U.S. patent application number 14/175307 was filed with the patent office on 2014-06-05 for fabrication of an optical wedge.
This patent application is currently assigned to Microsoft Corporation. The applicant listed for this patent is Microsoft Corporation. Invention is credited to Rajesh Manohar Dighde, Kurt Allen Jenkins, Timothy Large.
Application Number | 20140153894 14/175307 |
Document ID | / |
Family ID | 44530624 |
Filed Date | 2014-06-05 |
United States Patent
Application |
20140153894 |
Kind Code |
A1 |
Jenkins; Kurt Allen ; et
al. |
June 5, 2014 |
FABRICATION OF AN OPTICAL WEDGE
Abstract
Various embodiments are disclosed relating to fabrication of an
optical wedge. For example, one embodiment provides a method for
manufacturing an optical wedge comprising inserting a wedge blank
into a vacuum molding tool and applying a vacuum to the vacuum
molding tool to temporarily hold the wedge blank against a molding
surface of the vacuum molding tool. The method further comprises
removing a layer from a top surface of the wedge blank to expose a
machined surface of the wedge blank, and casting a finish layer on
the machined surface to form a finish layer of a finished optical
wedge.
Inventors: |
Jenkins; Kurt Allen;
(Sammamish, WA) ; Large; Timothy; (Bellevue,
WA) ; Dighde; Rajesh Manohar; (Redmond, WA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Microsoft Corporation |
Redmond |
WA |
US |
|
|
Assignee: |
Microsoft Corporation
Redmond
WA
|
Family ID: |
44530624 |
Appl. No.: |
14/175307 |
Filed: |
February 7, 2014 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12779790 |
May 13, 2010 |
8673186 |
|
|
14175307 |
|
|
|
|
61309702 |
Mar 2, 2010 |
|
|
|
Current U.S.
Class: |
385/146 ;
425/174.4; 425/174.8E; 425/342.1 |
Current CPC
Class: |
B29D 11/00663 20130101;
B29C 59/002 20130101; G02B 6/10 20130101; B29D 11/00932
20130101 |
Class at
Publication: |
385/146 ;
425/174.8E; 425/174.4; 425/342.1 |
International
Class: |
B29D 11/00 20060101
B29D011/00; G02B 6/10 20060101 G02B006/10; B29C 59/00 20060101
B29C059/00 |
Claims
1. A vacuum molding system for forming an optical wedge from a
wedge blank, the vacuum molding system comprising: a vacuum pump; a
vacuum molding tool comprising one or more vacuum ports fluidly
connected to the vacuum pump, the vacuum molding tool including a
molding surface configured to temporarily shape a molded surface of
the wedge blank under the urging of a pressure differential
generated by the vacuum pump; and a casting plate configured to be
retained across a finish layer of the wedge blank opposite from the
molded surface of the wedge blank.
2. The vacuum molding system of claim 1, wherein the molding
surface comprises an optical surface profile to be imparted to the
molded surface of the wedge blank.
3. The vacuum molding system of claim 2, wherein the molding
surface of the vacuum molding tool includes one or more local
topographic characteristics each configured to impart a
complementary local topographic feature to the molded surface of
the wedge blank.
4. The vacuum molding system of claim 1, wherein the casting plate
comprises a float glass plate configured to impart a planar surface
to a diffuser interface surface of a finished optical wedge.
5. The vacuum molding system of claim 4, wherein the casting plate
comprises a surface roughness average of two nanometers or
less.
6. The vacuum molding system of claim 1, further comprising an
ionizer gun configured to control one or more electrostatic
potentials of the vacuum molding system.
7. The vacuum molding system of claim 1, further comprising a
precursor-curing energy source.
8. The vacuum molding system of claim 7, wherein the
precursor-curing energy source comprises an ultraviolet lamp.
9. The vacuum molding system of claim 1, further comprising a wedge
blank inserted in the vacuum molding tool, the wedge blank
comprising a smoother surface in contact with the molding surface
and a rougher surface opposite the molding surface.
