U.S. patent application number 13/867579 was filed with the patent office on 2013-11-28 for process for obtaining catalyst composites meapo and their use in conversion of organics to olefins.
This patent application is currently assigned to TOTAL PETROCHEMICALS RESEARCH FELUY. The applicant listed for this patent is TOTAL PETROCHEMICALS RESEARCH FELUY. Invention is credited to Nikolai Nesterenko, Sander Van Donk, Walter Vermeiren.
Application Number | 20130317269 13/867579 |
Document ID | / |
Family ID | 39816666 |
Filed Date | 2013-11-28 |
United States Patent
Application |
20130317269 |
Kind Code |
A1 |
Nesterenko; Nikolai ; et
al. |
November 28, 2013 |
Process for Obtaining Catalyst Composites MeAPO and Their Use in
Conversion of Organics to Olefins
Abstract
A mixture can include 0.01 to 30 weight % of a medium or large
pore crystalline silicoaluminate, silicoaluminophosphate materials,
or silicoaluminate mesoporous molecular sieves (A), and 99.99 to 70
weight % of a MeAPO molecular sieve. The mixture can be included in
a catalyst. An XTO process can include contacting an
oxygen-containing, halogenide-containing, or sulphur-containing
organic feedstock with the catalyst under conditions effective to
convert the organic feedstock to olefin products. A combined XTO
and OCP process can include contacting the organic feedstock with
the catalyst at conditions effective to convert at least a portion
of the organic feedstock to form an XTO reactor effluent including
light olefins and a heavy hydrocarbon fraction, separating the
light olefins from the heavy hydrocarbon fraction, and contacting
the heavy hydrocarbon fraction in an OCP reactor at conditions
effective to convert at least a portion of the heavy hydrocarbon
fraction to light olefins.
Inventors: |
Nesterenko; Nikolai;
(Nivelles, BE) ; Vermeiren; Walter; (Houthalen,
BE) ; Van Donk; Sander; (Uccle, BE) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
TOTAL PETROCHEMICALS RESEARCH FELUY |
SENEFFE (FELUY) |
|
BE |
|
|
Assignee: |
TOTAL PETROCHEMICALS RESEARCH
FELUY
SENEFFE (FELUY)
BE
|
Family ID: |
39816666 |
Appl. No.: |
13/867579 |
Filed: |
April 22, 2013 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12811218 |
Dec 27, 2010 |
8450233 |
|
|
PCT/EP2009/050756 |
Jan 23, 2009 |
|
|
|
13867579 |
|
|
|
|
Current U.S.
Class: |
585/329 ; 502/61;
502/64; 502/65; 502/66; 502/71; 585/324; 585/638; 585/640;
585/642 |
Current CPC
Class: |
B01J 29/85 20130101;
C07C 1/22 20130101; Y02P 30/40 20151101; C07C 1/26 20130101; C07C
1/20 20130101; Y02P 30/20 20151101; B01J 2229/42 20130101; B01J
29/40 20130101; B01J 29/005 20130101; C07C 1/32 20130101; Y02P
30/42 20151101; B01J 2229/186 20130101; C07C 1/20 20130101; C07C
11/02 20130101 |
Class at
Publication: |
585/329 ;
585/324; 585/638; 585/640; 585/642; 502/64; 502/66; 502/71; 502/61;
502/65 |
International
Class: |
C07C 1/32 20060101
C07C001/32; C07C 1/26 20060101 C07C001/26; B01J 29/85 20060101
B01J029/85; C07C 1/22 20060101 C07C001/22 |
Foreign Application Data
Date |
Code |
Application Number |
Jan 25, 2008 |
EP |
08150686.7 |
Claims
1-41. (canceled)
42. A catalyst composite comprising: at least 0.5% by weight of at
least one metal salt, which is stable under temperatures of 200 to
700.degree. C. and pressures of 5 to 5000 kPa, wherein the metal
salt comprises a metal selected from a group consisting of Ga, Cs,
Sr, Mg, Ca, Ba, Sc, Sn, Li, Co, Zn, and combinations thereof, and
wherein the metal salt comprises an anion selected from a group
consisting of silicates, borates, and borosilicates; at least 10%
by weight of molecular sieves which comprise 70 to 100% by weight
of molecular sieves of at least one small pore aluminosilicate or
small pore metalloaluminophosphate (MeAPO) molecular sieve and 0 to
30% by weight of molecular sieves of at least one medium or large
pore molecular sieve comprising pore apertures defined by ring
sizes of at least 10 tetrahedric atoms; wherein the at least one
small pore aluminosilicate or small pore MeAPO molecular sieve
comprises pore apertures defined by ring sizes of up to 8
tetrahedric atoms; wherein the at least one medium or large pore
molecular sieve is selected from the group consisting of
crystalline silicoaluminates, silicoaluminophosphates, mesoporous
silicoaluminates and combinations thereof.
43. The catalyst composite of claim 42, wherein the metal is
selected from a group consisting of Zn, Co, Ca, Mg, and
combinations thereof.
44. The catalyst composite of claim 42, wherein the metal is
selected from a group consisting of Zn, Co, and combinations
thereof.
45. The catalyst composite of claim 42, wherein the metal is
selected from a group consisting of Ca, Mg, and combinations
thereof.
46. The catalyst composite of claim 42, wherein the MeAPO molecular
sieve has predominantly a plate crystal morphology in which the
width (W) and the thickness (T) are represented by the formula:
W/T.gtoreq.10.
47. The catalyst composite of claim 46, wherein W/T ranges from 10
to 100.
48. The catalyst composite of claim 46, wherein T ranges from 0.01
to 0.07 .mu.m.
49. The catalyst composite of claim 46, wherein T ranges from 0.04
to 0.07 .mu.m.
50. The catalyst composite of claim 42, wherein the catalyst
composite comprises from 0.5% to 10% by weight of the at least one
metal salt.
51. The catalyst composite of claim 42, wherein the molecular
sieves comprise 70 to 99.9% by weight of the MeAPO molecular sieve
and 0.01 to 30% by weight of the medium or large pore molecular
sieve.
52. The catalyst composite of claim 42, wherein the molecular
sieves comprise 75 to 99.5% by weight of the MeAPO molecular sieve
and 0.5 to 25% by weight of the medium or large pore molecular
sieve.
53. The catalyst composite of claim 42, wherein the medium pore
crystalline silicoaluminate molecular sieves are selected from a
group consisting of MFI, FER, MEL and combinations thereof.
54. The catalyst composite of claim 42, wherein the medium pore
crystalline silicoaluminate molecular sieve is selected from a
group consisting of ZSM-5, silicalite, P-ferrierite, and
combinations thereof.
55. The catalyst composite of claim 42, wherein the medium pore
silicoaluminophosphate material is AEL.
56. The catalyst composite of claim 42, wherein the large pore
crystalline silicoaluminates are selected from a group consisting
of FAU, MOR, LTL, MAZ, MWW, BEA, and combinations thereof.
57. The catalyst composite of claim 42, wherein the large pore
silicoaluminophosphate materials is AFI.
58. The catalyst composite of claim 42, wherein the mesoporous
silicoaluminate is MCM-41.
59. The catalyst composite of claim 42, wherein the MeAPO molecular
sieves have essentially a structure CHA or AEI or a mixture
thereof.
60. The catalyst composite of claim 42, wherein the MeAPO molecular
sieves have essentially the structure SAPO-18, SAPO-34, SAPO-44,
SAPO-17, SAPO-35 or a mixture thereof.
61. The catalyst composite of claim 42, wherein MeAPO is an
intergrown phase of two MeAPO having AEI and CHA framework
types.
62. The catalyst composite of claim 42, wherein the MeAPO molecular
sieve has an empirical chemical composition on an anhydrous basis,
after synthesis and calcination, expressed by the formula
H.sub.xMe.sub.yAl.sub.zP.sub.kO.sub.2, in which: y+z+k=1; and x is
less than or equal to y, wherein: y has a value ranging from 0.0008
to 0.4; z has a value ranging from 0.25 to 0.67; and k has a value
ranging from 0.2 to 0.67.
63. The catalyst composite of claim 42, wherein the MeAPO has been
prepared by a method comprising: forming a reaction mixture
containing a texture influencing agent (TIA), an organic templating
agent (TEMP), and a reactive source wherein the reactive source is
a reactive inorganic source of MeO.sub.2 essentially insoluble in
the TIA, Al.sub.2O.sub.3, P.sub.2O.sub.5 or combinations thereof;
crystallizing the above reaction mixture thus formed until crystals
of the metalloaluminophosphate (MeAPO) are formed; recovering a
solid reaction product; washing it with water to remove the TIA;
and calcinating it to remove the organic template.
64. The catalyst composite of claim 42, wherein in the MeAPO, Me is
a metal selected from a group consisting of Si, Ge, Mg, Zn, Fe, Co,
Ni, Mn, Cr, Ca, Ba, Mo, Cu, Ga, Sn, Ti, and mixtures thereof.
65. The catalyst composite of claim 64, wherein Me is Si.
66. The catalyst composite, of claim 42, wherein a metal selected
from a group consisting of Si, Mg, Zn, Ge, Fe, Co, Ni, Mn, Cr, Ca,
Ba, Mo, Cu, Ga, Sn, Ti, and mixtures thereof is added to the
molecular sieve(s) before blending with the metal salt.
67. The catalyst composite of claim 42, wherein the composite
further comprises metal phosphates and/or sulphates comprising at
least one metal selected from a group consisting of Zn, Co, Ca, Mg,
Ga, Al, Cs, Sr, Ba, Sc, Sn, and Li.
68. The catalyst composite of claim 42, wherein the metal salt is
introduced to the molecular sieve(s) by one of the following two
methods: during the formulation step of the catalyst by
mechanically blending the molecular sieve with a metal silicate
forming a precursor; or physical blending of a previously
formulated molecular sieve and a previously formulated metal
silicate in situ in an XTO and/or OCP reaction medium.
69. The catalyst composite of claim 68, wherein after introduction
of the metal salt to the molecular sieve(s), the catalyst composite
is post-treated by calcination, reduction, steaming, or
P-modification of zeolites.
70. A process for making an olefin product from an
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock wherein the oxygen-containing,
halogenide-containing or sulphur-containing organic feedstock is
contacted in an XTO reactor with the catalyst composite of claim 42
under conditions effective to convert the oxygen-containing,
halogenide-containing or sulphur-containing organic feedstock to
produce an XTO reactor effluent comprising a heavy hydrocarbon
fraction and olefin products comprising ethylene and propylene.
71. The process of claim 70, wherein the XTO reactor effluent
comprising light olefins and a heavy hydrocarbon fraction is sent
to a fractionation section to separate said light olefins from the
heavy hydrocarbon fraction and the heavy hydrocarbon fraction is
recycled to the XTO reactor at conditions in the XTO reactor
effective to convert at least a portion of the heavy hydrocarbon
fraction to olefin products.
72. The process of claim 71, wherein the olefin products are
fractionated to form a stream comprised essentially of ethylene and
at least a part of said stream is recycled to the XTO reactor to
increase the propylene production.
