U.S. patent application number 14/130531 was filed with the patent office on 2014-08-07 for multiple emulsions and techniques for the formation of multiple emulsions.
This patent application is currently assigned to President and Fellows of Harvard College. The applicant listed for this patent is Alireza Abbaspourrad, Shin-Hyn Kim, David A. Weitz. Invention is credited to Alireza Abbaspourrad, Shin-Hyn Kim, David A. Weitz.
Application Number | 20140220350 14/130531 |
Document ID | / |
Family ID | 46516865 |
Filed Date | 2014-08-07 |
United States Patent
Application |
20140220350 |
Kind Code |
A1 |
Kim; Shin-Hyn ; et
al. |
August 7, 2014 |
MULTIPLE EMULSIONS AND TECHNIQUES FOR THE FORMATION OF MULTIPLE
EMULSIONS
Abstract
Multiple emulsions and techniques for the formation of multiple
emulsions are generally described. A multiple emulsion, as used
herein, describes larger droplets that contain one or more smaller
droplets therein. In some embodiments, the larger droplet or
droplets may be suspended in a carrying fluid containing the larger
droplets that, in turn, contain the smaller droplets. As described
below, multiple emulsions can be formed in one step in certain
embodiments, with generally precise repeatability, and can be
tailored in some embodiments to include a relatively thin layer of
fluid separating two other fluids.
Inventors: |
Kim; Shin-Hyn; (Cambridge,
MA) ; Abbaspourrad; Alireza; (Cambridge, MA) ;
Weitz; David A.; (Bolton, MA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Kim; Shin-Hyn
Abbaspourrad; Alireza
Weitz; David A. |
Cambridge
Cambridge
Bolton |
MA
MA
MA |
US
US
US |
|
|
Assignee: |
President and Fellows of Harvard
College
Cambridge
MA
|
Family ID: |
46516865 |
Appl. No.: |
14/130531 |
Filed: |
July 5, 2012 |
PCT Filed: |
July 5, 2012 |
PCT NO: |
PCT/US12/45481 |
371 Date: |
April 17, 2014 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61504990 |
Jul 6, 2011 |
|
|
|
61505001 |
Jul 6, 2011 |
|
|
|
Current U.S.
Class: |
428/402.21 ;
516/9 |
Current CPC
Class: |
B01F 2005/0034 20130101;
B01F 3/0811 20130101; B01F 2215/0431 20130101; B01F 3/0807
20130101; B01J 13/14 20130101; B01F 13/0069 20130101; B01F
2215/0454 20130101; B01F 2215/0404 20130101; B01F 5/045 20130101;
B01F 5/0085 20130101; B01F 13/0062 20130101; B01F 2003/0838
20130101; B01J 13/12 20130101; B01J 13/04 20130101; B01F 13/0059
20130101; B01F 2215/0495 20130101; Y10T 428/2985 20150115 |
Class at
Publication: |
428/402.21 ;
516/9 |
International
Class: |
B01F 5/00 20060101
B01F005/00; B01F 3/08 20060101 B01F003/08 |
Claims
1. A method of forming droplets, the method comprising: flowing a
first fluid in a first conduit; expelling the first fluid from an
exit opening of the first conduit into a second fluid in a second
conduit such that droplets of the first fluid are not formed at the
exit opening of the first conduit; and expelling the first fluid
and the second fluid from an exit opening of the second conduit
into a third fluid to form a multiple emulsion droplets comprising
the second fluid surrounding droplets of the first fluid.
2. A method of forming droplets, the method comprising: expelling a
first fluid from an exit opening of a first conduit into a second
fluid in a second conduit; and expelling the first fluid and the
second fluid from an exit opening of the second conduit into a
third fluid to form a multiple emulsion droplets comprising a shell
of the second fluid surrounding droplets of the first fluid,
wherein: the shell has an average thickness of less than about 0.05
times the average cross-sectional diameter of the multiple emulsion
and/or the shell has an average thickness of less than about 1
micrometer.
3-6. (canceled)
7. The method of claim 1, wherein the flow rate of the first fluid
and the flow rate of the second fluid are selected such that
jetting flow of the first fluid within the second fluid occurs
within the second conduit.
8. The method of claim 1, further comprising collecting the
multiple emulsion droplets in a third conduit.
9. The method of claim 8, wherein the multiple emulsion droplets
are formed within the third conduit.
10. The method of claim 8, wherein the first fluid and the second
fluid ejected from the second conduit form multiple emulsion
droplets prior to entering the third conduit.
11. The method of claim 1, wherein substantially all of the
multiple emulsion droplets produced are double emulsion
droplets.
12. The method of claim 1, wherein the first conduit has a
capillary number such that no droplets are produced at the exit
opening of the first conduit.
13. The method of claim 1, wherein the first fluid and the second
fluid are selected to have viscosities such that no droplets are
produced at the exit opening of the first conduit.
14. The method of claim 1, wherein the first fluid and the second
fluid are expelled from the exit opening of the second conduit into
a third conduit.
15. The method of claim 1, wherein the second fluid comprises a
polymer suspended in the fluid.
16-33. (canceled)
34. An article, comprising: a particle having a shell comprising a
polymer, the particle having an average diameter of less than about
1 mm, the shell at least partially containing a fluid, wherein: the
shell has an average thickness of less than about 0.05 times the
average cross-sectional diameter of the particle and/or the shell
has an average thickness of less than about 1 micrometer; and
substantially all of the polymer within the shell has a glass
transition temperature of at least about 85.degree. C. and/or
substantially all of the polymer within the shell is at least
partially soluble in octane.
35. The article of claim 34, wherein the shell has an average
thickness of less than about 1 micrometer.
36. The article of claim 34, wherein the shell has an average
thickness of less than about 0.05 times the average cross-sectional
diameter of the particle.
37-42. (canceled)
43. The article of claim 34, wherein substantially all of the
polymer within the shell has a glass transition temperature of at
least about 85.degree. C.
44-47. (canceled)
48. A collection of particles as defined in claim 34, wherein the
collection has an overall average diameter and a distribution of
diameters such that the coefficient of variation of the
cross-sectional diameters of the particles is less than about
10%.
49-61. (canceled)
62. The method of claim 2, wherein the flow rate of the first fluid
and the flow rate of the second fluid are selected such that
jetting flow of the first fluid within the second fluid occurs
within the second conduit.
63. The method of claim 2, wherein the first conduit has a
capillary number such that no droplets are produced at the exit
opening of the first conduit.
64. The method of claim 2, wherein the first fluid and the second
fluid are selected to have viscosities such that no droplets are
produced at the exit opening of the first conduit.
65. The method of claim 2, wherein the first fluid and the second
fluid are expelled from the exit opening of the second conduit into
a third conduit.
Description
RELATED APPLICATIONS
[0001] This application claims the benefit of U.S. Provisional
Patent Application Ser. No. 61/505,001, filed Jul. 6, 2011, and of
U.S. Provisional Patent Application Ser. No. 61/504,990, filed Jul.
6, 2011, each of which is incorporated herein by reference in its
entirety.
TECHNICAL FIELD
[0002] Multiple emulsions and techniques for the formation of
multiple emulsions are generally described.
BACKGROUND
[0003] An emulsion is a fluidic state which exists when a first
fluid is dispersed in a second fluid that is typically immiscible
or substantially immiscible with the first fluid. Examples of
common emulsions are oil in water and water in oil emulsions.
Multiple emulsions are emulsions that are formed with more than two
fluids, or two or more fluids arranged in a more complex manner
than a typical two-fluid emulsion. For example, a multiple emulsion
may be oil-in-water-in-oil, or water-in-oil-in-water. Multiple
emulsions are of particular interest because of current and
potential applications in fields such as pharmaceutical delivery,
paints and coatings, food and beverage, and health and beauty
aids.
SUMMARY
[0004] Systems, articles, and methods related to multiple emulsions
are provided. The subject matter of the present invention involves,
in some cases, interrelated products, alternative solutions to a
particular problem, and/or a plurality of different uses of one or
more systems and/or articles.
[0005] In one aspect, a method of forming droplets is described. In
some embodiments, the method comprises flowing a first fluid in a
first conduit; expelling the first fluid from an exit opening of
the first conduit into a second fluid in a second conduit such that
droplets of the first fluid are not formed at the exit opening of
the first conduit; and expelling the first fluid and the second
fluid from an exit opening of the second conduit into a third fluid
to form a multiple emulsion droplets comprising the second fluid
surrounding droplets of the first fluid.
[0006] The method comprises, in some embodiments, expelling a first
fluid from an exit opening of a first conduit into a second fluid
in a second conduit; and expelling the first fluid and the second
fluid from an exit opening of the second conduit into a third fluid
to form a multiple emulsion droplets comprising a shell of the
second fluid surrounding droplets of the first fluid. In some
embodiments, the shell has an average thickness of less than about
0.05 times the average cross-sectional diameter of the multiple
emulsion and/or the shell has an average thickness of less than
about 1 micrometer.
[0007] In some embodiments, the method comprises expelling a first
fluid from an exit opening of a first conduit into a second fluid
being transported through a second conduit via a first entrance
opening of the second conduit; and flowing a third fluid and a
fourth fluid through a second entrance opening of the second
conduit to form multiple emulsion droplets comprising a shell of
the third fluid surrounding the second fluid and a shell of the
second fluid surrounding the first fluid.
[0008] In one aspect, a device is provided. In some embodiments,
the device comprises a first conduit, an outer injection conduit
having an exit opening contained within the first conduit, an inner
injection conduit having an exit opening contained within the outer
injection conduit, and a collection conduit having an entrance
opening contained within the first conduit but not contained within
the outer injection conduit. In some embodiments, the outer
injection conduit is at least partially coated with a hydrophobic
coating, and the other tubes are not coated with the hydrophobic
coating.
[0009] In one aspect, an article is provided. In some embodiments,
the article comprises a microfluidic device comprising a double
emulsion droplet production region, wherein the double emulsion
droplet production region consists essentially of a first conduit,
an outer injection conduit having an exit opening contained within
the first conduit, an inner injection conduit having an exit
opening contained within the outer injection conduit, and a
collection conduit having an entrance opening contained within the
first conduit but not contained within the outer injection
conduit.
[0010] The article comprises, in some embodiments, a particle
having a shell comprising a polymer, the particle having an average
diameter of less than about 1 mm, the shell at least partially
containing a fluid. In some embodiments, the shell has an average
thickness of less than about 0.05 times the average cross-sectional
diameter of the particle and/or the shell has an average thickness
of less than about 1 micrometer; and substantially all of the
polymer within the shell has a glass transition temperature of at
least about 85.degree. C. and/or substantially all of the polymer
within the shell is at least partially soluble in octane.
[0011] Other advantages and novel features of the present invention
will become apparent from the following detailed description of
various non-limiting embodiments of the invention when considered
in conjunction with the accompanying figures. In cases where the
present specification and a document incorporated by reference
include conflicting and/or inconsistent disclosure, the present
specification shall control.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] Non-limiting embodiments of the present invention will be
described by way of example with reference to the accompanying
figures. For purposes of clarity, not every component is labeled in
every figure, nor is every component of each embodiment of the
invention shown where illustration is not necessary to allow those
of ordinary skill in the art to understand the invention. In the
figures:
[0013] FIGS. 1A-1D are cross-sectional schematic diagrams
illustrating use of a particle to deliver a fluid and/or an agent
to a target medium, according to some embodiments;
[0014] FIGS. 2-4 show, according to some embodiments, exemplary
cross-sectional schematic diagrams of systems that can be used to
form multiple emulsions;
[0015] FIG. 5 is a schematic illustration outlining measurement of
a contact angle of a hydrophilic material;
[0016] FIGS. 6A-6E show (A) an exemplary cross-sectional schematic
diagram illustrating a system for producing certain multiple
emulsions and (B-E) optical microscope images illustrating a
production of certain multiple emulsions, according to some
embodiments;
[0017] FIGS. 7A-7E show, according to some embodiments, (A) a plot
of a flow rate of an inner stream as a function of a flow rate of a
middle stream and (B-E) optical microscope images illustrating a
production of multiple emulsions;
[0018] FIGS. 8A-8C show (A) an exemplary cross-sectional schematic
diagram illustrating a system for producing certain multiple
emulsions and (B-C) optical microscope images illustrating a
production of certain multiple emulsions, according to some
embodiments;
[0019] FIGS. 9A-9D show (A) a plot of droplet diameter as a
function of Q.sub.3 in accordance with some embodiments, (B)
optical microscope images of certain multiple emulsions, (C) a plot
of thickness as a function of flow ratios, and (D) optical
microscope images of certain multiple emulsions, according to some
embodiments;
[0020] FIGS. 10A-10D show, according to some embodiments, (A-B)
optical microscope images of certain multiple emulsions and (C-D)
confocal microscope images of certain multiple emulsions;
[0021] FIGS. 11A-11C show (A) an exemplary cross-sectional
schematic diagram illustrating a system for producing certain
multiple emulsions and (B-C) optical microscope images illustrating
a production of certain multiple emulsions, according to some
embodiments;
[0022] FIGS. 12A-12D show (A) an exemplary plot of droplet
diameters as a function of a volumetric flow rate of an inner
stream in accordance with some embodiments and (B-D) optical
microscope images illustrating a production of certain multiple
emulsions, according to some embodiments;
[0023] FIGS. 13A-13C show (A) an optical microscope image
illustrating the production of certain multiple emulsions, (B) an
exemplary plot of the number of core droplets formed as a function
of the volumetric flow rate of the inner stream according to
various embodiments, and (C) optical microscope images illustrating
a production of certain multiple emulsions, according to some
embodiments;
[0024] FIGS. 14A-14D show (A) an exemplary cross-sectional
schematic diagram illustrating a system for producing certain
multiple emulsions and (B-D) optical microscope images illustrating
a production of certain multiple emulsions, according to some
embodiments;
[0025] FIGS. 15A-15D show (A) an exemplary cross-sectional
schematic diagram illustrating a system for producing certain
multiple emulsions and (B-D) optical microscope images illustrating
the production of certain multiple emulsions, according to some
embodiments;
[0026] FIG. 16 illustrates, according to one set of embodiments, a
confocal microscope image of a particle comprising a polystyrene
shell;
[0027] FIGS. 17A-17B show (A) an optical microscope image
illustrating the production of a multiple emulsion, and (B) a
confocal microscope image of a particle containing fluorescently
labeled polystyrene nanoparticles, according to some
embodiments;
[0028] FIGS. 18A-18C show confocal microscope images illustrating a
controlled release mechanism, according to one set of
embodiments;
[0029] FIGS. 19A-19C show (A-B) confocal microscope images of
particles as they are squeezed through a glass microfluidic channel
and (C) a bright field image of a particle as it is passed through
a glass microfluidic channel, according to some embodiments;
and
[0030] FIG. 20 is a schematic illustration of delivery of an agent
to an oil-water interface, according to one set of embodiments.
