U.S. patent application number 13/620203 was filed with the patent office on 2013-01-10 for structure of solid oxide fuel cell.
This patent application is currently assigned to SAMSUNG ELECTRO-MECHANICS CO., LTD.. Invention is credited to Jae Hyoung GIL, Jae Hyuk JANG, Sung Han KIM, Eon Soo LEE, Kyong Bok MIN.
Application Number | 20130011767 13/620203 |
Document ID | / |
Family ID | 43625425 |
Filed Date | 2013-01-10 |
United States Patent
Application |
20130011767 |
Kind Code |
A1 |
GIL; Jae Hyoung ; et
al. |
January 10, 2013 |
STRUCTURE OF SOLID OXIDE FUEL CELL
Abstract
Disclosed is a structure of a solid oxide fuel cell, including a
porous tubular anode support having a plurality of through holes,
and an electrolyte layer and a cathode layer sequentially formed on
the inner surface of the tubular anode support, so that fuel flows
via the plurality of through holes and air flows through the inside
of the cathode layer, thus increasing a diffusion rate of fuel and
air to thereby increase the reaction rate, resulting in excellent
cell performance. This structure eliminates the flow of fuel and
air around the outside of the fuel cell, thus preventing the
formation of an oxidizing atmosphere at the inside and outside of
the tubular cell, thereby increasing lifespan of the cell and
ensuring cell reliability.
Inventors: |
GIL; Jae Hyoung; (Seoul,
KR) ; JANG; Jae Hyuk; (Seongnam-si, KR) ; MIN;
Kyong Bok; (Suwon, KR) ; KIM; Sung Han;
(Seoul, KR) ; LEE; Eon Soo; (Gyeongsangbuk-do,
KR) |
Assignee: |
SAMSUNG ELECTRO-MECHANICS CO.,
LTD.
Gyunggi-do
KR
|
Family ID: |
43625425 |
Appl. No.: |
13/620203 |
Filed: |
September 14, 2012 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12610118 |
Oct 30, 2009 |
8313874 |
|
|
13620203 |
|
|
|
|
Current U.S.
Class: |
429/497 |
Current CPC
Class: |
H01M 8/1286 20130101;
H01M 2008/1293 20130101; Y02E 60/50 20130101 |
Class at
Publication: |
429/497 |
International
Class: |
H01M 8/10 20060101
H01M008/10 |
Foreign Application Data
Date |
Code |
Application Number |
Aug 31, 2009 |
KR |
10-2009-0081190 |
Claims
1. A tubular solid oxide fuel cell, comprising: a porous tubular
cathode support having a plurality of through holes formed to
enable fuel to flow in a longitudinal direction thereof; an
electrolyte layer disposed on an inner surface of the tubular
cathode support; and an anode layer disposed on an inner surface of
the electrolyte layer.
2. The tubular solid oxide fuel cell as set forth in claim 1,
wherein an air impermeable cathode layer is formed on an outer
surface of the tubular cathode support.
3. The tubular solid oxide fuel cell as set forth in claim 1,
wherein the tubular solid oxide fuel cell has a cross-section of
any one shape selected from the group consisting of a circular
shape, a polygonal shape and a rounded rectangular shape.
4. The tubular solid oxide fuel cell as set forth in claim 1,
wherein the tubular solid oxide fuel cell having a cross-section of
the rounded rectangular shape has one or more bridges formed at the
anode layer.
5. The tubular solid oxide fuel cell as set forth in claim 1,
wherein the plurality of through holes of the cathode support
extends in an axial longitudinal direction of the tubular solid
oxide fuel cell and has a honeycomb shape in cross-section.
Description
CROSS REFERENCE TO RELATED APPLICATION
[0001] This application claims the benefit of U.S. patent
application Ser. No. 12/610,118 filed Oct. 30, 2009, entitled
"Structure Of Solid Oxide Fuel Cell", which claims priority to
Korean Patent Application No. 10-2009-0081190, filed Aug. 31, 2009,
entitled "Solid oxide fuel cell structure", which is hereby
incorporated by reference in its entirety into this
application.
