U.S. patent application number 14/347140 was filed with the patent office on 2014-08-21 for polylactic acid-based resin expanded beads and molded article thereof.
This patent application is currently assigned to JSP CORPORATION. The applicant listed for this patent is JSP CORPORATION. Invention is credited to Masaharu Oikawa, Mitsuru Shinohara.
Application Number | 20140235741 14/347140 |
Document ID | / |
Family ID | 47995123 |
Filed Date | 2014-08-21 |
United States Patent
Application |
20140235741 |
Kind Code |
A1 |
Shinohara; Mitsuru ; et
al. |
August 21, 2014 |
POLYLACTIC ACID-BASED RESIN EXPANDED BEADS AND MOLDED ARTICLE
THEREOF
Abstract
Polylactic acid-based resin expanded beads of the present
invention are obtained by releasing a softened, pressurized
foamable resin composition, which comprises a polylactic acid-based
resin and a physical blowing agent, to a low pressure atmosphere to
foam and expand the resin composition, wherein the polylactic
acid-based resin satisfies the conditions (1) to (3) shown below,
and exhibits excellent secondary expansion properties and fusion
bonding properties. A polylactic acid-based resin expanded beads
molded article obtained by in-mold molding of the polylactic
acid-based resin expanded beads exhibits excellent mechanical
properties. MT.ltoreq.30 mN (1) log MT.ltoreq.0.93 log .eta.-1.75
(2) CT.sub.1/2.gtoreq.600 sec (3) where MT represents a melt
tension [mN] at 190.degree. C., .eta. represents a melt viscosity
[Pas] at 190.degree. C. and a shear speed of 20 sec.sup.-1, and
CT.sub.1/2 represents a half crystallization time [sec] at
110.degree. C.
Inventors: |
Shinohara; Mitsuru;
(Yokkaichi-shi, JP) ; Oikawa; Masaharu;
(Yokkaichi-shi, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
JSP CORPORATION |
Tokyo |
|
JP |
|
|
Assignee: |
JSP CORPORATION
Tokyo
JP
|
Family ID: |
47995123 |
Appl. No.: |
14/347140 |
Filed: |
August 30, 2012 |
PCT Filed: |
August 30, 2012 |
PCT NO: |
PCT/JP2012/071956 |
371 Date: |
March 25, 2014 |
Current U.S.
Class: |
521/182 |
Current CPC
Class: |
C08J 9/18 20130101; C08J
9/12 20130101; C08J 9/232 20130101; C08J 2300/16 20130101; C08J
2333/02 20130101; C08G 63/08 20130101; C08J 9/122 20130101; C08J
2367/04 20130101 |
Class at
Publication: |
521/182 |
International
Class: |
C08G 63/08 20060101
C08G063/08 |
Foreign Application Data
Date |
Code |
Application Number |
Sep 28, 2011 |
JP |
2011-212209 |
Claims
1-5. (canceled)
6. Polylactic acid-based resin expanded beads obtained by releasing
a softened, pressurized foamable resin composition, which comprises
a polylactic acid-based resin and a physical blowing agent, to a
low pressure atmosphere to foam and expand the resin composition,
wherein the polylactic acid-based resin satisfies the following
conditions (1) to (3): MT.ltoreq.30 mN (1) log MT.ltoreq.0.93 log
.eta.-1.75 (2) CT.sub.1/2.gtoreq.600 sec (3) where MT represents a
melt tension [mN] of the polylactic acid-based resin at 190.degree.
C., .eta. represents a melt viscosity [Pas] of the polylactic
acid-based resin at 190.degree. C. and a shear speed of 20
sec.sup.-1, and CT.sub.1/2 represents a half crystallization time
[sec] of the polylactic acid-based resin at 110.degree. C.
7. The polylactic acid-based resin expanded beads as recited in
claim 6, wherein the polylactic acid-based expanded resin beads,
when measured by the below-mentioned heat flux differential
scanning calorimetry, give a first time DSC curve and a second time
DSC curve, wherein the second time DSC curve has a fusion peak
having a reference peak top temperature, wherein the first time DSC
curve has both a first fusion peak(s) with a peak top temperature
that is on a high temperature side which is higher than the
reference peak top temperature and a second fusion peak(s) with a
peak top temperature that is on a low temperature side which is not
higher than the reference peak top temperature, and wherein the
first and second time DSC curves are measured and defined as
follows: (a) a test DSC curve of a test sample of the expanded
polylactic acid-based resin beads is measured according to a heat
flux differential scanning calorimetry method referenced in JIS
K7122 (1987), by heating the test sample at a heating rate of
10.degree. C./minute from 23.degree. C. to a temperature higher by
30.degree. C. than the temperature at which an endothermic peak
ends, thereby obtaining the first time DSC curve; (b) the test
sample is then maintained for 10 minutes at the temperature higher
by 30.degree. C. than the temperature at which the endothermic peak
ends in the first time DSC curve; (c) the test sample is then
cooled to 30.degree. C. at a cooling rate of 10.degree. C./minute;
and (d) the test sample is then measured again by being heated at a
heating rate of 10.degree. C./minute to a temperature higher by
30.degree. C. than the temperature at which the endothermic peak
ends, thereby obtaining the second time DSC curve.
8. The polylactic acid-based resin expanded beads as recited in
claim 7, wherein the first fusion peak(s) with the peak top
temperature which is on a higher temperature side which is higher
than the reference peak top temperature has a calorific value of 1
to 8 J/g.
9. The polylactic acid-based resin expanded beads as recited in
claim 6, wherein the polylactic acid-based resin expanded beads
have an apparent density of 24 to 240 g/L.
10. A polylactic acid-based resin expanded beads molded article
obtainable by molding the polylactic acid-based resin expanded
beads according to claim 6 in a mold cavity, said molded article
having a density of 15 to 150 g/L and satisfying the following
formula: (Bending modulus (MPa) of the expanded beads molded
article)/(Density (g/L) of the expanded beads molded
article).gtoreq.0.20 (MPaL/g).
11. A polylactic acid-based resin expanded beads molded article
obtainable by molding the polylactic acid-based resin expanded
beads according to claim 7 in a mold cavity, said molded article
having a density of 15 to 150 g/L and satisfying the following
formula: (Bending modulus (MPa) of the expanded beads molded
article)/(Density (g/L) of the expanded beads molded
article).gtoreq.0.20 (MPaL/g).
12. A polylactic acid-based resin expanded beads molded article
obtainable by molding the polylactic acid-based resin expanded
beads according to claim 8 in a mold cavity, said molded article
having a density of 15 to 150 g/L and satisfying the following
formula: (Bending modulus (MPa) of the expanded beads molded
article)/(Density (g/L) of the expanded beads molded
article).gtoreq.0.20 (MPaL/g).
13. A polylactic acid-based resin expanded beads molded article
obtainable by molding the polylactic acid-based resin expanded
beads according to claim 9 in a mold cavity, said molded article
having a density of 15 to 150 g/L and satisfying the following
formula: (Bending modulus (MPa) of the expanded beads molded
article)/(Density (g/L) of the expanded beads molded
article).gtoreq.0.20 (MPaL/g).
Description
FIELD OF THE INVENTION
[0001] The present invention relates to polylactic acid-based resin
expanded beads and to a molded article thereof. More specifically,
the present invention is directed to polylactic acid-based resin
expanded beads having excellent in-mold moldability and capable of
producing an in-mold molded article having excellent mechanical
properties, and to a molded article thereof.
BACKGROUND ART
[0002] In recent years, with an increase of sensitivity to global
environment, a polylactic acid-based resin receives attention as a
material that is a substitute for general resins produced from the
conventional petroleum resources. The polylactic acid-based resin
is produced from a plant such as corn as a starting material and is
a thermoplastic resin that is regarded as being of a low
environmental load type from the standpoint of carbon neutral. Such
a polylactic acid-based resin is expected to be used as a
plant-derived general resin for foams. Thus studies are being made
on foams made of polylactic acid-based resins as a raw material.
Among such foams, polylactic acid-based resin expanded beads molded
articles can be obtained by in-mold molding in any desired shape
without restriction, similar to conventional polystyrene resin
expanded beads molded articles. Such molded articles are
particularly promising in that they are likely to allow easy design
of properties according to the aimed lightness in weight,
cushioning property and heat insulating property. In this
circumstance, inventions of Patent Documents 1 to 6 have been
hitherto made.
[0003] Patent Documents 1 to 5 describe that a gas impregnation
pre-expansion method was adopted in an attempt to obtain polylactic
acid-based expanded beads.
PRIOR ART DOCUMENTS
Patent Document
[0004] Patent Document 1: Japanese Kokai Publication No.
JP-A-2000-136261 [0005] Patent Document 2: Japanese Kokai
Publication No. JP-A-2004-83890 [0006] Patent Document 3: Japanese
Kokai Publication No. JP-A-2006-282750 [0007] Patent Document 4:
Japanese Kokai Publication No. JP-A-2006-282753 [0008] Patent
Document 5: Japanese Kokai Publication No. JP-A-2009-62502 [0009]
Patent Document 6: Japanese Kokai Publication No.
JP-A-2007-100025
SUMMARY OF THE INVENTION
Problems to be Solved by the Invention
[0010] An expanded beads molded article disclosed in Patent
Document 1 and obtained by expanding gas-impregnated resin
particles is found to have significant variation of the density
when portions thereof are compared to each other. Further, fusion
bonding between expanded beads and the dimensional stability of the
article are not sufficient, and mechanical properties thereof are
not satisfactory.
[0011] Polylactic acid-based resin expanded beads obtained by
pre-expanding the gas-impregnated resin particles disclosed in
Patent Documents 2 to 4 show an improvement in fusion bonding
property between the expanded beads and in secondary expandability
during in-mold molding stage. There is, however, a room for further
improvement in fusion bonding property in view of the fact that,
when a molded article having a complicated shape is intended to be
obtained, the fusion bonding between the expanded beads is
occasionally not sufficient and that, when the molded article
having a large thickness is intended to be obtained, the fusion
bonding between the expanded beads in a center region of the molded
article is not sufficient.
[0012] Expanded beads obtained by the method which is disclosed in
Patent Document 5 and which is similar to that of Patent Documents
2 to 4 have good fusion bonding property between the expanded beads
and permit the production of molded articles having a large
thickness or a complicated shape. However, the expanded beads have
a problem in production efficiency because it is necessary to
control the degree of crystallinity thereof and, therefore, to
severely control the temperature, etc. in order to obtain good
fusion bonding property between the expanded beads.
[0013] On the other hand, expanded beads obtained by the method of
Patent Document 6 in which a foamed extruded body of a polylactic
acid-based resin is cut into particles are capable of affording a
polylactic acid-based resin expanded beads molded article having
excellent heat resistance and mechanical strengths. However,
because a polylactic acid-based resin having a relatively high
degree of crystallinity is used for the purpose of improving heat
resistance, the degree of crystallinity of the polylactic acid
resin from which the expanded beads are formed is liable to become
high. Therefore, the expanded beads have a problem in stable
production of molded articles having good fusion bonding
property.
[0014] With a view toward solving the problems of the prior art
such as poor fusion bonding between expanded beads, insufficient
dimensional stability and insufficient mechanical properties, the
present inventors have tried a dispersing medium release foaming
method. Namely, the present inventors have tried a method in which
polylactic acid-based resin particles are dispersed in a dispersing
medium in a pressure resisting vessel in the presence of a physical
blowing agent with heating under a pressure to obtain foamable
polylactic acid-based resin particles, the foamable resin particles
being subsequently released together with the dispersing medium to
an atmosphere which is maintained at a pressure lower than that in
the pressure resisting vessel so that the resin particles are
foamed and expanded. It has been found that the above method can
produce polylactic acid-based resin expanded beads showing good
secondary expansion property and fusion bonding property at the
time of in-mold molding and having good heat resistance and
relatively high expansion ratio without need to severely control
the degree of crystallinity of the polylactic acid-based resin
expanded beads. However, although in-mold molding of the obtained
expanded beads gives an expanded beads molded article having good
appearance, the expanded beads are apt to shrink so that there
arises new problems that physical properties inherent to the
polylactic acid resin are not sufficiently maintained and the
mechanical properties of the expanded beads molded article are not
sufficiently developed.
[0015] Shrunken expanded beads require troublesome control of
expansion ratio. Additionally, although shrunken expanded beads,
when molded in a mold cavity, can further expand in the mold cavity
and can give a molded article, the physical property improving
effect attributed to the orientation of the polymer as a
consequence of expansion and stretching is not considered to be
fully achieved and, hence, it is difficult to sufficiently develop
the physical properties of the polylactic acid resin.
[0016] In view of the above-described new problems, the present
invention is aimed at the provision of expanded beads that excel in
secondary expansion efficiency and fusion-bonding property at the
time of in-mold molding and that can produce a polylactic
acid-based resin expanded beads molded article having excellent
mechanical properties.
Means for Solving the Problems
[0017] In accordance with the present invention there are provided
the following polylactic acid-based resin expanded beads:
[1] Polylactic acid-based resin expanded beads obtained by
releasing a softened, pressurized foamable resin composition, which
comprises a polylactic acid-based resin and a physical blowing
agent, to a low pressure atmosphere to foam and expand the resin
composition, wherein the polylactic acid-based resin satisfies the
following conditions (1) to (3):
MT.ltoreq.30 mN (1)
log MT.ltoreq.0.93 log .eta.-1.75 (2)
CT.sub.1/2.gtoreq.600 sec (3)
where MT represents a melt tension [mN] of the polylactic
acid-based resin at 190.degree. C., .eta. represents a melt
viscosity [Pas] of the polylactic acid-based resin at 190.degree.
