U.S. patent application number 14/252206 was filed with the patent office on 2014-10-16 for low iron, high redox ratio, and high iron, high redox ratio, soda-lime-silica glasses and methods of making same.
This patent application is currently assigned to PPG INDUSTRIES OHIO, INC.. The applicant listed for this patent is PPG INDUSTRIES OHIO, INC.. Invention is credited to Lawrence E. Jansen, Mark O. Naylor, Larry J. Shelestak.
Application Number | 20140309099 14/252206 |
Document ID | / |
Family ID | 51687176 |
Filed Date | 2014-10-16 |
United States Patent
Application |
20140309099 |
Kind Code |
A1 |
Naylor; Mark O. ; et
al. |
October 16, 2014 |
LOW IRON, HIGH REDOX RATIO, AND HIGH IRON, HIGH REDOX RATIO,
SODA-LIME-SILICA GLASSES AND METHODS OF MAKING SAME
Abstract
A glass has a basic soda-lime-silica glass portion, and a
colorant portion including total iron as Fe.sub.2O.sub.3 selected
from the group of total iron as Fe.sub.2O.sub.3 in the range of
greater than zero to 0.02 weight percent; total iron as
Fe.sub.2O.sub.3 in the range of greater than 0.02 weight percent to
less than 0.10 weight percent and total iron as Fe.sub.2O.sub.3 in
the range of 0.10 to 2.00 weight percent; redox ratio in the range
of 0.2 to 0.6, and tin and/or tin compounds, e.g. SnO.sub.2 greater
than 0.000 to 6.0 weight percent. In one embodiment of the
invention, the glass has a tin side and an opposite air side,
wherein the tin side of the glass is supported on a molten tin bath
during forming of the glass. The tin concentration at the tin side
of the glass is greater than, less than, or equal to the tin
concentration in "body portion" of the glass. The "body portion" of
the glass extending from the air side of the glass toward the tin
side and terminating short of the tin side of the glass.
Inventors: |
Naylor; Mark O.;
(Pittsburgh, PA) ; Jansen; Lawrence E.;
(Burkburnett, TX) ; Shelestak; Larry J.;
(Gibsonia, PA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
PPG INDUSTRIES OHIO, INC. |
Cleveland |
OH |
US |
|
|
Assignee: |
PPG INDUSTRIES OHIO, INC.
Cleveland
OH
|
Family ID: |
51687176 |
Appl. No.: |
14/252206 |
Filed: |
April 14, 2014 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61812006 |
Apr 15, 2013 |
|
|
|
Current U.S.
Class: |
501/71 ; 501/53;
501/70; 65/99.6 |
Current CPC
Class: |
C03C 4/0092 20130101;
C03B 18/12 20130101; C03C 4/02 20130101; C03C 3/087 20130101; C03C
3/095 20130101 |
Class at
Publication: |
501/71 ; 501/53;
501/70; 65/99.6 |
International
Class: |
C03C 3/087 20060101
C03C003/087; C03B 18/12 20060101 C03B018/12; C03C 4/02 20060101
C03C004/02 |
Claims
1. A glass having a tin side and an opposite air side, wherein the
tin side of the glass is supported on a molten tin bath during
forming of the glass, the glass, comprising: a basic
soda-lime-silica glass portion, and a colorant portion, comprising:
total iron as Fe.sub.2O.sub.3 selected from the group of total iron
as Fe.sub.2O.sub.3 in the range of greater than zero to 0.02 weight
percent; total iron as Fe.sub.2O.sub.3 in the range of greater than
0.02 weight percent to less than 0.10 weight percent and total iron
as Fe.sub.2O.sub.3 in the range of 0.10 to 2.00 weight percent;
redox ratio 0.2 to 0.6, and tin and/or tin containing compounds
providing tin in an amount within the range of greater than 0.005
to 5.0 weight percent, wherein the tin and/or the tin containing
compound provides a concentration of fin in the air side of the
glass that is equal to or different than the tin in the tin side of
the glass.
2. The glass according to claim 1 wherein the concentration of tin
is uniform from the air side of the glass toward the tin side of
the glass and the tin side of the glass has a higher concentration
of tin than the air side.
3. The glass according to claim 1 wherein the basic
soda-lime-silica glass portion comprises: TABLE-US-00013 SiO.sub.2
65-75 wt. % Na.sub.2O 10-20 wt. % CaO 5-15 wt. % MgO 0-5 wt. %
Al.sub.2O.sub.3 0-5 wt. % K.sub.2O 0-5 wt. %; and
total iron as Fe.sub.2O.sub.3 selected from total iron as
Fe.sub.2O.sub.3 in the range of greater than zero to 0.02 weight
percent.
4. The glass according to claim 3, wherein the colorant portion
comprises CoO 0-5 parts per million; Nd.sub.2O.sub.3 in the range
of 0-0.1 weight percent; and CuO 0-0.03 weight percent, wherein the
colorant portion provides the glass with a total solar energy
transmission ("TSET") of greater than 0% and equal to or less than
5%, a total solar energy reflection ("TSER") of greater than 3% and
equal to or less than 7%, and a total solar energy absorption
("TSEA") of greater than 90% and equal to or less than 97%, and
selected ones of the TSET, TSER, and TSEA are measured over a
wavelength range of 300 to 2500 nanometers ("nm") at a glass
thickness in the range of 3.6-4.1 millimeters ("mm").
5. The glass according to claim 1 wherein the basic
soda-lime-silica glass portion comprises: TABLE-US-00014 SiO.sub.2
65-75 wt. % Na.sub.2O 10-20 wt. % CaO 5-15 wt. % MgO 0-5 wt. %
Al.sub.2O.sub.3 0-5 wt. % K.sub.2O 0-5 wt. %; and
total iron as Fe.sub.2O.sub.3 selected from total iron as
Fe.sub.2O.sub.3 in the range of greater than 0.02 weight percent to
less than 0.10 weight percent, and the tin and/or tin compound at
the air side has a concentration of tin in the range of 0.1-3 wt.
%.
6. The glass according to claim 1 wherein the basic
soda-lime-silica glass portion comprises: TABLE-US-00015 SiO.sub.2
65-75 wt. % Na.sub.2O 10-20 wt. % CaO 5-15 wt. % MgO 0-5 wt. %
Al.sub.2O.sub.3 0-5 wt. % K.sub.2O 0-5 wt. %; and
total iron as Fe.sub.2O.sub.3 selected from total iron as
Fe.sub.2O.sub.3 in the range of 0.10 to 2.00 weight percent and the
tin and/or tin compound at the air side has a concentration of tin
in the range of 0.1-5 wt. %.
7. The glass according to claim 6 wherein the glass comprises:
TABLE-US-00016 Ingredient Ingredient in wt. % SiO.sub.2 73.11
Na.sub.2O 13.65 K.sub.2O 0.01 CaO 8.68 MgO 3.16 A.sub.l2O.sub.3
0.03 Fe.sub.2O.sub.3 0.0097 SrO 0.02 SO.sub.3 0.2 ZrO.sub.2 0.001
FeO/Fe.sub.2O.sub.3 0.505 SnO.sub.2 0.111
wherein the glass has an LTA of at least 91.23%; a dominant
wavelength of 496.66 nanometers; an excitation purity of 0.14%; a
TSUV of 89.07%; a TSIR of 87.82% and a TSET of 89.43% at a
thickness of 5.6 mm.
8. The glass according to claim 6 wherein the glass has water in
the range of 200 to 700 parts per million.
9. The glass according to claim I wherein the basic
soda-lime-silica glass portion comprises: TABLE-US-00017 SiO.sub.2
65-75 wt. % Na.sub.2O 10-20 wt. % CaO 5-15 wt. % MgO 0-5 wt. %
Al.sub.2O.sub.3 0-5 wt. % K.sub.2O 0-5 wt. %; and
the colorant portion comprises: total iron as Fe.sub.2O.sub.3 in
the range of 0.01 to 2.0 weight percent; and SnO.sub.2 in the range
of 0.005 to 5.0.
10. The glass according to claim 9 wherein the glass has a redox of
greater than 0.35 up to about 0.60, a luminous transmittance of at
least 55 percent, and a color characterized by a dominant
wavelength of 485 to 489 nanometers and an excitation purity of
about 3 to 18 percent, and wherein the glass has a total solar
ultraviolet transmittance of about 60 percent or less, a total
solar infrared transmittance of about 35 percent or less and a
total solar energy transmittance of about 55 percent or less at a
thickness of about 0.154 inches.
11. The glass according to claim 10 wherein the glass comprises:
TABLE-US-00018 Ingredients Ingredients in wt. % SiO.sub.2 71.83
Na2O 13.94 K2O 0.07 CaO 8.73 MgO 3.8 Al2O3 0.07 Fe2O3 0.515 SrO
0.003 SO3 0.18 ZrO2 0.0012 FeO/Fe.sub.2O.sub.3 0.559 SnO.sub.2
0.828
wherein the glass has an LTA of at 65.19%; a dominant wavelength of
487.95 nanometers; an excitation purity of 13.13%; a ISM of 48.46%;
a TSIR of 8.25% and a TSET of 34.59% at a thickness of 5.6 mm.