BACKGROUND OF THE INVENTION
[0002] 1. Technical Field
[0003] The present invention relates to a structure of a solid
oxide fuel cell.
[0004] 2. Description of the Related Art
[0005] As environmental pollution gradually increases, global
warming problems are becoming more serious. For this reason, the
Kyoto protocol was adopted in 1997 in order to set guidelines for
the reduction of carbon dioxide emission and to handle
energy-related environmental problems in earnest. Thus, fuel cell
technology which exhibits high cell performance and is
environmentally friendly is receiving renewed attention.
[0006] A fuel cell is a device for directly converting the chemical
energy of fuel (hydrogen, LNG, LPG, etc.) and air into electric
power and heat using an electrochemical reaction. Unlike
conventional techniques for generating power including combusting
fuel, generating steam, driving a turbine and driving a power
generator, the fuel cell neither undergoes a combustion procedure
nor requires an operator and is thus regarded as a novel power
generation technique which results in high cell performance without
being accompanied by any concomitant environmental problems. The
fuel cell discharges very small amounts of air pollutants such as
SOx and NOx and also generates a small amount of carbon dioxide and
is thus a pollution-free power generator, and is furthermore
advantageous in terms of producing very little noise and not
causing any vibrations.
[0007] The fuel cell includes for example a phosphoric acid fuel
cell (PAFC), an alkaline fuel cell (AFC), a polymer electrolyte
membrane fuel cell (PEMFC), a direct methanol fuel cell (DMFC), a
solid oxide fuel cell (SOFC) and so on. In particular, the SOFC
exhibits high power generation efficiency because of low
overvoltage based on activation polarization and low irreversible
loss. Furthermore, the SOFC is advantageous because various types
of fuel, such as hydrogen, carbon and a hydrocarbon, may be used,
and also because the reaction rate at the electrodes is high, thus
obviating the need to use an expensive noble metal as an electrode
catalyst. Moreover, the temperature of the heat generated during
power generation is very high, and thus the heat is very usable. In
addition, heat generated from the SOFC is used to reform fuel and
may also be utilized as an energy source for industrial purposes or
for air cooling in a cogeneration system. Hence, the SOFC is
essential for realizing the hydrogen-based society of the
future.
[0008] In accordance with the operating principle of the SOFC, the
SOFC typically generates power through the oxidation of hydrogen or
carbon monoxide, and the reactions at the anode and cathode are
represented by Reaction 1 below.
Anode: H.sub.2+O.sup.2-.fwdarw.H.sub.2O+2O+2e
CO+O.sup.2-.fwdarw.CO.sub.2+2e
Cathode: O.sub.2+4e.fwdarw.2O.sup.2-
Overall Reaction: H.sub.2+1/2O.sub.2.fwdarw.H.sub.2O Reaction 1
[0009] In the above reactions, electrons are delivered to the
cathode through an external circuit, and simultaneously the oxygen
ion generated at the cathode is transferred to the anode through an
electrolyte. At the anode, hydrogen or carbon monoxide is combined
with the oxygen ion, thus producing electrons and water or carbon
dioxide.
[0010] Many attempts have been made to improve the structure of the
SOFC in order to inhibit the oxidation of the material to thereby
more efficiently exhibit cell performance over a long period of
time. Examples of the structure of a conventional SOFC include a
planar type, a tubular type, a flat tubular type, a honeycomb type,
a delta type, etc. The structures thereof are classified into a
cathode-supported structure and an anode-supported structure
depending on whether the support is made of a cathode material or
an anode to material.
[0011] In the case of a general cathode-supported tubular fuel
cell, while air flows through the inside of the tubular cell and
fuel flows around the outside of the tubular cell, an
electrochemical reaction ensues. Such a cathode-supported tubular
fuel cell is problematic in that the cathode material is expensive,
but is advantageous because the outside atmosphere of the tubular
cell is a hydrogen atmosphere and thus a current collector such as
a nickel pelt, an interconnector and so on may not be oxidized,
resulting in extended cell lifespan and reliability.
[0012] However, when a support is made using a comparatively
inexpensive cathode material, hydrogen fuel passes through the
inside of the tubular cell and air flows around the outside of the
tubular cell, so that a current collection material outside the
tubular cell is oxidized when the cell is operated for a long time.
