U.S. patent application number 14/138242 was filed with the patent office on 2014-04-24 for room temperature single phase li insertion/extraction material for use in li-based battery.
The applicant listed for this patent is Philippe CARLACH, Pierre GIBOT, Stephane LEVASSEUR, Christian MASQUELIER, Jean-Marie TARASCON. Invention is credited to Philippe CARLACH, Pierre GIBOT, Stephane LEVASSEUR, Christian MASQUELIER, Jean-Marie TARASCON.
Application Number | 20140113188 14/138242 |
Document ID | / |
Family ID | 38456541 |
Filed Date | 2014-04-24 |
United States Patent
Application |
20140113188 |
Kind Code |
A1 |
GIBOT; Pierre ; et
al. |
April 24, 2014 |
Room Temperature Single Phase Li Insertion/Extraction Material for
Use in Li-Based Battery
Abstract
The invention relates to active materials for the manufacture of
Li-based batteries. A crystalline nanometric powdered material with
formula Li.sub.x(M, M')PO.sub.4, in particular Li.sub.xFePO.sub.4
(0.ltoreq.x.ltoreq.1), is disclosed, exhibiting single phase Li
insertion/extraction mechanism at room temperature when used as
positive electrode material in Li-based batteries. Compared to
current LiFePO.sub.4, the novel material results in smooth, sloping
charge/discharge voltage curves, greatly simplifying the monitoring
of the state of charge of the batteries. The coexistence of mixed
valence states for Fe (i.e. Fe.sup.IIIVFe.sup.II) is believed to
increase the electronic conductivity in the room temperature single
phase Li.sub.xFePO.sub.4 material, compared to state of the art
two-phase materials. This, together with the nanometric size of the
particles and their sharp monomodal size distribution, contributes
to the exceptional high-rate capability demonstrated in
batteries.
Inventors: |
GIBOT; Pierre; (Amiens,
FR) ; MASQUELIER; Christian; (Boves, FR) ;
TARASCON; Jean-Marie; (Mennecy, FR) ; LEVASSEUR;
Stephane; (Brussels, BE) ; CARLACH; Philippe;
(Antwerpen, BE) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GIBOT; Pierre
MASQUELIER; Christian
TARASCON; Jean-Marie
LEVASSEUR; Stephane
CARLACH; Philippe |
Amiens
Boves
Mennecy
Brussels
Antwerpen |
|
FR
FR
FR
BE
BE |
|
|
Family ID: |
38456541 |
Appl. No.: |
14/138242 |
Filed: |
December 23, 2013 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12530846 |
Nov 12, 2009 |
8641921 |
|
|
PCT/EP2008/002195 |
Mar 19, 2008 |
|
|
|
14138242 |
|
|
|
|
60907732 |
Apr 16, 2007 |
|
|
|
Current U.S.
Class: |
429/209 |
Current CPC
Class: |
H01M 2004/028 20130101;
H01M 4/5825 20130101; H01M 10/0525 20130101; C01B 25/45 20130101;
Y10T 428/2982 20150115; H01M 4/136 20130101; H01M 2004/021
20130101; Y02E 60/10 20130101 |
Class at
Publication: |
429/209 |
International
Class: |
H01M 4/136 20060101
H01M004/136 |
Foreign Application Data
Date |
Code |
Application Number |
Mar 19, 2007 |
EP |
07290328.9 |
Claims
1. A Li insertion/extraction powdered material comprising particles
of a crystalline material, the particles having a size distribution
d50 of less than 50 nm, wherein during Li extraction (discharging)
from said material and Li insertion (charging) in said material,
the Li insertion/extraction powdered material remains a single
phase material that is thermodynamically stable at 25.degree. C.
for any amount of Li present in said material.
2. The material of claim 1, wherein d50 is between 10 and 50
nm.
3. The material of claim 1, having a d99 of less than 300 nm.
4. The material of claim 1, having a ratio (d90-d10)/d50 of less
than 1.5.