73. The process of claim 70, wherein the XTO reactor effluent
comprising light olefins and a heavy hydrocarbon fraction is sent
to a fractionation section to separate the light olefins from said
heavy hydrocarbon fraction and the heavy hydrocarbon fraction is
sent in an OCP reactor at conditions in the OCP reactor effective
to convert at least a portion of the heavy hydrocarbon fraction to
light olefins.
74. The process of claim 73, wherein the OCP reactor effluent is
sent to a fractionator and the light olefins are recovered and
hydrocarbons having 4 carbon atoms or more are recycled to an inlet
of the OCP reactor, and mixed with the heavy hydrocarbon recovered
from the effluent of the XTO reactor.
75. The process of claim 74, wherein before recycling the
hydrocarbons having 4 carbon atoms or more to the inlet of the OCP
reactor, the hydrocarbons having 4 carbon atoms or more are sent to
a second fractionator to purge heavies.
76. The process of claim 75, wherein ethylene is recycled to the
OCP reactor, and wherein the ethylene is from the fractionation
section of the XTO reactor, from the fractionation section of the
OCP reactor, from both the fractionation section of the XTO reactor
and the fractionation section of the OCP reactor, or from a common
recovery section.
77. The process of claim 75, wherein ethylene is recycled to the
XTO reactor, and wherein the ethylene is from the fractionation
section of the XTO reactor, from the fractionation section of the
OCP reactor, from both the fractionation section of the XTO reactor
and the fractionation section of the OCP reactor, or from a common
recovery section.
78. The process of claim 70, wherein the ethylene is polymerized
with one or more comonomers.
79. The process of claim 70, wherein the propylene is polymerized
with one or more comonomers.
Description
FIELD OF THE INVENTION
[0001] The present invention relates to catalyst composites
comprising promoters and mixtures of molecular sieves containing
MeAPO, as well as their use in conversion of organics to olefins.
More precisely the mixture of molecular sieves comprises MeAPO and
a crystalline silicoaluminate or silicate molecular sieve. The
crystalline silicoaluminate or silicate molecular sieves have
medium to large pore sizes in comparison with the small pore sizes
of the MeAPO. The mixtures together with the promoter of the
invention provide useful catalyst composites suitable for a variety
of processes including cracking, hydrocracking, isomerization,
reforming, dewaxing, alkylation, transalkylation and conversion of
oxygenates (or halogenide-containing or sulphur-containing organic
compounds) to light olefins.
BACKGROUND OF THE INVENTION
[0002] The limited supply and increasing cost of crude oil has
prompted the search for alternative processes for producing
hydrocarbon products. One such process is the conversion of
oxygen-containing (by way of example methanol),
halogenide-containing or sulphur-containing organic compounds to
hydrocarbons and especially light olefins (by light olefins it is
meant C.sub.2 to C.sub.4 olefins) or gasoline and aromatics. In the
present application the conversion of said oxygen-containing (also
referred to as oxygenates), halogenide-containing or
sulphur-containing organic compounds to hydrocarbons and especially
light olefins is referred to as the XTO process. The interest in
the XTO process is based on the fact that feedstocks, especially
methanol can be obtained from coal, biomass, organic waste or
natural gas by the production of synthesis gas which is then
processed to produce methanol. The XTO process can be combined with
an OCP (olefins cracking process) process to increase production of
olefins. The XTO process produces light olefins such as ethylene
and propylene as well as heavy hydrocarbons such as butenes and
above. These heavy hydrocarbons are cracked in an OCP process to
give mainly ethylene and propylene.
[0003] U.S. Pat. No. 6,951,830B2 relates to a catalyst composition,
a method of making the same and its use in the conversion of a
feedstock, preferably an oxygenated feedstock, into one or more
olefin(s), preferably ethylene and/or propylene. The catalyst
composition comprises a molecular sieve, such as a
silicoaluminophosphate and/or an aluminophosphate, hydrotalcite,
and optionally a rare earth metal component. The rare earth metal
compound can be in the form of acetates, halides, oxides,
oxyhalides, hydroxides, sulphides, sulphonates, borides, borates,
carbonates, nitrates, carboxylates and mixtures thereof.
[0004] US20070043250A1 describes an oxygenate conversion catalyst
useful in the conversion of oxygenates such as methanol to olefinic
products which is improved by the use of a catalyst combination
based on a molecular sieve in combination with a co-catalyst
comprising a mixed metal oxide composition which has
oxidation/reduction functionality under the conditions of the
conversion. This metal oxide co-catalyst component will comprise a
mixed oxide of one or more, preferably at least two, transition
metals, usually of Series 4, 5 or 6 of the Periodic Table, with the
metals of Series 4 being preferred, as an essential component of
the mixed oxide composition. The preferred transition metals are
those of Groups 5, especially titanium and vanadium, Group 6,
especially chromium or molybdenum, Group 7, especially manganese
and Group 8, especially cobalt or nickel. Other metal oxides may
also be present. The preferred molecular sieve components in these
catalysts are the high silica zeolites and the
silicoaluminaphosphates (SAPOs), especially the small pore SAPOs
(8-membered rings), such as SAPO-34. These catalyst combinations
exhibiting reduced coke selectivity have the potential of achieving
extended catalyst life. In addition, these catalysts have the
capability of selectively converting the hydrogen produced during
the conversion to liquid products, mainly water, reducing the
demand on reactor volume and product handling.
[0005] U.S. Pat. No. 7,186,875 discloses a process for converting
an oxygenate-containing feedstock into one or more olefins in a
reactor system including a plurality of fixed bed reactors each
containing a catalyst composition comprising a molecular sieve and
at least one metal oxide having an uptake of carbon dioxide at
100.degree. C. of at least 0.03 mg/m.sup.2 of the metal oxide. Each
reactor is sequentially rotated between at least one operating
mode, wherein the catalyst composition in the reactor is contacted
with the oxygenate-containing feedstock, and a regeneration mode,
wherein the catalyst composition in the reactor is contacted with a
regeneration medium. The molecular sieve is a
silicoaluminophosphate (SAPO) and/or a metal substituted SAPO. The
metal oxide used in the composition, it is stated, is different
from typically used binders and/or matrix material, in that it
extends the life of the catalyst composition. Suitable metal oxides
include those metal oxides having a Group 2, Group 3 (including the
Lanthanides and Actinides) or Group 4 metal. There is no mention of
any metal salts.
[0006] US 2003/0176752 describes a catalyst composition, a method
making the same and its use in the conversion of a feedstock,
preferably an oxygenated feedstock, into one or more olefin(s),
preferably ethylene and/or propylene. The catalyst composition
comprises a molecular sieve and at least one oxide of a metal from
Group 4, optionally in combination with at least one metal from
Groups 2 and 3. The metal oxide has an uptake of carbon dioxide at
100.degree. C. of at least 0.03 mg/m.sup.3. The molecular sieve is
preferably a silicoaluminophosphate and/or metal derivatives
thereof.
[0007] US 2004/0030213 discloses describes an oxygenate conversion
catalyst based a combination of a molecular sieve such as SAPO-34
and an oxide of a metal of Group 3, including the lanthanide series
and the actinide series. Examples of such oxides include lanthanum
oxide, yttrium oxide, scandium oxide, cerium oxide, praseodymium
oxide, neodymium oxide, samarium oxide and thorium oxide.
[0008] This catalytic combination is reported to result in similar
advantages when used in methanol conversion reactions and, in
addition, results in a reduction in the amounts of undesirable
by-products such as aldehydes and ketones, especially acetaldehyde.
In addition, it is claimed that the catalyst compositions are less
susceptible to coke formation and thus have longer lifetimes. It is
also stated that the higher density of these catalyst compositions
is believed to improve operability in the overall conversion
process. The denser catalyst particles are retained to a greater
extent within the unit, whether in the reactor or its associated
regenerator, resulting in lower catalyst losses.
[0009] WO 1998029370 discloses the conversion of oxygenates to
olefins over a small pore (less than 5 nm) non-zeolitic molecular
sieve containing an oxide of a lanthanide metal or an actinide
metal, scandium, yttrium, a Group 4 metal, a Group 5 metal or
combinations thereof. The metal-containing compound is introduced
to the non-zeolitic molecular sieve in the form of the
corresponding halide, sulphate, acetate, formate, propionate,
oxalate, maleate, fumarate, carboxylate, alkoxide, carbonyl,
nitrate or mixtures thereof. These small pore molecular sieve
compositions are claimed to be more stable even at high conversion
rates. These salts however are oxide-precursor salts and thus not
stable at the high temperature conditions of the MTO process.
Furthermore, selectivity to propylene is markedly low.
[0010] Molecular sieves in combination with matrix and binder
components for XTO processes are known in the art. Usually, the
binder and matrix are chemically neutral materials, typically
serving only to provide desired physical characteristics to the
catalyst composition. Usually, they have very little effect on
catalytic performance. These molecular sieve catalyst compositions
are formed by combining the molecular sieve and the matrix e.g. an
inorganic oxide such as alumina, titania, zirconia, silica or
silica-alumina with a binder, e.g. clay, to form a cohesive,
mechanically stable, attrition-resistant composite of the sieve,
matrix material and binder. In particular, the use of silica
(SiO.sub.2) as a binder/matrix material is well known in the art.
This solid is neutral and is selected when catalytic effects of the
binder/matrix are undesired. Typically, rare earth elements, which
are very expensive, are used in such catalyst composites.
[0011] Metal is introduced typically in the form of
oxides/oxide-precursor salts by ion-exchange or impregnation.
However, ion-exchange/impregnation potentially leads to the
modification of the acidity of catalytic sites throughout the whole
microporous structure of the molecular sieve. This could lead to
decreased catalytic activity. Metal oxides are chemically active
compounds. Without taking special precautions during pre-treatment
and catalyst formulation these compounds may partially damage the
molecular sieve pore structure. The proposed present invention is
very different from the prior art. It avoids the use of metal
oxides or unstable oxide-precursor salts. The combination of
molecular sieves with chemically inert metal salts which are stable
under the conversion process of the oxygenates to the olefins,
allows selectively modifying only the sites located on the external
surface and in the pore mouths of the molecular sieve. As a result,
the formation of side products is minimised and coke formation is
decreased without losses in the catalyst's activity.
[0012] Small pore silicoaluminophosphate (SAPO) molecular sieve
catalysts have excellent selectivity in oxygenates to light olefin
reactions. However, these catalysts have a tendency to deactivate
rapidly during the conversion of oxygenates to olefins and the
ratio C3/C2 could be improved. Therefore a need exists for methods
to decrease the rate of deactivation of small pore molecular sieve
catalysts during such conversions and to improve the yield of light
olefins and the C3/C2 ratio.
[0013] It has been discovered that addition of a small amount of
metal salts to a small pore MeAPO molecular sieve or optionally to
a composite molecular sieve containing a combination of small pore
MeAPO molecular sieve with medium or large pore crystalline
silicoaluminate, silicoaluminophosphate materials or
silicoaluminate mesoporous molecular sieves leads to substantial
increase of C3/C2 ratio, yield of light olefins and stability in
XTO than was obtained over the parent molecular sieve alone
(MeAPO).
