[0036] The term "fibrils" refers to projections, elongate
projections, bumps that extend outwardly from a surface or
generally radially outwardly from an outer surface of a fiber. In
some instances, the projections, elongate projections, or bumps may
extend radially outwardly relative to a longitudinal axis of the
fiber. Radially outwardly means in the range of 1 to 89 degrees
relative to the longitudinal axis. In still other instances, the
projections, elongate projections, or bumps may extend radially
outwardly from a surface of a fiber at least in a longitudinal
central third of the fiber. The projections, elongate projections,
or bumps comprise, consist of, or consist essentially of (e.g., 51%
to 100% or 51% to 99%), melt additives. The projections, elongate
projections, or bumps grow from the fibers post-nonwoven substrate
formation only after a time period (e.g., 6-100 hours) under
ambient conditions. Fibrils can be viewed using an SEM at, at least
1,000 times magnification.
[0037] As used herein, the term "nonwoven web" refers to a web
having a structure of individual fibers or threads which are
interlaid, but not in a repeating pattern as in a woven or knitted
fabric, which do not typically have randomly oriented fibers. The
basis weight of nonwoven fabrics is usually expressed in grams per
square meter (gsm). The basis weight of a nonwoven web is the
combined basis weight of the constituent layers and any other added
components. Fiber diameters are usually expressed in microns; fiber
size can also be expressed in denier, which is a unit of weight per
length of fiber.
[0038] As used herein "philic" and "phobic" have meanings as well
established in the art with respect to the contact angle of a
referenced liquid on the surface of a material. Thus, a material
having a liquid contact angle of greater than about 75 degrees is
considered phobic, and a material having a liquid contact angle of
less than about 75 degrees is considered philic.
[0039] By "substantially randomly oriented" it is meant that, due
to processing conditions of a nonwoven layer, there may be a higher
amount of fibers oriented in the machine direction (MD) than the
cross direction (CD), or vice-versa.
[0040] The present invention pertains to a nonwoven web that is
suitable for use in a disposable absorbent article. In some
embodiments, the nonwoven web of the present invention is suitable
for use as a topsheet in a disposable absorbent article. The
nonwoven webs of the present invention comprise multiple layers of
nonwoven material which can be integral or discrete as discussed
herein. In some embodiments, the nonwoven web may comprise caps and
tufts which provide a softness benefit and a masking benefit.
Additionally, at least one of the nonwoven layers may comprise an
additive which blooms at the surface of at least a portion of the
constituent fibers of the at least one nonwoven layer. The
inventors have found that the additive can provide masking benefits
such that menses stains are less visible to a user of the
disposable absorbent article. Additionally, the inventors have
found that the additive can provide the treated nonwoven layer with
better draining capability such that less fluid sticks to the
fibers and/or interstices between intersecting fibers. The additive
and its application to the nonwoven are similarly discussed
hereafter. The better draining capability can lead to an increased
feeling of dryness for the consumer.
[0041] In addition to tufts and/or caps or independently therefrom,
webs of the present invention may comprise ridges and/or grooves.
Ridges and/or grooves generally have a much greater length than do
tufts and/or caps. For example, ridges and/or grooves may extend
across a width of a web in the cross machine direction. In other
forms, ridges and/or grooves may extend parallel with a machine
direction to a larger extent than tufts. Still in other examples,
ridges and/or grooves may have a length which s greater than a tuft
and/or cap. In some forms, a plurality of discontinuous ridges
and/or grooves may be provided. Methods of forming ridges and/or
grooves are discussed further in U.S. Pat. No. 7,954,213; U.S.
Patent Application Publication Nos. US2012/0045620; US2012/0196091;
US2012/0321839; US2013/0022784; and US2013/0017370; and PCT Patent
Application Publication Nos. WO2011/125893; and WO2012/137553.
Nonwoven web
[0042] Nonwoven webs of the present invention have a machine
direction (MD) (perpendicular to the plane of the sheet showing
FIGS. 1A, 1B, 2A-2C, and 7-9), a cross machine direction (CD), and
a Z direction, as is commonly known in the art of web manufacture.
As stated previously, the nonwoven webs of the present invention
comprise a laminate structure where the nonwoven web comprises a
plurality of nonwoven material layers. The material layers may be
discrete or may be integral as discussed hereafter. Additionally,
each of the nonwoven webs of the present invention comprises at
least two nonwoven material layers which are referred to herein as
generally planar, two-dimensional webs. Also, each of the
constituent nonwoven layers is a fibrous nonwoven web.
[0043] FIG. 1A shows an exploded view of a first embodiment of a
nonwoven web 100A of the present invention. The first nonwoven
layer 110 has a first surface 115 and a second surface 120, each of
which are generally planar. Similarly, the second nonwoven layer
150A has a first surface 155 and a second surface 160 each of which
are generally planar. The first surface 115 and 155 of the first
nonwoven layer 110 and the second nonwoven layer 150A,
respectively, can be body-facing surfaces and the second surfaces
120 and 160 of the first nonwoven layer 110 and the second nonwoven
layer 150A, respectively, can be garment-facing surfaces.
[0044] The first nonwoven layer 110 and second nonwoven layer 150A
can be a nonwoven web comprised of substantially randomly oriented
fibers. For example, the first nonwoven layer 110 comprises a first
plurality of substantially randomly oriented fibers, and the second
nonwoven layer 150A comprises a second plurality of substantially
randomly oriented fibers.
[0045] In one embodiment, the first nonwoven layer 110 may comprise
a first plurality of apertures 125 that extend through the first
nonwoven layer 110 from the first surface 115 to the second surface
120. In another embodiment, as shown in FIG. 1B, nonwoven web 100B
may comprise the first nonwoven layer 110 comprising the first
plurality of apertures 125 and a second nonwoven layer 150B
comprising a second plurality of apertures 165. The second nonwoven
layer 150B may otherwise be constructed similar to the second
nonwoven layer 150A.
[0046] In some embodiments, the second plurality of apertures 165
may be substantially aligned with the first plurality of apertures
125. The aperturing of the first nonwoven layer 110 and the second
nonwoven layer 150A or 150B may be by any suitable method; however,
in order to provide the blurring/masking benefits described
heretofore, the second nonwoven layer 150A, 150B should be in
liquid communication with the first plurality of apertures. Liquid
communication means that liquid insults to the first nonwoven layer
are transferred to the second nonwoven layer. Generally, more
interaction between the constituent fibers of the second nonwoven
layer with the first nonwoven layer, can result in better liquid
communication between the first nonwoven layer and the second
nonwoven layer.
[0047] Preferable methods of aperturing nonwoven webs are described
hereafter. The first nonwoven layer 110 and the second nonwoven
layer 150A, 150B, may be joined about the periphery of each of the
first plurality of apertures 125. For example, for those
embodiments where apertures are created by melting fibers of the
first nonwoven layer 110 typically an aperture periphery is formed.
Additionally during the melting, the melted fiber material can form
bonds with surrounding fibers including the fibers of the second
nonwoven layer 150A or 150B. Where the constituent fibers of the
first nonwoven layer 150A and the second nonwoven layer 150B are
melted together, liquid communication between the first nonwoven
layer 150A and the second nonwoven layer 150B can be enhanced. The
same can occur with regard to the embodiment where both the first
nonwoven layer 110 and the second nonwoven layer 150B comprise
apertures. In some embodiments, the first nonwoven layer 110 and
the second nonwoven layer 150A, 150B are attached to one another
about at least a portion of the periphery of each of the first
plurality of apertures 125. In some embodiments, the first nonwoven
layer 110 and the second nonwoven layer 150A, 150B are attached to
one another about at least a portion of the periphery of each of
the second plurality of apertures 165.
[0048] The resultant nonwoven webs 100A and 100B of FIGS. 1A and 1B
can provide a soft feel to a user of an absorbent article
incorporating either of the nonwoven webs 100A or 100B as the
topsheet of the absorbent article. An additional softness benefit
and/or masking benefits can be gained by the structures described
with regard to FIGS. 2A-2C and 8-10.
[0049] With regard to FIG. 2A, nonwoven web 200A constructed in
accordance with the present invention is shown. The nonwoven web
200A may comprise a first nonwoven layer 210A having a generally
planar first surface 215 and a generally planar second surface 220
opposed to the first surface 215 and a second nonwoven layer 250A
having a generally planar first surface 255 and a generally planar
second surface 260. The first nonwoven layer 210A comprises a first
plurality of substantially randomly oriented fibers, and the second
nonwoven layer 250A comprises a second plurality of substantially
randomly oriented fibers. At least a portion of the second
plurality of fibers in the second nonwoven layer 250A is in liquid
communication with the first nonwoven layer 210A. Similar to the
first nonwoven layer 110 and second nonwoven layers 150A and 150B
(shown in FIGS. 1A and 1B), the respective surfaces of the first
nonwoven layer 210A and second nonwoven layer 250A, can be arranged
such that the first surfaces 215 and 255, respectively, are
body-facing surfaces, and the second surfaces 220 and 260,
respectively, can be arranged as garment-facing surfaces.
[0050] As shown, in some embodiments, the second surface 220 of the
first nonwoven layer 210A may comprise a first plurality of
discontinuities 235. The first plurality of discontinuities 235 are
formed when localized areas of constituent fibers of the first
nonwoven layer 210A are urged in the Z-direction such that these
constituent fibers are disposed superjacent to the first surface
215 of the first nonwoven layer 210A. The disposition of the
constituent fibers, may, in some embodiments, form a cap 230. The
first nonwoven layer 210A may comprise a plurality of caps 230
positioned above the first surface 215. Each of the plurality of
caps 230 can partially overlie at least one of the first plurality
of discontinuities 235. For example, a first cap may at least
partially overly a first discontinuity, and a second cap may at
least partially overly a second discontinuity and so on. Caps 230
are discussed in additional detail hereafter.
[0051] Similarly, in some embodiments, the second surface 260 of
the second nonwoven layer 250A may comprise a second plurality of
discontinuities 275. The second plurality of discontinuities 275
can be formed as provided above with regard to the first plurality
of discontinuities 235 in the first nonwoven layer 210A. Namely,
localized areas of constituent fibers of the second nonwoven layer
250A are urged in the Z-direction such that these constituent
fibers are disposed superjacent to the first surface 255 of the
second nonwoven layer 250A. In some embodiments, this Z-direction
urging also forces these constituent fibers to extend through the
first plurality of discontinuities 235 in the second surface 220 of
the first nonwoven layer 210A. The urging of the constituent fibers
of the second nonwoven layer 250A forms tufts 270.
[0052] Tufts 270 extend through at least a portion of the first
plurality of discontinuities 235 in the first nonwoven layer 210A.
For example, tufts 270 may extend through at least one of the
plurality of discontinuities 235 in the second surface 220 of the
first nonwoven layers 210A and 210B. In other examples, tufts 270
may extend through each of the plurality of discontinuities 235.
Embodiments are contemplated where tufts 270 of the second nonwoven
layers 250A and 250B extend through more than about 90 percent of
the plurality of discontinuities 235 in the second surface 220. In
other embodiments, tufts 270 of the second nonwoven layer 250A and
250B extend through more than about 80 percent of the plurality of
discontinuities 235, more than about 70 percent of the plurality of
discontinuities 235, more than about 60 percent of the plurality of
discontinuities 235, more than about 50 percent of the plurality of
discontinuities 235, more than about 40 percent of the plurality of
discontinuities 235, more than about 30 percent of the plurality of
discontinuities 235, more than about 20 percent of the plurality of
discontinuities, and/or less than about 100 percent, or less than
about any of the above mentioned values or any number within the
range of the values above or any range within the values above.
Tufts 270 are discussed in additional detail hereafter.
[0053] The abrupt change of orientation exhibited by the previously
randomly-oriented fibers of the first nonwoven layer 210A and the
second nonwoven layer 250A, define the first plurality of
discontinuities 235 and the second plurality of discontinuities
275, respectively. Each of the first plurality of discontinuities
235 and the second plurality of discontinuities 275 exhibit a
linearity that can be described as having a longitudinal axis
generally parallel to longitudinal axis L (shown in FIG. 3) of the
cap 230 and tuft 270.
[0054] With regard to FIG. 2B, a nonwoven web 200B may comprise a
first nonwoven layer 210B which is constructed similar to the first
nonwoven layer 210A but may additionally comprise a first plurality
of apertures 225. The nonwoven web 200B may be constructed similar
to the nonwoven web 200A except as provided with regard to the
first nonwoven layer 210B. Similarly, with regard to FIG. 2C, a
nonwoven web 200C may comprise the first nonwoven layer 210B and a
second nonwoven layer 250B which comprises a second plurality of
apertures 265. The second nonwoven layer 250B may otherwise be
constructed similar to the second nonwoven layer 250A. The nonwoven
web 200C may be constructed similar to the nonwoven web 200A and
200B except as provided with regard to the second nonwoven layer
250B. Additional embodiments are contemplated where the second
nonwoven layer 250B comprises apertures in the absence of apertures
in the first nonwoven layer 210A.
[0055] Referring again to FIGS. 2B-2C, the nonwoven webs 200B and
200C, the second plurality of fibers of the second nonwoven layers
250A and 250B can be in liquid communication with a first plurality
of apertures 225 in the first nonwoven layer 210B and/or can be in
liquid communication with the first nonwoven layer 210B. In some
embodiments, at least a portion of the second plurality of
apertures 265 may be substantially aligned with the first plurality
of apertures 225 in the first nonwoven layer 210B.
[0056] The first nonwoven layer 210B and the second nonwoven layer
250B may be joined about the periphery of each of the first
plurality of apertures 225. For example, for those embodiments
where apertures are created by melting fibers of the first nonwoven
layer 210B or the first nonwoven layer 210B together with the
second nonwoven layer 250B, a bond may be created between the first
nonwoven layer 210B and the second nonwoven layer 250B where the
constituent fibers were melted. In some embodiments, the first
nonwoven layer 210B and the second nonwoven layers 250A or 250B are
attached to one another about at least a portion of the periphery
of each of the first plurality of apertures 225. In some
embodiments, the first nonwoven layer 210B and the second nonwoven
layer 250B are attached to one another about at least a portion of
the periphery of each of the second plurality of apertures 265. The
second nonwoven layer 250A may be joined about the periphery of
each of the first plurality of apertures 225 of the first nonwoven
layer 210B.
[0057] While the first nonwoven layer 210A, the second nonwoven
layer 250A, and the nonwoven web 200A are referenced below, the
disclosure below is applicable for the nonwoven webs 200B, 200C,
and first nonwoven layer 210B and second nonwoven layer 250B unless
otherwise expressly stated.