5. A secondary Li-based battery with an electrode comprising the Li
insertion/extraction powdered material of claim 1 as an active
component wherein during discharging and charging of the active
component, the contribution of said electrode to the EMF of the
battery at 25.degree. C. varies continuously with the state of
charge by more than 0.05 V, for any amount of Li present in said
material.
Description
[0001] This application is a national stage application of
International Application No. PCT/EP2008/002195, filed Mar. 19,
2008, which claims priority to European Patent Application No.
07290328.9, filed Mar. 19, 2007, and U.S. Provisional Patent
Application No. 60/907,732, filed Apr. 16, 2007, the entire
contents of which is hereby incorporated herein by reference.
[0002] This invention relates to crystalline nanometric materials,
in particular to Li.sub.xFePO.sub.4 (0.ltoreq.x.ltoreq.1) powder,
showing an unusual single phase Li insertion/extraction mechanism
at room temperature (25.degree. C.) when used as positive electrode
material in Li-based batteries.
[0003] Some years after the original work from Padhi et al. (J.
Electrochem. Soc., 144, 1188 (1997)) was published,
phospho-olivines LiMPO.sub.4 (with M is Fe, Mn, Co . . . ) now
appear to be potential candidates as positive electrode materials
for rechargeable lithium batteries. Thanks to smart processing,
e.g. by carbon coating, Li.sup.+ ions may be extracted out of
LiFePO.sub.4 leading to room-temperature capacities of about 160
mAh/g, i.e. close to the theoretical capacity of 170 mAh/g. The
room-temperature Li insertion/extraction is well known, e.g. from
WO2004/001881, to proceed at 3.45 V V5. Li.sup.+/Li, in a two-phase
reaction between LiFePO.sub.4 and FePO.sub.4. Note that, as raised
by Striebel et al. (J. Electrochem. Soc., 152, A664 (2005)) while
making a compilation of tests of various carbon-coated LiFePO.sub.4
compounds, even if the matrix conductivity has been improved by
coating, the battery developer would welcome so-far inexistent
compounds having a primary particle size in the 50-100 nm range
and, overall, attempts should be made to minimise the particle size
distribution, in order to yield better power efficiency.
[0004] WO2004/056702 and WO2007/00251 teach techniques to decrease
the average particle size down to the 140-150 nm range.
Nevertheless, it is admitted by the skilled persons that decreasing
the particle size below these values would allow a further increase
of the high-power performances.
[0005] Various authors, e.g. Yamada et al. (Electrochem. Solid
State Let., 8, A409 (2005)) and in US2007/0031732, have shown that
reducing the particle size would allow some deviation from the well
described two-phase Li insertion/extraction behaviour. Indeed,
materials showing small particle sizes exhibit some limited solid
solution (i.e. single phase) domains at room temperature, namely of
Li-poor Li.sub.xFePO.sub.4 (x<0.15) and of Li-rich
Li.sub.yFePO.sub.4 (y>0.85). Although it was recognized that the
x and y limits, which represent the boundaries of the two-phase
domain, may depend upon both the particle size and the particular
conditions of the synthesis, materials with a significantly broader
single phase domain were never obtained.
[0006] The recent discovery of a complete single phase
Li.sub.xFePO.sub.4 (0.ltoreq.x.ltoreq.1) solid solution at
temperatures of around 350.degree. C. has spurred great interest in
assessing its role in the performance of LiFePO4 as cathode
material for Li-ion batteries. Nevertheless, whatever the x values,
it was clearly demonstrated that the solid solution could not be
stabilised at room temperature, thus making it of limited practical
interest as standard battery material (Delacourt et al., Nature
Mat., 4, 254 (2005); Dodd et al., Electrochem. Solid State Let., 9,
A151 (2006)).
[0007] The most obvious distinction between a single phase and a
two-phase insertion/extraction mechanism is that the equilibrium
potential (EMF) of a single phase system is composition-dependent,
while that of a two-phase system is constant over the entire
composition range. A single phase electrode will thus show a
sloping voltage curve during charge or discharge cycles: this is
welcomed by the battery manufacturer as it enables monitoring of
the state of charge at reduced cost compared to systems presenting
a flat voltage curve.