12. The glass according to claim 11 wherein the glass has water in
the range of 200 to 700 parts per million.
13. A method of making a glass, comprising: providing a basic
soda-lime-silica glass portion, and a colorant portion, the
colorant portion, comprising: total iron as Fe.sub.2O.sub.3
selected from the group of total iron as Fe.sub.2O.sub.3 in the
range of greater than zero to 0.02 weight percent; total iron as
Fe.sub.2O.sub.3 in the range of greater than 0.02 weight percent to
less than 0.10 weight percent and total iron as Fe.sub.2O.sub.3 in
the range of 0.10 to 2.00 weight percent, and tin and/or tin
containing compounds providing tin in an amount within the range of
greater than 0.005 to 5.0 weight percent, melting the glass portion
and the colorant portion to provide a pool of molten glass; flowing
the molten glass onto a molten tin bath; moving the molten glass on
the surface of the molten tin bath, while controllably cooling the
glass and applying forces to the glass to provide a glass of a
desired thickness; removing the glass from the molten tin bath,
wherein the tin and/or tin containing compounds concentration at
the tin side of the glass may be greater than the Sn concentration
in body portion of the glass, the body portion of the glass
extending from the air side of the glass and terminating short of
the tin side of the glass.
14. The method according to claim 13 wherein the total iron as
Fe.sub.2O.sub.3 is selected from the group of total iron as
Fe.sub.2O.sub.3 in the range of greater than zero to 0.02 weight
percent.
15. The method according to claim 13 wherein the total iron as
Fe.sub.2O.sub.3 is in the range of greater than 0.02 weight percent
to less than 0.10 weight percent.
16. The method according to claim 13 wherein the total iron as
Fe.sub.2O.sub.3 is in the range of 0.10 to 2.00 weight percent.
17. The method according to claim 13 wherein tin and tin containing
compounds are added to the glass batch materials and/or molten
glass by an act selected from selected from (1) adding SnO.sub.2
and/or tin sulfate ("SnS") to the glass batch materials as a dry
powder; (2) adding pellets of SnO.sub.2 to the glass batch
materials; (3) adding glass cullet to the batch material, the
cullet having a coating of SnO.sub.2 over and/or on a glass surface
and/or glass Gullet having tin and/or tin containing compounds
within the body of the glass; (4) adding ground particles of tin
and/or tin containing compounds, e.g. but not limited to Sn,
SnO.sub.2, and SnS to the glass batch materials; (6) mixing dry
SnO.sub.2 with a liquid to make a slurry and adding the slurry to
the batch materials; (7) bubbling tin containing halogen gas into
the molten glass, and (8) adding organo-tin compounds and
organo-tin compounds containing halogens.
18. The method according to claim 13 wherein the glass has a redox
of greater than 0.35 up to about 0.60, a luminous transmittance of
at least 55 percent, and a color characterized by a dominant
wavelength of 485 to 489 nanometers and an excitation purity of
about 3 to 18 percent, and wherein the glass has a total solar
ultraviolet transmittance of about 60 percent or less, a total
solar infrared transmittance of about 35 percent or less and a
total solar energy transmittance of about 55 percent or less at a
thickness of about 0.154 inches.
19. The method according to claim 13 wherein the glass has water in
the range of 200 to 700 parts per million.
20. The method according to the method of claim 13 wherein the
glass has an LTc of 90.8%; a dominant wavelength of 490.50
nanometers; an excitation purity of 0.27%; a TSUV of 88.4%; a TSIR
of 86.4% and a TSET od 88.5% and the radiation transmittance data
is based on TSUV 300-390 nanometers; LTc 400-770 nanometers and
TSIR 800-2100 nanometers at a standard thickness of 5.5 mm.
Description
CROSS REFERENCE TO RELATED APPLICATION
[0001] This application claims the benefits of U.S. Provisional
Patent Application Ser. No. 61/812,006 filed Apr. 15, 2013, and
titled "LOW IRON, HIGH REDOX RATIO SODA-LIME-SILICA GLASS AND
METHOD OF MAKING SAME". Application Ser. No. 61/812,006 in its
entirety is incorporated herein by reference.
BACKGROUND OF THE INVENTION
[0002] 1. Field of the Invention
[0003] This invention relates generally to iron containing, high
redox ratio soda-lime-silica glasses and methods of making same,
and more particularly, to low iron, high redox ratio, and high
iron, high redox ratio, soda-lime-silica glasses, and methods of
making same.
[0004] 2. Discussion of Available Technology
[0005] As is appreciated by those skilled in the art of making
soda-lime-silica glass, parameters of interest include, but are not
limited to the redox ratio, and total iron expressed as
Fe.sub.2O.sub.3. For example and not limiting to the discussion,
U.S. Pat. No. 6,962,887, which patent is incorporated herein by
reference, discloses a glass having total iron expressed as
Fe.sub.2O.sub.3 in the range of greater than 0 to 0.02 weight
percent ("wt. %") and a redox ratio in the range of 0.2 to 0.6. The
glass is aesthetically pleasing and useful, for example, in
furniture applications such as tabletops or shelving. Further, this
glass is highly transparent when viewed normal to a major surface
of the glass but has an aesthetically desirable blue i.e., azure
edge color when viewed on edge. Such a glass is sold by PPG
Industries, Inc. under the PPG Industries Ohio registered trademark
"Starphire".
[0006] Another glass of interest in the present discussion is
disclosed in U.S. Pat. No. 6,313,053, which patent is incorporated
herein by reference. The patent discloses a blue colored glass
using a standard soda-lime-silica glass base composition and
additionally iron and cobalt, and optionally chromium, as solar
radiation absorbing materials and colorants. The blue colored glass
has total iron expressed as Fe.sub.2O.sub.3 in the range of 0.10 to
1.0 wt. %, and a redox ratio in the range of greater than 0.35 to
0.60. Such a glass is considered for purposes of discussion a high
iron, high redox ratio, soda-lime-silica glass. Such a glass is
sold by PPG Industries, Inc. under the PPG industries Ohio
registered trademark "Solextra".
[0007] The low iron, and high iron, high redox soda-lime-silica
glass compositions can be made in a multi-stage melting and
vacuum-assisted refining operation as disclosed in U.S. Pat. Nos.
4,792,636 and 5,030,584, and can be made in a conventional float
glass system as disclosed in U.S. Pat. No. 6,962,887. U.S. Pat.
Nos. 4,792,536, 5,030,594 and 6,962,887 are hereby incorporated by
reference. The high iron, and low iron, high redox ratio
soda-lime-silica glass compositions are generally made in a
conventional float glass system using oxyfuel as disclosed in U.S.
Pat. Nos. 4,604,123; 6,962,887 and 7,691,763 to obtain or maintain
a high redox ratio, and the low iron, high redox glasses can be
made using oxyfuel fired furnaces but are preferably made using
fuel and air mixtures fired in Siemens type furnaces. U.S. Pat.
Nos. 4,604,123; 6,962,887 and 7,691,763 are hereby incorporated by
reference. Although the presently available methods for making the
glasses disclosed in U.S. Pat. Nos. 4,792,536, 5,030,594, 6,313,053
and 6,962,887 are acceptable; there are limitations. More
particularly, the limitations of interest in the present discussion
are maintaining the redox ratio of the glasses within a range of
0.2 to 0.6 and preferably within the range of 0.35 to 0.6.
[0008] As is appreciated by those skilled in the art, the redox
ratio can be increased by additions of sulfur (see incorporated
U.S. patents) and carbon, e.g. but not limited to graphite, coal
and/or oil to reduce the Ferric iron (Fe+++) to Ferrous iron
(Fe++). Although presently there are available methods for making
glasses having low iron, high redox ratio, and high iron, high
redox ratios, it is appreciated by those skilled in the art that
the methods are usually tailored to meet the parameters of the
furnace. More particularly, the use of carbon to increase the redox
ratio of soda-lime-silica glasses made using oxyfuel fired
glassmaking furnaces can result in batch melting changes that can
result in silica stones. In view of the forgoing, it would be
advantageous to provide methods for making low iron and high iron
soda-lime-silica glasses having high redox ratios that can be used
regardless of the type of heating system or furnace used to melt
the glass batch materials and to eliminate the limitations
associated with the heating systems.
SUMMARY OF THE INVENTION
[0009] The invention relates to a glass having a tin side and an
opposite air side, wherein the tin side of the glass is supported
on a molten tin bath during forming of the glass. The glass
includes, among other things, a basic soda-lime-silica glass
portion, and a colorant portion. The colorant portion including,
among other things, total iron as Fe2O3 selected from the group of
total iron as Fe2O3 in the range of greater than zero to 0.02
weight percent; total iron as Fe2O3 in the range of greater than
0.02 weight percent to less than 0.10 weight percent and total iron
as Fe2O3 in the range of 0.10 to 2.00 weight percent; redox ratio
in the range of 0.2 to 0.6. The tin and/or tin containing compounds
providing tin in an amount within the range of greater than 0.005
to 5.0 weight percent, wherein the tin and/or the tin containing
compound provides a concentration of tin in the air side of the
glass that is less than the tin in the tin side of the glass.