[0014] Higher stability of the blended catalysts together with the
metal salt provides a possibility to operate at higher flow rate,
increase the catalyst on-stream time in XTO conversion reactor and
decrease the size of regeneration section or the frequency of
regeneration. (on-stream time is the time that a catalyst resides
in the conversion reactor and exhibits still sufficient catalytic
activity, before it has to be taken off-line for regeneration or
replacement)
[0015] Unexpectedly, this catalyst composite possesses reduced coke
selectivity in comparison with the weighted average of the
individual molecular sieves.
[0016] The excess of C4+ as well as ethylene can be converted to
propylene in an olefin cracking fixed bed reactor (OCP) in
combination with the XTO process. Ethylene can be recycled back in
XTO reactor or to the OCP reactor. The excess C4+ as well as the
ethylene can be converted to more propylene by recycling C4+ and
ethylene back to the XTO reactor. The catalyst blend allows the
conversion of organic compounds, C4+ and ethylene at the same
time.
[0017] Stated above, small pore MeAPO molecular sieves contain
8-membered rings as the largest pore aperture in the structure,
medium pore crystalline silicoaluminates contain 10-membered rings
as the largest pore aperture; large pore crystalline
silicoaluminates contain 12-membered rings as the largest pore
aperture. Stated above medium, large pore and mesoporous molecular
sieves have acidic properties, which are capable in catalysing the
formation of aromatic precursors from used feedstock.
[0018] In the XTO process the ethylene, propylene and higher
hydrocarbons are formed via a "carbon pool" mechanism (Dahl and
Kolboe 1994 Journal of Catalysis 149(2): 458-464; Dahl and Kolboe
1996 Journal of Catalysis 161(1): 304-309; Stocker 1999,
Microporous and Mesoporous Materials 29(1-2): 3-48). Ethylene,
propylene and C4+ olefins selectivities in XTO process are related
to the number of methyl groups attached to benzene rings trapped in
the nanocages. The product spectrum varies strongly with the pore
size of the catalytic material (shape selectivity), and when the
small pore SAPO-34 (chabasite structure) is used as catalyst the
hydrocarbon products are mostly ethene and propene, and some
substantially linear butenes, the only product molecules small
enough to escape with ease through the narrow pores.
[0019] It has been discovered that medium or large pore crystalline
silicoaluminate, silicoaluminophosphate materials or
silicoaluminate mesoporous molecular sieves play a role of a faster
in-situ supply for aromatic precursors for olefin production by the
carbon pool mechanism. One optional aspect of this invention is
in-situ on-purpose formation of some additional organic reaction
centers by adding to the MeAPO a small amount of acid co-catalyst
with larger pore opening than the MeAPO. These materials are
capable to produce a small amount of higher molecular weight
precursors that can enter into the pore system of the small pore
MeAPO where they are converted into the aromatics under XTO
conditions. These aromatics constitute the active centers for XTO
according to the carbon pool mechanism. These aromatics are trapped
by MeAPO micro porous system in a more optimum way without
formation of a lot of coke by-products. This allows an increased
catalyst stability and C3/C2 ratio.
[0020] Without being bonded by any theory, inventors think that an
optimum concentration of the methylbenzenes organic reaction
centers leads to higher light olefins production and to a slower
deactivation. However the olefin production is limited by diffusion
of heavy olefins out of the micropore system of MeAPO in which
usually methylbenzenes are trapped. Formation of the methylbenzenes
inside of MeAPO pore system requires a certain time and is
accompanied by coke formation. More coke formation in the small
pore MeAPO reduces the accessible pore volume and results in faster
loss of catalytic activity.
BRIEF SUMMARY OF THE INVENTION
[0021] The invention covers a catalyst composite comprising: [0022]
at least 0.5% by weight of at least one metal salt stable under XTO
conditions and [0023] at least 10% by weight of molecular sieve,
which comprises: [0024] 70 to 100% by weight of at least one small
pore aluminosilicate or metalloaluminophosphate (MeAPO) molecular
sieve selected from the group CHA, AEI, ERI, LEV or a mixture of
thereof and [0025] 0 to 30% by weight of at least one medium or
large pore molecular sieve selected from one or more of crystalline
silicoaluminates, silicoaluminophosphates or mesoporous
silicoaluminates.
[0026] Preferably, the composite comprises from 0.5 to 10% by
weight of at least one metal salt, more preferably from 1 to 10%.
The metal salt may comprise at least one metal from the following:
Zn, Co, Ca, Mg, Ga, Al, Cs, Sr, Ba, Sc, Sn and Li. Preferably, the
metal is Zn, Co, Ca, Mg. At least one of the anions of the metal
salt is advantageously selected from silicates, borates and
borosilicates.
[0027] Advantageously, the molecular sieves comprise 70 to 99.9% by
weight of the MeAPO molecular sieve and 0.01 to 30% by weight of
the medium or large pore molecular sieve. More advantageously, the
molecular sieves comprise 75 to 99.5% by weight of the MeAPO
molecular sieve and 0.5 to 25% by weight of the medium or large
pore molecular sieve. Most advantageously, the molecular sieves
comprise 85 to 99% by weight of the MeAPO molecular sieve and 1 to
15% by weight of the medium or large pore molecular sieve.
[0028] MFI, FER and MEL are the most preferable medium pore
crystalline silicoaluminates.
[0029] AEL is the most preferable medium pore
silicoaluminophosphate material.
[0030] FAU, MOR, LTL, MAZ, MWW and BEA are the most preferable
large pore crystalline silicoaluminates.
[0031] AFI is the most preferable large pore silicoaluminophosphate
materials,
[0032] MCM-41, SBA-15, SBA-16 are the most preferable mesoporous
molecular sieve.
[0033] MeAPO's have a three-dimensional microporous crystal
framework of PO.sub.2.sup.+, AlO.sub.2.sup.-, and MeO.sub.2
tetrahedral units. MeAPO molecular sieves having CHA (SAPO-34,
SAPO-44), LEV (SAPO-35), ERI (SAPO-17) or AEI (SAPO-18) structure
or mixture thereof are the most preferable. Silicon is the most
desirable metal in MeAPO.
[0034] According to another embodiment of the invention the MeAPO
molecular sieve has an empirical chemical composition on an
anhydrous basis, after synthesis and calcination, expressed by the
formula H.sub.xMe.sub.yAl.sub.2P.sub.kO.sub.2 in which,
y+z+k=1 [0035] x<=y [0036] y has a value ranging from 0.0008 to
0.4 and advantageously from 0.005 to 0.18 [0037] z has a value
ranging from 0.25 to 0.67 and advantageously from 0.38 to 0.55
[0038] k has a value ranging from 0.2 to 0.67 and advantageously
from 0.36 to 0.54
[0039] Advantageously said molecular sieve have predominantly plate
crystal morphology. Preferably said plate crystal morphology is
such as the width (W) and the thickness (T) are as follows:
W/T is >=10 and advantageously ranges from 10 to 100.
[0040] According to another embodiment of the invention the MeAPO
has been prepared by a method comprising:
a) forming a reaction mixture containing a texture influencing
agent (TIA), an organic templating agent (TEMP), at least a
reactive inorganic source of MeO.sub.2 essentially insoluble in the
TIA, reactive sources of Al.sub.2O.sub.3 and P.sub.2O.sub.5, b)
crystallizing the above reaction mixture thus formed until crystals
of the metalloaluminophosphate are formed, c) recovering a solid
reaction product, d) washing it with water to remove the TIA and e)
calcinating it to remove the organic template.
[0041] The catalyst composite can be obtained by introducing the
metal salt to the molecular sieve(s) by one of the following two
methods: [0042] During the formulation step of the catalyst by
mechanically blending the molecular sieve with the metal silicate
forming a precursor; [0043] Physical blending of the previously
formulated molecular sieve and the previously formulated metal
silicate in situ in the XTO and/or OCP reaction medium.
[0044] The present invention also relates to a process (hereunder
referred as "XTO process") for making an olefin product from an
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock wherein said oxygen-containing,
halogenide-containing or sulphur-containing organic feedstock is
contacted with the above catalyst composite (in the XTO reactor)
under conditions effective to convert at least a portion of the
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock to olefin products (the XTO reactor effluent). It
is desirable to have a substantially 100% conversion of the organic
compound in the XTO reactor. This conversion rate is adjusted by
optimization of the contact time and the frequency of regeneration
of the catalyst composite.
[0045] According to a specific embodiment the XTO reactor effluent
comprising light olefins and a heavy hydrocarbon fraction is sent
to a fractionation section to separate said light olefins from said
heavy hydrocarbon fraction; said heavy hydrocarbon fraction is
recycled in the XTO reactor at conditions effective to convert at
least a portion of said heavy hydrocarbon fraction to olefin
products.
[0046] With regards to said effluent of the XTO process, "light
olefins" means ethylene and propylene and the "heavy hydrocarbon
fraction" is defined herein as the fraction containing hydrocarbons
having a molecular weight greater than propane, which means
hydrocarbons having 4 carbon atoms or more and written as
C.sub.4.sup.+.
[0047] According to another embodiment of the invention said olefin
products (the effluent of the XTO) are fractionated to form a
stream comprising essentially ethylene and at least a part of said
stream is recycled in the XTO reactor to increase the propylene
production and then the flexibility of ethylene vs propylene
production.
[0048] According to another embodiment of the invention both
ethylene and the C4+ can be recycled in the XTO reactor.
[0049] The present invention also relates to a process (hereunder
referred as "combined XTO and OCP process") to make light olefins
from an oxygen-containing, halogenide-containing or
sulphur-containing organic feedstock comprising:
contacting said oxygen-containing, halogenide-containing or
sulphur-containing organic feedstock in the XTO reactor with the
above catalyst composite at conditions effective to convert at
least a portion of the feedstock to form an XTO reactor effluent
comprising light olefins and a heavy hydrocarbon fraction;
separating said light olefins from said heavy hydrocarbon fraction;
contacting said heavy hydrocarbon fraction in the OCP reactor at
conditions effective to convert at least a portion of said heavy
hydrocarbon fraction to light olefins. It is desirable to have a
substantially 100% conversion of the organic compound in the XTO
reactor. This conversion rate is adjusted by optimization of the
contact time and the frequency of regeneration of the catalyst.
DETAILED DESCRIPTION OF THE INVENTION
[0050] Regarding the small pore aluminosilicate and the small pore
metalloaluminophosphate (MeAPO), they are known per se. MeAPO are
described in U.S. Pat. No. 4,440,871, U.S. Pat. No. 6,207,872, U.S.
Pat. No. 6,540,970 and U.S. Pat. No. 6,303,534, the content of
which are enclosed in the present application. Preferably they have
essentially the structure SAPO-18 (AEI), SAPO-17(ERI),
SAPO-35(LEV), SAPO-34 (CHA) or SAPO-44 (CHA) or a mixture thereof.
In an advantageous embodiment the MeAPO molecular sieves have
essentially a structure CHA or AEI or a mixture thereof.
[0051] "Small pore" means typically having pore apertures defined
by ring sizes of no more than 8 tetrahedric atoms, preferably ring
sizes of 4, 6 or 8 tetrahedric atoms. Preferably, the average pore
size is less than about 0.5 nm.
