U.S. patent application number 14/354022 was filed with the patent office on 2015-10-15 for gas barrier film.
This patent application is currently assigned to TORAY INDUSTRIES, INC.. The applicant listed for this patent is TORAY INDUSTRIES, INC.. Invention is credited to Motoyuki Suzuki, Yusuke Tsukamura, Hiroyuki Uebayashi, Minoru Yoshida.
Application Number | 20150291753 14/354022 |
Document ID | / |
Family ID | 48167561 |
Filed Date | 2015-10-15 |
United States Patent
Application |
20150291753 |
Kind Code |
A1 |
Tsukamura; Yusuke ; et
al. |
October 15, 2015 |
GAS BARRIER FILM
Abstract
[Problem] The purpose of the present invention is to provide a
gas barrier film having high gas barrier performance and excellent
repeated reproducibility of gas barrier performance. [Solution] A
gas barrier film comprising a polymer base, an undercoat layer that
contains, as the main component, an acrylic resin having at least
one side chain selected from the group consisting of the side
chains (I) to (III) mentioned below, and an inorganic layer,
wherein the undercoat layer and the inorganic layer are arranged in
this order on at least one surface of the polymer base in such a
manner that the undercoat layer and the inorganic layer are in
contact with each other: (I) a side chain having an acrylic polymer
skeleton; (II) a side chain having a dimethylsioxane skeleton; and
(III) a side chain having a skeleton containing a fluorine
atom.
Inventors: |
Tsukamura; Yusuke;
(Otsu-shi, JP) ; Uebayashi; Hiroyuki; (Otsu-shi,
JP) ; Yoshida; Minoru; (Otsu-shi, JP) ;
Suzuki; Motoyuki; (Otsu-shi, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
TORAY INDUSTRIES, INC. |
TOKYO |
|
JP |
|
|
Assignee: |
TORAY INDUSTRIES, INC.
TOKYO
JP
|
Family ID: |
48167561 |
Appl. No.: |
14/354022 |
Filed: |
September 28, 2012 |
PCT Filed: |
September 28, 2012 |
PCT NO: |
PCT/JP2012/075077 |
371 Date: |
April 24, 2014 |
Current U.S.
Class: |
428/141 ;
204/192.1; 428/336; 428/447; 428/522; 428/523 |
Current CPC
Class: |
C08J 7/0423 20200101;
C08F 220/1811 20200201; C08J 2433/10 20130101; C08F 259/08
20130101; C23C 14/081 20130101; C08F 265/06 20130101; C23C 14/10
20130101; C08F 220/14 20130101; C23C 14/0629 20130101; C08F 230/08
20130101; C08F 259/08 20130101; C08F 259/08 20130101; C08F 265/06
20130101; C08F 290/068 20130101; C08F 265/06 20130101; C08F 265/06
20130101; C23C 14/3457 20130101; C23C 16/50 20130101; C08J 2433/00
20130101; C08F 290/068 20130101; C08F 220/14 20130101; C23C 14/086
20130101; B65D 65/40 20130101; C08J 2433/16 20130101; C08J 2367/02
20130101; C08F 220/20 20130101; C08F 220/06 20130101; C08F 220/18
20130101; C08F 220/06 20130101; C08F 220/06 20130101; C08F 220/20
20130101; C08F 259/08 20130101; C08L 33/066 20130101; C08J 2433/12
20130101; C08F 290/068 20130101; C08F 290/068 20130101; C08F
220/1811 20200201; C08J 2443/04 20130101; C23C 16/40 20130101; C08F
220/06 20130101; C08F 220/20 20130101; C08F 220/20 20130101; C08F
220/18 20130101; C08F 220/18 20130101; C08F 220/06 20130101; C08F
220/20 20130101; C08F 220/20 20130101; C08F 220/06 20130101 |
International
Class: |
C08J 7/04 20060101
C08J007/04; C23C 14/08 20060101 C23C014/08; C23C 14/10 20060101
C23C014/10 |
Foreign Application Data
Date |
Code |
Application Number |
Oct 28, 2011 |
JP |
2011-236951 |
Aug 8, 2012 |
JP |
2012-175608 |
Sep 19, 2012 |
JP |
2012-205385 |
Claims
1. A polymer base laminated, at least on one surface thereof, with
an undercoat layer containing, as the primary component, an acrylic
resin having at least one side chain selected from the group
consisting of (I) to (III) given below and an inorganic layer
stacked in contact with each other in this order: (I) a side chain
having an acrylic polymer skeleton, (II) a side chain having a
dimethyl siloxane skeleton, (III) a side chain having a fluorine
atom-containing skeleton.
2. Gas barrier film as described in claim 1, wherein the side chain
contains at least (II) and/or (III) given above.
3. Gas barrier film as described in claim 1, wherein the acrylic
resin has a structure produced by copolymerizing an acrylic monomer
and at least one macromonomer selected from the group consisting of
(i) to (iii) given below: (i) a macromonomer including an acrylic
polymer having a radically polymerizable group at an end thereof,
(ii) a macromonomer including a dimethyl siloxane skeleton-based
polymer having a radically polymerizable group at an end thereof,
(iii) a macromonomer including a fluorine atom-containing polymer
having a radically polymerizable group at an end thereof.
4. Gas barrier film as described in claim 3, wherein the
macromonomer contains at least (ii) or (iii) given above.
5. Gas barrier film as described in claim 1, wherein the undercoat
layer has a surface free energy of 10 to 45 mN/m.
6. Gas barrier film as described in claim 1, wherein the undercoat
layer has a surface free energy of 10 to 25 mN/m.
7. Gas barrier film as described in claim 3, wherein the acrylic
resin is one produced by copolymerizing 100 parts by mass of the
acrylic monomer having a composition as described below with 3 to 8
parts by mass of a macromonomer; 1 to 8 mass % of methacrylic acid,
5 to 16 mass % of 2-hydroxyethyl methacrylate, and 76 to 94 mass %
of methyl methacrylate and/or dicyclopentanyl methacrylate.
8. Gas barrier film as described in claim 1, wherein the inorganic
layer has a thickness of 10 to 1,000 nm and comprises a zinc
compound and a silicon oxide.
9. Gas barrier film as described in claim 8, wherein the inorganic
layer is either a layer [Bl] or a layer [B2] as specified below:
layer [Bl]: a layer of a phase in which zinc oxide, silicon
dioxide, and aluminum oxide coexist, layer [B2]: a layer of a phase
in which zinc sulfide and silicon dioxide coexist.
10. Gas barrier film as described in claim 9, wherein the inorganic
layer is a layer [Bl] as specified above and the layer [Bl] has a,
zinc (Zn) atom concentration of 20 to 40 atom %, a silicon (Si)
atom concentration of 5 to 20 atom %, an aluminum (A1) atom
concentration of 0.5 to 5 atom %, and an oxygen (O) atom
concentration of 35 to 70 atom % as determined by ICP emission
spectroscopy analysis.
11. Gas barrier film as described in claim 9, wherein the inorganic
layer is a layer [B2] as specified above and the layer [B2] has a
composition in which zinc sulfide accounts for a mole fraction of
0.7 to 0.9 of the total quantity of zinc sulfide and silicon
dioxide.
12. Gas barrier film as described in claim 1, wherein the inorganic
layer has a surface roughness Ra of 2 nm or less.
13. A production method for gas barrier film comprising: producing,
at least on one of the surfaces of a polymer base, an undercoat
layer containing, as the primary component, an acrylic resin
produced by copolymerizing an acrylic monomer and at least one
macromonomer selected from the group consisting of (i) to (iii)
given below, and forming an inorganic layer on the undercoat layer:
(i) a macromonomer including an acrylic polymer having a radically
polymerizable group at an end thereof, (ii) a macromonomer
including a dimethyl siloxane skeleton-based polymer having a
radically polymerizable group at an end thereof, (iii) a
macromonomer including a fluorine atom-containing polymer having a
radically polymerizable group at an end thereof.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This is the U.S. National Phase application of
PCT/JP2012/075077, filed Sep. 28, 2012, which claims priority to
Japanese Patent Application No. 2011-236951, filed Oct. 28, 2011,
Japanese Patent Application No. 2012-175608, filed Aug. 8, 2012,
and Japanese Patent Application No. 2012-205385, filed Sep. 19,
2012.
FIELD OF THE INVENTION
[0002] The present invention relates to gas barrier film to be used
as packaging materials for foodstuffs and pharmaceuticals, and
members of electronic devices such as solar battery, electronic
paper, and organic EL that are required to have high gas barrier
properties.
BACKGROUND OF THE INVENTION
[0003] Gas barrier films composed of a polymer base having an
deposited layer of an inorganic substance (or inorganic oxide) such
as aluminum oxide, silicon oxide, and magnesium oxide formed on a
surface thereof by a physical vapor deposition (PVD) technique such
as vacuum deposition, sputtering, and ion plating, or a chemical
vapor deposition (CVD) technique such as plasma chemical vapor
deposition, thermochemical vapor deposition, and photochemical
vapor deposition have been used as materials for packaging of
foodstuffs and pharmaceuticals and members of electronic devices
such as Flat-screen TV and solar battery that are required to be
impermeable to various gases including water vapor and oxygen.
[0004] Gas barrier properties improvement techniques that are
available now include, for example, forming a compound composed
mainly of silicon oxide and containing at least one element
selected from the group consisting of carbon, hydrogen, silicon,
and oxygen on a base by the plasma CVD technique using a gas
mixture containing vapor of an organic silicon compound and oxygen
to achieve improved gas barrier properties while maintaining
transparency (Patent document 1). Other gas barrier properties
improvement techniques that do not use a film formation process
such as plasma CVD include the use of a smooth-surfaced base or a
base with an undercoat that provides a smooth surface free from
protrusions and irregularities that can cause pinholes and cracks
that degrade the gas barrier properties (Patent document 2).
Patent Documents
[0005] Patent document 1: Japanese Unexamined Patent Publication
(Kokai) No. HEI-8-142252 (Claims)
[0006] Patent document 2: Japanese Unexamined Patent Publication
(Kokai) No. 2002-113826 (Claims)
SUMMARY OF THE INVENTION
[0007] In the case where a layer with gas barrier properties
containing silicon oxide as the primary component is formed by the
plasma CVD technique, however, the surface of the base is
influenced by the heat emitted from the plasma and collisions of
ions and radicals and accordingly, the film properties of the
resulting gas barrier layer will be largely dependent on the type
of base material used, leading to problems such as the fail to
ensure stable gas barrier properties.
[0008] In the case of forming a gas barrier layer having a
smooth-surfaced base or a base with an undercoat that provides a
smooth surface, on the other hand, dramatic improvement in
performance is not achieved because the resulting gas barrier layer
does not have improved film properties although the prevention of
the generation of pinholes and cracks serves to improve the
reproducibility of gas barrier properties.
[0009] In view of such a prior art background, the present
invention aims to provide a gas barrier film that achieves
dramatically improved gas barrier properties and stable development
of such gas barrier properties without using special types of base
material.
[0010] Embodiments of the present invention adopt the following
measures to solve these problems. Specifically, embodiments of the
invention provide a polymer base laminated, at least on one surface
thereof, with an undercoat layer containing, as the primary
component, acrylic resin having at least one side chain selected
from the group consisting of (I) to (III) given below and an
inorganic layer stacked in contact with each other in this
order:
(I) a side chain having an acrylic polymer skeleton, (II) a side
chain having a dimethyl siloxane skeleton, (III) a side chain
having a fluorine atom-containing skeleton.
[0011] It is preferable for the aforementioned side chain to
contain at least (II) and/or (III) given above.
[0012] It is also preferable that the aforementioned acrylic resin
be an acrylic resin having a structure produced by copolymerizing
an acrylic monomer and at least one macromonomer selected from the
group consisting of (i) to (iii) given below:
(i) a macromonomer including an acrylic polymer having a radically
polymerizable group at an end thereof, (ii) a macromonomer
including a dimethyl siloxane skeleton-based polymer having a
radically polymerizable group at an end thereof, (iii) a
macromonomer including a fluorine atom-containing polymer having a
radically polymerizable group at an end thereof.
[0013] It is preferable for the aforementioned macromonomer to
contain at least (II) or (III) given above.
[0014] It is preferable for the undercoat layer to have a surface
free energy of 10 to 45 mN/m, more preferably 10 to 25 mN/m.
[0015] It is preferable for the acrylic resin to be one produced by
copolymerizing 100 parts by mass of the acrylic monomer having a
composition as described below with 3 to 8 parts by mass of a
macromonomer:
1 to 8 mass % of methacrylic acid, 5 to 16 mass % of 2-hydroxyethyl
methacrylate, and 76 to 94 mass % of methyl methacrylate and/or
dicyclopentanyl methacrylate.
[0016] It is preferable for the inorganic layer to have a thickness
of 10 to 1,000 nm and comprise a zinc compound and silicon
oxide.
[0017] It is preferable for the inorganic layer to be either a
layer [B1] or a layer [B2] as described below:
layer [B1]: a layer of a phase in which zinc oxide, silicon
dioxide, and aluminum oxide coexist, layer [B2]: a layer of a phase
in which zinc sulfide and silicon dioxide coexist.
[0018] In the case where the aforementioned inorganic layer is a
layer [B1], it is preferable for the layer [B1] to have a
composition with a zinc (Zn) atom concentration of 20 to 40 atom %,
silicon (Si) atom concentration of 5 to 20 atom %, aluminum (Al)
atom concentration of 0.5 to 5 atom %, and oxygen (O) atom
concentration of 35 to 70 atom % as determined by ICP luminescence
spectroscopy analysis, while in the case where the inorganic layer
is a layer [B2], it is preferable for the layer [B2] to have a
composition in which the zinc sulfide accounts for a mole fraction
of 0.7 to 0.9 of the total quantity of zinc sulfide and silicon
dioxide.
[0019] It is preferable for the inorganic layer to have a surface
roughness Ra of 2 nm or less.