[0010] The invention further relates to a method of making a glass,
by, among other things, providing a basic soda-lime-silica glass
portion, and a colorant portion. The colorant portion, including,
among other things, total iron as Fe2O3 selected from the group of
total iron as Fe2O3 in the range of greater than zero to 0.02
weight percent; total iron as Fe2O3 in the range of greater than
0.02 weight percent to less than 0.10 weight percent and total iron
as Fe2O3 in the range of 0.10 to 2.00 weight percent, and tin
and/or tin containing compounds providing tin in an amount within
the range of greater than 0.005 to 5.0 weight percent, thereafter
melting the glass portion and the colorant portion to provide a
pool of molten glass; flowing the molten glass onto a molten tin
bath; moving the molten glass on the surface of the molten tin
bath, while controllably cooling the glass and applying forces to
the glass to provide a glass of a desired thickness; and removing
the glass from the molten tin bath, wherein the tin and/or tin
containing compounds concentration at the tin side of the glass is
greater than the Sn concentration in body portion of the glass, the
body portion of the glass extending from the air side of the glass
and terminating short of the tin side of the glass.
BRIEF DESCRIPTION OF DRAWINGS
[0011] FIGS. 1A and 1B are a horizontal section of a glass melting
furnace that can be used in the practice of the invention; FIG. 1A
is the melting section of the furnace, and FIG. 1B is the refining
and homogenizing section of the furnace.
[0012] FIG. 2 is a vertical section of the melting section shown in
FIG. 1A.
[0013] FIG. 3 is an elevated side view partially in cross section
of a glass melting and refining apparatus that can be used in the
practice of the invention.
[0014] FIG. 4 shows a set of measurements of low iron,
soda-lime-silica glass laboratory samples to show the effect of
graphite and tin dioxide on the redox ratio. A straight line
connects the measurements for each sample having similar amounts of
graphite. The batch for each sample was melted at a temperature of
2650.degree. F.
[0015] FIG. 5 shows a set of measurements of low iron,
soda-lime-silica glass laboratory samples (1) to show the effect of
temperature, (2) to show the effect of tin dioxide added to the
batch, and (3) to compare tin dioxide added to the batch to glass
with tin dioxide already in the glass as 100% cullet. The samples
were free of graphite and a straight line connects samples from
batches heated at the respective melt temperature.
[0016] FIG. 6 shows a set of measurements of low iron,
soda-lime-silica glass laboratory samples showing the effect tin
compounds on the redox ratio. The batch was melted at 2650.degree.
F. and a straight line connects common measurements.
[0017] FIG. 7 shows a comparative set of measurements between low
iron glasses produced during a plant trial in a real furnace under
real operating conditions to low iron glasses from laboratory
melts.
[0018] FIG. 8 shows a set of measurements of high iron
soda-lime-silicate glass samples showing the effect of graphite,
temperature, tin dioxide and tin on the redox ratio. A straight
line connects common measurements.
[0019] FIG. 9 is a fragmented side view of a glass ribbon supported
on a molten tin bath.
DETAILED DESCRIPTION OF THE INVENTION
[0020] As used in the following discussion, spatial or directional
terms, such as "top", "bottom", and the like, relate to the
invention as it is shown in the drawing figures. However, it is to
be understood that the invention can assume various alternative
orientations and, accordingly, such terms are not to be considered
as limiting. Unless otherwise indicated, all numbers expressing
dimensions, physical characteristics, quantities of ingredients,
reaction conditions, and so forth used in the specification and
claims are to be understood as being modified in all instances by
the term "about". Accordingly, unless indicated to the contrary,
the numerical values set forth in the following specification and
claims can vary depending upon the desired properties sought to be
obtained by the present invention. At the very least, and not as an
attempt to limit the application of the doctrine of equivalents to
the scope of the claims, each numerical parameter should at least
be construed in light of the number of reported significant digits
and by applying ordinary rounding techniques. Moreover, all ranges
disclosed herein are to be understood to include the beginning and
ending range values and to encompass any and all subranges subsumed
therein. For example, a stated range of "1 to 10" should be
considered to include any and all subranges between (and inclusive
of) the minimum value of 1 and the maximum value of 10; that is,
all subranges beginning with a minimum value of 1 or more and
ending with a maximum value of 10 or less, e.g., 5.5 to 10.
Additionally, ail documents, such as but not limited to issued
patents and patent applications, referred to herein are to be
considered to be "incorporated by reference" in their entirety.
Further, as used herein, the term "over", means formed, applied,
deposited, or provided on but not necessarily in contact with the
surface. For example, a coating layer formed or applied "over" a
substrate surface does not preclude the presence of one or more
other coating layers or films of the same or different composition
located between the formed coating layer and the surface of the
substrate. Still further the term "on" means formed, applied,
deposited, or provided on and in contact with the surface.
[0021] In one non-limiting embodiment of the invention, the
invention is practiced making soda-lime-silica glasses having a low
iron content, e.g. but not limited to total iron Fe.sub.2O.sub.3 in
the range of greater than 0.00-0.02 wt. % and a redox ratio in the
range of 0.2-0.6, e.g. but not limited to a glass disclosed in U.S.
Pat. No. 6,962,887.
[0022] In another non-limiting embodiment of the invention, the
invention is practiced to make soda-lime-silica glasses having a
high iron Fe.sub.2O.sub.3 content, e.g. but not limited to
Fe.sub.2O.sub.3 in the range of equal to and greater than 0.1 wt. %
and a redox ratio in the range of 0.2-0.6, e.g. but not limited to
a glass disclosed in U.S. Pat. No. 6,313,053. In the practice of
the invention, any known glass making process can be use to make
the high iron, high redox ratio glass, and the low iron, high redox
ratio glass, of the invention.
[0023] Any reference to composition amounts, unless otherwise
specified, is "by weight percent" based on the total weight of the
final glass composition. The "total iron" content of the glass
compositions disclosed herein is expressed in terms of
Fe.sub.2O.sub.3 in accordance with standard analytical practice,
regardless of the form actually present. Likewise, the amount of
iron in the ferrous state is reported as FeO, even though it may
not actually be present in the glass as FeO. The terms "redox",
"redox ratio" or "iron redox ratio" mean the amount of iron in the
ferrous state (expressed as FeO) divided by the amount of total
iron in the ferric state (expressed as Fe.sub.2O.sub.3). As used
herein soda-lime-silica glasses having total iron (expressed as
Fe.sub.2O.sub.3) in the range of greater than 0 to 0.02 wt. % is a
low iron soda-lime-silica glass; glasses having total iron in the
range of equal to and greater than 0.02 to 0.10 wt. % is a medium
iron soda-lime-silica glass, and soda-lime-silica glasses having
total iron equal to and greater than 0.10 wt. % is a high iron
glass. Generally and not limiting to the invention, high iron
soda-lime-silica glasses have total iron in the range of equal to
and greater than 0.10 wt. % to 2.0 wt. %; equal to and greater than
0.10 wt. % to 1,5 wt. %; equal to and greater than 0.10 wt. % to
0.10 wt. %; and equal to and greater than 0.10 wt. % to 0.80 wt.
%.
[0024] The high redox ratio is in the range of equal to 0.2 to 0.6,
the invention, however, is not limited thereto and contemplates
ranges of 0.3 to 0.6, 0.4 to 0.6 and 0.5 to 0.6. The glass
disclosed in U.S. Pat. No. 6,962,887 has a redox ratio in the range
of 0.2-0.6 and a total iron (expressed as Fe.sub.2O.sub.3) in the
range of greater than 0 to equal to 0.02 wt. % and is a low iron
soda-lime-silica glass. The glass disclosed in U.S. Pat. No.
6,313,053 has a redox ratio in the range of 0.2-0.6 and a total
iron (expressed as Fe.sub.2O.sub.3) in the range equal to 0.10 wt.
% to 0.90 wt. % and is a high iron soda-lime-silica glass.
[0025] As can now be appreciated, the invention is directed to
making high iron, high redox soda-lime-silica glasses and low iron,
high redox soda-lime-silica glasses and is not limited to the
optical properties, e.g. ultra violet, visible and IR transmission
and absorption and the color of the glass and physical properties,
e.g. glass thickness. In defining a non-limiting embodiment of a
glass of the invention reference can be made to specific ranges or
values of ultra violet, visible and IR transmission and absorption,
and/or color of the glass and/or physical properties, e.g. glass
thickness to identify a specific glass of the invention end/or a
glass made by the practice of the invention. Presented below are
common additives, e.g. color additives that are added to the glass
batch materials, and/or molten glass to alter optical and physical
properties of the glasses of the invention.
[0026] The "sulfur" content of the glass compositions disclosed
herein is expressed in terms of SO.sub.3 in accordance with
standard analytical practice, regardless of the form actually
present.
