U.S. patent application number 14/713235 was filed with the patent office on 2015-09-17 for coated and cured proppants.
The applicant listed for this patent is Preferred Technology, LLC. Invention is credited to Avis Lloyd McCrary, Robert Ray McDaniel.
Application Number | 20150259592 14/713235 |
Document ID | / |
Family ID | 47601460 |
Filed Date | 2015-09-17 |
United States Patent
Application |
20150259592 |
Kind Code |
A1 |
McDaniel; Robert Ray ; et
al. |
September 17, 2015 |
Coated And Cured Proppants
Abstract
Solid proppants are coated with a coating that exhibits the
handling characteristics of a precured coating while also
exhibiting the ability to form particle-to-particle bonds at the
elevated temperatures and pressures within a wellbore. The coating
includes a substantially homogeneous mixture of (i) at least one
isocyanate component having at least 2 isocyanate groups, and (ii)
a curing agent. The coating process can be performed with short
cycle times, e.g., less than about 4 minutes, and still produce a
dry, free-flowing, coated proppant that exhibits low dust
characteristics during pneumatic handling but also proppant
consolidation downhole for reduced washout and good
conductivity.
Inventors: |
McDaniel; Robert Ray;
(Cypress, TX) ; McCrary; Avis Lloyd; (Montgomery,
TX) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Preferred Technology, LLC |
Radnor |
PA |
US |
|
|
Family ID: |
47601460 |
Appl. No.: |
14/713235 |
Filed: |
May 15, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13188530 |
Jul 22, 2011 |
9040467 |
|
|
14713235 |
|
|
|
|
13099893 |
May 3, 2011 |
8993489 |
|
|
13188530 |
|
|
|
|
Current U.S.
Class: |
507/219 ;
427/212; 427/221 |
Current CPC
Class: |
C09K 8/805 20130101;
Y10S 507/924 20130101 |
International
Class: |
C09K 8/80 20060101
C09K008/80 |
Claims
1-33. (canceled)
34. A coated core particle that is substantially covered with a
substantially cured coating that comprises at least one isocyanate
component, a hydroxy-functional polyether polyol, at least one tin
complex catalyst, wherein said coating can form
particle-to-particle bonds under downhole conditions.
35. The coated core particle of claim 34, wherein said coating can
form particle-to-particle bonds that exhibit an unconfined
compressive strength sufficient to generate proppant consolidation
and provide flowback control.
36. The coated core particle of claim 34, wherein said coating can
form particle-to-particle bonds under downhole conditions that
exhibit an unconfined compressive strength of greater than 100
psi.
37. The coated core particle of claim 34, wherein the coated core
particle resists proppant flowback at elevated temperature and
pressure.
38. The coated core particle of claim 34, wherein the coated core
particle exhibits a negative TMA slope within the range of about
125.degree. C. and 175.degree. C.
39. The coated core particle of claim 34, wherein said coated core
particle exhibits a loss of coating of less than 15 wt % when
tested according to ISO 13503-5:2006(E).
40. The coated core particle of claim 34, wherein the coating
comprises one or more of decarboxylated cashew nut oil, castor oil,
cardol and cardanol.
41. The coated core particle of claim 34, wherein the coating
further comprises an adhesion agent.
42. The coated core particle of claim 41, wherein the adhesion
agent is a silane.
43. The coated core particle of claim 34, wherein the core particle
is a ceramic core particle.
44. The coated core particle of claim 34, wherein the core particle
is a sand particle.
45. The coated core particle of claim 34, wherein the coating
further comprises a pigment, dye, or tint.
46. The coated core particle of claim 34, wherein the coating
further comprises mica.
47. A process for making the coated core particle of claim 34, the
process comprising mixing a core particle with at least one
isocyanate component, a hydroxy-functional polyether polyol, and at
least one tin complex catalyst under conditions to coat the core
particle with a substantially cured coating that comprises at least
one isocyanate component, a hydroxy-functional polyether polyol and
at least one tin complex catalyst.
48. The process of claim 47, further comprising mixing the core
particle with an adhesion agent.
49. The process of claim 48, wherein the adhesion agent is a
silane.
50. The process of claim 47, wherein the core particle is a sand
particle or a ceramic particle.
51. The process of claim 47, further comprising mixing the core
particle with a pigment, dye, or tint.
52. The process of claim 47, wherein the process comprises: a)
mixing the core particle with a silane; b) mixing the product of
step a) with the polyol and the tin catalyst; c) mixing the product
of step b) with the isocyanate.
53. The process of claim 52, further comprising mixing the product
of step c) with a silane.
Description
RELATED APPLICATIONS
[0001] This application is a continuation-in-part of U.S. patent
application Ser. No. 13/099,893 entitled "Coated and Cured
Proppants" and filed on May 3, 2011. The contents of this
co-pending application are hereby incorporated by reference.
FIELD OF INVENTION
[0002] The invention relates to a method for the production of
coated proppants, and also to the proppants obtained according to
this method, to the uses thereof and to methods which use the
proppants.
BACKGROUND OF THE INVENTION
[0003] Well factoring is an often used technique to increase the
efficiency and productivity of oil and gas wells. Overly
simplified, the process involves the introduction of a fracturing
fluid into the well and the use of fluid pressure to fracture and
crack the well strata. The cracks allow the oil and gas to flow
more freely from the strata and thereby increase production rates
in an efficient manner.
[0004] There are many detailed techniques involved in well
fracturing, but one of the most important is the use of a solid
"proppant" to keep the strata cracks open as oil, gas, water and
other fluids found in well flow through those cracks. The proppant
is carried into the well with the fracturing fluid which itself may
contain a variety of viscosity enhancers, gelation agents,
surfactants, etc. These additives also enhance the ability of the
fracturing fluid to carry proppant to the desired strata depth and
location. The fracturing fluid for a particular well may or may not
use the same formulation for each depth in the strata.
[0005] Proppants can be made of virtually any generally solid
particle that has a sufficiently high crush strength to prop open
cracks in a rock strata at great depth and temperatures of about
35.degree. C. and higher. Sand and ceramic proppants have proved to
be especially suitable for commercial use.
[0006] A proppant that is flushed from the well is said to have a
high "flow back." Flow back is undesirable. In addition to closure
of the cracks, the flushed proppants are abrasive and can damage or
clog the tubular goods used to complete the well, valves and
pipelines in downstream processing facilities.
[0007] One type of synthetic resin coatings can be used to impart a
degree of adhesion to the proppant so that flow back is
substantially reduced or eliminated. Such resins can include phenol
resin, epoxy resin, polyurethane-phenol resin, furane resin, etc.
See published US Patent Application No. 2002/0048676, 2003/0131998,
2003/0224165, 2005/0019574, 2007/0161515 and 2008/0230223 as well
as U.S. Pat. Nos. 4,920,192; 5,048,608; 5,199,491; 6,406,789;
6,632,527; 7,624,802; and published international application WO
2010/049467, the disclosures of which are herein incorporated by
reference.
[0008] With some coatings, the synthetic coating is not completely
cured when the proppant is introduced into the well. The coated,
partially-cured proppants are free flowing, but the coating resin
is still slightly reactive. The final cure is intended to occur in
situ in the strata fracture at the elevated closure pressures and
temperatures found "down hole."
[0009] Such partially cured coating can also exhibit a number of
performance issues ranging from: [0010] A lack of storage stability
if stored in a hot environment. This type situation could result in
a completion of the curing process (while in storage) making the
coated proppant incapable of bonding when placed in the fracture.
[0011] Leaching chemicals out of the partially cured coating that
could interfere when the viscosity profile of the fluid used to
carry the proppant into the fracture or the chemical breaker system
that is relied on to reduce the frac fluid viscosity after
completion of the fracturing treatment. [0012] Erosion of the
partially cured coating when the coated proppant is handled
pneumatically in order to place in the field storage bins at the
well site.
[0013] A second type of synthetic coating is described as being
precured or tempered. In this case the coating is essentially cured
during the manufacturing process. This type of coating will
strengthen the substrate particle so that it can withstand a higher
stress level before grain failure. Such a precured coating with
also exhibit the following traits: 1) Excellent storage stability;
2) Minimal chemicals that can be leached out of the coating to
interfere with carrier fluid viscosity or breaker systems; and 3) A
coating that is resilient to the abrasion of pneumatic
handling.
[0014] The main limitation of a precured coating is that it can not
create significant particle to particle bonding when placed in the
fracture an temperature and closure pressure are applied. This
means that a precured coated particle can do little to prevent
proppant flowback after the well is opened up to start the clean-up
process or to produce the well.
[0015] Proppants based on polyurethane chemistries have a number of
potential advantages over phenol resin systems. Most notably, the
reaction rates used to make polyurethane coatings are generally
faster than phenol resins, cure at lower temperatures and do not
have gaseous emissions that require specialized recovery equipment.
The coating step with polyurethanes can be carried out at
temperatures of about 10.degree. C. to about 250.degree. C.
although temperatures of less than about 100.degree. C. are
preferred to minimize emissions during the coating process as well
as energy use. Polyurethane coatings can also be performed without
the use of solvents, whereas many of the known methods, as a rule,
require organic solvents for the resinous coating. The components
in polyurethane systems are also generally easier to use and pose
lower environmental issues. These factors could reduce the cost to
make coated proppants and could also permit the coating process to
be moved to the site of the well head.
[0016] Polyurethanes have not, however, achieved widespread
adoption due to their performance in the hot, wet, high pressured
environment encountered in the fracture. The stability of the
coating to this environment, the ability of the coating to prevent
particle failure (e.g., by crushing) and to develop strong
particle-to-particle bonds, have contributed to poor flowback
control and less than desirable fracture conductivity.
SUMMARY OF THE INVENTION
[0017] It would be desirable to develop a coated proppant that
combined adequate crush resistance, resistance to dusting when
handled pneumatically and the limited leaching of chemicals that is
exhibited by precured coatings with the ability to create the
particle-to-particle reaction bonds that resist proppant flowback
which are exhibited by a partially cured proppant coating.
