U.S. patent application number 14/035015 was filed with the patent office on 2015-03-26 for thermally assisted magnetic head, method of manufacturing the same, head gimbal assembly, and hard disk drive.
This patent application is currently assigned to SAE MAGNETICS (H.K.) LTD.. The applicant listed for this patent is Hironori ARAKI, Ryuji FUJII, Hiroyuki ITO, Yoshitaka SASAKI, Kazuki SATO, Shigeki TANEMURA. Invention is credited to Hironori ARAKI, Ryuji FUJII, Hiroyuki ITO, Yoshitaka SASAKI, Kazuki SATO, Shigeki TANEMURA.
Application Number | 20150085629 14/035015 |
Document ID | / |
Family ID | 52683354 |
Filed Date | 2015-03-26 |
United States Patent
Application |
20150085629 |
Kind Code |
A1 |
SASAKI; Yoshitaka ; et
al. |
March 26, 2015 |
THERMALLY ASSISTED MAGNETIC HEAD, METHOD OF MANUFACTURING THE SAME,
HEAD GIMBAL ASSEMBLY, AND HARD DISK DRIVE
Abstract
A thermally assisted magnetic head includes a main magnetic pole
layer, a near-field light generating layer having a generating end
part generating near-field light arranged within a medium-opposing
surface, and an optical waveguide guiding light to the near-field
light generating layer. The near-field light generating layer has a
laminated structure in which a first thin-film metal layer formed
in a thin film form along a direction intersecting the
medium-opposing surface and a second thin-film metal layer formed
in a thin film form and formed using a second metal larger in
hardness than a first metal forming the first thin-film metal layer
are alternately laminated. Further, in the second thin-film metal
layer, a defect part is formed, the defect part is a part smaller
in thickness than another part or is a hole part, and a flat layer
part other than the defect part surrounds the defect part.
Inventors: |
SASAKI; Yoshitaka;
(Milpitas, CA) ; ITO; Hiroyuki; (Milpitas, CA)
; ARAKI; Hironori; (Milpitas, CA) ; TANEMURA;
Shigeki; (Milpitas, CA) ; SATO; Kazuki;
(Milpitas, CA) ; FUJII; Ryuji; (Hong Kong,
CN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
SASAKI; Yoshitaka
ITO; Hiroyuki
ARAKI; Hironori
TANEMURA; Shigeki
SATO; Kazuki
FUJII; Ryuji |
Milpitas
Milpitas
Milpitas
Milpitas
Milpitas
Hong Kong |
CA
CA
CA
CA
CA |
US
US
US
US
US
CN |
|
|
Assignee: |
SAE MAGNETICS (H.K.) LTD.
Hong Kong
CA
HEADWAY TECHNOLOGIES, INC.
Milpitas
|
Family ID: |
52683354 |
Appl. No.: |
14/035015 |
Filed: |
September 24, 2013 |
Current U.S.
Class: |
369/13.33 ;
29/603.07 |
Current CPC
Class: |
G11B 5/3116 20130101;
Y10T 29/49032 20150115; G11B 2005/0021 20130101; G11B 5/3163
20130101; G02B 6/1226 20130101; G11B 5/314 20130101 |
Class at
Publication: |
369/13.33 ;
29/603.07 |
International
Class: |
G11B 5/48 20060101
G11B005/48; G11B 5/127 20060101 G11B005/127 |
Claims
1. A thermally assisted magnetic head comprising a main magnetic
pole layer having a magnetic pole end face arranged within a
medium-opposing surface opposing a magnetic recording medium; a
near-field light generating layer having a generating end part
arranged within the medium-opposing surface, the generating end
part generating near-field light for heating the magnetic recording
medium; and an optical waveguide guiding light to the near-field
light generating layer, wherein the near-field light generating
layer has a laminated structure in which a first thin-film metal
layer formed in a thin film form along a direction intersecting the
medium-opposing surface and a second thin-film metal layer formed
in a thin film form along the direction intersecting the
medium-opposing surface and formed using a second metal larger in
hardness than a first metal forming the first thin-film metal layer
are alternately laminated, and wherein in the second thin-film
metal layer, a defect part is formed, the defect part is a part
smaller in thickness than another part or is a hole part, and a
flat layer part other than the defect part surrounds the defect
part.
2. The thermally assisted magnetic head according to claim 1,
wherein in the near-field light generating layer, at least two
second thin-film metal layers are laminated, and the first
thin-film metal layer is laminated between the two second thin-film
metal layers, and wherein the second thin-film metal layer has a
net-like structure in which a plurality of the defect parts are
scattered not in contact with one another and the flat layer part
surrounds the respective defect parts, the flat layer part
continues without a break due to the defect parts.
3. The thermally assisted magnetic head according to claim 1,
wherein the optical waveguide has a waveguide end face arranged
within the medium-opposing surface, and extends in a depth
direction intersecting the medium-opposing surface from the
waveguide end face, and has an upper end face on a side closer to
the main magnetic pole layer, wherein the thermally assisted
magnetic head further comprises an interposed layer which is in
direct contact with the upper end face of the optical waveguide,
and a closely adhesive layer which makes the near-field light
generating layer closely adhere to the interposed layer, and
wherein in the closely adhesive layer, a closely adhesive layer
defect part similar to the defect part in the second thin-film
metal layer is formed and a closely adhesive layer flat layer part
other than the closely adhesive layer defect part surrounds the
closely adhesive layer defect part.
4. The thermally assisted magnetic head according to claim 2,
wherein the optical waveguide has a waveguide end face arranged
within the medium-opposing surface, and extends in a depth
direction intersecting the medium-opposing surface from the
waveguide end face, and has an upper end face on a side closer to
the main magnetic pole layer, wherein the thermally assisted
magnetic head further comprises an interposed layer which is in
direct contact with the upper end face of the optical waveguide,
and a closely adhesive layer which makes the near-field light
generating layer closely adhere to the interposed layer, and
wherein the closely adhesive layer has a net-like structure in
which a plurality of closely adhesive layer defect parts similar to
the defect parts in the second thin-film metal layer are scattered
not in contact with one another and a closely adhesive layer flat
layer part other than the closely adhesive layer defect parts
surrounds the respective closely adhesive layer defect parts, the
closely adhesive layer flat layer part continues without a break
due to the closely adhesive layer defect parts.
5. The thermally assisted magnetic head according to claim 2,
wherein the second thin-film metal layer has a quasi-honeycomb
structure approximate to a honeycomb structure in which each of the
plurality of defect parts is formed in a hexagonal shape.
6. The thermally assisted magnetic head according to claim 1,
wherein the second thin-film metal layer has an annular structure,
the annular structure is a structure in which a part of the second
thin-film metal layer disposed along an outer peripheral part of it
and distanced at an almost regular interval from the outer
peripheral part is formed as the flat layer part, and only one
defect part is formed inside the flat layer part.
7. The thermally assisted magnetic head according to claim 3,
wherein the closely adhesive layer has an annular structure, the
annular structure is a structure in which a part of the closely
adhesive layer disposed along an outer peripheral part of it and
distanced at an almost regular interval from the outer peripheral
part is formed as the closely adhesive layer flat layer part, and
only one closely adhesive layer defect part is formed inside the
closely adhesive layer flat layer part.
8. The thermally assisted magnetic head according to claim 1,
wherein the first thin-film metal layer is formed to be smaller in
thickness than the second thin-film metal layer.
9. The thermally assisted magnetic head according to claim 4,
wherein in the near-field light generating layer, the second
thin-film metal layer is laminated on the outside most distant from
the optical waveguide.
10. The thermally assisted magnetic head according to claim 1,
wherein in the near-field light generating layer, only a near-field
light generating part having the generating end part on the
magnetic recording medium side has the laminated structure, and a
metal component part formed using the first metal is disposed at a
part more distant from the medium-opposing surface than is the
near-field light generating part.
11. The thermally assisted magnetic head according to claim 1,
wherein in the near-field light generating layer, a sloping surface
sloping with respect to the medium-opposing surface is formed in
the near-field light generating part having the generating end part
on the magnetic recording medium side.
12. The thermally assisted magnetic head according to claim 3,
wherein the optical waveguide has a depression formed on the upper
end face, and wherein the near-field light generating layer is
formed integrally with a metal component part, the metal component
part is formed inside the depression using the first metal.
13. A method of manufacturing a thermally assisted magnetic head
comprising a main magnetic pole layer having a magnetic pole end
face arranged within a medium-opposing surface opposing a magnetic
recording medium; a near-field light generating layer having a
generating end part arranged within the medium-opposing surface,
the generating end part generating near-field light for heating the
magnetic recording medium; and an optical waveguide guiding light
to the near-field light generating layer, comprising a near-field
light generating layer forming step of forming the near-field light
generating layer, the near-field light generating layer forming
step comprising: a first metal layer forming step of forming a
first metal layer in a thin film form along a direction
intersecting the medium-opposing surface; a second metal layer
forming step of forming, on the first metal layer, a second metal
layer in a thin film form along the direction intersecting the
medium-opposing surface using a second metal larger in hardness
than a first metal forming the first metal layer; and a metal layer
defect step of forming a defect part in the second metal layer, the
defect part is a part smaller in thickness than another part or is
a hole part, such that a flat layer part other than the defect part
surrounds the defect part.
14. The method of manufacturing a thermally assisted magnetic head
according to claim 13, wherein the metal layer defect step is
performed such that a plurality of the defect parts are scattered
not in contact with one another and the flat layer part surrounds
the respective defect parts, and the flat layer part continues
without a break due to the defect parts, to make the second metal
layer have a net-like structure composed of the plurality of defect
parts and the flat layer part.
15. The method of manufacturing a thermally assisted magnetic head
according to claim 13, further comprising: an optical waveguide
forming step of forming an optical waveguide on a surface of a
laminated body to have a rectangular parallelepiped-shape part on a
side of a planned opposing surface position which will become the
medium-opposing surface afterward; an interposed layer forming step
of forming an interposed layer using a dielectric substance on an
upper end face of the optical waveguide; a metal thin-film layer
forming step of forming a metal thin-film layer which becomes a
closely adhesive layer afterward, the closely adhesive layer making
the near-field light generating layer closely adhere to the
interposed layer; and a closely adhesive layer defect step of
forming, in the metal thin-film layer, a closely adhesive layer
defect part similar to the defect part in the second metal layer
such that a closely adhesive layer flat layer part other than the
closely adhesive layer defect part surrounds the closely adhesive
layer defect part.
16. The method of manufacturing a thermally assisted magnetic head
according to claim 15, wherein the closely adhesive layer defect
step is performed such that a plurality of the closely adhesive
layer defect parts are scattered not in contact with one another
and the closely adhesive layer flat layer part surrounds the
respective closely adhesive layer defect parts, and the closely
adhesive layer flat layer part continues without a break due to the
closely adhesive layer defect parts to make the metal thin-film
layer have a net-like structure composed of the plurality of
closely adhesive layer defect parts and the closely adhesive layer
flat layer part.
17. The method of manufacturing a thermally assisted magnetic head
according to claim 14, wherein the metal layer defect step is
performed such that each of the plurality of defect parts is formed
in a hexagonal shape to make the second metal layer have a
quasi-honeycomb structure approximate to a honeycomb structure.
18. The method of manufacturing a thermally assisted magnetic head
according to claim 13, wherein the second metal layer forming step
is performed such that the second metal layer is laminated on the
outside most distant from the optical waveguide.
19. A head gimbal assembly comprising a slider having a thermally
assisted magnetic head formed thereon, wherein the thermally
assisted magnetic head comprising: a main magnetic pole layer
having a magnetic pole end face arranged within a medium-opposing
surface opposing a magnetic recording medium; a near-field light
generating layer having a generating end part arranged within the
medium-opposing surface, the generating end part generating
near-field light for heating the magnetic recording medium; and an
optical waveguide guiding light to the near-field light generating
layer, wherein the near-field light generating layer has a
laminated structure in which a first thin-film metal layer formed
in a thin film form along a direction intersecting the
medium-opposing surface and a second thin-film metal layer formed
in a thin film form along the direction intersecting the
medium-opposing surface and formed using a second metal larger in
hardness than a first metal forming the first thin-film metal layer
are alternately laminated, and wherein in the second thin-film
metal layer, a defect part is formed, the defect part is a part
smaller in thickness than another part or is a hole part, and a
flat layer part other than the defect part surrounds the defect
part.
