U.S. patent application number 14/765185 was filed with the patent office on 2016-03-03 for endless metal ring manufacturing method and endless metal ring resin removal device.
This patent application is currently assigned to TOYOTA JIDOSHA KABUSHIKI KAISHA. The applicant listed for this patent is TOYOTA JIDOSHA KABUSHIKI KAISHA. Invention is credited to Mitsue KOGA, Tomohiko NISHIYAMA.
Application Number | 20160059288 14/765185 |
Document ID | / |
Family ID | 51897859 |
Filed Date | 2016-03-03 |
United States Patent
Application |
20160059288 |
Kind Code |
A1 |
KOGA; Mitsue ; et
al. |
March 3, 2016 |
ENDLESS METAL RING MANUFACTURING METHOD AND ENDLESS METAL RING
RESIN REMOVAL DEVICE
Abstract
Provided is an endless metal ring manufacturing method for
manufacturing an endless metal ring by carrying out a barrel
polishing step for polishing the endless metal ring by using a
barrel of a resin material, a rolling step for rolling the endless
metal ring which was cleaned, and a nitriding step for nitriding
the endless metal ring which was rolled, wherein after the barrel
polishing step and before the rolling step, provided is a resin
removing step for removing resin that has adhered to the endless
metal ring.
Inventors: |
KOGA; Mitsue; (Toyota-shi,
JP) ; NISHIYAMA; Tomohiko; (Toyota-shi, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
TOYOTA JIDOSHA KABUSHIKI KAISHA |
Toyota-shi, Aichi |
|
JP |
|
|
Assignee: |
TOYOTA JIDOSHA KABUSHIKI
KAISHA
Toyota-shi, Aichi
JP
|
Family ID: |
51897859 |
Appl. No.: |
14/765185 |
Filed: |
May 13, 2013 |
PCT Filed: |
May 13, 2013 |
PCT NO: |
PCT/JP2013/063260 |
371 Date: |
July 31, 2015 |
Current U.S.
Class: |
72/39 ;
134/115R |
Current CPC
Class: |
F16G 5/16 20130101; C21D
8/10 20130101; B08B 3/12 20130101; C23C 8/24 20130101; B21H 1/06
20130101; C21D 1/06 20130101; C21D 1/74 20130101; B21B 45/0275
20130101; C21D 1/72 20130101; B08B 3/123 20130101; C21D 9/40
20130101; B21D 53/14 20130101 |
International
Class: |
B21B 45/02 20060101
B21B045/02; B08B 3/12 20060101 B08B003/12; B21H 1/06 20060101
B21H001/06 |
Claims
1. An endless metal ring manufacturing method including: a barrel
polishing step of polishing an endless metal ring by use of a
barrel made of resin; a rolling step of rolling the endless metal
ring having been washed; and a nitriding step of nitriding the
rolled endless metal ring, wherein the manufacturing method further
includes a resin removal step of removing the resin that has
adhered to the endless metal ring.
2. The endless metal ring manufacturing method according to claim
1, wherein the resin removal step is performed after the barrel
polishing step and before the rolling step.
3. The endless metal ring manufacturing method according to claim
1, wherein the resin removal step includes soaking the endless
metal ring in a decomposition treatment liquid to remove the
resin.
4. The endless metal ring manufacturing method according to claim
1, wherein the resin removal step includes causing a fluid to
collide against a surface of the endless metal ring to remove the
resin.
5. The endless metal ring manufacturing method according to claim
1, wherein the resin removal step includes soaking the endless
metal ring into a liquid to perform ultrasonic washing.
6. The endless metal ring manufacturing method according to claim
5, wherein the resin removal step includes rotating the endless
metal ring to wash the endless metal ring.
7. An endless metal ring resin removal device configured to wash
and hold an endless metal ring, wherein the endless metal ring
resin removal device includes: a holding tool for holding the
endless metal ring; a rotation mechanism configured to rotate the
endless metal ring in a circumferential direction of the endless
metal ring with the holding tool; a washing tank filled with a
liquid for ultrasonic washing of the endless metal ring; and an
ultrasonic wave generator for performing the ultrasonic
washing.
8. The endless metal ring resin removal device according to claim
7, wherein the ultrasonic wave generator is operated while the
rotation mechanism rotates the endless metal ring in the
circumferential direction to remove resin having adhered to a
surface of the endless metal ring.
Description
TECHNICAL FIELD
[0001] The present invention relates to a method of manufacturing
an endless metal ring for constituting a laminated ring mounted in
a CVT belt, and relates to a technique of preventing generation of
nitriding failure during manufacturing of the endless metal ring by
improving a washing process and a washing method.
