U.S. patent application number 13/438554 was filed with the patent office on 2013-10-03 for apparel and other products incorporating a thermoplastic polymer material.
This patent application is currently assigned to NIKE, INC.. The applicant listed for this patent is Carrie L. Davis, Bhupesh Dua. Invention is credited to Carrie L. Davis, Bhupesh Dua.
Application Number | 20130255103 13/438554 |
Document ID | / |
Family ID | 48483188 |
Filed Date | 2013-10-03 |
United States Patent
Application |
20130255103 |
Kind Code |
A1 |
Dua; Bhupesh ; et
al. |
October 3, 2013 |
Apparel And Other Products Incorporating A Thermoplastic Polymer
Material
Abstract
A yarn or thread may include a plurality of substantially
aligned filaments, with at least ninety-five percent of a material
of the filaments being a thermoplastic polymer material. Various
woven textiles and knitted textiles may be formed from the yarn or
thread. The woven textiles or knitted textiles may be thermal
bonded to other elements to form seams. A strand that is at least
partially formed from a thermoplastic polymer material may extend
through the seam, and the strand may be thermal bonded at the seam.
The woven textiles or knitted textiles may be shaped or molded,
incorporated into products, and recycled to form other
products.
Inventors: |
Dua; Bhupesh; (Portland,
OR) ; Davis; Carrie L.; (Portland, OR) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Dua; Bhupesh
Davis; Carrie L. |
Portland
Portland |
OR
OR |
US
US |
|
|
Assignee: |
NIKE, INC.
Beaverton
OR
|
Family ID: |
48483188 |
Appl. No.: |
13/438554 |
Filed: |
April 3, 2012 |
Current U.S.
Class: |
36/87 ; 112/402;
428/57 |
Current CPC
Class: |
B29C 66/244 20130101;
B29C 66/71 20130101; B29C 66/7294 20130101; D10B 2331/10 20130101;
B29C 66/91943 20130101; A41D 2300/52 20130101; B29C 66/73921
20130101; B29C 65/20 20130101; B29C 65/72 20130101; B29C 66/133
20130101; B29C 66/73118 20130101; D04B 1/16 20130101; B29D 35/126
20130101; Y10T 428/19 20150115; A41D 2500/52 20130101; B29C 65/62
20130101; B29C 66/1282 20130101; B29C 66/45 20130101; B29D 35/02
20130101; B29L 2031/50 20130101; D10B 2401/041 20130101; A41D
27/245 20130101; A43B 9/02 20130101; A41D 2500/20 20130101; A43B
23/0205 20130101; D03D 15/00 20130101; A41D 2500/10 20130101; A43B
23/042 20130101; B29C 66/91933 20130101; A43C 5/00 20130101; B29C
66/135 20130101; B29C 66/12841 20130101; A41B 1/00 20130101; A41D
2300/326 20130101; B29C 66/43 20130101; B29C 66/472 20130101; B29C
66/729 20130101; B29C 66/83221 20130101; B29C 66/91443 20130101;
B29C 66/1122 20130101; B29C 66/431 20130101; B29C 66/81422
20130101; A43B 23/0215 20130101; B29C 66/81435 20130101; D02G 3/402
20130101; A43C 1/04 20130101; B29C 66/14 20130101; A43B 23/0255
20130101; B29C 66/223 20130101; A43D 8/24 20130101; A43B 23/025
20130101; B29C 66/727 20130101; B29C 66/91411 20130101; B29C
66/91935 20130101; A43B 1/04 20130101; B29C 66/81423 20130101; A43C
3/00 20130101; B29C 66/73116 20130101; B29K 2313/00 20130101; B29L
2031/48 20130101; B29C 66/7392 20130101; B29L 2031/4842 20130101;
B29C 66/91951 20130101; B29C 65/18 20130101; B29C 66/71 20130101;
B29K 2075/00 20130101 |
Class at
Publication: |
36/87 ; 428/57;
112/402 |
International
Class: |
B32B 7/04 20060101
B32B007/04; A43B 1/14 20060101 A43B001/14; D05B 93/00 20060101
D05B093/00 |
Claims
1. An article of apparel comprising a plurality of textile elements
joined to each other at seams to form a structure for receiving a
part of a wearer, the textile elements including strands that have
a plurality of substantially aligned filaments formed from a
thermoplastic polymer material.
2. The article of apparel recited in claim 1, wherein the textile
elements are thermal bonded to each other at the seams.
3. The article of apparel recited in claim 1, wherein the seams
include a joining strand that stitches the textile elements to each
other, the joining strand including a thermoplastic polymer
material.
4. The article of apparel recited in claim 3, wherein the
thermoplastic polymer material of the filaments and the
thermoplastic polymer material of the joining strand are
thermoplastic polyurethane materials.
5. The article of apparel recited in claim 3, wherein the
thermoplastic polymer material of the filaments has a higher
melting temperature than the thermoplastic polymer material of the
joining strand.
6. The article of apparel recited in claim 3, wherein the joining
strand is thermal bonded to the textile elements at the seams.
7. The article of apparel recited in claim 1, wherein the seams
include a thread that stitches the textile elements to each other,
the thread including a plurality of substantially aligned
filaments, at least ninety-five percent of a material of the
filaments being a thermoplastic polymer material.
8. The article of apparel recited in claim 1, wherein at least one
of the textile elements has a fused region and an unfused region,
the filaments being thermal bonded to each other in the fused
region, and the filaments being unbonded to each other in the
unfused region.
9. The article of apparel recited in claim 1, wherein at least one
of the textile elements has (a) an unfused region where the
filaments are present and (b) a fused region where the
thermoplastic polymer material of the filaments are melted and
thermal bonded to form a non-filamentous area.
10. The article of apparel recited in claim 1, wherein the apparel
has a configuration of footwear with an upper and a sole structure
secured to each other, the upper being at least partially formed
from the textile elements.
11. An article of apparel comprising: a pair of textile elements at
least partially formed from a first thermoplastic polyurethane
material; and a seam where a strand joins the textile elements to
each other, the strand being at least partially formed from a
second thermoplastic polyurethane material, the textile elements
being thermal bonded to each other at the seam with the first
thermoplastic polyurethane material, and the strand being thermal
bonded to the textile elements at the seam with the second
thermoplastic polyurethane material.
12. The article of apparel recited in claim 11, wherein a melting
temperature of the first polyurethane material is higher than a
melting temperature of the second thermoplastic polyurethane
material.
13. The article of apparel recited in claim 12, wherein a
glass-transition temperature of the first polyurethane material is
higher than a glass-transition temperature of the second
thermoplastic polyurethane material.
14. The article of apparel recited in claim 11, wherein the textile
elements are one of a woven textile and a knitted textile that
includes at least one strand with a plurality of substantially
aligned filaments formed from the first thermoplastic polymer
material.
15. The article of apparel recited in claim 11, wherein the first
textile elements are formed from a plurality of filaments, at least
ninety-five percent of a material of the filaments being the first
thermoplastic polymer material.
16. The article of apparel recited in claim 11, wherein the strand
is a thread.
17. The article of apparel recited in claim 11, wherein the apparel
has a configuration of footwear with an upper and a sole structure
secured to each other, the upper being at least partially formed
from the textile elements.
18. Footwear comprising: an upper having at least one textile
element with a woven or knitted structure, the textile element
including a strand with a plurality of substantially aligned
filaments, at least ninety-five percent of a material of the
filaments being a thermoplastic polymer material; and a sole
structure thermal bonded to the upper with the thermoplastic
polymer material.
19. The footwear recited in claim 18, wherein the sole structure is
at least partially formed from the thermoplastic polymer
material.
20. The footwear recited in claim 18, wherein the textile element
and another textile element are thermal bonded to each other at a
seam with the thermoplastic polymer material.
21. The footwear recited in claim 18, wherein a joining strand is
stitched to a seam between the textile element and another textile
element, the joining strand including a thermoplastic polymer
material.
22. Footwear having an upper and a sole structure secured to each
other, the upper comprising: a plurality of material elements
joined to define a void for receiving a foot of a wearer, at least
one of the material elements being a woven or knitted textile that
is formed from a thermoplastic polymer material; and a lace that
engages a plurality of lace-receiving elements in a throat area of
the upper, the lace being formed from at least one strand that
includes a plurality of substantially aligned filaments, at least
ninety-five percent of the filaments being formed from the
thermoplastic polymer material.
Description
BACKGROUND
[0001] A variety of articles are at least partially formed from
textiles. As examples, apparel (e.g., shirts, pants, socks,
footwear, jackets and other outerwear, briefs and other
undergarments, hats and other headwear), containers (e.g.,
backpacks, bags), and upholstery for furniture (e.g., chairs,
couches, car seats) are often formed from various textile elements
that are joined through stitching or adhesive bonding. Textiles may
also be utilized in bed coverings (e.g., sheets, blankets), table
coverings, towels, flags, tents, sails, and parachutes. Textiles
utilized for industrial purposes are commonly referred to as
technical textiles and may include structures for automotive and
aerospace applications, filter materials, medical textiles (e.g.
bandages, swabs, implants), geotextiles for reinforcing
embankments, agrotextiles for crop protection, and industrial
apparel that protects or insulates against heat and radiation.
Accordingly, textiles may be incorporated into a variety of
articles for both personal and industrial purposes.
[0002] Textiles may be defined as any manufacture from fibers,
filaments, or yarns having a generally two-dimensional structure
(i.e., a length and a width that are substantially greater than a
thickness). In general, textiles may be classified as non-woven
textiles or mechanically-manipulated textiles. Non-woven textiles
are webs or mats of filaments that are bonded, fused, interlocked,
or otherwise joined. As an example, a non-woven textile may be
formed by randomly depositing a plurality of polymer filaments upon
a surface, such as a moving conveyor. Mechanically-manipulated
textiles are often formed by weaving or interlooping (e.g.,
knitting) a yarn or a plurality of yarns, usually through a
mechanical process involving looms or knitting machines. Whereas
woven textiles include yarns that cross each other at right angles
(i.e., warp and weft yarns), knitted textiles include one or more
yarns that form a plurality of intermeshed loops arranged in
courses and wales.
[0003] Although some products are formed from one type of textile,
many products are formed from two or more types of textiles in
order to impart different properties to different areas. As an
example, shoulder and elbow areas of a shirt may be formed from a
textile that imparts durability (e.g., abrasion-resistance) and
stretch-resistance, whereas other areas may be formed from a
textile that imparts breathability, comfort, stretch, and
moisture-absorption. As another example, an upper for an article of
footwear may have a structure that includes numerous layers formed
from various types of textiles and other materials (e.g., polymer
foam, leather, synthetic leather), and some of the layers may also
have areas formed from different types of textiles to impart
different properties. As yet another example, straps of a backpack
may be formed from non-stretch textile elements, lower areas of a
backpack may be formed from durable and water-resistant textile
elements, and a remainder of the backpack may be formed from
lightweight and compliant textile elements. Accordingly, many
products may incorporate various types of textiles in order to
impart different properties to different portions of the
products.
[0004] In order to impart the different properties to different
areas of a product, textile elements formed from the materials must
be cut to desired shapes and then joined together, usually with
stitching or adhesive bonding. As the number and types of textile
elements incorporated into a product increases, the time and
expense associated with transporting, stocking, cutting, and
joining the textile elements may also increase. Waste material from
cutting and stitching processes also accumulates to a greater
degree as the number and types of textile elements incorporated
into a product increases. Moreover, products with a greater number
of textile elements and other materials may be more difficult to
recycle than products formed from few elements and materials. By
decreasing the number of elements and materials utilized in a
product, therefore, waste may be decreased while increasing the
manufacturing efficiency and recyclability.
SUMMARY
[0005] A yarn may include a plurality of substantially aligned
filaments, with at least ninety-five percent of a material of the
filaments being a thermoplastic polymer material.
[0006] A thread may include a first yarn and a second yarn. The
first yarn includes a plurality of substantially aligned filaments,
with at least ninety-five percent of a material of the filaments
being a thermoplastic polymer material. The second yarn is twisted
with the first yarn.
[0007] A woven textile may include a warp strand and a weft strand.
The warp strand extends in a first direction and includes a
plurality of substantially aligned filaments, with at least
ninety-five percent of a material of the filaments being a
thermoplastic polymer material. The weft strand extends in a second
direction that is substantially perpendicular to the first
direction.
[0008] A knitted textile may include at least one strand that forms
a plurality of interlocked loops arranged in courses and wales. The
strand includes a plurality of substantially aligned filaments,
with at least ninety-five percent of a material of the filaments
being a thermoplastic polymer material.
[0009] An article may include a first material element, a second
material element, and a seam. The first material element is at
least partially formed from a first thermoplastic polymer material,
and the first material element is one of a woven textile and a
knitted textile. At the seam, a strand extends through each of the
first material element and the second material element, the strand
being at least partially formed from a second thermoplastic polymer
material. The first material element is thermal bonded to the
second material element with the first thermoplastic polymer
material at the seam. Additionally, the strand is thermal bonded to
the first material element and the second material element with the
second thermoplastic polymer material at the seam.
[0010] A method of joining includes stitching a pair of textile
elements together with a strand to form a seam. The textile
elements and the strand are heated and compressed at the seam to
(a) form a thermal bond between the textile elements and (b) melt
the strand.
[0011] An article of apparel includes a plurality of textile
elements joined to each other at seams to form a structure for
receiving a part of a wearer. The textile elements include strands
that have a plurality of substantially aligned filaments formed
from a thermoplastic polymer material.
[0012] The advantages and features of novelty characterizing
aspects of the invention are pointed out with particularity in the
appended claims. To gain an improved understanding of the
advantages and features of novelty, however, reference may be made
to the following descriptive matter and accompanying figures that
describe and illustrate various configurations and concepts related
to the invention.
FIGURE DESCRIPTIONS
[0013] The foregoing Summary and the following Detailed Description
will be better understood when read in conjunction with the
accompanying figures.
[0014] FIG. 1 is a plan view of a portion of a yarn.
[0015] FIG. 2 is a cross-sectional view of the yarn, as defined in
FIG. 1.
[0016] FIG. 3 is a plan view of a portion of a thread.
[0017] FIG. 4 is a cross-sectional view of the thread, as defined
in FIG. 3.
[0018] FIGS. 5 and 6 are plan views depicting further
configurations of the thread.
[0019] FIG. 7 is a plan view of a woven textile.
[0020] FIG. 8 is a cross-sectional view of the woven textile, as
defined in FIG. 7.
[0021] FIG. 9 is a plan view of a knitted textile.
[0022] FIG. 10 is a cross-sectional view of the knitted textile, as
defined in FIG. 9.
[0023] FIG. 11 is a plan view depicting a further configuration of
the knitted textile.
[0024] FIGS. 12 and 13 are cross-sectional views corresponding with
FIG. 2 and depicting examples of fused configurations of the
yarn.
