U.S. patent application number 14/053592 was filed with the patent office on 2015-04-16 for phase change inks comprising novel crystalline compounds.
This patent application is currently assigned to XEROX CORPORATION. The applicant listed for this patent is XEROX CORPORATION. Invention is credited to Naveen Chopra, ADELA GOREDEMA, Gabriel Iftime, Barkev Keoshkerian, Kentaro Morimitsu, Guerino G. Sacripante, Daryl W. Vanbesien.
Application Number | 20150101507 14/053592 |
Document ID | / |
Family ID | 52808545 |
Filed Date | 2015-04-16 |
United States Patent
Application |
20150101507 |
Kind Code |
A1 |
GOREDEMA; ADELA ; et
al. |
April 16, 2015 |
PHASE CHANGE INKS COMPRISING NOVEL CRYSTALLINE COMPOUNDS
Abstract
A phase change ink composition suitable for ink jet printing,
including robust printing on coated paper substrates. In
embodiments, the phase change ink composition comprises both a
crystalline compound and an amorphous compound which are derived
from bio-renewable materials. In particular, the present
embodiments provide novel crystalline compounds with at least two
aromatic moieties for use in the phase change inks.
Inventors: |
GOREDEMA; ADELA;
(Mississauga, CA) ; Sacripante; Guerino G.;
(Oakville, CA) ; Keoshkerian; Barkev; (Thornhill,
CA) ; Vanbesien; Daryl W.; (Burlington, CA) ;
Morimitsu; Kentaro; (Mississauga, CA) ; Chopra;
Naveen; (Oakville, CA) ; Iftime; Gabriel;
(Mississauga, CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
XEROX CORPORATION |
Norwalk |
CT |
US |
|
|
Assignee: |
XEROX CORPORATION
Norwalk
CT
|
Family ID: |
52808545 |
Appl. No.: |
14/053592 |
Filed: |
October 14, 2013 |
Current U.S.
Class: |
106/31.44 ;
106/31.78 |
Current CPC
Class: |
C08K 5/3417 20130101;
C08K 5/20 20130101; C08K 5/12 20130101; C08K 5/07 20130101; C09D
11/38 20130101; C09D 11/34 20130101 |
Class at
Publication: |
106/31.44 ;
106/31.78 |
International
Class: |
C09D 11/037 20060101
C09D011/037; C08K 5/20 20060101 C08K005/20; C08K 5/07 20060101
C08K005/07; C08K 5/12 20060101 C08K005/12; C09D 11/03 20060101
C09D011/03; C08K 5/3417 20060101 C08K005/3417 |
Claims
1. A phase change ink comprising: an amorphous component; a
crystalline component being a di-ester compound having the
following structure: ##STR00026## wherein R is a saturated or
ethylenically unsaturated aliphatic group; and an optional
colorant.
2. The phase change ink of claim 1, wherein R is an alkyl group
with at least 6 carbon atoms and no more than 60 carbon atoms.
3. The phase change ink of claim 1, wherein the crystalline
component has at least 60 percent by weight of bio-renewable
content.
4. The phase change ink of claim 1, wherein the crystalline
component has a viscosity of less than 10 cps at a temperature of
about 140.degree. C.
5. The phase change ink of claim 1, wherein the crystalline
component has a viscosity of from about 1 to about 10 cps in a
jetting range of from about 100 to about 140.degree. C.
6. The phase change ink of claim 1, wherein the crystalline
component has T.sub.melt of less than 150.degree. C.
7. The phase change ink of claim 1, wherein the crystalline
component has T.sub.crys of greater than 65.degree. C.
8. The phase change ink of claim 1, wherein the crystalline
component has a viscosity of greater than about 10.sup.6 cps at
room temperature.
9. The phase change ink of claim 1, wherein the crystalline
component comprises a dialkyl naphthalene dicarboxylate
compound.
10. The phase change ink of claim 1, wherein the ink is capable of
crystallizing at a total crystallization time of less than 15
seconds as measured by the standardized TROM procedure.
11. The phase change ink of claim 1 having at least 50% percent by
weight of bio-renewable content.
12. The phase change ink of claim 1, wherein the amorphous
component is selected from the group consisting of ##STR00027## and
mixtures thereof.
13. The phase change ink of claim 1, wherein the crystalline
component is present in an amount of from about 60 percent to about
95 percent by weight of the total weight of the phase change
ink.
14. The phase change ink of claim 1, wherein the amorphous
component is present in an amount of from about 5 percent to about
40 percent by weight of the total weight of the phase change
ink.
15. The phase change ink of claim 1 having a ratio of crystalline
to amorphous ratio of from about 60:40 to about 95:5.
16. The phase change ink of claim 1, wherein the optional colorant
selected from the group consisting of a pigment, dye or mixtures
thereof.
17. The phase change ink of claim 1 further comprising an additive
selected from the group consisting of antioxidant, defoamer, slip
and leveling agents, clarifier, viscosity modifier, adhesive,
plasticizer and mixtures thereof.
18. A phase change ink comprising: an amorphous component; a
crystalline component being a di-ester compound having the
following structure: ##STR00028## wherein R is a saturated or
ethylenically unsaturated aliphatic group; and an optional
colorant, wherein the phase change ink of claim 1 having a
viscosity of from about 1 to about 22 cps in a jetting range of
from about 100 to about 140.degree. C.
19. The phase change ink of claim 18 having a viscosity of greater
than about 10.sup.6 cps at room temperature.
20. A phase change ink comprising: an amorphous component
comprising an ester of tartaric acid of Formula I or an ester of
Abitol E of Formula II shown below: ##STR00029## wherein each
R.sub.1 and R.sub.2 can be the same or different, and wherein
R.sub.1 and R.sub.2 each independently of the other is an alkyl
group, wherein the alkyl can be straight, branched or cyclic,
saturated or unsaturated, substituted or unsubstituted, having from
about 1 to about 40 carbon atoms and R.sub.3 is an alkylene group,
including substituted and unsubstituted alkylene group, an amide of
formula III shown below: ##STR00030## wherein R is selected from
the group consisting of an alkyl group, an aryl group, an alkylaryl
group, an arylalkyl group, and combinations thereof or an aromatic
rosin ester selected from the group shown in formula IV below:
##STR00031## a crystalline component being a di-ester compound
having the following structure: ##STR00032## wherein R is a
saturated or ethylenically unsaturated aliphatic group; and an
optional colorant.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] Reference is made to commonly owned and co-pending, U.S.
patent application Ser. No. ______ (not yet assigned) entitled
"Novel Crystalline Compounds for Phase Change Inks" to Adela
Goredema et al., electronically filed on the same day herewith
(Attorney Docket No. 20120802-417885); U.S. patent application Ser.
No. ______ (not yet assigned), filed electronically on the same day
as the present application, entitled "Phase Change Ink Containing
Amorphous Amides," having the named inventors Naveen Chopra, Adela
Goredema, Kentaro Morimitsu, Barkev Keoshkerian, Jennifer L.
Belelie, and Gabriel Mime" (Attorney Docket No. 20120800-US-NP),
the entire disclosure of which is incorporated herein by reference
in its entirety; U.S. patent application Ser. No. ______ (not yet
assigned), filed electronically on the same day as the present
application, entitled "Amorphous Amides," having the named
inventors Naveen Chopra, Adela Goredema, Kentaro Morimitsu, Barkev
Keoshkerian, and Jennifer L. Belelie (Attorney Docket No.
20120801-US-NP), the entire disclosure of which is incorporated
herein by reference in its entirety; and U.S. patent application
Ser. No. ______ (not yet assigned), filed electronically on the
same day as the present application, entitled "Bio-renewable Phase
Change Inks," having the named inventors Adela Goredema, Jennifer
Belelie, James Mayo, Daryl Vanbesien, Barkev Keoshkerian, Nathan
Bamsey and Jenny Eliyahu (Attorney Docket No. 20120581-412786), the
entire disclosure of which is incorporated herein by reference in
its entirety.
BACKGROUND
[0002] The present embodiments relate to phase change ink
compositions characterized by being solid at room temperature and
molten at an elevated temperature at which the molten ink is
applied to a substrate. These phase change ink compositions can be
used for ink jet printing. The present embodiments are directed to
a novel phase change ink composition comprising an amorphous
compound, a crystalline compound, and optionally a colorant, and
methods of making the same. The specific formulations described
herein, including a combination of an amorphous compound and
crystalline compound which have low compatibility and are derived
from bio-renewable materials and provide fast crystallizing and
robust ink compositions that form high quality images when printed
on coated paper substrates. In particular, the present embodiments
provide novel crystalline compounds with at least two aromatic
moieties for use in the phase change inks.
