U.S. patent application number 14/669357 was filed with the patent office on 2015-10-15 for decorative wpc panel comprising a low-porous profiled edge and method for producing the same.
This patent application is currently assigned to AKZENTA PANEELE + PROFILE GMBH. The applicant listed for this patent is AKZENTA PANEELE + PROFILE GMBH. Invention is credited to Hans-Jurgen Hannig.
Application Number | 20150290968 14/669357 |
Document ID | / |
Family ID | 50440589 |
Filed Date | 2015-10-15 |
United States Patent
Application |
20150290968 |
Kind Code |
A1 |
Hannig; Hans-Jurgen |
October 15, 2015 |
DECORATIVE WPC PANEL COMPRISING A LOW-POROUS PROFILED EDGE AND
METHOD FOR PRODUCING THE SAME
Abstract
A decorative panel comprising a plate-shaped carrier made of a
wood plastic composite (WPC) material, wherein the plate-shaped
carrier comprises a profile and/or a cutting edge in at least one
edge region, and wherein the profile and/or the cutting edge has a
substantially sealed surface. A method for producing such panel
including a step of subjecting a surface of a profile and/or
cutting edge to a thermal treatment to at least partially melt the
WPC material in the region of the profile and seal the surface.
Inventors: |
Hannig; Hans-Jurgen;
(Bergisch Gladbach, DE) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
AKZENTA PANEELE + PROFILE GMBH |
Kaisersesch |
|
DE |
|
|
Assignee: |
AKZENTA PANEELE + PROFILE
GMBH
Kaisersesch
DE
|
Family ID: |
50440589 |
Appl. No.: |
14/669357 |
Filed: |
March 26, 2015 |
Current U.S.
Class: |
428/192 ;
427/258; 83/16 |
Current CPC
Class: |
B29C 2795/00 20130101;
E04C 2002/008 20130101; E04F 15/102 20130101; E04C 2002/004
20130101; B05D 3/12 20130101; B23B 41/00 20130101; B44F 9/04
20130101; E04C 2/16 20130101; B05D 1/28 20130101; B44F 9/02
20130101; B44C 5/06 20130101; E04C 2/22 20130101; B29C 39/123
20130101; B32B 3/00 20130101; B44C 5/04 20130101; B29C 2793/00
20130101 |
International
Class: |
B44F 9/04 20060101
B44F009/04; E04C 2/22 20060101 E04C002/22; B05D 3/12 20060101
B05D003/12; B44C 5/06 20060101 B44C005/06; B05D 1/28 20060101
B05D001/28; B44F 9/02 20060101 B44F009/02; E04C 2/16 20060101
E04C002/16 |
Foreign Application Data
Date |
Code |
Application Number |
Apr 9, 2014 |
EP |
14164042.5 |
Claims
1. Decorative panel comprising a plate-shaped carrier made of a
wood plastic composite (WPC) material, wherein the plate-shaped
carrier in at least one edge region has a profile and/or a cutting
edge, characterized in that the profile and/or cutting edge
comprises a substantially sealed surface.
2. The decorative panel according to claim 1, wherein the WPC
material comprises a plastic material from the group consisting of
polyvinyl chloride (PVC), polyethylene (PE), polypropylene (PP),
polyamide (PA), polystyrene (PS), acrylonitrile-butadiene-styrene
(ABS), polymethyl methacrylate (PMMA), polycarbonate (PC),
polyethylene terephthalate (PET), polyether ether ketone (PEEK),
polyisobutylene (PIB), polybutylene (PB), or mixtures or
co-polymerizates thereof.
3. The decorative panel according to claim 1, wherein the panel
comprises a decor applied onto the plate-shaped carrier by means of
direct printing.
4. A method for producing a decorative panel, comprising the steps
of: providing a plate-shaped carrier made of a WPC material;
forming a profile and/or a cutting edge in at least one edge of the
plate-shaped carrier; subjecting a surface of the introduced
profile and/or cutting edge to a thermal treatment to at least
partially melt the WPC material in the region of the profile and
seal the surface.
5. The method according to claim 4, wherein the forming of the
profile and/or the cutting edge is carried out by a machining or
cutting process.
6. The method according to claim 5, wherein the melting of the WPC
material is implemented by heating the a cutting or machining tool
used in the machining or cutting process for the profiling and/or
cutting of the at least one edge of the plate-shaped carrier to a
temperature greater than or equal to a melting temperature of the
WPC material and less than a decomposition temperature of the WPC
material.
7. The method according to claim 6, wherein the machining or
cutting tool is temperature controlled to a maximum temperature of
30.degree. C. above the melting temperature of the WPC
material.
8. The method according to claim 7, wherein the temperature control
of the machining or cutting tool is implemented by a heating and/or
cooling device.
9. The method according to claim 8, wherein the temperature of the
machining or cutting tool is monitored contact-free.
10. The method according to claim 8, wherein at least the profiled
region of the edge of the plate-shaped carrier is cooled down to a
temperature below the melting point after the melting of the WPC
material and sealing of the surface.
11. The method according to claim 10, wherein the cooling is
carried out within a period of .ltoreq.60 s.
12. The method according to claim 4, comprising applying a decor to
the carrier by a direct printing process subsequently to the
providing the plate-shaped carrier.
13. The method according to claim 12, comprising a step for
applying a printing base prior to the step of applying a decor.
14. The method according to claim 4, comprising applying a decor to
the carrier by a direct printing process subsequently to the
forming the profile and/or the cutting edge in the edge of the
plate-shaped carrier.
15. The method according to claim 4, comprising applying a decor to
the carrier by a direct printing process subsequently to the
forming the profile and/or the cutting edge in the edge of the
plate-shaped carrier.
