U.S. patent application number 13/651015 was filed with the patent office on 2013-02-07 for coated folded medical device.
This patent application is currently assigned to ATRIUM MEDICAL CORPORATION. The applicant listed for this patent is Atrium Medical Corporation. Invention is credited to Trevor Carlton, Joseph Ferraro, Steve A. Herweck, Theodore Karwoski, Roger Labrecque, Paul Martakos, Geoffrey Moodie, Lisa Rogers.
Application Number | 20130035637 13/651015 |
Document ID | / |
Family ID | 37698075 |
Filed Date | 2013-02-07 |
United States Patent
Application |
20130035637 |
Kind Code |
A1 |
Herweck; Steve A. ; et
al. |
February 7, 2013 |
COATED FOLDED MEDICAL DEVICE
Abstract
A non-polymeric or biological coating applied to a radially
expandable interventional medical device in a collapsed, wrapped,
or folded configuration, the coating applied within at least one
fold. Properties of the coating material applied to the medical
device are adjusted or varied to result in a desired combination of
coverage of the surface of the medical device, drug loading, and
coating thickness. The coating is sterile, and is capable of being
carried by a sterile medical device to a targeted tissue location
within the body following radial expansion. The therapeutic coating
transfers off the medical device due in part to a biological
attraction with the tissue and in part to a physical transference
from the medical device to the targeted tissue location in contact
with the medical device.
Inventors: |
Herweck; Steve A.;
(Wellesley, MA) ; Martakos; Paul; (Pelham, NH)
; Moodie; Geoffrey; (Hudson, NH) ; Labrecque;
Roger; (Londonderry, NH) ; Karwoski; Theodore;
(Hollis, NH) ; Carlton; Trevor; (Hudson, NH)
; Rogers; Lisa; (Londonderry, NH) ; Ferraro;
Joseph; (Londonderry, NH) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Atrium Medical Corporation; |
Hudson |
NH |
US |
|
|
Assignee: |
ATRIUM MEDICAL CORPORATION
Hudson
NH
|
Family ID: |
37698075 |
Appl. No.: |
13/651015 |
Filed: |
October 12, 2012 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13102876 |
May 6, 2011 |
8308684 |
|
|
13651015 |
|
|
|
|
11250768 |
Oct 14, 2005 |
8021331 |
|
|
13102876 |
|
|
|
|
10943075 |
Sep 15, 2004 |
|
|
|
11250768 |
|
|
|
|
60503357 |
Sep 15, 2003 |
|
|
|
Current U.S.
Class: |
604/103.02 |
Current CPC
Class: |
A61L 2300/606 20130101;
A61M 2025/1031 20130101; A61F 2250/0067 20130101; A61F 2/82
20130101; B05D 1/00 20130101; A61F 2/958 20130101; A61M 25/1027
20130101; Y10T 29/49 20150115; A61L 29/16 20130101; A61M 25/1038
20130101; A61L 29/08 20130101; B05D 2259/00 20130101 |
Class at
Publication: |
604/103.02 |
International
Class: |
A61M 25/10 20060101
A61M025/10 |
Claims
1. A radially expandable medical device with a coating formed
thereon, comprising: a body having an interior and an exterior
surface; and a coating material applied to at least a portion of
the exterior surface of the body when in a collapsed configuration
including within at least one fold to form a therapeutic coating;
wherein the coating is compositioned to transfer and adhere to a
targeted tissue location.
2. The device of claim 1, wherein the medical device comprises a
balloon.
3. The device of claim 1, wherein the medical device comprises a
balloon catheter or an angioplasty balloon.
4. The device of claim 1, wherein the coating material is a viscous
coating material which substantially covers the surface of the
medical device.
5. The device of claim 1, wherein the coating material is a viscous
coating material which covers only a portion of the surface of the
medical device.
6. The device of claim 1, wherein the coating material has a
viscosity between about 1 cPs and about 1,500 cPs.
7. The device of claim 1, wherein the coating material has a
viscosity between about 10,000 cPs and about 100,000 cPs.
8. The device of claim 1, wherein the coating material has a
viscosity of between about 1 cPs and about 100,000 cPs.
9. The device of claim 1, wherein the coating material further
comprises at least one therapeutic agent.
10. The device of claim 1, wherein the coating material further
comprises at least one therapeutic agent mixed with a solvent.
11. The device of claim 1, wherein the coating is applied to the
medical device subsequent to removal of solvent from the coating
material.
12. The device of claim 1, wherein the coating material further
comprises a solvent subsequent to application to the medical
device, wherein the solvent is removed prior to clinical use.
13. The device of claim 1, wherein the non-polymeric bio-absorbable
component is derived from an oil composition.
14. The device of claim 13, wherein the oil composition comprises a
fatty acid molecule or a glyceride.
15. The device of claim 1, wherein the coating material comprises a
non-polymeric bio-absorbable cross-linked gel component.
Description
RELATED APPLICATIONS
[0001] This application is a continuation of, claims priority to,
and the benefit of, co-pending U.S. patent application Ser. No.
13/102,876, filed May 6, 2011, which is a continuation of U.S.
patent application Ser. No. 11/250,768 (now U.S. Pat. No.
8,021,331), filed Oct. 14, 2005, which is a continuation-in-part
application of co-pending U.S. patent application Ser. No.
10/943,075, filed Sep. 15, 2004, which claims priority to U.S.
Provisional Application No. 60/503,357, filed Sep. 15, 2003, for
all subject matter common to said applications. The benefit of all
of the above-mentioned applications is claimed. Furthermore, the
disclosures of all of the above-mentioned applications are hereby
incorporated by reference herein in their entirety.
FIELD OF THE INVENTION
[0002] The present invention relates to a method of making a coated
medical device, and more particularly to a method of coating a
medical device in a collapsed, or partially collapsed and
potentially folded configuration to control an amount of coating
distribution to the medical device, and subsequent coating
distribution to a targeted tissue location within a patient upon
implantation.
BACKGROUND OF THE INVENTION
[0003] Mechanical drug and agent delivery devices are utilized in a
wide range of applications including a number of biological
applications, such as catheter interventions and other implantable
devices used to create a therapeutic or other biological effect
within the body. Often, such delivery devices take the form of
radially expandable devices used to mechanically open an occluded
or narrowed blood vessel. For example, inflatable non-elastomeric
balloons have been utilized for treatment of body passages occluded
by disease and for maintenance of the proper position of
catheter-delivered medical devices, such as stents, within such
body passages. With the use of drug carrying polymers applied to
the stents to form drug eluting stents, such stents are placed
within body lumens with drugs or agents embedded therein for
release of the drug or agent within the body.
[0004] Some intervention balloon catheters are made to deliver a
systemic bolus of liquid or gas that includes a drug, to a targeted
tissue location within the body using an open catheter lumen or
channel located at some length along the catheter shaft.
Unfortunately, when such systemic delivery means are used to
deliver a controlled volume of medication to a desired tissue
location, a majority of the medication is lost to systemic
circulation because of an inability of the drug to quickly
penetrate local tissue. Generally, most liquid formulations
containing a drug or agent that is delivered to the targeted tissue
location by liquid bolus does not penetrate the tissue sufficiently
at the targeted tissue location to result in a significant
therapeutic effect, and is consequently washed away by body fluids.