In order to prevent this problem, an expensive current collection
material is required.
[0013] Japanese Unexamined Patent Publication No. 2003-297388
discloses a fuel cell structure in which an electrode is disposed
inside the tubular cell and a plurality of holes is formed in an
anode, thus supplying fuel through the holes. Although this
structure may improve the collection of current, it suffers from
the above-mentioned oxidation problem and the cell lifespan similar
to that of the conventional cell structure.
SUMMARY OF THE INVENTION
[0014] Accordingly, the present invention has been made keeping in
mind the problems related to the oxidation of an SOFC in the
related art and is intended to provide a novel structure of an
anode-supported SOFC which exhibits high cell performance and an
extended lifespan.
[0015] Also the present invention is intended to provide a novel
structure of a cathode-supported SOFC.
[0016] An aspect of the present invention provides a tubular SOFC,
including a porous tubular anode support having a plurality of
through holes formed to enable fuel to flow in a longitudinal
direction thereof, an electrolyte layer disposed on an inner
surface of the tubular anode support, and a cathode layer disposed
on an inner surface of the electrolyte layer.
[0017] In this aspect, a fuel impermeable anode layer may be formed
on an outer surface of the tubular anode support.
[0018] In this aspect, the tubular SOFC has a cross-section of any
one shape selected from the group consisting of a circular shape, a
polygonal shape and a rounded rectangular shape.
[0019] In this aspect, the tubular SOFC having a cross-section of
the rounded rectangular shape may have one or more bridges formed
at the cathode layer.
[0020] In this aspect, the plurality of through holes of the anode
support may extend in an axial longitudinal direction of the
tubular SOFC and may have a honeycomb shape in cross-section.
[0021] Another aspect of the present invention provides a tubular
SOFC, including a porous tubular cathode support having a plurality
of through holes formed to enable fuel to flow in a longitudinal
direction thereof, an electrolyte layer disposed on an inner
surface of the tubular cathode support, and an anode layer disposed
on an inner surface of the electrolyte layer.
[0022] In this aspect, an air impermeable cathode layer may be
formed on an outer surface of the tubular cathode support.
[0023] In this aspect, the tubular SOFC may have a cross-section of
any one shape selected from the group consisting of a circular
shape, a polygonal shape and a rounded rectangular shape.
[0024] In this aspect, the tubular SOFC having a cross-section of
the rounded rectangular shape may have one or more bridges formed
at the anode layer.
[0025] In this aspect, the plurality of through holes of the
cathode support may extend in an axial longitudinal direction of
the tubular SOFC and may have a honeycomb shape in
cross-section.
BRIEF DESCRIPTION OF THE DRAWINGS
[0026] The features and advantages of the present invention will be
more clearly understood from the following detailed description
taken in conjunction with the accompanying drawings, in which:
[0027] FIG. 1 is a transverse cross-sectional view schematically
showing an anode-supported tubular SOFC according to the present
invention;
[0028] FIG. 2 is a longitudinal cross-sectional view schematically
showing an anode-supported tubular SOFC according to the present
invention;
[0029] FIG. 3 is a transverse cross-sectional view schematically
showing an anode-supported flat tubular SOFC according to the
present invention;
[0030] FIG. 4 is a transverse cross-sectional view schematically
showing a cathode-supported tubular SOFC according to the present
invention;
[0031] FIG. 5 is a longitudinal cross-sectional view schematically
showing a cathode-supported tubular SOFC according to the present
invention;
[0032] FIG. 6 is a transverse cross-sectional view schematically
showing a cathode-supported flat tubular SOFC according to the
present invention; and
[0033] FIGS. 7 and 8 are cross-sectional views showing the through
holes of the tubular SOFC according to the present invention.
DESCRIPTION OF SPECIFIC EMBODIMENTS
[0034] Hereinafter, a detailed description will be given of
embodiments of the present invention with reference to the
accompanying drawings.
[0035] The present invention provides a novel structure of an SOFC
having high cell performance because it solves problems related to
the oxidation of a material in a conventional structure of an
SOFC.
