U.S. patent application number 13/637448 was filed with the patent office on 2013-09-19 for resin composition and multilayered structure using same.
This patent application is currently assigned to KURARAY CO., LTD.. The applicant listed for this patent is Yasuhiko Haneda, Takeyuki Igarashi, Masahiro Kitamura, Shinji Tai. Invention is credited to Yasuhiko Haneda, Takeyuki Igarashi, Masahiro Kitamura, Shinji Tai.
Application Number | 20130244048 13/637448 |
Document ID | / |
Family ID | 44673302 |
Filed Date | 2013-09-19 |
United States Patent
Application |
20130244048 |
Kind Code |
A9 |
Igarashi; Takeyuki ; et
al. |
September 19, 2013 |
RESIN COMPOSITION AND MULTILAYERED STRUCTURE USING SAME
Abstract
A resin composition, containing: (A) polyolefin; (B) a
saponified ethylene-vinyl acetate copolymer having an ethylene
content of from 20 to 65 mol % and a degree of saponification of
vinyl acetate units of 96% or more; (C) a saponified ethylene-vinyl
acetate copolymer having an ethylene content of from 68 to 98 mol %
and a degree of saponification of vinyl acetate units of 20% or
more; and a pigment (E), wherein a mass ratio (A/B) is from 3 to
99.5, a mass ratio (B/C) is from 1 to 100, a mass ratio (E/C) is
from 0.04 to 50, and a content of (C) is from 0.01 to 2.4 parts by
mass based on 100 parts by mass of (A) and (B). A molded product,
in particular a multilayered structure, obtained by melt molding
the resin composition has good dispersibility of the pigment, and
improved uneven coloration.
Inventors: |
Igarashi; Takeyuki;
(Kurashiki-shi, JP) ; Haneda; Yasuhiko;
(Chiyoda-ku, JP) ; Kitamura; Masahiro;
(Chiyoda-ku, JP) ; Tai; Shinji; (Pasadena,
TX) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Igarashi; Takeyuki
Haneda; Yasuhiko
Kitamura; Masahiro
Tai; Shinji |
Kurashiki-shi
Chiyoda-ku
Chiyoda-ku
Pasadena |
TX |
JP
JP
JP
US |
|
|
Assignee: |
KURARAY CO., LTD.
Kurashiki-shi
JP
|
Prior
Publication: |
|
Document Identifier |
Publication Date |
|
US 20130040157 A1 |
February 14, 2013 |
|
|
Family ID: |
44673302 |
Appl. No.: |
13/637448 |
Filed: |
March 25, 2011 |
PCT Filed: |
March 25, 2011 |
PCT NO: |
PCT/JP11/57331 PCKC 00 |
371 Date: |
September 26, 2012 |
Current U.S.
Class: |
428/520; 524/190;
524/399; 524/400; 524/524; 524/88; 524/90 |
Current CPC
Class: |
C08K 2003/2241 20130101;
C08L 23/0861 20130101; C08L 2205/035 20130101; B32B 27/306
20130101; B32B 2439/70 20130101; B32B 27/32 20130101; C08L 23/02
20130101; C08K 5/098 20130101; C08L 29/04 20130101; C08L 23/02
20130101; B32B 2270/00 20130101; C08K 5/0041 20130101; Y10T
428/31928 20150401; C08L 23/0861 20130101; C08L 2666/06 20130101;
C08L 2666/06 20130101; C08L 23/0861 20130101; C08L 23/0853
20130101; C08L 2666/06 20130101; C08K 5/0041 20130101; C08K 3/22
20130101; B32B 2439/80 20130101; B32B 27/06 20130101; C08L 23/0861
20130101; B32B 27/20 20130101; C08L 23/02 20130101 |
Class at
Publication: |
428/520; 524/524;
524/399; 524/400; 524/190; 524/90; 524/88 |
International
Class: |
C08L 31/04 20060101
C08L031/04; C08K 5/098 20060101 C08K005/098; B32B 27/30 20060101
B32B027/30; C08K 5/23 20060101 C08K005/23; C08K 5/3437 20060101
C08K005/3437; C08K 5/3417 20060101 C08K005/3417; C08L 47/00
20060101 C08L047/00; C08K 3/22 20060101 C08K003/22 |
Foreign Application Data
Date |
Code |
Application Number |
Mar 26, 2010 |
JP |
2010-073601 |
Jun 23, 2010 |
JP |
2010-142902 |
Claims
1. A resin composition, comprising: (A) a polyolefin; (B) a
saponified ethylene-vinyl acetate copolymer comprising an ethylene
content of from 20 to 65 mol % and having a degree of
saponification of vinyl acetate units of 96% or more; (C) a
saponified ethylene-vinyl acetate copolymer comprising an ethylene
content of from 68 to 98 mol % and having a degree of
saponification of vinyl acetate units of 20% or more; and a pigment
(E), wherein: a mass ratio of the polyolefin (A) and the saponified
ethylene-vinyl acetate copolymer (B), (A/B), is from 3 to 99.5; a
mass ratio of the saponified ethylene-vinyl acetate copolymer (B)
and the saponified ethylene-vinyl acetate copolymer (C), (B/C), is
from 1 to 100; a mass ratio of the pigment (E) and the saponified
ethylene-vinyl acetate copolymer (C), (E/C), is from 0.04 to 50;
and a content of the saponified ethylene-vinyl acetate copolymer
(C) is from 0.01 to 2.4 parts by mass, based on 100 parts by mass
of a total amount of the polyolefin (A) and the saponified
ethylene-vinyl acetate copolymer (B).
2. The resin composition of claim 1, further comprising: (H) a
conjugated polyene compound, wherein a content of the conjugated
polyene compound (H) is from 0.000001 to 1 parts by mass, based on
100 parts by mass of the total amount of (A) and (B).
3. The resin composition of claim 1, further comprising: (I) a
lubricant, wherein a content of the lubricant (I) is from 0.00001
to 1 parts by mass, based on 100 parts by mass of the total amount
of (A) and (B).
4. The resin composition of claim 1, further comprising: an
ethylene-vinyl acetate copolymer (D), wherein a mass ratio of the
ethylene-vinyl acetate copolymer (D) and the saponified
ethylene-vinyl acetate copolymer (C), (D/C), is from 0.1 to 50.
5. The resin composition of claim 4, wherein: the mass ratio (B/C)
is from 1 to 30; the mass ratio (D/C) is from 0.1 to 15; the mass
ratio (E/C) is from 0.04 to 1.2; and the content of (C) is from 0.2
to 2 parts by mass, based on 100 parts by mass of the total amount
of (A) and (B).
6. The resin composition of claim 1, further comprising: a metal
salt (F) of fatty acid, wherein a mass ratio of the metal salt (F)
of fatty acid and the pigment (E), (F/E), is from 0.1 to 3.
7. The resin composition of claim 1, wherein the pigment (E) is at
least one inorganic pigment selected from the group consisting of
titanium oxide, zinc oxide, zinc sulfide, carbon black, a
lead-comprising pigment, a cadmium-comprising pigment, a
cobalt-comprising pigment, an iron-comprising pigment, a
chromium-comprising pigment, ultramarine blue, and prussian
blue.
8. The resin composition of claim 7, wherein the pigment (E) is
titanium oxide.
9. The resin composition of claim 8, wherein the titanium oxide
comprises titanium oxide particles comprising a surface coated with
a compound of a metal other than titanium or a silicon
compound.
10. The resin composition of claim 1, wherein the pigment (E) is at
least one organic pigment selected from the group consisting of an
azo-comprising pigment, a quinacridone-comprising pigment, and a
phthalocyanine-comprising pigment.
11. A method of producing the resin composition of claim 1, the
method comprising: melt kneading a recovery of a multilayered
structure comprising a first layer comprising a resin composition
comprising the polyolefin (A) and the pigment (E) and a second
layer comprising the saponified ethylene-vinyl acetate copolymer
(B), and a recycling agent comprising a resin composition
comprising the saponified ethylene-vinyl acetate copolymer (C).
12. The method of claim 11, wherein the recycling agent further
comprises an ethylene-vinyl acetate copolymer (D).
13. A multilayered structure, comprising a first layer comprising
the resin composition of claim 1; and a second layer comprising a
saponified ethylene-vinyl acetate copolymer comprising an ethylene
content of from 20 to 65 mol % and having a degree of
saponification of vinyl acetate units of 96% or more.
14. The resin composition of claim 2, further comprising: (I) a
lubricant, wherein a content of the lubricant (I) is from 0.00001
to 1 parts by mass, based on 100 parts by mass of the total amount
of (A) and (B).
15. The resin composition of claim 14, further comprising: an
ethylene-vinyl acetate copolymer (D), wherein a mass ratio of the
ethylene-vinyl acetate copolymer (D) and the saponified
ethylene-vinyl acetate copolymer (C), (D/C) is from 0.1 to 50.
16. The resin composition of claim 15, wherein: the mass ratio
(B/C) is from 1 to 30; the mass ratio (D/C) is from 0.1 to 15; the
mass ratio (E/C) is from 0.04 to 1.2; and the content of (C) is
from 0.2 to 2 parts by mass, based on 100 parts by mass of the
total amount of (A) and (B).
17. The resin composition of claim 16, further comprising: a metal
salt (F) of fatty acid, wherein a mass ratio of the metal salt (F)
of fatty acid and the pigment (E), (F/E), is from 0.1 to 3.
18. The resin composition of claim 17, wherein the pigment (E) is
at least one inorganic pigment selected from the group consisting
of titanium oxide, zinc oxide, zinc sulfide, carbon black, a
lead-comprising pigment, a cadmium-comprising pigment, a
cobalt-comprising pigment, an iron-comprising pigment, a
chromium-comprising pigment, ultramarine blue, and prussian
blue.
19. The resin composition of claim 18, wherein the pigment (E) is
titanium oxide.
20. The resin composition of claim 19, wherein the pigment (E) is
at least one organic pigment selected from the group consisting of
an azo-comprising pigment, a quinacridone-comprising pigment, and a
phthalocyanine-comprising pigment.
Description
TECHNICAL FIELD
[0001] The present invention relates to a resin composition
containing polyolefin, saponified ethylene-vinyl acetate
copolymers, and a pigment. The present invention also relates to a
multilayered structure made of the resin composition.
BACKGROUND ART
[0002] Conventionally, multilayered structures including a layer
made of a thermoplastic resin represented by polyolefin, such as
polyethylene and polypropylene, and a layer made of a saponified
ethylene-vinyl acetate copolymer (hereinafter, may be abbreviated
as an EVOH) excellent in barrier properties are widely used for
various applications, particularly such as food packaging
containers and fuel containers, taking advantage of their barrier
properties. Such a multilayered structure is used as various molded
products, such as a film, a sheet, a cup, a tray, and a bottle. At
this time, there is a case that chips, defective products, and the
like generated when obtaining the various molded products are
collected and melt molded to be reused as at least one layer of a
multilayered structure including a thermoplastic resin layer and an
EVOH layer. Such a recovery technique is useful from the
perspective of the reduction of wastes and the economic efficiency
and is employed widely.
[0003] However, when reusing a recovery of a multilayered structure
including a thermoplastic resin layer and an EVOH layer, gelation
occurs due to thermal degradation during the melt molding or a
degraded material adheres inside an extruder, and thus it used to
be difficult to carry out continuous melt molding for a long period
of time. Further, since such a degraded material is often mixed
into a molded product, there used to be problems of generating a
fish eye and generating a phase separation foreign matter (die
build-up) in a molded product thus obtained. There also used to be
a problem of generating a wave pattern on a surface due to the poor
compatibility. Further, in recent years, since there is a demand
for a colored molded product with good appearance due to
diversified consumer needs, a multilayered structure including an
EVOH layer and a thermoplastic resin layer often contains a
pigment. However, when the multilayered structure is collected for
reuse, a problem of generating uneven coloration has been occurring
due to insufficient dispersibility of the pigment blended
therein.
[0004] As a measure to solve such problems, Patent Document 1
describes a resin composition, made of: polyolefin (a); a
saponified ethylene-vinyl acetate copolymer (b) having an ethylene
content ratio of from 20 to 65 mol % and a degree of saponification
of 96 mol % or more; an inorganic substance (c) of at least one
type selected from titanium oxide, talc, calcium carbonate, mica,
and a water absorbing inorganic substance; and a saponified
ethylene-vinyl acetate copolymer (d) having an ethylene content
ratio of from 68 to 98 mol % and a degree of saponification of 20
mol % or more. This resin composition has significantly improved
compatibility of the polyolefin (a), the saponified ethylene-vinyl
acetate copolymer (b), and the inorganic substance (c) and is
significantly improved in a burnt on a screw, a die build-up, an
increase in a pressure of an extruder, and flow abnormality.
[0005] Patent Document 2 describes a resin composition made of a
thermoplastic resin, an EVOH, a colorant, and a metal salt of
higher fatty acid. According to this resin composition, it is
considered not to generate gels and hard spots such as an
aggregated colorant even in repeated scrap return and melt molded
process over a long period of time.
[0006] Patent Document 3 describes a resin composition made of a
thermoplastic resin, an EVOH, an inorganic filler, and a metal salt
of higher fatty acid. According to the resin composition, it is
considered that a resin pressure in an extruder does not increase
and the melt moldability is excellent even in repeated scrap return
and a continuous operation over a long period of time.
[0007] In Patent Document 4, it is considered that a resin
composition containing an ethylene-vinyl acetate copolymer and a
saponified ethylene-vinyl acetate copolymer having an ethylene
content of 70 mol % or more is blended into a recovery of a layered
product including a polyolefin-based resin layer and an EVOH layer
to be melt kneaded, thereby suppressing generation of a die
build-up, suppressing discoloration, and thus obtaining a molded
object excellent in appearance.