This systemic dilution substantially diminishes the effectiveness
of the drugs or agents provided through such delivery devices, and
increases the likelihood of a greater systemic effect caused by the
large quantity of drug or agent washed into the bloodstream. To
compensate for such delivery inefficiency, the dose of drugs or
agents must be volumetrically increased in anticipation that they
will be principally washed away before therapeutically effecting
the localized or targeted tissue area. However, because of the risk
of increased systemic effects and possibly toxic overload, the
volume of the drugs or agents must not exceed that which can still
be considered safe for exposure by systematic dilution and
subsequent systematic distribution throughout the patient's body.
The drug or agent used in such an intervention delivery method must
be safe enough in its diluted state to be washed away to other
parts of the patient's body and not have unwanted therapeutic or
otherwise detrimental effects. There is a delicate balance between
making the drugs or agents sufficiently concentrated to have
therapeutic characteristics at the targeted tissue location, while
also being sufficiently diluted to avoid harmful effects after
being washed away into the body's systemic circulation.
[0005] Alternative to a systemic delivery, a local delivery of
therapeutic agent can be administered. The local delivery can
involve provision of a therapeutic agent using an applicator or as
a portion of a coating on an implanted medical device. With
provision of the drug or agent directly at the desired targeted
tissue location, the systemic effects can be drastically reduced
and the concentration of the drug or agent at the targeted tissue
location can be substantially increased. One method for increasing
the amount of drug at a targeted tissue location is to deliver the
drug in relatively viscous configurations, such that when applied
to the targeted tissue location, the drug or agent is not easily
flushed away due to the adhesion of the viscous configuration to
the tissue.
[0006] In accordance with certain configurations and embodiments
for the local delivery of a therapeutic agent to a targeted tissue
location, a balloon catheter can be utilized to transport a
therapeutic agent, and then apply the therapeutic agent, to the
targeted tissue location. However, in a collapsed or folded
configuration, it can be difficult to evenly distribute the coating
across the outer surface of the balloon, or provide a sufficient
amount of coating on the exposed portions of the balloon surface. A
more viscous coating can have a heavier drug load, but not evenly
coat the collapsed or folded balloon, while a less viscous coating
can penetrate into the folds of the collapsed or folded balloon,
but may not have a high drug concentration.
SUMMARY
[0007] There is a need for a method of coating a medical device,
such as a collapsed, wrapped, or folded catheter balloon, that can
manipulate drug loading and coating viscosity to predictably result
in a desired amount of therapeutic agent or agents applied to a
medical device and correspondingly available for application to a
targeted tissue location. The present invention addresses this
need.
[0008] In accordance with one example embodiment of the present
invention, a method of forming a coating on a medical device
includes providing the medical device having a surface in a
collapsed configuration with at least one fold. A coating material
formulation is determined to achieve a predetermined coverage of
the surface of the medical device and a predetermined thickness of
the coating. The coating material is applied to form the coating on
the medical device. The coating is compositioned to transfer and
adhere to a targeted tissue location.
[0009] In accordance with aspects of the present invention, the
medical device can be a balloon, more specifically a balloon
catheter, or an angioplasty balloon.
[0010] In accordance with further aspects of the present invention,
the step of determining the coating material formulation can
include selecting between a relatively less viscous coating
material for improved coverage of the medical device and a
relatively more viscous coating material for a thicker coating on
the medical device. The step of determining the coating material
formulation can include selecting at least one therapeutic agent
for incorporation into the coating material. The step of
determining the coating material formulation can include mixing at
least one therapeutic agent with a solvent as a portion of the
coating material. The step of determining the coating material
formulation can include selecting a non-polymeric bio-absorbable
component to form a portion of the coating material. The step of
determining the coating material formulation can include selecting
a non-polymeric bio-absorbable cross-linked gel component to form a
portion of the coating material.
[0011] In accordance with further aspects of the present invention,
the step of determining the coating material formulation includes
selecting between a relatively less viscous coating material
between about 1 cPs and about 1,500 cPs for improved coverage of
the medical device and a relatively more viscous coating material
between about 10,000 cPs and about 100,000 cPs for a thicker
coating on the medical device. The coating material formulation can
have a viscosity of between about 1 cPs and about 100,000 cPs.
[0012] In accordance with further aspects of the present invention,
the step of applying the coating material formulation can include
removing solvent from the coating material prior to application to
the medical device. Alternatively, the step of applying the coating
material formulation can include removing solvent from the coating
material subsequent to application to the medical device.
[0013] In accordance with one example embodiment of the present
invention, a radially expandable medical device with a coating
formed thereon includes a body having an interior and an exterior
surface. A therapeutic coating is applied to at least a portion of
the exterior surface of the body when in a collapsed configuration
with at least one fold. The coating is compositioned to transfer
and adhere to a targeted tissue location.
[0014] In accordance with aspects of the present invention, the
coating material formulation can be a relatively less viscous
coating material which substantially covers the surface of the
medical device. Alternatively, the coating material formulation can
be a relatively more viscous coating material which covers only a
portion of the surface of the medical device. The coating material
formulation can include at least one therapeutic agent. The coating
material formulation can include at least one therapeutic agent
mixed with a solvent. The coating material formulation can include
a non-polymeric bio-absorbable component, such as a non-polymeric
bio-absorbable cross-linked gel component.
[0015] In accordance with further aspects of the present invention
determining the coating material formulation has a relatively less
viscous coating material between about 1 cPs and about 1,500 cPs.
Alternatively, the coating material formulation can have a
relatively more viscous coating material between about 10,000 cPs
and about 100,000 cPs. Furthermore, the coating material
formulation can have a viscosity of between about 1 cPs and about
100,000 cPs.
[0016] In accordance with further aspects of the present invention,
the coating material formulation is applied to the medical device
subsequent to removal of solvent from the coating material.
Alternatively, the coating material formulation includes a solvent
subsequent to application to the medical device, wherein the
solvent is removed prior to clinical.
BRIEF DESCRIPTION OF THE DRAWINGS
[0017] The present invention will become better understood with
reference to the following description and accompanying drawings,
wherein:
[0018] FIGS. 1A, 1B, 1C, 1D, 1E, 1F, and 1G are perspective
illustrations of a variety of medical devices according to aspects
of the present invention;
[0019] FIG. 2 is a diagrammatic cross-sectional view of a deflated
radially expandable device, according to one aspect of the present
invention;
[0020] FIG. 3 is a diagrammatic cross-sectional view of the
radially expandable device of FIG. 2 in expanded configuration,
according to one aspect of the present invention;
[0021] FIG. 4 is a diagrammatic illustration of a tightly wrapped
radially expandable device, according to one aspect of the present
invention;
[0022] FIG. 5 is a diagrammatic illustration of a loosely wrapped
radially expandable device, according to one aspect of the present
invention;
[0023] FIG. 6 is a flowchart showing a method of applying a coating
to the device of FIG. 4, according to one aspect of the present
invention; and
[0024] FIG. 7 is a flowchart showing a method of applying a coating
to the device of FIG. 5, according to one aspect of the present
invention.
DETAILED DESCRIPTION
[0025] An illustrative embodiment of the present invention relates
to use of a non-polymeric and/or biological coating that has been
made to deliver a therapeutic agent or drug when applied to
interventional medical devices for uniform drug distribution and
cellular uptake by a targeted treatment area within the body. The
present invention makes use of a sterile non-polymeric coating
capable of being carried by a sterile medical device to a targeted
tissue location within the body following radial expansion. The
therapeutic coating transfers off the medical device without
causing trauma to the local tissue being treated due in part to a
biological attraction and in part to a physical transference from
the medical device to the targeted tissue location in contact with
the medical device. The present invention more particularly relates
to a method of predictably coating the medical device in the
example embodiment wherein the medical device is collapsed,
wrapped, and/or folded, and is conventionally administered to a
targeted tissue location within a patient in a collapsed, wrapped,
and/or folded configuration, which may then be expanded for
application of the coating to the tissue. The type of medical
device to which the therapeutic substance is applied can vary, as
can the method of substance transference of the non-polymeric
coating from the medical device carrier and into the tissue of the
body. In addition, the present invention has application in a
number of different therapeutic blood vessel reperfusion
techniques, including angioplasty, stent deployment, transcatheter
balloon irrigation, angiography, embolic protection procedures, and
catheter interventions.