C. and a shear speed of 20 sec.sup.-1, and CT.sub.1/2 represents a
half crystallization time [sec] of the polylactic acid-based resin
at 110.degree. C.; [2] The polylactic acid-based resin expanded
beads as recited in above [1],
[0018] wherein the polylactic acid-based expanded resin beads, when
measured by the below-mentioned heat flux differential scanning
calorimetry, give a first time DSC curve and a second time DSC
curve,
[0019] wherein the second time DSC curve has a fusion peak having a
reference peak top temperature,
[0020] wherein the first time DSC curve has both a fusion peak(s)
with a peak top temperature that is on a high temperature side
which is higher than the reference peak top temperature and a
fusion peak(s) with a peak top temperature that is on a low
temperature side which is not higher than the reference peak top
temperature, and
[0021] wherein the first and second time DSC curves are measured
and defined as follows:
(a) a DSC curve of a test sample of the expanded polylactic
acid-based resin beads is measured according to a heat flux
differential scanning calorimetry method referenced in JIS K7122
(1987), by heating the test sample at a heating rate of 10.degree.
C./minute from 23.degree. C. to a temperature higher by 30.degree.
C. than the temperature at which the endothermic peak ends, thereby
obtaining the first time DSC curve; (b) the test sample is then
maintained for 10 minutes at the temperature higher by 30.degree.
C. than the temperature at which the endothermic peak ends in the
first time DSC curve; (c) the test sample is then cooled to
30.degree. C. at a cooling rate of 10.degree. C./minute; (d) the
test sample is then measured again for another DSC curve by being
heated at a heating rate of 10.degree. C./minute to a temperature
higher by 30.degree. C. than the temperature at which the
endothermic peak ends, thereby obtaining the second time DSC curve;
[3] The polylactic acid-based resin expanded beads as recited in
above [2], wherein the fusion peak(s) with the peak top temperature
that is on a higher temperature side which is higher than the
reference peak top temperature has a calorific value of 1 to 8 J/g;
[4] The polylactic acid-based resin expanded beads as recited in
above [1], wherein the polylactic acid-based resin expanded beads
have an apparent density of 24 to 240 g/L; [5] A polylactic
acid-based resin expanded beads molded article obtainable by
molding the polylactic acid-based resin expanded beads according to
any one of above [1] to [4] in a mold cavity, said molded article
having a density of 15 to 150 g/L and satisfying the following
formula (4):
(Bending modulus (MPa) of the expanded beads molded
article)/(Density (g/L) of the expanded beads molded
article).gtoreq.0.20 (MPaL/g) (4)
Effect of the Invention
[0022] The expanded beads of the present invention are those
obtained by releasing a softened expandable resin composition,
which comprises a specific polylactic acid-based resin impregnated
with a physical blowing agent, from a high pressure condition to a
low pressure atmosphere (generally an atmosphere of ambient
temperature and atmospheric pressure) to foam and expand the resin
composition. The obtained expanded beads after expansion are
prevented from shrinking and are small in variation of apparent
density (expansion ratio) thereof. Further, the expanded beads of
the present invention show excellent secondary expansion efficiency
and fusion bonding property during in-molding molding stage and,
hence, can give an expanded beads molded article having excellent
mechanical properties. Thus, the polylactic acid-based resin
expanded beads molded article obtained by in-mold molding of the
expanded beads of the present invention have excellent mechanical
properties.
BRIEF DESCRIPTION OF THE DRAWINGS
[0023] FIG. 1 is a graph for explaining a method of measuring a
half crystallization time;
[0024] FIG. 2 illustrates an example of a first time DSC curve
(I);
[0025] FIG. 3 illustrates an example of a second time DSC curve
(I);
[0026] FIG. 4 illustrates an example of a second time DSC curve
(II) showing an endothermic calorific value (Br:endo) of a
measurement sample as measured with a heat flux differential
scanning calorimeter;
[0027] FIG. 5 illustrates an example of a second time DSC curve
(II) showing an endothermic calorific value (Br:endo) of a
measurement sample as measured with a heat flux differential
scanning calorimeter;
[0028] FIG. 6 illustrates an example of a first time DSC curve (I)
showing an exothermic calorific value (Bfc:exo) and an endothermic
calorific value (Bfc:endo) of a measurement sample as measured with
a heat flux differential scanning calorimeter;
[0029] FIG. 7 illustrates an example of a first time DSC curve (I)
showing an exothermic calorific value (Bfc:exo) and an endothermic
calorific value (Bfc:endo) of a measurement sample as measured with
a heat flux differential scanning calorimeter; and
[0030] FIG. 8 illustrates an example of a first time DSC curve (I)
showing an exothermic calorific value (Bfc:exo) and an endothermic
calorific value (Bfc:endo) of a measurement sample as measured with
a heat flux differential scanning calorimeter.
EMBODIMENTS OF THE INVENTION
[0031] The polylactic acid-based resin expanded beads of the
present invention will be described in detail below. The polylactic
acid-based resin expanded beads (hereinafter occasionally simply
referred to as "expanded beads") of the present invention are
obtained by releasing a softened, pressurized expandable resin
composition, which contains a polylactic acid-based resin having
specific physical properties as described hereinafter and a
physical blowing agent, to a low pressure atmosphere to foam and
expand the resin composition. When the expandable resin composition
is in the form of particles of the polylactic acid-based resin, for
example, the release of the expandable resin composition may be
carried out by discharging the expandable polylactic acid-based
resin particles, which are dispersed in a dispersing medium in a
pressure resisting vessel and maintained in high temperature and
high pressure conditions, preferably a temperature of about 120 to
160.degree. C. and a pressure of about 1.0 to 5.0 MPa (G (gauge)),
to an atmosphere having a lower temperature and a lower pressure
than those within the vessel, preferably a temperature of about 0
to 50.degree. C. and a pressure of about 0 to 0.3 MPa (G), together
with the dispersing medium. As an expansion method which can
satisfy the condition of the present invention for releasing a
softened, pressurized expandable resin composition to a low
pressure atmosphere to foam and expand the resin composition, there
may be mentioned the above-described dispersing medium release
foaming method and, else, an extrusion foaming method. On the other
hand, a known method in which foamable resin particles impregnated
with a blowing agent are heated and expanded with a heating and
foaming apparatus cannot satisfy the expansion and foaming
conditions of the present invention. In the present specification,
the following description will be made mainly on the dispersing
medium release foaming method which is advantageous in control of
the stretch of the resin during the foaming step and in obtaining
of expanded beads with a small apparent density.
[0032] The expanded beads of the present invention are formed of a
polylactic acid-based resin (hereinafter occasionally referred to
simply as "PLA resin"). The PLA resin may be polylactic acid or a
mixture of polylactic acid with other resin or resins. The
polylactic acid is preferably a polymer containing at least 50 mol
% of component units derived from lactic acid. Examples of the
polylactic acid include (a) a polymer of lactic acid, (b) a
copolymer of lactic acid with other aliphatic hydroxycarboxylic
acid or acids, (c) a copolymer of lactic acid with an aliphatic
polyhydric alcohol and an aliphatic polycarboxylic acid, (d) a
copolymer of lactic acid with an aliphatic polycarboxylic acid, (e)
a copolymer of lactic acid with an aliphatic polyhydric alcohol,
and (f) a mixture of two or more of (a)-(e) above. Examples of the
polylactic acid also include so-called stereocomplex polylactic
acid and stereoblock polylactic acid. Specific examples of the
lactic acid include L-lactic acid, D-lactic acid, DL-lactic acid, a
cyclic dimer thereof (i.e. L-lactide, D-lactide or DL-lactide) and
mixtures thereof.
[0033] In the present invention, preferably used is polylactic acid
which satisfies conditions (1) to (3) described hereinafter and
which has a ratio of lactic acid isomers (D-isomer/L-isomer) of
99:1 to 94:6 or 6:94 to 1:99, particularly preferably 97:3 to 94:6
or 6:94 to 3:97.
[0034] Examples of other aliphatic hydroxycarboxylic acid in (b)
above include glycolic acid, hydroxybutyric acid, hydroxyvaleric
acid, hydroxycaproic acid and hydroxyheptoic acid. Examples of the
aliphatic polyhydric alcohol in (c) and (e) above include ethylene
glycol, 1,4-butanediol, 1,6-hexanediol, 1,4-cyclohexanedimethanol,
neopentyl glycol, decamethylene glycol, glycerin,
trimethylolpropane and pentaerythritol. Examples of the aliphatic
polycarboxylic acid in (c) and (d) above include succinic acid,
adipic acid, suberic acid, sebacic acid, dodecanedicarboxylic acid,
succinic anhydride, adipic anhydride, trimesic acid,
propanetricarboxylic acid, pyromellitic acid and pyromellitic
anhydride.
[0035] As specific examples of the method for preparing polylactic
acid used in the present invention, there may be mentioned a method
in which lactic acid or a mixture of lactic acid and aliphatic
hydroxycarboxylic acid is subjected to a direct dehydration
polycondensation (preparation method disclosed, for example, in
U.S. Pat. No. 5,310,865); a method in which a cyclic dimer of
lactic acid (namely lactide) is subjected to ring-open
polymerization (preparation method disclosed, for example, in U.S.
Pat. No. 2,758,987); a method in which cyclic dimers of lactic acid
and an aliphatic hydroxycarboxylic acid, such as lactide and
glycolide, and .epsilon.-caprolactone are subjected to ring-open
polymerization in the presence of a catalyst (preparation method
disclosed, for example, in U.S. Pat. No. 4,057,537); a method in
which a mixture of lactic acid, an aliphatic dihydric alcohol and
an aliphatic dibasic acid is subjected to direct dehydration
polycondensation (preparation method disclosed, for example, in
U.S. Pat. No. 5,428,126); a method in which lactic acid, an
aliphatic dihydric alcohol and an aliphatic dibasic acid are
subjected to polycondensation in an organic solvent (preparation
method disclosed, for example, in EP-A-0712880A2); and a method in
which a lactic acid polymer is subjected to dehydration
polycondensation in the presence of a catalyst to produce a
polyester and in which at least one step of polymerization in a
solid phase is involved during the course of the polycondensation.
The method for producing polylactic acid is not limited to the
above methods.
[0036] The PLA resin used in the present invention should satisfy
the following conditions (1) to (3):
MT.ltoreq.30 mN (1)
log MT.ltoreq.0.93 log .eta.-1.75 (2)
CT.sub.1/2.gtoreq.600 sec (3)
(wherein MT represents a melt tension [mN] at 190.degree. C., .eta.
represents a melt viscosity [Pas] at 190.degree. C. and a shear
speed of 20 sec.sup.-1, and CT.sub.1/2 represents a half
crystallization time [sec] at 110.degree. C.).
[0037] It is believed that because the melt tension, the melt
viscosity relative to the melt tension, and the half
crystallization time of the PLA resin fall within the specific
ranges defined by formulas (1) to (3), when the expandable resin
composition is released to a low pressure atmosphere to foam and
expand same, the resin that forms cell walls is stretched to cause
molecular orientation, so that the strength of the cell walls is
improved and shrinkage thereof after expansion is prevented. Among
the conditions (1) to (3), the conditions (1) and (2) indicate that
the PLA resin contains only a few branched chains or no branched
chains, while the condition (3) indicates that the PLA resin in a
softened state has a crystallization speed which is suited for
molecular orientation of the softened resin at the time of
foaming.
[0038] Hitherto, it has been the commonly accepted that a resin
which has a structure with a large number of branched chains and
which is high in melt tension is suited for foaming. Contrary to
the common sense, the present inventors have found that, a specific
PLA resin which contains only a few branched chains or no branched
chains and which is relatively slow in crystallization speed can
facilitate stretching of the resin that forms cell walls during the
expanding and foaming step by the aforementioned release to a low
pressure atmosphere and can give expanded beads having excellent
mechanical strengths.
[0039] The PLA resin which meets the above conditions (1) and (2)
exhibits such a viscoelastic behavior that is suited for foaming at
the time of the aforementioned release to a low pressure atmosphere
and can be stretched without receiving an excessive stress and
without causing breakage of cell walls. From this point of view, it
is preferred that the condition (1) is such that the melt tension
is 25 mN or less. Here, the lower limit of the melt tension is
generally 10 mN, preferably 12 mN. For the same reason as above, it
is preferred that the condition (2) is such as to satisfy the
following condition (5), particularly preferably the following
condition (6).
log MT.ltoreq.0.93 log .eta.-1.80 (5)
log MT.ltoreq.0.93 log .eta.-1.85 (6)
(wherein MT represents a melt tension [mN] at 190.degree. C., .eta.
represents a melt viscosity [Pas] at 190.degree. C. and a shear
speed of 20 sec.sup.-1.)
[0040] Stretching of the PLA resin that meets the above condition
(3) as well as the above conditions (1) and (2) stops when the cell
walls in a softened state solidify. Thus, the PLA resin can be
sufficiently stretched and can sufficiently undergo molecular
orientation until growth of the cells has been completed. As a
consequence, the obtained expanded beads are prevented from
shrinking so that an expanded beads molded article obtained by
molding the expanded beads in a mold cavity (hereinafter
occasionally referred to simply as "molded article") has improved
compressive strength and bending modulus as compared with those of
the conventional articles. From this point of view, the half
crystallization time is preferably 700 sec or more, more preferably
800 sec or more. The upper limit of the half crystallization time
is generally 4,000 sec, preferably 3,500 sec.
[0041] The expanded beads obtained from the PLA resin that
satisfies the above conditions (1) to (3) exhibit excellent
secondary expansion efficiency and fusion bonding property at the
time of in-mold molding. This is because the expanded beads
obtained from the PLA resin that satisfies the above conditions (1)
and (2) have cell walls that have been stretched without having
been applied with an excessive stress during stretching of the
resin and because it is therefore easy to achieve a high closed
cell content of the bead. Further, because the PLA resin satisfies
the above condition (3), it is easy to obtain expanded beads having
an appropriately low degree of crystallinity by expanding and
foaming expandable PLA resin in a softened state.
[0042] Accordingly, it is believed that because the obtained
expanded beads have an appropriately low degree of crystallinity
and a high closed cell content, the secondary expansion efficiency
and fusion bonding property of the expanded beads at the time of
in-mold molding are excellent.