[0003] Ink jet printing processes may employ inks that are solid at
room temperature and liquid at elevated temperatures. Such inks may
be referred to as solid inks, hot melt inks, phase change inks and
the like. For example, U.S. Pat. No. 4,490,731, the disclosure of
which is totally incorporated herein by reference, discloses an
apparatus for dispensing phase change ink for printing on a
recording medium such as paper. In piezo ink jet printing processes
employing hot melt inks, the phase change ink is melted by the
heater in the printing apparatus and utilized (jetted) as a liquid
in a manner similar to that of conventional piezo ink jet printing.
Upon contact with the printing recording medium, the molten ink
solidifies rapidly, enabling the colorant to substantially remain
on the surface of the recording medium instead of being carried
into the recording medium (for example, paper) by capillary action,
thereby enabling higher print density than is generally obtained
with liquid inks. Advantages of a phase change ink in ink jet
printing are thus elimination of potential spillage of the ink
during handling, a wide range of print density and quality, minimal
paper cockle or distortion, and enablement of indefinite periods of
nonprinting without the danger of nozzle clogging, even without
capping the nozzles.
[0004] In general, phase change inks (sometimes referred to as "hot
melt inks" or "solid inks") are in the solid phase at ambient
temperature, but exist in the liquid phase at the elevated
operating temperature of an ink jet printing device. At the jetting
temperature, droplets of liquid ink are ejected from the printing
device and, when the ink droplets contact the surface of the
recording medium, either directly or via an intermediate heated
transfer belt or drum, they quickly solidify to form a
predetermined pattern of solidified ink drops.
[0005] Phase change inks for color printing typically comprise a
phase change ink carrier composition which is combined with a phase
change ink compatible colorant. In a specific embodiment, a series
of colored phase change inks can be formed by combining ink carrier
compositions with compatible subtractive primary colorants. The
subtractive primary colored phase change inks can comprise four
component dyes or pigments, namely, cyan, magenta, yellow and
black, although the inks are not limited to these four colors.
These subtractive primary colored inks can be formed by using a
single dye or pigment or a mixture of dyes or pigments.
[0006] Phase change inks are desirable for ink jet printers because
they remain in a solid phase at room temperature during shipping,
long term storage, and the like. In addition, the problems
associated with nozzle clogging as a result of ink evaporation with
liquid ink jet inks are largely eliminated, thereby improving the
reliability of the ink jet printing. Further, in phase change ink
jet printers wherein the ink droplets are applied directly onto the
final recording medium (for example, paper, transparency material,
and the like), the droplets solidify immediately upon contact with
the recording medium, so that migration of ink along the printing
medium is prevented and dot quality is improved.
[0007] While the above conventional phase change ink technology is
generally successful in producing vivid images and providing
economy of jet use and substrate latitude on porous papers, such
technology has not been satisfactory for coated substrates. For
example, commercially available phase change inks also suffer from
poor adhesion to coated substrates, which leads to poor scratch
resistance and image robustness. Such inks also suffer from some of
the hard and brittle starting materials from which they are made.
This leads to the ink themselves becoming hard and brittle which
exacerbates the poor substrate adhesion by causing poor "paper
fold" performance and document offset. Thus, while known
compositions and processes are suitable for their intended
purposes, a need remains for additional means for forming images or
printing on coated paper substrates. As such, there is a need to
find alternative compositions, preferably those derived from
bio-renewable sources, for phase change ink compositions and future
printing technologies to provide customers with excellent image
quality on all substrates. There is further a need to provide such
phase change ink compositions which are suitable for fast printing
environments like production printing.
[0008] Each of the foregoing U.S. patents and patent publications
are incorporated by reference herein. Further, the appropriate
components and process aspects of the each of the foregoing U.S.
patents and patent publications may be selected for the present
disclosure in embodiments thereof.
SUMMARY
[0009] According to embodiments illustrated herein, there is
provided novel phase change ink compositions comprising an
amorphous and crystalline material with limited compatibility, and
a dye or an organic pigment, which are suitable for ink jet high
speed printing, such as printing on coated paper substrates.
Furthermore, the present embodiments provide novel crystalline
materials that provide the resulting phase change inks with
improved scratch resistance.
[0010] In particular, the present embodiments provide a phase
change ink comprising: an amorphous component; a crystalline
component being a di-ester compound having the following
structure:
##STR00001##
R is a saturated or ethylenically unsaturated aliphatic group; and
an optional colorant.
[0011] In further embodiments, there is provided a phase change ink
comprising: an amorphous component; a crystalline component being a
di-ester compound having the following structure:
##STR00002##
R is a saturated or ethylenically unsaturated aliphatic group; and
an optional colorant, wherein the phase change ink of claim 1
having a viscosity of from about 1 to about 22 cps in a jetting
range of from about 100 to about 140.degree. C.
[0012] In yet other embodiments, there is provided a phase change
ink comprising: an amorphous component comprising an ester of
tartaric acid of Formula I or an ester of Abitol E of Formula II
shown below:
##STR00003##
wherein each R.sub.1 and R.sub.2 can be the same or different, and
wherein R.sub.1 and R.sub.2 each independently of the other is an
alkyl group, wherein the alkyl can be straight, branched or cyclic,
saturated or unsaturated, substituted or unsubstituted, having from
about 1 to about 40 carbon atoms and R.sub.3 is an alkylene group,
including substituted and unsubstituted alkylene group, an amide of
formula III shown below:
##STR00004##
wherein R is selected from the group consisting of an alkyl group,
an aryl group, an alkylaryl group, an arylalkyl group, and
combinations thereof or an aromatic rosin ester selected from the
group shown in formula IV below:
##STR00005##
a crystalline component being a di-ester compound having the
following structure:
##STR00006##
wherein R is a saturated or ethylenically unsaturated aliphatic
group; and an optional colorant
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] For a better understanding of the present embodiments,
reference may be had to the accompanying FIGURE.
[0014] The FIGURE is a graph illustrating rheology data of
crystalline Compound 1 made according to the present
embodiments.
DETAILED DESCRIPTION
[0015] In the following description, it is understood that other
embodiments may be utilized and structural and operational changes
may be made without departure from the scope of the present
embodiments disclosed herein.
[0016] Phase change ink technology broadens printing capability and
customer base across many markets, and the diversity of printing
applications will be facilitated by effective integration of
printhead technology, print process and ink materials. The phase
change ink compositions are characterized by being solid at room
temperature (RT) (e.g., 20-27.degree. C.) and molten at an elevated
temperature at which the molten ink is applied to a substrate. As
discussed above, while current ink options are successful for
porous paper substrates, these options are not always satisfactory
for coated paper substrates.
[0017] Conventional phase change ink technology has been successful
in producing vivid images and providing economy of jet use and
substrate latitude on porous papers. However, such technology has
not been satisfactory for coated substrates. Thus, while known
compositions and processes are suitable for their intended
purposes, a need remains for additional means for forming images or
printing on coated paper substrates. As such, there is a need to
find alternative compositions for phase change ink compositions and
future printing technologies to provide customers with excellent
image quality on all substrates, including selecting and
identifying different classes of materials that are suitable for
use as desirable ink components. There is a further need for
printing these inks at high speeds as required by digital presses
in production environment.
[0018] For example, energy and environmental policies, increasing
and volatile oil prices, and public/political awareness of the
rapid depletion of global fossil reserves have created a need to
find sustainable monomers derived from biomaterials. The present
embodiments use bio-renewable materials for use in the ink
compositions. The term "bio-renewable" is used to mean a material
comprised of one or more monomers that are derived from plant
material. By using such bio-derived feedstock, which are renewable,
manufacturers may reduce their carbon footprint and move to a
zero-carbon or even a carbon-neutral footprint. Bio-based materials
are also very attractive in terms of specific energy and emission
savings. Utilizing bio-renewable feedstock can decrease the amount
of waste targeted for landfills, and reduce the economic risks and
uncertainty associated with reliance on petroleum imported from
unstable regions.
