U.S. patent application number 14/638033 was filed with the patent office on 2015-07-23 for surface diffusion inhibitor for hamr nft.
This patent application is currently assigned to HGST NETHERLANDS B.V.. The applicant listed for this patent is HGST Netherlands B.V.. Invention is credited to Hamid BALAMANE, Vijay Prakash Singh RAWAT.
Application Number | 20150206545 14/638033 |
Document ID | / |
Family ID | 52683346 |
Filed Date | 2015-07-23 |
United States Patent
Application |
20150206545 |
Kind Code |
A1 |
BALAMANE; Hamid ; et
al. |
July 23, 2015 |
SURFACE DIFFUSION INHIBITOR FOR HAMR NFT
Abstract
Embodiments of the present invention generally relate to a HAMR
head including a near field transducer having an antenna, a surface
diffusion inhibitor layer disposed on a portion of the antenna and
an aperture disposed over the surface diffusion inhibitor layer.
The surface diffusion inhibitor layer has a greater melting point
than the antenna, and the surface diffusion inhibitor layer
material is immiscible in the antenna material.
Inventors: |
BALAMANE; Hamid; (Portola
Valley, CA) ; RAWAT; Vijay Prakash Singh; (San Jose,
CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
HGST Netherlands B.V. |
Amsterdam |
|
NL |
|
|
Assignee: |
HGST NETHERLANDS B.V.
|
Family ID: |
52683346 |
Appl. No.: |
14/638033 |
Filed: |
March 4, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14158515 |
Jan 17, 2014 |
8988827 |
|
|
14638033 |
|
|
|
|
Current U.S.
Class: |
369/13.33 |
Current CPC
Class: |
G11B 5/314 20130101;
G11B 5/6088 20130101; G11B 2005/0021 20130101 |
International
Class: |
G11B 5/31 20060101
G11B005/31 |
Claims
1. A heat assisted magnetic recording head, comprising: a near
field transducer, wherein the near field transducer comprises: an
antenna having a first melting point; and at least one surface
diffusion inhibitor layer disposed on a portion of the antenna,
wherein the at least one surface diffusion inhibitor layer has a
second melting point that is different than the first melting
point.
2. The heat assisted magnetic recording head of claim 1, further
comprising: a first conductive layer disposed over the near field
transducer; a magnetic lip disposed over the first conductive
layer; a second conductive layer disposed over the first conductive
layer and over vertical sides of the magnetic lip; a heat sink
disposed over the second conductive layer; and a write pole
disposed over the heat sink, the second conductive layer and the
magnetic lip.
3. The heat assisted magnetic recording head of claim 1, wherein
the at least one surface diffusion inhibitor layer is an Au alloy
including a material selected from the group consisting of Rh, Ru,
W, Mo, Ir, Co, Pt, B and Ni.
4. The heat assisted magnetic recording head of claim 1, wherein
the second melting point is greater than the first melting
point.
5. The heat assisted magnetic recording head of claim 1, further
comprising an adhesion layer disposed on the at least one surface
diffusion inhibitor layer, wherein the adhesion layer includes a
material selected from the group consisting of Si, Ta, Ti, Zr, Cr,
Hf, NiTa, NiCr, NiTi, NiHf, and NiZr.
6. The heat assisted magnetic recording head of claim 1, further
comprising: a magnetic lip disposed over an aperture covering a
portion of the aperture; a first conductive layer disposed between
the magnetic lip and the aperture and over vertical sides of the
magnetic lip; a second conductive layer disposed over the antenna,
vertical sides and a top surface of the aperture not covered by the
first conductive layer, and vertical sides of the first conductive
layer; a heat sink disposed over the second conductive layer; and a
write pole disposed over the heat sink, the first conductive layer,
the second conductive layer and the magnetic lip.
7. The heat assisted magnetic recording head of claim 1, further
comprising: a first conductive layer disposed over the aperture; a
magnetic lip disposed over the first conductive layer covering a
first portion of the first conductive layer; a second conductive
layer disposed over the antenna, vertical sides of the aperture, a
second portion of the first conductive layer, and vertical sides of
the magnetic lip; a heat sink disposed over the second conductive
layer; and a write pole disposed over the heat sink, the second
conductive layer and the magnetic lip.
8. The heat assisted magnetic recording head of claim 7, wherein
the at least one surface diffusion inhibitor layer is an Au alloy
including a material selected from the group consisting of Rh, Ru,
W, Mo, Ir, Co, Pt, B and Ni.
9. The heat assisted magnetic recording head of claim 1, wherein
the at least one surface diffusion inhibitor layer comprises: a
first surface diffusion inhibitor layer disposed between the
antenna and an aperture; a second surface diffusion inhibitor layer
disposed between a first end of the antenna and a waveguide core;
and a third surface diffusion inhibitor layer disposed on a second
end of the antenna at a media facing surface.
10. The heat assisted magnetic recording head of claim 9, further
comprising: a conductive layer disposed over the aperture; a
magnetic lip disposed over the conductive layer; and a main pole
disposed over the magnetic lip, wherein the aperture, the
conductive layer, the magnetic lip and the main pole each has an
end at the media facing surface.