BACKGROUND ART
[0002] In recent years, there have been increased vehicles provided
with a continuously variable transmission (CVT). By loading a CVT
in a vehicle, a gear ratio on an engine output side can be
controlled in a stepless manner, and fuel efficiency of a vehicle
is enhanced. This is because stepless controlling of the gear ratio
by the CVT can efficiently derive or produce engine power. The CVT
is formed by a combination of laminated endless metal belts and a
plurality of elements and the CVT is wound around an input side
pulley and an output side pulley to transmit power. The input side
pulley and the output side pulley are each provided with a pair of
sheaves which steplessly can change each groove width between each
pair of the sheaves, and thereby the input side pulley and the
output side pulley can continuously change rotation ratios, i.e.,
gear ratio, at an input side and an output side in a stepless
manner by varying the groove widths.
[0003] Because of the above-mentioned configuration of the CVT, an
endless metal belt and an element used for the CVT are required to
have highly precise dimension. Engine output is transmitted to the
endless metal belt and the element, and therefore the endless metal
belt and the element are repeatedly subject to an amount of load
corresponding to engine operation. In view of strength and life
expectancy, it has been avoided to mount the CVT in a vehicle with
a high-power engine.
[0004] Patent Document 1 discloses a technique relating to a hoop
for a CVT belt and a manufacturing method therefor. In polishing a
hoop (an endless metal ring) for a CVT belt, barrel polishing is
conducted using media made by mixing abrasive grains and a binder
on condition that the abrasive grains are oxide-type and bulk
specific gravity of the media is equal to or less than 2.0 or on
condition that the abrasive grains are carbide-type and the bulk
specific gravity of the media is equal to or less than 1.6.
Accordingly, a size of foreign matter to be driven into the hoop is
restricted.
[0005] Patent Document 2 discloses a technique relating to a
manufacturing apparatus and a manufacturing method for an endless
metal ring used for a continuously variable transmission. A
polishing device for the endless metal ring includes an end face
polishing device and an inner and outer circumferential surface
polishing device. The inner and outer circumferential surface
polishing device includes: a ring rotation roller for rotating the
endless metal ring; an outer circumferential surface polishing
roller to be brought in contact with an outer circumferential
surface of the endless metal ring; an inner circumferential surface
polishing roller to be brought in contact with an inner
circumferential surface of the endless metal ring; and a
constant-pressure applying actuator for moving the outer
circumferential surface polishing roller and an inner
circumferential side backup roller to change a clearance
therebetween and surface pressures thereof and for moving the inner
circumferential surface polishing roller and an outer
circumferential side backup roller to change a clearance
therebetween and surface pressures thereof. Owing to this
configuration, it is possible to prevent unevenness in film
pressure of nitride films to be formed on an endless metal ring
surface by nitriding.
[0006] Patent Document 3 discloses a technique relating to a
manufacturing method for a steel belt. This is a method for
manufacturing a steel belt from a sheet material made of
high-tensile steel. The method includes: a multiple deep drawing
step in which a sheet material made of high-tensile steel is
subjected to deep drawing and further to another deep drawing at
least once or more at a different drawing ratio from the former
drawing; and a cutting step in which an element processed in the
multiple deep drawing step is circumferentially cut into a
belt-like shape. According to this method, a steel belt with high
strength can be manufactured without performing welding
operation.
RELATED ART DOCUMENTS
Patent Documents
[0007] Patent Document 1: JP-A-2003-049906
[0008] Patent Document 2: JP-A-2005-155755
[0009] Patent Document 3: JP-A-2007-152358
SUMMARY OF INVENTION
Problems to be Solved by the Invention
[0010] Accompanied with progress in a CVT technology, there has
been a demand for adapting CVTs to a high-powered engine, and
enhancing life expectancy and endurance of a CVT belt has also been
expected. However, when an endless metal ring to be used for a CVT
belt is manufactured by using the technology disclosed in Patent
Documents 1 to 3, those techniques have the following problems.
[0011] For forming an endless metal ring, every one of the Patent
Documents 1 to 3 requires a cutting process and a cylindrically
shaped element has to be cut with a predetermined width to make an
endless metal ring. In cutting, burrs could be generated in any
cutting methods, and therefore it is necessary to provide a process
to remove thus generated burrs. In a method shown in the Patent
Document 2, a removal process has to be performed for the endless
metal rings one by one, requiring a long processing time, which
could induce a cost problem. Accordingly, the present applicant
employed a method of removing burrs from an endless metal ring by
barrel polishing as indicated in the Patent Documents 1 and 3.
However, it is confirmed that nitriding failure occurs with a
certain probability when the endless metal ring is subjected to
surface treatment by rolling and nitriding after the barrel
polishing. Due to this nitriding failure of the endless metal ring,
it is assumed that life expectancy and endurance of a CVT belt
lower.
[0012] The present invention has been made in view of the
circumstances to solve the above problem and has a purpose to
provide an endless metal ring manufacturing method and an endless
metal ring resin removal device which are capable of lowering a
rate of nitriding failure of the endless metal ring.
Means of Solving the Problems
[0013] To achieve the above purpose, an endless metal ring
manufacturing method according to one aspect of the present
invention has the following features.
