U.S. patent application number 13/825674 was filed with the patent office on 2015-04-09 for substances and method for replacing natural tooth material.
This patent application is currently assigned to LOMA LINDA UNIVERSITY. The applicant listed for this patent is LOMA LINDA UNIVERSITY. Invention is credited to Homayoun Moaddel, Mahmoud Torabinejad.
Application Number | 20150099244 13/825674 |
Document ID | / |
Family ID | 49223327 |
Filed Date | 2015-04-09 |
United States Patent
Application |
20150099244 |
Kind Code |
A9 |
Torabinejad; Mahmoud ; et
al. |
April 9, 2015 |
SUBSTANCES AND METHOD FOR REPLACING NATURAL TOOTH MATERIAL
Abstract
A substance that sets in a relatively short time for use in
general dentistry and in endodontics to replace natural tooth
material, the substance comprising untreated mineral trioxide
aggregate and milled mineral trioxide aggregate, or comprising
untreated mineral trioxide aggregate, milled mineral trioxide
aggregate and water. A method of making a substance that sets in a
relatively short time for use in general dentistry and in
endodontics to replace natural tooth material, the method
comprising milling by high shear and impact impingement of
particles using high pressure homogenization. A method for use in
general dentistry and in endodontics to replace natural tooth
material.
Inventors: |
Torabinejad; Mahmoud; (Loma
Linda, CA) ; Moaddel; Homayoun; (Pomona, CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
LOMA LINDA UNIVERSITY |
Loma Linda |
CA |
US |
|
|
Assignee: |
LOMA LINDA UNIVERSITY
Loma Linda
CA
|
Prior
Publication: |
|
Document Identifier |
Publication Date |
|
US 20140134573 A1 |
May 15, 2014 |
|
|
Family ID: |
49223327 |
Appl. No.: |
13/825674 |
Filed: |
March 20, 2013 |
PCT Filed: |
March 20, 2013 |
PCT NO: |
PCT/US13/33164 PCKC 00 |
371 Date: |
March 22, 2013 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61712058 |
Oct 10, 2012 |
|
|
|
61613797 |
Mar 21, 2012 |
|
|
|
61768801 |
Feb 25, 2013 |
|
|
|
Current U.S.
Class: |
433/224 ; 106/35;
514/626 |
Current CPC
Class: |
C04B 7/02 20130101; A61K
6/17 20200101; A61K 6/849 20200101; A61K 6/54 20200101; C04B 14/30
20130101; A61C 5/40 20170201; A61K 6/84 20200101; A61K 6/851
20200101; A61K 6/853 20200101 |
Class at
Publication: |
433/224 ; 106/35;
514/626 |
International
Class: |
A61K 6/06 20060101
A61K006/06; A61C 5/04 20060101 A61C005/04 |
Claims
1. A substance for use in general dentistry and in endodontics to
replace natural tooth material, the substance comprising untreated
mineral trioxide aggregate and milled mineral trioxide aggregate,
where the untreated mineral trioxide aggregate and milled mineral
trioxide aggregate together are total mineral trioxide
aggregate.
2. The substance of claim 1, further comprising a liquid selected
from the group consisting of a local anesthetic and water.
3. The substance of claim 1, where the untreated mineral trioxide
aggregate comprises a median maximum particle diameter size of
between five and thirty times larger than the median maximum
particle diameter size of the milled mineral trioxide
aggregate.
4. The substance of claim 1, where the untreated mineral trioxide
aggregate comprises a median maximum particle diameter size of
between five and fifteen times larger than the median maximum
particle diameter size of the milled mineral trioxide
aggregate.
5. The substance of claim 1, where the untreated mineral trioxide
aggregate comprises a median maximum particle diameter size of
between eight and twelve times larger than the median maximum
particle diameter size of the milled mineral trioxide
aggregate.
6. The substance of claim 1, comprising between 1% and 99.9%
untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate.
7. The substance of claim 1, comprising between 25% and 99.5%
untreated mineral trioxide aggregate and between 0.5% and 75%
milled mineral trioxide aggregate.
8. The substance of claim 1, comprising between 40% and 99%
untreated mineral trioxide aggregate and between 1% and 60% milled
mineral trioxide aggregate.
9. The substance of claim 1, comprising between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate.
10. The substance of claim 1, comprising 75% untreated mineral
trioxide aggregate and 25% milled mineral trioxide aggregate.
11. The substance of claim 1, comprising 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate.
12. The substance of claim 2, comprising between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises between 1% and 99.9%
untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate.
13. The substance of claim 2, comprising between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises between 25% and 99.5%
untreated mineral trioxide aggregate and between 0.5% and 75%
milled mineral trioxide aggregate.
14. The substance of claim 2, comprising between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises between 40% and 99%
untreated mineral trioxide aggregate and between 1% and 60% milled
mineral trioxide aggregate.
15. The substance of claim 2, comprising between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate.
16. The substance of claim 2, comprising between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises 75% untreated mineral
trioxide aggregate and 25% milled mineral trioxide aggregate.
17. The substance of claim 2, comprising between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate.
18. The substance of claim 2, comprising between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises between 1% and 99.9%
untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate.
19. The substance of claim 2, comprising between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises between 25% and 99.5%
untreated mineral trioxide aggregate and between 0.5% and 75%
milled mineral trioxide aggregate.
20. The substance of claim 2, comprising between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises between 40% and 99%
untreated mineral trioxide aggregate and between 1% and 60% milled
mineral trioxide aggregate.