11. The heat assisted magnetic recording head of claim 10, wherein
the third surface diffusion inhibitor layer is disposed at the
media facing surface that covers the end of the aperture, the
conductive layer, the magnetic lip and the main pole.
12. The heat assisted magnetic recording head of claim 11, wherein
the antenna has a first melting point and the first, second and
third surface diffusion inhibitor layers have a second melting
point that is greater than the first melting point.
13. The heat assisted magnetic recording head of claim 1, further
comprising: a first cladding material; a waveguide core disposed on
the first cladding material; and a second cladding material
disposed on the waveguide core, wherein the antenna and the at
least one surface diffusion inhibitor layer is embedded in the
second cladding material, and wherein the antenna has a tapered
point at a media facing surface.
14. A hard disk drive, comprising: heat assisted magnetic recording
head, comprising: a near field transducer, wherein the near field
transducer comprises: an antenna having a first melting point; and
at least one surface diffusion inhibitor layer disposed on a
portion of the antenna, wherein the at least one surface diffusion
inhibitor layer has a second melting point that is different than
the first melting point.
15. The hard disk drive of claim 14, further comprising: a first
conductive layer disposed over the near field transducer; a
magnetic lip disposed over the first conductive layer; a second
conductive layer disposed over the first conductive layer and over
vertical sides of the magnetic lip; a heat sink disposed over the
second conductive layer; and a write pole disposed over the heat
sink, the second conductive layer and the magnetic lip.
16. The hard disk drive of claim 15, wherein the at least one
surface diffusion inhibitor layer is an Au alloy including a
material selected from the group consisting of Rh, Ru, W, Mo, Ir,
Co, Pt, B and Ni.
17. The hard disk drive of claim 14, wherein the second melting
point is greater than the first melting point.
18. The hard disk drive of claim 14, further comprising an adhesion
layer disposed on the at least one surface diffusion inhibitor
layer, wherein the adhesion layer includes a material selected from
the group consisting of Si, Ta, Ti, Zr, Cr, Hf, NiTa, NiCr, NiTi,
NiHf, and NiZr.
19. The hard disk drive of claim 14, wherein the at least one
surface diffusion inhibitor layer comprises: a first surface
diffusion inhibitor layer disposed between the antenna and an
aperture; a second surface diffusion inhibitor layer disposed
between a first end of the antenna and a waveguide core; and a
third surface diffusion inhibitor layer disposed on a second end of
the antenna at a media facing surface.
20. The hard disk drive of claim 14, further comprising: a first
cladding material; a waveguide core disposed on the first cladding
material; and a second cladding material disposed on the waveguide
core, wherein the antenna and the at least one surface diffusion
inhibitor layer is embedded in the second cladding material, and
wherein the antenna has a tapered point at a media facing surface.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of co-pending U.S. patent
application Ser. No. 14/158,515, filed Jan. 17, 2014, which is
herein incorporated by reference.
BACKGROUND
[0002] 1. Field
[0003] Embodiments of the present invention generally relate to
data storage systems, and more particularly, to write heads for
thermally assisted recording.
[0004] 2. Description of the Related Art
[0005] Higher storage bit densities in magnetic media used in disk
drives have reduced the size (volume) of magnetic bits to the point
where the magnetic bit dimensions are limited by the grain size of
the magnetic material. Although grain size can be reduced further,
the data stored within the cells may not be thermally stable. That
is, random thermal fluctuations at ambient temperatures may be
sufficient to erase data. This state is described as the
superparamagnetic limit, which determines the maximum theoretical
storage density for a given magnetic media. This limit may be
raised by increasing the coercivity of the magnetic media or by
lowering the operational temperature of magnetic hard drive.
Lowering the temperature may not always be practical when designing
hard disk drives for commercial and consumer use. Raising the
coercivity, on the other hand, will make it challenging for current
write heads to do the recording.
[0006] One additional solution has been proposed, which uses
magnetic media with high coercivity without the need to increase
the magnetic moment of write pole material. The solution heats up a
localized area on the media to a temperature above Curie
temperature, thereby, lowering the effective coercivity of the
localized region and thus, enabling writing with current write
heads within this heated region. The data state becomes "fixed"
once the media cools below Curie temperature. This technique is
broadly referred to as "thermally assisted (magnetic) recording"
(TAR or TAMR), "energy assisted magnetic recording" (EAMR), or
"heat-assisted magnetic recording" (HAMR) which are used
interchangeably herein. It can be applied to longitudinal and
perpendicular recording systems as well as "bit patterned media".
Heating of the media surface has been accomplished by a number of
techniques such as focused laser beams or near-field optical
sources.
[0007] While the laser beam or the near-field optical source is
positioned to induce heating in the magnetic media, a certain
percentage of heat will also be generated in the magnetic head.
This heating can affect the shape of the head at the media facing
surface, such as an air bearing surface (ABS), and therefore impact
the fly height. Heating of the head can also impact the reliability
and performance of the head because high temperatures can
accelerate thermal migration of various films and structures,
causing inter-diffusion and dimensional changes.
[0008] The primary areas of the HAMR head that get hot are the
near-field transducer (NFT) and magnetic pole placed proximate to
the NFT. The antenna material is comprised of noble metals with low
melting point and hence can show morphological changes at moderate
temperatures in the range of 150 to 400 degrees Celsius. Therefore,
there is a need in the art for an improved recording head for
HAMR.