[0008] However, in the inventions described in Patent Documents 1
through 4, dispersibility of the pigment is insufficient in a
molded object thus obtained and uneven coloration is prone to
occur, which sometimes becomes a problem.
PRIOR ART DOCUMENTS
Patent Documents
[0009] Patent Document 1: JP 3-72541A [0010] Patent Document 2: JP
2000-63683A [0011] Patent Document 3: JP 2000-53812A [0012] Patent
Document 4: JP 2009-97010A
SUMMARY OF THE INVENTION
Problems to be Solved by the Invention
[0013] The present invention has made to solve the above problems,
and it is an object of the present invention to provide a resin
composition containing polyolefin, EVOHs, and a pigment, having
good dispersibility of the pigment, and having improved uneven
coloration.
Means for Solving the Problems
[0014] The above problems are solved by providing a resin
composition, comprising: polyolefin (A); a saponified
ethylene-vinyl acetate copolymer (B) having an ethylene content of
from 20 to 65 mol % and having a degree of saponification of vinyl
acetate units of 96% or more; a saponified ethylene-vinyl acetate
copolymer (C) having an ethylene content of from 68 to 98 mol % and
having a degree of saponification of vinyl acetate units of 20% or
more; and a pigment (E), wherein a mass ratio (A/B) of the
polyolefin (A) and the saponified ethylene-vinyl acetate copolymer
(B) is from 3 to 99.5, a mass ratio (B/C) of the saponified
ethylene-vinyl acetate copolymer (B) and the saponified
ethylene-vinyl acetate copolymer (C) is from 1 to 100, a mass ratio
(E/C) of the pigment (E) and the saponified ethylene-vinyl acetate
copolymer (C) is from 0.04 to 50, and a content of the saponified
ethylene-vinyl acetate copolymer (C) is from 0.01 to 2.4 parts by
mass based on 100 parts by mass of a total amount of the polyolefin
(A) and the saponified ethylene-vinyl acetate copolymer (B).
[0015] At this time, it is preferred that the resin composition
comprises an ethylene-vinyl acetate copolymer (D), wherein a mass
ratio (D/C) of the ethylene-vinyl acetate copolymer (D) and the
saponified ethylene-vinyl acetate copolymer (C) is from 0.1 to
50.
[0016] It is more preferred that the mass ratio (B/C) of the
saponified ethylene-vinyl acetate copolymer (B) and the saponified
ethylene-vinyl acetate copolymer (C) is from 1 to 30, the mass
ratio (D/C) of the ethylene-vinyl acetate copolymer (D) and the
saponified ethylene-vinyl acetate copolymer (C) is from 0.1 to 15,
the mass ratio (E/C) of the pigment (E) and the saponified
ethylene-vinyl acetate copolymer (C) is from 0.04 to 1.2, and a
content of the saponified ethylene-vinyl acetate copolymer (C) is
from 0.2 to 2 parts by mass based on 100 parts by mass of the total
amount of the polyolefin (A) and the saponified ethylene-vinyl
acetate copolymer (B).
[0017] It is also preferred that the resin composition further
comprises a metal salt (F) of fatty acid, wherein a mass ratio
(F/E) of the metal salt (F) of fatty acid and the pigment (E) is
from 0.1 to 3.
[0018] It is also preferred that the pigment (E) is an organic
pigment of at least one type selected from the group consisting of
an azo-based pigment, a quinacridone-based pigment, and a
phthalocyanine-based pigment. It is also more preferred that the
pigment (E) is an inorganic pigment of at least one type selected
from the group consisting of titanium oxide, zinc oxide, zinc
sulfide, carbon black, a lead-based pigment, a cadmium-based
pigment, a cobalt-based pigment, an iron-based pigment, a
chromium-based pigment, ultramarine blue, and prussian blue. At
this time, it is more preferred that the pigment (E) is titanium
oxide, and it is even more preferred that it is made of titanium
oxide particles having a surface coated with a compound of metal
other than titanium or a silicon compound.
[0019] It is also preferred that the resin composition further
comprises a conjugated polyene compound (H), wherein a content of
the conjugated polyene compound (H) is from 0.000001 to 1 parts by
mass based on 100 parts by mass of a total amount of the polyolefin
(A) and the saponified ethylene-vinyl acetate copolymer (B). It is
also preferred that the resin composition further comprises a
lubricant (I), wherein a content of the lubricant (I) is from
0.00001 to 1 parts by mass based on 100 parts by mass of a total
amount of the polyolefin (A) and the saponified ethylene-vinyl
acetate copolymer (B).
[0020] The above problems are also solved by providing a method of
producing the above resin composition, comprising melt kneading a
recovery of a multilayered structure, including a layer made of a
resin composition containing the polyolefin (A) and the pigment (E)
and a layer made of the saponified ethylene-vinyl acetate copolymer
(B), and a recycling agent made of a resin composition containing
the saponified ethylene-vinyl acetate copolymer (C). At this time,
it is preferred that the recycling agent further contains an
ethylene-vinyl acetate copolymer (D).
[0021] The above problems are also solved by providing a
multilayered structure, comprising at least two layers of: a layer
made of the above resin composition; and a layer made of a
saponified ethylene-vinyl acetate copolymer having an ethylene
content of from 20 to 65 mol % and having a degree of
saponification of vinyl acetate units of 96% or more.
Effects of the Invention
[0022] By melt molding the resin composition of the present
invention, it is enabled to provide a molded product, in particular
a multilayered structure, made of the resin composition containing
the polyolefin, the EVOHs, and the pigment, having good
dispersibility of the pigment, and having improved uneven
coloration.
MODE FOR CARRYING OUT THE INVENTION
[0023] A resin composition of the present invention, comprises:
polyolefin (A); a saponified ethylene-vinyl acetate copolymer (B)
having an ethylene content of from 20 to 65 mol % and having a
degree of saponification of vinyl acetate units of 96% or more
(hereinafter, may be abbreviated as an EVOH); a saponified
ethylene-vinyl acetate copolymer (C) having an ethylene content of
from 68 to 98 mol % and having a degree of saponification of vinyl
acetate units of 20% or more (hereinafter, may be abbreviated as an
S-EVOH); and a pigment (E).
[0024] In a preferred embodiment, the resin composition of the
present invention contains the polyolefin (A), the EVOH (B), the
S-EVOH (C), an ethylene-vinyl acetate copolymer (hereinafter, may
be abbreviated as an EVAc) (D), and the pigment (E).
[0025] The polyolefin (A) used in the present invention contains,
for example: (low density, linear low density, medium density, high
density, or the like) polyethylene; an ethylene-based copolymer
obtained by copolymerizing ethylene with .alpha.-olefins, such as
1-butene, 1-hexene, and 4-methyl-1-pentene, or acrylic ester;
polypropylene; a propylene-based copolymer obtained by
copolymerizing propylene with .alpha.-olefins, such as ethylene,
1-butene, 1-hexene, and 4-methyl-1-pentene; poly(1-butene),
poly(4-methyl-1-pentene), or modified polyolefin obtained by
reacting maleic anhydride to the polyolefin described above; an
ionomer resin; or the like. Among all, as the polyolefin (A), a
polypropylene-based resin, such as polypropylene and a
propylene-based copolymer, or a polyethylene-based resin, such as
polyethylene and an ethylene-based copolymer, is preferred, and a
polypropylene-based resin is more preferred. One type of the
polyolefin (A) may be used singly, or two or more types may also be
used in combination.
[0026] The EVOH (B) used in the present invention is obtained by
saponifying vinyl acetate units in an ethylene-vinyl acetate
copolymer. An EVOH having a less ethylene content and having a high
degree of saponification of vinyl acetate units is prone to become
defective in compatibility with polyolefin. In contrast, when an
EVOH has an excessively large ethylene content, the gas barrier
properties decrease. In addition, an EVOH having a low degree of
saponification of vinyl acetate units is prone to become defective
in thermal stability of the EVOH itself. From such perspective, the
EVOH (B) used in the present invention has an ethylene content of
from 20 to 65 mol %. It is preferred that the ethylene content is
25 mol % or more. The ethylene content is preferably 55 mol % or
less and more preferably 50 mol % or less. Meanwhile, the degree of
saponification of vinyl acetate units of EVOH (B) is 96% or more,
preferably 98% or more, and even more preferably 99% or more. In
particular, an EVOH having an ethylene content of from 20 to 65 mol
% and having a degree of saponification of 99% can provide the
containers excellent in gas barrier properties by using it in
layers with polyolefin.
[0027] The EVOH (B) may also have another polymerizable monomer
copolymerized therein as long as not inhibiting the effects of the
invention, which is generally in a range of 5 mol % or less. Such
polymerizable monomer may include, for example: .alpha.-olefins,
such as propylene, 1-butene, 1-hexene, and 4-methyl-1-pentene;
(meth)acrylic ester; unsaturated carboxylic acid, such as maleic
acid, fumaric acid, and itaconic acid; alkyl vinyl ether;
N-(2-dimethylaminoethyl)methacrylamide or its quaternary compounds,
N-vinylimidazole or its quaternary compounds, N-vinylpyrrolidone,
N,N-butoxymethyl acrylamide, vinyltrimethoxysilane,
vinylmethyldimethoxysilane, vinyldimethylmethoxysilane, and the
like.
[0028] The EVOH (B) has a melt index (MI; measured at 190.degree.
C., under the load of 2160 g) of preferably 0.1 g/10 minutes or
more, more preferably 0.5 g/10 minutes or more. The EVOH (B) has a
melt index of preferably 100 g/10 minutes or less, more preferably
50 g/10 minutes or less, and most preferably 30 g/10 minutes or
less. At this time, from the perspective of dispersibility of the
EVOH (B), a ratio [MI (B)/MI (A)] when the MI of the EVOH (B) is MI
(B) and the MI (measured at 190.degree. C., under the load of 2160
g) of polyolefin (A) is MI (A) is preferably from 0.1 to 100 and
more preferably from 0.3 to 50. It should be noted that, for an MI
of those having a melting point around 190.degree. C. or more than
190.degree. C., a value is used that is obtained by measuring at a
plurality of temperatures of the melting point or higher under the
load of 2160 g and plotting the results with reciprocals of
absolute temperatures as abscissa against logarithms of MIs as
ordinate in a semi-logarithmic graph for extrapolation to
190.degree. C.
[0029] The S-EVOH (C) used in the present invention is a saponified
ethylene-vinyl acetate copolymer having an ethylene content of from
68 to 98 mol % and having a degree of saponification of vinyl
acetate units of 20% or more, and has a high ethylene content and
an effect of significantly improving the compatibility of the
polyolefin (A) and the EVOH (B). The S-EVOH (C) preferably has an
ethylene content of 70 mol % or more, and more preferably 72 mol %
or more. Meanwhile, the ethylene content is preferably 96 mol % or
less and more preferably 94 mol % or less. The degree of
saponification of the vinyl acetate units is more preferably 30% or
more and even more preferably 40% or more. An upper limit of the
degree of saponification is not particularly limited and may also
be 99 mol % or more, and it is also possible to use one
substantially having a degree of saponification of approximately
100%. When the ethylene content is less than 68 mol % or more than
98 mol %, or the degree of saponification of the vinyl acetate
units is less than 20%, the effect of improving the compatibility
of the polyolefin (A) and the EVOH (B) becomes insufficient.
[0030] The S-EVOH (C) has the ethylene content higher than the
ethylene content of the EVOH (B). From the perspective of improving
the compatibility of the polyolefin (A) and the EVOH (B), a
difference between the ethylene content of the S-EVOH (C) and the
ethylene content of the EVOH (B) is preferably 10 mol % or more and
more preferably 20 mol % or more.
[0031] The S-EVOH (C) has an MI (measured at 190.degree. C., under
the load of 2160 g) of preferably 0.1 g/10 minutes or more, more
preferably 0.5 g/10 minutes or more, and even more preferably 1
g/10 minutes or more. Meanwhile, the S-EVOH (C) has the MI of
preferably 100 g/10 minutes or less, more preferably 50 g/10
minutes or less, and even more preferably 30 g/10 minutes or less.
The S-EVOH (C) may also be modified with unsaturated carboxylic
acid or a derivative thereof, and such unsaturated carboxylic acid
or a derivative thereof may include, for example, acrylic acid,
methacrylic acid, maleic acid, fumaric acid, and itaconic acid;
methyl ester or ethyl ester of the above acids; maleic anhydride,
itaconic anhydride, and the like. One type of them may be used
singly, or two or more types may also be used in combination.
[0032] The pigment (E) used in the present invention is not
particularly limited, and various organic and inorganic pigments
are employed in accordance with a color of the intended
multilayered structure. The organic pigments may include azo-based
pigments, quinacridone-based pigments, and phthalocyanine-based
pigments, and one type of these may be used, or two or more types
may also be used.
[0033] The inorganic pigment may include oxide-based pigments, such
as titanium oxide, zinc oxide, and chromium oxide; sulfide-based
pigments, such as zinc sulfide, lithopone, cadmium yellow,
vermilion, and cadmium red; hydroxide-based pigments, such as
alumina hydrate, iron oxide yellow, and viridian; sulfate-based
pigments, such as precipitated barium sulfate and barites;
carbonate-based pigments, such as calcium carbonate and white lead;
phosphate-based pigments, such as manganese violet; carbon black;
lead-based pigments; cadmium-based pigments; cobalt-based pigments;
iron-based pigments, such as iron black; chromium-based pigments,
such as chrome yellow, molybdate orange, zinc chromate, and
strontium chromate; ultramarine blue and prussian blue;
silicate-based pigments, such as white carbon, clay, and talc, and
one type of these may be used, or two or more types may also be
used.