DETAILED DESCRIPTION
[0031] Multiple emulsions and techniques for the formation of
multiple emulsions are generally described. A multiple emulsion, as
used herein, describes one or more larger droplets that contain one
or more smaller droplets therein. In some embodiments, the larger
droplets may be suspended in a carrying fluid containing the larger
droplets that, in turn, contain the smaller droplets. As described
below, multiple emulsions can be formed in one step in certain
embodiments, with generally precise repeatability, and can be
tailored in some embodiments to include a relatively thin layer of
fluid separating two other fluids.
[0032] The formation of emulsions and multiple emulsions containing
droplets with a uniform size, shape, and/or a uniform number of
smaller droplets contained within larger droplets is known in the
art. For example, International Patent Publication No. WO
2008/121342 by Weitz, et al., describes the use of microfluidic
systems to produce multiple emulsions containing uniformly sized
larger droplets each containing smaller droplets. Generally, in
these systems, multiple emulsions are formed by nesting multiple
immiscible fluids within a microfluidic conduit system. The
multiple emulsions can be produced by first producing one or more
droplets of a first fluid within a second fluid at the exit of a
first conduit. These droplets are then transported to the end of a
second conduit, where a multiple emulsion is formed in which the
second fluid surrounds the droplets of the first fluid.
[0033] In addition, the formation of multiple emulsions in which
the first and second droplets are formed simultaneously is known in
the art. For example, International Patent Publication Number WO
2006/096571 by Weitz, et al., includes a description of various
microfluidic systems in which fluids are transported through two
nested conduits contained within another conduit to produce
multiple emulsions. However, multiple conduits are typically used
in these systems, and in some cases, an inner conduit is nested
within a surrounding conduit such that the exit opening of the
inner conduit extends past the exit opening of the surrounding
conduit. As another example, International Patent Publication
Number WO 2011/028764, by Weitz, et al., describes the formation of
multiple emulsions, but in various systems that include certain
intersections of different conduits.
[0034] The present invention is generally directed to surprising
new methods of flowing fluids in conduits (and associated articles
and systems) to produce multiple emulsions. As described in more
detail below, it has been discovered that increasing fluid flow
rates from a stable operating regime produces an unstable operating
regime, but unexpectedly, further increases in flow rates produce a
second stable operating regime. In some cases, the multiple
emulsions formed within the second, stable operating regime may
comprise relatively thin intermediate fluid shells. Rather than
first producing droplets of a first fluid at an exit opening of a
first conduit and subsequently passing these droplets through an
end of a second conduit to produce a double emulsion (i.e.,
operating under a "droplet flow" regime), the first and second
droplets within the multiple emulsions of the present invention may
be formed simultaneously. Simultaneous formation of the first and
second droplets can be achieved, in some embodiments, by
transporting a first fluid within a first conduit at a relatively
high flow rate such that the first fluid forms a continuous stream
of fluid within the second fluid as the first fluid exits the first
conduit (i.e., a "jetting flow" regime). As the jet of the first
fluid exits a second conduit located downstream of the first
conduit, the second fluid can surround the first fluid, thereby
forming a double emulsion. When operated under a jetting flow
regime, the multiple emulsions formed at the exit opening of the
second conduit may contain, in some embodiments, relatively thin
shells of the second fluid. In addition, operation under a jetting
flow regime may allow for high speed production of multiple
emulsions, relative to the droplet flow regime, at least in some
cases.
[0035] One reason the benefits of operation under a jetting flow
regime in certain embodiments are surprising is because, in order
to transition from the droplet flow regime to the jetting flow
regime, one must first pass through an intermediate regime in which
the fluid flow is unstable and generally unsuitable for producing
multiple emulsions, especially consistently-sized multiple
emulsions. In the present invention, it has been unexpectedly found
that further increases in fluid flow rates do not lead to increased
fluid instability, as would be expected; rather, further increases
in flow rates from an unsteady regime surprisingly lead to more
stability, not less. In particular, it has been found that
increasing the flow rate through the unsteady regime may lead to
stable operation, for example, in which consistently-sized multiple
emulsions with the relatively thin shells can be produced at
relatively high speeds.
[0036] A multiple emulsion droplet may contain one or more droplets
therein. A "droplet," as used herein, is an isolated portion of a
first fluid that is surrounded by a second fluid. It is to be noted
that a droplet is not necessarily spherical, but may assume other
shapes as well, for example, depending on the external environment.
In some embodiments, the droplet has a minimum cross-sectional
dimension that is substantially equal to the largest dimension of
the channel perpendicular to fluid flow in which the droplet is
located.
[0037] Using the methods and devices described herein, in certain
embodiments, a consistent volume and/or number of droplets are
produced, and/or a consistent ratio of volume and/or number of
outer droplets to inner droplets (or other such ratios) are
produced. In addition, as described elsewhere, the relative volumes
of the fluidic droplets within the multiple emulsion are configured
in some cases to include a relatively thin layer of fluid, e.g.,
separating two other fluids. For example, in some cases, a single
droplet within an outer droplet is configured/formed such that the
inner droplet occupies a relatively large percentage of the volume
of the outer droplet, thereby resulting in a thin layer of outer
droplet fluid surrounding the inner droplet fluid. The thin layer
of outer droplet fluid surrounding the inner droplet fluid, which
may contain a polymer, may be subsequently dried to form a solid
shell containing a fluid. The ability to precisely control the
dimensions of the thin layer of outer droplet fluid can allow one
to fabricate particles configured with thin shells, including any
of the thicknesses or other dimensions described elsewhere
herein.
[0038] In some embodiments, a triple emulsion may be produced,
i.e., an emulsion containing an inner droplet (or first) fluid,
surrounded by an outer droplet (or second) fluid, which in turn is
surrounded by a third or carrying fluid. In some cases, the
carrying fluid and the outer droplet fluid may be the same. These
fluids are often of varying miscibilities due to differences in
hydrophobicity. For example, the inner droplet fluid may be water
soluble, the outer droplet fluid oil soluble, and the carrying
fluid water soluble. This configuration is often referred to as a
W/O/W multiple emulsion ("water/oil/water"). Another multiple
emulsion may include an inner droplet fluid that is oil soluble, an
outer droplet fluid that is water soluble, and a carrying fluid
that is oil soluble. This type of multiple emulsion is often
referred to as an O/W/O multiple emulsion ("oil/water/oil"). It
should be noted that the term "oil" in the above terminology merely
refers to a fluid that is generally more hydrophobic and not
miscible or soluble in water, as is known in the art. Thus, the oil
may be a hydrocarbon in some embodiments, but in other embodiments,
the oil may comprise other hydrophobic fluids.
[0039] In the descriptions herein, multiple emulsions are generally
described with reference to a three phase system, i.e., having an
inner droplet fluid, an outer droplet fluid, and a carrying fluid.
However, it should be noted that this is by way of example only,
and that in other systems, additional fluids may be present within
the multiple emulsion. As examples, an emulsion may contain a first
fluid droplet and a second fluid droplet, each surrounded by a
third fluid, which is in turn surrounded by a fourth fluid; or an
emulsion may contain multiple emulsions with higher degrees of
nesting, for example, a first fluid droplet surrounded by a second
fluid droplet, which is surrounded by a third fluid droplet, which
is contained within a carrying fluid. Accordingly, it should be
understood that the descriptions of the inner droplet fluid, outer
droplet fluid, and carrying fluid are for ease of presentation, and
that the descriptions herein are readily extendable to systems
involving additional fluids, e.g., quadruple emulsions, quintuple
emulsions, sextuple emulsions, septuple emulsions, etc.
[0040] FIG. 2 includes an exemplary schematic diagram of a system
200 to form multiple emulsions, which may be used to form
particles, according to some embodiments. In FIG. 2, system 200
includes outer conduit 210, a first inner conduit (or injection
tube) 220, and a second inner conduit (or collection tube) 230.
First inner conduit 220 includes an exit opening 225 that opens
into the outer conduit 210, and second inner conduit 230 includes
an entrance opening 235 that opens within the outer conduit 210.
System 200 also includes a third inner conduit 240 disposed within
first inner conduit 220. Inner conduit 240 includes an exit opening
245 that opens into conduit 220. As illustrated in FIG. 2, conduits
210, 220, 230, and 240 are illustrated as being concentric relative
to each other. However, it should be noted that "concentric," as
used herein, does not necessarily refer to tubes that are strictly
coaxial, but also includes nested or "off-center" tubes that do not
share a common center line. In some embodiments, however, the tubes
may all be strictly coaxial with each other.
[0041] The inner diameter of conduit 220 generally decreases in a
direction from left to right, as shown in FIG. 2, and the inner
diameter of conduit 230 generally increases from the entrance
opening in a direction from left to right as exhibited in FIG. 2.
These constrictions, or tapers, provide geometries that aid in
producing consistent emulsions, at least in some cases. While the
rate of constriction is illustrated as being linear in FIG. 2, in
other embodiments, the rate of constriction may be non-linear.
[0042] As shown in FIG. 2, inner droplet fluid 250 flows through
third inner conduit 240 and out of exit opening 245 into conduit
220, in a left to right direction. In addition, outer droplet fluid
260 is illustrated flowing through conduit 220 in a left to right
direction, outside inner droplet fluid 250 and conduit 240.
Carrying fluid 270 is illustrated flowing in a left to right
direction in the pathway provided between outer conduit 210 and
conduit 220.
[0043] As illustrated in FIG. 2, inner droplet fluid 250 exits from
exit opening 225 and is restrained from contacting the inner
surface of conduit 220 by outer droplet fluid 260. As shown in the
example of FIG. 2, no portion of inner fluid 250 contacts the inner
surface of conduit 220 after its exit from conduit 240. In some
embodiments, various system parameters can be chosen such that
droplets of the first fluid are not formed at the exit opening of
the first conduit. For example, in some embodiments, the flow rates
of inner droplet fluid 250 and outer droplet fluid 260 can be
chosen such that inner droplet fluid 250 forms the inner fluid (or
core) and outer droplet fluid 260 forms the outer fluid (or sheath)
in a core-sheath flow arrangement. As illustrated in FIG. 2, outer
droplet fluid 260 does not completely surround inner droplet fluid
250 to form a droplet, but rather, outer droplet fluid 260 forms a
sheath that surrounds inner droplet fluid 250 about its
longitudinal axis. In some embodiments, conduit 240 has a capillary
number such that no droplets are produced at the exit opening of
conduit 240. As another example, inner droplet fluid 250 and/or
outer droplet fluid 260 can be selected to have viscosities such
that no droplets are produced at the exit opening of conduit
240.
[0044] Additionally, in some embodiments, outer droplet fluid 260
may not come into contact with the surface of conduit 230, at least
until after a multiple emulsion droplet has been formed, because
outer droplet fluid 260 is surrounded by carrying fluid 270 as the
droplet enters collection tube 230.
[0045] As inner droplet fluid 250 and outer droplet fluid 260 are
transported out of exit opening 225 of conduit 220, two droplets
may be formed: an outer droplet 280 (including outer droplet fluid
260) and an inner droplet 285 (including inner droplet fluid 250)
positioned within the outer droplet 280. As illustrated in FIG. 2,
outer droplet 280 may form a relatively thin shell around inner
droplet 285. Droplets 280 and 285 may be formed sequentially, or
substantially simultaneously. For example, in FIG. 2, as fluids 250
and 260 are transported out of the exit opening 225 of conduit 220,
the boundary between fluids 250 and 260 can be closed (e.g., by
forming a substantially enclosed interface between the two fluids)
at substantially the same time as the boundary between fluids 260
and 270 is formed. The droplets formed from the fluids exiting
conduit 220 may be transported away from exit opening 225 and
through opening 235 of conduit 230 by carrying fluid 270 as the
droplets are transported through conduit 210.
[0046] While inner droplet fluid 250 is illustrated as forming a
continuous jet extending from conduit 240 to exit opening 225 of
conduit 220 in FIG. 2, in some embodiments, inner droplet fluid 250
may form one or more droplets prior to reaching exit opening 225.
The droplets produced within conduit 220 may be further broken up
upon exiting exit opening 225 of conduit 220 in certain cases. In
some embodiments, the flow rates of inner droplet fluid 250 and/or
outer droplet fluid 260 and/or other parameters within the system
(e.g., fluid viscosities, channel dimensions, channel wall
properties, etc.) can be selected such that jetting flow of inner
droplet fluid 250 within outer droplet fluid occurs 260 within
conduit 220. As used herein, a "jetting flow" regime refers to a
condition in which a continuous stream of a first fluid (e.g.,
inner droplet fluid 250) extends longitudinally through a
continuous stream of a second fluid without, in the regime,
breaking up to form droplets of the inner fluid within the outer
fluid (although breakup of the same fluid into droplets typically
occurs outside of the jetting flow regime). In some embodiments,
the fluid in the jetting flow regime (e.g., inner droplet fluid 250
in FIG. 2) can be continuous over a length of at least about 5, at
least about 10, or at least about 25 times the cross-sectional
diameter of the droplets that are eventually formed from the fluid,
wherein the continuous length is measured from the exit opening of
the conduit through which the fluid is delivered to the point at
which the fluid breaks up to form droplets.
[0047] In contrast, a "dripping flow" regime refers to a condition
in which a first fluid is broken up into droplets in a second fluid
within a distance from the exit of the conduit through which it is
delivered (e.g., conduit 240 in FIG. 2) that is less than or equal
to about 2 times the average cross-sectional diameter of the first
fluid droplets that are formed. As one particular example, in the
set of embodiments illustrated in FIG. 2, inner droplet fluid 250
is illustrated as flowing from conduit 240 in a jetting flow
regime, while inner droplet fluid 250 and outer droplet fluid 260
are illustrated as flowing from conduit 220 in a dripping flow
regime.
[0048] In some embodiments, inner droplet fluid 250 and outer
droplet fluid 260 do not break to form droplets until the fluids
are inside of conduit 230 (i.e., to the right of end 235, which
defines the entrance orifice of conduit 230 in FIG. 2). In other
embodiments, however, inner droplet fluid 250 and outer droplet
fluid 260 break to from droplets prior to entering conduit 230
(i.e., to the left of end 235). Under "dripping" conditions, the
droplets are formed closer to the orifice at end 235 of conduit
230, while under "jetting" conditions, the droplets are formed
further downstream, i.e., farther to the right as illustrated in
FIG. 2. For example, under certain "dripping" conditions, droplets
are produced when positioned within a single orifice diameter; this
mode of operation can be analogized to a dripping faucet. Under
some jetting conditions, a long jet is produced that extends three
or more orifice diameters downstream down the length of the
collection tube, where the jet breaks into droplets.
[0049] Droplet formation and morphology (and/or the corresponding
morphology of particles formed from the droplets) can be affected
in a number of ways, in various embodiments of the invention. For
example, the geometry (physical configuration) of the device 200,
including the relationship of the outer conduit and the inner
conduits, may be configured to develop multiple emulsions of
desired volume, frequency, and/or content. For example, the
diameters of the exit openings at exit openings 225 and/or 245 of
conduits 220 and 240, respectively, may be selected to help control
the relative volumes of the formed droplets. Droplet formation may
be affected, in some cases, by the rate of flow of the inner
droplet fluid, the rate of flow of the outer droplet fluid, the
rate of flow of the carrying fluid, the total amount of flow or a
change in the ratios of any two of these, and/or combinations of
any of these flow rates.