[0018] It would also be desirable to have a coated proppant that
retained its conductivity under the conditions prevailing within an
actively producing well field stratum.
[0019] It would further be desirable to have a coating that not
only exhibited all of these properties but which had desirable
fracture conductivity and a short production cycle.
[0020] It would be especially preferred if a proppant could be
substantially covered with a fast cure coating that could be
produced to a free flowing state in a short period, e.g., less than
about four minutes, while also exhibiting good crush resistance,
resistance to hot water coating loss and low dust generation during
pneumatic conveyance.
[0021] These and other objectives of the invention that will become
apparent from the description herein can be accomplished by a
coating and coating process that comprises the step of: coating a
proppant solid with a substantially homogeneous coating mixture
that comprises (i) at least one isocyanate component having at
least 2 isocyanate groups, and (ii) at least one curing agent in an
amount sufficient and under conditions sufficient to substantially
cure said proppant coating and form free flowing, coated proppants
in a period of time of less than about four minutes to form a
free-flowing, substantially cured, coated proppant.
[0022] A coated, fee flowing proppant according to the invention
comprises a solid proppant core particle that is substantially
covered with a coating that comprises the reaction product of a
coating mixture that comprises at least one isocyanate component
and a curing agent to form a substantially fully cured proppant
coating that is capable of forming particle-to-particle bonds at
elevated temperature and pressure, such as those found downhole in
an oil or gas well.
[0023] The coating process of the present invention applies one or
more layers of cured polyurethane around a solid proppant core that
is substantially cured and crosslinked quickly to produce a coated
proppant product that acts like it has a hybrid coating, i.e., one
that acts like a precured coating in its resists dissolution of the
coating under the rigorous combination of high heat, agitation,
abrasion and water found downhole in an oil or gas well; exhibits
good crush resistance; and has a tough coating that exhibits low
levels of dust generation during pneumatic conveyance but also
exhibits traits of a partially cured coating in its ability to form
particle-particle bonds with similarly coated proppants at downhole
conditions. In addition, the coating process has a high production
rate due to its low cycle time for the coating/curing process, low
emission level and a low overall production cost.
BRIEF DESCRIPTION OF THE FIGURES
[0024] FIG. 1 is a TMA plot of Dimension Change at various
Temperatures in a TMA test of precured, partially cured Phenolic A,
partially cured Phenolic B that is more curable than Phenolic A,
and the coating of the present invention as discussed in Example
6.
[0025] FIG. 2 is a bar chart of crush test results of various
coated proppants tested in Example 6.
[0026] FIG. 3 is a chart of Unconfined Compressive Strength for the
coated proppants of Example 6.
[0027] FIG. 4 charts the fracture conductivity of three coated
proppants used in Example 6.
[0028] FIG. 5 depicts the results of coating loss tests
(colloquially referred to as "Loss On Ignition") in simulated well
down-hole conditions.
DETAILED DESCRIPTION OF THE INVENTION
[0029] The coating formulation of the present invention includes a
substantially homogeneous mixture that comprises: (a) at least one
isocyanate reactant having at least 2 isocyanate groups, and (ii)
at least one curing agent. The coating may further comprise one or
more curing agents in the form of amine reactants, metal catalysts,
hydroxyl-functional curing agents and/or polyols. The components
are used in an amount sufficient and under conditions that are also
sufficient to substantially cure the proppant coating and form free
flowing, coated proppants in a fairly short period of time. The
coated proppant thus exhibits the good handling and low dust
characteristics of a precured product but also exhibits in-strata
consolidation characteristics and flow-back resistance that are
like a partially cured product.
[0030] The coating process of the present invention applies one or
more layers of curable coating around a solid proppant core that is
quickly and substantially cured to resist dissolution of the
coating under the rigorous combination of high heat, agitation,
abrasion and water that are found downhole in a well. Preferably,
the cured coating exhibits a sufficient resistance to a 10 day
autoclave test or 10 day conductivity test so that the coating
resists loss by dissolution in hot water ("LOI loss") of less than
25 wt %, more preferably less than 15 wt %, and even more
preferably a loss of less than 5 wt %. The substantially cured
coating of the invention thus resists dissolution in the fractured
stratum while also exhibiting sufficient particle-to-particle
reaction bond strength to resist flow back and sufficiently high
crush strength to maintain conductivity of the fractures.
[0031] A preferred testing method for the effectiveness of a
proppant is described in ISO 13503-5:2006(E) "Procedures for
measuring the long term conductivity of proppants", the disclosure
of which is herein incorporated by reference. ISO 13503-5:2006
provides standard testing procedures for evaluating proppants used
in hydraulic fracturing and gravel packing operations. ISO
13503-5:2006 provides a consistent methodology for testing
performed on hydraulic fracturing and/or gravel packing proppants.
The "proppants" mentioned henceforth in this part of ISO
13503-5:2006 refer to sand, ceramic media, resin-coated proppants,
gravel packing media, and other materials used for hydraulic
fracturing and gravel-packing operations. ISO 13503-5:2006 is not
applicable for use in obtaining absolute values of proppant pack
conductivities under downhole reservoir conditions, but it does
serve as a consistent method by which such downhole conditions can
be simulated and compared in a laboratory setting.
The Isocyanate Component
[0032] The isocyanate component comprises an isocyanate with at
least 2 reactive isocyanate groups. Other isocyanate-containing
compounds may be used, if desired. Examples of suitable isocyanate
with at least 2 isocyanate groups an aliphatic or an aromatic
isocyanate with at least 2 isocyanate groups (e.g. a diisocyanate,
triisocyanate or tetraisocyanate), or an oligomer or a polymer
thereof can preferably be used. These isocyanates with at least 2
isocyanate groups can also be carbocyclic or heterocyclic and/or
contain one or more heterocyclic groups.
[0033] The isocyanate with at least 2 isocyanate groups is
preferably a compound or oligomer of compounds of the formula (III)
or a compound of the formula (IV):
##STR00001##
[0034] In the formulas (III) and (IV), A is each, independently, an
aryl, heteroaryl, cycloalkyl or heterocycloalkyl. Preferably, A is
each, independently, an aryl or cycloalkyl. More preferably A is
each, independently, an aryl which is preferably phenyl, naphthyl
or anthracenyl, and most preferably phenyl. Still more preferably A
is a phenyl.
[0035] The above mentioned heteroaryl is preferably a heteroaryl
with 5 or 6 ring atoms, of which 1, 2 or 3 ring atoms are each,
independently, an oxygen, sulfur or nitrogen atom and the other
ring atoms are carbon atoms. More preferably the heteroaryl is
selected among pyridinyl, thienyl, furyl, pyrrolyl, imidazolyl
pyrazolyl, pyrazinyl, pyrimidinyl, pyridazinyl, oxazolyl,
isoxazolyl or furazanyl.
[0036] The above mentioned cycloalkyl is preferably a
C.sub.3-10-cycloalkyl, more preferably a C.sub.5-7-cycloalkyl.
[0037] The above mentioned heterocycloalkyl is preferably a
heterocycloalkyl with 3 to 10 ring atoms (more preferably with 5 to
7 ring atoms), of which one or more (e.g. 1, 2 or 3) ring atoms are
each, independently, an oxygen, sulfur or nitrogen atom and the
other ring atoms are carbon atoms. More preferably the
heterocycloalkyl is selected from among tetrahydrofuranyl,
piperidinyl, piperazinyl, aziridinyl acetidinyl, pyrrolidinyl,
imidazolidinyl, morpholinyl, pyrazolidinyl, tetrahydrothienyl,
octahydroquinolinyl octahydroisoquinolinyl, oxazolidinyl or
isoxazolidinyl. Still more preferably, the heterocycloalkyl is
selected from among tetrahydrofuranyl, piperidinyl, piperazinyl,
pyrrolidinyl, imidazolidinyl, morpholinyl, pyrazolidinyl,
tetrahydrothienyl, oxazolidinyl or isoxazolidinyl.
[0038] In the formulas (III) and (IV), each R.sup.1 is,
independently, a covalent bond or C.sub.1-4-alkylene (e.g.
methylene, ethylene, propylene or butylene). Preferably each
R.sup.2 is hydrogen or a covalent bond.
[0039] In the formulas (III) and (IV), each R.sup.2 is each,
independently, hydrogen, a halogen (e.g. F, Cl, Br or I), a
C.sub.1-4-alkyl (e.g. methyl, ethyl, propyl or butyl) or
C.sub.1-4-alkyoxy (e.g. methoxy, ethoxy, propoxy or butoxy).
Preferably, each R.sup.2 is, independently, hydrogen or a
C.sub.1-4-alkyl. More preferably each R.sup.2 is hydrogen or
methyl.
[0040] In the formula (IV), R.sup.3 is a covalent bond, a
C.sub.1-4-alkylene (e.g. methylene, ethylene, propylene or
butylene) or a group --(CH.sub.2).sub.R31--O--(CH.sub.2).sub.R32--,
wherein R31 and R32 are each, independently, 0, 1, 2 or 3.
Preferably, R.sup.3 is a --CH.sub.2-- group or an --O-- group.
[0041] In the formula (III), p is equal to 2, 3 or 4, preferably 2
or 3, more preferably 2.
[0042] In the formulas (III) and (IV), each q is, independently, an
integer from 0 to 4, preferably 0, 1 or 2. When q is equal to 0,
the corresponding group A has no substituent R.sup.2, but has
hydrogen atoms instead of R.sup.2.
[0043] In the formula (IV), each r and s are, independently, 0, 1,
2, 3 or 4, wherein the sum of r and s is equal to 2, 3 or 4.
Preferably, each r and s are, independently, 0, 1 or 2, wherein the
sum of r and s is equal to 2. More preferably, r is equal to 1 and
s is equal to 1.