[0043] The PLA resin that satisfies the above conditions (1) to (3)
may be obtained by selecting a resin which satisfies the above
condition (3) from among those polylactic acids which have only a
few branched chains or no branched chains and which satisfy the
above conditions (1) and (2). The hereinafter described measurement
may be done for the purpose of the above selection. The PLA resins
which satisfy the above conditions (1) and (2) may be obtained by
mixing a plurality of polylactic acids or by adding a so-called
thickening agent as appropriate for adjusting the melt tension and
melt viscosity thereof. A substance such as polytetrafluoroethylene
which serves to function as a crystal nucleus agent and to
accelerate the crystallization speed or a substance which serves to
inhibit crystallization and to retard the crystallization speed may
be also added to polylactic acid as appropriate to formulate a PLA
resin that satisfies the condition (3). Thus, the PLA resin that
satisfies the above conditions (1) to (3) may be one which is
selected from commercially available polylactic acids, one which is
obtained by mixing a plural kinds of polylactic acids, one which is
obtained by mixing polylactic acid(s) with other resin or resins,
or one which is obtained by adding an additive such as a thickening
agent to polylactic acid(s). The measurement of each of the melt
viscosity, melt tension and half crystallization time of the PLA
resin is basically carried out on the resin particles to be placed
in a pressure resisting vessel when a dispersing medium release
foaming method is adopted and on the resin to be fed to an extruder
when an extrusion foaming method is adopted. However, when the
polylactic acid resin is to be modified with a thickening agent or
the like in the pressure resisting vessel or in the extruder, the
measurement of each of the melt viscosity, melt tension and half
crystallization time of the PLA resin is carried out after the
resin has been modified and sampled from the vessel or the
extruder.
[0044] The melt viscosity as used herein may be measured using a
measuring device such as Capirograph 1D (manufactured by Toyo Seiki
Selsaku-Sho, Ltd.). Concretely, use is made of a cylinder having a
cylinder diameter of 9.55 mm and a length of 350 mm and an orifice
having a nozzle diameter of 1.0 mm and a length of 10 mm. The
cylinder and the orifice are set at a temperature of 190.degree. C.
A required amount of a specimen which has been fully dried at
80.degree. C. is charged into the cylinder and held for 4 minutes.
The resulting molten specimen is then extruded in the form of a
string through the orifice at a shear speed of 20 sec.sup.-1 to
measure the melt viscosity under the described conditions.
[0045] The melt tension as used herein may be measured by a
speed-increasing winding method using Capirograph 1D (manufactured
by Toyo Seiki Selsaku-Sho, Ltd.). Concretely, use is made of a
cylinder having a cylinder diameter of 9.55 mm and a length of 350
mm and an orifice having a nozzle diameter of 2.095 mm and a length
of 8 mm. The cylinder and the orifice are set at a temperature of
190.degree. C. A required amount of a specimen which has been fully
dried at 80.degree. C. is charged into the cylinder and held for 4
minutes. The resulting molten specimen is then extruded in the form
of a string through the orifice at a piston speed of 10 mm/minute.
The extruded string is put on a tension-detecting pulley having a
diameter of 45 mm and is taken up on a take-up roller while
increasing the take-up speed at a constant take-up acceleration
rate such that the take-up speed increases from 0 m/minute to 200
m/min through a period of 10 minutes to detect the melt tension at
the breakage of the string by the Capirograph device. When the
string is not broken even when the take-up speed reaches 200 m/min,
the melt tension detected by the device at the take-up speed of 200
m/min is adopted. The above measurement is carried out for ten
different specimens. From the obtained ten measured maximum values,
the largest three values and the smallest three values are
excluded. The arithmetic mean of the rest four maximum values is
the melt tension (mN) for the purpose of the present invention.
[0046] The "half crystallization time" as used herein may be
measured using a crystallization speed analyzer (Model MK-801
manufactured by METRON Inc, (formerly Kotaki Shoji Co., Ltd.)). A
resin sample which has been heated at 200.degree. C. for 3 minutes
in an air bath is placed in a crystallization bath (oil bath)
maintained at 110.degree. C. and measured for the half
crystallization time. The resin sample for the measurement is in
the form of a PLA resin film. The film has a thickness of
0.1.+-.0.02 mm and is a square with a 15 mm.times.15 mm size. The
sample is sandwiched between cover glasses for a microscope. An
indicated voltage of 3 V is selected for setting the brightness of
the lamp for a light source.
[0047] The crystallization speed analyzer manufactured by METRON
Inc. utilizes a relationship between crystallization and
birefringence of the sample. The half-crystallization time as used
herein is determined as follows. Namely, the above measurement will
give a curve on a graph as illustrated in FIG. 1. From the curve, a
value A on the ordinate at which the quantity of the light
attributed to the birefringence becomes constant is determined.
Next, a value B is calculated by multiplying A by 0.5. The
half-crystallization time is a value C on the abscissa (axis
representing time) at which the curve assumes the value B.
[0048] The PLA resin used in the present invention is preferably
capped at its molecular chain ends. By this, it is possible to
surely suppress hydrolysis during the course of the preparation of
expanded beads, so that the dispersing medium release foaming
method (hereinafter described) can be much easily carried out.
Namely, it becomes easy to reliably form and control the high
temperature peak. Thus, it becomes easy to produce expanded beads
that are capable of withstanding in-mold molding. Additionally, a
molded article obtained by in-mold molding has improved durability.
In the case of an extrusion molding method, too, it is possible to
suppress hydrolysis which is not wanted.
[0049] Examples of the end capping agent include carbodiimide
compounds, oxazoline compounds, isocyanate compounds and epoxy
compounds. Above all, carbodiimide compounds are preferred.
Specific examples of the diimide compounds include an aromatic
monocarbodiimide such as bis(dipropylphenyl)carbodiimide, an
aliphatic polycarbodiimide such as
poly(4,4'-dicyclohexylmethanecarbodiimide, and an aromatic
polycarbodiimide.
[0050] These end capping agents may be used alone or in combination
of two or more thereof. The using amount of the end capping agent
is preferably 0.1 to 5 parts by weight, more preferably 0.5 to 3
parts by weight, per 100 parts by weight of the PLA resin.
[0051] The PLA resin which forms the expanded beads of the present
invention may contain other resins as long as the objects and
effects of the present invention are not adversely affected.
[0052] Examples of additives that may be compounded in the PLA
resin which forms the expanded beads of the present invention
include a coloring agent, a flame retardant, an antistatic agent, a
weatherability agent and an electric conductivity imparting
agent.
[0053] When the base resin is mixed with additives, the additives
may be kneaded as such together with the base resin. In view of
dispersing efficiency of the additives into the base resin,
however, the additives are generally formed into a master batch
which is then kneaded with the base resin. The additives are
preferably added in an amount of 0.001 to 20 parts by weight, more
preferably 0.01 to 5 parts by weight, per 100 parts by weight of
the base resin, though the amount varies with the kind of the
additives.
[0054] It is preferred that the expanded beads of the present
invention, when subjected to heat flux differential scanning
calorimetry, give such a first time DSC curve and a second time DSC
curve as follows. In the first time DSC curve, there appear a
fusion peak(s) (hereinafter occasionally referred to as "high
temperature peak") having a peak top temperature which is higher
than a reference peak top temperature, and another fusion peak(s)
(hereinafter occasionally referred to as "intrinsic peak") having a
peak top temperature which is not higher than the reference peak
top temperature, wherein the reference peak top temperature is a
peak top temperature of a fusion peak of the second time DSC curve.
When, in the second time DSC curve (I), there are a plurality of
fusion peaks or when there is a shoulder on high temperature side
of a fusion peak, then the peak top temperature of a fusion peak of
the second time DSC curve (I) is the peak top temperature of the
fusion peak or the flection point temperature of the shoulder that
is the highest among the peak top temperatures of the fusion peaks
and the flection point temperatures of the shoulders.
[0055] The first and second time DSC curves are measured and
defined as follows:
(a) a DSC curve of a test sample of the expanded beads is measured
according to a heat flux differential scanning calorimetry method
referenced in JIS K7122 (1987), by heating the test sample at a
heating rate of 10.degree. C./minute from 23.degree. C. to a
temperature higher by 30.degree. C. than the temperature at which
the endothermic peak ends, thereby obtaining the first time DSC
curve (I); (b) the test sample is then maintained for 10 minutes at
the temperature higher by 30.degree. C. than the temperature at
which the endothermic peak ends in the first time DSC curve; (c)
the test sample is then cooled to 30.degree. C. at a cooling rate
of 10.degree. C./minute; (d) the test sample is then measured again
for another DSC curve by being heated at a heating rate of
10.degree. C./minute to a temperature higher by 30.degree. C. than
the temperature at which the endothermic peak ends, thereby
obtaining the second time DSC curve (I).
[0056] It is believed that the expanded beads, which show the high
temperature peak, have improved heat resistance and solidity at
high temperatures and are prevented from excessively secondarily
expanding during in-mold molding of the expanded beads, so that a
heating medium can sufficiently heat the expanded beads located all
parts in the mold cavity. As a result, the fusion bonding of the
expanded beads during the in-mold molding is improved. It follows
that the obtained molded article shows excellent fusion bonding
even when the thickness thereof is large or the shape thereof is
complicated.
[0057] The above-described high temperature peak appears in a first
time DSC curve (I) obtained in the measurement of the expanded
beads by differential scanning calorimetry, but does not appear in
a second time DSC curve (I). The high temperature peak that appears
in the first time DSC curve (I) of the expanded beads is attributed
to crystal growth of the polylactic acid resin during a heat
treatment which will be described hereinafter. The intrinsic peak
that appears in the second time DSC curve (I) of the expanded beads
is a fusion peak which is attributed to the intrinsic crystal
structure of the PLA resin.
[0058] The phenomenon of appearance of such a high temperature peak
in the first time DSC curve (I) of the expanded beads is considered
to be ascribed to secondary crystals formed through the thermal
history in a process for expanding resin particles to obtain the
expanded beads.
[0059] FIG. 2 illustrates an example of the first time DSC curve
(I) and FIG. 3 illustrates an example of the second time DSC curve
(I). From a comparison of FIG. 2 and FIG. 3, it will be seen that,
when the peak top temperature of the higher temperature-side fusion
peak among the two fusion peaks in FIG. 3 is regarded as being a
reference peak top temperature, the high temperature peak is a
fusion peak in FIG. 2 which has a peak top temperature higher than
the reference peak top temperature, while the intrinsic peak is a
fusion peak which has a peak top temperature not higher than the
reference peak top temperature. That is, in FIG. 2, the intrinsic
peak is a fusion peak "a" while the high temperature peak is a
fusion peak "b".
[0060] In the present specification, a peak top temperature of a
fusion peak that has the largest area in the second time DSC curve
(I), i.e. the peak top temperature of the fusion peak "c" is
defined as a melting point Tm of the PLA resin, and the temperature
at which the skirt on a high temperature-side of the fusion peak
returns to base line is defined as a fusion peak ending temperature
Te.
[0061] Incidentally, although the two fusion peaks "a" and "b" in
FIG. 2 are each shown as a smooth curve, DSC curves are not always
smooth. There are cases where a plurality of overwrapped fusion
peaks appear in DSC curves so that a plurality of intrinsic peaks
and a plurality of high temperature peaks are present in the DSC
curves.
[0062] The calorific value (J/g) of the high temperature peak is
determined from the first time DSC curve (I) shown in FIG. 2 as
follows. A straight line connecting a point .alpha. which is a
point where an endothermic peak begins separating from a low
temperature-side base line and a point .beta. which is a point
where the endothermic peak returns to a high temperature-side base
line is drawn. Next, a line which is in parallel with the ordinate
and which passes a point .gamma. on the DSC curve at the bottom of
the valley between the intrinsic peak "a" and the high temperature
peak "b" is drawn. This line crosses the line connecting the points
.alpha. and .beta. at a point .delta.. The calorific value of the
high temperature peak is an amount of endotherm corresponding to
the area (shaded portion in FIG. 2) defined by the line connecting
the points .gamma. and .delta., the line connecting the points
.delta. and .beta., and the DSC curve. Incidentally, there is a
case where an exothermic peak contiguous with the fusion peak "a"
appears in the low-temperature side of the fusion peak "a" (this is
not the case in FIG. 2), so that it is difficult to determine the
point .alpha. as a point at which the fusion peak begins separating
from the low temperature-side base line in the above-described
manner. In such a case, the point .alpha. is determined as a point
at which the exothermic peak begins separating from the low
temperature-side base line.
[0063] The endothermic calorific value of the high temperature peak
(when the high temperature peak is constituted of a plurality of
fusion peaks, a total endothermic calorific value of the fusion
peaks) is preferably 1 to 8 J/g. When the expanded beads, whose
high temperature peak has an excessively small endothermic
calorific value, are heated by introducing steam into the mold
cavity at the time of in-mold molding, those portions of the
expanded beads located near the surface of the mold primarily
undergo secondary expansion beyond necessary. As a result, the
heating medium such as steam is prevented from sufficiently flowing
into all parts of the mold cavity filled with the expanded beads.
Accordingly, there is a possibility that it becomes difficult to
obtain a molded article having good fusion bonding in a center part
thereof. When the high temperature peak has an excessively large
endothermic calorific value, on the other hand, the expanded beads
cannot sufficiently secondarily expand in an in-mold molding stage.
As a result, there is a possibility that it becomes difficult to
obtain a molded article having good fusion bonding between the
expanded beads and good appearance. For these reasons, the
calorific value of the high temperature peak is more preferably 2
to 8 J/g. The upper limit of the calorific value of the high
temperature peak is generally 25 J/g.
[0064] It is preferred that the expanded beads of the present
invention each have a multi-layer structure (hereinafter
occasionally referred to as multi-layer expanded beads) which
includes a core layer formed of a PLA resin, and an outer layer
covering the core layer and formed of another PLA resin. In this
case, at least the core layer of the multi-layer expanded beads
should be formed of the PLA resin that meets the above-described
conditions (1) to (3). It is not necessary that the outer layer
should entirely cover the core layer. The resin of which the core
layer of the multi-layer expanded beads is formed may be exposed on
a part of the surface of the multi-layer expanded beads.