[0050] The relative volumes of the inner droplet and the outer
droplet may also be carefully controlled in certain embodiments,
i.e., the ratio of the size or volume of the inner and outer
droplets. The inner droplet may fill a relatively large portion of
the outer droplet. Such emulsions can be useful, for example, in
forming particles with relatively thin shells, as discussed herein.
In some embodiments, the inner fluid droplet may fill greater than
about 10%, about 20%, about 30%, about 40%, about 50%, about 60%,
about 70%, about 90%, about 95%, or about 99% of the volume of the
outer droplet. In some cases, the outer droplet can be considered a
fluid shell, or coating, when it contains an inner droplet, as some
or most of the outer droplet volume may be filled by the inner
droplet. In some embodiments, the outer fluid shell thickness can
be equal to or less than, for example, about 5%, about 4%, about
3%, about 2%, about 1%, or about 0.1% of the outer fluid droplet
radius. This allows, in some embodiments, for the formation of
multiple emulsions with only a very thin layer of material
separating, and thus stabilizing, two miscible fluids.
[0051] Of course, the invention is not limited to the formation of
multiple emulsions including thin outer droplets, and, in other
embodiments, the inner droplet may fill only a small portion of the
outer droplet. In some embodiments, the inner droplets may fill
less than about 90%, less than about 80%, less than about 70%, less
than about 60%, less than about 50%, less than about 30%, less than
about 20%, or less than about 10% of the volume of the outer
droplet. The shell material can also be greater than or equal to,
e.g., about 10%, about 20%, about 30%, about 40%, or about 50% of
the outer fluid droplet radius.
[0052] In addition, by controlling the geometry (physical
configurations) of the conduits and/or the flow of fluid through
the conduits, the average cross-sectional diameters of the droplets
that are produced may be controlled in certain embodiments. Those
of ordinary skill in the art will be able to determine the average
cross-sectional diameter (or other characteristic dimension) of a
plurality or series of droplets, for example, using laser light
scattering, microscopic examination, or other known techniques. The
average cross-sectional diameter of a single droplet, in a
non-spherical droplet, is the diameter of a perfect sphere having
the same volume as the non-spherical droplet. The average
cross-sectional diameter of a droplet (and/or of a plurality or
series of droplets) may be, for example, less than about 1 mm, less
than about 500 micrometers, less than about 200 micrometers, less
than about 100 micrometers, less than about 75 micrometers, less
than about 50 micrometers, less than about 25 micrometers, less
than about 10 micrometers, or less than about 5 micrometers in some
cases. The average cross-sectional diameter may also be at least
about 1 micrometer, at least about 2 micrometers, at least about 3
micrometers, at least about 5 micrometers, at least about 10
micrometers, at least about 15 micrometers, or at least about 20
micrometers in certain cases. In some embodiments, at least about
50%, at least about 75%, at least about 90%, at least about 95%, or
at least about 99% of the droplets within a plurality of droplets
has an average cross-sectional diameter within any of the ranges
outlined in this paragraph.
[0053] The droplets may be of substantially the same shape and/or
size (i.e., "monodisperse"), or of different shapes and/or sizes,
depending on the particular application. In some cases, the
droplets may have a homogenous distribution of cross-sectional
diameters, i.e., the droplets may have a distribution of
cross-sectional diameters such that no more than about 10%, about
5%, about 3%, about 1%, about 0.03%, or about 0.01% of the droplets
have an average diameter that is more than about 10%, about 5%,
about 3%, about 1%, about 0.03%, or about 0.01% different from the
average cross-sectional diameter of the droplets. Some techniques
for producing homogenous distributions of cross-sectional diameters
of droplets are disclosed in International Patent Application No.
PCT/US2004/010903, filed Apr. 9, 2004, entitled "Formation and
Control of Fluidic Species," by Link et al., published as WO
2004/091763 on Oct. 28, 2004, incorporated herein by reference, and
in other references as described below and/or incorporated herein
by reference.
[0054] In some cases, such as when the outer droplets (containing
outer droplet fluid 260) are formed at the same rate as are inner
droplets (containing inner droplet fluid 250), there can be a
one-to-one correspondence between the number of inner droplets and
the number of outer droplets; for example, in some embodiments,
each inner droplet is surrounded by an outer droplet, and each
outer droplet contains a single inner droplet of inner fluid. In
other embodiments, different ratios of the number of inner droplets
and the number of outer droplets may be present. In some
embodiments, substantially all of the multiple emulsion droplets
that are produced are double emulsion droplets.
[0055] In some embodiments of the invention, at least a portion of
a multiple emulsion may be solidified to form a particle, for
example, an outer fluid and/or an inner fluid. A fluid can be
solidified using any suitable method. For example, in some
embodiments, the fluid may be dried, gelled, and/or polymerized,
and/or otherwise solidified, e.g., to form a solid, or at least a
semi-solid. The solid that is formed may be rigid in some
embodiments, although in other cases, the solid may be elastic,
rubbery, deformable, etc. In some cases, for example, an outer
fluid may be solidified to form a solid shell at least partially
containing an interior containing a fluid and/or an agent. Any
technique able to solidify at least a portion of a fluidic droplet
can be used. For example, in some embodiments, a fluid within a
fluidic droplet may be removed to leave behind a material (e.g., a
polymer) capable of forming a solid shell. In other embodiments, a
fluidic droplet may be cooled to a temperature below the melting
point or glass transition temperature of a fluid within the fluidic
droplet, a chemical reaction may be induced that causes at least a
portion of the fluidic droplet to solidify (for example, a
polymerization reaction, a reaction between two fluids that
produces a solid product, etc.), or the like. Other examples
include pH-responsive or molecular-recognizable polymers, e.g.,
materials that gel upon exposure to a certain pH, or to a certain
species.
[0056] In some embodiments, a fluidic droplet is solidified by
increasing the temperature of the fluidic droplet. For instance, a
rise in temperature may drive out a material from the fluidic
droplet (e.g., within an outer fluid droplet) and leave behind
another material that forms a solid. For example, in embodiments
illustrated in FIG. 2, fluid 260 (and therefore, outer droplet 280)
may contain a polymer suspended in a liquid (e.g., a hydrophobic
liquid). The liquid within fluid 260 may be removed from outer
droplet 280 by heating the droplet, leaving behind a solidified
polymeric shell surrounding droplet 285 (containing inner droplet
fluid 250).
[0057] Thus, an outer droplet may be solidified to form a solid
shell that encapsulates one or more fluids and/or agents, for
example, for delivery to a target medium, as described elsewhere
herein. For example, in FIG. 2, a particle similar to the particle
described in FIGS. 1A-1D, described in detail below, may be formed
by hardened droplet 280 and fluid 250. Such particles can be used
to deliver the agent within fluid 250 to a target medium, as
described elsewhere herein.
[0058] In some embodiments, it may be desirable to control the
temperature at which the multiple emulsion droplet is dried. For
example, in some such embodiments in which shells are formed by
drying a multiple emulsion, controlling the drying temperature can
ensure that the shell is configured so that it does not rupture
during the drying process. In some embodiments, the multiple
emulsion may be dried at a temperature of between about 25.degree.
C. and about 100.degree. C., between about 40.degree. C. and about
80.degree. C., between about 50.degree. C. and about 70.degree. C.,
or between about 55.degree. C. and about 65.degree. C. In some
embodiments, the multiple emulsion may be washed prior to drying
(or after, in some cases) using a variety of suitable solvents
including, but not limited to toluene and water. For example, in
one set of embodiments, after particles are formed, the carrying
fluid containing the particles may be removed and/or replaced with
a vehicle (e.g., for delivery to a target medium), which may or may
not be the same as the carrying fluid.
[0059] It should be noted that FIG. 2 and the related description
is only exemplary, and other multiple emulsions (e.g., having
differing numbers of droplets, nesting levels, etc.), and other
systems are also contemplated within various embodiments of the
instant invention. For example, the device in FIG. 2 may be
configured to include other flow arrangements and/or additional
concentric tubes, for example, to produce more highly nested
droplets. By supplying fourth, fifth, sixth, etc. fluids,
increasingly complex droplets within droplets can be produced in
certain embodiments. Some of these fluids may be the same, in
certain embodiments of the invention (e.g., the first fluid may
have the same composition as the third fluid, the second fluid may
have the same composition as the fourth fluid, etc.).
[0060] As an example, FIG. 3 includes an exemplary schematic
illustration of system 300 in which triple emulsions are formed. In
FIG. 3, system 300 includes outer conduit 310, a first inner
conduit (or injection tube) 320, and a second inner conduit (or
collection tube) 330. First inner conduit 320 includes an exit
opening 325 that opens into the outer conduit 310, and second inner
conduit 330 includes an entrance opening 335 that opens within the
outer conduit 310.
[0061] As shown in FIG. 3, inner fluid 350 flows through conduit
320 and out of exit opening 325 into conduit 310, in a left to
right direction. In addition, fluid 360 is illustrated flowing
through conduit 310 in a left to right direction, outside inner
fluid 350 and conduit 320. Near entrance opening 335 of conduit
330, fluid 360 surrounds fluid 350 to form the first nesting of the
triple emulsion. Fluid 370 is illustrated entering conduit 310 from
the right side and flowing in a right to left direction. Upon
contacting fluid 360, fluid 370 reverses direction, and surrounds
fluids 350 and 360 near entrance opening 335 of conduit 330 to form
the second nesting of the triple emulsion. Fluid 380 is illustrated
entering conduit 310 from the right side and flowing in a right to
left direction. Fluids 370 and 380 are arranged such that fluid 370
forms the sheath and fluid 380 forms the core of a core-sheath flow
arrangement. Upon reaching entrance opening 335 of conduit 330,
fluid 380 changes direction and surrounds fluids 350, 360, and 370
to form the third nesting of the triple emulsion.
[0062] FIG. 4 includes an exemplary schematic illustration of
system 400 in which quadruple emulsions are formed. The arrangement
of conduits in FIG. 4 is similar to the arrangement in FIG. 3,
including outer conduit 410, a first inner conduit (or injection
tube) 420, and a second inner conduit (or collection tube) 430.
First inner conduit 420 includes an exit opening 425 that opens
into the outer conduit 410, and second inner conduit 430 includes
an entrance opening 435 that opens within the outer conduit
410.
[0063] As shown in FIG. 4, inner fluid 450 flows through conduit
420 and out of exit opening 425 into conduit 410, in a left to
right direction. In addition, fluid 460 is illustrated flowing
through conduit 410 in a left to right direction, outside inner
fluid 450 and conduit 420. Fluid 465 is illustrated flowing through
conduit 410 in a left to right direction while surrounding fluid
460. Fluid 470 is illustrated entering conduit 410 from the right
side and flowing in a right to left direction. Upon contacting
fluid 465, fluid 470 reverses direction, and flows toward entrance
opening 435 of conduit 430. Fluid 480 is illustrated entering
conduit 410 from the right side and flowing in a right to left
direction. Fluids 470 and 480 are arranged such that fluid 470
forms the sheath and fluid 480 forms the core of a core-sheath flow
arrangement. Upon reaching entrance opening 435 of conduit 430,
fluid 480 changes direction. Near entrance opening 435 of conduit
430, fluid 460 surrounds fluid 450 to form the first nesting; fluid
465 surrounds fluids 450 and 460 to form the second nesting; fluid
470 surrounds fluids 450, 460, and 465; and fluid 480 surrounds
fluids 450, 460, 465, and 570 to form the fourth nesting of the
quadruple emulsion.
[0064] The multiple emulsions including more than two nestings
(e.g., triple emulsions, quadruple emulsions, etc.) can have any of
the properties described elsewhere herein with respect to double
emulsions. For example, the flow rates of the fluids can be
controlled such that each nesting includes a single droplet. In
such embodiments, the multiple emulsion comprises a core fluid
surrounded by multiple layers of multiple outer fluids. Each
droplet within such multiple emulsions may have any of the
properties (e.g., thicknesses, variations in thickness (or lack
thereof), cross-sectional diameter, etc.) described elsewhere
herein. For example, in the embodiments illustrated in FIG. 4, any
of the shells formed by fluids 460, 465, and 470 within the
quadruple emulsions may have any of the thicknesses and/or
variations in thicknesses described elsewhere herein. As another
example, the quadruple emulsions formed in FIGS. 3 and 4 (or in
other embodiments comprising further nesting) may have any of the
cross-sectional diameters and/or distributions of cross-sectional
diameters described elsewhere herein.
[0065] While multiple emulsions containing a single droplet at each
nesting level have been described, it should be understood that the
invention is not so limited, and, in some embodiments, one or more
nesting levels contain more than one droplet. For example, in some
embodiments, the inner fluid forms a plurality of droplets within a
middle fluid, and the middle fluid is surrounded by a thin layer of
an outer fluid which is, in turn, surrounded by a carrying fluid.
Some such embodiments are illustrated in FIG. 13C. In some
embodiments, the outer fluid surrounds a middle fluid which
surrounds a plurality of outer fluids, each of which forms a thin
layer of fluid around a plurality of innermost fluids within a
carrying fluid. By controlling the relative flow rates of the
fluids used to form the multiple emulsion, a plurality of droplets
are formed within any nesting level of the multiple emulsion.
[0066] In some cases in which multiple droplets are present within
a given nesting level, for a given nesting level of a multiple
emulsion droplet, each of the fluidic droplets of that level may
contain substantially the same number of inner fluidic droplets
therein; for example, substantially all of the droplets may contain
substantially the same number of droplets therein. It should be
understood that, even if the droplets appear to be substantially
identical (in any portion of a multiple emulsion droplet), or to
contain substantially the same number of droplets therein, not all
of the droplets will necessarily be completely identical. In some
cases, there may be minor variations in the number and/or size of
droplets contained within a surrounding droplet. Thus, in some
cases, at least about 75%, at least about 80%, at least about 85%,
at least about 90%, at least about 92%, at least about 94%, at
least about 95%, at least about 96%, at least about 97%, at least
about 98%, or at least about 99% of a plurality of droplets may
each contain the same number of droplets therein.
[0067] The rate of production of multiple emulsion droplets may be
determined by the droplet formation frequency, which under many
conditions can vary between approximately 1 Hz and 5000 Hz. In some
cases, the rate of droplet production may be at least about 1 Hz,
at least about 10 Hz, at least about 100 Hz, at least about 200 Hz,
at least about 300 Hz, at least about 500 Hz, at least about 750
Hz, at least about 1,000 Hz, at least about 2,000 Hz, at least
about 3,000 Hz, at least about 4,000 Hz, or at least about 5,000
Hz.
