U.S. patent application number 14/426320 was filed with the patent office on 2015-08-27 for manufacture of polylactic acid foams using liquid carbon dioxide.
This patent application is currently assigned to BIOPOLYMER NETWORK LIMITED. The applicant listed for this patent is Jean-Philippe Paul Marie Pierre GARANCHER. Invention is credited to Jean-Philippe Paul Marie Pierre Garancher.
Application Number | 20150240044 14/426320 |
Document ID | / |
Family ID | 50236608 |
Filed Date | 2015-08-27 |
United States Patent
Application |
20150240044 |
Kind Code |
A1 |
Garancher; Jean-Philippe Paul Marie
Pierre |
August 27, 2015 |
MANUFACTURE OF POLYLACTIC ACID FOAMS USING LIQUID CARBON
DIOXIDE
Abstract
Methods of producing CO.sub.2-impregnated crystallisable
polylactic acid resins and expanded polylactic acid foams.
Inventors: |
Garancher; Jean-Philippe Paul Marie
Pierre; (Rotorua, NZ) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GARANCHER; Jean-Philippe Paul Marie Pierre |
Rotorua |
|
NZ |
|
|
Assignee: |
BIOPOLYMER NETWORK LIMITED
ROTOURA
NZ
|
Family ID: |
50236608 |
Appl. No.: |
14/426320 |
Filed: |
September 5, 2013 |
PCT Filed: |
September 5, 2013 |
PCT NO: |
PCT/IB2013/058296 |
371 Date: |
March 5, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61697029 |
Sep 5, 2012 |
|
|
|
Current U.S.
Class: |
521/60 ; 521/182;
521/97 |
Current CPC
Class: |
C08J 9/18 20130101; C08J
9/122 20130101; C08J 9/232 20130101; C08J 2367/04 20130101; C08J
2201/032 20130101; C08J 2203/06 20130101 |
International
Class: |
C08J 9/18 20060101
C08J009/18; C08J 9/12 20060101 C08J009/12 |
Claims
1. A method of producing CO.sub.2 impregnated crystallisable
polylactic acid resin, the method comprising providing a
crystallisable polylactic acid resin, and contacting the resin with
liquid CO.sub.2 at a temperature of about -57.degree. C. to about
2.degree. C. to impregnate the resin with CO.sub.2.
2. A method of claim 1 wherein the CO.sub.2 concentration of the
resin after impregnation is up to about 55% by weight.
3. A method of producing polylactic acid foam, the method
comprising providing a crystallisable polylactic acid resin that
has been impregnated with liquid CO.sub.2 at a temperature of about
-57.degree. C. to about 2.degree. C., and expanding the impregnated
resin to produce a foam.
4. A method of claim 3, wherein the foam has a density of about 5
to about 200 g/L.
5. A method of claim 4, wherein the foam exhibits a volumetric
shrinkage of less than about 35% at 70.degree. C.
6. A method of claim 5, further comprising holding the impregnated
resin under conditions to prevent a significant increase in
crystallinity prior to the expanding step.
7. A method of claim 6, further comprising holding the impregnated
resin at a temperature and pressure that prevents the resin from
expanding while allowing the level of impregnated CO.sub.2 to
reduce to about 5 to 35% by weight prior to the expanding step.
8. A method of claim 3, wherein the CO.sub.2 concentration of the
impregnated resin immediately before expansion is up to about 35%
by weight.
9. A method of claim 3, wherein the expanding step comprises
pre-expansion, pre-expansion then moulding, or moulding without
pre-expansion.
10. A method of claim 3, wherein the expanding step comprises
heating the impregnated polylactic acid resin at a temperature of
about 15.degree. C. to about 140.degree. C.
11. A method of claim 1, wherein the PLA comprises at least about
88% by weight L- or D-lactic acid or is a blend of poly(L-lactic
acid) and poly(D-lactic acid) homopolymer, or a blend of PLA block
copolymers where each block has an isomer purity of greater than
88% of L-lactic acid or D-lactic acid.
12. A method of claim 1, wherein the resin comprises a PLA
copolymer, a PLA block copolymer, a PLA homopolymer or a blend of
PLA with one or more other polymers.
13. A method of claim 1, wherein the impregnated resin is in the
form of a particle, bead, rod, bar, sheet, film, moulded shape or
extruded shape.
14. A method of claim 1, wherein the resin further comprises one or
more fillers, additives, nucleating agents, plasticisers or
co-blowing agents, or any combination of any two or more
thereof.
15. A method of claim 6, wherein impregnation step, the holding
step, or the impregnation step and the holding step are conducted
at a temperature at or below the glass transition temperature of
the resin.
16. An expanded polylactic acid foam comprising a density of less
than about 200 g/L and a volumetric shrinkage of less than about
35% at 70.degree. C.
17. A foam of claim 16 comprising at least about 88% by weight L or
D lactic acid or a blend of poly-L-lactic acid and poly-D-lactic
acid homopolymer, or a blend of PLA block copolymers where each
block has an isomer purity of greater than 88% of L-lactic acid or
D-lactic acid.
18. A foam of claim 16 further comprising one or more fillers,
additives, nucleating agents, plasticisers or co-blowing agents, or
any combination of any two or more thereof.
19. A foam of claim 16, wherein the foam exhibits linear shrinkage
of less than about 5% up to a temperature of about 70.degree. C.
when subjected to a compressive force of about 10 kPa.
20. A foam of claim 16, wherein the resin has a crystallinity of
less than about 20% by weight.
21. A foam of claim 16, wherein the resin has a crystallinity of
less than about 15% by weight.
22. A foam of claim 16, wherein the crystallinity of the expanded
resin or foam is at least about 5% by weight.
23. A method of claim 3, wherein the foam exhibits linear shrinkage
of less than about 5% up to a temperature of about 70.degree. C.
when subjected to a compressive force of about 10 kPa.
24. A method of claim 3, wherein the resin has a crystallinity of
less than about 20% by weight.
25. A method of claim 3, wherein the resin has a crystallinity of
less than about 15% by weight.
26. A method of claim 3, wherein the crystallinity of the expanded
resin or foam is at least about 5% by weight.
Description
FIELD OF THE INVENTION
[0001] The invention relates to methods for producing polylactic
acid (PLA) foam products with increased thermal stability
properties, the methods comprising use of liquid CO.sub.2
impregnation of crystallisable PLA.
BACKGROUND OF THE INVENTION
[0002] Polylactic acid is a thermoplastic polyester produced from
renewable resources and, because it can be foamed, is a practical
alternative to non-renewable polymers for many applications,
including packaging applications. Reported disadvantages with
polylactic acid-based materials include lower thermal stability
properties compared to alternative polymers derived from
petrochemicals.
[0003] It is an object of the invention to provide improved or
alternative foam products and methods for making them.
SUMMARY OF THE INVENTION
[0004] Accordingly, the present invention relates the use of liquid
CO.sub.2 impregnation, preferably low temperature liquid CO.sub.2
impregnation of crystallisable PLA resin to produce PLA foam
products having increased heat dimensional stability. The PLA resin
may comprise a PLA copolymer, a PLA block copolymer, a PLA
homopolymer or a blend of PLA with one or more other polymers.