[0026] FIGS. 1A through 7, wherein like parts are designated by
like reference numerals throughout, illustrate example embodiments
of an application of a therapeutic coating to a medical device for
application to a targeted tissue location within a patient,
according to the present invention. Although the present invention
will be described with reference to the example embodiments
illustrated in the figures, it should be understood that many
alternative forms can embody the present invention. One of ordinary
skill in the art will additionally appreciate different ways to
alter the parameters of the embodiments disclosed in a manner still
in keeping with the spirit and scope of the present invention.
[0027] The phrase "therapeutic drug and/or agent", "therapeutic
coating", and variations thereof, are utilized interchangeably
herein to indicate single drug or multiple therapeutic drugs,
single or multiple therapeutic agents, or any combination of single
or multiple drugs, agents, or bioactive substances. Such drugs or
agents include, but are not limited to, those listed in Table #3
below herein. As such, any subtle variations of the above phrase
should not be interpreted to indicate a different meaning, or to
refer to a different combination of drugs or agents. The present
invention is directed toward improved transference delivery of
therapeutic drugs and/or agents, or any combination thereof, as
understood by one of ordinary skill in the art.
[0028] It has been found, surprisingly, that certain biological
oils and fats with particular levels of viscosity temporarily
adhere sufficiently strong enough to both a temporary and
permanently placed intraluminal medical device so that most of the
biological coating remains on the intraluminal device as it is
inserted into an internal body cavity, passageway, or tissue space
of a patient. Once the medical device is positioned within the body
of the patient, the coating, with the therapeutic agents or
ingredients contained thereto, can be transferred directly into the
targeted tissue by the lypophilic absorptive action of the coating.
The natural attraction and cellular uptake of the oil and fat by
the tissue causes an unexpected benefit for efficient drug
permeation and delivery of the targeted treatment area within the
body. As with any localized drug delivery system, maximizing drug
permeation to the tissue treatment area without incurring high dose
systemic load to the outer surface of the cell membrane is
considered the ideal method of choice. Use of a biological oil or
fat that has been carefully mixed with a drug ingredient has been
found to substantially improve the effective penetration of the
drug ingredient into local tissue by bio-absorption of the oil drug
complex. Because of the biological attraction of the oil and fat
complex is high for many tissues within the body, the oil and fat
complex readily transfers from the medical device chemically
intact, without need for a secondary biochemical reaction or
biological reaction to remove the oil and fat coating from the
medical device. The therapeutic oil and fat complex readily
transfers off the medical device when engaged tightly to a targeted
tissue location with sufficient dwell time to allow the coated
medical device to remain in close contact with the tissue for a
short period of time. Once the coated device becomes adequately
engaged with the targeted treatment zone, the oil and or fat
complex readily transfers off during radial expansion of the
medical device with the therapeutic ingredients intact, directly
onto the contacted tissue with limited systemic effect.
[0029] It has further been found that certain oils and fats can
permeate the tissue of a patient more rapidly than other materials
can penetrate the tissue. More specifically, if a targeted tissue
location within a body cavity requires the application of a
therapeutic agent, the therapeutic agent can be applied to the
targeted tissue location using a variety of different methods. The
permeation of the tissue at the targeted tissue location by the
therapeutic agent can be improved by mixing the therapeutic agent
with a biological oil or fat, which permeates the tissue more
efficiently than most therapeutic agents alone. When a therapeutic
agent has been carefully solubilized, saturated, or mixed without
polymerizing the agents into the oil or fat, such a therapeutic
complex allows the medication to adequately permeate the tissue
cause a therapeutic response to the tissue. By chemically
stabilizing the active ingredients into the oil or fat without
chemical polymerization of the oil, fat and or drug ingredient, the
complex sufficiently delivers a dose of medication or drug directly
into the tissue. Thus, a mixture of an oil or fat and a therapeutic
agent, without any chemical bonds formed between the oil or fat and
the therapeutic agent, allows a medication to be more efficiently
delivered in a form suitable for permeation into the tissue when
engaged within a patient than local medication delivery without the
presence of a non-polymerized oil or fat complex.
[0030] Rather than reliance upon a chemical bond between drug
ingredient and the carrier, selected biological fats and oils allow
the therapeutic agents to solubilize, mix, or be carried intact
within the oil or fat to form an atraumatic therapeutic delivery
complex. The therapeutic agent can further be nano-particlized,
dissolved, emulsified, or otherwise suspended within the oil or
fat, enabling the therapeutic agents to be simultaneously absorbed
by the tissue during the oil and fat absorption by the tissue.
[0031] It has been found experimentally that use of an oil or fat
reduces the likelihood of there being an inflammatory reaction
caused by the introduction of the therapeutic agent to the cells
when exposed to the oil and fat complex. It is known that certain
oils and fats, such as omega 3 fatty acids, are not only well
received by body tissue, but have exhibited their own therapeutic
and bioactive benefits. Such oils and fats reduce the otherwise
common occurrence of an inflammatory reaction caused by the
mechanical contact with the local tissue by the introduction of a
mechanical delivery device, prosthesis, and/or therapeutic agent or
medication. By mixing the therapeutic agent with the oil or fat,
such inflammatory reactions are greatly reduced, thus improving the
outcome of cellular uptake of a medication into the tissue and its
biological effect. Furthermore, the oil or fat delivery system
improves cellular uptake of the therapeutic agent during absorption
of the smeared therapeutic coating.
[0032] Taking into account the ability of the oil or fat to perform
as characterized above, the entire engagement area of targeted
treatment zone can be treated. Example tissues can include a
treatment zone within a blood vessel, a trachea, esophagus,
urethra, or prostate lumen, and/or any engagement tissue location
within the body. The localized treatment involves engaging a
transferable biological oil or fat, combined with an active
therapeutic agent or series of medications, including non-polymeric
substances, which are engaged to a targeted treatment zone within
the body by catheter intervention steps or device deployment
methods used in radial expansion medical device intervention
procedures.
[0033] In accordance with one example embodiment of the present
invention, a medical device 10 is provided for application thereto
of a therapeutic coating. The medical device can be any number of
devices that have application within a patient. For example, as
shown in FIGS. 1A through 1G, the medical device 10 can include a
catheter 12 (such as a Foley catheter, suction catheter, urethral
catheter, perfusion catheter, PTCA catheter, and the like), a stent
14, a radially expandable device 16 (such as a catheter balloon or
a stent), a graft 18, a prosthesis 20, a surgical tool 22, a suture
wire 24, or any other device or tool that makes contact with, or is
proximal to, a targeted tissue location within a body cavity or
body lumen.
[0034] For purposes of the remaining description, a particular
embodiment of the present invention makes use of the radially
expandable device 16 connected to the catheter 12, as utilized in
conjunction with the stent 14, for an angioplasty type of
procedure. However, it should be noted that the present invention
is not limited to the particular system and method as described
herein, but rather has application to a number of different medical
devices 10 as identified above. It should furthermore be noted that
the remaining description focuses on an angioplasty application of
the above medical devices in combination with the therapeutic
coating. One of ordinary skill in the art will appreciate that the
present invention has application to medical devices in general
having a collapsed, wrapped, and/or folded configuration that
requires a coating be applied thereto. The radially expandable
device 16 is merely one implementation of such a medical
device.