[0019] It was previously discovered that using a mixture of
crystalline and amorphous small molecule compounds in phase change
ink formulations provides robust inks, and in particular, phase
change inks which demonstrate robust images on coated paper, as
disclosed in U.S. patent application Ser. No. 13/095,636 to
Jennifer L. Belelie et. al. filed Apr. 27, 2011, and hereby
incorporated by reference in its entirety. Print samples made with
such phase change inks demonstrate better robustness as compared to
currently available phase change inks.
[0020] The present inventors have also found that fast
crystallization of a composition made of a crystalline and an
amorphous component is not an inherent property of the composition.
The rate of crystallization of the crystalline/amorphous mixture is
a function of not only the crystalline and amorphous components
independently, but even more importantly, is influenced by the
selection of the pair of crystalline and amorphous materials. For
example, a given crystalline component may provide a fast
crystallizing composition when mixed with one amorphous component
but the same crystalline component can result in a slow
crystallizing composition when mixed with a different amorphous
component. The relationship between the chemical structures of the
pair of crystalline and amorphous components controls the rate of
crystallization of a given mixture. However, then the selection of
the particular pair of crystalline and amorphous components to
provide fast crystallizing inks is complicated.
[0021] The present embodiments provide a formulation for ink
compositions that are based on crystalline and amorphous components
which not only provide robust inks, and in particular, phase change
inks which demonstrate robust images on coated paper, but further
is fast crystallizing and derived from bio-renewable materials.
[0022] The present embodiments provide a new type of ink jet phase
change ink composition which comprises a blend of (1) crystalline
and (2) amorphous compounds, generally in a weight ratio of from
about 60:40 to about 95:5, respectively. In more specific
embodiments, the weight ratio of the crystalline to amorphous
compound is from about 65:35 to about 95:5, or is from about 70:30
to about 90:10.
[0023] Each compound or component imparts specific properties to
the phase change inks, and the resulting inks incorporating a blend
of these amorphous and crystalline compounds demonstrate excellent
robustness on uncoated and coated substrates. The crystalline
compound in the ink formulation drives the phase change through
rapid crystallization on cooling. The crystalline compound also
sets up the structure of the final ink film and creates a hard ink
by reducing the tackiness of the amorphous compound. The amorphous
compounds provide tackiness and impart robustness to the printed
ink.
[0024] U.S. patent application Ser. No. 13/457,157 to Gabriel
Iftime et al., electronically filed on Apr. 26, 2012 (Attorney
Docket No. 20110459-399389) discloses one method to achieve fast
solidifying inks by using a composition wherein the crystalline and
amorphous components have limited compatibility, which is hereby
incorporated by reference in its entirety. By limited
compatibility, it is meant that the two components have a tendency
to quickly phase separate when cooled down from a molten state.
Limited compatibility is achieved by selecting the crystalline and
amorphous components such as to satisfy a set of design rules
regarding the relationship between the functional groups present in
the chemical structures of a selected pair of a crystalline and
amorphous components respectively to provide the ability to rapidly
crystallize. Briefly, the design rules are set forth below:
[0025] (1) The phase change ink composition comprises an amorphous
compound and a crystalline compound;
[0026] (2) The amorphous compound comprises an amorphous core
moiety having at least one functional group and being attached to
at least one amorphous terminal group, wherein the amorphous
terminal group comprises an alkyl group, wherein the alkyl is
straight, branched or cyclic, saturated or unsaturated, substituted
or unsubstituted, having from about 1 to about 40 carbon atoms; a
diagram showing the structure of an amorphous compound is shown
below:
##STR00007##
[0027] (3) The crystalline compound comprises a crystalline core
moiety having at least one functional group and being attached to
at least one crystalline terminal group, wherein the crystalline
core group comprises an aromatic group; a diagram showing the
structure of a crystalline compound is shown below:
##STR00008##
and
[0028] (4) No one functional group in the amorphous core moiety is
the same as any of the functional group of the crystalline core
moiety.
[0029] In particular, the present embodiments use bio-renewable,
fast crystallizing di-esters with at least two fused aromatic core
groups and amorphous components derived from bio-renewable
materials. In embodiments, the present embodiments provide inks
that comprise at least 20% bio-renewable content, or from about 20
to about 85% bio-renewable content, or from about 50 to about 80%.
This means that at least 20% of the ink components are derived from
renewable resources such as plants. In particular, the ink
compositions contain inexpensive sharp-melting crystalline
materials derived from fatty monoalcohols and a dialkyl naphthalene
dicarboxylates, such as dimethyl naphthalene dicarboxylate, which
functions as the phase-change component, in addition to other
bio-renewable materials which function as the amorphous binder
resins. The fatty alcohols give the ink some hydrophobic character
which helps increase ink spreadability, an improvement from other
ink formulations. Moreover, the alcohols are bio-renewable and are
derived from plant oils such as cotton, coconut, palm kernel,
castor beans, rapeseed, soybeans and sunflowers. Thus, the
crystalline materials are both inexpensive and biodegradable. The
phase change inks made from these materials demonstrate excellent
robustness compared to commercially available phase change inks on
the same substrate.
[0030] In order to evaluate the suitability of a test ink for fast
printing, a quantitative method for measuring the rates of
crystallization of phase change inks containing crystalline
components was developed. Time-Resolved Optical Microscopy (TROM)
provides comparison between various test samples and, as a result,
is a useful tool for monitoring the progress made with respect to
the design of fast crystallizing inks. TROM is described in U.S.
patent application Ser. No. 13/456,847 to Gabriel Iftime et al.,
electronically filed on Apr. 26, 2012 (Attorney Docket No.
20110828-401275), which is hereby incorporated by reference in its
entirety.
[0031] TROM monitors the appearance and the growth of crystals by
using Polarized Optical Microscopy (POM). The sample is placed
between crossed polarizers of the microscope. Crystalline materials
are visible because they are birefringent. Amorphous materials or
liquids, such as inks in their molten state, that do not transmit
light, appear black under POM. Thus, POM provides an image contrast
when viewing crystalline components and allows for pursuing
crystallization kinetics of crystalline-amorphous inks when cooled
from the molten state to a set-temperature. In order to obtain data
that allow comparison between different and various samples,
standardized TROM experimental conditions were set, with the goal
of including as many parameters relevant to the actual printing
process. The ink or ink base is sandwiched between 18 mm circular
thin glass slides. The thickness of the ink layer is kept at 20-25
.mu.m (controlled with fiberglass spacers) which is close to actual
printed ink layers. For rate of crystallization measurement, the
sample is heated to the expected jetting temperature (viscosity of
about 10-12 cps) via an offline hotplate and then transferred to a
cooling stage coupled with an optical microscope. The cooling stage
is thermostated at a preset temperature which is maintained by
controlled supply of heat and liquid nitrogen. This experimental
set-up models the expected drum/paper temperature onto which a drop
of ink would be jetted in real printing process (40.degree. C. for
the experiments reported in this disclosure). Crystal formation and
growth is recorded with a camera.
[0032] It should be understood that the crystallization times
obtained with the TROM method for selected inks are not identical
to what would be the crystallization times of a droplet of ink in
an actual printing device. In an actual printing device such as a
printer, the ink solidifies much faster. It is determined that
there is a good correlation between the total crystallization time
as measured by the TROM method and the solidification time of an
ink in a printer. In the standardized conditions described above,
it is also determined that inks which solidify within 20 seconds,
within 15 seconds, or within 10 seconds (i.e., Total
crystallization time <20 s, <15 s or <10 s), as measured
by the TROM method, are suitable for fast printing, typically at
speeds from 100 feet/minute or higher. Therefore, for the purpose
of the present disclosure, a rate of crystallization lower than 15
seconds is considered to be fast crystallizing. However, very high
speed printing in the order of 500 feet/minute or higher require
inks with a crystallization rate as measured by TROM in the range
of less than about 7 seconds in the standardized TROM
conditions.
[0033] In practice, we have found that inks with time.sub.total
(Crystalline and Amorphous) lower or equal to 15 seconds in the
TROM test are suitable for fast printing at speeds of about 100
feet per minute or higher.
[0034] In certain embodiments, the total crystallization time of
the phase change ink is no more than 5 times the total
crystallization time of the crystalline compound alone. In further
embodiments, the total crystallization time of the phase change ink
is no more than 4 times the total crystallization time of the
crystalline compound alone. In yet further embodiments, the total
crystallization time of the phase change ink is no more than 3
times the total crystallization time of the crystalline compound
alone.