[0044] Examples of the isocyanate with at least 2 isocyanate groups
are: toluol-2,4-diisocyanate; toluol-2,6-diisocyanate;
1,5-naphthalindiisocyanate; cumol-2,4-diisocyanate;
4-methoxy-1,3-phenyldiisocyanate; 4-chloro-1,3-phenyldiisocyanate;
diphenylmethane-4,4-diisocyanate; diphenylmethane-2,4-diisocyanate;
diphenylmethane-2,2-diisocyanate; 4-bromo-1,3-phenyldiisocyanate;
4-ethoxy-1,3-phenyl-diisocyanate; 2,4'-diisocyanate diphenylether;
5,6-dimethyl-1,3-phenyl-diisocyanate; methylenediphenyl
diisocyanate (including 2,2'-MDI, 2,4'-MDI and 4,4''-MDI);
4,4-diisocyanato-diphenylether;
4,6-dimethyl-1,3-phenyldiisocyanate; 9,10-anthracene-diisocyanate;
2,4,6-toluol triisocyanate; 2,4,4'-triisocyanatodiphenylether;
1,4-tetramethylene diisocyanate; 1,6-hexamethylene diisocyanate;
1,10-decamethylene-diisocyanate; 1,3-cyclohexylene diisocyanate;
4,4'-methylene-bis-(cyclohexylisocyanate); xylol diisocyanate;
1-isocyanato-3-methyl-isocyanate-3,5,5-trimethylcyclohexane
(isophorone diisocyanate); 1-3-bis(isocyanato-1-methylethyl) benzol
(m-TMXDI); 1,4-bis(isocyanato-1-methylethyl) benzol (p-TMXDI);
oligomers or polymers of the above mentioned isocyanate compounds;
or mixtures of two or more of the above mentioned isocyanate
compounds or oligomers or polymers thereof.
[0045] Particularly preferred isocyanates with at least 2
isocyanate groups are toluol diisocyanate, methylenediphenyl
diisocyanate, diphenylmethane diisocyanate, an oligomer based on
toluol diisocyanate, an oligomer based on methylenediphenyl
diisocyanate (poly-MDI) or an oligomer based on diphenylmethane
diisocyanate and polymers thereof.
Curing Agents
[0046] The coatings of the invention can be cured with at least one
of a variety of curing agents, including reactive, non-reactive
(e.g., "catalysts") and partially reactive agents. Generally,
preferred curing agents are selected from amine-based curing
agents, hydroxyl-functional curing agents, polyols, and/or
metal-based catalysts. The amine-based curing agents may also be
used as a mixture of a fast-acting first curing agent and a second,
latent curing agent. Either of these first and/or second
amine-based curing agents may be reactive, nonreactive or partially
reactive.
[0047] Suitable single amine-based curing agent or a mixture of
amine-based curing agents can include, but are not limited to,
ethylene diamine; hexamethylene diamine; 1-methyl-2,6-cyclohexyl
diamine; 2,2,4- and 2,4,4-trimethyl-1,6-hexanediamine;
4,4'-bis-(sec-butylamino)-dicyclohexylmethane and derivatives
thereof; 1,4-bis-(sec-butylamino)-cyclohexane;
1,2-bis-(sec-butylamino)-cyclohexane; 4,4'-dicyclohexylmethane
diamine; 1,4-cyclohexane-bis-(methylamine);
1,3-cyclohexane-bis-(methylamine), isomers, and mixtures thereof;
diethylene glycol bis-(aminopropyl)ether;
2-methylpentamethylene-diamine; diaminocyclohexane, isomers, and
mixtures thereof; diethylene triamine; triethylene tetramine;
tetraethylene pentamine; propylene diamine; 1,3-diaminopropane;
dimethylamino propylamine; diethylamino propylamine;
imido-bis-(propylamine); monoethanolamine, diethanolamine;
triethanolamine; monoisopropanolamine, diisopropanolamine;
isophoronediamine; 4,4'-methylenebis-(2-chloroaniline);
3,5-dimethylthio-2,4-toluenediamine;
3,5-dimethylthio-2,6-toluenediamine;
3,5-diethylthio-2,4-toluenediamine;
3,5-diethylthio-2,6-toluenediamine;
4,4'-bis-(sec-butylamino)-benzene; and derivatives thereof;
1,4-bis-(sec-butylamino)-benzene; 1,2-bis-(sec-butylamino)-benzene;
N,N'-dialkylamino-diphenylmethane;
trimethyleneglycol-ci-p-aminobenzoate;
polytetramethyleneoxide-di-p-aminobenzoate;
4,4'-methylenebis-(3-chloro-2,6-diethyleneaniline);
4,4'-methylenebis-(2,6-diethylaniline); meta-phenylenediamine;
paraphenylenediamine; N,N'-diisopropyl-isophoronediamine;
polyoxypropylene diamine; propylene oxide-based triamine;
3,3'-dimethyl-4,4'-ciaminocyclohexylmethane; and mixtures thereof.
In one embodiment, the amine-terminated curing agent is
4,4'-bis-(sec-butylamino)-dicyclohexylmethane. Preferred
amine-based curing agents for use with the present invention
include triethylenediamine; bis(2-dimethylaminoethyl)ether;
tetramethlethylenediamine; pentamethyldiethylenetriamine;
1,3,5-tris(3-(dimethylamino)propyl)-hexahydro-s-triazine and other
tertiary amine products of alkyleneamines.
[0048] Additionally, other catalysts that promote the reaction of
isocyanates with hydroxyls and amines that are known by the
industry can be used in the present invention, e.g., transition
metal co-catalysis of Groups III or IV used for polyurethane foams.
A particularly preferred metal co-catalyst is a tin complex such as
stannous 2-ethylhexanoate.
[0049] The amine-based curing agent may have a molecular weight of
about 64 or greater. In one embodiment, the molecular weight of the
amine-curing agent is about 2000 or less. In addition, any of the
amine-terminated moieties listed above for use as the
isocyanate-reactive component to form the prepolymer may be used as
curing agents to react with the prepolymers.
[0050] Of the list above, the saturated amine-based curing agents
suitable for use with the present invention include, but are not
limited to, ethylene diamine; hexamethylene diamine;
1-methyl-2,6-cyclohexyl diamine; 2,2,4- and
2,4,4-trimethyl-1,6-hexanediamine;
4,4'-bis-(sec-butylamino)-dicyclohexylmethane;
1,4-bis-(sec-butylamino)-cyclohexane;
1,2-bis-(sec-butylamino-cyclohexane; derivatives of
4,4'-bis-(sec-butylamino)-dicyclohexylmethane;
4,4'-dicyclohexylmethane diamine;
1,4-cyclohexane-bis-(methylamine);
1,3-cyclohexane-bis-(methylamine); diethylene glycol
bis-(aminopropyl) ether; 2-methylpentamethylene-diamine;
diaminocyclohexane; diethylene triamine; triethylene tetramine;
tetraethylene pentamine; propylene diamine; dipropylene triamine;
1,3-diaminopropane; dimethylamino propylamine; diethylamino
propylamine; imido-bis-(propylamine); monoethanolamine,
diethanolamine; triethanolamine; monoisopropanolamine,
diisopropanolamine; triisopropanolamine; isophoronediamine;
N,N'-diisopropylisophorone diamine and mixtures thereof.
[0051] In one embodiment, the curative used with the prepolymer
include
3,5-dimethylthio-2,4-toluenediamine,3,5-dimethyl-thio-2,6-toluenediamine,
4,4'-bis-(sec-butylamino)-diphenylmethane,
N,N'-diisopropyl-isophorone diamine; polyoxypropylene diamine;
propylene oxide-based triamine;
3,3'-dimethyl-4,4'-diaminocyclohexylmethane; and mixtures
thereof.
[0052] Because unhindered primary diamines result in a rapid
reaction between the isocyanate groups and the amine groups, in
certain instances, a hindered secondary diamine may be more
suitable for use in the prepolymer. Without being bound to any
particular theory, it is believed that an amine with a high level
of stearic hindrance, e.g., a tertiary butyl group on the nitrogen
atom, has a slower reaction rate than an amine with no hindrance or
a low level of hindrance. For example,
4,4'-bis-(sec-butylamino)-dicyclohexylmethane (CLEARLINK 1000.RTM.
from Huntsman Corporation in The Woodlands, Tex.) may be suitable
for use in combination with an isocyanate to form the polyurea
prepolymer. In addition, N,N'-diisopropyl-isophorone diamine, also
available from Huntsman Corporation, under the tradename
JEFFLINK.RTM., may be used as the secondary diamine curing
agent.
[0053] In addition, a trifunctional curing agent can be used to
help improve cross-linking and, thus, to further improve the
chemical and/or abrasion resistance of the coating. In one
embodiment, a triol such as trimethylolpropane or a tetraol such as
N,N,N',N'-tetrakis (2-hydroxylpropyl)ethylenediamine may be added
to the formulations.
[0054] The curing agents of the present invention can be added to
the coating formulation with the polyol component, the
amine-reactive polyol component, any of the additives (e.g.,
coloring agents) or added simultaneously as any of these components
or pre-coated on the proppant. Preferably, the curing agent is
mixed with or co-applied to the solid proppant core as the first
isocyanate and any other reactants are mixed so that the curing
process has begun by the time the coating formulation is applied to
the surface of the solid proppant core. It is also possible to
premix the isocyanate and polyol together immediately before entry
into the mixer. This probably would give a slightly more uniform
distribution of the chemicals in the coating. Alternately, it would
be possible to premix the polyol and curing agent before they are
added to the isocyanate.
