U.S. patent application number 14/313651 was filed with the patent office on 2014-12-25 for materials for near field transducers and near field transducers containing same.
The applicant listed for this patent is SEAGATE TECHNOLOGY LLC. Invention is credited to Yuhang Cheng, Scott Franzen, Jie Gong, Sethuraman Jayashankar, Michael C. Kautzky, Ed F. Rejda, Sarbeswar Sahoo, Michael Allen Seigler, Kurt W. Wierman, Tong Zhao.
Application Number | 20140376351 14/313651 |
Document ID | / |
Family ID | 52110030 |
Filed Date | 2014-12-25 |
United States Patent
Application |
20140376351 |
Kind Code |
A1 |
Cheng; Yuhang ; et
al. |
December 25, 2014 |
MATERIALS FOR NEAR FIELD TRANSDUCERS AND NEAR FIELD TRANSDUCERS
CONTAINING SAME
Abstract
A device including a near field transducer, the near field
transducer including gold (Au) and at least one other secondary
atom, the at least one other secondary atom selected from: boron
(B), bismuth (Bi), indium (In), sulfur (S), silicon (Si), tin (Sn),
hafnium (Hf), niobium (Nb), manganese (Mn), antimony (Sb),
tellurium (Te), carbon (C), nitrogen (N), and oxygen (O), and
combinations thereof erbium (Er), holmium (Ho), lutetium (Lu),
praseodymium (Pr), scandium (Sc), uranium (U), zinc (Zn), and
combinations thereof and barium (Ba), chlorine (Cl), cesium (Cs),
dysprosium (Dy), europium (Eu), fluorine (F), gadolinium (Gd),
germanium (Ge), hydrogen (H), iodine (I), osmium (Os), phosphorus
(P), rubidium (Rb), rhenium (Re), selenium (Se), samarium (Sm),
terbium (Tb), thallium (Th), and combinations thereof.
Inventors: |
Cheng; Yuhang; (Edina,
MN) ; Zhao; Tong; (Eden Prairie, MN) ;
Kautzky; Michael C.; (Eagan, MN) ; Rejda; Ed F.;
(Bloomington, MN) ; Wierman; Kurt W.; (Eden
Prairie, MN) ; Franzen; Scott; (Savage, MN) ;
Jayashankar; Sethuraman; (Excelsior, MN) ; Sahoo;
Sarbeswar; (Shakopee, MN) ; Gong; Jie; (Eden
Prairie, MN) ; Seigler; Michael Allen; (Eden Prairie,
MN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
SEAGATE TECHNOLOGY LLC |
Cupertino |
CA |
US |
|
|
Family ID: |
52110030 |
Appl. No.: |
14/313651 |
Filed: |
June 24, 2014 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61838405 |
Jun 24, 2013 |
|
|
|
61838393 |
Jun 24, 2013 |
|
|
|
61897303 |
Oct 30, 2013 |
|
|
|
61838398 |
Jun 24, 2013 |
|
|
|
61838626 |
Jun 24, 2013 |
|
|
|
61984915 |
Apr 28, 2014 |
|
|
|
Current U.S.
Class: |
369/13.33 ;
420/3; 420/507; 420/555; 420/577; 423/289; 423/299; 423/344;
423/409; 423/439; 423/489; 423/491; 423/509; 423/561.1; 423/604;
423/645 |
Current CPC
Class: |
C22C 9/05 20130101; C22C
21/10 20130101; C22C 9/04 20130101; G11B 7/1387 20130101; C22C
21/003 20130101; C22C 9/02 20130101; G11B 13/08 20130101; C22C
21/02 20130101; C22C 27/02 20130101; C22C 20/00 20130101; C01F 7/00
20130101; C22C 5/06 20130101; C01G 5/00 20130101; C23C 14/5833
20130101; C22C 13/00 20130101; C22C 18/02 20130101; C22C 24/00
20130101; C22C 27/00 20130101; C22C 27/025 20130101; G11B 5/6088
20130101; C22C 38/06 20130101; G11B 5/3163 20130101; B32B 15/01
20130101; G11B 2005/0021 20130101; C22C 9/00 20130101; C22C 9/08
20130101; C22C 11/04 20130101; C22C 19/03 20130101; C22C 5/02
20130101; C22C 22/00 20130101; C22C 30/02 20130101; G11B 5/314
20130101; C22C 27/06 20130101; C22C 9/06 20130101; G11B 5/4866
20130101; G11B 7/24059 20130101; C22C 5/10 20130101; C22C 9/10
20130101; G11B 5/3106 20130101; C22C 19/07 20130101; C22C 28/00
20130101; C22C 21/00 20130101; B32B 15/018 20130101; C22C 21/06
20130101; C22C 5/04 20130101 |
Class at
Publication: |
369/13.33 ;
420/507; 420/577; 420/3; 420/555; 423/289; 423/299; 423/344;
423/409; 423/439; 423/489; 423/491; 423/509; 423/561.1; 423/604;
423/645 |
International
Class: |
G11B 5/48 20060101
G11B005/48; C22C 28/00 20060101 C22C028/00; C22C 5/02 20060101
C22C005/02 |
Claims
1. A device comprising: a near field transducer, the near field
transducer comprising gold (Au) and at least one other secondary
atom, the at least one other secondary atom selected from: boron
(B), bismuth (Bi), indium (In), sulfur (S), silicon (Si), tin (Sn),
hafnium (Hf), niobium (Nb), manganese (Mn), antimony (Sb),
tellurium (Te), carbon (C), nitrogen (N), and oxygen (O), and
combinations thereof; erbium (Er), holmium (Ho), lutetium (Lu),
praseodymium (Pr), scandium (Sc), uranium (U), zinc (Zn), and
combinations thereof; and barium (Ba), chlorine (Cl), cesium (Cs),
dysprosium (Dy), europium (Eu), fluorine (F), gadolinium (Gd),
germanium (Ge), hydrogen (H), iodine (I), osmium (Os), phosphorus
(P), rubidium (Rb), rhenium (Re), selenium (Se), samarium (Sm),
terbium (Tb), thallium (Th), and combinations thereof.
2. The device according to claim 1, wherein the at least one
secondary atom is selected from: boron (B), bismuth (Bi), indium
(In), sulfur (S), silicon (Si), tin (Sn), hafnium (Hf), niobium
(Nb), manganese (Mn), antimony (Sb), tellurium (Te), carbon (C),
nitrogen (N), and oxygen (O), and combinations thereof.
3. The device according to claim 1, wherein the at least one
secondary atom is selected from: boron (B), bismuth (Bi), sulfur
(S), silicon (Si), indium (In), or combinations thereof.
4. The device according to claim 1, wherein the at least one
secondary atom is selected from: boron (B), sulfur (S), silicon
(Si), or combinations thereof.
5. The device according to claim 1, wherein the at least one
secondary atom is selected from indium (In).
6. The device according to claim 1, wherein the NFT comprises at
least two secondary atoms.
7. The device according to claim 6, wherein a first secondary atom
is selected from: boron (B), bismuth (Bi), sulfur (S), silicon
(Si), carbon (C), antimony (Sb), tellurium (Te), or combinations
thereof, holmium (Ho), lutetium (Lu), praseodymium (Pr), uranium
(U), or combinations thereof; and cesium (Cs), dysprosium (Dy),
europium (Eu), gadolinium (Gd), germanium (Ge), rubidium (Rb),
selenium (Se), samarium (Sm), terbium (Tb), thallium (Th), or
combinations thereof; and a second secondary atom is selected from:
indium (In), tin (Sn), hafnium (Hf), niobium (Nb), manganese (Mn),
or some combination thereof; and erbium (Er), scandium (Sc), zinc
(Zn), or some combination thereof.
8. The device according to claim 1, wherein the NFT comprises about
0.1 atomic percent to about 50 atomic percent of the at least one
secondary atom.