10. The vacuum molding system of claim 1, further comprising a
finish layer applied over the wedge blank, wherein the casting
surface is in contact with the finish layer.
11. The vacuum molding system of claim 1, wherein the casting
surface comprises a mold release agent.
12. The vacuum molding tool of claim 1, wherein the casting plate
has a thickness of 20-25 mm.
13. An optical wedge, comprising: a wedge blank comprising a
surface having a non-planar shape; and a cured polymer disposed on
a surface of the wedge blank opposite the surface having the
non-planar shape, wherein the cured polymer comprises an index of
refraction of within +/-0.01 of an index of refraction of the wedge
blank, and wherein the cured polymer comprises a cast surface.
14. The optical wedge of claim 13, wherein the cast surface
comprises a surface roughness average of two nanometers or
less.
15. The optical wedge of claim 13, wherein the cast surface is
planar, and wherein the surface having the non-planar shape
comprises an aspheric optical feature.
16. The optical wedge of claim 13, wherein the cured polymer
comprises poly(methyl methacrylate).
17. A vacuum molding system for forming an optical wedge from a
wedge blank, the vacuum molding system comprising: a vacuum pump; a
vacuum molding tool comprising one or more vacuum ports fluidly
connected to the vacuum pump, the vacuum molding tool including a
molding surface configured to temporarily shape a molded surface of
the wedge blank under the urging of a pressure differential
generated by the vacuum pump, the molding surface defining an
aspheric optical feature; and a casting plate configured to be
retained across a finish layer of the wedge blank opposite from the
molded surface of the wedge blank.
18. The vacuum molding system of claim 17, wherein the casting
plate comprises a float glass plate.
19. The vacuum molding system of claim 17, wherein the casting
plate has a thickness of 20-25 mm.
20. The vacuum molding system of claim 18, further comprising an
ionizer gun.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application is a divisional of U.S. patent application
Ser. No. 12/779,790, filed on May 13, 2010, and titled "FABRICATION
OF AN OPTICAL WEDGE" which claims priority to U.S. Provisional
Application No. 61/309,702, filed Mar. 2, 2010. The above-listed
applications are hereby incorporated by reference in their
entireties for all purposes.
BACKGROUND
[0002] An optical wedge is a wedge-shaped light guide configured to
transmit light between a first light interface located at an end of
the light guide and a second light interface located at a major
face of the light guide via total internal reflection. Such guides
may be image-retaining where there is a one-to-one correspondence
between an angle of image light at the edge and a position of the
image light at a surface of the wedge. Thus, light input into the
first light interface within a suitable range of input angles
propagates through the optical wedge until the critical angle of
internal reflection is reached, thereby allowing the light to be
transmitted out of the optical wedge through the second interface.
Depending upon the design of a particular optical wedge, the first
light interface may be either at a thin end or a thick end of the
optical wedge. In either case, the internal reflection of light
within the optical wedge allows light to fan out to a desired beam
size within a relatively small volume of space, and therefore may
permit the construction of a relatively compact optical system
compared to a similar system without an optical wedge.
SUMMARY
[0003] Various embodiments are disclosed herein that relate to
fabrication of an optical wedge. For example, one embodiment
provides a method for manufacturing an optical wedge, the method
comprising inserting a wedge blank into a vacuum molding tool and
applying a vacuum to the vacuum molding tool to temporarily hold a
surface of the wedge blank against a surface of the vacuum molding
tool. The method further comprises removing a layer from a top
surface of the wedge blank to expose a machined surface of the
wedge blank, and casting a finish layer on the machined surface to
form a finished optical wedge.
[0004] This Summary is provided to introduce a selection of
concepts in a simplified form that are further described below in
the Detailed Description. This Summary is not intended to identify
key features or essential features of the claimed subject matter,
nor is it intended to be used to limit the scope of the claimed
subject matter. Furthermore, the claimed subject matter is not
limited to implementations that solve any or all disadvantages
noted in any part of this disclosure.