[0025] FIGS. 14 and 15 are cross-sectional views corresponding with
FIG. 4 and depicting examples of fused configurations of the
thread.
[0026] FIG. 16 is a plan view of the woven textile with a fused
region.
[0027] FIG. 17 is a cross-sectional view of the woven textile, as
defined in FIG. 16.
[0028] FIG. 18 is another plan view of the woven textile with a
fused region.
[0029] FIG. 19 is a cross-sectional view of the woven textile, as
defined in FIG. 18.
[0030] FIG. 20 is a plan view of the knitted textile with a fused
region.
[0031] FIG. 21 is a cross-sectional view of the knitted textile, as
defined in FIG. 20.
[0032] FIG. 22 is another plan view of the knitted textile with a
fused region.
[0033] FIG. 23 is a cross-sectional view of the knitted textile, as
defined in FIG. 22.
[0034] FIG. 24 is a plan view of the woven textile with multiple
fused regions.
[0035] FIG. 25 is a perspective view of a composite element.
[0036] FIG. 26 is a cross-sectional view of the composite element,
as defined in FIG. 25.
[0037] FIGS. 27A-27C are schematic perspective views of a
manufacturing process for the composite element.
[0038] FIG. 28 is a perspective view of the composite element with
a fused region.
[0039] FIG. 29 is a perspective view of a first configuration of a
seam element.
[0040] FIG. 30 is a cross-sectional view of the first configuration
of the seam element, as defined in FIG. 29.
[0041] FIGS. 31A-31D are schematic side elevational views of a
manufacturing process for the first configuration of the seam
element.
[0042] FIG. 32 is a perspective view of the first configuration of
the seam element with multiple fused regions.
[0043] FIG. 33 is a perspective view of a second configuration of
the seam element.
[0044] FIG. 34 is a cross-sectional view of the second
configuration of the seam element, as defined in FIG. 33
[0045] FIGS. 35A-35C are schematic side elevational views of a
manufacturing process for the second configuration of the seam
element.
[0046] FIG. 36 is a perspective view of the first configuration of
the seam element with a stitching strand.
[0047] FIGS. 37A-37C are alternate perspective views of the first
configuration of the seam element with a stitching strand.
[0048] FIGS. 38A-38D are schematic side elevational views of a
manufacturing process for the first configuration of the seam
element with a stitching strand.
[0049] FIG. 38E is a perspective view of a portion of the
manufacturing process for the first configuration of the seam
element with a stitching strand.
[0050] FIGS. 39A and 39B are graphs depicting temperature in the
manufacturing process for the first configuration of the seam
element with a stitching strand.
[0051] FIG. 40 is a perspective view of the second configuration of
the seam element with a stitching strand.
[0052] FIG. 41 is an elevational view of a first configuration of a
shirt.
[0053] FIGS. 42A-42C are cross-sectional views of the first
configuration of the shirt, as defined in FIG. 41.
[0054] FIG. 43 is an elevational view of a second configuration of
the shirt.
[0055] FIGS. 44A and 44B are cross-sectional views of the second
configuration of the shirt, as defined in FIG. 43.
[0056] FIG. 45 is an elevational view of a third configuration of
the shirt.
[0057] FIGS. 46A-46C are cross-sectional views of the third
configuration of the shirt, as defined in FIG. 45.
[0058] FIG. 47 is an elevational view of a fourth configuration of
the shirt.
[0059] FIG. 48 is a cross-sectional view of the fourth
configuration of the shirt, as defined in FIG. 47.
[0060] FIG. 49 is an elevational view of a first configuration of
footwear.
[0061] FIG. 50 is a cross-sectional view of the first configuration
of the footwear, as defined in FIG. 49.
[0062] FIG. 51 is an elevational view of a second configuration of
the footwear.
[0063] FIG. 52 is a cross-sectional views of the second
configuration of the footwear, as defined in FIG. 51.
[0064] FIG. 53 is an elevational view of a third configuration of
the footwear.
[0065] FIG. 54 is an elevational view of a fourth configuration of
the footwear.
[0066] FIGS. 55A-55C are perspective views of shaped textiles.
[0067] FIGS. 56A-56C are schematic perspective views of a
manufacturing process for the shaped textiles.
[0068] FIG. 57 is a schematic view of a recycling process.
DETAILED DESCRIPTION
[0069] The following discussion and accompanying figures disclose
various yarns, threads, and textiles formed from thermoplastic
polymer materials. Although the yarns, threads, and textiles are
disclosed below as being incorporated into various articles of
apparel (e.g., shirts and footwear) for purposes of example, the
yarns, threads, and textiles may also be incorporated into a
variety of other articles. For example, the yarns, threads, and
textiles may be utilized in other types of apparel, containers, and
upholstery for furniture. The yarns, threads, and textiles may also
be utilized in bed coverings, table coverings, towels, flags,
tents, sails, and parachutes. Various configurations of the yarns,
threads, and textiles may also be utilized for industrial purposes,
as in automotive and aerospace applications, filter materials,
medical textiles, geotextiles, agrotextiles, and industrial
apparel. Accordingly, the yarns, threads, and textiles may be
utilized in a variety of articles for both personal and industrial
purposes.
A. YARN CONFIGURATION
[0070] A section of a yarn 100 is depicted in FIG. 1 as having a
configuration that may be utilized for a variety of purposes,
including sewing, stitching, and embroidering. Yarn 100 may also be
utilized for making a thread, cable, cord, or rope. Various
textiles may also be produced from yarn 100 through weaving and
knitting, for example. Although a relatively short length of yarn
100 is shown, yarn 100 may have a significantly greater length.
More particularly, the length of yarn 100 may significantly exceed
one-thousand or even ten-thousand meters. Depending upon the manner
in which yarn 100 is formed, yarn 100 may be a spun yarn or an air
textured yarn.
[0071] Yarn 100 includes a plurality of filaments 101 that are
bundled or otherwise gathered to form a generally thin and elongate
structure. The number of filaments 101 that are incorporated into
yarn 100 may vary significantly and may range between two and
three-hundred or more. Fibers are often defined, in textile
terminology, as having a relatively short length that ranges from
one millimeter to a few centimeters or more, whereas filaments are
often defined as having a longer length than fibers or even an
indeterminate length. As utilized within the present document, the
term "filament" or variants thereof is intended to encompass
lengths of both fibers and filaments from the textile terminology
definitions. Accordingly, filaments 101 or other filaments referred
to herein may generally have any length. As an example, therefore,
filaments 101 may have a length that ranges from one millimeter to
hundreds of meters or more. Individual filaments 101 may also have
lengths that extend through an entire length of yarn 100.
[0072] Filaments 101 are substantially aligned in yarn 100. As
utilized herein, the term "substantially aligned" is intended to
convey that filaments 100 generally extend in a common direction,
which corresponds with a longitudinal axis of yarn 100. When
substantially aligned, some of filaments 101 or portions of
filaments 101 may be parallel with each other, but other filaments
101 or other portions of filaments 101 may cross each other or may
extend in directions that are offset by a few degrees (e.g., offset
in a range of zero to seven degrees) when yarn 100 is tensioned,
stretched, or otherwise arranged to have a linear or straight
structure.
[0073] Although filaments 101 are substantially aligned, yarn 100
is depicted as exhibiting twist, thereby imparting a rotational
aspect to various filaments 101. More particularly, filaments 101
may be twisted around each other such that some filaments 101 or
sections of filaments 101 have a helical structure that repeatedly
wraps around the longitudinal axis of yarn 100. Although sections
of filaments 101 may be generally straight, other sections may have
a spiral or helical configuration that imparts the twist. In some
configurations, portions of filaments 100 located in a central area
of yarn 100 may be generally straight, whereas portions of
filaments 100 located closer to a periphery or exterior of yarn 100
may have the spiral or helical configuration. Either an S-twist or
a Z-twist may be utilized in yarn 100. An advantage of the twist is
that filaments 101 are bundled more closely than in non-twist yarns
to effectively reduce the size of spaces between individual
filaments 101. As such filaments 101 lay against and contact each
other, as depicted in FIG. 2, to minimize the overall diameter of
yarn 100. Moreover, the twist in yarn 100 imparts the advantage of
reducing fraying that may occur if some of filaments 101 are
severed, sheared, or otherwise broken. Although yarn 100 may
exhibit twist, yarn 100 may also have a straight or untwisted
configuration.
[0074] Filaments 101 are primarily formed from a thermoplastic
polymer material. In general, a thermoplastic polymer material
softens or melts when heated and returns to a solid state when
cooled. More particularly, a thermoplastic polymer material
transitions from a solid state to (a) a softened state when heated
to a glass transition temperature of the thermoplastic polymer
material and (b) a generally liquid state when heated to a melting
temperature of the thermoplastic polymer material. Then, when
sufficiently cooled, the thermoplastic polymer material transitions
from the softened or liquid state to the solid state. As such, the
thermoplastic polymer material may be softened or melted, molded,
cooled, re-softened or re-melted, re-molded, and cooled again
through multiple cycles. When heated to at least the glass
transition temperature, thermoplastic polymer materials may also be
welded, fused, or thermal bonded, as described in greater detail
below, to join an element formed from the thermoplastic polymer
material to another object, item, or element. In contrast with
thermoplastic polymer materials, many thermoset polymer materials
do not melt when heated, simply degrading or burning instead.
[0075] Although a wide range of thermoplastic polymer materials may
be utilized for filaments 101, examples of suitable thermoplastic
polymer materials include thermoplastic polyurethane, polyamide,
polyester, polypropylene, and polyolefin. Although filaments 101
may be formed from any of the thermoplastic polymer materials
mentioned above, utilizing thermoplastic polyurethane imparts
various advantages. For example, various formulations of
thermoplastic polyurethane are elastomeric and stretch over
one-hundred percent, while exhibiting relatively high stability or
tensile strength. In comparison with some other thermoplastic
polymer materials, thermoplastic polyurethane readily forms thermal
bonds with other elements, as discussed in greater detail below.
Also, thermoplastic polyurethane may form foam materials and may be
recycled to form a variety of products.
[0076] In many configurations of yarn 100, each of filaments 101
are entirely or substantially formed from one or more thermoplastic
polymer materials. That is, at least ninety-five percent,
ninety-nine percent, or one-hundred percent of a material of
filaments 101 is a thermoplastic polymer material. Advantages of
substantially forming filaments 101 from a thermoplastic polymer
material are uniform properties, the ability to form thermal bonds,
efficient manufacture, elastomeric stretch, and relatively high
stability or tensile strength Although a single thermoplastic
polymer material may be utilized, individual filaments 101 may be
formed from multiple thermoplastic polymer materials. As an
example, an individual filament 101 may have a sheath-core
configuration, wherein an exterior sheath of the individual
filament 101 is formed from a first thermoplastic polymer material,
and an interior core of the individual filament 101 is formed from
a second thermoplastic polymer material. As a similar example, an
individual filament 101 may have a bi-component configuration,
wherein one half of the individual filament 101 is formed from a
first thermoplastic polymer material, and an opposite half of the
individual filament 101 is formed from a second thermoplastic
polymer material. Although each of filaments 101 may be formed from
a common thermoplastic polymer material, different filaments 101
may also be formed from different materials. As an example, some of
filaments 101 may be formed from a first type of thermoplastic
polymer material, whereas other filaments 101 may be formed from a
second type of thermoplastic polymer material.
[0077] The thermoplastic polymer material of filaments 101 may be
selected to have various stretch properties, and the material may
be considered elastomeric. Depending upon the specific properties
desired for yarn 100, filaments 101 may stretch between ten percent
to more than eight-hundred percent prior to tensile failure. As a
related matter, the thermoplastic polymer material utilized for
filaments 101 may be selected to have various recovery properties.
That is, yarn 100 or filaments 101 may be formed to return to an
original shape after being stretched. Many products that
incorporate yarn 100, such as textiles and articles of apparel
formed from the textiles, may benefit from properties that allow
yarn 100 to return or otherwise recover to an original shape after
being stretched by one-hundred percent or more. Although many
thermoplastic polymer materials exhibit stretch and recovery
properties, thermoplastic polyurethane exhibits suitable stretch
and recovery properties for various textiles and articles of
apparel.
[0078] The weight of yarn 100 may vary significantly depending upon
the thicknesses of individual filaments 101, the number of
filaments 101, and the specific material selected for filaments
101, for example. In general, weight is measured by the unit tex,
which is the weight in grams of a kilometer of yarn. Yarn 100 may
range from fifty to one-thousand denier or more.
[0079] A variety of conventional processes may be utilized to
manufacture yarn 100. In general, a manufacturing process for yarn
100 includes (a) extruding or otherwise forming a plurality of
filaments 101 from a thermoplastic polymer material and (b)
collecting or bundling filaments 101. Once bundled, filaments 101
may be twisted. Depending upon the specific characteristics
desired, yarn 100 may also be subjected to an air texturing
operation or other post-processing operations. Fusing processes, as
discussed below, may also be performed to form thermal bonds
between adjacent filaments 101.
B. THREAD CONFIGURATION
[0080] A thread 200 is depicted in FIGS. 3 and 4 as including two
yarns 201 that are twisted with each other. Although the
configuration of yarns 201 may vary significantly, each of yarns
201 may exhibit the general configuration of yarn 100 discussed
above. One or both of yarns 201 includes, therefore, a plurality of
substantially aligned filaments 202 that are substantially formed
from a thermoplastic polymer material. As such, at least
ninety-five percent, ninety-nine percent, or one-hundred percent of
a material of filaments 202 is a thermoplastic polymer material,
such as thermoplastic polyurethane.
[0081] Given that two yarns 201 are twisted together, this
configuration of thread 200 may be considered a two-ply thread. In
other configurations, any number of yarns 201 or other yarns may be
incorporated into thread 200. As an example of a three-ply threads,
FIG. 5 depicts thread 200 as incorporating three yarns 201 that are
twisted with each other. As another example, FIG. 6 depicts thread
200 as incorporating three yarns 201 that are twisted together
through braiding. Accordingly, the number of yarns 201 and the
manner in which yarns 201 are twisted with each other may vary
significantly.
[0082] As with yarn 100, the weight of thread 200 may vary
significantly depending upon the thicknesses of individual
filaments 202, the number of filaments 202 in each yarn 201, the
material selected for filaments 202, and the number of yarns 100,
for example. In general, weight is measured by the unit denier,
which is the weight in grams of nine-thousand meters of thread. As
examples, each of yarns 201 within thread 200 may range from 50
denier to 400 denier or more.
C. TEXTILE CONFIGURATIONS
[0083] Various types of textiles may be formed from one or more
strands, including either of yarn 100 and thread 200. For purposes
of the following discussion, the term "strand" is defined as a
generally elongate element having a length that is substantially
greater than a width and thickness. Examples of various types of
strands include filaments, yarns, threads, cables, cords, and
ropes. As such, either of yarn 100 and thread 200 may be a strand
that is incorporated into a textile.