20. A hard disk drive comprising a head gimbal assembly having a
thermally assisted magnetic head, and a magnetic recording medium
opposing the thermally assisted magnetic head, wherein the
thermally assisted magnetic head comprising: a main magnetic pole
layer having a magnetic pole end face arranged within a
medium-opposing surface opposing a magnetic recording medium; a
near-field light generating layer having a generating end part
arranged within the medium-opposing surface, the generating end
part generating near-field light for heating the magnetic recording
medium; and an optical waveguide guiding light to the near-field
light generating layer, wherein the near-field light generating
layer has a laminated structure in which a first thin-film metal
layer formed in a thin film form along a direction intersecting the
medium-opposing surface and a second thin-film metal layer formed
in a thin film form along the direction intersecting the
medium-opposing surface and formed using a second metal larger in
hardness than a first metal forming the first thin-film metal layer
are alternately laminated, and wherein in the second thin-film
metal layer, a defect part is formed, the defect part is a part
smaller in thickness than another part or is a hole part, and a
flat layer part other than the defect part surrounds the defect
part.
Description
BACKGROUND
[0001] 1. Field of the Invention
[0002] The present invention relates to a thermally assisted
magnetic head recording data on a magnetic recording medium by
thermally assisted magnetic recording using near-field light and a
method of manufacturing the same, and a head gimbal assembly and a
hard disk drive each having a thermally assisted magnetic head.
[0003] 2. Related Background Art
[0004] In recent years, as hard disk drives have been increasing
their recording densities, thin-film magnetic heads recording data
on magnetic recording media have been required to further improve
their performances. As the thin-film magnetic heads, those of
composite type having a structure in which a reproducing head
having a magnetoresistive device (hereinafter, referred to also as
an "MR device") for read and a recording head having an
electromagnetic coil device for write are laminated have been
conventionally in wide use. In a magnetic disk drive, the thin-film
magnetic head is provided on a slider which very slightly floats
from the magnetic recording medium.
[0005] Incidentally, the magnetic disk drive records data by
magnetizing magnetic fine particles on the magnetic recording
medium using the recording head. In order to increase the recording
density of the magnetic recording medium, it is effective to make
the magnetic fine particles smaller.
[0006] When the magnetic fine particles are made smaller, however,
there arises a problem that the magnetization thereof becomes
unstable with respect to heat as the particles reduce in volume,
thereby increasing the possibility that the data recorded on the
magnetic recording medium is lost. To solve the problem, it is
effective to increase the magnetic energy of the magnetic fine
particles to thereby enhance the stability of magnetization. When
the magnetic energy of the magnetic fine particles is increased,
however, there arises another problem that the coercive force
(difficulty in reversing magnetization) of the magnetic recording
medium increases to deteriorate the data recording performance.
[0007] To solve such problems, a method called thermally assisted
magnetic recording has been conventionally proposed. When recording
data on a magnetic recording medium having a large coercive force,
the thin-film magnetic head employing the thermally assisted
magnetic recording (hereinafter, referred to as a "thermally
assisted magnetic head") records data while instantaneously heating
and thereby increasing the temperature of a portion of the magnetic
recording medium where data will be recorded.
[0008] Since the magnetic fine particles decrease in coercive force
when the temperature is increased, instantaneous heating makes it
possible to record data even on the magnetic recording medium
having a high coercive force at room temperature. The portion of
the magnetic recording medium where the data has been recorded is
decreased in temperature after the recording of data and thereby
increases in coercive force. Therefore, by using the thermally
assisted magnetic head, it becomes possible to make the magnetic
fine particles finer as well as stabilize recording in the magnetic
disk drive.
[0009] On the other hand, near-field light is used as means for
heating the magnetic recording medium in the conventional thermally
assisted magnetic head. When light enters an opening smaller than
the wavelength of light, the light slightly seeps from the opening
and locally exists near the opening. The light locally existing
near the opening is called near-field light. The near-field light
is confined in a region much smaller than that of a spot light
obtained by collecting light using a lens, so that use of the
near-field light makes it possible to heat only a limited extremely
small recording region of the magnetic recording medium.
[0010] Known as a method of generating the near-field light in the
conventional thermally assisted magnetic head is a method using a
plasmon generator (also called a plasmon probe) that is a minute
metal piece. In this method, the near-field light is generated by
guiding laser light to the plasmon generator via an optical
waveguide.
[0011] As a conventional plasmon generator, a light scattering body
in a triangular thin plate structure is disclosed in Japanese
Patent Application Laid-Open No. 2005-4901 (referred also to as
patent document 1), for example. Further, a plasmon probe made of
metal such as gold, silver, aluminum or the like in the shape of a
triangle pole is disclosed in Japanese Patent Application Laid-Open
No. 2007-257753 (referred also to as patent document 2).
Furthermore, a near-field light generating part in an isosceles
triangle including a tip end reaching a medium-opposing surface is
disclosed in Japanese Patent Application Laid-Open No. 2007-164935
(referred also to as patent document 3). A near-field light
generating part in a triangle pole shape formed on an optical
waveguide is disclosed in Japanese Patent Application Laid-Open No.
2012-3830 (referred also to as patent document 4). A near-field
light generating part in a triangle shape formed on an optical
emitting surface of a medium-opposing surface side of an optical
waveguide is disclosed in Japanese Patent Application Laid-Open No.
2008-257819 (referred also to as patent document 5).
SUMMARY OF THE INVENTION
[0012] As described above, in the conventional thermally assisted
magnetic head, the laser light are guided to the plasmon generator
to excite surface plasmons to generate the near-field light based
on the surface plasmons. This near-field light is used as means for
heating the magnetic recording medium.
[0013] The plasmon generator, however, generates heat in itself
accompanying the generation of the near-field light. In addition,
the plasmon generator has a very small size and made of metal such
as gold, silver, aluminum, palladium or the like and thus causes
self expansion due to its own heat generation. Then, since the
thermally assisted magnetic head has a medium-opposing surface
opposing the magnetic recording medium and the plasmon generator
has a tip end portion reaching the medium-opposing surface, the tip
end portion projects to approach from the medium-opposing surface
to the magnetic recording medium. Thus, the conventional thermally
assisted magnetic head has a problem that the medium-opposing
surface is likely to project and collide with the magnetic
recording medium due to the magnetic recording action.
[0014] Further, the plasmon generator is likely to melt, when it
becomes high temperature due to the self heat generation. Then, the
shape of the plasmon generator changes, and thereby it becomes
difficult that an extremely small recording region of the magnetic
recording medium is heated intensively.
[0015] In addition, after the self-expansion due to the self heat
generation, the plasmon generator shrinks when it's temperature
falls down. On that occasion, a front end face of the plasmon
generator sometimes has receded more than another part of the
medium-opposing surface.
[0016] To increase the recording density in a magnetic recording
apparatus, a smaller spot diameter of the near-field light is more
preferable. To generate the near-field light having a small spot
diameter and sufficient intensity, it is effective to concentrate
much surface plasmons to the tip end part of the plasmon generator.
In such a configuration, however, there is another problem that
though near-field light having a high electric field intensity is
generated from the tip end part, the generated heat also increases
to cause the tip end part to be more likely to project from the
medium-opposing surface and to be more likely to melt.
[0017] In addition, gold or silver is softer than other metals and
thus causes especially the following problem when the plasmon
generator is formed only of gold or silver. Specifically, polishing
for forming the medium-opposing surface is performed in the
manufacturing process of the thermally assisted magnetic head. In
this event, etching is sometimes performed on a portion to be
polished, and the etching sometimes causes the plasmon generator to
recede more than the other part of the medium-opposing surface.
[0018] For the above-described reasons, there is a problem that the
reliability of the thermally assisted magnetic head is low,
especially when the plasmon generator is formed only of gold or
silver.
[0019] The present invention is made to solve the above problems,
and it is an object to provide a thermally assisted magnetic head
having a structure in which projection, melting, deformation and
recess of a plasmon generator is reduced to increase the
reliability of the thermally assisted magnetic head and a method of
manufacturing the same, and a head gimbal assembly and a hard disk
drive each including the thermally assisted magnetic head.
[0020] To solve the above problems, the present invention is a
thermally assisted magnetic head including a main magnetic pole
layer having a magnetic pole end face arranged within a
medium-opposing surface opposing a magnetic recording medium; a
near-field light generating layer having a generating end part
arranged within the medium-opposing surface, the generating end
part generating near-field light for heating the magnetic recording
medium; and an optical waveguide guiding light to the near-field
light generating layer, the near-field light generating layer has a
laminated structure in which a first thin-film metal layer formed
in a thin film form along a direction intersecting the
medium-opposing surface and a second thin-film metal layer formed
in a thin film form along the direction intersecting the
medium-opposing surface and formed using a second metal larger in
hardness than a first metal forming the first thin-film metal layer
are alternately laminated, and in the second thin-film metal layer,
a defect part is formed, the defect part is a part smaller in
thickness than another part or is a hole part, and a flat layer
part other than the defect part surrounds the defect part.
[0021] In the thermally assisted magnetic head, the near-field
light generating layer has a laminated structure in which a first
thin-film metal layer and a second thin-film metal layer are
alternately laminated, a defect part is formed in the second
thin-film metal layer, and a flat layer part other than the defect
part surrounds the defect part. The second thin-film metal layer is
formed using a second metal larger in hardness than a first metal
and thus exerts an effect of stopping deformation of the first
thin-film metal layer, and the defect part is formed in the second
thin-film metal layer to reduce the volume of the second metal
contained in the near-field light generating layer.
[0022] In the above-described thermally assisted magnetic head, it
is preferable that in the near-field light generating layer, at
least two second thin-film metal layers are laminated, and the
first thin-film metal layer is laminated between the two second
thin-film metal layers, and the second thin-film metal layer has a
net-like structure in which a plurality of the defect parts are
scattered not in contact with one another and the flat layer part
surrounds the respective defect parts, the flat layer part
continues without a break due to the defect parts.
[0023] When the second thin-film metal layer has a net-like
structure in which the flat layer part continues without a break
due to the defect parts, the defect parts are arranged in balanced
manner, so that the second thin-film metal layer maintains its
outer shape even if external force is applied thereto from any
direction.
[0024] Further, in the above-described thermally assisted magnetic
head, it is preferable that the optical waveguide has a waveguide
end face arranged within the medium-opposing surface, and extends
in a depth direction intersecting the medium-opposing surface from
the waveguide end face, and has an upper end face on a side closer
to the main magnetic pole layer, the thermally assisted magnetic
head further includes an interposed layer which is in direct
contact with the upper end face of the optical waveguide, and a
closely adhesive layer which makes the near-field light generating
layer closely adhere to the interposed layer, and in the closely
adhesive layer, a closely adhesive layer defect part similar to the
defect part in the second thin-film metal layer is formed and a
closely adhesive layer flat layer part other than the closely
adhesive layer defect part surrounds the closely adhesive layer
defect part.
[0025] The thermally assisted magnetic head has the closely
adhesive layer, whereby the adhesion between the near-field light
generating layer and the interposed layer increases, and thereby it
becomes difficult that the near-field light generating layer
exfoliate from the interposed layer.
[0026] Further, in the above-described thermally assisted magnetic
head, it is preferable that the optical waveguide has a waveguide
end face arranged within the medium-opposing surface, and extends
in a depth direction intersecting the medium-opposing surface from
the waveguide end face, and has an upper end face on a side closer
to the main magnetic pole layer, the thermally assisted magnetic
head further includes an interposed layer which is in direct
contact with the upper end face of the optical waveguide, and a
closely adhesive layer which makes the near-field light generating
layer closely adhere to the interposed layer, and the closely
adhesive layer has a net-like structure in which a plurality of
closely adhesive layer defect parts similar to the defect parts in
the second thin-film metal layer are scattered not in contact with
one another and a closely adhesive layer flat layer part other than
the closely adhesive layer defect parts surrounds the respective
closely adhesive layer defect parts, the closely adhesive layer
flat layer part continues without a break due to the closely
adhesive layer defect parts.