[0065] It is preferred that the softening point (B) [.degree. C.]
of the PLA resin of which the outer layer is formed is lower than
the softening point (A) [.degree. C.] of the PLA resin of which the
core layer is formed and that a difference [(A)-(B)] between the
softening point (A) and the softening point (B) be greater than
0.degree. C. and is not greater than 105.degree. C., more
preferably from 15 to 105.degree. C., still more preferably from 20
to 105.degree. C. The multi-layer expanded beads that show the
above specific range of the difference in softening point may be
produced by a method as described hereinafter which includes
coextruding PLA resins with softening points (B) and (A) of the
outer and core layers, and expanding the obtained multi-layered
resin particles. When the multi-layer expanded beads meet the
hereinafter described formulas (7) and (8), especially additionally
the formula (9) show excellent fusion bonding property in a further
stable manner during an in-mold molding stage. It is preferred,
from the standpoint of handling efficiency of the multi-layer
expanded beads and mechanical strengths at elevated temperatures of
molded articles obtained therefrom, that the softening point of the
PLA resin of the outer layer not only meets the above-mentioned
relationship with the softening point of the PLA resin of the core
layer but also is 50.degree. C. or more, more preferably 55.degree.
C. or more, particularly preferably 65.degree. C. or more.
[0066] As used herein, the term "softening point" is intended to
refer to a Vicat softening point as measured according to JIS K7206
(1999), Method A50. In particular, a PLA resin is sufficiently
dried in a vacuum oven and pressed at 200.degree. C. and 20 MPa (if
necessary, air evacuation is carried out so as to prevent inclusion
of air bubbles) to obtain a test piece with a length of 20 mm, a
width of 20 mm and a thickness of 4 mm. The test piece is annealed
in an oven at 80.degree. C. for 24 hours and then measured using,
for example, HDT/VSPT tester Model TM-4123 manufactured by Ueshima
Seisakusho Co., Ltd.
[0067] In the multi-layer expanded beads of the present invention
each having the core layer and outer layer, it is preferred that
the weight ratio of the resin of which the core layer is formed to
the resin of which the outer layer is formed is 99.9:0.1 to 75:25,
more preferably 99.7:0.3 to 85:15, still more preferably 99.5:0.5
to 90:10. When the weight proportion of the resin of the outer
layer of the multi-layer expanded beads is excessively small, the
thickness of the outer layer of the multi-layer expanded beads is
so thin that the effect of improving the fusion bonding efficiency
of the multi-layer expanded beads in an in-mold molding stage
decreases. Additionally, there may cause a problem in production
efficiency in the production of the multi-layer expanded beads.
When the weight proportion of the outer layer is excessively great,
the resin forming the outer layer tends to unnecessarily expand to
cause a reduction of the effect of improving the fusion bonding
efficiency of the multi-layer expanded beads in an in-mold molding
stage. Additionally, there is a possibility that the mechanical
properties of the molded article is deteriorated. In the
multi-layer expanded beads, the resin forming the outer layer may
be expanded as long as the objects and effects of the present
invention are not adversely affected.
[0068] In the multi-layer expanded beads, the weight ratio of the
resin of which the core layer is formed to the resin of which the
outer layer is formed may be controlled by controlling the weight
ratio of the resin of which a core layer of resin particles
(described hereinafter) is formed to the resin of which the outer
layer of the resin particles is formed.
[0069] The above-described end capping agent, when added to the PLA
resin forming the multi-layer expanded beads, is preferably
incorporated at least in the core layer, more preferably in each of
the core and outer layers. When at least the PLA resin of the core
layer, preferably the PLA resin of each of the core and outer
layers, is modified with the end capping agent, it is possible to
further suppress hydrolysis thereof during the course of the
preparation of expanded beads, so that expanded beads can be
produced in a stable manner. Further, it is also possible to
suppress hydrolysis during the course of the preparation of molded
articles so that the production efficiency of the molded articles
can be produced in a stable manner. Moreover, when the molded
articles are subjected to actual use, they are expected to show
improved durability and withstand use under a high temperature and
high humidity environment.
[0070] In the multi-layer expanded beads, the thickness of the
outer layer is desired to be thin, because cells are hard to be
formed in the outer layer and because mechanical strengths of the
expanded beads molded article are improved. When the thickness of
the outer layer is excessively low, there may be apprehension that
the effect of improving fusion bonding between the multi-layer
expanded beads is adversely affected. In actual, however,
sufficient fusion bonding improving effect is achieved when the
thickness is in the range described below. Namely, the outer layer
of the multi-layer expanded beads preferably has an average
thickness of 0.1 to 25 .mu.m, more preferably 0.2 to 15 .mu.m,
particularly preferably 0.3 to 10 .mu.m. The average thickness of
the outer layer of the multi-layer expanded beads may be controlled
by a control of the weight ratio of a resin of a core layer to a
resin of an outer layer of the multi-layered resin particles during
the fabrication thereof. The average thickness of the outer layer
of the multi-layered resin particles should be controlled as
appropriate in view of the weight of the resin particles and
desired expansion ratio, but preferably has an average thickness of
2 to 100 .mu.m, more preferably 3 to 70 .mu.m, particularly
preferably 5 to 50 .mu.m.
[0071] The average thickness of the outer layer of the multi-layer
expanded beads is measured as follows. One multi-layer expanded
bead is cut into nearly equal halves. From a photograph of the
enlarged cross section of the bead, the thickness of the outer
layer in each of the four positions (upper and lower sides, and
left and right sides) thereof is measured. The arithmetic mean of
the four thickness values is the thickness of the outer layer of
the expanded bead. Similar procedures are repeated for a total of
10 expanded beads. The arithmetic mean of the ten thickness values
is the average thickness of the outer layer of the expanded beads.
The average thickness of the outer layer of the multi-layered resin
particles is also measured in a similar manner. In the multi-layer
expanded beads and multi-layered resin particles, when the outer
layer is formed on parts of the peripheral surface of the core
layer, there may arise a case where the thickness of the outer
layer cannot be measured in any way at the above four positions. In
such a case, the thickness of the outer layer is measured at four
randomly selected measurable positions and the arithmetic mean
thereof is defined as the thickness of the outer layer of the
multi-layer expanded beads or resin particles. Also, when the outer
layer of the expanded beads is not easily discriminated, it is
preferable to produce the multi-layer expanded beads in such a
manner that a suitable colorant is incorporated in the resin of
which the outer layer is formed.
[0072] The expanded beads according to the present invention,
irrespective of whether they are multi-layer expanded beads or not,
it is preferred that the expanded bead as a whole shows a specific
endothermic calorific value (Br:endo). In the case of the
multi-layer expanded beads, it is preferred that the expanded bead
additionally shows a specific relationship between the endothermic
calorific value (Brs:endo) of a surface region of the expanded bead
and the endothermic calorific value (Brc:endo) of a center region
of the expanded bead.
[0073] More specifically, in the expanded beads of the present
invention, it is preferred that an endothermic calorific value
(Br:endo) [J/g] of the whole expanded bead after a heat treatment,
which is determined in accordance with heat flux differential
scanning calorimetry under the Condition 2 described below, meets
the following formula (7):
25<(Br:endo).ltoreq.40 (7)
[0074] In the above formula (7), the fact that (Br:endo) is within
the above range means that, when the expanded bead is heat treated
under such conditions that crystallization of the polylactic acid
which constitutes the expanded bead sufficiently proceeds, the
amount of the polylactic acid crystal components of the polylactic
acid in the expanded bead is not excessively large and is not
excessively small. Namely, it is meant that when the heat treatment
is carried out sufficiently to increase the degree of crystallinity
of the polylactic acid which constitutes the expanded bead, an
expanded beads-molded article having an appropriately increased
degree of crystallinity can be obtained. Therefore, there is no
fear of excessive reduction of the mechanical strengths and heat
resistance such as compressive strength at a high temperature of
the expanded beads-molded article. From this point of view,
(Br:endo) is preferably 30 to 40 J/g.
[0075] In the expanded beads of the present invention, it is
further preferred that the endothermic calorific value (Brs:endo)
[J/g] of a surface region of the expanded bead after a heat
treatment and the endothermic calorific value (Brc:endo) [J/g] of a
center region of the expanded bead after the heat treatment satisfy
a relationship represented by the following formula (8):
(Brc:endo)>(Brs:endo).gtoreq.0 (8)
[0076] The fact that the above formula (8) is met means that when
the expanded bead is heat treated under such conditions that
crystallization of the polylactic acid which constitutes the
surface region and center region of the expanded bead sufficiently
proceeds, the amount of the polylactic acid crystal components that
constitute the surface region of the expanded bead is smaller than
the amount of the polylactic acid crystal components that
constitute the center region of the expanded bead. This means that,
when the expanded bead is sufficiently heat treated, the degree of
crystallinity of the polylactic acid in the center region is
increased. Because of the improved degree of crystallinity of the
polylactic acid in the center region of the expanded bead, the
expanded bead can meet the above formula (7) and can show improved
heat resistance, etc. as a whole. On the other hand, since the
polylactic acid in the surface region of the expanded bead has a
lower degree of crystallinity as compared with that in the center
region of the expanded bead even when the expanded bead is
sufficiently heat treated, the softening point of surface region of
the expanded bead is low. Therefore, the expanded bead which
satisfies the relationship shown in the formula (8) is capable of
showing excellent fusion bonding between the expanded beads during
an in-mold molding stage, irrespective of the thermal history
before and after the fabrication of the expanded beads. From this
point of view, the endothermic calorific value (Brs:endo) of the
surface region of the expanded bead is preferably 35 J/g or less
(inclusive of 0) for reasons of improved fusion bonding property of
the expanded bead. For reasons of improved heat resistance and
mechanical strengths of the expanded bead, the endothermic
calorific value (Brc:endo) of the center region of the expanded
bead is preferably 30 to 40 J/g. It is also preferred that between
(Brc:endo) and (Brs:endo) there is a difference in calorific value
of at least 3 J/g, more preferably at least 4 J/g. Meanwhile, as
long as the formula (8) is met, the polylactic acid that
constitutes the surface region of the expanded bead may be
non-crystalline polylactic acid or a mixture of non-crystalline
polylactic acid and crystalline polylactic acid.
[0077] As used herein, the endothermic calorific value (Br:endo)
[J/g] of the whole expanded bead, the endothermic calorific value
(Brs:endo) [J/g] of a surface region of the expanded bead and the
endothermic calorific value (Brc:endo) [J/g] of a center region of
the expanded bead are values as determined in accordance with heat
flux differential scanning calorimetry referenced in JIS K7122
(1987) under the following Condition 2.
Condition 2
[Preparation of Measurement Specimens]
<Specimen for Measuring the Endothermic Calorific Value of the
Whole Expanded Bead>
[0078] The expanded bead is basically used as a measurement
specimen as such without cutting.
[0079] <Specimen for Measuring the Endothermic Calorific Value
of the Surface Region of the Expanded Bead>
[0080] A surface portion of the expanded bead, including an
exterior surface thereof, is cut out and collected to obtain a
measurement specimen, such that the entire exterior surface thereof
is removed and the measurement specimen has a weight of 1/6 to 1/4
the weight of the expanded bead before being cut. More
specifically, the expanded bead is cut using a cutter knife,
microtome or the like for collecting the surface portion as the
measurement specimen. In this case, it should be borne in mind that
the entire exterior surface of the expanded bead should be removed
and the weight of the surface portion removed from the bead should
be within the range of 1/6 to 1/4 the weight of the expanded bead
before being cut. In this case, the thickness of the surface
portion removed should be as equal as possible
<Specimen for Measuring the Endothermic Calorific Value of the
Center Region of the Expanded Bead>
[0081] An entire surface portion of the expanded bead is cut away
to leave a measurement specimen, such that the measurement specimen
has a weight of 1/5 to 1/3 the weight of the expanded bead before
being cut. More specifically, the expanded bead is cut using a
cutter knife or the like for the purpose of obtaining an inside
region of the foam of the expanded bead which region does not
include the exterior surface of the expanded bead. It should be
borne in mind that the entire exterior surface of the expanded bead
should be removed and a center region of the expanded bead which
has a weight of 1/5 to 1/3 the weight of the expanded bead before
being cut should be cut out, with the center of the center region
being made as close to the center of the expanded bead as possible.
In this case, the shape of the measurement specimen thus cut out is
desired to be as similar as possible to the shape of the expanded
bead.
[Measurement of Endothermic Calorific Values]
[0082] The calorific values (Br:endo), (Brc:endo) and (Brc:endo)
are values as determined from DSC curves obtained by first
subjecting each of the expanded bead, the measurement specimen
obtained from the surface region of the expanded bead and the
measurement specimen obtained from the center region of the
expanded bead to a heat treatment in which 1 to 4 mg of each of
them is heated, for melting, to a temperature higher by 30.degree.
C. than a fusion peak ending temperature, then maintained at that
temperature for 10 minutes, then cooled to 110.degree. C. at a
cooling speed of 10.degree. C./min and then maintained at that
temperature for 120 min, and then cooling the resulting sample to
30.degree. C. at a cooling speed of 10.degree. C./min, each of the
thus heat treated specimens being subsequently heated again, for
melting, to a temperature higher by 30.degree. C. than a fusion
peak ending temperature at a heating speed of 5.degree. C./min to
obtain the DSC curve (hereinafter occasionally referred to as
"second time DSC curve (II)") in accordance with heat flux
differential scanning calorimetry referenced in JIS K7122 (1987).
When the amount of the measurement specimen sampled for measurement
of (Brs:endo) or (Brc:endo) is less than the intended amount of 1
to 4 mg, the above-described sampling procedure should be repeated
for two or more expanded beads until the measurement specimen in
the intended amount of 1 to 4 mg is collected. When the weight of
one expanded bead sampled for measurement of (Br:endo) exceeds 4
mg, the expanded bead should be divided into parts with an equal
shape (such as into halves) so that the measurement specimen has a
weight within the range of 1 to 4 mg.