[0035] In embodiments, the phase change inks meet certain specific
physical properties. For example, the phase change inks of the
present embodiments have a melting point
(T.sub.melt)<150.degree. C. or from about 60.degree. C. to about
140.degree. C., or from about 70.degree. C. to about 130.degree. C.
In other embodiments, the ink has a T.sub.crys>60.degree. C. or
from about 65.degree. C. to about 110.degree. C., or from about
70.degree. C. to about 100.degree. C. In other embodiments, the ink
of the present embodiments has a viscosity of from about 1 to about
22 cps in a jetting range of from about 100 to about 140.degree. C.
In particular, the ink of the present embodiments has a viscosity
at 140.degree. C. of <12 cps or from about 12 cps to about 3
cps, or from about 10 cps to about 5 cps. The ink may have a
viscosity of greater than about 10.sup.6 cps at room
temperature.
[0036] The Amorphous Compound
[0037] In embodiments, the amorphous compound functions as the
binder agent for the crystalline component and any colorants or
other minor additives. In the present embodiments, the amorphous
compound is an ester compound having the general formula:
##STR00009##
wherein R.sub.1 and R.sub.2 each, independently of the other, is an
alkyl group, an aryl group, an arylalkyl group or a bicyclic system
and Z is an alkylene group, an arylene group, an arylalkylene
group, or an alkylarylene group. In specific embodiments, the
amorphous compound has the structure discussed below.
[0038] Some suitable amorphous materials are disclosed in U.S.
patent application Ser. No. 13/095,784 to Morimitsu et al., which
is hereby incorporated by reference in its entirety. The amorphous
materials may comprise an ester of tartaric acid having a formula
of
##STR00010##
wherein R.sub.1 and R.sub.2 each, independently of the other or
meaning that they can be the same or different, is selected from
the group consisting of alkyl group, wherein the alkyl portion can
be straight, branched or cyclic, saturated or unsaturated,
substituted or unsubstituted, having from about 1 to about 40
carbon atoms or a substituted or unsubstituted aromatic or
heteroaromatic group, and mixtures thereof. In certain embodiments,
each R.sub.1 and R.sub.2 is independently a cyclohexyl group
optionally substituted with one or more alkyl group(s) selected
from methyl, ethyl, n-propyl, isopropyl, n-butyl and t-butyl.
[0039] The tartaric acid backbone is selected from L-(+)-tartaric
acid, D-(-)-tartaric acid, DL-tartaric acid, or mesotartaric acid,
and mixtures thereof. Depending on the R groups and the
stereochemistries of tartaric acid, the esters could form crystals
or stable amorphous compounds. In specific embodiments, the
amorphous compound is selected from the group consisting of
di-L-menthyl L-tartrate, di-DL-menthyl L-tartrate (DMT),
di-L-menthyl DL-tartrate, di-DL-menthyl DL-tartrate, and any
stereoisomers and mixtures thereof.
[0040] These materials show, relatively low viscosity (<10.sup.2
centipoise (cps), or from about 1 to about 100 cps, or from about 5
to about 95 cps) near the jetting temperature (.ltoreq.140.degree.
C., or from about 100 to about 140.degree. C., or from about 105 to
about 140.degree. C.) but very high viscosity (>10.sup.5 cps) at
room temperature.
[0041] To synthesize the amorphous component, tartaric acid was
reacted with a variety of alcohols to make di-esters as shown in
the synthesis scheme shown in U.S. patent application Ser. No.
13/095,784. Suitable alcohols to be used with the present
embodiments may be selected from the group consisting of alkyl
alcohol, wherein the alkyl portion of the alcohol can be straight,
branched or cyclic, saturated or unsaturated, substituted or
unsubstituted, having from about 1 to about 40 carbon atoms, or a
substituted or unsubstituted aromatic or heteroaromatic group, and
mixtures thereof. A variety of alcohols may be used in the
esterification such as, for example, menthol, isomenthol,
neomenthol, isoneomentholand any stereoisomers and mixtures
thereof. Mixtures of aliphatic alcohols may be used in the
esterification. For example, a mixture of two aliphatic alcohols
may be used in the esterification. Suitable examples of aliphatic
alcohols that can be used in these mixed reactions are cyclohexanol
and substituted cyclohexanols (e.g., 2-, 3- or 4-t-butyl
cyclohexanol). The molar ratios of the aliphatic alcohols may be
from 25:75 to 75:25, from 40:60 to 60:40, or about 50:50,
[0042] Some more suitable amorphous materials are disclosed in U.S.
patent application Ser. No. 13/680,200 to Goredema et al. (Attorney
Docket No. 20110922-US-NP), which is hereby incorporated by
reference in its entirety.
[0043] In another embodiment, the amorphous material may comprise a
di-ester having the general formula;
##STR00011##
or a mixture of one or more compounds of General Formulas I and/or
II; wherein R.sub.1 is an alkylene group, arylene group,
arylalkylene group, alkylarylene group, including substituted and
unsubstituted alkylene groups, and wherein hetero-atoms either may
or may not be present in the alkylene group such an alkylene group
containing from 2 to about 12 carbon atoms, the R.sub.2-R.sub.25
groups are independently selected from the group consisting of
hydrogen, alkyl groups, arylalkyl groups, alkylaryl groups, and
heterocyclic groups; wherein one or more of R.sub.2-R.sub.25 groups
are included by a ring structure; and wherein (CH.sub.2)x denotes
one or more methylene groups, x an integer of from 1 to about 20 or
a mixture of one or more compounds of General Formulas I and/or
II.
[0044] More specifically the amorphous compound are esters of
succinic acid or tartaric acid and Abitol E alcohol with the
following structures;
##STR00012##
[0045] To synthesize the amorphous component, succinic acid or
tartaric acid was reacted with ABITOL E.TM. alcohol (available from
Hercules, Inc. (Wilmington, Del.)) as shown in the synthesis scheme
shown in U.S. patent application Ser. No. 13/680,200 to Goredema et
al. (Attorney Docket No. 20110922-US-NP). ABITOL E is shown by a
representative structure, and comprises hydroabietyl alcohol
(CAS[13393-93-6]), methyl ester of hydrogenated rosin
(CAS[8050-15-5]), and decarboxylated rosin (CAS[8050-18-8])).
[0046] Some more suitable amorphous materials are disclosed U.S.
patent application Ser. No. ______ to Goredema et al. (Attorney
Docket No. 20120801-US-NP) which is hereby incorporated by
reference in its entirety. In specific embodiments, the amorphous
material may comprise an amide having the general formula:
##STR00013##
[0047] wherein R is selected from the group consisting of an alkyl
group, an aryl group, an alkylaryl group, an arylalkyl group, and
combinations thereof. The amorphous amides described herein can be
prepared by any suitable or desired method. In embodiments, amine D
amorphous amide compounds herein are prepared by reacting amine D
available from Eastman Chemical Company with an acid of the
formula
##STR00014##
wherein R is an alkyl group having from about 1 to about 22 carbon
atoms, and wherein the alkyl group can be selected from linear,
branched, saturated, unsaturated, cyclic, substituted, and
unsubstituted alkyl.
[0048] Some more suitable amorphous materials are disclosed in U.S.
patent application Ser. No. ______ to Goredema et al. (Attorney
Docket No. 20120581-412786) which is hereby incorporated by
reference in its entirety.
[0049] In specific embodiments, the amorphous material can comprise
an aromatic rosin ester selected from the group consisting of
##STR00015##
and mixtures thereof. and mixtures thereof. In further embodiments,
the amorphous component comprises a mixture of
##STR00016##
in a range of from about 5% to about 15%, or from about 5% to about
10%, percent by weight of the total weight of the amorphous
component,
##STR00017##
in a range of from about 1% to about 6%, or from about 1% to about
3%, percent by weight of the total weight of the amorphous
component,
##STR00018##
in a range of from about 3% to about 8%, or from about 4% to about
6%, percent by weight of the total weight of the amorphous
component, and
##STR00019##
in a range of from about 75% to about 90%, or from about 75% to
about 85%, percent by weight of the total weight of the amorphous
component.