[0005] In one aspect the invention relates to a method of producing
CO.sub.2-impregnated crystallisable polylactic acid resin, the
method comprising
(a) providing a crystallisable polylactic acid resin, preferably
comprising less than about 20% crystallinity as determined by
differential scanning calorimetry, preferably a resin that has been
prepared in an amorphous state, and (b) contacting the resin with
liquid CO.sub.2 at a temperature of about -57.degree. C. to about
2.degree. C. to impregnate the resin with CO.sub.2.
[0006] In another aspect the invention relates to a method of
producing polylactic acid foam, the method comprising
(a) providing a crystallisable polylactic acid resin, preferably a
resin comprising less than about 20% crystallinity as determined by
differential scanning calorimetry, preferably a resin that has been
prepared in an amorphous state, that has been impregnated with
liquid CO.sub.2 at a temperature of about -57.degree. C. to about
2.degree. C. and that comprises up to about 55% by weight CO.sub.2,
and (b) expanding the impregnated resin to produce a foam.
[0007] A crystallinity of less than about 20% by weight may be
determined by differential scanning calorimetry (DSC). In various
embodiments, the resin comprises less than about 19, 18, 17, 16,
15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, 1% by weight
crystallinity, or 0% by weight crystallinity, as determined by
differential scanning calorimetry, and useful ranges may be
selected between any of these values (for example, about 0 to about
20, about 0 to about 15, about 0 to about 10, or about 0 to about
5%).
[0008] In another aspect the invention relates to an expanded PLA
foam comprising one or more of a uniform foam cell structure, a
density of less than about 200 g/L and a volumetric shrinkage of
less than about 35% at 70.degree. C.
[0009] CO.sub.2 concentration in the polymer is measured by weight
according to the following formula
C - 100 .times. W PLA - W PLA + CO 2 W PLA + CO 2 ##EQU00001##
[0010] To determine volumetric shrinkage, an exact volume of sample
is measured by water displacement and the sample put in an oven at
70.degree. C. for 24 hours.
[0011] After this thermal treatment, the volume of the sample is
re-measured, and the volumetric shrinkage .DELTA.V that was induced
by the thermal treatment is calculated as
.DELTA. V = 100 .times. V initial - V final V initial
##EQU00002##
[0012] The following embodiments may relate to any of the above
aspects in any combination.
[0013] In one embodiment the foam exhibits a volumetric shrinkage
of less than about 35% at 70.degree. C., including less than about
30, 25, 20, 15, 10 or 5% at 70.degree. C., or a shrinkage of about
0% at 70.degree. C., and useful ranges may be selected between any
of these values (for example, about 0 to about 35, about 0 to about
20 or about 0 to about 10%).
[0014] In one embodiment the foam exhibits linear shrinkage of less
than about 5% up to a temperature of about 70.degree. C. when
subjected to a compressive force of about 10 kPa. In various
embodiments the linear shrinkage is less than about 5, 4.5, 4, 3.5,
3, 2.5, 2, 1.5, 1 or 0.5%, and useful ranges may be selected
between any of these values (for example, about 0.5 to about 5%).
In various embodiments the temperature is about 70, 72, 75, 77, 80,
82, 85, 87, 90, 92, 95, 97, or 100.degree. C., and useful ranges
may be selected between any of these values (for example, about 70
to about 100, or about 75 to about 100.degree. C.).
[0015] To determine linear shrinkage, a cylindrical sample is cut
from a moulded block and tested in a RSA-G2 DMTA apparatus (TA
Instruments). The sample is subjected to a constant 10 kPa
compressive stress and heated from room temperature at 2.degree. C.
per minute. The linear shrinkage is measured as the deflection of
the sample (in % of the initial sample height) throughout the
test.
[0016] In one embodiment the foam has a density of less than about
5, 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 110, 120, 130, 140,
150, 160, 170, 180, 190 or 200 g/L and useful ranges may be
selected between any of these values (for example, about 20 to
about 200, about 30 to about 200, about 20 to about 180, about 30
to about 180, about 20 to about 160, about 30 to about 160, about
20 to about 140, about 30 to about 140, about 20 to about 120,
about 30 to about 120, about 20 to about 100 or about 30 to about
100 g/L).
[0017] In various embodiments the crystallinity of the expanded
resin or foam is at least about 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5,
5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, 10, 10.5, 11, 11.5, 12, 12.5,
13, 13.5, 14, 14.5, or 15% by weight, and useful ranges may be
selected between any of these values (for example, about 5 to about
10, about 5 to about 15%).
[0018] In one embodiment impregnation is conducted by contacting
the resin with liquid CO.sub.2, preferably immersing the resin in
liquid CO.sub.2, preferably until the amount of CO.sub.2 adsorbed
by the resin is at equilibrium. The amount of CO.sub.2 adsorbed by
the resin will depend on the nature of the resin and the
impregnation time, pressure and temperature. The amount of CO.sub.2
adsorbed by the resin at equilibrium may be determined
experimentally by determining the maximum amount of CO.sub.2 that a
selected amount of resin portions, such as resin beads, will adsorb
at a desired pressure or temperature. Going to equilibrium results
in the CO.sub.2 being dispersed evenly throughout the impregnated
resin, resulting in more even foaming and more uniform cell
structure.
[0019] The temperature for impregnation is selected to be at or
below, and is maintained at or below, the glass transition
temperature (Tg) of the resin, preferably at or below the Tg of the
resin at a given CO.sub.2 concentration, such as the concentrations
described below. In one embodiment the impregnation is carried out
at about -57, -55, -50, -45, -40, -35, -30, -25, -20, -15, -10, -5,
-1, 0, 1 or 2.degree. C., and useful ranges may be selected between
any of these values (for example, about 2 to about -57, about 1 to
about -57, about 0 to about -57, about -1 to about -57, about -30
to about -57 or about -35 to about -57.degree. C.).
[0020] In one embodiment impregnation is conducted for at least
about 1, 5, 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 110, 120, 130,
140, 150, 160, 170, 180, 190, 200, 210, 220, 230 or 240 minutes, or
1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19,
20, 21, 22, 23 or 24 hours, and useful ranges may be selected
between any of these values (for example, about 1 to 240, 10 to
240, 10 to 200, 10 to 150, 10 to 100, 20 to 240, 20 to 200, 20 to
150, or 20 to 100 minutes, or about 1 to 24, 2 to 23, 3 to 22, 4 to
21, 5 to 20, 6 to 18, 7 to 17, 8 to 16, 9 to 15 or 10 to 14
hours).
[0021] In one embodiment the CO.sub.2 concentration of the resin
after impregnation is up to about 55% by weight or otherwise up to
a saturated level, including about 1, 2, 3, 4, 5, 10, 15, 20, 25,
30, 35, 40, 45, 50 or 55% by weight, and useful ranges may be
selected between any of these values (for example, about 1 to about
50, about 10 to about 50, about 20 to about 50 or about 30 to about
45%).
[0022] In one embodiment the method further comprises holding the
impregnated resin under conditions to prevent a significant
increase in crystallinity.
[0023] In one embodiment the method further comprises holding the
impregnated resin at a temperature and pressure that prevents the
resin from expanding while allowing the level of impregnated
CO.sub.2 to reduce to about 5 to 35% by weight prior to the
expanding step, including 5, 10, 15, 20, 25, 30 or 35% by weight,
and useful ranges may be selected between any of these values (for
example, about 10 to about 30, about 15 to about 30 or about 15 to
about 25%).