[0083] FIG. 4 shows a second time DSC curve (II) in which a point
"a" is a point where an endothermic peak begins separating from a
low temperature-side base line and a point "b" is a point where the
endothermic peak returns to a high temperature-side base line. The
endothermic calorific value (Br:endo) is an area defined by a line
passing the points "a" and "b" and the DSC curve. The DSC device
should be preferably operated so that the base line is as straight
as possible. When the base line is inevitably curved as shown in
FIG. 5, the curved base line on the low temperature side is
extended to the high temperature side with the radius of the
curvature of the base line being maintained. The point at which the
endothermic peak begins separating from the low temperature side
curved base line is the point "a". Similarly, the curved base line
on the high temperature side is extended to the low temperature
side with the radius of the curvature of the base line being
maintained. The point at which the endothermic peak returns to the
high temperature side curved base line is the point "b". The
endothermic calorific values (Brs:endo) and (Brc:endo) may also be
obtained from their second DSC curves (II) by drawing base lines in
the same manner as in the case of (Br:endo) and may be each
determined from the area defined by a line passing the points "a"
and "b" and the DSC curve.
[0084] In the above-described measurement of the endothermic
calorific values (Br:endo), (Brs:endo) and (Brc:endo), each of the
specimens is measured for its DSC curve under conditions including
the maintenance at 110.degree. C. for 120 minutes. This is for the
purpose of determining the endothermic calorific values (Br:endo),
(Brs:endo) and (Brc:endo) in the state in which crystallization of
the PLA resin of each specimen has been allowed to proceed as much
as possible.
[0085] The endothermic calorific values (Br:endo), (Brs:endo) and
(Brc:endo) determined from the expanded beads that are used for a
molded article are nearly the same as those determined from the
expanded beads that are sampled from the molded article as long as
the sampling of the measurement specimens is carried out precisely.
Namely, the endothermic calorific values (Br:endo), (Brs:endo) and
(Brc:endo) do not vary depending upon the thermal history of the
expanded beads. Accordingly, the endothermic calorific values
(Br:endo), (Brs:endo) and (Brc:endo) of the expanded beads from
which a molded article is formed may be determined according to the
above-described Condition 2 from the expanded beads that have been
used for producing the molded article or from the expanded beads
that are sampled from the molded article.
[0086] In the present invention, since the expanded beads from
which a molded article is produced have the above-described
specific endothermic calorific value (Br:endo) as a whole, the
molded article obtained from the expanded beads has excellent
mechanical strengths and compressive strength at high temperatures,
when such expanded beads are in-mold molded after having been
subjected to a heat treatment or when the molded article obtained
from the expanded beads is subjected to a heat treatment. Further,
when the endothermic calorific value (Brs:endo) of the surface
region of the expanded bead is lower than the endothermic calorific
value (Brc:endo) of the center region thereof, the softening point
of the surface of the expanded beads may be maintained in a low
level, the expanded beads show excellent fusion bonding property at
the time of in-mold molding.
[0087] It is particularly preferred that the expanded beads used
for in-mold molding are such that an endothermic calorific value
(Bfc:endo) [J/g] and an exothermic calorific value (Bfc:exo) of a
center region of the expanded bead before being subjected to the
heat treatment, which values are determined in accordance with heat
flux differential scanning calorimetry referenced in JIS K7122
(1987) under Condition 3 shown below, meet the following formula
(9):
40>[(Bfc:endo)-(Bfc:exo)]>10 (9)
Condition 3
[Preparation of Measurement Specimen]
[Measurement Specimen for Measuring Endothermic Calorific Value and
Exothermic Calorific Value of the Center Region of the Expanded
Bead]
[0088] In the same manner as the preparation method for the
specimen for measuring the endothermic calorific value of the
center region of the expanded bead that is described in Condition
2, an entire surface portion of the expanded bead is cut away to
leave a measurement specimen, such that the measurement specimen
has a weight of 1/5 to 1/3 the weight of the expanded bead before
being cut.
[Measurement of Endothermic Calorific Value and the Exothermic
Calorific Value]
[0089] The endothermic calorific value (Bfc:endo) and the
exothermic calorific value (Bfc:exo) are determined from a DSC
curve (first time DSC curve (I)) obtained by heating, for melting,
1 to 4 mg of the measurement specimen, sampled from the center
region of the expanded bead, from 23.degree. C. to a temperature
higher by 30.degree. C. than a fusion peak ending temperature at a
heating speed of 10.degree. C./min in accordance with heat flux
differential scanning calorimetry referenced in JIS K7122 (1987).
When the amount of the measurement specimen sampled from one
expanded bead is less than the intended amount of 1 to 4 mg, the
above-described sampling procedure should be repeated for a
plurality of expanded beads until 1 to 4 mg of a measurement
specimen is collected.
[0090] The difference [(Bfc:endo)-(Bfc:exo)] in the above formula
(9) represents a difference between the endothermic calorific value
(Bfc:endo) that is an energy absorbed when the crystals, which are
originally contained in the center region of the expanded bead
before the heat flux differential scanning calorimetry measurement
is carried out, and crystals, which have been formed in the center
region of the expanded bead during the course of heating in the
measurement, are melted and the exothermic calorific value
(Bfc:exo) that is an energy emitted when the center region of the
expanded bead crystallizes during the course of heating in the heat
flux differential scanning calorimetry measurement. The fact that
the difference is small means that crystallization of the center
region of the expanded bead has not yet proceeded before the heat
flux differential scanning calorimetry is carried out, while the
fact that the difference is large and is near the endothermic
calorific value (Bfc:endo) means that crystallization of the center
region of the expanded bead has already fully proceeded before the
heat flux differential scanning calorimetry is carried out. The
difference [(Bfc:endo)-(Bfc:exo)] is preferably within the
above-described range for reasons that good secondary expansion
property of the expanded bead during an in-mold molding stage is
achieved and, further, the range of the molding temperature within
which good expanded beads molded articles are obtainable becomes
wide. The difference is more preferably 35 J/g or less,
particularly preferably 30 J/g or less, from the view point of the
secondary expansion property.
[0091] From the view point of easiness in controlling the
temperature of in-mold molding step as well as prevention of
shrinkage of the in-mold molded articles, the difference
[(Bfc:endo)-(Bfc:exo)] is preferably 15 J/g or more, particularly
preferably 20 J/g or more.
[0092] It is also preferred that the endothermic calorific value
(Bfc:endo) of the expanded bead of the present invention is 25 to
40 J/g. With an increase of the endothermic calorific value
(Bfc:endo), the degree of crystallinity of the PLA resin of which
the expanded bead is formed becomes higher upon a heat treatment of
the expanded bead. Thus, a high (Bfc:endo) is desirable because a
molded article having higher mechanical strengths may be prepared.
In the present invention, however, the endothermic calorific value
(Bfc:endo) is preferably within the above range from the standpoint
of achievement of molecular orientation of the resin during the
foaming stage for improving the physical properties thereof. When
the endothermic calorific value (Bfc:endo) is excessively small, on
the other hand, there is a possibility that the mechanical
strengths, especially mechanical strengths at high temperatures, of
the final molded article is unsatisfactory. From this point of
view, (Bfc:endo) is more preferably 30 to 40 J/g.
[0093] The exothermic calorific value (Bfc:exo)] is preferably 5 to
30 J/g, more preferably 10 to 25 J/g, for reasons of good secondary
expansion property and fusion bonding property of the expanded
beads, provided that difference [(Bfc:endo)-(Bfc:exo)] meets with
the above requirement. The fact that the exothermic calorific value
(Bfc:exo) is high means that crystallization of the PLA resin in
the center region of the expanded bead has not yet proceeded before
the heat flux differential scanning calorimetry measurement.
[0094] The exothermic calorific value (Bfc:exo) and the endothermic
calorific value (Bfc:endo) as used herein are determined by the
heat flux differential scanning calorimetry (Condition 3) as
referenced in JIS K7122 (1987), as described previously. The
measurement of the exothermic calorific value (Bfc:exo) and the
endothermic calorific value (Bfc:endo) is carried out as
follows.
[0095] In a first time DSC curve (I), when a point where the
exothermic peak begins separating from a low temperature-side base
line of the exothermic peak is assigned as point "c" and a point
where the exothermic peak returns to a high temperature-side base
line is assigned as point "d", the exothermic calorific value
(Bfc:exo) of the expanded beads is a calorific value determined
from the area defined by a line passing the points "c" and "d" and
the DSC curve. In the first time DSC curve (I), when a point where
the fusion peak begins separating from a low temperature-side base
line is assigned as point "e" and a point where the endothermic
peak returns to a high temperature-side base line is assigned as
point "f", the endothermic calorific value (Bfc:endo) of the
expanded beads is a calorific value determined from the area
defined by a line passing the points "e" and "f" and the DSC curve.
The DSC device should be preferably operated so that the base line
of the first time DSC curve (I) is as straight as possible. When
the base line is inevitably curved, the curved base line on the low
temperature side of the exothermic peak is extended to the high
temperature side with the radius of the curvature of the base line
being maintained. The point at which the exothermic peak begins
separating from the low temperature side curved base line is the
point "c". Similarly, the curved base line on the high temperature
side of the exothermic peak is extended to the low temperature side
with the radius of the curvature of the base line being maintained.
The point at which the exothermic peak returns to the high
temperature side curved base line is the point "d". Further, the
curved base line on the low temperature side of the endothermic
peak is extended to the high temperature side with the radius of
the curvature of the base line being maintained. The point at which
the endothermic peak begins separating from the low temperature
side curved base line is the point "e". Similarly, the curved base
line on the high temperature side of the endothermic peak is
extended to the low temperature side with the radius of the
curvature of the base line being maintained. The point at which the
endothermic peak returns to the high temperature side curved base
line is the point "f".
[0096] In the case of FIG. 6, for example, an exothermic calorific
value (Bfc:exo) of the expanded bead is a calorific value
determined from the area which is defined by the straight line
passing the points "c" and "d", that are determined in the manner
described above, and the DSC curve and which represents the
generated calorific value, while an endothermic calorific value
(Bfc:endo) is a calorific value determined from the area which is
defined by the straight line passing the points "e" and "f" and the
DSC curve and which represents the absorbed calorific value. In the
case of FIG. 7, it is difficult to determine points "d" and "e" by
the above-described method. Thus, in the illustrated case, points
"c" and "f" are first determined by the above-described method and
a point at which the straight line passing the points "c" and "f"
intersects the DSC curve is assigned as the point "d" (also point
"e"), whereupon the exothermic calorific value (Bfc:exo) and the
endothermic calorific value (Bfc:endo) of the expanded beads are
determined. As shown in FIG. 8, there is a case in which a small
exothermic peak exists on a low temperature side of the endothermic
peak. In such a case, the exothermic calorific value (Bfc:exo) is
determined from a sum of an area "A" of the first exothermic peak
and an area "B" of the second exothermic peak in FIG. 8. Namely,
when a point where the exothermic peak begins separating from a low
temperature-side base line of the first exothermic peak is assigned
as point "c" and a point where the first exothermic peak returns to
a high temperature-side base line is assigned as point "d", the
area "A" is an area defined by a straight line passing the points
"c" and "d" and the DSC curve and represents the generated
calorific value. On the other hand, when a point where the
exothermic peak begins separating from a low temperature-side base
line of the second exothermic peak is assigned as point "g" and a
point where the endothermic peak returns to a high temperature-side
base line is assigned as point "f", and when a point where a
straight line passing the points "g" and "f" intersects the DSC
curve is assigned as point "e", the area "B" is an area defined by
a straight line passing the points "g" and "e" and the DSC curve
and represents the generated calorific value. In FIG. 8, the
endothermic calorific value (Bfc:endo) is a calorific value
determined from the area which is defined by the straight line
passing the points "e" and "f" and the DSC curve and which
represents the absorbed calorific value.
[0097] The expanded beads of the present invention preferably have
an apparent density of 24 to 240 g/L, more preferably 40 to 200
g/L, from the standpoint of excellence in lightness in weight,
in-mold moldability, mechanical strengths and in-mold moldability.
When the apparent density is excessively small, there is a
possibility that a large shrinkage degree may result after in-mold
molding process. When the apparent density is excessively high, on
the other hand, there is a possibility that a large variation of
the apparent density may be apt to result. This causes variation of
expandability, fusion bonding property and apparent density of the
expanded beads at the time of being heated in a mold cavity and,
hence results in deterioration of the physical properties of the
obtained molded articles.
[0098] As used herein, the apparent density of the expanded beads
is measured by the following method. The expanded beads are allowed
to stand for aging in a constant temperature and humidity room at
23.degree. C. under atmospheric pressure and a relative humidity of
50% for 10 days. In the same room, about 500 mL of the aged
expanded beads are weighed to determine their weight W1 (g). The
weighed expanded beads are immersed in water at 23.degree. C.
contained in a measuring cylinder using a wire net or the like
tool. From a rise of the water level volume, the volume V1 (L) of
the expanded beads placed in the measuring cylinder is determined
by subtracting the volume of the wire net and the like tool placed
therein. The apparent density (g/L) is calculated by dividing the
weight W1 of the expanded beads placed in the measuring cylinder by
the volume V1 (W1/V1).
[0099] The expanded beads of the present invention preferably have
an average cell diameter of 30 to 500 .mu.m, more preferably 50 to
250 .mu.m, from the standpoint of their in-mold moldability and
improved appearance of the molded article obtained therefrom.
[0100] The average cell diameter of the expanded beads is measured
as follows. One expanded bead is cut into nearly equal halves. From
an enlarged image of the cross section taken by a microscope, the
average cell diameter is determined. Namely, on the enlarged image
of the cross section of the expanded bead, four line segments each
passing nearly through the center of the cross section and
extending from one surface of the expanded bead to the other
surface thereof are drawn such that eight angularly equally spaced
straight lines extend radially from nearly the center of the cross
section toward the external surface of the expanded bead. The
number of the cells that intersect each of the four lines is
counted. The total number N of the cells that intersect the above
four line segments is counted. Also measured is a total length L
(.mu.m) of the four line segments. The value (L/N) obtained by
dividing the total length L by the total number N is an average
cell diameter of the one expanded bead. Similar procedures are
repeated for randomly-selected 10 expanded beads in total. The
arithmetic mean of the average cell diameters of the ten expanded
beads represents the average cell diameter of the expanded
beads.