[0014] (1) One aspect of the invention provides an endless metal
ring manufacturing method including: a barrel polishing step of
polishing an endless metal ring by use of a barrel made of resin; a
rolling step of rolling the endless metal ring having been washed;
and a nitriding step of nitriding the rolled endless metal ring,
wherein the manufacturing method further includes a resin removal
step of removing the resin that has adhered to the endless metal
ring.
[0015] According to the aspect described in the above (1), it is
possible to lower the rate of nitriding failure of the endless
metal ring. The applicant made a research with various washing
conditions for the endless metal ring in nitriding the endless
metal ring. As a result of the research, it is confirmed that there
is a problem in removing the media used for barrel polishing. To be
specific, the media is made by mixing resin material and polishing
material, and the applicant has confirmed from the research result
that the nitriding failure occurs because the nitriding is
performed in a state that the resin material stays on a metal
surface. The resin adhered to the metal surface obstructs nitrogen
molecules from entering into the metal from the metal surface in
the nitriding step, resulting in thinning a thickness of a nitrogen
diffusion layer, so that the metal could be formed with portions
with low surface strength in a mottled appearance. This is the
nitriding failure to cause a product failure. Accordingly, by
removing this resin extraneous matter, it is possible to reduce the
nitriding failure of the endless metal ring.
[0016] (2) In the endless metal ring manufacturing method according
to (1), preferably, the resin removal step is performed after the
barrel polishing step and before the rolling step.
[0017] It is confirmed that it is effective to remove the resin
extraneous matter adhered to the surface of the endless metal ring
before the rolling step in order to lower the nitriding failure of
the endless metal ring. If the resin remains to adhere to the
surface of the endless metal ring before the rolling step, the
resin could be fixed or stick to the surface of the endless metal
ring in the rolling step, and exfoliation of the resin becomes
extremely difficult even if the endless metal ring surface is
thoroughly washed after the rolling step. Therefore, by removing
the resin before the rolling step, fixation of the resin to the
endless metal ring surface is prevented, and thereby the nitriding
failure can be prevented.
[0018] (3) In the endless metal ring manufacturing method according
to (1) or (2), preferably, the resin removal step includes soaking
the endless metal ring in a decomposition treatment liquid to
remove the resin.
[0019] According to the aspect described in the above (3), the
resin adhered to the endless metal ring is fused to be removed by
use of the decomposition treatment liquid and the rolling step is
subsequently performed, so that the resin is prevented from being
fixed to the endless metal ring surface, resulting in prevention of
the nitriding failure.
[0020] (4) In the endless metal ring manufacturing method according
to (1) or (2), preferably, the resin removal step includes causing
a fluid to collide against a surface of the endless metal ring to
remove the resin.
[0021] According to the aspect described in the above (4), a fluid
is caused to collide against the endless metal ring surface by a
large flow rate washing, for example, to remove the resin, and the
rolling step is subsequently performed, so that the resin is
prevented from being fixed to the endless metal ring surface,
resulting in prevention of the nitriding failure.
[0022] (5) In the endless metal ring manufacturing method according
to (1) or (2), preferably, the resin removal step includes soaking
the endless metal ring into a liquid to perform ultrasonic
washing.
[0023] According to the aspect described in the above (5), the
endless metal ring surface is subjected to the ultrasonic washing
to remove the resin and the rolling step is subsequently performed,
so that the resin is prevented from being fixed to the endless
metal ring surface, resulting in prevention of the nitriding
failure.
[0024] (6) In the endless metal ring manufacturing method according
to (5), preferably, the resin removal step includes rotating the
endless metal ring to wash the endless metal ring.
[0025] According to the aspect described in the above (6), the
endless metal ring is rotated during the ultrasonic washing in
order to change a location of ultrasonic wave irradiated on the
endless metal ring surface, and as a result, a location of
cavitation generated on the endless metal ring surface is changed.
Accordingly, it is possible to facilitate exfoliation of the resin
from the endless metal ring surface. In this manner, it is possible
to prevent the resin from being fixed to the endless metal ring
surface, resulting in prevention of the nitriding failure.
[0026] Further, to achieve the above purpose, an endless metal ring
resin removal device according to another aspect of the present
invention has the following features.
[0027] (7) Another aspect of the present invention provides an
endless metal ring resin removal device configured to wash and hold
the endless metal ring, wherein the endless metal ring resin
removal device includes: a holding tool for holding the endless
metal ring; a rotation mechanism configured to rotate the endless
metal ring in a circumferential direction of the endless metal ring
with the holding tool; a washing tank filled with a liquid for
ultrasonic washing of the endless metal ring; and an ultrasonic
wave generator for performing the ultrasonic washing.
[0028] (8) In the endless metal ring resin removal device according
to (7), preferably, the ultrasonic washing device is operated while
the rotation mechanism rotates the endless metal ring in the
circumferential direction to remove resin having adhered to a
surface of the endless metal ring.
[0029] According to the aspects described in the above (7) and (8),
the endless metal ring is washed while the ring is rotated, so that
the resin adhered to the endless metal ring surface can be
effectively removed.