[0084] As a first example of a textile, a woven textile 300 is
depicted in FIG. 7 as including a plurality of warp strands 301 and
weft strands 302. Whereas warp strands 301 extend in a first
direction, weft strands 302 extend in a second direction that is
substantially perpendicular to the first direction. Moreover,
strands 301 and 302 cross each other and weave over and below each
other, as depicted in FIG. 8. In manufacturing woven textile 300,
strands 301 and 302 are manipulated through a weaving process,
which may involve a weaving machine or loom, to cross and weave
among each other at the substantially right angles. In addition to
a plain weave, various configurations of woven textile may have a
twill weave, satin weave, jacquard weave, or dobby weave, for
example.
[0085] Although woven textile 300 is depicted as being formed from
strands 301 and 302, one or more additional strands may be
incorporated into the structure of woven textile 300. For example,
different warp strands, weft strands, or portions of these strands
may be formed from various types of strands having diverse
materials, colors, or properties. Any of strands 301 and 302 may
have the configuration of a filament, yarn, thread, cable, cord, or
rope. Either or both of strands 301 and 302 may also exhibit the
general configuration of yarn 100 or thread 200 discussed above.
Strands 301 and 302 may include, therefore, a plurality of
substantially aligned filaments that are substantially formed from
a thermoplastic polymer material. As such, at least ninety-five
percent, ninety-nine percent, or one-hundred percent of a material
of the filaments or other material forming strands 301 and 302 may
be a thermoplastic polymer material, such as thermoplastic
polyurethane. When strands 301 and 302 are formed as a filament,
cable, cord, or rope, such strands may also be substantially formed
from a thermoplastic polymer material.
[0086] As a second example of a textile, a knitted textile 400 is
depicted in FIGS. 9 and 10 as including at least one strand 401
that forms a plurality of intermeshed loops. More particularly,
sections of strand 401 forms various loops that extend through and
are intermeshed with other loops to define a variety of courses and
wales. As depicted, the courses are horizontal rows of loops formed
from strand 401, and the wales are vertical columns of loops formed
from strand 401. In manufacturing knitted textile 400, strand 401
is manipulated through a knitting process, which may involve a
knitting machine, to form and intermesh the loops, thereby defining
the various of courses and wales. Although a relatively simple knit
structure is depicted, numerous warp knit and weft knit structures
may be formed through flat knitting, wide tube circular knitting,
narrow tube circular knit jacquard, single knit circular knit
jacquard, double knit circular knit jacquard, double needle bar
raschel, warp knit jacquard, and tricot for example.
[0087] Although knitted textile 400 is depicted as being formed
from strand 401, multiple strands may be incorporated into the
structure of knitted textile 400. For example, different loops,
different courses, different portions of a single course, different
wales, and different portions of a single wale may be formed from
strands having diverse materials, colors, and properties.
[0088] Strand 401 may have the configuration of a filament, yarn,
thread, cable, cord, or rope. Strand 401 or other strands
incorporated into knitted textile 400 may also exhibit the general
configuration of yarn 100 or thread 200 discussed above. Strand 401
may include, therefore, a plurality of substantially aligned
filaments that are substantially formed from a thermoplastic
polymer material. As such, at least ninety-five percent,
ninety-nine percent, or one-hundred percent of a material of the
filaments or other material forming strand 401 may be a
thermoplastic polymer material, such as thermoplastic polyurethane.
When strand 401 is formed as a filament, cable, cord, or rope, such
strands may also be substantially formed from a thermoplastic
polymer material.
[0089] As a variation, knitted textile 400 may also incorporate an
inlaid strand 402, as depicted in FIG. 11. Inlaid strand 402
extends through the knit structure, thereby passing between the
various loops within knitted textile 400. Although inlaid strand
402 is depicted as extending along a course, inlaid strand 402 may
also extend along a wale. In addition to other types of strands,
inlaid strand 402 may be similar to yarn 100 or thread 200, or
inlaid strand 402 may have another configuration having a plurality
of substantially aligned filaments that are substantially formed
from a thermoplastic polymer material. Advantages of inlaid strand
402 include providing support, stability, and structure. For
example, inlaid strand 402 may assist with limiting stretch or
deformation in areas of knitted textile 400 and in specific
directions. Additional details relating to inlaid strands and
methods of incorporating inlaid strands into the structure of a
knitted textile may be found with reference to U.S. patent
application Ser. No. 13/048,540, which was filed in the U.S. Patent
and Trademark Office on 15 Mar. 2011 and entitled Method Of
Manufacturing A Knitted Component, such application being entirely
incorporated herein by reference.
[0090] Woven textile 300 and knitted textile 400 provide examples
of textile structures that may incorporate yarn 100, thread 200, or
other strands formed from thermoplastic polymer materials. A
variety of other types of textiles may also incorporate similar
strands. For example, textiles formed through crocheting or
intertwining and twisting may have strands with a plurality of
substantially aligned filaments that are substantially formed from
a thermoplastic polymer material. Similarly, mesh textiles, spacer
mesh textiles, jersey textiles, fleece textiles, and terry loop
textiles may have strands with a plurality of substantially aligned
filaments that are substantially formed from a thermoplastic
polymer material.
D. THERMAL BONDING OF YARNS, THREADS, AND TEXTILES
[0091] Thermal bonding is an advantage of thermoplastic polymer
materials not generally present in yarns, threads, and textiles,
for example, formed from natural materials (e.g., cotton, silk) and
thermoset polymer materials. As discussed above, a thermoplastic
polymer material softens or melts when heated and returns to a
solid state when cooled. In addition to permitting molding or
shaping, an element formed from a thermoplastic polymer material
may also be welded, fused, or thermal bonded to another object,
item, or element. That is, the thermoplastic polymer material may
be used to join two elements together through thermal bonding. As
utilized herein, the term "thermal bonding" or variants thereof is
defined as a securing technique between two elements that involves
a softening or melting of a thermoplastic polymer material within
at least one of the elements such that the elements are secured to
each other when cooled. Similarly, the term "thermal bond" or
variants thereof is defined as the bond, link, or structure that
joins two elements through a process that involves a softening or
melting of a thermoplastic polymer material within at least one of
the elements such that the elements are secured to each other when
cooled.
[0092] Examples of thermal bonding include (a) the melting or
softening of two elements incorporating thermoplastic polymer
materials such that the thermoplastic polymer materials intermingle
with each other (e.g., diffuse across a boundary layer between the
thermoplastic polymer materials) and are secured together when
cooled; (b) the melting or softening of an element incorporating a
thermoplastic polymer material such that the thermoplastic polymer
material extends into or infiltrates the structure of a strand
(e.g., extends around or bonds with filaments in the strand) to
secure the elements together when cooled; (c) the melting or
softening of an element incorporating a thermoplastic polymer
material such that the thermoplastic polymer material extends into
or infiltrates the structure of a textile element (e.g., extends
around or bonds with filaments or fibers in the textile element) to
secure the elements together when cooled; and (d) the melting or
softening of an element incorporating a thermoplastic polymer
material such that the thermoplastic polymer material extends into
or infiltrates crevices or cavities formed in another element
(e.g., polymer foam or sheet, plate, structural device) to secure
the elements together when cooled. Thermal bonding may occur when
only one element includes a thermoplastic polymer material or when
both elements include thermoplastic polymer materials. In general,
therefore, thermal bonding involves directly bonding elements to
each other with heat. In some situations, however, stitching or
adhesives may be utilized to supplement the thermal bond or the
joining of elements through thermal bonding.
[0093] One of the factors affecting the degree of fusing is
temperature. As noted above, a thermoplastic polymer material
transitions from a solid state to (a) a softened state when heated
to a glass transition temperature of the thermoplastic polymer
material and (b) a generally liquid state when heated to a melting
temperature of the thermoplastic polymer material. Thermal bonding
may occur when the thermoplastic polymer material is heated to the
glass transition temperature. Greater degrees of thermal bonding,
as discussed below, may occur at elevated temperatures approaching
or exceeding the melting temperature.
[0094] Given that yarn 100, thread 200, woven textile 300, and
knitted textile 400 incorporate thermoplastic polymer materials,
these elements may be subjected to thermal bonding processes. As an
example, FIG. 12 depicts a configuration of yarn 100 with thermal
bonds that fuse various filaments 101. When exposed to sufficient
heat, and possibly pressure, the thermoplastic polymer material of
the various filaments 101 in yarn 100 transitions from a solid
state to either a softened state or a liquid state. Moreover,
filaments 101 may fuse with each other through thermal bonding to
effectively combine two or more filaments 101. Although some of
filaments 101 remain separate from or unfused to other filaments
101, other filaments 101 are thermal bonded to each other in groups
of two, three, four, or more. That is, some thermal bonds fuse only
two filaments 101 to each other, whereas other thermal bonds fuse
three or more filaments 101 to each other. FIG. 13 depicts another
configuration wherein approximately half of filaments 101 remain
separate from or unfused to other filaments 101, whereas the other
half of filaments 101 are all thermal bonded to each other to form
a single mass of thermoplastic polymer material within yarn
100.
[0095] Based upon comparisons between FIGS. 2, 12 and 13, filaments
101 may exhibit a range of thermal bonding extending from (a) a
state where the various filaments 101 remain separate and
identifiable within yarn 100 to (b) a state where the various
filaments 101 combine to form a larger mass of thermoplastic
polymer material within yarn 100. That is, (a) filaments 101 remain
entirely separate from each other, (b) relatively small numbers of
filaments 101 may be thermal bonded to each other, but remain in a
generally filamentous configuration, or (c) numerous filaments 101
may be thermal bonded to each other to form a generally
non-filamentous configuration. Although not depicted, all of
filaments 101 in yarn 100 may be thermal bonded to each other to
effectively combine the thermoplastic polymer material from each of
filaments 101 into a single strand (e.g., similar to a
monofilament). Accordingly, the degree of thermal bonding in yarn
100 may vary considerably.
[0096] Another example of thermal bonding is depicted in FIG. 14,
wherein thread 200 exhibits thermal bonding. More particularly, the
various filaments 202 within yarns 201 of thread 200 are fused to a
degree that is comparable with FIG. 12. Notably, some of filaments
202 from one yarn 201 are fused or thermal bonded with some of
filaments 202 from the other yarn 201. That is, yarns 201 within
thread 200 are thermal bonded to each other, thereby effectively
joining the two yarns 201. As with the thermal bonding of yarn 100
discussed above, thread 200 may exhibit a range of thermal bonding
extending from (a) a state where the various filaments 202 remain
separate and identifiable to (b) a state where the various
filaments 202 combine to form a larger mass of thermoplastic
polymer material. Referring to FIG. 15, for example, each of
filaments 202 of yarns 201 in thread 200 may be thermal bonded to
each other to effectively combine the thermoplastic polymer
material from each yarn 201 into joined strands (i.e., joined
monofilaments). Accordingly, the degree of thermal bonding in
thread 200 may vary considerably.
[0097] A further example of thermal bonding is depicted in FIGS. 16
and 17, wherein woven textile 300 includes a fused region 303. In
comparison with other regions of woven textile 300, in which
strands 301 and 302 are unbonded or unfused to each other, strands
301 and 302 are fused or otherwise thermal bonded to each other in
fused region 303. That is, a thermoplastic polymer material within
one or both of strands 301 and 302 effectively forms a thermal bond
to join strands 301 and 302 to each other in fused region 303.
Given that strands 301 and 302 may have the general configuration
of a filament, yarn, thread, cable, cord, or rope, as well as the
configuration of yarn 100 or thread 200, the manner in which
strands 301 and 302 are fused to each other may vary considerably.
When, for example, strands 301 and 302 exhibit the configuration of
yarn 100, areas where strands 301 and 302 cross or contact each
other may be thermal bonded in a manner that is similar to FIGS. 14
and 15. Moreover, the filaments within strands 301 and 302 may
exhibit a range of thermal bonding extending from (a) a state where
the various filaments remain separate and identifiable to (b) a
state where the various filaments combine to form a larger mass of
thermoplastic polymer material. Similar concepts apply when strands
301 and 302 exhibit the configuration of thread 200 or another type
of strand.
[0098] Woven textile 300 may also exhibit thermal bonding in fused
region 303 when each of strands 301 and 302 have different
configurations or are formed from different materials. When, for
example, warp strand 301 is a filament formed from a thermoplastic
polymer material and weft strand 302 is a thread formed from a
thermoset polymer material, the thermoplastic polymer material in
warp strand 301 may infiltrate the structure of the thread forming
weft strand 302 by extending around filaments in the thread to
secure strands 301 and 302 together when cooled. As another
example, when warp strand 301 is a cord formed from a thermoplastic
polymer material and weft strand 302 is a filament formed from a
thermoset polymer material, the thermoplastic polymer material in
warp strand 301 may infiltrates crevices or cavities in the
filament forming weft strand 302 to secure strands 301 and 302
together when cooled.
[0099] The degree to which strands 301 and 302 melt or transition
from a filamentous to a non-filamentous state when forming the
thermal bonds may also vary. Referring again to FIGS. 16 and 17,
strands 301 and 302 remain identifiable within the structure of
fused region 303. Individual filaments may also remain identifiable
similar to FIGS. 12 and 14. In FIGS. 18 and 19, however, the
thermoplastic polymer material from strands 301 and 302 has melted
into a non-filamentous state that effectively forms a solid polymer
sheet in a fused region 304, with neither strands 301 and 302 nor
individual filaments in strands 301 and 302 being identifiable. As
such, thermal bonding in woven textile 300 may range from (a) a
state where the various elements remain separate and identifiable,
as in fused region 303, to (b) a state where the various elements
combine to form a larger mass of thermoplastic polymer material, as
in fused region 304.
[0100] A variety of factors relating to the configuration of woven
textile 300 and the processes by which fused regions 303 and 304
are formed determine the degree to which strands 301 and 302 are
thermal bonded. As examples, factors that determine the degree of
fusing include (a) the particular thermoplastic polymer material
forming strands 301 and 302, (b) the temperature (e.g., glass
transition and melting temperatures) that fused regions 303 and 304
are exposed to, (c) the pressure that fused regions 303 and 304 are
exposed to, and (d) the time at which fused regions 303 and 304 are
exposed to the elevated temperature and/or pressure. By varying
these factors, the degree of fusing or thermal bonding that results
within fused regions 303 and 304 may also be varied. Similar
factors also apply to the thermal bonding within yarn 100 and
thread 200.