BRIEF DESCRIPTION OF THE DRAWINGS
[0005] FIG. 1 is a schematic cross-sectional view of an embodiment
of a vacuum molding tool, and of an embodiment of a wedge blank
positioned over the vacuum molding tool.
[0006] FIG. 2 is a flowchart depicting an embodiment of a method of
fabricating an optical wedge.
[0007] FIG. 3 is a schematic cross-sectional view of an embodiment
of the vacuum molding tool of FIG. 1 showing a wedge blank inserted
into the vacuum molding tool.
[0008] FIG. 4 is a schematic cross-sectional view of an embodiment
of the vacuum molding tool of FIG. 1 showing a machined surface of
the wedge blank being exposed.
[0009] FIG. 5 is a schematic cross-sectional view of an embodiment
of the vacuum molding tool of FIG. 1 showing a finish layer cast on
top of the machined surface of the wedge blank.
[0010] FIG. 6 is a schematic cross-sectional view of a finished
optical wedge produced by the vacuum molding tool embodiment of
FIG. 1.
[0011] FIG. 7 is an exaggerated schematic view of a thickness
profile of the finished optical wedge embodiment of FIG. 6.
DETAILED DESCRIPTION
[0012] As described above, surface smoothness and dimensional
accuracy may be goals in the fabrication of an optical wedge. In
some applications, a thickness tolerance of approximately 1% of the
maximum thickness of the wedge may be needed to achieve desired
optical performance. For example, surface ripples having a period
approaching a magnitude of a beam width of a projection device may
cause degradation in image focus, which may be magnified over the
course of multiple reflections from the rippled surface.
Accordingly, in some applications, surface roughness may be
controlled to 1 micron per 20 mm maximum gradient deviation.
[0013] However, manufacturing an optical wedge with such properties
may pose various challenges. For example, a PMMA (poly(methyl
methacrylate)) extruded optical wedge may have surface roughness on
the order of 10 nm RA arising from the extrusion aperture, which is
well above the <2 nm RA desired for some applications. An
optical wedge cast between two float glass sheets may have
acceptable smoothness. However, PMMA may shrink by approximately
12-24% during curing. Due to the non-uniform thickness of an
optical wedge, this shrinkage may result in poor thickness profile
tolerance, leading to loss of functionality.
[0014] Accordingly, various embodiments are provided herein that
relate to manufacturing an optical wedge in a manner that may help
to avoid such issues. It will be appreciated that the schematic
views presented herein are greatly exaggerated for illustrative
purposes. Further, it will be appreciated that the wedge profiles
presented in these exaggerated schematic views are merely example
wedge profiles, and that any suitable wedge profile may be achieved
within the scope of the present disclosure.
[0015] FIG. 1 is a schematic view of an embodiment of a vacuum
molding tool 102 for molding an optical wedge from a wedge blank
150, wherein wedge blank 150 is a starting material for molding an
optical wedge. Wedge blank 150 may be made from any suitable
material, including but not limited to an optical-grade material,
such as acrylic PMMA, polycarbonate, polystyrene, etc. For example,
in some embodiments, wedge blank 150 may be a cast acrylic sheet
formed by curing a monomer poured between two float glass forms
separated by a gasket. The resulting cast sheet may exhibit
approximately similar average surface roughness values as those of
the float glass forms, which in some embodiments may be 2 nm RA or
less. Thus, the surface of wedge blank 150, in some embodiments,
may have an average surface roughness of approximately 2 nm RA or
less, and in some embodiments, 1 nm RA or less.
[0016] Wedge blank 150 may have any suitable dimensions. For
example, in some non-limiting example embodiments, wedge blank 150
may have a pre-processing thickness of approximately 1 mm-20 mm.
Because some acrylic polymerization processes result in
approximately 12%-24% shrinkage of the acrylic material as the
polymerization reactions progress, it will be appreciated that a
thicker initial charge of monomer may be used in some embodiments
to achieve such a final thickness for wedge blank 150.