[0024] In one embodiment the temperature for the holding
(conditioning) step is selected to be at or below and is maintained
at or below the glass transition temperature (Tg) of the resin,
preferably at or below the Tg of the resin at a given CO.sub.2
concentration, such as the concentrations described below. In one
embodiment the impregnated resin is held at about -57, -55, -50,
-45, -40, -35, -30, -25, -20, -15, -10, -5, -1, 0, 1, 2, 3 or
4.degree. C., and useful ranges may be selected between any of
these values (for example, about 4 to about -57.degree. C.).
[0025] In various embodiments the impregnation step, the holding
step, or the impregnation step and the holding step are conducted
at a temperature that is at or below the glass transition
temperature of the resin, preferably at or below the Tg of the
resin at a given CO.sub.2 concentration, such as the concentrations
described above and below.
[0026] In one embodiment the impregnated resin is held at a
pressure that prevents the resin from expanding.
[0027] In one embodiment the impregnated resin is held until the
CO.sub.2 concentration reduces to about 5, 10, 15, 20, 25, 30 or
35% by weight, and useful ranges may be selected between any of
these values (for example, about 5 to about 30% or about 10 to
about 25%).
[0028] In one embodiment the CO.sub.2 concentration of the
impregnated resin immediately before expansion is up to about 35%
by weight.
[0029] In one embodiment the expanding step comprises
pre-expansion, pre-expansion then moulding, or moulding without
pre-expansion.
[0030] In one embodiment the expanding step comprises heating the
impregnated polylactic acid resin at a temperature of about
15.degree. C. to about 150.degree. C.
[0031] In one embodiment the pre-expansion comprises a temperature
of about 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80,
85, 90, 95, 100, 105, 110, 115, 120, 125, 130, 135 or 140.degree.
C., and useful ranges may be selected between any of these values
(for example, about 15 to about 140.degree. C.). Pre-expansion
comprises contacting the resin or a mould containing the resin with
a hot fluid such as hot water, steam, hot air or hot oil, or by
exposing the resin to electromagnetic radiation such as
microwaves.
[0032] In one embodiment pre-expanding the resin is conducted by
heating the resin to the pre-expansion temperature for at least
about 1, 5, 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 110, 120, 130,
140, 150, 160, 170, 180, 190, 200, 210, 220, 230 or 240 seconds,
and useful ranges may be selected between any of these values (for
example, about 1 to 240, 1 to 120, 5 to 240, 5 to 120, 10 to 240,
10 to 120, 20 to 240, or 20 to 120 seconds).
[0033] In one embodiment moulding comprises placing the impregnated
or pre-expanded resin in a mould and heating the mould at about 50,
55, 60, 65, 70, 75, 80, 85, 90, 95, 100, 105, 110, 115, 120, 125,
130, 135, 140, 145 or 150.degree. C., and useful ranges may be
selected between any of these values (for example, about 50 to
about 150.degree. C.).
[0034] In one embodiment the mould is heated for about 5, 10, 20,
30, 40, 50, 60, 70, 80, 90, 100, 110, 120, 150 or 180 seconds, and
useful ranges may be selected between any of these values (for
example, about 1 to about 180 seconds).
[0035] In one embodiment moulding comprises application of a vacuum
to the mould for about 1, 5, 10, 20, 30, 40, 50, 60, 70, 80, 90,
100, 110, 120, 130, 140, 150, 160, 170, 180, 190, 200, 210, 220,
230 or 240 seconds, or about 1, 2, 3, 4, 5, 6, 7, 8, 9 or 10
minutes, and useful ranges may be selected between any of these
values (for example, about 1 to 240, 1 to 120, 5 to 240, 5 to 120,
10 to 240, 10 to 120, 20 to 240, or 20 to 120 seconds, or about 1
second to about 10 minutes).
[0036] In various embodiments the resin comprises at least about
40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 99, or 100% PLA by
weight, and useful ranges may be selected between any of these
values (for example, about 40 to about 100, about 50 to about 100,
or about 60 to about 100%).
[0037] In one embodiment the resin comprises a PLA copolymer, a PLA
block copolymer, a PLA homopolymer or a blend of PLA with one or
more other polymers.
[0038] In one embodiment the PLA copolymer comprises at least about
88% by weight L- or D-lactic acid or is a blend of poly(L-lactic
acid) and poly(D-lactic acid) homopolymer, or a blend of PLA block
copolymers where each block has an isomer purity of greater than
88% of L-lactic acid or D-lactic acid.
[0039] In one embodiment a PLA copolymer comprises an isomer purity
of about 88, 89, 90, 91, 21, 92, 94, 95, 96, 97, 98, 99, 99.5 or
99.9% by weight, and useful ranges may be selected between any of
these values (for example, about 88 to about 99.9, about 90 to
about 99.9, or about 92 to about 99.9%).
[0040] In one embodiment a PLA copolymer blend comprises a blend
with an isomer purity of about 88, 89, 90, 91, 21, 92, 94, 95, 96,
97, 98, 99, 99.5 or 99.9% by weight, and useful ranges may be
selected between any of these values (for example, about 88 to
about 99.9, about 90 to about 99.9, or about 92 to about
99.9%).
[0041] In one embodiment a PLA copolymer comprises a D-isomer
content of from about 0% to about 12% by weight and an L-isomer
content of from about 88 to about 100% by weight.
[0042] In one embodiment a PLA copolymer comprises a L-isomer
content from about 0% to about 12% by weight and a D-isomer content
of from about 88% to about 100% by weight.
[0043] In one embodiment a PLA copolymer blend comprises a blend of
a copolymer comprising a total D-isomer content of about 0% to
about 12% by weight with a copolymer comprising a total L-isomer
content of about 0% to about 12% by weight.
[0044] In one embodiment the PLA resin comprises stereocomplex
blends of pure PDLA (or high-purity PDLA) and PLLA (or high-purity
PLLA). The blends may comprise about 1, 3, 5, 10, 20, 30, 40 or 50%
PLLA (or PDLA) by weight, and useful ranges may be selected between
any of these values (for example, about 1 to about 50, about 10 to
about 50, or about 20 to about 50%).
[0045] In various embodiments the PLA resin comprises lactic acid
polymerised with co-monomers other than lactic acid, a PLA polymer
blended with one or more crystallisable or amorphous non-PLA
polymers, or a modified PLA such as a cross-linked PLA or a
functionalised PLA.
[0046] In one embodiment the resin comprises PLA polymerised with
other co-monomers, PLA blends with other polymers, and modified
PLA, including cross-linked PLA or functionalised PLA.
[0047] In various embodiments, blends of any two or more of the
polymers described above are contemplated. Other polymers known to
be used in blends with PLA can also be used.
[0048] In one embodiment the copolymer is a copolymer of lactic
acid and a comonomer capable of forming a polymer, preferably a
biodegradable polymer, such as an ester, methacrylate, methyl
methacrylate, glycolic acid, .epsilon.-caprolactone, a
hydroxyalkanoate, hydroxybutyrate, hydroxyvalerate,
hydroxyhexanoate, or hydroxyoctanoate, for example. In one
embodiment the copolymer is poly(lactic-co-glycolic acid), or
poly(lactic-co-caprolactone). In one embodiment, the copolymer
comprises at least 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95,
or 99% PLA by weight, and useful ranges may be selected between any
of these values (for example, about 40 to about 99, about 50 to
about 99, about 60 to about 99, about 70 to about 99, about 80 to
about 99, or about 90 to about 99%).