[0055] Most preferably, the isocyanate, polyol, combination of (a)
polyol and (b) curing agent or each individually are continuously
added to solid proppant in a moving mixer at a rate that is not
substantially greater than the rate of the crosslinking reaction
between and among the ingredients. The specific rate will depend on
the size of the mixer, the type of mixer, and whether batch or
continuous production is desired. The goal is to substantially
completely coat the proppant solid with a coating that becomes
cured in the mixer and is discharged as a free-flowing, discrete
particulates. The amperage draw rate of the mixer can be used as a
guide in tumbling-type mixers because the build-up of an uncured,
tacky coating on the proppant solids will increase the load on the
mixer motor which can be monitored by a simple amp meter. Adding
the reaction components at a rate that is consistent with the
reaction rate of the curing process avoids substantial increases in
amperage allows the coating process, avoids stalling the motor or
interrupting the coating process, and maximizes the productivity of
the equipment used to perform the coating/curing process. In a
preferred process using laboratory scale equipment, a few seconds
after beginning to add the polyol, the isocyanate is added at a
controlled rate over a relatively short period, e.g., about a
minute.
Hydroxy-Functional Cubing Agents
[0056] The prepolymers of the invention may also be cured with a
single hydroxy-terminated curing agent or a mixture of
hydroxy-terminated curing agents. Suitable hydroxy-terminated
curing agents include, but are not limited to, ethylene glycol;
diethylene glycol; polyethylene glycol; propylene glycol;
2-methyl-1,3-propanediol; 2,-methyl-1,4-butanediol; dipropylene
glycol; polypropylene glycol; 1,2-butanediol; 1,3-butanediol;
1,4-butanediol; 2,3-butanediol; 2,3-dimethyl-2,3-butanediol;
trimethylolpropane; cyclohexyldimethylol; triisopropanolamine;
N,N,N'N'-tetra-(2-hydroxypropyl)-ethylene diamine; diethylene
glycol bis-(aminopropyl)ether; 1,5-pentanediol; 1,6-hexanediol;
1,3-bis-(2-hydroxyethoxy)cyclohexane; 1,4-cyclohexyldimethylol;
1,3-bis-[2-(2-hydroxyethoxy)ethoxy]cyclohexane;
1,3-bis-{2-[2-(2-hydroxyethoxy)ethoxy]ethoxy}cyclohexane;
polytetramethylene ether glycol, preferably having a molecular
weight ranging from about 250 to about 3900;
resorcinol-di-(beta-hydroxyethyl)ether and its derivatives;
hydroquinone-di-(beta-hydroxyethyl)ether and its derivatives:
1,3-bis-(2-hydroxyethoxy)benzene;
1,3-bis-[2-(2-hydroxyethoxy)ethoxy]benzene;
1,3-bis-{2-[2-(2-hydroxyethoxy)ethoxy]ethoxy}benzene;
N,N-bis(.beta.-hydroxypropyl)aniline;
2-propanol-1,1'-phenylaminobis; and mixtures thereof.
[0057] The hydroxy-terminated curing agent may have a molecular
weight of at least about 50. In one embodiment, the molecular
weight of the hydroxy-terminated curing agent is about 2000 or
less. In yet another embodiment, the hydroxy-terminated curing
agent has a molecular weight of about 250 to about 3900. It should
be understood that molecular weight, as used herein, is the
absolute weight average molecular weight and would be understood as
such by one of ordinary skill in the art.
[0058] The saturated hydroxy-terminated curing agents, included in
the list above, are preferred when making a light stable
composition. Those saturated hydroxy-terminated curing agents
include, but are not limited to, ethylene glycol; diethylene
glycol; polyethylene glycol; propylene glycol;
2-methyl-1,3-propanediol; 2,-methyl-1,4-butanediol; dipropylene
glycol; polypropylene glycol; 1,2-butanediol; 1,3-butanediol;
1,4-butanediol; 2,3-butanediol; 2,3-dimethyl-2,3-butanediol;
trimethylolpropane; cyclohexyldimethylol; triisopropanolamine;
N,N,N',N'-tetra-(2-hydroxypropyl)-ethylene diamine; diethylene
glycol bis-(aminopropyl)ether; 1,5-pentanediol; 1,6-hexanediol;
1,3-bis-(2-hydroxyethoxy)cyclohexane; 1,4-cyclohexyldimethylol;
1,3-bis-[2-(2-hydroxyethoxy)ethoxy]cyclohexane;
1,3-bis-{2-[2-(2-hydroxyethoxy)ethoxy]ethoxy}cyclohexane;
polytetramethylene ether glycol having molecular weight ranging
from about 250 to about 3900; and mixtures thereof.
[0059] The amount of curing agent that is added to the coating will
generally fall within the range from about 0.01 wt % to about 95 wt
% of the complete coating formulation.
Polyol Curing Agents
[0060] A polyol component can be added to the coating formulation.
The polyol component may or may not have reactive amine
functionality. An especially preferred polyurethane coating is a
phenolic polyurethane made with a phenolic polyol according to a
patent application that was filed with the German Patent Office
under no. DE 10 2010 051 817.4 on Nov. 19, 2010 and entitled
"Proppant Coating Technology", the disclosure of which is herein
incorporated by reference and summarized below in the context of
the process of the present invention.
[0061] Another preferred polyol component for the present process
comprises a phenol resin that comprises a condensation product of a
phenol and an aldehyde, such as formaldehyde. The phenol resin is
preferably a resole or novolak phenol resin and more preferably a
benzyl ether resin.
[0062] The resole-type phenol resin can be obtained, for example,
by condensation of phenol or of one or more compounds of the
following formula (I), with aldehydes, preferably formaldehyde,
under basic conditions.
##STR00002##
[0063] In the formula (I):
[0064] "R" is in each case, independently, a hydrogen atom, a
halogen atom, C.sub.1-16-alkyl (preferably C.sub.1-12-alkyl more
preferably C.sub.1-6-alkyl, and still more preferably methyl,
ethyl, propyl or butyl) or --OH;
[0065] "p" is an integer from 0 to 4, preferably 0, 1, 2 or 3, and
more preferably 1 or 2. Those in the art will understand that when
p is 0, the compound of formula (I) is phenol.
[0066] Novolak-type phenol resin for the present invention
comprises the condensation product of phenol or of one or more
compounds of the formula (I) defined above, with aldehydes,
preferably formaldehyde, under acidic conditions.
[0067] In another preferred embodiment, the phenol resin is a
benzyl ether resin of the general formula (II):
##STR00003##
[0068] In the formula (II):
[0069] A, B and D each are, independently, a hydrogen atom, a
halogen atom, a C.sub.1-16-hydrocarbon residue,
--(C.sub.1-16-alkylene)-OH, --OH, an --O--(C.sub.1-16-hydrocarbon
residue), phenyl, --(C.sub.1-16-alkylene)-phenyl, or
--(C.sub.1-6-alkylene)-phenylene-OH;
[0070] The halogen atom is F, Cl, Br or I;
[0071] The C.sub.1-16-hydrocarbon-residue is preferably
C.sub.1-16-alkyl, C.sub.2-16-alkenyl or C.sub.2-16-alkinyl, more
preferably C.sub.1-12-alkyl, C.sub.2-12-alkenyl or
C.sub.2-12-alkinyl, still more preferably C.sub.1-6-alkyl,
C.sub.2-6-alkenyl or C.sub.2-6-alkinyl, and still more preferably
C.sub.1-4-alkyl, C.sub.2-4-alkenyl or C.sub.2-4alkinyl, and still
more preferably C.sub.1-12-alkyl, and still more preferably
C.sub.1-6-alkyl, and still more preferably methyl, ethyl, propyl or
butyl, and most preferably methyl;
[0072] The residue --(C.sub.1-16-alkylene)-OH is preferably
--(C.sub.1-12-alkylene)-OH, more preferably
--(C.sub.1-6-alkylene)-OH, and still more preferably
--(C.sub.1-4-alkylene)-OH, and most preferably a methylol group
(--CH.sub.2--OH);
[0073] The --O--(C.sub.1-16-hydrocarbon)-residue is preferably
C.sub.1-16-alkoxy, more preferably C.sub.1-12-alkoxy, and still
more preferably C.sub.1-6-alkoxy, and still more preferably
C.sub.1-4-alkoxy, and still more preferably --O--CH.sub.3,
--O--CH.sub.2CH.sub.3, --O--(CH.sub.2).sub.2CH.sub.3 or
--O--(CH.sub.2).sub.3CH.sub.3;
[0074] The residue --(C.sub.1-6-alkylene)-phenyl is preferably
--(C.sub.1-4-alkylene)-phenyl, and more preferably
--CH.sub.2-phenyl;
[0075] The residue --(C.sub.1-6-alkykne)-phenylene-OH is preferably
--(C.sub.1-4-alkylene)-phenylene-OH, and more preferably
--CH.sub.2-phenylene-OH;
[0076] R is a hydrogen atom of a C.sub.1-6-hydrocarbon residue
(e.g. linear or branched C.sub.1-6-alkyl). R is particularly
preferred as a hydrogen atom. This is the case, for example, when
formaldehyde is used as aldehyde component in a condensation
reaction with phenols in order to produce the benzyl ether resin of
the formula (II);
[0077] m.sup.1 and m.sup.2 are each, independently, 0 or 1.
[0078] n is an integer from 0 to 100, preferably an integer from 1
to 50, more preferably from 2 to 10, and still more preferably from
2 to 5; and
[0079] wherein the sum of n, m.sup.1 and m.sup.2 is at least 2.
[0080] In a still further embodiment, the polyol component is a
phenol resin, with monomer units based on cardol and/or cardanol.
Cardol and cardanol are produced from cashew nut oil which is
obtained from the seeds of the cashew nut tree. Cashew nut oil
consists of about 90% anacardic acid and about 10% cardol. By heat
treatment in an acid environment, a mixture of cardol and cardanol
is obtained by decarboxylation of the anacardic acid. Cardol and
cardanol have the structures shown below:
##STR00004##
[0081] As shown in the illustration above, the hydrocarbon residue
(--C.sub.15H.sub.31-n) in cardol and/or in cardanol can have one
(n=2), two (n=4) or three (n=6) double bonds. Cardol specifically
refers to compound CAS-No. 57486-25-6 and cardanol specifically to
compound CAS-No. 37330-39-5.
[0082] Cardol and cardanol can each be used alone or at any
particular mixing ratio in the phenol resin. Decarboxylated cashew
nut oil can also be used.