[0027] Further, it is possible that the second thin-film metal
layer has a quasi-honeycomb structure approximate to a honeycomb
structure in which each of the plurality of defect parts is formed
in a hexagonal shape.
[0028] It is possible that the second thin-film metal layer has an
annular structure, the annular structure is a structure in which a
part of the second thin-film metal layer disposed along an outer
peripheral part of it and distanced at an almost regular interval
from the outer peripheral part is formed as the flat layer part,
and only one defect part is formed inside the flat layer part.
[0029] Further, it is possible that the closely adhesive layer has
an annular structure, the annular structure is a structure in which
a part of the closely adhesive layer disposed along an outer
peripheral part of it and distanced at an almost regular interval
from the outer peripheral part is formed as the closely adhesive
layer flat layer part, and only one closely adhesive layer defect
part is formed inside the closely adhesive layer flat layer
part.
[0030] It is preferable that the first thin-film metal layer is
formed to be smaller in thickness than the second thin-film metal
layer.
[0031] It is preferable that in the near-field light generating
layer, the second thin-film metal layer is laminated on the outside
most distant from the optical waveguide.
[0032] Further, in the above-described thermally assisted magnetic
head, it is preferable that in the near-field light generating
layer, only a near-field light generating part having the
generating end part on the magnetic recording medium side has the
laminated structure, and a metal component part formed using the
first metal is disposed at a part more distant from the
medium-opposing surface than is the near-field light generating
part.
[0033] It is also possible that in the near-field light generating
layer, a sloping surface sloping with respect to the
medium-opposing surface is formed in the near-field light
generating part having the generating end part on the magnetic
recording medium side.
[0034] It is also possible that the optical waveguide has a
depression formed on the upper end face, and the near-field light
generating layer is formed integrally with a metal component part,
the metal component part is formed inside the depression using the
first metal.
[0035] Further, the present invention provides a method of
manufacturing a thermally assisted magnetic head including a main
magnetic pole layer having a magnetic pole end face arranged within
a medium-opposing surface opposing a magnetic recording medium; a
near-field light generating layer having a generating end part
arranged within the medium-opposing surface, the generating end
part generating near-field light for heating the magnetic recording
medium; and an optical waveguide guiding light to the near-field
light generating layer, including a near-field light generating
layer forming step of forming the near-field light generating
layer, the near-field light generating layer forming step including
the following steps (1) to (3):
[0036] (1) a first metal layer forming step of forming a first
metal layer in a thin film form along a direction intersecting the
medium-opposing surface
[0037] (2) a second metal layer forming step of forming, on the
first metal layer, a second metal layer in a thin film form along
the direction intersecting the medium-opposing surface using a
second metal larger in hardness than a first metal forming the
first metal layer
[0038] (3) a metal layer defect step of forming a defect part in
the second metal layer, the defect part is a part smaller in
thickness than another part or is a hole part, such that a flat
layer part other than the defect part surrounds the defect
part.
[0039] In the above-described method of manufacturing, it is
preferable that the metal layer defect step is performed such that
a plurality of the defect parts are scattered not in contact with
one another and the flat layer part surrounds the respective defect
parts, and the flat layer part continues without a break due to the
defect parts, to make the second metal layer have a net-like
structure composed of the plurality of defect parts and the flat
layer part.
[0040] In the above-described method of manufacturing, it is
preferable that the method of manufacturing a thermally assisted
magnetic head further including an optical waveguide forming step
of forming an optical waveguide on a surface of a laminated body to
have a rectangular parallelepiped-shape part on a side of a planned
opposing surface position which will become the medium-opposing
surface afterward; an interposed layer forming step of forming an
interposed layer using a dielectric substance on an upper end face
of the optical waveguide; a metal thin-film layer forming step of
forming a metal thin-film layer which becomes a closely adhesive
layer afterward, the closely adhesive layer making the near-field
light generating layer closely adhere to the interposed layer; and
a closely adhesive layer defect step of forming, in the metal
thin-film layer, a closely adhesive layer defect part similar to
the defect part in the second metal layer such that a closely
adhesive layer flat layer part other than the closely adhesive
layer defect part surrounds the closely adhesive layer defect
part.
[0041] Further, it is preferable that the closely adhesive layer
defect step is performed such that a plurality of the closely
adhesive layer defect parts are scattered not in contact with one
another and the closely adhesive layer flat layer part surrounds
the respective closely adhesive layer defect parts, and the closely
adhesive layer flat layer part continues without a break due to the
closely adhesive layer defect parts to make the metal thin-film
layer have a net-like structure composed of the plurality of
closely adhesive layer defect parts and the closely adhesive layer
flat layer part.
[0042] It is possible that the metal layer defect step is performed
such that each of the plurality of defect parts is formed in a
hexagonal shape to make the second metal layer have a
quasi-honeycomb structure approximate to a honeycomb structure.
[0043] In case of the above-described method of manufacturing, it
is preferable that the second metal layer forming step is performed
such that the second metal layer is laminated on the outside most
distant from the optical waveguide.
[0044] Further, the present invention provides a head gimbal
assembly including a slider having a thermally assisted magnetic
head formed thereon, the thermally assisted magnetic head including
a main magnetic pole layer having a magnetic pole end face arranged
within a medium-opposing surface opposing a magnetic recording
medium; a near-field light generating layer having a generating end
part arranged within the medium-opposing surface, the generating
end part generating near-field light for heating the magnetic
recording medium; and an optical waveguide guiding light to the
near-field light generating layer, the near-field light generating
layer has a laminated structure in which a first thin-film metal
layer formed in a thin film form along a direction intersecting the
medium-opposing surface and a second thin-film metal layer formed
in a thin film form along the direction intersecting the
medium-opposing surface and formed using a second metal larger in
hardness than a first metal forming the first thin-film metal layer
are alternately laminated, and in the second thin-film metal layer,
a defect part is formed, the defect part is a part smaller in
thickness than another part or is a hole part, and a flat layer
part other than the defect part surrounds the defect part.
[0045] Further, the present invention provides a hard disk drive
including a head gimbal assembly having a thermally assisted
magnetic head, and a magnetic recording medium opposing the
thermally assisted magnetic head, the thermally assisted magnetic
head including a main magnetic pole layer having a magnetic pole
end face arranged within a medium-opposing surface opposing the
magnetic recording medium; a near-field light generating layer
having a generating end part arranged within the medium-opposing
surface, the generating end part generating near-field light for
heating the magnetic recording medium; and an optical waveguide
guiding light to the near-field light generating layer, the
near-field light generating layer has a laminated structure in
which a first thin-film metal layer formed in a thin film form
along a direction intersecting the medium-opposing surface and a
second thin-film metal layer formed in a thin film form along the
direction intersecting the medium-opposing surface and formed using
a second metal larger in hardness than a first metal forming the
first thin-film metal layer are alternately laminated, and in the
second thin-film metal layer, a defect part is formed, the defect
part is a part smaller in thickness than another part or is a hole
part, and a flat layer part other than the defect part surrounds
the defect part.
[0046] The present invention will be more fully understood from the
detailed description given hereinbelow and the accompanying
drawings which are given by way of illustration only, and thus are
not to be considered as limiting the present invention.
BRIEF DESCRIPTION OF THE DRAWINGS
[0047] FIG. 1 is a sectional view of the thermally assisted
magnetic head in accordance with an embodiment of the present
invention taken along the line 1-1 of FIG. 2, which is a direction
intersecting with an air bearing surface (which will hereinafter be
referred also to as "ABS");
[0048] FIG. 2 is a front view illustrating the ABS of the thermally
assisted magnetic head;
[0049] FIG. 3 is a perspective view illustrating principal parts of
a near-field light generating layer, a closely adhesive layer, an
interposed layer and an optical waveguide;
[0050] FIG. 4 is a sectional view of the near-field light
generating layer and closely adhesive layer taken along the line
4-4 in FIG. 3;
[0051] FIG. 5 is an exploded perspective view of the near-field
light generating layer and closely adhesive layer, which are
partially omitted;
[0052] FIG. 6 is a plan view of a second thin-film metal layer;
[0053] FIG. 7 is a sectional view taken along the line 7-7 in FIG.
6;
[0054] FIG. 8 is a plan view of the closely adhesive layer;
[0055] FIG. 9 is a sectional view similar to FIG. 1, illustrating
principal part of the thermally assisted magnetic head in
accordance with an embodiment of the present invention;
[0056] FIG. 10 is a front view similar to FIG. 2, illustrating
principal part of the thermally assisted magnetic head in
accordance with an embodiment of the present invention;
[0057] FIG. 11 is a plan view illustrating principal parts of the
near-field light generating layer, the interposed layer, the
optical waveguide and a heat sink;
[0058] FIG. 12 is a view illustrating a process of manufacturing
the thermally assisted magnetic head in accordance with an
embodiment of the present invention, in which (A) is a sectional
view corresponding to FIG. 1, (B) is a front view corresponding to
FIG. 2;
[0059] FIG. 13 is a view illustrating a process subsequent to that
in FIG. 12, in which (A) is a sectional view corresponding to FIG.
1, (B) is a front view corresponding to FIG. 2;
[0060] FIG. 14 is a view illustrating a process subsequent to that
in FIG. 13, in which (A) is a sectional view corresponding to FIG.
1, (B) is a front view corresponding to FIG. 2;
[0061] FIG. 15 is a view illustrating a process subsequent to that
in FIG. 14, in which (A) is a sectional view corresponding to FIG.
1, (B) is a front view corresponding to FIG. 2;
[0062] FIG. 16 is a view illustrating a process subsequent to that
in FIG. 15, in which (A) is a sectional view corresponding to FIG.
1, (B) is a front view corresponding to FIG. 2;
[0063] FIG. 17 is a sectional view illustrating a principal part of
a process subsequent to that in FIG. 16 (A);
[0064] FIG. 18 is a plan view corresponding to FIG. 17;
[0065] FIG. 19 is a sectional view illustrating a principal part of
a process subsequent to that in FIG. 17;
[0066] FIG. 20 is a plan view corresponding to FIG. 19;
[0067] FIG. 21 is a sectional view illustrating a principal part of
a process subsequent to that in FIG. 19;
[0068] FIG. 22 is a plan view corresponding to FIG. 21;
[0069] FIG. 23 is a sectional view illustrating a principal part of
a process subsequent to that in FIG. 21;
[0070] FIG. 24 is a plan view corresponding to FIG. 23;
[0071] FIG. 25 is a sectional view illustrating a principal part of
a process subsequent to that in FIG. 23;
[0072] FIG. 26 is a plan view corresponding to FIG. 25;
[0073] FIG. 27 is a perspective view illustrating the near-field
light generating layer and closely adhesive layer according to a
modified example 1;
[0074] FIG. 28 is a perspective view illustrating the near-field
light generating layer and closely adhesive layer according to a
modified example 2;
[0075] FIG. 29 is a perspective view illustrating principal parts
of the near-field light generating layer, the interposed layer and
optical waveguide;
[0076] FIG. 30 is a sectional view of the near-field light
generating layer and closely adhesive layer taken along the line
30-30 in FIG. 29;
[0077] FIG. 31 is a perspective view illustrating principal parts
of the near-field light generating layer, closely adhesive layer,
the interposed layer and optical waveguide;
[0078] FIG. 32 is a sectional view of the thermally assisted
magnetic head, corresponding to FIG. 9, having the near-field light
generating layer illustrated in FIG. 31;
[0079] FIG. 33 is a sectional view of the thermally assisted
magnetic head, corresponding to FIG. 9, having the near-field light
generating layer according to a modified example 5;
[0080] FIG. 34 is a sectional view of the thermally assisted
magnetic head, corresponding to FIG. 9, having the near-field light
generating layer according to another modified example 5;
[0081] FIG. 35 is a plan view of the second thin-film metal layer
according to a modified example 6;
[0082] FIG. 36 (A) is a plan view illustrating the second thin-film
metal layer 180 according to a modified example, FIG. 36 (B) is a
plan view illustrating the second thin-film metal layer 181
according to a modified example;
[0083] FIG. 37 is a perspective view illustrating the near-field
light generating layer and closely adhesive layer according to a
modified example 7;
[0084] FIG. 38 is an exploded perspective view of the near-field
light generating layer and closely adhesive layer according to a
modified example 7, which are partially omitted;
[0085] FIG. 39 is an exploded perspective view of the near-field
light generating layer and another closely adhesive layer according
to a modified example 7, which are partially omitted;
[0086] FIG. 40 is a perspective view illustrating principal parts
of the near-field light generating layer, interposed layer and
optical waveguide according to a modified example 8; and
[0087] FIG. 41 (a) is a perspective view illustrating a hard disk
drive equipped with a thermally assisted magnetic head in FIG. 1,
FIG. 41 (b) is a perspective view illustrating a rear side of
HGA.