[0020] The production method for gas barrier film according to an
embodiment of the present invention includes: [0021] producing, at
least on one of the surfaces of a polymer base, an undercoat layer
containing, as the primary component, an acrylic resin produced by
copolymerizing an acrylic monomer with at least one macromonomer
selected from the group consisting of (i) to (iii) given below, and
[0022] forming an inorganic layer on the undercoat layer: (i) a
macromonomer including an acrylic polymer having a radically
polymerizable group at an end thereof, (ii) a macromonomer
including a dimethyl siloxane skeleton-based polymer having a
radically polymerizable group at an end thereof, (iii) a
macromonomer including a fluorine atom-containing polymer having a
radically polymerizable group at an end thereof.
[0023] The present invention can provide a gas barrier film that
achieves dramatic improvement in gas barrier properties and stable
development of such gas barrier properties without using special
types of base material.
BRIEF DESCRIPTION OF THE DRAWINGS
[0024] FIG. 1 is a cross-sectional diagram of the gas barrier film
according to an embodiment of the present invention.
[0025] FIG. 2 is a schematic cross-sectional diagram of a wind-up
type sputtering apparatus designed for the production of the gas
barrier film according to an embodiment of the present
invention.
DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION
[0026] As a result of intensive studies aimed at obtaining a gas
barrier film with good gas barrier properties without using a
particular type of polymer base material, the present inventors
found that the problems described above can be solved by adopting a
polymer base laminated, at least on one of the surfaces thereof,
with an undercoat layer containing, as the primary component, an
acrylic resin having a skeleton with a specific type of side chain,
and an inorganic layer stacked in this order. In particular, it was
found that the inorganic layer used for an embodiment of the
present invention, which plays the central role in developing gas
barrier properties, can serve to dramatically improve the gas
barrier properties when it is formed on, and in contact with, a
specific type of undercoat layer. An undercoat layer containing an
acrylic resin as the primary component as referred to herein
contains the acrylic resin at a content of 65 mass % or more,
preferably 80 mass % or more, of the undercoat layer. The other
components contained in the undercoat layer (hereinafter referred
to as the minor components of the undercoat layer) will be
described later.
[0027] FIG. 1 is across-sectional diagram of the gas barrier film
according to an embodiment of the present invention. As illustrated
in FIG. 1, the gas barrier film according to an embodiment of the
present invention includes a polymer base 1 laminated, on one of
the surfaces thereof, with a specific type of undercoat layer 2 and
an inorganic layer 3 stacked in this order in such manner that the
undercoat layer 2 and the inorganic layer 3 are in contact with
each other. Here, FIG. 1 shows an embodiment in which the polymer
base 1 is in contact with the undercoat layer 2, but another layer
may be disposed between the polymer base 1 and the undercoat layer
2 with the aim of improving the contact in a high temperature, high
humidity environment (wet-heat-resistant contact) as long as a
flexibility required for the gas barrier film is maintained.
[Polymer Base]
[0028] There are no specific limitations on the material to be used
for the polymer base according to the present invention as long as
it is in the form of a film, but it is preferably a polymer base of
an organic polymer because it has flexibility necessary for the
production of a gas barrier film. Organic polymers used favorably
for the present invention include, for example, polyolefins such as
polyethylene and polypropylene; polyesters such as polyethylene
terephthalate (PET) and polyethylene naphthalate (PEN); and various
other polymers such as polyamide, ABS resin, polycarbonate,
polystyrene, polyvinyl alcohol, saponification products of ethylene
vinyl acetate copolymers, polyacrylonitrile, and polyacetal. Of
these, polyethylene terephthalate is preferably contained.
Furthermore, the organic polymer to be used may be either a
homopolymer or a copolymer, and either a single organic polymer or
a blend of a plurality of organic polymers.
[0029] Furthermore, as listed above, the organic polymers that can
be used favorably for the present invention have a linear basic
skeleton (the term "linear" means that the skeleton does not have a
network structure even if it has branching. Hereinafter, an organic
polymer having a linear basic skeleton is referred to as linear
organic polymer.). In addition, even if partial crosslinking is
formed by, for example, adding and reacting a crosslinking agent
having two or more functional groups in a molecule or applying
radiations, an organic polymer is assumed to be linear if it has a
number average molecular weight of 5,000 to 20,000.
[0030] The polymer base may be in the form of a monolayer film or a
two or more layered film produced by, for example, coextrusion. In
regard to film type, it may be a uniaxially or biaxially stretched
film. The surface of the polymer base where an undercoat layer and
inorganic layer are to be formed may be pre-treated by such
techniques as corona treatment, ion bombardment treatment, solvent
treatment, and surface roughening treatment in order to ensure good
contact with the undercoat layer. The surface of the polymer base
opposite to the one where an undercoat layer and inorganic layer
are to be formed may be coated with a coat layer of an organic
substance, inorganic substance, or a mixture thereof with the aim
of improving the slip properties of the film during the winding up
step.
[0031] There are no specific limitations on the thickness of the
polymer base to be used for the present invention, but it is
preferably 500 .mu.m or less from the viewpoint of maintaining a
required flexibility and preferably 5 .mu.m or more from the
viewpoint of maintaining a required resistance to tension and
impact. To ensure a required film processability and handleability,
furthermore, it is still more preferably 10 .mu.m or more as the
lowest limit and 200 .mu.m or less as the highest limit.
[Acrylic Resin]
[0032] An acrylic resin to be used according to an embodiment of
the present invention contains, as the primary component, an
acrylic resin having at least one side chain selected from the
group consisting of (I) to (III) given below:
(I) a side chain having an acrylic polymer skeleton, (II) a side
chain having a dimethyl siloxane skeleton, (III) a side chain
having a fluorine atom-containing skeleton.
[0033] It is preferable that the acrylic resin to be used for the
present invention be an acrylic resin having a structure produced
by copolymerizing an acrylic monomer and at least one macromonomer
selected from the group consisting of (i) to (iii) given below:
(i) a macromonomer including an acrylic polymer having a radically
polymerizable group at an end thereof, (ii) a macromonomer
including a dimethyl siloxane skeleton-based polymer having a
radically polymerizable group at an end thereof, (iii) a
macromonomer including a fluorine atom-containing polymer having a
radically polymerizable group at an end thereof.
[0034] Hereinafter, (i) a macromonomer including an acrylic polymer
having a radically polymerizable group at an end thereof, (ii) a
macromonomer including a dimethyl siloxane skeleton-based polymer
having a radically polymerizable group at an end thereof, and (iii)
a macromonomer including a polymer of a structure with a fluorine
atom-containing skeleton having a radically polymerizable group at
an end thereof are occasionally referred to as macromonomer (A),
macromonomer (Si), and macromonomer (F), respectively. In the
present Description, furthermore, the simple term of "a
macromonomer" refers to at least one macromonomer selected from the
group consisting of (i) to (iii) or a mixture of two or more
thereof.
[0035] The mechanism by which dramatically improved gas barrier
properties are achieved by using an acrylic resin having at least
one side chain selected from the group consisting of (I) to (III)
given above, or preferably an acrylic resin having a structure
produced by copolymerizing an acrylic monomer and at least one
macromonomer selected from the group consisting of (i) to (iii)
given above, has not been clarified, but inferred to be as follows.
Specifically, the use of a specific acrylic resin as listed above
serves to depress the surface free energy of the undercoat layer at
a relatively low level as explained later, and accordingly, the
atoms and particles acting as growth nuclei at an initial stage of
the growth process for inorganic layer formation can move and
diffuse easily in the surface to allow a dense film structure to be
formed near the undercoat layer. From this point of view, because
of the effect of depressing the surface free energy of the
undercoat layer at a low level, it is preferable for the side
chains to contain at least (II) and/or (III) and it is preferable
for the macromonomers to be acrylic resins having a structure
containing at least (ii) or (iii). Because of easy fine control of
the denseness of the inorganic layer, it is more preferable that
the side chains contain (a) (I) and (b) (II) and/or (III) and it is
particularly preferable that the macromonomers are acrylic resins
having a structure containing (a) (i) and (b) (ii) or (iii).
[0036] Furthermore, it is preferable that an acrylic resin to be
used for the present invention have a structure produced by
copolymerizing (1) 1 to 8 mass % of a methacrylic acid, (2) 5 to 16
mass % of 2-hydroxyethyl methacrylate, and (3) 76 to 94 mass % of
methyl methacrylate and/or dicyclopentanyl methacrylate, which
altogether constitute 100 mass % of the acrylic monomers involved,
and macromonomers that account for 3 to 8 parts by mass relative to
the 100 parts by mass of the acrylic monomers. Here, products such
as Fancryl FA-513M (manufactured by Hitachi Chemical Co., Ltd.) can
be used as the dicyclopentanyl methacrylate.
[0037] If the (1) methacrylic acid accounts only for less than 1
mass % of the acrylic monomers used for the copolymerization of the
acrylic resin, the resulting acrylic resin occasionally fails to
have a sufficient cohesion force, leading to inadequate adhesion
with the polymer base, while if the (1) methacrylic acid accounts
for more than 8 mass %, the acrylic resin occasionally fails to
have sufficient chemical resistance such as water resistance and
alkaline resistance. From this point of view, it is preferable for
the (1) methacrylic acid to account for 1 to 7 mass %, more
preferably 1 to 5 mass %.
[0038] If the (2) 2-hydroxyethyl methacrylate accounts only for
less than 5 mass % of the acrylic monomers used for the
copolymerization of the acrylic resin, the resulting acrylic resin
occasionally fails to achieve a sufficient adhesion with a polymer
base material such as PET, PEN, polyamide, and ABS resin, while the
(2) 2-hydroxyethyl methacrylate accounts for more than 16 mass %,
the acrylic resin, for example, occasionally fails to produce a
coating liquid with a sufficiently long pot life when blended with
a crosslinking agent, leading to insufficient coating workability.
From this point of view, it is preferable for the (2)
2-hydroxyethyl methacrylate to account for 5 to 12 mass %, more
preferably 8 to 12 mass %.
[0039] If the (3) methyl methacrylate and/or dicyclopentanyl
methacrylate account for only less than 76 mass % of the acrylic
monomers used for the copolymerization of the acrylic resin, they
occasionally fail to have a high compatibility with the
macromonomers, leading to poor contact with the polymer base. If
the (3) methyl methacrylate and/or dicyclopentanyl methacrylate
account for more than 94 mass %, they occasionally fail to have a
moderate incompatibility with the macromonomers, leading to the
loss of the function to further reduce the surface roughness of the
undercoated. From this point of view, it is preferable for the (3)
methyl methacrylate and/or dicyclopentanyl methacrylate to account
for 76 to 94 mass %, more preferably 81 to 94 mass %, and still
more preferably 83 to 91 mass %.
[0040] In the acrylic resin, the compatibility of the skeleton
chain and side chain in the molecule changes depending on the
compounding ratio of the skeleton chain originating from the
acrylic monomer and the side chain originating from the
macromonomers and also on the ratio of the side chains originating
from the macromonomers (ratio between (a) side chains having an
acrylic polymer skeleton and (b) side chains having a dimethyl
siloxane skeleton and/or side chains having a fluorine
atom-containing skeleton). The compatibility of the skeleton chain
and side chain in the molecule can be controlled, and accordingly
characteristics such as free energy of the entire molecule can be
varied, by changing the type and compounding ratio of the acrylic
monomer or changing the type and compounding ratio of the
macromonomers. It is known that such variations in characteristics
of the macromonomers can influence the changes in the microscopic
layer separation structures (such as lamella, gyroid, cylinder, and
BCC).
[0041] It is preferable that an acrylic resin to be used for the
present invention have a structure produced by copolymerizing 100
parts by mass of the acrylic monomer with 3 to 8 parts by mass of
macromonomers. If the proportion of the macromonomers used as
material for the acrylic resin (hereinafter, occasionally referred
to as the proportion of the macromonomers in the acrylic resin) is
less than 3 parts by mass, the formation of an undercoat layer
possibly cannot serve effectively for reducing the irregularities
in the surface of the polymer base, leading to an undercoat layer
with insufficient surface smoothness. If the proportion of the
macromonomers in the acrylic resin is more than 8 parts by mass,
the compatibility between the main structure of the acrylic resin
having a structure produced by copolymerizing methacrylic
acid/2-hydroxyethyl methacrylate/methyl methacrylate and/or
dicyclopentanyl methacrylate and the side chains originating from
the macromonomers tends to be low and the undercoat layer formed
from the acrylic resin possibly suffers from inadequate adhesion
with the polymer base and poor transparency. From this point of
view, the proportion of the macromonomers in the acrylic resin is
preferably 3 to 8 parts by mass, more preferably 3 to 7 parts by
mass, still more preferably 3 to 5 parts by mass. If the proportion
of the macromonomers in the acrylic resin used for the present
invention is 3 to 8 parts by mass, it is preferable because the
resulting undercoat layer will achieve a good balance among the
adhesion with the polymer base, transparency, and smoothness and
show high performance.
[0042] The number average molecular weight of the macromonomers to
be used for the present invention is preferably 2,000 to 50,000,
more preferably 3,000 to 30,000, and still more preferably 5,000 to
10,000. If the number average molecular weight of the macromonomers
is less than 2,000, the side chains will be relatively short
compared to the main structures originating from the acrylic
monomer composed of methacrylic acid/2-hydroxyethyl
methacrylate/methyl methacrylate and/or dicyclopentanyl
methacrylate, and accordingly, they will be trapped by the main
structures, possibly making it difficult to decrease the surface
free energy of the coat film. If the number average molecular
weight of the macromonomers is more than 50,000, on the other hand,
a rise in viscosity can take place during polymerization, possibly
leading to a decrease in the monomer-to-polymer conversion
percentage.
[0043] In regard to the macromonomers to be used for the present
invention, it is preferable to adopt at least one macromonomer
selected from the group consisting of (i) to (iii) given below.
(i) Macromonomer including an acrylic polymer having a radically
polymerizable group at an end thereof: macromonomer (A) (ii)
Macromonomer including a dimethyl siloxane skeleton-based polymer
having a radically polymerizable group at an end thereof:
macromonomer (Si) (iii) Macromonomer including a fluorine
atom-containing polymer having a radically polymerizable group at
an end thereof: macromonomer (F)
[0044] The macromonomer (A) to be used for the present invention is
preferably a polymethyl methacrylate macromonomer which is composed
of a polymethyl methacrylate having a methacryloyl group at an end.