[0068] Production of large quantities of emulsions may be
facilitated by the parallel use of multiple devices such as those
described herein, in some instances. In some cases, relatively
large numbers of devices may be used in parallel, for example at
least about 10 devices, at least about 30 devices, at least about
50 devices, at least about 75 devices, at least about 100 devices,
at least about 200 devices, at least about 300 devices, at least
about 500 devices, at least about 750 devices, or at least about
1,000 devices or more may be operated in parallel. The devices may
comprise different conduits (e.g., concentric conduits), openings,
microfluidics, etc. In some cases, an array of such devices may be
formed by stacking the devices horizontally and/or vertically. The
devices may be commonly controlled, or separately controlled, and
can be provided with common or separate sources of various fluids,
depending on the application.
[0069] The systems and methods described herein can be used in a
plurality of applications. For example, fields in which the
particles and multiple emulsions described herein may be useful
include, but are not limited to, food, beverage, health and beauty
aids, paints and coatings, chemical separations, and drugs and drug
delivery. For instance, a precise quantity of a fluid, drug,
pharmaceutical, or other agent can be contained by a shell designed
to release its contents under particular conditions. In some
instances, cells can be contained within a droplet, and the cells
can be stored and/or delivered, e.g., to a target medium, for
example, within a subject. Other agents that can be contained
within a particle and delivered to a target medium include, for
example, biochemical species such as nucleic acids such as siRNA,
RNAi and DNA, proteins, peptides, or enzymes. Additional agents
that can be contained within an emulsion include, but are not
limited to, colloidal particles, magnetic particles, nanoparticles,
quantum dots, fragrances, proteins, indicators, dyes, fluorescent
species, chemicals, or the like. The target medium may be any
suitable medium, for example, water, saline, an aqueous medium, a
hydrophobic medium, or the like.
[0070] In one particular set of embodiments, particles comprising
thin shells can be formed using the multiple emulsion techniques
described herein. In some embodiments, as a non-limiting
illustrative example, one or more particles can be used to deliver
a fluid and/or an agent to a target medium, such as a hydrocarbon,
crude oil, petroleum, or other medium. In some cases, at least some
of the particles may comprise a solid portion or shell at least
partially containing an interior containing a fluid and/or an
agent. The shells of the particles can comprise a polymer, and in
some cases, substantially all of the polymer within the shells is
at least partially soluble in the target medium. The carrying fluid
in which the particles are formed may be used as a vehicle used to
contact the particles with a target medium, and/or the carrying
fluid may be substituted by a suitable vehicle, as discussed
elsewhere herein. When the particles contact the target medium, at
least a portion of the shells of the particles can be disrupted,
for instance, such that at least some of the fluid and/or agent
within the particles is expelled or otherwise transported from the
particles and into the target medium. Of course, it should be
understood that the particles may be used in other applications as
well, e.g., as discussed herein.
[0071] In some embodiments, the inventive particles are configured
to withstand relatively high absolute pressures.
[0072] FIGS. 1A-1D are exemplary schematic diagrams illustrating
use of a particle 100 to deliver a fluid 112 and/or an agent 114 to
a target medium 116 (e.g., a medium containing an oil, such as
crude oil, a hydrocarbon, etc.), in accordance with some
embodiments of the invention. Particle 100 may be, for example,
suspended in vehicle 105. In these figures, particle 100 includes
shell 110, which partially or fully surrounds a fluid 112. As shown
in this example, fluid 112 contains an agent 114, such as a
surfactant or other agent as is discussed herein, although in other
cases, there may be no agent present. In some embodiments, shell
110 may partially or fully surround any suitable material. The
material may be, for example, a solid or a semisolid, an agent,
etc. Also, in some cases, more than one material may be
present.
[0073] Shell 110 may comprise one or more polymers, such as
polystyrene, polycaprolactone, polyisoprene, poly(lactic acid), and
the like. Shell 110 can be formed, for example, by removing a
liquid from a suspension of droplets of polymers in an outer fluid,
leaving behind a solidified polymeric shell. Examples of this are
discussed below.
[0074] Vehicle 105 may comprise any suitable fluid configured for
delivering the particles 100 to the target medium 116. In some
embodiments (e.g., in cases where target medium 116 contains crude
oil and/or other hydrocarbons), vehicle 105 is hydrophilic (e.g.,
an aqueous vehicle).
[0075] In some embodiments, when the particles 100 contained within
vehicle 105 are exposed to a medium 116 (e.g., a medium containing
oil) such that the shell contacts the medium (for example medium
116 in FIG. 1A), at least a portion of the shell 100 is disrupted.
For example, the polymer within the shell 110 may be configured to
be at least partially soluble in an oil (e.g., in crude oil) such
that, when the shell 110 contacts a medium 116 containing the oil,
at least a portion of the shell 110 dissolves in the medium 116,
thereby causing a disruption in the shell 110. The polymer may also
be configured so that it is at least partially soluble in a
hydrocarbon, etc., as discussed herein, instead of (or in addition
to) an oil such as crude oil. In some cases, a hole may form (and
grow in some cases), or the shell 110 may crack, fragment, become
distorted, etc. as a result of the disruption. In some embodiments,
the fluid 112 and/or agent 114 contained by the shell 110 can be at
least partially exposed to the medium 116 containing the oil, for
example, as a result of this disruption in the shell 110.
[0076] FIGS. 1B-1D include schematic illustrations showing an
exemplary process by which a shell 110 of a particle 100 is
disrupted, leading the particle 100 to release a fluid 112 and/or
an agent 114 contained therein. However, it should be understood
that this discussion is by way of example only, and is not intended
to be a limiting description of the disruption of a shell 110. In
FIG. 1B, shell 110 of particle 100, contained within vehicle 105,
is in contact with medium 116. Upon contacting medium 116, portion
118 of shell 110 dissolves, as illustrated in FIG. 1C. In some
embodiments, after portion 118 dissolves, some or all of fluid 112
and/or agent 114 is transported out of shell 110 to be exposed to
medium 116, as illustrated in FIG. 1D. Transport may be, for
example, by convection, diffusion, osmosis, electrical drift, etc.
In some embodiments, the shell 110 shrinks as its contents (e.g.,
fluid 112 and/or agent 114) are released. For example, shell 110 in
FIG. 1D is depicted as smaller than shell 110 in FIG. 1C to
represent such shrinkage of the shell 110. In addition, the
contents (e.g., fluid 112 and/or agent 114) of the shell 100 may be
directionally released into a medium 116 in certain embodiments.
For example, in FIG. 1D, fluid 112 and/or agent 114 are shown as
having been released from shell 110 in the direction of arrow
120.
[0077] In some embodiments, some or all of the polymer within the
shell is configured to be at least partially soluble in the target
medium (e.g., a medium containing crude oil, a hydrocarbon,
petroleum, an oil, etc.). As used herein, a material is configured
to be "soluble" in a liquid medium when the material is exposed to
a liquid medium at 25.degree. C. and 1 atm, where the liquid medium
has a mass of at least 100 times the mass of the material, and the
material enters the liquid medium such that, at equilibrium, all of
the material is contained within the liquid medium and no portion
of the material forms a separate, macroscopic phase (e.g., as a
precipitated solid or a phase-separated fluid). It should be
understood that "solubility," as used herein, does not necessarily
require that the soluble material be dissolved within the medium at
a molecular level, for example, a finely-dispersed suspension, a
dispersion, an emulsion, etc. may be formed at equilibrium in some
cases. In addition, a material is configured to be "partially
soluble" when some, but not all, of the material is soluble within
the liquid medium using the screening test discussed above. In
certain cases, one or more of the polymers within the shell may be
configured to be at least partially soluble in a chemical
"indicative" of the target medium in certain cases, for instance,
where the target medium is one that is not readily compositionally
defined. For example, in some embodiments, one or more polymers
within the shell may be configured to be at least partially soluble
in octane, which may be used as a chemical indicative of crude
oil.
[0078] In some embodiments, the shell may comprise one or more
materials that are configured to not be soluble in hydrophilic
fluids such as water, an alcohol, etc. The materials may, in some
embodiments, include one or more polymers such as those described
herein. The use of such shell materials in a particle allows, in
some embodiments, for delivery of fluids and/or agents contained
within the particle to a medium that the particle comes in contact
with, for example, hydrocarbons, petroleum, an oil, etc.
[0079] In an example, a plurality of particles comprising
water-insoluble shells and containing a surfactant (or any other
suitable fluid and/or agent such as those described herein) are
suspended in water, or another suitable vehicle. In this example,
the suspension of particles in water is transported to or otherwise
brought into contact with a region or location containing, or at
least suspected of containing, oil, such as an oil well, a
subterranean oil reservoir, a container of oil (e.g., a vial or a
barrel), a chemical plant, a refinery, etc. In this example, prior
to contacting the oil, the water-insoluble shells of the particles
are configured to remain substantially intact, ensuring that the
surfactant remains contained within the particles. In some
embodiments, once the shells of the particles contact the target
medium, the shell is disrupted, e.g., at least partially dissolving
within the medium, thereby exposing at least some of the surfactant
to the medium.
[0080] As noted above, the shell may comprise a polymer in some
embodiments. Exemplary polymers suitable for use in shells include,
but are not limited to, polystyrene (PS), polycaprolactone (PCL),
polyisoprene (PIP), poly(lactic acid), polyethylene, polypropylene,
polyacrylonitrile, polyimide, polyamide, and/or mixtures and/or
co-polymers of these and/or other polymers.
[0081] In some embodiments, the polymer may include a relatively
linear polymer. Generally, linear polymers dissolve more quickly
than highly cross-linked polymers, and are therefore be
particularly useful in many applications. In some embodiments, the
linear polymers are not substantially crosslinked (i.e., the
polymers include linear chains of carbon atoms that do not include
chemical bonding to other chains, although pendant groups may be
present). It should be understood that, while the linear polymers
may not be cross-linked, the linear polymers may be physically
entangled with one another.
[0082] All or part of the shell of a particle may comprise a
polymer that has a relatively high glass transition temperature
(T.sub.g), in some embodiments. Polymers with high glass transition
temperatures are more resistant to rupture or disruption at high
temperatures and/or pressures, which can make their use desirable
for certain high temperature applications, such as some enhanced
oil recovery processes. However, in other applications, polymers
with lower glass transition temperatures may also be used. In some
embodiments, substantially all of the polymer within the shell has
a glass transition temperature of at least about 85.degree. C., at
least about 100.degree. C., between about 85.degree. C. and about
250.degree. C., or between about 85.degree. C. and about
200.degree. C. One of ordinary skill in the art would be capable of
determining the glass transition temperature of a polymer used in a
shell by, for example, using differential scanning calorimetry
(DSC). Generally, DSC defines the glass transition temperature as
the temperature at which the polymer matrix goes from the glass
state to the rubber state. Generally, polymers with relatively long
chain lengths have relatively smaller chain mobility and relatively
higher strength, toughness, and glass transition temperatures.
Exemplary polymers with relatively high glass transition
temperatures include, but are not limited to, polystyrene (PS),
polycaprolactone (PCL), and polyisoprene (PIP), and/or mixtures
and/or co-polymers of these and/or other polymers.
[0083] The molecular weight of the polymeric material used in the
shell of the particle can also be selected to impart desirable
physical properties, in accordance with some embodiments of the
invention. For example, in certain embodiments in which relatively
quick disruption of the shell of the particle is desired upon
contact with the target medium, polymers with low weight-averaged
molecular weights (e.g., less than about 20,000 g/mol) can be
employed. In some embodiments in which it is desirable to rupture
the shell relatively slowly, polymers with relatively high
weight-averaged molecular weights (e.g., greater than about 20,000
g/mol, e.g., between about 20,000 g/mol and about 800,000 g/mol)
can be employed.
[0084] In some embodiments, the shell of the particle is configured
to withstand the application of relatively high pressures without
rupturing. Mechanically robust shells may be produced by
fabricating the shell from a mechanically resistant material, such
as polystyrene, polycaprolactone, polyisoprene, and/or other
mechanically resistant polymer or other material. In some
embodiments, one or more particles (e.g., after drying) may be
subjected to an absolute pressure of at least about 200 kPa, at
least about 500 kPa, at least about 750 kPa, between about 100 kPa
and about 1000 kPa, or between about 200 kPa and about 750 kPa (for
example, in embodiments where the particles are suspended in water
or another vehicle that is pressurized for delivery to a
subterranean oil reservoir) without rupturing. In some embodiments,
including some embodiments in which high pressure resistance is
desired, the materials used in the shell are relatively elastic.
For example, in some embodiments, the Young's modulus of the
polymeric material used in the shell may be at least about 1 MPa,
at least about 10 MPa, at least about 100 MPa, or at least about 1
GPa. In some embodiments, the Young's modulus of the polymeric
material used in the shell may be less than about 10 GPa, less than
about 5 GPa, or less than about 3 GPa.
[0085] The particles may be configured to be able to deliver a
variety of agents. The agents may be fluid or solid, and/or the
agent may be contained within a fluid (e.g., dissolved, suspended,
etc.) In some embodiments, for example, the agent may include one
or more surfactants. The surfactants can be delivered, for example,
to a medium containing oil, or other medium as discussed herein.
When the surfactant is delivered to a medium containing oil, for
instance, the surfactant stabilizes the oil-water interface, which
prevents the oil from forming a fine emulsion in the water, thus
making the oil easier to separate from the water. A variety of
surfactants may be contained within the particles. In some
embodiments, for example, the particles may contain an ionic (e.g.,
cationic or anionic) surfactant. Exemplary anionic surfactants
suitable for use include, but are not limited to, sodium dodecyl
sulfate (SDS), ammonium lauryl sulfate, sodium lauryl sulfate,
sodium laureth sulfate, dioctyl sodium sulfosuccinate,
perfluorooctanesulfonate (PFOS), perfluorobutanesulfonate, alkyl
aryl ether phosphate, alkyl ether phosphate, alkyl carboxylates,
fatty acid salts (soaps), sodium stearate, sodium lauroyl
sarcosinate, carboxylate fluorosurfactants, perfluorononanoate,
perfluorooctanoate (PFOA or PFO), or the like. Exemplary cationic
surfactants suitable for use include, but are not limited to, cetyl
trimethylammonium bromide (CTAB), hexadecyl trimethyl ammonium
bromide, cetyl trimethylammonium chloride (CTAC),
cetylpyridiniumchloride (CPC), polyethoxylated tallow amine (POEA),
benzalkonium chloride (BAC), benzethonium chloride (BZT), or the
like. In some embodiments, non-ionic surfactants are used,
including, but not limited to: sorbitan monooleate (also referred
to as Span 80); Poly(ethylene glycol)-block-poly(propylene
glycol)-block-poly(ethylene glycol), Poly(propylene
glycol)-block-poly(ethylene glycol)-block-poly(propylene glycol)
(also referred to as F 108); polyvinyl alcohol (PVA); cetyl
alcohol, stearyl alcohol; cetostearyl alcohol (e.g., consisting
predominantly of cetyl and stearyl alcohols); oleyl alcohol;
polyoxyethylene glycol alkyl ethers (Brij); octaethylene glycol
monododecyl ether; pentaethylene glycol monododecyl ether;
polyoxypropylene glycol alkyl ethers; glucoside alkyl ethers; decyl
glucoside; lauryl glucoside; octyl glucoside; polyoxyethylene
glycol octylphenol ethers; triton X-100; polyoxyethylene glycol
alkylphenol ethers; nonoxynol-9; glycerol alkyl esters; glyceryl
laurate; polyoxyethylene glycol sorbitan alkyl esters;
polysorbates; sorbitan alkyl esters; cocamide MEA; cocamide DEA;
dodecyldimethylamine oxide; block copolymers of polyethylene glycol
and polypropylene glycol; Poloxamers; or the like.