DETAILED DESCRIPTION OF THE EMBODIMENTS
[0088] In the following, embodiments of the present invention will
be described with reference to the drawings. Note that the same
components will be referred to with the same numerals or letters,
while omitting their overlapping descriptions.
(Structures of Thermally Assisted Magnetic Head)
[0089] To begin with, the structure of a thermally assisted
magnetic head will be explained with reference to FIG. 1 to FIG.
11.
[0090] Here, FIG. 1 is a sectional view of a thermally assisted
magnetic head 100 in accordance with an embodiment of the present
invention taken along the line 1-1 of FIG. 2, which is a direction
intersecting with an air bearing surface (which will hereinafter be
referred also to as "ABS"), while FIG. 2 is a front view
illustrating an ABS 101 of the thermally assisted magnetic head
100. FIG. 3 is a perspective view illustrating principal parts of a
near-field light generating layer 28, a closely adhesive layer 37,
an interposed layer 18 and an optical waveguide 31. FIG. 4 is a
sectional view of the near-field light generating layer 28 and
closely adhesive layer 37 taken along the line 4-4 in FIG. 3, FIG.
5 is an exploded perspective view of the near-field light
generating layer 28 and the closely adhesive layer 37, which are
partially omitted. Further, FIG. 6 is a plan view of a second
thin-film metal layer 39A, FIG. 7 is a sectional view taken along
the line 7-7 in FIG. 6. FIG. 8 is a plan view of the closely
adhesive layer 37. FIG. 9 is a sectional view similar to FIG. 1,
illustrating principal part of the thermally assisted magnetic head
100. FIG. 10 is a front view similar to FIG. 2, illustrating
principal part of the thermally assisted magnetic head 100. FIG. 11
is a plan view illustrating principal parts of the near-field light
generating layer 28, the interposed layer 18, the optical waveguide
31 and a heat sink 35.
[0091] In the thermally assisted magnetic head 100, the near-field
light generating layer 28 has, as illustrated in FIG. 3 to FIG. 5,
a laminated structure in which first thin-film metal layers 38 and
second thin-film metal layers 39 are alternately laminated.
Further, the second thin-film metal layer 39 is formed using a
second metal such as Zr, Ru, Ta or the like larger in hardness than
the first thin-film metal layer 38, so that the near-field light
generating layer 28 is higher in mechanical strength and less
likely to be deformed than a near-field light generating layer (not
illustrated) formed using only a first metal such as Au, Ag or the
like. In addition, defect parts 58 are formed in the second
thin-film metal layer 39 and a flat layer part 59 surrounds the
defect parts 58, whereby the volume of the second metal contained
in the near-field light generating layer 28 is reduced, resulting
in a reduction of the volume of heat generation in the second
thin-film metal layers 39. Therefore, projection, melting,
deformation and recess of the near-field light generating layer 28
is reduced, and deformation, melting, and chipping of a main
magnetic pole layer 40 arranged close thereto is also reduced.
[0092] Note that the right and left direction in FIG. 2 is the
track width direction, the upper direction is the moving direction
of a magnetic recording medium, and the direction perpendicular to
the paper surface is the direction perpendicular to the surface of
the magnetic recording medium.
[0093] Thermally assisted magnetic head 100 comprises a substrate
1, reproducing head and recording head laminated on the substrate
1, while having the ABS 101 as a medium-opposing surface opposing a
magnetic recording medium, as illustrated in FIG. 1.
[0094] The following will explain structures of main parts of the
thermally assisted magnetic head 100, while structures of parts
other than the main parts will later be explained in manufacturing
processes.
[0095] The reproducing head has an MR device 5, arranged near the
ABS 101, for detecting a magnetic signal. The reproducing head
comprises a lower shield layer 3, a lower shield gap film 4, an
upper shield gap film 6 and an upper shield layer 7.
[0096] An insulating layer 2 is further formed on the substrate 1,
and the lower shield layer 3 made of a magnetic material is formed
on the insulating layer 2. The lower shield gap film 4 as an
insulating film is further formed on the lower shield layer 3, and
the upper shield gap film 6 shielding the MR device 5 is formed on
the lower shield gap film 4. The upper shield layer 7 made of a
magnetic material is formed on the upper shield gap film 6, and an
insulating layer 8 is formed on the upper shield layer 7.
[0097] The MR device 5 is constituted by a magnetosensitive film
exhibiting a magnetoresistive effect, such as AMR (anisotropic
magnetoresistive), GMR (giant magnetoresistive), and TMR (tunneling
magnetoresistive) devices.
[0098] The GMR device may be of a CIP (Current In Plane) type or a
CPP (Current Perpendicular to Plane) type. In the CIP type, current
for detecting a magnetic signal flows in a direction almost
parallel to planes of the layers constituting the GMR device. In
the CPP type, current for detecting a magnetic signal flows in a
direction almost perpendicular to planes of the layers constituting
the GMR device.
[0099] Next, the recording head will be explained. The recording
head has a lower thin-film coil 11, a shield magnetic pole layer
20, the interposed layer 18, the near-field light generating layer
28, the optical waveguide 31, the closely adhesive layer 37, the
main magnetic pole layer 40, a yoke magnetic pole layer 41, a
linking magnetic pole layer 42 and an upper thin-film coil 51, and
has a structure in which they are stacked on the substrate 1.
[0100] The lower thin-film coil 11 has three turn parts. The
respective turn parts are insulated from each other by a
photoresist 15. The lower thin-film coil 11 is wound like a flat
spiral about the linking magnetic pole layer 42 of the shield
magnetic pole layer 20.
[0101] The lower thin-film coil 11 is connected to the upper
thin-film coil 51. The upper thin-film coil 51 has also three turn
parts. The upper thin-film coil 51 is wound like a flat spiral
about the yoke magnetic pole layer 41.
[0102] Further, a current modulated according to data to be
recorded on the magnetic recording medium flows through the lower
thin-film coil 11 and upper thin-film coil 51, the current causes
the lower thin-film coil 11 and upper thin-film coil 51 to generate
a recording magnetic field.
[0103] The shield magnetic pole layer 20 has a shield layer 21, a
connecting magnetic pole layer 22 and a linking magnetic pole layer
23.
[0104] The shield layer 21 has an end face arranged within the ABS
101. The shield layer 21 is junctioned to the connecting magnetic
pole layer 22 on a side closer to the ABS 101 than is the lower
thin-film coil 11.
[0105] The connecting magnetic pole layer 22 has an end face
arranged within the ABS 101 and has a part that is more distant
from the ABS 101 than is the end face being embedded in the
insulating layer 8. Further, to the connecting magnetic pole layer
22, the shield layer 21 is junctioned on the side closer to the ABS
101 than is the lower thin-film coil 11, and the linking magnetic
pole layer 23 is junctioned at a position more distant from the ABS
101 than is the three turn parts of the lower thin-film coil
11.
[0106] The linking magnetic pole layer 23 is arranged at a position
more distant from the ABS 101 than is the three turn parts of the
lower thin-film coil 11, and is junctioned to the connecting
magnetic pole layer 22.
[0107] The shield magnetic pole layer 20 is provided to return a
magnetic flux to the main magnetic pole layer 40. When a magnetic
flux generated by the recording magnetic field is emitted from a
later-described magnetic pole end face 40a of the main magnetic
pole layer 40 to the magnetic recording medium, the magnetic flux
flows back to the shield magnetic pole layer 20 via the magnetic
recording medium (a not-depicted soft magnetic layer in detail).
This magnetic flux passes through the linking magnetic pole layer
23 and reaches the main magnetic pole layer 40.
[0108] The interposed layer 18 is in direct contact with an upper
end face 31b of the optical waveguide 31. The interposed layer 18
is formed using a dielectric substance having a lower refractive
index than that of the optical waveguide 31, and for example, using
alumina (Al.sub.2O.sub.3). The interposed layer 18 has a thickness
of, for example, about 10 nm to about 70 nm, which is much smaller
than those of the main magnetic pole layer 40 and the optical
waveguide 31, and is thus referred also to as a very-thin
interposed layer. Further, the near-field light generating layer 28
is formed on the interposed layer 18 via the closely adhesive layer
37.
[0109] The near-field light generating layer 28 has, as illustrated
in FIG. 3 to FIG. 10, a first thin-film metal layers 38 and a
second thin-film metal layers 39, and has a laminated structure
which the first thin-film metal layers 38 and the second thin-film
metal layers 39 are laminated alternatively. Further, the
near-field light generating layer 28 has a generating end part 28a
which generates a near-field light. The generating end part 28a is
arranged within the ABS 101. The generating end part 28a generates
a near-field light for heating the magnetic recording medium.
[0110] The near-field light generating layer 28 has three first
thin-film metal layers 38A, 38B, 38C as the first thin-film metal
layers 38 and three second thin-film metal layers 39A, 39B, 39C as
the second thin-film metal layers 39. The second thin-film metal
layer 39A is laminated between the first thin-film metal layers
38A, 38B, and the second thin-film metal layer 39B is laminated
between the first thin-film metal layers 38B, 38C. Further, in the
near-field light generating layer 28, the second thin-film metal
layer 39C is laminated on the outside most distant from the optical
waveguide 31.
[0111] Every one of the first thin-film metal layers 38A, 38B, 38C
is formed in a thin-film form along a direction intersecting the
ABS 101 (a direction perpendicularly intersecting the ABS 101), and
formed equal in shape and thickness. Every one of the second
thin-film metal layers 39A, 39B, 39C is also formed in a thin-film
form along the direction intersecting the ABS 101 and formed equal
in shape and thickness.
[0112] The first thin-film metal layers 38A, 38B, 38C are formed
using the first metal. The first metal here is a metal having a low
resistivity and a high conductivity and can be, for example, any
one of Au, Ag, Al, Cu.
[0113] The second thin-film metal layers 39A, 39B, 39C are formed
using the second metal. The second metal is a metal having a
hardness (Vickers hardness is assumed in this embodiment but
another index may be used) higher than that of the first metal and
can be, for example, any one of Ru, Zr, ZrN, Ta, Mo, Pt, Cr, Ni,
Fe, Pd, Ti, NiCr, TiW, TiN, Hf. The second metal is higher in
mechanical strength than the first metal. Note that when the first
metal is a metal other than Cu, Cu can be used as the second
metal.
[0114] Further, the thickness of the first thin-film metal layer
38A, 38B, 38C is, for example, about 5 nm to about 20 nm, whereas
the thickness of the second thin-film metal layer 39A, 39B, 39C is,
for example, about 0.3 nm to about 5 nm, preferably, about 0.2 nm
to about 0.6 nm. Therefore, the second thin-film metal layers 39A,
39B, 39C are formed to be smaller in thickness than the first
thin-film metal layers 38A, 38B, 38C.
[0115] Further, in each of the second thin-film metal layers 39A,
39B, 39C, a plurality (about 10 to 20 in FIG. 3) of defect parts 58
are formed to be scattered not in contact with one another. Each of
the defect parts 58 is a part that is smaller in thickness than the
other part or is a hole part. The thickness of each defect part 58
is about 0 nm to about 0.2 nm.
[0116] In every one of the second thin-film metal layers 39A, 39B,
39C, the flat layer part 59 surrounds almost all of the plurality
of defect parts 58. The flat layer part 59 is a part other than the
defect parts 58 in each of the second thin-film metal layers 39A,
39B, 39C and is a flat part having a fixed thickness. The flat
layer part 59 continues without a break due to the defect parts 58,
so that each of the second thin-film metal layers 39A, 39B, 39C is
thus formed as one layer.