If a polymethyl methacrylate macromonomer is used, there will be a
high compatibility between the skeleton chains originating from the
acrylic monomer and the side chains originating from the
macromonomer (A), leading to strong adhesion between the undercoat
layer and the polymer base and an improved transparency of the
undercoat layer. Commercial products of polymethyl methacrylate
macromonomers include Macromonomer AA-6 and Macromonomer 45% AA-6
(both manufactured by Toagosei Co., Ltd.).
[0045] The macromonomer (Si) to be used for the present invention
is preferably a polydimethyl siloxane macromonomer that includes a
dimethyl siloxane skeleton-based polymer having a radically
polymerizable group at an end thereof. The use of a polydimethyl
siloxane macromonomer is preferable because it will be easy to
control the surface free energy at a low level as described later.
Commercial products of polydimethyl siloxane macromonomers include,
for example, AK-5, AK-30, and AK-32 (manufactured by Toagosei Co.,
Ltd.) and X-22-174DK, X-24-8201, and X-22-2426 (manufactured by
Shin-Etsu Chemical Co., Ltd.). The macromonomer (Si) to be used may
be one of these commercial products or may be polymerized by, for
example, an appropriate method found in literature (such as
Japanese Unexamined Patent Publication (Kokai) No.
2009-197042).
[0046] The macromonomer (F) to be used for the present invention is
preferably one that includes a fluorine atom-containing polymer
having a radically polymerizable group at an end thereof. Such a
macromonomer (Si) may be a commercial product or may be newly
polymerized by, for example, an appropriate method found in
literature (such as Japanese Unexamined Patent Publication (Kokai)
No. HEI-10-120738). Useful precursors serving to polymerize a
macromonomer (F) include (meth)acrylates such as
2,2,2-trifluoroethyl acrylate, 2,2,2-trifluoroethyl methacrylate,
2,2,3,3-tetrafluoropropyl acrylate, 1H,1H,5H-octafluoropentyl
acrylate, and 1H,1H,5H-octafluoropentyl acrylate; and fluoroolefins
such as tetrafluoroethylene, chlorotrifluoroethylene,
trifluoroethylene, vinylidene fluoride, vinyl fluoride, and
hexafluoropropylene. These may be used singly or appropriate ones
of each group may be mixed at an appropriate ratio.
[0047] For the present invention, it is preferable to use acrylic
monomers and macromonomers that contain only those radically
polymerizable groups which have a methacryloyl group
(CH.sub.2.dbd.C(CH.sub.3)--C(.dbd.O)O--). If the acrylic monomers
and macromonomers used are ones containing only those radically
polymerizable groups which have a methacryloyl group, it is
preferable because the resulting acrylic resin will have a further
increased cohesion force and accordingly will achieve an improved
adhesion with the polymer base, leading to improvement in solvent
resistance and heat resistance.
[0048] Furthermore, the contribution of the surface free energy of
the undercoat layer to the effect of achieving dramatically
improved gas barrier properties according to an embodiment of the
present invention is inferred to arise as follows: if a surface
free energy is controlled at less than 45 mN/m, the atoms and
particles that act as nuclei for film growth will be able to move
and diffuse easily in the surface during the initial growth step in
the inorganic layer formation process, and accordingly, dense film
properties will be developed near the undercoat layer, resulting in
the formation of an entirely dense layer that can control the
penetration of gases. From such a point of view, the surface free
energy of the undercoat layer is more preferably 30 mN/m or less,
still more preferably 25 mN/m or less. It is also preferable for
the surface free energy to be 10 mN/m or more. If the surface free
energy is less than 10 mN/m, the contact between the undercoat
layer and the inorganic layer will possibly be weak, failing to
form a dense structure in the inorganic layer. From these
considerations, the surface free energy of the undercoat layer is
preferably 10 to 45 mN/m, more preferably 10 to 30 mN/m, and still
more preferably 10 to 25 mN/m.
[0049] For adjusting the surface free energy of the undercoat layer
used according to an embodiment of the present invention, the
available methods include controlling the surface free energy of
the acrylic monomer, a macromonomer, or a minor component of the
undercoat layer, of which the method of selecting an optimum
compounding ratio, type, or combination of the macromonomers is
preferable because of a high degree of freedom for adjusting them
without having a significant influence on other characteristics.
(a) Macromonomer (A) has a relatively large surface free energy
and, for example, the use of 3 to 8 parts by mass of it per 100
parts by mass of the acrylic monomer will permit adjustment in the
range of about 30 to 45 mN/m. (b) Macromonomer (Si) and/or
macromonomer (F) has a relatively small surface free energy and,
for example, the use of 3 to 8 parts by mass of it per 100 parts by
mass of the acrylic monomer will permit adjustment in the range of
about 10 to 25 mN/m. These facts suggest that if (a) macromonomer
(A) and (b) macromonomer (Si) and/or macromonomer (F) are used, the
surface free energy can be controlled by adjusting their content
ratio. There are no specific limitations on the compounding ratio
of the macromonomers, but in order to adjust the surface free
energy in a moderate range, the content of (a) macromonomer (A) is
preferably 10 to 70 mass %, more preferably 20 to 50 mass %,
relative to the total quantity of the macromonomers.
[0050] For the present invention, the term "(b) macromonomer (Si)
and/or macromonomer (F)" means the single use of either a
macromonomer (Si) or a macromonomer (F) or the use of their mixture
combined at an appropriate mixing ratio.
[0051] In addition, another macromonomer different from the above
ones may also be contained. It may also be effective to use a
mixture of two or more macromonomers that have different molecular
weight distributions.
[0052] To examine the surface free energy of the undercoat layer
according to an embodiment of the present invention, four measuring
liquids (water, formamide, ethylene glycol, and methylene iodide)
with known component forces (dispersion force, polar force, and
hydrogen bonding force) are prepared and the contact angle of each
measuring liquid is determined, followed by calculating the
components using the following formula that is derived from the
extended Fowkes' equation and Young's equation.
[Formula 1]
(.gamma.Sd.gamma.Ld).sup.0.5+(.gamma.Sp.gamma.Lp).sup.0.5+(.gamma.Sh.gam-
ma.Lh).sup.0.5=.gamma.L(1+cos .theta.)/2 (1)
where [0053] .gamma.S=.gamma.Sd+.gamma.Sp+.gamma.Sh [0054]
.gamma.L=.gamma.Ld+.gamma.Lp+.gamma.Lh [0055] .gamma.S: surface
energy of undercoat layer [0056] .gamma.Sd: dispersion force
component of undercoat layer [0057] .gamma.Sp: polar force
component of undercoat layer [0058] .gamma.Sh: hydrogen bonding
force component of undercoat layer [0059] .gamma.L: surface energy
of measuring liquid [0060] .gamma.Ld: dispersion force component
[0061] .gamma.Lp: polar force component [0062] .gamma.Lh: hydrogen
bonding force component [0063] .theta.: contact angle of measuring
liquid on undercoat layer
[Characteristics of Acrylic Resin]
[0064] The acrylic resin used for the present invention preferably
has a glass transition temperature (hereinafter also referred to as
Tg) of 50 to 180.degree. C. If the acrylic resin used for the
present invention has a Tg of less than 50.degree. C., the acrylic
resin will possibly be low in cohesion force and unable to achieve
a sufficient adhesion with the inorganic layer. If the acrylic
resin has a Tg of more than 180.degree. C., the acrylic resin is
possibly brittle and unable to deform in coordination with
processing such as bending and molding of the polymer base. From
this point of view, the acrylic resin preferably has a Tg of 55 to
175.degree. C., more preferably 60 to 170.degree. C., and still
more preferably 80 to 160.degree. C. If the acrylic resin used for
the present invention has a Tg of 55 to 175.degree. C., it is
preferable because the resin tends to have well-balanced
characteristics including adhesion with polymer base materials such
as PET film, PEN film, nylon, and ABS resin, as well as flexibility
and chemical resistance and show high performance, and a Tg of 80
to 160.degree. C. is more preferable because the resulting
undercoat layer will have a high surface denseness due to high
smoothness and cohesiveness at the surface of the undercoat layer,
allowing the inorganic layer formed thereon to have further
improved uniformity and surface smoothness.
[0065] The number average molecular weight of the acrylic resin to
be used for the present invention is preferably 5,000 to 30,000,
more preferably 8,000 to 28,000, and still more preferably 8,000 to
25,000. If the number average molecular weight of the acrylic resin
to be used for the present invention is 5,000 to 30,000, it is
preferable because a moderate leveling property is maintained to
minimize the surface roughness of the undercoat layer.
[Production Method for Acrylic Resin]
[0066] It is preferable that the acrylic resin to be used for the
present invention be one produced by copolymerizing an acrylic
monomer and at least one macromonomer selected from the group
consisting of (i) to (iii) given below:
(i) a macromonomer including an acrylic polymer having a radically
polymerizable group at an end thereof, (ii) a macromonomer
including a dimethyl siloxane skeleton-based polymer having a
radically polymerizable group at an end thereof, (iii) a
macromonomer including a fluorine atom-containing polymer having a
radically polymerizable group at an end thereof.
[0067] In this copolymerization step, it is desirable that the
acrylic resin be produced by solution polymerization using an
organic peroxide such as benzoyl peroxide, an azo polymerization
initiator such as azobisisobutyronitrile and
2,2'-azobis(2,4-dimethylvaleronitrile), and a chain transfer agent
such as n-dodecyl mercaptan and t-dodecyl mercaptan, in an organic
solvent such as ethyl acetate, butyl acetate, toluene, and xylene
at a polymerization temperature of 50 to 120.degree. C. To describe
this solution polymerization in detail, a preferable method is
feeding the macromonomer and the organic solvent in a
polymerization container, heating them at an appropriate
polymerization temperature, and adding a mixture of the acrylic
monomer, polymerization initiator, and chain transfer agent. Thus,
it is considered that the feeding of a macromonomer in an organic
solvent and the subsequent addition of an acrylic monomer,
polymerization initiator, and chain transfer agent ensure efficient
copolymerization between the macromonomer and the acrylic monomer,
which is preferable because it leads to further improvement in the
adhesion with the polymer base and the smoothness of the surface of
the undercoat layer.
[0068] The polymerization reaction for preparing the acrylic resin
to be used for the present invention is preferably carried out in
an inert gas atmosphere such as nitrogen gas, and it is preferable
to fill the polymerization container with an inert gas before
feeding the monomers to the polymerization container and then add
the acrylic monomer and macromonomer s (and an organic solvent if
necessary) while continuing to supply the inert gas. By carrying
out the polymerization reaction in an inert gas atmosphere, the
radicals formed from the acrylic monomer and macromonomers during
the reaction process are prevented from reacting with active gases
(such as oxygen gas).
[0069] A production method for the acrylic resin used according to
an embodiment of the present invention is described concretely
below. An organic solvent (such as toluene and ethyl acetate) and
the polymethyl methacrylate macromonomer are fed to a
polymerization apparatus equipped with a stirrer, nitrogen gas
supply nozzle, capacitor, and monomer dropping device while
supplying nitrogen gas, followed by heating to a predetermined
polymerization temperature. Then, the acrylic monomer,
polymerization initiator (such as azobisisobutyronitrile and
tertiary butylperoxy-2-ethyl hexanoate), chain transfer agent (such
as n-dodecyl mercaptan and t-dodecyl mercaptan), which are weighed
and mixed in advance to prepare a uniform mixture solution, are
dropped to a polymerization container at a predetermined rate.
After the completion of the dropping, an additional amount of the
polymerization initiator is added to increase the
monomer-to-polymer conversion percentage, and the solution is
continued to be heated and stirred for a predetermined period, and
then cooled.
[0070] According to an embodiment of the present invention, an
undercoat layer containing, as the primary component, an acrylic
resin as produced above is formed at least on one surface of a
polymer base, and it is also preferable here for the undercoat
layer to contain minor components as specified below.
[Minor Components of Undercoat Layer]
[0071] The undercoat layer used for the present invention
preferably contains a crosslinking agent, modifier polymer, or
other substances as minor components. Preferred crosslinking agents
to be used as minor components of the undercoat layer include
polyisocyanate compounds such as tolylene diisocyanate,
hexamethylene diisocyanate, meta-xylene diisocyanate, and
isophorone diisocyanate that react with the acrylic resin to form a
required crosslinked structure. Preferred modifier polymers to be
used as minor components of the undercoat layer include polyester
diols and polyurethane diols that are compatible with the acrylic
resin. When these minor components for the undercoat layer are
added to the acrylic resin which is the primary component of the
undercoat layer, it is preferable that these minor components be
added to the acrylic resin solution resulting from the
aforementioned solution polymerization. It is also preferable that
the viscosity is decreased by lowering the solid content and the
coating workability is improved by adding an organic solvent during
the addition of these minor components, or before or after the
addition of these minor components, in preparing an acrylic resin
coating liquid. Useful organic solvents for this purpose include
alcohols such as ethyl alcohol, isopropyl alcohol, ethanol,
isopropanol, n-propanol, and butyl alcohol; esters such as ethyl
acetate, butyl acetate, and triethyl orthoacetate; ketones such as
cyclohexanone, methyl ethyl ketone, and methyl isobutyl ketone;
alkylene glycol ethers such as propylene glycol monopropyl ether,
propylene glycol monobutyl ether, ethylene glycol monoethyl ether,
and ethylene glycol monobutyl ether; and aromatic substances such
as toluene and xylene.
[0072] Using a polyisocyanate compound such as hexamethylene
diisocyanate as a minor component that acts as a crosslinking agent
for the undercoat layer used for the present invention is
preferable because the undercoat layer will have an improved
toughness and achieve a strong adhesion with the plane that defines
the undercoat layer (the surface of the polymer base or the surface
of the additional layer disposed between the undercoat layer and
the polymer base in the case where such an additional layer exists)
of PET, PEN, polyamide, ABS resin, etc.
[0073] Using a modifier polymer such as polyester diol as a minor
component for the undercoat layer used for the present invention is
preferable because the resulting undercoat layer will have
increased and improved hardness, flaw resistance, toughness,
flexibility, and other mechanical properties and achieve an
improved adhesion with the polymer base of PET, PEN, polyamide, ABS
resin, etc., and also because the undercoat layer will have further
improved surface smoothness. Commercial polymer products that can
serve as such modifiers include Flexorez 148, Flexorez 188,
Flexorez XP-171-90, and Flexorez UD-320 (all manufactured by King
Industries, Inc.).