[0017] Vacuum molding tool 102 includes one or more vacuum ports
106 fluidly connected to a vacuum pump (not shown) and configured
to channel air and/or other gases from the vacuum molding tool 102
toward the vacuum pump. It will be appreciated that any suitable
vacuum pump may be employed within the scope of the present
disclosure. In some embodiments, vacuum molding tool 102 may be
mounted on a stabilized surface, such as an optical mount platform,
to provide a level surface for the molding and casting operations
described in more detail.
[0018] Vacuum molding tool 102 also includes a molding surface 104
configured to provide a form for shaping a molded surface of the
optical wedge into a desired profile. For example, in FIG. 1,
molding surface 104 exhibits an optical surface profile that
changes in thickness along a direction L running from end A of
vacuum molding tool 102 to an opposite end B. Ends A and B
correspond respectively to thick and thin edges of the resulting
optical wedge. Thus, the optical wedge fabricated in vacuum molding
tool 102 of FIG. 1 will exhibit an optical surface profile matching
the optical surface profile of molding surface 104. It will be
appreciated that the optical surface profile of molding surface 104
may have any suitable profile along a length and/or a width of
molding surface 104 to achieve optical and/or structural
characteristics for a particular end-use application, provided
sufficient atmospheric pressure to overcome a stress opposing
temporary formation of wedge blank 150 to the optical surface
profile of molding surface 104.
[0019] In some embodiments, molding surface 104 may include one or
more local topographic characteristics 108, each of which is
configured to impart a corresponding complementary topographic
feature to the finished optical wedge. For example, in the scenario
shown in FIG. 1, local topographic characteristic 108 is shown as a
thickness maximum configured to impart an aspherical optical
feature to the finished optical wedge. It will be appreciated that
molding surface 104 may be formed by any suitable process, such as
by machining with a milling tool such as a computer numeric
controlled (CNC) machine tool. Further, it will be appreciated that
molding surface 104 may be processed with any suitable surface
treatment, such as by electropolishing, chemical mechanical
polishing, etc. to provide a suitably smooth molding surface.
[0020] FIG. 2 is a flowchart showing an embodiment of a method 200
for operating a vacuum molding tool for fabricating an optical
wedge. It will be appreciated that method 200 may be performed by
any suitable vacuum molding tool for fabrication of an optical
wedge, and is not limited to the embodiments described herein.
[0021] Method 200 comprises, at 202, inserting a wedge blank into a
vacuum molding tool. For example, FIG. 3 shows a cross-sectional
view of wedge blank 150 inserted into vacuum molding tool 102.
Continuing, method 200 comprises, at 204, applying a vacuum to the
mold. In the example shown in FIG. 3, a vacuum has been applied to
vacuum molding tool 102 via vacuum ports 106. Application of the
vacuum causes wedge blank 150 to be pressed against molding surface
104, so that the optical surface profile of molding surface 104 is
imparted to molded surface 152 of wedge blank 150. Thus, in a
scenario where a cast acrylic blank is inserted into wedge molding
tool 102, the cast acrylic molding surface may be conformed to the
shape of the optical surface profile and yet retain the surface
smoothness native to the cast acrylic blank.
[0022] Continuing, method 200 comprises, at 206, removing a portion
of the top surface of the wedge blank while the vacuum molding tool
is still under vacuum. For example, FIG. 4 shows a cross-sectional
view of wedge blank 150 inserted into vacuum molding tool 102. Top
surface 404 of wedge blank 150 is being machined by milling machine
402 to produce machined surface 406. It will be appreciated that
any suitable machining process may be employed to form machined
surface 406. For example, in the scenario shown in FIG. 4, a CNC
milling machine equipped with a fly cutter bit may be used to
produce machined surface 406. As a result of the machining process,
the A end of the wedge blank is thicker than the B end. In some
embodiments, the top surface of the wedge blank may be machined
into a planar surface; in some other embodiments, the top surface
of the wedge blank may be machined into another suitable
topography. In some embodiments, as much as 50 percent of the wedge
blank may be removed by machining, while in other embodiments
either more or less material may be removed.