[0058] Referencing FIGS. 3-6, caps 230 and tufts 270 alike can
comprise a plurality of looped fibers that are substantially
aligned such that each of the caps 230 and tufts 270 have a
distinct linear orientation and a longitudinal axis L. By "looped"
fibers it is meant to refer to fibers of the caps 230 that are
integral with and begin and end in the first nonwoven layer 210A
but extend generally outwardly in the Z-direction from the first
surface 215 of the first nonwoven layer 210A. Similarly, "looped"
fibers with regard to tufts 270 is meant to refer to fibers of the
tufts 270 that are integral with and begin and end in the second
nonwoven layer 250A but extend generally outwardly in the
Z-direction from the first surface 255 of the second nonwoven layer
250A and extend beyond the first surface 215 of the first nonwoven
layer 210A. By "aligned", it is meant that looped fibers are all
generally oriented such that, if viewed in plan view as in FIG. 5,
each of the looped fibers has a significant vector component
parallel to a transverse axis T, and can have a major vector
component parallel to the transverse axis T. The transverse axis T
is generally orthogonal to longitudinal axis L in the MD-CD plane
and the longitudinal axis L is generally parallel to the MD.
[0059] While the looped fibers of caps 230 are not shown as are the
looped fibers 408 of the tufts 270, the looped fibers of the caps
230 may be similarly disposed as with regard to the looped fibers
408 of the tufts 270 except that as shown the looped fibers of the
caps 230 may be disposed superjacent to the looped fibers of the
tufts 270. As such, reference to the looped fibers herein shall be
applicable to the looped fibers of the caps 230 and the looped
fibers of the tufts 270 unless otherwise noted.
[0060] As used herein, a looped fiber 408 oriented at an angle of
greater than 45 degrees from the longitudinal axis L when viewed in
plan view, as in FIG. 5, can have a significant vector component
parallel to the transverse axis T. As used herein, a looped fiber
408 oriented at an angle of greater than 60 degrees from
longitudinal axis L when viewed in plan view, can have a major
vector component parallel to the transverse axis T. In some
embodiments, at least 50%, at least 70%, and at least 90% of looped
fibers 408 of tuft 270 have a significant or a major vector
component parallel to transverse axis T. Fiber orientation can be
determined by use of magnifying means if necessary, such as a
microscope fitted with a suitable measurement 45 scale. In general,
for a non-linear segment of fiber viewed in plan view, a
straight-line approximation for both longitudinal axis L and the
looped fibers 408 can be used for determining angle of looped
fibers 408 from longitudinal axis L. For example, as shown in FIG.
5, one fiber 408A is shown emphasized by a heavy line, and its
linear approximation 408B is shown as a dashed line. This fiber
makes an angle of approximately 80 degrees with the longitudinal
axis (measured counterclockwise from L).
[0061] In one embodiment, tufts 270 may be spaced apart from
adjacent tufts 270, and similarly caps 230 may be spaced apart from
adjacent caps 230. In some embodiments, each of the spaced apart
tufts 270 and/or spaced apart caps 230 have generally parallel
longitudinal axes L. The number of tufts 270 and/or caps 230 per
unit area of a nonwoven web of the present invention, i.e., the
area density of tufts 270 and/or caps 230, can be varied from one
tuft per unit area, e.g., square centimeter to as high as 100 tufts
per square centimeter or similarly with regard to caps 230. There
can be at least 10, or at least 20 tufts 270 and/or caps 230 per
square centimeter, depending on the end use. In general, the area
density need not be uniform across the entire area of nonwoven webs
of the present invention, and, in some embodiments, tufts 270
and/or caps 230 can be only in certain regions of nonwoven webs of
the present invention, such as in regions having predetermined
shapes, such as lines, stripes, bands, circles, and the like. In
some embodiments, tufts 270 and/or caps 230 can be spaced
sufficiently closely so as to effectively cover the first surface
215 of the first nonwoven 210A.
[0062] Tufts 270 are, in a sense, "punched above" the first
nonwoven 210A and can be "locked" in place by frictional engagement
with discontinuities 235 of the second surface 220. In some
embodiments, for example, the lateral width of a discontinuity 235
(i.e., the dimension measured parallel to its transverse axis) can
be less than the maximum width of the tooth that formed the
discontinuity (per the process described below). This indicates a
certain amount of recovery at the discontinuity that tends to
constrain tuft 270 from pulling back out through discontinuity 235.
The frictional engagement of the tufts 270 and discontinuities 235
can provide a structure having permanent tufting on one side that
can be formed without adhesives or thermal bonding. This tufting
can provide a softness benefit to the user of the article
incorporating the nonwoven web.
[0063] While the embodiments described with regard to FIGS. 2A-2C,
have longitudinal axes L of tufts 270 and/or caps 230 generally
aligned in the MD, tufts 270 and/or caps 230 and, therefore,
longitudinal axes L, can, in principle, be aligned in any
orientation with respect to the MD or CD. Therefore, in general, it
can be said that for each tuft 270 and/or cap 230, the looped
aligned fibers 408 (shown in FIGS. 3 and 4) are aligned generally
orthogonal to the longitudinal axis L such that they have a
significant vector component parallel to transverse axis T, and can
have a major vector component parallel to transverse axis T.
[0064] Referring again to FIGS. 3 and 4, in some embodiments, as
described below, another characteristic of tufts 270 can be their
generally open structure characterized by open void area 433
defined interiorly of tufts 270. The void area 433 may have a shape
that is wider or larger at a distal portion 431 of the tuft 270 and
narrower at the tuft base 417 of the tuft 270. This is opposite to
the shape of the tooth which is used to form the tuft 270 which is
discussed hereafter. The term "void area" is not meant to refer to
an area completely free of any fibers. Rather, the term is meant as
a general description of the general appearance of tufts 270.
Therefore, it may be that in some tufts 270 a non-looped fiber 418
or a plurality of loose non-looped fibers 418 may be present in the
void area 433. By "open" void area is meant that the two
longitudinal ends of tuft 270 are generally open and free of
fibers, such that tuft 270 can form something like a "tunnel"
structure in an uncompressed state, as shown in FIG. 4. Generally,
discontinuities 275 at the tuft base 417 are narrow. The closing or
narrowing or squeezing of other fibers at the tuft base 417 can
help to stabilize the tufts 270. The general shape of the caps 230
may be similar to that of the tufts 270; however, as shown in FIGS.
2A-2C, void space of a cap 230 may be occupied, in part, by a tuft
270.
[0065] Due to the nature of many nonwoven webs useful as second
nonwoven layer 250A (shown in FIG. 2A) discontinuities 275 may not
be as distinctly noticeable as tufts 270. For this reason, the
discontinuities 275 on the second surface 260 of the second
nonwoven layer 250A can go unnoticed and may be generally
undetected unless nonwoven web 200A (shown in FIG. 2A) is closely
inspected. As such, the second surface 260 of the second nonwoven
250A can have the look and feel of an un-tufted first nonwoven
layer. Thus in some embodiments, nonwoven webs 200A can have the
textured look and feel of terry cloth on one surface, and a
relatively smooth, soft look and feel on second surface. In other
embodiments, discontinuities 275 can appear as apertures, and may
be apertures through the second nonwoven 250A via the ends of the
tunnel-like tufts 270.
[0066] Looped fibers 408 and /or non-looped fibers 418 of tuft 270
can originate and extend from either the first surface 255 or the
second surface 260 of second nonwoven layer 250A. Of course the
looped fibers 408 or non-looped fibers 418 of tuft 270 can also
extend from an interior of second nonwoven layer 250A. In general,
with regard to tufts 270, the looped fibers 408 and non-looped
fibers 418 comprise fibers that are integral with and extend from
the fibers of the second nonwoven layer 250A.
[0067] Similarly, caps 230 may comprise looped fibers and/or
non-looped fibers which originate and extend from either the first
surface 215 or the second surface 220 of the first nonwoven layer
210A. The looped fibers and/or non-looped fibers may also extend
from an interior of the first nonwoven layer 210A. The looped
fibers and/or non-looped fibers of the caps 230 are integral with
and extend from the fibers of the first nonwoven layer 210A.
[0068] In some embodiments, the extension and/or urging of looped
fibers 408 and non-looped fibers 418 can be accompanied by a
general reduction in fiber cross sectional dimension (e.g.,
diameter for round fibers) due to plastic deformation of the fibers
and Poisson's ratio effects. Therefore, the aligned looped fibers
408 of caps 230 and/or tufts 270 can have a tuft average fiber
diameter less than the average fiber diameter of the fibers of the
first nonwoven layer 210A and the second nonwoven layer 250A,
respectively. It is believed that this reduction in fiber diameter
can contribute to the perceived softness. Still in other
embodiments, the fibers/nonwoven material may be selected such that
there is little to no reduction in fiber cross section when fibers
are urged either in the Z-direction or negative Z-direction due to
fiber mobility. Embodiments are contemplated where the first and/or
second nonwoven layers are chosen to reduce the likelihood of
thinning of the fibers and enhance fiber mobility.
[0069] Fiber-to-fiber mobility can be increased by reducing or
eliminating the fiber-to-fiber bonds (e.g. with lower bond area or
higher bond spacing or lower bond temperature in point bonded
nonwovens or via reduced temperature or air flow in through-air
bonded nonwovens). Thermal bonds can be completely eliminated (i.e.
avoided by not bonding) or significantly reduced in certain
nonwoven webs to increase fiber-to-fiber mobility. Similarly,
hydroentangled webs can be less entangled to increase
fiber-to-fiber mobility. For any web, lubricating it prior to
processing as disclosed herein can also increase fiber-to-fiber
mobility. For example, a mineral oil or silicone lubricant can be
applied. Additionally a slip agent or plasticizing agent can be
added to some synthetic fiber webs, such as polyethylene or
polypropylene.
[0070] Referencing FIGS. 4 and 6, in some embodiments, the void
space 433 of tufts 270 may comprise a first void space opening 451
which can be arch shaped such that the first void space opening 451
is broadest proximal the first surface 215 of the first nonwoven
layer 210A and generally becomes narrower towards the portion of
the cap covering the distal portion 431 of the tuft 270. The cap
230 can have a cap base 471 proximal the first surface 215 of the
first nonwoven layer 210A, 210B. The cap base 471 can be narrower
than a portion of the cap 230 away from the cap base 471. That is,
the distance between extension locations 454 can be less than
maximum lateral extent of the cap 230 away (i.e. above) from the
cap base 471. In some embodiments, the first void space opening 451
can be uppercase omega shaped (.OMEGA.) such the first void space
opening 451 is narrower proximal the first surface 215 of the first
nonwoven layer 210A than at a location midway between the tuft base
417 and the distal portion 431 of tuft 270. Similarly, if a second
void space opening 452 is present, the second void space opening
452 can be arch shaped such that the second void space opening 452
is broadest proximal the first surface 215 of the first nonwoven
layer 210A and generally narrows towards the portion of the cap 230
covering the distal portion 431 of the tuft 270. The second void
space opening 452 can be uppercase omega shaped (.OMEGA.) such that
the second void space opening 452 is narrower proximal the first
surface 215 of the first nonwoven layer 210 than at a location
midway between the tuft base 417 and the distal portion 431 of tuft
270. The second void space opening 452 can oppose the first void
space opening 451 in that at least part of the tuft 270 is between
second void space opening 452 and first void space opening 451. The
first void space opening 451, the second void space opening 452,
and any additional openings can make the nonwoven web 200A liquid
pervious. In some forms, the tufts 270 and/or caps 230 may have a
shape which is similar to an inverted capital "U"--specifically for
those forms where the tufts 270 and/or caps 230 are provided in the
positive Z-direction. In other forms, where the tufts and/or caps
are provided in the negative Z-direction, the tufts and/or caps may
have the shape of a capital "U". The "U" shaped tufts and/or caps
may appear like a plurality of bumps on the web.
[0071] If there is a first void space opening 451 and a second void
space opening 452, the cap 230 can integrally extend from the first
nonwoven layer 210A at at least two extension locations 454 spaced
apart from one another by the first void space opening 451 and
second void space opening 452. The at least two extension locations
454 can be at opposing positions on opposing sides of the tuft 270.
The cap 230 can integrally extend from the first nonwoven layer
210A at at least two extension locations 454.
[0072] Caps of the present invention are thought to mask or
partially mask fluid that is collected by the nonwoven web and
remains in the capillaries between fibers 408 of the tufts. Such a
nonwoven web employed in an absorbent article such as a wipe, a
sanitary napkin, a tampon, or a diaper can be appealing to the user
(or caregiver) in that potentially unsightly fluids retained in the
capillaries between fibers 408 of the tufts will be obscured or
partially obscured from the viewer. The caps cover or partially
cover tufts in which fluids can be held and can make the nonwoven
web appear less soiled.
[0073] Embodiments including additional arrangements of caps and/or
tufts are provided with respect to FIGS. 7-9. With regard to FIG.
7, a nonwoven web 700 is shown which comprises a first nonwoven
layer 710 and a second nonwoven layer 750. The first nonwoven layer
710 comprises a generally planar first surface 715 and a generally
planar second surface 720 opposed to the first surface 715, and the
second nonwoven layer 750 has a generally planar first surface 755
and a generally planar second surface 760. The first nonwoven layer
710 comprises a first plurality of substantially randomly oriented
fibers, and the second nonwoven layer 750 comprises a second
plurality of substantially randomly oriented fibers. At least a
portion of the second plurality of fibers in the second nonwoven
layer 750 is in liquid communication with the first nonwoven layer
710. Similar to the first nonwoven layer 110 and second nonwoven
layers 150A and 150B (shown in FIGS. 1A and 1B), the respective
surfaces of the first nonwoven layer 710 and second nonwoven layer
750, can be arranged such that the first surfaces 715 and 755,
respectively, are body-facing surfaces, and the second surfaces 720
and 760, respectively, can be arranged as garment-facing
surfaces.
[0074] While the embodiment shown in FIG. 7 depicts the first
nonwoven layer 710 having a first plurality of apertures 725 and
the second nonwoven layer 750 with a second plurality of apertures,
these are optional. For example, embodiments are contemplated where
the first nonwoven layer 710 comprises the first plurality of
apertures 725 while the second nonwoven layer 750 does not comprise
apertures. As another example, the second nonwoven layer 750 may
comprise the second plurality of apertures 765 while the first
nonwoven layer 710 does not comprise apertures. Additional
embodiments are contemplated where both the first nonwoven layer
710 and the second nonwoven layer 750 are sans apertures.
[0075] As shown, in some embodiments, the second surface 720 of the
first nonwoven layer 710 may comprise a first plurality of
discontinuities 735. The first plurality of discontinuities 735 are
formed when localized areas of constituent fibers of the first
nonwoven layer 210A are urged in the Z-direction such that these
constituent fibers are disposed superjacent to the first surface
715 of the first nonwoven layer 710. However, instead of forming a
cap 230 (shown in FIGS. 2A-2C and 3-6), the urging in the
Z-direction of the constituent fibers of the first nonwoven layer
710 may be such that a plurality of fibers break thereby forming
the first plurality of discontinuities 735.