[0074] Of the modifier polymers such as polyester polyols and
polyester diols to be contained in the undercoat layer used for the
present invention, polyester diols are preferable. This is because
it serves to ensure further improvement in the adhesion between the
undercoat layer and the plane that defines the undercoat layer (the
surface of the polymer base or the surface of the additional layer
disposed between the undercoat layer and the polymer base in the
case where such an additional layer exists) and in the smoothness
of the surface (the plane defining the inorganic layer) of the
resulting undercoat layer. The use of polyester polyol is
preferable also because the acrylic resin coating liquid will have
improved storage stability.
[0075] In the present Description, the term "acrylic resin coating
liquid" refers to a mixture of an acrylic resin that acts as the
primary component of the undercoat layer, minor components for the
undercoat layer such as crosslinking agents and modifier polymers,
and an appropriate organic solvent. Furthermore, the primary
component and minor components for the undercoat layer contained in
the acrylic resin coating liquid are collectively referred to
undercoat layer formation components.
[0076] In the acrylic resin coating liquid used for the present
invention, the polyester polyol preferably accounts for 5 to 35
mass % of the total quantity of the undercoat layer formation
components. If the content of the polyester polyol is 5 to 35 mass
%, the acrylic resin coating liquid will have high storage
stability, and the mixture produced by adding a polyisocyanate
compound such as isophorone diisocyanate, xylene diisocyanate, and
hexamethylene diisocyanate will have a long pot life, leading to
improved workability. Furthermore, the undercoat layer will have
improved flexibility, impact resistance, and flaw resistance
(hardness). If the content of the polyester polyol is less than 5
mass %, the resulting undercoat layer will possibly be brittle with
inadequate flexibility and impact resistance while if the content
of the polyester polyol is more than 35 mass %, the adhesion with
the plane that defines the undercoat layer (the surface of the
polymer base or the surface of the additional layer disposed
between the undercoat layer and the polymer base in the case where
such an additional layer exists) will possibly be weak.
[0077] If a polyester polyol is added to the acrylic resin coating
liquid used for the present invention, it is preferable for the
polyester polyol to have a hydroxyl equivalent of 200 to 500, more
preferably 220 to 500, and still more preferably 230 to 480. If the
polyester polyol has a hydroxyl equivalent of 200 to 500 in such a
case, it is preferable because, for example, the mixture produced
by adding a polyisocyanate compound such as isophorone
diisocyanate, xylene diisocyanate, and hexamethylene diisocyanate
in order to form urethane crosslinks in the acrylic resin will have
a long pot life. Furthermore, the undercoat layer will have
improved bending properties, flexibility, and hardness, and the
undercoat layer will also have minimized surface roughness.
[0078] In addition to the undercoat layer formation components and
organic solvent, the acrylic resin coating liquid used for the
present invention may also contain a stabilizer such as
antioxidant, photostabilizer, and ultraviolet absorber; a paint
additive such as antifoam agent, leveling agent, and wetting agent;
silane coupling agent such as .gamma.-glycidoxy propyl
trimethoxysilane and 3-aminopropyl triethoxysilane; methacrylic
acid or metal salt of acrylic acid such as zinc methacrylate; and
other materials generally used in paints.
[0079] In addition, with the aim of reducing the surface free
energy of the undercoat layer, a silicone-based surface active
agent or silicone resin, i.e., a compound containing a silicon (Si)
atom, may be added unless they work to decrease the contact of the
undercoat layer with the inorganic layer or its gas barrier
properties. Compounds that serve for this purpose include amino
modified silicone, epoxy modified silicone, carboxyl modified
silicone, carbinol modified silicone, alkoxy modified silicone,
polyether modified silicone, alkyl modified silicone, fluorine
modified silicone, polyether modified polydimethyl siloxane,
polyester modified polydimethyl siloxane, aralkyl modified
polymethyl alkyl siloxane, polyether modified siloxane, polyether
modified acrylate-containing polydimethyl siloxane, silicone
modified polyacrylic, isocyanate-containing polysiloxane, vinyl
silane, methacryl silane, epoxy silane, mercaptosilane,
aminosilane, ureidosilane, and isocyanate silane. In addition,
fluorine (F) atom-containing compounds such as perfluoroalkyl can
also be used for the same purpose.
[Organic Solvents Used for Coating Liquid]
[0080] Organic solvents that can be used to prepare the acrylic
resin coating liquid used for embodiments of the present invention
include hydrocarbons such as petroleum naphtha, methyl cyclohexane,
toluene, xylene, and turpentine; alcohols such as methanol,
ethanol, n-propanol, isopropanol, n-butanol, isobutanol, secondary
butanol, and tertiary butanol; ethers such as isopropyl ether,
n-butyl ether, and di-isoamyl ether; ketones such as acetal,
acetone, methyl acetone, methyl ethyl ketone, methyl-n-propyl
ketone, methyl-n-butyl ketone, methyl isobutyl ketone,
methyl-n-amyl ketone, and cyclohexanone; and esters such as methyl
acetate, ethyl acetate, n-propyl acetate, isopropyl acetate,
n-butyl acetate, isobutyl acetate, and n-amyl acetate; and
polyhydric alcohols and derivatives thereof such as ethylene
glycol, ethylene glycol monomethyl ether, ethylene glycol
monomethyl ether acetate, ethylene glycol monoethyl ether, ethylene
glycol monoethyl ether acetate, propylene glycol monomethyl ether,
propylene glycol monoethyl ether, and propylene glycol methyl ether
acetate. For preparing the acrylic resin to be used according to an
embodiment of the present invention, the organic solvents described
above may be used singly or two or more thereof may be used as a
mixture.
[0081] The acrylic resin coating liquid used for the present
invention preferably contains at least one organic solvent selected
from the group consisting of ester-based organic solvents and
ketone-based organic solvents.
[0082] In regard to the organic solvent to be adopted to prepare
the acrylic resin coating liquid used for the present invention,
the use of at least one organic solvent selected from the group
consisting of ester-based organic solvents and ketone-based organic
solvents is preferable because the acrylic resin will have high
coating workability due to increased storage stability and drying
property as well as decreased viscosity. The organic solvent to be
adopted to prepare the acrylic resin coating liquid used for the
present invention is preferably a ketone-based organic solvent,
particularly preferably methyl ethyl ketone or methyl isobutyl
ketone, because the resulting undercoat layer will have minimized
surface roughness.
[Coating with Acrylic Resin Coating Liquid]
[0083] Useful coating techniques for the acrylic resin coating
liquid that is applied to form an undercoat layer used for the
present invention include, for example, generally known coating
techniques such as bar coating, reverse coating, gravure coating,
rod coating, die coating, spray coating, and coil coating, as well
as electrostatic coating and electric force-based coating. For the
present invention, gravure coating is preferred for use as the
coating technique.
[0084] The undercoat layer used for the present invention
preferably has a thickness of 0.2 .mu.m or more and 10 .mu.m or
less. If the layer has a thickness of less than 0.2 .mu.m, the
inorganic layer will possibly have uneven film properties, and
accordingly degraded gas barrier properties, as a result of the
influence of surface irregularities in the polymer base. If the
layer has a thickness of more than 10 .mu.m, the undercoat layer
will possibly suffer from a large residual stress in the layer that
can cause warping of the polymer base and cracking in the inorganic
layer, leading to degraded gas barrier properties. Thus, the
thickness of the undercoat layer is preferably 0.2 .mu.m or more
and 10 .mu.m or less, and from the viewpoint of maintaining high
flexibility, it is preferably 0.5 .mu.m or more and 5 .mu.m or
less. The thickness of an undercoat layer can be determined from
cross-sectional images observed by transmission electron microscopy
(TEM).
[0085] After coating a polymer base with the acrylic resin coating
liquid, it is preferable to treat it in a drier to remove the
organic solvent by volatilization. If the drying temperature is
low, the organic solvent will possibly remain in the undercoat
layer to make the undercoat layer brittle while if the drying
temperature is high, the polymer film will suffer from thermal
deformation to cause an increase in the surface roughness in the
undercoat layer. Accordingly, the drying temperature is preferably
80 to 150.degree. C., more preferably 100 to 130.degree. C.
[0086] If the treatment period for volatilization of the organic
solvent after coating the polymer base with the acrylic resin
coating liquid is short, the coated surface of the acrylic resin
coating liquid will not possibly be leveled sufficiently, causing
an increase in surface roughness in the undercoat layer. If the
treatment period for volatilization of the organic solvent is long,
on the other hand, the polymer film will suffer from thermal
deformation to cause an increase in surface roughness in the
undercoat layer. Accordingly, the drying period is preferably 0.1
to 3 minutes, preferably 0.2 to 2 minutes.
[0087] If an undercoat layer formation component containing a
crosslinking agent is used, the volatilization of the organic
solvent is preferably followed by curing it in a constant
temperature bath to promote the crosslinking reaction between the
acrylic resin and the crosslinking agent. The temperature for the
acceleration of crosslinking reaction is preferably 30 to
60.degree. C., more preferably 40 to 50.degree. C. The curing is
preferably continued for 0.5 day or more to improve the degree of
the crosslinking reaction, but the effect for increasing the
crosslinking reaction will level off and the polymer film will
suffer from thermal deformation as the period is lengthened and
therefore, it is preferably 7 days or shorter. In view of the
productivity as well, the curing period is more preferably 1 to 3
days.
[0088] The undercoat layer used for the present invention
preferably has a smooth surface. To allow the gas barrier film to
function effectively, the surface of the undercoat layer is
required not to have significant quantities of particles, such as
foreign objects, and protrusions. Therefore, the coating of the
polymer base with the acrylic resin is preferably performed in a
clean room. The degree of cleanness is preferably class 10000 or
lower, more preferably class 1000 or lower.
[Inorganic Layer]
[0089] Next, the inorganic layer is described in detail below.
According to an embodiment of the present invention, the inorganic
layer functions as the main layer in developing gas barrier
properties. It is preferable that the material to be used for
inorganic layer of the present invention be able to from a dense
amorphous film and contain silicon dioxide, which serves to develop
gas barrier properties.
[0090] The inorganic layer to be used for an embodiment of the
present invention preferably has a thickness of 10 nm or more. If
the inorganic layer has a thickness of less than 10 nm, a
sufficiently high degree of gas barrier properties may not be
maintained at some positions, leading to problems such as uneven
gas barrier properties. From this point of view, the inorganic
layer more preferably has a thickness of 100 nm or more. If the
thickness of the inorganic layer is more than 1,000 nm, a large
residual stress will take place in the layer, and cracks will be
generated easily in the inorganic layer under bending and external
impact, possibly leading to deterioration in the gas barrier
properties in the course of long-term use. Therefore, the inorganic
layer preferably has a thickness of 1,000 nm or less, and from the
viewpoint of maintaining required flexibility, its thickness is
preferably 500 nm or less. The thickness of the inorganic layer can
be determined from cross-sectional observations by transmission
electron microscopy (TEM).
[0091] The inorganic layer to be used for the present invention
preferably has a surface roughness Ra of 2 nm or less. According to
an embodiment of the present invention, the inorganic layer plays
the main role in developing gas barrier properties, and the gas
barrier properties are developed as a result of the inorganic layer
having dense film properties. To form an inorganic layer with a
higher degree of denseness, the inorganic layer should have a dense
surface structure. Thus, the inorganic layer has an increased
surface smoothness and a decreased surface roughness Ra.
[0092] As a result of investigations by the inventors, it was found
that the formation of an inorganic layer that covers the undercoat
layer of an embodiment of the present invention serves to develop
dramatically improved gas barrier properties.
[0093] Any useful material adopted for the inorganic layer of the
present invention preferably has a composition containing a zinc
compound and a silicon compound, and more preferably has a
composition containing a zinc compound and a silicon oxide because
they can form an amorphous film with dense properties and serve to
develop high gas barrier properties. The silicon oxide used here is
preferably a silicon dioxide. Hereinafter, silicon dioxide may be
abbreviated as SiO.sub.2. In regard to silicon dioxide (SiO.sub.2),
a substance having a composition ratio slightly differing from that
based on the silicon-oxygen ratio in the above composition formula
(between SiO and SiO.sub.2) may result depending on the production
conditions adopted, but such a substance is herein referred to as
silicon dioxide or SiO.sub.2.
[0094] According to an embodiment of the present invention, the
mechanism by which the advantageous effect of an embodiment of the
invention is achieved as a result of forming an inorganic layer on,
and in contact with, the aforementioned undercoat layer is
considered to be as follows. Specifically, as compared with a
structure in which a layer of silicon dioxide is formed directly on
the polymer base, the formation of an inorganic layer on the
undercoat layer serves effectively to prevent the polymer base from
being damaged by ions and radicals of the plasma used to produce
the silicon dioxide layer, allowing a dense silicon dioxide layer
to be produced stably. It is expected, furthermore, that if the
surface free energy of the undercoat layer is maintained in the
range of 45 mN/m or less, the sputtering particles will be able to
diffuse easily in the surface of the silicon dioxide layer on the
polymer base surface and finer dense film properties will be
developed near the polymer base surface as compared with
conventional cases, leading to improved gas barrier properties.
[0095] The inorganic layer to be used for the present invention may
additionally contain an oxide, nitride, or sulfide of Zn, Al, Ti,
Zr, Sn, In, Nb, Mo, or Ta, or, a mixture thereof, as long as it
contains silicon oxide.
[0096] As a result of investigations by the preferably inventors,
it was found that high gas barrier properties can be achieved by
using [B1] a layer of a phase in which zinc oxide, silicon dioxide,
and aluminum oxide coexist (hereinafter abbreviated as layer [B1])
or [B2] a layer of a phase in which zinc sulfide and silicon
dioxide coexist (hereinafter abbreviated as layer [B2]) as the
inorganic layer. (Details of layer [B1] and layer [B2] will be
described later.)