SUMMARY OF THE INVENTION
[0009] Embodiments of the present invention generally relate to a
HAMR head including a near field transducer having an antenna, a
surface diffusion inhibitor layer disposed on a portion of the
antenna and an aperture disposed over the surface diffusion
inhibitor layer. The surface diffusion inhibitor layer has a
greater melting point than the antenna, and the surface diffusion
inhibitor layer material is immiscible in the antenna material.
[0010] In one embodiment, a HAMR head is disclosed. The HAMR head
includes a near field transducer. The near field transducer
includes an antenna having a first melting point and a surface
diffusion inhibitor layer disposed on a portion of the antenna. The
surface diffusion inhibitor layer has a second melting point that
is greater than the first melting point. The near field transducer
further includes an aperture disposed over the surface diffusion
inhibitor layer.
[0011] In another embodiment, a HAMR head is disclosed. The HAMR
head includes a near field transducer, where the near field
transducer includes an antenna, where the antenna has a first end
at a media facing surface and a second end adjacent to a waveguide
core. The near field transducer further includes an aperture
disposed over the antenna, a first surface diffusion inhibitor
layer disposed between the antenna and the aperture, a second
surface diffusion inhibitor layer disposed between the second end
of the antenna and the waveguide core, and a third surface
diffusion inhibitor layer disposed on the first end of the antenna
at the media facing surface.
[0012] In another embodiment, a HAMR head is disclosed. The HAMR
head includes a first cladding material, a waveguide core disposed
on the first cladding material, a second cladding material disposed
on the waveguide core, and an antenna surrounded by multiple
surface diffusion inhibitor layers, where the antenna and the
surface diffusion inhibitor layers are embedded in the second
cladding material, and where the antenna has a tapered point at a
media facing surface.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] So that the manner in which the above recited features of
the present invention can be understood in detail, a more
particular description of the invention, briefly summarized above,
may be had by reference to embodiments, some of which are
illustrated in the appended drawings. It is to be noted, however,
that the appended drawings illustrate only typical embodiments of
this invention and are therefore not to be considered limiting of
its scope, for the invention may admit to other equally effective
embodiments in any field involving magnetic heads.
[0014] FIGS. 1A-1B illustrate a disk drive system, according to
embodiments described herein.
[0015] FIG. 2 illustrates a cross-sectional schematic diagram of a
HAMR enabled head, according to one embodiment described
herein.
[0016] FIGS. 3A-3J are ABS views of a magnetic head at different
processing stages according to one embodiment of the invention.
[0017] FIGS. 4A-4D are ABS views of a magnetic head at different
processing stages according to one embodiment of the invention.
[0018] FIGS. 5A-5H are ABS views of a magnetic head at different
processing stages according to one embodiment of the invention.
[0019] FIGS. 6A-6B are cross-sectional schematic diagrams of a HAMR
enabled head, according to embodiments of the invention.
[0020] FIG. 7 is a cross-sectional schematic diagram of a HAMR
enabled head, according to one embodiment of the invention.
[0021] FIG. 8 is a top view of an antenna shown in FIG. 7,
according to one embodiment of the invention.
[0022] To facilitate understanding, identical reference numerals
have been used, where possible, to designate identical elements
that are common to the figures. It is contemplated that elements
disclosed in one embodiment may be beneficially utilized on other
embodiments without specific recitation.
DETAILED DESCRIPTION
[0023] In the following, reference is made to embodiments of the
invention. However, it should be understood that the invention is
not limited to specific described embodiments. Instead, any
combination of the following features and elements, whether related
to different embodiments or not, is contemplated to implement and
practice the invention. Furthermore, although embodiments of the
invention may achieve advantages over other possible solutions
and/or over the prior art, whether or not a particular advantage is
achieved by a given embodiment is not limiting of the invention.
Thus, the following aspects, features, embodiments and advantages
are merely illustrative and are not considered elements or
limitations of the appended claims except where explicitly recited
in a claim(s). Likewise, reference to "the invention" shall not be
construed as a generalization of any inventive subject matter
disclosed herein and shall not be considered to be an element or
limitation of the appended claims except where explicitly recited
in a claim(s).
[0024] Embodiments of the present invention generally relate to a
HAMR head including a near field transducer having an antenna, a
surface diffusion inhibitor layer disposed on a portion of the
antenna and an aperture disposed over the surface diffusion
inhibitor layer. The surface diffusion inhibitor layer has a
greater melting point than the antenna, and the surface diffusion
inhibitor layer material is immiscible in the antenna material.
[0025] FIG. 1A illustrates a disk drive 100 embodying this
invention. As shown, at least one rotatable magnetic disk 112 is
supported on a spindle 114 and rotated by a disk drive motor 118.
The magnetic recording on each disk is in the form of annular
patterns of concentric data tracks (not shown) on the magnetic disk
112.
[0026] At least one slider 113 is positioned near the magnetic disk
112, each slider 113 supporting one or more magnetic head
assemblies 121 that may include a radiation source (e.g., a laser
or electrically resistive heater) for heating the disk surface 122.