[0027] As used herein, "visible transmittance" and "dominant
wavelength" values are those determined using the conventional CIE
Illuminant C and 2-degree observer angle. Those skilled in the art
will understand that properties such as visible transmittance and
dominant wavelength can be calculated at an equivalent standard
thickness, e.g., 5.5 millimeters ("mm"), even though the actual
thickness of a measured glass sample is different than the standard
thickness.
[0028] A non-limiting embodiment of the present invention is
practiced to make a low iron, high redox glass, e.g. but not
limited to the type disclosed in U.S. Pat. No. 6,962,887, that
provides an aesthetically desirable glass that is high in visible
light transmittance in a normal (i.e. perpendicular) direction to a
sheet of the glass but has an aesthetically pleasing blue or azure
edge color when viewed on edge. By "high visible light
transmittance" is meant visible light transmittance greater than or
equal to 85%, such as greater than or equal to 87%, such as greater
than or equal to 90%, such as greater than or equal to 91%, such as
greater than or equal to 92%, at 5.5 mm equivalent thickness for
glass from 2 mm to 25 mm sheet thickness. By "visible light" is
meant electromagnetic radiation having a wavelength in the range of
380 nanometers (nm) to 770 nm. By "blue edge color" or "azure edge
color" glass is meant having a dominant wavelength in the range of
480 nanometers ("nm") to 510 nm, such as in the range of 485 nm to
505 nm, such as in the range of 486 nm to 500 nm, such as in the
range of 487 nm to 497 nm, when viewed on edge at an equivalent
thickness of 5.5 mm.
[0029] In another non-limiting embodiment of the present invention,
the present invention is practiced to make a high iron
Fe.sub.2O.sub.3, high redox glass, e.g. but not limited to the type
disclosed in U.S. Pat. No. 6,313,053 that provides a blue colored
glass using a standard soda-lime-silica glass base composition and
additionally iron and cobalt, and optionally chromium, as solar
radiation absorbing materials and colorants. In particular, the
blue colored glass includes about 0.40 to 1.0 wt. % total iron
Fe.sub.2O.sub.3, preferably about 0.50 to 0.75 wt. %, about 4 to 40
PPM CoO, preferably about 4 to 20 PPM, and 0 to 100 PPM chromium
oxide ("Cr.sub.2O.sub.3"). The redox ratio for the glass of the
present invention is greater than 0.35 to 0.60, and preferably
between 0.35 to 0.50. In one particular embodiment of the
invention, the glass has a luminous transmittance of at least 55%
and a color characterized by a dominant wavelength of 485 to 489
nanometers and an excitation purity of about 3 to 18 percent. In
another embodiment of the invention, the glass has a luminous
transmittance of at least 65% at a thickness of about 0.154 inches
(3.9 mm) and a color characterized by a dominant wavelength of 486
to 492 nanometers and an excitation purity of about 3 to 18
percent.
[0030] As is appreciated, the invention is not limited to the color
additives discussed above and any color additives to a
soda-lime-silica glass known in the art can be used in the practice
of the invention, for example, but not limited to the colorants
selected from the group of CoO, Se, NiO, Cl, V.sub.2O.sub.5,
CeO.sub.2, Cr.sub.2O.sub.3, TiO.sub.2, Er.sub.2O.sub.3,
Nd.sub.2O.sub.3, MnO.sub.2, La.sub.2O.sub.3 and combinations
thereof.
[0031] As can now be appreciated, the invention is not limited to
the process of, and/or equipment for, practicing the invention to
make glasses of the invention, and any of the glass making
processes and/or equipment known in the art can be used in the
practice of the invention.
[0032] Referring to FIGS. 1 and 2 as needed, there is shown a
conventional continuously fed, cross-tank fired, glass melting and
non-vacuum refining furnace 20 having an enclosure formed by a
bottom 22, roof 24, and sidewalls 26 made of refractory materials.
The glass batch materials 28 are introduced through inlet opening
30 in an extension 32 of the furnace 20 known as the fill doghouse
in any convenient or usual manner to form a blanket 34 floating on
surface 36 of molten glass 38. Overall progression of the glass as
shown in FIGS. 1A and 1B is from left to right in the figures,
toward entrance end of a glass forming chamber 40 of the type used
in the art to make float flat glass.
[0033] Flames (not shown) to melt the batch materials 28 and to
heat the molten glass 38 issue from burner ports 42 spaced along
the sidewalls 26 (see FIG. 2) and are directed onto and across the
surface 36 of the molten glass 38. As is known by those skilled in
the art, during the first half of a heating cycle, the flames issue
from a nozzle 43 (see FIG. 2) in each of the ports on one side of
the tank 20, as the exhaust of the furnace moves through the ports
on the opposite side of the furnace. During the second half of the
heating cycle, the function of the ports is reversed, and the
exhaust ports are the firing ports, and the firing ports are the
exhaust ports. The firing cycle for furnaces of the type shown in
FIGS. 1 and 2 are well known in the art and no further discussion
is deemed necessary. As can be appreciated by those skilled in the
art, the invention contemplates using a mixture of air and fuel
gas, or a mixture of oxygen and fuel gas, to generate the flames to
heat the batch materials and the molten glass. For a discussion of
using oxygen and fuel gas in the furnace of the type shown in FIG.
1, reference can be made to U.S. Pat. Nos. 4,604,123; 6,962,887;
7,691,763, and 8,420,928, which patents are hereby incorporated by
reference.
[0034] The glass batch materials 28 as they move downstream from
the batch feeding end or doghouse end wall 46 are melted in the
melting section 48 of the furnace 20, and the molten glass 38 moves
through waist 54 to refining section 66 of the furnace 20. In the
refining section 56, bubbles in the molten glass 38 are removed,
and the molten glass 38 is mixed or homogenized as the molten glass
passes through the refining section 56. The molten glass 38 is
delivered in any convenient or usual manner from the refining
section 56 onto a pool of molten metal (not shown) contained in the
glass-forming chamber 40. As the delivered molten glass 38 moves
through the glass-forming chamber 40 on the pool of molten metal
(not shown), the molten glass is sized and cooled. A dimensionally
stable sized glass ribbon (not shown) moves out of the
glass-forming chamber 40 into an annealing lehr (not shown). Glass
making apparatus of the type shown in FIGS. 1 and 2, and of the
type discussed above are well known in the art and no further
discussion is deemed necessary.
[0035] Shown in FIG. 3 is continuously fed glass melting and vacuum
refining equipment 78 for melting glass batch materials and
refining the molten glass. Batch materials 80, preferably in a
pulverulent state, are fed into cavity 82 of a liquefying vessel,
e.g. a rotating drum 84. A layer 86 of the batch material 80 is
retained on the interior walls of the vessel 84 aided by the
rotation of the drum and serves as an insulating lining. As the
batch material 80 on the surface of the lining 84 is exposed to the
heat within the cavity 82, it forms a liquefied layer 88 that flows
out of a central drain opening 90 at the bottom 92 of the vessel 84
to a dissolving vessel 94 to complete the dissolution of unmelted
particles in the liquefied material coming from the vessel 84.
[0036] A valve 96 controls the flow of material from the dissolving
vessel 94 into a generally cylindrical vertically upright vessel 98
having an interior ceramic refractory lining (not shown) shrouded
in a gas-tight, water-cooled casing 100. A molten stream 102 of
refined glass falls freely from the bottom of the refining vessel
98 and can be passed to a subsequent stage in the glass making
process. For a detailed discussion on the operation of the
equipment 78 shown in FIG. 3 reference can be made to U.S. Pat. No.
4,792,538.
[0037] The glasses of the invention can be made using any known
glass making process. For example, but not limiting to the
invention, the low iron, and high iron, high redox glasses of the
invention can be made in the multistage melting and vacuum-assisted
refining operation shown in FIG. 3. The refining stage of this
known process is performed under a vacuum to reduce the
concentration of dissolved gasses and volatile gaseous components,
particularly sulfur-containing components. As will be appreciated
by one skilled in the art, it can be advantageous to remove
sulfur-containing components from certain float glass compositions
since the combination of sulfur with iron in the glass can result
in amber coloration of the glass at high redox ratios, for example,
iron redox ratios above 0.4, especially above 0.5, due to the
formation of ferric sulfide (also conventionally referred to as
iron sulfide or iron polysulfide). Ferric sulfide can form
throughout the bulk glass or in streaks or layers of a glass sheet.
As used herein, the term "bulk glass" means the internal portion of
a glass piece, such as a glass sheet, that is not chemically
altered in the process of forming the glass. For a 2 millimeter
("mm") or thicker glass sheet made by a float glass process, the
bulk glass does not include the outer region of the glass adjacent
the glass surface, for example the outer 25 microns (as measured
from the glass surface). The elimination of gaseous sulfur
components in the vacuum refining stage of this known process helps
prevent the formation of ferric sulfide in the glass and, thus,
helps prevent amber coloration.
[0038] In the preferred practice of the invention, the glass of the
invention is made using a conventional non-vacuum float glass
system. By "conventional" or "non-vacuum" float glass system is
meant that the molten glass is not subjected to a vacuum stage such
as that in U.S. Pat. Nos. 4,792,536 and 5,030,594 during the glass
melting or refining operations. In one embodiment of the invention,
the glass can be essentially free of sulfur. By "essentially free
of sulfur" is meant that no intentional addition of
sulfur-containing compounds is made to the glass composition.