[0097] Furthermore, in order to improve the abrasion resistance, an
additional layer such as hard coat layer may be formed on the
inorganic layer used for the present invention unless it causes
deterioration in the gas barrier properties. Alternatively, the gas
barrier film according to the present invention may be combined
with a functional member formed of a material such as other resin
film, paper base material, metallic material, synthetic paper, and
cellophane to provide various layered laminate products. Such a
laminate can be a multifunctional one having heat resistance, high
transparency, weather resistance, electric conductivity, and
decorative properties, in addition to the high gas barrier
properties that preferably represent the major feature of an
embodiment of the present invention, and accordingly, serves as,
for example, a packaging material for foodstuffs, drug, and
electronic parts and a member of electronic devices such as liquid
crystal displays, organic EL displays, electronic papers, other
thin-type displays, and solar batteries.
[0098] There are no specific limitations on the method to be used
for forming the inorganic layer for the present invention, and
useful formation methods include, for example, vacuum deposition,
sputtering, ion plating, and CVD. Of these methods, sputtering is
preferable as a method for forming the inorganic layer by a simple,
low-cost process.
[Layer of a Phase in which Zinc Oxide, Silicon Dioxide, and
Aluminum Oxide Coexist.]
[0099] Next, described in detail below is a layer of a phase in
which zinc oxide, silicon dioxide, and aluminum oxide coexist that
serves as a layer [B1] to be used favorably as a silicon-containing
inorganic layer for an embodiment of the present invention.
Hereinafter, the phase in which zinc oxide, silicon dioxide, and
aluminum oxide coexist is sometimes referred to simply as
ZnO--SiO.sub.2--Al.sub.2O.sub.3. In regard to silicon dioxide
(SiO.sub.2), a substance having a composition ratio slightly
differing from that based on the silicon-oxygen ratio in the above
composition formula (between SiO and SiO.sub.2) may result
depending on the production conditions adopted, but such a
substance is herein referred to as silicon dioxide or SiO.sub.2.
For zinc oxide and aluminum oxide as well, such a difference in the
composition ratio from the chemical formula is treated in the same
manner, and they are herein referred to as zinc oxide or ZnO, and
aluminum oxide or Al.sub.2O.sub.3, respectively, regardless of the
differences in their composition ratios that may occur depending on
the production conditions.
[0100] In the phase in which zinc oxide, silicon dioxide, and
aluminum oxide coexist, the coexistence of a crystalline component
contained in the zinc oxide and an amorphous component contained in
the silicon dioxide acts to depress the crystal growth of the zinc
oxide, which tends to form crystallites easily, leading to the
formation of particles with small diameters and, in turn, a dense
layer, which would depress the penetration of oxygen and water
vapor. This is considered to be the reason why the existence of the
layer [B1] serves to allow the gas barrier film according to an
embodiment of the present invention to have improved gas barrier
properties.
[0101] It is also inferred that the coexistence of aluminum oxide
acts to further prevent the crystal growth as compared with the
case of the coexistence of only zinc oxide and silicon dioxide,
thereby depressing the deterioration in gas barrier properties
attributable to the formation of cracks.
[0102] The composition of the layer [B1] can be determined by ICP
emission spectroscopy analysis as described later. The Zn atom
concentration determined by ICP emission spectroscopy analysis is
preferably 20 to 40 atom % for the Zn atom, 5 to 20 atom % for the
Si atom, 0.5 to 5 atom % for the Al atom, and 35 to 70 atom % for
the O atom. If the Zn atom concentration is more than 40 atom % or
if the Si atom concentration is less than 5 atom %, there will be a
lack of oxides that can depress the crystal growth of zinc oxide
and the portions occupied by gaps and defects will increase,
possibly making it difficult to develop gas barrier properties
adequately. If the Zn atom concentration is less than 20 atom % or
if the Si atom concentration is more than 20 atom %, the amorphous
component of silicon dioxide in the layer will account for an
increased proportion, possibly leading to a layer with decreased
flexibility. If the Al atom concentration is more than 5 atom %,
the affinity between zinc oxide and silicon dioxide will be so high
that the film will have an increased hardness, possibly leading to
the formation of cracks under heat or external stress. If the Al
atom concentration is less than 0.5 atom %, the affinity between
zinc oxide and silicon dioxide will not be sufficiently high, and
accordingly, the binding force among the particles forming the
layer will not be increased, possibly leading to decreased
flexibility. If the O atom concentration is more than 70 atom %,
the quantity of defects in the layer [B1] will increase, possibly
leading to a failure to realize required gas barrier properties. If
the O atom concentration is less than 35 atom %, zinc, silicon, and
aluminum will not be in a sufficiently oxidized state, and
accordingly, the crystal growth will not be depressed, leading to
particles with large diameters and possibly resulting in
insufficient gas barrier properties. In view of these points, the
atom concentration is preferably 25 to 35 atom % for the Zn atom,
10 to 15 atom % for the Si atom, 1 to 3 atom % for the Al atom, and
50 to 64 atom % for the O atom.
[0103] There are no specific limitations on the components of the
layer [B1] as long as zinc oxide, silicon dioxide, and aluminum
oxide are the primary components and in the composition range
specified above, and the layer may contain a metal oxide
containing, for example, Al, Ti, Zr, Sn, In, Nb, Mo, Ta, and Pd.
Here, the term "primary` means that the components account for 60
mass % or more, preferably 80 mass % or more, of all the components
of the layer [B1].
[0104] The layer [B1] has a composition similar to that of the
mixed sintered material used for producing the layer, and
accordingly, the composition of the layer [B1] can be optimized by
using a mixed sintered material having a composition similar to
that of the intended layer.
[0105] For the composition analysis of the layer [B1], quantitative
analysis of each element of zinc, silicon, and aluminum is
performed by ICP emission spectroscopy, thereby determining the
composition ratio of zinc oxide, silicon dioxide, aluminum oxide,
and other inorganic oxides contained. Calculation for the oxygen
atom is carried out on the assumption that the zinc atom, silicon
atom, and aluminum atom exist in the form of zinc oxide (ZnO),
silicon dioxide (SiO.sub.2), and aluminum oxide (Al.sub.2O.sub.3),
respectively. ICP emission spectroscopy analysis can perform
simultaneous multi-element examination based on the luminescence
emission spectrum observed when a specimen is introduced along with
argon gas to a plasma source, and can be applied to composition
analysis. If still another layer is disposed on the layer [B1], ICP
luminescence spectroscopy analysis may be performed after removing
the layer by ion etching or chemical treatment as required.
[0106] There are no specific limitations on the method to be used
to form a layer [B1] on a polymer base, and an appropriate layer
can be produced by vacuum deposition, sputtering, or ion plating of
a mixed sintered material of zinc oxide, silicon dioxide, and
aluminum oxide. In the case where separate materials of zinc oxide,
silicon dioxide, and aluminum oxide are used, zinc oxide, silicon
dioxide, and aluminum oxide are deposited or sputtered
simultaneously from separate deposition sources or sputtering
electrodes to produce a mixed film with an intended composition. Of
these methods, sputtering using a mixed sintered material is
preferably adopted for forming the layer [B1] for the present
invention from the viewpoint of the gas barrier properties and the
composition reproducibility for the layer to be formed.
[Layer of a Phase in which Zinc Sulfide and Silicon Dioxide
Coexist.]
[0107] Next, a layer of a phase in which zinc sulfide and silicon
dioxide coexist that acts as layer [B2] is described in detail
below. Hereinafter, the layer of a phase in which zinc sulfide and
silicon dioxide coexist is occasionally referred to ZnS--SiO.sub.2.
In regard to silicon dioxide (SiO.sub.2), furthermore, a substance
having a composition ratio slightly differing from that based on
the silicon-oxygen ratio in the above composition formula will also
be referred to as silicon dioxide or SiO.sub.2 regardless of the
difference, as in the case of the layer [B1].
[0108] In the phase in which zinc sulfide and silicon dioxide
coexist, the coexistence of a crystalline component contained in
the zinc sulfide and an amorphous component contained in the
silicon dioxide acts to depress the crystal growth of the zinc
sulfide, which tends to form crystallites easily, leading to the
formation of particles with small diameters and, in turn, a dense
layer, which would depress the penetration of oxygen and water
vapor. This is considered to be the reason why the existence of the
layer [B2] serves to allow the gas barrier film according to an
embodiment of the present invention to have improved gas barrier
properties. It is also considered that the coexisting zinc sulfide
and silicon dioxide phase containing a zinc sulfide component with
a depressed crystal growth rate is higher in flexibility than a
layer composed only of an inorganic oxide or metal oxide and less
liable to cracks under heat or external stress, thus allowing the
layer [B2] to serve to depress the deterioration in gas barrier
properties that is attributed to the formation of cracks.
[0109] In regard to the layer [B2], zinc sulfide accounts for a
mole fraction of 0.7 to 0.9 of the total quantity of zinc sulfide
and silicon dioxide. If zinc sulfide accounts for a mole fraction
of more than 0.9 of the total quantity of zinc sulfide and silicon
dioxide, there will be a lack of oxides that can depress the
crystal growth of zinc sulfide and the portions occupied by gaps
and defects will increase, possibly making it difficult to develop
required gas barrier properties. If zinc sulfide accounts for a
mole fraction of less than 0.7 of the total quantity of zinc
sulfide and silicon dioxide, the quantity of the amorphous
component of silicon dioxide in the layer [B2] will increase and
the layer will decrease in flexibility, possibly leading to a gas
barrier film with decreased flexibility under mechanical bending.
It is more preferably in the range of 0.75 to 0.85.
[0110] There are no specific limitations on the components of the
layer [B2] as long as zinc sulfide and silicon dioxide are the
primary components and in the composition range specified above,
and the layer may contain a metal oxide of, for example, Al, Ti,
Zr, Sn, In, Nb, Mo, Ta, and Pd. Here, the term "primary` means that
the components account for 60 mass % or more, preferably 80 mass %
or more, of all the components of the layer [B2].
[0111] The layer [B2] has a composition similar to that of the
mixed sintered material used for producing the layer, and
accordingly, the composition of the layer [B2] can be optimized by
using a mixed sintered material having a composition that meets the
objective.
[0112] Composition analysis of the layer [B2] can be carried out by
first determining the contents of zinc and silicon by ICP emission
spectroscopy, and applying the results to quantitative analysis of
each element by the Rutherford backscattering technique to
determine the contents of zinc sulfide, silicon dioxide, and other
inorganic oxides contained. ICP emission spectroscopy analysis can
perform simultaneous multi-element examination based on the
luminescence emission spectrum observed when a specimen is
introduced along with argon gas to a plasma source, and can be
applied to composition analysis. Furthermore, the Rutherford
backscattering technique can accelerate charged particles at a high
voltage, apply them to a specimen, and identify the species and
determine the quantities of the elements involved from the number
and energy of the charged particles rebounded from the specimen,
thereby determining the content of each element. Here, since the
layer [B2] is a composite layer of a sulfide and oxide, it is
necessary to perform analysis by the Rutherford backscattering
technique which can analyze the contents of sulfur and oxygen. If
still another layer is disposed on the layer [B2], analysis by ICP
luminescence spectroscopy and the Rutherford backscattering
technique may be performed after removing the layer by ion etching
or chemical treatment as required.
[0113] There are no specific limitations on the method to be used
to form a layer [B2] on a polymer base, and an appropriate layer
can be produced by vacuum deposition, sputtering, or ion plating of
a mixed sintered material of zinc sulfide and silicon dioxide. In
the case where separate materials of zinc sulfide and silicon
dioxide are used, zinc sulfide and silicon dioxide are deposited or
sputtered simultaneously from separate deposition sources or
sputtering electrodes to produce a mixed film with an intended
composition. Of these methods, sputtering using a mixed sintered
material is preferably adopted for forming the layer [B2] for the
present invention from the viewpoint of the gas barrier properties
and the composition reproducibility for the layer to be formed.
[0114] Having high gas barrier properties for oxygen gas and water
vapor, the gas barrier film according to the present invention can
serve as a sealing member of devices such as liquid crystal
displays, organic EL displays, electronic papers, and solar
batteries. Applying the gas barrier film according to the present
invention to devices that require higher gas barrier properties
serves to provide displays, lighting apparatuses, and solar
batteries with higher performance. Those displays to which the gas
barrier film according to the present invention can be applied
include, for example, organic EL displays and liquid crystal
displays. Those lighting apparatuses to which the gas barrier film
according to the present invention can be applied include, for
example, organic EL lighting apparatuses. Those solar batteries to
which the gas barrier film according to the present invention can
be applied include, for example, thin film silicon solar batteries,
thin film compound semiconductor solar batteries, and organic thin
film solar batteries. Furthermore, the gas barrier film according
to the present invention can also serves as packaging material for
foodstuffs and drugs.
EXAMPLES
[0115] An embodiment of the invention is described specifically
below with reference to Examples. It should be noted that the
present invention should not be construed as limited to the
Examples given below.
[Evaluation Methods]
[1] Evaluation of Acrylic Resin
(1) Heating Residue (in Mass %)
[0116] The heating residue of acrylic resin was measured according
to JIS K 5407 (1997) for specimens heated at 140.degree. C. for 60
minutes. Two specimens were sampled for each test item and their
average was taken as the representative value.
(2) Acid Value (in mgKOH)
[0117] The acid value of acrylic resin was measured according to
JIS K 5407 (1997). Two specimens were sampled for each test item
and their average was taken as the representative value.
(3) Hydroxyl Value (in mgKOH)
[0118] The hydroxyl value of a structural portion originating from
an acrylic monomer of acrylic resin (simply referred to as hydroxyl
value of acrylic resin) was calculated by the following formula
based on the proportions of the fed materials.
Hydroxyl value of acrylic resin=proportion of 2-hydroxyethyl
methacrylate in acrylic monomer (mass %)/130.times.561
(4) Molecular Weight
[0119] The mass average molecular weight (hereinafter referred to
as Mw), number average molecular weight (hereinafter referred to as
Mn), and molecular weight distribution (hereinafter referred to as
d) (Mw/Mn) of an acrylic resin was measured using a HLC-8220 GPC
system manufactured by Tosoh Corporation with a TSKge1 G1000HXL or
G2000HXL preparative column manufactured by Tosoh Corporation. The
carrier used was tetrahydrofuran (THF) and the molecular weight
standard used was a polystyrene standard. A small amount of the
reaction solution was sampled after the completion of
polymerization and diluted with THF before measurement.
(5) Glass Transition Temperature (Tg) (.degree. C.)