9. The device according to claim 1, wherein the NFT comprises about
0.1 atomic percent to about 5 atomic percent of the at least one
secondary atom.
10. The apparatus according to claim 1 further comprising an energy
source.
11. A device comprising: a light source; a waveguide; and a near
field transducer, the near field transducer comprising gold (Au)
and at least one other secondary atom, the at least one other
secondary atom selected from: boron (B), bismuth (Bi), indium (In),
sulfur (S), silicon (Si), tin (Sn), hafnium (Hf), niobium (Nb),
manganese (Mn), antimony (Sb), tellurium (Te), carbon (C), nitrogen
(N), and oxygen (O), and combinations thereof; erbium (Er), holmium
(Ho), lutetium (Lu), praseodymium (Pr), scandium (Sc), uranium (U),
zinc (Zn), and combinations thereof; and barium (Ba), chlorine
(Cl), cesium (Cs), dysprosium (Dy), europium (Eu), fluorine (F),
gadolinium (Gd), germanium (Ge), hydrogen (H), iodine (I), osmium
(Os), phosphorus (P), rubidium (Rb), rhenium (Re), selenium (Se),
samarium (Sm), terbium (Tb), thallium (Th), and combinations
thereof, wherein the light source, waveguide and near field
transducer are configured to transmit light from the light source
to the waveguide and finally the near field transducer.
12. The device according to claim 11, wherein the at least one
secondary atom is selected from: boron (B), bismuth (Bi), sulfur
(S), silicon (Si), indium (In), or combinations thereof.
13. The device according to claim 11, wherein the at least one
secondary atom is selected from: boron (B), sulfur (S), silicon
(Si), or combinations thereof.
14. The device according to claim 11, wherein the at least one
secondary atom is selected from indium (In).
15. The device according to claim 11, wherein the NFT comprises at
least two secondary atoms.
16. The device according to claim 15, wherein a first secondary
atom is selected from: boron (B), bismuth (Bi), sulfur (S), silicon
(Si), carbon (C), antimony (Sb), tellurium (Te), or combinations
thereof, holmium (Ho), lutetium (Lu), praseodymium (Pr), uranium
(U), or combinations thereof; and cesium (Cs), dysprosium (Dy),
europium (Eu), gadolinium (Gd), germanium (Ge), rubidium (Rb),
selenium (Se), samarium (Sm), terbium (Tb), thallium (Th), or
combinations thereof; and a second secondary atom is selected from:
indium (In), tin (Sn), hafnium (Hf), niobium (Nb), manganese (Mn),
or some combination thereof; and erbium (Er), scandium (Sc), zinc
(Zn), or some combination thereof.
17. The device according to claim 11, wherein the NFT comprises
about 0.1 atomic percent to about 5 atomic percent of the at least
one secondary atom.
18. A disc drive comprising: at least one actuator arm having a
first and a second end; at least one head, wherein each arm has a
head at the first end thereof and wherein each head comprises: a
light source; a near field transducer, the near field transducer
comprising gold (Au) and at least one other secondary atom, the at
least one other secondary atom selected from: boron (B), bismuth
(Bi), indium (In), sulfur (S), silicon (Si), tin (Sn), hafnium
(Hf), niobium (Nb), manganese (Mn), antimony (Sb), tellurium (Te),
carbon (C), nitrogen (N), and oxygen (O), and combinations thereof;
erbium (Er), holmium (Ho), lutetium (Lu), praseodymium (Pr),
scandium (Sc), uranium (U), zinc (Zn), and combinations thereof;
and barium (Ba), chlorine (Cl), cesium (Cs), dysprosium (Dy),
europium (Eu), fluorine (F), gadolinium (Gd), germanium (Ge),
hydrogen (H), iodine (I), osmium (Os), phosphorus (P), rubidium
(Rb), rhenium (Re), selenium (Se), samarium (Sm), terbium (Tb),
thallium (Th), and combinations thereof; a magnetic reader; and a
magnetic writer, wherein the light source and the near field
transducer are configured to transmit light from the light source
to the near field transducer in order to assist the magnetic writer
with writing.
19. The disc drive according to claim 18, wherein the at least one
secondary atom is selected from: boron (B), bismuth (Bi), sulfur
(S), silicon (Si), indium (In), or combinations thereof.
20. The disc drive according to claim 18, wherein the NFT comprises
about 0.1 atomic percent to about 5 atomic percent of the at least
one secondary atom.
Description
PRIORITY
[0001] This application claims priority to U.S. Provisional
Application Nos. 61/838,405 entitled "NEAR FIELD TRANSDUCER
MATERIALS" filed on Jun. 24, 2013, 61/838,393 entitled "MATERIALS
FOR NEAR FIELD TRANSDUCERS AND NEAR FIELD TRANSDUCERS INCLUDING THE
SAME" filed on Jun. 24, 2013, 61/897,303 entitled "MATERIALS FOR
NEAR FIELD TRANSDUCERS AND NEAR FIELD TRANSDUCERS INCLUDING THE
SAME" filed on Oct. 30, 2013, 61/838,398 entitled "NEAR FIELD
TRANSDUCERS AND METHODS OF FORMING THE SAME" filed on Jun. 24,
2013, 61/838,626 entitled "NEAR FIELD TRANSDUCERS AND METHODS OF
FORMING THE SAME" filed on Jun. 24, 2013, and 61/984,915 entitled
"METHODS OF FORMING NEAR FIELD TRANSDUCERS (NFTS) USING ION
IMPLANTATION" filed on Apr. 28, 2014, the disclosure of which is
incorporated herein by reference thereto.
SUMMARY
[0002] A device including a near field transducer, the near field
transducer including gold (Au) and at least one other secondary
atom, the at least one other secondary atom selected from: boron
(B), bismuth (Bi), indium (In), sulfur (S), silicon (Si), tin (Sn),
hafnium (Hf), niobium (Nb), manganese (Mn), antimony (Sb),
tellurium (Te), carbon (C), nitrogen (N), and oxygen (O), and
combinations thereof; erbium (Er), holmium (Ho), lutetium (Lu),
praseodymium (Pr), scandium (Sc), uranium (U), zinc (Zn), and
combinations thereof; and barium (Ba), chlorine (Cl), cesium (Cs),
dysprosium (Dy), europium (Eu), fluorine (F), gadolinium (Gd),
germanium (Ge), hydrogen (H), iodine (I), osmium (Os), phosphorus
(P), rubidium (Rb), rhenium (Re), selenium (Se), samarium (Sm),
terbium (Tb), thallium (Th), and combinations thereof.
[0003] A device including a light source; a waveguide; and a near
field transducer, the near field transducer including gold (Au) and
at least one other secondary atom, the at least one other secondary
atom selected from: boron (B), bismuth (Bi), indium (In), sulfur
(S), silicon (Si), tin (Sn), hafnium (Hf), niobium (Nb), manganese
(Mn), antimony (Sb), tellurium (Te), carbon (C), nitrogen (N), and
oxygen (O), and combinations thereof; erbium (Er), holmium (Ho),
lutetium (Lu), praseodymium (Pr), scandium (Sc), uranium (U), zinc
(Zn), and combinations thereof; and barium (Ba), chlorine (Cl),
cesium (Cs), dysprosium (Dy), europium (Eu), fluorine (F),
gadolinium (Gd), germanium (Ge), hydrogen (H), iodine (I), osmium
(Os), phosphorus (P), rubidium (Rb), rhenium (Re), selenium (Se),
samarium (Sm), terbium (Tb), thallium (Th), and combinations
thereof, wherein the light source, waveguide and near field
transducer are configured to transmit light from the light source
to the waveguide and finally the near field transducer.