[0086] In some embodiments, the use of ionic surfactants is
advantageous because the shells may be more stable, for example in
applications where the particles are suspended in a saline
environment (e.g., sea water) or other suitable vehicle. Not
wishing to be bound by any particular theory, it is believed that
the use of ionic surfactants in saline provides an osmotic balance
between the fluid (or other contents) inside the shell, and the
fluid outside the shell, and this osmotic balance helps to
stabilize the shell.
[0087] The particles may be suspended in any suitable vehicle
(e.g., vehicle 105 in FIGS. 1A-1D). In some embodiments, the
vehicle in which the particles are suspended is hydrophilic. In an
example, vehicle 105 comprises seawater, which may be used, for
example, to deliver particles to crude oil or other hydrocarbons
that have been released into a sea and/or that lie within an oil
reservoir beneath the surface of a sea. Examples of suitable
hydrophilic vehicles include, but are not limited to, water,
alcohols (e.g., butanol (e.g., n-butanol), isopropanol (IPA),
propanol (e.g., n-propanol), ethanol, methanol, glycerin, or the
like), saline solutions, blood, acids (e.g., formic acid, acetic
acid, or the like), amines (e.g., dimethyl amine, diethyl amine, or
the like), mixtures of these, and/or other similar fluids. In some
embodiments, polar protic solvents (e.g., alcohols, acids, bases,
etc.) can be used in the hydrophilic vehicle. In some embodiments,
polar aprotic solvents can be used in the hydrophilic vehicle,
including, for example, dimethyl sulfoxide (DMSO), acetonitrile
(MeCN), dimethylformamide (DMF), acetone, or the like. It should be
understood that the invention is not limited to hydrophilic
vehicles, and, in other embodiments, hydrophobic vehicles could be
used.
[0088] The particles described herein may have any suitable average
cross-sectional diameter. Those of ordinary skill in the art will
be able to determine the average cross-sectional diameter of a
single particle and/or a plurality of particles, for example, using
laser light scattering, microscopic examination, or other known
techniques. The average cross-sectional diameter of a single
particle, in a non-spherical particle, is the diameter of a perfect
sphere having the same volume as the non-spherical particle. The
average cross-sectional diameter of a particle (and/or of a
plurality or series of particles) may be, for example, less than
about 1 mm, less than about 500 micrometers, less than about 200
micrometers, less than about 100 micrometers, less than about 75
micrometers, less than about 50 micrometers, less than about 25
micrometers, less than about 10 micrometers, or less than about 5
micrometers, or between about 50 micrometers and about 1 mm,
between about 10 micrometers and about 500 micrometers, or between
about 50 micrometers and about 100 micrometers in some cases. The
average cross-sectional diameter may also be at least about 1
micrometer, at least about 2 micrometers, at least about 3
micrometers, at least about 5 micrometers, at least about 10
micrometers, at least about 15 micrometers, or at least about 20
micrometers in certain cases. In some embodiments, at least about
50%, at least about 75%, at least about 90%, at least about 95%, or
at least about 99% of the particles within a plurality of particles
has an average cross-sectional diameter within any of the ranges
outlined in this paragraph.
[0089] In some embodiments, the shell of the particle(s) are
relatively thin. The use of thin shells can provide a number of
advantages. For example, thin shells can dissolve relatively
quickly in some cases. In some embodiments, this may allow a
particle to deliver its contents prior to being transported away
from the target medium. Another advantage of using particles with
thin shells is that, during the process by which the outer liquid
of a fluidic droplet is dried to form the shell of a particle,
where the outer liquid contains a polymer that solidifies to form
the shell, removal of the liquid can be performed relatively easily
without rupturing the shell that is formed, at least according to
certain embodiments. In some embodiments, when relatively thick
shells are employed, the shells tend to rupture when the liquid in
which the polymer is suspended is removed. Not wishing to be bound
by any particular theory, it is believed that, when relatively
thick shells are employed (e.g., shells with thicknesses greater
than about 10 micrometers), the outermost portion of the shell
dries more quickly than the innermost portion of the shell,
producing a stress that can rupture or otherwise disrupt the shell.
Without wishing to be bound by any theory, it is believed that
using a middle phase with a very thin thickness allows the middle
phase to act as a lubricant such that the fluids are within a
lubrication regime. In this regime, the drag force on the innermost
fluid is significantly increased. The increase in drag force is
believed to enhance the stability of thin shell fluid. For example,
the migration velocity of a 98-micrometer diameter inner droplet
surrounded by a 100 micrometer shell is 100,000 times lower than
the migration velocity of a 50-micrometer diameter inner droplet
surrounded by a 100 micrometer shell.
[0090] In some embodiments, the shell of a particle has an average
thickness (averaged over the entire particle) of less than about
0.05, less than about 0.01, less than about 0.005, or less than
about 0.001 times the average cross-sectional diameter of the
particle, or between about 0.0005 and about 0.05, between about
0.0005 and about 0.01, between about 0.0005 and about 0.005, or
between about 0.0005 and about 0.001 times the average
cross-sectional diameter of the particle. In some embodiments, the
shell of a particle has an average thickness of less than about 1
micron, less than about 500 nm, or less than about 100 nm, or
between about 50 nm and about 1 micron, between about 50 nm and
about 500 nm, or between about 50 nm and about 100 nm. In some
embodiments, at least about 50%, at least about 75%, at least about
90%, at least about 95%, or at least about 99% of the particles
within a plurality of particles includes a shell having an average
thickness within any of the ranges outlined in this paragraph. One
of ordinary skill in the art would be capable of determining the
average thickness of a shell by, for example, examining scanning
electron microscope (SEM) images of the particles.
[0091] For many applications, it may be desirable to deliver a
plurality of particles, at least some of which contain a fluid
and/or an agent such as a surfactant, to a target medium. In order
to ensure predictable agent delivery, some embodiments
advantageously employ particles with relatively consistent
properties. For example, in some embodiments, a plurality of
particles are provided wherein the distribution of shell
thicknesses among the plurality of particles is relatively uniform.
The use of particles with relatively uniform shell thicknesses can
ensure, in some cases, consistent shell dissolution times, making
agent delivery more predictable. In some embodiments, a plurality
of particles are provided having an overall average shell
thickness, measured as the average of the average shell thicknesses
of each of the plurality of particles. In some cases, the
distribution of the average shell thicknesses can be such that no
more than about 5%, no more than about 2%, or no more than about 1%
of the particles have a shell with an average shell thickness
thinner than 90% (or thinner than 95%, or thinner than 99%) of the
overall average shell thickness and/or thicker than 110% (or
thicker than 105%, or thicker than about 101%) of the overall
average shell thickness.
[0092] The plurality of particles may have relatively uniform
cross-sectional diameters in certain embodiments. The use of
particles with relatively uniform cross-sectional diameters can
allow one to control the viscosity of the particle suspension, the
amount of agent delivered to the target medium, and/or other
parameters of the delivery of fluid and/or agent from the
particles. In some embodiments, the plurality of particles has an
overall average diameter and a distribution of diameters such that
no more than about 5%, no more than about 2%, or no more than about
1% of the particles have a diameter less than about 90% (or less
than about 95%, or less than about 99%) and/or greater than about
110% (or greater than about 105%, or greater than about 101%) of
the overall average diameter of the plurality of particles.
[0093] In some embodiments, the plurality of particles has an
overall average diameter and a distribution of diameters such that
the coefficient of variation of the cross-sectional diameters of
the particles is less than about 10%, less than about 5%, less than
about 2%, between about 1% and about 10%, between about 1% and
about 5%, or between about 1% and about 2%. The coefficient of
variation can be determined by those of ordinary skill in the art,
and may be defined as:
c v = .sigma. .mu. [ 1 ] ##EQU00001##
wherein .sigma. is the standard deviation and .mu. is the mean.
[0094] As used herein, two fluids are immiscible, or not miscible,
with each other when one is not soluble in the other to a level of
at least 10% by weight at the temperature and under the conditions
at which the emulsion is produced. For instance, two fluids may be
selected to be immiscible within the time frame of the formation of
the fluidic droplets. In some embodiments, two fluids (e.g., the
carrying fluid and the inner droplet fluid of a multiple emulsion)
are compatible, or miscible, while the outer droplet fluid is
incompatible or immiscible with one or both of the carrying and
inner droplet fluids. In other embodiments, however, all three (or
more) fluids may be mutually immiscible, and in certain cases, all
of the fluids do not all necessarily have to be water soluble. In
still other embodiments, as mentioned, additional fourth, fifth,
sixth, etc. fluids may be added to produce increasingly complex
droplets within droplets, e.g., a carrying fluid may surround a
first fluid, which may in turn surround a second fluid, which may
in turn surround a third fluid, which in turn surround a fourth
fluid, etc. In addition, the physical properties of each nesting
layer of fluidic droplets may each be independently controlled,
e.g., by control over the composition of each nesting level.
[0095] As used herein, the term "fluid" generally refers to a
substance that tends to flow and to conform to the outline of its
container, i.e., a liquid, a gas, a viscoelastic fluid, etc.
Typically, fluids are materials that are unable to withstand a
static shear stress, and when a shear stress is applied, the fluid
experiences a continuing and permanent distortion. The fluid may
have any suitable viscosity that permits flow. If two or more
fluids are present, each fluid may be independently selected among
essentially any fluids (liquids, gases, and the like) by those of
ordinary skill in the art, by considering the relationship between
the fluids.
[0096] In an aspect of the present invention, as discussed,
multiple emulsions are formed by flowing fluids through one or more
conduits. The system may be a microfluidic system. "Microfluidic,"
as used herein, refers to a device, apparatus, or system including
at least one fluid channel having a cross-sectional dimension of
less than about 1 millimeter (mm), and in some cases, a ratio of
length to largest cross-sectional dimension of at least 3:1. One or
more conduits of the system may be a capillary tube. In some cases,
multiple conduits are provided, and in some embodiments, at least
some are nested, as described herein. The conduits may be in the
microfluidic size range and may have, for example, average inner
diameters, or portions having an inner diameter, of less than about
1 millimeter, less than about 300 micrometers, less than about 100
micrometers, less than about 30 micrometers, less than about 10
micrometers, less than about 3 micrometers, or less than about 1
micrometer, thereby providing droplets having comparable average
diameters. One or more of the conduits may (but not necessarily),
in cross-section, have a height that is substantially the same as a
width at the same point. A conduit may include an opening that may
be smaller, larger, or the same size as the average diameter of the
conduit. For example, conduit openings may have diameters of less
than about 1 mm, less than about 500 micrometers, less than about
300 micrometers, less than about 200 micrometers, less than about
100 micrometers, less than about 50 micrometers, less than about 30
micrometers, less than about 20 micrometers, less than about 10
micrometers, less than about 3 micrometers, etc. In cross-section,
the conduits may be rectangular or substantially non-rectangular,
such as circular or elliptical. The conduits of the present
invention may also be disposed in or nested in another conduit, and
multiple nestings are possible in some cases. In some embodiments,
one conduit may be concentrically retained in another conduit and
the two conduits are considered to be concentric. However, one
concentric conduit may be positioned off-center with respect to
another, surrounding conduit, i.e., "concentric" does not
necessarily refer to tubes that are strictly coaxial. By using a
concentric or nesting geometry, two fluids that are miscible may
avoid contact.
[0097] In some embodiments, fluids, conduits (including conduit
walls), and other materials may be referred to as hydrophobic or
hydrophilic. A material is "hydrophobic" when a droplet of water
forms a contact angle greater than 90.degree. when placed in
intimate contact with the material in question in air at 1 atm and
25.degree. C. A material is "hydrophilic" when a droplet of water
forms a contact angle of less than 90.degree. when placed in
intimate contact with the material in question in air at 1 atm and
25.degree. C. The "contact angle," in the context of hydrophobicity
and hydrophilicity is the angle measured between the surface of the
material and a line tangent to the external surface of the water
droplet at the point of contact with the material surface, and is
measured through the water droplet. FIG. 5 is a schematic
illustration of the contact angle 591 formed by a water droplet 592
on a hydrophilic material 593 in air 597. As shown in FIG. 5,
contact angle 591 is measured from surface 594 of material 593
through droplet 592 and to a line 595 tangent to the external
surface of droplet 592 at the point of contact 596 between droplet
592 and material surface 594.
[0098] A variety of materials and methods, according to certain
aspects of the invention, may be used to form systems (such as
those described above) configured to produce the multiple emulsions
and/or particles described herein. In some cases, the various
materials selected lend themselves to various methods. For example,
various components of the invention are configured from solid
materials, in which the conduits are configured via micromachining,
film deposition processes such as spin coating and chemical vapor
deposition, laser fabrication, photolithographic techniques,
etching methods including wet chemical or plasma processes, and the
like. See, for example, Scientific American, 248:44-55, 1983
(Angell, et al). In one embodiment, at least a portion of the
fluidic system is formed of silicon by etching features in a
silicon chip. Technologies for precise and efficient fabrication of
various fluidic systems and devices of the invention from silicon
are known. In another embodiment, various components of the systems
and devices of the invention are configured of a polymer, for
example, an elastomeric polymer such as polydimethylsiloxane
("PDMS"), polytetrafluoroethylene ("PTFE" or Teflon.RTM.), or the
like.
[0099] Different components can be fabricated of different
materials. For example, a base portion including a bottom wall and
side walls can be fabricated from an opaque material such as
silicon or PDMS, and a top portion can be fabricated from a
transparent or at least partially transparent material, such as
glass or a transparent polymer, for observation and/or control of
the fluidic process. Components can be coated so as to expose a
desired chemical functionality to fluids that contact interior
conduit walls, where the base supporting material does not have a
precise, desired functionality. For example, components can be
fabricated as illustrated, with interior conduit walls coated with
another material. Material used to fabricate various components of
the systems and devices of the invention, e.g., materials used to
coat interior walls of fluid conduits, may desirably be selected
from among those materials that will not adversely affect or be
affected by fluid flowing through the fluidic system, e.g.,
material(s) that is chemically inert in the presence of fluids to
be used within the device. A non-limiting example of such a coating
is disclosed below; additional examples are disclosed in Int. Pat.