21. The substance of claim 2, comprising between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate.
22. The substance of claim 2, comprising between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises 75% untreated mineral
trioxide aggregate and 25% milled mineral trioxide aggregate.
23. The substance of claim 2, comprising between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate.
24. The substance of claim 2, comprising between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises between 1% and 99.9%
untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate.
25. The substance of claim 2, comprising between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises between 25% and 99.5%
untreated mineral trioxide aggregate and between 0.5% and 75%
milled mineral trioxide aggregate.
26. The substance of claim 2, comprising between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises between 40% and 99%
untreated mineral trioxide aggregate and between 1% and 60% milled
mineral trioxide aggregate.
27. The substance of claim 2, comprising between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate.
28. The substance of claim 2, comprising between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises 75% untreated mineral
trioxide aggregate and 25% milled mineral trioxide aggregate.
29. The substance of claim 2, comprising between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate.
30. The substance of claim 2, comprising 75% total mineral trioxide
aggregate and 25% water, where the total mineral trioxide aggregate
comprises 75% untreated mineral trioxide aggregate and 25% milled
mineral trioxide aggregate.
31. The substance of claim 2, comprising 75% total mineral trioxide
aggregate and 25% water, where the total mineral trioxide aggregate
comprises 50% untreated mineral trioxide aggregate and 50% milled
mineral trioxide aggregate.
32. A method for use in general dentistry and in endodontics to
replace natural tooth material, the method comprising: a)
performing a dental procedure; b) providing a substance according
to claim 1; c) using the substance to fill a space in the tooth;
and d) allowing the substance to set.
33-35. (canceled)
36. The method of claim 32, where the dental procedure is selected
from the group consisting of apexification, pulp capping,
pulpotomy, regenerative endodontics, root canal filling, root-end
filling, root perforation repair and sealer during filling or root
canals.
37. A method of making a substance for use in general dentistry and
in endodontics to replace natural tooth material, where the
substance sets in a relatively short time, the method comprising:
a) selecting a material suitable for use in the method to make a
substance for use in general dentistry and in endodontics to
replace natural tooth material, where the material comprises
particles having a median maximum particle diameter; b) mixing the
selected material with a non-aqueous liquid creating a mixture of
the material and liquid; c) providing an instrument for milling by
high shear and impact impingement of particles using high pressure
homogenization; d) placing the mixture of material and liquid into
the instrument for milling by high shear and impact impingement of
particles using high pressure homogenization; and e) actuating the
instrument thereby milling the material within the mixture, thereby
reducing the median maximum particle diameter, and thereby making
the substance for use in general dentistry and in endodontics to
replace natural tooth material.
38. The method of claim 37, where the material is mineral trioxide
aggregate.
39. The method of claim 37, where the liquid is selected from the
group consisting of methanol, ethanol and isopropanol.
40-57. (canceled)
58. A substance made according to the method of claim 37.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present application claims the benefit of U.S.
Provisional Patent Application 61/768,801, titled "Substances and
Method for Replacing Natural Tooth Material," filed Feb. 25, 2013;
U.S. Provisional Patent Application 61/712,058, titled "Substances
and Method for Replacing Natural Tooth Material," filed Oct. 10,
2012; and U.S. Provisional Patent Application 61/613,797, titled
"Substances and Method for Replacing Natural Tooth Material," filed
Mar. 21, 2012; the contents of which are incorporated herein by
reference in their entirety.
BACKGROUND
[0002] Mineral trioxide aggregate (MTA) (sold under the trade names
gray or white ProRoot.RTM. MTA (Dentsply International Inc., York,
Pa., US) is a substance currently used in general dentistry and in
endodontics to replace natural tooth material in apexification,
pulp capping, pulpotomy, regenerative endodontics, root canal
filling, root-end filling and root perforation repair. While
mineral trioxide aggregate has proven to be biocompatible and
suitable for these procedures, mineral trioxide aggregate
disadvantageously takes approximately three hours to set. This
extended time for setting usually requires a patient to return for
a second visit to complete treatment increasing the cost and
inconvenience of treatment. Further disadvantageously, irrigating
the operative field before the mineral trioxide aggregate has set
can evacuate some of the mineral trioxide aggregate thereby
requiring an additional application of mineral trioxide
aggregate.
[0003] Therefore, there is a need for a substance to replace
natural tooth material that is not subject to these
disadvantages.
SUMMARY
[0004] According to one embodiment of the present invention, there
is provided a substance for use in general dentistry and in
endodontics to replace natural tooth material. The substance
comprises untreated mineral trioxide aggregate and milled mineral
trioxide aggregate, where the untreated mineral trioxide aggregate
and milled mineral trioxide aggregate together are total mineral
trioxide aggregate. In one embodiment, the substance further
comprises water. In one embodiment, the untreated mineral trioxide
aggregate comprises a median maximum particle diameter size of
between five and thirty times larger than the median maximum
particle diameter size of the milled mineral trioxide aggregate. In
another embodiment, the untreated mineral trioxide aggregate
comprises a median maximum particle diameter size of between five
and fifteen times larger than the median maximum particle diameter
size of the milled mineral trioxide aggregate. In another
embodiment, the untreated mineral trioxide aggregate comprises a
median maximum particle diameter size of between eight and twelve
times larger than the median maximum particle diameter size of the
milled mineral trioxide aggregate. In one embodiment, the substance
comprises between 1% and 99.9% untreated mineral trioxide aggregate
and between 0.1% and 99% milled mineral trioxide aggregate. In
another embodiment, the substance comprises between 25% and 99.5%
untreated mineral trioxide aggregate and between 0.5% and 75%
milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 40% and 99% untreated mineral trioxide
aggregate and between 1% and 60% milled mineral trioxide aggregate.