[0050] In specific embodiments, the amorphous binder is a di-ester
of menthol and tartaric acid (DMT) (Compound 1 shown in Table 1
below). Tartaric acid is a bio-renewable material which is a common
by-product from the wine industry. Menthol can also be
bio-renewable, depending on where it is sourced. In other
embodiments, the amorphous binder is an ester of a mixture of
cyclohexanol and t-butylcyclohexanol (50:50 ratio) and tartaric
acid (Compound 2 in Table 1 below). Compounds 1 and 2 are disclosed
in U.S. patent application Ser. No. 13/095,784 to Morimitsu et al.,
which is hereby incorporated by reference in its entirety. In
another specific embodiment, the amorphous binder is an ester of
Abitol E and succinic acid di-ester (Compound 3 shown in Table 1
below). Abitol E is a resin derived from pine sap and bio-based
succinic acid available from corn or sorghum. The bio-renewable
content is based on the weight percent of bio-based materials.
Compound 3 is disclosed in U.S. patent application Ser. No.
13/680,200 to Goredema et al. (Attorney Docket No. 20110922-US-NP)
which is hereby incorporated by reference in its entirety. Compound
4 is an amide derived from Amine D, a terpenoid compound derived
from dehydroabeitic acid as the backbone material and which is
commercially available from Eastman Chemicals Co. (Kingsport,
Tenn.). In another specific embodiment, the amorphous binder is an
amide of amine D available from Eastman Chemical Company and
hexanoic acid (Compound 4 shown in Table 1 below). Compound 4 is
disclosed in U.S. patent application Ser. No. ______ to Goredema et
al. (Attorney Docket No. 20120801-US-NP) which is hereby
incorporated by reference in its entirety.
[0051] In yet another specific embodiment, the amorphous binder is
an aromatic rosin-based binder commercially available from Arizona
Chemicals Jacksonville, Fla. (compound 5 shown in Table 1).
Compound 5 is disclosed in U.S. patent application Ser. No. ______
to Goredema et al. (Attorney Docket No. 20120581-412786) which is
hereby incorporated by reference in its entirety.
TABLE-US-00001 TABLE 1 Bio- renewable Compound Structure Content
(%) 1 ##STR00020## 27-100* 2 ##STR00021## 30 3 ##STR00022## 100 4
##STR00023## 71 5 ##STR00024## 80 *BRC depends on menthol
source
[0052] The amorphous compounds show relatively low viscosity
(<10.sup.2 centipoise (cps), or from about 1 to about 100 cps,
or from about 5 to about 95 cps) near the jetting temperature
(.ltoreq.140.degree. C.) but very high viscosity (>10.sup.5 cps)
at room temperature.
[0053] In embodiments, the amorphous compounds are formulated with
a crystalline compound to form a phase change ink composition. All
of the crystalline components and some of the binders are esters.
This class of materials is well known to be readily biodegradable.
The ink compositions show good rheological profiles. Print samples
created by the phase change ink composition on coated paper by
K-proof exhibit excellent robustness.
[0054] In embodiments, the amorphous material is present an amount
of from about 5 percent to about 40 percent by weight, or from
about 10 percent to about 35 percent by weight, or from about 15
percent to about 30 percent by weight of the total weight of the
ink composition.
[0055] The Crystalline Compound
[0056] The novel sustainable crystalline materials of the present
embodiments are synthesized from dialkyl naphthalene
dicarboxylates, such as dimethyl naphthalene dicarboxylate (NDC),
which is reacted with different alcohols to give di-esters with two
aromatic groups in the core as shown in the scheme below.
##STR00025##
wherein R is a saturated or ethylenically unsaturated aliphatic
group in one embodiment with at least about 6 carbon atoms, and in
another embodiment with at least about 8 carbon atoms, and in one
embodiment with no more than about 100 carbon atoms, in another
embodiment with no more than about 80 carbon atoms, and in yet
another embodiment with no more than about 60 carbon atoms,
although the number of carbon atoms can be outside of these ranges.
In a specific embodiment, the crystalline compound is derived from
natural fatty alcohols such as octanol, stearyl alcohol, lauryl
alcohol, behenyl alcohol, myristyl alcohol, capric alcohol,
linoleyl alcohol, and mixtures thereof and the like. The above
reaction may be conducted by combining dimethyl terephthalate and
alcohol in the melt in the presence of a tin catalyst, such as,
dibutyl tin dilaurate (Fascat 4202), dibutyl tin oxide (Fascat
4100); a zinc catalyst, such as Bi cat Z; or a bismuth catalyst,
such as Bi cat 8124; Bi cat 8108, a titanium catalyst such as
titanium dioxide. Only trace quantities of catalyst are required
for the process.
[0057] In embodiments, the catalyst is present in an amount of
about 0.01 weight percent to 2 weight percent or of about 0.05
weight percent to about 1 weight percent by weight of the total
product.
[0058] The reaction is carried out at an elevated temperature of
about 150.degree. C. to about 250.degree. C. or from about
160.degree. C. to about 210.degree. C. The solvent-free process is
environmentally sustainable and eliminates problems with byproducts
and also means higher reactor throughput.
[0059] Most of these alcohols are bio-renewable materials derived
from plant oils such as cotton, coconut, palm kernel, castor beans,
rapeseed, soybeans, and sunflowers. These alcohols are reacted with
dimethyl naphthalene carboxylate to give the corresponding
di-ester.
[0060] Examples of alcohols used in this invention include natural
fatty alcohols such as stearyl alcohol, lauryl alcohol, behenyl
alcohol and mixtures thereof. All of these alcohols are
bio-renewable materials derived from plant oils such as cotton,
coconut, palm kernel, castor beans, rapeseed, soybeans, and
sunflowers.
[0061] Samples of specific alcohols for use to make the di-ester
compounds (for use as the crystalline compound) were evaluated and
the results are shown in Table 2. Most of the compounds showed very
sharp transitions within the desirable temperature range (i.e.,
60.degree. C.<T<130.degree. C.) indicating promising
properties for the phase changing material of the ink.
TABLE-US-00002 TABLE 2 Bio- Sample renewable T.sub.melt Viscosity
ID Content (.degree. C.) T.sub.cryst .degree. C.) at 140.degree. C.
No. R--OH (%)* (DSC) (DSC) (cps) Com- Stearyl alcohol 74 80 77 5.99
pound 1 (CH.sub.3(CH.sub.2).sub.17OH Com- Behenyl Alcohol 78 97 88
8.67 pound 2 (CH.sub.3(CH.sub.2).sub.21OH 3 Lauryl Alcohol 67 -- --
-- (CH.sub.3(CH.sub.2).sub.11OH
[0062] The bio-renewable content is based on the weight percent of
bio-based materials. All of the starting materials used to make the
crystalline components of the present embodiments are inexpensive.
Moreover, these materials are prepared by simple, low-cost and
environmentally benign synthetic routes using solventless
condensation procedures with methanol as the only by-product. For
example, in embodiments, the crystalline components have a
bio-renewable content of at least 65 percent by weight, or from
about 60 to about 85 percent by weight or from about 60 to about 80
percent by weight
[0063] The crystalline materials show sharp crystallization,
relatively low viscosity (.ltoreq.10.sup.1 centipoise (cps), or
from about 0.5 to about 10 cps, or from about 1 to about 10 cps) at
a temperature of about 140.degree. C., but very high viscosity
(>10.sup.6 cps) at room temperature. These materials have a
sharp melting temperature (T.sub.melt) of less than 150.degree. C.,
or from about 65 to about 150.degree. C., or from about 66 to about
145.degree. C., and a sharp crystallization temperature
(T.sub.crys) of greater than 60.degree. C., or from about 60 to
about 140.degree. C., or from about 65 to about 120.degree. C. The
.DELTA.T between T.sub.melt and T.sub.crys is less than about
55.degree. C.
[0064] In embodiments, the crystalline material is present in an
amount of from about 60 percent to about 95 percent by weight, or
from about 65 percent to about 95 percent by weight, or from about
70 percent to about 90 percent by weight of the total weight of the
ink composition.
[0065] Additives
[0066] The ink of embodiments may further include conventional
additives to take advantage of the known functionality associated
with such conventional additives. Such additives may include, for
example, at least one antioxidant, defoamer, slip and leveling
agents, clarifier, viscosity modifier, adhesive, plasticizer and
the like.
[0067] The ink may optionally contain antioxidants to protect the
images from oxidation and also may protect the ink components from
oxidation while existing as a heated melt in the ink reservoir.