BRIEF DESCRIPTION OF THE DRAWINGS
[0030] FIG. 1 is a perspective view of a CVT ring in a first
embodiment;
[0031] FIG. 2 is an exploded perspective view of the CVT ring in
the first embodiment;
[0032] FIG. 3 is an explanatory view explaining a manufacturing
process of an endless metal ring in the first embodiment, in which
(a) is a strip cutting step, (b) is a strip welding step, (c) is a
first solutionizing step, (d) is a cylindrical body cutting step,
(e) is a barrel polishing step, (f) is a washing step, (g) is a
rolling step, (h) is a second solutionizing step, (i) is a
circumferential length adjusting step, (j) is an aging and
nitriding step, and (k) is a laminating step;
[0033] FIG. 4 is a diagram showing a carbo-nitriding mechanism in
the first embodiment, in which (a) is an ammonia gas charging step,
(b) is a nitrogen adsorption step, (c) is an ammonia dissolution
step, (d) is a nitrogen infiltration step, and (e) is a nitrogen
diffusion step;
[0034] FIG. 5 is a schematic view of a washing device in the first
embodiment;
[0035] FIG. 6 is a perspective view of a washing jig in the first
embodiment;
[0036] FIG. 7 is a diagram showing a first model of nitriding
failure for explanation;
[0037] FIG. 8 is a diagram showing a second model of nitriding
failure for explanation;
[0038] FIG. 9 is a schematic view of a configuration of a six-tank
washing for explanation;
[0039] FIG. 10 is a graph showing results of resin removal tests
conducted by the applicant;
[0040] FIG. 11 is a perspective view of a washing jig for
explanation;
[0041] FIG. 12 is a schematic plan view of a washing device in a
second embodiment;
[0042] FIG. 13 is a schematic perspective view of the washing
device in the second embodiment;
[0043] FIG. 14 is a perspective view showing an image of washing an
endless metal ring in a third embodiment; and
[0044] FIG. 15 is a table showing washing results of the endless
metal ring in the first embodiment.
MODE FOR CARRYING OUT THE INVENTION
[0045] A first embodiment of the present invention is now explained
referring to the accompanying drawings.
[0046] FIG. 1 is a perspective view of a CVT ring 100 in the first
embodiment. FIG. 2 is an exploded perspective view of the CVT ring
100. The CVT ring 100 is formed of a laminated ring 104 and a
plurality of elements 102 stacked in a thickness direction thereof.
The laminated ring 104 is formed by laminating nine layers of
endless metal rings 110, each layer having the different
circumferential length. In FIG. 2, the endless metal rings 110 are
omitted partly and illustrated by only three layers thereof for
explanation. The adjacent endless metal rings 110 are each designed
to have different inner diameters by the thickness of each endless
metal ring 110. Accordingly, the overlapped endless metal rings 110
are laminated with no clearance. The elements 102 are each made of
plate-like metal material formed at both ends with grooves 116, and
the laminated rings 104 are inserted in these grooves 116 as shown
in FIG. 2.
[0047] FIG. 3 is a schematic view for explaining a manufacturing
process for the endless metal ring 110. In FIG. 3, (a) is a strip
cutting step pr1, (b) is a strip welding step pr2, (c) is a first
solutionizing step pr3, (d) is a cylindrical body cutting step pr4,
(e) is a barrel polishing step pr5, (f) is a resin removal step
pr6, (g) is a rolling step pr7, (h) is a second solutionizing step
pr8, (i) is a circumferential length adjusting step pr9, (j) is an
aging-nitriding step pr10, and (k) is a laminating step pr11. For
manufacturing the endless metal ring 110, as shown in FIG. 3(a), a
strip plate P2 is cut out from a material roll P1 to a specified
length in the strip cutting step pr1. High-tensile steel such as
maraging steel is used for the material roll P1. This material roll
P1 is uncoiled to be flattened, and then cut with a predetermined
width to form the strip plate P2. The width of the strip plate P2
is determined in consideration of being subject to subsequent
process such as the rolling step pr7.
[0048] Then, in the strip welding step pr2 shown in FIG. 3(b), a
cylindrical body C1 formed by roll-bending the strip plate P2 is
welded by abutting its end faces to form the cylindrical body C1 of
cylindrical shape. In the first solutionizing step pr3 shown in
FIG. 3(c), the cylindrical body C1 is solutionized under nitride
atmosphere. By this solutionizing, structure anisotropy of the
welded portion is relaxed. In the cylindrical body cutting step pr4
shown in FIG. 3(d), the cylindrical body C1 is cut into round
slices each having a predetermined width to make a material ring
C2. Since burrs are generated on end faces of the material ring C2
in the process of cutting the cylindrical body C2 into round
slices, the barrel polishing step pr5 shown in FIG. 3(e) is
performed to remove the burrs generated on the end faces of the
material ring C2. What is used in the barrel polishing step pr5 is
resin media in which alumina abrasive grain with a prescribed grain
diameter is mixed with a resin-based binder.