[0076] As shown, in some embodiments, the second surface 760 of the
second nonwoven layer 750 may comprise a second plurality of
discontinuities 775 which may be configured as described with
regard to the second plurality of discontinuities 275 (shown in
FIGS. 2A-2C and 3-4). Namely, localized areas of constituent fibers
of the second nonwoven layer 750 are urged in the Z-direction such
that these constituent fibers are disposed superjacent to the first
surface 755 of the second nonwoven layer 750. This Z-direction
urging also forces these constituent fibers to extend through the
first plurality of discontinuities 735 in the second surface 720 of
the first nonwoven layer 710. The extension of the constituent
fibers of the second nonwoven layer 750 forms tufts 770.
[0077] Tufts 770 extend through at least a portion of the first
plurality of discontinuities 735 in the first nonwoven layer 710.
Tufts 770 may be configured as described herein with regard to
tufts 230 (shown in FIGS. 2A-2C and 3-4). As shown, in some
embodiments, tufts 770 may be uncovered by a corresponding cap
formed by the constituent fibers of the first nonwoven layer
710.
[0078] With regard to FIG. 8, a nonwoven web 800 constructed in
accordance with the present invention is shown. The nonwoven web
800 may comprise a first nonwoven layer 810 having a generally
planar first surface 815 and a generally planar second surface 820
opposed to the first surface 815 and a second nonwoven layer 850
having a generally planar first surface 855 and a generalldy planar
second surface 860. The first nonwoven layer 810 comprises a first
plurality of substantially randomly oriented fibers, and the second
nonwoven layer 850 comprises a second plurality of substantially
randomly oriented fibers. At least a portion of the second
plurality of fibers in the second nonwoven layer 850 is in liquid
communication with the first nonwoven layer 810. Similar to the
first nonwoven layer 110 and second nonwoven layers 150A and 150B
(shown in FIGS. 1A and 1B), the respective surfaces of the first
nonwoven layer 810 and second nonwoven layer 850, can be arranged
such that the first surfaces 815 and 855, respectively, are
body-facing surfaces, and the second surfaces 820 and 860,
respectively, can be arranged as garment-facing surfaces.
[0079] While the embodiment shown in FIG. 8 depicts the first
nonwoven layer 810 having a first plurality of apertures 825 and
the second nonwoven layer 850 with a second plurality of apertures,
these are optional. For example, embodiments are contemplated where
the first nonwoven layer 810 comprises the first plurality of
apertures 825 while the second nonwoven layer 750 does not comprise
apertures. As another example, the second nonwoven layer 850 may
comprise the second plurality of apertures 865 while the first
nonwoven layer 810 does not comprise apertures. Additional
embodiments are contemplated where both the first nonwoven layer
810 and the second nonwoven layer 850 are sans apertures.
[0080] As shown, in some embodiments, the first surface 815 of the
first nonwoven layer 810 may comprise a first plurality of
discontinuities 835. The first plurality of discontinuities 835 are
formed when localized areas of constituent fibers of the first
nonwoven layer 810 are urged in the negative Z-direction such that
these constituent fibers are disposed subjacent to the first
surface 815 of the first nonwoven layer 810 thereby forming tufts
870. In some embodiments, the tufts 870 may extend beyond the
second surface 860 of the second nonwoven layer 850 such that at
least a portion of the tuft 870 is subjacent to the second surface
860.
[0081] The second nonwoven layer 850 may comprise a second
plurality of discontinuities 875. As shown, in some embodiments,
the plurality of tufts 870 may extend through the second plurality
of discontinuities 875. The second plurality of discontinuities 875
may be created when localized areas of constituent fibers of the
second nonwoven layer 850 are urged in the negative Z-direction
such that these constituent fibers are disposed subjacent to the
first surface 855 of the second nonwoven layer 850. However,
instead of forming a cap 230 (shown in FIGS. 2A-2C and 3-6), the
urging in the Z-direction of the constituent fibers of the second
nonwoven layer 850 may be such that a plurality of fibers break
thereby forming the second plurality of discontinuities 875.
[0082] Tufts 870 extend through at least a portion of the second
plurality of discontinuities 875 in the second nonwoven layer 850.
For example, tufts 870 may extend through at least one of the
plurality of discontinuities 875 in the second surface 860 of the
second nonwoven layer 850. Tufts 870 may be configured as described
herein with regard to tufts 230 (shown in FIGS. 2A-2C and 3-4). As
shown, in some embodiments, tufts 870 may be uncovered by a
corresponding cap formed by the constituent fibers of the second
nonwoven layer 860. The nonwoven web 800 can provide a softness
benefit as well as improve fluid communication to an absorbent core
of a disposable absorbent article incorporating such nonwoven web
800.
[0083] With regard to FIG. 9, nonwoven web 900, constructed in
accordance with the present invention, is shown. The nonwoven web
900 may comprise a first nonwoven layer 910 having a generally
planar first surface 915 and a generally planar second surface 920
opposed to the first surface 915 and a second nonwoven layer 950
having a generally planar first surface 955 and a generally planar
second surface 960. The first nonwoven layer 910 comprises a first
plurality of substantially randomly oriented fibers, and the second
nonwoven layer 950 comprises a second plurality of substantially
randomly oriented fibers. At least a portion of the second
plurality of fibers in the second nonwoven layer 950 is in liquid
communication with the first nonwoven layer 910. Similar to the
first nonwoven layer 910 and second nonwoven layers 150A and 150B
(shown in FIGS. 1A and 1B), the respective surfaces of the first
nonwoven layer 910 and second nonwoven layer 950, can be arranged
such that the first surfaces 915 and 955, respectively, are
body-facing surfaces, and the second surfaces 920 and 960,
respectively, can be arranged as garment-facing surfaces.
[0084] While the embodiment shown in FIG. 9 depicts the first
nonwoven layer 910 having a first plurality of apertures 925 and
the second nonwoven layer 950 with a second plurality of apertures
965, these are optional. For example, embodiments are contemplated
where the first nonwoven layer 910 comprises the first plurality of
apertures 925 while the second nonwoven layer 950 does not comprise
apertures. As another example, the second nonwoven layer 950 may
comprise the second plurality of apertures 965 while the first
nonwoven layer 910 does not comprise apertures. Additional
embodiments are contemplated where both the first nonwoven layer
910 and the second nonwoven layer 950 are sans apertures.
[0085] As shown, in some embodiments, the first surface 955 of the
second nonwoven layer 950 may comprise a second plurality of
discontinuities 975. The second plurality of discontinuities 975
are formed when localized areas of constituent fibers of the second
nonwoven layer 950 are urged in the negative Z-direction such that
these constituent fibers are disposed subjacent to the second
surface 960 of the second nonwoven layer 950. The disposition of
the constituent fibers, may, in some embodiments, form a cap 930.
The second nonwoven layer 950 may comprise a plurality of caps 930
extending below the second surface 960. Each of the plurality of
caps 930 can partially overlie at least one of the second plurality
of discontinuities 975. For example, a first cap at least partially
overlies a first discontinuity, and a second cap at least partially
overlies a second discontinuity and so on.
[0086] Similarly, in some embodiments, the first surface 915 of the
first nonwoven layer 910 may comprise a first plurality of
discontinuities 935. The first plurality of discontinuities 935 can
be formed when localized areas of constituent fibers of the first
nonwoven layer 910 are urged in the negative Z-direction such that
these constituent fibers are disposed subjacent to the second side
920 of the first nonwoven layer 910. This negative Z-direction
urging also forces these constituent fibers to extend through the
second plurality of discontinuities 975 in the first surface 955 of
the second nonwoven layer 950. The extension of the constituent
fibers of the first nonwoven layer 910 forms tufts 970.
[0087] Tufts 970 extend through at least a portion of the second
plurality of discontinuities 975 in the second nonwoven layer 950.
Tufts 970 may be configured similarly as described with regard to
tufts 270 (shown in FIGS. 2A-2C and 3-4).
[0088] Additionally, embodiments are contemplated where the
nonwoven web comprises a single nonwoven layer which is provided
with an additive. The additive, similar to the embodiments above,
can be provided to the nonwoven as part of the master batch or may
be applied post fiber production via spraying, slot coating or the
like. The single nonwoven layer may be subjected to processing as
described herein. For example, the single nonwoven layer may have a
portion of its fibers urged in a Z-direction and/or urged in a
negative Z-direction. In conjunction with the Z-direction urging
and/or negative Z-direction urging, or independently therefrom, the
single nonwoven layer may also comprise a plurality of apertures.
The single nonwoven layer may comprise multiple nonwoven substrates
as described hereafter.
Nonwoven Web Processing
[0089] Depending on the orientations of caps and tufts described
heretofore, processing of nonwoven webs of the present invention
can vary. Referring to FIG. 10, there is shown an apparatus 1000
and method for producing the nonwoven webs of the present
invention. The apparatus 1000 comprises a pair of intermeshing
rolls 1002 and 1004, each rotating about an axis A--the axes A
being parallel and in the same plane. Roll 1002 comprises a
plurality of ridges 1006 and corresponding grooves 1008 which
extend unbroken about the entire circumference of roll 1002.
[0090] Roll 1004 is similar to roll 1002, but rather than having
ridges that extend unbroken about the entire circumference, roll
1004 comprises a plurality of rows of circumferentially-extending
ridges that have been modified to be rows of
circumferentially-spaced teeth 1010 that extend in spaced
relationship about at least a portion of roll 1004. The individual
rows of teeth 1010 of roll 1004 are separated by corresponding
grooves 1012. In operation, rolls 1002 and 1004 intermesh such that
the ridges 1006 of roll 1002 extend into the grooves 1012 of roll
1004 and the teeth 1010 of roll 1004 extend into the grooves 1008
of roll 1002. A nip 1016 is formed between the counter-rotating
intermeshing rolls 1002 and 1004. Both or either of rolls 1002 and
1004 can be heated by means known in the art such as by using hot
oil filled rollers or electrically-heated rollers.
[0091] The apparatus 1000 is shown in a configuration having one
patterned roll, e.g., roll 1004, and one non-patterned grooved roll
1002. However, in certain embodiments it may be preferable to use
two patterned rolls similar to roll 1004 having either the same or
differing patterns, in the same or different corresponding regions
of the respective rolls. Such an apparatus can produce webs with
tufts protruding from both sides of the nonwoven web.
[0092] Nonwoven webs of the present invention can be made by
mechanically deforming the first nonwoven layer 210A and the second
nonwoven layer 250A that can each be described as generally planar
and two dimensional prior to processing by the apparatus shown in
FIG. 10. By "planar" and "two dimensional" is meant simply that the
webs start the process in a generally flat condition relative to
the finished nonwoven web 200A that has distinct, out-of-plane,
Z-direction three-dimensionality due to the formation of tufts 270
and/or caps 230. "Planar" and "two-dimensional" are not meant to
imply any particular flatness, smoothness or dimensionality.
Additionally, nonwoven web 700 (shown in FIG. 7) can be processed
as described above.
[0093] The nonwoven webs 800 and 900 (shown in FIGS. 8 and 9,
respectively) can be processed as described above with some
variation described hereafter. For example, in order to accomplish
the negative Z-direction urging as described herein, the nonwoven
layers may be provided to the apparatus 1000 such that the second
nonwoven layer 850 or 950 is disposed superjacent to the first
nonwoven layer 810 or 910. However, flipping the resultant nonwoven
web at rapid production speeds for processing is difficult to
manage and would introduce much complexity into the production of
such nonwoven webs. In some embodiments, particularly for those
where the desired resultant nonwoven web is as described with
regard to nonwoven webs 800 and 900, the rolls 1002 and 1004 of
apparatus 1000 can be inverted. For example, the patterned roll
1004 may be positioned superjacent to the non-patterned grooved
roll 1002.
[0094] The number, spacing, and dimensions of tufts and/or caps can
be varied to give varying texture to nonwoven webs of the present
invention. For example, if tufts and/or caps are sufficiently
closely spaced the resultant nonwoven web can have a terry
cloth-like feel. Alternatively, tufts and/or caps can be arranged
in patterns such as lines or filled shapes to create portions of a
web having greater texture, softness, bulk, absorbency or visual
design appeal. For example, when tufts and/or caps are arranged in
a pattern of a line or lines, the tufts and/or caps can have the
appearance of stitching Likewise, the size dimensions, such as the
height, length and width of individual tufts can be varied.
[0095] Single tufts and/or caps can be as long as about 3 cm in
length and can be made alone or dispersed among tufts and/or caps
of various sizes. In some embodiments, the tufts and/or caps may
have a length ranging from about 1 mm to about 10 mm. In some
embodiments, the tufts and/or caps may have a length ranging from
about 2 mm to about 8 mm; from about 3 mm to about 7 mm, or any
ranges within the values recited or any numbers within the values
recited.
[0096] Additionally, embodiments are contemplated where a nonwoven
web includes a plurality of tufts and/or caps which are configured
differently. For example, a nonwoven web of the present invention
may comprise a tuft 270 and a cap 230 (shown in FIGS. 2A-2C) in a
first area of the nonwoven web and may comprise a tuft 770 (shown
in FIG. 7) in a second area of the nonwoven web. In other
embodiments, a nonwoven web may comprise a tuft 770 (shown in FIG.
7) in a first area of a nonwoven web and may comprise a tuft 970
and a cap 930 (shown in FIG. 9) in a second area of the nonwoven
web. In other embodiments, a nonwoven web may comprise a tuft 770
(shown in FIG. 7) in a first area of the nonwoven web and a tuft
870 (shown in FIG. 8) in a second area of the nonwoven web. In
other embodiments, a nonwoven web may comprise a tuft 270 and a cap
230 (shown in FIGS. 2A-2C) in a first area of the nonwoven web and
a tuft 870 (shown in FIG. 8) in a second area of the nonwoven web.
In some embodiments, a nonwoven web may comprise a tuft 270 and a
cap 230 (shown in FIGS. 2A-2C) in a first area of the nonwoven web
and a tuft 970 and a cap 930 (shown in FIG. 9) in a second area of
the nonwoven web. Still in other embodiments, a nonwoven web may
comprise a tuft 970 and a cap 930 (shown in FIG. 9) in a first area
of the nonwoven web and may comprise a tuft 870 (shown in FIG. 8)
in a second area of the nonwoven web. Nonwoven webs of the present
invention may utilize any and all combinations of the tufts and/or
caps described with regard to FIGS. 2A-2C, 7, 8, and 9) in
accordance with the foregoing embodiments, e.g. first area with
first set of tufts and/or caps, second area with second set of
tufts and/or caps, third area with third set of tufts and/or caps,
and so on, wherein each of the first, second and third sets of
tufts and/or caps are different.
[0097] While the first nonwoven layer and the second nonwoven layer
are referred to as 210A and 250A, it should be understood that any
of the first nonwoven layers and second nonwoven layers described
herein may be processed similarly. The first nonwoven layer 210A
and the second nonwoven layer 250A are provided either directly
from their respective web making processes or indirectly from
supply rolls (neither shown) and moved in the machine direction to
the nip 1016 of counter-rotating intermeshing rolls 1002 and 1004.