[0004] A disc drive including at least one actuator arm having a
first and a second end; at least one head, wherein each arm has a
head at the first end thereof and wherein each head includes: a
light source; a near field transducer, the near field transducer
including gold (Au) and at least one other secondary atom, the at
least one other secondary atom selected from: boron (B), bismuth
(Bi), indium (In), sulfur (S), silicon (Si), tin (Sn), hafnium
(Hf), niobium (Nb), manganese (Mn), antimony (Sb), tellurium (Te),
carbon (C), nitrogen (N), and oxygen (O), and combinations thereof;
erbium (Er), holmium (Ho), lutetium (Lu), praseodymium (Pr),
scandium (Sc), uranium (U), zinc (Zn), and combinations thereof;
and barium (Ba), chlorine (Cl), cesium (Cs), dysprosium (Dy),
europium (Eu), fluorine (F), gadolinium (Gd), germanium (Ge),
hydrogen (H), iodine (I), osmium (Os), phosphorus (P), rubidium
(Rb), rhenium (Re), selenium (Se), samarium (Sm), terbium (Tb),
thallium (Th), and combinations thereof; a magnetic reader; and a
magnetic writer, wherein the light source and the near field
transducer are configured to transmit light from the light source
to the near field transducer in order to assist the magnetic writer
with writing.
[0005] The above summary of the present disclosure is not intended
to describe each disclosed embodiment or every implementation of
the present disclosure. The description that follows more
particularly exemplifies illustrative embodiments. In several
places throughout the application, guidance is provided through
lists of examples, which examples can be used in various
combinations. In each instance, the recited list serves only as a
representative group and should not be interpreted as an exclusive
list.
BRIEF DESCRIPTION OF THE FIGURES
[0006] FIG. 1 is a pictorial representation of a data storage
device in the form of a disc drive that can include a recording
head constructed in accordance with an aspect of this
disclosure.
[0007] FIG. 2 is a side elevation view of a recording head
constructed in accordance with an aspect of the invention.
[0008] FIG. 3 is a schematic representation of a near field
transducer.
[0009] FIG. 4 is a schematic representation of another near field
transducer.
[0010] FIG. 5 shows the total energies of the grain boundary with
the boron atom in the bulk interstitial site and in the grain
boundary hollow site with respect to expansion distances of the
cell.
[0011] FIG. 6 shows a graph comparing the experimental T and
C.sub.o ranges with calculated positions of T.sub.B and T.sub.C for
Pb--In--Sn and Bi--In--Sn grain growth.
[0012] FIG. 7 shows the relative atomic size difference versus the
grain boundary segregation energy of various elements.
[0013] The figures are not necessarily to scale. Like numbers used
in the figures refer to like components. However, it will be
understood that the use of a number to refer to a component in a
given figure is not intended to limit the component in another
figure labeled with the same number.
DETAILED DESCRIPTION
[0014] Heat assisted magnetic recording (referred to through as
HAMR) utilizes radiation, for example from a laser, to heat media
to a temperature above its curie temperature, enabling magnetic
recording. In order to deliver the radiation, e.g., a laser beam,
to a small area (on the order of 20 to 50 nm for example) of the
medium, a NFT is utilized. During a magnetic recording operation,
the NFT absorbs energy from a laser and focuses it to a very small
area; this can cause the temperature of the NFT to increase. The
temperature of the NFT can be elevated up to about 400.degree. C.
or more.
[0015] The very high temperatures that the NFT reaches during
operation can lead to diffusion of the material of the NFT (for
example gold) from the peg and towards the disk. In addition, a
portion of the NFT may be exposed at the air bearing surface of the
recording head and is thus subject to mechanical wearing. NFT
performance is greatly influenced by the heat and mechanical stress
during HAMR operation. It would therefore be advantageous to have
NFT devices that are more durable.
[0016] Disclosed devices can offer the advantage of providing more
efficient transfer of energy from an energy source to the magnetic
storage media to be heated, a smaller focal point at the point of
heating, or some combination thereof. In some embodiments,
disclosed devices can be used within other devices or systems, such
as magnetic recording heads, more specifically, thermally or heat
assisted magnetic recording (HAMR) heads, or disc drives that
include such devices.
[0017] Disclosed herein are NFTs and devices that include such
NFTs. FIG. 1 is a pictorial representation of a data storage device
in the form of a disc drive 10 that can utilize disclosed NFTs. The
disc drive 10 includes a housing 12 (with the upper portion removed
and the lower portion visible in this view) sized and configured to
contain the various components of the disc drive. The disc drive 10
includes a spindle motor 14 for rotating at least one magnetic
storage media 16 within the housing. At least one arm 18 is
contained within the housing 12, with each arm 18 having a first
end 20 with a recording head or slider 22, and a second end 24
pivotally mounted on a shaft by a bearing 26. An actuator motor 28
is located at the arm's second end 24 for pivoting the arm 18 to
position the recording head 22 over a desired sector or track 27 of
the disc 16. The actuator motor 28 is regulated by a controller,
which is not shown in this view and is well-known in the art. The
storage media may include, for example, continuous media or bit
patterned media.
[0018] For heat assisted magnetic recording (HAMR), electromagnetic
radiation, for example, visible, infrared or ultraviolet light is
directed onto a surface of the data storage media to raise the
temperature of a localized area of the media to facilitate
switching of the magnetization of the area. Recent designs of HAMR
recording heads include a thin film waveguide on a slider to guide
light toward the storage media and a near field transducer to focus
the light to a spot size smaller than the diffraction limit. While
FIG. 1 shows a disc drive, disclosed NFTs can be utilized in other
devices that include a near field transducer.
[0019] FIG. 2 is a side elevation view of a recording head that may
include a disclosed NFT; the recording head is positioned near a
storage media. The recording head 30 includes a substrate 32, a
base coat 34 on the substrate, a bottom pole 36 on the base coat,
and a top pole 38 that is magnetically coupled to the bottom pole
through a yoke or pedestal 40. A waveguide 42 is positioned between
the top and bottom poles. The waveguide includes a core layer 44
and cladding layers 46 and 48 on opposite sides of the core layer.
A mirror 50 is positioned adjacent to one of the cladding layers.
The top pole is a two-piece pole that includes a first portion, or
pole body 52, having a first end 54 that is spaced from the air
bearing surface 56, and a second portion, or sloped pole piece 58,
extending from the first portion and tilted in a direction toward
the bottom pole. The second portion is structured to include an end
adjacent to the air bearing surface 56 of the recording head, with
the end being closer to the waveguide than the first portion of the
top pole. A planar coil 60 also extends between the top and bottom
poles and around the pedestal. In this example, the top pole serves
as a write pole and the bottom pole serves as a return pole.
[0020] An insulating material 62 separates the coil turns. In one
example, the substrate can be AlTiC, the core layer can be
Ta.sub.2O.sub.5, and the cladding layers (and other insulating
layers) can be Al.sub.2O.sub.3. A top layer of insulating material
63 can be formed on the top pole. A heat sink 64 is positioned
adjacent to the sloped pole piece 58. The heat sink can be
comprised of a non-magnetic material, such as for example Au.
[0021] As illustrated in FIG. 2, the recording head 30 includes a
structure for heating the magnetic storage media 16 proximate to
where the write pole 58 applies the magnetic write field H to the
storage media 16. In this example, the media 16 includes a
substrate 68, a heat sink layer 70, a magnetic recording layer 72,
and a protective layer 74. However, other types of media, such as
bit patterned media can be used. A magnetic field H produced by
current in the coil 60 is used to control the direction of
magnetization of bits 76 in the recording layer of the media.