[0035] In accordance with one example embodiment of the present
invention, a radially expandable device 16 is constructed of a
generally inelastic, polyester nylon blend material as illustrated
in FIGS. 2 and 3. A catheter 12 and radially expandable device 16
are provided as shown in FIG. 2. The catheter 12 includes a guide
wire 26 for guiding the catheter 12 and radially expandable device
16 to the body lumen. The catheter 12 has a number of openings 28
for providing a fluid to inflate the radially expandable device 16.
FIG. 3 shows the radially expandable device 16 inflated.
[0036] Radially expandable devices in accordance with the present
invention are suitable for a wide range of applications including,
for example, a range of medical treatment applications within the
body. Exemplary biological applications include use as a catheter
balloon for treatment of implanted vascular grafts, stents, a
permanent or temporary prosthesis, or other type of medical
implant, used to treat a targeted tissue within the body, and
treatment of any body cavity, space, or hollow organ passage(s)
such as blood vessels, the urinary tract, the intestinal tract,
nasal cavity, neural sheath, bone cavity, kidney ducts, and those
previously intervened body spaces that have implanted vascular
grafts, stents, prosthesis', or other type of medical implants. The
catheter balloon can be of the type with a catheter passing through
a full length of the balloon, or of the type with a balloon placed
at an end of a catheter. Additional examples include as a device
for the removal of obstructions such as emboli and thrombi from
blood vessels, as a dilation device to restore patency to an
occluded body passage as an occlusion device to selectively deliver
a means to obstruct or fill a passage or space, and as a centering
mechanism for transluminal instruments and catheters. The radially
expandable device 16 can also be used as a sheath for covering
conventional catheter balloons to control the expansion of the
conventional balloon. Furthermore, the radially expandable device
16 can be porous or non-porous, depending on the particular
application.
[0037] The body of the example radially expandable device 16 is
deployable upon application of an expansion force from a first,
reduced diameter configuration, illustrated in FIG. 2, to a second,
increased diameter configuration, illustrated in FIG. 3. The body
of the radially expandable device 16 preferably features a
monolithic construction, i.e., a singular, unitary article of
generally homogeneous material, however the monolithic construction
is not required for implementation of the coating method of the
present invention. The example radially expandable device 16 can
be, for example, manufactured using an extrusion and expansion
process. In addition, the radially expandable device 16 is merely
one example embodiment. Any therapeutic drug or agent delivery
device capable of sustaining a desired elevated pressure as
described below, some of which can deliver a fluid with a
therapeutic drug or agent under pressure to an isolated location,
as understood by one of ordinary skill in the art, can be utilized,
depending on the particular application. As shown, the radially
expandable device 16 is an expandable shape that can be coupled
with a catheter or other structure, potentially able to provide
fluid (in the form of a slurry of nanoparticles, semi-solid, solid,
gel, liquid or gas, if fluid delivery is desired and the device is
porous) to the radially expandable device 16. If the radially
expandable device 16 is not porous, then the catheter can deliver a
fluid (of a number of different types) to inflate the radially
expandable device 16 and maintain a desired pressure. The material
utilized for the radially expandable device 16 can be, for example,
PTFE or PET, among other materials known to those of ordinary skill
in the art, depending on the particular application desired.
[0038] The radially expandable device 16 can be dependably and
predictably expanded to the predefined, fixed maximum diameter and
to the predefined shape independent of the expansion force used to
expand the device.
[0039] The radially expandable device 16 can be generally tubular
in shape when expanded, although other cross-sections, such as
rectangular, oval, elliptical, or polygonal, can be utilized,
depending on a particular application. The cross-section of the
radially expandable device 16 can be continuous and uniform along
the length of the body. However, in alternative embodiments, the
cross-section can vary in size and/or shape along the length of the
body. FIG. 2 illustrates the radially expandable device 16 relaxed
in the first, reduced diameter configuration. The radially
expandable device 16 has a central lumen extending along a
longitudinal axis between two ends of the device.
[0040] A deployment mechanism in the form of an elongated hollow
tube, such as the catheter 12, is shown positioned within the
central lumen of the radially expandable device 16 to provide a
radial deployment or expansion force to the radially expandable
device 16. The radial deployment force effects radial expansion of
the radially expandable device 16 from the first configuration to
the second increased diameter configuration illustrated in FIG. 3.
The radially expandable device 16 can be formed by thermal or
adhesive bonding, or attached by other means suitable for
inhibiting fluid leakage where unwanted.
[0041] The catheter 12 includes an internal, longitudinal extending
lumen and a number of openings 28 that provide for fluid
communication between the exterior of the catheter 12 and the
lumen. The catheter 12 can be coupled to a fluid source or sources
to selectively provide fluid to the radially expandable device 16
through the openings 28.
[0042] The pressure from the fluid provides a radially expandable
force on the body 12 to radially expand the body 12 to the second,
increased diameter configuration. Because the body 12 is
constructed from an inelastic material, uncoupling the tube 20 from
the fluid source or otherwise substantially reducing the fluid
pressure within the lumen 13 of the body 12, does not generally
result in the body 12 returning to the first, reduced diameter
configuration. However, the body 12 will collapse under its own
weight to a reduced diameter. Application of negative pressure,
from, for example, a vacuum source, can be used to completely
deflate the body 12 to the initial reduced diameter
configuration.
[0043] One skilled in the art will appreciate that the radially
expandable device 16 is not limited to use with deployment
mechanisms employing a fluid deployment force, such as the catheter
12. Other known deployment mechanisms can be used to radially
deploy the radially expandable device 16 including, for example,
mechanical operated expansion elements, such as mechanically
activated members or mechanical elements constructed from
temperature activated materials such as nitinol.
[0044] Various fluoropolymer materials are additionally suitable
for use in the present invention. Suitable fluoropolymer materials
include, for example, polytetrafluoroethylene ("PTFE") or
copolymers of tetrafluoroethylene with other monomers may be used.
Such monomers include ethylene, chlorotrifluoroethylene,
perfluoroalkoxytetrafluoroethylene, or fluorinated propylenes such
as hexafluoropropylene. PTFE is utilized most often. Accordingly,
while the radially expandable device 16 can be manufactured from
various fluoropolymer materials, and the manufacturing methods of
the present invention can utilize various fluoropolymer materials,
the description set forth herein refers specifically to PTFE. In
addition, PET or polyester nylon blend can be utilized, depending
on the desired material properties.
[0045] Turning now to an example application of the radially
expandable device 16, a description of an angioplasty will be
described. In general, an angioplasty procedure is a procedure used
to widen vessels narrowed by stenosis, restenosis, or occlusions.
There are a number of different types of angioplasty procedures. In
individuals with an occlusive vascular disease such as
atherosclerosis, blood flow is impaired to an organ, such as the
heart, or to a distal body part, such as an arm or leg, by the
narrowing of the vessel's lumen due proliferation of a certain
luminal cell type that has been impaired by vulnerable plaques,
fatty deposits or calcium accumulation. The angioplasty procedure
is a mechanical radial expansion procedure performed to radially
open or widen the cross-sectional area of the vessel. Once the
reperfusion procedure is completed, a desired blood flow returns
within the mechanically opened area.
[0046] Over time, the vessel may constrict again, e.g., cellular
proliferation called restenosis. The angioplasty procedure can be
performed to re-open the vessel to a larger cross-sectional area.