The first nonwoven layer 210A and the second nonwoven layer 250 A
are preferably held in a sufficient web tension so as to enter the
nip 1016 in a generally flattened condition by means well known in
the art of web handling. As each of the first nonwoven layer 210A
and the second nonwoven layer 250A goes through the nip 1016, the
teeth 1010 of roll 1004--which are intermeshed with grooves 1008 of
roll 1002--simultaneously urge fibers of the first nonwoven layer
210A out of the plane of the first nonwoven layer 210A thereby
forming caps 230 and urge fibers of the second nonwoven layer 250A
out of the plane of the second nonwoven layer 250A and through the
plane of the first nonwoven layer 210A to form tufts 270.
[0098] The number, spacing, and size of tufts 270 and/or caps 230
(shown in FIGS. 3 and 4) can be varied by changing the number,
spacing, and size of teeth 1010 and making corresponding
dimensional changes as necessary to roll 1004 and/or roll 1002.
This variation, together with the variation possible in first
nonwoven layer 210A and the second nonwoven layer 250A permits many
varied nonwoven webs 200A to be made for many purposes. The size of
teeth as well as additional details regarding processing of
nonwovens and laminates comprising nonwovens can be found in U.S.
Pat. No. 7,410,683; U.S. Pat. No. 7,789,994; U.S. Pat. No.
7,838,099; U.S. Pat. No. 8,440,286; and U.S. Pat. No.
8,697,218.
[0099] As stated previously, the first nonwoven layer and the
second nonwoven layer, as described herein, may be provided as
discrete layers. For example, embodiments are contemplated where
the first nonwoven layer is derived from a first supply roll having
a first specific fiber makeup while the second nonwoven layer is
derived from a second supply roll having a second specific fiber
makeup. In some embodiments, the fiber makeup between the first
supply roll and the second supply roll can be different as
described below.
[0100] Embodiments are contemplated where the first nonwoven layer
and the second nonwoven layer are both spunbonded nonwoven
materials. In some embodiments, the first nonwoven and the second
nonwoven are produced by different spin beams on a single spunbond
nonwoven manufacturing line. As used herein, "spunbond fibers"
refers to small diameter fibers which are formed by extruding
molten thermoplastic material as filaments from a plurality of
fine, usually circular capillaries of a spinneret with the diameter
of the extruded filaments then being rapidly reduced. Spunbond
fibers are generally not tacky when they are deposited on a
collecting surface. Spunbond fibers are generally continuous and
have average diameters (from a sample of at least 10) larger than 7
microns, and more particularly, between about 8 and 40 microns. For
example, the first nonwoven layer may be produced by a first spin
beam while the second nonwoven layer is produced by a second spin
beam.
[0101] In some embodiments, the first nonwoven layer and/or the
second nonwoven layer may comprise meltblown nonwoven materials. In
some embodiments, the first nonwoven layer and/or the second
nonwoven layer may comprise finer fibers, including fibers with
average diameters less than one micron or 1000 nanometers (an
"N-fiber"), may comprise melt fibrillation, advanced meltblowing
technology, or electrospinning. Advanced melt-blowing technology is
described, for example, in U.S. Pat. No. 4,818,464 to Lau, U.S. Pat
No. 5,114,631 to Nyssen et al., U.S. Pat No. 5,620,785 to Watt et
al., and U.S. Pat. No. 7,501,085 to Bodaghi et al. Melt film
fibrillation technology, as example of melt fibrillation, is a
general class of making fibers defined in that one or more polymers
are molten and are extruded into many possible configurations
(e.g., hollow tubes of films, sheets of films, co-extrusion,
homogeneous or bi-component films or filaments) and then
fibrillated or fiberized into filaments. Examples of such processes
are described in U.S. Pat. No. 4,536,361 to Torobin, U.S. Pat No.
6,110,588 to Perez et al., U.S. Pat. No. 7,666,343 to Johnson et
al., U.S. Pat. No. 6,800,226 to Gerking. Electrospinning processes
useful to make fine fibers are described in U.S. Pat. No. 1,975,504
to Formhals et al., U.S. Pat. No. 7,585,437, to Jirsak et al., U.S.
Pat. No. 6,713,011 to Chu et al., U.S. Pat. No. 8,257,641 to Qi et
al.; and also in "Electrospinning", by A. Greiner and J. Wendorff,
in Angew. Chem. Int. Ed., 2007, 46(30), 5670-5703.
[0102] In some embodiments, the first nonwoven layer and/or the
second nonwoven layer may comprise spunlaid or spunbond nonwoven
materials. The spunlaid or spunbond fibers typically have an
average diameter in the range of about 8 microns to about 40
microns, or a fiber titer in the range from 0.5 to 10 denier. The
meltblown fibers have a diameter of typically in the range from 0.5
microns to 10 microns on average, or 0.001 denier to 0.5 denier,
and range from about 0.1 microns to over 10 microns. Fine fibers
range in average or median diameter from 0.1 microns to 2 microns,
and some fine fibers have a number-average diameter of less than
about 1 micron, a mass-average diameter of less than about 1.5
microns, and a ratio of the mass-average diameter to the
number-average diameter less than about 2.
Dry-Laid and Wet-Laid Nonwoven Substrates
[0103] In addition to nonwoven substrates made from the fiber
spinning technologies of molten materials, the first nonwoven layer
and/or the second nonwoven layer may be made by other means from
pre-formed fibers (including natural fibers), such as by drylaid or
wetlaid technologies. Drylaid technologies include carding and
airlaying. These technologies may be combined with each other,
e.g., drylaid with meltspun, to form multi-layer, functional
nonwoven substrates.
[0104] The carding process uses fibers cut into discrete lengths
called staple fiber. The type of fiber and the desired end product
properties determine the fiber length and denier. Typical staple
fibers have a length in the range of 20 mm to 200 mm and a linear
density in the range of 1 dpf to 50 dpf (denier per fiber), though
staple fibers beyond this range have also been used for carding.
The carding technology processes these staple fibers into a formed
substrate. Staple fibers are typically sold in compressed bales
that need to be opened to make uniform nonwoven substrates. This
opening process may be done through a combination of bale opening,
coarse opening, fine opening, or by a similar process. Staple
fibers are often blended in order to mix different fiber types
and/or to improve uniformity. Fibers may be blended by blending
fiber hoppers, bale openers, blending boxes, or by similar methods.
The opened and blended fibers are transported to a chute that
deposits the fibers across the width of the card and with a density
as uniform as practical in order to make a nonwoven substrate with
the desired basis weight uniformity. The card contains a series of
parallel rollers and/or fixed plates that are covered with metallic
clothing, rigid saw-toothed wires with specific geometry that
staple fibers are processed between. Carding takes place when fiber
tufts transport between the tangent points of two surfaces that
have a differential surface speed and opposing angle directions on
the metallic clothing. Cards may have a single main cylinder to
card with or multiple cylinders. Cards may have a single doffer or
multiple doffers to remove the carded fibers and the cards may
contain randomizing rollers or condenser rollers to reduce the
highly isotropic orientation of the individual fibers in the web.
The carding process may contain a single card or multiple cards in
line with one another, where the fibers of a subsequent card are
deposited on top of the fibers from a preceding card and thus can
form multiple layers, e.g., of different fiber compositions. The
orientation of these cards may be parallel to the downstream
operation or perpendicular to the downstream operation by means of
turning or cross-lapping.
[0105] The airlaid process also uses fibers of discrete length,
though these fibers are often shorter than the staple fibers used
for carding. The length of fibers used in airlaying typically
ranges from 2 mm to 20 mm, though lengths beyond this range may
also be used. Particles may also be deposited into the fibrous
structure during the airlaying process. Some fibers for airlaying
may be prepared similarly as for carding, i.e., opening and
blending as described above. Other fibers, such as pulp, may use
mills, such as hammer mills or disc mills, to individualize the
fibers. The various fibers may be blended to improve the uniformity
of properties of the finished nonwoven substrate. The airlaying
forming device combines external air and the fibers and/or
particles so that the fibers and/or particles are entrained in the
airsteam. After entrainment, the fibers and/or particles are
collected as a loose web upon a moving foraminous surface, such as
a wire mesh conveyor belt, for example. The airlaying process may
contain a single airlaying forming device or multiple airlaying
forming devices in line with one another, where the fibers and/or
particles of the subsequent airlaying forming device are deposited
on top of the fibers and/or particles from a preceding airlaying
forming device, thereby allowing manufacture of a multi-layered
nonwoven substrate.
[0106] Wet-laid nonwovens are made with a modified papermaking
process and typically use fibers in the range of 2 mm to 20 mm,
though lengths beyond this range have also been used. Some fibers
for wetlaying may be prepared similarly as for carding, i.e.,
opening and blending as described above. Other fibers, such as
pulp, may use mills, such as hammer mills or disc mills, to
individualize the fibers. The fibers are suspended in water,
possibly with other additives like bonding agents, and this slurry
is typically added to a headbox from where it flows onto a wetlaid
forming device to create a sheet of material. After initial water
removal, the web is bonded and dried.
[0107] Spunlace nonwovens are typically carded and hydroentangled.
The fibers of the spunlace nonwoven are first carded. In order to
provide the carded fibers with integrity in the Z-direction and in
CD, the carded fibers are then subjected to hydroentangling.
Instead of carded nonwovens, spunlace nonwovens may be air-laid or
wet-laid and subsequently hydroentangled.
[0108] Embodiments are contemplated where the first nonwoven layer
and/or the second nonwoven layer comprise a plurality of
constituent nonwoven substrates. For the examples below, spunbonded
shall be referred to with an "S"; meltblown shall be referred to
with an "M"; spunlace shall be referred to with an "SL"; carded
shall be referred to with a "C"; and fine fiber layers shall be
referred to with an "N". The first nonwoven layer and/or the second
nonwoven layer may comprise an S first substrate and an M second
substrate. Additional substrates may be added for example, an SMS
structure may be created. In other examples, the constituent
substrates of the first nonwoven layer and/or the second nonwoven
layer may comprise an S and a C substrate; an S and SL substrates;
an SNMS substrates or any combination thereof. In some embodiments,
the first nonwoven layer and/or the second nonwoven layer may
comprise a spunbond fine fiber laminate, "SNL".
[0109] The constituent substrates of the first nonwoven layer
and/or the second nonwoven layer may be provided with structural
integrity via a variety of different processes. Some examples
include thermal point bonding, air through bonding,
hydroentangling, and needlepunching each of which is well known in
the art. Similarly, the attachment of the first nonwoven layer to
the second nonwoven layer may be achieved by a variety of different
processes. Examples of such processes are discussed hereafter.
[0110] Embodiments are contemplated where the constituent
substrates of the first nonwoven layer and the second nonwoven
layer are subjected to similar attachment processes. For example,
the constituent substrates of the first nonwoven layer and the
second nonwoven layer may each be subjected to a hydroentangling
process, a through air bonding process, a needlepunching process,
or a thermal bonding process. In such embodiments, the attachment
processes for the first nonwoven and/or the second nonwoven may be
different. For example, the constituent substrates of the first
nonwoven layer may be subjected to a first hydroentangling process
while the constituent substrates of the second nonwoven layer are
subjected to a second hydroentangling process. The first
hydroentangling process, in some embodiments, may provide a higher
degree of structural integrity in the first nonwoven layer versus
that provided to the second nonwoven layer via the second
hydroentangling process. Alternatively, in some embodiments, the
first hydroentangling process may provide a lesser degree of
structural integrity in the first nonwoven layer versus that
provided to the second nonwoven layer via the second
hydroentangling process. Similar embodiments are contemplated with
regard to through air bonding, needlepunching, and thermal point
bonding.
[0111] Additionally, embodiments are contemplated where the
constituent substrates of the first nonwoven layer and the second
nonwoven layer are subjected to disparate forming or bonding
processes. For example, the constituent substrates of the first
nonwoven layer may be subjected to a hydroentangling process while
the constituent substrates of the first nonwoven layer are
subjected to a through air bonding process. Other examples include
subjecting one of the first nonwoven layer or the second nonwoven
layer to hydroentangling and the other nonwoven layer to
needlepunching, through air bonding, or thermal point bonding.
Another example includes subjecting one of the first nonwoven layer
or the second nonwoven layer to needlepunching and the other
nonwoven layer to through air bonding or thermal point bonding. Yet
another example includes subjecting one of the first nonwoven layer
or the second nonwoven layer to through air bonding and the other
to thermal point bonding. Embodiments are contemplated where the
forming or bonding process of the first nonwoven layer provides a
higher degree of structural integrity than that provided to the
second nonwoven layer. Alternatively, embodiments are contemplated
where the forming or bonding process of the first nonwoven layer
provides a lesser degree of structural integrity than that provided
to the second nonwoven layer.
[0112] It can be appreciated that in some embodiments, suitable
first and second nonwoven layers should comprise fibers capable of
experiencing sufficient plastic deformation and tensile elongation,
or are capable of sufficient fiber mobility, such that looped
fibers 408 (shown in FIGS. 3 and 4) are formed. However, it is
recognized that a certain percentage of fibers urged out of the
plane of the first surface of second nonwoven layer will not form a
loop, but instead will break and form loose ends. Such fibers are
referred to herein as "loose" fibers or non-looped fibers (i.e.
loose fiber ends) 418 (shown in FIGS. 3 and 4).
[0113] In some embodiments, most or all of the fibers of tufts can
be non-looped fibers. Non-looped fibers can also be the result of
forming tufts from nonwoven webs consisting of, or containing, cut
staple fibers. In such a case, some number of the staple fiber ends
may protrude into the tuft, depending upon such things as the
number of staple fibers in the web, the staple fiber cut length,
and the height of the tufts. In some instances, it may be desired
to use a blend of fibers of different lengths in a precursor web or
fibers of different lengths in different layers. This may be able
to selectively separate the longer fibers from the shorter fibers.
The longer fibers may predominately form the tuft while the shorter
fibers predominately remain in the portion of the web not forming
the tuft. A mixture of fiber lengths can include fibers of
approximately 2 to 8 centimeters for the longer fibers and less
than about 1 centimeter for the shorter fibers.
[0114] Regarding the nonwoven webs 200A, 200B, and 200C (shown in
FIGS. 2A-2C), for those embodiments where the nonwoven web is
utilized as a topsheet for a disposable absorbent article, it may
be desirable to increase the likelihood of the occurrence of
non-looped fibers 418 in the caps. The increase of non-looped
fibers 418 in the caps can increase the comfort to the wearer of
the absorbent article. Accordingly, shorter fibers may be utilized
for the first nonwoven layer or in those areas of the first
nonwoven layer that will urged into caps than those of the second
nonwoven layer. Similarly, in some embodiments, the fibers of the
first nonwoven layer may be more capable of experiencing more
plastic deformation before fracturing than the fibers of the second
nonwoven layer. In some embodiments, a combination of the above
approaches may be utilized with regard to the constituent fibers of
the first nonwoven layer versus the constituent fibers of the
second nonwoven layer.