However, trace amounts of sulfur can be present in the glass due to
impurities in the batch materials or other sources, including
cullet. By "trace amounts of sulfur" is meant sulfur in the range
of greater than 0 wt. % to 0.03 wt. %. In another embodiment,
sulfur-containing materials, such as sulfur-containing refining
aids, can be intentionally added to the glass composition, e.g., to
improve the melting characteristics of the grass batch materials.
However, in this embodiment, if such sulfur-containing materials
are intentionally added, they can be added such that the retained
sulfur content (e.g., the average amount of SO.sub.3 left in the
resultant bulk glass) is less than or equal to 0.2 wt. %, such as
less than or equal to 0.15 wt. %, such as less than 0.11 wt %, such
as less than or equal to 0.1 wt. %, such as less than or equal to
0.08 wt %, such as less than or equal to 0.05 wt. %. In one
embodiment, the residual sulfur can be in the range of 0.005 wt. %
to 0.2 wt. %.
[0039] As mentioned above and as shown. In FIGS. 1 and 2
conventional float glass systems typically include a furnace or
melter into which the glass batch materials are placed for melting.
In one practice of the invention, the melter can be an oxygen fuel
furnace in which the fuel is mixed with oxygen to supply heat to
melt the batch materials. In another practice of the invention, the
melter can be a conventional air-fuel melter in which air is mixed
with the combustion fuel to provide heat to melt the batch
materials. In a still further practice of the invention, the melter
can be a hybrid-type melter in which a conventional air-type melter
is augmented with oxygen lances to supplement the heated air with
oxygen before combustion.
[0040] One difference between glasses made from batch materials
melted in an oxygen fuel furnace and a conventional air-fuel melter
is that the glass made from batch materials melted in an oxygen
fuel furnace typically has a water content in the range of 425-600
parts per million, whereas the glass made from batch materials
melted in a conventional air-fuel melter typically has a water
content in the range of 200-400 parts per million, and glass made
from 100% cullet melted in an oxygen fuel furnace typically has a
water content of about 700 parts per million. In the preferred
practice of the invention, the glass batch materials are melted in
an oxygen fuel furnace or a conventional air-fuel melter. In the
following discussion of the invention, the invention is practiced
using an oxygen fuel furnace, however, the invention is not limited
thereto, and the invention can be practiced using any type of glass
melting system.
[0041] In one non-limited embodiment of the invention, the redox
ratio is within the range of 0.2 to 0.6, and the total iron
(Fe.sub.2O.sub.3) is within the range of greater than 0 to 0.02 wt.
%, and in another non-limited embodiment of the invention, the
redox ratio is within the range of 0.2 to 0.6, and the total iron
(Fe.sub.2O.sub.3) is within the range of 0.10 to 2.0 wt. %. In the
practice of the invention typical batch materials for making
soda-lime-silica glass are introduced into the melter, the furnace
20 shown in FIG. 1 and furnace 84 shown in FIG. 3. Typical batch
materials for a soda-lime-silica glass composition include sand,
soda ash, limestone, alumina and dolomite. As will be appreciated
by one skilled in the art, conventional soda-lime-silica batch
materials also include melting and refining aids, such as salt cake
(sodium sulfate). Salt cake can also be an oxidizer when
incorporated into the glass batch. As discussed above, the presence
of sulfur with iron can lead to amber or yellowish coloration on
the bottom surface of the float glass ribbon due to the local
formation of iron polysulfides at or near the bottom surface of the
glass. Therefore, in one aspect of the invention, to reduce
retained sulfate and subsequent coloration from iron polysulfide,
no sulfur-containing melting and refining aid materials, e.g., salt
cake, are intentionally added to the glass batch materials. Due to
the absence of the salt cake, melting the batch materials can be
more difficult than would be with the salt cake. Therefore, to
offset the absence of salt cake, the temperature in the melter can
be increased and/or the throughput of the melter can be decreased
to provide sufficient melting of the batch materials. Typical batch
materials to make a soda-lime-silicate glass can be selected to
provide a final glass product having a high iron, high redox ratio
glass, or a low iron, high redox ratio glass having the ingredients
in the weight percent ranges shown in following Table 1:
TABLE-US-00001 TABLE 1 Ingredient Range of Ingredient in Weight
Percent SiO.sub.2 65-75 Na.sub.2O 10-20 CaO 5-15 MgO 0-5
Al.sub.2O.sub.3 0-5 K.sub.2O 0-5 Sn0.sub.2 greater than 0 to 5
[0042] In the preferred non-limiting embodiment of the invention,
the redox ratio is increased by the addition of tin alone, and/or
in combination with other additives, to the glass batch materials
and/or molten glass, and/or temperature increases to melt the glass
batch materials and/or heat the molten glass, to reduce the ferric
iron (Fe+++) to the ferrous iron (Fe++). As is appreciated the
invention contemplates changing glass campaigns from making
soda-lime-silica glasses having low redox iron ratio to
soda-lime-silica glasses having high redox iron ratio, and changing
glass campaigns from making soda-lime-silica glasses having high
redox iron ratio to soda-lime-silica glasses having low redox iron
ratio.
[0043] The following discussion is directed to additives to reduce
the ferric iron (Fe+++) to the ferrous iron (Fe++) to increase the
redox ratio and/or to maintain the redox ratio in the range of 0.2
to 0.6. The glass in this non-limiting embodiment of the invention
is a low iron, high redox glass of the type disclosed in, but not
limited to U.S. Pat. No. 6,962,887. To provide the azure edge
color, a colorant portion can be added to the batch materials. In
one embodiment, the colorant portion can include one or more
iron-containing compounds with the total iron (Fe.sub.2O.sub.3)
being less than 0.02 wt. %, such as in the range of 0.007 to 0.02
wt. %. Additional or alternative colorants can include one or more
of cobalt oxide (CoO) such as in the range of 0 ppm to 5 ppm,
neodymium oxide (Nd.sub.2O.sub.3) in the range of 0 wt. % to 0.1
wt. %, and/or copper oxide (CuO) in the range of 0 wt. % to 0.03
wt. %. The redox ratio of the glass can be controlled in accordance
to the invention to be within the range of 0.2 to 0.6, such as
0.3-0.5, such as 0.4 to 0.6, such as 0.4-0.5, such as 0.6. In one
embodiment of the invention, the glass batch materials can be
essentially free of sulfur, i.e., no intentional addition of
sulfur-containing materials is made to the batch materials.
However, as will be appreciated by one skilled in the art, sulfur
could be present from other sources, such as impurities in the
batch materials and/or cullet.
[0044] If salt cake is totally eliminated from the batch materials,
in addition to increased melting difficulties, the redox ratio of
the glass can increase to the point where polysulfides can be
formed in the bulk glass, thus providing the bulk glass with an
amber tint. In order to control the redox ratio of the glass,
non-sulfur containing oxidizers can be added to the batch materials
in place of salt cake to oxidize the Fe++ to Fe+++ to decrease the
redox ratio. One non-limiting example of such a material is sodium
nitrate (NaNO.sub.3). While sodium nitrate can prevent the redox
ratio of the glass from increasing to the point where bulk
polysulfide formation results in an undesirable amber tint in the
bulk glass, sodium nitrate can lead to the production of NO.sub.x
emissions during the glass production process. These NO.sub.x
emissions can be treated in conventional manner before release of
the melter gasses to the atmosphere to meet governmental
restrictions on NO.sub.x emissions.
[0045] In a further embodiment, manganese oxide (MnO.sub.2) and
cerium oxide (CeO.sub.2) can be added to the batch materials to
control the redox. Manganese oxide is used in concentration of
0-1.0 wt. % and preferably greater than 0 to 1.0 wt. %. Cerium
oxide can be very effective even at concentrations in the range of
greater than 0 wt. % to 0.2 wt. %, such as less than or equal to
0.1 wt. %. One result of the use of cerium oxide is that it can
cause surface fluorescence when the glass is exposed to ultraviolet
light, such as that present in normal sunlight.
[0046] In a still further embodiment of the invention, rather than
completely eliminating salt cake from the batch materials, a
mixture of salt cake and one or more non-sulfur containing
oxidizing materials, such as but not limited to sodium nitrate,
manganese dioxide, and/or cerium oxide, can be added to the batch
materials to aid in melting and refining the batch materials. If
salt cake is present, the initial introduction of
non-sulfur-containing oxidizing materials can result in increased
retention of sulfate but ultimately the amount of salt cake added
to the batch materials can be controlled to provide a final glass
product that is substantially free of sulfur. By "substantially
free of sulfur" is meant that residual sulfur (i.e., SO.sub.3) in
the bulk glass is less than or equal to 0.2 wt. %, such as less
than or equal to 0.15 wt. %, such as less than or equal to 0.11 wt.
%, such as less than or equal to 0.1 wt. %, such as less than or
equal to 0.08%, such as less than or equal to 0.05 wt. %. The
utilization of both salt cake and non-sulfur containing oxidizing
agents can maintain the melting and refining conditions of the
glass batch materials and redox ratio of the glass without leading
to or promoting the undesirable formation of polysulfides at the
region adjacent the bottom of the glass.