[0101] Another example of thermal bonding is depicted in FIGS. 20
and 21, wherein knitted textile 400 includes a fused region 403. In
comparison with other regions of knitted textile 400, in which
strand 401 is unbonded or unfused to itself, strand 401 is fused or
otherwise thermal bonded to itself in fused region 403. That is, a
thermoplastic polymer material within one portion of strand 401
effectively forms a thermal bond with another portion of strand 401
in fused region 403. Given that strand 401 may have the general
configuration of a filament, yarn, thread, cable, cord, or rope, as
well as the configuration of yarn 100 or thread 200, the manner in
which portions of strand 401 are fused to each other may vary
considerably. When, for example, strand 401 exhibits the
configuration of yarn 100, the portions of strand 401 that cross or
contact each other may be thermal bonded in a manner that is
similar to FIGS. 14 and 15. Moreover, the filaments within strand
401 may exhibit a range of thermal bonding extending from (a) a
state where the various filaments remain separate and identifiable
to (b) a state where the various filaments combine to form a larger
mass of thermoplastic polymer material. Similar concepts apply when
strand 401 exhibits the configuration of thread 200 or another type
of strand.
[0102] Knitted textile 400 may also exhibit thermal bonding in
fused region 403 when strand 401 and one or more additional strands
(e.g., inlaid strand 402) are incorporated into knitted textile
400. In this configuration, thermal bonding may be similar to the
various examples provided above for different types of strands 301
and 302 in fused region 303 of woven textile 300. In effect,
thermal bonding may join strands within fused region 403 that have
different configurations or are formed from different
materials.
[0103] The degree to which strand 401 melts or transitions from a
filamentous to a non-filamentous state when forming the thermal
bonds may also vary. Referring again to FIGS. 20 and 21, sections
of strand 401 remain identifiable within the structure of fused
region 403. Individual filaments may also remain identifiable
similar to FIG. 14. In FIGS. 22 and 23, however, the thermoplastic
polymer material from strand 401 has melted into a non-filamentous
state that effectively forms a solid polymer sheet in a fused
region 404, with neither strand 401 nor individual filaments in
strand 401 being identifiable. As such, thermal bonding in knitted
textile 400 may range from (a) a state where the various elements
remain separate and identifiable, as in fused region 403, to (b) a
state where the various elements combine to form a larger mass of
thermoplastic polymer material, as in fused region 404.
[0104] As with woven textile 300, factors that determine the degree
of fusing in knitted textile 400 include (a) the particular
thermoplastic polymer material forming strand 401, (b) the
temperature (e.g., glass transition and melting temperatures) that
fused regions 403 and 404 are exposed to, (c) the pressure that
fused regions 403 and 404 are exposed to, and (d) the time at which
fused regions 403 and 404 are exposed to the elevated temperature
and/or pressure. By varying these factors, the degree of fusing or
thermal bonding that results within fused regions 403 and 404 may
also be varied.
[0105] Based upon the above discussion, yarn 100, thread 200, other
strands, textiles 300 and 400, and other textiles may exhibit
fusing or may form thermal bonds due to the presence of a
thermoplastic polymer material. As presented in the various
examples, filaments 101 within yarn 100 may form thermal bonds with
each other to various degrees, and filaments 202 or yarns 201
within thread 200 may form thermal bonds with each other to various
degrees. Moreover, woven textile 300 may have a fused region 303 or
304 and a remaining unfused region, with warp strand 301 and weft
strand 302 being thermal bonded to each other in fused regions 303
and 304 and being unbonded to each other in the unfused region.
Similarly, knitted textile 400 may include a fused region 403 or
404 and a remaining unfused region, with a section of strand 401
being thermal bonded to a different section of strand 401 in fused
regions 403 and 404. Although fused regions 303, 304, 403, and 404
are shown as being a relatively small part of textiles 300 and 400,
a larger part or substantially all of textiles 300 and 400 may
exhibit thermal bonding.
E. PROPERTIES OF FUSED REGIONS
[0106] The properties of fused regions 303 and 304 may be different
than the properties of unfused regions in woven textile 300. In
configurations where woven textile 300 has multiple fused regions,
the properties of one of the fused regions may be different than
the properties of another of the fused regions. For example, FIG.
24 depicts a configuration of woven textile 300 having both fused
regions 303 and 304. In comparison, the properties of fused region
303 may be different than the properties of fused region 304 to
impart different properties to different areas of woven textile
300.
[0107] In manufacturing woven textile 300 and forming fused regions
303 and 304, specific properties may be applied to woven textile
300 in the areas of fused regions 303 and 304. More particularly,
the shapes of fused regions 303 and 304, positions of fused regions
303 and 304, sizes of fused regions 303 and 304, degree to which
strands 301 and 302 are fused within fused regions 303 and 304, and
other aspects of woven textile 300 may be varied to impart specific
properties to specific areas of woven textile 300. As an example,
fused regions 303 and 304 have different shapes (e.g., square and
circular) in FIG. 24. Accordingly, woven textile 300 may be
engineered, designed, or otherwise structured to have particular
properties in different areas.
[0108] Examples of properties that may be varied through the
addition or the configuration of fused regions 303 and 304 include
permeability, durability, and stretch-resistance. By forming one of
fused regions 303 and 304 in a particular area of woven textile
400, the permeability of that area generally decreases, whereas
both durability and stretch-resistance generally increases. As
discussed in greater detail below, the degree to which strands 301
and 302 are fused to each other has a significant effect upon the
change in permeability, durability, and stretch-resistance. Other
factors that may affect permeability, durability, and
stretch-resistance include the shapes, positions, and sizes of
fused regions 303 and 304, as well as the specific thermoplastic
polymer material forming strands 301 and 302.
[0109] Permeability generally relates to ability of air, water, and
other fluids (whether gaseous or liquid) to pass through or
otherwise permeate woven textile 300. Depending upon the degree to
which strands 301 and 302 are fused to each other, the permeability
may vary significantly. In general, the permeability is highest in
areas of woven textile 300 where strands 301 and 302 are fused the
least, and the permeability is lowest in areas of woven textile 300
where strands 301 and 302 are fused the most. As such, the
permeability may vary along a spectrum depending upon the degree to
which strands 301 and 302 are fused to each other. Areas of woven
textile 300 that are separate from fused regions 303 and 304 (i.e.,
unfused areas of woven textile 300) generally exhibit a relatively
high permeability. Due to the openings between strands 301 and 302,
fused region 303 may also exhibit a relatively high permeability,
but the permeability is generally less than in areas separate from
fused regions 303 and 304. Due to the non-filamentous state that
effectively forms a solid polymer sheet, fused region 304 exhibits
a relatively low permeability.
[0110] Durability generally relates to the ability of woven textile
300 to remain intact, cohesive, or otherwise undamaged, and may
include resistances to wear, abrasion, and degradation from
chemicals and light. Depending upon the degree to which strands 301
and 302 are fused to each other, the durability may vary
significantly. Although the durability of any portion of woven
textile 300 may be considered high, the durability is lowest in
areas of woven textile 300 where strands 301 and 302 are fused the
least, and the durability is highest in areas of woven textile 300
where strands 301 and 302 are fused the most. As such, the
durability may vary along a spectrum depending upon the degree to
which strands 301 and 302 are fused to each other. Moreover, fused
region 303 may have lesser durability than fused region 304. Other
factors that may affect the general durability of fused regions 303
and 304 and other areas of woven textile 300 include the initial
thickness and density of woven textile 300 and the type of
thermoplastic polymer material forming strands 301 and 302.
[0111] Stretch-resistance generally relates to the ability of woven
textile 300 to resist stretching when subjected to a textile force.
As with permeability and durability, the stretch-resistance of
woven textile 300 may vary significantly depending upon the degree
to which strands 301 and 302 are fused to each other. Although the
stretch-resistance of any portion of woven textile 300 may be
considered high, the stretch-resistance is lowest in areas of woven
textile 300 where strands 301 and 302 are fused the least, and the
stretch-resistance is highest in areas of woven textile 300 where
strands 301 and 302 are fused the most. The thermoplastic polymer
material or other materials utilized for woven textile 300 may be
considered elastomeric or may stretch at least one-hundred percent
prior to tensile failure. Although the stretch-resistance of woven
textile 300 may be greater in areas where strands 301 and 302 are
fused the most, fused region 304 may still be elastomeric or may
stretch at least one-hundred percent prior to tensile failure.
Other factors that may affect the general stretch properties of
fused regions 303 and 304 and other areas of woven textile 300
include the initial thickness and density of woven textile 300 and
the type of thermoplastic polymer material forming strands 301 and
302.
[0112] As discussed in greater detail below, woven textile 300 may
be incorporated into a variety of products, including various
articles of apparel (e.g., shirts, footwear). Taking a shirt as an
example, woven textile 300 may form a majority of the shirt,
including a torso region and two arm regions. Given that moisture
may accumulate within the shirt from perspiration, a majority of
the shirt may be formed from portions of woven textile 300 that do
not include fused regions 303 and 304 in order to provide a
relatively high permeability. Given that elbow areas of the shirt
may be subjected to relatively high abrasion as the shirt is worn,
some of fused regions 303 and 304 may be located in the elbow areas
to impart greater durability. Additionally, given that the neck
opening may be stretched as the shirt is put on an individual and
taken off the individual, one of fused regions 303 and 304 may be
located around the neck opening to impart greater
stretch-resistance. Accordingly, one material (i.e., woven textile
300) may be used throughout the shirt, but by fusing different
areas to different degrees, the properties may be
advantageously-varied in different areas of the shirt.
[0113] The above discussion focused primarily on the properties of
permeability, durability, and stretch-resistance. A variety of
other properties may also be varied through the addition or the
configuration of fused regions 303 and 304. For example, the
overall density of woven textile 300 may be increased as the degree
of fusing increases. The transparency of woven textile 300 may also
be increased as the degree of fusing increases. Depending upon
various factors, the saturation of a color of woven textile 300 may
also increase as the degree of fusing increases. Fused regions 303
and 304 may also contrast visually with other areas. The overall
thickness of woven textile 300 may decrease as the degree of fusing
increases. The degree to which woven textile 300 recovers after
being stretched, the overall flexibility of woven textile 300, and
resistance to various modes of failure may also vary depending upon
the degree of fusing. Accordingly, a variety of properties may be
varied by forming fused regions similar to fused regions 303 and
304.
[0114] Although the above discussion focused upon woven textile
300, similar concepts apply to knitted textile 400. As such, the
properties of fused regions 403 and 404 may be different than the
properties of unfused regions in knitted textile 400. In
configurations where knitted textile 400 has multiple fused regions
403 and 404, the properties of fused region 403 may be different
than the properties of one of fused region 404. Moreover, the
properties of one of fused regions 403 may be different than the
properties of another of fused regions 403. In addition to varying
the degree of fusing, the shapes of multiple fused regions 403 and
404 and other aspects of knitted textile 400 may be varied to
impart specific properties to specific areas. Accordingly, knitted
textile 400 may be engineered, designed, or otherwise structured to
have particular properties in different areas, including the
properties of permeability, durability, and stretch-resistance.
F. COMPOSITE ELEMENTS
[0115] A composite element 500 is depicted in FIGS. 25 and 26 as
including a first component 501 and a second component 502 that lay
adjacent to each other and are thermal bonded to each other.
Although component 501 and 502 are depicted as having similar
dimensions, first component 501 may have a lesser or greater
length, a lesser or greater width, or a lesser or greater thickness
than second component 502. That is, the relative dimensions of
components 501 and 502 may vary considerably depending upon the
product in which composite element 500 is intended to be
incorporated.
[0116] In order to facilitate thermal bonding, at least one of
components 501 and 502 includes a thermoplastic polymer material.
Either or both of components 501 and 502 may be woven textile 300,
knitted textile 400, other textiles that incorporate yarn 100 or
thread 200, or other textiles that incorporate a thermoplastic
polymer material. Moreover, one of components 501 and 502 may be
another textile (e.g., knitted, woven, non-woven), an element of
polymer foam, a polymer sheet, or a plate. As examples, (a) each of
components 501 and 502 may be woven textile 300, (b) each of
components 501 and 502 may be knitted textile 400, (c) first
component 501 may be woven textile 300 and second component 502 may
be knitted textile 400, (d) first component 501 may be woven
textile 300 and second component 502 may be another textile formed
from cotton, silk, thermoset polymer filaments, or other materials
that do not include a thermoplastic polymer material, (e) first
component 501 may be knitted textile 400 and second component 502
may be an element of polymer foam formed from either thermoplastic
or thermoset polymer material, (f) first component 501 may be woven
textile 300 and second component 502 may be a polymer sheet formed
from either thermoplastic or thermoset polymer material, or (g)
first component 501 may be knitted textile 400 and second component
502 may be a plate formed from metal, wood, or a rigid polymer
formed from either thermoplastic or thermoset polymer material.
[0117] As a further example, first component 501 may be woven
textile 300. If second component 502 is another textile that
absorbs or wicks water, then the combination of woven textile 300
and second component 502 may be suitable for articles of apparel
utilized during athletic activities where an individual wearing the
apparel is likely to perspire. If second component 502 is a
compressible material, such as an element of polymer foam, then the
combination of woven textile 300 and second component 502 may be
suitable for articles of apparel where cushioning (i.e.,
attenuation of impact forces) is advantageous, such as padding for
athletic activities that may involve contact or impact with other
athletes, equipment, or the ground. If second component 502 is a
polymer sheet or plate, then the combination of woven textile 300
and second component 502 may be suitable for articles of apparel
that impart protection from acute impacts. Similar combinations may
be formed where first component 501 is knitted textile 400.
Accordingly, a variety of materials or other components maybe
joined through thermal bonding to either of textiles 300 and 400
form composite elements with additional properties.
[0118] A general manufacturing process for forming composite
element 500 will now be discussed with reference to FIGS. 27A-27C.
Initially, components 501 and 502 are located between a heat press
having a pair of platens 11, as depicted in FIG. 27A. Platens 11
then translate or otherwise move toward each other in order to
compress or induce contact between components 501 and 502, as
depicted in FIG. 27B. While compressed, heat is applied to form the
thermal bond that joins components 501 and 502. That is, the
temperatures of components 501 and 502 are elevated to at least a
glass transition temperature of a thermoplastic polymer material in
one or both of components 501 and 502, thereby causing softening or
melting of the thermoplastic polymer material at the interface
between components 501 and 502. Depending upon the materials of
both components 501 and 502, as well as the overall configuration
of components 501 and 502, only one of platens 11 or both of
platens 11 may be heated to elevate the temperatures of components
501 and 502 through conduction. Upon separating platens 11, as
depicted in FIG. 27C, the thermal bonded composite element 500 may
be removed and permitted to cool.
[0119] Although the general process discussed above may be utilized
to form composite element 500, other methods may also be utilized.