[0049] In one embodiment the block copolymer comprises one or more
blocks of one or more polymers, preferably biodegradable polymers,
such as a polymer of an ester (a polyester), methacrylate
(polymethacrylate), methyl methacrylate (poly(methyl methacrylate),
PMMA), glycolic acid (polygloycolic acid, PGA),
.epsilon.-caprolactone (polycaprolactone, PCL), a hydroxyalkanoate
(poly-hydroxyalkanoate, PHA), hydroxybutyrate
(poly-hydroxybutyrate, PHB), hydroxyvalerate (poly-hydroxyvalerate,
PHV), hydroxyhexanoate (poly-hydroxyhexanoate, PHH), or
hydroxyoctanoate (poly-hydroxyoctanoate, PHO), for example. In one
embodiment, the block copolymer comprises at least 40, 45, 50, 55,
60, 65, 70, 75, 80, 85, 90, 95, or 99% PLA by weight, and useful
ranges may be selected between any of these values (for example,
about 40 to about 99, about 50 to about 99, about 60 to about 99,
about 70 to about 99, about 80 to about 99, or about 90 to about
99%).
[0050] In one embodiment the blend is a blend of lactic acid and a
polymer, preferably a biodegradable polymer, such as a polymer of
an ester (a polyester), methacrylate (polymethacrylate), methyl
methacrylate (poly(methyl methacrylate), PMMA), glycolic acid
(polygloycolic acid, PGA), .epsilon.-caprolactone
(polycaprolactone, PCL), a hydroxyalkanoate (poly-hydroxyalkanoate,
PHA), hydroxybutyrate (poly-hydroxybutyrate, PHB), hydroxyvalerate
(poly-hydroxyvalerate, PHV), hydroxyhexanoate
(poly-hydroxyhexanoate, PHH), or hydroxyoctanoate
(poly-hydroxyoctanoate, PHO), for example. In one embodiment, the
blend comprises at least 40, 45, 50, 55, 60, 65, 70, 75, 80, 85,
90, 95, or 99% PLA by weight, and useful ranges may be selected
between any of these values (for example, about 40 to about 99,
about 50 to about 99, about 60 to about 99, about 70 to about 99,
about 80 to about 99, or about 90 to about 99%). In one embodiment
the blend comprises about 50 to about 70% by weight PLA. In one
embodiment the blend comprises poly(methyl methacrylate) and about
50 to about 70% by weight PLA.
[0051] In one embodiment the resin is in the form of a particle,
bead, rod, bar, sheet, film, moulded shape (such as a clamshell,
pot, box, bowl, cup, plate or tray) or extruded shape. Accordingly,
in one embodiment the impregnated resin is in the form of a
particle, bead, rod, bar, sheet, film, moulded shape (such as a
clamshell, pot, box, bowl, cup, plate or tray) or extruded
shape.
[0052] In one embodiment the resin further comprises one or more
fillers, additives, nucleating agents, plasticisers or co-blowing
agents, or any combination of any two or more thereof.
[0053] In one embodiment the resin comprises about 1, 5, 10, 15,
20, 25, 30, 35, 40, 45 or 50% by weight of one or more fillers,
additives, nucleating agents, plasticisers or co-blowing agents, or
any combination of any two or more thereof, and useful ranges may
be selected between any of these values (for example, about 1 to
about 10, about 1 to about 20, about 1 to about 30, about 1 to
about 40, or about 1 to about 50%). In one embodiment the resin
comprises about 1 to about 10% or about 1 to about 5% by weight
bark.
[0054] In one embodiment the foam comprises polylactic acid, or
otherwise comprises a resin as is described above.
[0055] In one embodiment the foam comprises at least about 88% by
weight L or D lactic acid or a blend of poly-L-lactic acid and
poly-D-lactic acid homopolymer, or a blend of PLA block copolymers
where each block has an isomer purity of greater than 88% of
L-lactic acid or D-lactic acid.
[0056] In one embodiment the foam comprises one or more fillers,
additives, nucleating agents, plasticisers or co-blowing agents, or
any combination of any two or more thereof, as described above.
[0057] It is intended that reference to a range of numbers
disclosed herein (for example, 1 to 10) also incorporates reference
to all rational numbers within that range (for example, 1, 1.1, 2,
3, 3.9, 4, 5, 6, 6.5, 7, 8, 9 and 10) and also any range of
rational numbers within that range (for example, 2 to 8, 1.5 to 5.5
and 3.1 to 4.7) and, therefore, all sub-ranges of all ranges
expressly disclosed herein are hereby expressly disclosed. These
are only examples of what is specifically intended and all possible
combinations of numerical values between the lowest value and the
highest value enumerated are to be considered to be expressly
stated in this application in a similar manner.
[0058] In this specification where reference has been made to
patent specifications, other external documents, or other sources
of information, this is generally for the purpose of providing a
context for discussing the features of the invention. Unless
specifically stated otherwise, reference to such external documents
is not to be construed as an admission that such documents, or such
sources of information, in any jurisdiction, are prior art, or form
part of the common general knowledge in the art.
[0059] The invention may also be said broadly to consist in the
parts, elements and features referred to or indicated in the
specification of the application, individually or collectively, in
any or all combinations of two or more of said parts, elements or
features, and where specific integers are mentioned herein which
have known equivalents in the art to which the invention relates,
such known equivalents are deemed to be incorporated herein as if
individually set forth.
BRIEF DESCRIPTION OF THE FIGURES
[0060] FIG. 1 is a graph showing the relationship between the glass
transition temperature, Tg for PLA and CO.sub.2 concentration (1.4%
D PLA).
[0061] FIG. 2 is a graph showing the minimum density and
corresponding CO.sub.2 concentration at foaming as a function of
impregnation temperature (1.4% D PLA).
[0062] FIG. 3 is a graph showing the minimum density and
corresponding CO.sub.2 concentration at foaming as a function of
impregnation temperature (4.3% D PLA).
[0063] FIG. 4 is a graph showing the minimum density and
corresponding CO.sub.2 concentration at foaming as a function of
impregnation temperature (7.7% D PLA).
[0064] FIG. 5 is a graph showing the DSC trace of a 60 g/L
stereocomplex PLA foam (10.degree. C./min).
[0065] FIG. 6 is a graph showing the volumetric shrinkage plotted
against D-content at 40 g/L.
[0066] FIG. 7 is a graph showing the volumetric shrinkage of foamed
1.4% D PLA beads as a function of foam crystallinity (A) and foam
density (B), for various foaming temperatures.
[0067] FIG. 8 is a graph showing the linear shrinkage under 10 kPa
compression (heating rate is 2.degree. C. per minute) for moulded
PLA 4060D and PLA 3001D foams.
[0068] FIG. 9 is a graph showing the density versus impregnation
temperature relationship for 70:30 and 50:50 semi-crystalline
PLA:PMMA blends.
DETAILED DESCRIPTION
[0069] The inventor has discovered that crystallisable grades of
polylactic acid (PLA) and crystallisable PLA resins, including
copolymers and blends, can be impregnated and foamed to low
density. Crystallisable grades of PLA (including stereocomplex PLA)
and PLA resins lead to better thermal stability than found
previously for PLA foam and indeed other PLA foam structures.