16. The method according to claim 4 comprising: the providing the
carrier; the forming the profile; and the thermal treatment;
wherein the thermal treatment is performed during the forming the
profile by heating a tool used in the forming the profile; and
applying a decor to the carrier by a printing process performed
after the forming the profile.
17. The method according to claim 14 further comprising applying a
wear layer over the decor.
18. The method according to claim 16 further comprising applying a
wear layer over the decor.
Description
REFERENCE TO RELATED APPLICATIONS
[0001] This application claims priority to European application EP
14 164 042.5, filed Apr. 9, 2014, the entire disclosure of which is
incorporated by reference.
FIELD OF THE INVENTION
[0002] The present invention relates to a decorative WPC panel
comprising a low-porous profiled edge and a method for producing in
particular direct printed decorative panels comprising a low-porous
profiled edge.
BACKGROUND OF THE INVENTION
[0003] Decorative plates or decorative panels are known per se and
used in a variety of ways for covering walls, ceilings or floors.
They normally consist of a carrier or core of a solid material, for
example a wood-based material, which is provided on at least one
side with a decorative layer and a top layer and optionally with
further layers, such as a wearing layer. The decorative layer is
usually a printed paper which is impregnated with a resin. The top
layer and the remaining layers often comprise a resin.
[0004] The carrier of such a decorative panel consists usually of
wood or a wood-based material such as a MDF or HDF board or an OSB
board, onto which an appropriate decoration, e.g. by applying a
decorative sheet of paper, and usually further top layers are
applied. Despite of this laminate structure there is a risk for
decorative panels based on corresponding carriers made of
wood-based materials that these will swell when exposed to moisture
resulting in a damage of the panels.
[0005] The risk of swelling due to moisture is reduced
significantly with the use of alternative materials as carriers,
such as plastic or wood polymer composite (WPC
wood-plastic-composite). WPC is a mixture of wood particles and
plastic, which are mixed by a suitable production process into a
homogeneous composite material having plastic-like processing
properties.
[0006] In processing plate-shaped carriers on the basis of a WPC
the plate-shaped carriers are usually processed as large format
plates, which are divided in the course of the processing into a
plurality of panels of a desired size. Then in addition the panels
are generally provided with a functional profiling such as a tongue
and groove profile or a locking profile at at least one edge by
means of which the panels can be connected during the assembly in
order to provide a contiguous surface.
[0007] Herein, one disadvantage in cutting or profiling of the
plate-shaped carriers is that at the cutting surfaces wood fibers
of the WPC material may be exposed, which may swell when exposed to
moisture and thus can lead to a damage of the panel.
SUMMARY OF THE INVENTION
[0008] It is therefore an object of the present invention to
provide a decorative WPC panel improved in this respect and a
method for producing such a decorative WPC panel.
[0009] This object is achieved by a decorative panel comprising a
plate-shaped carrier made of a wood plastic composite (WPC)
material, wherein the plate-shaped carrier in at least one edge
region has a profile and/or a cutting edge, and wherein the profile
and/or cutting edge comprises a substantially sealed surface.
[0010] In another aspect, the object is achieved by a method for
producing a decorative panel, comprising the steps of forming a
profile and/or a cutting edge in at least one edge of the
plate-shaped carrier made from a WPC material, and subjecting a
surface of the introduced profile and/or cutting edge to a thermal
treatment to at least partially melt the WPC material in the region
of the profile and the surface is sealed.
BRIEF DESCRIPTION OF THE FIGURES
[0011] FIG. 1 is a schematic illustration of a panel of the
invention.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
[0012] The invention thus proposes a decorative panel comprising a
plate-shaped carrier made of a wood plastic composite (WPC)
material, wherein the plate-shaped carrier has in at least one edge
region a profile and/or a cutting edge, characterized in that the
profile and/or the cutting edge has a substantially sealed surface.
FIG. 1 shows the decorative panel 100 comprising the plate-shaped
carrier 110 made of the WPC material. Decor 120 is applied to the
carrier. In at least one edge region 130 the plate-shaped carrier
has a profile and/or a cutting edge. The profile and/or cutting
edge comprises a substantially sealed surface 150, as shown at
detail 200.
[0013] A sealed surface in the sense of the invention is a surface
which essentially comprises no open wood fibers at the direct
surface, rather the surface substantially consists of a closed
layer of plastic. This does not preclude that wood fibers are
disposed on the surface, but they are surrounded by plastic in such
a way that moisture cannot penetrate into the wood fibers.
[0014] The term "decorated wall or floor panel" or "decorative
panel" in the sense of the invention means in particular wall,
ceiling or floor panels comprising a decor simulating a decoration
template applied onto a carrier plate. Decorative panels are used
in a variety of ways both in the field of interior design of rooms
and for decorative cladding of buildings, for example in exhibition
stand construction. One of the most common uses of decorative
panels is their use as a floor covering. Here, the decorative
panels often comprise a decor intended to replicate a natural
material.
[0015] Examples of such replicated natural materials or decoration
templates are wood species such as maple, oak, birch, cherry, ash,
walnut, chestnut, wenge or even exotic woods such as Panga Panga,
mahogany, bamboo and bubinga. In addition, often natural materials
such as stone surfaces or ceramic surfaces are replicated.
[0016] Accordingly, a "decoration template" in the sense of the
present invention in particular means such an original natural
material or at least a surface of such a material which is to be
imitated or replicated by the decor.
[0017] A "pourable" material in particular means a material which
can be applied onto a base by a pouring or scattering process.
Herein, the material may be provided as a fluid or in particular as
a pourable solid.
[0018] A "granulate material" or "granular material" means a solid
or a head of a solid comprising or consisting of a plurality of
solid particles, such as grains or beads. Here by way of example
but not limited thereto grainy or powdery materials can be
mentioned.