[0008] Also, it is now admitted that in the two-phase system
LiFePO.sub.4/FePO.sub.4, both end members present very limited
electronic conductivity, and that no mixed valence state is present
either in FePO.sub.4 (Fe.sup.(III)) or in LiFePO.sub.4
(Fe.sup.(II)) (Delacourt et al., Electrochem. Soc., 152, A913
(2005). As emphasized by Chiang et al. in US2007/0031732, greater
population of both Fe species at every point within the
deintercalation range could provide a higher electronic
conductivity for the material. A good material conductivity is
particularly advantageous with respect to high drain
applications.
[0009] The same quest for enhanced material conductivity applies to
similar active materials for Li batteries, such as LiMnPO.sub.4 and
in Li(Fe,M)PO.sub.4 (with M is Co and/or Mn), as reported
respectively in the patent applications WO2008-77447 and
WO2008-77448.
[0010] Further, in US2006/0035150 A1, for the preparation of coated
LiFePO.sub.4, sources of Li, Fe and phosphate are dissolved in an
aqueous solution together with a polycarboxylic acid and a
polyhydric alcohol. Upon water evaporation, polyesterification
occurs while a mixed precipitate is formed containing Li, Fe and
phosphate. The resin-encapsulated mixture is then heat treated at
700.degree. C. in a reducing atmosphere.
[0011] In WO2007/000251 A1, a direct precipitation process is
described for preparing crystalline LiFePO.sub.4 powder, comprising
the steps of: [0012] providing a water-based mixture having at a pH
between 6 and 10, containing a water-miscible boiling point
elevation additive, and Li.sup.(I), Fe.sup.(II) and p.sup.(V) as
precursor components; [0013] heating said water-based mixture to a
temperature less than or equal to its boiling point at atmospheric
pressure, thereby precipitating crystalline LiFePO.sub.4
powder.
[0014] An extremely fine 50 to 200 nm particle size is obtained,
with a narrow distribution.
[0015] In US2004/0175614 A1, a process is disclosed for the
manufacture of LiFePO.sub.4, comprising the steps of [0016]
providing an equimolar aqueous solution of Li.sup.1+, Fe.sup.3+ and
PO.sub.4.sup.3-, [0017] evaporating the water from the solution,
thereby producing a solid mixture, [0018] decomposing the solid
mixture at a temperature below 500.degree. C. to form a pure
homogeneous Li and Fe phosphate precursor, and [0019] annealing the
precursor at a temperature of less than 800.degree. C. in a
reducing atmosphere, thereby forming a LiFePO.sub.4 powder.
[0020] The obtained powders have a particle size of less than 1
.mu.m.
[0021] In Delacourt et al., Solid State Ionics 173 (2004) 113-118,
the thermodynamics and kinetics governing the precipitation of pure
powders of phosphates phases for Li batteries are described.
Optimized electrodes were synthesized through a chemical conductive
carbon coating at the surface of LiFePO.sub.4 prepared by
evaporation of an Fe.sup.III-containing aqueous solution.
[0022] The disclosed process is aimed at providing a material with
a higher conductivity than that of conventional materials, and at
solving the monitoring problem of the state of charge.
[0023] To this end, a powdered Li insertion/extraction material is
disclosed, comprising Li.sub.x(M,M')PO.sub.4 as an active
component, wherein 0.ltoreq.x.ltoreq.1, M is one or more cations
selected from the group consisting of Mn, Fe, Co, Ni, Cu, and M' is
an optional substitutional cation selected from the group
consisting of Na, Mg, Ca, Ti, Zr, V, Nb, Cr, Zn, B, AI, Ga, Ge, Sn,
characterized in that said material is a single phase material that
is thermodynamically stable at 25.degree. C. during Li
insertion/extraction, for x varying from less than 0.2 to more than
0.8. In the above formula, M is preferably Fe; moreover, an M to M'
molar ratio of more than 5, and preferably of more than 8, is
advised. When M is Fe and M/M'>5, then the invented material is
typically characterized by a crystallographic cell volume lower
than 291 .ANG..sup.3, preferably equal to or lower than 290
.ANG..sup.3, and more preferably equal to or lower than 289
.ANG..sup.3. This volume is deduced from XRD measurements using a
Pmna or Pmnb space group.