[0052] About "essentially" referring to the CHA or AEI structure it
means that advantageously more than 80% by weight, preferably more
than 90%, of the MeAPO has the structure CHA or AEI or a mixture
thereof. About "essentially" referring to the SAPO-18, SAPO-34,
SAPO-17, SAPO-35 and SAPO-44 structure, it means that
advantageously more than 80% by weight, preferably more than 90%,
of the MeAPO has the structure SAPO-18, SAPO-34, SAPO-44, SAPO-17,
SAPO-35 or a mixture thereof.
[0053] Me is advantageously a metal selected from the group
consisting of silicon, germanium, magnesium, zinc, iron, cobalt,
nickel, manganese, chromium and mixtures thereof. Preferred metals
are silicon, magnesium and cobalt with silicon or germanium being
especially preferred.
[0054] The MeAPO could be also an intergrown phase of two MeAPO
having AEI and CHA framework types. They are described in U.S. Pat.
No. 7,067,095, U.S. Pat. No. 6,953,767 and U.S. Pat. No. 6,334,994,
the content of which are enclosed in the present application.
[0055] Before introduction of the metal salt promoter, other metals
such as Si, Co, Zn, Ge, Mg, Ca, Ba, Ni, Mo, Cr, Cu, Fe, Ga, Mn, Sn,
Ti may be introduced.
[0056] Regarding the MeAPO according to another embodiment of the
invention, the MeAPO molecular sieve has an empirical chemical
composition on an anhydrous basis, after synthesis and calcination,
expressed by the formula H.sub.xMe.sub.yAl.sub.zP.sub.kO.sub.2 in
which,
y+z+k=1 [0057] x<=y [0058] y has a value ranging from 0.0008 to
0.4 and advantageously from 0.005 to 0.18 [0059] z has a value
ranging from 0.25 to 0.67 and advantageously from 0.38 to 0.55
[0060] k has a value ranging from 0.2 to 0.67 and advantageously
from 0.36 to 0.54
[0061] In an advantageous embodiment y has a value ranging from
0.005 to 0.18, z has a value ranging from 0.38 to 0.55 and k has a
value ranging from 0.36 to 0.54.
[0062] In a first preferred embodiment y has a value ranging from
0.005 to 0.16, z has a value ranging from 0.39 to 0.55 and k has a
value ranging from 0.37 to 0.54.
[0063] In a second preferred embodiment y has a value ranging from
0.011 to 0.16, z has a value ranging from 0.39 to 0.55 and k has a
value ranging from 0.37 to 0.54.
[0064] In a third preferred embodiment y has a value ranging from
0.011 to 0.14, z has a value ranging from 0.40 to 0.55 and k has a
value ranging from 0.38 to 0.54.
[0065] In an advantageous embodiment the MeAPO molecular sieves
have essentially a structure CHA or AEI or a mixture thereof.
Preferably they have essentially the structure SAPO 18 or SAPO 34
or a mixture thereof.
[0066] Advantageously said molecular sieve have predominantly a
plate crystal morphology. Preferably said plate crystal morphology
is such that the width (W) and the thickness (T) are as
follows:
W/T is >=10 and advantageously ranges from 10 to 100.
[0067] In a preferred embodiment T is <=0.15 .mu.m, more
desirably <=0.10 .mu.m, more desirably <=0.08 .mu.m,
advantageously ranges from 0.01 to 0.07 .mu.m and preferably from
0.04 to 0.07 .mu.m.
[0068] About the plate crystal morphology, said plates have
advantageously the shape of a simple polygon comprised in a square.
The square's length is named W. The MeAPO molecular sieves have
predominantly a plate crystal morphology. By predominantly is meant
advantageously greater than 50% of the crystals. Preferably at
least 70% of the crystals have a plate morphology and most
preferably at least 90% of the crystals have a plate morphology.
About "essentially" referring to the CHA or AEI structure it means
that advantageously more than 80% by weight, preferably more than
90%, of the MeAPO of the invention has the structure CHA or AEI or
a mixture thereof. About "essentially" referring to the SAPO-18,
SAPO-34 and SAPO-44 structure it means that advantageously more
than 80% by weight, preferably more than 90%, of the MeAPO has the
structure SAPO 18 or SAPO 34 or a mixture thereof.
[0069] With regards to a method to make said MeAPO, it can be made
by a method which comprises:
a) forming a reaction mixture containing a texture influencing
agent (TIA), an organic templating agent (TEMP), at least a
reactive inorganic source of MeO.sub.2 essentially insoluble in the
TIA, reactive sources of Al.sub.2O.sub.3 and P.sub.2O.sub.5, said
reaction mixture having a composition expressed in terms of molar
oxide ratios of: TEMP/Al.sub.2O.sub.3=0.3-5, more desirable 0.5-2
MeO.sub.2/Al.sub.2O.sub.3=0.005-2.0, more desirable 0.022-0.8
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.5-2, more desirable 0.8-1.2
TIA/Al.sub.2O.sub.3=3-30, more desirable 6-20 b) crystallizing the
above reaction mixture thus formed until crystals of the
metalloaluminophosphate are formed, c) recovering a solid reaction
product, d) washing it with water to remove the TIA and e)
calcinating it to remove the organic template.
[0070] In an advantageous embodiment TEMP/Al.sub.2O.sub.3=0.5-2;
MeO.sub.2/Al.sub.2O.sub.3=0.022-0.8;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0071] In a first preferred embodiment TEMP/Al.sub.2O.sub.3=0.5-2;
MeO.sub.2/Al.sub.2O.sub.3=0.022-0.7;
P.sub.2O.sub.51Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0072] In a second preferred embodiment TEMP/Al.sub.2O.sub.3=0.7-2;
MeO.sub.2/Al.sub.2O.sub.3=0.05-0.7;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0073] In a third preferred embodiment TEMP/Al.sub.2O.sub.3=0.7-2;
MeO.sub.2/Al.sub.2O.sub.3=0.05-0.6;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0074] With regards to the TIA, mention may be made, by way of
example, of 1,2-propanediol, 1,3-propanediol, methanol, ethanol,
propanol, isopropanol, butanol, glycerol or ethylene glycol.
[0075] With regards to the organic templating agent, it can be any
of those heretofore proposed for use in the synthesis of
conventional zeolitic aluminosilicates and microporous
aluminophosphates. In general these compounds contain elements of
Group VA of the Periodic Table of Elements, particularly nitrogen,
phosphorus, arsenic and antimony, preferably N or P and most
preferably N, which compounds also contain at least one alkyl or
aryl group having from 1 to 8 carbon atoms. Particularly preferred
nitrogen-containing compounds for use as templating agents are the
amines and quaternary ammonium compounds, the latter being
represented generally by the formula R.sub.4N.sup.+ wherein each R
is an alkyl or aryl group containing from 1 to 8 carbon atoms.
Polymeric quaternary ammonium salts such as
[(C.sub.14H.sub.32N.sub.2)(OH).sub.2].sub.x wherein "x" has a value
of at least 2 are also suitably employed. Both mono-, di and
tri-amines are advantageously utilized, either alone or in
combination with a quaternary ammonium compound or other templating
compound. Representative templating agents include
tetramethylammonium, tetraethylammonium, tetrapropylammonium or
tetrabutylammonium cations; di-n-propylamine, tripropylamine,
triethylamine; diethylamine, triethanolamine; piperidine;
morpholine; cyclohexylamine; 2-methylpyridine;
N,N-dimethylbenzylamine; N,N-diethylethanolamine;
dicyclohexylamine; N,N-dimethylethanolamine; choline;
N,N'-dimethylpiperazine; 1,4-diazabicyclo(2,2,2)octane;
N-methyldiethanolamine, N-methylethanolamine; N-methylpiperidine;
3-methylpiperidine; N-methylcyclohexylamine; 3-methylpyridine;
4-methylpyridine; quinuclidine;
N,N'-dimethyl-1,4-diazabicyclo(2,2,2)octane ion; di-n-butylamine,
neopentylamine; di-n-pentylamine; isopropylamine; t-butylamine;
ethylenediamine; pyrrolidine; and 2-imidazolidone. Advantageously
organic templating agent is selected among tetraethylammonium
hydroxide (TEAOH), diisopropylethylamine (DPEA), tetraethyl
ammonium salts, cyclopentylamine, aminomethyl cyclohexane,
piperidine, triethylamine, diethylamine, cyclohexylamine, triethyl
hydroxyethylamine, morpholine, dipropylamine, pyridine,
isopropylamine di-n-propylamine, tetra-n-butylammonium hydroxide,
diisopropylamine, di-n-propylamine, n-butylethylamine,
di-n-butylamine, and di-n-pentylamine and combinations thereof.
Preferably the template, is a tetraethyl ammonium compound selected
from the group of tetraethyl ammonium hydroxide (TEAOH), tetraethyl
ammonium phosphate, tetraethyl ammonium fluoride, tetraethyl
ammonium bromide, tetraethyl ammonium chloride, tetraethyl ammonium
acetate. Most preferably, the template is tetraethyl ammonium
hydroxide.
[0076] With regards to the reactive inorganic source of MeO.sub.2
essentially insoluble in the TIA and relating to silicon,
non-limiting examples of useful inorganic silicon source materials
non-soluble in alcohols include, fumed silica, aerosol, pyrogenic
silica, precipitated silica and silica gel.
[0077] With regards to the reactive sources of Al.sub.2O.sub.3, it
can be any aluminum species capable of being dispersed or dissolved
in an aqueous synthesis solution. Useful sources of alumina are one
or more sources selected from the group consisting of the
following: hydrated alumina, organo alumina, in particularly
Al(OiPr).sub.3, pseudo-boehmite, aluminum hydroxide, colloidal
alumina, aluminium halides, aluminium carboxylates, aluminium
sulfates and mixtures thereof.
[0078] With regards to the reactive sources of P.sub.2O.sub.5, it
can be one or more sources selected from the group consisting of
phosphoric acid; organic phosphates, such as triethyl phosphate,
tetraethyl-ammonium phosphate; aluminophosphates; and mixtures
thereof. The phosphorous source should also be capable of being
dispersed or dissolved in an alcohol synthesis solution.
[0079] These MeAPO can be prepared by the usual methods of the
molecular sieves synthesis technology provided it is in accordance
with the above-cited ratios. The reaction mixture is in the form of
a gel. The ratios MeO.sub.2/Al.sub.2O.sub.3 and
P.sub.2O.sub.5/Al.sub.2O.sub.3 are selected among the above
described advantageous and preferred ratios and are in accordance
with the advantageous and preferred y, z and k described above. By
way of example to make a MeAPO having the y, z and k according to
the second preferred embodiment one has to use the ratios of the
ingredients according to the second preferred embodiment of the
method to make said MeAPO.
[0080] With regards to the step b), the reaction mixture obtained
by mixing the reactive sources of alumina, MeO.sub.2, phosphorus,
organic templating agent and TIA is submitted to autogenous
pressure and elevated temperature. The reaction mixture is heated
up to the crystallization temperature that may range from about
120.degree. C. to 250.degree. C., preferably from 130.degree. C. to
225.degree. C., most preferably from 150.degree. C. to 200.degree.