Apl. Ser. No. PCT/US2009/000850, filed Feb. 11, 2009, entitled
"Surfaces, Including Microfluidic Channels, With Controlled Wetting
Properties," by Weitz, et al., published as WO 2009/120254 on Oct.
1, 2009, incorporated herein by reference.
[0100] In some embodiments, various components of the invention are
fabricated from polymeric and/or flexible and/or elastomeric
materials, and can be conveniently formed of a hardenable fluid,
facilitating fabrication via molding (e.g. replica molding,
injection molding, cast molding, etc.). The hardenable fluid may be
essentially any fluid that can be induced to solidify, or that
spontaneously solidifies, into a solid capable of containing and/or
transporting fluids contemplated for use in and with the fluidic
network. In some embodiments, the hardenable fluid comprises a
polymeric liquid or a liquid polymeric precursor (i.e. a
"prepolymer"). Suitable polymeric liquids include, for example,
thermoplastic polymers, thermoset polymers, or mixture of such
polymers heated above their melting point. As another example, a
suitable polymeric liquid may include a solution of one or more
polymers in a suitable solvent, which solution forms a solid
polymeric material upon removal of the solvent, for example, by
evaporation. Such polymeric materials, which can be solidified
from, for example, a melt state or by solvent evaporation, are well
known to those of ordinary skill in the art. A variety of polymeric
materials, many of which are elastomeric, are suitable, and are
also suitable for forming molds or mold masters, for embodiments
where one or both of the mold masters is composed of an elastomeric
material. A non-limiting list of examples of such polymers includes
polymers of the general classes of silicone polymers, epoxy
polymers, and acrylate polymers. Epoxy polymers are characterized
by the presence of a three-membered cyclic ether group commonly
referred to as an epoxy group, 1,2-epoxide, or oxirane. For
example, diglycidyl ethers of bisphenol A can be used, in addition
to compounds based on aromatic amine, triazine, and cycloaliphatic
backbones. Another example includes the well-known Novolac
polymers. Non-limiting examples of silicone elastomers suitable for
use according to the invention include those formed from precursors
including the chlorosilanes such as methylchlorosilanes,
ethylchlorosilanes, phenylchlorosilanes, etc.
[0101] Silicone polymers are utilized in some embodiments, for
example, the silicone elastomer polydimethylsiloxane. Non-limiting
examples of PDMS polymers include those sold under the trademark
Sylgard by Dow Chemical Co., Midland, Mich., and particularly
Sylgard 182, Sylgard 184, and Sylgard 186. Silicone polymers
including PDMS have several beneficial properties simplifying
fabrication of the microfluidic structures of the invention. For
instance, such materials are inexpensive, readily available, and
can be solidified from a prepolymeric liquid via curing with heat.
For example, PDMSs are typically curable by exposure of the
prepolymeric liquid to temperatures of about, for example, about
65.degree. C. to about 75.degree. C. for exposure times of, for
example, about an hour. Also, silicone polymers, such as PDMS, can
be elastomeric, and thus may be useful for forming very small
features with relatively high aspect ratios, necessary in certain
embodiments of the invention. Flexible (e.g., elastomeric) molds or
masters can be advantageous in this regard.
[0102] An advantage of forming structures such as microfluidic
structures of the invention from silicone polymers, such as PDMS,
is the ability of such polymers to be oxidized, for example by
exposure to an oxygen-containing plasma such as an air plasma, so
that the oxidized structures contain, at their surface, chemical
groups capable of cross-linking to other oxidized silicone polymer
surfaces or to the oxidized surfaces of a variety of other
polymeric and non-polymeric materials. Thus, components can be
fabricated and then oxidized and essentially irreversibly sealed to
other silicone polymer surfaces, or to the surfaces of other
substrates reactive with the oxidized silicone polymer surfaces,
without the need for separate adhesives or other sealing means. In
most cases, sealing can be completed simply by contacting an
oxidized silicone surface to another surface without the need to
apply auxiliary pressure to form the seal. That is, the
pre-oxidized silicone surface acts as a contact adhesive against
suitable mating surfaces. Specifically, in addition to being
irreversibly sealable to itself, oxidized silicone such as oxidized
PDMS can also be sealed irreversibly to a range of oxidized
materials other than itself including, for example, glass, silicon,
silicon oxide, quartz, silicon nitride, polyethylene, polystyrene,
glassy carbon, and epoxy polymers, which have been oxidized in a
similar fashion to the PDMS surface (for example, via exposure to
an oxygen-containing plasma). Oxidation and sealing methods useful
in the context of the present invention, as well as overall molding
techniques, are described in the art, for example, in an article
entitled "Rapid Prototyping of Microfluidic Systems and
Polydimethylsiloxane," Anal. Chem., 70:474-480, 1998 (Duffy et
al.), incorporated herein by reference.
[0103] In some embodiments, certain microfluidic structures of the
invention (or interior, fluid-contacting surfaces) may be formed
from certain oxidized silicone polymers. Such surfaces may be more
hydrophilic than the surface of an elastomeric polymer. Such
hydrophilic conduit surfaces can thus be more easily filled and
wetted with aqueous solutions.
[0104] In some embodiments, a bottom wall of a microfluidic device
of the invention is formed of a material different from one or more
side walls or a top wall, or other components. For example, in some
embodiments, the interior surface of a bottom wall comprises the
surface of a silicon wafer or microchip, or other substrate. Other
components may, as described above, be sealed to such alternative
substrates. Where it is desired to seal a component comprising a
silicone polymer (e.g. PDMS) to a substrate (bottom wall) of
different material, the substrate may be selected from the group of
materials to which oxidized silicone polymer is able to
irreversibly seal (e.g., glass, silicon, silicon oxide, quartz,
silicon nitride, polyethylene, polystyrene, epoxy polymers, and
glassy carbon surfaces which have been oxidized). Alternatively,
other sealing techniques may be used, as would be apparent to those
of ordinary skill in the art, including, but not limited to, the
use of separate adhesives, bonding, solvent bonding, ultrasonic
welding, etc.
[0105] The following documents are incorporated herein by reference
in their entirety for all purposes: International Patent
Publication Number WO 2004/091763, filed Apr. 9, 2004, entitled
"Formation and Control of Fluidic Species," by Link et al.;
International Patent Publication Number WO 2004/002627, filed Jun.
3, 2003, entitled "Method and Apparatus for Fluid Dispersion," by
Stone et al.; International Patent Publication Number WO
2006/096571, filed Mar. 3, 2006, entitled "Method and Apparatus for
Forming Multiple Emulsions," by Weitz et al.; International Patent
Publication Number WO 2005/021151, filed Aug. 27, 2004, entitled
"Electronic Control of Fluidic Species," by Link et al.;
International Patent Publication Number WO 2008/121342, filed Mar.
28, 2008, entitled "Emulsions and Techniques for Formation," by Chu
et al.; International Patent Publication Number WO 2010/104604,
filed Mar. 12, 2010, entitled "Method for the Controlled Creation
of Emulsions, Including Multiple Emulsions," by Weitz et al.;
International Patent Publication Number WO 2011/028760, filed Sep.
1, 2010, entitled "Multiple Emulsions Created Using Junctions," by
Weitz et al.; International Patent Publication Number WO
2011/028764, filed Sep. 1, 2010, entitled "Multiple Emulsions
Created Using Jetting and Other Techniques," by Weitz et al; and a
U.S. Provisional patent application, filed on Jul. 6, 2011,
entitled "Delivery to Hydrocarbons or Oil, Including Crude Oil," by
Abbaspourrad et al. Also incorporated herein by reference in their
entireties are U.S. Provisional Patent Application Ser. No.
61/505,001, filed Jul. 6, 2011, entitled "Delivery to Hydrocarbons
or Oil, Including Crude Oil," by Abbaspourrad, et al., and of U.S.
Provisional Patent Application Ser. No. 61/504,990, filed Jul. 6,
2011, entitled "Multiple Emulsions and Techniques for the Formation
of Multiple Emulsions," by Kim, et al.
[0106] All other patents, patent applications, and documents cited
herein are also hereby incorporated by reference in their entirety
for all purposes.
[0107] The following examples are intended to illustrate certain
embodiments of the present invention, but do not exemplify the full
scope of the invention.
Example 1
[0108] This example describes an approach to making relatively
monodisperse double emulsion droplets including a thin middle layer
of fluid, using microfluidic techniques. Two immiscible streams
confined in a microfluidic channel can form a stable jet or
droplets under certain physical conditions, and the streams can be
emulsified together to form double emulsion droplets, as discussed
herein. The resultant double emulsion droplets have a thin outer
layer which can enhance the stability of the double emulsion. The
systems and methods described in this example can be applied to any
viscous organic solvent, and in some embodiments, can facilitate
the making of particles having a shell containing material, with a
small amount of shell material. In addition, the systems and
methods described in this example can produce double emulsions, or
higher-order multiple emulsions, in a single step, at least in some
cases. Relatively monodisperse particles with a shell thicknesses
of less than 100 nm may be formed in some instances by evaporation
of an outer phase (such as toluene) to leave behind a polymer (such
as poly(lactic acid)) that solidifies to form the shell.
[0109] Two immiscible fluids flowing through a single microfluidic
channel can show different distinct flow patterns of droplets and
jets, depending upon several physical parameters. The fluid with
the higher affinity to the walls of the microfluidic channel may
form a continuous phase, while the fluid with the lower affinity
may flow in the form of droplets or jets without contacting the
walls of the channel. In many instances, the flow may produce a jet
that is unstable due to Rayleigh-Plateau instability, which results
in the breakup of the jet into separate droplets; however, spatial
confinement of the interface may be used to produce a more stable
jet. When the interface is formed proximate to a channel wall, the
instability may be reduced in some cases.
[0110] In some experiments in this example, double emulsion
droplets were produced through emulsification of a stable biphasic
jet into a continuous phase. To make water-in-oil-in-water (W/O/W)
double emulsion droplets, microfluidic devices were employed. FIG.
6A includes a schematic illustration of a microfluidic device used
for the preparation of double emulsion droplets. The microfluidic
devices used here included a hydrophobic tapered injection channel
610 inserted in a second square channel 612 whose inner dimension
was slightly larger than that of an outer diameter of injection
channel 610 as depicted in FIG. 6A. By using a square channel with
an inner diameter slightly larger than the outer diameter of the
injection channel, the two channels fit snugly, which can allow for
easier channel alignment of the tubes in the system. (Although a
square channel was used here, channels having other shapes may also
be used.) To flow two immiscible fluids ("oil" phase 602 and
"water" phase 604) into the single injection channel, channel 614
was inserted into injection channel 610. In addition, a collection
tube 616 was inserted into the square channel to confine the flow
near the injection tip, thereby increasing the flow velocity and to
collect droplets that are produced from injection channel 610. To
produce W/O/W double emulsion droplets, n-octadecyltrimethoxyl
silane (Aldrich) was coated on the injection capillary wall to
render it hydrophobic, and
2-[methoxy(polyethyleneoxy)propyl]trimethoxyl silane (Gelest, Inc.)
was coated onto the collection capillary wall to render it
hydrophophilic.)
[0111] In these experiments, 25 wt % aqueous solution of
poly(ethylene glycol) (PEG, MW 6000) and hexadecane ("oil" phase
602) with 1 wt % SPAN 80 was passed through the injection channel
to form a dispersed phase of droplets, and 10 wt % aqueous solution
of poly(vinyl alcohol) (PVA, MW 13,000-23,000) ("water" phase 606)
was passed through channel 612 to form a continuous phase. It
should be noted that the "oil" phase is used here to conveniently
refer to a phase that is not substantially miscible in water or the
"aqueous" phase (which is miscible in water). The "oil" phase
should not be construed as being limited only to oils, and may
include any fluid that is not substantially miscible in water.
[0112] Depending on the inner diameter of the injection channel
that was used in the microfluidic device, different resulting flow
patterns were observed. For example, in an injection channel with
an inner diameter of 580 micrometers, a variety of water droplet
formations for a wide range of flow rates were observed. As a
specific non-limiting example, when the ratio of the volumetric
flow rate of the inner fluid stream to the volumetric flow rate of
the outer fluid was set at 4:1, a "train" of plug-like or elongated
droplets was observed, as shown in the optical microscope image in
FIG. 6B; these droplets were emulsified into a cocurrent continuous
fluid stream, flowing along the outer surface of the injection
capillary in the same direction with the inner and outer fluid
streams. When the plug-like droplets passed through the opening at
the end of the channel, relatively monodisperse double emulsion
droplets having relatively thin outer layers were generated, while
large oil (hexadecane) blobs were generated for oil flow between
water droplets. The discontinuous generation of double emulsion
droplets is shown in the optical microscope image in FIG. 6C.
[0113] As another non-limiting example, when an injection channel
with an inner diameter of 200 micrometers was used, a stable water
jet was formed under these particular conditions, as shown in the
optical microscope image in FIG. 6D. This jet was emulsified at or
near the opening of the collection tube in a continuous manner,
resulting in monodisperse double emulsion droplets. The use of a
channel with a smaller inner diameter provided higher confinement
of the interface under these conditions, thereby reducing
perturbations and producing a stable jet. As seen in FIGS. 6C and
6E, the thickness of the outer layer of the resultant double
emulsion droplet was too thin to accurately measure with an optical
microscope.
[0114] The flow rates of the entering streams influenced the flow
pattern in the injection channel and thus, the generation of double
emulsion droplets. FIG. 7A shows a plot of the flow behavior in the
system as a function of the flow rates of the inner or "core"
stream (fluid 604 in FIG. 6A) and the outer or "cladding" stream
(fluid 602 in FIG. 6A), indicating various flow regimes observed at
different flow rates of each, including regimes in which a stable
jet and/or dropets are produced and in which unstable flow occurs
and droplets are not produced. For example, when the flow rate of
the inner stream was sufficiently high relative to a given flow
rate of the outer stream, a stable water jet (circles) was formed
in the injection channel, as shown in the top optical microscope
image of FIG. 7B. In contrast, when the flow rate of the inner
stream decreased, the jet became unstable and showed fluctuations
of the interface without breakup (triangles), as shown in the
middle optical microscope image of FIG. 7B. A further reduction of
the flow rate of the inner stream yielded plug-like water droplets
(crosses), as shown in the bottom optical microscope image of FIG.
7B.
[0115] Although a high flow rate of the inner stream could produce
a stable jet, a double emulsion was not always generated from the
jet. High inertia of the inner stream at a high flow rate can cause
leakage of the inner stream into the continuous phase near the tip
of the injection channel, which corresponds to region (a) in FIG.
7A. Setting the flow rate of the inner stream to a value within
region (b) allows double emulsion droplets to be generated in both
jetting and dripping modes. For example, for an inner stream flow
rate of about 1200 microliters/hour, the biphasic jet passed
through the opening at the end of the collection channel and
subsequently broke up into double emulsion droplets at the end of
the jet, well inside the collection channel, as shown in the
optical microscope image in FIG. 7C. By contrast, the biphasic jet
was emulsified near the opening of the collection channel in the
dripping mode for an inner stream flow rate of 800 microliters/hour
in this particular device, as shown in the optical microscope image
in FIG. 7D. When the flow rate of the inner stream was set to 400
microliters/hour (or any other flow rate within region (d) of FIG.