Examples of suitable antioxidants include N,N'-hexamethylene
bis(3,5-di-tert-butyl-4-hydroxy hydrocinnamamide) (IRGANOX 1098,
available from BASF);
2,2-bis(4-(2-(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyloxy))
ethoxyphenyl)propane (TOPANOL-205, available from Vertellus);
tris(4-tert-butyl-3-hydroxy-2,6-dimethyl benzyl)isocyanurate
(Aldrich); 2,2'-ethylidene bis(4,6-di-tert-butylphenyl)fluoro
phosphonite (ETHANOX-398, available from Albermarle Corporation);
tetrakis(2,4-di-tert-butylphenyl)-4,4'-biphenyl diphosphonite
(Aldrich); pentaerythritol tetrastearate (TCI America);
tributylammonium hypophosphite (Aldrich);
2,6-di-tert-butyl-4-methoxyphenol (Aldrich);
2,4-di-tert-butyl-6-(4-methoxybenzyl)phenol (Aldrich);
4-bromo-2,6-dimethylphenol (Aldrich); 4-bromo-3,5-didimethylphenol
(Aldrich); 4-bromo-2-nitrophenol (Aldrich); 4-(diethyl
aminomethyl)-2,5-dimethylphenol (Aldrich); 3-dimethylaminophenol
(Aldrich); 2-amino-4-tert-amylphenol (Aldrich);
2,6-bis(hydroxymethyl)-p-cresol (Aldrich); 2,2'-methylenediphenol
(Aldrich); 5-(diethylamino)-2-nitrosophenol (Aldrich);
2,6-dichloro-4-fluorophenol (Aldrich); 2,6-dibromo fluoro phenol
(Aldrich); .alpha.-trifluoro-o-cresol (Aldrich);
2-bromo-4-fluorophenol (Aldrich); 4-fluorophenol (Aldrich);
4-chlorophenyl-2-chloro-1,1,2-tri-fluoroethyl sulfone (Aldrich);
3,4-difluoro phenylacetic acid (Adrich); 3-fluorophenylacetic acid
(Aldrich); 3,5-difluoro phenylacetic acid (Aldrich);
2-fluorophenylacetic acid (Aldrich); 2,5-bis (trifluoromethyl)
benzoic acid (Aldrich);
ethyl-2-(4-(4-(trifluoromethyl)phenoxy)phenoxy)propionate
(Aldrich); tetrakis (2,4-di-tert-butyl phenyl)-4,4'-biphenyl
diphosphonite (Aldrich); 4-tert-amyl phenol (Aldrich);
3-(2H-benzotriazol-2-yl)-4-hydroxy phenethylalcohol (Aldrich);
NAUGARD 76, NAUGARD 445, NAUGARD 512, and NAUGARD 524 (manufactured
by Chemtura Corporation); and the like, as well as mixtures
thereof. The antioxidant, when present, may be present in the ink
in any desired or effective amount, such as from about 0.25 percent
to about 10 percent by weight of the ink or from about 1 percent to
about 5 percent by weight of the ink.
[0068] Colorants
[0069] In embodiments, the phase change ink compositions described
herein also include a colorant. The ink of the present embodiments
can thus be one with or without colorants. The phase change ink may
optionally contain colorants such as dyes or pigments. The
colorants can be either from the cyan, magenta, yellow, black
(CMYK) set or from spot colors obtained from custom color dyes or
pigments or mixtures of pigments. Dye-based colorants are miscible
with the ink base composition, which comprises the crystalline and
amorphous components and any other additives.
[0070] In embodiments, the phase change ink compositions described
herein also include a colorant. Any desired or effective colorant
can be employed in the phase change ink compositions, including
dyes, pigments, mixtures thereof, and the like, provided that the
colorant can be dissolved or dispersed in the ink carrier. Any dye
or pigment may be chosen, provided that it is capable of being
dispersed or dissolved in the ink carrier and is compatible with
the other ink components. The phase change carrier compositions can
be used in combination with conventional phase change ink colorant
materials, such as Color Index (C.I.) Solvent Dyes, Disperse Dyes,
modified Acid and Direct Dyes, Basic Dyes, Sulphur Dyes, Vat Dyes,
and the like. Examples of suitable dyes include Neozapon Red 492
(BASF); Orasol Red G (Pylam Products); Direct Brilliant Pink B
(Oriental Giant Dyes); Direct Red 3BL (Classic Dyestuffs); Supranol
Brilliant Red 3BW (Bayer AG); Lemon Yellow 6G (United Chemie);
Light Fast Yellow 3G (Shaanxi); Aizen Spilon Yellow C-GNH (Hodogaya
Chemical); Bemachrome Yellow GD Sub (Classic Dyestuffs); Cartasol
Brilliant Yellow 4GF (Clariant); Cibanone Yellow 2G (Classic
Dyestuffs); Orasol Black RLI (BASF); Orasol Black CN (Pylam
Products); Savinyl Black RLSN (Clariant); Pyrazol Black BG
(Clariant); Morfast Black 101 (Rohm & Haas); Diaazol Black RN
(ICI); Thermoplast Blue 670 (BASF); Orasol Blue GN (Pylam
Products); Savinyl Blue GLS (Clariant); Luxol Fast Blue MBSN (Pylam
Products); Sevron Blue 5GMF (Classic Dyestuffs); Basacid Blue 750
(BASF); Keyplast Blue (Keystone Aniline Corporation); Neozapon
Black X51 (BASF); Classic Solvent Black 7 (Classic Dyestuffs);
Sudan Blue 670 (C.I. 61554) (BASF); Sudan Yellow 146 (C.I. 12700)
(BASF); Sudan Red 462 (C.I. 26050) (BASF); C.I. Disperse Yellow
238; Neptune Red Base NB543 (BASF, C.I. Solvent Red 49); Neopen
Blue FF-4012 (BASF); Fatsol Black BR (C.I. Solvent Black 35)
(Chemische Fabriek Triade BV); Morton Morplas Magenta 36 (C.I.
Solvent Red 172); metal phthalocyanine colorants such as those
disclosed in U.S. Pat. No. 6,221,137, the disclosure of which is
totally incorporated herein by reference, and the like. Polymeric
dyes can also be used, such as those disclosed in, for example.
U.S. Pat. No. 5,621,022 and U.S. Pat. No. 5,231,135, the
disclosures of each of which are herein entirely incorporated
herein by reference, and commercially available from, for example,
Milliken & Company as Milliken Ink Yellow 869, Milliken Ink
Blue 92, Milliken Ink Red 357, Milliken Ink Yellow 1800, Milliken
Ink Black 8915-67, uncut Reactint Orange X-38, uncut Reactint Blue
X-17, Solvent Yellow 162, Acid Red 52, Solvent Blue 44, and uncut
Reactint Violet X-80.
[0071] Pigments are also suitable colorants for the phase change
inks. Examples of suitable pigments include PALIOGEN Violet 5100
(BASF); PALIOGEN Violet 5890 (BASF); HELIOGEN Green L8730 (BASF);
LITHOL Scarlet D3700 (BASE); SUNFAST Blue 15:4 (Sun Chemical);
Hostaperm Blue B2G-D (Clariant); Hostaperm Blue B4G (Clariant);
Permanent Red P--F7RK; Hostaperm Violet BL (Clariant); LITHOL
Scarlet 4440 (BASF); Bon Red C (Dominion Color Company); ORACET
Pink RF (BASF); PALIOGEN Red 3871 K (BASF); SUNFAST Blue 15:3 (Sun
Chemical); PALIOGEN Red 3340 (BASF); SUNFAST Carbazole Violet 23
(Sun Chemical); LITHOL Fast Scarlet L4300 (BASF); SUNBRITE Yellow
17 (Sun Chemical); HELIOGEN Blue L6900, L7020 (BASF); SUNBRITE
Yellow 74 (Sun Chemical); SPECTRA PAC C Orange 16 (Sun Chemical);
HELIOGEN Blue K6902, K6910 (BASF); SUNFAST Magenta 122 (Sun
Chemical); HELIOGEN Blue D6840, D7080 (BASF); Sudan Blue OS (BASF);
NEOPEN Blue FF4012 (BASF); PV Fast Blue B2GO1 (Clariant); IRGALITE
Blue GLO (BASF); PALIOGEN Blue 6470 (BASF); Sudan Orange G
(Aldrich); Sudan Orange 220 (BASF); PALIOGEN Orange 3040 (BASF);
PALIOGEN Yellow 152, 1560 (BASF); LITHOL Fast Yellow 0991 K (BASF);
PALIOTOL Yellow 1840 (BASF); NOVOPERM Yellow FGL (Clariant); Ink
Jet Yellow 4G VP2532 (Clariant); Toner Yellow HG (Clariant);
Lumogen Yellow D0790 (BASF); Suco-Yellow L1250 (BASF); Suco-Yellow
D1355 (BASF); Suco Fast Yellow D1355, D1351 (BASF); HOSTAPERM Pink
E 02 (Clariant); Hansa Brilliant Yellow 5GX03 (Clariant); Permanent
Yellow GRLO2 (Clariant); Permanent Rubine L6B 05 (Clariant); FANAL
Pink D4830 (BASF); CINQUASIA Magenta (DU PONT); PALIOGEN Black
L0084 (BASF); Pigment Black K801 (BASF); and carbon blacks such as
REGAL 330.TM. (Cabot), Nipex 150 (Evonik) Carbon Black 5250 and
Carbon Black 5750 (Columbia Chemical), and the like, as well as
mixtures thereof.