[0120] The glass transition temperature of a structural portion
originating from an acrylic monomer of acrylic resin (simply
referred to as glass transition temperature of acrylic resin) (Tg)
(.degree. C.) was calculated by the following formula based on the
proportions of the fed materials.
Tg (.degree. C.) of acrylic resin=1/{(proportion (mass fraction) of
methacrylic acid in acrylic monomer/Tg (=403.degree. K) of
polymethacrylic acid)+(proportion (mass fraction) of 2-hydroxyethyl
methacrylate in acrylic monomer/Tg (=328.degree. K) of
poly2-hydroxyethyl methacrylate)+(proportion (mass fraction) of
methyl methacrylate in acrylic monomer/Tg (=378.degree. K) of
polymethyl methacrylate)+(proportion (mass fraction) of
dicyclopentanyl methacrylate in acrylic monomer/Tg (=448.degree. K)
of polydicyclopentanyl methacrylate)}-273
[2] Evaluation of Laminate Composed of Polymer Base and Undercoat
Layer
(6) Adhesion Between Polymer Base and Undercoat Layer
[0121] A laminate structure produced by forming an undercoat layer
on a polymer base is examined according to JIS K 5400 (1997) to
evaluate the adhesion between the polymer base and the undercoat
layer. The adhesion was ranked as good or (A) in the case where 100
squares of a total of 100 squares under test remained unremoved. It
was ranked as (B) when even one square was removed.
(7) Total Light Transmittance and Haze
[0122] Light was incident on the polymer base and evaluation was
carried out using a NDH2000 turbidity meter manufactured by Nippon
Denshoku Industries Co., Ltd. according to JIS K 7361 (1997). For
the total light transmittance evaluation, a specimen was ranked as
good (A) when it was 87% or more, and (B) when it was smaller. For
the haze evaluation, a specimen was ranked as good (A) when it was
smaller than 1%, and (B) when it was 1% or larger.
(8) Surface Free Energy
[0123] To evaluate the surface of the undercoat layer, four
measuring liquids (water, formamide, ethylene glycol, and methylene
iodide) with a known surface free energy and known component forces
(dispersion force, polar force, and hydrogen bonding force) were
adopted to determine the contact angle of each measuring liquid on
the layered film at a temperature of 23.degree. C. and relative
humidity of 65% using a CA-D contact angle gauge (manufactured by
Kyowa Interface Science Co., Ltd.). Five measurements were made for
each test and their average was used. The value was applied to the
following formula, which is derived from the extended Fowkes'
equation and Young's equation, to calculate each component
force.
[Formula 2]
(.gamma.Sd.gamma.Ld).sup.0.5+(.gamma.Sp.gamma.Lp).sup.0.5+(.gamma.Sh.gam-
ma.Lh).sup.0.5=.gamma.L(1+cos .theta.)/2 (1)
where [0124] .gamma.S=.gamma.Sd+.gamma.Sp+.gamma.Sh [0125]
.gamma.L=.gamma.Ld+.gamma.Lp+.gamma. Lh [0126] .gamma.S: surface
energy of undercoat layer [0127] .gamma.Sd: dispersion force
component of undercoat layer [0128] .gamma.Sp: polar force
component of undercoat layer [0129] .gamma.Sh: hydrogen bonding
force component of undercoat layer [0130] .gamma.L: surface energy
of measuring liquid [0131] .gamma.Ld: dispersion force component
[0132] .gamma.Lp: polar force component [0133] .gamma.Lh: hydrogen
bonding force component [0134] .theta.: contact angle of measuring
liquid on undercoat layer
[3] Evaluation of Gas Barrier Film
(9) Adhesion Between Undercoat Layer and Inorganic Layer
[0135] The adhesion was evaluated by examining the surface of the
inorganic layer in a gas barrier film specimen according to JIS K
5400 (1997). The adhesion was judged to be good or ranked as (A) in
the case where 100 squares of a total of 100 squares under test
remained unremoved. It was ranked as (B) when even one square was
removed.
(10) Water Vapor Permeability
[0136] Evaluation of gas barrier film was carried out by using a
water vapor transmission rate measuring machine (Deltaperm
(registered trademark)) manufactured by Technolox, U.K., under the
conditions of a temperature of 40.degree. C., humidity of 90% RH,
and measuring area of 50 cm.sup.2. Two specimens were sampled for
each test, and five measurements were made for each specimen,
followed by averaging the 10 measurements obtained to represent the
water vapor transmittance.
(11) Thickness of Layer
[0137] Specimens for cross-sectional observation were prepared by
the FIB technique using Microsampling System (FB-2000A,
manufactured by Hitachi, Ltd.) (specifically, according to the
procedure described in "Kobunshi Hyomen Kako" (Polymer Surface
Processing)", Satoru Iwamori, pp. 118-119. A transmission electron
microscope (H-9000UHRII, manufactured by Hitachi, Ltd.) was used at
an accelerating voltage of 300 kV and the cross section of a
specimen prepared for observation was examined to determine the
thickness of the inorganic layer. The interfaces between the base
material and inorganic layer and between the undercoat layer and
inorganic layer were identified from cross-sectional observation
photographs taken by transmission electron microscopy.
(12) Composition of Layer [B1]
[0138] The composition of a layer [B1] analyzed by ICP emission
spectroscopy (SPS4000, manufactured by SII NanoTechnology Inc.).
The contents of the zinc atom, silicon atom, and aluminum atom in a
specimen were measured, and converted to the ratio in the number of
atoms. Calculation for the oxygen atom was carried out on the
assumption that the zinc atom, silicon atom, and aluminum atom
exist in the form of zinc oxide (ZnO), silicon dioxide (SiO.sub.2),
and aluminum oxide (Al.sub.2O.sub.3), respectively.
(13) Surface Roughness Ra of Inorganic Layer
[0139] The surface roughness Ra of an inorganic layer was measured
three times by atomic force microscopy under the following
conditions, and the specimen was ranked as good or (A) when the
average was 2 nm or less and (B) when it was larger.
System: NanoScopeIII/MMAFM (manufactured by Digital
Instruments)
Scanner: AS-130 (J-Scanner)
[0140] Probe: NCH-W single crystal silicon (manufactured by
Nanoworld) Scanning mode: tapping mode Scanning range: 1
.mu.m.times.1 .mu.m Scanning speed: 0.5 Hz Measuring environment:
atmosphere with temperature of 23.degree. C. and relative humidity
of 65%
Example 1
Production of Acrylic Resin
[0141] First, 95.0 g of toluene, 45.0 g of methyl isobutyl ketone,
and 5 g of a polymethyl methacrylate macromonomer (Macromonomer
AA-6, manufactured by Toagosei Co., Ltd., number average molecular
weight 6,000), which was used as macromonomer (A), were fed to a
500 mL flask equipped with a stirrer, capacitor, nitrogen gas
supply nozzle, heating/cooling device, and thermometer. The
temperature was raised to 85.degree. C. while continuing the supply
of nitrogen gas.
[0142] A mixture of an acrylic monomer, polymerization initiator
(a), and chain transfer agent (b) prepared in advance by weighing
out and mixing 1.0 g of methacrylic acid, 8.0 g. of 2-hydroxyethyl
methacrylate, 91.0 g of methyl methacrylate, 1.5 g of
2,2'-azobisisobutyronitrile, and 0.5 g of n-dodecyl mercaptan was
supplied to the flask by constant-rate dropping continued for 3
hours.
[0143] After the completion of the dropping, polymerization was
carried out for one hour, followed by adding a solution of a
polymerization initiator (c) (5.0 g of toluene and 0.05 g of
2,2'-azobisisobutyronitrile). After leaving it to stand for 30
minutes, a solution of a polymerization initiator (d) (5.0 g of
toluene and 0.05 g of 2,2'-azobisisobutyronitrile) was added.
[0144] After the addition, stirring was continued for one hour
while maintaining a warm temperature, followed cooling to room
temperature to provide a solution of acrylic resin (AA-1).
[0145] The acrylic resin AA-1 had a heating residue of 40.2 mass %,
acid value of 6.5 mgKOH, hydroxyl value of 34.5 mgKOH, mass average
molecular weight of 23,900, number average molecular weight of
14,500, molecular weight distribution of 1.65, and glass transition
temperature of 82.degree. C.
[0146] Details including composition, production method, and major
characteristics are shown in Table 1.
TABLE-US-00001 TABLE 1 Example 1 Example 2 Example 3 Example 4
Example 5 Acrylic resin A.sub.A-1 A.sub.A-2 A.sub.A-3 A.sub.A-4
A.sub.A-5 Organic solvent toluene (g) 95.0 95.0 95.0 95.0 95.0
ethyl acetate (g) 45.0 45.0 45.0 45.0 45.0 Macromonomer
macromonomer (A) (g) 5.0 5.0 5.0 5.0 12.0 macromonomer (Si) (g) 0.0
0.0 0.0 0.0 0.0 macromonomer (F) (g) 0.0 0.0 0.0 0.0 0.0
macromonomer (St) (g) 0.0 0.0 0.0 0.0 0.0 Acrylic methacrylic acid
(g) 1.0 1.0 1.0 1.0 1.0 monomer 2-hydroxyethyl methacrylate (g) 8.0
8.0 8.0 8.0 8.0 methyl methacrylate (g) 91.0 0.0 45.5 91.0 91.0
dicyclopentanyl methacrylate (g) 0.0 91.0 45.5 0.0 0.0 total for
acrylic monomers (g) 100.0 100.0 100.0 100.0 100.0 Total for
monomers (g) 105.0 105.0 105.0 105.0 112.0 Polymerization
2,2'-azobisisobutyronitrile (g) 1.5 1.5 1.5 1.5 1.7 initiator (a)
Chain transfer n-dodecyl mercaptan (g) 0.5 0.5 0.5 0.5 0.6 agent
(b) Solution of toluene (g) 5.0 5.0 5.0 5.0 5.6 polymerization
2,2'-azobisisobutyronitrile (g) 0.05 0.05 0.05 0.05 0.06 initiator
(c) Solution of toluene (g) 5.0 5.0 5.0 5.0 5.6 polymerization
2,2'-azobisisobutyronitrile (g) 0.05 0.05 0.05 0.05 0.06 initiator
(d) Total (g) 257.1 257.1 257.1 257.1 265.6 Evaluation heating
residue (mass %) 40.2 40.2 40.2 40.2 40.3 results acid value
(mgKOH) 6.5 6.5 6.5 6.5 6.5 hydroxyl value (mgKOH) 34.5 34.5 34.5
34.5 34.5 molecular mass average molecular -- 23900 18900 18900
23900 21800 weight weight number average molecular -- 14500 11500
11500 14500 12000 weight molecular weight distribution -- 1.65 1.64
1.64 1.65 1.82 glass transition temperature (.degree. C.) 82 141
109 82 56 Example 6 Example 7 Example 8 Example 9 Acrylic resin
A.sub.A-6 A.sub.A-7 A.sub.A-8 A.sub.A-9 Organic solvent toluene (g)
95.0 95.0 95.0 95.0 ethyl acetate (g) 45.0 45.0 45.0 45.0
Macromonomer macromonomer (A) (g) 10.0 12.0 5.0 5.0 macromonomer
(Si) (g) 0.0 0.0 0.0 0.0 macromonomer (F) (g) 0.0 0.0 0.0 0.0
macromonomer (St) (g) 0.0 0.0 0.0 0.0 Acrylic methacrylic acid (g)
0.0 12.0 1.0 1.0 monomer 2-hydroxyethyl methacrylate (g) 8.0 8.0
0.0 24.0 methyl methacrylate (g) 91.0 91.0 91.0 91.0
dicyclopentanyl methacrylate (g) 0.0 0.0 0.0 0.0 total for acrylic
monomers (g) 99.0 111.0 92.0 116.0 Total for monomers (g) 109.0
123.0 97.0 121.0 Polymerization 2,2'-azobisisobutyronitrile (g) 1.6
1.8 1.5 1.5 initiator (a) Chain transfer n-dodecyl mercaptan (g)
0.5 0.6 0.5 0.6 agent (b) Solution of toluene (g) 5.5 6.2 5.0 5.0
polymerization 2,2'-azobisisobutyronitrile (g) 0.05 0.06 0.05 0.06
initiator (c) Solution of toluene (g) 5.5 6.2 5.0 5.0
polymerization 2,2'-azobisisobutyronitrile (g) 0.05 0.06 0.05 0.06
initiator (d) Total (g) 262.2 277.9 249.1 273.2 Evaluation heating
residue (mass %) 40.3 40.2 40.1 40.6 results acid value (mgKOH) 0.0
78.3 6.5 6.5 hydroxyl value (mgKOH) 34.5 34.5 0.0 103.6 molecular
mass average molecular -- 22600 23100 19600 22900 weight weight
number average molecular -- 12300 12500 10600 12200 weight
molecular weight distribution -- 1.84 1.85 1.85 1.88 glass
transition temperature (.degree. C.) 66 29 118 28
[Formation of Undercoat Layer]
[0147] A mixture is produced by mixing 100 g of the acrylic resin
(AA-1) solution, 19 g of a polyester diol (Flexorez XP-171-90,
manufactured by King Industries, Inc.) as a modifier polymer, and
xylene diisocyanate in an amount intended to adjust the NCO index
to 1.0 and diluting it with 75.2 g of methyl ethyl ketone, 75.2 g
of ethyl acetate, 16.6 g of cyclohexanone, 1.2 g of triethyl
orthoacetate, and 1.2 g of ethanol to prepare an acrylic resin
coating liquid. The polymer base used was a polyethylene
terephthalate film (Lumirror (registered trademark) U48,
manufactured by Toray Industries, Inc.) with a thickness of 100
.mu.m, and one of its surfaces was coated with the acrylic resin
coating liquid with a Micro Gravure coater (gravure cell count
200UR, gravure rotation ratio 100%), dried at 120.degree. C. for
two minutes, and cured at 40.degree. C. for one week to form an
undercoat layer with a thickness of 3 .mu.m, thereby providing an
undercoated laminate (a structure consisting of a polymer base
coated with acrylic resin).
[0148] Table 2 shows details of a laminate (JA-1) produced by
forming an undercoat layer on a polymer base.