[0083] Cardol and/or cardanol can be condensed into the above
described phenol resins, for example, into the resole- or
novolak-type phenol resins. For this purpose, cardol and/or
cardanol can be condensed e.g. with phenol or with one or more of
the above defined compounds of the formula (I), and also with
aldehydes, preferably formaldehyde.
[0084] The amount of cardol and/or cardanol which is condensed in
the phenol resin is not particularly restricted and preferably is
from about 1 wt % to about 99 wt %, more preferably about 5 wt % to
about 60 wt %, and still mom preferably about 10 wt % to about 30
wt %, relative to 100 wt % of the amount of phenolic starting
products used in the phenol resin.
[0085] In another embodiment, the polyol component is a phenol
resin obtained by condensation of cardol and/or cardanol with
aldehydes, preferably formaldehyde.
[0086] A phenol resin which contains monomer units based on cardol
and/or cardanol as described above, or which can be obtained by
condensation of cardol and/or cardanol with aldehydes, has a
particularly low viscosity and can thus preferably be employed with
a low addition or without addition of reactive thinners. Moreover,
this kind of long-chain, substituted phenol resin is comparatively
hydrophobic, which results in a favorable shelf life of the coated
proppants obtained by the method according to the present
invention. In addition, a phenol resin of this kind is also
advantageous because cardol and cardanol are renewable raw
materials.
[0087] Apart from the phenol resin, the polyol component can still
contain other compounds containing hydroxyl groups. The other
compounds containing hydroxyl groups can be selected from the
compounds containing hydroxyl groups that are known to be useful
for making polyurethanes, e.g., hydroxy-functional polyethers,
hydroxy-functional polyesters, alcohols or glycols. One preferred
compound containing hydroxyl groups is, for instance, castor oil.
Compounds containing hydroxyl groups such as alcohols or glycols,
in particular cardol and/or cardanol, can be used as reactive
thinners.
[0088] The amount of the other compounds containing hydroxyl groups
depends on the desired properties of the proppant coating and can
suitably be selected by the person skilled in the art. Typical
amounts of compounds containing hydroxyl groups are in the range of
between about 10 wt % and about 80 wt %, preferably from about 20
wt % to about 70 wt %, relative to 100 wt % of the polyol
component.
[0089] The process of the present invention is particularly useful
when the proppants are coated with a condensation reaction product
that has been made with an excess of isocyanate component with
respect to the polyol or curing agent component. In step (a)
therefore, 100 parts by weight of the polyol component is used with
about 100 to about 600, preferably about 210 to about 530, more
preferably about 220 to about 420, and still more preferably about
230 to about 400 parts by weight of the isocyanate base value.
Ratios of iso:polyol from about 50:50 to as low as 100:0 are usable
depending on the equipment, conditions and production rate provided
that the coating and reaction are completed during the coating
process.
[0090] The isocyanate base value defines the amount of the
isocyanate component which is equivalent to 100 parts by weight of
the polyol component. The NCO-content (%) of the isocyanate
component is defined herein according to DIN ISO 53183. To
determine the OH-content (%) of the polyol component, first the
so-called OH-number is determined in mg KOH/g according to DIN ISO
53240 and this value is divided by 33, in order to determine the
OH-content. Thus, in step (a) an excess of NCO-groups in the
isocyanate component of between about 100 and about 500%,
preferably about 110 to about 430%, more preferably about 120% to
about 320%, and still more preferably about 130% to about 300%,
relative to the OH-groups in the polyol component is used.
[0091] Moreover, in step (a) one or more additives can be mixed
with the proppant, the polyol component and the isocyanate
component. These additives are not particularly restricted and can
be selected from the additives known in the specific field of
coated proppants. Provided that one of these additives has hydroxyl
groups, it should be considered as a different
hydroxyl-group-containing compound, as described above in
connection with the polyol component. If one of the additives has
isocyanate groups, it should be considered as a different
isocyanate-group-containing compound. Additives with hydroxyl
groups and isocyanate groups can be simultaneously considered as
different hydroxyl-group-containing compounds and as different
isocyanate-group-containing compounds.
Reactive Amines
[0092] The coating formulation of the present invention also
optionally includes a reactive amine component, preferably an
amine-terminated compound. The coating formulation can, however, be
made effectively and with good properties in the absence or
substantial absence of a reactive amine component apart from the
reactive polyol and isocyanate components. The reactive amine
component can enhance crosslink density within the coating and,
depending on component selection, can provide additional
characteristics of benefit to the cured coating. Reactive amine
components for use in the present invention include
amine-terminated compounds such as diamines, triamines,
amine-terminated glycols such as the amine-terminated polyalkylene
glycols sold commercially under the trade name JEFFAMINE from
Huntsman Performance Products in The Woodlands, Tex.
[0093] Suitable diamines include primary, secondary and higher
polyamines and amine-terminated compounds. Suitable compounds
include, but are not limited to, ethylene diamine;
propylenediamine; butanediamine; hexamethylenediamine;
1,2-diaminopropane; 1,4-diaminobutane; 1,3-diaminopentane;
1,6-diaminohexane; 2,5-diamino-2,5-dimethlhexane; 2,2,4- and/or
2,4,4-trimethyl-1,6-diaminohexane; 1,11-diaminoundecane;
1,12-diaminododecane; 1,3- and/or 1,4-cyclohexane diamine;
1-amino-3,3,5-trimethyl-5-aminomethyl-cyclohexane; 2,4- and/or
2,6-hexahydrotoluylene diamine: 2,4' and/or
4,4'-diaminodicyclohexyl methane and
3,3'-dialkyl--4,4'-diamino-dicyclohexyl methanes such as
3,3'-dimethyl-4,4-diamino-dicyclohexyl methane and
3,3'-diethyl-4,4'-diaminodicyclohexyl methane; aromatic polyamines
such as 2,4- and/or 2,6-diaminotoluene and 2,6-diaminotoluene and
2,4' and/or 4,4'-diaminodiphenyl methane; and polyoxyalkylene
polyamines (also referred to herein as amine terminated
polyethers).
[0094] Mixtures of polyamines may also be employed in preparing
aspartic esters, which is a secondary amine derived from a primary
polyamine and a dialkyl maleic or fumaric acid ester, for use in
the invention. Representative examples of useful maleic acid esters
include dimethyl maleate, diethyl maleate, dibutyl maleate, dioctyl
maleate, mixtures thereof and homologs thereof.
[0095] Suitable triamines and higher multifunctional polyamines for
use in the present coating include diethylene triamine,
triethylenetetramine, and higher homologs of this series.
[0096] JEFFAMINE diamines include the D, ED, and EDR series
products. The D signifies a diamine, ED signifies a diamine with a
predominately polyethylene glycol (PEG) backbone, and EDR
designates a highly reactive, PEG based diamine.
[0097] JEFFAMINE D series products are amine terminated
polypropylene glycols with the following representative
structure:
##STR00005##
[0098] JEFFAMINE EDR-148 (XTJ-504) and JEFFAMINE EDR-176 (XTJ-590)
amines are much more reactive than the other JEFFAMINE diamines and
triamines. They are represented by the following structure:
##STR00006##
[0099] JEFFAMINE T series products are triamines prepared by
reaction of propylene oxide (PO) with a triol intiator followed by
animation of the terminal hydroxyl groups. They are exemplified by
the following structure:
##STR00007##
[0100] The SD Series and ST Series products consist of secondary
amine versions of the JEFFAMINE core products. The SD signifies a
secondary diamine and ST signifies a secondary trimine. The amine
end-groups are reacted with a ketone (e.g. acetone) and reduced to
create hindered secondary amine end groups represented by the
following terminal structure;
##STR00008##
[0101] One reactive hydrogen on each end group provides for more
selective reactivity and makes these secondary di- and triamines
useful for intermediate synthesis and intrinsically slower
reactivity compared with the primary JEFFAMINE amines.
TABLE-US-00001 JEFFAMINE .RTM. Base Product MW* SD-231 (XTJ-584)
D-230 315 SD-401 (XTJ-585) D-400 515 SD-2001 (XTJ-576) D-2000 2050
ST-404 (XTJ-586) T-403 565
[0102] See also U.S. Pat. Nos. 6,093,496; 6,306,964; 5,721,315;
7,012,043; and Publication U.S. Patent Application No. 2007/0208156
the disclosures of which are hereby incorporated by reference.
Additives
[0103] The proppant coating compositions of the invention may also
include various additives. For example, the coatings of the
invention may also include pigments, tints, dyes, and fillers in an
amount to provide visible coloration in the coatings. Other
materials conventionally included in coating compositions may also
be added to the compositions of the invention. These additional
materials include,, but are not limited to, reaction enhancers or
catalysts, crosslinking agents, optical brighteners, propylene
carbonates, coloring agents, fluorescent agents, whitening agents,
UV absorbers, hindered amine light stabilizers, defoaming agents,
processing aids, mica, talc, nano-fillers and other conventional
additives. All of these materials are well known in the art and are
added for their usual purpose in typical amounts. For example, the
additives are preferably present in an amount of about 15 weight
percent or less. In one embodiment, the additive is present in an
amount of about 5 percent or less by weight of the coating
composition.
[0104] Other additives can include, for example, solvents,
softeners, surface-active agents, molecular sieves for removing the
reaction water, thinners and/or adhesion agents can be used.
Silanes are a particularly preferred type of adhesion agent that
improves the affinity of the coating resin for the surface of the
proppant. Silanes can be mixed in as additives in step (a), but can
also be converted chemically with reactive constituents of the
polyol component or of the isocyanate component. Functional silanes
such as amino-silanes, epoxy-, aryl- or vinyl silanes are
commercially available and, as described above, can be used as
additives or can be converted with the reactive constituents of the
polyol component or of the isocyanate component. In particular,
amino-silanes and epoxy-silanes can be easily converted with the
isocyanate component.