[0024] The invented material is a powder with a preferred particle
size distribution with a d50 of less than 50 nm, and preferably
between 10 and 50 nm. A d99 of less than 300 nm, and preferably of
less than 200 nm is advised. Moreover, a mono-modal particle size
distribution where the ratio (d90-d10)/d50 is less than 1.5,
preferably less than 1.2, is advised.
[0025] Another aspect of the invention concerns a process for the
synthesis of the above-described Li.sub.x(M,M')PO.sub.4 materials.
The process comprises the steps of: [0026] providing a first
water-based mixture having a pH between 6 and 10, containing a
bipolar (i.e. water miscible) aprotic additive, and Li and P
precursors introduced as Li.sup.(I) and p.sup.(V); [0027] adding an
M precursor as M.sup.(II), and an M' precursor, to said first
waterbased mixture, thereby obtaining a second water-based mixture;
[0028] heating said second water-based mixture to a temperature of
less than or equal to its boiling point at atmospheric pressure,
thereby precipitating the powdered Li insertion/extraction
material.
[0029] In a preferred embodiment, Li.sup.(I) is introduced as
LiOH.H.sub.2O, and p.sup.(V) as H.sub.3PO.sub.4. It is advisable to
adjust the pH of the first mixture by using a proper ratio of
LiOH.H.sub.2O and H.sub.3PO.sub.4. The also process covers the
synthesis Li.sub.x(M,M')PO.sub.4, wherein M=Fe, M' being absent,
and wherein the pH of the first water-based mixture is between 6.5
and 8, and preferably between 6.5 and 7.5.
[0030] The bipolar aprotic additive is preferably selected and
dosed so as to elevate the atmospheric boiling point of the second
water-based mixture to between 100 and 150.degree. C., preferably
between 105 and 120.degree. C.
[0031] Dimethylsulfoxide is a preferred additive. The first
water-based mixture contains between 5 and 50% mol, and preferably
between 10 and 30% mol of dimethylsulfoxide.
[0032] In a still preferred embodiment, the precipitating powdered
Li insertion/extraction material is subjected to a thermal
post-treatment by heating it in non-oxidising conditions, at a
temperature of up to 650.degree. C., and preferably of at least
300.degree. C.
[0033] In a still preferred embodiment, an electron conducting
substance, or its precursor, is added to either one or more of the
first water-based mixture, the second water-based mixture, and the
powder before the thermal posttreatment.
[0034] The electronic conducting substance can advantageously be
carbon, in particular conductive carbon or carbon fibres, and the
precursor of the electron conducting substance can be a
carbon-based polymerizable structure.
[0035] Another aspect of the invention concerns a secondary
Li-based battery, comprising an anode, an electrolyte and a
cathode, said cathode comprising the above-described material.
[0036] Yet another aspect of the invention concerns an electrode
mix for secondary Li-based batteries, comprising the
above-described material.
[0037] A first embodiment is related to an electrode mix for
secondary Li-based batteries with non-aqueous liquid electrolyte,
comprising at least 80% wt of the invented material, characterised
by a reversible capacity of at least 75% of the theoretical
capacity (about 170 mAh/g), when used as an active component in a
cathode cycled between 2.5 and 4.5 V vs. Li.sup.+/Li at a discharge
rate of 0.1 C at 25.degree. C. The amount of additives (binder and
carbon) in the electrode mixture can be limited to less than 20%
wt, preferably to less than 10% wt, because the mixture, being
pasted on a current collector, needs not to be self-supporting for
this type of batteries.