As the magnetic disk rotates, the slider 113 moves radially in and
out over the disk surface 122 so that the magnetic head assembly
121 may access different tracks of the magnetic disk 112 where
desired data are written. Each slider 113 is attached to an
actuator arm 119 by way of a suspension 115. The suspension 115
provides a slight spring force which biases the slider 113 towards
the disk surface 122. Each actuator arm 119 is attached to an
actuator means 127. The actuator means 127 as shown in FIG. 1A may
be a voice coil motor (VCM). The VCM comprises a coil movable
within a fixed magnetic field, the direction and speed of the coil
movements being controlled by the motor current signals supplied by
control unit 129.
[0027] During operation of a TAR or HAMR enabled disk drive 100,
the rotation of the magnetic disk 112 generates an air bearing
between the slider 113 and the disk surface 122 which exerts an
upward force or lift on the slider 113. The air bearing thus
counter-balances the slight spring force of suspension 115 and
supports slider 113 slightly above the disk 112 surface by a small,
substantially constant spacing during normal operation. The
radiation source heats up the high-coercivity media so that the
write elements of the magnetic head assemblies 121 may correctly
magnetize the data bits in the media.
[0028] The various components of the disk drive 100 are controlled
in operation by control signals generated by control unit 129, such
as access control signals and internal clock signals. Typically,
the control unit 129 comprises logic control circuits, storage
means and a microprocessor. The control unit 129 generates control
signals to control various system operations such as drive motor
control signals on line 123 and head position and seek control
signals on line 128. The control signals on line 128 provide the
desired current profiles to optimally move and position slider 113
to the desired data track on disk 112. Write and read signals are
communicated to and from write and read heads on the assembly 121
by way of recording channel 125.
[0029] The above description of a typical magnetic disk storage
system and the accompanying illustration of FIG. 1A are for
representation purposes only. It should be apparent that disk
storage systems may contain a large number of disks and actuators,
and each actuator may support a number of sliders.
[0030] FIG. 1B is a cross sectional schematic of a HAMR enabled
write head 101, according to one embodiment described herein. The
head 101 is operatively attached to a laser 155 (i.e., a radiation
source) that is powered by a laser driver 150. The laser 155 may be
placed directly on the head 101 or radiation may be delivered from
a laser 155 located separate from the slider through an optical
fiber or waveguide. Similarly, the laser driver 150 circuitry may
be located on the slider 113 or on a system-on-chip (SOC)
associated with the disk drive 100 such as the control unit 129 as
shown in FIG. 1A. The head 101 includes a spot-size converter 130
for focusing the radiation transmitted by the laser 155 into the
waveguide 135. In another embodiment, the head 101 may include one
or more lens for focusing the beamspot of the laser 155 before the
emitted radiation reaches the spot-size converter 130. The
waveguide 135 is a channel that transmits the radiation through the
height of the head 101 to a NFT 140--e.g., a plasmonic device or
optical transducer --which is located at or near a media facing
surface, such as an air-bearing surface (ABS). The NFT 140 further
focuses the beamspot to avoid heating neighboring tracks of data on
the disk 112--i.e., creates a beamspot much smaller than the
diffraction limit. As shown by arrows 142, this optical energy
emits from the NFT 140 to the surface of the disk 112 below the ABS
of the head 101. The embodiments herein, however, are not limited
to any particular type of radiation source or technique for
transferring the energy emitted from the radiation source to the
ABS.
[0031] FIG. 2 illustrates a cross-sectional schematic diagram of
the HAMR enabled head 101, according to one embodiment of the
invention. As shown, this portion of the head 101 includes the
waveguide 135, which consists of waveguide core 235 and waveguide
cladding 230, but with some of the cladding 230 (and any cladding
on the back-side of the head 101) removed to better illustrate the
details of heat sink 225. The NFT 140 may be directly or thermally
coupled to the heat sink 225 for removing excess heat from the NFT
140. Because FIG. 2 is a cross-section of head 101, there may be
another heat sink located opposite the heat sink 225 depicted. The
return pole 240 is located between the NFT 140 and shield layers or
the read pole which are not shown in this figure.
[0032] In one embodiment, the write pole 205 includes a magnetic
lip 210 portion that may extend underneath the core 235 of the
waveguide 135. The placement of magnetic lip 210 close to the NFT
140 aids in bringing magnetic flux close to the optical field
generated by the NFT onto the magnetic media.
[0033] The core 235 (and the waveguide 135) may terminate at the
NFT 140. The NFT 140 at least includes an antenna 220 and an
aperture 215. The antenna 220 has a base layer and a notch
(described in detail below). In some embodiments, because the
design and/or material of the pole lip 210 may improve the
efficiency of the antenna 220, the pole lip 210 may be considered
as part of the NFT 140. The antenna 220 may be Au, Cu, Ag, Al or
alloys comprising these elements. The aperture 215 is an opening
that may be filled with low refractive index and optically
transparent material such as, for example, SiO.sub.2 or other
dielectric material. The aperture 215 may refer to the material
that is filling the opening. In one embodiment, the aperture 215
may comprise of the same material as the cladding 230. The write
pole 205 and pole lip 210 may comprise of Ni, Co, Fe, Cr, or some
combination or alloy thereof. The NFT 140 uses the antenna 220 and
aperture 215 to further focus the optical energy delivered by the
waveguide 135 onto the magnetic media.