[0019] A "carrier" in particular can be understood as a layer
serving as a core or as a base layer in a finished panel, which in
particular includes a material comprising a plastic and wood fibers
and/or wood particles. For example, the carrier can already provide
or contribute to a suitable stability for the panel.
[0020] Herein, a "web-like carrier" can be understood as a carrier
which, for example, during its manufacturing process has a web-like
shape and thus a length which is substantially greater than its
thickness or width, wherein its length may be greater than 15
meters.
[0021] Herein, the term "plate-shaped carrier" in the sense of the
present invention can be understood as a carrier which is formed by
separation from the web-like carrier and is formed in the shape of
a plate. The plate-shaped carrier can already define the shape
and/or size of the panel to be produced. However, the plate-shaped
carrier can also be provided as a large plate. A large plate in the
sense of the invention in particular is a carrier whose dimensions
several times exceed the dimensions of the final decorative panels,
and which is cut during the course of the manufacturing process
into a corresponding plurality of decorative panels, for example by
sawing, laser or water jet cutting. For example, the large plate
may correspond to the web-like carrier.
[0022] Wood-based materials in the sense of the invention in
particular are wood-based materials such as wood polymer materials
(Wood Plastic Composite, WPC).
[0023] In the sense of the invention the term "fiber materials"
means materials such as paper and non-woven fabrics on the basis of
plant, animal, mineral or even synthetic fibers as well as
cardboards. Examples are fiber materials on the basis of plant
fibers and in addition to papers and non-woven fabrics made of
cellulose fibers boards made of biomass such as straw, maize straw,
bamboo, leaves, algae extracts, hemp, cotton or oil palm fibers.
Examples of animal fiber materials are keratin-based materials such
as wool or horsehair. Examples of mineral fiber materials are
mineral wool or glass wool.
[0024] According to one embodiment a carrier material based on a
plastic or a wood plastic composite material (WPC) can be provided.
For example, the carrier plate can be formed from a thermoplastic,
elastomeric or duroplastic plastic material. In addition, recycling
materials from said materials can be used in the context of the
method according to the invention. Herein, preferred plate
materials may be in particular thermoplastic plastic materials,
such as polyvinyl chloride, polyolefins (for example polyethylene
(PE), polypropylene (PP), polyamide (PA)), polyurethane (PU),
polystyrene (PS), acrylonitrile-butadiene-styrene (ABS), polymethyl
methacrylate (PMMA), polycarbonate (PC), polyethylene terephthalate
(PET), polyether ether ketone (PEEK) or mixtures or copolymerizates
thereof. Herein, irrespective of the base material of the carrier,
for example, plasticizers may be provided which may be present in a
range of .gtoreq.0 wt. % to .ltoreq.20 wt. %, in particular
.ltoreq.10 wt. %, preferably .ltoreq.7 wt. %, for example in a
range of .gtoreq.5 wt. % to .ltoreq.10 wt. %. A suitable
plasticizer, for example, is a plasticizer available under the
trade name "Dinsch" from BASF company. Moreover, as a substitute
for conventional plasticizers copolymers such as acrylates or
methacrylates can be used.
[0025] In particular thermoplastic plastic materials offer the
advantage that the products made from them can easily be recycled.
It is also possible to use recycling materials from other sources.
This enables a further reduction of the manufacturing costs.
[0026] Such carriers are very elastic or springy, which allows a
comfortable feeling when walking on them and also a suppression of
noises occurring during walking on them compared to conventional
materials, thus, an improved impact sound can be realized.
[0027] In addition, the abovementioned carriers offer the advantage
of a good water resistance, because they have a degree of swelling
of 1% or less. This in a surprising way besides pure plastic
carriers also applies to WPC materials, as will be explained in
detail below.
[0028] In a particularly advantageous manner the carrier material
can comprise or consist of wood polymer materials (Wood Plastic
Composite, WPC). Here, as an example wood and a polymer may be
suitable, which can be present in a ratio of 40/60 to 70/30, such
as 50/50. As polymeric components polypropylene, polyethylene or a
copolymer of the two abovementioned materials can be used. Such
materials offer the advantage that they can be formed into a
carrier in the above-described process already at low temperatures,
such as in a range of 180.degree. C. to 200.degree. C., so that a
particularly effective process control, such as with exemplary line
speeds in a range of 6 m/min, is possible. For example, a WPC
product with a 50/50 proportion of wood and polymer components with
an exemplary product thickness of 4.1 mm is possible, which may
allow for a particularly effective manufacturing process.
[0029] In addition, in this way very stable panels can be produced,
which moreover have a high elasticity, which in particular can be
advantageous for an effective and cost-efficient configuration of
connecting elements at the edge region of the carrier and further
with respect to an impact sound insulation. Furthermore, the
above-mentioned good water tolerance with a degree of swelling of
less than 1% can be achieved with such WPC materials. Herein, WPC
materials can include, for example, stabilizers and/or other
additives which preferably may be present in the plastic
portion.
[0030] Furthermore, it may be particularly advantageous that the
carrier material comprises or consists of a PVC-based material.
Even such materials can be used in a particularly advantageous
manner for high quality panels that can easily be used even in wet
rooms. Furthermore, also PVC-based carrier materials may be useful
for a particularly effective manufacturing process, since here line
speeds of 8 m/min for an exemplary product thickness of 4.1 mm may
be possible, which could allow for a particularly effective
manufacturing process. Moreover, also such carriers have an
advantageous elasticity and water tolerance, which can lead to the
above-mentioned advantages.