7A), discontinuous generation of double emulsion droplets was
observed, as shown in the optical microscope image in FIG. 7E. For
all of the experiments illustrated in FIGS. 7C-7E the flow rate of
the cladding stream was maintained at 100 microliters/hour.
[0116] O/W/O double emulsion droplets may be prepared in a similar
manner. To produce O/W/O double emulsion droplets,
2-[methoxy(polyethyleneoxy)propyl]trimethoxyl silane (Gelest, Inc.)
was coated onto the injection capillary wall to render it
hydrophilic, and n-octadecyltrimethoxyl silane (Aldrich) was coated
onto the collection capillary wall to render it hydrophobic. Using
a microfluidic device with the same geometry but opposite surface
modifications, double emulsion droplets of silicone oil (AR 20)/1
wt % aqueous solution of F108/2 wt % silicone oil of DC749 were
prepared, as illustrated in FIGS. 8A-8C. FIG. 8A is a schematic
illustration of the microfluidic device used to prepare O/W/O
double emulsion droplets. FIGS. 8B-8C are optical microscope images
showing generation of O/W/O double emulsion droplets in the
dripping mode and the resultant monodisperse double emulsion
droplets.
[0117] When operating in the dripping mode, droplet generation
appeared to be governed by two competing forces: the capillary
force that holds the droplet to the end of the channel and the drag
force that pulls the droplet downstream. The size of double
emulsion droplets may be controlled, for example, by controlling
the flow rate of the continuous phase (which is proportional to the
drag force). FIG. 9A includes a plot of emulsion diameter as a
function of the rate of a continuous fluid flow in the outer
channel 612, Q.sub.3, and FIG. 9B shows optical microscope images
of relatively monodisperse double emulsion droplets prepared at the
denoted flow rates of the continuous phase. When the flow rate was
increased, the diameter of the double emulsion droplets decreased,
as shown in FIGS. 9A-9B. The resultant double emulsion droplets
were relatively monodisperse, and the diameter had a coefficient of
variation in range of 1.0-1.9%.
[0118] The thickness, t, of the outer layer of the double emulsion
droplets was difficult to accurately measure from optical
microscope images. However, the thicknesses of the outer layer
could also be estimated by comparing the radius of the double
emulsion droplet (R) to the radius of a single "oil" droplet
(R.sub.rup) prepared by rupturing the double emulsion droplet such
that the inner "water" phase is transported out of the "oil" shell
and into the continuous "water" phase, leaving behind an "oil"
droplet. The thickness of the "oil" shell prior to rupturing can be
calculated using the following mass balance equation, noting that
the volume of the initial "oil" shell (the left-hand side of
Equation 2) will be equivalent to the volume of the "oil" droplet
formed after rupturing the double emulsion (the right-hand side of
Equation 2):
4 .pi. R 3 3 - 4 .pi. ( R - t ) 3 3 = 4 .pi. R rup 3 3 [ 2 ]
##EQU00002##
Rearranging Equation 2 to calculate the shell thickness yields:
t=R-(R.sup.3-R.sub.rup.sup.3).sup.1/3 [3]
[0119] As an example, two optical microscope images are shown in
FIG. 9D, which exhibits rupturing of double emulsion droplets by
applying a mechanical force to the double emulsion suspension.
Specifically, the double emulsion droplets were ruptured by placing
a suspension of double emulsion droplets on the top of a glass
slide and tapping the glass slide on a solid surface, such as a
tabletop. Rupturing a double emulsion droplet resulted in a single
emulsion droplet (denoted with the dotted circle in FIG. 9D). The
radii observed in these two images were R=61 micrometers and
R.sub.rup=19 micrometers, resulting in a thickness of 620 nm.
[0120] In the same manner, using various double emulsion droplets
produced at various relative flow rates of inner stream 604
(Q.sub.1) to outer stream 602 (Q.sub.2), the thicknesses of the
outer layers of these double emulsion droplets were calculated (see
FIG. 9C). In FIG. 9C, the top curve shows the thicknesses of the
outer fluids of the double emulsion droplets prepared by the stable
jetting or dripping modes, while the two data points at the bottom
of the plot are from double emulsion droplets prepared using
discontinuous dripping. The top curve in FIG. 9C fitted to the data
is related to the mass balance equation. Specifically, Equations 4
and 5 below can be derived from mass conservation:
Q 1 = f 4 .pi. ( R - t ) 3 3 [ 4 ] Q 2 = f ( 4 .pi. R 3 3 - 4 .pi.
( R - t ) 3 3 ) [ 5 ] ##EQU00003##
where f is frequency of drop generation. By dividing Equation 5 by
Equation 4, and rearranging, the following equation can be
obtained:
1 R = 1 - ( 1 + Q 1 Q 2 ) - 1 3 [ 6 ] ##EQU00004##
[0121] By contrast, the discontinuous dripping mode produced double
emulsion droplets including outer fluid layers with very small
relative thicknesses, regardless of the flow rates. Not wishing to
be bound by any particular theory, this regime may have formed
consistently thin outer fluid layers because the amount of the oil
phase positioned between the plug-like water droplets and the inner
wall of the injection channel (which eventually formed the outer
layer of the double emulsion droplets) was very small. In fact, in
this flow regime, most of the injected oil was situated between the
plug-like water droplets, producing relatively large oil plugs
contained between the water droplets that eventually formed the
cores of the double-emulsion droplets. Because very little oil was
positioned adjacent the water droplets, little oil was available to
produce the outer layers, and the outer layers were very thin. Most
of the injected oil flow was between two neighboring water
droplets, forming large oil droplets at the exit opening rather
than double emulsion droplets. Although the discontinuous dripping
mode produced both relatively monodisperse double emulsion droplets
with a thin outer fluid layer, as well as large oil
(single-emulsion) droplets, separation of the double emulsion
droplets from the mixture was easily achieved by taking advantage
of the density difference between the double emulsion droplets and
the single emulsion droplets: the average density of the double
emulsion droplets was almost same as the density of the aqueous
inner fluid, while the density of the single emulsion oil droplets
was almost the same as the density of the oil solution surrounding
the droplets. Thus, the two types of droplets could readily be
separated based on their density differences.
[0122] Double emulsion droplets were used to make microcapsules by
removing fluid from the outer phase to produce a solid phase from
material that was originally contained within the fluid of the
outer phase. As a specific example, in some cases, a concentrated
organic solution of polymers with high molecular weights in water
was used as the outer phase. Double emulsion droplets containing a
relatively thin outer fluid layer were produced, and this
relatively thin outer fluid layer was solidified to form a shell
that provided stability to the resulting particles. These particles
could maintain their respective solidified shells around the
contained inner fluid without being disrupted for relatively long
times.
[0123] To illustrate some of the advantages discussed herein,
polymeric particles having a shell containing a fluid were
prepared, in which the shell was formed from poly(lactic acid)
(PLA, MW 15,000). To produce W/O/W double emulsion droplets, a 10
wt % aqueous solution of PVA containing a green dye,
8-hydroxyl-1,3,6-pyrenetrisulfonic acid, trisodium salt, was used
for the inner phase. 20 wt % of PLA in toluene containing a red
dye, nile red, was used for the outer phase. A 3 wt % aqueous
solution of PVA was employed for the carrying fluid. Approximately
1,000 double emulsion droplets were generated each second in the
dripping mode. The resultant droplets, illustrated in the optical
microscope images in FIGS. 10A-10B, were found to be relatively
monodisperse.
[0124] To remove toluene from the outer fluid layer, the suspension
was exposed to a temperature of 65.degree. C. for 2 hours. During
this process, the toluene diffused from the outer phase to the PVA
carrying fluid, from which the toluene was subsequently evaporated
at 65.degree. C. After the consolidation step, polymeric particles
were produced, as shown in the confocal microscope images of FIGS.
10C-10D. At the maximum magnification, the thickness of the shells
of the particles were observed to be smaller than 500 nm, as seen
in FIG. 10D. A scanning electron microscope (SEM) image of the
shell cross-section was also taken, showing that the thickness of
the shell was about 80 nm, as shown in the inset of FIG. 10D. This
was consistent with the confocal microscope images, especially
considering that the outer fluid layer may have shrunk
significantly during consolidation.
[0125] Higher-order multiple emulsion droplets were produced
through a single-step emulsification process using a stable coaxial
flow in a confining microfluidic channel. The device configuration
used for producing triple emulsion droplets of
water-in-oil-in-water-in-oil (W.sub.1/O.sub.2/W.sub.3/O.sub.4) is
illustrated schematically in FIG. 11A, including three
cross-sectional schematics taken along the A-A' plane, the B-B'
plane, and the C-C' plane. The device included a tapered injection
channel 702 and a collection channel 704 inserted in a third square
channel 706. A small tapered channel 708 was also inserted into the
space between the collection and square channel 706, as shown in
the cross-section taken along C-C' to flow two immiscible fluids at
the same time. An aqueous phase fluid 710 was passed through the
injection channel to form the inner cores, while an oil phase fluid
712 was passed through channel 706 around injection channel 702 to
form an outer layer of fluid for the resulting multiple emulsion
droplets.
[0126] In this example, inner surface of channel 706 has a
hydrophilic surface, while the outer surfaces of channels 702 and
704 (facing channel 706) are hydrophobic.
2-[methoxy(polyethyleneoxy)propyl]trimethoxyl silane (Gelest, Inc.)
was used to make the walls of channel 706 hydrophilic, while
n-octadecyltrimethoxyl silane (Aldrich) was used to make the walls
of channels 702 and 704 hydrophobic. To prepare triple emulsion
droplets, water was used for the innermost phase 710, hexadecane
with 1 wt % SPAN 80 surfactant was used for oil phase 712 (i.e.,
for the first, "oil" shell), an aqueous solution of 3 wt % poly
(vinyl alcohol) (PVA) and 1 wt % F108 surfactant was used for water
phase 714 (i.e., for the second, "water" shell), and hexadecane
with 1 wt % SPAN 80 was used as continuous phase 716. When both
water 714 and oil 716 were introduced from the right side of
channel 706, between collection channel 704 and channel 706, oil
passed along the outer surface of collection channel 704 with water
714 shielding oil 716, as shown in the cross-section of B-B'. In
this arrangement, the fluids formed coaxial interfaces in the
opening of collection channel 704, which facilitated the formation
of triple emulsion droplets in a single step emulsification
process.
[0127] For the preparation of triple emulsion droplets, water
(W.sub.1) and hexadecane with 1 wt % SPAN 80 surfactant (O.sub.2)
were passed through injection channel 702 and the channel between
injection channel 702 and channel 706, respectively, while both an
aqueous solution of 3 wt % poly(vinyl alcohol) (PVA) and 1 wt %
F108 surfactant (W.sub.3) and hexadecane with 1 wt % SPAN 80
(O.sub.4) were passed through the channel between collection
channel 704 and square channel 706. The aqueous (W.sub.3) and the
hexadecane surfactant solutions (O.sub.4) formed a coaxial
interface, and were passed into the opening of collection channel
704, together with the water (W.sub.1) and the hexadecane (O.sub.2)
from the left side. Using this arrangement, triple emulsion
droplets of W.sub.1/O.sub.2/W.sub.3/O.sub.4 were prepared in
collection channel 704. The triple emulsion droplets are displayed
in the optical microscope images of FIGS. 11B-11C. The white arrows
in FIG. 1B denote the aqueous stream for fluid layer W.sub.3. The
three phases of O.sub.2, W.sub.3, and O.sub.4 were passed through
the opening of collection channel 704 by forming two coaxial
interfaces of O.sub.2/W.sub.3 and W.sub.3/O.sub.4 while the inner
fluid water droplets (W.sub.1) (which were produced at the tip of
injection channel 702 in a dripping mode, at least in this example)
triggered the breakup of the coaxial interfaces to form the final
multiple emulsion droplets.
[0128] In this arrangement, the flow rate of the aqueous inner
phase (Q.sub.1) determined the sizes of the triple emulsion
droplets. FIG. 12A is a plot of the diameters of the inner
(D.sub.1), the middle (D.sub.2) and the outer fluid droplets
(D.sub.3) in a W/O/W/O triple emulsion droplets as a function of
the flow rate of the inner aqueous phase (Q.sub.1), where the flow
rates of the middle fluid (Q.sub.2), the outer fluid (Q.sub.3), and
the carrying oil fluid (Q.sub.4) phases were kept at 2 ml/h, 1
ml/h, and 3 ml/h, respectively. Triangles (.tangle-solidup.) and
upside down triangles () denote the calculated diameters D.sub.2
and D.sub.3 from mass balances. As the flow rate of the aqueous
inner phase Q.sub.1 was increased, the frequency by which inner
fluid droplets were generated increased without a significant
change of diameter (D.sub.1) under dripping conditions. In
addition, as Q.sub.1 increased, the frequency of breakup increased,
which resulted in the reduction of the diameter of the middle
droplets (D.sub.2) and the outer droplets (D.sub.3). Not wishing to
be bound by any particular theory, the slight increase of inner
droplet diameter D.sub.1 may be attributable to a change in the
position of the contact line of the aqueous inner stream on the tip
of the hydrophobic injection channel. Diameters D.sub.2 and D.sub.3
can be calculated using the following mass balance equations, which
describe core drop-triggered breakup:
D 2 = D 1 ( 1 + Q 2 Q 1 ) 1 / 3 and D 3 = D 1 ( 1 + Q 2 + Q 3 Q 1 )
1 / 3 [ 7 ] ##EQU00005##
where Q.sub.2 and Q.sub.3 are volumetric flow rates of O.sub.2 and
W.sub.3, respectively. The calculated diameter of D.sub.3 appeared
to be consistent with the experimentally measured diameters.
[0129] FIG. 12B shows optical microscope images of the downstream
emulsions at Q.sub.1 values of 50 microliters/hour (top), 200
microliters/hour, 800 microliters/hour, and 2600 microliters/hour
(bottom). Optical microscope images of the monodisperse triple
emulsion droplets produced at two different values of Q.sub.1 (0.2
ml/h and 1.6 ml/h) are displayed in FIGS. 12C and 12D,
respectively.
[0130] For larger values of Q.sub.2, the droplet breakup mechanism
changed from core drop-triggering to jetting. The coaxial
interfaces formed a long jet, and plug-like droplets containing any
desirable number of core droplets could be produced, as illustrated
in the optical microscope image of FIG. 13A. FIG. 13B is a plot of
the number of inner fluid droplets formed in the emulsion as a
function of the volumetric flow rate of the inner fluid stream
(Q.sub.1). As shown in FIG. 13B, the number of inner fluid droplets
may be controlled by adjusting Q.sub.1, which determined the
relative frequency of inner droplet generation and interface
breakup. In FIG. 13B, the flow rates of the middle oil (Q.sub.2),
the outer aqueous (Q.sub.3), and the carrying oil (Q.sub.4) phases
were kept at 4.0 ml/h, 1.4 ml/h, and 3.0 ml/h, respectively. FIG.