[0101] The expanded beads of the present invention preferably have
a closed cell content of 80% or more, more preferably 85% or more,
still more preferably 90% or more from the standpoint of excellence
in in-mold moldability of the expanded beads and capability of
providing sufficient mechanical strengths of a molded article
produced therefrom.
[0102] As used herein, the closed cell content of the expanded
beads is measured as follows. The expanded beads are allowed to
stand for aging in a constant temperature and humidity room at
23.degree. C. under atmospheric pressure and a relative humidity of
50% for 10 days. In the same room, about 20 cm.sup.3 bulk volume of
the expanded beads thus aged are sampled and measured for the
precise apparent volume Va by a water immersion method. The sample
whose apparent volume Va has been measured is fully dried and
measured for its true volume Vx according to Procedure C of ASTM
D-2856-70 using Air Comparison Pycnometer Type-930 manufactured by
Toshiba Beckman Inc. From the volumes Va and Vx, the closed cell
content is calculated by the formula (10) shown below. The average
(N=5) is the closed cell content of the expanded beads.
Closed cell content (%)=(Vx-W/.rho.).times.100/(Va-W/.rho.)
(10)
[0103] wherein
[0104] Vx represents the true volume (cm.sup.3) of the expanded
beads measured by the above method, which corresponds to a sum of a
volume of the resin constituting the expanded beads and a total
volume of all the closed cells of the expanded beads,
[0105] Va represents an apparent volume (cm.sup.3) of the expanded
beads, which is measured by a rise of the water level when the
expanded beads are immersed in water contained in a measuring
cylinder,
[0106] W is a weight (g) of the sample expanded beads used for the
measurement; and
[0107] .rho. is a density (g/cm.sup.3) of the resin constituting
the expanded beads.
[0108] The expanded beads of the present invention give, upon being
subjected to in-mold molding, a molded article. The shape of the
molded article is not specifically limited. Not only molded article
with a plate-like, columnar, vessel-like or block-like form but
also a molded article with a complicated three-dimensional shape or
an article with a large thickness may be produced. The molded
articles may be suitably used in various applications such as
packaging vessels, interior materials for automobiles, cushioning
materials and core materials of FRP.
[0109] The molded article of the present invention, in which the
PLA resin is considered to be molecularly oriented as a result of
stretching of cell walls during expansion of the expanded beads,
shows excellent compressive strength and bending modulus. Further,
when the expanded beads have a high temperature peak as described
above, fusion bonding therebetween is improved so that the
dimensional stability and mechanical strengths are further
improved. Incidentally, when the molded article is heat treated
(heat set) for sufficiently increasing the degree of crystallinity
of the PLA resin, more excellent heat resistance can be
achieved.
[0110] The molded article of the present invention preferably has a
density of 15 to 150 g/L, more preferably 25 to 125 g/L, for
reasons of lightness in weight and excellence in mechanical
strength.
[0111] The molded article of the present invention, which is
obtained by in-mold molding of the excellent expanded beads as
described above, shows excellent mechanical strengths and has a
relationship between its density and its bending modulus which
satisfies the formula (4) shown below, preferably the formula (11)
shown below:
(Bending modulus (MPa) of the molded article)/(Density (g/L) of the
molded article).gtoreq.0.20 (MPaL/g) (4)
(Bending modulus (MPa) of the molded article)/(Density (g/L) of the
molded article).gtoreq.0.23 (MPaL/g) (11)
[0112] The molded article preferably has a closed cell content of
50% or more, more preferably 60% or more, still more preferably 70%
or more. When the closed cell content is excessively low, there is
a possibility that the mechanical strengths such as compressive
strength of the expanded beads molded article is deteriorated.
[0113] The closed cell content of the molded article may be
determined in the same manner as that for the measurement of the
closed cell content of the expanded beads except that a measurement
sample with a size of 25.times.25.times.30 mm is cut out from a
center part of the molded article (skin should be completely cut
off).
[0114] The degree of fusion bonding of the molded article is
preferably 50% or more, more preferably 60% or more, particularly
preferably 80% or more. The molded article having a high degree of
fusion bonding excels in mechanical strengths, particularly in
bending strength. The degree of fusion bonding is intended to refer
to a percentage of the expanded beads which undergo material
failure when the molded article is ruptured, based on the all
expanded beads present on the ruptured cross section. When all the
expanded beads in the ruptured cross section undergo material
failure, the degree of fusion bonding is 100%. Those beads which
are not fuse-bonded to each other do not undergo material failure
in the ruptured cross section but are separated from each other at
their interface.
[0115] A method for preparing the expanded beads of the present
invention will be next described. As the preferred method for
preparing the expanded beads of the present invention, there may be
mentioned a dispersing medium release foaming method. By adopting
the dispersing medium release foaming method, it is easy to control
stretching of cell walls, formation of the high temperature peak
and the calorific value of the high temperature peak at the time of
foaming.
[0116] The dispersing medium release foaming method is a method
including melting and kneading a PLA resin in an extruder,
extruding the kneaded resin in the form of strands, cutting the
extrudate to obtain resin particles, dispersing the resin particles
in an aqueous dispersing medium contained in a pressure resisting
vessel, impregnating a physical blowing agent into the resin
particles, while heating them, to obtain foamable resin particles,
and releasing the foamable resin particles together with the
aqueous dispersing medium, at a high temperature and a high
pressure, from the pressure resisting vessel into a lower pressure
atmosphere to obtain expanded beads. In this method, while a resin
particle preparation step, a blowing agent impregnation step and a
foaming step may be performed separately, the blowing agent
impregnation step and the foaming step are generally carried out in
a single stage.
[0117] In the resin particle preparation step, resin particles may
be prepared by extruding a PLA resin into which required additives
have been incorporated, the extrudate being then pelletized by, for
example, a strand cutting method or an under-water cutting method.
When the above-described multi-layered resin particles each
composed of a core layer and an outer layer are intended to be
produced, there may be utilized a coextrusion molding technique
which is disclosed in, for example, Japanese Kokoku Publications
Nos. JP-B-S41-16125, JP-B-S43-23858 and JP-B-S44-29522 and Japanese
Kokai Publication No. JP-A-S60-185816 and which uses, for example,
a device including an extruder for forming the core layer, an
extruder for forming the outer layer, and a coextrusion die
connected to each of the extruders.
[0118] In pelletization in the resin particle preparation step, a
PLA resin and, if needed, additives are fed to an extruder and
melted and kneaded. The molten kneaded mass thus obtained is
extruded in the form of strands through small holes of a mouthpiece
attached to a die exit at a tip of the extruder. The extruded
strands are cooled by being immersed in water and then cut with a
pelletizer such that the resin particles obtained each have a
specific weight, whereby resin particles are obtained.
Alternatively, such resin particles may be obtained by cutting the
extruded strands into resin particles each have a specific weight,
the resin particles being cooled after or simultaneous with the
cutting.
[0119] The resin particles preferably have an average weight per
one particle of 0.05 to 10 mg, more preferably 0.1 to 4 mg. When
the average weight is excessively small, it is necessary to use a
special production method. When the average weight is excessively
large, on the other hand, there is a possibility that the expanded
beads obtained therefrom have a broad density distribution and
cannot be filled in a mold cavity in an efficient manner at the
time of molding. The shape of the resin particles may be, for
example, a cylindrical column, a sphere, a rectangular column, an
oval sphere or a cylinder. Expanded beads obtained by foaming and
expanding the resin particles have a shape that is similar to that
of the resin particles before expansion.
[0120] When the resin particles are produced by melting and
kneading the PLA resin with an extruder followed by extrusion into
strands, it is preferable to dry the PLA resin before kneading for
reasons of prevention of degradation of the PLA resin by
hydrolysis. In order to suppress degradation of the PLA resin by
hydrolysis, a method using an extruder provided with a vent hole
may also be adopted so that moisture is removed from the PLA resin
by evacuation through the vent hole. The removal of moisture from
the PLA resin may permit the prevention of the generation of air
bubbles in the resin particles and may improve the stability of the
extrusion procedures.
[0121] Description will be next made of the blowing agent
impregnation step and foaming step of the dispersing medium release
foaming method. In one embodiment of the dispersing medium release
foaming method, the resin particles are impregnated with a physical
blowing agent to form foamable resin particles, for example, by
heating, in a pressure resisting vessel, the resin particles
dispersed in a dispersing medium together with a physical blowing
agent, or by first dispersing and heating the resin particles in a
dispersing medium in a pressure resisting vessel, a blowing agent
being subsequently injected into the pressure resisting vessel. The
obtained foamable resin particles in a molten state are then
released together with the dispersing medium into a zone having a
lower temperature and lower pressure than those in the high
temperature and high pressure resisting vessel so that the foamable
resin particles are allowed to foam and expand to obtain the
expanded beads.
[0122] An additive may be previously incorporated into the resin
particles for the purpose of controlling the apparent density and
cell diameter of the obtained expanded beads. Examples of the
additive include an inorganic powder such as talc, calcium
carbonate, borax, zinc borate, aluminum hydroxide and silica, and a
polymer such as polytetrafluoroethylene, polyethylene wax,
polycarbonate and crosslinked polystyrene. Among the above
additives, polytetrafluoroethylene, polyethylene wax and
crosslinked polystyrene are preferred. Particularly preferred is
hydrophobic polytetrafluoroethylene powder.
[0123] In incorporation of the additive into the PLA resin, the
additive may be kneaded as such together with the PLA resin in the
pelletization step. For reasons of improved dispersibility,
however, it is preferred that the additive is formed into a master
batch and the master batch be kneaded with the PLA resin.
[0124] Since the apparent density and cell diameter of the expanded
beads according to the present invention vary depending upon the
blending amount of the additive, it is expected that the additive
has an effect of controlling these properties. The amount of the
additive is generally 0.001 to 5 parts by weight, preferably 0.005
to 3 parts by weight, more preferably 0.01 to 2 parts by weight,
per 100 parts by weight of the PLA resin. Within such a range, it
is possible to reduce the apparent density (to increase the
expansion ratio) and to uniformize the cell diameter of the
expanded beads.
[0125] Since the PLA resin is easily hydrolyzed, the additive to be
blended with the PLA resin is desired to be selected from
hydrophobic substances while avoiding the use of a hydrophilic
substance as much as possible. Thus, when a hydrophobic additive is
used, it is possible to obtain an effect of the additive while
preventing degradation of the PLA resin due to hydrolysis.
[0126] The high temperature peak of the expanded beads of the
present invention may develop when resin particles are heat
treated, at a temperature at which crystals thereof are not
completely melted, when the resin particles are impregnated with a
blowing agent in a pressure resisting vessel with heating. The heat
treatment is carried out by holding the resin particles at a
specific temperature and for a specific period of time as described
below. The temperature at which the high temperature peak is
allowed to develop is generally in the range from [melting point
minus 30.degree. C.] to [melting point minus 10.degree. C.] where
the melting point is that of the PLA resin of which the resin
particles are formed, although the temperature varies depending
upon the kind of the blowing agent and the aimed apparent density
of the expanded beads. The heat treatment time is generally 5 to 60
minutes, preferably 5 to 15 minutes. Too long a heat treatment time
may cause hydrolysis of the PLA resin and is not preferred. Thus,
the resin particles are preferably held in the above temperature
range for at least 5 minutes in order for the a temperature peak to
develop in the expanded beads.
[0127] As described above, in the dispersing medium release foaming
method, resin particles are dispersed in a dispersing medium, such
as, water in a pressure resisting vessel, such as an autoclave, to
which a blowing agent is fed under a pressure in a predetermined
amount. The dispersion is then stirred at an elevated temperature
for a predetermined time to impregnate the blowing agent into the
resin particles to obtain foamable resin particles. The resin
particles in the molten state and the dispersing medium in the
vessel are then released from the high temperature and high
pressure vessel into a lower temperature and lower pressure
atmosphere to obtain the expanded beads. At the time of the
release, it is preferred that the contents in the vessel are
discharged while applying a back pressure to space in the
vessel.
[0128] When particularly low apparent density (high expansion
ratio) expanded beads are to be produced, there may be adopted
so-called two-step expansion in which expanded beads produced in
the above method are aged in an atmospheric pressure in the
customarily employed manner, then charged again in a pressure
resisting vessel, then subjected to a pressurizing treatment using
a pressurized gas such as air so that the internal pressure of the
expanded beads is increased to 0.01 to 0.10 MPa(G) and, finally,
heated in the expansion vessel with a heating medium, such as hot
wind, steam or a mixture of steam and air, to obtain the desired
expanded beads with a high expansion ratio.
[0129] In the production of expanded beads of the present
invention, it is desired that the foamable resin particles prepared
using a PLA resin that satisfies the above conditions (1) to (3)
are released to a low pressure zone at such a temperature condition
in which a temperature range in which the PLA resin can be properly
foamed overlaps a temperature range in which the PLA resin that
forms the cell walls as a result of stretching of the resin
particles can be properly oriented. In order to enable the
overlapping of the above temperature requirement, such a PLA resin
as to satisfy the above conditions (1) to (3) is employed in the
present invention. To be more specific, the foaming temperature is
preferably between (melting point minus 10.degree. C.) to (melting
point minus 30.degree. C.), more preferably between (melting point
minus 15.degree. C.) to (melting point minus 25.degree. C.), where
the melting point is that of the PLA resin. When the foaming
temperature is excessively low, it is difficult to obtain expanded
beads with a low apparent density. When excessively high, on the
other hand, shrinkage of the expanded beads is apt to occur and,
thus, there is a possibility that the mechanical properties of
molded articles obtained by in-mold molding of the obtained beads
are deteriorated. In order to obtain expanded beads in which the
resin forming cell walls as a result of foaming is stretched and
molecularly oriented and which have excellent mechanical strengths,
it is preferred that the expanded beads immediately after the
foaming are rapidly cooled. When the expanded beads after the
foaming are rapidly cooled to a temperature lower than the glass
transition temperature of the PLA resin particles, the mobility of
non-crystalline molecular chains in the molecularly oriented state
decreases so that a high stretching effect may be obtained. For
this reason, shrinkage of the expanded beads may also be prevented
by the rapid cooling. Examples of the method for rapidly cooling
the expanded beads include a method in which air as a cooling
medium is fed to the atmosphere where the expansion has been
completed, a method in which water as a cooling medium is fed to
the atmosphere where the expansion has been completed, and a method
in which the resin particles are allowed to foam and expand in
water contained in a tank.