[0070] The present invention relates to a method of foaming
crystallisable PLA, including stereocomplex PLA and other PLA
resins, the method comprising impregnating solid polymer, such as
PLA resin with CO.sub.2 by contacting the resin with liquid
CO.sub.2 at temperatures below about 2.degree. C., 1.degree. C. or
0.degree. C. and more preferably at a temperature of about
-57.degree. C. to about 2.degree. C. at a corresponding pressure
that ensures the CO.sub.2 remains in the liquid phase, removing the
resin from the liquid CO.sub.2, and holding the impregnated resin
at a temperature and pressure that prevents it from crystallising
or foaming while allowing the level of impregnated CO.sub.2 to
reduce to a level suitable for foaming.
[0071] Liquid CO.sub.2 impregnation of PLA is performed at a
temperature that minimises premature crystallisation. For example,
impregnation of crystallisable PLA can be carried out at a
temperature of from about -57.degree. C. to about 2.degree. C.,
more preferably about -57.degree. C. to about -30.degree. C. for
high expandability.
[0072] This method can be used for crystallisable PLA which has
been prepared in an amorphous state.
[0073] This method can also be applied to PLA polymerised with
other co-monomers, PLA blends with other polymers, and modified
PLA, including cross-linked PLA or functionalised PLA. The optimum
impregnation temperature range may be adjusted for these PLA-based
polymers, according to the material's initial Tg, CO.sub.2 uptake
and Tg--CO.sub.2 relationship. That is, the temperature for
impregnation will vary with each polymer but will be such that
temperature of impregnation and/or conditioning is at or below the
Tg of the newly plasticised (by CO.sub.2 or another plasticiser)
polymer.
[0074] This method can be used for PLA in various physical shapes
including particles, beads, rods, bars, sheets, films, moulded
shapes (such as clamshells, pots, boxes, bowls, cups, plates or
trays) or extruded shapes.
[0075] As noted above, the liquid CO.sub.2 impregnation is carried
out under conditions that minimise premature crystallisation of the
polymer.
[0076] Post-impregnation, the polymer is held under conditions that
prevent crystallisation of the polymer. That is, a temperature at
or below the glass transition temperature, Tg, of the PLA, that is
influenced by the concentration of CO.sub.2 as defined by the graph
of FIG. 1.
[0077] The percentage of CO.sub.2 absorbed by the PLA through
impregnation is about 1 to about 55% by weight of the
polymer-CO.sub.2 mixture, or otherwise up to a saturated level. The
residence time in the liquid CO.sub.2 is chosen to ensure the PLA
sample is impregnated with the desired amount of CO.sub.2 for the
intended application. The residence time is dependent sample shape,
size and temperature, but not pressure (provided the pressure used
retains the CO.sub.2 in the liquid phase). For example, 2 mm PLA
rods (Ingeo.TM. grade 3001D) require an impregnation time of
greater than 2 hours if impregnated at -50.degree. C.
[0078] After impregnation, the PLA is held to allow the level of
CO.sub.2 in the PLA to reduce to a level suitable for foaming. The
level of CO.sub.2 in the PLA suitable for foaming can vary but
typically is about 5 to about 30% by weight, preferably about 10 to
about 25% by weight.
1. DEFINITIONS
[0079] The term "comprising" as used in this specification and
claims means "consisting at least in part of". When interpreting
statements in this specification and claims which include the
"comprising", other features besides the features prefaced by this
term in each statement can also be present. Related terms such as
"comprise" and "comprised" are to be interpreted in similar
manner.
[0080] The term "crystallisable" in relation to a polymer means
that the polymer is capable of crystallising and also melting. The
term "semi-crystalline" has a similar meaning. For a
poly(D,L)lactic acid copolymer, the lower the concentration of one
of the monomers with respect to the other, the higher the potential
crystallinity of the PLA will be. In addition, when PLA comprising
of 100% L-lactic acid (PLLA), or high-purity PLLA, is blended with
PLA comprising of 100% D-lactic acid (PDLA), or high-purity PDLA, a
highly regular stereocomplex can be formed upon crystallisation.
Temperature stability after foaming is maximised when a 50:50 blend
is used, but even at lower concentrations of 3-10% of PDLA in PLLA
(or vice versa), there is still a substantial improvement.
[0081] The term "crystallisable" in relation to PLA refers to PLA
copolymers with an isomer purity of about 88% or more and blends of
one or more such copolymers wherein the isomer purity of the blend
is still about 88% or more--for example, copolymers with a D-isomer
content of from about 0% to about 12% by weight and an L-isomer
content of from about 88 to about 100% by weight, copolymers with
an L-isomer content from about 0% to about 12% by weight and a
D-isomer content of from about 88% to about 100% by weight, blends
of such copolymers with a total D-isomer content of about 0% to
about 12% by weight, and blends of such copolymers with a total
L-isomer content of about 0% to about 12% by weight. Furthermore,
the term "crystallisable" in relation to PLA also refers to
stereocomplex blends of pure PDLA (or high-purity PDLA) and PLLA
(or high-purity PLLA).
2. POLYLACTIC ACID AND OTHER RESINS
[0082] Polylactic acid (PLA) is a polymer comprising of lactic acid
monomer units. PLA is produced industrially by polymerisation of
lactic acid obtained by the bacterial fermentation of biomass such
as beet, sugarcane, cornstarch or milk products. Lactic acid occurs
in two stereoisomers, L-lactic acid and D-lactic acid. PLA
comprises of a certain proportion of L-lactic acids monomers and a
certain proportion of D-lactic acid monomers. The ratio between the
L- and D-lactic acid monomers in PLA determines its properties.
When PLA contains more than approximately 12% of one lactic monomer
(either L or D) it can no longer crystallise and is hence
completely amorphous. The lower the concentration of one of the
monomers with respect to the other, the higher the potential
crystallinity of the PLA will be.
[0083] Crystallisable PLA copolymers, crystallisable PLA block
copolymers or crystallisable PLA homopolymers, or a blend of any
two or more thereof, or a blend of any one or more thereof with one
or more other polymers, each as described above, are contemplated
for use herein.
[0084] PLA can be polymerised with co-monomers other than lactic
acid, or blended with other polymers, and modified in various ways
such as cross-linking or functionalizing.
[0085] For a crystallisable resin to be expanded into a foam, it
should be prepared in such a way as to minimise crystallinity in
the polymer prior to impregnation with liquid CO.sub.2. Minimised
crystallinity can be achieved by melting a resin and rapidly
cooling the resin from the melt, or by using a
dissolution/precipitation method. Such methods are known in the
art.
[0086] In addition, liquid CO.sub.2 impregnation, and the
subsequent conditioning phase, should be carried out to minimise
any increase in the crystallinity of the polymer prior to any
expansion/foaming step.
3. METHOD OF IMPREGNATION
[0087] There are a number of reported processes that use CO.sub.2
to impregnate expandable (foamable) polymers such as PLA, where the
CO.sub.2 acts as a blowing agent to produce a polymer foam.
Reported foaming and moulding processes using, for example, PLA
impregnated with CO.sub.2 generally involve impregnating PLA resin,
such as resin beads with gaseous or supercritical CO.sub.2,
pre-expanding the impregnated resin, resting and optionally
treating the pre-expanded resin, before re-impregnating the resin
with more CO.sub.2 or another blowing agent and further
expanding/fusing the resin in a mould. The present invention uses
liquid CO.sub.2 to impregnate PLA.