Rather than components 501 and 502 through conduction, other
methods that include radio frequency heating, ultrasonic heating,
radiant heating, laser heating, or chemical heating may be
utilized. In some processes, radiant heating may utilize to raise
the temperature of at least one of components 501 and 502 prior to
being compressed between platens 11. An advantage of utilizing
radiant heating to elevate the temperature of only the surfaces
forming the thermal bond is that the thermoplastic polymer material
within other portions of components 501 and 502 may not heated
significantly. In some processes, stitching or adhesives may also
be utilized between components 501 and 502 to supplement the
thermal bond.
[0120] Using the process discussed above, the thermoplastic polymer
material in either of components 501 and 502 may be utilized to
secure components 501 and 502 to each other. A thermoplastic
polymer material melts when heated and returns to a solid state
when cooled sufficiently. Based upon this property of thermoplastic
polymer materials, thermal bonding processes may be utilized to
form a thermal bond that joins components 501 and 502 to each
other. The configuration of the thermal bond at least partially
depends upon the materials and structure of components 501 and 502.
As a first example, each of components 501 and 502 may be woven
textile 300. Upon heating, the thermoplastic polymer material from
each element of woven textile 300 may intermingle with each other
to secure components 501 and 502 to each other when cooled. Similar
processes may be utilized when each of components 501 and 502 are
knitted textile 400 or when first component 501 is woven textile
300 and second component 502 is knitted textile 400. As a second
example, first component 501 may be woven textile 300 and second
component 502 may be another textile formed from cotton, silk, or
thermoset polymer filaments. Upon heating, the thermoplastic
polymer material of woven textile 300 may extend around or bond
with filaments in the other textile to secure components 501 and
502 to each other when cooled. As a third example, first component
501 may be knitted textile 400 and second component 502 may be an
element of polymer foam (or a polymer sheet or plate) formed from a
thermoplastic polymer material. Upon heating, the thermoplastic
polymer materials of knitted textile 400 and the polymer foam may
intermingle with each other to secure components 501 and 502 to
each other when cooled. If, however, the polymer foam has a glass
transition temperature that is higher than the thermoplastic
polymer material of knitted textile 400, then the thermoplastic
polymer material of knitted textile 400 may extend into the
structure, crevices, or cavities of the polymer foam to secure
components 501 and 502 to each other when cooled. As a fourth
example, first component 501 may be knitted textile 400 and second
component 502 may be an element of polymer foam (or a polymer sheet
or plate) formed from a thermoset polymer material. Upon heating,
the thermoplastic polymer material of knitted textile 400 may
extend into the structure, crevices, or cavities of the polymer
foam to secure components 501 and 502 to each other when cooled.
Accordingly, a thermal bond may be utilized to join components 501
and 502 even when components 501 and 502 have a variety of
structures or are formed from a diverse range of materials.
[0121] In order to impart varying properties to composite element
500, either of components 501 and 502 may include various fused
regions, similar to fused regions 303, 304, 403, and 404. Referring
to FIG. 28, for example, composite element 500 is depicted as
incorporating woven textile 300 as first component 501, and a fused
region 304 is formed in woven textile 300. In some processes fused
region 304 (or fused region 303) may be formed prior to joining
woven textile 300 with second component 502. In other processes,
however, fused region 304 (or fused region 303) may be formed
during the thermal bonding process or following the thermal bonding
process. Accordingly, fused regions 303 and 304 may be formed at
any stage of the manufacturing process for composite elements.
Although composite element 500 in this example incorporates woven
textile 300, knitted textile 400 may also be utilized in a similar
manner. That is, a composite element incorporating knitted textile
400 may also include various fused regions 403 and 404 to impart
varying properties.
G. THERMAL BONDED SEAM CONFIGURATIONS
[0122] When incorporated into products, such as apparel, textile
elements are often joined at various seams. Although stitching and
adhesive bonding may be utilized to form a seam between the textile
elements, the seam may also be formed through a thermal bonding
process when at least one of the textile elements includes a
thermoplastic polymer material. That is, a thermal bond may be
utilized to form the seam in products that incorporate woven
textile 300, knitted textile 400, or other textiles that
incorporate a thermoplastic polymer material.
[0123] A seam element 600 is depicted in FIGS. 29 and 30 as
including a first component 601 and a second component 602 with
edge areas that are thermal bonded at a seam 603. Although
component 601 and 602 are depicted as having similar dimensions,
first component 601 may have a lesser or greater length, a lesser
or greater width, or a lesser or greater thickness than second
component 602. That is, the relative dimensions of components 601
and 602 may vary considerably depending upon the product in which
seam 603 is intended to be incorporated.
[0124] In order to facilitate thermal bonding at seam 603, at least
one of components 601 and 602 includes a thermoplastic polymer
material. Either or both of components 601 and 602 may be woven
textile 300, knitted textile 400, other textiles that incorporate
yarn 100 or thread 200, or other textiles that incorporate a
thermoplastic polymer material. Moreover, one of components 601 and
602 may be another textile (e.g., knitted, woven, non-woven), an
element of polymer foam, or a polymer sheet, for example. As
examples, (a) each of components 601 and 602 may be woven textile
300, (b) each of components 601 and 602 may be knitted textile 400,
(c) first component 601 may be woven textile 300 and second
component 602 may be knitted textile 400, (d) first component 601
may be woven textile 300 and second component 602 may be another
textile formed from cotton, silk, thermoset polymer filaments, or
other materials that do not include a thermoplastic polymer
material, (e) first component 601 may be knitted textile 400 and
second component 602 may be an element of polymer foam formed from
either thermoplastic or thermoset polymer material, or (f) first
component 601 may be woven textile 300 and second component 602 may
be a polymer sheet formed from either thermoplastic or thermoset
polymer material.
[0125] A general manufacturing process for forming seam 603 will
now be discussed with reference to FIGS. 31A-31D. Initially,
components 601 and 602 are located between a pair of seam-forming
dies 12, as depicted in FIG. 31A. Seam-forming dies 12 then
translate or otherwise move toward each other in order to compress
or induce contact between edge areas components 601 and 602, as
depicted in FIG. 31B. In order to form the thermal bond and join
the edge areas of components 601 and 602, seam-forming dies 12
apply heat to the edge areas. That is, seam-forming dies 12 elevate
the temperature of the edge areas of components 601 and 602 to
cause softening or melting of the thermoplastic polymer material at
the interface between the edge areas. Although the temperature of
the edge areas is generally raised to at least the glass-transition
temperature of the thermoplastic polymer material forming one or
both of components 601 and 602, the temperature may also exceed the
melting temperature. Upon separating seam-forming dies 12, as
depicted in FIG. 31C, seam 603 is formed between the edge areas of
components 601 and 602. After being permitted to cool, components
601 and 602 may be unfolded, as depicted in FIG. 31D. Seam 603 may
also be trimmed to limit the degree to which the end areas protrude
outward at seam 603. Rather than heating the edge areas of
components 601 and 602 through conduction, other methods that
include radio frequency heating, ultrasonic heating, radiant
heating, laser heating, or chemical heating may be utilized.
[0126] As with the formation of fused regions 303, 304, 403, and
404, the formation of seam 603 involves softening or melting the
thermoplastic polymer material in one or both of components 601 and
602. Depending upon the temperature and pressure applied to the
edge areas of components 601 and 602, as well as the time that the
edge areas are heated and compressed, for example, the degree to
which the thermoplastic polymer material in components 601 and 602
softens or melts may vary significantly. As such, the thermal bond
at seam 603 may range from (a) a state where filaments or strands
in components 601 and 602 remain separate and identifiable, as in
fused regions 303 and 403, to (b) a state where filaments or
strands in components 601 and 602 form a larger mass of
thermoplastic polymer material, as in fused regions 304 and
404.
[0127] Using the process discussed above, the thermoplastic polymer
material in either of components 601 and 602 may be utilized to
secure components 601 and 602 to each other at seam 603. The
configuration of the thermal bond at seam 603 at least partially
depends upon the materials and structure of components 601 and 602.
As a first example, each of components 601 and 602 may be woven
textile 300. Upon heating, the thermoplastic polymer material from
each element of woven textile 300 may intermingle with each other
to secure components 601 and 602 to each other when cooled. Similar
processes may be utilized when each of components 601 and 602 are
knitted textile 400 or when first component 601 is woven textile
300 and second component 602 is knitted textile 400. As a second
example, first component 601 may be woven textile 300 and second
component 602 may be another textile formed from cotton, silk, or
thermoset polymer filaments. Upon heating, the thermoplastic
polymer material of woven textile 300 may extend around or bond
with filaments in the other textile to secure components 601 and
602 to each other when cooled. As a third example, first component
601 may be knitted textile 400 and second component 602 may be an
element of polymer foam (or a polymer sheet) formed from a
thermoplastic polymer material. Upon heating, the thermoplastic
polymer materials of knitted textile 400 and the polymer foam may
intermingle with each other to secure components 601 and 602 to
each other when cooled. If, however, the polymer foam has a glass
transition temperature that is higher than the thermoplastic
polymer material of knitted textile 400, then the thermoplastic
polymer material of knitted textile 400 may extend into the
structure, crevices, or cavities of the polymer foam to secure
components 601 and 602 to each other when cooled. As a fourth
example, first component 601 may be knitted textile 400 and second
component 602 may be an element of polymer foam (or a polymer
sheet) formed from a thermoset polymer material. Upon heating, the
thermoplastic polymer material of knitted textile 400 may extend
into the structure, crevices, or cavities of the polymer foam to
secure components 601 and 602 to each other when cooled.
Accordingly, a thermal bond forming seam 603 may be utilized to
join components 601 and 602 even when components 601 and 602 have a
variety of structures or are formed from a diverse range of
materials.
[0128] In order to impart varying properties to seam element 600,
either of components 601 and 602 may include various fused regions.
Moreover, the fused regions may extend across seam 603 As an
example of this, FIG. 32 depicts seam element 600 as incorporating
woven textile 300 for first component 601 and knitted textile 400
as second component 602. Woven textile 300 includes a fused region
303 in an area spaced from seam 603, and knitted textile 400
includes a fused region 403 in an area spaced from seam 603. Seam
element 600 also includes a larger fused region that extends across
seam 603 and includes elements of both fused regions 304 and 404.
In some processes, one or more of fused regions 303, 304, 403, and
404 may be formed prior to joining components 601 and 602 at seam
603. In other processes, however, one or more of fused regions 303,
304, 403, and 404 may be formed during the thermal bonding process
or following the thermal bonding process that forms seam 603.
Accordingly, fused regions 303, 304, 403, and 404 may be formed at
any stage of the process for forming seam 603.
[0129] During the thermal bonding process discussed above, the edge
areas of components 601 and 602 are heated and compressed. In
addition to forming seam 603, the heating and compression may also
cause the edge areas of components 601 and 602 to compress or
reduce in thickness. More particularly, processes that form a
thermal bond, as at seam 603, may effectively cause thinning in the
area of the thermal bond. This effect may be seen in FIG. 30, as
well as various other figures discussed below. Although not always
depicted, similar effects may occur at any of fused regions 303,
304, 403, and 404 or at any other location where thermal bonding or
fusing occurs.
[0130] Whereas components 601 and 602 curve at seam 603 and
protrude outward, other seam configurations may have a more planar
or flat configuration. Referring to FIGS. 33 and 34, for example,
seam component 600 includes components 601 and 602, which are
joined to form a seam 604. In this configuration, an edge area of
first component 601 overlaps and is joined with an edge of second
component 602 at seam 604. Although a thermal bond is utilized to
join components 601 and 602 at seam 604, stitching or adhesive
bonding may also be utilized to reinforce seam 604.
[0131] A general manufacturing process for forming seam 604 will
now be discussed with reference to FIGS. 35A-35C. Initially,
components 601 and 602 are positioned in an overlapping
configuration between seam-forming dies 12, as depicted in FIG.
35A. Seam-forming dies 12 then translate or otherwise move toward
each other in order to compress or induce contact between edge
areas of components 601 and 602, as depicted in FIG. 35B. In order
to form the thermal bond and join the edge areas of components 601
and 602, seam-forming dies 12 apply heat to the edge areas. That
is, seam-forming dies 12 elevate the temperature of the edge areas
of components 601 and 602 to cause softening or melting of the
thermoplastic polymer material at the interface between the edge
areas, thereby inducing thermal bonding and forming seam 604.
Although the temperature of the edge areas is generally raised to
at least the glass-transition temperature of the thermoplastic
polymer material forming one or both of components 601 and 602, the
temperature may also exceed the melting temperature. Upon
separating seam-forming dies 12, as depicted in FIG. 35C,
components 601 and 602 are permitted to cool and the manufacturing
process for forming seam 604 is complete.
H. STITCHED AND THERMAL BONDED SEAM CONFIGURATIONS
[0132] Thermal bonding is utilized to join components 601 and 602
at the various seams 603 and 604 discussed above. Although thermal
bonding alone is sufficient, stitching or adhesive bonding may also
be utilized to reinforce seams 603 and 604. Moreover, stitching may
be utilized to temporarily join or otherwise pre-join components
601 and 602 prior to thermal bonding. When the stitching (e.g.,
yarn, thread, monofilament) incorporates a thermoplastic polymer
material, the stitching may also form a thermal bond with each of
components 601 and 602. Depending upon the temperature at which
thermal bonding occurs, the stitching may also melt into the
structure of components 601 and 602.
[0133] Referring to FIG. 36, components 601 and 602 are joined to
form seam 603. At least one of components 601 and 602 includes a
thermoplastic polymer material, which we will refer to as a "first
thermoplastic polymer material" for purposes of the present
discussion. As such, components 601 and 602 are thermal bonded to
each other with the first thermoplastic polymer material at seam
603. Additionally, a stitching strand 605 extends through
components 601 and 602 at seam 603, thereby stitching components
601 and 602 together. Stitching strand 605 also includes a
thermoplastic polymer material, which we will refer to as a "second
thermoplastic polymer material" for purposes of the present
discussion. Given that stitching strand 605 includes the second
thermoplastic polymer material, stitching strand 605 may be thermal
bonded to components 601 and 602 with the second thermoplastic
polymer material at seam 603.
[0134] Stitching strand 605 may be a yarn, thread, or monofilament,
for example. In some configurations, stitching strand 605 may have
the general configuration of thread 200. As such, stitching strand
605 may include two or more yarns (e.g., yarns 201) that are
twisted with each other. Moreover, the yarns may include a
plurality of substantially aligned filaments (e.g., filaments 202)
that are substantially formed from the second thermoplastic polymer
material. As such, at least ninety-five percent, ninety-nine
percent, or one-hundred percent of a material of the filaments in
stitching strand 605 may be the second thermoplastic polymer
material. Although stitching strand 605 is depicted as forming a
zigzag stitch, other stitch configurations may be used for joining
components 601 and 602 with stitching strand 605.