[0049] Then, in the resin removal step pr6 shown in FIG. 3(f), the
material ring C2 after barrel polishing is cleaned. This resin
removal step pr6 will be explained later. In the rolling step pr7
shown in FIG. 3(g), a thickness of the material ring C2 is
adjusted. Even though the material roll P1 is provided to have a
thickness as uniform as possible, the rolling step pr7 of rolling
the material ring C2 by use of rolling rollers R1 is performed in
order to correct a deviation in the thickness direction, thickness
variation and minute deformation in the strip welding step pr2 and
the cylindrical body cutting step pr4, and influence in the barrel
polishing step pr5. A rolled ring C3 formed in this step has a
thickness set assuming that a circumferential length is to be
elongated in the subsequent circumferential length adjusting step
pr9.
[0050] In the second solutionizing step pr8 indicated in FIG. 3(h),
the rolled ring C3 is heated in a furnace at a predetermined
temperature for a predetermined period of time. This solutionizing
process is aimed for homogenization. In the circumferential length
adjusting step pr9 shown in FIG. 3(i), each of the rolled rings C3
is adjusted to a required circumferential length, and then the
endless metal ring 110 is formed. Then, a carbo-nitriding treatment
is performed in the aging-nitriding step pr10 indicated in FIG.
3(j). FIG. 4 is a diagram showing a carbo-nitriding mechanism. In
FIG. 4, (a) is an ammonia gas charging step, (b) is a nitrogen
adsorption step, (c) is an ammonia dissolution step, (d) is a
nitrogen infiltration step, and (e) is a nitrogen diffusion step.
The endless metal ring 110 set in a not-shown pressure-reduced
furnace is placed under ammonia gas atmosphere in "the ammonia gas
charging step" in FIG. 4(a).
[0051] When the temperature in the furnace is raised after that,
ammonia molecules adhere to a surface of the endless metal ring 110
in "the nitrogen adsorption step" in FIG. 4(b). Then, as shown in
"the nitrogen dissolution step" in FIG. 4(c), the ammonia molecules
dissolved on the surface of the endless metal ring 110 are
decomposed to nitrogen and hydrogen. The nitrogen reacts with
minute particles in the endless metal ring 110 and then enters into
the endless metal ring 110 from its surface as indicated in "the
nitrogen infiltration step" in FIG. 4(d). This reaction occurs
because of the influence of components that have high affinity with
nitrogen among elements included in the steel material. The
nitrogen is diffused mainly from a grain boundary of the endless
metal ring 110 in "the nitrogen diffusion step" in FIG. 4(e), and
as a result, the effect of hardening the surface of the endless
metal ring 110 is obtained.
[0052] Thus formulated endless metal rings 110 are laminated in the
laminating step pr11 shown in FIG. 3(k). In the first embodiment,
the endless metal rings 110 are laminated in nine layers to form
the laminated ring 104. The thus laminated ring 104 is utilized to
form the CVT ring 100 by combination with the elements 102 as shown
in FIG. 2.
[0053] FIG. 5 is a schematic view showing a washing device 10. FIG.
6 is a perspective view showing a washing jig 20. The washing
device 10 used in the resin removal step pr6 is configured such
that the washing jig 20 shown in FIG. 6 is held in a rotatable
manner in a washing tank 40 filled with water for washing, and an
ultrasonic wave generator 30 is placed below the washing jig 20.
The washing jig 20 is a basket made of thin wire to hold the
material rings C2 as shown in FIG. 6, and the washing jig 20 is
covered with an unillustrated lid and fixed in the washing device
10. The washing jig 20 provided in the washing device 10 is
provided with a not-shown rotation mechanism so that the jig 20
rotates about an axis of the material ring C2. The ultrasonic wave
generator 30 is placed to generate ultrasonic wave from below the
washing jig 20. In this manner, the material ring C2 after the
barrel polishing step pr5 is washed.
[0054] According to the above configuration of the manufacturing
method of the endless metal ring 110 in the first embodiment, the
following operations and effects are obtained.
[0055] The method of manufacturing the endless metal ring 110 in
the first embodiment is the method for manufacturing the endless
metal ring 110 through the process of: the barrel polishing step
pr5 of polishing the material ring C2 (the endless metal ring 110)
by use of a barrel made of resin; the rolling step pr7 of rolling
the washed material ring C2 (the endless metal ring 110); and the
nitriding step pr10 of nitriding the rolled ring C3 (the endless
metal ring 110) which has been rolled. The method includes the
resin removal step pr6 of removing the resin adhered to the
material ring C2 (the endless metal ring 110) after the barrel
polishing step pr5 and before the rolling step pr7.