TABLE-US-00002 TABLE 2 Exam- Exam- Exam- ple 1 ple 2 ple 3 Example
4 Example 5 Example 6 Example 7 Example 8 Example 9 Layered product
composed of J.sub.A-1 J.sub.A-2 J.sub.A-3 J.sub.A-4 J.sub.A-5
J.sub.A-6 J.sub.A-7 J.sub.A-8 J.sub.A-9 polymer base and undercoat
layer Thickness of polyethylene terephthalate (.mu.m) 100 100 100
100 100 100 100 100 100 film Type of acrylic resin A.sub.A-1
A.sub.A-2 A.sub.A-3 A.sub.A-4 A.sub.A-5 A.sub.A-6 A.sub.A-7
A.sub.A-8 A.sub.A-9 Thickness of acrylic resin (.mu.m) 3 3 3 3 3 3
3 3 3 Evaluation adhesion between polymer -- A A A A A B A B B
results base and undercoat layer total light transmittance -- A A A
A B A B B B haze -- A A A A B A B B B surface free energy (mN/m)
42.9 38.8 40.1 42.9 41.6 42.0 43.3 40.5 46.3
[Production of Inorganic Layer (Layer [B1])]
[0149] A wind-up type sputtering apparatus having a structure as
illustrating FIG. 2 was set up, and a sputtering target, that is, a
mixed sintered material formed of zinc oxide, silicon dioxide, and
aluminum oxide, was installed on a sputtering electrode 12 and
sputtered on the surface of the undercoat layer of the laminate 4,
which was composed of a polymer base and an undercoat layer formed
thereon, using argon gas and oxygen gas to produce an inorganic
layer [B1].
[0150] Concrete operations were as described below. First, in a
wind-up chamber 6 of a wind-up type sputtering apparatus 5
containing a sputtering electrode 12 carrying a sputtering target
composed of zinc oxide, silicon dioxide, and aluminum oxide
sintered at a mass composition ratio of 77:20:3, the laminate 4,
which was composed of a polymer base and an undercoat layer formed
thereon, was set on an unwinding roll 7 in such a manner that the
surface to be provided with a layer [B1] faced the sputtering
electrode 12 and that the film was allowed to travel on the guide
rolls 8, 9, and 10 in the unwinding zone before reaching a cooling
drum 11. Argon gas and oxygen gas, with an oxygen gas partial
pressure of 10%, were introduced so that the degree of vacuum would
be 2.times.10.sup.-1 Pa, and a power of 4,000 W was applied by a
direct current power source to generate argon-oxygen gas plasma,
thereby producing a layer [B1] by sputtering on the surface of the
laminate 4, which was composed of a polymer base and an undercoat
layer formed thereon. The thickness was adjusted by controlling the
film conveyance speed. Subsequently, the film was wound up on a
wind-up roll 16 after travelling on guide rolls 13, 14, and 15 in
the winding-up zone, thereby providing a gas barrier film
(F.sub.A-1).
[0151] Table 3 shows details of the gas barrier film.
TABLE-US-00003 TABLE 3 Example 1 Example 2 Example 3 Example 4
Example 5 Example 6 Example 7 Example 8 Example 9 Gas barrier
properties film F.sub.A-1 F.sub.A-2 F.sub.A-3 F.sub.A-4 F.sub.A-5
F.sub.A-6 F.sub.A-7 F.sub.A-8 F.sub.A-9 Layered product composed of
J.sub.A-1 J.sub.A-2 J.sub.A-3 J.sub.A-4 J.sub.A-5 J.sub.A-6
J.sub.A-7 J.sub.A-8 J.sub.A-9 polymer base and undercoat layer Type
of inorganic layer -- [B1] [B1] [B1] [B2] [B1] [B1] [B1] [B1] [B1]
Thickness of inorganic layer (nm) 100 100 100 100 100 100 100 100
100 Surface roughness Ra of -- A A A A B B B B B inorganic layer
Evaluation adhesion between -- A A A A A A A A A results undercoat
layer and inorganic layer water vapor (g/m.sup.2/ 7.2 .times.
10.sup.-3 5.7 .times. 10.sup.-3 5.9 .times. 10.sup.-3 9.5 .times.
10.sup.-3 6.3 .times. 10.sup.-2 6.8 .times. 10.sup.-2 6.1 .times.
10.sup.-2 7.7 .times. 10.sup.-2 8.2 .times. 10.sup.-2 transmittance
day)
[0152] Table 4 shows results of composition analysis of the layer
[B1] obtained in Example 1.
TABLE-US-00004 TABLE 4 Proportion in number of atoms (atom %)
Inorganic layer Zn Si Al O Example 1 [B1] layer 27.5 13.1 2.3
57.1
Examples 2 to 9
[0153] Except for using each of the compositions given in Table 1,
the same procedure as in Example 1 was carried out to prepare an
acrylic resin (A.sub.A-2 to A.sub.A-9), form an undercoat layer on
a polymer base (laminates J.sub.A-2 to J.sub.A-9 composed of a
polymer base and an undercoat layer), and form an inorganic layer
on the undercoat layer, thereby producing a gas barrier film
(F.sub.A-2 to F.sub.A-9). The inorganic layer formed was a layer
[B1] except in Example 4, and a layer [B2] was formed in Example 4
by the following procedure instead of forming a layer [B1].
(Formation of Layer [B2])
[0154] A wind-up type sputtering apparatus having a structure as
illustrating FIG. 2 was set up, and a sputtering target, that is, a
mixed sintered material formed of zinc sulfide and silicon dioxide
was installed on a sputtering electrode 12 and sputtered on the
surface of the undercoat layer of the undercoated laminate 4 using
argon gas plasma to produce a layer [B2].
[0155] Concrete operations were as described below. First, in a
wind-up chamber 6 of a wind-up type sputtering apparatus 5
containing a sputtering electrode 12 carrying a sputtering target
composed of zinc sulfide and silicon dioxide sintered at a molar
composition ratio of 80:20, the laminate 4, which was composed of a
polymer base and an undercoat layer formed thereon, was set on an
unwinding roll 7 in such a manner that the film would travel on the
guide rolls 8, 9, and 10 in the unwinding zone before reaching a
cooling drum 11. Argon gas was introduced so that the degree of
vacuum would be 2.times.10.sup.-1 Pa, and a power of 500 W was
applied by a high frequency power source to generate argon gas
plasma, thereby producing a layer [B2] by sputtering on the surface
of the laminate 4, which was composed of a polymer base and an
undercoat layer formed thereon. The thickness was adjusted by
controlling the film conveyance speed. Subsequently, the film was
wound up on a wind-up roll 16 after travelling on guide rolls 13,
14, and 15 in the winding-up zone, thereby providing a gas barrier
film (F.sub.A-4).
Examples 11 to 20
[0156] Except for using each of the compositions given in Table 5,
the same procedure as in Example 1 was carried out to produce an
acrylic resin (A.sub.Si-1 to A.sub.Si-4, A.sub.F-5, A.sub.Si-6 to
9, and A.sub.Si--F-10). Here, the macromonomer used in Examples 11
to 14 and Examples 16 to 19 was a macromonomer (Si) (Macromonomer
AK-32, manufactured by Toagosei Co., Ltd., number average molecular
weight 6,000), and the macromonomer (F) used in Example 15 was
synthesized from V-8FM (manufactured by Osaka Organic Chemical
Industry Ltd. industry, number average molecular weight 6,000)
employed as input material according to the method described in
Japanese Unexamined Patent Publication (Kokai) No. HEI-10-120738.
For Example 20, furthermore, a resin was synthesized according to
the method described in Japanese Unexamined Patent Publication
(Kokai) No. HEI-10-120738 from the macromonomer (Si) and the
macromonomer (F) mixed at a compounding ratio given Table 5.
Details including composition, production method, and major
characteristics are shown in Table 5.
TABLE-US-00005 TABLE 5 Example Example Example Example Example 11
12 13 14 15 Acrylic resin Asi-1 Asi-2 Asi-3 Asi-4 A.sub.F-5 Organic
toluene (g) 95.0 95.0 95.0 95.0 95.0 solvent ethyl acetate (g) 45.0
45.0 45.0 45.0 45.0 Macromonomer macromonomer (A) (g) 0.0 0.0 0.0
0.0 0.0 macromonomer (Si) (g) 5.0 5.0 5.0 5.0 0.0 macromonomer (F)
(g) 0.0 0.0 0.0 0.0 5.0 macromonomer (St) (g) 0.0 0.0 0.0 0.0 0.0
Acrylic methacrylic acid (g) 1.0 1.0 1.0 1.0 1.0 monomer
2-hydroxyethyl methacrylate (g) 8.0 8.0 8.0 8.0 8.0 methyl
methacrylate (g) 91.0 0.0 45.5 91.0 91.0 dicyclopentanyl
methacrylate (g) 0.0 91.0 45.5 0.0 0.0 total for acrylic monomers
(g) 100.0 100.0 100.0 100.0 100.0 Total for monomers (g) 105.0
105.0 105.0 105.0 105.0 Polymerization 2,2'-azobisisobutyronitrile
(g) 1.5 1.5 1.5 1.5 1.5 initiator (a) Chain transfer n-dodecyl
mercaptan (g) 0.5 0.5 0.5 0.5 0.5 agent (b) Solution of toluene (g)
5.0 0.0 1.0 2.0 3.0 polymerization 2,2'-azobisisobutyronitrile (g)
0.05 0.05 0.05 0.05 0.05 initiator (c) Solution of toluene (g) 5.0
5.0 5.0 5.0 5.0 polymerization 2,2'-azobisisobutyronitrile (g) 0.05
0.05 0.05 0.05 0.05 initiator (d) Total (g) 257.1 252.1 253.1 254.1
255.1 Evaluation heating residue (mass %) 40.0 40.0 40.0 40.0 40.0
results acid value (mgKOH) 6.5 6.5 6.5 6.5 6.5 hydroxyl value
(mgKOH) 34.5 34.5 34.5 34.5 34.5 molecular mass average -- 24400
18900 18900 24400 22400 weight molecular weight number average --
15800 11500 11500 16500 14700 molecular weight molecular weight --
1.54 1.64 1.64 1.48 1.52 distribution glass transition temperature
(.degree. C.) 101 162 129 101 101 Example Example Example Example
Example 16 17 18 19 20 Acrylic resin Asi-6 Asi-7 Asi-8 Asi-9
A.sub.si--F-10 Organic toluene (g) 95.0 95.0 95.0 95.0 95.0 solvent
ethyl acetate (g) 45.0 45.0 45.0 45.0 45.0 Macromonomer
macromonomer (A) (g) 0.0 0.0 0.0 0.0 0.0 macromonomer (Si) (g) 12.0
5.0 5.0 5.0 2.5 macromonomer (F) (g) 0.0 0.0 0.0 0.0 2.5
macromonomer (St) (g) 0.0 0.0 0.0 0.0 0.0 Acrylic methacrylic acid
(g) 1.0 12.0 1.0 1.0 1.0 monomer 2-hydroxyethyl methacrylate (g)
8.0 8.0 0.0 24.0 8.0 methyl methacrylate (g) 91.0 91.0 91.0 91.0
91.0 dicyclopentanyl methacrylate (g) 0.0 0.0 0.0 0.0 0.0 total for
acrylic monomers (g) 100.0 111.0 92.0 116.0 100.0 Total for
monomers (g) 112.0 116.0 97.0 121.0 105.0 Polymerization
2,2'-azobisisobutyronitrile (g) 1.7 1.7 1.5 1.5 1.5 initiator (a)
Chain transfer n-dodecyl mercaptan (g) 0.6 0.6 0.5 0.6 0.5 agent
(b) Solution of toluene (g) 5.6 5.8 5.0 5.0 5.0 polymerization
2,2'-azobisisobutyronitrile (g) 0.06 0.06 0.05 0.06 0.05 initiator
(c) Solution of toluene (g) 5.6 5.8 5.0 5.0 5.0 polymerization
2,2'-azobisisobutyronitrile (g) 0.06 0.06 0.05 0.06 0.05 initiator
(d) Total (g) 265.6 270.0 249.1 273.2 257.1 Evaluation heating
residue (mass %) 40.0 40.0 40.0 40.0 40.0 results acid value
(mgKOH) 6.5 78.3 6.5 6.5 6.5 hydroxyl value (mgKOH) 34.5 34.5 0.0
103.6 34.5 molecular mass average -- 21800 23100 19600 22900 24900
weight molecular weight number average -- 12000 12500 10600 12200
16300 molecular weight molecular weight -- 1.82 1.85 1.85 1.88 1.52
distribution glass transition temperature (.degree. C.) 101 70 139
43 101
[0157] Subsequently, laminates (J.sub.Si-1 to 4, J.sub.F-5,
J.sub.51-6 to 9, and J.sub.Si--F-10), each composed of a polymer
base and an undercoat layer formed thereon, were produced. Details
are given in Table 6.
TABLE-US-00006 TABLE 6 Exam- Exam- Exam- Exam- Exam- Exam- Exam-
Exam- Example Example ple 11 ple 12 ple 13 ple 14 ple 15 ple 16 ple
17 ple 18 19 20 Layered product composed of J.sub.Si-1 J.sub.Si-2
J.sub.Si-3 J.sub.Si-4 J.sub.F-5 J.sub.Si-6 J.sub.Si-7 J.sub.Si-8
J.sub.Si-9 J.sub.Si--F-10 polymer base and undercoat layer
Polyethylene terephthalate film (.mu.m) 100 100 100 100 100 100 100
100 100 100 with a thickness of Type of acrylic resin Asi-1 Asi-2
Asi-3 Asi-4 A.sub.F-5 Asi-6 Asi-7 Asi-8 Asi-9 A.sub.si--F-10
Thickness of acrylic resin (.mu.m) 3 3 3 3 3 3 3 3 3 3 Evaluation
adhesion between polymer -- A A A A A A A B B A results base and
undercoat layer total light transmittance -- A A A A A B B B B A
haze -- A A A A A B B B B A surface free energy (mN/m) 20.1 15.9
19.2 20.1 23.2 13.2 17.7 16.5 24.0 22.2
[0158] Then, an inorganic layer [B1] was formed by sputtering on
the surface of the undercoat layer of the laminate 4, which was
composed of a polymer base and an undercoat layer formed thereon,
according to the same procedure as in Example 1 to provide a gas
barrier film (F.sub.Si-1 to F.sub.Si-3, F.sub.F-5, F.sub.Si-6 to 9,
and F.sub.Si--F-10). In Example 14, the same procedure as in
Example 4 was carried to form a layer [B2], instead of forming a
layer [B1], to provide a gas barrier film (F.sub.Si-4).