[0072] Pigment dispersions in the ink base may be stabilized by
synergists and dispersants. Generally, suitable pigments may be
organic materials or inorganic. Magnetic material-based pigments
are also suitable, for example, for the fabrication of robust
Magnetic Ink Character Recognition (MICR) inks. Magnetic pigments
include magnetic nanoparticles, such as for example, ferromagnetic
nanoparticles.
[0073] Also suitable are the colorants disclosed in U.S. Pat. No.
6,472,523, U.S. Pat. No. 6,726,755, U.S. Pat. No. 6,476,219, U.S.
Pat. No. 6,576,747, U.S. Pat. No. 6,713,614, U.S. Pat. No.
6,663,703, U.S. Pat. No. 6,755,902, U.S. Pat. No. 6,590,082, U.S.
Pat. No. 6,696,552, U.S. Pat. No. 6,576,748, U.S. Pat. No.
6,646,111, U.S. Pat. No. 6,673,139, U.S. Pat. No. 6,958,406, U.S.
Pat. No. 6,821,327, U.S. Pat. No. 7,053,227, U.S. Pat. No.
7,381,831 and U.S. Pat. No. 7,427,323, the disclosures of each of
which are incorporated herein by reference in their entirety.
[0074] In embodiments, solvent dyes are employed. An example of a
solvent dye suitable for use herein may include spirit soluble dyes
because of their compatibility with the ink carriers disclosed
herein. Examples of suitable spirit solvent dyes include Neozapon
Red 492 (BASF); Orasol Red G (Pylam Products); Direct Brilliant
Pink B (Global Colors); Aizen Spilon Red C--BH (Hodogaya Chemical);
Kayanol Red 3BL (Nippon Kayaku); Spirit Fast Yellow 3G; Aizen
Spilon Yellow C-GNH (Hodogaya Chemical); Cartasol Brilliant Yellow
4GF (Clariant); Pergasol Yellow 5RA EX (Classic Dyestuffs); Orasol
Black RLI (BASF); Orasol Blue GN (Pylam Products); Savinyl Black
RLS (Clariant); Morfast Black 101 (Rohm and Haas); Thermoplast Blue
670 (BASF); Savinyl Blue GLS (Sandoz); Luxol Fast Blue MBSN
(Pylam); Sevron Blue 5GMF (Classic Dyestuffs); Basacid Blue 750
(BASF); Keyplast Blue (Keystone Aniline Corporation); Neozapon
Black X51 (C.I. Solvent Black, C.I. 12195) (BASF); Sudan Blue 670
(C.I. 61554) (BASF); Sudan Yellow 146 (C.I. 12700) (BASF); Sudan
Red 462 (C.I. 260501) (BASF), mixtures thereof and the like.
[0075] The colorant may be present in the phase change ink in any
desired or effective amount to obtain the desired color or hue such
as, for example, at least from about 0.1 percent by weight of the
ink to about 20 percent by weight of the ink, at least from about 1
percent by weight of the ink to about 15 percent by weight of the
ink, and at least from about 2 percent by weight of the ink to
about 10 percent by weight of the ink.
[0076] The ink compositions can be prepared by any desired or
suitable method. For example, each of the components of the ink
carrier can be mixed together, followed by heating, the mixture to
at least its melting point, for example from about 60.degree. C. to
about 150.degree. C., 80.degree. C. to about 145.degree. C. and
85.degree. C. to about 140.degree. C. The colorant may be added
before the ink ingredients have been heated or after the ink
ingredients have been heated. When pigments are the selected
colorants, the molten mixture may be subjected to grinding in an
attritor or media mill apparatus to effect dispersion of the
pigment in the ink carrier. The heated mixture is then stirred for
about 5 seconds to about 30 minutes or more, to obtain a
substantially homogeneous, uniform melt, followed by cooling the
ink to ambient temperature (typically from about 20.degree. C. to
about 25.degree. C.). The inks are solid at ambient temperature.
The inks can be employed in apparatus for direct printing ink jet
processes and in indirect (offset) printing ink jet applications.
Another embodiment disclosed herein is directed to a process which
comprises incorporating an ink as disclosed herein into an ink jet
printing apparatus, melting the ink, and causing droplets of the
melted ink to be ejected in an imagewise pattern onto a recording
substrate. A direct printing process is also disclosed in, for
example, U.S. Pat. No. 5,195,430, the disclosure of which is
totally incorporated herein by reference. Yet another embodiment
disclosed herein is directed to a process which comprises
incorporating an ink as disclosed herein into an ink jet printing
apparatus, melting the ink, causing droplets of the melted ink to
be ejected in an imagewise pattern onto an intermediate transfer
member, and transferring the ink in the imagewise pattern from the
intermediate transfer member to a final recording substrate. In a
specific embodiment, the intermediate transfer member is heated to
a temperature above that of the final recording sheet and below
that of the melted ink in the printing apparatus. In another
specific embodiment, both the intermediate transfer member and the
final recording sheet are heated; in this embodiment, both the
intermediate transfer member and the final recording sheet are
heated to a temperature below that of the melted ink in the
printing apparatus; in this embodiment, the relative temperatures
of the intermediate transfer member and the final recording sheet
can be (1) the intermediate transfer member is heated to a
temperature above that of the final recording substrate and below
that of the melted ink in the printing apparatus; (2) the final
recording substrate is heated to a temperature above that of the
intermediate transfer member and below that of the melted ink in
the printing apparatus; or (3) the intermediate transfer member and
the final recording sheet are heated to approximately the same
temperature. An offset or indirect printing process is also
disclosed in, for example, U.S. Pat. No. 5,389,958, the disclosure
of which is totally incorporated herein by reference. In one
specific embodiment, the printing apparatus employs a piezoelectric
printing process wherein droplets of the ink are caused to be
ejected in imagewise pattern by oscillations of piezoelectric
vibrating elements. Inks as disclosed herein can also be employed
in other hot melt printing processes, such as hot melt acoustic ink
jet printing, hot melt thermal ink jet printing, hot melt
continuous stream or deflection ink jet printing, and the like.
Phase change inks as disclosed herein can also be used in printing
processes other than hot melt ink jet printing processes.
[0077] Any suitable substrate or recording sheet can be employed,
including plain papers such as XEROX 4200 papers, XEROX Image
Series papers, Courtland 4024 DP paper, ruled notebook paper, bond
paper, silica coated papers such as Sharp Company silica coated
paper, JuJo paper, HAMMERMILL LASERPRINT paper, and the like,
glossy coated papers such as XEROX Digital Color Elite Gloss, Sappi
Warren Papers LUSTROGLOSS, specialty papers such as Xerox
DURAPAPER, and the like, transparency materials, fabrics, textile
products, plastics, polymeric films, inorganic recording mediums
such as metals and wood, and the like, transparency materials,
fabrics, textile products, plastics, polymeric films, inorganic
substrates such as metals and wood, and the like.
[0078] The inks described herein are further illustrated in the
following examples. All parts and percentages are by weight unless
otherwise indicated.
[0079] It will be appreciated that various of the above-disclosed
and other features and functions, or alternatives thereof, may be
desirably combined into many other different systems or
applications. Also, various presently unforeseen or unanticipated
alternatives, modifications, variations or improvements therein may
be subsequently made by those skilled in the art, and are also
intended to be encompassed by the following claims.
[0080] While the description above refers to particular
embodiments, it will be understood that many modifications may be
made without departing from the spirit thereof. The accompanying
claims are intended to cover such modifications as would fall
within the true scope and spirit of embodiments herein.
[0081] The presently disclosed embodiments are, therefore, to be
considered in all respects as illustrative and not restrictive, the
scope of embodiments being indicated by the appended claims rather
than the foregoing description. All changes that come within the
meaning of and range of equivalency of the claims are intended to
be embraced therein.