[0056] For manufacturing the endless metal ring 110, the applicant
examined the surface of the endless metal ring 110 after the
nitriding step pr10 and confirmed that the surface is shaded or
mottled with black speckles or specks and white speckles and that
thus mottled portion is low in its hardness compared to other
portions on the surface. Generally, nitrogen are diffused into the
grain boundary from a surface layer of the endless metal ring 110
by "the nitrogen diffusion step" shown in FIG. 4(e) so that a
nitride layer r2 is formed. As a result, the surface of the endless
metal ring 110 is hardened. However, the mottled portion with the
black and white speckles has low hardness and thus the nitride
failure is conceived to have occurred. This failure in the surface
hardness leads to product defect in the endless metal ring 110,
lowering product yield. When the surface of the endless metal ring
110 is processed with shot peening as shown in FIG. 7(g) and FIG.
8(f) which will be mentioned later, the surface hardness failure
further cause surface asperities.
[0057] Conventionally, some measures have been taken, for example,
a manufacturing process is conducted in a clean room and humidity
control is performed for static electricity prevention in order to
solve the above problem. These measures are intended to prevent
adhesion of dirt or wastes generated in the manufacturing process
as much as possible since the nitriding failure has been considered
to result from adhesion of the dirt or wastes to the surface of the
endless metal ring 110 due to static electricity.
[0058] However, even if the above measures are taken and the ring
is carefully washed in the washing process corresponding to the
resin removal step pr6, the nitriding failure has occurred at a
certain ratio. FIG. 9 is a schematic view showing a configuration
of six-tank washing for comparison. Conventionally, the endless
metal ring 110 was carefully washed through the six-tank washing
process as shown in FIG. 9 after the barrel polishing step pr5.
Through the first to fourth tanks, the endless metal ring 110 is
washed by the combination of ultrasonic washing using pure water
and oscillation. The endless metal ring 110 is then washed with
pure water in the fifth tank and applied with spin-dry to spin off
drops of water by rotating the ring 110 at high speed in the sixth
tank. Even by this washing method, it is hard to prevent the
nitriding failure. Accordingly, the present applicant has analyzed
foreign matters detected after washing by the six-tank washing and
noticed the fact that a large number of resin components are
detected from the foreign matters.
[0059] This resin component is considered to be mainly derived from
the media used in the barrel polishing step pr5. Accordingly, in
the first embodiment, the resin removal step pr6 is performed
before the rolling step pr7 to wash the endless metal ring 110 by
use of the washing device 10 and the washing jig 20 shown in FIGS.
5 and 6. As a result, it is confirmed that the resin can be
preferably removed.
[0060] FIG. 7 is a diagram showing a first model having the
nitriding failure caused therein for explanation. In FIG. 7(a),
washing failure causes emulsification of resin wastes, rolling oil,
and compounds which are mixed with dust generated during the
process and adhere to the surface of the endless metal ring 110. It
is expected that this emulsified substance b1 turns into a
carbon-based high polymer b2 in (b) indicating a timing of the
first solutionizing step pr3 and this polymer b2 sticks to the
surface of the endless metal ring 110. Then, the carbon-based high
polymer b2 turns into a carbide substance b3 in an aging process
(d). This carbide substance b3 obstructs creation of an iron oxide
layer r1 which is to be formed on the surface of the endless metal
ring 110 in an oxidizing process (d). Also when a nitride layer r2
is formed in a nitriding process (e), the carbide substance b3
partly obstructs creation of the nitride layer r2 by interrupting
carbo-nitriding indicated in FIG. 4(d). This obstruction is
considered to cause the black speckles on the endless metal ring
110 surface.
[0061] At that time, if the carbide substance b3 is peeled off due
to some reasons as indicated in (f), it may lead to generation of
the white speckles. The endless metal ring 110 formed in this
manner could have the low surface hardness due to the nitriding
failure in portions of the black speckles and the white speckles.
Further, in a case that a shot peening process is performed before
the laminating process pr11 thereafter, there are created partial
unevenness as indicated in (g), which is not preferable.
[0062] FIG. 8 is a diagram showing a second model having the
nitriding failure occurred therein. Unlike the first model of the
nitriding failure, no obvious reason to cause the failure is found,
but an oxide layer r3 of such as titanium is formed on the endless
metal ring 110 surface in a solutionizing process (b), and this
oxide layer has an influence of obstructing creation of the iron
oxide layer r1 as indicated in the following (d). As a result, the
nitriding failure indicated in (e) is considered to occur. Further,
when the shot peening process is performed as indicated in (f),
partial unevenness could be generated, which is not preferable.
[0063] FIG. 10 is a graph showing results of resin removal tests in
which the washing device of the first embodiment is used under
different washing conditions. The applicant has confirmed from the
resin removal tests that the washing device 10 can be applied to
any one or the whole of the first to fourth tanks of the washing
tank shown in FIG. 9, and that the efficiency in resin removal
changes depending on the washing conditions. The graph of FIG. 10
is indicated with its vertical axis indicating a partial
correlation coefficient and its horizontal axis indicating test
conditions. The test results are obtained by further performing
ultrasonic washing with carbon tetrachloride solution, filtrating
the solution with a filter, and then evaluating a resin waste
amount in the filter after washing so that the grading is made.