C. Heating up to the crystallization temperature is typically
carried out for a period of time ranging from about 0.5 to about 16
hours, preferably from about 1 to 12 hours, most preferably from
about 2 to 9 hours. The temperature may be increased stepwise or
continuously. However, continuous heating is preferred. The
reaction mixture may be kept static or agitated by means of
tumbling or stirring the reaction vessel during hydrothermal
treatment. Preferably, the reaction mixture is tumbled or stirred,
most preferably stirred. The temperature is then maintained at the
crystallization temperature for a period of time ranging from 2 to
200 hours. Heat and agitation is applied for a period of time
effective to form crystalline product. In a specific embodiment,
the reaction mixture is kept at the crystallization temperature for
a period of from 16 to 96 hours.
[0081] With regards to the step c), the usual means can be used.
Typically, the crystalline molecular sieve product is formed as a
slurry and can be recovered by standard means, such as by
sedimentation, centrifugation or filtration.
[0082] With regards to the step d), the separated molecular sieve
product is washed, recovered by sedimentation, centrifugation or
filtration and dried.
[0083] With regards to the step e), calcination of molecular sieves
is known per se. As a result of the molecular sieve crystallization
process, the recovered molecular sieve contains within its pores at
least a portion of the template used. In a preferred embodiment,
activation is performed in such a manner that the template is
removed from the molecular sieve, leaving active catalytic sites
with the microporous channels of the molecular sieve open for
contact with a feedstock. The activation process is typically
accomplished by calcining, or essentially heating the molecular
sieve comprising the template at a temperature of from 200 to
800.degree. C. in the presence of an oxygen-containing gas. In some
cases, it may be desirable to heat the molecular sieve in an
environment having a low oxygen concentration. This type of process
can be used for partial or complete removal of the template from
the intracrystalline pore system.
[0084] Additionally, if during the synthesis alkaline or alkaline
earth metals have been used, the molecular sieve might be subjected
to an ion-exchange step. Conventionally, ion-exchange is done in
aqueous solutions using ammonium salts or inorganic acids.
[0085] Regarding the MeAPO according to another embodiment of the
invention the MeAPO has been prepared by a method comprising:
a) forming a reaction mixture containing a texture influencing
agent (TIA), an organic templating agent (TEMP), at least a
reactive inorganic source of MeO.sub.2 essentially insoluble in the
TIA, reactive sources of Al.sub.2O.sub.3 and P.sub.2O.sub.5, b)
crystallizing the above reaction mixture thus formed until crystals
of the metalloaluminophosphate are formed, c) recovering a solid
reaction product, d) washing it with water to remove the TIA and e)
calcinating it to remove the organic template.
[0086] In a usual embodiment said reaction mixture has a
composition expressed in terms of molar oxide ratios of:
TEMP/Al.sub.2O.sub.3=0.3-5, more desirable 0.5-2
MeO.sub.2/Al.sub.2O.sub.3=0.005-2.0, more desirable 0.022-0.8
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.5-2, more desirable 0.8-1.2
TIA/Al.sub.2O.sub.3=3-30, more desirable 6-20
[0087] In an advantageous embodiment TEMP/Al.sub.2O.sub.3=0.5-2;
MeO.sub.2/Al.sub.2O.sub.3=0.022-0.8;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0088] In a first preferred embodiment TEMP/Al.sub.2O.sub.3=0.5-2;
MeO.sub.2/Al.sub.2O.sub.3=0.022-0.7;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0089] In a second preferred embodiment TEMP/Al.sub.2O.sub.3=0.7-2;
MeO.sub.2/Al.sub.2O.sub.3=0.05-0.7;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0090] In a third preferred embodiment TEMP/Al.sub.2O.sub.3=0.7-2;
MeO.sub.2/Al.sub.2O.sub.3=0.05-0.6;
P.sub.2O.sub.5/Al.sub.2O.sub.3=0.8-1.2 and
TIA/Al.sub.2O.sub.3=6-20.
[0091] In a usual embodiment the metalloaluminophosphate (MeAPO)
molecular sieves made with the above method have a lamellar crystal
morphology having an empirical chemical composition on an anhydrous
basis, after synthesis and calcination, expressed by the formula
H.sub.xMe.sub.yAl.sub.zP.sub.kO.sub.2 wherein,
y+z+k=1
x<=y y has a value ranging from 0.0008 to 0.4 and more desirable
from 0.005 to 0.18 z has a value ranging from 0.25 to 0.67 and more
desirable from 0.38 to 0.55 k has a value ranging from 0.2 to 0.67
and more desirable from 0.36 to 0.54 said molecular sieve having
predominantly a plate crystal morphology.
[0092] The values of y, z and k in the usual embodiment are
obtained by the ratios of the ingredients described in the usual
embodiment method above described.
[0093] In an advantageous embodiment y has a value ranging from
0.005 to 0.18, z has a value ranging from 0.38 to 0.55 and k has a
value ranging from 0.36 to 0.54.
[0094] In a first preferred embodiment y has a value ranging from
0.005 to 0.16, z has a value ranging from 0.39 to 0.55 and k has a
value ranging from 0.37 to 0.54.
[0095] In a second preferred embodiment y has a value ranging from
0.011 to 0.16, z has a value ranging from 0.39 to 0.55 and k has a
value ranging from 0.37 to 0.54.
[0096] In a third preferred embodiment y has a value ranging from
0.011 to 0.14, z has a value ranging from 0.40 to 0.55 and k has a
value ranging from 0.38 to 0.54.
[0097] The values of y, z and k in the advantageous, first, second
and third embodiments described above are obtained by using the
ingredients ratios described respectively in the advantageous,
first, second and third embodiments of the method described
above.
[0098] All the conditions already cited above relating to the
synthesis of the MeAPO apply to said other embodiment of the
invention.
[0099] The Catalyst Composite May Also Comprise One or More Medium
or Large Pore Molecular Sieves.
[0100] According to an embodiment of the invention, the catalyst
composite may comprise a mixture of MeAPO molecular sieves and
medium or large pore crystalline silicoaluminates,
silicoaluminophosphates or mesoporous silicoaluminates. Among the
products, which may be used for the molecular sieves of medium or
large pore size, these include MFI, MEL, FER, MOR, FAU, BEA, AEL,
AFI, LTL, MAZ, MWW and MCM-41. Preferably, they have pore apertures
defined by ring sizes of 10 or more, preferably up to 12
tetrahedric atoms. More preferably, they have pore apertures
defined by ring sizes of 10 or more, preferably up to 12
tetrahedric atoms and 10 or 12 oxygen atoms. Even more preferably,
they have pore sizes greater than 0.5 nm. Most preferably they are
of the MFI (ZSM-5 or silicalite), FAU, MOR, MEL or FER type.
Zeolites may be pretreated by various ways, modified by P, by
alkali, alkali-earth and/or rare-earth metals. Pretreatment may be
carried out by acid leaching, steaming or combination thereof.
[0101] Advantageously (A) is a crystalline silicate of the MFI
family which may be a zeolite, a silicalite or any other silicate
in that family or the MEL family which may be a zeolite or any
other silicate in that family. Examples of MFI silicates are ZSM-5
and silicalite. An example of an MEL zeolite is ZSM-11 which is
known in the art. Other examples are Boralite D and silicalite-2 as
described by the International Zeolite Association (Atlas of
Zeolite Structure Types, 1987, Butterworths). Preferably, the
medium or large pore molecular sieve is one or more of ZSM-5, a
silicalite, a ferrierite, a P-ZSM-5, a P-silicalite, or a
P-ferrierite.
[0102] Crystalline silicates are microporous crystalline inorganic
polymers based on a framework of XO.sub.4 tetrahydra linked to each
other by sharing of oxygen ions, where X may be trivalent (e.g. Al,
B, . . . ) or tetravalent (e.g. Ge, Si, . . . ). The crystal
structure of a crystalline silicate is defined by the specific
order in which a network of tetrahedral units are linked together.
The size of the crystalline silicate pore openings is determined by
the number of tetrahedral units, or, alternatively, oxygen atoms,
required to form the pores and the nature of the cations that are
present in the pores. They possess a unique combination of the
following properties: high internal surface area; uniform pores
with one or more discrete sizes; ion exchangeability; good thermal
stability; and ability to adsorb organic compounds. Since the pores
of these crystalline silicates are similar in size to many organic
molecules of practical interest, they control the ingress and
egress of reactants and products, resulting in particular
selectivity in catalytic reactions. Crystalline silicates with the
MFI structure possess a bi-directional intersecting pore system
with the following pore diameters: a straight channel along [010]:
0.53-0.56 nm and a sinusoidal channel along [100]: 0.51-0.55 nm.
Crystalline silicates with the MEL structure possess a
bi-directional intersecting straight pore system with straight
channels along [100] having pore diameters of 0.53-0.54 nm.
[0103] The MFI or MEL catalyst having a high silicon/aluminum
atomic ratio may be manufactured by removing aluminum from a
commercially available crystalline silicate. A typical commercially
available silicalite has a silicon/aluminum atomic ratio of around
120 to 300. The commercially available MFI crystalline silicate may
be modified by a steaming process which reduces the tetrahedral
aluminum in the crystalline silicate framework and converts the
aluminum atoms into octahedral aluminum in the form of amorphous
alumina. Although in the steaming step aluminum atoms are
chemically removed from the crystalline silicate framework
structure to form alumina particles, those particles cause partial
obstruction of the pores or channels in the framework. Accordingly,
following the steaming step, the crystalline silicate is subjected
to an extraction step wherein amorphous alumina is removed from the
pores and the micropore volume is, at least partially, recovered.
The physical removal, by a leaching step, of the amorphous alumina
from the pores by the formation of a water-soluble aluminum complex
yields the overall effect of de-alumination of the MFI crystalline
silicate. In this way by removing aluminum from the MFI crystalline
silicate framework and then removing alumina formed therefrom from
the pores, the process aims at achieving a substantially
homogeneous de-alumination throughout the whole pore surfaces of
the catalyst. This reduces the acidity of the catalyst and thereby
reduces the occurrence of hydrogen transfer reactions in the
cracking process. The framework silicon/aluminum ratio may be
increased by this process to a value of at least about 180,
preferably from about 180 to 1000, more preferably at least 200,
yet more preferably at least 300 and most preferably around
480.
[0104] Regarding the mixture of the medium/large pore molecular
sieve and MeAPO, if used, it can be made by co-synthesis procedure
(synthesis of MeAPO-(A) composites materials) optionally followed
by formulation into a catalyst. In another embodiment it can be
formulated into a catalyst by combining with other materials that
provide additional hardness or catalytic activity to the finished
catalyst product. Materials, which can be blended with the mixture
of medium/large pore molecular sieve and MeAPO can be various inert
or catalytically active materials, or various binder materials.
These materials include compositions such as kaolin and other
clays, various forms of rare earth metals, alumina or alumina sol,
titania, zirconia, quartz, silica or silica sol, and mixtures
thereof. These components are effective in densifying the catalyst
and increasing the strength of the formulated catalyst. The
catalyst may be formulated into pellets, spheres, extruded into
other shapes, or formed into a spray-dried powder.
[0105] The mixture of the medium/large pore molecular sieve and
MeAPO can also be made by co-formulation procedure (blending of the
separately synthesized medium/large pore molecular sieve and MeAPO)
optionally followed by combination with a binder. This mixture of
medium/large pore molecular sieve and MeAPO can be used as itself
as a catalyst. In another embodiment it can be formulated into a
catalyst by combining with other materials that provide additional
hardness or catalytic activity to the finished catalyst product.