In another embodiment, the substance comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate. In another embodiment, the substance
comprises 75% untreated mineral trioxide aggregate and 25% milled
mineral trioxide aggregate. In another embodiment, the substance
comprises 50% untreated mineral trioxide aggregate and 50% milled
mineral trioxide aggregate. In one embodiment, the substance
comprises between 50% and 95% total mineral trioxide aggregate and
between 5% and 50% water, where the total mineral trioxide
aggregate comprises between 1% and 99.9% untreated mineral trioxide
aggregate and between 0.1% and 99% milled mineral trioxide
aggregate. In another embodiment, the substance comprises between
50% and 95% total mineral trioxide aggregate and between 5% and 50%
water, where the total mineral trioxide aggregate comprises between
25% and 99.5% untreated mineral trioxide aggregate and between 0.5%
and 75% milled mineral trioxide aggregate. In another embodiment,
the substance comprises between 50% and 95% total mineral trioxide
aggregate and between 5% and 50% water, where the total mineral
trioxide aggregate comprises between 40% and 99% untreated mineral
trioxide aggregate and between 1% and 60% milled mineral trioxide
aggregate. In another embodiment, the substance comprises between
50% and 95% total mineral trioxide aggregate and between 5% and 50%
water, where the total mineral trioxide aggregate comprises between
45% and 75% untreated mineral trioxide aggregate and between 25%
and 55% milled mineral trioxide aggregate. In another embodiment,
the substance comprises between 50% and 95% total mineral trioxide
aggregate and between 5% and 50% water, where the total mineral
trioxide aggregate comprises 75% untreated mineral trioxide
aggregate and 25% milled mineral trioxide aggregate. In another
embodiment, the substance comprises between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate. In
another embodiment, the substance comprises between 60% and 90%
total mineral trioxide aggregate and between 10% and 40% water,
where the total mineral trioxide aggregate comprises between 1% and
99.9% untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 60% and 90% total mineral trioxide
aggregate and between 10% and 40% water, where the total mineral
trioxide aggregate comprises between 25% and 99.5% untreated
mineral trioxide aggregate and between 0.5% and 75% milled mineral
trioxide aggregate. In another embodiment, the substance comprises
between 60% and 90% total mineral trioxide aggregate and between
10% and 40% water, where the total mineral trioxide aggregate
comprises between 40% and 99% untreated mineral trioxide aggregate
and between 1% and 60% milled mineral trioxide aggregate. In
another embodiment, the substance comprises between 60% and 90%
total mineral trioxide aggregate and between 10% and 40% water,
where the total mineral trioxide aggregate comprises between 45%
and 75% untreated mineral trioxide aggregate and between 25% and
55% milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 60% and 90% total mineral trioxide
aggregate and between 10% and 40% water, where the total mineral
trioxide aggregate comprises 75% untreated mineral trioxide
aggregate and 25% milled mineral trioxide aggregate. In another
embodiment, the substance comprises between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate. In
another embodiment, the substance comprises between 70% and 80%
total mineral trioxide aggregate and between 20% and 30% water,
where the total mineral trioxide aggregate comprises between 1% and
99.9% untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 70% and 80% total mineral trioxide
aggregate and between 20% and 30% water, where the total mineral
trioxide aggregate comprises between 25% and 99.5% untreated
mineral trioxide aggregate and between 0.5% and 75% milled mineral
trioxide aggregate. In another embodiment, the substance comprises
between 70% and 80% total mineral trioxide aggregate and between
20% and 30% water, where the total mineral trioxide aggregate
comprises between 40% and 99% untreated mineral trioxide aggregate
and between 1% and 60% milled mineral trioxide aggregate. In
another embodiment, the substance comprises between 70% and 80%
total mineral trioxide aggregate and between 20% and 30% water,
where the total mineral trioxide aggregate comprises between 45%
and 75% untreated mineral trioxide aggregate and between 25% and
55% milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 70% and 80% total mineral trioxide
aggregate and between 20% and 30% water, where the total mineral
trioxide aggregate comprises 75% untreated mineral trioxide
aggregate and 25% milled mineral trioxide aggregate. In another
embodiment, the substance comprises between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises 50% untreated mineral
trioxide aggregate and 50% milled mineral trioxide aggregate. In
another embodiment, the substance comprises 75% total mineral
trioxide aggregate and 25% water, where the total mineral trioxide
aggregate comprises 75% untreated mineral trioxide aggregate and
25% milled mineral trioxide aggregate. In another embodiment, the
substance comprises 75% total mineral trioxide aggregate and 25%
water, where the total mineral trioxide aggregate comprises 50%
untreated mineral trioxide aggregate and 50% milled mineral
trioxide aggregate.
[0005] According to another embodiment of the present invention,
there is provided a method for use in general dentistry and in
endodontics to replace natural tooth material. The method
comprises: a) performing a dental procedure; b) providing a
substance according to the present invention; c) using the
substance to fill a space in the tooth; and d) allowing the
substance to set. In one embodiment, the dental procedure is an
endodontic procedure. In another embodiment, the dental procedure
comprises removing part of the natural tooth material of a tooth.