[0022] The storage media 16 is positioned adjacent to or under the
recording head 30. The waveguide 42 conducts light from a source 78
of electromagnetic radiation, which may be, for example,
ultraviolet, infrared, or visible light. The source may be, for
example, a laser diode, or other suitable laser light source for
directing a light beam 80 toward the waveguide 42. Specific
exemplary types of light sources 78 can include, for example laser
diodes, light emitting diodes (LEDs), edge emitting laser diodes
(EELs), vertical cavity surface emitting lasers (VCSELs), and
surface emitting diodes. In some embodiments, the light source can
produce energy having a wavelength of 830 nm, for example. Various
techniques that are known for coupling the light beam 80 into the
waveguide 42 may be used. Once the light beam 80 is coupled into
the waveguide 42, the light propagates through the waveguide 42
toward a truncated end of the waveguide 42 that is formed adjacent
the air bearing surface (ABS) of the recording head 30. Light exits
the end of the waveguide and heats a portion of the media, as the
media moves relative to the recording head as shown by arrow 82. A
near-field transducer (NFT) 84 is positioned in or adjacent to the
waveguide and at or near the air bearing surface. The heat sink
material may be chosen such that it does not interfere with the
resonance of the NFT.
[0023] Although the example of FIG. 2 shows a perpendicular
magnetic recording head and a perpendicular magnetic storage media,
it will be appreciated that the disclosure may also be used in
conjunction with other types of recording heads and/or storage
media where it may be desirable to concentrate light to a small
spot.
[0024] FIG. 3 is a schematic view of a lollypop NFT 90 in
combination with a heat sink 92. The NFT includes a disk shaped
portion 94 and a peg 96 extending from the disk shaped portion. The
heat sink 92 can be positioned between the disk shaped portion and
the sloped portion of the top pole in FIG. 2. When mounted in a
recording head, the peg may be exposed at the ABS and thus can be
subjected to mechanical wearing.
[0025] FIG. 4 is a schematic view of a coupled nanorod (CNR) NFT
100. This NFT includes two nanorods 102 and 104 separated by a gap
106. Nanorod 102 includes a first portion 108 and a second portion
110. Nanorod 104 includes a first portion 112 and a second portion
114. When mounted in a recording head, the ends 116 and 118 of the
nanorods may be exposed at the ABS and thus be subject to
mechanical wearing. FIGS. 3 and 4 show example NFTs. However, the
disclosure is not limited to any particular type of NFT. The
materials described below may be used in various NFT
configurations.
[0026] Disclosed NFTs may be made of a primary atom and at least
one secondary atom. In some embodiments, the primary atom may have
a higher atomic percentage (at %) in the NFT. In some embodiments,
the primary atom may be gold (Au). In some embodiments, more than
one secondary atom is included in a NFT. A secondary atom(s) may be
chosen by considering one or more properties of a material,
mechanisms of atomic diffusion, or combinations thereof.
[0027] It is thought that, atoms, for example gold atoms diffuse
through defects in the NFT. In solids, there are three kinds of
defects: point defects (atoms missing, lattice vacancies,
substitutional, interstitial impurities, and self-interstitials);
linear defects (screw and edge dislocations); and planar defects
(large angle and small angle grain boundaries, stacking faults, and
external surfaces). Each type of defect provides its own mechanism
for diffusion. As a result, there are three major mechanisms by
which a NFT material (e.g., gold) may diffuse from the peg to the
disk, namely, bulk or lattice diffusion, defect diffusion, and
surface diffusion.
[0028] Bulk or lattice diffusion generally involves vacancy-atom
exchange. It is by this process that the atoms in the layers
intermingle so that the latter become of increasingly similar
composition while totally in the solid state. Bulk diffusion is
highly temperature dependent, and has a relatively small diffusion
coefficient at temperatures below the melting point of the
material.
[0029] The second mechanism is that of rapid diffusion along defect
paths. This process is less dependent on temperature than is
lattice diffusion and usually becomes dominant at lower
temperatures. Defects like grain boundaries, dislocations and twin
boundaries, which are common and practically unavoidable in metals,
can serve as rapid transport pipes through a metallic layer.
[0030] The third mechanism is surface or interface diffusion. Due
to the mismatch, there are high density defects at the surface
and/or interface between the NFT and the surrounding CNS, NPS, and
HOC. As a result, NFT atoms, e.g., gold atoms, have a relatively
high diffusion coefficient through surface and/or interface
diffusion.
[0031] Disclosed secondary atoms to combine with a primary atom may
be chosen, at least in part, by keeping these diffusion mechanisms
in mind. Various properties that may be considered then can
include, for example bond energy/strength of the secondary atoms to
the primary atom in comparison to the bond energy/strength of the
primary atom to the primary atom, solubility of the secondary atom
in the primary atom, size of the atomic radius, optical properties,
oxidation resistance, melting point, or some combination
thereof.
[0032] In some embodiments, at least one of the secondary atoms has
a higher bond energy/strength than does the primary atom-primary
atom bond. Such an atom may serve to reduce the primary material
atom diffusion from the peg to the disk and thereby increase peg
reliability. By considering, as an example, gold as the primary
atom, the following can explain the effect of the bond
energy/strength consideration. Gold has a face centered cubic (fcc)
structure. In a gold lattice, each gold atom is bonded to the atoms
at the 6 corners and 12 atoms at the center of the face, which
means that one gold atom is connected to 18 other gold atoms.
Potentially, adding one other atom with a high bond strength with
gold could therefore affect the movement of 18 gold atoms. Due to
the larger bond strength, it is expected that this atom will bond
to the surrounding gold atoms and form atom clusters. This could
prevent the separation of the gold atoms from the grain, which
limits the source of free gold atoms. Also, the cluster could pin
the defects, such as dislocations, small angle grain boundaries,
and large angle grain boundary, which could obstruct movement of
the defects, and therefore, hinder the gold diffusion. Furthermore,
the unbound secondary atoms at the interface, the grain boundary,
the dislocation, and other defects could attract the free gold
atoms, which could further hinder transportation of the gold atoms
through defect channels and thereby increase the NFT stability.
[0033] The existence of the secondary atom(s) on the NFT surface
and at the NFT/surrounding material interfaces could also block the
primary atom diffusion through surfaces and interfaces. Especially
in circumstances, when the free primary atoms on the surface or at
the interface diffuse away, leaving a relatively high concentration
of secondary atoms on the surface or at the interface, which could
prevent the further diffusion of the remaining primary atoms and
increase the peg stability.
[0034] In some embodiments, the bond energy/strength of a secondary
atom to the primary atom in comparison to the bond energy/strength
of the primary atom to the primary atom may be relevant when
considering elements to include as a secondary atom(s). Table 1
below shows bond dissociation energies of different atoms with
gold. The bond dissociation energy of a bond indicates the bond
energy/strength of a bond. The higher the bond dissociation energy,
the stronger the bond is.