[0159] Table 7 shows details of the gas barrier film.
TABLE-US-00007 TABLE 7 Exam- Exam- Exam- Exam- Exam- Example
Example Example Example Example ple 11 ple 12 ple 13 ple 14 ple 15
16 17 18 19 20 Gas barrier properties film F.sub.Si-1 F.sub.Si-2
F.sub.Si-3 F.sub.Si-4 F.sub.F-5 F.sub.Si-6 F.sub.Si-7 F.sub.Si-8
F.sub.Si-9 F.sub.Si--F-10 Layered product composed of J.sub.Si-1
J.sub.Si-2 J.sub.Si-3 J.sub.Si-4 J.sub.F-5 J.sub.Si-6 J.sub.Si-7
J.sub.Si-8 J.sub.Si-9 J.sub.Si--F-10 polymer base and undercoat
layer Type of inorganic layer -- [B1] [B1] [B1] [B2] [B1] [B1] [B1]
[B1] [B1] [B1] Thickness of inorganic layer (nm) 100 100 100 100
100 100 100 100 100 100 Surface roughness Ra of -- A A A A A B B B
B A inorganic layer Evaluation adhesion between -- A A A A A B A A
A A results undercoat layer and inorganic layer water vapor
(g/m.sup.2/ 4.1 .times. 7.2 .times. 5.5 .times. 7.6 .times. 6.2
.times. 2.8 .times. 10.sup.-2 4.4 .times. 10.sup.-2 3.8 .times.
10.sup.-2 6.5 .times. 10.sup.-2 6.8 .times. 10.sup.-3 transmittance
day) 10.sup.-3 10.sup.-3 10.sup.-3 10.sup.-3 10.sup.-3
[0160] In addition, Table 8 shows results of composition analysis
of the layer [B1] obtained in Example 11.
TABLE-US-00008 TABLE 8 Proportion in number of atoms (atom %)
Inorganic layer Zn Si Al O Example 11 [B1] layer 26.5 14.4 2.1
57.0
Examples 21 to 26
[0161] Except for using each of the compositions given in Table 9,
the same procedure as in Example 1 was carried out to produce an
acrylic resin (A.sub.A-Si-1 to A.sub.A-Si-3, A.sub.A-F-4,
A.sub.A-Si--F-5, and A.sub.A-Si-6). Here, the macromonomer (F) used
in Examples 24 and 25 was synthesized from V-8FM (manufactured by
Osaka Organic Chemical Industry Ltd. industry, number average
molecular weight 6,000) employed as input material according to the
method described in Japanese Unexamined Patent Publication (Kokai)
No. HEI-10-120738. Details including composition, production
method, and major characteristics are shown in Table 9.
TABLE-US-00009 TABLE 9 Example Example Example Example Example
Example 21 22 23 24 25 26 Acrylic resin A.sub.A-Si-1 A.sub.A-Si-2
A.sub.A-Si-3 A.sub.A-F-4 A.sub.A-Si--F-5 A.sub.A-Si-6 Organic
toluene (g) 95.0 95.0 95.0 95.0 95.0 95.0 solvent ethyl acetate (g)
45.0 45.0 45.0 45.0 45.0 45.0 Macromonomer macromonomer (A) (g) 2.0
2.0 2.0 2.0 1.0 2.0 macromonomer (Si) (g) 3.0 3.0 3.0 0.0 2.0 3.0
macromonomer (F) (g) 0.0 0.0 0.0 3.0 2.0 0.0 macromonomer (St) (g)
0.0 0.0 0.0 0.0 0.0 0.0 Acrylic methacrylic acid (g) 1.0 1.0 1.0
1.0 1.0 1.0 monomer 2-hydroxyethyl methacrylate (g) 8.0 8.0 8.0 8.0
8.0 8.0 methyl methacrylate (g) 91.0 0.0 45.5 91.0 91.0 91.0
dicyclopentanyl methacrylate (g) 0.0 91.0 45.5 0.0 0.0 0.0 total
for acrylic monomers (g) 100.0 100.0 100.0 100.0 100.0 100.0 Total
for monomers (g) 105.0 105.0 105.0 105.0 105.0 105.0 Polymerization
2,2'-azobisisobutyronitrile (g) 1.5 1.5 1.5 1.5 1.5 2.5 initiator
(a) Chain transfer n-dodecyl mercaptan (g) 0.5 0.5 0.5 0.5 0.5 0.5
agent (b) Solution of toluene (g) 5.0 0.0 1.0 2.0 3.0 4.0
polymerization 2,2'-azobisisobutyronitrile (g) 0.05 0.05 0.05 0.05
0.05 0.05 initiator (c) Solution of toluene (g) 5.0 5.0 5.0 5.0 5.0
6.0 polymerization 2,2'-azobisisobutyronitrile (g) 0.05 0.05 0.05
0.05 0.05 0.05 initiator (d) Total (g) 257.1 252.1 253.1 254.1
255.1 258.1 Evaluation heating residue (mass %) 40.0 40.0 40.0 40.0
40.0 41.0 results acid value (mgKOH) 6.5 6.5 6.5 6.5 6.5 6.5
hydroxyl value (mgKOH) 34.5 34.5 34.5 34.5 34.5 34.5 molecular mass
average molecular weight -- 23100 19100 20300 22100 24000 23100
weight number average molecular weight -- 14700 11900 12900 14000
15400 14700 molecular weight distribution -- 1.57 1.61 1.57 1.58
1.56 1.57 glass transition temperature (.degree. C.) 101 162 129
101 101 101
[0162] Subsequently, laminates (J.sub.A-Si-1 to 3, J.sub.A-F-4,
J.sub.A-Si--F-5, and J.sub.A-Si-6), each composed of a polymer base
and an undercoat layer formed thereon, were produced. Details are
given in Table 10.
TABLE-US-00010 TABLE 10 Example 21 Example 22 Example 23 Example 24
Example 25 Example 26 Layered product composed of polymer
J.sub.A-Si-1 J.sub.A-Si-2 J.sub.A-Si-3 J.sub.A-F-4 J.sub.A-Si--F-5
J.sub.A-Si-6 base and undercoat layer Thickness of polyethylene
terephthalate (.mu.m) 100 100 100 100 100 100 film Type of acrylic
resin A.sub.A-Si-1 A.sub.A-Si-2 A.sub.A-Si-3 A.sub.A-F-4
A.sub.A-Si--F-5 A.sub.A-Si-6 Thickness of acrylic resin (82 m) 3 3
3 3 3 3 Evaluation adhesion between polymer -- A A A A A A results
base and undercoat layer total light transmittance -- A A A A A A
haze -- A A A A A A surface free energy (mN/m) 20.1 15.9 19.2 20.1
23.2 20.1
[0163] Then, an inorganic layer [B1] was formed by sputtering on
the surface of the undercoat layer of the laminate 4, which was
composed of a polymer base and an undercoat layer formed thereon,
according to the same procedure as in Example 1 to provide a gas
barrier film (F.sub.A-Si-1 to F.sub.A-Si-3, F.sub.A-F-4, and
F.sub.A-Si--F-5). In Example 26, the same procedure as in Example 4
was carried to form a layer [B2], instead of forming a layer [B1],
to provide a gas barrier film (F.sub.A-Si-6).
[0164] Table 11 shows details of the gas barrier film.
TABLE-US-00011 TABLE 11 Example 21 Example 22 Example 23 Example 24
Example 25 Example 26 Gas barrier properties film F.sub.A-Si-1
F.sub.A-Si-2 F.sub.A-Si-3 F.sub.A-F-4 F.sub.A-Si--F-5 F.sub.A-Si-6
Layered product composed of polymer J.sub.A-Si-1 J.sub.A-Si-2
J.sub.A-Si-3 J.sub.A-F-4 J.sub.A-Si--F-5 J.sub.A-Si-6 base and
undercoat layer Type of inorganic layer -- [B1] [B1] [B1] [B1] [B1]
[B2] Thickness of inorganic layer (nm) 100 100 100 100 100 101
Surface roughness Ra of inorganic layer -- A A A A A A Evaluation
adhesion between undercoat -- A A A A A A results layer and
inorganic layer water vapor transmittance (g/m.sup.2/day) 3.3
.times. 10.sup.-3 6.7 .times. 10.sup.-3 5.0 .times. 10.sup.-3 9.6
.times. 10.sup.-3 8.8 .times. 10.sup.-3 7.3 .times. 10.sup.-3
[0165] Table 12 shows results of composition analysis of the layer
[B1] obtained in Example 21.
TABLE-US-00012 TABLE 12 Proportion in number of atoms (atom %)
Inorganic layer Zn Si Al O Example 21 [B1] layer 27.1 13.5 2.6
56.8
Comparative Examples 1 to 3
[0166] Except for using each of the compositions given in Table 13,
the same procedure as in Example 1 was carried out to produce an
acrylic resin (a-1, a.sub.St-2, and a.sub.A-3). The macromonomer
used in Comparative example 2, however, was a macromonomer (St)
(Macromonomer AS-6, manufactured by Toagosei Co., Ltd., number
average molecular weight 6,000). Details including composition,
production method, and major characteristics are shown in Table
13.
TABLE-US-00013 TABLE 13 Comparative Comparative Comparative example
1 example 2 example 3 Acrylic resin a-1 a.sub.St-2 a.sub.A-3
Organic solvent toluene (g) 95.0 95.0 95.0 ethyl acetate (g) 45.0
45.0 45.0 Macromonomer macromonomer (A) (g) 0.0 0.0 5.0
macromonomer (Si) (g) 0.0 0.0 0.0 macromonomer (F) (g) 0.0 0.0 0.0
macromonomer (St) (g) 0.0 5.0 0.0 Acrylic monomer methacrylic acid
(g) 1.0 1.0 1.0 2-hydroxyethyl methacrylate (g) 8.0 8.0 8.0 methyl
methacrylate (g) 91.0 91.0 91.0 dicyclopentanyl methacrylate (g)
0.0 0.0 0.0 total for acrylic monomers (g) 100.0 100.0 100.0 Total
for monomers (g) 100.0 100.0 105.0 Polymerization
2,2'-azobisisobutyronitrile (g) 1.5 1.5 1.5 initiator (a) Chain
transfer n-dodecyl mercaptan (g) 0.5 0.5 0.5 agent (b) Solution of
toluene (g) 5.0 5.0 5.0 polymerization 2,2'-azobisisobutyronitrile
(g) 0.05 0.05 0.05 initiator (c) Solution of toluene (g) 5.0 5.0
5.0 polymerization 2,2'-azobisisobutyronitrile (g) 0.05 0.05 0.05
initiator (d) Total (g) 252.1 252.1 257.1 Evaluation results
heating residue (mass %) 40.0 40.0 40.2 acid value (mgKOH) 6.5 6.5
6.5 hydroxyl value (mgKOH) 34.5 34.5 34.5 molecular mass average --
20500 24300 23900 weight molecular weight number average -- 12100
13700 14500 molecular weight molecular weight -- 1.69 1.77 1.65
distribution glass transition temperature (.degree. C.) 101 101
82
[0167] Subsequently, laminates (j-1, j.sub.St-2, and j.sub.A-3),
each composed of a polymer base and an undercoat layer formed
thereon, were produced. Details are given in Table 14.
TABLE-US-00014 TABLE 14 Comparative Comparative Comparative example
1 example 2 example 3 Layered product composed of polymer base and
undercoat layer j-1 j.sub.St-2 j.sub.A-3 Thickness of polyethylene
terephthalate film (.mu.m) 100 100 100 Type of acrylic resin a-1
a.sub.St-2 a.sub.A-1 Thickness of acrylic resin (.mu.m) 3 3 3
Evaluation adhesion between polymer base and undercoat -- A A A
results layer total light transmittance -- A A A haze -- A A A
surface free energy (mN/m) 43.1 39.0 42.9
[0168] Then, an inorganic layer [B1] was formed by sputtering on
the surface of the undercoat layer of the laminate 4, which was
composed of a polymer base and an undercoat layer formed thereon,
to provide a gas barrier film (f-1 and f.sub.St-2).
[0169] In Comparative example 3, the laminate 4, which was composed
of a polymer base and an undercoat layer formed thereon, was coated
with a macromonomer-free ultraviolet-cured clear hard coat, namely,
Pholucid No. 300C (manufactured by Chugoku Marine Paints, Ltd.),
with an intended dry thickness of 3 .mu.m using a Micro Gravure
coater (gravure cell count 200UR, and gravure rotate ratio 100%),
dried at 80.degree. C. for 30 seconds and cured by exposure to
ultraviolet ray of 300 mJ/cm.sup.2, followed by forming an
inorganic layer [B1] to provide a gas barrier film (f.sub.A-3).
Table 15 shows details of the gas barrier film.
TABLE-US-00015 TABLE 15 Comparative Comparative Comparative example
1 example 2 example 3 Gas barrier properties film f-1 f.sub.St-2
f.sub.A-3 Layered product composed of polymer base and undercoat
layer j-1 j.sub.St-2 j.sub.A-3 Type of inorganic layer -- [B1] [B1]
[B1] Thickness of inorganic layer (nm) 100 100 100 Surface
roughness Ra of inorganic layer -- B B A Evaluation adhesion
between undercoat layer and -- A A A results inorganic layer water
vapor transmittance (g/m.sup.2/day) 1.3 .times. 10.sup.-1 9.2
.times. 10.sup.-2 5.3 .times. 10.sup.-1
EXPLANATION OF NUMERALS
[0170] 1. polymer base [0171] 2. undercoat layer [0172] 3.
inorganic layer [0173] 4. laminate composed of a polymer base and
an undercoat layer formed thereon [0174] 5. wind-up type sputtering
apparatus [0175] 6. wind-up chamber [0176] 7. unwinding roll [0177]
8, 9, and 10. guide roll in unwinding zone [0178] 11. cooling drum
[0179] 12. sputtering electrode [0180] 13, 14, and 15. guide roll