[0034] The heat generated in the NFT 140 may be cause the
temperature of the NFT 140 to rise beyond 400 degrees Celsius. The
antenna 220 typically comprised of materials that have melting
temperatures in the range of 950 to 1070 degrees Celsius. However,
once the temperature reaches 150 degrees Celsius, the surface
diffusion of atoms of the antenna 220 increases, leading to
morphological changes in the antenna 220 such as rounding off of
the edges of the antenna 220 or the notch of the antenna 220 to
disappear. An antenna with damaged or absent notch will cause
drastic reduction in optical efficiency of the NFT since the notch
is a focal point for the NFT. To avoid this issue, a surface
diffusion inhibitor layer 250 is disposed between the antenna 220
and the aperture 215. The surface diffusion inhibitor layer 250 is
made of a material that has a higher melting temperature than the
antenna 220, such as Rh, Ru, W, Mo, Ir, Co, Pt, B or Ni and is
immiscible with the antenna 220. In one embodiment, the surface
diffusion inhibitor layer 250 is made of an Au alloy of Rh, Ru, W,
Mo, Ir, Co, Pt, B or Ni. The surface diffusion inhibitor layer 250
has a thickness of less than 10 nm and has a melting temperature
that is higher than 1100 degrees Celsius. Having the surface
diffusion inhibitor layer 250 will ensure morphological stability
of the NFT 140 at operational temperatures, such as up to 400
degrees Celsius.
[0035] FIGS. 3A-3J are ABS views of a magnetic head 300 at
different processing stages according to one embodiment of the
invention. FIG. 3A shows a layer 301 that is made of Au. The
thickness of layer 301 is between about 100 nm to about 200
nanometers (nm) and is deposited on a substrate that has a
partially formed HAMR head disposed thereon. As shown in FIG. 3B, a
mask 304 is disposed on a portion of the layer 301, and portions of
the layer 301 not covered by the mask 304 are removed, forming an
antenna 302. The removal process may be ion milling or reactive ion
etching (RIE). The antenna 302 may be the antenna 220 in FIG. 2.
The antenna 302 has a base layer 303 and a notch 306, which serves
as a focal point for the NFT 140. The notch 306 has a thickness
"T1" of about 50 nm and the base layer 303 has a thickness "T2" of
about 150 nm. The width "W1" of the notch 306 is between 10 nm and
50 nm.
[0036] Next, as shown in FIG. 3C, the mask 304 is removed and a
surface diffusion inhibitor layer 308 is deposited on the antenna
302. The surface diffusion inhibitor layer 308 may be the surface
diffusion inhibitor layer 250 in FIG. 2. An adhesion layer 309 may
be deposited on the surface diffusion inhibitor layer 308. The
adhesion layer 309 may have a thickness of less than about 5 nm and
may be made of a material such as Ti, Ta, Cr, Zr, Hf, Si or alloys
thereof, such as NiTi, NiTa, NiCr, NiZr, or NiHf. Both layers 308,
309 may be deposited by physical vapor deposition (PVD), ion beam
deposition (IBD), atomic layer deposition (ALD), or plasma enhanced
chemical vapor deposition (PECVD). A dielectric layer 311 is
deposited over the surface diffusion inhibitor layer 308, as shown
in FIG. 3D. The dielectric layer 311 may be deposited on the
surface diffusion inhibitor layer 308. The dielectric layer 311 may
be SiO.sub.2. In one embodiment, the adhesion layer 309 is
deposited in-situ prior to deposition of dielectric layer 311.
[0037] A mask 312 is deposited on a portion of the dielectric layer
311, and portions of the dielectric layer 311 and the surface
diffusion inhibitor layer 308 not covered by the mask 312 are
removed. The removal process may be ion milling and/or reactive ion
etching (RIE). As a result, an aperture 310 is formed, as shown in
FIG. 3E. The aperture 310 may be the aperture 215 in FIG. 2. The
aperture 310 may have a thickness "T3" of about 50 nm and a width
"W2" of about 300 nm. The notch 306 may be centrally located within
the aperture 310.
[0038] Next, as shown in FIG. 3F, the mask 312 is removed, leaving
the antenna 302, the aperture 310 and the diffusion inhibitor layer
308, which forms the NFT 140. The antenna 302 and the aperture 310
may have various shapes. In one embodiment, the antenna 302 may
have a shape that looks like the letter "E" rotated 90 degrees in
counter clockwise direction. The aperture 310 is disposed over the
antenna 302 and may have a shape that looks like the letter "C"
rotated 90 degrees in the clockwise direction.
[0039] Next, as shown in FIG. 3G, a conductive layer 318 is
deposited over the antenna 302 and the aperture 310. The conductive
layer 318 may also cover the exposed vertical sides 314 of the
aperture 310. The conductive layer 318 may have good thermal
conductivity and may be made of a noble metal, such as Au, Rh, Ru,
Ir, Pd, Pt, Re, or Os. The conductive layer 318 may also be an
alloy having over 95% of one of the noble metals, such as Au, Rh,
Ru, Ir, Pd, Pt, Re, or Os as described in U.S. patent application
Ser. No. 14/133,003 filed Dec. 18, 2013, which is incorporated
herein by reference. The thickness of the conductive layer 318 may
be less than or equal to 10 nm. In one embodiment, the thickness of
the conductive layer 318 is about 5 nm. The conductive layer 318
may be formed using any suitable deposition process, such as
sputtering.