[0088] During liquid CO.sub.2 impregnation at a given temperature
(T), CO.sub.2 is known to plasticise PLA and decrease its glass
transition temperature, Tg. If Tg is decreased significantly below
T, PLA can crystallise. This crystallisation is generally
detrimental to foaming. The decrease of Tg is a function of
CO.sub.2 absorption, which itself is a function of impregnation
temperature.
[0089] The process can be applied to any crystallisable PLA as
previously defined but it is preferentially applied to PLA with a
high crystallisation ability, for example PLA homopolymer (L or D)
with a purity higher than 95%, 97% or 99%, or a stereocomplex
blend, a PLA copolymer or block copolymer, or a PLA-based resin
with equivalent or better crystallisation ability.
[0090] In one embodiment, the process is applied to a
crystallisable PLA resin that has been prepared in an amorphous
state of, for example, less than about 20% crystallinity. An
amorphous state comprising less than about 20% crystallinity may be
determined by differential scanning calorimetry (DSC). A suitable
DSC method comprises heating 5-10 mg of material from 20.degree. C.
to at least 20.degree. C. above the end of the melting endotherm
under a heating rate of 5.degree. C. per minute. Crystallinity is
calculated by subtracting the crystallisation exotherm area from
the melting endotherm area. The melting enthalpy of PLA
homocrystals and PLA stereocomplex crystals are assumed to be 93
J/g and 142 J/g respectively.
[0091] Liquid CO.sub.2 impregnation is carried out between -57 and
2.degree. C., or preferentially between -57 and -30.degree. C.
Pressure is applied to ensure that CO.sub.2 is in its liquid state.
For example, in an impregnation carried out at -50, -40, -30, -20,
-10 or 0.degree. C., the pressure is at least 6.8, 10.1, 14.3,
19.7, 26.5 or 34.9 bar respectively.
[0092] Polymer resin, such as in bead, extruded or moulded form, is
placed in a pressure vessel. The vessel is cooled to the required
temperature of about -57.degree. C. to about 2.degree. C. Liquid
CO.sub.2 is introduced into the vessel to the required pressure
(e.g. about 5 to 100 bar). After a period of time suitable for the
desired degree of impregnation, CO.sub.2 pressure is released and
the vessel removed from temperature control. Impregnation continues
for at least about 10, 30, 60, 90, 120 minutes, or about 3, 6, 7 or
12 hours or more until CO.sub.2 impregnation is complete. CO.sub.2
impregnation is complete when the CO.sub.2 content of the polymer
resin is about 0 to about 55% by weight of the polymer-CO.sub.2
mixture, or otherwise up to a saturated level.
[0093] Impregnated resin may be stored under refrigerated
conditions at a temperature of about -57 to about 4.degree. C. or
is processed directly. The CO.sub.2 content of stored resin will
reduce over time and is optionally allowed to reduce to a CO.sub.2
concentration of about 5 to about 30% by weight, including about 10
to about 25% by weight.
[0094] Impregnated resin, whether after storage or directly after
impregnation, is then subjected to pre-expansion, or pre-expansion
and moulding, or moulding without pre-expansion.
[0095] A pre-expansion step involves heating the impregnated resin
or a mould containing the resin for a suitable time, such as for
about 1 to about 120 seconds, at a suitable temperature, such as
about 15 to about 140.degree. C., using a suitable heating
mechanism, such as, for example, a hot fluid such as hot water,
steam, hot air or hot oil, or by exposing the resin to
electromagnetic radiation such as microwaves.
[0096] Once impregnated or pre-expanded resin is added to a mould,
a combination of steam heating, such as at about 50 to about
150.degree. C., for about 5 to 180 seconds, for example, and
optional vacuum, such as for about 1 second to about 10 minutes,
for example, is applied to expand or further expand and fuse the
resin. Steam and optionally vacuum are applied to fuse the
impregnated resin and fill the mould shape, to make a foam block.
Other methods known in the art for expanding and fusing the resin
in the mould may be used, such as heating with microwaves, oil, or
water, for example, with or without the application of vacuum.
Cooling may be applied before de-moulding, using water cooling of
the mould for example. Average block density can be readily
calculated from the weight and dimensions of the block. Block
density is preferably measured 48 hours after moulding by which
time the CO.sub.2 levels have stabilised.
4. FILLERS AND ADDITIVES
[0097] The resin may be blended with other fillers, additives,
nucleating agents (e.g. talc), plasticisers or co-blowing agents up
to 50% by weight.
[0098] In one embodiment the fillers are inert and/or
biodegradable. Suitable fillers include but are not limited to
talc, calcium carbonate, calcium stearate, sand, clay, zeolite,
bark (including pine bark), sawdust, wood flour, biomass, polymers,
biodegradable polymers, flour or fibre derived from plants,
inorganic filler, borax, zinc borate, aluminium hydroxide, natural
fibres, pigments, or any mixture of any two or more thereof.
Preferred fillers include talc, calcium carbonate, clay, zeolite,
bark (including pine bark), sawdust, wood flour, biomass, polymers,
biodegradable polymers, or flour or fibre derived from plants, or
any mixture of any two or more thereof. In one embodiment the PLA
is blended with about 1, 5, 10, 15, 20, 25, 30, 35, 40, 45 or 50%
by weight of one or more fillers or additives, and useful ranges
may be selected between any of these values (for example, about 1
to about 50%).
[0099] Various aspects of the invention will now be illustrated in
non-limiting ways by reference to the following examples.
EXAMPLES
General Protocol
[0100] Unless otherwise stated, the following general protocol was
followed. Crystallisable PLA, typically as beads, rods, injection
moulded articles or solvent casted sheet was prepared with low
levels of crystallinity. In some experiments, fillers or other
additives were included (e.g. talc). The PLA articles were placed
in a pressure vessel suited to withstand the required pressure and
temperature ranges. The vessel was cooled to the required
temperature (-55 to 0.degree. C.). Liquid CO.sub.2 was introduced
into the vessel to the required pressure (e.g. about 25 to 35 bar).
The pressure was monitored throughout the impregnation to ensure it
remained within the range required. After a period of time (at
-50.degree. C., this is at least 60 minutes for 1.5 mm diameter
beads, 120 minutes for extruded 2 mm rods, 90 minutes for 1 mm
thick moulded bars for best results, optionally longer--overnight
for example) CO.sub.2 pressure was released and the vessel removed
from temperature control. The PLA was weighted before and after
impregnation to calculate % CO.sub.2 uptake by weight.
[0101] In some cases, CO.sub.2 impregnated PLA was expanded
directly. Alternatively, the impregnated PLA was stored in
refrigerated conditions, for example in a standard freezer at
-18.degree. C., and then subjected to pre-expansion, pre-expansion
and moulding, or moulding without pre-expansion. A third option was
to store the impregnated PLA until all CO.sub.2 had been lost.
[0102] The pre-expansion step involves heating the impregnated
beads (e.g. for about 5 seconds) at a suitable temperature (15 to
120.degree. C.) using hot water, steam or hot air.