[0117] The second thin-film metal layer 39A, 39B, 39C has a
structure like a net-like pattern because of the plurality of
defect parts 58 scattered as illustrated in FIG. 3. The structure
like the net-like pattern is called a net-like structure in this
embodiment.
[0118] Note that since a defect part 58 is arranged at a portion of
the peripheral part of the second thin-film metal layer 39A, 39B,
39C in FIG. 3, the defect part 58 is far from being surrounded by
the flat layer part 59. However, the whole peripheries of many
other defect parts 58 are surrounded by the flat layer part 59.
[0119] In FIG. 3, the plurality of defect parts 58 in the second
thin-film metal layer 39C are illustrated. The defect parts 58 are
scattered in the second thin-film metal layer 39C and form
respective hole parts having no thickness (namely, penetrating from
the front side to the rear side). Therefore, the front surface of
the first thin-film metal layer 38C arranged under the defect parts
58 is exposed inside each of the defect parts 58 (dots in FIG. 3
illustrate the front surface of the first thin-film metal layers
38C).
[0120] Every one of the defect parts 58 illustrated in FIG. 3, FIG.
5 and the like is formed in an approximately oval shape. The defect
parts 58 are non-uniform in size and shape and are not unified. An
arrangement spot has no regularity and is thus irregular.
[0121] In the second thin-film metal layers 39A, 39B, 39C, the
defect parts 58 are able to be unified in size, shape, arrangement
spot, unlike the illustrated case, but may not be unified as in the
illustrated case. However, in each of the second thin-film metal
layers 39A, 39B, 39C, it is preferable to arrange the defect parts
58 in a manner to evenly disperse them as much as possible without
unevenly distributing them at a specific spot, namely, to scatter
the plurality of the defect parts 58 as illustrated in FIG. 3.
[0122] The near-field light generating layer 28 closely adheres to
the interposed layer 18 with the closely adhesive layer 37. The
closely adhesive layer 37 is formed to make the near-field light
generating layer 28 closely adhere to the interposed layer 18 so as
to prevent the near-field light generating layer 28 from
exfoliating from the interposed layer 18.
[0123] The closely adhesive layer 37 has an outer shape in common
with the first thin-film metal layer 38A, the second thin-film
metal layer 39A and the like, and formed in a thin-film form having
a thickness of about 0.3 nm to about 1 nm. The closely adhesive
layer 37 is formed using, for example, a third metal such as Zr,
Ti, Cr, Ta, W. The third metal is known as a closely adhesive
material with a property of making the first metal such as Au, Ag
or the like closely adhere to alumina (Al.sub.2O.sub.3).
[0124] As illustrated in FIG. 5, a plurality of closely adhesive
layer defect parts 88 similar to the defect parts 58 are formed in
the closely adhesive layer 37. The closely adhesive layer defect
parts 88 are formed to be scattered not in contact with one
another. Also in the closely adhesive layer 37, a closely adhesive
layer flat layer part 89 surrounds almost all of the plurality of
closely adhesive layer defect parts 88. The closely adhesive layer
flat layer part 89 is a part other than the closely adhesive layer
defect parts 88 of the closely adhesive layer 37 and is a flat part
having a fixed thickness. The closely adhesive layer flat layer
part 89 continues without a break due to the closely adhesive layer
defect parts 88, so that the closely adhesive layer 37 is formed as
one layer. The closely adhesive layer 37 also has a net-like
structure because of the plurality of scattered closely adhesive
layer defect parts 88.
[0125] Note that the closely adhesive layer defect parts 88 can be
made similar to the defect parts 58 in size, shape, arrangement
spot but may be made different therefrom.
[0126] On the other hand, a surrounding dielectric substance layer
32 is filled in the surrounding space of the near-field light
generating layer 28, as illustrated in FIG. 1, FIG. 2, FIG. 9. The
surrounding dielectric substance layer 32 is formed using a
dielectric substance such as alumina or the like.
[0127] Further, the near-field light generating layer 28 has a part
whose width along the ABS 101 (lateral width) is fixed, and a part
whose width gradually increases as it is distanced more from the
ABS 101 (wider part). Further, a heat sink 35 is connected to the
wider part. The heat sink 35 is formed of a material having a high
thermal conductivity, such as Au, Ag, Al, Cu or the like.
[0128] The optical waveguide 31 has, as illustrated in FIG. 3, the
waveguide end face 31a arranged within the ABS 101. Further, the
optical waveguide 31 extends from the ABS 101 in a direction
perpendicular to the ABS 101 (referred also to as a depth
direction), and the optical waveguide 31 is formed to approach from
the rear side to the ABS 101 passing through (penetrating) the
linking magnetic pole layer 42. The optical waveguide 31 has the
upper end face 31b on the main magnetic pole layer 40 side.
[0129] The optical waveguide 31 is formed using a dielectric
substance which transmits laser light, such as Ta.sub.2O.sub.5 or
the like and has a thickness of about 0.4 .mu.m to about 1.5 .mu.m.
An optical fiber 208 is connected to the optical waveguide 31, as
illustrated in FIG. 41. Laser light generated by a semiconductor
laser 207 are inputted to the optical waveguide 31 via the optical
fiber 208. Note that the semiconductor laser 207 and the optical
fiber 208 are illustrated in FIG. 41 (both of them will be
described later in detail).
[0130] Next, the main magnetic pole layer 40 will be explained with
reference to FIG. 1 and FIG. 2. The main magnetic pole layer 40 is
arranged on an upper side of the near-field light generating layer
28 (side distant from the substrate 1). The main magnetic pole
layer 40 has a magnetic pole end face 40a arranged within the ABS
101. Further, the main magnetic pole layer 40 opposes to the
generating end part 28a via a dielectric substance layer 29 within
the ABS 101 and is formed to decrease its height along the ABS 101,
as it is distanced more from the ABS 101. The upper end part of the
main magnetic pole layer 40 is a flat surface along the
intersecting direction, the yoke magnetic pole layer 41 is
connected to the flat surface.
[0131] Further, the main magnetic pole layer 40 have a symmetrical
structure in width direction formed to be bilaterally symmetrical
about part thereof opposed to the generating end part 28a.
[0132] The yoke magnetic pole layer 41 is arranged in a position
recedes from the ABS 101. The yoke magnetic pole layer 41 is
junctioned to a flat upper side part of the main magnetic pole
layer 40. Further, the yoke magnetic pole layer 41 extends along
the depth direction, and is connected to the linking magnetic pole
layer 42 straddling the upper thin-film coil 51 and the insulating
layer 52. The upper surface of yoke magnetic pole layer 41 (surface
of the side distant from the substrate 1) is partially formed
flat.
[0133] The linking magnetic pole layer 42 is connected to the yoke
magnetic pole layer 41 at a position distant from the ABS 101 than
are the three turn parts of the upper thin-film coil 51. Further,
the linking magnetic pole layer 42 is arranged in a manner to hold
the optical waveguide 31 and the interposed layer 18 from both
right and left sides.
[0134] The linking magnetic pole layer 42 is a magnetic pole layer
magnetically links the shield magnetic pole layer 20 to the yoke
magnetic pole layer 41. The linking magnetic pole layer 42 has a
role of returning, to the main magnetic pole layer 40, the magnetic
flux flown back to the shield magnetic pole layer 20.
(Operation Contents of Thermally Assisted Magnetic Head)
[0135] Subsequently, the magnetic recording operation of the
thermally assisted magnetic head having the above structure will be
explained as follows.
[0136] When a current modulated according to data to be recorded on
the magnetic recording medium is caused to flow through the lower
thin-film coil 11 and upper thin-film coil 51, the current
generates a recording magnetic field. The recording magnetic field
passes through the main magnetic pole layer 40, and a magnetic flux
caused by the recording magnetic field is emitted from the magnetic
pole end face 40a to the magnetic recording medium. With this
magnetic flux, the data is recorded on the magnetic recording
medium.
[0137] On the other hand, when the semiconductor laser 207
generates laser light, the laser light are transmitted to the
optical waveguide 31 via the optical fiber 208. The laser light
move through the optical waveguide 31 to the ABS 101. Since the
interposed layer 18 is formed so as to cover with the outer face of
the optical waveguide 31, and the near-field light generating layer
28 is formed outside of the interposed layer 18, the laser light is
applied to the near-field light generating layer 28 via the
interposed layer 18.
[0138] Further, the interposed layer 18 having a lower refractive
index than that of optical waveguide 31 is in contact with the
optical waveguide 31. Therefore, when laser light enter the
interposed layer 18 having lower refractive index from the optical
waveguide 31 having higher refractive index and are totally
reflected, evanescent light seeps near the surface of the
interposed layer 18 having a lower refractive index. The use of the
evanescent light makes it possible to match the phase speed thereof
with the phase speed of surface plasmons and excite surface
plasmons.
[0139] The surface plasmons propagate to the generating end part
28a of the near-field light generating layer 28. The surface
plasmons are concentrated on the generating end part 28a. Then, a
near-field light having a very high electric field intensity is
generated near the generating end part 28a.
[0140] The near-field light is applied from the generating end part
28a to the magnetic recording medium and reaches the surface of the
magnetic recording medium. Then, a limited extremely small region
in the magnetic recording layer of the magnetic recording medium is
intensively heated by the near-field light. In the magnetic
recording layer, the coercive force reduces to an extent at which
data is able to be recorded by the magnetic flux caused by the
recording magnetic field.
[0141] In the thermally assisted magnetic head 100, the coercive
force is able to be reduced in the above-descried manner, so that
data can be recorded also on a magnetic recording medium having a
high coercive force for high-density recording.
[0142] (Operation and Effect of the Thermally Assisted Magnetic
Head)
[0143] The near-field light generating layer 28 generates the
near-field light when the thermally assisted magnetic head 100
performs the above-described magnetic recording operation.
[0144] Now, a case, where a near-field light generating layer is
formed using only Au or Ag as in the conventional thermally
assisted magnetic head, is considered. In the near-field light
generating layer, a temperature increase occurs accompanying
generation of near-field light, thus causing self expansion.
[0145] Since Au or Ag is particularly higher in coefficient of
thermal expansion than other metals, the near-field light
generating layer largely expands accompanying the generation of
near-field light to project from the ABS when the near-field light
generating layer is formed using only Au or Ag. Thus, in the
conventional thermally assisted magnetic head, collision with the
magnetic recording medium is likely to occur and the hard disk
drive is likely to fail. Further, when temperature decreases, the
near-field light generating layer shrinks and a front end surface
of the near-field light generating layer sometimes recedes from the
ABS. In addition, if the heat generated by the near-field light
generating layer is conducted to the main magnetic pole layer, the
heat may deform or chip a portion on the ABS side of the main
magnetic pole layer.
[0146] On the other hand, since Au or Ag is not so high in melting
point as compared with other metals, the near-field light
generating layer highly possibly melts or deforms accompanying an
increase in temperature.
[0147] In the thermally assisted magnetic head 100 according to the
embodiment of the present invention, however, the near-field light
generating layer 28 has the above-described laminated structure and
the defect parts 58 and the flat layer part 59 are formed in the
second thin-film metal layer 39, so that the operation and effect
described below can be provided to solve the above problems.
[0148] First, in the near-field light generating layer 28, the
first thin-film metal layer 38 is formed using the first metal such
as Au, Ag, Al, Cu or the like as in the conventional near-field
light generating layer, whereas the second thin-film metal layer 39
is formed using the second metal. The second metal is composed of
Ru, Zr, Pt, Pd, ZrN or the like which is higher in hardness
(Vickers hardness) and mechanical strength than the first metal,
and so the second metal is higher in stiffness.
[0149] For this reason, the second thin-film metal layer 39 is less
likely to be deformed than the first thin-film metal layer 38. The
second thin-film metal layer 39 is included in the near-field light
generating layer 28, so that the near-field light generating layer
28 increases in mechanical strength as a whole.
[0150] Furthermore, the second thin-film metal layers 39 and the
first thin-film metal layers 38 are alternately laminated and are
in direct contact with each other, so that even if the first
thin-film metal layer 38 tries to deform, the second thin-film
metal layer 39 displays an operation of stopping the deformation.