[0115] Similarly, with regard to FIG. 7, as the tuft 770 may form a
portion of the user facing surface of a disposable absorbent
article, appropriate selection of fibers for the second nonwoven
layer 750 may be desirable to increase the likelihood of non-looped
fibers 418 in the tufts 770. Additionally, non-looped fibers 418
may be beneficial for the nonwoven webs 800 and 900 (shown in FIGS.
8 and 9). For example, since the tufts 870 and 970 are oriented in
the negative Z-direction, a large number of non-looped fibers 418
in the first nonwoven layer 810 or 910 may increase the
permeability of the first nonwoven layer 810 or 910. This increase
in permeability may reduce the need for apertures or in some
embodiments, fewer apertures may be required for adequate liquid
transfer to subjacent layers of a disposable absorbent article.
[0116] The first nonwoven layer and the second nonwoven layer, as
discussed previously, comprise, in some embodiments, a plurality of
randomly oriented fibers. The plurality of randomly oriented fibers
of the first nonwoven layer and/or the second nonwoven layer may
comprise any suitable thermoplastic polymer.
[0117] Suitable thermoplastic polymers, as used in the disclosed
compositions, are polymers that melt and then, upon cooling,
crystallize or harden, but can be re-melted upon further heating.
Suitable thermoplastic polymers used herein have a melting
temperature (also referred to as solidification temperature) from
about 60.degree. C. to about 300.degree. C., from about 80.degree.
C. to about 250.degree. C., or from 100.degree. C. to 215.degree.
C. And, the molecular weight of the thermoplastic polymer should be
sufficiently high to enable entanglement between polymer molecules
and yet low enough to be melt spinnable.
[0118] In some embodiments, the thermoplastic polymers can be
derived from renewable resources or from fossil minerals and oils.
The thermoplastic polymers derived from renewable resources are
bio-based, for example such as bio produced ethylene and propylene
monomers used in the production polypropylene and polyethylene.
These material properties are essentially identical to fossil based
product equivalents, except for the presence of carbon-14 in the
thermoplastic polymer. Renewable and fossil based thermoplastic
polymers can be combined together in the present invention in any
ratio, depending on cost and availability.
[0119] Recycled thermoplastic polymers can also be used, alone or
in combination with renewable and/or fossil derived thermoplastic
polymers. The recycled thermoplastic polymers can be
pre-conditioned to remove any unwanted contaminants prior to
compounding or they can be used during the compounding and
extrusion process, as well as simply left in the admixture. These
contaminants can include trace amounts of other polymers, pulp,
pigments, inorganic compounds, organic compounds and other
additives typically found in processed polymeric compositions. The
contaminants should not negatively impact the final performance
properties of the admixture, for example, causing spinning breaks
during a fiber spinning process.
[0120] Some suitable examples of thermoplastic polymers include
polyolefins, polyesters, polyamides, copolymers thereof, and
combinations thereof. In some embodiments, the thermoplastic
polymer can be selected from the group consisting of polypropylene,
polyethylene, polypropylene co-polymer, polyethylene co-polymer,
polyethylene terephthalate, polybutylene terephthalate, polylactic
acid, polyhydroxyalkanoates, polyamide-6, polyamide-6,6, and
combinations thereof. The polymer can be polypropylene based,
polyethylene based, polyhydroxyalkanoate based polymer systems,
copolymers and combinations thereof.
[0121] In some embodiments, the thermoplastic polymers include
polyolefins such as polyethylene or copolymers thereof, including
low density, high density, linear low density, or ultra low density
polyethylenes such that the polyethylene density ranges between
0.90 grams per cubic centimeter to 0.97 grams per cubic centimeter,
between 0.92 and 0.95 grams per cubic centimeter or any values
within these ranges or any ranges within these values. The density
of the polyethylene may be determined by the amount and type of
branching and depends on the polymerization technology and
co-monomer type. Polypropylene and/or polypropylene copolymers,
including atactic polypropylene; isotactic polypropylene,
syndiotactic polypropylene, and combination thereof can also be
used. Polypropylene copolymers, especially ethylene can be used to
lower the melting temperature and improve properties. These
polypropylene polymers can be produced using metallocene and
Ziegler-Natta catalyst systems. These polypropylene and
polyethylene compositions can be combined together to optimize
end-use properties. Polybutylene is also a useful polyolefin and
may be used in some embodiments.
[0122] Other suitable polymers include polyamides or copolymers
thereof, such as Nylon 6, Nylon 11, Nylon 12, Nylon 46, Nylon 66;
polyesters or copolymers thereof, such as maleic anhydride
polypropylene copolymer, polyethylene terephthalate; olefin
carboxylic acid copolymers such as ethylene/acrylic acid copolymer,
ethylene/maleic acid copolymer, ethylene/methacrylic acid
copolymer, ethylene/vinyl acetate copolymers or combinations
thereof; polyacrylates, polymethacrylates, and their copolymers
such as poly(methyl methacrylates). Other nonlimiting examples of
polymers include polycarbonates, polyvinyl acetates,
poly(oxymethylene), styrene copolymers, polyacrylates,
polymethacrylates, poly(methyl methacrylates), polystyrene/methyl
methacrylate copolymers, polyetherimides, polysulfones, or
combinations thereof. In some embodiments, thermoplastic polymers
include polypropylene, polyethylene, polyamides, polyvinyl alcohol,
ethylene acrylic acid, polyolefin carboxylic acid copolymers,
polyesters, and combinations thereof.
[0123] Biodegradable thermoplastic polymers also are contemplated
for use herein. Biodegradable materials are susceptible to being
assimilated by microorganisms, such as molds, fungi, and bacteria
when the biodegradable material is buried in the ground or
otherwise contacts the microorganisms (including contact under
environmental conditions conducive to the growth of the
microorganisms). Suitable biodegradable polymers also include those
biodegradable materials which are environmentally-degradable using
aerobic or anaerobic digestion procedures, or by virtue of being
exposed to environmental elements such as sunlight, rain, moisture,
wind, temperature, and the like.
[0124] The biodegradable thermoplastic polymers can be used
individually or as a combination of biodegradable or
non-biodegradable polymers. Biodegradable polymers include
polyesters containing aliphatic components. Among the polyesters
are ester polycondensates containing aliphatic constituents and
poly(hydroxycarboxylic) acid. The ester polycondensates include
diacids/diol aliphatic polyesters such as polybutylene succinate,
polybutylene succinate co-adipate, aliphatic/aromatic polyesters
such as terpolymers made of butylenes diol, adipic acid and
terephthalic acid. The poly(hydroxycarboxylic) acids include lactic
acid based homopolymers and copolymers, polyhydroxybutyrate (PHB),
or other polyhydroxyalkanoate homopolymers and copolymers. Such
polyhydroxyalkanoates include copolymers of PHB with higher chain
length monomers, such as C.sub.6-C.sub.12, and higher,
polyhydroxyalkanaotes, such as those disclosed in U.S. Pat. Nos. RE
36,548 and 5,990,271.
[0125] An example of a suitable commercially available polylactic
acid is NATUREWORKS from Cargill Dow and LACEA from Mitsui
Chemical. An example of a suitable commercially available
diacid/diol aliphatic polyester is the polybutylene
succinate/adipate copolymers sold as BIONOLLE 1000 and BIONOLLE
3000 from the Showa High Polymer Company, Ltd. (Tokyo, Japan). An
example of a suitable commercially available aliphatic/aromatic
copolyester is the poly(tetramethylene adipate-co-terephthalate)
sold as EASTAR BIO Copolyester from Eastman Chemical or ECOFLEX
from BASF.
[0126] Non-limiting examples of suitable commercially available
polypropylene or polypropylene copolymers include Basell Profax
PH-835 (a 35 melt flow rate Ziegler-Natta isotactic polypropylene
from Lyondell-Basell), Basell Metocene MF-650W (a 500 melt flow
rate metallocene isotactic polypropylene from Lyondell-Basell),
Polybond 3200 (a 250 melt flow rate maleic anhydride polypropylene
copolymer from Crompton), Exxon Achieve 3854 (a 25 melt flow rate
metallocene isotactic polypropylene from Exxon-Mobil Chemical),
Mosten NB425 (a 25 melt flow rate Ziegler-Natta isotactic
polypropylene from Unipetrol), Danimer 27510 (a
polyhydroxyalkanoate polypropylene from Danimer Scientific LLC),
Dow Aspun 6811A (a 27 melt index polyethylene polypropylene
copolymer from Dow Chemical), and Eastman 9921 (a polyester
terephthalic homopolymer with a nominally 0.81 intrinsic viscosity
from Eastman Chemical).
[0127] Polypropylene can have a melt flow index of greater than 5
g/10 min, as measured by ASTM D-1238, used for measuring
polypropylene. Other contemplated melt flow indices for
polypropylene include greater than 10 g/10 min, greater than 20
g/10 min, or about 5 g/10 min to about 50 g/10 min.
[0128] The thermoplastic polymer component can be a single polymer
species as described above or a blend of two or more thermoplastic
polymers as described above.
[0129] In some embodiments, the first nonwoven layer and second
nonwoven layer may be fibrous woven or nonwoven webs comprising
elastic or elastomeric fibers. Elastic or elastomeric fibers can be
stretched at least about 50% and return to within 10% of their
original dimension. Tufts can be formed from elastic fibers if the
fibers are simply displaced due to the mobility of the fiber within
the nonwoven, or if the fibers are stretched beyond their elastic
limit and are plastically deformed.
[0130] In some embodiments, the constituent fibers of the first
nonwoven layer can be comprised of polymers such as polypropylene
and blends of polypropylene and polyethylene. In some embodiments,
the second nonwoven layer may comprise fibers selected from
polypropylene, polypropylene/polyethylene blends, and
polyethylene/polyethylene teraphthalate blends. In some
embodiments, the second nonwoven layer may comprise fibers selected
from cellulose rayon, cotton, other hydrophilic fiber materials, or
combinations thereof. The fibers can also comprise a super
absorbent material such as polyacrylate or any combination of
suitable materials.
[0131] In one embodiment, the constituent fibers of the first
nonwoven layer are selected such that the first nonwoven layer is
hydrophobic, and the constituent fibers of the second nonwoven
layer are selected such that the second nonwoven layer is
hydrophilic. For example, in some embodiments, the fibers of the
first nonwoven layer may comprise polypropylene, while the fibers
of the second nonwoven layer comprise rayon. In one specific
embodiment, the fibers of the second nonwoven layer comprise
thermoplastic fibers that are treated with a topical surfactant or
comprise a hydrophilic melt additive that blooms to the surface in
order to render the second nonwoven layer hydrophilic. In such
embodiments, the second nonwoven layer may comprise the fibers as
mentioned previously for the first nonwoven layer. Some examples of
suitable hydrophilic treatments include Silastol PH26 available
from Schill & Seilacher or Stantex S6327 available from Pulcra
Chemicals GmbH each of which is a post fiber production hydrophilic
treatment. Suitable hydrophilic melt additives are available from
Polyvel, Inc. sold under the trade name VW351 wetting agent and
from Goulston Technologies Inc. under the trade name Hydrosorb
1001. Other suitable hydrophilic additives are available from
Techmer PM, LLC under the trade names PPM15560, TPM12713, PPM19913,
PPM19441, PPM 19914 (for polypropylene) and PPM19668 (for
polyethylene). Additional examples of hydrophilic additives whether
as a master batch or post fiber production are described in U.S.
Patent Application No. 2012/0077886; U.S. Pat. No. 5,969,026; and
U.S. Pat. No. 4,578,414.
[0132] The fibers of the nonwoven layer and/or the second nonwoven
layer can be monocomponent, bi-component, and/or bi-constituent,
round or non-round (e.g., capillary channel fibers), and can have
major cross-sectional dimensions (e.g., diameter for round fibers)
ranging from 0.1-500 microns. For example, one type of fibers
suitable for the nonwoven web includes nanofibers. Nanofibers are
described as fibers having a mean diameter of less than 1 micron.
Nanofibers can comprise all of the fibers in a nonwoven web or a
portion of the fibers in a nonwoven web. The constituent fibers of
the nonwoven precursor web may also be a mixture of different fiber
types, differing in such features as chemistry (e.g. polyethylene
and polypropylene), components (mono- and bi-), denier (micro
denier and >20 denier), shape (i.e. capillary and round) and the
like. The constituent fibers can range from about 0.1 denier to
about 100 denier.
[0133] Embodiments are contemplated where the first plurality of
fibers and/or the second plurality of fibers comprise agents in
addition to their constituent chemistry. For example, suitable
additives include additives for coloration, antistatic properties,
lubrication, hydrophilicity, and the like and combinations thereof.
These additives, for example titanium dioxide for coloration, are
generally present in an amount less than about 5 weight percent and
more typically about 2 weight percent.
[0134] As used herein, the term "monocomponent" fiber refers to a
fiber formed from one extruder using one or more polymers. This is
not meant to exclude fibers formed from one polymer to which small
amounts of additives have been added for coloration, antistatic
properties, lubrication, hydrophilicity, etc.
[0135] As used herein, the term "bi-component fibers" refers to
fibers which have been formed from at least two different polymers
extruded from separate extruders but spun together to form one
fiber. Bi-component fibers are also sometimes referred to as
conjugate fibers or multicomponent fibers. The polymers are
arranged in substantially constantly positioned distinct zones
across the cross-section of the bi-component fibers and extend
continuously along the length of the bi-component fibers. The
configuration of such a bi-component fiber may be, for example, a
sheath/core arrangement wherein one polymer is surrounded by
another, or may be a side-by-side arrangement, a pie arrangement,
or an "islands-in-the-sea" arrangement. Some specific examples of
fibers which can be used in the first nonwoven layer include
polyethylene/polypropylene side-by-side bi-component fibers.
Another example, is a polypropylene/polyethylene bi-component fiber
where the polyethylene is configured as a sheath and the
polypropylene is configured as a core within the sheath. Still
another example, is a polypropylene/polypropylene bi-component
fiber where two different propylene polymers are configured in a
side-by-side configuration. Additionally, embodiments are
contemplated where the constituent fibers of the first nonwoven
layer are crimped.
[0136] As used herein, the term "bi-constituent fibers" refers to
fibers which have been formed from at least two polymers extruded
from the same extruder as a blend. Bi-constituent fibers do not
have the various polymer components arranged in relatively
constantly positioned distinct zones across the cross-sectional
area of the fiber and the various polymers are usually not
continuous along the entire length of the fiber, instead usually
forming fibrils which start and end at random. Bi-constituent
fibers are sometimes also referred to as multi-constituent
fibers.
[0137] As used herein, the term "non-round fibers" describes fibers
having a non-round cross-section, and includes "shaped fibers" and
"capillary channel fibers." Such fibers can be solid or hollow, and
they can be tri-lobal, delta-shaped, and can be fibers having
capillary channels on their outer surfaces. The capillary channels
can be of various cross-sectional shapes such as "U-shaped",
"H-shaped", "C-shaped" and "V-shaped". One practical capillary
channel fiber is T-401, designated as 4DG fiber available from
Fiber Innovation Technologies, Johnson City, Tenn. T-401 fiber is a
polyethylene terephthalate (PET polyester).