TABLE-US-00001 TABLE 1 Bond dissociation energy (kJ/mol) Bond Bond
Bond Energy Energy Energy Bond (kJ/mol) Bond (kJ/mol) Bond (kJ/mol)
Ag--Au 203 Al--Au 326 Au--Au 224.7 Au--B 367.8 Au--Ba 254.8 Au--Be
285 Au--Bi 297 Au--Ca 243 Au--Ce 339 Au--Cl 343 Au--Co 222 Au--Cr
213 Au--Cs 255 Au--Cu 228 Au--D 318 Au--Dy 259 Au--Eu 241 Au--F 294
Au--Fe 187 Au--Ga 234 Au--Ge 274.1 Au--H 292 Au--Ho 267 Au--I 276
Au--In 286 Au--La 336.4 Au--Li 284.5 Au--Lu 332 Au--Mg 243 Au--Mn
185.4 Au--Na 215 Au--Nd 299.2 Au--Ni 255 Au--O 221.8 Au--Pb 130
Au--Pd 155 Au--Pr 310 Au--Rb 243 Au--Rh 231 Au--S 418 Au--Sc 280
Au--Se 243 Au--Si 305.4 Au--Sn 254.8 Au--Sr 264 Au--Tb 289 Au--Te
317.6 Au--U 318 Au--V 240.6 Au--W 207.9 Au--Y 307.1
[0035] In some embodiments, the secondary atom can be boron (B),
bismuth (Bi), indium (In), sulfur (S), silicon (Si), tin (Sn),
manganese (Mn), tellurium (Te), or combinations thereof, for
example. In some embodiments, the secondary atom can be holmium
(Ho), lutetium (Lu), praseodymium (Pr), scandium (Sc), uranium (U),
or combinations thereof, for example. In some embodiments, the
secondary atom can be barium (Ba), chlorine (Cl), cesium (Cs),
dysprosium (Dy), europium (Eu), fluorine (F), germanium (Ge),
hydrogen (H), iodine (I), rubidium (Rb), selenium (Se), terbium
(Tb), or combinations thereof, for example. In some embodiments,
the secondary atom can be boron (B), bismuth (Bi), indium (In),
sulfur (S), silicon (Si), tin (Sn), manganese (Mn), tellurium (Te),
holmium (Ho), lutetium (Lu), praseodymium (Pr), scandium (Sc),
uranium (U), barium (Ba), chlorine (Cl), cesium (Cs), dysprosium
(Dy), europium (Eu), fluorine (F), germanium (Ge), hydrogen (H),
iodine (I), rubidium (Rb), selenium (Se), terbium (Tb), or
combinations thereof, for example.
[0036] In some embodiments, the solubility of the secondary atom in
the primary atom may be relevant when considering elements to
include as a secondary atom(s). If a secondary atom(s) has a
relatively low solubility in the primary atom, the secondary
atom(s) will exist mainly in the defects of the structure of the
primary atoms. This can serve to reduce the diffusion of the gold
atoms through the defects. In some embodiments, the secondary atom
can be boron (B), bismuth (Bi), sulfur (S), silicon (Si), carbon
(C), antimony (Sb), tellurium (Te), or combinations thereof, for
example. In some embodiments, the secondary atom can be boron (B),
bismuth (Bi), sulfur (S), silicon (Si), tellurium (Te), or
combinations thereof, for example. In some embodiments, the
secondary atom can be holmium (Ho), erbium (Er), lutetium (Lu),
praseodymium (Pr), uranium (U), or combinations thereof, for
example. In some embodiments, the secondary atom can be cesium
(Cs), dysprosium (Dy), europium (Eu), gadolinium (Gd), germanium
(Ge), rubidium (Rb), selenium (Se), samarium (Sm), terbium (Tb),
thallium (Th), or combinations thereof, for example. In some
embodiments, the secondary atom can be cesium (Cs), dysprosium
(Dy), europium (Eu), germanium (Ge), rubidium (Rb), selenium (Se),
terbium (Tb), or combinations thereof, for example. In some
embodiments, the secondary atom can be boron (B), bismuth (Bi),
sulfur (S), silicon (Si), carbon (C), antimony (Sb), tellurium
(Te), holmium (Ho), lutetium (Lu), praseodymium (Pr), uranium (U),
cesium (Cs), dysprosium (Ds), europium (Eu), gadolinium (Gd),
germanium (Ge), rubidium (Rb), selenium (Se), samarium (Sm),
terbium (Tb), thallium (Th), cadmium (Cd), neodymium (Nd),
phosphorus (P), lead (Pb), or combinations thereof, for
example.
[0037] In some embodiments, atoms with high solubility in gold can
have advantageous effects, while in some other embodiments, atoms
with low solubility in gold can have advantageous effects. In some
embodiments, only insoluble atoms can be added to a primary
material so that the atoms stay in the defects. In some embodiment,
only soluble atoms can be added to a primary material in order to
increase the thermal stability of the primary material. In some
embodiments, both soluble and insoluble atoms can be added to a
primary material in order to increase the thermal stability of the
primary material. In some embodiments, a combination of atoms with
low solubility and atoms with high solubility may have an
advantageous effect of improving the thermal stability of a primary
material.
[0038] In some embodiments at least two secondary atoms can be
included with a primary atom to form a NFT. In some such
embodiments, a first secondary atom can include an element that has
a relatively low solubility with the primary atom. In embodiments
where the primary atom is gold, the secondary atoms listed in the
preceding paragraph can be utilized in this embodiment. The second
secondary atom in such an embodiment may have a relatively high
solubility in the primary atom (e.g., gold) so that the second
secondary atoms are distributed uniformly in the grains of the
primary atoms. This may serve to prevent the primary atoms from
leaving the grain. This could then eliminate the source of free
gold atoms and block the diffusion of gold atoms through defects
such as dislocations, interfaces, surfaces, grain boundaries, twin
boundaries, or combinations thereof. In some such embodiments, the
second secondary atom can be indium (In), tin (Sn), hafnium (Hf),
niobium (Nb), manganese (Mn), or some combination thereof, for
example. In some such embodiments, the second secondary atom can be
erbium (Er), scandium (Sc), zinc (Zn), or some combination thereof,
for example. In some such embodiments, the second secondary atom
can be indium (In), tin (Sn), hafnium (Hf), niobium (Nb), manganese
(Mn), erbium (Er), scandium (Sc), zinc (Zn), or some combination
thereof, for example. In some embodiments, the second secondary
atoms can be silver (Ag), copper (Cu), magnesium (Mg), palladium
(Pd), vanadium (V), zinc (Zn), chromium (Cr), iron (Fe), lithium
(Li), nickel (Ni), platinum (Pt), scandium (Sc), or some
combination thereof, for example. It should also be noted that the
atoms noted as second secondary atoms can also be used in
combination with a primary material without the first secondary
atom, e.g., a NFT can include only a primary material and a
secondary material from the above noted second secondary atoms.
[0039] In some embodiments, secondary atom(s) can be chosen based
on their atomic radii. In some embodiments, secondary atom(s) can
be those that have larger atomic radii than the primary atom so
that the secondary atom(s) have a low diffusion rate into the
primary metal. Table 2 shows the atomic radii of a number of
atoms.
TABLE-US-00002 TABLE 2 Atomic Atomic Atomic Atomic Symbol radius
Symbol radius Symbol radius Symbol radius H 0.046 Pd 0.137 Cr 0.125
Ho 0.176 Li 0.152 Ag 0.144 Mn 0.112 Er 0.175 Be 0.114 Cd 0.15 Fe
0.124 Tm 0.174 Be 0.097 In 0.157 Co 0.125 Yb 0.193 C 0.077 Sn 0.158
Ni 0.125 Lu 0.173 N 0.071 Sb 0.161 Cu 0.128 Hf 0.159 O 0.06 Te
0.143 Zn 0.133 Ta 0.147 Na 0.186 In 0.136 Ga 0.135 W 0.137 Mg 0.16
Cs 0.265 Ge 0.122 Re 0.138 Al 0.143 Ba 0.217 As 0.125 Os 0.135 Si
0.117 La 0.187 Se 0.116 Ir 0.135 P 0.109 Ce 0.182 Rb 0.251 Pt 0.138
S 0.106 Pr 0.183 Sr 0.215 Au 0.144 Cl 0.107 Nd 0.182 Y 0.181 Hg
0.15 K 0.231 Sm 0.181 Zr 0.158 Tl 0.171 Ca 0.197 Eu 0.204 Nb 0.143
Pb 0.175 Sc 0.16 Gd 0.18 Mo 0.136 Bi 0.182 Ti 0.147 Tb 0.177 Ru
0.134 Th 0.18 V 0.132 Dy 0.177 Rh 0.134 U 0.138
[0040] In some embodiments, the secondary atom(s) can be bismuth
(Bi), indium (In), tin (Sn), hafnium (Hf), niobium (Nb), antimony
(Sb), tellurium (Te), or some combination thereof, for example. In
some embodiments, the secondary atom(s) can be erbium (Er), holmium
(Ho), lutetium (Lu), praseodymium (Pr), scandium (Sc), or some
combination thereof, for example. In some embodiments, the
secondary atom(s) can be barium (Ba), cesium (Cs), dysprosium (Dy),
europium (Eu), gadolinium (Gd), samarium (Sm), terbium (Tb),
thallium (Th), or some combination thereof, for example.