To prevent recoil or help control the occurrence or rate of
restenosis, a stent can be implanted in the vessel. The stent is
typically in the form of a radially expandable porous metal mesh
tube, which following expansion forms a supporting scaffolding
structure. As with any non-biological or foreign object or material
in the body, like a stent or polymer coating, the risk of both
acute and chronic inflammation and thrombosis is increased.
Inflammation is due in part to the acute natural foreign body
reaction. Inflammation caused by foreign body response is a primary
reason why patients receive systemic medication, including,
anti-inflammation, anti-proliferation, and anti-clotting
medications before, during, and after interventional procedures,
including stent implantations. However, such medications are not
delivered specifically at the location of the injury to the vessel
at the time of reperfusion injury or radial stent deployment into
the vessel wall.
[0047] Generally, the implantation of a stent follows an
angioplasty, but this is not always a requirement. For many
patients, a direct stenting technique may be preferred to speed the
reperfusion of the vessel, and to improve the delivery of the
implant with a one step technique. In either instance, the stent is
positioned in the vessel at the targeted tissue location by use of
a deflated radially expandable balloon catheter. The radially
expandable catheter device is inflated, expanding the stent against
the vessel walls. The radially expandable catheter device is
removed, leaving the stent in place in an expanded condition to
mechanically hold the vessel open. Occasionally, another radially
expandable balloon catheter device is inserted either entirely or
partially into the previously stented vessel at the location of the
stent and inflated to ensure the stent is properly expanded
throughout so as to not migrate or move along the vessel wall, and
to insure no gaps occur under the expanded stent, which are sources
for excessive clot formation when not fully expanded.
[0048] In addition to the radially expandable device 16, FIG. 3
shows a therapeutic coating 30 applied to the radially expandable
device 16. The therapeutic coating is applied to the medical device
10, in this case the radially expandable device 16, to create a
therapeutic effect on the tissue at the targeted tissue location in
a patient. The inclusion of the therapeutic coating 30 creates the
opportunity to provide a medical or therapeutic effect for tissue
that makes contact with the medical device 10. The therapeutic
effect can be varied by the particular therapeutic agent
incorporated into the therapeutic coating 30. The therapeutic
coating 30 is made to coat the medical device 10 in a manner such
that an efficacious amount of the therapeutic coating 30 does not
wash away with bodily fluid passing by the medical device 10. The
therapeutic coating 30 additionally will transfer from the medical
device 10 to the targeted tissue location of the patient upon
substantive contact between tissue and the medical device 10, and
remain at or on the targeted tissue location to penetrate the
tissue. The therapeutic coating can be applied to the radially
expandable device 16, e.g., at a manufacturing stage, or just prior
to insertion of the radially expandable device 16 into the body
lumen.
[0049] As applied to the example angioplasty procedure, the present
invention provides for an effective and efficient therapeutic agent
or drug delivery, with more effective surface area coverage of the
targeted tissue relative to known interventional drug eluting or
systemic delivery procedures. The radially expandable devices
expand from a first smaller diameter to a second larger diameter
with a non-polymeric transferable therapeutic coating. Use of a
therapeutic coating, agent, or biological material further aids in
the transfer and tissue adhesion property of the material being
applied directly onto and into the targeted treatment site during
radial expansion of either the first intervention or second
intervention, within or at least partially within the same targeted
treatment sites.
[0050] The therapeutic coating 30 can be applied to the medical
device 10 utilizing a number of different processes. In addition,
the therapeutic coating can be sterilized prior to packaging, or
prior to clinical use. The entire sterile medical device 10, or a
portion thereof, can be submerged into a container containing the
sterile therapeutic coating. The sterile medical device 10 can be
rolled in a sterile tray containing the therapeutic coating.
Additional methods of applying the therapeutic coating to the
medical device can involve heating, or drying, or combinations
thereof. One of ordinary skill in the art will appreciate that the
invention is not limited by the particular method of preparing the
sterile medical device 10 with the sterile therapeutic coating 30.
Instead, any number of different methods can be utilized to result
with the therapeutic coating 30 applied to the medical device 10 in
a manner that promotes transfer of the therapeutic coating 30 to a
targeted tissue location within a patient upon intervention by the
medical device 10.
[0051] For example in accordance with the present invention, the
therapeutic coating 30 can be applied with different relative
viscosities, different drug (therapeutic agent) loadings, and
applied to tightly wrapped or loosely wrapped radially expandable
devices, all in different permutations, to result in the
therapeutic coating 30 on the medical device 10.
[0052] The present invention can make use of a number of different
therapeutic coatings 30 to coat the medical device 10. For purposes
of illustration, a bio-absorbable cross-linked gel formulation. It
should be noted that the term cross-linked gel, as utilized herein,
refers to a gel that is non-polymeric and is derived from an oil
composition comprising molecules covalently cross-linked into a
three-dimensional network by one or more of ester, ether, peroxide,
and carbon-carbon bonds in a substantially random configuration. In
various exemplar embodiments, the oil composition comprises a fatty
acid molecule, a glyceride, and combinations thereof.
[0053] The therapeutic coating 30 can provide a drug load or
therapeutic agent load on the surface of the medical device 10. In
the instance of the radially expandable device, such as a balloon
attached to a catheter, the device can be placed at the targeted
tissue location for delivery of the therapeutic agent via release
off the coated balloon into the tissue. The efficiency of delivery
is dependent upon the kinetics of transfer from the balloon into
the targeted tissue location. The formulation of the therapeutic
coating can be modified to impact the kinetics of transfer and as a
result change the amount of drug or therapeutic agent uptake into
the tissue.
[0054] Coating methodologies can initially involve the use of a
solvent, which serves to dissolve or solvate the therapeutic agent
into the coating formulation for subsequent application to medical
devices. The solvent is completely removed prior to packaging the
final coated product. The solvent can be removed from the coating
material either before or after application of the coating material
to the medical device. If the solvent is removed prior to coating
the medical device, a relatively thicker therapeutic coating 30
results. A thicker and more viscous therapeutic coating 30 on the
medical device 10 subsequently provides a relatively slower
transference from the medical device to the targeted tissue
location. Alternatively, coating methodologies that include leaving
the solvent in the coating material for application to the medical
device can be performed. If the solvent remains in the coating
material and when first applied as the therapeutic coating 30, a
relatively thinner and less viscous therapeutic coating 30 results.
A thinner and less viscous therapeutic coating 30 on the medical
device 10 subsequently provides a relatively faster transference
from the medical device to the targeted tissue location.
[0055] As used herein, the term "viscosity" refers to the
resistance of a fluid to shear or flow, and is a measure of the
fluids adhesive/cohesive or frictional properties. This resistance
is caused by intermolecular friction exerted when layers of fluids
attempts to slide by an other. One of ordinary skill in the art
would be readily able to measure the viscosity of the coating
formulation by using, for example, a viscometer. The phrases "high
viscosity" or "higher viscosity" refer to an increase in the
resistance of a fluid to shear or flow, as compared to a reference
fluid of "low viscosity" or "lower viscosity". The reference fluid,
for purposes of this description, is intended as a fluid of similar
viscosity to an oil-based material, such as fish oil, that has not
been modified with additives, drugs, thickeners, or cured to any
substantial degree to form or increase amounts of cross-links
within the oil.
[0056] The units of viscosity can be centipoises (cP), centistokes
(cSt), Saybolt Universal Seconds (SSU), Pascal seconds (Pa-s) and
degrees Engler. In one embodiment, the oil-based reference fluid
has a viscosity measurement from about 15 cPs to about 100,000 cPs.