[0138] In some embodiments, the first nonwoven layer and/or second
nonwoven layer is a nonwoven web in which there are minimal
fiber-to-fiber bonds. For example, the first nonwoven layer and/or
second nonwoven layer can be a nonwoven web having a pattern of
discrete thermal point bonds, as is commonly known in the art for
nonwoven webs. In general, however, it is desirable to minimize the
number of bond points and maximize the spacing so as to allow for
maximum fiber mobility and dislocation during formation of tufts
and/or caps. In general, using fibers having relatively high
diameters, and/or relatively high extension to break, and/or
relatively high fiber mobility, might result in better and more
distinctly formed tufts and/or caps. In another embodiment, the
first nonwoven layer and/or the second nonwoven layer can be
through air bonded nonwoven material.
[0139] Although nonwoven webs of the present invention disclosed
herein are described as a two layer web made from two nonwoven
layers, it is not necessary that it be limited to two layers. For
example, a three-layer or more laminate can be made from three
nonwoven layer. Embodiments are contemplated where there are three
or more layers of nonwoven material.
[0140] The first nonwoven layer and the second nonwoven layer of
the nonwoven webs 200A, 200B, 200C, 700, 800, and 900, (shown in
FIGS. 2A-2C and 7-9, respectively), can be held in a face-to-face
laminated relationship by virtue of the "locking" effect of the
tufts that extend through the discrepancies in first nonwoven layer
or second nonwoven layer as described herein. In some embodiments
(including the nonwoven webs 100A and 100B shown in FIGS. 1A and
1B) it may be desirable to use adhesives or thermal bonding or
other bonding means, depending on the end use application of the
nonwoven web. Additionally, it may be desirable to apply adhesive
to at least a portion of one of the first nonwoven layer and/or the
second nonwoven layer. For example, in some embodiments adhesive,
chemical bonding, resin or powder bonding, or thermal bonding
between layers can be selectively applied to certain regions or all
of the nonwoven layers. In the case of adhesive application, for
example, adhesive can be applied in a continuous manner, such as by
slot coating, or in a discontinuous manner, such as by spraying,
extruding, and the like. Discontinuous application of adhesive can
be in the form of stripes, bands, droplets, and the like. Any
suitable adhesive may be utilized.
[0141] In one embodiment, after tufts and/or caps are formed, the
nonwoven material (the constituents of the first nonwoven layer,
and/or the constituents of the second nonwoven layer, and/or the
resultant nonwoven web that is a combination of the first nonwoven
layer and the second nonwoven layer) may be attached as described
in U.S. Pat. No. 7,682,686. For example, the first nonwoven layer
and the second nonwoven layer may be attached adjacent the cap base
471 (shown in FIG. 4). As another example, the first nonwoven layer
and the second nonwoven layer may be attached adjacent an apex of
the cap. In yet another example, the first nonwoven layer and the
second nonwoven layer may be attached adjacent the cap base 471 and
adjacent the apex of the cap. Regarding the above embodiments,
attachment may be provided for each cap present or provided to less
than the totality of caps.
[0142] Any suitable process for aperturing the first nonwoven layer
and/or the second nonwoven layer may be utilized. However, the
aperturing process selected should not preclude the liquid
communication relationship between the first nonwoven layer and the
second nonwoven layer. Some suitable aperturing processes for the
first nonwoven layer and/or the second nonwoven layer are described
in U.S. Pat. Nos. 5,628,097; 5,916,661; 5,658,639; 6,884,494; and
7,037,569. Additional suitable processes are described in U.S. Pat.
Nos. 8,679,391; 8,241,543; and 8,158,043. Additionally, in some
embodiments, aperturing may be achieved via a spunlacing process.
For example, the first nonwoven layer and/or the second nonwoven
layer may transported to a hydroentangling apparatus. A carrier
transporting the first and/or second nonwoven layer, may comprise
large openings which allow fluid to pass therethrough. During the
hydroentangling process, the constituent fibers of the first and/or
second nonwoven layers may be moved via the water jets of the
hydroentangling and generally mimic the pattern of the carrier. As
such, the first and/or second nonwoven layer may comprise apertures
which mimic the openings in the carrier.
[0143] The aperturing of the first and/or second nonwoven layers
may be done separately or contemporaneously where the first
nonwoven layer and the second nonwoven layer are configured as a
laminate web. The area of each of the individual apertures of the
present invention may be about 0.8 mm.sup.2 to about 4.0 mm.sup.2
or, in some embodiments, from about 1.5 mm.sup.2 to about 2.5
mm.sup.2, specifically including any values within these ranges or
any ranges created thereby. In some embodiments, the overall open
area of the first nonwoven layer and/or the second nonwoven layer
may be from about 9 percent to about 30 percent, specifically
including all values within this range and any ranges created
thereby. The percentage open area is defined as a ratio of the sum
of the area of apertures divided by the total area of the layer
(apertures plus land areas).
[0144] It is worth noting that care should be exercised in
selecting both the aperture area and overall open area. For
example, while larger apertures may facilitate fluid acquisition
into lower layers of an absorbent article, larger apertures can
create a problem from a rewet standpoint. Additionally, larger
aperture sizes can weaken the nonwoven to such an extent as to
introduce tearing issues during manufacture or during use by the
wearer.
Hydrophobic Additive
[0145] As mentioned previously, the first nonwoven layers described
herein, comprise a first plurality of substantially randomly
oriented fibers. Additionally, the first nonwoven layers described
herein may comprise an additive which blooms on a surface of at
least a portion of the first plurality of fibers. The additive may
be applied on the fibers post production or may be added directly
or as master batch to the polymer melt during spinning of the
filaments as a melt additive. For those embodiments where the
additive is melt blended into the filaments, the additive can bloom
to the surface of the fibers and create a film covering a portion
of the external surface of the fiber and/or can create fibrils,
flakes, particles, and/or other surface features. For those
embodiments where the additive is applied to the fibers post
production, the additive can form particles, films, flakes, and/or
droplets. For those fibers comprising fibrils, the fibrils may
extend outwardly, or radially outwardly, from the surface.
[0146] While the fibrils extend outwardly from surfaces of
individual fibers, the fibrils may also extend to or from (i.e.,
contact) other fibers within the same layer or a different layer of
a nonwoven substrate and/or to fibrils extending from fibers within
the same layer or a different layer of the nonwoven substrate. When
the fibrils extend between fibers and/or other fibrils, the
nonwoven substrate may achieve a greater liquid contact angle for
polar and non-polar liquids. A similar effect may be obtained for
additives which are applied to the first plurality of fibers post
production. Without wishing to be bound by theory, it is believed
that the additive, regardless of whether a melt additive or applied
post fiber production, changes the surface energy of the
constituent fibers. The change in surface energy increases the
hydrophobic nature of the constituent fibers and therefore the
first nonwoven layer. Additionally, it is believed that the
additive, whether a melt additive or applied post fiber production,
increases the surface roughness of the constituent fibers which can
increase hydrophobicity. It is believed that an increase in
hydrophobicity due to surface roughness is achieved by metastable
Wenzel and stable Cassie-Baxter non-wetting states.
[0147] The additive suitable for the present invention may be any
suitable hydrophobic additive. Thus, the additives may increase the
hydrophobicity of the fibers upon whose surface they bloom. This
can lead to increased low surface tension fluid strikethrough times
and higher hydrophobicity for the first nonwoven layer and/or when
compared to the second nonwoven layer.
[0148] Some examples of suitable additives include fatty alcohols
and fatty acid esters. Non-limiting examples of suitable fatty
alcohols having from about 12 to about 24 carbon atoms include
saturated, un-substituted, monohydric alcohols or combinations
thereof, which have a melting point less than about 110.degree. C.,
preferably from about 45.degree. C. to about 110.degree. C.
Specific examples of fatty alcohol carriers for use in the skin
care compositions of the present invention include, but are not
limited to, cetyl alcohol, stearyl alcohol, cetearyl alcohol,
behenyl alcohol, arachidyl alcohol, lignocaryl alcohol, and
combinations thereof. Examples of commercially available cetearyl
alcohol are Stenol 1822 and behenyl alcohol is Lanette 22, both of
which are available from the Cognis Corporation located in
Cincinnati, Ohio.
[0149] Non-limiting examples of suitable fatty acid esters include
those fatty acid esters derived from a mixture of C.sub.12-C.sub.28
fatty acids and short chain (C.sub.1-C.sub.8, preferably
C.sub.1-C.sub.3) monohydric alcohols preferably from a mixture of
C.sub.16-C.sub.24 saturated fatty acids and short chain
(C.sub.1-C.sub.8, preferably C.sub.1-C.sub.3) monohydric alcohols.
Representative examples of such esters include methyl palmitate,
methyl stearate, isopropyl laurate, isopropyl myristate, isopropyl
palmitate, ethylhexyl palmitate, and mixtures thereof. Suitable
fatty acid esters can also be derived from esters of longer chain
fatty alcohols (C.sub.12-C.sub.28, preferably C.sub.12-C.sub.16)
and shorter chain fatty acids such as lactic acid, specific
examples of which include lauryl lactate and cetyl lactate.
[0150] In some embodiments, the additives of the present
disclosure, may have a melting point in the range of about 40
degrees C. to about 80 degrees C., about 55 degrees C. to about 75
degrees C., about 60 degrees C. to about 73 degrees C.,
specifically reciting all one degree C. increments within the
specified ranges and all ranges formed therein or thereby. In
various embodiments, the additives of the present disclosure may
have a melting temperature above 30.degree. C., above 40.degree.
C., or above 50.degree. C., but less than 80 degrees C., including
all ranges within the values expressed and all numbers within the
ranges created by the values expressed.
[0151] In some embodiments, the additive may have a
hydrophilic/lipophilic balance ("HLB") value of less than about 4.
In some embodiments, the HLB value may be greater than about 0 and
less than about 4, between about 1 and about 3.5, between about 2
and about 3.3, or any ranges within the values provided or any
value within the ranges provided. It is believed that above an HLB
value of about 4, the additive will start to take on more
surfactant-like hydrophilic properties and would thereby reduce the
benefit provided by the highly hydrophobic additive. Namely, as
mentioned previously, the hydrophobic additive can provide a
masking benefit which makes the disposable absorbent article
utilizing the nonwoven web of the present invention appear more
"clean" after a liquid insult has occurred.
[0152] In some embodiments, the additive may have an IOB (inorganic
value/organic value) value of greater than about 0 and less than
about 0.4, between about 0.1 and about 0.35, between about 0.2 and
0.33, specifically including all values within these ranges and any
ranges created thereby. The IOB value is discussed in additional
detail in EP Patent Application Publication No. 2517689.
[0153] The additives used, may comprise fatty acid derivatives,
such as a fatty acid ester; typically an ester formed from an
alcohol with two or more hydroxyl groups and one or more fatty
acids having between at least 12 carbon atoms to 22 carbon atoms,
or at least 14 carbon atoms, whereby within one ester compound,
different fatty acid-derived groups may be present (herein referred
to as fatty acid ester).
[0154] The fatty acid ester compound may be an ester of an alcohol
carrying two or more, or three or more, functional hydroxyl group
per alcohol molecule, whereby all of the hydroxyl groups form an
ester bond with fatty acids (either the fatty acid or mixtures
thereof).
[0155] In an embodiment, the alcohol may have three functional
hydroxyl groups. It is understood that in a fatty acid ester having
more than one ester bond, such as in di- or tri-glycerides, the
fatty acid-derived group may be the same, or they may be two or
even three different fatty acids-derived groups. It is further
understood that the additive component may comprise a mixture of
mono- di-and/or tri-fatty acid ester (e.g. mono- di-, and/or
triglyceride) esters with the same fatty-acid derived group per
molecule, and/or with different fatty acid-derived groups without
exceeding the scope of the invention. Preferred fatty acids in at
least one embodiment may range from a C8 fatty acid to a C30 fatty
acid; or, in another embodiment range from a C12 fatty acid to a
C22 fatty acid. Suitable vegetable fatty acids typically include
unsaturated fatty acids. The fatty acid may suitably be selected
from the group comprising an arachidec acid, a stearic acid, a
palmitic acid, a myristic acid, a myristoleic acid, an oleic acid,
a limoleic acid, a linolenic acid, and an arachidonic acid. In
another further embodiment, a substantially saturated fatty acid is
preferred, particularly when saturation arises as a result of
hydrogenation of fatty acid precursor. The fatty acids may range
from a C12 fatty acid to a C22 fatty acid as illustrated in
[1],
##STR00001##
where R1' R2, and R3 each have a number of carbon atoms ranging
from 11 to 21. In at least one other embodiment, the fatty acids
may range from a C16 fatty acid to a C20 fatty acid.
[0156] In at least one further embodiment, a substantially
saturated fatty acid is preferred, particularly when saturation
arises as a result of hydrogenation of fatty acid precursor. In at
least one further embodiment, a C18 fatty acid, stearic acid, is
preferred. An example of the stearic acid-substituted fatty acid is
[2-octadecanoyloxy-1-(octadecanoyloxymethyl)ethyl]octadecanoate
having a CAS registry number of 555-43-1. It should be understood
that the preferred triglyceride ester has an esterified glycerol
backbone having no non-hydrogen sub-stitutents on the glycerol
backbone.
[0157] In an embodiment, the one or more additives may comprise a
mono- and/or di-glyceride ester, and/or a triglyceride ester, (with
one, two or three fatty acid-derived groups). It should be
understood that while [1] illustrates a simple triglyceride in
which all three pendent fatty acids may be the same, other
embodiments may include a mixed triglyceride in which two or even
three different pendent fatty acids are present without exceeding
the scope of the invention. It should be further understood that
while the triglyceride ester is illustrated in [1] is a single
triglyceride ester formulation, the triglyceride ester used in the
preparation of the master batch may include a plurality of
triglyceride esters having different pendent fatty acid groups
and/or one or more derivatives of the fatty acid, without exceeding
the scope of the invention. It should be further understood that
while the triglyceride ester illustrated in [1] is a monomer, the
triglyceride ester used in the preparation of the master batch may
include a polymerized triglyceride ester, such as a polymerized,
saturated glyceride ester without exceeding the scope of the
invention. It should be further understood that the polymerized
triglyceride ester may comprise a mixture of polymers having
different numbers of monomeric units included in the polymer. For
example the polymerized triglyceride ester may include a mixture of
monoesters, diesters, and the like.
[0158] The fatty acids used to form the ester compounds include
fatty acid derivatives for the purpose of the present disclosure. A
mono-fatty acid ester, or for example, amono-glyceride, comprises a
single fatty acid, e.g., connected a glycerol; a di-fatty acid
ester, or e.g., di-glyceride, comprises two fatty acids, e.g.,
connected to the glycerol; a tri-fatty acid ester, or e.g.
tri-glyceride, comprises three fatty acids, e.g., connected to a
glycerol. In an embodiment, the additive may comprise at least a
triglyceride ester of fatty acids (i.e., the same or different
fatty acids).