[0130] As the dispersing medium in which the resin particles are
dispersed, water is preferred. However, other than water, a
dispersing medium that does not dissolve the polylactic acid resin
particles may be used.
[0131] A dispersing agent or a dispersing aid may be added to the
dispersing medium, if necessary, in dispersing the resin particles
in the dispersing medium. Examples of the dispersing agent include
inorganic substances such as aluminum oxide, tribasic calcium
phosphate, magnesium pyrophosphate, titanium oxide, zinc oxide,
basic magnesium carbonate, basic zinc carbonate, calcium carbonate,
kaolin, mica and clay; and water soluble polymer protective colloid
agents such as polyvinylpyrrolidone, polyvinyl alcohol and methyl
cellulose. The dispersing medium may also be incorporated with a
dispersing aid such as an anionic surfactant, e.g. sodium
dodecylbenzenesulonate and sodium alkanesulfonate.
[0132] The dispersing agent may be used in an amount of 0.05 to 3
parts by weight per 100 parts by weight of the resin particles,
while the dispersing aid may be used in an amount of 0.001 to 0.3
part by weight per 100 parts by weight of the resin particles.
[0133] As the physical blowing agent, there may be used, for
example, organic physical blowing agents such as hydrocarbons (e.g.
butane, pentane and hexane), and halogenated hydrocarbons (e.g.
1,1-difluoroethane and dichloromethane) and inorganic physical
blowing agents such as inorganic gas (e.g. carbon dioxide, nitrogen
and air) and water. These physical blowing agents may be used
singly or in combination of two or more thereof. Among the physical
blowing agents, those which are composed mainly of an inorganic
physical blowing agent such as carbon dioxide, nitrogen and air are
preferably used. Carbon dioxide is particularly preferred. The term
"physical blowing agent composed mainly of an inorganic physical
blowing agent" as used herein is intended to refer to a physical
blowing agent which contains at least 50% by mole, preferably at
least 70% by mole, more preferably at least 90% by mole, of an
inorganic physical blowing agent in 100% by mole of the total
physical blowing agent.
[0134] The amount of the physical blowing agent is determined as
appropriate in consideration of the kind of the blowing agent,
amount of the additives, the apparent density of the desired
expanded beads, etc. For example, the inorganic physical blowing
agent is used in an amount of about 0.1 to 30 parts by weight,
preferably 0.5 to 15 parts by weight, more preferably 1 to 10 parts
by weight, per 100 parts by weight of the PLA resin.
[0135] Description will next be made of a method for producing a
molded article using the expanded beads of the present invention.
For the preparation of a molded article, any known in-mold molding
method may be adopted. In the present invention, an expanded beads
molded article may be easily obtained by molding the expanded beads
preferably having a high temperature peak in a mold cavity in any
known method. Examples of such a method include a compression
molding method, a cracking molding method, a pressure molding
method, a compression filling molding method and an ambient
pressure filling molding method, in each of which a conventional
mold for expanded beads is used (see, for example, Japanese Kokoku
Publications No. JP-B-S46-38359, No. JP-B-S51-22951, No.
JP-B-H04-46217, No. JP-B-H06-22919 and No. JP-B-H06-49795).
[0136] As the generally preferably adopted in-mold molding method,
there may be mentioned a batch-type in-mold molding method in which
expanded beads are filled in a mold cavity of a conventional mold
for thermoplastic resin expanded beads adapted to be heated and
cooled and to be opened and closed. Steam having a saturation vapor
pressure of 0.01 to 0.25 MPa(G), preferably 0.01 to 0.20 MPa(G), is
then fed to the mold cavity to heat the expanded beads and to foam,
expand and fuse bond the beads together. The obtained molded
article is then cooled and taken out of the mold cavity.
[0137] The feed of the steam may be carried out by a conventional
method such as a combination of one-direction flow heating,
reversed one-direction flow heating and both-direction flow
heating. The particularly preferred heating method includes
preheating, one-direction flow heating, reversed one-direction flow
heating and both-direction flow heating which are successively
performed in this order.
[0138] The molded article may be also produced by a continuous
in-mold molding method in which the expanded beads are fed to a
mold space which is defined between a pair of vertically spaced,
continuously running belts disposed in a path. During the passage
through a steam-heating zone, saturated steam with a saturation
vapor pressure of 0.01 to 0.25 MPa(G) is fed to the mold space so
that the expanded beads foamed and fuse bonded together. The
resulting molded article is cooled during its passage through a
cooling zone, discharged from the path and successively cut into a
desired length (see, for example, Japanese Kokai Publications No.
JP-A-H09-104026, No. JP-A-H09-104027 and No. JP-A-H10-180888).
[0139] Prior to the above in-mold molding, the expanded beads
obtained by the above-described method may be charged in a pressure
resisting vessel and treated with a pressurized gas such as air to
increase the pressure inside the cells thereof to 0.01 to 0.15
MPa(G). The treated beads are taken out of the vessel and then
subjected to in-mold molding. The treated expanded beads exhibit
further improved in-mold moldability.
Example I
[0140] The expanded beads of the present invention will be
described in more detail below by way of examples. These examples
are not restrictive of the present invention, however.
Examples 1 to 3, 5, 7 to 11 and Comparative Examples 1 to 3
[0141] An extrusion device was used which had an extruder (inside
diameter: 65 mm) for forming a core layer, an extruder (inside
diameter: 30 mm) for forming an outer layer and a coextrusion die
attached to exits of the two extruders for forming multi-layered
strands. The PLA resins shown in Tables 1-1, 1-2 and 2 for forming
a core layer and an outer layer were fed to respective extruders
and melted and kneaded. The molten kneaded masses were introduced
into the coextrusion die and combined in the die and coextruded in
the form of multi-layer strands through small holes of a mouthpiece
of the coextrusion die attached to a tip of the extrusion device.
Each of the strands had a core layer and an outer layer covering
the core layer with a weight ratio shown in Tables 1-1, 1-2 and 2.
The coextruded strands were cooled with water and then cut with a
pelletizer into particles each having a weight 2 mg. Drying of the
cut particles gave multi-layered resin particles.
[0142] Meanwhile, the PLA resin of the core layer contained 1,000
ppm by weight of polytetrafluoroethylene powder (Trade name:
TFW-1000, manufactured by Seishin Enterprise Co., Ld.) as a cell
controlling agent and 1.5% by weight of a carbodiimide compound
(bis(dipropylphenyl)carbodiimide, Stabaxol 1-LF produced by Rhein
Chemie) as an end capping agent. The cell controlling agent and end
capping agent were mixed into the PLA resin in the form of a master
batch. The PLA resin of the outer layer contained 1.5% by weight of
a carbodiimide compound (bis(dipropylphenyl)carbodiimide, Stabaxol
1-LF produced by Rhein Chemie) as an end capping agent. The end
capping agent was mixed into the PLA resin in the form of a master
batch.
[0143] In Example 8, only the extruder for forming a core layer was
operated (the extruder for forming an outer layer was stopped) so
that single layer resin particles were prepared.
[0144] Using the thus obtained resin particles, expanded beads were
prepared. First, 50 kg of the obtained resin particles were charged
in a 400 L pressure resisting vessel equipped with a stirrer
together with 270 L of water as a dispersing medium, to which 300 g
of aluminum oxide as a dispersing agent and 4 g (as effective
amount) of a surfactant (sodium alkylbenzenesulfonate, Trade name:
Neogen S-20F, manufactured by Dai-ichi Kogyou Seiyaku Co., Ltd.)
were added. The contents were then heated with stirring to the
foaming temperature (FT) shown in Tables 1-1, 1-2 and 2. Carbon
dioxide (CO2) as a blowing agent was then injected into the
pressure resisting vessel until the pressure within the pressure
resisting vessel reached the value shown in Tables 1-1, 1-2 and 2.
After having been allowed to stand at that temperature for 15
minutes, the contents were released from the pressure resisting
vessel (inside of which was maintained at the foaming temperature
and the pressure shown in Tables 1-1, 1-2 and 2) to the atmospheric
having an ambient temperature and an ambient pressure while
applying a back pressure with carbon dioxide to maintain the
pressure within the vessel at constant, whereby expanded beads
having an apparent density as shown in Tables 1-1, 1-2 and 2 were
obtained. The expanded beads obtained in Examples 1 to 3, 5, 8, 9
and 11 and Comparative Examples 1 to 3 each had a crystal structure
that gave an intrinsic peak and a high temperature peak in the
first time DSC curves (I) thereof. The expanded beads obtained in
Example 7 had a crystal structure that gave only an intrinsic peak
in the first time DSC curves (I) thereof.
[0145] Various physical properties of the thus obtained expanded
beads such as endothermic calorific value of the high temperature
peak, apparent density, closed cell content, average cell diameter
and presence or absence of shrinkage thereof (determined with naked
eyes), were measured and evaluated and the results are shown in
Tables 1-1, 1-2 and 2.
Example 4
[0146] Using the resin particles obtained in Example 1, expanded
beads were produced as follows. The resin particles (1 kg) obtained
in the manner as described above were charged in a 5 L pressure
resisting vessel together with 3 L of water as a dispersing medium,
to which 3 g of aluminum oxide as a dispersing agent and 0.1 g (as
effective amount) of a surfactant (sodium alkylbenzenesulfonate,
Trade name: Neogen S-20F, manufactured by Dai-ichi Kogyou Seiyaku
Co., Ltd.) were added. Then, 75 g of isobutane (iBut) as a blowing
agent were added to the pressure resisting vessel with stirring.
The contents in the vessel were then heated to the foaming
temperature shown in Table 1-1 and maintained at that temperature
for 15 minutes. Thereafter, the contents were released from the
pressure resisting vessel (inside of which was maintained at the
foaming temperature and the pressure shown in Table 1-1) to the
atmospheric having an ambient temperature and an ambient pressure
while applying a back pressure with nitrogen gas to maintain the
pressure within the vessel at constant, whereby expanded beads
having an apparent density as shown in Table 1-1 were obtained. The
expanded beads obtained in Example 4 had a crystal structure that
gave an intrinsic peak and a high temperature peak in the first
time DSC curves (I) thereof.
[0147] Various physical properties of the thus obtained expanded
beads such as endothermic calorific value of the high temperature
peak, apparent density, closed cell content, average cell diameter
and presence or absence of shrinkage thereof (determined with naked
eyes), were measured and evaluated and the results are shown in
Table 1-1.
Example 6
[0148] Expanded beads were prepared in the same manner as that of
Example 1 except for incorporation of polytetrafluoroethylene
powder (Trade name: TFW-1000, manufactured by Seishin Enterprise
Co., Ld.) into the PLA resin of the core layer in an amount of
3,000 weight ppm. The expanded beads obtained in Example 6 had a
crystal structure that gave an intrinsic peak and a high
temperature peak in the first time DSC curves (I) thereof.
Comparative Examples 4 and 5
[0149] Using the resin particles obtained in Comparative Example 1,
expanded beads were produced as follows. The resin particles (1 kg)
obtained were charged in a 5 L pressure resisting vessel equipped
with a stirrer together with 3 L of water as a dispersing medium,
to which 3 g of aluminum oxide as a dispersing agent and 0.1 g (as
effective amount) of a surfactant (sodium alkylbenzenesulfonate,
Trade name: Neogen S-20F, manufactured by Dai-ichi Kogyou Seiyaku
Co., Ltd.) were added. The contents were then heated with stirring
to the foaming temperature shown in Table 2. Carbon dioxide as a
blowing agent was then injected into the pressure resisting vessel
until the pressure within the pressure resisting vessel reached the
value shown in Table 2. After having been allowed to stand at that
temperature for 15 minutes, the contents were released from the
pressure resisting vessel (inside of which was maintained at the
foaming temperature and the pressure shown in Table 2) to the
atmospheric having an ambient temperature and an ambient pressure
while applying a back pressure with nitrogen to maintain the
pressure within the vessel at constant, whereby expanded beads
having an apparent density as shown in Table 2 were obtained. The
expanded beads obtained in Comparative Example 4 had a crystal
structure that gave only an intrinsic peak in the first time DSC
curve (I) thereof. The expanded beads obtained in Comparative
Example 5 had a crystal structure that gave an intrinsic peak and a
high temperature peak in the first time DSC curve (I) thereof.
[0150] Various physical properties of the thus obtained expanded
beads such as endothermic calorific value of the high temperature
peak, apparent density, closed cell content, average cell diameter
and presence or absence of shrinkage thereof (determined with naked
eyes), were measured and evaluated and the results are shown in
Table 2.
TABLE-US-00001 TABLE 1-1 Example 1 2 3 4 5 6 Resin Core Resin
Composition *1) *1) *1) *1) *5) *5) Particles layer Melting point
(.degree. C.) 155 155 155 155 158 158 Outer Resin Composition *3)
*3) *3) *3) *3) *3) layer Melting point (.degree. C.) none none
none none none none Core layer/Outer layer (weight ratio) 95/5 95/5
95/5 95/5 95/5 95/5 MFR (g/10 min); 190.degree. C., 2.16 kgf 3.5
3.5 3.5 3.5 3.4 3.5 Glass transition temperatureTg (.degree. C.) 56
56 56 56 56 56 Melting point (.degree. C.) 155 155 155 155 157 157
Melt tension MT (mN); 190.degree. C. *0 19 19 19 19 18 19 Melt
viscosity .eta.(Pa s); 190.degree. C., 20 sec.sup.-1 *0 2,830 2,830
2,830 2,830 2,890 2,790 0.93log.eta. - logMT *0 1.93 1.93 1.93 1.93
1.95 1.93 Half crystallizataion time CT.sub.1/2 (sec) *0 1,720
1,720 1,720 1,720 1,350 760 Expanded Blowing agent CO.sub.2
CO.sub.2 CO.sub.2 iBut CO.sub.2 CO.sub.2 Beads Autoclave inside
pressure (MPa (G)) 2.2 2.2 2.5 2.9 2.2 2.2 Foaming temperature FT
(.degree. C.) 137.5 138 136.5 135 139 139.5 FT - Tg (.degree. C.)