[0041] In some embodiments, two secondary atoms can be utilized, a
first secondary atom that has a low solubility in the primary atom
and a second secondary atoms that has a high solubility in gold. In
such embodiments, the first secondary atom (that have a low
solubility in the primary atom) may reduce the diffusion of the
primary atoms through defects, such as dislocations and grain
boundaries, and the second secondary atoms (that have a high
solubility in the primary atom) may reduce the diffusion of the
primary atoms through lattice and surface/interface
interactions.
[0042] In some embodiments, the first secondary atom (that has a
low solubility in the primary atom) may be boron (B), bismuth (Bi),
sulfur (S), silicon (Si), carbon (C), antimony (Sb), tellurium
(Te), or combinations thereof, for example. In some embodiments,
the first secondary atom can be boron (B), bismuth (Bi), sulfur
(S), silicon (Si), tellurium (Te), or combinations thereof, for
example. In some embodiments, the first secondary atom can be
holmium (Ho), lutetium (Lu), praseodymium (Pr), uranium (U), or
combinations thereof, for example. In some embodiments, the first
secondary atom can be cesium (Cs), dysprosium (Dy), europium (Eu),
gadolinium (Gd), germanium (Ge), rubidium (Rb), selenium (Se),
samarium (Sm), terbium (Tb), thallium (Th), or combinations
thereof, for example. In some embodiments, the first secondary atom
can be cesium (Cs), dysprosium (Dy), europium (Eu), germanium (Ge),
rubidium (Rb), selenium (Se), terbium (Tb), or combinations
thereof, for example. In some embodiments, the first secondary atom
can be boron (B), bismuth (Bi), sulfur (S), silicon (Si), carbon
(C), antimony (Sb), tellurium (Te), holmium (Ho), lutetium (Lu),
praseodymium (Pr), uranium (U), cesium (Cs), dysprosium (Ds),
europium (Eu), gadolinium (Gd), germanium (Ge), rubidium (Rb),
selenium (Se), samarium (Sm), terbium (Tb), thallium (Th), or
combinations thereof, for example.
[0043] In some embodiments, the second secondary atom can be indium
(In), tin (Sn), hafnium (Hf), niobium (Nb), manganese (Mn), or some
combination thereof, for example. In some such embodiments, the
second secondary atom can be erbium (Er), scandium (Sc), zinc (Zn),
or some combination thereof, for example. In some such embodiments,
the second secondary atom can be indium (In), tin (Sn), hafnium
(Hf), niobium (Nb), manganese (Mn), erbium (Er), scandium (Sc),
zinc (Zn), or some combination thereof, for example. In some
embodiments, the second secondary atom can be silver (Ag), copper
(Cu), magnesium (Mg), palladium (Pd), vanadium (V), zinc (Zn),
aluminum (Al), chromium (Cr), iron (Fe), nickel (Ni), lithium (Li),
platinum (Pt), scandium (Sc), tantalum (Ta), or some combination
thereof, for example.
[0044] In some embodiments, a NFT can also include a third
secondary atom. In some embodiments, the third secondary atom can
be one where the bond energy/strength of the third secondary
atom-third secondary atom bond is less than that of the third
secondary atom-primary atom bond so that the third secondary atom
tends to bond to the primary atom instead of other third secondary
atoms. As a result, the third secondary atoms may be substantially
uniformly distributed in the primary atoms, which can increase the
obstruction efficiency of the third secondary atoms.
[0045] In some embodiments, the secondary atom(s) can also be
chosen by considering optical properties of the atoms or a material
that includes the atoms (e.g., an alloy containing the primary atom
and the secondary atom(s)). In some embodiments, atoms useful in a
NFT can have optical properties that enable efficient coupling of
incident light to the surface plasmons and effective energy
transfer to the magnetic medium. The optical properties of NFT
materials are often characterized by their optical refractive index
(n) and extinction coefficient (k) which can be measured by
ellipsometry. From the n and k values, the real and imaginary part
of the dielectric constant (permittivity) can be calculated by:
.di-elect cons..sub.1=n.sup.2-k.sup.2 and .di-elect
cons..sub.2=2nk. The plasmonic effect arises from the negative real
part of the dielectric constant of the material. The strength of
plasmonic coupling depends on the absolute value of .di-elect
cons..sub.1. On the other hand, the surface plasmon mode needs to
propagate over a substantial distance. The loss of this propagation
is proportional to the imaginary part of the dielectric .di-elect
cons..sub.2. A good plasmonic material will have high |.di-elect
cons..sub.1.di-elect cons. and low .di-elect cons..sub.2. Hence a
figure-of-merit (FOM) has been developed to characterize the
"goodness" of plasmonic materials: FOM=3*|.di-elect
cons..sub.1/.di-elect cons..sub.2|.
[0046] The near field transducers described above can be fabricated
using a variety of techniques, including for example: sputtering
from an alloy target; co-sputtering from multiple targets; reactive
sputtering from an alloy target; reactive co-sputtering from
multiple targets; co-evaporation from multiple sources; reactive
co-evaporation from multiple sources; ion beam deposition from an
alloy target; codeposition in electrochemical ways, including
electroless deposition, electrodeposition, displacement reaction,
chemical reduction, or electrophoretic deposition.
[0047] In some embodiments, secondary atom(s) can be chosen based
on other considerations. For example, secondary atom(s) can be
chosen based on mechanistic considerations involved in pinning
grain growth. The NFT grain and interface boundary can be
atomically engineered by the preferential adsorption of secondary
atom(s) in order to pin the grain boundary and improve the grain
boundary migration resistance of a NFT that includes, a primary
atoms, such as gold for example. This can also be described as
utilizing minor alloying elements (e.g., secondary atom(s)) to
alter the fundamental grain boundary migration kinetics of the
primary atom (e.g., gold). Mechanical high temperature reliability
of the NFT may therefore be improved by intentional microalloying
additions of one or more secondary atom(s) into the NFT material.
Such intentional alloying can pin the grain boundary movement by
the so called "solute drag" effect, making it harder for the peg to
recess.
[0048] Disclosed concepts may provide stable NFT element dimensions
during operating temperatures by pinning grain growth. This concept
utilizes the preferential placement of secondary atoms at the grain
boundaries of the NFT material to pin grain movement. The secondary
atoms are chosen such that the total strain energy and total
chemical potential energy of the system of atoms is reduced when
they are at the grain boundary. Thus the grain boundary secondary
atom is in a potential "well" and therefore "locks" the movement of
the grain boundary.
[0049] The preferential placement of secondary atoms can be
accomplished by facilitating the movement of secondary atoms to the
grain boundaries. Such secondary atoms may be able to stabilize the
NFT against grain growth through the following mechanisms:
increased drag force on the moving grain boundary due to the
binding chemical potential and elastic strain interaction of
secondary atom to the grain boundary; reduction of grain boundary
diffusion by poisoning of the primary atom (e.g., gold) grain
boundary by the tightly adsorbed secondary atoms blocking of the
diffusion jump sites at the boundary by the secondary atoms;
reduction of the efficiency of secondary atom transfer across the
grain boundary by the secondary atom; change in the grain boundary
structure brought about by the secondary atom; preferential
formation of vacancy-secondary atom pairs and secondary
atom-primary atom pairs at the grain boundary which make boundary
migration harder; improving the grain boundary cohesion; or some
combination thereof.