This makes it possible to suppress as much as possible the
deformation of the near-field light generating layer 28 due to its
own heat generation and to prevent as much as possible the
projection thereof from the ABS 101.
[0151] Further, even if the second thin-film metal layer 39 is
included in the near-field light generating layer 28, the first
thin-film metal layer 38 high in electric conductivity is included
in the near-field light generating layer 28 and can thus make the
near-field light generating layer 28 efficiently generate
near-field light.
[0152] The second metal (for example, Zr), however, is higher in
hardness than the first metal (for example, Au) but lower in
thermal conductivity than the first metal (for example, Au).
Therefore, the second metal (for example, Zr) is less likely to
conduct heat to the outside than the first metal. Accordingly, the
second thin-film metal layer 39 is more likely to accumulate heat
inside thereof than the first thin-film metal layer 38.
[0153] When the second thin-film metal layer 39 is included in part
of the near-field light generating layer 28, the near-field light
generating layer 28 will generate more heat, as a whole, than the
conventional near-field light generating layer including no second
metal.
[0154] When the near-field light generating layer 28 generates more
heat, surface plasmons excited thereby will decrease. To compensate
for the decrease, the output of the semiconductor laser 207 needs
to be increased. Then, laser light with higher energy is guided
into the near-field light generating layer 28, resulting in an
increase in heat generation by the near-field light generating
layer 28.
[0155] To improve such a situation, in the thermally assisted
magnetic head 100 according to the embodiment of the present
invention, the defect parts 58 and the flat layer part 59 are
formed in the second thin-film metal layer 39 constituting the
near-field light generating layer 28.
[0156] As has been described above, the defect parts 58 are parts
that are smaller in thickness than the other part or are hole
parts. Therefore, the defect parts 58 are formed in the second
thin-film metal layer 39, whereby the volume of the second metal
contained in the near-field light generating layer 28 is smaller
than that in the case of not including the defect parts 58. When
the second metal lower in thermal conductivity than the first metal
is decreased in volume, the heat remaining in the second thin-film
metal layer 39 is accordingly decreased, whereby the volume of heat
generation in the near-field light generating layer 28 is able to
be reduced as a whole.
[0157] Accordingly, the near-field light generating layer 28 can be
prevented from melting, deforming, and projecting from the ABS 101
due to its own heat generation.
[0158] This eliminates the situation in which the generating end
part 28a melts and deforms, and therefore the generating end part
28a is able to heat surely the very small recording region of the
magnetic recording medium. Therefore a reliability of the thermally
assisted magnetic head 100 is able to be increased.
[0159] Further, in the thermally assisted magnetic head 100, the
main magnetic pole layer 40 is arranged very near the near-field
light generating layer 28, and the heat generated at the near-field
light generating layer 28 unlikely to reach the main magnetic pole
layer 40. Therefore, chipping and deformation of the main magnetic
pole layer 40 are also able to be effectively prevented.
[0160] On the other hand, when the defect parts 58 are not formed
in the second thin-film metal layer 39, the second thin-film metal
layer 39 comes to be in contact with the entire front surface and
rear surface of the first thin-film metal layer 38, thereby
possibly decreasing the generation efficiency of the near-field
light.
[0161] However, since the defect parts 58 are formed in the second
thin-film metal layer 39, the portion of the first thin-film metal
layer 38 with which the second thin-film metal layer 39 comes into
contact is smaller than that in the case where the defect parts 58
are not formed. Accordingly, the near-field light generating layer
28 is configured such that it does not decrease so much in
generation efficiency of the near-field light though it includes
the second thin-film metal layer 39.
[0162] Further, the thermally assisted magnetic head 100 is able to
prevent a situation that the near-field light generating layer 28
projects from the ABS 101, and thus is able to prevent failure of
the hard disk drive.
[0163] On the other hand, in the second thin-film metal layer 39,
the peripheries of the plurality of defect parts 58 are surrounded
by the flat layer part 59. Therefore, in the near-field light
generating layer 28, the volume of the second metal is reduced
while the mechanical strength of the second thin-film metal layer
39 is substantially maintained as a whole.
[0164] Especially, the near-field light generating layer 28 has the
net-like structure in which the flat layer part 59 continues
without a break and the defect parts 58 are arranged in balanced
manner as a whole in the second thin-film metal layer 39.
Therefore, the second thin-film metal layer 39 is one thin film
though the volume of the second metal is small. Accordingly, the
second thin-film metal layer 39 can maintain its outer shape as a
whole even if external force is applied thereto from any
direction.
[0165] If the flat layer part 59 is broken by the defect parts 58,
for example, if the flat layer part 59 is divided into two parts by
the defect parts 58, the second thin-film metal layer 39 may become
difficult to maintain its outer shape depending on the direction in
which the external force is applied thereto. Then, the function of
stopping the deformation of the first thin-film metal layer 38 by
the second thin-film metal layer 39 decreases to make it also
difficult to prevent deformation and the like of the near-field
light generating layer 28 due to its own heat generation.
[0166] Hence, the near-field light generating layer 28 is made such
that the second thin-film metal layer 39 is formed in the net-like
structure in which the flat layer part 59 continues without a break
due to the defect parts 58 so that the second thin-film metal layer
39 can maintain its outer shape as a whole.
[0167] In addition, in the near-field light generating layer 28, at
least two second thin-film metal layers 39 are laminated and the
first thin-film metal layer 38 is laminated between them.
Therefore, the near-field light generating layer 28 has a structure
in which the first thin-film metal layer 38 which is comparatively
soft, is covered from the outside by the second thin-film metal
layers 39 which are high in mechanical strength. Accordingly, the
mechanical strength of the near-field light generating layer 28 can
be made higher as a whole.
[0168] Further, the second thin-film metal layer 39 has the
net-like structure by the plurality of defect parts 58, and the
defect parts 58 are substantially evenly arranged without being
unevenly distributed at a portion in the second thin-film metal
layer 39. Therefore, there is no part that is relatively low in
mechanical strength in second thin-film metal layer 39. Even if the
volume of the second metal is reduced, the mechanical strength of
the second thin-film metal layer 39 is maintained as a whole.
[0169] Furthermore, the near-field light generating layer 28 is
formed on the interposed layer 18 via the closely adhesive layer 37
so as to avoid such a situation that the near-field light
generating layer 28 exfoliates from them. The closely adhesive
layer 37 is formed using the third metal and is formed also with
the closely adhesive layer defect parts 88 and the closely adhesive
layer flat layer part 89. Therefore, the volume of the closely
adhesive layer 37 is also reduced while the mechanical strength is
maintained as a whole. Accordingly, since accumulation of heat in
the closely adhesive layer 37 is also suppressed, the heat
conducted from the closely adhesive layer 37 to the near-field
light generating layer 28 is reduced.
[0170] Further, since the second thin-film metal layer 39 is formed
to be smaller in thickness than the first thin-film metal layer 38,
the proportion of the second thin-film metal layer 39 with a lower
thermal conductivity in the near-field light generating layer 28 is
able to be decreased. This makes it possible to reduce the volume
of heat generation in the near-field light generating layer 28 as a
whole.
[0171] In the near-field light generating layer 28, the second
thin-film metal layer 39C is laminated on the outside most distant
from the optical waveguide 31. If the second thin-film metal layer
39C is not laminated, the second thin-film metal layer in contact
with the outside of the first thin-film metal layer 38C no longer
exists, and the function of stopping the deformation of the first
thin-film metal layer 38C possibly decreases. However, since the
second thin-film metal layer 39C is laminated in the near-field
light generating layer 28, there is no such possibility.
[0172] (Method of Manufacturing Thermally Assisted Magnetic
Head)
[0173] Next, a method of manufacturing the thermally assisted
magnetic head 100 having the structure mentioned above will now be
explained with reference to FIG. 12 (A), (B) to FIG. 16 (A), (B)
and FIG. 17 to FIG. 26 together with FIG. 1 and FIG. 2 mentioned
above.
[0174] Here, FIG. 12(A) to FIG. 16(A) are sectional views
corresponding to FIG. 1 in the processes of manufacturing the
thermally assisted magnetic head 100, and FIG. 12(B) to FIG. 16(B)
are front views corresponding to FIG. 2 in the processes of
manufacturing the thermally assisted magnetic head 100. In each
drawing, the left end face in (A) indicates a position (a planned
opposing surface position) which will become the ABS 101 afterward.
Further, FIG. 17, 19, 21, 23, 25 are sectional views illustrating
principal part in the subsequent processes of FIG. 16 (A) in order.
FIG. 18, 20, 22, 24, 26 are plan views corresponding to FIG. 17,
19, 21, 23, 25 respectively.
[0175] First, the substrate 1 made of a ceramic material such as
aluminum oxide-titanium carbide (Al.sub.2O.sub.3.TiC) is prepared.
Subsequently, as shown in FIG. 12 (A), (B), the insulating layer 2
made of an insulating material such as alumina (Al.sub.2O.sub.3),
the lower shield layer 3 made of a magnetic material and the lower
shield gap film 4 are successively laminated on the substrate
1.
[0176] Next, the upper shield gap film 6 is formed by an insulating
material such as to shield the MR device 5. Here, an undepicted
lead connected to the MR device 5 is formed, and the MR device 5
and lead are covered with the upper shield gap film 6. Thereafter,
using a magnetic material, the upper shield layer 7 is formed on
the upper shield gap film 6.
[0177] Then, on the upper shield layer 7, the insulating layer 8 is
formed using an insulating material such as alumina
(Al.sub.2O.sub.3) or the like. Thereafter, a portion of the
insulating layer 8 which is located on the planned opposing surface
position side is removed, and the connecting magnetic pole layer 22
is formed using a magnetic material such as CoNiFe, CoFe, NiFe,
CoFeN or the like.
[0178] Then, as illustrated in FIG. 13(A), (B), an insulating layer
14 is formed on the whole surface of the laminated body using an
insulating material such as alumina (Al.sub.2O.sub.3) or the like,
and parts of the insulating layer 14, that the shield layer 21 and
the linking magnetic pole layer 23 are formed, are removed.
[0179] Then, the shield layer 21 and the linking magnetic pole
layer 23 are formed at the opened parts of the insulating layer 14
in the surface of the laminated body, for example, by the frame
plating method.
[0180] Next, as illustrated in FIG. 14(A), FIG. 14(B), an
insulating layer 16 (having a thickness of about 0.02 .mu.m to 0.3
.mu.m, preferably about 0.1 .mu.m to 0.2 .mu.m) made of alumina
(Al.sub.2O.sub.3) is formed on the whole surface of the laminated
body by CVD (Chemical Vapor Deposition) according to an atomic
layer method. The insulating layer 16 is formed so as to cover the
shield layer 21 and the linking magnetic pole layer 23.
[0181] Then, a conductor layer for forming the lower thin-film coil
11 is formed between the shield layer 21 and the linking magnetic
pole layer 23 by the frame plating method. Next, a photoresist
layer 91 (having a thickness of about 1.5 .mu.m to 2.5 .mu.m) is
formed so as to fill up the interstice part of the conductor layer.
Next, an insulating film 26 adapted to cover the surface of the
laminated body is formed using alumina (Al.sub.2O.sub.3) by a
thickness of about 3 .mu.m to 4 .mu.m. Subsequently, the surface of
the laminated body is polished by CMP until the shield layer 21 and
the linking magnetic pole layer 23 emerge, so as to become
flat.
[0182] Then, as illustrated in FIG. 15(A), (B), flattening step of
the shield layer 21 and the linking magnetic pole layer 23 together
with the conductor layer is performed. By this, the lower thin-film
coil 11 and the photoresist 15 are formed.
[0183] Subsequently, as illustrated in FIG. 16(A), (B), an
insulating layer 17 adapted to cover the surface of the laminated
body is formed using alumina (Al.sub.2O.sub.3). Then, an optical
waveguide forming step is performed. In this step, the optical
waveguide 31 is formed on the surface of the laminated body, as
illustrated in FIG. 1. The optical waveguide 31 is formed using a
dielectric substance such as Ta.sub.2O.sub.5 or the like
transmitting the laser light. The optical waveguide 31 is formed to
have a rectangular parallelepiped-shape part on the planned
opposing surface position side.