[0038] A second embodiment is related to an electrode mix for
secondary Li-based batteries with non-aqueous gel-like polymer
electrolyte, comprising at least 80% wt of the invented material,
characterised by a reversible capacity of at least 75% of the
theoretical capacity when used as an active component in a cathode
cycled between 2.5 and 4.5 V vs. Li.sup.+/Li at a discharge rate of
0.1 C at 25.degree. C. The amount of additives in the electrode
mixture can be as high as 20% wt in this case, because the mixture,
being rolled in the form of a sheet to be laminated to a current
collector, needs to be self-supporting during assembly of this type
of batteries.
[0039] A third embodiment is related to an electrode mix for
secondary Li-based batteries with non-aqueous dry polymer
electrolyte, comprising at least 70% wt of the invented material,
characterised by a reversible capacity of at least 75% of the
theoretical capacity, when used as an active component in a cathode
cycled between 2.5 and 4.5 V vs. Li.sup.+/Li at a discharge rate of
0.1 C at 25.degree. C.
[0040] A further embodiment concerns a secondary Li-based battery
with an electrode comprising nanometric powdered
Li.sub.x(M,M')PO.sub.4 as an active component, wherein
0.ltoreq.x.ltoreq.1, M is one or more cations selected from the
group consisting of Mn, Fe, Co, Ni, Cu, and M' is an optional
substitutional cation selected from the group consisting of Na, Mg,
Ca, Ti, Zr, V, Nb, Cr, Zn, B, AI, Ga, Ge, Sn, characterized in that
the contribution of said electrode to the EMF of the battery at
25.degree. C. varies continuously with the state of charge by more
than 0.05 V, for x varying from 0.2 to 0.8. In the above formula, M
is preferably Fe; moreover, an M to M' molar ratio of more than 5,
and preferably of more than 8, is advised. When M is Fe and
M/M'>5, then the said nanometric powdered active component is
typically characterized by a crystallographic cell volume lower
than 291 .ANG..sup.3, preferably equal to or lower than 290
.ANG..sup.3, and more preferably equal to or lower than 289
.ANG..sup.3. This volume is deduced from XRD measurements using a
Pnma or Pmnb space group.
[0041] By "continuously varying EMF" is meant a continuously
sloping charge/discharge voltage curve. This slope, according to
the present invention, amounts to at least 5 mV per
inserted/extracted Li, and preferably to at least 15 mV per
inserted/extracted Li, and this along the complete charge/discharge
cycle.
[0042] The said nanometric powdered active component has a
preferred particle size distribution with a d50 of less than 50 nm,
and preferably between 10 and 50 nm. A d99 of less than 300 nm, and
preferably of less than 200 nm is advised. Moreover, a mono-modal
particle size distribution where the ratio (d90-d10)/d50 is less
than 1.5, preferably less than 1.2 is advised.
[0043] It should be noted that, in the invented material, M and M'
are considered as at least partially interchangeable, whilst
however respecting electroneutrality rules assuming Li.sup.(I),
M.sup.(II), M'.sup.(I) to (V), and p.sup.(V).
[0044] Products finer than 10 nm are not particularly advisable, as
they could lead to processability problems during electrode
manufacturing.
[0045] According to the invented process, the first water-based
mixture has a pH between 6 and 10, preferably 6 to 8, in order to
avoid precipitation of Li.sub.3PO.sup.4 as impurities.
[0046] Use is made of a bipolar additive as a co-solvent that will
increase the precipitate nucleation kinetics, and thus reducing the
size of the room temperature single phase Li insertion/extraction
Li.sub.xFePO.sub.4 (0.ltoreq.x.ltoreq.1) nanometric particles. In
addition to being bipolar, i.e. miscible with water, useful
co-solvents should be aprotic, i.e. show only a minor or complete
absence of dissociation accompanied by release of hydrogen ions.