[0050] The selection of the secondary atom can be based, at least
in part on considerations involving the energetics of segregation
of the secondary atom to the grain boundary. One consideration is
the size of the secondary atom. In some embodiments the size of the
secondary atom can be less than the size of the primary atom. If
such a relationship exists the secondary atom can occupy
interstitial positions in the bulk and at the grain boundary. In a
face centered cubic (FCC) structure, the octahedral site is the
largest interstitial site. FIG. 5 shows the total energies of the
grain boundary with the boron atom in the bulk interstitial site
and in the grain boundary hollow site with respect to expansion
distances of the cell. By comparing the energetics of a grain
boundary with a boron atom in the interstitial site, a grain
boundary with hollow sites, and a pure aluminum grain boundary it
can be seen that the boron atom does not expand the grain boundary
hollow site. In fact the boron atom fits neatly into the grain
boundary. The segregation energy is the difference in the total
energy of the system with the boron atom in the grain boundary
hollow site and the total energy of the grain boundary system with
the boron atom in the bulk interstitial site. The driving force
between the bulk and the grain boundary configuration is, in effect
segregation energy. A negative segregation energy would enhance the
grain boundary cohesion.
[0051] The same basic mechanism allows the secondary atom to poison
the grain boundary/surface diffusivity. Secondary atoms having
smaller radii may be more amenable to providing this effect. Grain
boundary precipitants may also be formed based on the energetics of
the system. From a consideration of this effect, boron (B), carbon
(C), nitrogen (N), oxygen (O), or some combination thereof may be
useful as a secondary atom(s).
[0052] It should be understood, having read this disclosure, that
grain boundaries as discussed herein include high angle and low
angle grain boundaries, coherent and incoherent boundaries, tilt
and twist boundaries, intergranular phases as well as high symmetry
boundaries such as twin boundaries.
[0053] An important consequence of these considerations is that
NFTs without secondary atom(s) will have higher grain boundary
mobilities and lower stabilities. Thus NFTs as typically formulated
will have lower resistance to grain boundary movement since, by
definition, they do not have secondary atoms in the system that can
preferentially locate to the grain boundary. They will therefore
possess undesirable grain migration and reliability
performance.
[0054] In contrast, disclosed NFTs can utilize a secondary atom(s)
to pin the grain boundary. A secondary atom(s) present even at a
few 10s or 100s of ppm may make a dramatic impact in curtailing the
mobility of the grain boundaries. Secondary atom(s) which reduce
the strain energy and chemical potential at the grain boundary may
lead to preferential clustering of secondary atoms near the grain
boundaries (called Cottrell atmospheres) which may provide locking
mechanisms that impede grain boundary movement. It should be
emphasized that the primary function of the secondary atom(s) is
grain boundary mobility impairment, although other functions such
as solid solution strengthening are also possible.
[0055] A secondary atom can be chosen based, at least in part, on
the ability for preferential segregation of the secondary atom
(solute atom) to the grain boundary. The secondary atom(s)
preferentially bond to the grain boundary because of the lowering
of the energy at the grain boundary. The choice of solute atom is
thus governed by the Grain Boundary Segregation energy, which is
the lowering of the system energy due to reduction of the elastic
misfit strain energy and the electronic (valence) interaction
energy. The choice of secondary atoms can be aided by the use of
DFT computations, as well as electronegativity and atomic elastic
strain field energy calculations.
[0056] Faster secondary atoms may lead to better pinning of the
grain boundary. It is also understood that a combination of more
than one secondary atom may lead to better pinning of the grain
boundary due to efficient boundary interstitial site filling
(space-fill efficiency) due to the combination of varying secondary
atom atomic radii. This is analogous to achieving better space
filling when a mixture of different sized balls is used rather than
a single sized ball.
[0057] A possible advantage of utilizing the solute drag method of
grain boundary stabilization is that very low concentrations of
secondary atoms, compared to solid solution strengthening or
precipitation hardening, is needed. This in turn minimizes the
impact of the modification on the plasmonic properties. Larger
grain sizes possess smaller grain boundary area, and therefore
require lower amounts of solute phase to percolate the boundary. In
fact, only several hundred ppm of secondary atom (dopant)
concentration may produce a 3 to 4 order of magnitude change in the
grain boundary mobility. Initially the grain boundaries are pinned
to the secondary atom atmospheres thereby immobilizing them. As the
temperature is raised, the secondary atoms gain vibrational energy.
The boundary then has an increasing tendency to decouple from the
solute atoms pinning it. At a certain temperature, the boundary
breaks away from the secondary atoms surrounding it. The breakaway
temperature of the grain boundary is related to the concentration
of secondary atoms at the boundary. Higher secondary atom
concentrations at the boundary lead to higher break away
temperatures. The NFT operating temperature will thus be dependent
on the secondary atom concentration as shown schematically in FIG.
6.
[0058] FIG. 7 shows the solute segregation enthalpy of various
atoms and indicates that atoms such as boron (B), and carbon (C);
scandium (Sc); thallium (Th); and combinations thereof may be
useful. Such atoms may have a higher propensity to grain boundary
segregation and solute drag stabilization. As a general rule,
elements with misfit energies (grain boundary solute segregation
energies) higher than 12.5 kJ/mol will tend to easily segregate to
the grain boundary. Therefore all the elements with segregation
energies above the dashed lines can be considered candidates for
alloying elements for solute drag strengthening of the Au NFT. Such
elements can include, for example sodium (Na), strontium (Sr),
calcium (Ca), yttrium (Y), thorium (Th), antimony (Sb), thallium
(Tl), boron (B), scandium (Sc), carbon (C), beryllium (Be),
lutetium (Lu), thulium (Tm), erbium (Er), holmium (Ho), dysprosium
(Dy), ytterbium (Yb), terbium (Tb), gadolinium (Gd), samarium (Sm),
phosphorus (P), sulfur (S), promethium (Pm), neodymium (Nd), nickel
(Ni), cobalt (Co), cerium (Ce), lanthanum (La), praseodymium (Pr),
iron (Fe), and copper (Cu) for example. Elements included in FIG. 7
that have misfit energies less than 12.5 kJ/mol include europium
(Eu), germanium (Ge), hafnium (Hf), cadmium (Cd), manganese (Mn),
silicon (Si), barium (Ba), potassium (K), and rubidium (Rb).
[0059] In some embodiments, the amount of the secondary atom can be
not less than 10 ppm (0.001 at %), or in some embodiments not less
than 100 ppm (0.01 at %). In some embodiments, the amount of the
secondary atom can be not greater than 100 ppm (0.01 at %), in some
embodiments not greater than 5 at %, or in some embodiments not
greater than 10 at %.
[0060] In some embodiments, solute drag stabilization (or solute
pinning) can be accomplished by carrying out the following steps
prior to operating the NFT: (1) incorporation of one or more
secondary atoms to the primary atom lattice; and (2) driving of the
secondary atoms from the grain interior to the grain boundary
through a suitably chosen temperature-time schedule. In some
embodiments, secondary atoms that are added based on the solute
drag mechanistic approach can be introduced through implantation,
vacuum deposition, carburizing, nitridization, electrodeposition,
incorporation through seed layers, or other techniques for example.
Alternatively, secondary atom(s) may be introduced into the NFT by
a variety of other methods. For example, the secondary atom(s)
could be incorporated in the target material compositions which are
deposited or co-deposited. Alternatively, secondary atom(s) could
be incorporated into the NFT by ion implantation, by diffusion from
or through the seed layer underneath.
[0061] Annealing can also optionally be included. The annealing
schedule can be chosen so as to initially drive the secondary atoms
from the grain interior to the grain boundary. The annealing
temperature may help in the preferential segregation of the
secondary atoms to the grain boundaries. Therefore, exposure of the
NFT to heat during the annealing and operating temperature
strengthens, rather than weakens the NFT alloy.
[0062] The method can be applicable to wafer and slider processing.