[0031] Herein, in plastic-based panels as well as in WPC-based
panels mineral fillers may be advantageous. Particularly suitable
are talc or calcium carbonate (chalk), aluminum oxide, silicagel,
quartz powder, wood flour and gypsum. For example, chalk may be
provided in a range of .gtoreq.30 wt. % to .ltoreq.70 wt. %,
wherein the fillers, in particular chalk can improve the slip of
the carrier. They also can be colored in a known manner. In
particular, it can be provided that the plate material comprises a
flame retardant.
[0032] According to a particularly preferred embodiment of the
invention the carrier material consists of a mixture of a PE/PP
block copolymer with wood. Herein, the proportion of the PE/PP
block copolymer and the proportion of wood can range between
.gtoreq.45 wt. % and .ltoreq.55 wt. %. Furthermore, the carrier
material can comprise between .gtoreq.0 wt. % and .ltoreq.10 wt. %
of other additives such as flow agents, heat stabilizers or UV
stabilizers. Here, the particle size of the wood is between >0
.mu.m and .ltoreq.600 .mu.m with a preferred particle size
distribution of D.sub.50.gtoreq.400 .mu.m. In particular, the
carrier material may comprise wood with a particle size
distribution of D.sub.10.gtoreq.400 .mu.m. The particle size
distribution is based on the volumetric diameter and refers to the
volume of the particles. Particularly preferably the carrier
material is provided as granular or pelletized pre-extruded mixture
of a PE/PP block copolymer with wood particles with the specified
particle size distribution. Here, the granules and/or pellets can
preferably have a particle size in the range of .gtoreq.400 .mu.m
to .ltoreq.10 mm, preferably .gtoreq.600 .mu.m to .ltoreq.10 mm, in
particular 800 .mu.m to 10 mm.
[0033] According to a further preferred embodiment of the invention
the carrier material consists of a mixture of a PE/PP polymer blend
with wood. Here, the proportion of PE/PP polymer blend as well as
the proportion of wood can range between .gtoreq.45 wt. % and
.ltoreq.55 wt. %. Furthermore, the carrier material can comprise
between .gtoreq.0 wt. % and .ltoreq.10 wt. % of other additives
such as flow agents, heat stabilizers or UV stabilizers. Here, the
particle size of the wood is between >0 .mu.m and 600 .mu.m with
a preferred particle size distribution of D.sub.50.gtoreq.400
.mu.m. In particular, the carrier material may comprise wood with a
particle size distribution of D.sub.10.gtoreq.400 .mu.m. The
particle size distribution is based on the volumetric diameter and
refers to the volume of the particles. Particularly preferably, the
carrier material is provided as a granular or pelletized
preextruded mixture of a PE/PP polymer blend with wood particles
with the specified particle size distribution. Here, the granules
and/or pellets can preferably have a particle size in the range of
.gtoreq.400 .mu.m to .ltoreq.10 mm, preferably .gtoreq.600 .mu.m to
.ltoreq.10 mm, in particular .gtoreq.800 .mu.m to .ltoreq.10
mm.
[0034] In a further embodiment of the invention, the carrier
material consists of a mixture of a PP homopolymer with wood. The
proportion of the PP homopolymer and the proportion of wood can
range between .gtoreq.45 wt. % and .ltoreq.55 wt. %. Furthermore,
the carrier material can comprise between .gtoreq.0 wt. % and
.ltoreq.10 wt. % of other additives, such as flow agents, heat
stabilizers or UV stabilizers. Here, the particle size of the wood
is between >0 .mu.m and .ltoreq.600 .mu.m with a preferred
particle size distribution of D.sub.50.gtoreq.400 .mu.m. In
particular, the carrier material can comprise wood with a particle
size distribution of D.sub.10.gtoreq.400 .mu.m. The particle size
distribution is based on the volumetric diameter and refers to the
volume of the particles. Particularly preferably the carrier
material is provided as a granular or pelletized pre-extruded
mixture of a PP homopolymer with wood particles of the specified
particle size distribution. The granules and/or pellets can
preferably have a particle size in the range of .gtoreq.400 .mu.m
to .ltoreq.10 mm, preferably .gtoreq.600 .mu.m to .ltoreq.10 mm, in
particular .gtoreq.800 .mu.m to .ltoreq.10 mm.
[0035] In another embodiment of the invention, the carrier material
consists of a mixture of a PVC polymer with chalk. Herein, the
proportion of the PVC polymer and the proportion of chalk can range
between .gtoreq.45 wt. % and .ltoreq.55 wt. %. Furthermore, the
carrier material can comprise between .gtoreq.0 wt. % and
.ltoreq.10 wt. % of other additives, such as flow agents, heat
stabilizers or UV stabilizers. The particle size of the chalk is
between >0 .mu.m and .ltoreq.600 .mu.m with a preferred particle
size distribution of D.sub.50.ltoreq.400 .mu.m. In particular, the
carrier material may comprise chalk with a particle size
distribution of D.sub.10.gtoreq.400 .mu.m. The particle size
distribution is based on the volumetric diameter and refers to the
volume of the particles. Particularly preferably the carrier
material is provided as a granular or pelletized pre-extruded
mixture of a PVC polymer with chalk with the specified particle
size distribution. The granules and/or pellets can preferably have
a particle size in the range of 400 .mu.m to 10 mm, preferably 600
.mu.m to 10 mm, in particular 800 .mu.m to 10 mm.
[0036] In a further embodiment of the invention the carrier
material consists of a mixture of PVC polymer with wood. Herein,
the proportion of the PVC polymer and the proportion of the wood
can range between 45 wt. % and 55 wt. %. Furthermore, the carrier
material can comprise between 0 wt. % and 0 wt. % of other
additives, such as flow agents, heat stabilizers or UV stabilizers.