EXAMPLES
[0082] The examples set forth herein below and are illustrative of
different compositions and conditions that can be used in
practicing the present embodiments. All proportions are by weight
unless otherwise indicated. It will be apparent, however, that the
present embodiments can be practiced with many types of
compositions and can have many different uses in accordance with
the disclosure above and as pointed out hereinafter.
Example 1
Synthesis of distearyl naphthalene-2,6-dicarboxylate (Compound 1,
Table 2)
[0083] To a 3 neck 100 mL round bottomed flask equipped with a Dean
Stark trap and condenser, thermocouple and argon inlet was added
dimethyl naphthalene-2,6-dicarboxylate (10 grams, 40.94 mmoles,
available from Sigma Aldrich), stearyl alcohol (22.15 grams, 81.89
mmoles, available from Spectrum Chemical), Fascat 4100 (0.03 grams,
0.1 wt %, available from Arkema Inc) and Xylenes (50 ml, available
from Sigma Aldrich). The mixture was slowly heated under argon to
160.degree. C. during which reagents melted/dissolved. The
temperature was raised to 180.degree. C. The reaction mixture was
stirred at 180.degree. C. overnight (.about.20 hours) during which
46 mL of a mixture of xylenes and methanol was collected. Vacuum
was applied (1-2 mm-Hg) for about 10 minutes during which an
additional 5 mL of a mixture of Xylenes and methanol was collected.
The solution was cooled under argon to about 140.degree. C. and
discharged in an aluminum tray where it was allowed to cool to room
temperature to give product as an off-white solid. The product was
transferred to a 1 L Erlenmeyer flask, about 100 mL of isopropyl
alcohol was added, heated to about 100.degree. C. during which
product dissolved. The solution was cooled to room temperature
during which product crystallized out, filtered and dried on a
vacuum pump overnight to give 25.33 grams product as an off-white
solid (86% yield). The product was shown to be pure by .sup.1H NMR
with trace amounts of the mono-ester. Physical properties of this
compound are shown in Table 2 above. The FIGURE shows the
rheological profile.
[0084] A small amount of Xylenes was used to help prevent
sublimation of the dimethyl naphthalene-2,6-dicarboxylate. If the
reaction is done in a pressurized reactor, the solvent will not be
required.
Example 2
Synthesis of dibehenyl naphthalene-2,6-dicarboxylate (Compound 2,
Table 2)
[0085] Compound 2 was synthesized using the same procedure outlined
for Compound 1 except Behenyl alcohol was used instead of stearyl
alcohol and was not recrystallized. Physical properties for this
compound is shown in Table 1 above. The rheological profile of
Compound 3 is shown in the FIGURE. As shown in the FIGURE, both
Compounds 1 and 2 have very sharp phase changes above 90.degree. C.
and low viscosity (<10 cps) in the jetting range of
100-140.degree. C. making them suitable candidates for the robust
phase change inks of the present embodiments.
Example 3
Synthesis of dilauryl naphthalene-2,6-dicarboxylate (Compound 3,
Table 2)
[0086] Compound 3 was synthesized using the same procedure outlined
for Compound 1 except Lauryl alcohol was used instead of stearyl
alcohol. All the starting materials used to make the crystalline
components of the present embodiments are inexpensive and safe. In
fact, some of the fatty alcohols are used in the pharmaceutical
industry. The crystalline materials are prepared by simple,
low-cost and environmentally benign synthetic routes using
solventless condensation procedures with methanol as the only
by-product. Dimethyl naphthalene-2,6-dicarboxylate is used for the
synthesis because the melting point of Naphthalene dicarboxylate
(NDC) is too high. The fatty alcohols used to make the crystalline
components of the present embodiments are derived from plants
giving these components, in embodiments, at least greater than 65%
bio-renewable content.
Example 4
Ink Compositions
[0087] Five amorphous binders were used to make inks of the present
embodiments, as shown in Table 2.
[0088] Inks were formulated using mixtures of some of the novel
sustainable crystalline components listed in Table 2 and amorphous
binders components listed in Table 1. Table 3 shows the composition
and properties of the bio-renewable and robust phase change inks
made with the dialkyl naphthalene dicarboxylate crystalline
materials.
TABLE-US-00003 TABLE 3 Ink 1 Ink 2 Ink 3 Ink 4 Ink 5 Crystalline
Compound 1 78.4 78.4 76.48 76.48 76.48 material (BRC = 74%)
Amorphous DMT 19.6 component (BRC ~27-100%) TBCT (30% BRC) 19.12
Abitol E SA 19.6 (BRC ~100%) Sylvatac RE 40 19.12 ((BRC ~80%) Amine
D Diamide 19.12 (~71% (BRC) Solsperse 3200 dispersant 2 2 2 SunFlo
SFD-B124 Synergist 0.4 0.4 0.4 Keystone Solvent blue 101 Dye 2 2
Hostapern B4G Cyan Pigment 2 2 2 Total 100 100 100 100 100 *BRC (%)
~78 ~61-78 ~53 ~72 ~70 **Viscosity @ 140.degree. C. (cps) 7.28 6.25
12.09 10.23 7.98 Tcryst. (.degree. C .) (by rheology) 80 80 80 80
80 Rate of Crystallization (seconds) -- -- 3 -- -- *Bio-renewable
content-weight percent of bio-based materials **Frequency = 1 Hz;
25 mm parallel plate geometry; gap = 0.2 mm; strain % = 400%
[0089] Rate of Crystallization
[0090] Rate of crystallization is a very important characteristic
of production inks--it dictates the rate at which the ink can be
touched after printing which affects the printing speed. As a
result, the faster the rate of crystallization, the faster the
printing speed. The rate of crystallization of ink example 3 was
measured using Time Resolved Optical Microscopy (TROM) experiments
as described above in U.S. patent application Ser. No. 13/456,847
to Gabriel Iftime et al. Ink example 3 had very fast rate of
crystallization as shown in table 3 above.
[0091] Evaluation of Ink Robustness
[0092] Inks 1-5 were printed onto DCEG coated papers (120 gsm
stock) using a K-proofer gravure printing plate, which was rigged
with a pressure roll set at low pressure. The gravure plate
temperature was set at 142.degree. C., but the actual plate
temperature was about 134.degree. C. The K-proofer apparatus
(manufactured by RK Print Coat Instrument Ltd., Litlington,
Royston, Heris, SG8 0OZ, U.K.) is a useful printing tool to screen
a variety of inks at small scale and to assess image quality on
various substrates, before an ink formulation is scaled up and
optimized for more in-depth inkjet printing tests.
[0093] K-proofs were fed through a Xerox PHASER 4200 printer
(Saturn) at 1 inch per second (1 ips) at a drum temperature of
50.degree. C. with the ink surface facing the oiled drum. One
K-proof of each ink was then scratched using a three-finger gouge
system. No ink was visibly removed from the images made with ink
examples 1-5 indicating that images are robust, Another K-proof was
folded along with a Xerox Business 4200 (75 gsm) facing page in a
Duplo D-590 folder and evaluated for fold crease and fold
offset,
[0094] The folded K-proof of Inks 1-5 showed no fold crease
indicating good image robustness.
SUMMARY
[0095] In summary, novel crystalline materials with two fused
aromatic rings in the core were synthesized from naphthalene
dicarboxylate and various bio-renewable alcohols. The alcohols used
are derived from bio-renewable resources giving materials with up
to 78% bio-renewable content. In addition, the crystalline
materials can be synthesized using simple neat conditions. The
resulting crystalline materials demonstrated physical properties
desirable for robust phase change inks.
[0096] The present embodiments thus also provide sustainable and
robust phase change inks with excellent scratch resistance, even on
coated substrates, made from the novel crystalline materials.
[0097] The claims, as originally presented and as they may be
amended, encompass variations, alternatives, modifications,
improvements, equivalents, and substantial equivalents of the
embodiments and teachings disclosed herein, including those that
are presently unforeseen or unappreciated, and that, for example,
may arise from applicants/patentees and others. Unless specifically
recited in a claim, steps or components of claims should not be
implied or imported from the specification or any other claims as
to any particular order, number, position, size, shape, angle,
color, or material.
[0098] All the patents and applications referred to herein are
hereby specifically, and totally incorporated herein by reference
in their entirety in the instant specification.
* * * * *