[0040] The conductive layer 318 may not have good adhesion to the
aperture 310, thus, a seed layer 316 may be first deposited over
the antenna 302 and the aperture 310, and the conductive layer 318
is then deposited on the seed layer 316. The seed layer 316 may be
any suitable material, such as Ta, NiTa, Cr, Ti, Si or alloys
thereof, such as NiTi, NiTa, NiCr, NiZr, or NiHf. In one
embodiment, the seed layer 316 is about 1 nm thick.
[0041] Next, as shown in FIG. 3H, a resist 320 is deposited over
the conductive layer 318 and a second conductive layer 322 is
deposited over the conductive layer 318 and the resist 320. The
resist 320 may be deposited and patterned using any suitable
processes. The second conductive layer 322 may also cover vertical
sides 323 of the resist 320. The second conductive layer 322 may
also have good thermal conductivity and may be made of a noble
metal, such as Au, Rh, Ru, Ir, Pd, Pt, Re, or Os. The second
conductive layer 322 may also be an alloy having over 95% of one of
the noble metals, such as Au, Rh, Ru, Ir, Pd, Pt, Re, or Os. Any
suitable deposition process may be used to deposit the second
conductive layer 322, and one example of such process is
sputtering. The second conductive layer 322 may have a thickness of
less than or equal to 100 nm.
[0042] In one embodiment, the second conductive layer 322 comprises
the same material as the conductive layer 318. In another
embodiment, the second conductive layer 322 comprises a different
material as the conductive layer 318. A second seed layer (not
shown) may be optionally deposited over the conductive layer 318
and the resist 320, and the second conductive layer 322 is
deposited on the second seed layer. Next, a heat sink 324 is
deposited over the second conductive layer 322. The heat sink 324
is made of a material having good thermal conductivity, such as Cr,
Au, Ir, Pt, Pd, Ru, or Rh, and is deposited using any suitable
deposition process, such as physical vapor deposition (PVD).
[0043] One or more removal processes are performed to form an
opening 330, as shown in FIG. 3I. The removal process will include
a combination of subtractive processes such as resist wet strip,
ion milling and reactive ion etch. The opening 330 has vertical
sides 332 and a bottom 334. The vertical sides 332 are the second
conductive layer 322 and the bottom 334 is the conductive layer
318. Because both conductive layers 318, 322 may be a noble metal
or an alloy of a noble metal, no oxidation may occur at the
vertical sides 332 and the bottom 334 of the opening 330.
Therefore, no oxide films may be formed on the vertical sides 332
and the bottom 334 of the opening 330 as the magnetic head 300 at
the current processing stage is exposed to oxygen.
[0044] A magnetic material is deposited in the opening 330 and over
the heat sink 324, as shown in FIG. 3J. The portion of the magnetic
material that is in the opening 330 is the pole lip 340 and the
portion of the magnetic material that is over the heat sink 324 and
the pole lip 340 is the write pole 350. The pole lip 340 and the
write pole 350 may be the pole lip 210 and the write pole 205 in
FIG. 2. The resulting magnetic head 300 as shown in FIG. 3J has the
surface diffusion inhibitor layer 308 disposed on the antenna 302,
and the surface diffusion inhibitor layer 308 inhibits the atoms of
the antenna 302 from diffusing, which ensures morphological
stability of the NFT 140 at operational temperatures.
[0045] FIGS. 4A-4D are ABS views of a magnetic head 400 at
different processing stages according to one embodiment of the
invention. FIG. 4A shows the antenna 302, the surface diffusion
inhibitor layer 308, the adhesion layer 309, the aperture 310, and
a resist 402 coated and lithographically patterned over the
aperture 310. Again the resist 402 may be deposited and patterned
using any suitable process. Next, as shown in FIG. 4B, a conductive
layer 404 is deposited over the antenna 302, a portion of the
aperture 310 that is not covered by the resist 402, and the resist
402. Vertical sides 413 of the resist 402 and vertical sides 405 of
the aperture 310 are also covered by the conductive layer 404.
[0046] The conductive layer 404 may be deposited using any
deposition process, such as PVD or ALD and may have a thickness of
less than or equal to 100 nm. The conductive layer 404 may be a
noble metal, such as Au, Rh, Ru, Ir, Pd, Pt, Re, or Os. The
conductive layer 404 may also be an alloy having over 95% of one of
the noble metals, such as Au, Rh, Ru, Ir, Pd, Pt, Re, or Os.
[0047] Prior to depositing the conductive layer 404, an optional
seed layer (not shown) may be deposited over the antenna 302, a
portion of the aperture 310 that is not covered by the resist 402,
and the resist 402. The conductive layer 404 is then deposited over
the seed layer. A heat sink 414 is deposited over the conductive
layer 404. The heat sink 414 is made of a material having good
thermal conductivity, such as Cr, Au, Ir, Pt, Pd, Ru, or Rh, and is
deposited using any suitable deposition process, such as physical
vapor deposition (PVD).