In another embodiment, the dental procedure comprises removing
material that replaced natural tooth material. In another
embodiment, the dental procedure is selected from the group
consisting of apexification, pulp capping, pulpotomy, regenerative
endodontics, root canal filling, root-end filling, root perforation
repair and sealer during filling or root canals.
[0006] According to another embodiment of the present invention,
there is provided a method of making a substance for use in general
dentistry and in endodontics to replace natural tooth material,
where the substance sets in a relatively short time. The method
comprises: a) selecting a material suitable for use in the method
to make a substance for use in general dentistry and in endodontics
to replace natural tooth material, where the material comprises
particles having a median maximum particle diameter; b) mixing the
selected material with a non-aqueous liquid creating a mixture of
the material and liquid; c) providing an instrument for milling by
high shear and impact impingement of particles using high pressure
homogenization; d) placing the mixture of material and liquid into
the instrument for milling by high shear and impact impingement of
particles using high pressure homogenization; and e) actuating the
instrument thereby milling the material within the mixture, thereby
reducing the median maximum particle diameter, and thereby making
the substance for use in general dentistry and in endodontics to
replace natural tooth material. In one embodiment, the material is
mineral trioxide aggregate. In one embodiment, the liquid is
selected from the group consisting of methanol, ethanol and
isopropanol. In a preferred embodiment, the liquid is ethanol. In
one embodiment, the material is mixed with the liquid in a ratio of
between 1 part material to between 1 and 100 parts liquid. In
another embodiment, the material is mixed with the liquid in a
ratio of between 1 part material to between 1 and 20 parts liquid.
In another embodiment, the material is mixed with the liquid in a
ratio of between 1 part material to between 5 and 20 parts liquid.
In another embodiment, the material is mixed with the liquid in a
ratio of between 1 part material to between 5 and 10 parts liquid.
In another embodiment, the material is mixed with the liquid in a
ratio of 1 part material to 9 parts liquid. In one embodiment,
mixing the material with a liquid comprises using a magnetic stir
bar to produce a suspension. In one embodiment, placing the mixture
of material and liquid into the instrument comprises pouring the
mixture into a reservoir of the instrument. In one embodiment, the
reservoir comprises a device for preventing premature settling of
the mixture which would cause a concentration gradient within the
instrument or a part of the instrument, and the method further
comprises actuating the device to prevent premature settling of the
mixture which would cause a concentration gradient within the
instrument or a part of the instrument. In one embodiment, the
device is an overhead propeller. In another embodiment, milling the
material within the mixture comprises cycling the instrument
between two and one hundred cycles. In another embodiment, milling
the material within the mixture comprises cycling the instrument
between two and fifty cycles. In another embodiment, milling the
material within the mixture comprises cycling the instrument
between two and thirty cycles. In another embodiment, milling the
material within the mixture comprises cycling the instrument
between five and thirty cycles. In another embodiment, milling the
material within the mixture comprises is using a pressure between
1000 to 70,000 psi. In another embodiment, milling the material
within the mixture comprises is using a pressure of 30,000 psi. In
another embodiment, the method further comprises evaporating the
liquid from the milled material. In another embodiment, the method
further comprises collecting the milled material after milling the
material. According to another embodiment of the present invention,
there is provided a substance made according to the method of the
present invention.
DESCRIPTION
[0007] According to one embodiment of the present invention, there
is provided a substance that sets in a relatively short time for
use in general dentistry and in endodontics to replace natural
tooth material. In one embodiment, the substance comprises
untreated mineral trioxide aggregate and milled mineral trioxide
aggregate (prepared by high shear and impact impingement of
particles using high pressure homogenization). In a preferred
embodiment, the substance comprises untreated mineral trioxide
aggregate, milled mineral trioxide aggregate and water. According
to another embodiment of the present invention, there is provided a
method of making a substance that sets in a relatively short time
for use in general dentistry and in endodontics to replace natural
tooth material. According to another embodiment of the present
invention, there is provided a substance made according to the
present method. According to another embodiment of the present
invention, there is provided a method for use in general dentistry
and in endodontics to replace natural tooth material. In one
embodiment, the method comprises providing a substance according to
the present invention. The substances and method will now be
disclosed in detail.
[0008] As used in this disclosure, except where the context
requires otherwise, the term "comprise" and variations of the term,
such as "comprising," "comprises" and "comprised" are not intended
to exclude other additives, components, integers or steps.
[0009] As used in this disclosure, except where the context
requires otherwise, the method steps disclosed are not intended to
be limiting nor are they intended to indicate that each step is
essential to the method or that each step must occur in the order
disclosed.
[0010] As used in this disclosure, except where indicated
otherwise, "mineral trioxide aggregate," and "untreated mineral
trioxide aggregate," mean the substance generally sold under the
trade name gray or white ProRoot.RTM. MTA (Dentsply International
Inc., York, Pa., US). As will be understood by those with skill in
the art with respect to this disclosure, before mixing with liquid
to cause the untreated mineral trioxide aggregate to set, mineral
trioxide aggregate is mixture of a refined Portland cement and
bismuth oxide, and generally comprises a mixture of bismuth oxide,
dicalcium silicate, tetracalcium aluminoferrite, tricalcium
aluminate and tricalcium silicate. Additionally, "mineral trioxide
aggregate," and "untreated mineral trioxide aggregate," also mean
the substance generally sold under the trade name white
ProRoot.RTM. MTA (Dentsply International Inc., York, Pa., US),
which is similar in composition to gray ProRoot.RTM. MTA except
that white ProRoot.RTM. MTA lacks tetracalcium alumino-ferrite.