[0135] Based upon the discussion above, seam 603 effectively
includes two thermal bonds. The first thermal bond is formed by the
first thermoplastic polymer material from one or both of components
601 and 602. Although the first thermal bond primarily joins
components 601 and 602 to each other, thereby forming seam 603, the
first thermal bond may also join stitching strand 605 to components
601 and 602. The second thermal bond is formed by the second
thermoplastic polymer material from stitching strand 605. Although
the second thermal bond primarily joins stitching strand 605 to
components 601 and 602, the second thermal bond may also join (a)
sections of stitching strand 605 to each other or (b) components
601 and 602 to each other. An advantage of utilizing the first and
second thermal bonds relates to strength. That is, seam 603 may
exhibit greater strength than seams that are only utilize one of
stitching or thermal bonding.
[0136] The first thermoplastic polymer material and the second
thermoplastic polymer material may be the same thermoplastic
polymer material. That is, the thermoplastic polymer materials of
components 601 and 602 and stitching strand 605 may be the same
thermoplastic polymer material (e.g., both being thermoplastic
polyurethane) with common glass transition and melting
temperatures. Similarly, the first thermoplastic polymer material
and the second thermoplastic polymer material may be the same
thermoplastic polymer material (e.g., both being thermoplastic
polyurethane), but with different glass transition and melting
temperatures. As an example, the first and second thermoplastic
polymer materials may be thermoplastic polyurethane, with the first
thermoplastic polymer material having higher glass transition and
melting temperatures than the second thermoplastic polymer
material. Additionally, the first thermoplastic polymer material
and the second thermoplastic polymer material may be different
thermoplastic polymer materials, such as thermoplastic polyurethane
and thermoplastic polyolefin.
[0137] An advantage of incorporating the same thermoplastic polymer
material into components 601 and 602 and stitching strand 605
relates to thermal bonding compatibility. Although different
thermoplastic polymer materials may form thermal bonds with each
other, thermal bonds may form more easily and with greater strength
when components 601 and 602 and stitching strand 605 are formed
from the same thermoplastic polymer material. A further advantage
may be gained when components 601 and 602 and stitching strand 605
include the same thermoplastic polymer material, but with different
glass transition and melting temperatures. More particularly, by
configuring components 601 and 602 to have a different glass
transition and melting temperature than stitching strand 605, the
degree to which the first thermoplastic polymer material in
components 601 and 602 softens or melts may be less than the degree
to which the second thermoplastic polymer material in stitching
strand 605 softens or melts when forming (a) the first thermal bond
between components 601 and 602 and (b) the second thermal bond
between stitching strand 605 and components 601 and 602.
[0138] The degree to which individual yarns or filaments within
stitching strand 605 soften or melt when heated to form the second
thermal bond with components 601 and 602 may vary significantly.
Referring again to FIG. 36, stitching strand 605 is clearly seen as
stitching components 601 and 602 together. Although stitching
strand 605 may be thermal bonded with components 601 and 602,
stitching strand 605 remains coherent in this configuration,
possibly with individual yarns or filaments within stitching strand
605 remaining identifiable. In this configuration, the second
thermoplastic polymer material of stitching strand 605 may form
thermal bonds at areas of contact with components 601 and 602, but
may not melt to form thermal bonds in other areas. As another
example, FIG. 37A depicts stitching strand 605 as having a less
coherent structure, which indicates some degree of melting in
stitching strand 605. That is, the second thermoplastic polymer
material of stitching strand 605 may have melted so as to extend
around yarns or filaments in components 601 and 602, and some of
the second thermoplastic polymer material may have been wicked or
otherwise drawn into the filamentous structure of components 601
and 602. Referring to FIG. 37B, stitching strand 605 has an even
less coherent structure, which indicates a greater degree of
melting in stitching strand 605. That is, the second thermoplastic
polymer material of stitching strand 605 may have melted so as to
extend around more distant yarns or filaments in components 601 and
602, and a greater amount of the second thermoplastic polymer
material may have been wicked or otherwise drawn into the
filamentous structure of components 601 and 602. Finally, FIG. 37C
depicts a configuration wherein stitching strand 605 has
significantly melted and is almost entirely wicked or otherwise
drawn into the filamentous structure of components 601 and 602.
Although the second thermoplastic polymer material remains within
seam 305, stitching strand 605 is entirely non-coherent and is
effectively absorbed or otherwise integrated into the structure of
components 601 and 602. The degree to which individual yarns or
filaments within stitching strand 605 soften or melt when heated to
form the thermal bond may affect the strength of seam 305, as well
as the aesthetic properties of articles of apparel or other
products that incorporate seam 603.
[0139] Comparisons between FIGS. 36 and 37A-37C demonstrate
variations in the degree to which stitching strand 605 softens or
melts when forming the thermal bond with the elements of components
601 and 602. Although not depicted, the thermal bond formed by the
first thermoplastic polymer material from the elements of
components 601 and 602 may vary in a similar manner. In many
configurations, however, the first thermoplastic polymer material
of components 601 and 602 may melt or soften to a lesser degree
than the second thermoplastic polymer material of stitching strand
605. An advantage of lesser melting or softening of the first
thermoplastic polymer material is that a fibrous or filamentous
structure of components 601 and 602, when formed from textiles
(e.g., textile 200 or 300), remains intact or otherwise coherent.
When utilized in articles of apparel, the lesser melting or
softening of the first thermoplastic polymer material may ensure
that seam 603 remain flexible and does not form hard areas of the
apparel that may cause discomfort to the wearer. Additionally, the
lesser melting or softening of the first thermoplastic polymer
material in one or both of components 601 and 602 may enhance the
aesthetic properties of the apparel.
[0140] In order to ensure that the first thermoplastic polymer
material of components 601 and 602 melts or softens to a lesser
degree than the second thermoplastic polymer material of stitching
strand 605, different melting and glass transition temperatures may
be selected for each of the first and second thermoplastic polymer
materials. More particularly, the melting and glass transition
temperatures of the first thermoplastic polymer material may be
higher than the respective melting and glass transition
temperatures of the second thermoplastic polymer material. That is,
the melting temperature of the first thermoplastic polymer material
is higher than the melting temperature of the second thermoplastic
polymer material, and the glass transition temperature of the first
thermoplastic polymer material is higher than the glass transition
temperature of the second thermoplastic polymer material. Depending
upon the desired degree of melting or softening of the second
thermoplastic polymer material, as in FIGS. 36 and 37A-37C, the
melting temperature of the second thermoplastic polymer material
may be higher or lower than the glass transition temperature of the
first thermoplastic polymer material. More particularly, for
example, stitching strand 605 may melt more (e.g., FIGS. 37B and
37C) in configurations where the melting temperature of the second
thermoplastic polymer material is lower than the glass transition
temperature of the first thermoplastic polymer material, and
stitching strand 605 may melt less (e.g., FIGS. 36 and 37A) in
configurations where the melting temperature of the second
thermoplastic polymer material is higher than the glass transition
temperature of the first thermoplastic polymer material.
[0141] Although the temperatures may vary significantly, examples
values for the melting and glass transition temperatures of the
first and second thermoplastic polymer materials will now be
discussed. As an example, the first thermoplastic polymer material
of components 601 and 602 may be thermoplastic polyurethane with a
glass transition temperature of 180 degrees Celsius and a melting
temperature of 210 degrees Celsius, and the second thermoplastic
polymer material of stitching strand 605 may be thermoplastic
polyurethane with a glass transition temperature of 140 degrees
Celsius and a melting temperature of 160 degrees Celsius. With
these temperatures, the melting temperature of the second
thermoplastic polymer material is lower than the glass transition
temperature of the first thermoplastic polymer material. As another
example, the first thermoplastic polymer material of components 601
and 602 may be thermoplastic polyurethane with a glass transition
temperature of 170 degrees Celsius and a melting temperature of 210
degrees Celsius, and the second thermoplastic polymer material of
stitching strand 605 may be thermoplastic polyurethane with a glass
transition temperature of 150 degrees Celsius and a melting
temperature of 190 degrees Celsius. With these temperatures, the
melting temperature of the second thermoplastic polymer material is
higher than the glass transition temperature of the first
thermoplastic polymer material. A general manufacturing process for
forming seam 603 with stitching strand 605 will now be discussed
with reference to FIGS. 38A-38E. Initially, components 601 and 602
are located within a stitching machine 13 that dispenses stitching
strand 605 and extends stitching strand 605 through components 601
and 602, thereby stitching edge areas of components 601 and 602
together. In addition to stitching strand 605, stitching machine 13
may also dispense a bobbin strand (not depicted). Stitching machine
13 may be any conventional sewing machine, surger, or device that
performs a stitching operation. Hand stitching may also be
utilized. Although the relatively simple configuration of
components 601 and 602 is depicted, many articles of apparel and
other products may be formed from multiple components or other
material elements. As such, joining components 601 and 602 with
stitching strand 605 serves to temporarily join or otherwise
pre-join components 601 and 602 prior to thermal bonding. In
effect, stitching strand 605 temporarily joins the multiple
components or other elements of an article of apparel or other
product prior to thermal bonding.
[0142] Once properly joined with stitching strand 605, the edge
areas of components 601 and 602 that include stitching strand 605
are located between the pair of seam-forming dies 12, as depicted
in FIG. 38B. Seam-forming dies 12 then translate or otherwise move
toward each other in order to compress or induce contact between
the edge areas of components 601 and 602, as depicted in FIG. 38C.
Seam-forming dies 12 also apply heat to components 601 and 602 and
stitching strand 605 to (a) form a first thermal bond with the
first thermoplastic polymer material from components 601 and 602,
thereby joining components 601 and 602 to each other at seam 603
and (b) form a second thermal bond with the second thermoplastic
polymer material from stitching strand 605, thereby joining
stitching strand 605 to components 601 and 602. Accordingly, heat
from seam-forming dies 12 effectively forms two thermal bonds at
seam 603.
[0143] Upon separating seam-forming dies 12, as depicted in FIG.
38D, seam 603 is formed permitted to cool. Components 601 and 602
may then be unfolded, as depicted in FIG. 38E. Seam 603 may also be
trimmed to limit the degree to which the end areas protrude outward
at seam 603. Rather than heating components 601 and 602 and
stitching strand 605 through conduction, other methods that include
radio frequency heating, ultrasonic heating, radiant heating, laser
heating, or chemical heating may be utilized.
[0144] The degree of thermal bonding in seam 603 may vary
significantly. In some configurations, as discussed above,
advantages may be gained with a lesser degree of melting or
softening of the first thermoplastic polymer material in components
601 and 602. In order to ensure that (a) the fibrous or filamentous
structure of components 601 and 602 remains intact or otherwise
coherent and (b) stitching strand 605 melts or softens to a greater
degree, the melting and glass transition temperatures of the first
thermoplastic polymer material are higher than the respective
melting and glass transition temperatures of the second
thermoplastic polymer material. That is, the melting temperature of
the first thermoplastic polymer material is higher than the melting
temperature of the second thermoplastic polymer material, and the
glass transition temperature of the first thermoplastic polymer
material is higher than the glass transition temperature of the
second thermoplastic polymer material. Moreover, the melting
temperature of the second thermoplastic polymer material may be
higher or lower than the glass transition temperature of the first
thermoplastic polymer material.
[0145] FIG. 39A depicts a graph of the manner in which the
temperature of seam 603 changes between the steps discussed above
for FIGS. 38B-38D. Moreover, this graph shows the situation where
the melting temperature of the second thermoplastic polymer
material is higher than the glass transition temperature of the
first thermoplastic polymer material. Prior to being compressed by
seam forming dies 12, the elements of seam 603 (i.e., components
601 and 602 and stitching strand 605) are at a constant initial
temperature, which may room temperature of a factory. Once
compressed by seam-forming dies 12, the temperature of the elements
of seam 603 rises to exceed the glass transition temperatures of
both the first and second thermoplastic polymer materials. When the
temperature of the elements of seam 603 exceeds the two glass
transition temperatures, thermal bonding may occur (a) between
components 601 and 602 and (b) between stitching strand 605 and
components 601 and 602. That is, both thermal bonds may be formed
when the temperature of the components of seam 603 exceeds the two
glass transition temperatures. Note that the melting temperature of
the second thermoplastic polymer material is higher than the glass
transition temperature of the first thermoplastic polymer material.
As such, the second thermoplastic polymer material in stitching
strand 605 does not reach the melting point in this example. As a
result, stitching strand 605 may melt to a lesser degree, as in the
configurations of FIGS. 36 and 37A. Once seam-forming dies 12
separate and the elements of seam 605 are removed, the temperature
of the components may cool or otherwise decrease to the initial
temperature.
[0146] FIG. 39B also depicts a graph of the manner in which the
temperature of seam 603 changes between the steps discussed above
for FIGS. 38B-38D. Moreover, this graph shows the situation where
the melting temperature of the second thermoplastic polymer
material is lower than the glass transition temperature of the
first thermoplastic polymer material. Prior to being compressed by
seam forming dies 12, the elements of seam 603 (i.e., components
601 and 602 and stitching strand 605) are at a constant initial
temperature, which may room temperature of a factory. Once
compressed by seam-forming dies 12, the temperature of the
components of seam 603 rises to exceed the glass transition
temperature of the first thermoplastic polymer material. When the
temperature of the components of seam 603 exceeds the glass
transition temperature of the first thermoplastic polymer material,
thermal bonding may occur (a) between components 601 and 602 and
(b) between stitching strand 605 and components 601 and 602. That
is, both thermal bonds may be formed when the temperature of the
components of seam 603 exceeds the glass transition temperature of
the first thermoplastic polymer material. Note that the melting
temperature of the second thermoplastic polymer material is lower
than the glass transition temperature of the first thermoplastic
polymer material. As such, the second thermoplastic polymer
material in stitching strand 605 reaches the melting point in this
example. As a result, stitching strand 605 may melt to a greater
degree, as in the configurations of FIGS. 37B and 37C. Once
seam-forming dies separate and the components of seam 603 are
removed, the temperature of the components may cool or otherwise
decrease to the initial temperature.
[0147] Although the glass transition temperatures and the melt
temperatures of the first and second thermoplastic polymer
materials may conform to the relationships discussed above, other
relationships may also be utilized. For example, the melting
temperature of the second thermoplastic polymer material may be
higher than the melting temperature of the first thermoplastic
polymer material, and the glass transition temperature of the
second thermoplastic polymer material may be between the glass
transition and melting temperatures of the first thermoplastic
material. As another example, the glass transition and melting
temperatures of the second thermoplastic polymer material may be
higher than the melting temperature of the first thermoplastic
polymer material. The various concepts discussed above relating to
the use of stitching strand 605 in seam 603 also applies to the
configuration of seam 604. As an example, FIG. 40 depicts
overlapping components 601 and 602 that are joined to form a seam
604 that includes stitching strand 605. That is, edge areas of
components 601 and 602 overlap and lay against each other, where
thermal bonding forms seam 604, and stitching strand 605 extends
through the edge areas of components 601 and 602. Moreover, seam
604 effectively includes two thermal bonds. The first thermal bond
is formed by the first thermoplastic polymer material from
components 601 and 602. The second thermal bond is formed by the
second thermoplastic polymer material from stitching strand
605.