Cosolvents showing complexation or chelating properties such as
ethylene glycol do not appear suitable as they will reduce the
kinetics of precipitation of Li.sub.xMPO.sub.4 and thus lead to
larger particle sizes. Suitable dipolar aprotic solvents are
dioxane, tetrahydrofuran, N-(C.sub.1-C.sub.18-alkyl) pyrrolidone,
ethylene glycol dimethyl ether, C.sub.1-C.sub.4-alkylesters of
aliphatic C.sub.1-C.sub.6-carboxylic acids, C.sub.1-C.sub.6-dialkyl
ethers, N,N-di-(C.sub.1-C.sub.4-alkyl)amides of aliphatic
C.sub.1-C.sub.4-carboxylic acids, sulfolane,
1,3-di-(C.sub.1-C.sub.8alkyl)-2-imidazolidinone,
N-(C.sub.1-C.sub.8-alkyl)caprolactam,
N,N,N',N'-tetra-(C.sub.1-C.sub.8-alkyl)urea,
1,3-di-(C.sub.1-C.sub.8-alkyl)-3,4,5,6-tetrahydro-2(1H)-pyrimidone,
N,N,N',N'-tetra-(C.sub.1-C.sub.8-alkyl)sulfamide,
4-formylmorpholine, 1formylpiperidine or 1-formylpyrrolidine, in
particular N-(C.sub.1-C.sub.18-alkyl)pyrrolidone,
N,N-di-(C.sub.1-C.sub.4-alkyl)amid-e of aliphatic
C.sub.1-C.sub.4-carboxylic acids, 4-formylmorpholine,
1-formylpiperidine or 1-formylpyrrolidine, preferably
N-methyJpyrrolidone (NMP), N-octylpyrrolidone, Ndodecylpyrrolidone,
N,N-dimethylformamide, N,N-dimethylacetamide, 4-formylmorpholine,
1-formylpiperidine or 1-formylpyrrolidine, particularly preferably
N-methylpyrrolidone, N,N-dimethylformamide, N,Ndimethylacetamide or
hexamethylphosphoramide. Other alternatives such as tetraalkyl
ureas are also possible. Mixtures of the abovementioned dipolar
aprotic solvents may also be used. In a preferred embodiment,
dimethylsulfoxide (DM50) is used as solvent.
[0047] It cannot be excluded that the novel room temperature single
phase insertion/extraction material could lead to a two-phase
system at temperatures well below 25.degree. C., such as below
10.degree. C. This phase transition should however be reversible.
Its effect should therefore only minimally affect the operation of
batteries in most practical circumstances.
[0048] The disclosed process leads to an initial material that may
contain traces of Fe(III). Due to the nanometric particle size,
some Fe.sup.(III) could arise from a deviation from stoichiometry
at the surface of the material. The presence of Fe.sup.(III) could
also be due to a second amorphous phase, most likely
LiFePO.sub.4(OH) or FePO.sub.4.nH.sub.2O, at the surface of the
crystals or at grain boundaries. The skilled person may minimize
the Fe.sup.(III) by working under reducing atmosphere or by relying
on reducing agents such as hydrazine or SO.sub.2. The possible Li
deficit in the initial material could moreover be compensated
during the first full discharge cycle of the battery if the
environment is able to provide the necessary Li (as it is likely
the case in many practical batteries).
[0049] Compared to state of the art LiFePO.sub.4 materials, the
advantages of the invented material are: [0050] a sloping
charge/discharge curve, allowing direct monitoring of the state of
charge by simple potential measurement; [0051] a nanometric
particles size, which alleviates kinetic limitations due to Li ion
transport within the particles, and allows fast charge/discharge of
the battery; [0052] a narrow particle size distribution, ensuring a
homogeneous current distribution within the battery; this is again
especially important at high charge/discharge rates, where finer
particles would get more depleted than coarser ones, a phenomenon
leading to the eventual deterioration of the particles and to the
fading of the battery capacity upon use; a narrow particle size
distribution furthermore facilitates the manufacture of electrodes;
[0053] the coexistence of mixed valence state for Fe (i.e.