[0036] FIG. 1 is a transverse cross-sectional view schematically
showing an anode-supported cylindrical SOFC according to the
present invention. With reference to this drawing, the
anode-supported cylindrical SOFC according to the present invention
is formed by using a porous tubular anode as a support.
[0037] A conventional SOFC is typically configured such that an
electrolyte layer and an electrode layer are sequentially formed on
the outer surface of a support layer. In the present invention,
however, the SOFC is configured such that an electrolyte layer 12
is formed on the inner surface of an anode support 11 and a cathode
layer 13 is formed on the inner surface of the electrolyte layer
12. This anode-supported cylindrical SOFC has an air flow passage
formed inside of the cathode layer 13, and is thus different from a
general anode-supported cylindrical oxide fuel cell in which fuel
flows in the tubular cell.
[0038] The cathode is typically made of a Perovskite type oxide.
Particularly useful is lanthanum strontium manganite
(La.sub.0.84Sr.sub.0.16).sub.MnO.sub.3 having high catalytic
performance and high electronic conductivity. Oxygen is converted
into the oxygen ion through the catalytic action of LaMnO.sub.3.
The Perovskite type oxide containing the transition metal has both
ionic conductivity and electronic conductivity, and thus is
efficiently used in the cathode. However, Perovskite other than the
manganite may cause a chemical reaction with YSZ used in the
electrolyte, undesirably creating a concern about the deterioration
of performance of the electrode. In particular, LaCoO.sub.3-based
Perovskite is a material having high electrode catalyst activity
but it chemically reacts with YSZ and has a different coefficient
of thermal expansion, and thus is considered to be a material which
is inappropriate for use in an electrode. Except for these
materials which have just been mentioned, the cathode may be made
of any other type of material which is appropriate for use
therein.
[0039] The anode may be made of metal nickel/oxide ion conductor
cermet. The metal nickel has high electronic conductivity and
adsorbs hydrogen and hydrocarbon fuel, thus exhibiting excellent
electrode catalyst activity. Compared to platinum and so on, nickel
is inexpensive and therefore an advantageous electrode material. In
the case of an SOFC operating at high temperature, a material
(Ni/YSZ cermet) obtained by sintering nickel oxide power containing
40.about.60% zirconia power may be used. However, the present
invention is not limited to this material.
[0040] Because a solid oxide electrolyte has lower ionic
conductivity than that of a liquid electrolyte such as an aqueous
solution or a molten salt, it reduces voltage drop due to
resistance polarization and should thus be formed as thin as
possible. As such, however, small clearances, pores or decants may
undesirably be formed. Hence, the solid oxide electrolyte requires
homogeneity, density, heat resistance, mechanical strength and
stability, as well as ionic conductivity. The material for the
electrolyte may include but is not limited to yttria-stabilized
zirconia (YSZ) in which yttria (Y.sub.2O.sub.3) is dissolved to
about 3.about.10% in zirconia (ZrO.sub.2).
[0041] The porous anode support 11 has a plurality of holes 14
formed to enable the flow of fuel in a longitudinal direction
thereof. Because it is not sufficient to supply fuel only through
the pores, the provision of the through holes 14 enables fuel to
flow into the tubular fuel cell.
[0042] A fuel impermeable anode layer 15 may be further applied on
the exposed outer surface of the porous anode support 11. When the
fuel impermeable anode layer 15 is formed in this way, outflow of
the fuel through the porous anode support 11 may be prevented.
[0043] The plurality of through holes 14 formed in the porous anode
support 11 may be formed in a longitudinal direction of the support
11, and the cross-section thereof may have a rounded rectangular
shape, a circular shape, etc. In addition, the plurality of through
holes may have a honeycomb shape in cross-section.
[0044] Although the cylindrical fuel cell is illustrated in FIG. 1,
any tubular shape, for example, a tetragonal prism shape, a
trigonal prism shape, a hexagonal prism shape, or a flat tubular
shape, may be used.
[0045] FIG. 2 is a longitudinal cross-sectional view showing the
anode-supported cylindrical fuel cell. As mentioned above, this
fuel cell is configured such that an electrolyte layer 22 and a
cathode layer 23 are sequentially applied on the inner surface of
an anode support 21, and an air flow passage 24 is formed in the
center thereof.