[0011] Unless specified otherwise, all ratios given in this
disclosure are by weight.
[0012] As used in this disclosure, "relatively short time" means
between five minutes and twenty minutes, a clinically desirable
setting time for substances that replace natural tooth
material.
[0013] As used in this disclosure, "median maximum particle
diameter size" means that 50% of the sample has a smaller maximum
particle diameter and 50% of the sample has a larger maximum
particle diameter.
[0014] As used in this disclosure, "milled" in reference to
substances and methods of the present invention means "impingement
of particles at high shear rate and impact by high pressure
homogenization."
[0015] According to one embodiment of the present invention, there
is provided a substance for use in general dentistry and in
endodontics to replace natural tooth material. The substance sets
within a tooth in a relatively short time, minutes rather than
hours as is usual for currently used substances. In one embodiment,
the substance comprises untreated mineral trioxide aggregate and
milled mineral trioxide aggregate (prepared by high shear and
impact impingement of particles using high pressure
homogenization). In a preferred embodiment, the substance comprises
untreated mineral trioxide aggregate, milled mineral trioxide
aggregate and water. Mineral trioxide aggregate as currently used,
such as sold under the trade name gray or white ProRoot.RTM. MTA
(Dentsply International Inc., York, Pa., US), was tested to
determine the maximum particle diameter size of the mineral
trioxide aggregate particles before contacting with liquid for
setting. Mineral trioxide aggregate particles (hereinafter referred
to as "untreated mineral trioxide aggregate") were found to have a
maximum particle diameter of between 0.7 and 42.2 microns with a
median of 3.5 microns and a standard deviation of 4.1 microns. A
study was performed to determine the effect of adding mineral
trioxide aggregate that had been milled by high shear and impact
impingement of particles using high pressure homogenization
(hereinafter referred to as "milled mineral trioxide aggregate" in
the context of the present invention) to the setting time of
untreated mineral trioxide aggregate, where milling the mineral
trioxide aggregate reduced the maximum particle diameter to between
0.16 and 2.45 microns with a median of 0.49 microns, and a standard
deviation of 0.5 microns. That is, the untreated mineral trioxide
aggregate had a median maximum particle diameter size approximately
eight times the median maximum particle diameter size of the milled
mineral trioxide aggregate. The study was performed following ISO
standard 6876:1986 for dental materials which specifies the
requirements for dental materials used as filling materials. The
milled mineral trioxide aggregate was prepared as follows. First,
untreated mineral trioxide aggregate (gray ProRoot.RTM. MTA) was
obtained from Dentsply International Inc. (York, Pa., US). The
starting median particle size for the untreated mineral trioxide
aggregate was determined to be 3.8 microns. The untreated mineral
trioxide aggregate was mixed with ethanol in a ratio of 1 to 9 by
weight using a magnetic stir bar to produce a suspension. The
suspension was poured into the reservoir of an M-110EH
Microfluidizer.RTM. (Microfluidics, Newton, Mass., US) with an
overhead propeller mixer also in the reservoir (to prevent
premature settling causing a concentration gradient in the
check-valve of the processor due to the high density of mineral
trioxide aggregate). The suspension was forced at extreme high
pressure through a very small diamond orifice. The high pressures
(up to 40,000 psi/) used delivers the product into the interaction
chamber using a constant pressure pumping system. Precisely
engineered microchannels within the chamber range from 50-500
microns and generate unsurpassed shear and impact forces that cause
homogenization and de-agglomerates the mineral trioxide aggregate
particles. The temperature was regulated by a heat exchanger, and
the lack of moving parts maximizes uptime. The use of M-110EH
Microfluidizer.RTM. equipment forced the entire dispersion through
the same tortuous path, and as a result, produced tighter/smaller
particle size distributions than other technologies. It also
creates a narrower particle size distribution. Next, the suspension
was milled for between five and thirty cycles in a G 10Z (87
microns) diamond Interaction Chamber (IXC) at 30,000 psi and the
maximum particle diameter size was measured during the cycles. In
general, the suspension can be milled for between two and one
hundred cycles. Further in general, the suspension can be milled at
pressure between 1000 to 70,000. The median maximum particle
diameter size of the untreated mineral trioxide aggregate was
reduced to 0.49 microns after fifty passes, thereby producing the
milled mineral trioxide aggregate, or approximately an eight-fold
reduction in median particle size. Next, the ethanol was evaporated
off in an oven at 65.degree. C. and the solids were collected for
analysis of the effects of adding the milled mineral trioxide
aggregate to untreated mineral trioxide aggregate to the setting
time of untreated mineral trioxide aggregate.
[0016] Referring now to Table 1, there are shown the results of
this study.
TABLE-US-00001 TABLE 1 Untreated Mineral Trioxide Aggregate to
Setting Average Milled Mineral Setting Time Setting Time Time
Setting Trioxide Aggregate* Sample #1 Sample #2 Sample #3 Time
100%/0% 02:25:55 02:26:11 03:12:00 02:41:22 75%/25% 00:11:52
00:12:30 00:14:30 00:12:57 50%/50% 00:06:45 00:07:05 00:06:30
00:06:47 0%/100% 00:06:33 00:06:33 00:06:33 00:06:33 *All tests
were done using a ratio of three parts solids (milled mineral
trioxide aggregate and untreated mineral trioxide aggregate) to one
part distilled water (600 mg solids/200 liquid).