13C shows optical microscope images showing the triple emulsion
droplets containing various numbers of core droplets, as denoted in
each respective microscope image.
[0131] Substantially monodisperse quadruple emulsion droplets were
also prepared using a single-step emulsification process. The
device used to produce quadruple emulsion droplets was similar to
the device used to produce triple emulsion droplets, and is
illustrated schematically in FIG. 14A (including cross-sectional
schematic illustrations along planes A-A', B-B', C-C', and D-D').
Two biphasic streams from both the left and right sides of channel
806 formed three coaxial interfaces. Quadruple emulsion droplets
were made by breaking up the interfaces triggered by core droplets.
For W.sub.1/O.sub.2/W.sub.3/O.sub.4/W.sub.5 quadruple emulsion
droplets, injection channel 802 and portion 804 of the square
channel 806 on the opposite side of the injection channel were
treated to be hydrophobic, and the collection channel 808 and the
remaining part 810 of square channel are treated to be hydrophilic,
using techniques similar to those described above. To modify the
inner wall of square channel 806 into two distinct regions, two
square channels were treated with different silane coupling agents
and then connected together to form a single channel. The gap
between the two channels was sealed by an epoxy resin to form a
single channel. The breakup of the three concentric interfaces of
O.sub.2/W.sub.3, W.sub.3/O.sub.4, and O.sub.4/W.sub.5 was triggered
by the injection of inner fluid droplets, resulting in
substantially monodisperse quadruple emulsion droplets as shown in
the optical microscope images of FIGS. 14B-14D. The breakup
occurred sequentially from the inner interfaces to the outer
interfaces.
[0132] Inverse quadruple emulsion droplets with an O/W/O/W/O
arrangement were also produced using a device with the same
geometry as the device used to produce W/O/W/O/W emulsions, but
with the opposite chemical modifications, as illustrated
schematically in FIG. 15A (including cross-sectional schematic
illustrations along planes A-A', B-B', C-C', and D-D'). FIGS.
15B-15D include optical microscope images showing the resultant
quadruple emulsions.
Example 2
[0133] This example describes the use of certain microfluidic
techniques to make polymer particles comprising shells with
nano-scale thicknesses. The polymer shell was designed such that it
remained solid during transit and liquefied upon contact with a
suitable target medium, such as hydrocarbons or oil (e.g., any
aromatic or short chain hydrocarbon oil, or other oil as discussed
herein), locally transporting a fluid and/or an agent contained
within the particle to the oil (or other target medium). Release of
the contents of the particles was triggered when the solid polymer
shell was exposed to the oil, after which the shell became
disrupted. For example, at least a portion of the shell may liquefy
and/or behave like a viscoelastic fluid, exposing the fluid and/or
agent within the particle to the target medium. The liquefied shell
of the particle may shrink rapidly in some embodiments, expelling
or otherwise transporting the fluid and/or agent out of the
particle, into the oil. Not wishing to be bound by any particular
theory, it is believed that the shell of the particle shrinks in
some cases in order to decrease the interfacial area and/or the
surface energy of the particle. The time required for the particle
to expose the agent and/or fluid to the target medium (e.g., by
expelling the fluid and/or agent from the particle) may be tuned,
for instance, by varying the molecular weight of the polymer. This
may also be adjusted depending on the composition of the oil or
other target medium. This method of triggered release may be used
for a variety of different applications, for example, for reservoir
applications such as enhanced oil recovery (EOR), or other
applications such as those described herein.
[0134] A double emulsion template using microfluidic devices
(generally described in Example 1) was used to contain one or more
agents within shells having thicknesses ranging from, e.g., about
100 nm to about 1 micrometer. The microfluidic devices allowed for
the control of particle properties, for example, mechanical
stability, release, and/or loading efficiencies in various
embodiments. The microfluidic devices also allowed for easy
fabrication, e.g., for the production of particles having desirable
properties and/or for tailoring the properties of the particles for
use in various applications.
[0135] In this example, the carrying fluid was prepared by
dissolving 10 g PVA (MW=13000-23000, Aldrich) in 90 mL of water.
The outer fluid was formed using a solution of 8 wt % linear
polystyrene (MW=20000-800000, Aldrich) and 0.01 g of Nile Red
(fluorescent dye, Sigma) dissolved in toluene. The inner or core
fluid was prepared by dissolving 1 g of PVA (MW=13000-23000,
Aldrich) in 9 mL of water. To visualize the core via confocal
microscopy, 0.05 g Dex-FITC (Polysciences) was added to the inner
fluid solution. All fluids were pumped into the microfluidic device
using syringe pumps (Harvard PHD 2000 series). Flow rates for the
continuous, middle and the core fluids were set at 300, 500, and
20,000 microliters/h, respectively. In FIG. 16, as an example, the
confocal microscope image shows a polystyrene (PS) shell
encapsulating a labeled surfactant, 10 wt % PVA.
[0136] The outer fluid was solidified to form shells by evaporating
the solvent (toluene) inside the outer fluid away from the droplets
using a heat treatment process (65.degree. C. for 2 hours) to form
a shell comprising the solid linear polymer.
[0137] The ability to produce thin particle shells offers several
advantages. For example, the thin shell was found to be robust, and
could contain a wide range of materials without failing
mechanically, while the shell was still able to be disrupted upon
contact with even small concentrations or amounts of oils or
hydrocarbons (or other suitable target medium).
[0138] In this example, the microfluidic fabrication process was
monitored using an inverted optical microscope (DM-IRB, Leica) fit
with a fast camera (Phantom V9, Vision Research). Confocal images
of the particles were obtained using a scanning confocal microscope
(Leica TCS-SP5).
Example 3
[0139] This example describes the production of particles
comprising thin polymeric shells that were configured to
controllably release their contents. In this example, the carrying
fluid was prepared by dissolving 10 g PVA (weight-averaged
MW=52500-23000; Aldrich) in 90 mL of water. The outer fluid was
formed using a solution of 8 wt % linear polystyrene
(MW=20,000-800,000, Aldrich) and 0.01 g of Nile Red (fluorescent
dye, Sigma) dissolved in toluene. The inner or core fluid was
prepared by dispersing 0.1 g of fluorescently labeled magnetic poly
styrene particles (Polyscience, size=1 micrometers) in 5 mL of
water. All fluids were pumped into the microfluidic device using
syringe pumps (Harvard PHD 2000 series). Flow rates for the core,
middle, and continuous fluids were set at 650, 400 and 12,000
microliters/h, respectively.
[0140] FIG. 17A illustrates the microfluidic production of a
particle having a thin PS shell containing smaller magnetic
nanoparticles as an example agent. The particles having the thin PS
shells were produced at the opening of an injection channel inside
the collection channel. The microfluidic system was similar to the
ones discussed above. The confocal microscope image in FIG. 17B
shows a particle containing fluorescently labeled PS nanoparticles
contained within an unlabeled PS shell. The PS nanoparticles were
found to be confined to the PS container, as discussed below,
confirming a high encapsulation efficiency.
[0141] Controlled release of fluids or agents contained within the
particles may be achieved by first contacting the shells of the
particles with an oil, after which, in some cases, the shell
absorbs the oil and becomes more fluid or otherwise disrupted. This
solid to fluid-like transition created a shell defect, which
initiated shell collapse and subsequent release of agent contained
within the shell. FIGS. 18A-18C include three confocal microscope
images illustrating the controlled release mechanism. In FIGS.
18A-18C, the shells of various particles containing a divinyl
benzene/polystyrene (DVB-PS) shell viscoelastically transformed
from solid to liquid. The period of time over which this transition
occurred varied depended on the oil composition. As the shell of
the particle absorbed the oil, the solid shell became more like a
liquid-like viscoelastic material. During contact with oil, a small
amount of the shell dissolved in the oil, producing a defect in the
shell. In FIG. 18A, the particle forced the nanoparticles contained
within the particle out through the defect of the shell into the
surrounding oil. The nanoparticles were pushed out of the
collapsing particle while the particle decreased in size. Expelling
of nanoparticles proceeded through the shell defect until
substantially all of the nanoparticles were completely forced out
of the particle (FIGS. 18B and 18C).
[0142] In another set of experiments, additional particles were
formed that comprised a triblock copolymer (PS-PIP-PS) inside a
shell. These particles exhibited a similar release mechanism as the
one discussed above. The shells of these particles comprising the
PS-PIP-PS triblock copolymer were relatively flexible, which
allowed the particles to be passed through confined geometries
smaller than the particle diameter without disruption or release of
agents contained within the particles. FIGS. 19A-19B include
confocal microscope images of the PS-PIP-PS capsules (Diameter=150
micrometers) as they were squeezed through a confined glass
microfluidic channel (diameter=80 micrometers). FIG. 19C includes a
bright field image of the same process. The use of flexible shells
in the particles can allow the particles to retain their mechanical
integrity, e.g., while being manipulated, packed, passed through
confined channels, openings, etc.
[0143] FIG. 20 includes a schematic illustration showing how
particles may be used in an enhanced oil recovery (EOR) process,
according to certain embodiments of the invention. In FIG. 20,
particle 902 includes a shell 904 encapsulating a surfactant 906.
Particle 902 may be suspended in an aqueous vehicle 907 (e.g.,
water) and transported to a target medium 908 containing oil. Upon
encountering interface 910 between vehicle 907 and target medium
908, at least a part of shell 904 of particle 902 may absorb oil
and undergo a viscoelastic solid-to-liquid transition, which may
initiate shell 904 liquefaction to expose agents contained within
the particles to target medium 908. In some cases, the agent may be
locally released to the target medium, as illustrated in FIG.
20.
[0144] The polymer shell in these examples may be formed using a
variety of polymers including polystyrene (PS), polycaprolactone
(PCL), and/or a variety of other polymers. As an example, by
incorporating PCL in the shell of particle, controlled release of a
fluid and/or an agent contained within the particle may be made
dependent upon the pH of the environment, e.g., of the target
medium. The use of pH-dependent materials in the shell could also
be useful in applications such as targeted drug delivery. As an
example, targeted delivery of magnetic particles (useful, for
example, for identification of residual oil in place (ROIP) by NMR
sensing) may also be achieved. Examples of magnetic particles that
may be used include iron oxide, magnetite, hematite, other
compounds containing iron, or the like.
[0145] For all experiments in this example, the microfluidic
fabrication process was monitored using an inverted optical
microscope (DM-IRB, Leica) fit with a fast camera (Phantom V9,
Vision Research). Brightfield images of dried particles were taken
with an inverted optical microscope (DM-IRB, Leica) equipped with a
camera (Qlmaging QICAM). Confocal images of the particles were
obtained using a scanning confocal microscope (Leica TCS-SP5). SEM
(scanning electron microscopy) images were collected with a Zeiss
Ultra55 field emission microscope (FESEM) (field emission scanning
electron microscopy).
[0146] While several embodiments of the present invention have been
described and illustrated herein, those of ordinary skill in the
art will readily envision a variety of other means and/or
structures for performing the functions and/or obtaining the
results and/or one or more of the advantages described herein, and
each of such variations and/or modifications is deemed to be within
the scope of the present invention. More generally, those skilled
in the art will readily appreciate that all parameters, dimensions,
materials, and configurations described herein are meant to be
exemplary and that the actual parameters, dimensions, materials,
and/or configurations will depend upon the specific application or
applications for which the teachings of the present invention
is/are used. It is, therefore, to be understood that the foregoing
embodiments are presented by way of example only and that, within
the scope of the appended claims and equivalents thereto, the
invention may be practiced otherwise than as specifically described
and claimed. The present invention is directed to each individual
feature, system, article, material, kit, and/or method described
herein. In addition, any combination of two or more such features,
systems, articles, materials, kits, and/or methods, if such
features, systems, articles, materials, kits, and/or methods are
not mutually inconsistent, is included within the scope of the
present invention.
[0147] The indefinite articles "a" and "an," as used herein in the
specification and in the claims, unless clearly indicated to the
contrary, should be understood to mean "at least one."
[0148] The phrase "and/or," as used herein in the specification and
in the claims, should be understood to mean "either or both" of the
elements so conjoined, i.e., elements that are conjunctively
present in some cases and disjunctively present in other cases.
Other elements may optionally be present other than the elements
specifically identified by the "and/or" clause, whether related or
unrelated to those elements specifically identified unless clearly
indicated to the contrary. Thus, as a non-limiting example, a
reference to "A and/or B," when used in conjunction with open-ended
language such as "comprising" can refer, in one embodiment, to A
without B (optionally including elements other than B); in another
embodiment, to B without A (optionally including elements other
than A); in yet another embodiment, to both A and B (optionally
including other elements); etc.
[0149] As used herein in the specification and in the claims, "or"
should be understood to have the same meaning as "and/or" as
defined above. For example, when separating items in a list, "or"
or "and/or" shall be interpreted as being inclusive, i.e., the
inclusion of at least one, but also including more than one, of a
number or list of elements, and, optionally, additional unlisted
items. Only terms clearly indicated to the contrary, such as "only
one of" or "exactly one of," or, when used in the claims,
"consisting of," will refer to the inclusion of exactly one element
of a number or list of elements. In general, the term "or" as used
herein shall only be interpreted as indicating exclusive
alternatives (i.e. "one or the other but not both") when preceded
by terms of exclusivity, such as "either," "one of," "only one of,"
or "exactly one of." "Consisting essentially of," when used in the
claims, shall have its ordinary meaning as used in the field of
patent law.
[0150] As used herein in the specification and in the claims, the
phrase "at least one," in reference to a list of one or more
elements, should be understood to mean at least one element
selected from any one or more of the elements in the list of
elements, but not necessarily including at least one of each and
every element specifically listed within the list of elements and
not excluding any combinations of elements in the list of elements.
This definition also allows that elements may optionally be present
other than the elements specifically identified within the list of
elements to which the phrase "at least one" refers, whether related
or unrelated to those elements specifically identified. Thus, as a
non-limiting example, "at least one of A and B" (or, equivalently,
"at least one of A or B," or, equivalently "at least one of A
and/or B") can refer, in one embodiment, to at least one,
optionally including more than one, A, with no B present (and
optionally including elements other than B); in another embodiment,
to at least one, optionally including more than one, B, with no A
present (and optionally including elements other than A); in yet
another embodiment, to at least one, optionally including more than
one, A, and at least one, optionally including more than one, B
(and optionally including other elements); etc.
[0151] In the claims, as well as in the specification above, all
transitional phrases such as "comprising," "including," "carrying,"
"having," "containing," "involving," "holding," and the like are to
be understood to be open-ended, i.e., to mean including but not
limited to. Only the transitional phrases "consisting of" and
"consisting essentially of" shall be closed or semi-closed
transitional phrases, respectively, as set forth in the United
States Patent Office Manual of Patent Examining Procedures, Section
2111.03.
* * * * *