[0103] Once impregnated or pre-expanded beads are added to the
mould, a combination of steam heating (about 50 to 150.degree. C.,
for about 5 to 180 seconds for example) and optional vacuum (for
about 1 second to 10 minutes for example) was applied to further
expand and fuse the beads. Steam and optionally vacuum are applied
for a short time (e.g. 2 to 10 minutes) to fuse the impregnated
beads and fill the mould shape, to make a foam block. Cooling may
be applied before de-moulding, using water cooling of the mould for
example. Average block density can be readily calculated from the
weight and dimensions of the block. Block density is preferably
measured 48 hours after moulding by which time the CO.sub.2 levels
have stabilised.
Example 1
1.4% D PLA rods, -50 to -20.degree. C. impregnation, foaming at
various CO.sub.2 concentrations
[0104] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) was
extruded and subsequently cooled from the melt to room temperature
using a water bath, ensuring negligible crystallisation. The
extruded strands (2 mm in diameter) were then cut into 15 mm long
rods. Rod samples were impregnated with liquid CO.sub.2 at -50,
-40, -35, -30 and -20.degree. C. for a duration that allowed full
saturation of PLA with CO.sub.2. After impregnation, the samples
were placed into a freezer at -18.degree. C. to allow the CO.sub.2
concentration to drop. Samples were taken out regularly, their
CO.sub.2 concentration measured by weight, and were foamed in
80.degree. C. water for 20 seconds. Density of the foamed samples
was measured. For each impregnation temperature, an optimum
CO.sub.2 concentration existed at which density was minimal
(indicated in FIG. 2). Only impregnations below -35.degree. C.
produced low densities (approx. 40 g/L) as shown in FIG. 2.
Impregnation above -35.degree. C. produced high densities (approx.
300 g/L).
Example 2
4.3% D PLA Rods, -50 to -20.degree. C. Impregnation, Foaming at
Various CO.sub.2 Concentrations
[0105] Crystallisable 4.3% D PLA (Ingeo.TM. grade 4042D) was
prepared and foamed as in example 1. A similar foaming behaviour
was observed (FIG. 3).
Example 3
7.7% D PLA Rods, -50 to -20.degree. C. Impregnation, Foaming at
Various CO.sub.2 Concentrations
[0106] Crystallisable 7.7% D PLA (a blend of 40% Ingeo.TM. grade
4042D and 60% Ingeo.TM. grade 8032D) was extruded and then foamed
as described in example 1 except that the foaming temperature used
was 75.degree. C. instead of 80.degree. C. The minimum density
showed a linear trend over the impregnation temperature range used
as seen in FIG. 4.
Example 4
Stereo-Complex PLA Rods, -50.degree. C. Impregnation, Foaming at
80.degree. C.
[0107] Stereo-complex PLA was prepared by extrusion-blending of
PLLA and PDLA homo-polymers with a 1:1 ratio. The extruded rods
were impregnated with liquid CO.sub.2 at -50.degree. C. for 4
hours, then stored at -18.degree. C. for 2 to 21/2 hours, and
finally foamed in 80.degree. C. water for 20 seconds. The foamed
rods had a density between 50 and 70 g/L. DSC showed that the
foamed samples comprised approximately 45% homocrystals, and 25%
stereocomplex crystals (FIG. 5). The melting enthalpies of pure
crystals are assumed to be 93 J/g and 142 J/g for the homocrystals
and stereocomplex crystals respectively.
Example 5
Poly(D-lactide)
[0108] Poly(D-lactic acid) (<1% L-isomer, melt flow index=22
g/minute at 190.degree. C.) was melted at 190.degree. C. and
extruded and quenched using a CEAST melt flow tester. The strands
(0.3-0.4 mm in diameter) were impregnated with liquid CO.sub.2 at
-50.degree. C. for 1 hour. The impregnated material was stored at
-18.degree. C. until the CO.sub.2 concentration decreased to 14-17
wt. %. The samples were then foamed in hot water (80.degree. C.)
for 10 seconds. The density of the foamed samples was measured at
between 34 and 36 g/L.
Example 6
Fusing 1.4% D PLA Beads
[0109] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) extruded,
subsequently cooled from the melt in a water bath, and pelletised
(2 mm diameter beads). The beads were impregnated with liquid
CO.sub.2 at -50.degree. C. for 2 hours 20 minutes, thus ensuring
saturation with CO.sub.2. The beads were stored in a freezer at
-18.degree. C. for 90 minutes when the CO.sub.2 concentration
reached 19 wt %. They were then prefoamed for 20 seconds in
65.degree. C. hot water then quenched in cold water. The prefoamed
beads were placed into a cylindrical mould (36 mm in diameter, 50
mm long) and fused with steam (approx. 90.degree. C.) for 20
seconds. The moulded product exhibited good fusing and had a final
density of approximately 42 g/L.
Example 7
Fusing 1.4% D PLA Beads
[0110] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) beads were
prepared, impregnated and stored as in example 6. Prefoaming was
performed in 60.degree. C. water for 35 seconds then quenched in
cold water. Fusing was done with 90.degree. C. steam for 20 or 60
seconds. The mouldings exhibited good fusing and a density of
approximately 46 g/L.
Example 8
Fusing 1.4% D PLA Beads
[0111] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) beads were
prepared, impregnated and stored as in example 6. Prefoaming was
performed in 70.degree. C. water for 7 seconds then quenched in
cold water. Fusing was done with 90.degree. C. steam for 20 or 60
seconds. The mouldings exhibited good fusing and a density of
approximately 47 g/L.
Example 9
Fusing 4.3% D PLA Beads
[0112] Crystallisable 4.3% D PLA (Ingeo.TM. grade 4042D) beads were
prepared, impregnated and stored as in example 6. Prefoaming was
performed in 70.degree. C. water for 10 seconds then quenched in
cold water. Fusing was done with 90.degree. C. steam for 10, 20 or
60 seconds. The moulding exhibited good fusing and a density of
42-46 g/L.
Example 10
Dimensional Stability--Comparison Between Various Grades Using
Rods
[0113] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D), 4.3% D
PLA (Ingeo.TM. grade 4042D), 7.7% D PLA (a blend of 40% Ingeo.TM.
grade 4042D and 60% Ingeo.TM. grade 8032D), and 11.8% D PLA
(Ingeo.TM. grade 4060D), were extruded into rods as in example 1.
The first three grades were impregnated with liquid CO.sub.2 at
-50.degree. C. for 2 hours, then stored at -18.degree. C. for 60
minutes before being foamed in 80.degree. C. water to a density of
approximately 40 g/L. 11.8% D PLA was impregnated at 0.degree. C.
for 50 minutes and stored 90 minutes at -18.degree. C. before being
foamed in 75.degree. C. water to a density of 40 g/L. The foamed
samples were dried at room temperature under air flow and then
equilibrated for at least 48 hours. The exact volume of the samples
was then measured and the samples were put in an oven at 70.degree.
C. for 24 hours. After this thermal treatment, the volume of the
samples was re-measured, and the volumetric shrinkage .DELTA.V
induced by the thermal treatment calculated as:
.DELTA. V = 100 .times. V initial - V final V initial
##EQU00003##
[0114] Lower D-content led to lower shrinkage. In particular,
shrinkage was significantly reduced for 1.4% D PLA (FIG. 6).