I. GENERAL PRODUCT CONFIGURATIONS
[0148] The above discussion and associated FIGS. 1-40 disclose
various elements that may be incorporated into a variety of
products, including (a) yarn 100, thread 200, woven textile 300,
and knitted textile 400; (b) fused regions 303, 304, 403, and 404;
(c) composite element 500; (d) seams 603 and 604 from seam element
600, with or without stitching strand 605; and (e) thermal bonding
to join or fuse. Any of these various elements may be utilized
alone or in combination in articles of apparel, such as shirts,
pants, socks, footwear, outerwear, undergarments, and headwear.
Various aspects of the various elements may also be utilized in
containers, upholstery for furniture, bed coverings, table
coverings, towels, flags, tents, sails, and parachutes, as well as
industrial purposes that include automotive and aerospace
applications, filter materials, medical textiles, geotextiles,
agrotextiles, and industrial apparel. Accordingly, the various
elements may be utilized in a variety of products for both personal
and industrial purposes.
[0149] Although the various elements may be utilized in a variety
of products, the following discussion provides examples of articles
of apparel. That is, the following discussion demonstrates numerous
ways in which the various elements may be incorporated into a shirt
700 and footwear 800. More particularly, examples of various
configurations of shirt 700 and footwear 800 are provided in order
to demonstrate products utilizing yarns, threads, and textiles that
incorporate thermoplastic polymer materials, as well as the manner
in which thermal bonding may impart advantages to the products.
Accordingly, while the concepts outlined below are specifically
applied to various articles of apparel, the concepts may be applied
to a variety of other products.
J. SHIRT CONFIGURATIONS
[0150] A first configuration of shirt 700 is depicted in FIG. 41 as
including a torso region 701 and a pair of arm regions 702. Torso
region 701 corresponds with a torso of a wearer and covers at least
a portion of the torso when worn. An upper area of torso region 701
defines a neck opening 703 through which the neck and head of the
wearer protrude when shirt 700 is worn. Similarly, a lower area of
torso region 701 defines a waist opening 704 through which the
waist or pelvic area of the wearer protrudes when shirt 700 is
worn. Arm regions 702 extend outward from torso region 701 and
respectively correspond with a right arm and a left arm of the
wearer when shirt 700 is worn. As such, one of arm regions 702
covers at least a portion of the right arm, and the other of arm
regions 702 covers at least a portion of the left arm. Each of arm
regions 702 define an arm opening 705 through which the hands,
wrists, or arms of the wearer protrude when shirt 700 is worn.
[0151] Torso region 701 and arm regions 702 are formed from various
textile elements 706 that are joined at a plurality of seams 707.
Textile elements 706 are generally formed to have the configuration
of woven textile 300, knitted textile 400, or any other textile
that incorporates a thermoplastic polymer material. As such,
textile elements 706 may incorporate strands (e.g., yarn 100,
thread 200) that have a plurality of substantially aligned
filaments formed from a thermoplastic polymer material. Although
each of textile elements 706 may be woven or knitted, other textile
elements 706 may be a non-woven textile or a polymer sheet, for
example, that incorporates a thermoplastic polymer material. Some
of textile elements 706 may also be formed from cotton, silk,
thermoset polymer filaments, or other materials that do not include
a thermoplastic polymer material. Shirt 700 may also include
elastic components, zippers, hook-and-loop fasteners, or other
closure devices, for example.
[0152] Two of seams 707 extend between torso region 701 and arm
regions 702 in order to join various textile elements 706 together.
Although not depicted, additional seams 707 may extend along (a)
side areas of torso region 701 to join front and back textile
elements 706 and (b) rear areas of arm regions 702 to join edge
areas of the textile element 706 forming each arm region 702, for
example. In general, seams 707 define regions where edge areas of
textile elements 706 are joined with each other, possibly through
thermal bonding. Referring to FIG. 42A, one of seams 707 is
depicted as having the general configuration of seam 603, but may
also have the general configuration of seam 604. Moreover, any of
the various methods discussed above for forming seams 603 and 604,
with or without stitching strand 605, may be utilized to form seams
707. As such, an article of apparel incorporating textile elements
formed from a thermoplastic polymer material may include thermal
bonds that join textile elements at various seams.
[0153] Many of the edge areas of textile elements 706 are joined at
seams 707. Other edge areas are present at openings 703, 704, and
705. In order to prevent fraying or unraveling of strands forming
textile elements 706 at openings 703, 704, and 705, various types
of thermal bonds may be employed. Referring to FIG. 42B, the edge
area of textile element 706 that forms waist opening 704 is thermal
bonded to effectively fuse the various strands within textile
element 706. That is, filaments or yarns that incorporate a
thermoplastic polymer material may be thermal bonded with each
other adjacent to waist opening 704 to prevent fraying or
unraveling of strands forming textile elements 706. Another manner
in which thermal bonding may be utilized to prevent fraying or
unraveling is depicted in FIG. 42C. More particularly, the edge
area of textile element 706 at one of arm openings 705 is turned
inward and folded back on itself. A thermal bond is formed to join
surfaces of textile element 706, and the thermal bond also
effectively fuses the various strands within textile element 706.
That is, filaments or yarns that incorporate a thermoplastic
polymer material may be thermal bonded with each other adjacent to
arm openings 705 to prevent fraying or unraveling of strands
forming textile elements 706.
[0154] A second configuration of shirt 700 is depicted in FIG. 43
as having many of the features discussed with reference to FIG. 41.
Although seams 707 may exhibit the configuration in FIG. 42A, seam
707 is depicted in FIG. 44A as having the general configuration of
seam 604. As such, an edge area of one textile element 706 overlaps
and is thermal bonded with an edge of the other textile element
706. A variety of seam configurations, including those of seams 603
and 604, may be utilized in articles of apparel.
[0155] In order to impart different properties to specific areas of
shirt 700, various fused regions 708 are formed in textile elements
706. More particularly, fused regions 708 are formed around neck
opening 703, waist opening 704, and each of arm openings 705. Given
that each of openings 703-705 may be stretched as shirt 700 is put
on an individual and taken off the individual, fused regions 708
are located around openings 703-705 in order to impart greater
stretch-resistance to these areas. Strands incorporating a
thermoplastic polymer material in fused regions 708 are generally
fused to a greater degree than in other areas of shirt 700. Similar
to the discussion of FIGS. 42B and 42C above, some of fused regions
708 may prevent fraying or unraveling in the areas around openings
703-705.
[0156] Given that elbow areas of shirt 700 may be subjected to
relatively high abrasion as shirt 700 is worn, some of fused
regions 708 may be located in the elbow areas to impart greater
durability. Also, backpack straps that extend over shoulder areas
of shirt 700 may abrade and stretch the shoulder areas. Additional
fused regions 708 are, therefore, located in the shoulder areas of
shirt 200 to impart both durability and stretch-resistance.
Portions of textile elements 706 that are located in the shoulder
areas and around seams 707 effectively form both seams 707 and
fused regions 708 in the shoulder areas. Two separate processes may
be utilized to form these areas. That is, one thermal bonding
process may form seams 707, and another thermal bonding process may
form fused regions 708 in the shoulder areas. In some processes,
however, seams 707 and fused regions 708 in the shoulder areas may
be formed through a single thermal bonding process.
[0157] During the thermal bonding that forms fused regions 708,
areas of textile elements 706 are heated and compressed. In
addition to fusing strands within textile elements 706, the heating
and compression may also cause fused regions 708 to compress or
reduce in thickness. More particularly, processes that form a fused
regions 708 may effectively cause thinning in the areas of fused
regions 708. This effect may be seen in FIG. 44B and may occur in
other locations where thermal bonding or fusing forms areas similar
to fused regions 303, 304, 403, 404, and 708.
[0158] A third configuration of shirt 700 is depicted in FIG. 45 as
including various components 709 are secured to textile elements
706. More particularly, components 709 are thermal bonded to an
interior surface of shirt 700, as depicted in FIGS. 46A-46C. In
other configurations, components 700 may be secured to an exterior
surface of shirt 700. Components 709 may be additional textile
elements that may incorporate thermoplastic polymer materials or
may be formed from other materials. Additionally, components 709
may be a compressible material, such as elements of polymer foam.
Components 709 may also be a polymer sheet or plate. Moreover, each
of components 709 may be formed from different materials to impart
different properties to areas of shirt 700. In effect, the
combination of textile elements 706 and components 709 form
structures similar to composite element 500.
[0159] Components 709 may have various configurations. If component
709 is another textile that absorbs or wicks water, then the
combination of textile elements 706 and the other textile may be
suitable for configurations of shirt 700 utilized during athletic
activities where an individual wearing shirt 700 is likely to
perspire. If component 709 is a compressible material, such as an
element of polymer foam, then the combination of textile elements
706 and the compressible material may be suitable for
configurations of shirt 70 where cushioning (i.e., attenuation of
impact forces) is advantageous, such as padding for athletic
activities that may involve contact or impact with other athletes,
equipment, or the ground. If component 709 is a polymer sheet or
plate, then the combination of textile elements 706 and the polymer
sheet or plate may be suitable for articles of apparel that impart
protection from acute impacts. Accordingly, a variety of materials
or other components maybe joined through thermal bonding to textile
elements 706 of shirt 700.
[0160] Various fused regions 708 are also formed in textile
elements 706 and adjacent to some of components 709. As an example,
two fused regions 708 extend around the areas where components 709
are located in the side areas of torso region 701. A pair of fused
regions 708 extend over the areas where components 709 are located
in the elbow areas of arm regions 702. These fused regions 708 may
be utilized to reinforce or add stretch-resistance to areas
surrounding components 709 or provide greater durability to areas
over components 709, for example.
[0161] A fourth configuration of shirt 700 is depicted in FIG. 47
as including a pocket 710, which may be utilized to hold or
otherwise contain relatively small objects (e.g., keys, wallet,
identification card, mobile phone, portable music player). Pocket
710 is formed as two overlapping layers of material, at least one
of which is textile element 708. Additionally, a thermal bond is
utilized to join the overlapping layers of material to each other.
That is, a thermal bond joins a periphery of the material element
forming pocket 710 to textile element 706. A central area of pocket
710 remains unbonded. A pocket similar to pocket 710 may also be
formed in other products and articles of apparel, including pants
and jackets.
[0162] Based upon the above discussion, textile elements (e.g.,
textiles 300 and 400) including a thermoplastic polymer material
may be utilized in shirt 700. Given that many other types of
apparel have constructions that are similar to shirt 700. That is,
pants, socks, outerwear, undergarments, and headwear are all formed
from one or more textile elements joined at seams. These other
types of apparel may, therefore, incorporate structures that are
substantially similar to seams 707 (i.e., seams 603, 604). In order
to impart different properties to areas of the apparel, various
structures that are substantially similar to fused regions 708
(i.e., fused regions 303, 304, 403, 404) may also be utilized.
Similarly, the other types of apparel may also incorporate
structures that are substantially similar to components 709 (i.e.,
components 501, 502). By forming fused regions and combining the
textile elements with other components, various properties and
combinations of properties may be imparted to different areas of
the apparel. That is, the various concepts disclosed herein may be
utilized individually or in combination to engineer the properties
of apparel to a specific purpose.
K. FOOTWEAR CONFIGURATIONS
[0163] A first configuration of footwear 800 is depicted in FIG. 49
as including a sole structure 810 and an upper 820. Sole structure
810 is secured to a lower area of upper 820 and extends between
upper 820 and the ground. Upper 820 provides a comfortable and
secure covering for a foot of a wearer. As such, the foot may be
located within upper 820, which effectively secures the foot within
footwear 800, and sole structure 810 extends under the foot to
attenuate forces, enhance stability, or influence the motions of
the foot, for example.
[0164] Sole structure 810 includes a midsole 811, an outsole 812,
and an sockliner 813. Midsole 811 is secured to a lower surface of
upper 820 and may be formed from a compressible polymer foam
element (e.g., a polyurethane or ethylvinylacetate foam) that
attenuates ground reaction forces (i.e., provides cushioning) when
compressed between the foot and the ground during walking, running,
or other ambulatory activities. In further configurations, midsole
811 may incorporate fluid-filled chambers, plates, moderators, or
other elements that further attenuate forces, enhance stability, or
influence the motions of the foot, or midsole 811 may be primarily
formed from a fluid-filled chamber. Outsole 812 is secured to a
lower surface of midsole 811 and may be formed from a
wear-resistant rubber material that is textured to impart traction.
Sockliner 813 is located within upper 820, as depicted in FIG. 50,
and is positioned to extend under a lower surface of the foot.
Although this configuration for sole structure 810 provides an
example of a sole structure that may be used in connection with
upper 820, a variety of other conventional or nonconventional
configurations for sole structure 810 may also be utilized.
[0165] Upper 820 may be formed from a variety of elements that are
joined together to form a structure for receiving and securing the
foot relative to sole structure 810. As such, upper 820 extends
along opposite sides of the foot, over the foot, around a heel of
the foot, and under the foot. Moreover, upper 820 defines a void
821, which is a generally hollow area of footwear 800, that has a
general shape of the foot and is intended to receive the foot.
Access to void 821 is provided by an ankle opening 822 located in
at least a heel region. A lace 823 extends through various lace
apertures 824 and permits the wearer to modify dimensions of upper
820 to accommodate the proportions of the foot. More particularly,
lace 823 permits the wearer to tighten upper 820 around the foot,
and lace 823 permits the wearer to loosen upper 820 to facilitate
entry and removal of the foot from the void (i.e., through ankle
opening 822). As an alternative to lace apertures 824, upper 820
may include other lace-receiving elements, such as loops, eyelets,
hooks, and D-rings. In addition, upper 820 includes a tongue 825
that extends between void 821 and lace 823 to enhance the comfort
and adjustability of footwear 800. In some configurations, upper
820 may also incorporate other elements, such as reinforcing
members, aesthetic features, a heel counter that limits heel
movement, a wear-resistant toe guard, or indicia (e.g., a
trademark) identifying the manufacturer. Accordingly, upper 820 is
formed from a variety of elements that form a structure for
receiving and securing the foot.