[0159] It should be understood that the triglyceride ester may have
an esterified glycerol backbone having no nonhydrogen substituents
on the glycerol backbone; however, the glycerol backbone may also
comprise other substituents.
[0160] In an embodiment, the glycerol backbone of the glycerol
ester may only comprise hydrogen. The glyceride esters may also
comprise polymerized (e.g., tri) glyceride esters, such as a
polymerized, saturated glyceride esters.
[0161] In a fatty acid ester having more than one ester bond, such
as in di- or tri-glycerides, the fatty acid-derived group may be
the same, or they may be two or even three different fatty
acids-derived groups.
[0162] The additive may comprise a mixture of mono-, di-, and/or
tri-fatty acid ester (e.g., mono-di- and/or triglyceride) esters
with the same fatty-acid derived group per molecule, and/or with
different fatty acid-derived groups.
[0163] The fatty acids may originate from vegetable, animal, and/or
synthetic sources. Some fatty acids may range from a C8 fatty acid
to a C30 fatty acid, or from a C12 fatty acid to a C22 fatty acid.
Suitable vegetable fatty acids typically include unsaturated fatty
acids such as oleic acid, palmitic acid, linoleic acid, and
linolenic acid. The fatty acid may be arachidec, stearic, palmitic,
myristic, myristoleic, oleic, limoleic, linolenic, and/or
arachidonic acid.
[0164] In another embodiment, a substantially saturated fatty acid
may be used, particularly when saturation arises as a result of
hydrogenation of fatty acid precursor. In an embodiment, a C18
fatty acid, or octadecanoic acid, or more commonly called stearic
acid may be used to form an ester bond of the fatty acid ester
herein; stearic acid may be derived from animal fat and oils as
well as some vegetable oils. The stearic acid may also be prepared
by hydrogenation of vegetable oils, such as cottonseed oil. The
fatty acid ester herein may comprise fatty acids of mixed
hydrogenated vegetable oil, such as one having CAS registration
number 68334-28-1.
[0165] At least one stearic acid, at least two, or three stearic
acids are connected to a glycerol, to form a glycerol tristearate,
for the additive herein. In an embodiment, the additive may
comprise a glycerol tristearate (CAS No. 555-43-1), also known by
such names as tristearin or 1,2,3-Trioctadecanoylglycerol. (In the
following, the name glycerol tristearate will be used, and in case
of doubt the CAS No., shall be seen as the primary identifier).
[0166] In other embodiments, additives with chemical structures
similar to glycerol tristearate or tristearin such as
triacylglycerols (triglycerides) including but not limited to
trimyristin, tripalmitin, trilaurin, trimargarine, and waxes such
as distearin, and mixtures of saturated and unsaturated glycerides,
such as 1,3-distearoyl-2-oleoylglycerol (SOS) may be utilized.
Non-limiting examples additives having molecular and crystallite
structures as similar to tristearin include Alkylketene dimers
(AKD), inorganic and organic salts of fatty acids (also known as
alkyl carboxylic acids) that comprise of alkyl chains that are
mostly saturated, and contain between 12 and 22 carbon atoms.
Non-limiting examples of salts of fatty acids include zinc
stearate, calcium stearate, magnesium stearate, titanium stearate,
silver stearate, aluminum di- and tri-stearates, aluminum
tripalmitate, aluminum trimyristate, aluminum trilaurate, sorbitan
tristearate, sorbitan tripalmitate, sorbitan trimyristate, sorbitan
trilaurate, and combinations thereof, which are believed to form
flaky and fibrillar lamellar structures on surfaces due to
blooming.
[0167] In an embodiment, the fatty acid ester of the additive may
have a number-averaged molecular weight ranging from 500 to 2000,
from 650 to 1200, or from 750 to 1000, specifically reciting all
whole integer increments within the above-specified ranges and any
ranges formed therein or thereby.
[0168] The additive may comprise very little or no halogen atoms;
for example, the additive may comprise less than 5 wt. % halogen
atoms (by weight of the additive), or less than 1 wt. %, or less
than 0.1 wt. % of the additive; the additive may be substantially
halogen-free.
[0169] In an embodiment, the additive may be or may comprise a
lipid ester or glycerol tristearate. In various embodiments, the
fibrils may comprise, consist of, or consist essentially of (i.e.,
51% to 100%, 51% to 99%, 60% to 99%, 70% to 95%, 75% to 95%, 80% to
95%, specifically including all 0.1% increments within the
specified ranges and all ranges formed therein or thereby) of the
additive.
[0170] Nonlimiting examples of suitable alkyl ethoxylates include
C.sub.12-C.sub.22 fatty alcohol ethoxylates having an average
degree of ethoxylation of from about 2 to about 30. Non-limiting
examples of suitable lower alcohols having from about 1 to about 6
carbon atoms include ethanol, isopropanol, butanediol,
1,2,4-butanetriol, 1,2 hexanediol, ether propanol, and mixtures
thereof. Non-limiting examples of suitable low molecular weight
glycols and polyols include ethylene glycol, polyethylene glycol
(e.g., Molecular Weight 200-600 g/mole), butylene glycol, propylene
glycol, polypropylene glycol (e.g., Molecular Weight 425-2025
g/mole), and mixtures thereof.
[0171] The master batch added to the composition from which the
fibers of the present disclosure are formed may be the master batch
disclosed in U.S. Pat. No. 8,026,188 to Mor.
[0172] In an embodiment, the fibrils may grow out of the fibers
post-nonwoven substrate formation under ambient conditions. The
fibrils may be noticeable using an SEM after about 6 hours
post-nonwoven substrate formation under ambient conditions. Fibril
growth may reach a plateau after about 50 hours, 75 hours, 100
hours, 200 hours, or 300 hours post-nonwoven substrate formation
under ambient conditions. In some embodiments, fibril growth may
continue well beyond 300 hours. The time range of noticeable fibril
growth post-nonwoven substrate formation may be in the range of 1
minute to 300 hours, 5 hours to 250 hours, 6 hours to 200 hours, 6
hours to 100 hours, 6 hours to 24 hours, 6 hours to 48 hours, or 6
hours to 72 hours, under ambient conditions, specifically reciting
all 1 minute increments within the above specified ranges and all
ranges formed therein or thereby. The time to allow full fibril
growth post-nonwoven substrate formation may be 12 hours, 24 hours,
48 hours, 60 hours, 72 hours, 100 hours, or 200 hours, for example,
under ambient conditions. In some embodiments, fibril growth may
occur almost immediately post nonwoven production.
[0173] Typical size scale of fibril or flake or other surface
structures protruding from surface due to blooming may be of the
order of few nanometers to few tens of micrometers. For example,
the average length of the bloomed surface structures can range from
about 5 nanometers to about 50 micrometers, from about 100
nanometers to about 30 micrometers, or from about 500 nanometers to
about 20 micrometers. Preferred average width of the bloomed
surface structures can range from about 5 nanometers to about 50
micrometers, from about 100 nanometers to about 20 micrometers, or
from about 500 nanometers to about 5 micrometers. Preferred average
thickness of the bloomed surface structures would range from about
5 nanometers to about 10 micrometers, more preferably from about 50
nanometers to about 5 micrometers, and most preferably from about
100 nanometers to about 1 micrometers. Preferred average hydraulic
diameter, calculated as 4*(Cross-sectional Area)/(Cross-sectional
Perimeter) of the bloomed surface structure can range from about 5
nanometers to about 20 micrometers, from about 50 nanometers to
about 10 micrometers, or from about 100 nanometers to about 1.5
micrometers. In a specific embodiment, the average hydraulic
diameter of a fibril is in the range of from about 100 nanometers
to about 800 nanometers. Average separation of the bloomed surface
structures from one another can range from about 100 nanometers to
about 20 micrometers, from about 500 nanometers to about 10
micrometers, or from about 500 nanometers to about 5
micrometers.
[0174] The nonwoven substrates of the present disclosure having at
least one layer comprising fibers comprising fibrils may be
configured to be softer or harder than, or have the same softness
as, conventional nonwoven substrates and/or may have a rougher,
smoother, or the same tactile property as compared to conventional
nonwoven substrates. The softness, hardness, and/or tactile
property of the nonwoven substrates may vary depending on the type
and amount of lipid esters present in the composition used to form
the fibers and the length of the fibrils, for example. The
softness, hardness, and/or texture may also vary depending on where
the one or more layers of fibers having fibrils are positioned
within a nonwoven substrate.
[0175] In an embodiment, the fibrils/droplets may have a different
color than the fibers from which they grow. Stated another way, the
fibrils may have a first color and the fibers from which they grow
may have a second color in non-fibril areas of the fibers. The
first color may be different than the second color (e.g., the
fibers in non-fibril areas may be white and the fibrils may be blue
or the fibers in non-fibril areas may be light blue and the fibrils
may be dark blue). This color variation can be accomplished by
adding a colorant, such as a pigment or dye to the lipid esters
before they are mixed into the composition used to form the fibers.
When the additive blooms from the fibers, they can be a different
color than the fibers from which they grow, thereby producing a
color contrast between the fibrils and the fibers from which they
grow. In an embodiment, the first nonwoven layer comprising the
fibers comprising the fibrils may appear to change color over a
period of time (i.e., the period of time in which the fibrils grow
or a portion thereof) due to the contrasting color of the fibrils
with respect to the fibers from which they grow. Different layers
of fibers may have different colored fibrils and/or fiber therein
within the same nonwoven substrate. In an embodiment, the colorant
added to the lipid esters may be dissolvable in urine, menses,
runny BM, other bodily fluid, or other fluid (e.g., water). In
various embodiments, the dissolving colorant in the fibrils may be
used as a wetness indicator in an absorbent article, for
example.
[0176] For those embodiments where the hydrophobic additive is
applied post fiber production, the additive may be selectively
applied. For example, the additive may be applied in a first area
of the nonwoven web and may not be applied in a second area. As
another example, the additive may be applied in specific patterns
with void spaces to encourage fluid drainage to the second nonwoven
layer. The additive may be applied at a basis weight of from about
0.1 gsm to 10 gsm, preferably <1 gsm. The additive may be
blended with other melt additive or topical ingredients, for
example in a lotion composition. The additive may be applied
uniformly throughout the nonwoven material or alternatively be
applied in zones or layers or gradients, for example preferentially
in the center portion of a topsheet. For those embodiments where
bi-component fibers are utilized, the additive may be present at
the same level in each of the constituents of the bi-component
fiber, may be at different levels with regard to the constituents
of the bi-component fiber, or may be preset in one constituent but
not the other of a bi-component fiber.
[0177] For those embodiments where the hydrophobic additive is
provided as a melt additive, e.g. part of the master batch,
preferably between 0.5 percent by weight to about 20 percent by
weight, preferably less than 10 percent by weight or any range
within these values or any value within these ranges.
[0178] The additive may be applied to the fibers of the nonwoven
web by any suitable process. Some examples include spraying, slot
coating, or the like. Other suitable hydrophobic additives are
available from Techmer PM, LLC.
[0179] Embodiments are contemplated where the first nonwoven layer
and/or the second nonwoven layer include compositions in addition
to the additive. Some examples include lotions, skin care actives,
odor absorbing or inhibiting or masking, fragrances, pigments,
dyes, agents affecting the coefficient of friction,
antimicrobial/antibacterial agents, the like or combinations
thereof.
EXAMPLES
[0180] FIG. 11 is an SEM photo of a polypropylene fiber with
glycerol tristearate additive added to the fibers as a master batch
(8 wt % Techmer PPM 17000 High Load Hydrophobic). The masterbatch
comprised about 60 percent by weight polypropylene and about 40
percent by weight glycerol tristearate. As shown the fiber 1191
comprise a plurality of fibrils 1192 extending from the surface
thereof.
[0181] FIG. 12 is an SEM photo of a bi-component fiber 1291 of
polyethylene and polypropylene arranged in 30/70 sheath/core
configuration--the polyethylene being the sheath. The additive
(glycerol tristearate) was added to the fibers as a master batch
(17% of Techmer PPM 17000 High Load Hydrophobic). The master batch
comprised about 60 percent by weight polyethylene and about 40
percent by weight glycerol tristearate. The sheath of the fiber
comprised 17 percent by weight master batch and 83 percent by
weight polyethylene. As shown, the fiber 1291 comprises a plurality
of fibrils 1292 extending therefrom.
[0182] FIG. 13 is an SEM photo of a bi-component fiber 1391 of
polyethylene and polypropylene arranged in 30/70 sheath/core
configuration--polyethylene being the sheath. The additive
(glycerol tristearate) was added to the fibers as a master batch.
The master batch comprised about 60 percent by weight polyethylene
and about 40 percent by weight glycerol tristearate. The sheath of
the fiber comprised 30 percent by weight master batch and 70
percent by weight polyethylene. As shown, the fiber 1391 comprises
a plurality of fibrils 1392 extending therefrom.
[0183] FIGS. 14 and 15 demonstrate that the additive can be added
variably with regard to differing components of a fiber. FIG. 14 is
an SEM photo of a polypropylene/polyethylene bi-component fiber
1491 where the polypropylene and the polyethylene are configured
side by side--polyethylene 1491A and polypropylene 1491B. The
additive was added at varying levels as a master batch (Techmer
PPM17000 High Load Hydrophobic)--10% master batch was added to the
polypropylene component and 5% of the same master batch was added
to the polyethylene component.
[0184] FIG. 15 is an SEM photo of a polypropylene/polyethylene
bi-component fiber 1591 where the polypropylene and polyethylene
are configured side by side--polypropylene 1591A and polyethylene
1591B comprising fibrils 1592. The additive was added at varying
levels as a master batch (Techmer PPM17000 High Load
Hydrophobic)--16% master batch was added to the polypropylene
component and 8% master batch was added to the polyethylene
component. In some instances, the additive may bloom more on one
side of the bi-component fiber 1591 than the other.
[0185] FIG. 16 is an SEM photo showing a plurality of fibers of a
nonwoven where the additive has been applied post fiber production.
As shown, the additive forms a plurality of droplets/particles 1692
on the surface of the fibers.
[0186] FIGS. 17 and 18 are SEM photos showing fibers comprising a
melt additive. In FIG. 17, the additive has bloomed to the surface
of the fibers to form a film, and in FIG. 18, the additive has
bloomed to the surface of the fiber to form a film/fibril
combination. In FIG. 17, polypropylene fibers with 16 percent by
weight master batch (Techmer PPM17000 High Load Hydrophobic) are
shown.
[0187] In FIG. 18, the fibers are bi-component
polypropylene/polyethylene fibers in a side by side configuration.