[0047] In a still further embodiment of the invention, the melter
can be an oxygen fuel furnace. It has been observed that for batch
materials having a given level of salt cake, the retained sulfate
in the resultant glass when the batch materials are melted using an
oxygen fuel furnace is less than that retained for the same glass
batch composition using a conventional air furnace. Thus, salt cake
or another sulfur-containing oxidizer can be added to the batch
materials and melted in an oxygen fuel furnace to provide lower
retained sulfate than would be present if the same batch
composition were melted in a conventional air-fuel furnace. In this
embodiment, the sulfur-containing batch material should be added at
a level to provide a glass product that is substantially free of
sulfur.
[0048] Thus, as discussed above, the formation of undesirable amber
coloration in the glass can be reduced or eliminated by adjusting
and/or selecting the components of the glass composition. However,
in another aspect of the invention, this undesirable amber
coloration can be affected by additionally or alternatively
controlling the amount of dissolved iron in the molten metal of the
molten metal bath.
[0049] In a float glass process, molten glass flows from a furnace
onto a pool of molten tin in a float bath to form a float glass
ribbon. During the float process, oxygen from the bottom surface of
the float glass ribbon, i.e., the surface of the ribbon in contact
with the molten tin, can diffuse into the molten tin. Consequently,
multivalent ions at the bottom surface of the glass can become
chemically reduced. For example, sulfur in or near the bottom
surface of the glass can be reduced from S.sup.+6 (hexavalent
sulfur) to S.sup.-2 (sulfide). These sulfides can react with iron,
particularly ferric iron (Fe.sup.+3), to form iron polysulfides at
the bottom surface of the glass ribbon. The iron can already be
present in the glass or, in some instances, iron present in the
molten tin can diffuse into the bottom surface of the glass to
react with the sulfides. Iron polysulfide is a powerful colorant
and can produce a region or layer of amber color several microns
thick on the bottom of the glass ribbon. Thus, if one were to look
through the edge of the resultant glass sheet at an oblique angle,
the region of amber coloration on the bottom of the glass can make
blue glass appear green or yellowish-green. This perceived color
shift of the glass edge at oblique viewing angles is not
aesthetically desirable for most applications. The undesirable
effect of amber coloration on the bottom surface of the glass can
also be present in other tinted glass, such as those having a bulk
glass color of green or bluish green.
[0050] As will be appreciated by one of ordinary skill in the glass
making art, medium iron float glass and low iron float glass is
particularly susceptible to an iridescent bloom formation on the
bottom surface. During the float glass forming process, tin oxide
(SnO) from the tin bath can diffuse into the bottom surface of the
float glass ribbon. When the resultant glass is reheated in the
presence of oxygen, e.g., air, such as during bending, tempering,
or sagging operations, highly concentrated tin oxide (SnO) on the
bottom surface of the glass can oxidize to form tin dioxide
(SnO.sub.2). The subsequent microscopic volume expansion can cause
the appearance of an iridescent haze on the glass. U.S. Pat. No.
3,305,337 teaches adding certain reactive elements, including iron,
to the tin bath can capture oxygen, thus reducing the migration of
tin oxide into the bottom of the glass and, therefore, the
potential for bloom formation. Under equilibrium conditions, a
given concentration of iron in the molten tin will be reached as a
function of the concentration of iron in the glass. For example,
while producing a medium iron float glass with a concentration of
0.1 wt. % iron oxide, the equilibrium concentration of iron in the
molten tin bath can be about 0.01 wt. % Fe. If the concentration of
iron in the tin is increased to 0.04 wt. % by a deliberate addition
of iron to reduce the potential for bloom formation, increased
diffusion of iron from the tin bath into the bottom surface of the
glass can raise the average concentration of iron in the bottom
surface of the glass to about 0.2 wt. % iron oxide. This additional
iron in the bottom surface of the glass can react with sulfur
(particularly sulfides S.sup.-2) to form iron polysulfides to
produce an amber color center. Therefore, in order to decrease the
formation of the iron polysulfide color centers at the bottom
surface of the glass, the molten tin is substantially free of iron.
By "substantially free of iron" is meant that no or substantially
no iron is intentionally added to the molten tin. In one
embodiment, the concentration of iron (Fe) in the molten fin is
less than or equal to 0.05 wt. %, such as less than or equal to
0.04 wt. %, such as less than or equal to 0.03 wt. %, such as less
than or equal to 0.02 wt. %, such as less than or equal to 0.01 wt.
% based on the total weight of the molten metal. Therefore, in one
aspect of the invention, no iron is intentionally added to the
molten tin, e.g., for two or more months prior to or during
production of the low iron glass of the invention.
[0051] As will be appreciated by one skilled in the art, even
though no iron may be intentionally added to the molten tin, iron
concentrations greater than those desired above could still be
present in the molten fin as a consequence of the previous
production of glass having a higher iron content than the desired
ranges disclosed above. Therefore, the molten tin can be treated,
e.g., cleaned, to remove dissolved iron as disclosed in U.S. Pat.
No. 6,962,887.
[0052] The discussion is now directed to non-limiting embodiments
of the invention to increase the redox ratio by the addition of tin
and fin containing compounds to the glass batch materials and/or to
the molten glass to reduce the ferric iron (Fe+++) to the ferrous
iron (Fe++). In the preferred practice of the invention, fin and/or
tin containing compounds are added to the glass batch materials
and/or molten glass in any convenient manner, e.g. but not limited
to (1) adding SnO.sub.2 and/or tin sulfate ("SnS") to the glass
batch materials as a dry powder; (2) adding pellets of SnO.sub.2 to
the glass batch materials; (3) adding glass cullet to the batch
material, the cullet having a coating of SnO.sub.2 over and/or on a
glass surface and/or glass cullet having tin and/or tin containing
compounds within the body of the glass; (4) adding ground particles
of tin and/or tin containing compounds, e.g. but not limited to Sn,
SnO.sub.2, and SnS to the glass batch materials; (6) mixing dry
SnO.sub.2 with a liquid to make a slurry and adding the slurry to
the batch materials; (7) bubble fin containing gas, e.g. but not
limited thereto tin halogens, e.g. but not limited to tin chloride
("SnCl.sub.4") into the molten glass in the furnace or melter using
the bubblers 150 shown in FIGS. 1A and 2, (8) adding organo-tin
compounds and organo-tin compounds containing halogens, e.g. but
not limited to Sn(C.sub.4H.sub.9).sub.3H.
[0053] In the preferred practice of the invention, tin and/or tin
dioxide is added to the glass batch and molten glass in the furnace
20 (FIG. 1A) or melter 84 (FIG. 3); the invention, however, is not
limited thereto and tin oxides, tin oxynitrides, tin nitrides, tin
halogens, to name a few and combinations thereof can be added to
provide tin ions to increase the redox ratio.
[0054] It is believed that the reaction to reduce the ferric iron
(Fe+++) to the ferrous iron (Fe++) in the resultant glass is better
appreciated by the following discussion:
Sn.sup.4+=Sn.sup.2++2e.sup.- Equation 1
Sn.sup.2++2Fe.sup.3++2e.sup.-=Sn.sup.4++2Fe.sup.2+ Equation 2
Equations Discussion:
[0055] Equation shows reactions believed to occur where the
Sn.sup.4+ ions (SnO.sub.2) that are added at room temperature
become reduced to Sn.sup.2+ ions (SnO) plus two electrons when the
material is heated and incorporated into the glass structure. Those
2 electrons from the single Sn.sup.4+ on can facilitate reduction
of two ferric iron (Fe+++) ions to two ferrous iron (Fe++) ions
while the glass is cooling as shown in Equation 2. Essentially the
Sn.sup.2+ ions prefer the Sn.sup.4+ state at some temperature lower
than melting temperatures and thus reduction of the iron ions
occurs while the ions can still transfer charge.
[0056] Laboratory melts were made to determine the effect of tin
alone or in combination with temperature changes and/or graphite.
The batch for the soda-lime-silica glass included the material
listed in TABLE 2 below:
TABLE-US-00002 TABLE 2 Material Amount Low iron sand 369.44 grams
Soda Ash 119.96 grams Low iron Limestone 38.83 grams Low iron
dolomite 73.36 grams Graphite (when added) 0.303 grams Iron oxide
from sand 70 parts per million
[0057] The batch materials were heated in 50.degree. F. steps
within a temperature range 2450.degree. F. to 2600.degree. F. in a
platinum crucible. The batch was heated for a period of 1/2 hour at
each step and for 1 hour at 2600.degree. F. The melted batch was
fritted (placed in water) and placed in a platinum crucible and
heated to a temperature of 2650.degree. F. or 2800.degree. F. (as
noted below), and held at that temperature for 2 hours. The melt
was poured on a metal sheet and annealed at a temperature near
1130.degree. F. Specimens were cut from the annealed glass and the
redox ratio of the specimens determined. Preparing laboratory glass
samples and determining the redox ratio of soda-lime-glass are well
known in the art and no further discussion is deemed necessary.