[0166] Portions of upper 820 that extend along sides of the foot,
over the foot, and under the foot include various textile elements
826, which are generally formed to have the configuration of woven
textile 300, knitted textile 400, or any other textile that
incorporates a thermoplastic polymer material. As such, textile
elements 826 may incorporate strands (e.g., yarn 100, thread 200)
that have a plurality of substantially aligned filaments formed
from a thermoplastic polymer material. Although each of textile
elements 826 may be woven or knitted, other textile elements 826
may be a non-woven textile or a polymer sheet, for example, that
incorporates a thermoplastic polymer material. Some of textile
elements 826 may also be formed from cotton, silk, thermoset
polymer filaments, or other materials that do not include a
thermoplastic polymer material. Tongue 825 may also incorporate one
or more of textile elements 826.
[0167] Although a single textile element 826 may form a relatively
large area of upper 820, multiple textile elements 826 are joined
at various seams 827. In general, seams 827 define regions where
edge areas of textile elements 826 are joined with each other,
possibly through thermal bonding. As an example, two seams 827 are
located on opposite sides of upper 820 and join a textile element
826 that forms lace apertures 824 with a textile element 826 that
extends along sides of the foot. These seams 827 exhibit the
general configuration of seam 603, but may also have the general
configuration of seam 604. An advantage to the configuration of
seam 604 is that the edge areas of textile element 826 do not
protrude inward, which may cause discomfort for the wearer. As
another example, two seams 827 are located on opposite sides of
upper 820 and join the textile element 826 that extends along sides
of the foot with a textile element 826 that extends under the foot,
which may be a strobel material. These seams 827 exhibit the
general configuration of seam 604, but may also have the general
configuration of seam 603. Accordingly, various textile elements
826 may be joined with seams 827, which may be formed through the
various thermal bonding processes discussed above for forming seams
603 and 604.
[0168] Two of seams 707 extend between torso region 701 and arm
regions 702 in order to join various textile elements 706 together.
Although not depicted, additional seams 707 may extend along (a)
side areas of torso region 701 to join front and back textile
elements 706 and (b) rear areas of arm regions 702 to join edge
areas of the textile element 706 forming each arm region 702, for
example. Referring to FIG. 42A, one of seams 707 is depicted as
having the general configuration of seam 603, but may also have the
general configuration of seam 604. Moreover, any of the various
methods discussed above for forming seams 603 and 604, with or
without stitching strand 605, may be utilized to form seams 707. As
such, an article of apparel incorporating textile elements formed
from a thermoplastic polymer material may include thermal bonds
that join textile elements at various seams.
[0169] A relatively large percentage of footwear 800 may be formed
from thermoplastic polymer materials. As discussed above, textile
elements 826 may be at least partially formed from thermoplastic
polymer materials. Although lace 823 is not generally joined to
upper 820 through bonding or stitching, lace 823 may also be formed
from a thermoplastic polymer material. Similarly, each of midsole
811 and outsole 812 may be formed from a thermoplastic polymer
material. Depending upon the number of elements of footwear 800
that incorporate thermoplastic polymer materials or are entirely
formed from thermoplastic polymer materials, the percentage by mass
of footwear 800 that is formed from the thermoplastic polymer
materials may range from thirty percent to one-hundred percent. In
some configurations, at least sixty percent of a combined mass of
sole structure 810 and upper 820 may be from thermoplastic polymer
materials. Accordingly, a majority or even all of footwear 400 may
be formed from one or more thermoplastic polymer materials.
[0170] Adhesives are conventionally utilized to join uppers to sole
structures and midsoles to outsoles. An advantage of forming
various elements of footwear 800 from thermoplastic polymer
materials is that a thermal bond may be utilized to join upper 820
to sole structure 810 and midsole 811 to outsole 812. In addition
to reducing the environmental effects of utilizing adhesives, the
recyclability of footwear 800 may also be enhanced.
[0171] A second configuration of footwear 800 is depicted in FIG.
51 as having many of the features discussed above. In order to
impart different properties to specific areas of upper 820, three
generally linear fused regions 828 extend from a heel area to a
forefoot area of footwear 800. As an example, fused regions 828 may
impart stretch-resistance. That is, upper 820 may have a tendency
to stretch during walking, running, or other ambulatory activities,
and fused regions 828 impart greater stretch-resistance along the
length of footwear 800. Given that textile elements 826 may (a) be
woven textile 300, knitted textile 400, or any other textile that
incorporates a thermoplastic polymer material or (b) incorporate
strands (e.g., yarn 100, thread 200) that are formed from a
thermoplastic polymer material, the strands in fused regions 828
are generally fused to a greater degree than in other areas of
footwear 800.
[0172] During the thermal bonding process that forms fused regions
828, areas of textile elements 826 are heated and compressed. In
addition to fusing strands within textile elements 826, the heating
and compression may also cause fused regions 828 to compress or
reduce in thickness. More particularly, processes that form a fused
regions 828 may effectively cause thinning in the areas of fused
regions 828. This effect may be seen in FIG. 52 and may occur in
other locations where thermal bonding or fusing forms areas similar
to fused regions 303, 304, 403, and 404.
[0173] Although upper 820 may be formed to have a thickness of a
single layer of textile elements 826, upper 820 may also have a
thickness of multiple layers. Referring again to FIG. 52, the areas
of upper 820 that extend along sides of the foot include textile
elements 826, as well as components 829 and 830. More particularly,
each side of upper 820 has a layered configuration wherein (a)
textile element 826 forms an exterior surface of upper 820, (b)
component 829 forms an interior surface that defines a portion of
void 821, and (c) component 830 is located between textile element
826 and component 829 to form a middle layer. As examples,
component 829 may absorb or wick water to manage perspiration
within footwear 800, and component 830 may be a compressible
polymer foam material that enhances the comfort of footwear
800.
[0174] On each side of upper 820, textile element 826 may be
thermal bonded to component 830. If one or both of components 829
and 830 incorporate a thermoplastic polymer material, then
components 829 and 830 may also be thermal bonded to each other.
The process for joining textile element 826 and components 829 and
830 in a layered configuration may, therefore, be similar to the
thermal bonding process discussed above for composite element
500.
[0175] A third configuration of footwear 800 is depicted in FIG. 53
as including further examples of fused regions 828. One of fused
regions 828 extends around and is proximal to ankle opening 822,
which may add greater stretch-resistance to the area around ankle
opening 822 and assists with securely-retaining the foot within
upper 820. Another fused region 828 is located in the heel region
and extends around a rear area of footwear 800 to form a heel
counter that resists movement of the heel within upper 820. A
further fused region 828 is located in the forefoot area and
adjacent to sole structure 810, which adds greater durability to
the forefoot area. More particularly, the forefoot area of upper
820 may experience greater abrasive-wear than other portions of
upper 820, and the addition of fused region 828 in the forefoot
area may enhance the abrasion-resistance of footwear 800 in the
forefoot area. An additional fused region 828 extends around lace
apertures 824, which may enhance the durability and
stretch-resistance of areas that receive lace 823. This fused
region 828 also extends downward in various locations to an area
that is proximal sole structure 810 in order to enhance the
stretch-resistance along the sides of footwear 800. More
particularly, tension in lace 823 may place tension in the sides of
upper 820. By forming fused regions 828 that extend downward along
the sides of upper 820, the stretch in upper 820 may be
reduced.
[0176] A fourth configuration of footwear 400 is depicted in FIG.
54 as including three fused region 828 with shapes of the letters
"A," "B," and "C." Fused regions 828 may be utilized to modify
various properties of textile elements 826, including the
properties of permeability, durability, and stretch-resistance.
Various aesthetic properties may also be modified by forming fused
regions 828, including the transparency, saturation of a color, and
contrast in textile elements 826. Utilizing this change in
aesthetic properties, fused regions 828 may be utilized to form
indicia in areas of footwear 800. That is, fused regions 828 may be
utilized to form a name or logo of a team or company, the name or
initials of an individual, or an esthetic pattern, drawing, or
element. Similarly, fused regions 828 may be utilized to form
indicia in shirt 700, other articles of apparel, or any other
product incorporating textiles with thermoplastic polymer
materials.
[0177] As an alternative to forming indicia with fused regions 828,
other elements may be thermal bonded to upper 820 to form indicia.
For example, a polymer sheet may be cut to form the letters "A,"
"B," and "C" and then joined with the sides of upper 820 through
thermal bonding to textile elements 826. As a related matter,
elements of woven textile 300 or knitted textile 400, for example,
may be thermal bonded or otherwise joined to various products to
form indicia. For example, elements of woven textile 300 or knitted
textile 400 with the shapes of the letters "A," "B," and "C" may be
thermal bonded to the sides of an article of footwear where the
upper is primarily formed from leather, synthetic leather, or any
other material. Given that woven textile 300, knitted textile 400,
or other textiles incorporating a thermoplastic polymer material
may be thermal bonded to a variety of other materials, elements
these elements may be thermal bonded to a variety of products in
order to form indicia.
[0178] Based upon the above discussion, textile elements (e.g.,
textiles 300 and 400) including a thermoplastic polymer material
may be utilized in footwear 800. Other types of footwear may also
incorporate structures that are substantially similar to seams 827
(i.e., seams 603, 604). In order to impart different properties to
areas of the footwear, various structures that are substantially
similar to fused regions 828 (i.e., fused regions 303, 304, 403,
404) may also be utilized. Similarly, other types of footwear may
also incorporate structures that are substantially similar to
components 829 and 830 (i.e., components 501, 502). By forming
fused regions and combining the textile elements with other
components, various properties and combinations of properties may
be imparted to footwear. That is, the various concepts disclosed
herein may be utilized individually or in combination to engineer
the properties of footwear to a specific purpose.
L. SHAPING TEXTILES
[0179] Woven textile 300 and knitted textile 400, as respectively
depicted in FIGS. 7 and 9, have a generally planar configuration.
Textiles incorporating a thermoplastic polymer material may also
exhibit a variety of three-dimensional or otherwise non-planar
configurations. As an example, an element of a shaped textile 900
is depicted as having a wavy or undulating configuration in FIG.
55A. Shaped textile 900 may be either of textiles 300 and 400, for
example, as well as any textile that includes strands (e.g., yarn
100, thread 200) incorporating a thermoplastic polymer material. A
similar configuration with squared waves in shaped textile 900 is
depicted in FIG. 55B. As another example, shaped textile 900 may
have waves that extend in two directions to impart an egg crate
configuration, as depicted in FIG. 55C. Accordingly, shaped textile
900 may be formed to have a variety of three-dimensional or
otherwise non-planar configurations.
[0180] A variety of processes may be utilized to form a
three-dimensional configuration in shaped textile 900. In general,
however, the processes involve forming thermal bonds within shaped
textile 900 to impart the non-planar configuration. Referring to
FIGS. 56A-56C, an example of a method is depicted as involving heat
press that includes a pair of shaped platens 14, which each have
surfaces that correspond with the resulting three-dimensional
aspects of shaped textile 900. Initially, shaped textile 900 is
located between shaped platens 14, as depicted in FIG. 56A. That
is, a planar textile element that becomes shaped textile 900 is
located within the heat press, which has non-planar surfaces.
Shaped platens 14 then translate or otherwise move toward each
other in order to contact and compress shaped textile 900, as
depicted in FIG. 56B. In order to form the three-dimensional
configuration in shaped textile 900, heat from one or both of
shaped platens 14 is applied to shaped textile 900 so as to soften
or melt the thermoplastic polymer material within strands forming
shaped textile 900. As such, shaped textile 900 is heated to at
least a glass transition temperature of the thermoplastic polymer
material within shaped textile 900. Upon separating shaped platens
14 and permitting shaped textile 900 to cool, as depicted in FIG.
56C, shaped textile 900 exhibits the three-dimensional
configuration from the surfaces of shaped platens 14. In effect,
cooling the textile element forming shaped textile 900 sets or
otherwise imparts the non-planar configuration. Through this
process, shaped textile 900 is molded to have a non-planar
configuration, but other shaping or molding processes may be
utilized. Although heat may be applied through conduction, radio
frequency heating, ultrasonic heating, radiant heating, laser
heating, or chemical heating may also be used.
[0181] Based upon the above discussion, a textile incorporating a
thermoplastic polymer material may be shaped or molded to exhibit a
three-dimensional or non-planar configuration. When incorporated
into products (e.g., shirt 700, footwear 800), these features may
provide both structural and aesthetic enhancements to the products.
For example, the three-dimensional configurations may provide
enhanced impact force attenuation and greater permeability by
increasing surface area.
M. RECYCLING
[0182] Woven textile 300 and knitted textile 400 are substantially
formed from a thermoplastic polymer material. Given that textile
elements 706 of shirt 700 may have the configuration of either of
woven textile 300 and knitted textile 400, for example, a majority
or substantially all of shirt 700 may be formed from the
thermoplastic polymer material. Similarly, a relatively large
percentage of footwear 800 may also be formed from a thermoplastic
polymer material. Unlike many articles of apparel, therefore, the
materials within shirt 700 and footwear 800 may be recycled
following their useful lives.
[0183] Utilizing shirt 700 as an example, the thermoplastic polymer
material from shirt 700 may be extracted, recycled, and
incorporated into another product (e.g., apparel, container,
upholstery) as a non-woven textile, a woven textile, a knitted
textile, a polymer foam, or a polymer sheet. This process is
generally shown in FIG. 57, in which shirt 700 is recycled in a
recycling center 15, and thermoplastic polymer material from shirt
700 is incorporated into one or more of another shirt 700, footwear
800, or another product. Moreover, given that a majority or
substantially all of shirt 700 is formed from the thermoplastic
polymer material, then a majority or substantially all of the
thermoplastic polymer material may be utilized in another product
following recycling. Although the thermoplastic polymer material
from shirt 700 was initially utilized within one textile, such as
woven textile 300, the thermoplastic polymer material from shirt
700 may be subsequently utilized in another element of textile,
such as knitted textile 400. Continuing, the newly-formed shirt 700
and footwear 800 may also be recycled through a similar process.
Accordingly, an advantage of forming shirt 700, footwear 800, or
other products with the various strands and textiles discussed
above relates to recyclability.
N. CONCLUSION
[0184] Yarn 100, thread 200, woven textile 300, knitted textile
400, composite element 500, seam element 600, shirt 700, and
footwear 800 all are at least partially formed from a thermoplastic
polymer material. Various fused regions may be formed in these
elements through thermal bonding processes to modify various
properties that include permeability, durability, and
stretch-resistance. Various components (textiles, polymer sheets,
foam layers, strands) may also be secured to or combined with these
elements through thermal bonding processes to impart additional
properties or advantages. Seams may be formed to join these
elements with thermal bonding processes. Accordingly, the various
structures and techniques discussed above combined to form numerous
products and impart a variety of properties to the products.
[0185] The invention is disclosed above and in the accompanying
figures with reference to a variety of configurations. The purpose
served by the disclosure, however, is to provide an example of the
various features and concepts related to the invention, not to
limit the scope of the invention. One skilled in the relevant art
will recognize that numerous variations and modifications may be
made to the configurations described above without departing from
the scope of the present invention, as defined by the appended
claims.
* * * * *