As can be seen, combining 75% or 50% with untreated mineral
trioxide aggregate (comprising a maximum particle diameter of
between 0.7 and 42.2 microns with a median of 3.8 microns) with 25%
or 50%, respectively, milled mineral trioxide aggregate (comprising
a maximum particle diameter of between 0.16 and 2.45 microns with a
median of 0.49 microns), and then mixing the combination with one
part water to three parts (combined mineral trioxide aggregate) by
weight reduced setting time from hours to between approximately six
and fourteen minutes. Using one part water with three parts 100%
milled mineral trioxide aggregate by weight also reduced the
setting time to between six to seven minutes similar to the
reduction achieved with the combination of 50% milled mineral
trioxide aggregate and 50% untreated mineral trioxide aggregate in
water; however, as there are costs associated with milling mineral
trioxide aggregate and no apparent advantages with respect to
setting time for increasing the amount of milled mineral trioxide
aggregate in the substance, it is preferred to use the minimum
amount of milled mineral trioxide aggregate in the substance
suitable for reducing setting time to a clinically acceptable
amount as will be understood by those with skill in the art with
respect to this disclosure. Further, because distilled water is
non-toxic in the clinical setting, inexpensive and readily
available, distilled water is preferred as the mineral trioxide
aggregate combination solvent for the substance of the present
invention.
[0017] In one embodiment, the substance according to the present
invention comprises untreated mineral trioxide aggregate and milled
mineral trioxide aggregate by high pressure homogenization. In one
embodiment, the untreated mineral trioxide aggregate comprises a
median maximum particle diameter size of between five and twelve
times larger than the median maximum particle diameter size of the
milled mineral trioxide aggregate. In another embodiment, the
untreated mineral trioxide aggregate comprises a median maximum
particle diameter size of between five and ten times larger than
the median maximum particle diameter size of the milled mineral
trioxide aggregate. In another embodiment, the untreated mineral
trioxide aggregate comprises a median maximum particle diameter
size of between seven and eight times larger than the median
maximum particle diameter size of the milled mineral trioxide
aggregate.
[0018] According to another embodiment of the present invention,
there is provided a substance for use in general dentistry and in
endodontics to replace natural tooth material. The substance sets
within a tooth in a relatively short time, minutes rather than
hours. In one embodiment, the substance comprises a combination of
milled mineral trioxide aggregate, untreated mineral trioxide
aggregate and a liquid. In one embodiment, the liquid is water. In
a preferred embodiment, the water is distilled water. In one
embodiment, the water is selected from the group consisting of
deionized water, filtered water, slurry water and tap water. In
another embodiment, the liquid is a local anesthetic, such as for
example lidocaine hydrochloride, with or without epinephrine
bitartrate. Other local anesthetic can also be used, as will be
understood by those with skill in the art with respect to this
disclosure.
[0019] In one embodiment, the substance comprises between 50% and
95% total mineral trioxide aggregate and between 5% and 50% water,
where the total mineral trioxide aggregate comprises between 1% and
99.9% untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 50% and 95% total mineral trioxide
aggregate and between 5% and 50% water, where the total mineral
trioxide aggregate comprises between 25% and 99.5% untreated
mineral trioxide aggregate and between 0.5% and 75% milled mineral
trioxide aggregate. In one embodiment, the substance comprises
between 50% and 95% total mineral trioxide aggregate and between 5%
and 50% water, where the total mineral trioxide aggregate comprises
between 40% and 99% untreated mineral trioxide aggregate and
between 1% and 60% milled mineral trioxide aggregate. In one
embodiment, the substance comprises between 50% and 95% total
mineral trioxide aggregate and between 5% and 50% water, where the
total mineral trioxide aggregate comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate. In one embodiment, the substance
comprises between 50% and 95% total mineral trioxide aggregate and
between 5% and 50% water, where the total mineral trioxide
aggregate comprises 75% untreated mineral trioxide aggregate and
25% milled mineral trioxide aggregate. In one embodiment, the
substance comprises between 50% and 95% total mineral trioxide
aggregate and between 5% and 50% water, where the total mineral
trioxide aggregate comprises 50% untreated mineral trioxide
aggregate and 50% milled mineral trioxide aggregate.
[0020] In one embodiment, the substance comprises between 60% and
90% total mineral trioxide aggregate and between 10% and 40% water,
where the total mineral trioxide aggregate comprises between 1% and
99.9% untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 60% and 90% total mineral trioxide
aggregate and between 10% and 40% water, where the total mineral
trioxide aggregate comprises between 25% and 99.5% untreated
mineral trioxide aggregate and between 0.5% and 75% milled mineral
trioxide aggregate. In one embodiment, the substance comprises
between 60% and 90% total mineral trioxide aggregate and between
10% and 40% water, where the total mineral trioxide aggregate
comprises between 40% and 99% untreated mineral trioxide aggregate
and between 1% and 60% milled mineral trioxide aggregate. In one
embodiment, the substance comprises between 60% and 90% total
mineral trioxide aggregate and between 10% and 40% water, where the
total mineral trioxide aggregate comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate. In one embodiment, the substance
comprises between 60% and 90% total mineral trioxide aggregate and
between 10% and 40% water, where the total mineral trioxide
aggregate comprises 75% untreated mineral trioxide aggregate and
25% milled mineral trioxide aggregate. In one embodiment, the
substance comprises between 60% and 90% total mineral trioxide
aggregate and between 10% and 40% water, where the total mineral
trioxide aggregate comprises 50% untreated mineral trioxide
aggregate and 50% milled mineral trioxide aggregate.