The particle size of the wood is between >0 .mu.m and
.ltoreq.600 .mu.m with a preferred particle size distribution of
D.sub.50.gtoreq.400 .mu.m. In particular, the carrier material can
comprise wood with a particle size distribution of
D.sub.10.gtoreq.400 .mu.m. The particle size distribution is based
on the volumetric diameter and refers to the volume of the
particles. Particularly preferably the carrier material is provided
as granular or pelletized pre-extruded mixture of a PVC polymer
with wood particles of the specified particle size distribution.
The granules and/or pellets can preferably have a particle size in
the range of .gtoreq.400 .mu.m to .ltoreq.10 mm, preferably
.gtoreq.600 .mu.m to .ltoreq.10 mm, in particular .gtoreq.800 .mu.m
to .ltoreq.10 mm.
[0037] For determining the particle size distribution well-known
methods such as laser diffractometry can be used, by means of which
particle sizes in the range from a few nanometers up to several
millimeters can be determined. Using this method also D.sub.50 or
D.sub.10 values can be determined, according to which 50% and 10%,
respectively, of the measured particles are smaller than the
specified value.
[0038] According to another embodiment the carrier material may
comprise hollow microspheres. This kind of additives can in
particular cause that the density of the carrier and thus of the
produced panel can be significantly reduced, such that a
particularly simple and cost-effective transportation and also a
very comfortable laying can be guaranteed. Herein, in particular by
the insertion of hollow microspheres a stability of the produced
panel can be ensured which is not significantly reduced compared to
a material without hollow microspheres. Thus, the stability is
sufficient for most applications. Herein, hollow microspheres can
be understood in particular as structures, which have a hollow
basis body and a size or a maximum diameter in the micrometer
range. For example, usable hollow spheres may have a diameter in
the range of .gtoreq.5 .mu.m to .ltoreq.100 .mu.m, such as
.gtoreq.20 .mu.m to .ltoreq.50 .mu.m. As a material of the hollow
microspheres basically any material comes into consideration, such
as glass or ceramic. Further, due to the weight plastics, such as
the plastics used in the carrier material, such as PVC, PE or PP
can be advantageous, wherein these optionally can be prevented from
deforming during the manufacturing process by suitable
additives.
[0039] According to a further embodiment of the invention the
decorative panel comprises a decor which is applied onto the
plate-shaped carrier by means of direct printing. Here, in the
sense of the invention the term "direct printing" means applying a
decor directly onto the carrier of a panel or onto an unprinted
fiber material layer or decor base applied onto the carrier. To
this end different printing techniques such as flexographic
printing, offset printing or screen printing can be used. In
particular, as digital printing techniques, for example, inkjet or
laser printing processes can be used.
[0040] For example, in order to imitate or replicate a decoration
template in a particularly detailed and highly accurate manner in a
three-dimensional form, the decor can be applied identically to the
template. In particular, the three-dimensional decor data can be
provided by three-dimensionally scanning the decoration template by
means of electromagnetic radiation such as by a three-dimensional
scanner (3D scanner). Herein, a plurality of decor layers with at
least partially different surface application amounts can
successively be applied on the basis of provided three-dimensional
decor data.
[0041] Moreover, the decorative layers may be formed of a
particularly radiation curable paint and/or ink. For example, a
UV-curable paint or ink can be used. In this embodiment a
particular detailed and matching replica of the decoration template
can be obtained. On the one side a highly accurate synchronous pore
can be achieved in this way without providing further measures.
Herein, a synchronous pore can in particular be a pore or another
structure, which is spatially located exactly there where it is
displayed visually by a haptic texture matching with the optical
decor features. In this embodiment this is essentially
automatically the case, because the structural design is created by
the paint or ink. In addition, decoration templates, such as
wood-based materials, often comprise a variation of the color
impression not only along their width or length but also along
their depth. Even this color impression or color gradient can be
simulated particularly detailed in this embodiment, such that the
overall appearance of the panel looks even more identical. Herein,
a particularly rapid solidification can be achieved especially when
the paint or ink used is radiation curable, whereby the plurality
of layers may be applied rapidly in succession, such that the
entire process can be realized within a reduced time and thus is
particularly cost-efficient.
[0042] The term radiation curable paint in the sense of the
invention means a composition which includes a binder and/or a
filler as well as color pigments and which induced by
electromagnetic radiation of a suitable wavelength, such as UV
radiation or electron beams, can be at least partially
polymerized.
[0043] The term radiation curable ink in the sense of the invention
means a composition essentially free of fillers and comprising
color pigments, which induced by electromagnetic radiation of a
suitable wavelength, such as UV radiation or electron beams, can be
at least partially polymerized.
[0044] Herein, the decorative layers each can be applied in a
thickness in the range of .gtoreq.5 .mu.m to .ltoreq.10 .mu.m.
[0045] In addition to a positive image with respect to the color
and/or texture it can also be provided to apply a corresponding
negative image of the decoration template. In detail, as is known,
for example, from positive staining or negative staining of
wood-based materials, by the use of digital data the color
impression e.g. of a texture can be inverted, so that with respect
to the color and in particular with respect to lighter and darker
areas a negative is created. A similar effect, in addition to the
color impression, is possible for the applied texture, too, such
that also with respect to the structural design a negative can be
realized. Such effects, too, can be integrated into a manufacturing
process based on digital three-dimensional data without any
problems and without lead-time or retrofitting.
[0046] The invention is also directed to a method for producing a
decorative panel comprising the steps of: [0047] providing a
plate-shaped carrier of a WPC material; and [0048] introducing a
profile and/or a cutting edge at at least one edge of the
plate-shaped carrier, which is characterized in that the surfaces
of the introduced profile and/or cutting edge are subjected to a
thermal treatment in which the WPC material is at least partially
molten in the region of the profile and the surface is sealed.