Proppant Core Solids
[0105] The proppants can be virtually any small solid with an
adequate crush strength and lack of chemical reactivity. Suitable
examples include sand, ceramic particles (for instance, aluminum
oxide, silicon dioxide, titanium dioxide, zinc oxide, zirconium
dioxide, cerium dioxide, manganese dioxide, iron oxide, calcium
oxide or bauxite), or also other granular materials.
[0106] Proppant sands are a preferred type of proppant for the
present invention. Sand is mainly used in the hydraulic fracturing
process of natural gas and oil wells to increase their productivity
of valuable natural resources. Proppant sand is monocrystalline
with a high silica content of at least 80 wt %, and more typically
greater than about 97 wt % silica.
[0107] American Petroleum Institute specifications place the
following limitations on sieve distribution for proppants suitable
tor use in a fracture: [0108] At least 90% of material must fall
between the two mesh sizes. [0109] No more than 10% of the material
may be coarser than the largest mesh size, [0110] No more than 0.1
% of the material may be coarser than the next largest mesh size
[e.g. for 20/40, up to 10% of the proppant may be between 16 and 20
mesh, but no more than 0.1% can exceed 16 mesh], and [0111] No more
than 1% of material is permitted to fall onto the pan.
[0112] According to bulk density, proppant is divided into:
low-density, medium density, high-density. According to the
anti-crushing strength, proppant is divided into 52 Mpa, 69 Mpa, 86
Mpa and 103 Mpa four series. Specifications of proppant sand are
generally: 12-18 mesh, 12-20 mesh, 16-20 mesh, 16-30 mesh, 20-40
mesh between 30-50 mesh, 40-60 mesh, 40-70 mesh and smaller. The
proppants to be coated preferably have an average particle size
within the range from about 50 .mu.m and about 3000 .mu.m, and more
preferably within the range from about 100 .mu.m to about 2000
.mu.m.
Coating Method
[0113] The method for the production of coated proppants according
to the present invention can be implemented without the use of
solvents. Accordingly, the mixture obtained in step (a) in one
embodiment of the method is solvent-free, or is essentially
solvent-free. The mixture is essentially solvent-free, if it
contains less than 20 wt %, preferably less than 10 wt %, more
preferably less than 5 wt %, and still more preferably less than 3
wt %, and most preferably less than 1 wt % of solvent, relative to
the total mass of components of the mixture.
[0114] Preferably, the method is implemented without the use of
organic solvents. In this case, the mixture obtained in step (a) is
free of organic solvents, or is essentially free of organic
solvents. The mixture is essentially free of organic solvents, if
it contains less than 20 wt %, preferably less than 10 wt %, more
preferably less than 3 wt %, and still more preferably less than 3
wt %, and most preferably less than 1 wt % of solvent, relative to
the total mass of components of the mixture.
[0115] In step (a) the proppant is preferably heated to an elevated
temperature and then contacted with the coating components.
Preferably, the proppant is heated to a temperature within the
range of about 50.degree. C. to about 150.degree. C. to accelerate
crosslinking reactions in the applied coating.
[0116] The temperature of the coating process is not particularly
restricted outside of practical concerns for safety and component
integrity. The preferred conditions for the coating/curing step of
the present invention are generally at conditions within the range
of about 50.degree. to about 175.degree. C., more preferably at a
temperature within the range from about 75.degree. C. to about
150.degree. C., and most preferably at a temperature within the
range from about 80.degree. C. to about 135.degree. C. This
temperature avoids a number of emissions issues, reduces the amount
of energy consumed in the coating process and also reduces the
cooling time for the coated proppants for further handling and
packaging.
[0117] The mixer used for the coating process is not particularly
restricted and can be selected from among the mixers known in the
specific field. For example, a pug mill mixer, agitation mixer,
drum mixer, plate-type mixer, tubular mixer, trough mixer or
conical mixer can be used. The easiest way is mixing in a rotating
drum. As continuous mixer, a worm gear can, for example, be
used.
[0118] Mixing can be carried out on a continuous or discontinuous
basis. In suitable mixers it is possible, for example, to add
adhesion agents, isocyanate, amine and optional ingredients
continuously to the heated proppants. For example, isocyanate
components, amine reactant and optional additives can be mixed with
the proppant solids in a continuous mixer (such as a worm gear) in
one or more steps to make one or more layers of cured coating.
[0119] Preferably, the proppant, isocyanate component, curing
agent, amine reactant, polyol, and optional additives are mixed
homogeneously. Thus, the isocyanate component and amine reactant
are distributed uniformly on the surface of the proppants. The
coating ingredients are preferably kept in motion throughout the
entire mixing process.
[0120] It is also possible to arrange several mixers in parallel,
series, or serially in several runs in one mixer.
[0121] Importantly, the time, temperature, chemistry and reaction
rate of the coating/curing process are combined to substantially
completely react all of the --NGO groups within the applied
proppant coating by the time the product is discharged as a
free-flowing solid. Preferably, the proppant coating is cured to an
amount less than about 10 wt % of reactive --NCO groups, more
preferably less than about 5 wt % and even more preferably less
than about 2 wt % of reactive --NCO groups remain, based on the
originally applied weight of the proppant coating.
[0122] The coating is preferably performed at the same time as the
curing of the coating on the proppant. In the present invention,
the coated proppant becomes free-flowing at a time of less than 5
minutes, preferably within the range of 1-4 minutes, more
preferably within the range of 1-3 minutes, and most preferably
within the range of 1-2.5 minutes to form a coated, substantially
cured, free-flowing, coated proppant. This short cycle time
combines with the relatively moderate coating temperatures to form
a coating/curing process that provides lower energy costs, smaller
equipment, reduced emissions from the process and the associated
scrubbing equipment, and overall increased production for the
coating facility.
[0123] The coating material may be applied in more than one layer.
In this case, the coating process is repeated as necessary (e.g.
1-5 times, 2-4 times or 2-3 times) to obtain the desired coating
thickness. In this manner, the thickness of the coating of the
proppant can be adjusted and used as either a relatively narrow
range of proppant size or blended with proppants of other sizes,
such as those with more or less numbers of coating layers of
polyurethane according to the present invention, so as to form a
proppant blend have more than one range of size distribution. A
typical size range for coated proppant is typically within the
range of about 16-100 mesh.
[0124] The amount of coating resin, that is, of the polyurethane
resin applied to a proppant, is preferably between about 0.5 and
about 10 wt %, more preferably between about 1% and about 5 wt %,
resin relative to the mass of the proppant as 100 wt %. With the
method according to the present invention proppants can be coated
at temperatures between about 10.degree. C. and about 150.degree.
C. and preferably in a solvent-free rnanner. The coating process
requires a comparatively little equipment and if necessary can also
be carried out near the sand or ceramic substrate source, near the
geographically location of the producing field or at/near the well
itself.
[0125] The coated proppants can additionally be treated with
surtace-active agents or auxiliaries, such as talcum powder or
stearate or other processing aids, to improve pourability.
[0126] If desired, the coated proppants can be baked or heated for
a period of time sufficient to further react at least substantially
all of the available isocyanate, hydroxyl and reactive amine groups
that might remain in the coated proppant. Such a post-coating cure
may occur even if additional contact time with a catalyst is used
after a first coating layer or between layers. Typically, the
post-coating cure step is performed like a baking step at a
temperature within the range from about 100.degree.-200.degree. C.
for a time of about 30 minutes to 4 hours, preferably the
temperature is about 125.degree.-175.degree. C. for 5-30
minutes.
[0127] Even more preferably, the coated proppant is cured for a
time and under conditions sufficient to produce a coated proppant
that exhibits a loss of coating of less than 25 wt %, preferably
less than 15 wt %, and even more preferably less than 5 wt % when
tested according to simulated downhole conditions under ISO
13503-5:2006(E). Even more preferably, the coated proppant exhibits
the low dust and handling characteristics of a precured proppant
(see API RP 60) but also exhibits a crush test result at 10,000 psi
of less than 2%, more preferably less than 1.5%, and especially
less than 1%. The coated proppants of the invention preferably also
have an unconfined compressive strength of greater than 100 psi and
more preferably more than 500 psi with a fracture conductivity at
4000 psi that is equal to, or greater than, the conductivity of a
phenolic coating at the same weight percent of coating.
Using the Coated Proppants
[0128] The invention also includes the use of the coated proppants
in conjunction with a fracturing liquid to increase the production
of petroleum or natural gas. Techniques for fracturing an
unconsolidated formation that include injection of consolidating
fluids are also well known in the art. See U.S. Pat. No. 6,732,800
the disclosure of which is herein incorporated by reference.
Generally speaking, a fluid is injected through the wellbore into
the formation at a pressure less than the fracturing pressure of
the formation. The volume of consolidating fluid to be injected
into the formation is a function of the formation pore volume to be
treated and the ability of the consolidating fluid to penetrate the
formation and can be readily determined by one of ordinary skill in
the art. As a guideline, the formation volume to be treated relates
to the height of the desired treated zone and the desired depth of
penetration, and the depth of penetration is preferably at least
about 30 cm radially into the formation. Please note that since the
consolidation fluid is injected through the perforations, the
treated zone actually stems from the aligned perforations.
[0129] Before consolidating the formation, according to a preferred
embodiment, an acid treatment is performed by injection of an
acidic fluid. As it is well known in the art, this acidic treatment
typically includes several stages such as an acid preflush, one or
more stages of acid injection and an overflush.
[0130] After the perforation and the consolidation, the final step
is the fracturing step. Although a resin treatment alone may have
been sufficient in preventing early sand production the resin
reduces the permeability of the formation around the wellbore. The
primary purpose of the fracture treatment is to connect the
wellbore to the formation and in doing so by pass any damage and
act as a filter allowing the production of hydrocarbons while
holding back formation material. The high surface area associated
with a fracture makes it a very effective filter, for example, a
13.7 m fracture length with 25 cm height has a surface area of 368
m.sup.2, compared to the open hole flow area for a gravel pack of
3.2 m.sup.2 with the same zone height.