[0058] It has been concluded from the results of the laboratory
melts that temperature and/or carbon based reducing agents, e.g.
but not limited to graphite, in combination with tin dioxide
(SnO.sub.2) have an effect on reducing the ferric iron (Fe+++) to
the ferrous iron (Fe++) to increase the redox ratio. More
particularly and with reference to FIGS. 4-7 as needed there is
shown connected data points providing graph curves for
soda-lime-silica low iron containing glass. The graph curves 130,
132, 134, and 136 of FIG. 4 show connected data points for samples
having varying amounts of tin dioxide in the range of 0 to 0.2 wt.
%. and graphite in the amounts of 0 wt. % (curve 136), 0.025 wt. %
(curve 134), 0.050 wt. % (curve 132) and 0.075 wt. % (curve 130).
The glass samples were heated to a temperature of 2650.degree. F.
Graph curve 136 shows the increase of the redox ratio by increasing
the tin dioxide and having 0 wt. % graphite. The data points for
the graph curves 130, 132, 134, and 136 at 0 wt. % tin dioxide
shows an increase in the redox ratio for increases of graphite. The
graph curves 130, 132, 134, and 136 show an increase in the redox
ratio for increases in graphite and tin dioxide that out perform
increases of graphite and tin dioxide alone.
[0059] FIG. 5 shows three graph curves 136, 138 and 140 for samples
that did not contain graphite additions to highlight the effects of
temperature. The graph curve 136 is also shown in FIG. 4 and shows
an increase in the redox ratio by increasing the tin dioxide. In
FIG. 5 the graph curve 136 shows an increase in the redox ratio as
the tin dioxide is increased and the redox ratio for glass melted
at 2650.degree. F. Graph curve 138 shows an increase in the redox
ratio as the tin dioxide increases with a melting temperature of
2800.degree. F. The graph curves 136 and 138 show an increase in
the redox ratio for a higher melting temperature, and tin dioxide
that out perform the lower melting temperature and tin dioxide. The
graph curve 140 shows data points for melted glass cullet having
tin dioxide alone. Graph curve 140 shows that tin dioxide can be
added to the glass batch by additions of glass containing tin
oxide, e.g. glass having a coating of tin oxide and/or tin dioxide
within the body of the glass.
[0060] The graph curves of FIG. 6 include the graph curves 132,
142, 144 and 146 to show the performance of tin dioxide (curve
146), tin oxide (curve 142) and tin metal (curve 144) compared to
graph curve 137 discussed above. From the data points shown in FIG.
6 the tin metal provides the highest redox ratio. In one
non-limiting embodiment of the invention SnO.sub.2 in the glass
composition is in the range of greater than 0 to 0.70 wt. %, and
preferably greater than zero to 0.60 wt. % or greater than 0.015 to
0.58 wt. %. The SnO.sub.2 in addition to increasing the redox ratio
is expected to act as a fining agent and reduce the seeds in the
glass.
[0061] FIG. 7 shows a comparative set of measurements between low
iron glasses (graph curve 148) produced during a plant trial in a
real furnace under real operating conditions to low iron glasses
from laboratory melts (graph curves 132, 136-138 and 140). The
results from the plant trial indicate the laboratory samples can be
used to describe the effects of SnO.sub.2 concentration on iron
redox under real processing conditions. The redox is higher for the
plant trial due to higher furnace temperatures near 2950.degree. F.
vs. the highest temperature of 2800.degree. F. in the laboratory.
The plant trial samples were made under the following operating
conditions: 490 tons of glass per day, SnO.sub.2 was added as dry
powder to a slurry and mixed into the batch materials, .about.15%
cullet that did not have SnO.sub.2, melting temperature near
2950.degree. F., water content in the glass near 500 ppm, floated
and formed on a tin bath, glass was annealed.
[0062] With reference to FIG. 8 there is shown a set of graph
curves 150-154 showing changes in the redox ratio for changes in
tin dioxide for high iron glasses with Fe.sub.2O.sub.3 content near
0.52wt. %. The graph curves 150-154 provide data on redox effects
from tin dioxide content, temperature changes and changes in wt. %
of graphite. More particular, the graph curve 150 shows redox
changes with tin additions, the glass melted at 2650.degree. F. and
no graphite; the graph curve 151 shows redox changes with tin
additions, the glass melted at 2800.degree. F. and has no graphite;
the graph curve 152 shows redox changes with tin additions, the
glass melted at 2650.degree. F. and 0.05 wt. % graphite; the graph
curve 153 shows redox changes with tin additions, the glass melted
at 2650.degree. F. and 0.10 wt. % graphite, and the graph curve 164
shows redox changes with tin additions, the glass melted at
2650.degree. F. and 0.15 wt. % graphite. The data point 152A
provides a base line for 0 wt. % tin dioxide.
[0063] From the information provided by FIGS. 4-8, it can now be
appreciated that the invention is not limited by the amount of tin
and/or tin containing compound added to oxidize the ferrous iron
(Fe++) to ferric iron (Fe+++) to reduce the redox ratio of the
glass being made. More particularly Sn and tin containing compounds
can be used alone, in combination with carbon, e.g. but not limited
graphite, coal and/or oil, altering the glass batch melting
temperature and combinations thereof. In the practice of
non-limiting embodiments of the invention, the tin and tin
containing compounds provide tin in the range of greater than zero
to 5 wt. %; 0.10 to 4 wt. %, 0.4 to 3 wt. % and any wt. % within
the rages recited.
[0064] Shown in Tables 3-7 is a range of glass compositions and
approximate batch component ranges with SnO.sub.2 and/or graphite
to make the low iron, high redox ratio glass of the invention,
[0065] Table 3 is a range of glass compositions including SnO.sub.2
and graphite, and corresponding batch ingredients to make the
glass.
TABLE-US-00003 TABLE 3 Min Max Minimum Maximum Ingredient (lbs)
(lbs) Ingredient Wt. % Wt. % sand 1000 1000 SiO.sub.2 65.00 80.00
soda ash 200 400 Na.sub.2O 10.00 20.00 limestone 40 100 CaO 5.00
15.00 dolomite 100 400 MgO 0.00 8.00 salt cake 0 20 SO.sub.3 0.00
1.000 SnO.sub.2 0.07 40 Fe.sub.2O.sub.3 0.00 0.0200 graphite 0 8
Al.sub.2O.sub.3 0.00 5.00 K.sub.20 0.00 5.00 SnO.sub.2 0.0050
2.00
[0066] Table 4 is a glass composition and approximate batch
ingredient weights without SnO.sub.2 and with graphite.
TABLE-US-00004 TABLE 4 Ingredients lbs. Ingredient Wt. Wt. % sand
1000.00 SiO.sub.2 997.50 73.30 soda ash 316.00 Na.sub.2O 188.06
13.82 limestone 88.00 CaO 120.42 8.85 dolomite 234.00 MgO 51.45
3.78 salt cake 9.50 SO.sub.3 2.67 0.197 graphite 1.00
Fe.sub.2O.sub.3 0.10 0.0077 Al.sub.2O.sub.3 0.50 0.04
[0067] Table 5 is a preferred glass composition and approximate
batch ingredient weights with SnO.sub.2 and graphite.
TABLE-US-00005 TABLE 5 Ingredients lbs. Ingredient Wt. Wt. % sand
1000.00 SiO.sub.2 997.50 73.18 soda ash 320.00 Na.sub.2O 190.39
13.97 limestone 80.00 CaO 117.76 8.84 dolomite 240.00 MgO 52.72
3.87 salt cake 9.50 SO.sub.3 2.67 0.196 SnO.sub.2 0.70
Fe.sub.2O.sub.3 0.31 0.0230 Graphite 0.70 Al2O.sub.3 0.50 0.04
SnO.sub.2 0.6913 0.0507
[0068] Table 6 shows a preferred range of colorants and/or redox
controlling agents:
TABLE-US-00006 TABLE 6 Ingredients Amount Nd.sub.2O.sub.3 0-0.1 wt.
% CoO 0-40 ppm Fe.sub.2O.sub.3 0-0.02 wt. % Cr.sub.2O.sub.3 0-0.05
wt. % TiO.sub.2 0-0.05 wt. % CeO.sub.2 0-1 wt. % MnO.sub.2 0-1 wt.
%
[0069] The invention contemplates the lower range of all or
selected ones of the ingredients of Table 6 to have a lower range
of greater than 0.
[0070] Shown in Table 7 is an example of a glass composition of the
invention with 0.075 wt. % graphite in the batch and 0.1 wt. % tin
dioxide added to the batch with a melting temperature of
2650.degree. F. and the performance:
TABLE-US-00007 TABLE 7 Ingredient Ingredient in wt. % SiO.sub.2
73.11 Na.sub.2O 13.65 K.sub.2O 0.1 CaO 8.68 MgO 3.16
A.sub.l2O.sub.3 0.03 Fe.sub.2O.sub.3 0.0097 SrO 0.02 SO.sub.3 0.2
ZrO.sub.2 0.001 FeO/Fe.sub.2O.sub.3 0.505 SnO.sub.2 0.111
[0071] The glass sample in Table 7 had an LTA of at least 91.23%; a
dominant wavelength in the range of 490-500, e.g. 496.66
nanometers; an excitation purity in the range of 0.10 to 0.15, e.g.