[0049] Surprisingly, it has been shown that the wood fibers and/or
particles exposed by processing the decorative panel or the carrier
plate can be sealed by a thermal treatment which effects a melting
of the surface such that the swelling behavior with respect to the
impact by moisture can be reduced significantly. Thus, swelling of
the profiled edges and/or cutting surfaces and the concomitant
damage of the decorative panel in the case of impact by moisture
can be avoided.
[0050] Herein, the WPC material is merely molten near-surface.
Near-surface means in the sense of the invention up to a depth of
.ltoreq.3 mm, preferably .ltoreq.2 mm, more preferably .ltoreq.1 mm
and in particular .ltoreq.0,8 mm.
[0051] According to one embodiment of the method it is provided
that after profiling or sawing the decorative panels or the
plate-shaped carrier melting of the WPC material in the
near-surface region is implemented in a process step downstream of
the profiling and/or sawing process. To this end, for example, the
use of a temperature controlled melting head may be provided which
with respect to its profile corresponds to the profile or cut
introduced in the edge and is guided over the surfaces of the
profile or cutting surfaces, wherein the WPC material melts
near-surface.
[0052] In one embodiment of the invention the melting head is
preferably maximally heated up to a temperature .ltoreq.30.degree.
C. above the melting temperature of the WPC material.
[0053] According to a further embodiment of the invention, the
introduction of the profile and/or the cutting edge is implemented
by means of a cutting or machining process such as by milling or
sawing. Herein, according to another embodiment of the invention it
can be particularly provided that the melting of the WPC material
is implemented by heating the cutting tool used for profiling
and/or cutting of the at least one edge of the plate-shaped carrier
by machining to a temperature greater than or equal to the melting
temperature and lower than the decomposition temperature of the WPC
material. As a result, an additional process step can be
avoided.
[0054] In one embodiment of the invention it may be provided that
the cutting tool is maximally temperature controlled to a
temperature .ltoreq.30.degree. C. above the melting temperature of
the WPC material. Herein, it can be provided that the temperature
control of the cutting or machining tool is implemented by a
heating and/or cooling device.
[0055] Here, it can preferably be provided that the temperature of
the cutting or machining tool is monitored contact-free, for
example by means of an infrared temperature sensor or an infrared
thermometer. Then the temperature control of the tool can
preferably be carried out as a function of the data collected in
the course this monitoring.
[0056] According to a particularly preferred embodiment of the
invention at least a part of the temperature control of the cutting
and/or machining tool is implemented by use of the heat produced by
the cutting and/or machining process itself. This heat is caused by
the friction between the tool and the material. Herein, in a
particularly preferred embodiment of the invention it can be
provided that the processing speed, in particular the rotation
speed of the tool and the relative velocity between the decorative
panel/carrier plate and the cutting or milling head is adjusted
such that the heat of the tool generated during the machining
process occurs in a temperature range greater than or equal to the
melting temperature of the WPC material and lower than the
decomposition temperature of the WPC material.
[0057] According to a further embodiment of the invention it can be
provided that at least the profiled region of the edge of the
plate-shaped carrier and/or the cutting surface is cooled down to a
temperature below the melting temperature after melting of the WPC
material and sealing the surface.
[0058] This cooling according to the invention, for example, can be
carried out by an air flow directed onto the corresponding surface.
Herein, it may in particular be provided that the air flow is
cooled and thus has a temperature below the ambient temperature of
the machining site.
[0059] Alternatively, a temperature controlled cooling head can be
used which with respect to its profile corresponds to the profile
or cut introduced into the edge and is guided over the surfaces of
the profile or cutting surfaces, wherein the WPC material is cooled
down to a temperature below the melting temperature of the WPC
material.
[0060] According to a further embodiment of the invention it may be
provided that the cooling of the WPC material molten near-surface
is implemented within a period of .ltoreq.60 s, preferably
.ltoreq.45 s, in particular .ltoreq.30 s. In this way it can be
ensured that no subsequent unwanted deformation of the profile is
caused.
[0061] To produce a finished panel the method may comprise further
process steps to provide the carrier with a decor and to coat the
decor with a protective layer. Herein, if appropriate, first a
pretreatment of the carrier for electrostatic discharge or specific
charge before applying a decorative image using a direct printing
method can be implemented. This in particular can serve to prevent
the occurrence of blurring in the course of the decor application.
This is particularly suitable for printing processes for applying
the decorative layers, because the electrostatic charge which
builds up in the carriers to be printed in the course of the
production process results in a deflection of paint or ink droplets
on their way from the print head to the surface to be printed. The
thus induced inaccuracy of the paint application leads to a
perceivable blurring of the printed image.
[0062] Herein the means for discharging electrostatic charges may
at least comprise a roller, a brush or a lip of a conductive
material having a conductivity .ltoreq.110.sup.3 Sm.sup.-1, which
electrically conductive contacts the carrier at least in the region
of the printing mechanism and which is connected to an electrical
ground potential. In this case, the electrical ground potential may
be provided, for example, by a grounding. In addition, for example,
a means for discharging electrostatic charges may be a means for
producing a corona discharge.
[0063] Moreover, it can be provided that a decor base or print base
is applied to at least a portion of the carrier. For example, first
a primer particularly suited for printing processes can be applied
as a decor base, for example in a thickness of 10 .mu.m to 60
.mu.m. Herein, as a primer a liquid radiation curable mixture based
on a urethane or urethane acrylate, optionally with one or more of
a photo initiator, a reactive diluent, a UV stabilizer, a
rheological agent such as a thickener, radical scavengers, leveling
agent, antifoam or preservative, pigment, and/or a dye can be used.