Secondary atoms can be introduced at wafer (or slider) level for
NFTs. The addition of secondary atom(s) can be advantageously
combined with annealing to further improve NFT strength.
[0063] A particular illustrative example of a process sequence for
implementation of the solute drag stabilization can include the
following: deposit a gold film of the required thickness on a wafer
(or slider bar); implant a carefully chosen species which lowers
the total system energy at the grain boundary; for example, metals,
metalloids, B, C, N, (O) at concentrations from about 100 ppm to
100000 ppm; implant conditions (temperature, voltage, dose,
current) can be chosen and calculated so as to confine the
implanted species (solute) in the thickness of the film; the wafer
can be heated or cooled during the duration of the implant; the
implant can be a line beam implanter, or it can be a Plasma
immersion implanter, the implant can be a line of sight, or it can
be in a retrograde profile; the implanted species can be implanted
by itself, or it can be preceded or followed up by another
co-implanted species which serves to control the degree of
crystallinity, the dopant profile before and after the implant, the
co implant can be a substitutional or an interstitial species, in
some embodiments a substitutional species; a thermal activation
anneal can then drive implant species to grain boundary from the
grain interior, the time-temperature schedule can be carefully
chosen; and the dose of the implant is chosen such that the penalty
in n and k should be minimal.
[0064] The implementation of the solute dopant step can be preceded
or followed by appropriate laser, furnace, spike or RTA processes.
The aim of such processes are to advantageously modify and control
the grain structure, point, line and volume defects of the gold for
optimal reliability performance. These include vacancies, clusters,
grain size, degree of crystallinity or amorphousness, twin and
stacking fault density, grain boundary intergranular phases, etc.
The annealing can be solid state annealing or epitaxy, or it can be
liquid phase annealing or epitaxy.
[0065] It should be understood that the implantation and annealing
steps can be carried out at sheet film of a plasmonic metal or a
suitably chosen binary or ternary plasmonic alloy at wafer or bar
level. It can also be combined with wafer or slider based
patterning methods which can serve to selectively dope the solute
atoms in only the needed regions of the wafer (slider) while
protecting the other regions. Implementing such a process at the
bar level may reduce the risk of damage to the optical layers of
the NFT device from the implanted beam. An added benefit of such an
implantation scheme is that there is no degradation in mechanical
strength due to implant. Possible interfacial strength enhancements
due to intentional mixing at interface are also possible.
[0066] Alternate methods of doping interstitials and solute atoms
are also possible. For example, e-beam heating of the NFT film will
lead to incorporation of carbon atoms. Likewise, the deposition of
a metal layer (or carbon or boron) followed by a diffusion anneal,
surface nitridation, surface carburization are also methods of
incorporation of the secondary atom in the lattice. Alternatively,
the dopant atom can be incorporated in the seed layer and driven by
diffusion into the NFT material.
[0067] In some embodiments, disclosed NFTs may include a primary
atom and at least one secondary atom, regardless of the mechanistic
approach which is being relied upon as providing an effect. In some
embodiments, a primary atom can be gold (Au) and the at least one
secondary atom can be selected from: boron (B), bismuth (Bi),
indium (In), sulfur (S), silicon (Si), tin (Sn), hafnium (Hf),
niobium (Nb), manganese (Mn), antimony (Sb), tellurium (Te), carbon
(C), nitrogen (N), and oxygen (O), for example. In some
embodiments, gold and B, Si or S can be utilized in a NFT. NFTs
including gold and B, Si, S, or combinations thereof may be useful.
In some embodiments, gold and In can be utilized in a NFT. NFTs
including gold and In may be useful. In some embodiments, gold and
B, C, N, or O can be utilized in a NFT. NFTs including gold and B,
C, N, or O, or combinations thereof may be useful.
[0068] In some embodiments, disclosed NFTs may include gold (Au)
and at least one of the following elements: erbium (Er), holmium
(Ho), lutetium (Lu), praseodymium (Pr), scandium (Sc), uranium (U),
zinc (Zn). In some embodiments, disclosed NFTs may include gold
(Au) and at least one of the following elements: barium (Ba),
chlorine (Cl), cesium (Cs), dysprosium (Dy), europium (Eu),
fluorine (F), gadolinium (Gd), germanium (Ge), hydrogen (H), iodine
(I), osmium (Os), phosphorus (P), rubidium (Rb), rhenium (Re),
selenium (Se), samarium (Sm), terbium (Tb), thallium (Th).
[0069] Generally, a NFT can include a primary atom and at least one
secondary atom. In some embodiments, the secondary atom(s) can have
an atomic percent (at %) that is not greater than 50 at %, in some
embodiments, not greater than 30 at %, in some embodiments, not
greater than 5 at %, and in some embodiments, not greater than 1 at
%. In some embodiments, the second atom(s) can have an at % that is
not less than 0.001 at %, in some embodiments not less than 0.01 at
%, and in some embodiments not less than 0.1 at %.
[0070] While the present disclosure is not so limited, an
appreciation of various aspects of the disclosure will be gained
through a discussion of the examples provided below.
Examples
[0071] All scientific and technical terms used herein have meanings
commonly used in the art unless otherwise specified. The
definitions provided herein are to facilitate understanding of
certain terms used frequently herein and are not meant to limit the
scope of the present disclosure.
[0072] As used in this specification and the appended claims, "top"
and "bottom" (or other terms like "upper" and "lower") are utilized
strictly for relative descriptions and do not imply any overall
orientation of the article in which the described element is
located.
[0073] As used in this specification and the appended claims, the
singular forms "a", "an", and "the" encompass embodiments having
plural referents, unless the content clearly dictates
otherwise.
[0074] As used in this specification and the appended claims, the
term "or" is generally employed in its sense including "and/or"
unless the content clearly dictates otherwise. The term "and/or"
means one or all of the listed elements or a combination of any two
or more of the listed elements.
[0075] As used herein, "have", "having", "include", "including",
"comprise", "comprising" or the like are used in their open ended
sense, and generally mean "including, but not limited to". It will
be understood that "consisting essentially of", "consisting of",
and the like are subsumed in "comprising" and the like. For
example, a conductive trace that "comprises" silver may be a
conductive trace that "consists of" silver or that "consists
essentially of" silver.
[0076] As used herein, "consisting essentially of," as it relates
to a composition, apparatus, system, method or the like, means that
the components of the composition, apparatus, system, method or the
like are limited to the enumerated components and any other
components that do not materially affect the basic and novel
characteristic(s) of the composition, apparatus, system, method or
the like.
[0077] The words "preferred" and "preferably" refer to embodiments
that may afford certain benefits, under certain circumstances.
However, other embodiments may also be preferred, under the same or
other circumstances. Furthermore, the recitation of one or more
preferred embodiments does not imply that other embodiments are not
useful, and is not intended to exclude other embodiments from the
scope of the disclosure, including the claims.
[0078] Also herein, the recitations of numerical ranges by
endpoints include all numbers subsumed within that range (e.g., 1
to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, 5, etc. or 10 or less
includes 10, 9.4, 7.6, 5, 4.3, 2.9, 1.62, 0.3, etc.). Where a range
of values is "up to" a particular value, that value is included
within the range.
[0079] Use of "first," "second," etc. in the description above and
the claims that follow is not intended to necessarily indicate that
the enumerated number of objects are present. For example, a
"second" substrate is merely intended to differentiate from another
infusion device (such as a "first" substrate). Use of "first,"
"second," etc. in the description above and the claims that follow
is also not necessarily intended to indicate that one comes earlier
in time than the other.
[0080] Thus, embodiments of materials for near field transducers
and near field transducers containing the same are disclosed. The
implementations described above and other implementations are
within the scope of the following claims. One skilled in the art
will appreciate that the present disclosure can be practiced with
embodiments other than those disclosed. The disclosed embodiments
are presented for purposes of illustration and not limitation.
* * * * *