[0064] "Ultrasonic power" is an element indicating an influence of
an ultrasonic power output w/L, and "Work set jig" is an element
indicating the influence of using jigs different in shape,
material, or the like. From the test results, it is confirmed that
increasing energy per unit area from 8 w/L to 24 w/L, could improve
detergency by three ranks.
[0065] FIG. 11 shows a jig which has been conventionally used. A
jig 21 made of resin is configured with a thick frame with high
rigidity compared to the washing jig 20. Both the jig 21 and the
washing jig 20 are capable of accommodating the same number of the
endless metal rings 110. As for "Work set jig," tests are made with
the jig 21 shown in FIG. 11, the washing jig 20, and without using
a jig. What is the most effective in washing is the case when the
ring is washed without using any jig, and the washing effect
gradually becomes low in the order of using the washing jig 20 and
using the jig 21. This is because the high washing effect is
obtained when there is no jig which interrupts the ultrasonic
wave.
[0066] "Rotation" is an element indicating an influence of
performing or not performing rotation by the washing jig 20.
Compared to not performing the rotation, washing with rotation
exhibits higher washing effect by about four ranks. "Air blow" is
an element indicating an influence of air blowing on the surface of
the endless metal ring 110 after the ultrasonic washing for
comparison. It is confirmed that resin on the endless metal ring
110 surface is not removed by the air blow. "Number of work sets"
is an element indicating an influence of changing the number of the
endless metal rings 110 accommodated in the washing jig 20. It is
confirmed that the washing effect is not largely influenced by the
number of the work sets.
[0067] "Temperature" is an element indicating an influence of the
temperature of a solution used for washing the endless metal ring
110. As a result of tests made by changing the temperature from the
room temperature in several different patterns, it is confirmed
that the washing effect is improved by raising the temperature to a
certain degree. "Solution" is an element indicating an influence of
types of the solution filled in the washing tank 40 of the washing
device 10. As the solution, pure water and hydrocarbon-related
solution are used for the tests. These tests revealed that,
compared to the pure water, the hydrocarbon-related solution hardly
makes the washing effects, and the hydrocarbon-related solution is
less effective by five ranks compared to the pure water.
[0068] As results from this research, as shown in FIG. 10, the
elements of "Ultrasonic power," "Work set jig," "Rotation,"
"Temperature," and "Solution" have the partial correlation
coefficient of more than 0.4, and it is concluded that they are
effective. From these results, in the first embodiment, the washing
jig 20 shown in FIG. 6 is employed as the work set jig to be
rotated as shown in FIG. 4 so as to increase the ultrasonic power,
and water is employed as the solution so that the washing effect of
washing the resin dusts is further increased. Namely, the washing
device 10 is thus arranged so that the resin dusts are further
effectively removed from the endless metal ring 110 surface,
realizing decrease in the nitriding failure of the endless metal
ring 110. The applicant has confirmed that by embodying the
invention as the first embodiment, a nitriding failure ratio of the
endless metal ring 100 is reduced to almost zero while the ratio is
used to be about 40%. Consequently, the present invention can
attribute to cost reduction in producing the endless metal ring
110.
[0069] FIG. 15 is a table showing that a rank of the washing effect
varies in accordance with test conditions. In a row indicated with
"Comparative example," the jig 21 shown in FIG. 11 is used and a
result of the six-tank washing illustrated in FIG. 9 in which the
washing is performed without rotating the jig 21 is indicated. In
the table, the steps in the fifth and sixth tanks are omitted. A
row indicated as "Test 1" shows the result of washing performed by
the washing jig 20 shown in FIG. 6 while the jig 20 is rotated to
wash the ring through the first to third tanks. A row indicated as
"Test 2" shows the result of washing performed on the same
condition with "Test 1" while the jig 20 is used through the first
to fourth tanks. A row indicated as "Test 3" shows the result of
washing performed by increasing the output from the ultrasonic wave
generator 30 on the same condition with "Test 1." A row indicated
as "Test 4" shows the result of washing performed by increasing the
output from the ultrasonic wave generator 30 on the same condition
with "Test 2." Every one of the tests are made with one hundred
material rings C2 and washing with pure water to compare the
washing effect.
[0070] According to the table, under the condition indicated in
"Comparative example," the washing effect is graded low as ninth
with regard to the resin dust. On the other hand, the washing
result of "Test 1" is graded as a rank 4, "Test 2" is graded as 2,
"Test 3" is graded as 1, and "Test 4" is graded as 1. The rank 1 of
the washing effect means that no nitriding failure is confirmed in
the endless metal ring 110. In other words, the washing effect is
improved by the washing method for the endless metal ring 110 (the
material ring C2) according to the first embodiment in which the
output of the ultrasonic wave generator 30 is increased from 8 w/L
to 24 w/l, and the ring C2 is rotated and washed by the washing jig
20. As a result, the number of the washing tanks 40 can be reduced.
Accordingly, a lead time for manufacturing the endless metal ring
110 is shortened, thus reducing the manufacturing cost. Further, it
is possible to contribute to extending the life expectancy of the
CVT ring 100.