For example, the urethane acrylate may be included in the primer
composition in the form of reactive oligomers or prepolymers. The
term "reactive oligomer" and "prepolymer" in the sense of the
invention is a compound comprising urethane acrylate units which is
able to react radiation-induced, optionally with addition of a
reactive binder or a reactive diluent, into urethane polymer or
urethane acrylate polymer. Herein, urethane acrylates in the sense
of the invention are compounds which substantially are composed of
one or more aliphatic structural elements and urethane groups.
Aliphatic structural elements comprise both alkylene groups,
preferably comprising 4 to 10 carbon (C) atoms and cycloalkylene
groups preferably comprising 6 to 20 carbon atoms. Both the
alkylene and the cycloalkylene groups may be mono- or
polysubstituted with C.sub.1-C.sub.4 alkyl, in particular methyl
and include one or more non-adjacent oxygen atoms. The aliphatic
structural elements are optionally linked to each other via
quaternary or tertiary carbon atoms, via urea groups, biuret,
uretdione, allophanate, cyanurate, urethane, ester or amide groups
or via ether oxygen or amine nitrogen. Furthermore, urethane
acrylates in the sense of the invention can also include
ethylenically unsaturated structural elements. These preferably
include vinyl or allyl groups, which may be substituted with
C.sub.1-C.sub.4 alkyl, in particular methyl and which, in
particular, are derived from .alpha.,.beta.-ethylenically
unsaturated carboxylic acids and their amides. Particularly
preferred ethylenically unsaturated structural units are acryloyl
and methacryloyl groups such as acrylamido and methacrylamido and
in particular acryloxy and methacryloxy. Radiation-curable in the
sense of the invention means that the primer composition induced by
electromagnetic radiation of a suitable wavelength, such as
ultraviolet radiation or electron beams, can be at least partially
polymerized.
[0064] The use of radiation-curable primers based on urethane
acrylates allows in a particularly advantageous manner an
application of the decor immediately subsequent to the application
and the radiation-induced curing of the primer layer, for example,
by means of a digital printing technique. Herein, the primer layer
provides for a good adhesion of the applied decor onto the carrier
surface coated with the primer. Herein, urethane acrylates offer
the advantage of a good adhesion to both the carrier material and
the decorative layer, i.e. the decor paint or ink. This inter alia
resides in the polymerization reactions occurring in this type of
polymers, in which on the one hand a radiation-induced radical
polymerization of the OH groups occurs and on the other hand
post-curing of the polymer via the NCO groups occurs. Thus, after
the radiation-induced curing immediately a tack-free and further
processable surface is obtained, while the final properties of the
primer layer are also influenced by the post-curing process based
on the NCO groups and provide for a secure bond to the carrier
material. In addition, the occurring post-curing process ensures
that a sufficient layer stability is achieved even in less or
non-exposed areas of the carrier. Thus, the method according to the
invention enables in particular also pre-textured carriers, i.e.
carriers whose surface already have a three-dimensional structure,
to be provided with a primer layer, thereby ensuring that the
subsequently applied decor firmly adheres to the carrier.
[0065] In the method according to the invention the primer can be
preferably applied onto the carrier plate by means of rubber
rollers, a pouring device, or by spraying. Preferably the primer is
applied in an amount between .gtoreq.1 g/m.sup.2 and .ltoreq.100
g/m.sup.2, more preferably between .gtoreq.10 g/m.sup.2 and
.ltoreq.50 g/m.sup.2, in particular between .gtoreq.20 g/m.sup.2
and .ltoreq.40 g/m.sup.2. Subsequently to the application of the
primer onto the carrier surface an irradiation process by means of
a radiation source of an appropriate wavelength is carried out.
[0066] In addition to the use of a primer it is possible to apply
the decor onto a decorative paper printable with the corresponding
decor, which may be provided by means of a resin layer as a bonding
agent previously applied onto the carrier. Such a printing base is
suitable for flexographic printing, offset printing or screen
printing as well as in particular for digital printing techniques
such as inkjet processes or laser printing. For the application of
the resin layer it may be preferably provided that a resin
composition is applied, which as a resin component at least
comprises one compound selected from the group consisting of
melamine resin, formaldehyde resin, urea resin, phenol resin, epoxy
resin, unsaturated polyester resin, diallyl phthalate or mixtures
thereof. Herein, the resin composition can, for example, be applied
in an area density between .gtoreq.5 g/m.sup.2 and .ltoreq.40
g/m.sup.2, preferably .gtoreq.10 g/m.sup.2 and .ltoreq.30
g/m.sup.2. Further, a paper or a non-woven fabric with a grammage
between .gtoreq.30 g/m.sup.2 and .ltoreq.80 g/m.sup.2, preferably
between .gtoreq.40 g/m.sup.2 and .ltoreq.70 g/m.sup.2, can be
applied onto the plate-shaped carrier.
[0067] Moreover according to the invention a protective layer can
be applied on at least a portion of the decor. Such a layer for
protecting the applied decor can in particular be applied in a
subsequent process step as a wearing or top layer on top of the
decorative layer, and in particular protects the decorative layer
against wear or damage caused by dirt, moisture or mechanical
impacts, such as abrasion. For example, it may be provided that the
wearing and/or top layer is laid onto the printed carrier as a
prefabricated overlay layer, such as based on melamine, and is
bonded thereto by means of pressure and/or heat. Moreover, it may
be preferred that for the formation of the wearing and/or top
layer, too, a radiation curable composition, for example a
radiation curable varnish such as an acrylic varnish, is applied.
Herein, it may be provided that the wearing layer includes hard
materials such as titanium nitride, titanium carbide, silicon
nitride, silicon carbide, boron carbide, tungsten carbide, tantalum
carbide, alumina (corundum), zirconia or mixtures thereof, in order
to increase the wear resistance of the layer. Herein, the coating
can be applied, for example, by means of rollers such as rubber
rollers or by means of pouring devices.