[0131] Techniques for hydraulically fracturing a subterranean
formation will be known to persons of ordinary skill in the art,
and will involve pumping the fracturing fluid into the borehole and
out into the surrounding formation. The fluid pressure is above the
minimum in situ rock stress, thus creating or extending fractures
in the formation. In order to maintain the fractures formed in the
formation after the release of the fluid pressure, the fracturing
fluid carries a proppant whose purpose is to prevent the fracturing
from closing after pumping has been completed.
[0132] The fracturing liquid is not particularly restricted and can
be selected from among the frac liquids known in the specific
field. Suitable fracturing liquids are described, for example, in W
C Lyons, G J Plisga, Standard Handbook Of Petroleum And Natural Gas
Engineering, Gulf Professional Publishing (2005). The fracturing
liquid can be, for example, water gelled with polymers, an
oil-in-water emulsion gelled with polymers, or a water-in-oil
emulsion gelled with polymers. In one preferred embodiment, the
fracturing liquid comprises the following constituents in the
indicated proportions: 1000 l water, 20 kg potassium chloride,
0.120 kg sodium acetate, 3.6 kg guar gum (water-soluble polymer),
sodium hydroxide (as needed) to adjust a pH-value from 9 to 11,
0.120 kg sodium thiosulfate, and 0.180 kg ammonium persulfate.
[0133] In addition, the invention relates to a method for the
production of petroleum or natural gas which comprises the
injection of the coated proppant into the fractured stratum with
the fracturing liquid, i.e., the injection of a fracturing liquid
which contains the coated proppant, into a petroleum- or natural
gas-bearing rock layer, and/or its introduction into a fracture in
the rock layer bearing petroleum or natural gas. The method is not
particularly restricted and can be implemented in the manner known
in the specific field.
[0134] Suitable proppants include, but are not limited to, sand,
bauxite, glass beads, and ceramic beads and resin-coated sand
versions of each. The proppant will typically exhibit a size within
the range from about 8 to about 100 U.S. Standard Mesh in size.
Mixtures of suitable proppants can be used. The concentration of
proppant in the fracturing fluid can be any concentration known in
the art, and will typically be in the range of about 0.5 to about
20 pounds of proppant added per gallon of clean fluid.
[0135] The fracturing fluid can contain an added proppant-retention
agent, e.g. a fibrous material, a curable resin coated on the
proppant, platelets, deformable particles, or a sticky proppant
coating to trap proppant particles in the fracture and prevent
their production through the wellbore. Fibers, in concentration
that preferably ranges front about 0.1% to about 5.0% by weight of
proppant, for example selected from natural organic fibers,
synthetic organic fibers, glass fibers, carbon fibers, ceramic
fibers, inorganic fibers, metal fibers and mixtures thereof, in
combination with curable resin-coated proppants are particularly
preferred. The proppant-retention agent is intended to keep
proppant solids in the fracture, and the proppant and
proppant-retention agent keep formation particles from being
produced.
EXAMPLES
[0136] Conductivity testing was performed at simulated downhole
conditions using the method and procedures found in ISO
13503-5:2006. In such tests, a closure stress is applied across a
test unit for 50 hours to allow the proppant sample bed to reach a
semi-steady state condition. As the fluid is forced through the
proppant bed, the pack width, differential pressure, temperature
and flow rates are measured at each stress. Proppant pack
permeability and conductivity are then calculated.
[0137] Multiple flow rates are used to verify the performance of
the transducers, and to determine Darcy flow regime at each stress;
an average of the data at these flow rates is reported. The test
fluid is potassium chloride substitute solution filtered to 3 .mu.m
absolute. The initial conductivity, permeability and width is
measured and compared to the final conductivity, permeability and
width after each stress period. Stress is applied and maintained
using an Isco 260D. Stress is applied at 100 psi/minute.
[0138] Width of the proppant pack is determined by assembling the
conductivity cell with the Ohio sandstone wafers and shims without
the sample proppants. The distance between the width bars that are
attached to each end of the conductivity cells are measured at each
of the four corners and recorded. The cells are then assembled with
the proppant samples. The measurements are made again at the
beginning and ending of each stress period. Width is determined by
subtracting the average of the zero from the average of each of the
stress width values. Conductivity is calculated using Darcy's
equation.
Conductivity; kW.sub.f=26.78 .mu.Q/(.DELTA.P)
Permeability; k=321.4 .mu.Q/[(.DELTA.P)W.sub.r]
wherein: [0139] k is the proppant pack permeability; expressed in
Darcy's; [0140] kW.sub.f is the proppant pack conductivity,
expressed in millidarcy-feet [0141] .mu. is the viscosity of the
test liquid at test temperature, expressed in centipoises; [0142] Q
is the flow rate, expressed in cubic centimeters per minute; [0143]
.DELTA.P is the differential pressure, expressed in psi; [0144]
W.sub.f is proppant pack width, expressed in inches.
[0145] Sieve analysis is performed using the procedure found in ISO
13503-2 "Measurements of proppants used in hydraulic fracturing and
gravel pack operations" Standard US mesh screens are used to
separate the sample by size. Not more than 0.1% should be greater
than the first specified sieve and not more than 1% should be
retained in the pan. There should be at least 90% retained in the
specified screens.
[0146] To determine the magnitude of coating loss during the
conductivity test, samples of the proppant pack are taken, dried in
an oven, and weighed. They are then subjected to a temperature of
96.degree. C. for 2.5 hours. At the end of this period the samples
are cooled and weighed again. The difference between the sample
weight after drying but before being subjected to the furnace
compared to the sample weight after the time in the furnace,
equates to the coating weight. Comparing this number to the same
test performed on a sample of the coated material before being
subjected to the conductivity test, will equate to the coating
weight lost due to the long term exposure to the conditions of the
conductivity tests.
[0147] The procedure used in an autoclave test would be as
follows:
[0148] The autoclave test utilizes what amounts to a pressure
cooker to subject the coated sands to a hot wet environment that is
above the boiling temperature of water. Approximately 20 g of
sample is placed in a jar along with 150 ml of distilled water. The
lids are placed on sample jars but not tightened. The samples are
placed in the autoclave and the chamber is sealed. Heat is applied
until the autoclave temperature reaches 250-265.degree. F.
(121.degree.-129.degree. C.). The samples are maintained under
these conditions for the ten day period. At the end of the test
period the autoclave is cooled down, opened and the sample jars
removed. Each sample is washed with distilled water and then placed
in an oven to dry. The dried samples are then put through a
standard test for determination of coating loss. This result is
compared to the results of a coating test that was run on the
original sample. The difference in coating weight before and after
the autoclave test, quantifies the amount of coating that was
dissolved by the exposure to a hot water environment.
Example 1
[0149] Ten pounds of Minnesota 40/70 fracturing sand is heated to
200.degree. F. in a laboratory mixer at which point the following
components are added in the sequence and timing as given below in
Tables 1 and 2. The weight ratio of the poly-MDI to phenolic polyol
in this example is 75/25.
TABLE-US-00002 TABLE 1 WEIGHT (grams) COMPONENT 4540 Minnesota sand
4.5 silane coupling agent 2.3 50% red iron oxide in castor oil 6.9
1,3,5-tris(3-(dimethylamino)propyl)-hexahydro-s-triazine (JEFFCAT
TR90) 34.2 Phenolic Polyol comprising 48% phenolic resin, 28%
cashew nut oil, 24% castor oil 102.2 Poly-MDI (32% NCO content) 2.5
Wetting agent
TABLE-US-00003 TABLE 2 TIME (minutes:seconds) ADDITION/COMMENT 0:00
Sand is at 200.degree. F. 0:00 4.5 gms silane coupling agent is
added over 30 secs 0:00 JEFFCAT TR90 is added over 20 secs 0:00
Blend of red iron oxide and Phenolic Polyol is added over 60
seconds 0:10 Poly-MDI is added over 60 seconds 2:00 Product is free
flowing 3:30 Wetting agent is added over 5 seconds 4:00 Product is
discharged at 180.degree. F.
[0150] In this and the other examples presented herein, it was
noticed that the JEFFCAT TR90 catalyst increased the reaction rate
sufficiently that the amperage on the associated mixer was not
exceeded as the coating reactants were metered into the proppant
solids in the moving mixer. This suggests that the coating became
cured at a rate that was consistent with the feed rate so that the
liquid viscosity did not increase the electrical load on the mixer.
This same method of controlled, metered addition would also apply
for other formulations and chemistries under the present invention
in order to keep the contents reacting at a rate that does not tax
the load on the mixing equipment.
[0151] The resin coated sand from the example above tested at 2.75%
coating loss from the mixer. When subjected to a three day
250.degree. F. autoclave test, the coating loss was measured again
at 2.34% reflecting the good resistance to hot water removal of the
coating.
Example 2
[0152] Ten pounds of Genoa 40/70 fracturing sand is heated to
204.degree. F. in a laboratory mixer at which point the following
components are added in the sequence and timing as given below in
Tables 3 and 4. The weight ratio of the poly MDI to phenolic polyol
in this example is 75/25.
TABLE-US-00004 TABLE 3 WEIGHT (grams) COMPONENT 4540 Genoa sand 4.5
A1100 silane coupling agent 2.3 50% red iron oxide in castor oil
6.9 JEFFCAT TR90 18.2 Phenolic Polyol comprised of 48% phenolic
resin, 28% cashew nut oil, 24% castor oil 54.5 Poly-MDI (32% NCO
content) 2.3 Wetting agent
TABLE-US-00005 TABLE 4 TIME (minutes:seconds) ADDITION/COMMENT 0:00
Sand is at 204.degree. F. 0:00 4.5 gms A1100 is added over 10 secs
0:00 JEFFCAT TR90 is added over 10 secs 0:00 blend of red iron
oxide and Phenolic Polyol is added over 30 seconds 0:10 polyMDI is
added over 30 seconds 2:00 Product is free-flowing 3:30 Wetting
agent is added over 5 seconds 4:00 Product is discharged at
182.degree. F.