Accordingly, the low viscosity, or lower viscosity, coating
formulation can have a viscosity of about 1 cPs (similar viscosity
to that of water), of about 15 cPs (similar viscosity to that of
glycol), of about 28 cPs (similar viscosity to that of linseed
oil), of about 90 cPs (similar viscosity to that of olive oil), of
about 180 cPs (similar viscosity to that of motor oil), of about
700 cPs (similar viscosity to that of heavy machine oil), of about
1,000 cPs (similar viscosity to that of SAE 50 motor oil), of about
1,500 cPs (similar viscosity to that of glycerin at 20.degree. F.),
or an amount generally proximal to, or equivalent to, such
viscosity measurements. Likewise, the high viscosity, or higher
viscosity, coating formulation can have a viscosity of about 10,000
cPs (similar viscosity to that of molasses), of about 20,000 cPs
(similar viscosity to that of chocolate syrup), of about 28,000
cPs, of about 50,000 cPs (similar viscosity to that of ketchup), of
about 100,000 cPs (similar viscosity to that of ketchup at
25.degree. C.), or an amount generally proximal to, or equivalent
to, such viscosity measurements. It should be noted that the
present invention is by no means limited to the specific viscosity
ranges described herein. One of ordinary skill in the art will
appreciate that the present invention is directed to a method that
takes into consideration relative viscosities of coating
formulations and their corresponding ability to coat a medical
device with varying degrees of surface coverage. The above
viscosity measurements are intended to provide some general
indication of the type of viscosities that can be utilized to form
the coating formulations, and subsequent coatings. However, any
coating formulation that can be applied to a medical device,
including coating formulations that fall outside of the example
ranges, fall within the scope of the present invention in that
determinations of relative viscosities of the coating formulations
are utilized in creating the coated medical device.
[0057] One additional, but related, factor that influences the
ability of the coating material to coat the medical device 10 to
form the therapeutic coating 30, especially in the instance of the
radially expandable device 16, or a balloon catheter device, is the
degree to which the device is tightly folded or collapsed against
itself. FIG. 4 shows a catheter balloon 300, such as an angioplasty
type balloon, that is tightly wrapped as is commonly provided by
catheter balloon manufacturers. The catheter balloon 300 includes
the catheter 304 portion and the balloon 302 portion. The balloon
302 can be of the type used in conjunction with stents, or with a
stent crimped thereon, as understood by one of ordinary skill in
the art. The balloon 302 is tightly wrapped upon itself and the
catheter 304, as evidenced by the minimal clearance 306 between
flaps or folds of the balloon 302. In contrast, FIG. 5 shows the
same catheter balloon 300 that has been unwrapped and more loosely
re-wrapped together. The catheter balloon 300 includes the catheter
304 portion and the balloon 302 portion. The balloon 302 is more
loosely wrapped upon itself and the catheter 304, as evidenced by
the relatively greater clearances 308 between flaps or folds of the
balloon 302 as compared with the catheter balloon 300 as
illustrated in FIG. 4. Said differently, and with reference to
Table #1 below, the tightly wrapped configuration, in accordance
with one example embodiment of the present invention, has a
measured outer diameter of about 0.037 inches. When the tightly
wrapped configuration is unwrapped and then re-wrapped in a more
loosely wrapped configuration, the measured outer diameter is on
the order of about 0.041 inches.
[0058] Accordingly, as utilized herein, the terms "tightly wrapped"
and "loosely wrapped" are intended as being relative to one
another. The relative difference between a tightly wrapped balloon
and a loosely wrapped balloon is evidenced by the example
embodiment, and characterized by an example outer diameter
measurement difference of about 0.004 inches on a 0.037 inch outer
diameter tightly wrapped balloon (or about a 10% increase in the
outer diameter). The example 10% increase is embodied in the
increase in dimension of the greater clearance 308 relative to the
minimal clearance 306. One of ordinary skill in the art will
appreciate that the present invention is not limited to the
specific diameter measurements described herein, or the relative
percentage change in diameter measurements as an expression of
tightly wrapped versus loosely wrapped. Rather, the example
diameter measurements are merely intended to provide additional
detail with regard to approximate scale of the relative
relationship between a tightly wrapped balloon versus a loosely
wrapped balloon.
[0059] For manufacturing, it is desirable to be able to load the
therapeutic coating 30 onto the medical device 10 (for example, the
catheter balloon 300) either tightly wrapped as shown in FIG. 4, or
loosely wrapped as shown in FIG. 5, instead of requiring the
balloon 302 be inflated for application of the coating. As
understood by one of ordinary skill in the art, a fewer number of
steps involved in manufacturing processes results in a more
efficient manufacturing process.
[0060] In accordance with the present invention, methods are
provided for coating the catheter balloon 300 (or other medical
device) in one of the two folded configurations, without requiring
partial or complete inflation of the balloon for application of the
coating. A relatively less viscous coating material formulation in
accordance with the present invention is more effective at
completely covering and coating the surface of the balloon 302 that
is tightly wrapped with minimal clearances 306 relative to a
coating material of greater viscosity, because the coating material
can gain better access to all of the folded surfaces through the
minimal clearances 306. A more viscous, coating formulation does
not achieve good access to all of the folded surfaces through the
minimal clearances 306. However, the more viscous coating
formulation results in a thicker therapeutic coating 30, and
therefore a greater quantity of coating material per area covered,
and a greater overall therapeutic agent or drug loading. The
balloon 302 itself can be modified by being unfolded and re-folded
in a looser manner, creating the greater clearances 308 between
flaps or folds. In such a configuration, a less viscous coating
material can again gain access to all of the folded surfaces
through the greater clearances 308. In addition, the more viscous
coating formulation can also gain better access to the folded
surfaces through the greater clearances 308 relative to the access
through the minimal clearances 306 of the tightly wrapped
configuration. Variations in drug or therapeutic agent loading,
coating material viscosity, and tightness of wrapping can influence
the eventual coverage of the coating and thickness of the coating,
and therefore the overall amount of coating and therapeutic agent
or drug loaded on the balloon 302.
[0061] FIG. 6 is a flowchart illustrating one method of coating a
medical device, such as a balloon 302 of a balloon catheter 300, in
accordance with the present invention. The catheter balloon is
provided (step 320). In a first embodiment, the catheter balloon
302 is tightly wrapped, as conventionally provided by manufacturers
and similar to the embodiment of FIG. 4. A determination is made as
to what formulation of coating material to apply (relatively low
viscosity or relatively high viscosity) considering such factors as
degree of coverage desired on the balloon surface, total amount of
coating material desired on the balloon, thickness of resulting
coating desired, amount of drug or therapeutic agent loading on the
balloon and in the coating, and the like (step 322). The coating
material is applied to the medical device (step 324) to result in
the therapeutic coating. If there is any solvent remaining in the
coating, the solvent is removed, such as by vacuum or heat (step
326).
[0062] FIG. 7 is a flowchart illustrating one method of coating a
medical device, such as a balloon 302 of a balloon catheter 300, in
accordance with the present invention. The catheter balloon is
provided (step 330). In a second embodiment, the catheter balloon
302 is loosely wrapped, similar to the embodiment of FIG. 5. A
determination is made as to what formulation of coating material to
apply (lower viscosity formulation or higher viscosity formulation)
considering such factors as degree of coverage desired on the
balloon surface, total amount of coating material desired on the
balloon, thickness of resulting coating desired, amount of drug or
therapeutic agent loading on the balloon and in the coating, and
the like (step 332). The coating material is applied to the medical
device (step 334) to result in the therapeutic coating. If there is
any solvent remaining in the coating, the solvent is removed, such
as by vacuum or heat (step 336).