[0034] Among the above pigments, as the pigment (E) used in the
present invention, in views of allowing uniform and uneven
coloration and not easily impairing the thermal stability of the
composition, inorganic pigments are preferred and oxide-based
pigments are more preferred. Among the oxide-based pigments, from
the perspective of food hygiene, titanium oxide (TiO.sub.2) and
zinc oxide are preferred and titanium oxide is particularly
preferred.
[0035] A method of producing titanium oxide used in the present
invention is not particularly limited, and those produced in a
sulfuric acid method, a chlorine method, or another known method
can be used, while it is preferred to use titanium oxide produced
in a chlorine method from the perspective of weather resistance.
When using titanium oxide produced in a chlorine method, it is
preferred that an amount of residual chlorine is 500 ppm or less.
When the amount of residual chlorine exceeds 500 ppm, the thermal
stability of an obtained resin composition decreases, and there is
a possibility of generating a degraded material, such as a scorch
and a burnt, in a case of melt extrusion process over a long period
of time. The amount of residual chlorine is more preferably 200 ppm
or less, and even more preferably 100 ppm or less. The amount of
residual chlorine in the titanium oxide can be analyzed by
dissolving titanium oxide powder in hydrofluoric acid for
coulometric titration of the liquid. A crystalline structure of the
titanium oxide is not particularly limited and may be either a
rutile type or an anatase type, while a rutile type is preferred
from the perspective of weather resistance.
[0036] The titanium oxide used in the present invention is not
particularly limited in its shape, while one in a particle shape is
preferred. The titanium oxide preferably has an average particle
diameter of, from the perspective of coloration, from 0.01 to 0.4
.mu.m, more preferably from 0.1 to 0.3 .mu.m, and even more
preferably from 0.15 to 0.25 .mu.m. Such an average particle
diameter is calculated by measuring an equivalent circle diameter
of an individual single particle from observation in an electron
microscope from a number average of them.
[0037] It is preferred that the titanium oxide used in the present
invention is made of titanium oxide particles having a surface
coated with a compound of metal other than titanium or a silicon
compound. By using the titanium oxide particles having a surface
coated with a compound of metal other than titanium or a silicon
compound, thermal degradation of the resin composition while melt
kneading is suppressed and generation of a degraded material, such
as a scorch and a burnt, in a case of melt extrusion process over a
long period of time can be reduced. In addition, by suppressing the
thermal degradation of the resin composition, white streaks becomes
not easily generated in a shaped article thus obtained.
[0038] The compound of metal other than titanium or the silicon
compound coating the titanium oxide particles is not particularly
limited, and examples of it may be an oxide, sulfide, nitride,
carbide, boride, chloride, carbonate, hydroxide, sulfate, nitrate,
phosphate, carboxylate, or the like of aluminum, silicon,
zirconium, zinc, magnesium, calcium, or the like. Among these, it
is preferably an oxide, more preferably alumina (Al.sub.2O.sub.3)
and/or silica (SiO.sub.2), and it is particularly preferred to coat
with both alumina and silica. When coating with both alumina and
silica, they may coat as a multilayered structure and may also coat
as a mixture, while it is more preferred to coat as a mixture.
[0039] It is preferred that an amount of coating surfaces of the
titanium oxide particles with the compound of metal other than
titanium or the silicon compound is from 2 to 20 parts by mass in
terms of oxides based on 100 parts by mass of titanium oxide. When
the amount of coating is 0.2 parts by mass or less, the effect of
suppressing the thermal degradation of the resin composition while
melt kneading is not obtained sufficiently and there is a risk of
not obtaining the effect of reducing the generation of a degraded
material, such as a scorch and a burnt, in a case of melt extrusion
process over a long period of time. The amount of coating is more
preferably 0.5 parts by mass or more, even more preferably 1 part
by mass or more, and particularly preferably 3 parts by mass or
more. In contrast, when the amount of coating exceeds 20 parts by
mass, there is a risk of decreasing coloring capabilities as a
white pigment. The amount of coating is more preferably 15 parts by
mass or less and even more preferably 10 parts by mass or less.
[0040] As a method of coating the surfaces of the titanium oxide
particles with the compound of metal other than titanium or the
silicon compound, conventionally known methods can be used. For
example, it may include a method comprising adding a surface
treatment agent to a slurry containing titanium oxide particles and
subsequently adjusting the pH in the slurry, thereby precipitating
hardly-soluble oxides, hydroxides, and the like to coat the
surfaces of the titanium oxide particles. When coating with
alumina, a water soluble aluminum salt is used preferably as the
surface treatment agent. As the water soluble aluminum salt, a
metal salt of aluminic acid, in particular, its alkali metal salt
such as sodium aluminate, is preferably used. When coating with
silica, water soluble silicate is preferably used as the surface
treatment agent. The water soluble silicate may be condensed
silicate, such as water glass. An alkali metal salt, such as sodium
silicate, is preferably used. Acid is usually used for pH
adjustment, and inorganic strong acids, such as sulfuric acid,
hydrochloric acid, and nitric acid, are preferably used.
[0041] It is also preferred that the titanium oxide used in the
present invention is made of titanium oxide particles having a
surface coated with an organic compound. It is preferred that an
amount of coating the surfaces of the titanium oxide particles with
an organic compound is from 0.1 to 1 parts by mass based on 100
parts by mass of titanium oxide. When the amount of coating is less
than 0.1 parts by mass, there is a risk of causing an insufficient
effect of reducing generation of a degraded material, such as a
scorch and a burnt, in a case of melt extrusion process over a long
period of time. In contrast, when the amount of treatment exceeds 1
part by mass, the organic treatment agent bleeds to a surface of a
molded product obtained from the resin composition and there is a
risk of impairing the design of a molded product.
[0042] As a method of coating the surfaces of the titanium oxide
particles with the organic compound, a conventionally known method
can be used. For example, it may include a method comprising adding
a liquid of a surface treatment agent made of the organic compound
when grinding the titanium oxide with a grinder, and evaporating
the solvent while heating to process the surfaces of the titanium
oxide particles. In addition, as a simple method, it may include a
method comprising dropping a liquid of a surface treatment agent
made of the organic compound while stirring titanium oxide
particles in a Henschel mixer or the like for mixing, and
evaporating the solvent while heating to process the surfaces of
the titanium oxide. The surface treatment agent made of the organic
compound may include polyol-based surface treatment agents,
alkanolamine-based surface treatment agents, such as an organic
acid salt of triethanolamine, silane-based surface treatment
agents, and silicone-based surface treatment agents, and among
these, polyol-based surface treatment agents are preferably used.
As the polyol-based surface treatment agent, a hydrocarbon compound
containing from 2 to 4 of hydroxyl groups in a molecule having a
carbon atom number of 10 or less is preferred, and it may include,
for example, trimethylolethane, trimethylolpropane, and
pentaerythritol. The silane-based surface treatment agent may
include silane coupling agents, such as alkylalkoxysilane and
alkylchlorosilane, and the like. The silicone-based surface
treatment agent may include dimethylpolysiloxane and the like. One
type of these surface treatment agents made of an organic compound
may be used, or two or more types may also be used in
combination.
[0043] It is preferred that the titanium oxide particles having a
surface coated with the compound of metal other than titanium or
the silicon compound is further coated with an organic compound. By
using the titanium oxide particles coated further with, in addition
to the compound of metal other than titanium or the silicon
compound, an organic compound, the thermal degradation of the resin
composition while melt kneading is further suppressed and the
generation of a degraded material, such as a scorch and a burnt, in
a case of melt extrusion process over a long period of time is
further reduced. In this case, the surfaces of the titanium oxide
particles are coated with the compound of metal other than titanium
or the silicon compound in accordance with the above method,
followed by further coating the surfaces with an organic compound
in the above method.
[0044] It is preferred to blend, as components of the resin
composition of the present invention, the EVAc (D) as well as the
polyolefin (A), the EVOH (B), the S-EVOH (C), and the pigment (E).
Blending the EVAc (D) enables to further improve the dispersibility
of the EVOH (B) and to suppress the uneven coloration in the molded
product thus obtained. The EVAc (D) used in the present invention
may be a random copolymer obtained by polymerizing ethylene with
vinyl acetate in a known method and may also be a ternary copolymer
obtained by further copolymerizing another monomer and a modified
EVAc obtained by modified by grafting or the like. The content of
vinyl acetate units in the EVAc (D) is preferably from 2 to 40 mol
% and more preferably from 5 to 25 mol %. When the content of vinyl
acetate units is less than 2 mol % or more than 40 mol %, an effect
sufficient to improve the dispersibility of the EVOH (B) may not be
obtained. The EVAc (D) preferably has a melt index (MI: measured at
190.degree. C., under the load of 2160 g) of from 0.1 to 50 g/10
minutes, more preferably from 0.5 to 30 g/10 minutes, and even more
preferably from 1 to 20 g/10 minutes.
[0045] As components of the resin composition of the present
invention, it is also preferred to blend the metal salt (F) of
fatty acid as well as the polyolefin (A), the EVOH (B), the S-EVOH
(C), and the pigment (E). Containing the metal salt (F) of fatty
acid in the resin composition enables suppression of generating a
fish eye derived from aggregation of the pigment. The metal salt
(F) of fatty acid may include a metal salt of higher aliphatic acid
having a carbon number of from 10 to 26, such as lauric acid,
stearic acid, myristic acid, behenic acid, and montanoic acid,
particularly a metal salt of Group I, II, or III in the periodic
table, which is, for example, a sodium salt, a potassium salt, a
calcium salt, and a magnesium salt. It is also possible to use a
zinc salt or a lead salt of the above fatty acid. Among these, a
metal salt of Group II in the periodic table, such as a calcium
salt and a magnesium salt, exhibits the effect by being added in a
small amount. In addition, using a metal salt of metal having
electronegativity of Allread (A. L. Allred) and Rochow (E. G.
Rochow) of 1.5 or more, such as a zinc salt and a lead salt,
enables to suppress adhesion of a degraded material of the resin
composition to a screw and enables to reduce generation of a
degraded material, such as a scorch and a burnt, in a case of melt
extrusion process over a long period of time. It is more effective
to use a metal salt of Group II in the periodic table and a metal
salt of the metal having electronegativity of Allread (A. L.
Allred) and Rochow (E. G. Rochow) of 1.5 or more in
combination.
[0046] As the components of the resin composition of the present
invention, it is preferred to blend hydrotalcite (G) as well as the
polyolefin (A), the EVOH (B), the S-EVOH (C), and the pigment (E).
Containing the hydrotalcite (G) in the resin composition enables to
suppress the thermal degradation of the resin composition and to
reduce the generation of a degraded material, such as a scorch and
a burnt, in a case of melt extrusion process over a long period of
time. The hydrotalcite (G) may preferably include double salt
hydrotalcite (G) represented by
M.sub.xAl.sub.y(OH).sub.2x+3y-2z(A).sub.z.aH.sub.2O
(M denotes one or more of Mg, Ca, Sr, Ba, Zn, Cd, Pb, and Sn, A
denotes CO.sub.3 or HPO.sub.4, x, y, and z are positive numbers, a
is 0 or a positive number, and 2x+3y-2z>0).
[0047] In the above hydrotalcite, it is preferred that M is Mg, Ca,
or Zn, and more preferred that it is a combination of two or more
of them. Among these hydrotalcites, examples of particularly
preferred ones may be as follows:
Mg.sub.6Al.sub.2(OH).sub.16CO.sub.3.4H.sub.2O;
Mg.sub.8Al.sub.2(OH).sub.20CO.sub.3.5H.sub.2O;
Mg.sub.5Al.sub.2(OH).sub.14CO.sub.3.4H.sub.2O;
Mg.sub.10Al.sub.2(OH).sub.22(CO.sub.3).sub.2.4H.sub.2O;
Mg.sub.6Al.sub.2(OH).sub.18HPO.sub.4.4H.sub.2O;
Ca.sub.6Al.sub.2(OH).sub.18CO.sub.3.4H.sub.2O;
Zn.sub.8Al.sub.2(OH).sub.16CO.sub.3.4H.sub.2O;
Mg.sub.3ZnAl.sub.2(OH).sub.12CO.sub.3.2.7H.sub.2O;
Mg.sub.8Zn.sub.2Al.sub.2(OH).sub.20CO.sub.3.1.6H.sub.2O;
Mg.sub.5Zn.sub.1.7Al.sub.3.3(OH).sub.20(CO.sub.3).sub.1.65.4.5H.sub.2O.
[0048] As components of the resin composition of the present
invention, it is preferred to blend the conjugated polyene compound
(H) as well as the polyolefin (A), the EVOH (B), the S-EVOH (C),
and the pigment (E). Blending the conjugated polyene compound (H)
in the resin composition of the present invention enables to
improve the dispersibility of the pigment (E) by suppressing
generation of aggregates of the EVOH (B) at a micro-scale level and
to suppress generation of flow marks due to flow abnormality caused
by aggregates of the EVOH (B) and the pigment (E). It also enables
to reduce generation of a degraded material, such as a scorch and a
burnt, derived from such aggregates in a case of melt extrusion
process of the resin composition over a long period of time.
Further, it enables to suppress coloration in yellowish brown due
to thermal degradation of the resin composition and deterioration
of the color phase of a shaped article thus obtained.