[0021] In one embodiment, the substance comprises between 70% and
80% total mineral trioxide aggregate and between 20% and 30% water,
where the total mineral trioxide aggregate comprises between 1% and
99.9% untreated mineral trioxide aggregate and between 0.1% and 99%
milled mineral trioxide aggregate. In another embodiment, the
substance comprises between 70% and 80% total mineral trioxide
aggregate and between 20% and 30% water, where the total mineral
trioxide aggregate comprises between 25% and 99.5% untreated
mineral trioxide aggregate and between 0.5% and 75% milled mineral
trioxide aggregate. In one embodiment, the substance comprises
between 70% and 80% total mineral trioxide aggregate and between
20% and 30% water, where the total mineral trioxide aggregate
comprises between 40% and 99% untreated mineral trioxide aggregate
and between 1% and 60% milled mineral trioxide aggregate. In one
embodiment, the substance comprises between 70% and 80% total
mineral trioxide aggregate and between 20% and 30% water, where the
total mineral trioxide aggregate comprises between 45% and 75%
untreated mineral trioxide aggregate and between 25% and 55% milled
mineral trioxide aggregate. In one embodiment, the substance
comprises between 70% and 80% total mineral trioxide aggregate and
between 20% and 30% water, where the total mineral trioxide
aggregate comprises 75% untreated mineral trioxide aggregate and
25% milled mineral trioxide aggregate. In one embodiment, the
substance comprises between 70% and 80% total mineral trioxide
aggregate and between 20% and 30% water, where the total mineral
trioxide aggregate comprises 50% untreated mineral trioxide
aggregate and 50% milled mineral trioxide aggregate.
[0022] In one embodiment, the substance comprises 75% total mineral
trioxide aggregate and 25% water, where the total mineral trioxide
aggregate comprises 75% untreated mineral trioxide aggregate and
25% milled mineral trioxide aggregate. In one embodiment, the
substance comprises 75% total mineral trioxide aggregate and 25%
water, where the total mineral trioxide aggregate comprises 50%
untreated mineral trioxide aggregate and 50% milled mineral
trioxide aggregate.
[0023] According to another embodiment of the present invention,
there is provided a method of making a substance for use in general
dentistry and in endodontics to replace natural tooth material,
where the substance sets in a relatively short time, minutes as
compared to hours. The method comprises milling by high shear and
impact impingement of particles using high pressure homogenization
to reduce particle size thereby producing milled particles, rather
than ball milling as is currently generally used. Ball milling
comprises contacting the particles to be reduced in size with a
grinding media in a chamber, where the grinding media is different
in composition from the particles, and where repeated contact with
the grinding media reduces the size of the particles, thereby
producing milled particles. The grinding media is frequently one or
more than one ball, such as for example one or more than one glass
ball, from which the method is named. By contrast, milling by high
shear and impact impingement of particles using high pressure
homogenization according to the present invention comprises forcing
particles through a channel using pressure, where repeated contact
of the particles to be reduced in size with each other and with the
pressure and the channel walls reduces the size of the particles,
thereby producing milled particles. While milling by high shear and
impact impingement of particles using high pressure homogenization
has been used in other fields, it has never been used in connection
with the preparation of substances for use in general dentistry and
in endodontics to replace natural tooth material. Further, the
method of milling by high shear and impact impingement of particles
using high pressure homogenization according to the present
invention produces milled particles that have unexpected advantages
over all other used methods, in particular decreasing the setting
time of the milled particles, as disclosed in this disclosure, when
the milled particles are used by themselves or when the milled
particles are combined with unmilled particles in general dentistry
and in endodontics to replace natural tooth material. Additionally,
milling by high shear and impact impingement of particles using
high pressure homogenization takes less time to reduce particle
size than ball milling. Further, pieces of the grinding media used
in ball milling can contaminate the milled particles produced as
the grinding media wears, while the method of milling by high shear
and impact impingement of particles using high pressure
homogenization does not use a grinding media that can contaminate
the milled particles produced. Additionally, the particle size
reduction of the milled particles produced by ball milling is less
uniform than the particle size reduction of the milled particles
produced by milling by high shear and impact impingement of
particles using high pressure homogenization, and the decreased
uniformity of the milled particles produced by ball milling
increases their setting time as compared with the setting time for
milled particles produced by milling by high shear and impact
impingement of particles using high pressure homogenization that
have a more uniform size. Further, the particle size of the milled
particles produced by ball milling is generally larger than the
particle size of the milled particles produced by milling by high
shear and impact impingement of particles using high pressure
homogenization, and the larger particle size of the milled
particles produced by ball milling increases their setting time as
compared with the setting time for milled particles that have a
smaller particle size produced by milling by high shear and impact
impingement of particles using high pressure homogenization.
Additionally, instruments used in ball milling are more difficult
to clean in preparation for reuse than instruments used in milling
by high shear and impact impingement of particles using high
pressure homogenization according to the present invention, because
in ball milling the milled particles must be separated from the
grinding media, where in milling by high shear and impact
impingement of particles using high pressure homogenization, the
milled particles are merely flushed out of the instrument as there
is no grinding media. Because of these advantages, milling by high
shear and impact impingement of particles using high pressure
homogenization is more efficient and cost effective than ball
milling for making a substance for use in general dentistry and in
endodontics to replace natural tooth material.