The details are the same as above.
[0106] The mixture of the medium/large pore molecular sieve and
MeAPO can also be made by blending of MeAPO and the medium/large
pore molecular sieve, wherein at least one of the two components
has been combined with a binder prior to the blending. The obtained
mixture can be used as itself as a catalyst. In another embodiment
it can be formulated into a catalyst by combining with other
materials that provide additional hardness or catalytic activity to
the finished catalyst product. The details are the same as
above.
[0107] Preferably, the molecular sieves combination is a
combination of SAPO-34, SAPO-44 or SAPO-18 with a ZSM-5, a
silicalite, a ferrierite or a P-ZSM-5, a P-silicalite, a
P-ferrierite.
[0108] The presence of the medium and large pore molecular sieve is
optional. Advantageously, the molecular sieves comprise 70 to 99.9%
by weight of the MeAPO molecular sieve and 0.01 to 30% by weight of
the medium or large pore molecular sieve. More advantageously, the
molecular sieves comprise 75 to 99.5% by weight of the MeAPO
molecular sieve and 0.5 to 25% by weight of the medium or large
pore molecular sieve. Most advantageously, the molecular sieves
comprise 85 to 99% by weight of the MeAPO molecular sieve and 1 to
15% by weight of the medium or large pore molecular sieve.
[0109] According to an embodiment, the molecular sieves consist
essentially of the MeAPO molecular sieve.
[0110] Regarding the metal salt, the catalyst composite further
comprises at least 0.5% by weight of a metal salt, which,
advantageously, contains a polyvalent metal or a metal possessing a
large hydration diameter. More preferably, the content of metal
salt in the catalyst composite ranges from 0.5 up to 95% by weight
of the composite, more preferably 5 to 80% by weight. Preferably,
the metal in the metal salt is selected from Ga, Al, Cs, Sr, Mg,
Ca, Ba, Sc, Sn, Li, Co, Zn, more preferably from among Zn, Co, Ca,
Mg. Without wishing to be bound by theory, the ion exchange
reaction with these ions is very slow. For example, calcium must
lose many of the strongly coordinated water molecules in order to
enter the structure. Therefore, most of these ions cannot penetrate
inside of the micropores and selectively poison the external
surface. The specificity of the catalyst can thereby be better
controlled.
[0111] The metal salt composition comprises at least one inorganic
anion selected preferably from the group of silicates, borates and
borosilicates. Suitable silicate anions include SiO.sub.3.sup.2-,
SiO.sub.4.sup.4-, Si.sub.2O.sub.7.sup.6- and so on. Suitable borate
anions include BO.sub.2.sup.-, BO.sub.3.sup.2-,
B.sub.2O.sub.5.sup.4-, B.sub.4O.sub.7.sup.2-,
B.sub.6O.sub.11.sup.4-, B.sub.10O.sub.19.sup.8- and so on.
[0112] Bi-, tri- and poly-metal silicates, borates and
borosilicates containing one, two or more metals selected from the
list above can be used too.
[0113] The metal salt may also comprise other anions besides
silicate, borates and borosilicates.
[0114] In an embodiment of the invention, a mixture of metal
borates and metal silicates can be used.
[0115] The metal salt according to the invention are stable under
the XTO conditions of the reactor i.e. at a temperature of 200 to
700.degree. C. and at a pressure of 5 kPa to 5 MPa, thus acting as
a catalyst promoter. "Stable" refers to the fact that the elements
constituting the metal salt and having a positive valence remain
part of the catalyst under pre-treatment conditions, XTO and
regeneration conditions. This means that unlike metal oxides, the
metal salts can be dehydrated, they may change morphology and even
change colour under the conditions of the XTO reactor, yet the
inorganic anion would still be essentially present as such.
Furthermore, without wishing to be bound by theory, it is thought
that the presence of one or more of silicate, borate and
borosilicate anions further improves the catalytic properties of
the catalyst composite.
[0116] Examples of suitable metal salt promoters include
Mg.sub.2B.sub.2O.sub.5.H.sub.2O, CaMgB.sub.6O.sub.11.6H.sub.2O
(hydroboracite), Ca.sub.2B.sub.6O.sub.11.5H.sub.2O (colemanite),
Ca.sub.4B.sub.10O.sub.19.7H.sub.2O, Mg(BO.sub.2).8H.sub.2O,
Ca(BO.sub.2).2H.sub.2O, BaB.sub.6O.sub.10.4H.sub.2O,
CaSi.sub.6O.sub.17(OH).sub.2 (Xonotlite),
CaMg(Si.sub.2O.sub.6).sub.x, Mg.sub.2(Si.sub.2O.sub.6).sub.x,
CaAl.sub.2Si.sub.2O.sub.8 and mixtures thereof.
[0117] The preferred catalyst promoter is a calcium silicate with a
very open and accessible pore structure. An even more preferred
catalyst promoter comprises a synthetic crystalline hydrated
calcium silicate having a chemical composition of
Ca.sub.6Si.sub.6O.sub.17(OH).sub.2 which corresponds to the known
mineral xonotlite (having a molecular formula
6CaO.6SiO.sub.2.H.sub.2O).
[0118] Generally, a synthetic hydrated calcium silicate is
synthesised hydrothermally under autogeneous pressure. A
particularly preferred synthetic hydrated calcium silicate is
available in commerce from the company Promat of Ratingen in
Germany under the trade name Promaxon.
[0119] In order to demonstrate the thermal stability of xonotlite,
and therefore the applicability of xonotlite as a catalyst promoter
in MTO processes, commercial xonotlite sold under the trade name
Promaxon D was calcined in ambient air at a relative humidity of
about 50% at 650.degree. C. for a period of 24 hours. The initial
xonotlite had a crystalline phase
Ca.sub.6Si.sub.6O.sub.17(OH).sub.2 with a BET surface area of 51
m.sup.2/gram and a pore volume (of less than 100 nanometres) of
0.35 ml/gram. After calcination at 650.degree. C., the carrier
retained its crystallinity, which corresponds to that of xonotlite.
Thus after a 24 hour calcination at 650.degree. C., the crystalline
phase still comprised xonotlite
(Ca.sub.6Si.sub.6O.sub.17(OH).sub.2) with a BET surface area of
47.4 m.sup.2/gram and a pore volume (less than 100 nanometres) of
0.30 ml/gram.
[0120] Before mixing with the molecular sieve said metal salt may
be modified by calcination, steaming, ion-exchange, impregnation,
or phosphatation. Said metal salt may be an individual compound or
may be a part of mixed compounds, for example mixed with mineral,
natural or chemical fertilizer.
[0121] The Metal Salt and Molecular Sieve(s) are Blended Together
to Form the Catalyst Composite of the Invention.
[0122] The metal salt can be brought into contact with the
molecular sieve by a co-formulation procedure or in situ blending
in the reaction medium prior to the XTO process. Said contact can
be realised by mechanically blending the molecular sieves with the
metal salt. This can be carried out via any known blending method.
Blending can last for a period of time starting from 1 minute up to
24 hours, preferably from 1 min to 10 hours. If not carried out in
the XTO reactor in situ, it can be carried out in a batchwise mixer
or in a continuous process, such as in an extruder e.g. a single or
twin screw extruder at a temperature of from 20 to 300.degree. C.
under vacuum or elevated pressure. Said contact may be performed in
an aqueous or non-aqueous medium. Prior to the formulation step,
other compounds that aid the formulation may be added, like
thickening agents or polyelectrolytes that improve the cohesion,
dispersion and flowing properties of the precursor. In case of
extrusion, rotating granulation or pelletisng a rather dry (low
water content) paste-like precursor is prepared. In case of
oil-drop or spray-drying a rather liquid (high water content) is
prepared. In another embodiment, the contact is carried out in the
presence of phosphorus containing compounds. In a particular
embodiment, the contact is carried out in the aqueous medium,
preferably at a pH lower than 5, more preferably lower than 3.
[0123] Either prior to, after or simultaneously with the
formulation step to form the composite, other components may be
optionally blended with the molecular sieve. In a particular
embodiment, the molecular sieve can be combined with other
materials that provide additional hardness or catalytic activity to
the finished catalyst product. Materials, which can be blended with
the molecular sieve, can be various inert or catalytically active
matrix materials and/or various binder materials. Such materials
include clays, silica and/or metal oxides such as alumina. The
latter is either naturally occurring or in the form of gelatinous
precipitates or gels including mixtures of silica and metal oxides.
In an embodiment, some binder materials can also serve as diluents
in order to control the rate of conversion from feed to products
and consequently improve selectivity. According to one embodiment,
the binders also improve the crush strength of the catalyst under
industrial operating conditions.
[0124] Naturally occurring clays, which can be used as binder, are
for example clays from the kaolin family or montmorillonite family.
Such clays can be used in the raw state as mined or they can be
subjected to various treatments before use, such as calcination,
acid treatment or chemical modification.
[0125] In addition to the foregoing, other materials, which can be
included in the catalyst composite of the invention, include
various forms of metal phosphates and sulphates (wherein the metal
is chosen from one or more of Ca, Ga, Al, Ca, Ce, In, Cs, Sr, Mg,
Ba, Sc, Sn, Li, Zn, Co, Mo, Mn, Ni, Fe, Cu, Cr, Ti and V), alumina
or alumina sol, titania, zirconia, quartz, silica or silica sol,
and mixtures thereof. Examples of possible phospates include
amorphous calcium phosphate, monocalcium phosphate, dicalcium
phosphate, dicalcium phosphate dehydrate, .alpha.- or
.beta.-tricalcium phosphate, octacalcium phosphate, hydroxyapatite
etc.
[0126] Examples of possibly binary oxide binder compositions
include, silica-alumina, silica magnesia, silica-zirconia,
silica-thoria, silica-beryllia, silica-titania, calcium-alumina.
Examples of ternary binder compositions include for instance
calcium-silica-alumina or silica-alumina-zirconia.
[0127] These components are effective in increasing the density of
the catalyst and increasing the strength of the formulated
catalyst. The catalyst may be formulated into pellets, spheres,
extruded into other shapes, or formed into spray-dried particles.
Generally, the size of the catalyst particles can vary from about
20 to 5,000,000 .mu.m. In general pellets, spheres and extrudates
are employed in fixed bed reactors and exhibit a particle size of
from about 0.5 mm to 5 mm. In general spray-dried particles are
used in fluidised bed reactors, which exhibit a particle size of
from about 20 to 200 .mu.m. In particular, spheres are employed in
moving bed reactors, which exhibit a size from about 0.5 to 5 mm.
Spheres can be made in rotating granulator or by oil-drop methods.
The crystal size of the molecular sieve contained in the catalyst
composite is preferably less than about 10 .mu.m, more preferably
less than about 5 .mu.m and most preferably less than about 4
.mu.m. The amount of molecular sieve, which is contained in the
final catalyst composite ranges from 10 to 99.5% by weight of the
total catalyst composite, preferably 20 to 80% by weight.
[0128] According to another embodiment, non-modified molecular
sieves were first formulated with a binder and matrix materials and
then modified with phosphorous and alkaline earth metal
silicates.