[0023] The machined surface of the wedge blank may have a surface
roughness greater than desired for some applications of the
finished optical wedge. Thus, method 200 comprises, at 208, casting
a finish layer in-situ on the machined surface of the wedge blank
while the vacuum molding tool is still under vacuum. For example,
FIG. 5 shows a cross-sectional view of machined surface 406 of
wedge blank 150, on which a finish layer 502 has been cast. Finish
layer 502 may be any suitable material having an index of
refraction sufficiently matched to the index of refraction of the
wedge blank material. For example, in some embodiments, the index
of refraction of the wedge blank material may be within +/-0.01 of
the index of refraction of the precursor material when cured. As a
more specific example, PMMA has a refractive index of 1.492. Thus,
a casting polymer for casting a finish layer onto a PMMA wedge
blank may have an index of refraction between 1.482 and 1.502. It
will be understood this specific example is described for the
purpose of illustration, and is not intended to be limiting in any
manner. In some embodiments, the indices of refraction may be
sufficiently matched so that the interface formed between finish
layer 502 and machined surface 406 will be invisible. For example,
in a scenario where wedge blank 150 is a cast PMMA acrylic blank,
finish layer 502 may be cast in-situ from PMMA, and will thus have
approximately the same index of refraction (n approximately 1.5) as
wedge blank 150.
[0024] Accordingly, process 208 may comprise, at 210, depositing a
precursor for the finish layer on the machined surface of the wedge
blank. Thus, in a scenario where the finish layer is PMMA, methyl
methacrylate monomer (MMA) may be deposited on machined surface 406
for subsequent polymerization into PMMA. This deposition may be
performed in any suitable fashion. For example, in some
embodiments, liquid precursor material may be deposited via
pouring, spraying in a pattern, injected in preparation for a
reaction injection molding process, etc. Further, the precursor may
be deposited in any suitable thickness to achieve a final finish
layer thickness suited to an application of the finished optical
wedge. For example, in one scenario, 100 microns thickness of
precursor may be deposited on the machined surface. Alternatively,
in some embodiments, the precursor may be a molten thermoplastic
polymer of suitable refractive index formulated for injection
molding of finish layer 502.
[0025] It will be appreciated that any suitable precursor
formulation may be used. For example, in some embodiments, a
mixture of precursor materials, such as a monomer and a suitable
solvent may be combined to create a precursor formulation having a
viscosity within a range of approximately 10 cp-400 cp.
Formulations within the higher viscosity end of this range may be
easy to handle during the deposition process, while formulations
within the lower viscosity end of this range may more readily wet
the machined surface, etc. It will be appreciated that this range
is merely illustrative, and that any suitable viscosity achieved by
any suitable precursor formulation may be utilized.
[0026] Continuing, 208 may further comprise, at 212, positioning
and retaining, such as by clamping, a casting plate in continuous
contact with a top surface of the precursor while the vacuum
molding tool is still under vacuum. For example, FIG. 5 shows
casting plate 504 retained within vacuum molding tool 102 above
finish layer 502 under the downward force of clamps 506 located at
the edges of casting plate 504. Optionally, in some embodiments,
additional downward force may be applied elsewhere on the casting
plate.
[0027] Casting plate 504 may be any suitable material exhibiting a
surface roughness characteristic to be imparted onto a diffuser
interface surface 510 of finish layer 502. For example, in some
embodiments, casting plate 504 is a glass plate, such as a
borosilicate float glass plate, having an average surface roughness
of approximately 2 nm RA or less. Further, in some embodiments,
casting plate 504 may be configured to avoid bowing, so that
diffuser interface surface 510 is approximately flat on the
finished optical wedge. For example, in one scenario, casting plate
504 may be approximately 20 mm-25 mm thick to provide structural
rigidity and avoid bowing or deflection in casting plate 504. In
another scenario, the casting plate may include one or more
structural ribs, members, etc. (not shown) to provide structural
rigidity.