[0049] The conjugated polyene compound (H) used in the present
invention is a compound having a structure in which a carbon-carbon
double bond and a carbon-carbon single bond are alternately
connected and having a number of carbon-carbon double bonds of two
or more, which is a so-called conjugated double bond. The
conjugated polyene compound (H) may be a conjugated diene compound
having a structure in which two carbon-carbon double bonds and one
carbon-carbon single bond are alternately connected, a conjugated
triene compound having a structure in which three carbon-carbon
double bonds and two carbon-carbon single bonds are alternately
connected, or a conjugated polyene compound having a structure in
which numbers of more than that of carbon-carbon double bonds and
carbon-carbon single bonds are alternately connected. It should be
noted that, when the number of carbon-carbon double bonds becomes
eight or more, it is concerned to color a molded object by the
color of the conjugated polyene compound itself, so that it is
preferably a polyene having a number of carbon-carbon double bonds
of seven or less. There may also be a plurality of pairs of the
conjugated double bond made of two or more of carbon-carbon double
bonds without conjugated to each other. For example, the conjugated
polyene compound (H) also includes a compound having three
conjugated trienes in a same molecule, such as tung oil. Further,
the conjugated polyene compound (H) may also have, in addition to
the conjugated double bonds, other functional groups, for example,
various functional groups, such as a carboxyl group and a salt
thereof, a hydroxyl group, an ester group, a carbonyl group, an
ether group, an amino group, an imino group, an amide group, a
cyano group, a diazo group, a nitro group, a sulfone group, a
sulfoxide group, a sulfide group, a thiol group, a sulfonic acid
group and a salt thereof, a phosphoric acid group and a salt
thereof, a phenyl group, a halogen atom, a double bond, and a
triple bond.
[0050] Specific examples of the conjugated polyene compound (H) may
include conjugated diene compounds having a conjugated structure of
two carbon-carbon double bonds, such as isoprene,
2,3-dimethyl-1,3-butadiene, 2,3-diethyl-1,3-butadiene,
2-t-butyl-1,3-butadiene, 1,3-pentadiene,
2,3-dimethyl-1,3-pentadiene, 2,4-dimethyl-1,3-pentadiene,
3,4-dimethyl-1,3-pentadiene, 3-ethyl-1,3-pentadiene,
2-methyl-1,3-pentadiene, 3-methyl-1,3-pentadiene,
4-methyl-1,3-pentadiene, 1,3-hexadiene, 2,4-hexadiene,
2,5-dimethyl-2,4-hexadiene, 1,3-octadiene, 1,3-cyclopentadiene,
1,3-cyclohexadiene, 1-phenyl-1,3-butadiene,
1,4-diphenyl-1,3-butadiene, 1-methoxy-1,3-butadiene,
2-methoxy-1,3-butadiene, 1-ethoxy-1,3-butadiene,
2-ethoxy-1,3-butadiene, 2-nitro-1,3-butadiene, chloroprene,
1-chloro-1,3-butadiene, 1-bromo-1,3-butadiene,
2-bromo-1,3-butadiene, fulvene, tropone, ocimene, phellandrene,
myrcene, farnesene, cembrene, sorbic acid, sorbic acid ester,
sorbate, and abietic acid; conjugated triene compounds having a
conjugated structure of three carbon-carbon double bonds, such as
1,3,5-hexatriene, 2,4,6-octatriene-1-carboxylic acid, eleostearic
acid, tung oil, and cholecalciferol; and conjugated polyene
compounds having a conjugated structure of four or more of
carbon-carbon double bonds, such as cyclooctatetraene,
2,4,6,8-decatetraene-1-carboxylic acid, retinol and retinoic acid.
One type of these conjugated polyene compound (H) may be used
singly, or two or more types of the compounds may also be used in
combination.
[0051] As components of the resin composition of the present
invention, it is preferred to blend the lubricant (I) as well as
the polyolefin (A), the EVOH (B), the S-EVOH (C), and the pigment
(E). Blending the lubricant (I) in the resin composition of the
present invention has the effects of suppressing the aggregation of
the EVOH (B) at a micro-scale level to improve the dispersibility
of the pigment (E) and to suppress the uneven coloration. It also
enables to reduce the generation of a degraded material, such as a
scorch and a burnt, derived from aggregates of the EVOH (B) and the
pigment (E) in a case of melt extrusion process of the resin
composition over a long period of time.
[0052] Such lubricant may include higher fatty acid esters (for
example, methyl ester, isopropyl ester, butyl ester, octyl ester,
and the like of lauric acid, myristic acid, palmitic acid, stearic
acid, behenic acid, oleic acid, and the like); higher fatty acid
amides (saturated aliphatic amides, such as stearic acid amide and
behenic acid amide, unsaturated fatty acid amides, such as oleic
acid amide and erucic acid amide, bis-fatty acid amides, such as
ethylenebis stearic acid amide, ethylenebis oleic acid amide,
ethylenebis erucic acid amide, and ethylenebis lauric acid amide,
and the like); low molecular weight polyolefin (for example, low
molecular weight polyethylene or low molecular weight polypropylene
or an acid-modified product thereof having a number average
molecular weight of approximately from 500 to 10000); higher
alcohol, an ethylene fluoride resin, and the like. Among these,
higher fatty acid esters and higher fatty acid amides are used
preferably, and higher fatty acid amides are used even more
preferably.
[0053] The resin composition of the present invention contains the
polyolefin (A), the EVOH (B), the S-EVOH (C), and the pigment (E),
where a mass ratio (A/B) of the polyolefin (A) and the EVOH (B) is
from 3 to 99.5, a mass ratio (B/C) of the EVOH (B) and the S-EVOH
(C) is from 1 to 100, a mass ratio (E/C) of the pigment (E) and the
S-EVOH (C) is from 0.04 to 50, and an amount of the S-EVOH (C)
blended therein is from 0.01 to 2.4 parts by mass based on 100
parts by mass of a total amount of the polyolefin (A) and the EVOH
(B).
[0054] Further, it is preferred that the resin composition of the
present invention contains the polyolefin (A), the EVOH (B), the
S-EVOH (C), the EVAc (D), and the pigment (E), where the mass ratio
(B/C) of the EVOH (B) and the S-EVOH (C) is from 1 to 30, the mass
ratio (D/C) of the EVAc (D) and the S-EVOH (C) is from 0.1 to 15,
the mass ratio (E/C) of the pigment (E) and the S-EVOH (C) is from
0.04 to 1.2.
[0055] It is required that the mass ratio (A/B) of the polyolefin
(A) and the EVOH (B) in the resin composition of the present
invention is from 3 to 99.5. In a case that the mass ratio (A/B) is
less than 3, that is, when there is a lot of EVOH (B), the
dispersibility of the EVOH (B) in the polyolefin (A) becomes
insufficient and poor dispersion of the pigment (E) occurs, and
thus uneven coloration is prone to occur. It is preferred that the
mass ratio (A/B) is 5 or more. It is more preferred that the mass
ratio (A/B) is 7 or more. In contrast, in a case that the mass
ratio (A/B) is more than 99.5, even when the resin composition of
the present invention is applied to a recovery technique, it
becomes poor in the effect on waste reduction and the economic
efficiency for reutilization. It is preferred that the mass ratio
(A/B) is 50 or less. It is more preferred that the mass ratio (A/B)
is 35 or less. It is required that the mass ratio (B/C) of the EVOH
(B) and the S-EVOH (C) is from 1 to 100. In a case that the mass
ratio (B/C) is more than 100, the dispersibility of the EVOH (B)
becomes insufficient and poor dispersion of the pigment (E) occurs,
and thus there is a risk of occurring uneven coloration. The mass
ratio (B/C) is preferably 50 or less and more preferably 30 or
less. It is even more preferably 18 or less and particularly
preferably 15 or less. Meanwhile, even when the ratio of the S-EVOH
(C) is increased as much as the mass ratio (B/C) becomes less than
1, there is a tendency not to obtain further improvement of the
dispersibility. The mass ratio (B/C) is preferably 2 or more and
more preferably 3 or more.
[0056] It is preferred that the mass ratio (D/C) of the EVAc (D)
and the S-EVOH (C) is from 0.1 to 50. In a case that the mass ratio
(D/C) is more than 50, the dispersibility of the EVOH (B) is
insufficient and poor dispersion of the pigment (E) occurs, and
there is a risk of occurring uneven coloration. The mass ratio
(D/C) is more preferably 15 or less, even more preferably 7 or
less, and particularly preferably 3.3 or less. It is most
preferably 3 or less. In contrast, in a case that the mass ratio
(D/C) is less than 0.1, dispersibility of the EVOH (B) is
insufficient and poor dispersion of the pigment (E) occurs, and
thus there is a risk of occurring uneven coloration. The mass ratio
(D/C) is more preferably 1 or more and even more preferably 1.5 or
more.
[0057] It is required that the mass ratio (E/C) of the pigment (E)
and the S-EVOH (C) is from 0.04 to 50. In a case that the mass
ratio (E/C) is more than 50, poor dispersion derived from
aggregation of the pigment (E) occurs, and thus there is a risk of
occurring uneven coloration. The mass ratio (E/C) is preferably 25
or less and more preferably 1.2 or less. It is even more preferably
0.8 or less. In a case that the mass ratio (E/C) is less than 0.04,
dispersion of the pigment (E) is rather inhibited by the S-EVOH (C)
and thus uneven coloration occurs. Accordingly, it is preferred
that the mass ratio (E/C) is 0.1 or more.
[0058] It is preferred that a mass ratio (E/D) of the pigment (E)
and the EVAc (D) is from 0.02 to 10. In a case that the mass ratio
(E/D) is more than 10, poor dispersion derived from aggregation of
the pigment (E) occurs and thus uneven coloration is prone to
occur. In a case of melt extrusion process over a long period of
time, a degraded material, such as a scorch and a burnt, becomes
prone to be generated. The mass ratio (E/D) is more preferably 5 or
less and even more preferably 1 or less. In a case that the mass
ratio (E/D) is less than 0.02, dispersion of the pigment (E) is
rather inhibited by the EVAc (D) and thus there is a risk of
occurring uneven coloration. Therefore, the mass ratio (E/D) is
more preferably 0.05 or more and even more preferably 0.08 or
more.
[0059] It is preferred that the resin composition of the present
invention has a structure in which particles of the EVOH (B) are
dispersed in a polyolefin (A) matrix. The EVOH (B) preferably has a
dispersed particle diameter of 2 .mu.m or less and more preferably
from 0.1 to 1.5 .mu.m. In a case that the dispersed particle
diameter is more than 2 .mu.m, dispersibility of the EVOH (B) is
insufficient and poor dispersion of the pigment (E) occurs, and
thus there is a tendency to occur uneven coloration.
[0060] In a case there is the metal salt (F) of fatty acid in the
resin composition of the present invention as a component, it is
preferred that a mass ratio (F/E) of the metal salt (F) of fatty
acid and the pigment (E) is from 0.1 to 3. In a case that the mass
ratio (F/E) is more than 3, dispersibility of the pigment becomes
insufficient and thus there is a risk of occurring uneven
coloration. It is more preferred that the mass ratio (F/E) is 2.8
or less. In contrast, in a case that the mass ratio (F/E) is less
than 0.1, there is a risk of generating a fish eye derived from
aggregation of the pigment (E). It is more preferred that the mass
ratio (F/E) is 0.2 or more.
[0061] It is required that the amount of the S-EVOH (C) blended in
the resin composition of the present invention is from 0.01 to 2.4
parts by mass based on 100 parts by mass of a total amount of the
polyolefin (A) and the EVOH (B). In a case that the amount of the
S-EVOH (C) blended therein is large, dispersibility of the EVOH (B)
is insufficient and poor dispersion of the pigment (E) occurs, and
thus there is a risk of occurring uneven coloration. The amount of
the S-EVOH (C) blended therein is preferably 2 parts by mass or
less based on 100 parts by mass of a total amount of the polyolefin
(A) and the EVOH (B) and more preferably 1.5 parts by mass or less.
In contrast, also in a case that the amount of the S-EVOH (C)
blended therein is small, dispersibility of the EVOH (B) is
insufficient and poor dispersion of the pigment (E) occurs, and
thus there is a risk of occurring uneven coloration. It is
preferred that the amount of the S-EVOH (C) blended therein is 0.2
parts by mass or more based on 100 parts by mass of a total amount
of the polyolefin (A) and the EVOH (B). It is more preferred that
the amount is 0.3 parts by mass or more.
[0062] It is preferred that an amount of the EVAc (D) blended
therein is from 0.2 to 10 parts by mass based on 100 parts by mass
of a total amount of the polyolefin (A) and the EVOH (B). In a case
that the amount of the EVAc (D) blended therein is large, there is
a risk of decreasing the mechanical properties. It is more
preferred that the amount of the EVAc (D) blended therein is 3
parts by mass or less based on 100 parts by mass of a total amount
of the polyolefin (A) and the EVOH (B). In contrast, in a case that
the amount of the EVAc (D) blended therein is small, dispersibility
of the EVOH (B) is insufficient and poor dispersion of the pigment
(E) occurs, and thus there is a risk of occurring uneven
coloration. It is more preferred that the amount of the EVAc (D)
blended therein is 1 part by mass or more based on 100 parts by
mass of a total amount of the polyolefin (A) and the EVOH (B).
[0063] It is preferred that an amount of the pigment (E) blended
therein is from 0.03 to 10 parts by mass based on 100 parts by mass
of a total amount of the polyolefin (A) and the EVOH (B). In a case
that the amount of the pigment (E) blended therein is large, there
is a risk of generating a fish eye derived from aggregation of the
pigment (E). It is more preferred that the amount of the pigment
(E) blended therein is 8 parts by mass or less based on 100 parts
by mass of a total amount of the polyolefin (A) and the EVOH (B).