[0071] Next, a second embodiment of the present invention is
explained with reference to the accompanying drawings. A
configuration is similar to the first embodiment except a resin
removal step pr6, and therefore only the different features are
explained.
[0072] FIG. 12 is a schematic plan view of a washing device
according to the second embodiment. FIG. 13 is a schematic
perspective view of the washing device. In the second embodiment, a
carbon tetrachloride solution is used for washing the endless metal
ring 110 (the material ring C2). The washing tank 40 shown in FIG.
12 as a first tank is filled with the carbon tetrachloride solution
to wash the endless metal ring 110 (the material ring C2). In
washing, the material ring C2 may be held by the washing jig 20 and
rotated as necessary. Further, the ultrasonic wave generator 30 is
also provided. Another washing tank 40 as a second tank shown in
FIG. 12 is filled with pure water and the ultrasonic washing is
performed by the ultrasonic wave generator 30 as similar to the
first tank. The ultrasonic washing is thus performed by the
ultrasonic wave generator 30 while the material ring C2 is soaked
in a decomposition-removal liquid in order to dissolve and remove
the resin adhered to the endless metal ring 110 surface. As long as
the solution used for washing is the one capable of dissolving and
removing the resin, the solution is not limited to the carbon
tetrachloride solution and other decomposition-removal liquid
capable of dissolving and removing the resin may be used.
[0073] Next, a third embodiment of the present invention is
explained with reference to the accompanying drawings. A
configuration is similar to the first embodiment except a resin
removal step pr6, and therefore only the different features are
explained.
[0074] FIG. 14 is a perspective view showing a washing image of an
endless metal ring in the third embodiment. The third embodiment is
configured such that the surface of the endless metal ring 110 (the
material ring C2) is washed away by high-pressure washing. An inner
surface washing nozzle 70 is provided inside the washing tank 40 of
the washing device 10 and an outer surface washing nozzle 71 is
provided to be directed to an outer circumferential surface so that
the endless metal ring 110 surface is washed with the pressure of
at least about some tens of MPa. As an alternative, the surface of
the material ring C2 may be washed by employing the method of
washing at large flow rate with the pressure of about some tens to
some hundreds of L/min. In this case, the washing tank 40 does not
have to be provided with the ultrasonic wave generator 30, and it
is possible to remove the resin adhered to the surface of the
material ring C2 by washing outer and inner circumferential
surfaces of the endless metal ring 110 with the washing liquid such
as pure water sprayed from the nozzles.
[0075] From the above mentioned test results, it is confirmed that
washing with the washing liquid at high temperature is also
effective, and therefore, it is possible to remove the resin from
the endless material ring C2 surface by steam-washing the material
ring C2 surface by the same nozzles. Thus, by washing the material
ring C2 surface with a fluid, it is possible in the resin removal
step pr6 to wash away particles of the resin media that adhered to
the material ring C2 surface in the barrel polishing step pr5.
[0076] According to the washing device 10 and the washing method of
the second or the third embodiment, the same effect as the first
embodiment can be obtained, and it is possible to reduce the
nitriding failure of the endless metal ring 110 as a result.
Specifically, providing the resin removal step pr6 for removing the
resin dust which is considered to adhere to the endless metal ring
110 surface can realize great reduction in the nitriding failure of
the endless metal ring 110.
[0077] The present invention is illustrated in accordance with the
embodiments, but the invention is not limited to the above
mentioned embodiments and may be appropriately modified with its
part of configuration without departing from the scope of the
invention. For example, the manufacturing steps of the endless
metal ring 110 are illustrated in FIG. 3, but the steps may be
increased or reduced and may be replaced with its order as long as
the resin removal step pr6 is performed after the barrel polishing
step pr5, which is performed after the cylindrical body cutting
step pr4 for cutting the cylindrical body C1, and before the second
solutionizing step pr8. As mentioned above, it is preferable that
the resin removal step pr6 is performed before the rolling step
pr7, but even in a case that the resin removal step pr6 is
performed after the rolling step pr7, for example, the resin
removal effect can be expected to a certain degree.
[0078] The shape of the CVT ring 100 is also only an example for
illustration, and the present invention may be applied to a CVT
ring in which a shape of the element 102 is different from that of
the present invention as corresponding to the laminating number of
the laminated rings 104. Further, the shape and others of the
washing jig 20 may also be modified. In modifying, it is preferable
to configure the flame of the washing jig 20 as thin to reduce a
portion of the flame that covers the material ring C2 to the most
extent so that the ultrasonic wave generated from the ultrasonic
wave generator 30 is not interrupted.
REFERENCE SIGNS LIST
[0079] 10 Washing device
[0080] 20 Washing jig
[0081] 21 Jig
[0082] 30 Ultrasonic wave generator
[0083] 40 Washing tank
[0084] 100 CVT ring
[0085] 102 Element
[0086] 104 Laminated ring
[0087] 110 Endless metal ring
[0088] 116 Groove
* * * * *