[0068] Furthermore, the top layer can initially be partially cured
and subsequently a final coating with an urethane acrylate and a
final curing step e.g. by use of a gallium emitter can be
conducted.
[0069] Moreover, the top and/or wearing layer can comprise means
for reducing the static (electrostatic) charging of the finished
laminate. For example, it may be provided that the top and/or
wearing layer to this end comprises compounds such as choline
chloride. Herein, the antistatic agent may, for example, be
included in the composition for forming the top and/or wearing
layer at a concentration between .gtoreq.0,1 wt. % and .ltoreq.40,0
wt. %, preferably between .gtoreq.1,0 wt. % and .ltoreq.30,0 wt.
%.
[0070] Moreover, it can be provided that in the protective layer or
in the wearing or top layer a texture, in particular a surface
texture matching with the decor is produced by introducing pores.
Herein, it may be provided that the carrier plate already has a
texture and an alignment of a printing tool for applying the decor
with respect to the carrier plate is implemented depending on the
texture of the carrier plate which is detected by means of optical
methods. Herein, for aligning the printing tool and the carrier
plate relative to each other it can be provided that a relative
movement between the printing tool and the carrier plate necessary
for the alignment is implemented by shifting the carrier plate or
by shifting the printing tool. Moreover, it can be provided that a
texturing of the decorative panel is implemented subsequently to
the application of the top and/or wearing layer. To this end it may
be preferred to apply a settable composition as the top and/or
wearing layer and a curing process is done solely to the extent
that only a partial curing of the top and/or wearing layer is
achieved. In the thus partially cured layer by means of appropriate
tools, such as a hard metal texture roller or a die, a desired
surface texture is embossed. Herein, the embossing process is
implemented in correspondence with the applied decor. In order to
ensure a sufficient correspondence of the texture to be produced
with the decor it may be provided that the carrier plate and the
embossing tool are aligned relative to each other by corresponding
relative movements. Subsequently to the production of the desired
texture within the partially cured top and/or wearing layer a
further curing step is implemented with respect to the now textured
top and/or wearing layer.
[0071] In many cases it is provided that a surface texture matching
with the decor is introduced within such a wearing and/or top
layer. A surface texture matching with the decor means that the
surface of the decorative panel has a haptically perceptual
structure, which according to its shape and pattern corresponds to
the applied decor in order to achieve a reproduction of a natural
material as close to the original as possible even with respect to
the haptic.
[0072] In addition, on the side opposite to the decor side a
counteracting means may be applied. Herein, it is particularly
preferred that the counteracting means is applied in a common
calendering step with the paper or non-woven fabric on the decor
side.
[0073] By partially profiling the decorative panel not all profiles
to be provided in the finished panel are produced, but only a part
of the profiles, while other profiles are produced in a subsequent
step. Thus, it may be provided, for example, that the decorative
profile to be provided in a panel, such as a chamfer, is produced
in one step, while the functional profile, e.g. groove/tongue, is
produced in a subsequent step.
[0074] By means of the application of the decor subsequently to the
at least partially profiling of the carrier, for example, by means
of the above-described methods, such as direct printing, abrasion
or damage of the decor in the course of the profiling process is
avoided in an advantageous way. Thus, the decor also in the regions
of the profile corresponds in detail the desired imitation, for
example, of a natural material.
[0075] In order to provide a particular detailed imitation even in
the profiled regions the master used for the printing process can
be distortion corrected in the region of the profile of the panel.
Distortion correction in the sense of the invention means, for
example, with respect to the exemplary case of application by means
of a printing process, that the distortion of the printed image
caused by the deviation of the profiling out of the surface plane
of the carrier, for example, at a chamfer edge, is corrected by
matching the master with the deviation. Herein, it may be provided,
for example, that the correction of the distortion is implemented
by matching the pixel spacing, the pixel size and/or the ink
application depending on the intended edge profile of the finished
decorative panel. Herein, in case of printing by means of digital
printing the print head can be driven depending on the distortion
to be corrected, such that the print head, for example, is
deflected beyond the profiled region and the ink discharge is
adapted to the profile.
[0076] Here, it is e.g. possible that prior to the application of
the decorative layer of the carrier provided as a large plate, the
joints (such as V-joints) to be provided in the final panel
laminate, are milled into the carrier, on the thus profiled carrier
at least the decorative layer is applied and subsequently the
carrier is cut and separated at least in the profiled areas.
Herein, depending on the cutting method, such as sawing, laser or
water jet cutting, it may be preferred that the required bleed
allowance is taken into account in the produced profile.
[0077] For example, the plate-shaped carrier can comprise a
material which is based on a WPC material or a PVC material. With
respect to the exact composition and the advantages resulting
therefrom we explicitly refer to the above description of the
method.
[0078] According to another embodiment, it may be provided that the
decorative panel is profiled at least in an edge region of the
carrier plate. Here, it may be in particular provided that the
decor is applied also in the region of the profiling, such that the
profiling can be implemented prior to the application of the
decorative layer onto the plate-shaped carrier. Alternatively or in
addition a profiling can be implemented subsequently to the
application of the decorative layer. In profiling in the sense of
the invention it is provided that by means of suitable machining
tools at least in a portion of the edges of the decorative panel a
decorative and/or functional profile is introduced. Here, a
functional profile, for example, means the introduction of a groove
and/or tongue profile in an edge in order to make decorative panels
connectable to each other by means of the introduced profiles. A
decorative profile in the sense of the invention, for example, is a
chamfer formed at the edge region of the decorative panel, for
example, in order to simulate a joint between two interconnected
panels, such as for example in so-called wide planks.
* * * * *