[0184] Next, a first dielectric substance layer forming step is
performed. In this step, a dielectric substance layer 19 is formed
on the surface of the laminated body, using a dielectric substance
such as alumina or the like.
[0185] Subsequently, a flattening step is performed. In this step,
the surface of the laminated body is polished by chemical
mechanical polishing (hereinafter, referred to as "CMP") until a
surface of the optical waveguide 31 emerges, so as to be made
flat.
[0186] Next, an interposed layer forming step is performed. In this
step, the interposed layer 18 is formed on the whole surface of the
laminated body, including the upper end face 31b of the optical
waveguide 31, for example, by the atomic layer deposition, using a
dielectric substance such as alumina or the like.
[0187] Next, a metal thin-film layer forming step and a closely
adhesive layer defect step are performed. A metal thin-film layer
65 which becomes the closely adhesive layer afterward is formed in
the metal thin-film layer forming step, as illustrated in FIG. 17,
18. This metal thin-film layer 65 is able to be formed with the
above-described third metal by sputtering, for example.
[0188] Subsequent to the metal thin-film layer forming step, the
closely adhesive layer defect step is performed. In this step, the
plurality of closely adhesive layer defect parts 88 are formed in
the metal thin-film layer 65 as illustrated in FIG. 19, FIG. 20. In
this case, the closely adhesive layer defect parts 88 are formed
such that the closely adhesive layer flat layer part 89 surrounds
the plurality of closely adhesive layer defect parts 88
respectively and the closely adhesive layer flat layer part 89
continues without a break. Thus, the closely adhesive layer defect
step is performed so that the metal thin-film layer 65 has the
above-described net-like structure and will become the closely
adhesive layer 37 afterward.
[0189] The closely adhesive layer defect step can be performed, for
example, by the electron beam irradiation method. The electron beam
irradiation method is performed as follows. First, electrons are
generated in vacuum and accelerated. Then, the group of the
electrons are focused into a thin flux of high energy using a
not-illustrated electromagnetic lens and applied to a workpiece.
This instantaneously melts the irradiated part and vaporizes and
removes it.
[0190] The above electron beam irradiation method is used to remove
portions of the metal thin-film layer 65 to form the plurality of
closely adhesive layer defect parts 88. In this case, the plurality
of closely adhesive layer defect parts 88 are formed not to be
uneven in size, shape and arrangement spot.
[0191] Subsequently, the near-field light generating layer 28 is
formed by performing a near-field light generating layer forming
step. This near-field light generating layer forming step has a
first metal layer forming step, a second metal layer forming step
and a metal layer defect step.
[0192] To begin with, a first metal layer forming step is
performed. In this first metal layer forming step, a first metal
layer 66 having thin-film like form is formed, as illustrated in
FIG. 21, FIG. 22. The first metal layer 66 is formed along the
direction intersecting the ABS 101, and it becomes the first
thin-film metal layer 38A afterward. The first metal layer 66 is
able to be formed with the above-described first metal for example,
by sputtering.
[0193] Subsequently, a second metal layer forming step is
performed. In this second metal layer forming step, a second metal
layer 67 having thin-film like form is formed on the first metal
layer 66, as illustrated in FIG. 23, FIG. 24. The second metal
layer 67 is formed along the direction intersecting the ABS 101,
and it becomes the second thin-film metal layer 39A afterward. The
second metal layer 67 is able to be formed with the above-described
second metal for example, by sputtering.
[0194] Thereafter, the metal layer defect step is performed on the
second metal layer 67. In the metal layer defect step, the
plurality of defect parts 58 are formed in the second metal layer
67 as illustrated in FIG. 23, FIG. 24. In this case, the defect
parts 58 are formed such that the flat layer part 59 surrounds the
plurality of defect parts 58 respectively and the flat layer part
59 continues without a break. Thus, the metal layer defect step is
performed so that the second metal layer 67 has the net-like
structure composed of the plurality of defect parts 58 and the flat
layer part 59. The metal layer defect step can be performed, for
example, by the electron beam irradiation method as in the closely
adhesive layer defect step.
[0195] Next, the first metal layer forming step is performed again.
In this step, a first metal layer 68 having thin-film like form is
formed, as illustrated in FIG. 25, FIG. 26. The first metal layer
68 will become the first thin-film metal layer 38B afterward.
[0196] Thereafter, the second metal layer forming step is performed
to form a second metal layer 69 which will become the second
thin-film metal layer 39B afterward. Subsequently, the metal layer
defect step is performed on the second metal layer 69 to form the
plurality of defect parts 58. Further, the first metal layer
forming step is performed again to form a first metal layer 70
which will become the first thin-film metal layer 38C afterward.
Thereafter, the second metal layer forming step is performed again
to form a second metal layer 71 which will become the second
thin-film metal layer 39C afterward. By forming the second metal
layer 71, the second metal layer forming step is performed such
that the second metal layer 71 is laminated on the outside most
distant from the optical waveguide 31. Then, the metal layer defect
step is performed on the second metal layer 71 to form the
plurality of defect parts 58. Thus, a metal laminated part 72 which
will become the near-field light generating layer 28 afterward is
formed.
[0197] Next, a photomask is formed on the metal laminated part 72
using a photoresist and then, for example, RIE or ion beam etching
is performed using the photomask to pattern the metal laminated
part 72. By removing an unnecessary portion of the metal laminated
part 72 in this manner, the above-described near-field light
generating layer 28 is formed.
[0198] Next, as illustrated in FIG. 1, the surrounding insulating
layer 32 is formed using an insulating material such as alumina
(Al.sub.2O.sub.3) or the like on the surface of the laminated body.
Subsequently, the surface of the laminated body is polished by CMP
until the surface of the near-field light generating layer 28
emerges.
[0199] Subsequently, the heat sink 35 is formed so as to cover a
part of the near-field light generating layer 28 and a part of the
surrounding insulating layer 32.
[0200] Next, an insulating layer 33 is formed so as to cover the
heat sink 35. Next, an insulating layer 29 is formed so as to cover
the insulating layer 33. After that, etching is performed
selectively to the interposed layer 18 and the insulating layers
32, 33, 29.
[0201] Next, the main magnetic pole layer 40 is formed on the ABS
101 side of the insulating layer 29, and the linking magnetic pole
layer 42 is formed on a part distanced from the ABS 101.
[0202] After that, an insulating layer 49 is formed on the whole
surface of the laminated body. The surface of the laminated body is
polished by CMP afterward, until the surfaces of the main magnetic
pole layer 40 and the linking magnetic pole layer 42 emerge.
Furthermore, the upper thin-film coil 51 is formed on the
insulating layer 49. After that, an insulating layer 52 is formed
so as to cover the upper thin-film coil 51.
[0203] Then, the yoke magnetic pole layer 41 is formed so as to
cover the main magnetic pole layer 40, the linking magnetic pole
layer 42 and the insulating layer 52. After that, a protective
insulating layer 60 is formed on the surface of the laminated body
so as to cover the yoke magnetic pole layer 41. After that, the
thermally assisted magnetic head 100 having the above-described
structure is manufactured by being formed the ABS 101.
Modified Example 1
[0204] Successively, the near-field light generating layer 128 in
accordance with modified example illustrated in FIG. 27 will be
explained. FIG. 27 is a perspective view illustrating the
near-field light generating layer 128 and closely adhesive layer 37
according to a modified example. The near-field light generating
layer 128 is different in that it has second thin-film metal layers
139 (139A, 139B, 139C) in place of the second thin-film metal
layers 39 (39A, 39B, 39C), as compared with the near-field light
generating layer 28.
[0205] The respective second thin-film metal layers 139A, 139B,
139C are different in that a plurality of defect parts 158 are
formed in place of the plurality of defect parts 58 as compared
with the respective second thin-film metal layers 39A, 39B,
39C.
[0206] In the case of the above-described near-field light
generating layer 28, every one of the plurality of defect parts 58
is formed in an approximately oval shape but non-uniform in size
and shape, and thus has no regularity in arrangement spot.
[0207] In contrast to the above, every one of the plurality of
defect parts 158 is formed in a hexagonal shape and their size are
also unified except for a part of them. Further, the vertical and
lateral intervals thereof are unified and the directions in which
they are arranged are also unified. The number of arranged defect
parts 158 regularly changes to be one, two, three, four toward the
direction more distant from the ABS 101 side so that the defect
parts 158 have regularity also in arrangement spot.
[0208] By forming the plurality of defect parts 158, the second
thin-film metal layer 139A, 139B, 139C has a structure approximate
to the honeycomb structure (also referred to as a quasi-honeycomb
structure).
[0209] Generally, the honeycomb structure is a structure in which
regular hexagons are arranged without gap therebetween, and is
known as a structure which can maintain the strength of the member
formed with the structure while reducing its volume. The second
thin-film metal layer 139A, 139B, 139C has the quasi-honeycomb
structure approximate to the honeycomb structure, so that the
volume of the material constituting the respective second thin-film
metal layer, namely, the second metal can be reduced even though it
can maintain the strength.
[0210] Accordingly, since the volume of the second metal is
reduced, the volume of heat generation can further be suppressed in
the near-field light generating layer 128, and it can be more
efficiently prevented from melting, deforming, and projecting due
to heat generation.
Modified Example 2
[0211] Next, the near-field light generating layer 148 in
accordance with modified example illustrated in FIG. 28 will be
explained. FIG. 28 is a perspective view illustrating the
near-field light generating layer 148 and closely adhesive layer
37. The near-field light generating layer 148 is different in that
it has first thin-film metal layers 138 (38A, 38B, 138C) in place
of the first thin-film metal layers 38 (38A, 38B, 38C), and it has
second thin-film metal layers 140 (139A, 139B, 140C) in place of
the second thin-film metal layers 139 (139A, 139B, 139C) as
compared with the above-described near-field light generating layer
128.
[0212] The first thin-film metal layers 138 are different in that
they have a first thin-film metal layer 138C in place of the first
thin-film metal layer 38C as compared with the first thin-film
metal layers 38. The first thin-film metal layer 138C is different
in that a sloping surface 138Ca is formed on the ABS 101 side as
compared with the first thin-film metal layer 38C.
[0213] The second thin-film metal layers 140 are different in that
they have second thin-film metal layer 140C in place of the second
thin-film metal layer 139C. The second thin-film metal layer 140C
is different in that a sloping surface 140Ca is formed on the ABS
101 side as compared with the second thin-film metal layer
139C.
[0214] In the near-field light generating layer 148, the second
thin-film metal layers 139A, 139B, 140C have the quasi-honeycomb
structure as in the near-field light generating layer 128, so that
the volume of the second metal constituting the respective second
thin-film metal layer can be reduced even though it can maintain
the strength. Accordingly, the near-field light generating layer
148 can also suppress its own volume of heat generation and can be
more efficiently prevented from melting, deforming, and projecting
due to heat generation as with the near-field light generating
layer 128.
[0215] To efficiently generate the near-field light by the
near-field light generating layer 128, it is desirable to have the
plurality of first thin-film metal layers 38A, 38B, 38C which are
formed to be large in thickness as in the near-field light
generating layer 128.
[0216] This, however, increases the thickness of the near-field
light generating layer 128 as a whole, so that the near-field light
generating layer 128 exposed to the ABS 101 may increase in height.
This makes it difficult to keep the height of the near-field light
generating layer 128 exposed to the ABS 101 in a fixed size.
[0217] In this case, it is desirable to form sloping surfaces like
the sloping surfaces 138Ca, 140Ca on the ABS 101 side as in the
near-field light generating layer 148. Formation of the sloping
surfaces like the sloping surfaces 138Ca, 140Ca makes it possible
to keep the height of the near-field light generating layer 148
exposed to the ABS 101 in a fixed size while the near-field light
generating layer 148 is made large in height.
Modified Example 3
[0218] Further, in the thermally assisted magnetic head 100 in
accordance with an embodiment of the present invention, a
near-field light generating layer 149 illustrated in FIG. 29, FIG.
30 may be formed in place of the near-field light generating layer
28.