Example 11
Dimensional Stability of 1.4% D PLA with Various Foaming
Conditions
[0115] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) beads were
extruded and impregnated with liquid CO.sub.2 at -50.degree. C. as
described in example 6. After impregnation, they were stored at
-18.degree. C. for 90 minutes and then foamed in 60, 70 or
80.degree. C. water for times ranging from 1 to 90 seconds.
Crystallinity of the foamed beads was measured by DSC.
Crystallinity appeared to increase with expansion during foaming.
Dimensional stability at 70.degree. C. was assessed as in example
10. FIG. 7 shows the link between crystallinity and shrinkage.
Shrinkage virtually disappeared above a crystallinity
threshold.
Example 12
Comparison of 1.4% D PLA Rods Prepared in the Amorphous State
(Non-Annealed) and Crystallised State (Annealed) State,
Impregnation and Foaming
[0116] PLA 3001D rods (2 mm diameter) were annealed for 2 hours at
103.degree. C. The samples were impregnated at -50.degree. C. in
liquid CO.sub.2 for 4 hours along with non-annealed samples. The
annealed samples were `foamed` in a water bath (80.degree. C.) at
CO.sub.2 concentration between 11 and 13%. They did not expand. The
non-annealed samples were foamed at CO.sub.2 concentrations of 11
and 20% and expanded to densities of 67 and 38 g/L,
respectively.
Example 13
1.4% D PLA moulding and properties
[0117] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) was
extruded, subsequently cooled from the melt in a water bath, and
pelletised (2 mm diameter beads). The beads were impregnated with
liquid CO.sub.2 at -50.degree. C. for 2 hours 20 minutes, thus
ensuring saturation with CO.sub.2. The beads were stored in a
freezer at -18.degree. C. until the CO.sub.2 concentration reached
19-21 wt %. They were then prefoamed for 20 to 27 seconds in
65.degree. C. hot water then quenched in cold water. The prefoamed
beads were placed into a 5.5.times.5.5.times.10 cm mould and fused
with steam for 20 to 40 seconds. The steam was provided by a
pressurised boiler set at 95 to 110.degree. C. The moulded blocks
exhibited good fusing and had a final density of 33 to 42 g/L. For
comparison, non-crystallisable 12% D PLA (Ingeo.TM. grade 4060D)
was extruded the same way and impregnated with liquid CO.sub.2 at
10.degree. C. for 1 hour. The beads were stored at -18.degree. C.
until the CO.sub.2 concentration reached 14 wt %. They were then
prefoamed for 14 seconds in 70.degree. C. hot water then quenched
in cold water. They were fused in the previously described setup
for 40 seconds with the boiler set at 90.degree. C. These samples
had a density of approximately 40 g/L. Typical properties are
listed in Table 1. Cylindrical samples were cut from the moulded
blocks and tested in a RSA-G2 DMTA apparatus (TA Instruments). The
samples were subjected to a constant 10 kPa compressive stress and
heated from room temperature at 2.degree. C. per minute. The linear
shrinkage was measured as the deflection of the sample (in % of the
initial sample height) throughout the test. FIG. 8 shows typical
examples of linear shrinkage-temperature obtained.
TABLE-US-00001 TABLE 1 Properties of moulded PLA foams at 40 g/L.
PLA 3001D PLA 4060D Compressive modulus (MPa) 7 10 Compressive
strength at 10% strain (MPa) 0.27 0.27 Tensile modulus (MPa) 24 29
Tensile strength (MPa) 0.16 0.47 Temperature at 5% linear shrinkage
(.degree. C.) 81-90 67 Crystallinity (%) 40-47 <5
Example 14
PMMA-PLA Blends
[0118] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) was
blended with poly(methyl methacrylate) (PMMA, Chi Mei Corporation,
Acryrex CM207) via extrusion. Two blends were made 70:30 and 50:50
(PLA:PMMA ratio) and pelletised into 2 mm beads. The beads were
impregnated with liquid CO.sub.2 at -30, -20 and -10.degree. C.
until saturation. After impregnation, the samples were stored at
-18.degree. C. and foamed at various CO.sub.2 concentrations for 20
seconds in 90.degree. C. water. The minimum density obtained at
each impregnation temperature is displayed in FIG. 9. Furthermore,
50:50 blend beads were impregnated at -20.degree. C. and stored at
-18.degree. C. until their CO.sub.2 concentration reached 18-20%.
They were then prefoamed in 80.degree. C. water for 10 seconds and
moulded as described in Example 13. The moulded samples had density
between 27 and 40 g/L, showed excellent fusing and mechanical
properties.
Example 15
PLA with Talc
[0119] Crystallisable PLA (Ingeo.TM. grade 3051D, approximately
4-5% D) was extruded with (5% by weight) or without talc into 2 mm
beads. The beads were impregnated with liquid CO.sub.2 between -50
and -40.degree. C. for at least 21/2 hours. The impregnated beads
were then stored at -18.degree. C. When their CO.sub.2
concentrations reached approximately 18% they were prefoamed in a
65.degree. C. water bath for 15 seconds and then moulded in the
setup described earlier in Example 13 with the boiler set at
110.degree. C. Steam was applied for 20 seconds. Samples without
talc exhibited excellent fusing and had a density of 40 g/L. The
samples containing talc had good fusing and density of 43 g/L.
Example 16
PLA with Bark
[0120] Crystallisable PLA (Ingeo.TM. grade 3051D, approximately
4-5% D) was extruded with 1, 5 or 20% bark and then
injection-moulded into a 1 mm thick article. Strip samples were cut
from these and were impregnated with liquid CO.sub.2 between -50
and -40.degree. C. for 2.sup.1/2 hours. The impregnated samples
were then stored at -18.degree. C. When their CO.sub.2
concentrations reached approximately 22% they were prefoamed at
80.degree. C. for 20 seconds. The samples were dried at room
temperature. Samples with 1 and 5% bark foamed to low density
(<40 g/L).
Example 17
PLA with Bark--Moulded Shape
[0121] Crystallisable PLA (Ingeo.TM. grade 3051D, approximately
4-5% D) was extruded with 5% bark and then injection-moulded into
pots with 1 mm thick walls. The samples were impregnated with
liquid CO.sub.2 between -20 and -10.degree. C. at 40 bar in a 2 L
Parr pressure vessel for 2 hours 20 minutes. The impregnated
samples were then stored at -18.degree. C. When their CO.sub.2
concentrations reached approximately 16 wt. % they were prefoamed
at 80.degree. C. for 20 seconds. The samples were then dried at
room temperature. The density of the samples was measured at 55-68
g/L.
Example 18
Expansion with Air
[0122] Crystallisable 1.4% D PLA (Ingeo.TM. grade 3001D) was
extruded and pelletised into 2 mm beads. The beads were impregnated
with liquid CO.sub.2 between -50 and -40.degree. C. for 3 hours.
After impregnation, the samples were stored at -18.degree. C. until
their CO.sub.2 concentrations reached 17-20%. The beads were then
foamed for approximately 1 minute with hot air in a modified
kitchen pop corn maker set at 80.degree. C. The bulk density of the
foamed beads was measured at 25-30 g/L.
INDUSTRIAL APPLICABILITY
[0123] The products and processes of the present invention have
application in the packaging industry and other areas employing
expanded polymer foams.
[0124] Those persons skilled in the art will understand that the
above description is provided by way of illustration only and that
the invention is not limited thereto.
* * * * *