82 82 81 79 83 84 Apparent density (g/L) 119 119 119 119 119 119
High temperature peak calorific value (J/g) 3.1 1.4 7.4 3.2 3.7 2.7
Br:endo (J/g) 32 32 30 32 34 34 Brc:endo (J/g) 33 32 31 32 34 35
Brs:endo (J/g) 26 25 26 24 26 25 Bfc:exo (J/g) 16 16 16 14 14 9
Bfc:endo (J/g) 30 29 32 28 34 35 Bfc:endo - Bfc:exo (J/g) 14 13 16
14 20 26 Shrinkage of expanded beads none none none none none none
Closed cell content (%) 95 95 95 95 96 95 Average cell diameter
(.mu.m) 117 143 124 85 121 80
TABLE-US-00002 TABLE 1-2 Example 7 8 9 10 11 Resin Particles Core
Resin Composition *1) *1) *1) *1) *1) layer Melting point (.degree.
C.) 155 155 155 155 155 Outer Resin Composition *3) -- *3) *3) *3)
layer Melting point (.degree. C.) none -- none none none Core
layer/Outer layer (weight ratio) 95/5 -- 95/5 95/5 95/5 MFR (g/10
min); 190.degree. C., 2.16 kgf 3.5 3.3 3.5 3.5 3.5 Glass transition
temperatureTg (.degree. C.) 56 56 56 56 56 Melting point (.degree.
C.) 155 155 155 155 155 Melt tension MT (mN); 190.degree. C. *0 19
19 19 19 19 Melt viscosity .eta.(Pa s); 190.degree. C., 20
sec.sup.-1 *0 2,830 2,790 2,830 2,830 2,830 0.93log.eta. - logMT *0
1.93 1.93 1.93 1.93 1.93 Half ciystallizataion time CT.sub.1/2
(sec) *0 1,720 1,680 1,720 1,720 1,720 Expanded Beads Blowing agent
CO.sub.2 CO.sub.2 CO.sub.2 CO.sub.2 CO.sub.2 Autoclave inside
pressure (MPa (G)) 2.2 2.4 3.5 4 4 Foaming temperature FT (.degree.
C.) 139 137.5 134.5 133.5 133 FT - Tg (.degree. C.) 83 82 79 78 77
Apparent density (g/L) 119 119 61 49 49 High temperature peak
calorific value (J/g) 0.0 2.2 2.5 0.0 0.4 Br:endo (J/g) 32 32 32 33
32 Brc:endo (J/g) 31 32 32 33 33 Brs:endo (J/g) 26 32 25 26 26
Bfc:exo (J/g) 19 22 14 16 12 Bfc:endo (J/g) 27 31 28 27 30 Bfc:endo
- Bfc:exo (J/g) 8 9 14 11 18 Shrinkage of expanded beads none none
none slightly slightly Closed cell content (%) 96 96 95 94 94
Average cell diameter (.mu.m) 143 103 98 124 80 In the Tables 1-1
and 1-2, *0, *1, *3 and *5 are as follows: *0: Values measured on a
cut out core layer of the multi-layered resin particle; *1):
Crystalline PLA; produced by Nature Works LLC (D-isomer content:
4.4%, melting point: 155.degree. C., MFR (190.degree. C./2.16 kgf):
2.9 g/10 min; *3): Non-crystalline PLA; produced by Nature Works
LLC (D-isomer content: 11.8%, melting point: not confirmed, MFR
(190.degree. C./2.16 kgf): 4.4 g/10 min; *5): Crystalline PLA;
produced by Nature Works LLC (D-isomer content: 4.1%, melting
point: 158.degree. C., MFR (190.degree. C./2.16 kgf): 3.1 g/10
min;
TABLE-US-00003 TABLE 2 Comparative Example 1 2 3 4 5 Resin Core
Resin Composition *2) *4) *2)/ *3) = 6/4 *2) *2) Particles layer
(weight ratio) Melting point (.degree. C.) 168 168 167 168 168
Outer Resin Composition *3) *3) *3) *3) *3) layer Melting point
(.degree. C.) none none none none none Core layer/Outer layer
(weight ratio) 95/5 95/5 95/5 95/5 95/5 MFR (g/10 min); 190.degree.
C., 2.16 kgf 3.7 11.4 4.5 3.7 3.7 Glass transition temperatureTg
(.degree. C.) 56 57 56 56 56 Melting point (.degree. C.) 169 168
166 169 169 Melt tension MT (mN); 190.degree. C. *0 18 unable to 15
18 18 measure Melt viscosity .eta.(Pa s); 190.degree. C., 20
sec.sup.-1 *0 2,920 990 2,300 2,920 2,920 0.93log.eta. - logMT *0
1.97 -- 1.95 1.97 1.97 Half crystallizataion time CT.sub.1/2 (sec)
*0 350 310 470 350 350 Expanded Blowing agent CO.sub.2 CO.sub.2
CO.sub.2 CO.sub.2 CO.sub.2 Beads Autoclave inside pressure (MPa
(G)) 2.0 2.2 2.5 4.0 4.5 Foaming temperature FT (.degree. C.) 147.5
148.5 146.5 143.5 141.5 FT - Tg (.degree. C.) 92 92 91 88 86
Apparent density (g/L) 119 119 119 61 49 High temperature peak
calorific value (J/g) 3.0 2.6 3.3 0.0 0.7 Br:endo (J/g) 42 43 26 42
41 Brc:endo (J/g) 42 44 26 42 42 Brs:endo (J/g) 33 33 21 32 32
Bfc:exo (J/g) 14 11 9 13 15 Bfc:endo (J/g) 39 42 24 38 39 Bfc:endo
- Bfc:exo (J/g) 25 31 15 25 24 Shrinkage of expanded beads present
present present present present Closed cell content (%) 92 92 90 88
88 Average cell diameter (.mu.m) 149 170 161 110 102 In the Table
2, *0, *2, *3 and *4 are as follows: *0: Values measured on a cut
out core layer of the multi-layered resin particle; *2):
Crystalline PLA; produced by Nature Works LLC (D-isomer content:
1.5%, melting point: 168.degree. C., MFR (190.degree. C./2.16 kgf):
3.1 g/10 min; *3): Non-crystalline PLA; produced by Nature Works
LLC (D-isomer content: 11.8%, melting point: not confirmed, MFR
(190.degree. C./2.16 kgf): 4.4 g/10 min; *4): Crystalline PLA;
produced by Nature Works LLC (D-isomer content: 1.4%, melting
point: 168.degree. C., MFR (190.degree. C./2.16 kgf): 11.6 g/10
min;
[0151] Next, molded articles were prepared using the expanded beads
obtained in the foregoing Examples and Comparative Examples. The
expanded beads obtained in each of the above Examples and
Comparative Examples were first subjected to a pressurizing
treatment to impart the internal pressure shown in Tables 3 and 4.
The expanded beads having the increased internal pressure were
placed in a cavity of the flat plank mold having a length of 200
mm, a width of 250 mm and a thickness of 50 mm and subjected to an
in-mold molding process by steam heating to obtain molded articles
each in the form of a plank. The heating with steam was performed
as follows. Steam was fed for 5 seconds for preheating in such a
state that drain valves of the stationary and moveable molds were
maintained in an open state (purging step). Next, while maintaining
only the drain valve on the stationary mold in an open state, steam
was fed from the moveable mold for 3 seconds. Then, while
maintaining only the drain valve on the moveable mold in an open
state, steam was fed from the stationary mold for 3 seconds.
Thereafter, heating was carried out with the heating steam pressure
(molding vapor pressure) shown in Tables 3 and 4.
[0152] After completion of the heating, cooling with water was
carried out until a surface pressure attributed to the expanding
force of the molded article was reduced to 0.01 MPa(G). The molds
were then opened and the molded body was taken out therefrom. The
molded body was aged in an oven at 40.degree. C. for 15 hours, then
aged in an oven at 70.degree. C. for another 15 hours, and
thereafter allowed to gradually cool to room temperature to obtain
a molded article.
[0153] Each of the thus prepared molded articles were evaluated for
their various physical properties such as appearance, bending
modulus, 50% compression stress, degree of fusion bonding and
shrinkage. The results are summarized in Tables 3 and 4.
TABLE-US-00004 TABLE 3 Example 1 2 3 4 5 6 7 8 9 10 11 Expanded
Molding Bead internal 0.05 0.05 0.10 0.05 0.05 0.05 0.05 0.05 0.06
0.06 0.06 Beads Conditions pressure (MPa (G)) Molded Vapor pressure
0.08 0.04 0.16 0.10 0.12 0.08 0.06 0.16 0.08 0.08 0.08 Article (MPa
(G)) Physical Density of molded 84 84 84 84 84 84 84 84 42 33 33
Properties article (g/L) Shrinkage (%) 1.7 1.6 1.7 1.6 1.6 1.7 1.6
1.7 1.6 1.6 1.6 Fusion bonding 90 90 80 80 90 90 70 50 100 100 100
degree (%) 50% compressive 0.87 0.81 1.00 0.88 0.92 0.90 0.81 0.85
0.46 0.31 0.34 stress (MPa) Bending modulus 30 21 31 29 29 29 18 29
17 10 10 (MPa) Bending modulus/ 0.35 0.25 0.37 0.35 0.35 0.34 0.22
0.34 0.40 0.30 0.30 Density of molded article (MPa L/g) Heat
resistance; -0.5 -0.5 -0.3 -0.6 -0.4 -0.5 -0.3 -0.3 -1.2 -1.8 -1.8
dimension change upon heating [120.degree. C.] (%) Appearance good
good fair good good good good good good good good
TABLE-US-00005 TABLE 4 Comparative Example 1 2 3 4 5 Expanded Beads
Molding Bead internal 0.05 0.05 0.05 0.06 0.06 Molded Article
Conditions pressure (MPa (G)) Vapor pressure 0.08 0.08 0.08 0.08
0.08 (MPa (G)) Physical Density of molded 84 84 84 42 33 Properties
article (g/L) Shrinkage (%) 1.4 1.4 2.0 1.4 1.6 Fusion bonding 90
80 80 90 80 degree (%) 50% compressive 0.80 0.73 0.77 0.38 0.33
stress (MPa) Bending modulus 15 13 14 7 6 (MPa) Bending modulus/
0.18 0.16 0.17 0.16 0.19 Density of molded article (MPa L/g) Heat
resistance; -0.3 -0.4 -2.3 -1.0 -1.6 dimension change upon heating
[120.degree. C.](%) Appearance good good fair good good
[0154] Methods for evaluating physical properties of the expanded
beads and foamed molded articles are as follows.
Appearance:
[0155] Appearance was evaluated by observation of a surface of a
molded article with naked eyes and rated as follows:
Good: Almost no spaces between beads are observed in the surface of
the molded article and the surface state is good. Fair: Spaces
between beads are observed, although not significantly, in the
surface of the molded article. Poor: Spaces between beads are
significantly observed in the surface of the molded article.
Degree of Fusion Bonding:
[0156] A degree of fusion bonding is evaluated in terms of a
proportion (percentage) of the number of expanded beads that
underwent material failure based on the number of expanded beads
that were exposed on a ruptured cross section obtained by rupturing
a molded article. More specifically, a test piece was cut out from
each of the molded articles. A cut with a depth of about 5 mm was
then formed on each test piece with a cutter knife. Each test piece
was then ruptured along the cut line. The ruptured cross section
was observed to count a number (n) of the expanded beads present on
the cross section and a number (b) of the expanded beads which
underwent material failure. The ratio (b/n) in terms of percentage
of (b) based on (n) represents the fusion bonding degree (%).
Density of Molded Article:
[0157] The density of the molded article was measured as follows.
The molded article was allowed to stand at a temperature of
23.degree. C. under a relative humidity of 50% for 24 hours and
measured for its outer dimension to determine the bulk volume
thereof. The molded article was then weighed precisely. The weight
(g) of the molded article was divided by the bulk volume and the
unit was converted to determine the bulk density (g/L) thereof.
50% Compression Stress:
[0158] A test piece (without skin) having a length of 50 mm, a
width of 50 mm and a thickness of 25 mm was cut out from a molded
article and was subjected to a compression test in which the test
piece was compressed in the thickness direction at a compression
rate of 10 mm/min according to JIS K6767 (1999) to determine 50%
compression stress of the molded article.
Bending Modulus:
[0159] A test piece (without skin) having a length of 120 mm, a
width of 25 mm and a thickness of 20 mm was cut out from a molded
article and was subjected to a bending test in which the test piece
was bent at a rate of 10 mm/min according to JIS K7221-1 (1999) to
determine bending modulus of the molded article.
Dimension Change Upon Heating:
[0160] The molded articles were each evaluated for their heat
resistance in terms of dimension change upon heating. In accordance
with JIS K6767 (1999), "thermal stability (Dimensional Stability at
High Temperatures", method B)", a test piece was heated for 22
hours in a gear oven maintained at 120.degree. C. Thereafter, the
test piece was taken out of the oven and allowed to stand for 1
hour in a constant temperature and humidity room maintained at
23.degree. C. and 50% relative humidity. From the dimensions before
and after the heating, a change in dimension upon heating is
calculated according to the following formula:
Dimension change upon heating (%)=(([Dimension after
heating]-[Dimension before heating])/[Dimension before
heating]).times.100
[0161] From the comparison between Examples and Comparative
Examples, it is seen that the expanded beads obtained in Examples
are free of or almost free of shrinkage and that the molded
articles obtained therefrom have excellent mechanical properties
(bending modulus and compressive strength) and heat resistance.
* * * * *