[0028] In some embodiments, a finish layer interface surface of
casting plate 504 may be conditioned with a mold release agent
adsorbed to the finish layer interface surface of the casting
plate. The mold release agent may be configured to repel the
precursor formulation. For example, the mold release agent may be a
suitable silicone compound or a fluorocarbon compound, though it
will be appreciated that other suitable mold release agents may be
employed within the scope of the present disclosure. In some
embodiments, casting plate 504 is separated from wedge blank 150
only by finish layer 502 so that an edge bead is formed, while in
other embodiments, a gasket may be included around a perimeter of
casting plate 504 to avoid formation of an edge bead. For example,
in an embodiment where molten polymer is used as a precursor, a
gasket may be included to provide a space between machined surface
406 and casting plate 504 to facilitate an injection molding
process.
[0029] In some embodiments, electrostatic potentials of casting
plate 504, vacuum molding tool 102, and/or wedge blank 150 may be
controlled to avoid differential charging at machined surface 406
and/or at the finish layer interface surface of casting plate 504.
This may beneficially enhance wetting of the precursor on machined
surface 406 and/or the finish layer interface surface of casting
plate 504, avoid bubble formation on said surfaces, etc. In one
scenario, control of the electrostatic potentials may be via an
electron flood supplied via ionizer gun 512. In other embodiments,
any other suitable mechanism may be used to reduce electrostatic
potential differences between surfaces.
[0030] Continuing, process 208 further comprises, at 214, curing
the precursor. In the embodiment shown in FIG. 5, an ultraviolet
source 508 is configured to cure, finish layer 502 via ultraviolet
(UV) light, which may be supplied by a UV lamp. It will be
appreciated that any other suitable curing mechanism may used,
including but not limited to thermal curing, etc. Once cured,
finish layer 502 may help to maintain molded surface 152 in the
conformation imparted by the profile of molding surface 104. In
some embodiments, 214 may further include one or more post-cure
annealing processes. Such post-cure processes and/or treatments may
modulate stress within the finished optical wedge.
[0031] Method 200 next comprises, at 216, disconnecting the vacuum
from the vacuum molding tool and removing the finished optical
wedge from the vacuum molding tool. For example, FIG. 6 shows a
cross-section of an example finished optical wedge 600 taken along
the same plane as the cross-sections of FIG. 1 and FIGS. 3-5.
Finished optical wedge 600 includes finish layer 502 with an
optically smooth surface 510. Finished optical wedge 600 also
includes molded surface 152, which has been conformed to the
optical surface profile of molding surface 104. Further, in the
example shown in FIG. 6, finished optical wedge 600 includes local
topographic characteristic 608, corresponding to local topographic
characteristic 108 of molding surface 104.
[0032] By way of illustrating the thickness characteristics
imparted to the finished optical wedge, FIG. 7 shows a schematic
view of thickness profile of the cross-section of finished optical
wedge 600 of FIG. 6. It will be appreciated that the effect of
local topographic characteristic 608, represented by thickness
reference 702, is greatly exaggerated in FIG. 7, as the scale of
the horizontal (length) axis is greatly compressed in comparison to
the scale of the vertical (thickness) axis.
[0033] It is to be understood that the configurations and/or
approaches described herein are exemplary in nature, and that these
specific embodiments or examples are not to be considered in a
limiting sense, because numerous variations are possible. The
specific routines or methods described herein may represent one or
more of any number of processing strategies. As such, various acts
illustrated may be performed in the sequence illustrated, in other
sequences, in parallel, or in some cases omitted. Likewise, the
order of the above-described processes may be changed.
[0034] The subject matter of the present disclosure includes all
novel and nonobvious combinations and subcombinations of the
various processes, systems and configurations, and other features,
functions, acts, and/or properties disclosed herein, as well as any
and all equivalents thereof.
* * * * *