[0048] Next, one or more removal processes are performed to form an
opening 420, as shown in FIG. 4C. The removal process will include
a combination of subtractive processes such as resist wet strip,
ion milling and reactive ion etch. A second conductive layer 422 is
then deposited into the opening 420, covering the vertical sides
and the bottom of the opening 420.
[0049] The second conductive layer 422 may also have good thermal
conductivity and may be made of a noble metal, such as Au, Rh, Ru,
Ir, Pd, Pt, Re, or Os. The second conductive layer 422 may also be
an alloy having over 95% of one of the noble metals, such as Au,
Rh, Ru, Ir, Pd, Pt, Re, or Os. Any suitable deposition process may
be used to deposit the second conductive layer 422. One example of
such process is ALD. The second conductive layer 422 may have a
thickness of less than or equal to 10 nm. In one embodiment, the
thickness of the second conductive layer is about 5 nm.
[0050] A seed layer 423 may be first deposited into the opening
420, and then the second conductive layer 422 is deposited on the
seed layer 423. The seed layer 423 may be any suitable material,
such as Ta, NiTa, Cr, Ti or Si. In one embodiment, the seed layer
423 is about 1 nm thick. The conductive layer 404 and the second
conductive layer 422 may be the same material or may be different
materials. The magnetic head 400 at the current processing stage
may not have oxide films formed in the opening 420 since the sides
and the bottom of the opening 420 are covered by the second
conductive layer 422, which may be a noble metal that would not
react with oxygen.
[0051] A magnetic material is deposited in the opening 420 and over
the heat sink 414. The portion of the magnetic material that is in
the opening 420 is the pole lip 430 and the portion of the magnetic
material that is over the heat sink 420 and the pole lip 430 is the
write pole 440. The pole lip 430 and the write pole 440 may be the
pole lip 210 and the write pole 205 in FIG. 2.
[0052] FIGS. 5A-5H are ABS views of a magnetic head 500 at
different processing stages according to one embodiment of the
invention. FIG. 5A shows an "E" shaped antenna 502 having openings
503 formed therein. The antenna 502 may be the antenna 220 in FIG.
2. A Surface diffusion inhibitor layer 501 is deposited on the
antenna 502, as shown in FIG. 5B. The surface diffusion inhibitor
layer 501 may be the surface diffusion inhibitor layer 308 in FIGS.
3 and 4. An adhesion layer 550 is deposited on the surface
diffusion inhibitor layer 501 and the adhesion layer 550 may be the
adhesion layer 309 in FIGS. 3 and 4. A "C" shaped aperture 504 is
deposited over the surface diffusion inhibitor layer 501 and over
the antenna 502, and planarized as shown in FIG. 5B. Next, as shown
in FIG. 5C, a seed layer 505 is deposited over the aperture 504.
The seed layer 505 may be any suitable material, such as Ta, NiTa,
Cr, Ti or Si and has a thickness of about 1 nm.
[0053] A conductive layer 506 is deposited on the seed layer 505.
The conductive layer 506 may be deposited using any deposition
process, such as ALD and may have a thickness of less than or equal
to 10 nm. In one embodiment, the thickness of the conductive layer
506 is about 2 nm. The conductive layer 506 may be a noble metal,
such as Au, Rh, Ru, Ir, Pd, Pt, Re, or Os. The conductive layer 506
may also be an alloy having over 95% of one of the noble metals,
such as Au, Rh, Ru, Ir, Pd, Pt, Re, or Os.
[0054] A mask 508 is deposited over the conductive layer 506 and
covers a portion of the conductive layer 506. One or more removal
processes are performed to remove portions of the conductive layer
506, the aperture 504, the adhesion layer 550 and the surface
diffusion inhibitor layer 501 not covered by the mask 508. The
removal processes may be multiple ion milling processes, multiple
reactive ion etching (RIE) processes, or a combination of ion
milling and RIE processes. The mask 508 is also removed as the
result of the one or more removal processes. The resulting
structure, as shown in FIG. 5D, has the aperture 504 exposing
portions of vertical sides above the antenna 502, and the seed
layer 505 and the conductive layer 506 are disposed over the
aperture 504. The aperture 504 may be the aperture 215 in FIG.
2.
[0055] Next, as shown in FIG. 5E, a resist 510 is deposited over
the conductive layer 506 and covers a portion of the conductive
layer 506. A second conductive layer 512 is deposited over the
antenna 502, the conductive layer 506 not covered by the resist
510, and the resist 510. The vertical sides of the resist 510,
conductive layer 506, seed layer 505, and aperture 504 are also
covered by the second conductive layer 512. The second conductive
layer 512 may be deposited using any deposition process, such as
ALD and may have a thickness of less than or equal to 100 nm. The
second conductive layer 512 may be a noble metal, such as Au, Rh,
Ru, Ir, Pd, Pt, Re, or Os. The second conductive layer 512 may also
be an alloy having over 95% of one of the noble metals, such as Au,
Rh, Ru, Ir, Pd, Pt, Re, or Os.
[0056] A heat sink 514 is deposited over the second conductive
layer 512, as shown in FIG. 5F. The heat sink 514 is made of a
material having good thermal conductivity, such as Cr, Ir, Pt, Pd,
Ru, or Rh, and is deposited using any suitable deposition process,
such as physical vapor deposition (PVD).