[0063] To demonstrate the application of the methods of the present
invention, several example implementations were performed using
rapamycin as the drug or therapeutic agent loaded into a coating
carrier component of vitamin E and fish oil. Both relatively higher
viscosity and relatively lower viscosity implementations were
performed to highlight the ability to control the coating
parameters as described herein.
[0064] Specifically, viscosity variations of the same coating
materials were utilized in the example implementations. Rapamycin
was mixed together with a mixture of 70% vitamin E and 30% Epax
3000TG Fish oil. The rapamycin, dissolved in nMp solvent, was mixed
together with the vitamin E/fish oil mixture at a ratio of 50:50.
Once the solvent was removed, the final drug concentration in the
therapeutic coating was about 32%.
[0065] As described previously, the difference between a relatively
higher viscosity coating formulation and a relatively lower
viscosity coating formulation relates to when the solvent is
removed in the process. For the low viscosity formulation, the nMp
was removed after coating the balloon. For the high viscosity
formulation, the nMp was removed prior to coating the balloon. The
coating was applied to 4.0 mm.times.10 mm balloons. Table #1,
below, illustrates the amount of drug (rapamycin) loaded onto the
balloons using both the low viscosity and high viscosity coating
formulations.
TABLE-US-00001 TABLE #1 High Low Viscosity Viscosity Normalized
using Wrapping Coating Coating drug/mm.sup.2 Configuration
Formulation Formulation Low visc./High visc. Pre-Wrapped 723 .mu.g
of drug 980 .mu.g 4.7/6.4 (a 0.037'' of drug profile) Loosely
Wrapped 949 .mu.g of drug 1095 .mu.g of 6.2/7.1 (to a 0.041'' drug
profile)
[0066] After demonstrating the results of the above Table #1, a
further illustrative implementation demonstrated the ability of the
drug to transfer from the coated balloon catheter using the same
formulations implanted in pig vessels.
[0067] Specifically, 3.0 mm.times.10 mm balloons were coated with
the low viscosity and high viscosity formulations of Table #1,
prepared with two drug variations, namely, with rapamycin and with
paclitaxel. The balloons were expanded in pig carotid arteries for
60 seconds. The vessels were then attached to a flow system and
flushed with 1 liter of Krebs-Henseleit buffer to remove any loose
coating. Fresh buffer solution was then re-circulated through the
vessels for one hour at physiologically normal temperature and
pressure. The vessels were then removed from the system and drug
uptake into the tissue was determined using HPLC analysis. Table
#2, below, shows the average uptake into the vessel segments for
each drug type and low viscosity or high viscosity coating
formulation.
TABLE-US-00002 TABLE #2 Coating Formulation Rapamycin Paclitaxel
Low Viscosity Formulation 3.26 .mu.g/segment 4.26 .mu.g/segment
High Viscosity Formulation 1.76 .mu.g/segment 3.48
.mu.g/segment
[0068] As evidenced in the described illustrative implementations,
the efficiency of drug transfer into the tissue can be varied
according to the coating process. Despite the ability to provide a
thicker coating using the higher viscosity formulation, the lower
viscosity formulation can be formulated to provide a higher drug
uptake into the tissue. The interplay of each of the
above-mentioned variables results in the desired drug loading and
ultimately in the amount of drug uptake into the tissue. A thin
coating carries less drug quantity, but has better coverage of the
balloon surface, relative to the thick coating on a tightly folded
or loosely folded balloon. The thick coating carries a higher drug
loading, but has a lesser amount of coverage of the balloon surface
when applied to a tightly folded balloon. However, as the above
results illustrate, the lower drug loading in the thin coating can
actually result in a higher drug uptake by the tissue, which is in
part due to the improved surface coverage of the balloon by the
coating.
[0069] The therapeutic coating 30 can be formed of a number of
different agents and compositions. The therapeutic coating can be a
non-polymeric, biologically compatible coating. The coating can be
formed entirely of a single substance, or can be formed using a
mixture, aggregate, compilation, composition, and the like, of two
or more substances, including one or more different therapeutic
agent nano-particles, one or more of which can be a therapeutic
agent having therapeutic properties, and/or biological effects to
the targeted tissue location.
[0070] In accordance with one example embodiment, the therapeutic
coating can be formed of a non-polymeric, biologically compatible,
oil or fat, such as the non-polymeric bio-absorbable cross-linked
gel derived at least in part from a fatty acid. There are a number
of different therapeutic agents that are either lipophilic, or do
not have a substantial aversion to oils or fats. Such therapeutic
agents can be mixed with the oil or fat, without forming a chemical
bond, and delivered to a targeted tissue location within a patient
in accordance with the teachings of the present invention. The
therapeutic agent component can take a number of different forms
including anti-oxidants, anti-inflammatory agents, anti-coagulant
agents, drugs to alter lipid metabolism, anti-proliferatives,
anti-neoplastics, tissue growth stimulants, functional
protein/factor delivery agents, anti-infective agents, anti-imaging
agents, anesthetic agents, therapeutic agents, tissue absorption
enhancers, anti-adhesion agents, germicides, anti-septics,
analgesics, prodrugs, and any additional desired therapeutic agents
such as those listed in Table #3 below.
TABLE-US-00003 TABLE #3 CLASS EXAMPLES Antioxidants
Alpha-tocopherol, lazaroid, probucol, phenolic antioxidant,
resveretrol, AGI-1067, vitamin E Antihypertensive Agents Diltiazem,
nifedipine, verapamil Antiinflammatory Agents Glucocorticoids (e.g.
dexamethazone, methylprednisolone), leflunomide, NSAIDS, ibuprofen,
acetaminophen, hydrocortizone acetate, hydrocortizone sodium
phosphate, macrophage-targeted bisphosphonates Growth Factor
Angiopeptin, trapidil, suramin Antagonists Antiplatelet Agents
Aspirin, dipyridamole, ticlopidine, clopidogrel, GP IIb/IIIa
inhibitors, abcximab Anticoagulant Agents Bivalirudin, heparin (low
molecular weight and unfractionated), wafarin, hirudin, enoxaparin,
citrate Thrombolytic Agents Alteplase, reteplase, streptase,
urokinase, TPA, citrate Drugs to Alter Lipid Fluvastatin,
colestipol, lovastatin, atorvastatin, amlopidine Metabolism (e.g.