In contrast, in a case that the amount of the pigment (E) blended
therein is small, dispersibility of the pigment (E) becomes
insufficient and thus there is a risk of occurring uneven
coloration. It is more preferred that the amount of the pigment (E)
blended therein is 0.1 parts by mass or more based on 100 parts by
mass of a total amount of the polyolefin (A) and the EVOH (B).
[0064] It is preferred that an amount of the metal salt (F) of
fatty acid blended therein is from 0.01 to 1 parts by mass based on
100 parts by mass of a total amount of the polyolefin (A) and the
EVOH (B). In a case that the amount of the metal salt (F) of fatty
acid blended therein is large, there is a risk of deteriorating the
color phase. It is more preferred that the amount of the metal salt
(F) of fatty acid blended therein is 0.8 parts by mass or less
based on 100 parts by mass of a total amount of the polyolefin (A)
and the EVOH (B). In contrast, in a case that the amount of the
metal salt (F) of fatty acid blended therein is small, there is a
risk of generating a fish eye derived from aggregation of the EVOH
(B). It is more preferred that the amount of the metal salt (F) of
fatty acid blended therein is 0.03 parts by mass or more based on
100 parts by mass of a total amount of the polyolefin (A) and the
EVOH (B).
[0065] It is preferred that an amount of the hydrotalcite (G)
blended therein is from 0.0001 to 10 parts by mass based on 100
parts by mass of a total amount of the polyolefin (A) and the EVOH
(B). In a case that the amount of the hydrotalcite (G) blended
therein is small, the effect of reducing generation of a degraded
material, such as a scorch and a burnt, in a case of melt extrusion
process over a long period of time is sometimes not obtained
sufficiently. It is more preferred that the amount of the
hydrotalcite (G) blended therein is 0.001 parts by mass or more
based on 100 parts by mass of a total amount of the polyolefin (A)
and the EVOH (B). In contrast, in a case that the amount of the
hydrotalcite (G) blended therein is large, thermal degradation of
the EVOH in the resin composition thus obtained is accelerated and
thus there is a risk of occurring forming due to a decomposition
gas and coloration. It is more preferred that the amount of the
hydrotalcite (G) blended therein is 1 part by mass or less based on
100 parts by mass of a total amount of the polyolefin (A) and the
EVOH (B).
[0066] It is preferred that an amount of the conjugated polyene
compound (H) blended therein is from 0.000001 to 1 parts by mass
based on 100 parts by mass of a total amount of the polyolefin (A)
and the EVOH (B). In a case that the amount of the conjugated
polyene compound (H) blended therein is small, the effects of
reducing generation of a degraded material, such as a scorch and a
burnt, in a case of melt extrusion process of the resin composition
over a long period of time and suppressing deterioration of the
color phase of a molded article thus obtained are not sometimes
obtained sufficiently. It is more preferred that the amount of the
conjugated polyene compound (H) blended therein is 0.00001 parts by
mass or more based on 100 parts by mass of a total amount of the
polyolefin (A) and the EVOH (B). In contrast, in a case that the
amount of the conjugated polyene compound (H) blended therein is
large, there is a risk of accelerating gelation of a resin
composition thus obtained. It is more preferred that the amount of
the conjugated polyene compound (H) blended therein is 0.5 parts by
mass or less based on 100 parts by mass of a total amount of the
polyolefin (A) and the EVOH (B).
[0067] It is preferred that an amount of the lubricant (I) blended
therein is from 0.00001 to 1 parts by mass based on 100 parts by
mass of a total amount of the polyolefin (A) and the EVOH (B). In a
case that the amount of the lubricant (I) blended therein is small,
a flow of the resin composition is suppressed on a metal wall of a
cylinder, a screw, an adapter, or the like when melt molded
processing over a long period of time and thus the effect of
reducing generation of a degraded material, such as a scorch and a
burnt, is not sometimes obtained sufficiently. It is more preferred
that the amount of the lubricant (I) blended therein is 0.00005
parts by mass or more based on 100 parts by mass of a total amount
of the polyolefin (A) and the EVOH (B). In contrast, in a case that
the amount of the lubricant (I) blended therein is large, the
lubricant (I) is separated when a resin composition thus obtained
is melt molded and thus there is a risk of decreasing adhesiveness
to an adjacent layer when molding a multilayered structure. It is
preferred that the amount of the lubricant (I) blended therein is
0.5 parts by mass or less based on 100 parts by mass of a total
amount of the polyolefin (A) and the EVOH (B).
[0068] It is also possible to blend other additives into the resin
composition of the present invention as long as not inhibiting the
effects of the invention. Examples of such an additive may include
an antioxidant, an ultraviolet absorber, a plasticizer, an
antistatic, a filler, and other polymer compounds. Specific
examples of the additives may include the following. A content of
the additives is preferably 30 mass % or less based on a total mass
of the resin composition and more preferably 10 mass % or less.
[0069] Antioxidant: 2,5-di-t-butylhydroquinone,
2,6-di-t-butyl-p-cresol, 4,4'-thiobis(6-t-butylphenol),
2,2'-methylenebis(4-methyl-6-t-butylphenol),
octadecyl-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate,
4,4'-thiobis(6-t-butylphenol), and the like.
[0070] Ultraviolet Absorber:
ethylene-2-cyano-3,3'-diphenylacrylate,
2-(2'-hydroxy-5'-methylphenyl)benzotriazole,
2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole,
2-hydroxy-4-methoxybenzophenone,
2,2'-dihydroxy-4-methoxybenzophenone,
2-hydroxy-4-octoxybenzophenone, and the like.
[0071] Plasticizer: dimethyl phthalate, diethyl phthalate, dioctyl
phthalate, wax, liquid paraffin, phosphate ester, and the like.
[0072] Antistatic: pentaerythritol monostearate, sorbitan
monopalmitate, sulfated polyolefins, polyethylene oxide, carbowax,
and the like.
[0073] Filler: glass fibers, asbestos, ballastnite, calcium
silicate, and the like.
[0074] In addition, many other polymer compounds can also be
blended into the resin composition of the present invention as long
as not inhibiting the actions and the effects of the present
invention.
[0075] Next, a description is given to a method of obtaining the
resin composition of the present invention by mixing the polyolefin
(A), the EVOH (B), the S-EVOH (C), and the pigment (E) and method
of molding the resin composition.
[0076] Examples of means for mixing each component to obtain the
resin composition of the present invention may be a ribbon blender,
a high speed mixer cokneader, a mixing roll, an extruder, an
intensive mixer, and the like.
[0077] A mixing method to obtain the resin composition of the
present invention is not particularly limited, and may include: a
method comprising melt kneading after dry blending the polyolefin
(A), the EVOH (B), the S-EVOH (C) and the pigment (E) in one time;
a method comprising melt kneading a portion of the polyolefin (A),
the EVOH (B), the S-EVOH (C) and the pigment (E) in advance,
followed by blending other components thereinto and melt kneading;
and a method comprising melt kneading after blending a multilayered
structure containing a portion of the polyolefin (A), the EVOH (B),
the S-EVOH (C) and the pigment (E) into other components.
[0078] Among all, a method of melt kneading a scrap of collected
chips and defective products generated when obtaining a molded
object made of a multilayered structure, containing the polyolefin
(A) the EVOH (B) and the pigment (E), and the S-EVOH (C) is
preferred. Thus, the additive blended when melt kneading collected
scraps is referred to as a recycling agent, and here, the S-EVOH
(C) is used as the recycling agent. At this time, in a case of
adding another component to the S-EVOH (F), it is preferred that
they are melt kneaded in advance to make up a resin composition
containing all of them, followed by adding it to the scraps. It is
preferred that such recycling agent is blended into the scraps in
the form of pellets. It is preferred that the scraps are preground
into an appropriate size, and it is a preferred method of producing
a resin composition of the present invention to dry blend the
recycling agent in the form of pellets with the ground scraps,
followed by melt kneading. As the scraps, scraps obtained from one
molded object may be used and related scraps obtained from two or
more molded objects may also be used by mixing them.
[0079] A particularly preferred embodiment is a method comprising
melt kneading a recovery of a multilayered structure, including a
layer made of a resin composition containing the polyolefin (A) and
the pigment (E) and a layer made of the saponified ethylene-vinyl
acetate copolymer (B), and a recycling agent made of a resin
composition containing the saponified ethylene-vinyl acetate
copolymer (C). At this time, a more preferred embodiment is a
method comprising melt kneading a recovery of a multilayered
structure, including a layer made of a resin composition containing
the polyolefin (A) and the pigment (E) and a layer made of the
saponified ethylene-vinyl acetate copolymer (B), and a recycling
agent made of a resin composition containing the saponified
ethylene-vinyl acetate copolymer (C) and the ethylene-vinyl acetate
copolymer (D).
[0080] Further, the scraps as a raw material for the resin
composition of the present invention may also be made of a
multilayered structure including a recovery layer. That is, a
molded product may be produced made of a multilayered structure
including a recovery layer made of a resin composition obtained
from a recovery and a scrap recovery of the molded product may also
be used again as a raw material for a recovery layer in a similar
multilayered structure.
[0081] When the resin composition of the present invention contains
components other than the polyolefin (A), the EVOH (B), the S-EVOH
(C) and the pigment (E), a method of blending those components is
not particularly limited and they can be blended in operations
similar to each component of the (A), (B), (C), and (E) described
above. Among all, when the resin composition of the present
invention contains the EVAc (D) or the metal salt (F) of fatty
acid, it is preferred to add to the S-EVOH (C) to use as the
recycling agent. Also in a case that the resin composition of the
present invention contains the hydrotalcite (G), it is preferred to
add to the S-EVOH (C) to use as the recycling agent. For a method
of producing such recycling agent, similar methods as above are
employed.
[0082] In a case that the conjugated polyene compound (H) is
contained in the resin composition of the present invention, it may
be contained in the EVOH (B) in advance and may also be added to
the S-EVOH (C) to use as the recycling agent. Alternatively, it can
also be blended when producing the resin composition. From the
perspective of suppressing coloration in yellowish brown due to
deterioration of the EVOH (B) in the resin composition when melt
extrusion processing the resin composition of the present invention
over a long period of time, it is preferred to contain it in the
EVOH (B) in advance.
[0083] Particularly in a case that the conjugated polyene compound
(H) is blended in the EVOH (B) in advance, a high effect of
suppressing aggregation of the EVOH (B) at a micro-scale level can
be obtained even when the amount of the conjugated polyene compound
(H) blended therein is small, so that it is preferred. A method of
blending the conjugated polyene compound (H) into the EVOH (B) in
advance is not particularly limited, while its example may be a
method comprising dissolving from 0.000001 to 10 parts by mass of
the conjugated polyene compound (H) based on 100 parts by mass of
the EVOH (B) in a product of dissolving the EVOH (B) in a good
solvent of the EVOH (B), such as a water/methanol mixed solvent,
extruding the mixed liquid from a nozzle to a poor solvent for
precipitation and coagulation, and washing and drying it to obtain
the EVOH (B) having the conjugated polyene compound (H) blended
therein, and the like.
[0084] In a case that the lubricant (I) is contained in the resin
composition of the present invention, it may be contained in the
EVOH (B) in advance and may also be added to the S-EVOH (C) to use
as the recycling agent. Alternatively, it can also be blended when
producing the resin composition. From the perspective of
suppressing generation of a degraded material, such as a scorch and
a burnt, occurring when melt extrusion processing the resin
composition of the present invention over a long period of time, in
particular, a scorch and a burnt caused by deterioration of the
EVOH (B), it is preferred to contain it in the EVOH (B) in
advance.
[0085] Particularly in a case that the lubricant (I) is blended in
the EVOH (B) in advance, even when the amount of the lubricant (I)
blended therein is less, the effect of suppressing adhesion of the
EVOH (B) to a metal wall of a cylinder, a screw, an adapter, or the
like can be high, so that it is preferred. A method of blending the
lubricant (I) into the EVOH (B) in advance is not particularly
limited, while its example may be a method comprising melt mixing
the EVOH (B) and the lubricant (I) using an extruder, and the
like.
[0086] The resin composition of the present invention can be molded
into any molded product, such as a film, a sheet, a tube, a bottle,
and a cup using a melt extrusion molding machine, a compression
molding machine, a transfer molding machine, an injection molding
machine, a blow molding machine, a thermoforming machine, a
rotational molding machine, a dip molding machine, or the like that
is well known. An extrusion temperature while molding is
appropriately selected depending on the type of the polyolefin (A)
constituting the resin composition of the present invention, the
melt indexes of the polyolefin (A) and the EVOH (B), the
composition ratio of the polyolefin (A) and the EVOH (B), the type
of the molding machine, or the like, while it is in a range of from
170 to 350.degree. C. in many cases.
[0087] A preferred embodiment of the present invention is a
multilayered structure including at least two layers of a layer
made of the above resin composition and a layer made of the
saponified ethylene-vinyl acetate copolymer having an ethylene
content of from 20 to 65 mol % and having a degree of
saponification of vinyl acetate units of 96% or more. Appropriate
examples of the layer constitution are expressed, for example, as
the following layer constitutions while indicating the resin
composition of the present invention as c, the polyolefin as a, the
EVOH as b, and the adhesive resin as ad. Here, as the ad, it is
possible to preferably use a modified polyolefin resin modified
with unsaturated carboxylic acid or a derivative thereof.
Three Layers c/ad/b Four Layers a/c/ad/b Five Layers c/ad/b/ad/c,
a/ad/b/ad/c Six Layers a/c/ad/b/ad/a, c/a/ad/b/ad/a, c/a/ad/b/ad/c,
a/c/ad/b/ad/c Seven Layers a/c/ad/b/ad/c/a
[0088] It is also possible to obtain the resin composition of the
present invention by melt kneading a scrap of such multilayered
structure. Accordingly, in a case that there is an ad layer in the
multilayered structure, it is considered that an adhesive resin
(ad) is contained in the resin composition of the present invention
as a component.