[0024] As disclosed above, the method of making a substance for use
in general dentistry and in endodontics to replace natural tooth
material, where the substance sets in a relatively short time,
minutes as compared to hours, comprises milling by high shear and
impact impingement of particles using high pressure homogenization
to reduce particle size thereby producing milled particles. The
method comprises, first, selecting a material suitable for use in
the method to make a substance for use in general dentistry and in
endodontics to replace natural tooth material, where the material
comprises particles having a median maximum particle diameter. In
one embodiment, the material is mineral trioxide aggregate, such as
for example mineral trioxide aggregate (gray ProRoot.RTM. MTA,
Dentsply International Inc., York, Pa., US).
[0025] Next, the method comprises mixing the selected material with
a liquid creating a mixture of the material and liquid. Water is
generally used in milling by high shear and impact impingement of
particles using high pressure homogenization, however, water cannot
be used in the present method because it would cause the material
to set prematurely. Therefore, the liquid must be non-aqueous. In
one embodiment, the liquid is an alcohol, though any suitable
non-aqueous liquid can be used as will be understood by those with
skill in the art with respect to this disclosure. In one
embodiment, the liquid is selected from the group consisting of
methanol, ethanol and isopropanol. In a preferred embodiment, the
liquid is ethanol. In one embodiment, the material is mixed with
the liquid in a ratio of between 1 part material to between 1 and
100 parts liquid. In one embodiment, the material is mixed with the
liquid in a ratio of between 1 part material to between 1 and 20
parts liquid. In one embodiment, the material is mixed with the
liquid in a ratio of between 1 part material to between 5 and 20
parts liquid. In one embodiment, the material is mixed with the
liquid in a ratio of between 1 part material to between 5 and 10
parts liquid. In one embodiment, the material is mixed with the
liquid in a ratio of 1 part material to 9 parts liquid. In a
preferred embodiment, mixing the material with a liquid comprises
using a magnetic stir bar to produce a suspension.
[0026] Then, the method comprises providing an instrument for
milling by high shear and impact impingement of particles using
high pressure homogenization. In one embodiment, the instrument
provided is an M-110EH Microfluidizer.RTM. (Microfluidics, Newton,
Mass., US), though any suitable instrument for milling by high
shear and impact impingement of particles using high pressure
homogenization can be used, as will be understood by those with
skill in the art with respect to this disclosure.
[0027] Next, the method comprises placing the mixture of material
and liquid into the instrument for milling by high shear and impact
impingement of particles using high pressure homogenization. In one
embodiment, placing the mixture of material and liquid into the
instrument comprises pouring the mixture into a reservoir of the
instrument. In a preferred embodiment, the reservoir comprises a
device for preventing premature settling of the mixture which would
cause a concentration gradient within the instrument or a part of
the instrument, and the method further comprises actuating the
device to prevent premature settling of the mixture which would
cause a concentration gradient within the instrument or a part of
the instrument. In one embodiment, the device is an overhead
propeller.
[0028] Then, the method comprises actuating the instrument thereby
milling the material within the mixture, thereby reducing the
median maximum particle diameter, and thereby making the substance
for use in general dentistry and in endodontics to replace natural
tooth material. In one embodiment, milling the material within the
mixture comprises cycling the instrument between two and one
hundred cycles. In one embodiment, milling the material within the
mixture comprises cycling the instrument between two and fifty
cycles. In one embodiment, milling the material within the mixture
comprises cycling the instrument between two and thirty cycles. In
one embodiment, milling the material within the mixture comprises
cycling the instrument between five and thirty cycles. In one
embodiment, milling the material is performed at a pressure between
1000 to 70,000 psi. In one embodiment, milling the material is
performed at a pressure of 30,000 psi. In one embodiment, the
method further comprises evaporating the liquid from the milled
material. For example, in one embodiment, the liquid is ethanol,
and evaporating the liquid from the milled material comprises
placing the milled material and liquid in an oven at 65.degree. C.
for sufficient time to evaporate the ethanol. In one embodiment,
the method further comprises collecting the milled material after
milling the material.
[0029] According to another embodiment of the present invention,
there is provided a substance made according to the present method.
In one embodiment, the substance is a substance according to the
present invention.
[0030] According to another embodiment of the present invention,
there is provided a method for use in general dentistry and in
endodontics to replace natural tooth material. The method
comprises, first performing a dental procedure. In one embodiment,
the dental procedure is an endodontic procedure. In one embodiment,
the dental procedure comprises removing part of the natural tooth
material of a tooth. In another embodiment, the dental procedure
comprises removing material that replaced natural tooth material.
In a preferred embodiment, the dental procedure is selected from
the group consisting of apexification, pulp capping, pulpotomy,
regenerative endodontics, root canal filling, root-end filling,
root perforation repair and sealer during filling or root canals.
Next, the method comprises providing a substance according to the
present invention. Then, the method comprises using the substance
to fill a space in the tooth, and allowing the substance to
set.
[0031] Although the present invention has been discussed in
considerable detail with reference to certain preferred
embodiments, other embodiments are possible. Therefore, the scope
of the appended claims should not be limited to the description of
preferred embodiments contained in this disclosure. All references
cited herein are incorporated by reference in their entirety.
* * * * *