statins) ACE Inhibitors Elanapril, fosinopril, cilazapril
Antihypertensive Agents Prazosin, doxazosin Antiproliferatives and
Cyclosporine, cochicine, mitomycin C, sirolimus Antineoplastics
micophenonolic acid, rapamycin, everolimus, tacrolimus, paclitaxel,
QP-2, actinomycin, estradiols, dexamethasone, methatrexate,
cilostazol, prednisone, cyclosporine, doxorubicin, ranpirnas,
troglitzon, valsarten, pemirolast, C- MYC antisense, angiopeptin,
vincristine, PCNA ribozyme, 2-chloro-deoxyadenosine Tissue growth
stimulants Bone morphogeneic protein, fibroblast growth factor
Promotion of hollow Alcohol, surgical sealant polymers, polyvinyl
particles, 2- organ occlusion or octyl cyanoacrylate, hydrogels,
collagen, liposomes thrombosis Functional Protein/Factor Insulin,
human growth hormone, estradiols, nitric oxide, delivery
endothelial progenitor cell antibodies Second messenger Protein
kinase inhibitors targeting Angiogenic Angiopoetin, VEGF
Anti-Angiogenic Endostatin Inhibitation of Protein Halofuginone,
prolyl hydroxylase inhibitors, C-proteinase Synthesis/ECM formation
inhibitors Antiinfective Agents Penicillin, gentamycin, adriamycin,
cefazolin, amikacin, ceftazidime, tobramycin, levofloxacin, silver,
copper, hydroxyapatite, vancomycin, ciprofloxacin, rifampin,
mupirocin, RIP, kanamycin, brominated furonone, algae byproducts,
bacitracin, oxacillin, nafcillin, floxacillin, clindamycin,
cephradin, neomycin, methicillin, oxytetracycline hydrochloride,
Selenium. Gene Delivery Genes for nitric oxide synthase, human
growth hormone, antisense oligonucleotides Local Tissue perfusion
Alcohol, H2O, saline, fish oils, vegetable oils, liposomes Nitric
oxide Donor NCX 4016--nitric oxide donor derivative of aspirin,
Derivatives SNAP Gases Nitric oxide, compound solutions Imaging
Agents Halogenated xanthenes, diatrizoate meglumine, diatrizoate
sodium Anesthetic Agents Lidocaine, benzocaine Descaling Agents
Nitric acid, acetic acid, hypochlorite Anti-Fibrotic Agents
Interferon gamma-1b, Interluekin-10
Immunosuppressive/Immunomodulatory Cyclosporine, rapamycin,
mycophenolate motefil, Agents leflunomide, tacrolimus, tranilast,
interferon gamma-1b, mizoribine Chemotherapeutic Agents
Doxorubicin, paclitaxel, tacrolimus, sirolimus, fludarabine,
ranpirnase Tissue Absorption Fish oil, squid oil, omega 3 fatty
acids, vegetable oils, Enhancers lipophilic and hydrophilic
solutions suitable for enhancing medication tissue absorption,
distribution and permeation Anti-Adhesion Agents Hyaluronic acid,
human plasma derived surgical sealants, and agents comprised of
hyaluronate and carboxymethylcellulose that are combined with
dimethylaminopropyl, ehtylcarbodimide, hydrochloride, PLA, PLGA
Ribonucleases Ranpirnase Germicides Betadine, iodine, sliver
nitrate, furan derivatives, nitrofurazone, benzalkonium chloride,
benzoic acid, salicylic acid, hypochlorites, peroxides,
thiosulfates, salicylanilide Antiseptics Selenium Analgesics
Bupivicaine, naproxen, ibuprofen, acetylsalicylic acid
[0071] Some specific examples of therapeutic agents useful in the
anti-restenosis realm include cerivastatin, cilostazol,
fluvastatin, lovastatin, paclitaxel, pravastatin, rapamycin, a
rapamycin carbohydrate derivative (for example, as described in US
Patent Application Publication 2004/0235762), a rapamycin
derivative (for example, as described in U.S. Pat. No. 6,200,985),
everolimus, seco-rapamycin, seco-everolimus, and simvastatin. With
systemic administration, the therapeutic agent is administered
orally or intravenously to be systemically processed by the
patient. However, there are drawbacks to a systemic delivery of a
therapeutic agent, one of which is that the therapeutic agent
travels to all portions of the patient's body and can have
undesired effects at areas not targeted for treatment by the
therapeutic agent. Furthermore, large doses of the therapeutic
agent only amplify the undesired effects at non-target areas. As a
result, the amount of therapeutic agent that results in application
to a specific targeted location in a patient may have to be reduced
when administered systemically to reduce complications from
toxicity resulting from a higher dosage of the therapeutic
agent.
[0072] Accordingly, an alternative to the systemic administration
of a therapeutic agent is the use of a targeted local therapeutic
agent delivery approach. With local delivery of a therapeutic
agent, the therapeutic agent is administered using a medical device
or apparatus, directly by hand, or sprayed on the tissue, at a
selected targeted tissue location of the patient that requires
treatment. The therapeutic agent emits, or is otherwise delivered,
from the medical device apparatus, and/or carrier, and is applied
to the targeted tissue location. The local delivery of a
therapeutic agent enables a more concentrated and higher quantity
of therapeutic agent to be delivered directly at the targeted
tissue location, without having broader systemic side effects. With
local delivery, the therapeutic agent that escapes the targeted
tissue location dilutes as it travels to the remainder of the
patient's body, substantially reducing or eliminating systemic side
effects.
[0073] The act of mixing the therapeutic agent with the oil or fat
results in a therapeutic mixture for application to the medical
device 10 as a therapeutic coating. The therapeutic mixture can
stick sufficiently well enough to the medical device, such as a
delivery device or prosthesis, to transfer the therapeutic coating
to a targeted tissue location within a patient following radial
expansion of the device. An improved permeability of the tissue at
the targeted tissue location by the oil or fat results in improved
permeation by the therapeutic agent as well. In addition, a natural
lipophilic tissue adherence characteristic of the oil or fat
reduces the likelihood that most of the therapeutic mixture will be
washed away by passing body fluids following placement of the
device at the targeted tissue location. Therefore, the therapeutic
mixture is held in place along the treatment area of the targeted
tissue location, improving the permeation potential of the tissue
by the mixture, and thus improving the therapeutic effect to the
targeted treatment area within the body.
[0074] There are several oils and fats that are appropriate for use
with the present invention. One fatty acid found to perform well
was an omega 3 fatty acid, such as fish oil. Another component of
the oils and fats found to function well with the present invention
is alfa-tocopherol. There are a plurality of additional oils and
fats and other components, some of which are listed in Table #4
below.
TABLE-US-00004 TABLE #4 Fish Oil Cod-liver Oil Squid Oil Olive Oil
Linseed Oil Sunflower Oil Corn Oil Palm/Palmnut Oil Flax Seed
Oil
[0075] In addition, and as previously mentioned, the mixture of
therapeutic agent and oil or fat can include other components such
as a solvent. The solvent serves to control or adjust the viscosity
of the mixture. Other components can be added to stabilize the
therapeutic mixture or affect other characteristics of the mixture.
Furthermore, the mixture itself can be modified, such as through
hydrogenation.
[0076] The present invention relates to a plurality of combinations
involving some form of therapeutic application of a therapeutic
coating onto and into the targeted tissue location during use of a
medical device supporting the therapeutic coating. Such
combinations can include implantation procedures, such as a radial
stent deployment procedure, to the same area location (within or
partially within the same treatment location). The technique and
device technology allows a multiple application step means to
deliver more coating, medicated or therapeutic agent, or
biological, over a larger surface area than can be applied solely
by a single catheter step means, or by a single step means using
solely a drug eluting stent means. Typically, a drug eluting stent
has a surface area equal to no more than 20% of the vessel wall,
and therefore cannot deliver a coating, medicated agent, or
biological to more than 20% of the targeted tissue site. The method
of the present invention provides a means to deliver more
therapeutics over a larger treatment area. In addition, the use of
the porous radially expandable device enables additional control
over the amount of therapeutic coating delivered to the targeted
tissue location, increasing the therapeutic effect of the
coating.
[0077] Numerous modifications and alternative embodiments of the
present invention will be apparent to those skilled in the art in
view of the foregoing description. Accordingly, this description is
to be construed as illustrative only and is for the purpose of
teaching those skilled in the art the best mode for carrying out
the present invention. Details of the structure may vary
substantially without departing from the spirit of the invention,
and exclusive use of all modifications that come within the scope
of the disclosed invention is reserved.
* * * * *