[0089] As a method of producing the multilayered structure, a
method comprising performing so-called coextrusion molding is
preferred to use a number of extruders corresponding to the types
of resin layer for simultaneous extrusion molding of flows of the
resins melt in this extruder in a state of laminated layers. As
another method, it is also possible to employ a molding method,
such as extrusion coating and dry lamination. In addition,
stretching, such as uniaxial stretching, biaxial stretching, or
blow stretching, of a molded product using only the resin
composition of the present invention or a multilayered structure
containing a resin composition of the present invention is
performed, thereby enabling to obtain a molded object excellent in
mechanical properties, gas barrier properties, and the like.
[0090] Since the multilayered structure having the above layer
constitutions contains the EVOH excellent in barrier properties, it
is useful as a packaging material for foods, medicine, medical
devices requiring the gas barrier properties.
[0091] Since the resin composition of the present invention has the
EVOH with high dispersibility and the pigment with high
dispersibility, it is possible to provide a molded object having
improved uneven coloration. Since it is excellent in the mechanical
properties and the barrier properties and a molded object with a
good appearance is obtained, its industrial significance is
great.
EXAMPLES
[0092] In present Examples, the following raw materials were used.
In Production Examples, Examples, and Comparative Examples below,
parts are based on mass, unless otherwise specified.
[Polyolefin (A)]
[0093] A-1: polypropylene [density of 0.90 g/cm.sup.3, melt index
of 1.4 g/10 minutes (ASTM-D 1238, 230.degree. C., load of 2160 g)]
A-2: low density polyethylene [density of 0.919 g/cm.sup.3, melt
index of 1.0 g/10 minutes (ASTM-D 1238, 190.degree. C., load of
2160 g)]
[EVOH (B)]
[0094] B-1: ethylene content of 32 mol %, degree of saponification
of 99.7 mol %, limiting viscosity of 1.1 dL/g at 30.degree. C. in
aqueous phenol (water/phenol=15/85 (mass ratio)), density of 1.15
g/cm.sup.3, melt index of 1.6 g/10 minutes (ASTM-D 1238,
190.degree. C., load of 2160 g) B-2: ethylene content of 32 mol %,
degree of saponification of 99.8 mol %, limiting viscosity of 0.092
dL/g at 30.degree. C. in aqueous phenol (water/phenol=15/85 (mass
ratio)), density of 1.15 g/cm.sup.3, melt index of 6.6 g/10 minutes
(ASTM-D 1238, 190.degree. C., load of 2160 g)
[S-EVOH (C)]
[0095] C-1: ethylene content of 89 mol %, degree of saponification
of 97 mol %, melt index of 5.1 g/10 minutes (ASTM-D 1238,
190.degree. C., load of 2160 g)
[EVAc (D)]
[0096] D-1: vinyl acetate content of 19 mass %, melt index of 2.5
g/10 minutes (ASTM-D 1238, 190.degree. C., load of 2160 g)
[Pigment (E)]
[0097] E-1: titanium oxide (rutile type titanium dioxide obtained
by a chlorine method, white inorganic pigment, TiO.sub.2, average
particle diameter of 0.19 .mu.m, chlorine content of 42 ppm)
[Metal Salt (F) of Fatty Acid]
[0098] F-1: calcium stearate F-2: zinc stearate
[Hydrotalcite (G)]
[0099] G-1: "ZHT-4A" produced by Kyowa Chemical Industry Co.,
Ltd.
[Conjugated Polyene Compound (H)]
[0100] H-1: sorbic acid
[Lubricant (I)]
[0101] I-1: ethylenebis stearic acid amide
[Others]
[0102] Adhesive Resin: "MODIC AP P604V" produced by Mitsubishi
Chemical Corporation (brand for polypropylene), density of 0.90
g/cm.sup.3, melt index of 3.2 g/10 minutes (ASTM-D 1238,
230.degree. C., load of 2160 g), Antioxidant:
pentaerythritol-tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate]
[0103] Measurements were carried out in the following methods
respectively for a multilayered film obtained in Example regarding
a dispersed particle diameter of the EVOH (B) particles contained
in a recovery layer, whiteness of the multilayered film, and uneven
coloration of a thermoformed container.
[Dispersed Particle Diameter of EVOH Contained in Recovery
Layer]
[0104] A multilayered film was carefully cut with a microtome in a
direction perpendicular to the film surface and a recovery layer
was further taken out using a scalpel. Platinum was vapor deposited
on the exposed cross section in a reduced pressure atmosphere. The
cross section with platinum vapor deposited thereon was taken in a
picture using a scanning electron microscope (SEM) with 10000
magnification, a region in this picture including approximately 20
particles of the EVOH (E) was selected, particle diameters of the
respective particle images in the region were measured, and their
average value was calculated to define it as a dispersed particle
diameter. For the particle diameters of the respective particles, a
longer diameter (longest part) of the particles observed in the
picture was measured to define it as the particle diameter. The
film was cut vertically in a direction of extrusion, and the
picture was taken from a direction vertical to the cross
section.
[Whiteness of Multilayered Film]
[0105] A multilayered film was measured using a spectroscopic color
difference meter (Spectro Color Meter SE2000, manufactured by NDK,
Incorporated) in accordance with a method of ASTM E313. Whiteness
was applied only in a case of the pigment (E) being titanium oxide.
High whiteness indicates good dispersion of the pigment in the
resin composition.
[Uneven Coloration of Thermoformed Container]
[0106] Five thermoformed containers were prepared at random and a
side of each container was seen through a fluorescent lamp to
visually check the following conditions.
A: No shadow is found at all in all containers. B: Shadows can be
found in several areas when looked carefully. C: Shadows can be
found.
[0107] In accordance with the following methods, titanium oxides
coated with alumina and/or silica (E-2 through E-5) were
obtained.
E-2:
[0108] Based on 100 parts of E-1 (titanium oxide) as the pigment
(E), 4.0 parts, in terms of alumina, of an aqueous sodium aluminate
solution was added and it was stirred for 30 minutes. To this, 20%
sulfuric acid was added gradually for adjustment at pH=7.0 to be
further matured for 2 hours. After maturation, a slurry of titanium
oxide having a surface coated with the water-containing alumina was
filtered, and washed with running water, followed by drying. The
titanium oxide thus obtained was ground in a steam mill to obtain
titanium oxide (E-2) having a surface coated with alumina and
having an average particle diameter of 0.2 .mu.m. The amount of
chlorine contained in E-2 was 35 ppm.
E-3:
[0109] Octyltriethoxysilane was diluted with pure water in 2-fold
and it was stirred and hydrolyzed for 10 minutes to prepare a
hydrolysis product solution. The octyltriethoxysilane hydrolysis
product solution was added when grinding E-2 above in a steam mill,
and coating treatment was carried out on a surface of the titanium
oxide in an amount of coating at 0.3% based on the titanium oxide
pigment weight to obtain titanium oxide having a surface coated
with alumina and an alkylsilane compound (E-3). The amount of
chlorine contained in E-3 was 34 ppm.
E-4:
[0110] Based on 100 parts of E-1 (titanium oxide) as the pigment
(E), 3.2 parts, in terms of alumina, of an aqueous sodium aluminate
solution and 2.1 parts, in terms of silica, of an aqueous sodium
silicate solution were added and it was stirred for 30 minutes. To
this, 20% sulfuric acid was gradually added for adjustment at
pH=7.0 to be further matured for 2 hours. After maturation, a
slurry of titanium oxide having a surface coated with a mixture of
alumina and silica in a water-containing state was filtered, and
washed with running water, followed by drying to obtain titanium
oxide having a surface coated with a mixture of alumina and silica.
The titanium oxide thus obtained was ground in a steam mill to
obtain titanium oxide having a surface coated with a mixture of
alumina and silica and having an average particle diameter of 0.24
.mu.m (E-4). The amount of chlorine contained in E-4 was 20
ppm.
E-5:
[0111] Based on 100 parts of E-1 (titanium oxide) as the pigment
(E), 3.2 parts, in terms of alumina, of an aqueous sodium aluminate
solution and 2.1 parts, in terms of silica, of an aqueous sodium
silicate solution were added and it was stirred for 30 minutes. To
this, 20% sulfuric acid was gradually added for adjustment at
pH=7.0 to be further matured for 2 hours. After maturation, a
slurry of titanium oxide having a surface coated with a mixture of
alumina and silica in a water-containing state was filtered, and
washed with running water, followed by drying to obtain titanium
oxide having a surface coated with a mixture of alumina and silica.
Subsequently, while titanium oxide was stirred in a Henschel mixer,
0.2 parts of trimethylolethane (polyol) was added to be stirred for
10 minutes, and it was further ground in a steam mill to obtain
titanium dioxide (E-5) having a surface coated with polyol and a
mixture of alumina and silica and having an average particle
diameter of 0.24 .mu.m. The amount of chlorine contained in E-5 was
20 ppm.
[0112] In accordance with the following methods, masterbatches (MB1
through MB10) were obtained.
MB1
[0113] Using C-1 as the S-EVOH (C), D-1 as the EVAc (D), F-1 as the
metal salt (F) of fatty acid, G-1 as the hydrotalcite (G), and an
antioxidant, they were blended by dry blending to have a mass ratio
of C-1/D-1/F-1/G-1/antioxidant=25/67.5/5/2.5/0.2. A mixture thus
obtained was melt kneaded at an extrusion temperature of
200.degree. C. using a corotating twin screw extruder (TEX-30N
manufactured by Japan Steel Works, Ltd.) of 30 mm4, followed by
pelletizing to obtain a masterbatch (MB1).
MB2
[0114] In a same manner as MB1 other than using C-1 as the S-EVOH
(C), D-1 as the EVAc (D), F-1 as the metal salt (F) of fatty acid,
G-1 as the hydrotalcite (G), and an antioxidant and blending them
by dry blending to have a mass ratio of
C-1/D-1/F-1/G-1/antioxidant=10/82.5/5/2.5/0.2, a masterbatch (MB2)
was obtained.
MB3
[0115] In a same manner as MB1 other than using C-1 as the S-EVOH
(C), D-1 as the EVAc (D), F-1 as the metal salt (F) of fatty acid,
G-1 as the hydrotalcite (G), and an antioxidant and blending them
by dry blending to have a mass ratio of
C-1/D-1/F-1/G-1/antioxidant=25/71.5/1/2.5/0.2, a masterbatch (MB3)
was obtained.
MB4
[0116] In a same manner as MB1 other than using C-1 as the S-EVOH
(C), D-1 as the EVAc (D), F-1 as the metal salt (F) of fatty acid,
G-1 as the hydrotalcite (G), and an antioxidant and blending them
by dry blending to have a mass ratio of
C-1/D-1/F-1/G-1/antioxidant=25/52.5/20/2.5/0.2, a masterbatch (MB4)
was obtained.
MB5
[0117] In a same manner as MB1 other than using C-1 as the S-EVOH
(C), D-1 as the EVAc (D), F-1 as the metal salt (F) of fatty acid,
G-1 as the hydrotalcite (G), and an antioxidant and blending them
by dry blending to have a mass ratio of
C-1/D-1/F-1/G-1/antioxidant=5/85/5/5/0.2, a masterbatch (MB5) was
obtained.
MB6
[0118] In a same manner as MB1 other than using C-1 as the S-EVOH
(C), D-1 as the EVAc (D), F-1 as the metal salt (F) of fatty acid,
G-1 as the hydrotalcite (G), and an antioxidant and blending them
by dry blending to have a mass ratio of
C-1/D-1/F-1/G-1/antioxidant=85/5/5/5/0.2, a masterbatch (MB6) was
obtained.
MB7
[0119] Using C-1 as the S-EVOH (C), D-1 as the EVAc (D), F-1 as the
metal salt (F) of fatty acid, and an antioxidant, they were blended
by dry blending to have a mass ratio of
C-1/D-1/F-1/antioxidant=25/70/5/0.2. A mixture thus obtained was
melt kneaded at an extrusion temperature of 200.degree. C. using a
corotating twin screw extruder (TEX-30N manufactured by Japan Steel
Works, Ltd.) of 30 mm.phi., followed by pelletizing to obtain a
masterbatch (MB7).
MB8
[0120] In a same manner as MB1 other than using polyolefin (A-2)
instead of the EVAc (D), a masterbatch (MB8) was obtained.
MB9
[0121] Using C-1 as the S-EVOH (C), D-1 as the EVAc (D), F-2 as the
metal salt (F) of fatty acid, G-1 as the hydrotalcite (G), and an
antioxidant, they were blended by dry blending to have a mass ratio
of C-1/D-1/F-2/G-1/antioxidant=25/67.5/5/2.5/0.2. A mixture thus
obtained was melt kneaded at an extrusion temperature of
200.degree. C. using a corotating twin screw extruder (TEX-30N
manufactured by Japan Steel Works, Ltd.) of 30 mm.phi., followed by
pelletizing to obtain a masterbatch (MB9).
MB10
[0122] Using C-1 as the S-EVOH (C), D-1 as the EVAc (D), F-1 and
F-2 as the metal salt (F) of fatty acid, G-1 as the hydrotalcite
(G), and an antioxidant, they were blended by dry blending to have
a mass ratio of
C-1/D-1/F-1/F-2/G-1/antioxidant=25/65/2.5/5/2.5/0.2. A mixture thus
obtained was melt kneaded at an extrusion temperature of
200.degree. C. using a corotating twin screw extruder (TEX-30N
manufactured by Japan Steel Works, Ltd.) of 30 mm4, followed by
pelletizing to obtain a masterbatch (MB10).