[0057] Next, one or more removal processes are performed to form an
opening 520, as shown in FIG. 5G. The removal process will include
a combination of subtractive processes such as resist wet strip,
ion milling and reactive ion etch. Portions of the heat sink 514
and the second conductive layer 512 covering the top surface of the
resist 510 are first removed to expose the top surface of the
resist 510 by any suitable removal process, such as ion milling.
Then the resist 510 is removed by any suitable removal process,
such as wet stripping, to form the opening 520.
[0058] The opening 520 has vertical sides 522 and a bottom 524. The
vertical sides 522 are the second conductive layer 512 and the
bottom 524 is the conductive layer 506. Because both conductive
layers 506, 512 may be a noble metal or an alloy of a noble metal,
no oxidation may occur at the vertical sides 522 and the bottom 524
of the opening 520. Therefore, no oxide films may be formed on the
vertical sides 522 and the bottom 524 of the opening 520 as the
magnetic head 500 at the current processing stage is exposed to
oxygen.
[0059] A magnetic material is deposited in the opening 520 and over
the heat sink 514, as shown in FIG. 5H. The portion of the magnetic
material that is in the opening 520 is the pole lip 530 and the
portion of the magnetic material that is over the heat sink 514 and
the pole lip 530 is the write pole 540. The pole lip 530 and the
write pole 540 may be the pole lip 210 and the write pole 205 in
FIG. 2.
[0060] FIGS. 2, 3, 4 and 5 illustrate a surface diffusion inhibitor
layer disposed between the antenna and the aperture. However, the
surface diffusion inhibitor layer may not be limited to the
location between the antenna and the aperture to help prevent
surface diffusion of atoms of the antenna. FIGS. 6A and 6B are
cross-sectional views of the HAMR enabled head 101 that illustrates
multiple locations for the surface diffusion inhibitor layer.
[0061] As shown in FIG. 6A, the surface diffusion inhibitor layer
601 may be disposed between the antenna 605 and the aperture 604. A
conductive layer 606 is disposed between the aperture 604 and the
magnetic lip 608. A dielectric underlayer material 610 is disposed
over the magnetic lip 608, the conductive layer 606, the aperture
604, the surface diffusion inhibitor layer 601, and the antenna
605. A waveguide core 611 is disposed over the dielectric
underlayer material 610, a top cladding 640 is disposed adjacent
the waveguide core 611 and a bottom cladding 630 is disposed
adjacent the dielectric underlayer material 610 and the antenna
605. A second surface diffusion inhibitor layer 612 may be disposed
between the antenna 605 and the dielectric material 610. A third
surface diffusion inhibitor layer 614 may be disposed between the
antenna 605 and the ABS.
[0062] FIG. 6B shows surface diffusion inhibitor layers 601 and
612, and instead of the surface diffusion inhibitor layer 614, a
surface diffusion inhibitor layer 616 may be disposed at the ABS,
covering not only the antenna 605, but also the aperture 604, the
conductive layer 606, the magnetic lip 608, the main pole 618 and
the bottom cladding 630. The surface diffusion inhibitor layers
601, 612, 614 and 616 may be the surface diffusion inhibitor layer
308, which is utilized to prevent surface diffusion of atoms of the
antenna 605.
[0063] The antenna may have a shape other than that discussed
above. For example, the antenna could be a nano-beak design having
a shape similar to a bird's beak, narrowing to a point at the ABS.
FIGS. 7 and 8 illustrate such an embodiment where the antenna is a
nano-beak antenna 712. A cladding material 704 is disposed on a
substrate 702, which may have components of a HAMR head disposed
thereon. A waveguide core 706 is disposed on the cladding material
704 and a cladding material 708 is disposed on the waveguide core
706. The cladding materials 704, 708 and the waveguide core 706
form the waveguide 710. The nano-beak antenna 712 is surrounded by
surface diffusion inhibitor layers 714, 716 and 718, and is
embedded in the cladding material 708. The surface diffusion
inhibitor layers 714, 716 and 718 may be the surface diffusion
inhibitor layer 308. The magnetic lip 720 is disposed over the
antenna 712 and adjacent a non-magnetic spacer layer 22. Disposed
on the magnetic lip 720 and the non-magnetic spacer layer 722 may
be an upper return pole 724. FIG. 8 is a top view of the nano-beak
antenna 712, where it can be seen that the antenna 712 also narrows
to a point at the ABS as viewed from the top. Light traveling
through the waveguide 710 is drawn to the antenna 712 forming an
extremely focused hot spot at the pointed tip of the antenna 712.
The surface diffusion inhibitor layers 714, 716 and 718 are
utilized to prevent surface diffusion of atoms of the nano-beak
antenna 712.
[0064] In summary, an improved magnetic head is disclosed. The
magnetic head has a surface diffusion inhibitor layer disposed
between the antenna and the aperture. The surface diffusion
inhibitor layer is made of a material that has a higher melting
point than the antenna and is immiscible with the antenna. Thus,
during operating, surface diffusion of atoms of the antenna caused
by high temperature is prevented by the surface diffusion inhibitor
layer.
[0065] While the foregoing is directed to embodiments of the
present invention, other and further embodiments of the invention
may be devised without departing from the basic scope thereof, and
the scope thereof is determined by the claims that follow.
* * * * *