0.14%; a TSUV in the range of 85-93%, e.g. 89.07%; a TSIR in the
range of 85-90%, e.g. 87.82% and a TSET in the range of 87-91%,
e.g. 89.43% at a thickness of 5.6 mm. Similar compositions would be
expected to exhibit LTA greater than or equal to 85%, DW in the
range of 480 nm to 510 nm at 5.5 mm equivalent thickness for glass
from 2 mm to 25 mm sheet thickness. The radiation transmittance
data would be based on TSUV 300-390 nanometers; LTc 400-770
nanometers and TSIR 800-2100 nanometers.
[0072] In another non-limiting embodiment of the present invention,
the present invention is practiced to make a high iron
Fe.sub.2O.sub.3, high redox glass, e.g. but not limited to the type
disclosed in U.S. Pat. No. 6,313,053 that provides a blue colored
glass using a standard soda-lime-silica glass base composition and
additionally iron and cobalt, and optionally chromium, as solar
radiation absorbing materials and colorants. In particular, the
blue colored glass includes about 0.40 to 1.0 wt. % total iron
Fe.sub.2O.sub.3, preferably about 0.50 to 0.75 wt. %, about 4 to 40
PPM CoO, preferably about 4 to 20 PPM, and 0 to 100 PPM chromium
oxide ("Cr.sub.2O.sub.3"). The redox ratio for the glass of the
present invention is greater than 0.2 to 0.60, and preferably
between 0.35 to 0.50. In one particular embodiment of the
invention, the glass has a luminous transmittance of at least 55%
and a color characterized by a dominant wavelength of 485 to 489
nanometers and an excitation purity of about 3 to 18 percent. In
another embodiment of the invention, the glass has a luminous
transmittance of at least 65% at a thickness of about 0.154 inches
(3.9 mm) and a color characterized by a dominant wavelength of 485
to 492 nanometers and an excitation purity of about 3 to 18
percent.
[0073] Shown in Tables 8-12 are a range of glass compositions and
approximate batch component ranges with SnO.sub.2 and graphite
compositions and approximate batch component ranges with SnO.sub.2
and graphite to make the high iron, high redox ratio glass of the
invention.
[0074] Table 8 is a range of glass compositions including SnO.sub.2
and excluding graphite, and corresponding batch ingredients to make
the glass.
TABLE-US-00008 TABLE 8 Min Max Minimum Maximum Ingredient (lbs)
(lbs) wt. % wt. % sand 1000 1000 SiO.sub.2 65.00 80.00 soda ash 200
400 Na.sub.2O 10.00 20.00 limestone 40 100 CaO 5.00 15.00 dolomite
100 400 MgO 0.00 8.00 salt cake 0 20 SO.sub.3 0.10 1.00 SnO.sub.2
0.07 77 Fe.sub.2O.sub.3 0.10 2.0 graphite 0 8 Al.sub.2O.sub.3 0.00
5.00 rouge 0 33 K.sub.20 0.00 5.00 SnO.sub.2 0.0050 5.0
[0075] Table 9 is a glass composition and approximate hatch
ingredient weights without SnO.sub.2 and with graphite.
TABLE-US-00009 TABLE 9 Ingredient lbs. wt. wt % sand 1000.00
SiO.sub.2 997.50 72.83 soda ash 316.00 Na.sub.2O 188.06 13.73
limestone 88.00 CaO 120.42 8.79 dolomite 234.00 MgO 51.45 3.76 salt
cake 9.50 SO.sub.3 2.67 0.195 graphite 2 Fe.sub.2O.sub.3 6.87 0.502
rouge 6.8 Al.sub.2O.sub.3 2.00 0.15
[0076] Table 10 is a preferred glass composition and approximate
batch ingredient weights with graphite and SnO.sub.2.
TABLE-US-00010 TABLE 10 Ingredient wt. wt. % sand 1000.00 SiO.sub.2
997.55 71.89 soda ash 320.00 Na.sub.2O 190.39 13.72 limestone 80.00
CaO 117.76 8.49 dolomite 240.00 MgO 52.72 3.80 salt cake 9.50
SO.sub.3 2.67 0.193 SnO.sub.2 17.42 Fe.sub.2O.sub.3 6.49 0.488
Graphite 1 Al.sub.2O.sub.3 2.00 0.14 rouge 6.4 SnO.sub.2 17.20
1.23
[0077] Table 11 shows preferred ranges of colorants and/or redox
controlling agents.
TABLE-US-00011 TABLE 11 Ingredients Amount Nd.sub.2O.sub.3 0-0.5 wt
% CoO 0-80 ppm Fe.sub.2O.sub.3 0.01-2.0 wt % Cr.sub.2O.sub.3 0-1 wt
% TiO.sub.2 0-1 wt % CeO.sub.2 0-1 wt % MnO.sub.2 0-1 wt %
[0078] The invention contemplates the lower range of all or
selected ones of the ingredients of Table 11 to have a lower range
of greater than 0.
[0079] Shown in Table 12 is an example of a glass composition of
the invention and the expected performance.
TABLE-US-00012 TABLE 12 Ingredients Ingredients in wt. % SO.sub.2
71.83 Na.sub.2O 13.94 K.sub.2O 0.07 CaO 8.73 MgO 3.8
Al.sub.2O.sub.3 0.07 Fe.sub.2O.sub.3 0.515 SrO 0.003 SO.sub.3 0.18
ZrO.sub.2 0.0012 FeO/Fe.sub.2O.sub.3 0.559 SnO.sub.2 0.828
[0080] The glass sample in Table 12 had an LTA of at least 65.19%;
a dominant wavelength in the range of 485-490 nanometers, e.g.
487.95 nanometers; an excitation purity in the range of 10-15%,
e.g. 13.13%; a TSUV in the range 45-50%, e.g. 48.46%; a TSIR in the
range of 7-9%, e.g. 8.25% and a TSET in the range of 32-36%, e.g.
34.59% at a thickness of 5.6 mm. Similar samples are expected to
have a redox of greater than 0.35 up to about 0.60, a luminous
transmittance of at least 55 percent, and a color characterized by
a dominant wavelength of 485 to 489 nanometers and an excitation
purity of about 3 to 18 percent, and wherein the glass has a total
solar ultraviolet transmittance of about 60 percent or less, a
total solar infrared transmittance of about 35 percent or less and
a total solar energy transmittance of about 55 percent or less at a
thickness of about 0.154 inches.
[0081] As can be appreciated, the invention is not limited to the
non-limited embodiments of the invention disclosed herein and the
invention can be practiced on glasses having medium wt. % of total
iron, e.g, greater than 0.02 to less than 0.10 wt. %, and having
redox ratio less than 0.2 to 0.6.
[0082] With reference to FIG. 9, as can be appreciated by those
skilled in the art, the glass of the invention made using the float
process, which includes supporting and advancing a glass ribbon 170
on a molten tin bath 172 while controllably cooling and applying
forces to the glass ribbon 170 has an air side 174 and an opposite
tin side 176. The tin side 176 is the side of the glass ribbon 170
supported on the molten tin bath 172. The tin dioxide concentration
generally is higher at the tin side 176 (tin dioxide concentration
at the tin side 172 designated by the number 178) of the glass
ribbon 170 than the tin dioxide concentration in body portion 180
of the glass ribbon 170. A reason for the difference in tin
concentration is that the tin dioxide concentration 178 at the tin
side 176 of the glass ribbon 170 includes the tin added to the
batch and/or molten glass to maintain a high redox ratio for the
glass ribbon 170 and the tin from the tin bath 172 that diffuses
into the tin side 176 of the glass ribbon 170 as discussed above;
whereas, the tin concentration in the body portion 180 of the glass
ribbon is the tin dioxide added to the batch and/or molten glass to
maintain a high redox ratio for the glass ribbon 170. As can be
appreciated the transition between the tin dioxide concentration at
the tin side 176 and the tin concentration in the body portion 180
is shown in FIG. 8 as a straight line 182 for purposes of clarity;
however, the transition 182 is not a straight line but a gradual
transition having decreasing concentration of tin as the distance
from the surface 184 of the tin side increases. Further as the
thickness of the glass ribbon increases, the thickness of the tin
dioxide concentration at the tin side of the glass ribbon can
increase. As can now be appreciate, the addition of tin and/or tin
containing compounds may result in tin being extracted from the tin
side of the ribbon resulting in the concentration of the tin ions
at the tin side of the ribbon being equal to or less than the tin
ions in the air side of the glass ribbon.
[0083] It will be readily appreciated by those skilled in the art
that modifications can be made to the invention without departing
from the concepts disclosed in the foregoing description.
Accordingly, the particular embodiments described in detail herein
are illustrative only and are not limiting to the scope of the
invention, which is to be given the full breadth of the appended
claims and any and all equivalents thereof.
* * * * *