Example 1
Production of Recovery
[0123] Using A-1 as the polyolefin (A) for outermost layers, B-1 as
the EVOH (B) for an innermost layer, "MODIC AP P604V" for the
adhesive resin layers, three-type five-layer coextrusion of
polyolefin layer/adhesive resin layer/EVOH layer/adhesive resin
layer/polyolefin layer=200.mu./20.mu./20.mu./20.mu./200.mu. was
carried out with a feedblock die to prepare a multilayered film.
The respective resins were supplied to the feedblock using a 32
mm.phi. extruder for the polyolefin layers, a 25 mm.phi. extruder
for the adhesive resin layers, and a 20 mm.phi. extruder for the
EVOH layer, respectively, and it was carried out at the temperature
for extrusion at 220.degree. C. for each resin, and also at
220.degree. C. in a die section and a feedblock section.
[0124] Subsequently, the multilayered film thus obtained was ground
with a grinder of 8 mm.phi. diameter meshes to obtain a recovery. A
recovery thus obtained had a mass ratio of polyolefin (A-1)/EVOH
(B-1)/adhesive resin=85.9/5.5/8.6.
[Preparation of Multilayered Structure Containing Pigment]
[0125] Using a mixture of a recovery, a masterbatch (MB1), and a
pigment (E-1) dry blended at a mass ratio of recovery/masterbatch
(MB1)/pigment (E-1)=100/3/0.3 for outermost layers, the EVOH (B-1)
for an innermost layer, and "MODIC AP P604V" for the adhesive resin
layers, three-type five-layer coextrusion of mixture layer/adhesive
resin layer/EVOH layer/adhesive resin layer/mixture
layer=200.mu./20.mu./20.mu./20.mu./200.mu. was carried out with a
feedblock die to prepare a multilayered film. The respective resins
were supplied to the feedblock using a 32 mm.phi. extruder for the
mixture layers, a 25 mm.phi. extruder for the adhesive resin
layers, a 20 mm.phi. extruder for the EVOH layer, respectively, and
it was carried out at the temperature for extrusion at 220.degree.
C. for each resin, and also at 220.degree. C. in a die section and
a feedblock section.
[0126] The whiteness of the multilayered film having mixture layers
and the particle diameter of the EVOH (B) in the mixture layers
were measured. Results are shown in Table 1 in collection.
[0127] The multilayered film having the mixture thus obtained was
thermoformed to obtain a thermoformed container. Forming conditions
were as follows. Thermoforming Machine: vacuum pressure deep draw
forming machine, model FX-0431-3 (manufactured by Asano
Seisakusho)
Compressed Air Pressure: 5 kgf/cm.sup.2 Die Shape (Round Cup
Shape): top of 75 mm.phi., bottom of 60 mm.phi., depth of 75 mm,
drawing ratio S=1.0
Die Temperature: 70.degree. C.
Sheet Temperature: 130.degree. C.
Heater Temperature: 400.degree. C.
Plug Dimensions: 45.phi..times.65 mm
Plug Temperature: 120.degree. C.
[0128] The uneven coloration of the thermoformed container thus
obtained was evaluated. Results and conditions were shown in Table
1 in collection.
Example 2
[0129] In a same manner as Example 1 other than using a masterbatch
(MB2) instead of the masterbatch (MB1), a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. Results are shown in Table 1 in
collection.
Example 3
[0130] In a same manner as Example 1 other than using a masterbatch
(MB3) instead of the masterbatch (MB1), a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. Results are shown in Table 1 in
collection.
Example 4
[0131] In a same manner as Example 1 other than using a masterbatch
(MB4) instead of the masterbatch (MB1), a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. Results are shown in Table 1 in
collection.
Example 5
[0132] In a same manner as Example 1 other than coextrusion molding
using a mixture of a recovery, a masterbatch (MB1), and a pigment
(E-1) dry blended at a mass ratio of recovery/masterbatch
(MB1)/pigment (E-1)=100/3/0.05 for outermost layers, a multilayered
film having mixture layers was prepared to obtain a thermoformed
container, and they were evaluated. Results are shown in Table 1 in
collection.
Example 6
[0133] In a same manner as Example 1 other than preparing a
recovery having layer thicknesses of polyolefin layer/adhesive
resin layer/EVOH layer/adhesive resin layer/polyolefin
layer=200.mu./20.mu./4.mu./20.mu./200.mu. in the production of a
recovery of Example 1, a multilayered film having mixture layers
was prepared to obtain a thermoformed container, and they were
evaluated. The mass ratio of each component of the recovery was
polyolefin (A-1)/saponified ethylene-vinyl acetate copolymer
(B-1)/adhesive resin=89.9/1.1/9. Results are shown in Table 1 in
collection.
Example 7
[0134] In a same manner as Example 1 other than using a masterbatch
(MB7) instead of the masterbatch (MB1), a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. Results are shown in Table 1 in
collection.
Example 8
[0135] In a same manner as Example 1 other than, using polyolefin
containing a pigment having polyolefin (A-1) and a pigment (E-1)
dry blended at a mass ratio of polyolefin (A-1)/pigment
(E-1)=100/0.3 for outermost layers, B-1 as the EVOH (B) for an
innermost layer, "MODIC AP P604V" for the adhesive resin layers,
preparing a multilayered film by carrying out three-type five-layer
coextrusion of polyolefin layer/adhesive resin layer/EVOH
layer/adhesive resin layer/polyolefin
layer=200.mu./20.mu./20.mu./20.mu./200.mu. with a feedblock die in
the production of a recovery of Example 1, a multilayered film
having mixture layers was prepared to obtain a thermoformed
container, and they were evaluated. Results are shown in Table 1 in
collection.
Example 9
[0136] In a same manner as Example 1 other than using a masterbatch
(MB5) instead of the masterbatch (MB1), a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. Results are shown in Table 1 in
collection.
Example 10
[0137] In a same manner as Example 1 other than using a masterbatch
(MB8) instead of the masterbatch (MB1), a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. Results are shown in Table 1 in collection. It
should be noted that the content of the polyolefin (A) shown in
Table 1 represents a total of the polyolefin (A-1) and the
polyolefin (A-2).
Comparative Example 1
[0138] In a same manner as Example 1 other than preparing a
recovery using a multilayered film having layer thicknesses of
polyolefin layer/adhesive resin layer/EVOH layer/adhesive resin
layer/polyolefin layer=200.mu./20.mu./120.mu./20.mu./200.mu. in the
production of a recovery of Example 1, a multilayered film having
mixture layers was prepared to obtain a thermoformed container, and
they were evaluated. The mass ratio of each component of the
recovery was polyolefin (A-1)/saponified ethylene-vinyl acetate
copolymer (B-1)/adhesive resin=67.4/25.8/6.7. Results are shown in
Table 1 in collection.
Comparative Example 2
[0139] In a same manner as Example 1 other than using a masterbatch
(MB6) instead of the masterbatch (MB1) in Example 1, a multilayered
film having mixture layers was prepared to obtain a thermoformed
container, and they were evaluated. Results are shown in Table 1 in
collection.
Comparative Example 3
[0140] In a same manner as Example 1 other than using a mixture of
a recovery, a masterbatch (MB1), and a pigment (E-1) dry blended at
a mass ratio of recovery/masterbatch (MB1)/pigment
(E-1)=100/3/0.025 for outermost layers in Example 1, a multilayered
film having mixture layers was prepared to obtain a thermoformed
container, and they were evaluated. Results are shown in Table 1 in
collection.
TABLE-US-00001 TABLE 1 Example Example Example Example Example
Example Example Example 1 2 3 4 5 6 7 8 Resin Composition
Conditions Composition (parts by mass) Polyolefin (A) 85.9 85.9
85.9 85.9 85.9 89.9 85.9 85.9 EVOH (B) 5.5 5.5 5.5 5.5 5.5 1.1 5.5
5.5 S-EVOH (C) 0.75 0.3 0.75 0.75 0.75 0.75 0.75 0.75 EVAc (D) 2
2.5 2.1 1.6 2 2 2.1 2 Pigment (E) 0.3 0.3 0.3 0.3 0.05 0.3 0.3 0.56
Metal salt (F) 0.15 0.15 0.03 0.60 0.15 0.15 0.15 0.15 of fatty
acid Hydrotalcite (G) 0.075 0.075 0.075 0.075 0.075 0.075 0 0.075
Adhesive resin 8.6 8.6 8.6 8.6 8.6 9 8.6 8.6 Antioxidant 0.006
0.006 0.006 0.006 0.006 0.006 0.006 0.006 Mass Ratio (A/B) 15.6
15.6 15.6 15.6 15.6 81.7 15.6 15.6 (B/C) 7.3 18.3 7.3 7.3 7.3 1.5
7.3 7.3 (D/C) 2.7 8.3 2.9 2.1 2.7 2.7 2.8 2.7 (E/C) 0.4 1 0.4 0.4
0.07 0.4 0.4 0.75 (E/D) 0.15 0.12 0.14 0.19 0.02 0.15 0.14 0.28
(F/E) 0.5 0.5 0.1 2 3 0.5 0.5 0.3 Content of (C) *1 0.82 0.33 0.82
0.82 0.82 0.82 0.82 0.82 Evaluation Results EVOH particle 1.2 1.7
1.3 1.3 1.3 1.2 1.4 1.2 diameter (.mu.) Uneven coloration A A A A A
A A A Whiteness 92.3 91.3 91.6 92.0 90.1 92.1 90.5 92.3 Example
Example Comparative Comparative Comparative 9 10 Example 1 Example
2 Example 3 Resin Composition Conditions Composition (parts by
mass) Polyolefin (A) 85.9 87.9 67.4 85.9 85.9 EVOH (B) 5.5 5.5 25.8
5.5 5.5 S-EVOH (C) 0.15 0.75 0.75 2.5 0.75 EVAc (D) 2.5 -- 2 0.15 2
Pigment (E) 0.3 0.3 0.3 0.3 0.025 Metal salt (F) 0.15 0.15 0.15
0.15 0.15 of fatty acid Hydrotalcite (G) 0.15 0.075 0.075 0.15
0.075 Adhesive resin 8.6 8.6 6.7 8.6 8.6 Antioxidant 0.006 0.006
0.006 0.006 0.006 Mass Ratio (A/B) 15.6 16.0 2.6 15.6 15.6 (B/C)
36.7 7.3 34.5 2.2 7.3 (D/C) 17 -- 2.7 0.059 2.7 (E/C) 2 0.4 0.4
0.12 0.03 (E/D) 0.12 -- 0.15 2 0.01 (F/E) 0.5 0.5 0.5 0.5 6 Content
of (C) *1 0.16 0.80 0.80 2.78 0.82 Evaluation Results EVOH particle
2.1 2.0 2.3 2.5 1.3 diameter (.mu.) Uneven coloration B B C C C
Whiteness 90.2 90.4 87.1 88.9 86.1 *1 Content of (C) based on 100
parts by mass of (A) + (B) (parts by mass )
[0141] According to the above results, in Example 1 having all of
the mass ratio (A/B) of the polyolefin (A) and the EVOH (B), the
mass ratio (B/C) of EVOH (B)/S-EVOH (C), the mass ratio (E/C) of
pigment (E)/S-EVOH (C), and the content of the S-EVOH (C) in the
range of claims, a molded object having a small particle diameter
of the EVOH (B) and good dispersibility thereof, excellent in
whiteness without uneven coloration was obtained
[0142] In both Comparative Example 1 having a large thickness of
the EVOH (B) in the recovery, and as a result, having a large
amount of EVOH (B) and Comparative Example 2 having a large amount
of S-EVOH (C) in the masterbatch, the particle diameter of the EVOH
(B) in the resin composition became large, there was uneven
coloration, and the whiteness was insufficient. In Comparative
Example 3 having a small amount of pigment (E), the particle
diameter of EVOH (B) was small. However, the dispersibility of the
pigment was insufficient, there was uneven coloration, and the
whiteness was insufficient.
Example 11
[0143] The evaluation results of the multilayered film having
mixture layers and the thermoformed container in Example 1 are
shown again in Table 2 as Example 11. Further, a single layer film
was prepared as follows for evaluation. Evaluation results are
shown in Table 2.
[Preparation of Single Layer Structure Containing Pigment]
[0144] Using a mixture of the recovery obtained in Example 1, a
masterbatch (MB1), and a pigment (E-1) dry blended at a mass ratio
of recovery/masterbatch (MB1)/pigment (E-1)=100/3/0.3, extrusion
molding of a 100 .mu.m single layer film was carried out for 48
hours. The extrusion molding of the mixture was carried out using a
32 mmq) extruder at a temperature for extrusion of 220.degree. C.
and at a temperature in a die section of 220.degree. C.
[Evaluation of White Streaks in Single Layer Film]
[0145] The single layer film was cut out in 20 cm.times.20 cm and
presence of white streaks in the single layer film was visually
checked to evaluate the presence of white streaks as follows.
Results are shown in Table 2.
A: No white streak was generated at all. B: Small white streaks
were slightly generated. C: Large white streaks were generated.
[Measurement of YI Value of Single Layer Film]
[0146] As a surface color of the single layer film, a YI value was
measured in conformity to JIS-K-7103. Results are shown in Table
2.
[Measurement of Screw Adhesion Amount After Extrusion of Single
Layer Film]
[0147] After carrying out extrusion of a single layer film for 48
hours, 2 kg of LDPE ("NOVATEC LD LA320" produced by Japan
polyethylene Corporation) was continuously charged to carry out
purging of the extruder, the adapter, and the die. After finished
flowing the LDPE, the operation was stopped to take out a screw and
the LDPE remained on the screw was eliminated, and the deteriorated
screw build-up was collected to weight the mass of the screw
build-up thus obtained. Results are shown in Table 2.