[0046] As shown in FIG. 2, through holes 25 are formed in the anode
support 21, thus enabling the supply of fuel along the through
holes 25.
[0047] Also, a fuel impermeable anode layer 26 is applied on the
outer surface of the anode support 21, thus preventing the loss of
fuel.
[0048] Therefore, the structure of the anode-supported SOFC
according to the present invention may exhibit the same effect as
that of a typical cathode-supported tubular fuel cell in which air
is supplied into the tubular cell. Specifically, according to the
present invention, an oxidizing atmosphere is formed only inside
the tubular cell, without being formed on the outside of the
tubular cell where current is collected, considerably preventing
the oxidation of the material.
[0049] Furthermore, a comparatively inexpensive anode support
material may be used to achieve the above effect, thus generating
financial benefits.
[0050] FIG. 3 is a transverse cross-sectional view schematically
showing an anode-supported flat tubular SOFC according to the
present invention. The fundamental structure thereof is the same as
that of the anode-supported cylindrical SOFC which was described
above. Specifically, the flat tubular SOFC is configured such that
an electrolyte layer 32 is formed on the inner surface of an anode
support 31 and a cathode layer 33 is formed on the inner surface of
the electrolyte layer 32. The anode support 31 is porous, and has a
plurality of through holes 34 enabling the flow of fuel.
[0051] Further, a fuel impermeable anode layer 35 may be applied on
the outer surface of the anode support 31 in order to prevent the
outflow of fuel.
[0052] Also, in order to impart an additional supporting force to
the flat tubular structure when in a fuel cell stack, a plurality
of bridges 36 which extend from the cathode layer may be
formed.
[0053] Conventional flat tubular fuel cells are problematic because
one side thereof is not used upon stacking. However, the flat
tubular fuel cell according to the present invention is
advantageous because both fuel and air flow in the fuel cell, both
sides thereof may be used.
[0054] FIG. 4 is a transverse cross-sectional view schematically
showing a cathode-supported tubular SOFC according to the present
invention.
[0055] The cathode-supported tubular SOFC according to the present
invention allows the flow of both fuel and air into the fuel
cell.
[0056] In the case of a typical cathode-supported tubular fuel cell
configured such that an electrolyte layer and an anode layer are
sequentially formed on the outer surface of a cathode support, air
flows through the inside of the fuel cell, whereas fuel is supplied
from the outside.
[0057] However, with reference to FIG. 4, the cathode-supported
tubular SOFC according to the present invention is configured such
that an electrolyte layer 42 is applied on the inner surface of a
cathode support 41 and an anode layer 43 is applied on the inner
surface to of the electrolyte layer 42.
[0058] The cathode support 41 is porous and has a plurality of
through holes 44 enabling the flow of air. The through holes 44
enable the fuel which flows outside a conventional cylindrical fuel
cell to flow in the fuel cell by traveling through the support.
[0059] Further, an air impermeable cathode layer 45 may be applied
on the outer surface of the cathode support 41. The air impermeable
cathode layer 45 prevents air from leaking to the outside of the
fuel cell and efficiently diffuses air to the electrolyte layer 42
from the porous support 41.
[0060] Hence, an oxidizing atmosphere is not formed in the anode
and the cathode, thus collecting current using an inexpensive
material and reducing the risk for oxidation. As the oxidation
decreases, cell durability and lifespan may be increased.
[0061] FIG. 5 is a longitudinal cross-sectional view schematically
showing a cathode-supported tubular SOFC according to the present
invention.
[0062] As mentioned above, the cathode-supported tubular SOFC is
configured such that an electrolyte layer 52 is applied on the
inner surface of a cathode support 51 and an anode layer 53 is
applied on the inner surface of the electrolyte layer 52. Thus,
fuel flows through the inside of the anode 53, and air flows along
a plurality of through holes 54 formed in the cathode support 51,
thus causing a reaction, resulting in current being produced.