[0129] According to a further particular embodiment, molecular
sieves were optionally dealuminated and then modified with
phosphorous during the formulation step. Introduction of the
alkaline earth metal silicate can be performed during the
formulation step or on the formulated solid.
[0130] According to a preferred embodiment, molecular sieves were
first optionally dealuminated and modified with phosphorous and
then formulated. Introduction of the metal is performed
simultaneously with the phosphorous modification step and/or on the
already formulated catalyst.
[0131] After physically blending the two components together, the
catalyst composite may undergo further treatments including further
steaming, leaching, washing, drying, calcination, impregnations and
ion exchanging steps. If a zeolite is present, it can be modified
with phosphorus prior to or after the step of introducing the metal
salt to the molecular sieve.
[0132] With regards to the XTO process, the catalyst composite
comprising the molecular sieves and metal salt according to the
invention is particularly suited for the catalytic conversion of
oxygen-containing, halogenide-containing or sulphur-containing
organic compounds to hydrocarbons. Accordingly, the present
invention also relates to a method for making an olefin product
from an oxygen-containing, halogenide-containing or
sulphur-containing organic feedstock wherein said
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock is contacted with the above catalyst composite
under conditions effective to convert the oxygen-containing,
halogenide-containing or sulphur-containing organic feedstock to
olefin products (the effluent of the XTO). Said effluent comprises
light olefins and a heavy hydrocarbon fraction.
[0133] In this process a feedstock containing an oxygen-containing,
halogenide-containing or sulphur-containing organic compound
contacts the above described catalyst composite in a reaction zone
of a reactor at conditions effective to produce light olefins,
particularly ethylene and propylene. Typically, the
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock is contacted with the catalyst composite when the
oxygen-containing, halogenide-containing or sulphur-containing
organic compounds are in vapour phase. Alternately, the process may
be carried out in a liquid or a mixed vapour/liquid phase. In this
process, converting oxygen-containing, halogenide-containing or
sulphur-containing organic compounds, olefins can generally be
produced at a wide range of temperatures. An effective operating
temperature range can be from about 200.degree. C. to 700.degree.
C. At the lower end of the temperature range, the formation of the
desired olefin products may become markedly slow. At the upper end
of the temperature range, the process may not form an optimum
amount of product. An operating temperature of at least 300.degree.
C., and up to 575.degree. C. is preferred.
[0134] The pressure also may vary over a wide range. Preferred
pressures are in the range of about 5 kPa to about 5 MPa, with the
most preferred range being of from about 50 kPa to about 0.5 MPa.
The foregoing pressures refer to the partial pressure of the
oxygen-containing, halogenide-containing, sulphur-containing
organic compounds and/or mixtures thereof.
[0135] The process can be carried out in any system using a variety
of transport beds, although a fixed bed or moving bed system could
be used. Advantageously a fluidized bed is used. It is particularly
desirable to operate the reaction process at high space velocities.
The process can be conducted in a single reaction zone or a number
of reaction zones arranged in series or in parallel. Any standard
commercial scale reactor system can be used, for example fixed bed,
fluidised or moving bed systems. After a certain time on-stream the
catalyst needs to be regenerated. This regeneration can be carried
out in a separate reactor or in the same reactor. In case of a
moving bed or fluidised bed reactor, a part of the catalyst is
continuously or intermittently withdrawn from the conversion
reactor and sent to a second reactor for regeneration. After the
regeneration, the regenerated catalyst is continuously or
intermittently sent back to the conversion reactor. In case of
fixed bed reactor the reactor is taken off-line for regeneration.
Generally this requires a second spare reactor that can take over
the conversion into light olefins. After regeneration the fixed bed
reactor is in stand-by until the spare reactor needs regeneration
and the regenerated reactor takes over the conversion. Regeneration
is carried out by injecting an oxygen-containing stream over the
catalyst at sufficiently high temperature to burn the deposited
coke on the catalyst. The commercial scale reactor systems can be
operated at a weight hourly space velocity (WHSV) of from 0.1
hr.sup.-1 to 1000 hr.sup.-1.
[0136] One or more inert diluents may be present in the feedstock,
for example, in an amount of from 1 to 95 molar percent, based on
the total number of moles of all feed and diluent components fed to
the reaction zone. Typical diluents include, but are not
necessarily limited to helium, argon, nitrogen, carbon monoxide,
carbon dioxide, hydrogen, water, paraffins, alkanes (especially
methane, ethane, and propane), aromatic compounds, and mixtures
thereof. The preferred diluents are water and nitrogen. Water can
be injected in either liquid or vapour form.
[0137] The oxygenate feedstock is any feedstock containing a
molecule or any chemical having at least an oxygen atom and
capable, in the presence of the above MeAPO catalyst composite, to
be converted to olefin products. The oxygenate feedstock comprises
at least one organic compound which contains at least one oxygen
atom, such as aliphatic alcohols, ethers, carbonyl compounds
(aldehydes, ketones, carboxylic acids, carbonates, esters and the
like). Representative oxygenates include but are not necessarily
limited to lower straight and branched chain aliphatic alcohols and
their unsaturated counterparts. Examples of suitable oxygenate
compounds include, but are not limited to: methanol; ethanol;
n-propanol; isopropanol; C.sub.4-C.sub.20 alcohols; methyl ethyl
ether; dimethyl ether; diethyl ether; di-isopropyl ether;
formaldehyde; dimethyl carbonate; dimethyl ketone; acetic acid; and
mixtures thereof. Representative oxygenates include lower straight
chain or branched aliphatic alcohols, their unsaturated
counterparts. Analogously to these oxygenates, compounds containing
sulphur or halides may be used. Examples of suitable compounds
include methyl mercaptan; dimethyl sulfide; ethyl mercaptan;
di-ethyl sulfide; ethyl monochloride; methyl monochloride, methyl
dichloride, n-alkyl halides, n-alkyl sulfides having n-alkyl groups
of comprising the range of from about 1 to about 10 carbon atoms;
and mixtures thereof. Preferred oxygenate compounds are methanol,
dimethyl ether, or a mixture thereof.
[0138] In XTO effluent among the olefins having 4 carbon atoms or
more there are 50 to 85 weight % of butenes. More than 85% by
weight and advantageously more than 95% of the hydrocarbons having
4 carbon atoms or more are C4 to C8 olefins.
[0139] According to an advantageous embodiment of the invention
said olefin products (the effluent of the XTO) are fractionated to
form a stream comprising essentially ethylene and at least a part
of said stream is recycled on the catalyst composite to increase
the propylene production and then the flexibility of ethylene vs
propylene production. Advantageously the ratio of ethylene to the
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock is 1.8 or less.
[0140] The present invention also relates to a process (hereunder
referred to as the "combined XTO and OCP process") to make light
olefins from an oxygen-containing, halogenide-containing or
sulphur-containing organic feedstock comprising:
contacting said oxygen-containing, halogenide-containing or
sulphur-containing organic feedstock in the MTO reactor with the
above catalyst at conditions effective to convert at least a
portion of the feedstock to form an MTO reactor effluent comprising
light olefins and a heavy hydrocarbon fraction; separating said
light olefins from said heavy hydrocarbon fraction; contacting said
heavy hydrocarbon fraction in the OCP reactor at conditions
effective to convert at least a portion of said heavy hydrocarbon
fraction to light olefins.
[0141] The effluent of the XTO reactor comprising light olefins and
a heavy hydrocarbon fraction is sent to a fractionation section to
separate said light olefins from said heavy hydrocarbon fraction.
With regards to said effluent of the XTO process, "light olefins"
means ethylene and propylene and the "heavy hydrocarbon fraction"
is defined herein as the fraction containing hydrocarbons having a
molecular weight greater than propane, which means hydrocarbons
having 4 carbon atoms or more and written as C.sub.4.sup.+. It is
desirable to have a substantially 100% conversion of the organic
compound in the primary reactor. This conversion rate is adjusted
by optimization of contact time and the frequency of regeneration
of the catalyst.
[0142] With regards to the OCP process, said process is known per
se. It has been described in EP 1036133, EP 1035915, EP 1036134, EP
1036135, EP 1036136, EP 1036138, EP 1036137, EP 1036139, EP
1194502, EP 1190015, EP 1194500 and EP 1363983 the content of which
are incorporated in the present invention.
[0143] The heavy hydrocarbon fraction produced in the XTO reactor
is converted in the OCP reactor, also called an "olefin cracking
reactor" herein, to produce additional amounts of ethylene and
propylene. Advantageously the catalysts found to produce this
conversion comprise a crystalline silicate of the MFI family, which
may be a zeolite, a silicalite or any other silicate in that
family, or of the MEL family, which may be a zeolite or any other
silicate in that family. These catalysts have been described above
in the description of the medium and large pore molecular sieves
suitable for the invention.
[0144] The crystalline silicate catalyst has structural and
chemical properties and is employed under particular reaction
conditions whereby the catalytic cracking of the C.sub.4.sup.+
olefins readily proceeds. Different reaction pathways can occur on
the catalyst. Under the process conditions, having an inlet
temperature of around 400.degree. to 600.degree. C., preferably
from 520.degree. to 600.degree. C., yet more preferably 540.degree.
to 580.degree. C., and an olefin partial pressure of from 0.1 to 2
bars, most preferably around atmospheric pressure. Olefinic
catalytic cracking may be understood to comprise a process yielding
shorter molecules via bond breakage. With such high
silicon/aluminum ratio in the crystalline silicate catalyst, a
stable olefin conversion can be achieved with a high propylene
yield on an olefin basis.
[0145] The MFI catalyst having a high silicon/aluminum atomic ratio
for use in the OCP reactor of the present invention may be
manufactured by removing aluminum from a commercially available
crystalline silicate. A typical commercially available silicalite
has a silicon/aluminum atomic ratio of around 120. The commercially
available MFI crystalline silicate may be modified by a steaming
process, which reduces the tetrahedral aluminum in the crystalline
silicate framework and converts the aluminum atoms into octahedral
aluminum in the form of amorphous alumina. Although in the steaming
step aluminum atoms are chemically removed from the crystalline
silicate framework structure to form alumina particles, those
particles cause partial obstruction of the pores or channels in the
framework. This inhibits the olefin cracking processes of the
present invention. Accordingly, following the steaming step, the
crystalline silicate is subjected to an extraction step wherein
amorphous alumina is removed from the pores and the micropore
volume is, at least partially, recovered. The physical removal, by
a leaching step, of the amorphous alumina from the pores by the
formation of a water-soluble aluminum complex yields the overall
effect of de-alumination of the MFI crystalline silicate. In this
way by removing aluminum from the MFI crystalline silicate
framework and then removing alumina formed there from the pores,
the process aims at achieving a substantially homogeneous
de-alumination throughout the whole pore surfaces of the catalyst.
This reduces the acidity of the catalyst and thereby reduces the
occurrence of hydrogen transfer reactions in the cracking process.
The reduction of acidity ideally occurs substantially homogeneously
throughout the pores defined in the crystalline silicate framework.