[0219] The near-field light generating layer 149 is different in
that it has a protective layer 141 in place of the second thin-film
metal layer 39C as compared with the above-described near-field
light generating layer 28. The protective layer 141 is a layer for
preventing a material constituting the first thin-film metal layer
38C from diffusing. The protective layer 141 is formed of a
dielectric substance. The protective layer 141 is able to form with
either one of SiO.sub.2, alumina, MgO, ZrO.sub.2, Amorphous SiC for
example.
[0220] The protective layer 141 is not formed with the plurality of
defect parts 58 unlike the second thin-film metal layer 39C, but
the near-field light generating layer 149 has the second thin-film
metal layers 39A, 39B each having the plurality of defect parts 58
and the flat layer part 59. Accordingly, the near-field light
generating layer 149 is also able to suppress its own volume of
heat generation and is able to be prevented from melting,
deforming, and projecting due to heat generation.
Modified Example 4
[0221] Further, in the thermally assisted magnetic head 100 in
accordance with an embodiment of the present invention, a
near-field light generating layer 151 illustrated in FIG. 31 to
FIG. 32 may be formed in place of the near-field light generating
layer 149.
[0222] The near-field light generating layer 151 is different in
that it has a metal component part 150 as compared with the
above-described near-field light generating layer 149. The metal
component part 150 is disposed at a part distanced from the ABS
101, in the first thin-film metal layers 38B, 38C and second
thin-film metal layers 39A, 39B. The metal component part 150 is
formed of the first metal. The second thin-film metal layers 39A,
39B made of the second metal are arranged on the ABS 101 side of
the near-field light generating layer 151. Therefore, in the
near-field light generating layer 151, mechanical strength is able
to increase in a part which influence due to melting and
deformation likely to occur, and prevent from deforming and
projecting.
[0223] Further, the volume of the second metal in the near-field
light generating layer 151 is reduced as compared with that in the
near-field light generating layer 149 because the metal component
part 150 is disposed. In addition to that, the second thin-film
metal layer 39A, 39B have the net-like structure to further reduce
the volume of the second metal contained in the near-field light
generating layer 151.
Modified Example 5
[0224] Further, in the thermally assisted magnetic head 100 in
accordance with an embodiment of the present invention, a
near-field light generating layer 152 illustrated in FIG. 33 may be
formed in place of the near-field light generating layer 28.
[0225] The near-field light generating layer 152 is different in
that it has a metal component part 160 as compared with the
above-described near-field light generating layer 28. The metal
component part 160 is formed with the above-described first metal.
The metal component part 160 is formed in a depression 31c of the
optical waveguide 31. The depression 31c is formed on the upper end
face 31b of the optical waveguide 31. The interposed layer 18 is
inserted in the depression 31c, and the metal component part 160 is
formed on the interposed layer 18. The metal component part 160 is
connected to the first thin-film metal layer 38 (38A) on the
substrate 1 side of the near-field light generating layer 152.
[0226] The near-field light generating layer 152 has the metal
component part 160 and is thus high in electric conductivity as a
whole but is likely to be low in mechanical strength as a whole
because the metal component part 160 is formed using the first
metal.
[0227] The near-field light generating layer 152 has, however, the
second thin-film metal layers 39A, 39B, 39C and thus can be
prevented from being reduced in mechanical strength. In addition,
since each of them has the net-like structure, the volume of the
second metal contained in the near-field light generating layer 152
can be reduced. Accordingly, the near-field light generating layer
152 can also be prevented from melting, deforming, and projecting
from the ABS 101 due to its own heat generation.
[0228] Note that a dielectric substance layer 131 may be formed on
the upper end face 31b side of the optical waveguide 31, as
illustrated in FIG. 34. The dielectric substance layer 131 is
formed on the upper end face 31b. A depression may be formed in the
dielectric substance layer 131, and the metal component part 160
may be formed in the depression.
Modified Example 6
[0229] Furthermore, the near-field light generating layer 28 may
have a second thin-film metal layer 170 as illustrated in FIG. 35,
in place of the second thin-film metal layer 39. A plurality of
defect parts 168 and a flat layer part 169 are formed in the second
thin-film metal layer 170. The respective defect parts 168 are
formed rectangular shape having equal size. Further, an interval in
every direction is unified, and an arrangement direction is also
unified, about respective defect parts 168. An arrangement spot has
also regularity.
[0230] The second thin-film metal layer 170 can maintain its
strength while reducing the volume of the second metal, and thus
can provide the same operation and effect as those of the second
thin-film metal layer 39.
[0231] Besides, the near-field light generating layer 28 may have
second thin-film metal layer 180 as illustrated in FIG. 36 (A), in
place of the second thin-film metal layer 39. Further, the
near-field light generating layer 28 may have second thin-film
metal layer 181 as illustrated in FIG. 36 (B).
[0232] A defect part 178 having approximately oval shape is formed
at the almost center of the second thin-film metal layer 180, and a
flat layer part 179 is formed so as to surround the defect part
178. Three defect parts 188 having approximately oval shape are
formed in the second thin-film metal layer 181, and a flat layer
part 189 is formed so as to surround the respective defect parts
188.
Modified Example 7
[0233] Next, a near-field light generating layer 228 and closely
adhesive layer 237 in accordance with modified example illustrated
in FIG. 37, 38 will be explained. FIG. 37 is a perspective view
illustrating the near-field light generating layer 228 and closely
adhesive layer 237. FIG. 38 is an exploded perspective view of the
near-field light generating layer 228 and closely adhesive layer
237, which are partially omitted.
[0234] The near-field light generating layer 228 is different in
that it has second thin-film metal layers 239 (239A, 239B, 239C) in
place of the second thin-film metal layers 39 (39A, 39B, 39C) as
compared with the above-described near-field light generating layer
28.
[0235] The second thin-film metal layers 239 (239A, 239B, 239C) are
different in that any one of them have one defect part 258 and flat
layer part 259 in place of the plurality of defect parts 58 and
flat layer part 59, as compared with the second thin-film metal
layers 39 (39A, 39B, 39C). Only one the defect part 258 is formed
inside of the flat layer part 259. The flat layer part 259 is
formed along an outer peripheral part 239E of the second thin-film
metal layers 239. The flat layer part 259 has a narrow band shape
of a part, distanced from the outer peripheral part 239E at an
almost regular interval.
[0236] Since the flat layer part 259 is formed in an annular shape
trimming narrowly the outside of one defect part 258 as in the
illustration, the second thin-film metal layer 239 has an annular
structure composed of the defect part 258 and the flat layer part
259.
[0237] In the second thin-film metal layer 239, since the flat
layer part 259 is formed along the outer peripheral part 239E which
is sensitive to deformation, the volume of the second metal
contained in the near-field light generating layer 228 can be
reduced while the reduction in mechanical strength is prevented.
Accordingly, the near-field light generating layer 228 can also be
prevented from melting, deforming, and projecting from the ABS 101
due to its own heat generation.
[0238] Further, the closely adhesive layer 237 is different in that
it has one closely adhesive layer defect part 268 and one closely
adhesive layer flat layer part 269 in place of the plurality of
closely adhesive layer defect parts 88 and the closely adhesive
layer flat layer part 89, as compared with the closely adhesive
layer 37. Only one closely adhesive layer defect part 268 is formed
inside the closely adhesive layer flat layer part 269. The closely
adhesive layer flat layer part 269 is formed in the same narrow
band shape as that of the flat layer part 259. The closely adhesive
layer 237 has the same annular structure as that of the second
thin-film metal layer 239. The volume of the closely adhesive layer
237 is also reduced while the mechanical strength is maintained as
a whole.
[0239] Further, a closely adhesive layer 247 illustrated in FIG. 39
may be formed in place of the closely adhesive layer 237, about the
near-field light generating layer 228. The closely adhesive layer
247 has a closely adhesive layer defect part 278 and a closely
adhesive layer flat layer part 279. Though the closely adhesive
layer flat layer part 279 is formed by narrow band shape similar to
the closely adhesive layer flat layer part 269, a part of the
closely adhesive layer flat layer part 279 near the ABS 101 is
divided. The volume of the closely adhesive layer 247 is also
reduced while the mechanical strength is maintained as a whole.
[0240] Since the part of closely adhesive layer 247 near the ABS
101 is divided, the size of the closely adhesive layer 247 being in
contact with the near-field light generating layer 228 is small, as
compared with closely adhesive layer 237. Accordingly, the
near-field light is generated effectively by using the closely
adhesive layer 247 than the closely adhesive layer 237.
Modified Example 8
[0241] Furthermore, in the thermally assisted magnetic head 100 in
accordance with an embodiment of the present invention, a
near-field light generating layer 153 illustrated in FIG. 40 may be
formed in place of the near-field light generating layer 28.
[0242] The near-field light generating layer 153 is different in
that it has a second thin-film metal layer 99 in place of the
second thin-film metal layers 39C, as compared with the
above-described near-field light generating layer 149. The second
thin-film metal layer 99 is different in that it has a second
thin-film metal layer 39D in place of the second thin-film metal
layer 39A, as compared with the second thin-film metal layer 39. A
depth from the ABS 101 about the second thin-film metal layer 39D
is small than that of the second thin-film metal layer 39A.
[0243] (Embodiments of Head Gimbal Assembly and Hard Disk
Drive)
[0244] Next, embodiments of the head gimbal assembly and hard disk
drive will now be explained with reference to FIG. 41.
[0245] FIG. 41 (a) is a perspective view showing a hard disk drive
201 equipped with the above-mentioned thermally assisted magnetic
head 100. The hard disk drive 201 includes a hard disk (magnetic
recording medium) 202 rotating at a high speed and a head gimbal
assembly (HGA) 210. The hard disk drive 201 is an apparatus which
actuates the HGA 210, so as to record/reproduce data onto/from
recording surfaces of the hard disk 202. The hard disk 202 has a
plurality of (4 in the drawing) platters. Each platter has a
recording surface opposing its corresponding thermally assisted
magnetic head 100.
[0246] The hard disk drive 201 positions a slider 230 on a track by
an assembly carriage device 203. Further, the hard disk drive 201
has a plurality of drive arms 209. The drive arms pivot about a
pivot bearing shaft 206 by means of a voice coil motor (VCM) 205,
and are stacked in a direction along the pivot bearing shaft 206.
Further, an HGA 210 is attached to the tip of each drive arm.
[0247] Further, the hard disk drive 201 has a semiconductor laser
207 generating laser light for heating, a control circuit 204
controlling recording/reproducing and the generation of light by
the semiconductor laser 207, and an optical fiber 208 guiding the
laser light to the slider 230.
[0248] The HGA 210 will now be described with reference to FIG. 41
(b). FIG. 41 (b) is a perspective view illustrating a rear face
side of the HGA 210. In the HGA 210, the slider 230 is fixed to a
tip portion of a suspension 220. Further, in the HGA 210, one end
portion of a wiring member 224 is electrically connected to a
terminal electrode of the slider 230.
[0249] The suspension 220 has a load beam 222, a base plate 221
provided at a base portion of the load beam 222, a flexure 223
fixed to and supported on the load beam 222 from the tip end side
to the front side of the base plate 221 and having elasticity, and
the wiring member 224. The wiring member 224 has a lead conductor
and connection pads electrically connected to both ends of the lead
conductor.
[0250] Next, the slider 230 will be explained. The slider 230 has a
slider base plate having the ABS 101 and a device formation part,
and an output end part of the optical fiber 208 is inserted into
the slider 230. Further, the thermally assisted magnetic head 100
is formed at the device formation part. This slider 230 floats from
the magnetic recording medium 202 by a minute distance.
[0251] In the hard disk drive 201, when the HGA 210 is rotated, the
slider 230 moves in a radial direction of the hard disk 202, i.e.,
a direction traversing track lines.
[0252] Since the aforementioned HGA 210 and hard disk drive 201
have the thermally assisted magnetic head 100, they are capable of
preventing a melting and deformation of the near-field light
generating layer, and are capable of preventing a deformation,
melting and chipping of the magnetic layer arranged near the
near-field light generating layer.
[0253] Though the above-mentioned embodiments explain a type in
which a thin-film coil is wound like a flat spiral about the
linking magnetic pole layer by way of example, the present
invention is also applicable to a thermally assisted magnetic head
of a type in which the thin-film coil is wound about the main
magnetic pole layer.
* * * * *