Fe.sup.(III)/Fe.sup.(II)), which is believed to increase the
electronic conductivity of the room temperature single phase
Li.sub.xFePO.sub.4 material compared to state of the art two-phase
materials, represented as (1-x)FePO.sub.4+xLiFePO.sub.4
(0.ltoreq.x.ltoreq.1).
SUMMARY OF THE FIGURES
[0054] FIG. 1: Galvanostatic charge/discharge curve of the invented
material at 25.degree. C. and C/20 rate, showing a sloping voltage
curve. The plot shows the voltage of the battery as a function of
the normalized capacity; 0% state of charge (SOC) corresponds to
starting LiFePO.sub.4 material, while 100% corresponds to charged
delithiated FePO.sub.4 material.
[0055] FIG. 2: FEG-SEM picture of product of the Example, showing
the small particle size and the sharp particle size
distribution.
[0056] FIG. 3: Volumetric particle size distribution and cumulative
distribution (% vs. nm) for the product of the Example showing d50
values about 45 nm, while the relative span, defined as
(d90-d10)/d50, is about 1.2 (d10=25 nm, d90=79 nm).
[0057] FIG. 4: In situ XRD recorded at different states of charge
and at 25.degree. C. for invented material; 0% state of charge
(SOC) corresponds to starting LiFePO.sub.4 material, while 100%
corresponds to charged delithiated FePO.sub.4 material.
[0058] FIG. 5: Evolution with composition of the cell parameters
for LixFePO.sub.4 (0.ltoreq.x.ltoreq.1) calculated from the in situ
XRD recorded at measured at 25.degree. C. at different states of
charge. This clearly shows a continuous solid solution between
LiFePO.sub.4 and FePO.sub.4 with continuous variation between the
limiting values of the cell parameters as the lithium concentration
varies from 1 to 0.
[0059] FIG. 6: Galvanostatic charge/discharge curve of state of the
art material at 25.degree. C. and C/20 rate, showing the constant
voltage curve. The plot shows the voltage of the battery as a
function of the normalized capacity; 0% state of charge (SOC)
corresponds to starting LiFePO.sub.4 material, while 100%
corresponds to charged delithiated FePO.sub.4 material.
[0060] FIG. 7: in situ XRD recorded at different states of charge
for state of the art products; 0% state of charge (SOC) corresponds
to starting LiFePO.sub.4 material, while 100% corresponds to
charged delithiated FePO.sub.4 material.
[0061] FIG. 8: Evolution with composition of the cell parameters
for (1-x)FePO.sub.4+xLiFePO.sub.4 (0.ltoreq.x.ltoreq.1) calculated
from the in situ XRD recorded at different states of charge. This
clearly shows a classical two-phase system, the proportion of each
end member varying with the lithium concentration in the
material.
EXAMPLE
[0062] The invention is further illustrated in the following
example. In a first step, DMSO is added to a solution of 0.1 M
H.sub.3PO.sub.4, diluted in H.sub.2O under stirring. The amount of
DMSO is adjusted in order to reach a global composition of 50% vol.
water and 50% vol. DMSO.
[0063] In a second step, an aqueous solution of 0.3M LioH.H.sub.2O
is added at 25.degree. C. in a quantity so as to increase the pH up
to a value between 6.5 and 7.5, and leading to the precipitation of
Li.sub.3PO.sub.4.
[0064] In a third step, a solution of 0.1M Fe(II) in
FeSO.sub.4.7H.sub.2O is added at 25.degree. C. This is believed to
lead to the re-dissolution of Li.sub.3PO.sub.4. The final Li:Fe:P
ratio in the solution is close to 3:1:1. By adding the Fe(II)
precursor after the pH of the solution has been set at a certain
value between 6.5 and 7.5, it is possible to perform a controlled
precipitation of Fe-species resulting in much lower particle sizes
than obtained in the prior art.
[0065] In a fourth step, the temperature of the solution is
increased up to the solvent boiling point, which is 108 to
110.degree. C. After 6 h, the obtained precipitate is filtered and
washed thoroughly with water.