This is because in the olefin-cracking process hydrocarbon species
can enter deeply into the pores. Accordingly, the reduction of
acidity and thus the reduction in hydrogen transfer reactions which
would reduce the stability of the MFI catalyst are pursued
throughout the whole pore structure in the framework. The framework
silicon/aluminum ratio may be increased by this process to a value
of at least about 180, preferably from about 180 to 1000, more
preferably at least 200, yet more preferably at least 300 and most
preferably around 480.
[0146] The MEL or MFI crystalline silicate catalyst may be mixed
with a binder, preferably an inorganic binder, and shaped to a
desired shape, e.g. extruded pellets. The binder is selected so as
to be resistant to the temperature and other conditions employed in
the catalyst manufacturing process and in the subsequent catalytic
cracking process for the olefins. The binder is an inorganic
material selected from clays, silica, metal oxides such as
ZrO.sub.2 and/or metals, or gels including mixtures of silica and
metal oxides. The binder is preferably alumina-free, although
aluminum in certain chemical compounds as in aluminium phosphates
(AlPO.sub.4) may be used as the latter are quite inert and not
acidic in nature. If the binder which is used in conjunction with
the crystalline silicate is itself catalytically active, this may
alter the conversion and/or the selectivity of the catalyst.
Inactive materials for the binder may suitably serve as diluents to
control the amount of conversion so that products can be obtained
economically and orderly without employing other means for
controlling the reaction rate. It is desirable to provide a
catalyst having a good crush strength. This is because in
commercial use, it is desirable to prevent the catalyst from
breaking down into powder-like materials. Such clay or oxide
binders have been employed normally only for the purpose of
improving the crush strength of the catalyst. A particularly
preferred binder for the catalyst of the present invention
comprises silica or AlPO.sub.4.
[0147] The relative proportions of the finely divided crystalline
silicate material and the inorganic oxide matrix of the binder can
vary widely. Typically, the binder content ranges from 5 to 95% by
weight, more typically from 20 to 50% by weight, based on the
weight of the composite catalyst. Such a mixture of crystalline
silicate and an inorganic oxide binder is referred to as a
formulated crystalline silicate.
[0148] In mixing the catalyst with a binder, the catalyst may be
formulated into pellets, spheres, extruded into other shapes, or
formed into a spray-dried powder. In the catalytic cracking process
of the OCP reactor, the process conditions are selected in order to
provide high selectivity towards propylene or ethylene, as desired,
a stable olefin conversion over time, and a stable olefinic product
distribution in the effluent. Such objectives are favoured by the
use of a low acid density in the catalyst (i.e. a high Si/Al atomic
ratio) in conjunction with a low pressure, a high inlet temperature
and a short contact time, all of which process parameters are
interrelated and provide an overall cumulative effect. The process
conditions are selected to disfavour hydrogen transfer reactions
leading to the formation of paraffins, aromatics and coke
precursors. The process operating conditions thus employ a high
space velocity, a low pressure and a high reaction temperature. The
LHSV ranges from 5 to 30 hr.sup.-1, preferably from 10 to 30
hr.sup.-1. The olefin partial pressure ranges from 0.1 to 2 bars,
preferably from 0.5 to 1.5 bars (absolute pressures referred to
herein). A particularly preferred olefin partial pressure is
atmospheric pressure (i.e. 1 bar). The heavy hydrocarbon fraction
feedstock is preferably fed at a total inlet pressure sufficient to
convey the feedstocks through the reactor. Said feedstock may be
fed undiluted or diluted in an inert gas, e.g. nitrogen or steam.
Preferably, the total absolute pressure in the second reactor
ranges from 0.5 to 10 bars. The use of a low olefin partial
pressure, for example atmospheric pressure, tends to lower the
incidence of hydrogen transfer reactions in the cracking process,
which in turn reduces the potential for coke formation, which tends
to reduce catalyst stability. The cracking of the olefins is
preferably performed at an inlet temperature of the feedstock of
from 400.degree. to 650.degree. C., more preferably from
450.degree. to 600.degree. C., yet more preferably from 540.degree.
C. to 590.degree. C., typically around 560.degree. to 585.degree.
C.
[0149] In order to maximize the amount of ethylene and propylene
and to minimize the production of methane, aromatics and coke, it
is desired to minimize the presence of diolefins in the feed.
Diolefin conversion to monoolefin hydrocarbons may be accomplished
with a conventional selective hydrogenation process such as
disclosed in U.S. Pat. No. 4,695,560 hereby incorporated by
reference.
[0150] The OCP reactor can be a fixed bed reactor, a moving bed
reactor or a fluidized bed reactor. A typical fluid bed reactor is
one of the FCC type used for fluidized-bed catalytic cracking in
the oil refinery. A typical moving bed reactor is of the continuous
catalytic reforming type. As described above, the process may be
performed continuously using a pair of parallel "swing" reactors.
The heavy hydrocarbon fraction cracking process is endothermic;
therefore, the reactor should be adapted to supply heat as
necessary to maintain a suitable reaction temperature. Online or
periodic regeneration of the catalyst may be provided by any
suitable means known in the art.
[0151] The various preferred catalysts of the OCP reactor have been
found to exhibit high stability, in particular being capable of
giving a stable propylene yield over several days, e.g. up to ten
days. This enables the olefin cracking process to be performed
continuously in two parallel "swing" reactors wherein when one
reactor is operating, the other reactor is undergoing catalyst
regeneration. The catalyst can be regenerated several times.
[0152] The OCP reactor effluent comprises methane, light olefins
and hydrocarbons having 4 carbon atoms or more. Advantageously said
OCP reactor effluent is sent to a fractionator and the light
olefins are recovered. Advantageously the hydrocarbons having 4
carbon atoms or more are recycled at the inlet of the OCP reactor,
optionally mixed with the heavy hydrocarbon recovered from the
effluent of the XTO reactor. Advantageously, before recycling said
hydrocarbons having 4 carbon atoms or more at the inlet of the OCP
reactor, said hydrocarbons having 4 carbon atoms or more are sent
to a second fractionator to purge the heavies. In a preferred
embodiment the light olefins recovered from the effluent of the XTO
reactor and the light olefins recovered from the fractionator
following the OCP reactor are treated in a common recovery
section.
[0153] Optionally, in order to adjust the propylene to ethylene
ratio of the whole process (XTO+OCP), ethylene in whole or in part
can be recycled over the OCP reactor and advantageously converted
into more propylene. This ethylene can either come from the
fractionation section of the XTO reactor or from the fractionation
section of the OCP reactor or from both the fractionation section
of the XTO reactor and the fraction section of the OCP reactor or
even from the optional common recovery section.
[0154] Optionally, in order to adjust the propylene to ethylene
ratio of the whole process (XTO+OCP), ethylene in whole or in part
can be recycled over the XTO reactor where it combines with the
oxygen-containing, halogenide-containing or sulphur-containing
organic feedstock to form more propylene. This ethylene can either
come from the fractionation section of the XTO reactor or from the
fractionation section of the OCP reactor or from both the
fractionation section of the XTO reactor and the fraction section
of the OCP reactor or even from the optional common recovery
section.
[0155] These ways of operation allow to respond with the same
equipment and catalyst to market propylene to ethylene demand.
[0156] The performance of the catalyst of the present invention is
substantially better than the simple sum of the individual
components. This shows a synergy of at least one molecular sieve in
the XTO and a metal salt to produce very particular catalytic
properties. The catalyst composite shows good behaviour in XTO
processes in terms of stability and C3/C2 ratio, propylene purity
and heavy olefins production (higher C4+ olefin yield for
recycling).
[0157] FIG. 1 illustrates a specific embodiment of the invention.
The effluent of the XTO reactor is passed to a fractionator 11. The
overhead, a C1-C3 fraction including the light olefins is sent via
line 2 to a common recovery section (not shown). The bottoms (the
heavy hydrocarbon fraction) are sent via line 3 to the OCP reactor.
The effluent of the OCP reactor is sent via line 10 to a
fractionator 8. The overhead, a C1-C3 fraction including the light
olefins, is sent via line 9 to a common recovery section (not
shown). The bottoms, hydrocarbons having 4 carbon atoms or more,
are sent to a fractionator 5. The overhead, hydrocarbons having 4
to substantially 5 carbon atoms are recycled via line 4 at the
inlet of the OCP reactor. The bottoms, hydrocarbons having
substantially 6 carbon atoms or more, are purged via line 6.
[0158] The method of making the olefin products from an oxygenate
feedstock can include the additional step of making the oxygenate
feedstock from hydrocarbons such as oil, coal, tar sand, shale,
biomass and natural gas. Methods for making oxygenate feedstocks
are known in the art. These methods include fermentation to alcohol
or ether, making synthesis gas, then converting the synthesis gas
to alcohol or ether. Synthesis gas can be produced by known
processes such as steam reforming, autothermal reforming and
partial oxidization in case of gas feedstocks or by reforming or
gasification using oxygen and steam in case of solid (coal, organic
waste) or liquid feedstocks. Methanol, methylsulfide and
methylhalides can be produced by oxidation of methane with the help
of dioxygen, sulphur or halides in the corresponding
oxygen-containing, halogenide-containing or sulphur-containing
organic compound.
[0159] One skilled in the art will also appreciate that the olefin
products made by the oxygenate-to-olefin conversion reaction using
the molecular sieve of the present invention can be polymerized to
form polyolefins, particularly polyethylenes and polypropylenes.
The present invention relates also to said polyethylenes and
polypropylenes.
EXAMPLES
Example 1
[0160] A sample of SAPO-34 from UOP was obtained through
"Customec". This sample showed a silicon content (Si/(Si+Al+P)) of
0.41 and represents a cubic crystal morphology with an average size
of 0.4 .mu.m.
[0161] The sample is hereinafter identified as Comparative I.
Example 2
[0162] A sample identified hereinafter as Sample A was prepared by
mechanically blending 80 wt % of the solid described in example I
with 20 wt % of xonotlite CaSi.sub.6O.sub.17(OH).sub.2.
Example 3
[0163] Catalyst tests were performed on 2 g catalyst samples with
an essentially pure methanol feed at 450.degree. C., at a pressure
of 0.5 barg and WHSV=1.6 h.sup.-1, in a fixed-bed, down-flow
stainless-steel reactor. Catalyst powder was pressed into wafers
and crushed to 35-45 mesh particles. Prior to catalytic run all
catalysts were heated in flowing N.sub.2 (5 NI/h) up to the
reaction temperature. Analysis of the products has been performed
on-line by a gas chromatograph equipped with a capillary column.
Catalytic performances of MeAPOs molecular sieves were compared at
100% methanol conversion and maximum catalyst activity just before
appearance of DME in the effluent. The results are provided in
Table I. The values regarding the composition of the effluent from
the MTO reactor are the weight percent on a carbon basis and
water-free.
TABLE-US-00001 TABLE I Comparative I Sample A SAPO-34 SAPO-34 +
xonotlite 100 wt % 80 wt % + 20 wt % T/.degree. C. 450 450
WHSV/h.sup.-1 1.6 1.6 P/barg 0.5 0.5 C1 5.4 3.9 Paraffins 8.4 5.8
Olefins 90.7 92.7 Aromatics 0.3 0.3 Purity C3's 97.8 99.4 C3/C2 0.7
0.7 C2 + C3 77.6 81.4 ethylene 44.8 46.7 propylene 32.7 34.7
* * * * *