Example 12
[0148] Based on 100 parts of EVOH chips of B-1 as the EVOH (B),
0.02 parts of 1-1 was added as the lubricant (I) for dry blending,
and it was shaken until the lubricant (I) was dispersed uniformly
on the surfaces of the EVOH chips to obtain a mixture of the EVOH
(B-1) and the lubricant (1-1).
[0149] In a same manner as Example 1 other than using the mixture
obtained as above instead of B-1 in Example 1, a recovery was
produced to prepare a multilayered film having mixture layers and a
thermoformed container was obtained to evaluate them. Results are
shown in Table 2 in collection. In addition, in a same manner as
Example 11 other than using the recovery produced as above instead
of the recovery obtained in Example 1 in Example 11, a single layer
film was prepared to carry out evaluation of white streaks in the
single layer film, measurement of a YI value, and measurement of a
screw adhesion amount after extrusion of the single layer film.
Results are shown in Table 2 in collection.
Example 13
[0150] As the EVOH (B), 2000 parts of B-2 was put into 18000 parts
of mixed solvent of water/methanol=40/60 (mass ratio) and it was
stirred at 60.degree. C. for six hours to be dissolved completely.
To this solution, 2 parts of H-1 (sorbic acid) as the conjugated
polyene compound (H) was added, and it was further stirred at
60.degree. C. for one hour to completely dissolve H-1, and thus an
EVOH solution containing the conjugated polyene compound (H-1) was
obtained. This EVOH solution was continuously extruded from a
nozzle having a diameter of 4 mm into a coagulation bath of
water/methanol=95/5 (mass ratio) adjusted at 0.degree. C. to
coagulate the EVOH in strands. This strand was introduced into a
pelletizer to obtain porous EVOH chips. After washing the porous
EVOH chips thus obtained in order using 2000 parts of a 0.1 mass %,
based on 100 parts of the chips, aqueous acetic acid solution and
subsequently 2000 parts of ion exchanged water at 20.degree. C.,
they were immersed in 2000 parts of an aqueous solution containing
0.092% boric acid at 20.degree. C. for four hours. The EVOH chips
were subjected to deliquoring and separation to carry out drying
with a hot air dryer at 80.degree. C. for four hours, and further
drying at 100.degree. C. for sixteen hours, and thus EVOH chips of
the EVOH (B-2) containing the conjugated polyene compound (H-1)
were obtained. The H-1 (sorbic acid) content in the EVOH chips thus
obtained was 0.01 parts based on 100 parts of EVOH, and the boric
acid content was 0.019 in terms of boron. The EVOH chips had a melt
index (ASTM-D 1238, 190.degree. C., load of 2160 g) of 1.6 g/10
minutes.
[0151] In a same manner as Example 1 other than using the EVOH
chips of the EVOH (B-2) containing the conjugated polyene compound
(H-1) obtained as above instead of B-1 in Example 1, a recovery was
produced to prepare a multilayered film having mixture layers and a
thermoformed container was obtained to evaluate them. Results are
shown in Table 2 in collection. In addition, in a same manner as
Example 11 other than using the recovery produced as above instead
of the recovery obtained in Example 1 in Example 11, a single layer
film was prepared to carry out evaluation of white streaks in the
single layer film, measurement of a YI value, and measurement of a
screw adhesion amount after extrusion of the single layer film.
Results are shown in Table 2 in collection.
Example 14
[0152] Based on 100 parts of EVOH chips of the EVOH (B-2)
containing the conjugated polyene compound (H-1) obtained in
Example 13, 0.02 parts of 1-1 (ethylene stearic acid bisamide) was
added as the lubricant (I) for dry blending, and it was shaken
until the lubricant (I) was dispersed uniformly on the surfaces of
the EVOH chips to obtain a mixture of the EVOH (B-2) containing the
conjugated polyene compound (H-1) and the lubricant (I-1).
[0153] In a same manner as Example 1 other than using the mixture
obtained as above instead of B-1 in Example 1, a recovery was
produced to prepare a multilayered film having mixture layers and a
thermoformed container was obtained to evaluate them. Results are
shown in Table 2 in collection. In addition, in a same manner as
Example 11 other than using the recovery produced as above instead
of the recovery obtained in Example 1 in Example 11, a single layer
film was prepared to carry out evaluation of white streaks in the
single layer film, measurement of a YI value, and measurement of a
screw adhesion amount after extrusion of the single layer film.
Results are shown in Table 2 in collection.
Example 15
[0154] In a same manner as Example 14 other than using a
masterbatch (MB8) instead of a masterbatch (MB1), a recovery was
produced to prepare a multilayered film having mixture layers and a
thermoformed container was obtained for evaluation. Results are
shown in Table 2 in collection. In addition, in a same manner as
Example 14 other than using the recovery produced as above instead
of the recovery obtained in Example 14 in Example 14, a single
layer film was prepared to carry out evaluation of white streaks in
the single layer film, measurement of a YI value, and measurement
of a screw adhesion amount after extrusion of the single layer
film. Results are shown in Table 2 in collection. Here, the content
of the polyolefin (A) shown in Table 2 represents a total of the
polyolefin (A-1) and the polyolefin (A-2).
Example 16
[0155] In a same manner as Example 12 other than using E-2 instead
of E-1 as the pigment in Example 12, a multilayered film having
mixture layers was prepared and a thermoformed container was
obtained to evaluate them. In addition, in a same manner as Example
12 other than using E-2 instead of E-1 as the pigment in Example
12, a single layer film was prepared to carry out evaluation of
white streaks in the single layer film, measurement of a YI value,
and measurement of a screw adhesion amount after extrusion of the
single layer film. Results are shown in Table 2 in collection.
Example 17
[0156] In a same manner as Example 13 other than using E-2 instead
of E-1 as the pigment in Example 13, a multilayered film having
mixture layers was prepared and a thermoformed container was
obtained to evaluate them. In addition, in a same manner as Example
13 other than using E-2 instead of E-1 as the pigment in Example
13, a single layer film was prepared to carry out evaluation of
white streaks in the single layer film, measurement of a YI value,
and measurement of a screw adhesion amount after extrusion of the
single layer film. Results are shown in Table 2 in collection.
Example 18
[0157] In a same manner as Example 14 other than using E-2 instead
of E-1 as the pigment in Example 14, a multilayered film having
mixture layers was prepared and a thermoformed container was
obtained to evaluate them. In addition, in a same manner as Example
14 other than using E-2 instead of E-1 as the pigment in Example
14, a single layer film was prepared to carry out evaluation of
white streaks in the single layer film, measurement of a YI value,
and measurement of a screw adhesion amount after extrusion of the
single layer film. Results are shown in Table 2 in collection.
Example 19
[0158] In a same manner as Example 18 other than using a
masterbatch (MB9) instead of a masterbatch (MB1) in Example 18, a
multilayered film having mixture layers was prepared and a
thermoformed container was obtained to evaluate them. In addition,
in a same manner as Example 18 other than using a masterbatch (MB9)
instead of a masterbatch (MB1) in Example 18, a single layer film
was prepared to carry out evaluation of white streaks in the single
layer film, measurement of a YI value, and measurement of a screw
adhesion amount after extrusion of the single layer film. Results
are shown in Table 2 in collection.
Example 20
[0159] In a same manner as Example 18 other than using a
masterbatch (MB10) instead of a masterbatch (MB1) in Example 18, a
multilayered film having mixture layers was prepared and a
thermoformed container was obtained to evaluate them. In addition,
in a same manner as Example 18 other than using a masterbatch
(MB10) instead of a masterbatch (MB1) in Example 18, a single layer
film was prepared to carry out evaluation of white streaks in the
single layer film, measurement of a YI value, and measurement of a
screw adhesion amount after extrusion of the single layer film.
Results are shown in Table 2 in collection.
Example 21
[0160] In a same manner as Example 14 other than using E-3 instead
of E-1 as the pigment in Example 14, a multilayered film having
mixture layers was prepared and a thermoformed container was
obtained to evaluate them. In addition, in a same manner as Example
14 other than using E-3 instead of E-1 as the pigment in Example
14, a single layer film was prepared to carry out evaluation of
white streaks in the single layer film, measurement of a YI value,
and measurement of a screw adhesion amount after extrusion of the
single layer film. Results are shown in Table 2 in collection.
Example 22
[0161] In a same manner as Example 14 other than using E-4 instead
of E-1 as the pigment in Example 14, a multilayered film having
mixture layers was prepared and a thermoformed container was
obtained to evaluate them. In addition, in a same manner as Example
14 other than using E-4 instead of E-1 as the pigment in Example
14, a single layer film was prepared to carry out evaluation of
white streaks in the single layer film, measurement of a YI value,
and measurement of a screw adhesion amount after extrusion of the
single layer film. Results are shown in Table 2 in collection.
Example 23
[0162] In a same manner as Example 14 other than using E-5 instead
of E-1 as the pigment in Example 14, a multilayered film having
mixture layers was prepared and a thermoformed container was
obtained to evaluate them. In addition, in a same manner as Example
14 other than using E-5 instead of E-1 as the pigment in Example
14, a single layer film was prepared to carry out evaluation of
white streaks in the single layer film, measurement of a YI value,
and measurement of a screw adhesion amount after extrusion of the
single layer film. Results are shown in Table 2 in collection.
TABLE-US-00002 TABLE 2 Example Example Example Example Example
Example Example 11 12 13 14 15 16 17 Resin Composition Conditions
Composition (parts by mass) Polyolefin (A) 85.9 85.9 85.9 85.9 87.9
85.9 85.9 EVOH (B) 5.5 5.5 5.5 5.5 5.5 5.5 5.5 Conjugated polyene
-- -- 0.0006 0.0006 0.0006 -- 0.0006 compound (H) Lubricant (I) --
0.0011 -- 0.0011 0.0011 0.0011 -- S-EVOH (C) 0.75 0.75 0.75 0.75
0.75 0.75 0.75 EVAc (D) 2 2 2 2 -- 2 2 Pigment (E) 0.3 0.3 0.3 0.3
0.3 0.3 0.3 Metal salt (F) 0.15 0.15 0.15 0.15 0.15 0.15 0.15 of
fatty acid Hydrotalcite (G) 0.075 0.075 0.075 0.075 0.075 0.075
0.075 Adhesive resin 8.6 8.6 8.6 8.6 8.6 8.6 8.6 Antioxidant 0.006
0.006 0.006 0.006 0.006 0.006 0.006 Mass Ratio (B/C) 7.3 7.3 7.3
7.3 7.3 7.3 7.3 (D/C) 2.7 2.7 2.7 2.7 -- 2.7 2.7 (E/C) 0.4 0.4 0.4
0.4 0.4 0.4 0.4 (E/D) 0.15 0.15 0.15 0.15 -- 0.15 0.15 (F/E) 0.5
0.5 0.5 0.5 0.5 0.5 0.5 Type Pigment (E) E-1 E-1 E-1 E-1 E-1 E-2
E-2 Metal salt (F) E-1 F-1 F-1 F-1 F-1 F-1 F-1 of fatty acid
Multilayered Film Evaluation EVOH particle 1.2 1.1 1.2 1.0 1.9 1.0
1.1 diameter (.mu.) Uneven coloration A A A A B A A Whiteness 92.3
92.8 93.1 93.7 91.1 93.3 93.8 Single Layer Film Evaluation White
streaks B B B A B A A YI value 8.5 7.4 6.3 5.5 6.5 4.9 4.6 Screw
adhesion 2.8 1.5 1.7 1.3 1.9 1.2 1.3 degraded material amount (g)
Example Example Example Example Example Example 18 19 20 21 22 23
Resin Composition Conditions Composition (parts by mass) Polyolefin
(A) 85.9 85.9 85.9 85.9 85.9 85.9 EVOH (B) 5.5 5.5 5.5 5.5 5.5 5.5
Conjugated polyene 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006
compound (H) Lubricant (I) 0.0011 0.0011 0.0011 0.0011 0.0011
0.0011 S-EVOH (C) 0.75 0.75 0.75 0.75 0.75 0.75 EVAc (D) 2 2 2 2 2
2 Pigment (E) 0.3 0.3 0.3 0.3 0.3 0.3 Metal salt (F) 0.15 0.15 0.22
0.15 0.15 0.15 of fatty acid Hydrotalcite (G) 0.075 0.075 0.075
0.075 0.075 0.075 Adhesive resin 8.6 8.6 8.6 8.6 8.6 8.6
Antioxidant 0.006 0.006 0.006 0.006 0.006 0.006 Mass Ratio (B/C)
7.3 7.3 7.3 7.3 7.3 7.3 (D/C) 2.7 2.7 2.6 2.7 2.7 2.7 (E/C) 0.4 0.4
0.4 0.4 0.4 0.4 (E/D) 0.15 0.15 0.15 0.15 0.15 0.15 (F/E) 0.5 0.5
0.7 0.5 0.5 0.5 Type Pigment (E) E-2 E-2 E-2 E-3 E-4 E-5 Metal salt
(F) F-1 F-2 F-1/F-2 F-1 F-1 F-1 of fatty acid Multilayered Film
Evaluation EVOH particle 0.9 0.7 0.7 0.8 0.8 0.7 diameter (.mu.)
Uneven coloration A A A A A A Whiteness 94.2 94.7 94.9 95.3 95.4
95.8 Single Layer Film Evaluation White streaks A A A A A A YI
value 4.1 4.4 4.2 3.9 3.8 3.4 Screw adhesion 1.0 0.9 0.8 0.6 0.6
0.4 degraded material amount (g)
* * * * *