[0153] The resin coated sand from the example above tested at 1.48%
LOI from the mixer. When subjected to a three day 250.degree. F.
autoclave test, the coating loss was measured again at 1.43%
reflecting the good resistance to hot water removal of the
coating.
Example 3
[0154] Ten pounds of Minnesota fracturing sand is heated to
200.degree. F. in a laboratory mixer at which point the following
components are added in the sequence and timing as given below in
Tables 5 and 6. The weight ratio of the poly MDI to phenolic polyol
in this example is 92/8.
TABLE-US-00006 TABLE 5 WEIGHT (grams) COMPONENTS: 4540 Minnesota
sand 4.5 A1100 silane coupling agent 2.3 50% red iron oxide in
castor oil 6.9 JEFFCAT TR 90 12 Phenolic Polyol comprised of 48%
phenolic resin, 28% cashew nut oil, 24% castor oil 135 Poly-MDI
(32% NCO content) 2.5 Wetting agent
TABLE-US-00007 TABLE 6 TIME (minutes:seconds) ADDITION/COMMENT 0:00
Sand is at 202.degree. F. 0:00 A1100 is added over 20 secs 0:00
JEFFCAT TR90 is added over 20 secs 0:00 Blend of red iron oxide and
Phenolic Polyol is added over 60 seconds 0:10 Poly-MDI is added
over 60 seconds 2:00 Product is free flowing 3:30 Wetting agent is
added over 5 seconds 4:00 Product is discharged at 170.degree.
F.
[0155] The resin coated sand from example 3 tested at 2.80% coating
loss from the mixer. When subjected to a three day 250.degree. F.
autoclave test, the coating loss was measured again at 2.56%
reflecting the good resistance to hot water removal of the
coating.
Example 4
[0156] One kg of 40/70 Minnesota fracturing sand is heated to
210.degree. F. in a laboratory mixer at which point the following
components are added in the sequence and timing as given below in
Tables 7 and 8. The weight ratio of the poly-MDI to the aminated
polyalkyleneglycol (JEFFAMINE D230) is 63/37.
TABLE-US-00008 TABLE 7 WEIGHT (grams) COMPONENTS 1000 Minnesota
sand 1 A1100 silane coupling agent 20 Poly-MDI (32% NCO content) 12
JEFFAMINE D230
TABLE-US-00009 TABLE 8 TIME (minutes:seconds) ADDITION/COMMENT 0:00
Sand is at 210.degree. F. 0:00 A1100 is added over 10 secs 0:10
Poly-MDI is added over 30 secs 0:50 JEFFAMINE D230 is added over 10
secs 2:00 Product is free flowing 4:00 Product is discharged at
140.degree. F.
[0157] The resin coated sand from the example above tested at 2.90%
coating loss from the mixer. When subjected to a three day
250.degree. F. autoclave test, the coating loss was measured again
at 2.83% reflecting the good resistance to hot water removal of the
coating.
Example 5
[0158] One kg of 40/70 Minnesota fracturing sand is heated to
210.degree. F. in a laboratory mixer at which point the following
components are added in the sequence and timing as given below in
Tables 9 and 10. The weight ratio of the poly-MDI to the aminated
polyalkyleneglycol (JEFFAMINE D230 from Huntsman Corporation) is
63/37.
TABLE-US-00010 TABLE 9 WEIGHT (grams) COMPONENTS 1000 Minnesota
sand 1 A1100 silane coupling agent 20 Poly-MDI (32% NCO content) 12
Aminated polyalkyleneglycol 0.6 Triethylenediamine
TABLE-US-00011 TABLE 10 TIME (minutes:seconds) ADDITION/COMMENT
0:00 Sand is at 210.degree. F. 0:00 A1100 is added over 10 secs
0:10 Poly-MDI is added over 30 secs 0:50 Preblended Aminated
polyalkyleneglycol and Triethylenediamine are added over 10 s 2:00
Product is free flowing 4:00 Product is discharged at 145.degree.
F.
[0159] The resin coated sand from the example above tested at 2.84%
coating loss from the mixer. When subjected to a three day
250.degree. F. autoclave test, the coating loss was measured again
at 2.63% reflecting the good resistance to hot water removal of the
coating.
Example 6
[0160] In this example, a series of test results were performed to
demonstrate the properties of proppant coatings that include
completely reacted (precured) and partially cured phenolic coatings
as compared to the coating of the present invention ("new
technology coating"). The graph in FIG. 1 illustrates the TMA
results for (a) Precured phenolic coated sand, (b) New Technology
coated sand using the formulation of Example 1, (c) a partially
cured, phenolic-coated sand (also identified as Phenolic A) and (d)
a somewhat more curable, phenolic-coated sand (also identified as
Phenolic B)
[0161] The ThermoMechanical Analyzer (TMA) as supplied by TA
Instruments is a device that accurately imposes a small force
(i.e., a load) onto a sample which is then subjected to a desired
temperature over a defined time. During this increasing temperature
period, the force is held constant. The probe which imposes the
force is connected to a sophisticated micrometer that is capable of
measuring fractions of a micron change in the position of the
probe. Any change in the position of the probe can be interpreted
to reflect an expansion or contraction of the sample that is
brought about by the temperature change(s). In many applications,
the sample merely expands as it is being heated (for instance raw
sand) thereby creating a database that refers to the coefficient of
themral expansion. The TMA has the ability to run the samples in a
variety of environments.
[0162] In general, a precured, phenolic-coated sand will be
characterized by a plot that is essential flat (parallel to the X
axis) or has a positive slope. This response is indicative of a
coating that is essentially reacted in which there is little to no
remaining reactivity that remains in the coating.
[0163] If, however, a more curable or partially cured phenolic
coating is tested, the TMA plot will exhibit a negative slope as
early as 80.degree. C. to 100.degree. C., but more often after
about 125.degree. C. to about 175.degree. C. This type of plot is
characteristic of a coating that has retained a level of reactivity
even after completing the manufacturing process. The more negative
the slope and the lower the temperature in which the slope turns
negative, the more reactivity that has been left in the
coating.
[0164] As shown in FIG. 1, the top curve is labeled "Precured" and
is indicative of the response of a phenolic coating that is no
longer reactive. The two lower curves are labeled "Partially Cured
Phenolic A" and "More Curable Phenolic B." These curves represent
the TMA results from two levels of partially cured coatings. The
second curve labeled "New Technology" shows a response that is
similar to the precured coating curve but actually shows properties
that fall between a precured coating and the less reactive
partially cured coating. The shape of the New Technology curve
indicates that the New Technology coating would exhibit some
properties that are similar to a precured coating and others that
may be similar to the partially cured coatings.
[0165] The plot of "Crush Results" in FIG. 2 illustrates the
comparable strength of sand coated with precured phenolic coating,
two partially cured coatings (labeled A and B) and the New
technology coating. Historically, the precured phenolic coated sand
would show a lower crush percentage (in the ISO test procedure)
than partially cured coated sand. These crush test results follow
this trend with the precured coating sand having a crush of 2.05%
and the two partially coatings (Phenolic coatings A and B) having
crushes of 3.93% and 4.95% respectively. It is important to notice
that the coating having the more remaining reactivity (Phenolic B)
has the highest crush value. The New Technology coating actually
tested out having the lowest crush value (0.69%). So in the crush
evaluation The New Technology coating performed like a superior,
precured coated sand.
[0166] The plot entitled "Unconfined Compressive Strength" in FIG.
3 represents a strength measurement of the particle to particle
bonds of a coated sand. Historically, a precured coated phenolic
sand possess little if any ability to form particle to particle
bonds of any measureable strength. In this test the coating labeled
Phenolic A exhibited a bond strength UCS of 449 psi. The coating
labeled Phenolic B had a UCS of 155 psi. Since the TMA indicated
that Phenolic B was a more reactive coating than Phenolic A, one
would expect that the UCS results should be reversed. That would be
true if the coated sands had the same resin level (LOI). However
the plot entitled "Coated Sand Loss On Ignition" in FIG. 5, shows
that Phenolic A actually has a 3.97% phenolic coating while
phenolic coating B has a 2.84% resin coating. This could be one
explanation for the unexpected UCS results.
[0167] In FIG. 3, the precured phenolic coating sand showed only a
weak bonding capability with a measurement of 7 psi. This level of
bonding would indicate that the precured phenolic coating is not
capable of forming particle-to-particle bonds that would
consolidate the proppant or be effective in controlling proppant
flowback.
[0168] The New Technology coating exhibited the TMA appearance of a
precured coated sand in FIG. 1, it yielded the highest bond
strength (UCS=576 psi) of any sample tested. See FIG. 3. These dual
results are new and unexpected for a coated proppant.
[0169] The plot entitled "Fracture Conductivity @ 4000 psi" in FIG.
4 reveals a data point from a long term conductivity test.
Presented on the plot are the conductivity numbers for the two
partially cured phenolic coated sands and a sand coated with the
New Technology. Historically, the conductivity test results for a
partially cure phenolic coating will meet or exceed that of a
precured coating. The plot shows that the New Technology coating
has a conductivity similar to the partially cured coating of
Phenolic A and superior to partially cured coating of Phenolic B.
This is in spite of the fact the Phenolic A has a significantly
higher coating level than the New technology and Phenolic B is
marginally higher than the New Technology coating (see FIG. 5).
[0170] In summary, The New Technology coated sand exhibits the TMA
of a precured phenolic coated sand and crush resistance superior to
a precured phenolic coating. It also shows a bonding capability
superior to the partially cured phenolic coated sand and a
comparable if not superior fracture conductivity (when measured at
4,000 psi in a long term conductivity test). This would seem to
indicate that the new technology contains traits and performance
properties from both type coating and would best be described as a
"hybrid" coating technology.
[0171] Once those skilled in the art are taught the invention, many
variations and modifications are possible without departing from
the inventive concepts disclosed herein. The invention, therefore,
is not to be restricted except in the spirit of the appended
claims.
* * * * *