The polypropylene comprises 16 percent by weight master batch
(Techmer PPM 17000 High Load Hydrophobic), and the polyethylene
component comprises 8 percent by weight of the same master
batch.
[0188] In FIGS. 19A-19C nonwoven layers comprising fibers with
hydrophobic melt additive are shown; however, the melt additive did
not present itself in the form of fibrils. In FIG. 19A, the fibers
are 2.6 denier per filament and comprise 60/40 side/side
polypropylene/polypropylene, using Lyondell Basell HP561R in the
first component and Lyondell Basell HP552 R in the second
component. Both components additionally comprise 16% Techmer
PPM17000 High Load Hydrophobic masterbatch, and 1% of TiO.sub.2
masterbatch (MBWhite009). In FIG. 19A, the hydrophobic melt
additive creates a wrinkled texture on the fiber surface.
[0189] In FIGS. 19B and 19C, a nonwoven layer comprising fibers
having a denier of 2.0 and comprise 60/40 side/side
polypropylene/polypropylene, using Lyondell Basell HP561R in the
first component and Lyondell Basell HP552 R in the second
component. Both components additionally comprise 10% Techmer
PPM17000 High Load Hydrophobic masterbatch, and 1% of TiO.sub.2
masterbatch (MBWhite009). As shown, the lower amount of hydrophobic
melt additive does not provide the same surface structure as that
depicted with regard to FIG. 19A. But some wrinkled structures are
seen in FIG. 19B.
[0190] FIGS. 20A-20C show examples of nonwoven webs comprising a
spray on hydrophobic additive. For example, as shown in FIG. 20A,
fibers 2091 of a nonwoven web were spray coated with glycerol
tristearate 2092 at a basis weight of about 5 gsm. It is worth
noting that the spray application appears to leave large portions
of the fibers 2091 uncovered. Regarding FIG. 20B, the fibers 2091
were spray coated with glycerol tristearate 2092 at a basis weight
of about 10 gsm. Regarding FIG. 20C, the fibers 2091 were spray
coated with glycerol tristearate 2092 at a basis weight of about 20
gsm.
Laminates Comprising Examples
[0191] Four total laminates were made, two of the laminates
comprised examples above. Rewet data was gathered for the laminates
post a cumulative liquid insult of about 21 ml of artificial
menstrual fluid.
[0192] Laminate 1 was a 25 gsm spubond bi-component fiber nonwoven.
The filaments were 2.5 denier per filament and comprised a 50/50
sheath core configuration of polyethylene/polypropylene. The lower
layer was as described with regard to Laminate 2.
[0193] Laminate 2 comprised an upper layer which was described with
regard to FIG. 12 and a lower layer comprising bi-component fibers
spunbond with topical hydrophilic surfactant. The basis weight of
the lower layer was 28 gsm, 2.8 denier per filament, 50/50
sheath/core, polyethylene/polypropylene. The web was coated with
0.4% by weight Silastol PHP26 surfactant made by Schill &
Seilacher, Germany.
[0194] Laminate 3 is the same as Laminate 4 but without the melt
additive in the upper layer. Laminate 4 comprised an upper layer
which was described with regard to FIGS. 19B and 19C and a lower
layer comprising crimped fiber spunbond with topical hydrophilic
surfactant. The lower layer comprised fibers having 2.6 denier per
filament, 70/30 side/side, polypropylene/polypropylene, using
Lyondell Basell HP561R in the first component and Lyondell Basell
HP552 R in the second component. Both components additionally
comprise 1% of TiO.sub.2 masterbatch (MBWhite009). The lower layer
was coated with 0.4% by weight Silastol PHP26 surfactant made by
Schill & Seilacher, Germany.
[0195] Laminates 2 and 4 had lower rewet scores than laminates 1
and 3. Because Laminates 2 and 4 comprised an upper nonwoven layer
which comprised a hydrophobic melt additive, it is believed that
the hydrophobic melt additive can provide laminates with a rewet
benefit.
Tests
HLB (Hydrophilic/Lipophilic Balance)
[0196] The term "HLB" or "HLB value" of a surfactant refers to the
Hydrophilic-Lipophilic Balance and is a measure of the degree to
which it is hydrophilic or lipophilic, determined by calculating
values for the different regions of the molecule. For nonionic
surfactants the HLB=20*Mb/M, where M is the molecular mass of the
whole molecule and Mb is the molecular mass of the hydrophilic
portion of the Molecule. An HLB value of 0 corresponds to a
completely lipidphilic/hydrophobic molecule, and a value of 20
corresponds to a completely hydrophilic/lipidphobic molecule. The
above represents the Griffin method of HHB calculation which is
well known in the art.
Basis Weight Test
[0197] A 9.00 cm.sup.2 large piece of nonwoven substrate, i.e., 1.0
cm wide by 9.0 cm long, is used. The sample may be cut out of a
consumer product, such as a wipe or an absorbent article or a
packaging material therefor. The sample needs to be dry and free
from other materials like glue or dust. Samples are conditioned at
23.degree. Celsius (.+-.2.degree. C.) and at a relative humidity of
about 50% (.+-.5%) for 2 hours to reach equilibrium. The weight of
the cut nonwoven substrate is measured on a scale with accuracy to
0.0001 g. The resulting mass is divided by the specimen area to
give a result in g/m.sup.2 (gsm). Repeat the same procedure for at
least 20 specimens from 20 identical consumer products or packaging
materials therefor. If the consumer product or packaging materials
therefor are large enough, more than one specimen can be obtained
from each. An example of a sample is a portion of a topsheet of an
absorbent article. If the local basis weight variation test is
done, those same samples and data are used for calculating and
reporting the average basis weight.
Fiber Diameter and Denier Test
[0198] The diameter of fibers in a sample of a nonwoven substrate
is determined by using a Scanning Electron Microscope (SEM) and
image analysis software. A magnification of 500 to 10,000 times is
chosen such that the fibers are suitably enlarged for measurement.
The samples are sputtered with gold or a palladium compound to
avoid electric charging and vibrations of the fibers in the
electron beam. A manual procedure for determining the fiber
diameters is used. Using a mouse and a cursor tool, the edge of a
randomly selected fiber is sought and then measured across its
width (i.e., perpendicular to fiber direction at that point) to the
other edge of the fiber. For non-circular fibers, the area of the
cross-section is measured using the image analysis software. The
effective diameter is then calculated by calculating the diameter
as if the found area was that of a circle. A scaled and calibrated
image analysis tool provides the scaling to get actual reading in
micrometers (.mu.m). Several fibers are thus randomly selected
across the sample of the nonwoven substrate using the SEM. At least
two specimens from the nonwoven substrate are cut and tested in
this manner. Altogether, at least 100 such measurements are made
and then all data is recorded for statistical analysis. The
recorded data is used to calculate average (mean) of the fiber
diameters, standard deviation of the fiber diameters, and median of
the fiber diameters. Another useful statistic is the calculation of
the amount of the population of fibers that is below a certain
upper limit. To determine this statistic, the software is
programmed to count how many results of the fiber diameters are
below an upper limit and that count (divided by total number of
data and multiplied by 100%) is reported in percent as percent
below the upper limit, such as percent below 1 micrometer diameter
or %-submicron, for example.
[0199] If the results are to be reported in denier, then the
following calculations are made.
Fiber Diameter in denier=Cross-sectional area(in m2)*density(in
kg/m3)*9000 m*1000 g/kg.
[0200] For round fibers, the cross-sectional area is defined by the
equation:
A=.pi.*(D/2) 2.
The density for polypropylene, for example, may be taken as 910
kg/m3.
[0201] Given the fiber diameter in denier, the physical circular
fiber diameter in meters (or micrometers) is calculated from these
relationships and vice versa. We denote the measured diameter (in
microns) of an individual circular fiber as D.
[0202] In case the fibers have non-circular cross-sections, the
measurement of the fiber diameter is determined as and set equal to
the hydraulic diameter, as discussed above.
Specific Surface Area
[0203] The specific surface area of the nonwoven substrates of the
present disclosure is determined by Krypton gas adsorption using a
Micromeritic ASAP 2420 or equivalent instrument, using the
continuous saturation vapor pressure (Po) method (according to ASTM
D-6556-10), and following the principles and calculations of
Brunauer, Emmett, and Teller, with a Kr-BET gas adsorption
technique including automatic degas and thermal correction. Note
that the specimens should not be degassed at 300 degrees Celsius as
the method recommends, but instead should be degassed at room
temperature. The specific surface area should be reported in
m.sup.2/g.
[0204] Obtaining Samples of Nonwoven Substrates
[0205] Each surface area measurement is taken from a specimen
totaling 1 g of the nonwoven substrate of the present disclosure.
In order to achieve 1 g of material, multiple specimens may be
taken from one or more absorbent articles, one or more packages, or
one or more wipes, depending on whether absorbent articles,
packages, or wipes are being tested. Wet wipe specimens will be
dried at 40 degrees C. for two hours or until liquid does not leak
out of the specimen under light pressure. The specimens are cut
from the absorbent articles, packages, or wipes (depending on
whether absorbent articles, packages, or wipes are being tested) in
areas free of, or substantially free of, adhesives using scissors.
An ultraviolet fluorescence analysis cabinet is then used on the
specimens to detect the presence of adhesives, as the adhesives
will fluoresce under this light. Other methods of detecting the
presence of adhesives may also be used. Areas of the specimens
showing the presence of adhesives are cut away from the specimens,
such that the specimens are free of the adhesives. The specimens
may now be tested using the specific surface areafibrils method
above.
Fibril Length Measurement Test
[0206] 1) Using a software program such as Image J software,
measure the number of pixels within the length of the legend on an
SEM image of a nonwoven substrate using a straight line (i.e., a
line with a length and no thickness). Record the length of the line
and the number of microns that the legend corresponds to.
[0207] 2) Pick a fibril and measure its length from its free end to
the end originating out of the fiber as best visualized. Record the
length of the line.
[0208] 3) Divide this length by the length of the legend in pixels
and then multiply by the length of the legend in microns to get the
length of the fibril in microns.
[0209] If the fibrils are long and curly, then the length of such
fibrils is taken in linear increments.
Fibril Width Measurement Test
[0210] 1) Using a software program such as Image J software,
measure the number of pixels within the length of the legend on an
SEM image of a nonwoven substrate using a straight line (i.e., a
line with a length and no thickness). Record the length of the line
and the number of microns that the legend corresponds to.
[0211] 2) Pick a fibril and measure its width as best visualized.
Record the length of the line.
[0212] 3) Divide this width by the length of the legend in pixels
and then multiply by the length of the legend in microns to get the
width of the fibril in microns.
[0213] If the fibrils are curved, then the width of such fibrils is
taken in linear increments.
Fibril Thickness Measurement Test
[0214] 1) Using a software program such as Image J software,
measure the number of pixels within the length of the legend on an
SEM image of a nonwoven substrate using a straight line (i.e., a
line with a length and no thickness). Record the length of the line
and the number of microns that the legend corresponds to.
[0215] 2) Pick a fibril and measure its thickness as best
visualized. Record the length of the line.
[0216] 3) Divide this thickness by the length of the legend in
pixels and then multiply by the length of the legend in microns to
get the thickness of the fibril in microns.
[0217] If the fibril has variable thickness across its width, then
the thickness of such fibril is taken as numeric average of
measurements across its width.
Fibril Separation Measurement Test
[0218] 1) Using a software program such as Image J software,
measure the number of pixels within the length of the legend on an
SEM image of a nonwoven substrate using a straight line (i.e., a
line with a length and no thickness). Record the length of the line
and the number of microns that the legend corresponds to.
[0219] 2) Pick a fibril and measure its distance from one of its
nearest neighbor as best visualized. Record the length of the
line.
[0220] 3) Divide this thickness by the length of the legend in
pixels and then multiply by the length of the legend in microns to
get the thickness of the fibril in microns.
[0221] Repeat steps (2) and (3) above to measure distance of the
fibril from the rest of its nearest neighbors. Take numeric average
of the measured distances to calculate average separation distance
of the fibrils.
Mass-Average Diameter
[0222] The mass-average diameter of fibers is calculated as
follows:
mass average diameter , d mass = i = 1 n ( m i d i ) i = 1 n m i =
i = 1 n ( .rho. V i d i ) i = 1 n ( .rho. V i ) = i = 1 n ( .rho.
.pi. d i 2 .differential. x 4 d i ) i = 1 n ( .rho. .pi. d i 2
.differential. x 4 ) = i = 1 n d i 3 i = 1 n d i 2 ##EQU00001##
where
[0223] fibers in the sample are assumed to be
circular/cylindrical,
[0224] d.sub.i=measured diameter of the i.sup.th fiber in the
sample,
[0225] .differential.x=infinitesimal longitudinal section of fiber
where its diameter is measured, same for all the fibers in the
sample,
[0226] m.sub.i=mass of the i.sup.th fiber in the sample,
[0227] n=number of fibers whose diameter is measured in the
sample
[0228] .rho.=density of fibers in the sample, same for all the
fibers in the sample
[0229] V.sub.i=volume of the i.sup.th fiber in the sample.
[0230] The mass-average fiber diameter should be reported in
.mu.m.
Gravimetric Weight Loss Test
[0231] The Gravimetric Weight Loss Test is used to determine the
amount of lipid ester (e.g., GTS) in a nonwoven substrate of the
present disclosure. One or more samples of the nonwoven substrate
are placed, with the narrowest sample dimension no greater than 1
mm, into acetone at a ratio of 1 g nonwoven substrate sample per
100 g of acetone using a refluxing flask system. First, the sample
is weighed before being placed into the reflux flask, and then the
mixture of the sample and the acetone is heated to 60.degree. C.
for 20 hours. The sample is then removed and air dried for 60
minutes and a final weight of the sample is determined. The
equation for calculating the weight percent lipid ester in the
sample is:
weight % lipid ester=([initial mass of the sample-final mass of the
sample]/[initial mass of the sample]).times.100%.
[0232] The dimensions and values disclosed herein are not to be
understood as being strictly limited to the exact numerical values
recited. Instead, unless otherwise specified, each such dimension
is intended to mean both the recited value and a functionally
equivalent range surrounding that value. For example, a dimension
disclosed as "40 mm" is intended to mean "about 40 mm."
[0233] Every document cited herein, including any cross referenced
or related patent or application, is hereby incorporated herein by
reference in its entirety unless expressly excluded or otherwise
limited. The citation of any document is not an admission that it
is prior art with respect to any invention disclosed or claimed
herein or that it alone, or in any combination with any other
reference or references, teaches, suggests or discloses any such
invention. Further, to the extent that any meaning or definition of
a term in this document conflicts with any meaning or definition of
the same term in a document incorporated by reference, the meaning
or definition assigned to that term in this document shall
govern.
[0234] While particular embodiments of the present invention have
been illustrated and described, it would be obvious to those
skilled in the art that various other changes and modifications can
be made without departing from the spirit and scope of the
invention. It is therefore intended to cover in the appended claims
all such changes and modifications that are within the scope of
this invention.
* * * * *