[0066] The powdery precipitate is pure crystalline LiFePO.sub.4,
according to XRD measurements. The full pattern matching refinement
done on XRD pattern (Pmnb space group) leads to cell parameters
a=10.294 .ANG..sup.3, b=5.964 .ANG..sup.3 and c=4.703 .ANG..sup.3,
corresponding to a crystallographic cell volume of 288.7
.ANG..sup.3. The FEG-SEM picture on FIG. 2 shows monodisperse small
crystalline particles in the 30 to 60 nm range. The volumetric
particle size distribution of the product was measured by using
image analysis. As shown in FIG. 3, the d50 values is about 45 nm,
while the relative span, defined as (d90d10)/d50, is about 1.2
(d10=25 nm, d90=79 nm).
[0067] A slurry is prepared by mixing the LiFePO.sub.4 powder
obtained with the process described above with 10% wt carbon black
and 10% wt PVDF into N-Methyl Pyrrolidone (NMP) and deposited on an
AI foil as current collector. The obtained electrode containing 80%
wt active material is used to manufacture coin cells, using a
loading of 6 mg/cm.sup.2 active material. The negative electrodes
are made of metallic Li. The coin cells are cycled in LiBF.sub.4
based electrolyte between 2.5 and 4.0 V. FIG. 1 shows that high
reversible capacity is obtained at low rate with a sloping voltage
curve upon cycling characteristic of a single phase Li
insertion/extraction mechanism. It should be emphasised that the
curve of FIG. 1 has been recorded in galvanostatic conditions, and,
as such, only approximates the EMF of the electrode. The EMF is in
this case varying continuously as a function of Li
insertion/extraction; the slope of the EMF curve is thus definitely
nonzero, although it might be slightly less pronounced than in the
figure.
[0068] FIG. 4 shows in situ XRD data collected in the battery upon
cycling. It is clearly visible on FIG. 5 that the
insertion/extraction proceeds from LiFePO.sub.4 to FePO.sub.4 with
a continuous evolution of the cell parameters, which evidences the
presence of a single Li.sub.xFePO.sub.4 (0.ltoreq.x.ltoreq.1)
phase. It also emphasizes the good reversibility of this single
phase mechanism upon cycling.
Counter Example
[0069] As a counter example, materials are synthesised according to
the example illustrating WO2007/000251. Compared to the example
according to the invention, one notes that the order of addition of
the reactants is different; this change is of crucial importance
with respect to the final particle size of the precipitated
material, this latter being about 130 to 150 nm for product
precipitated according to the mentioned prior art. It is understood
that the difference between the present invention and this prior
art lies in the fact that the Fe-precursor is added to a solution
having already a fixed and stable pH, between 6.5 and 7.5; whilst
in the prior art the Fe-precursor is added to a solution having a
pH of less than 6, whereafter the addition of the Li-precursor
raised the pH to around 7. The Fe-precursor can also be added in a
solid form.
[0070] Also, the obtained counter example material, as
characterized by Rietveld refinement from XRD pattern, shows a
crystallographic cell volume of 291.7 .ANG..sup.3.
[0071] With his material, batteries are prepared as described
above. FIG. 6 shows the charge/discharge curve of the prior art
material at room temperature and C/20 cycling rate. There is a
constant voltage plateau, which is characteristic of a two-phase Li
insertion/extraction mechanism. It should be emphasised that the
curve of FIG. 6 has been recorded in galvanostatic conditions, and,
as such, only approximates the EMF of the cell. The EMF is in this
case constant, the slope of the EMF as a function of Li
insertion/extraction being essentially zero.
[0072] FIG. 7 shows in situ XRD recorded at different state of
charge/discharge. The evolution of the cell parameters is
illustrated in FIG. 8. This clearly shows a classical two-phase
system, the proportion of each end member FePO.sub.4 and
LiFePO.sub.4 varying with the lithium concentration in the
material, as opposed to the product according to the invention.
* * * * *