[0063] An air impermeable cathode layer 55 may be further applied
on the outer surface of the cathode support 51, so that air may be
more efficiently diffused to the electrolyte layer 52 through the
porous cathode support 51.
[0064] As mentioned above, fuel and air do not flow outside the
cathode-supported cylindrical fuel cell according to the present
invention. In particular, because air does not flow outside the
fuel cell, problems related to the oxidation may be solved.
[0065] In a conventional tubular fuel cell, air flows out of the
tubular cell and infiltrates a porous support, thus causing the
electrochemical reaction of the fuel cell. However, in the
cathode-supported tubular fuel cell according to the present
invention, air directly flows through the inside of the cathode
support, thus increasing the diffusion rate of air to thereby
increase the reaction rate, resulting in excellent cell
performance.
[0066] Although the cylindrical fuel cell is described as above,
the structure of the fuel cell according to the present invention
may be applied to any type of tubular fuel cell, the cross-section
of which may be circular, polygonal or rounded rectangular.
[0067] FIG. 6 is a transverse cross-sectional view schematically
showing a cathode-supported flat tubular SOFC according to the
present invention.
[0068] This fuel cell has the same structure as that of the
cathode-supported cylindrical SOFC described above. Specifically,
the flat tubular SOFC is configured such that an electrolyte layer
62 is applied on the inner surface of a cathode support 61 and an
anode layer 63 is formed on the inner surface of the electrolyte
layer 62. The cathode support 61 is porous and has a plurality of
through holes 64 enabling the flow of air.
[0069] Also, an air impermeable cathode layer 65 may be further
applied on the outer surface of the cathode support 61 in order to
prevent the outflow of air.
[0070] Also, in order to impart an additional supporting force to
the flat tubular structure when in a fuel cell stack, a plurality
of bridges 66 which extend from the anode layer may be formed.
[0071] Conventional flat tubular fuel cells are problematic because
one side thereof is not used upon stacking. However, the flat
tubular fuel cell according to the present invention is
advantageous because both fuel and air may flow in the fuel cell,
and thus both sides thereof may be used.
[0072] FIGS. 7 and 8 illustrate the through holes of the tubular
SOFCs according to the present invention.
[0073] FIG. 7 shows an anode-supported tubular fuel cell. As in the
anode-supported to tubular fuel cell according to the present
invention described above, an electrode layer 72 and a cathode
layer 73 are sequentially applied on the inner surface of an anode
support 71. The porous anode support 71 has a plurality of through
holes 74 having a cross-section of a rounded rectangular shape
corresponding to the shape of the cross-section of the porous anode
support 71 divided into quarters. In this case, it is possible to
more easily supply fuel. Also, a fuel impermeable anode layer 75
may be formed on the outer surface of the anode support 71.
[0074] FIG. 8 shows a cathode-supported tubular fuel cell. As in
the cathode-supported tubular fuel cell according to the present
invention described above, an electrode layer 82 and an anode layer
83 are sequentially applied on the inner surface of a cathode
support 81. Like the description of FIG. 7, through holes 84 have a
specific shape which enables air to be more easily supplied.
Further, an air impermeable cathode layer 85 may be formed on the
outer surface of the cathode support 81.
[0075] Because both fuel and air are supplied into the fuel cell
and thus react with each other, the outside atmosphere of the fuel
cell may be an inert gas atmosphere. In this case, the oxidation of
a current collector, an outer electrode and so on may be
prevented.
[0076] As described hereinbefore, the present invention provides a
structure of an SOFC. According to the present invention, the
structure of the SOFC causes fuel and air to be more efficiently
diffused, thus increasing the reaction rate, resulting in excellent
cell performance. Furthermore, both the inside atmosphere and the
outside atmosphere of the tubular cell are not oxidizing
atmospheres, thus achieving an extended cell lifespan and ensuring
cell reliability.
[0077] Although the embodiments of the present invention have been
disclosed for illustrative purposes, those skilled in the art will
appreciate that various modifications, additions and substitutions
are possible, without departing from the scope and spirit of the
invention as disclosed in the accompanying claims. Accordingly,
such modifications, additions and substitutions should also be
understood as falling within the scope of the present
invention.
* * * * *