U.S. patent application number 11/579475 was filed with the patent office on 2012-09-20 for polymer derivatives comprising an imide branching point.
Invention is credited to Antoni Kozlowski, Samuel P. McManus.
Application Number | 20120238640 11/579475 |
Document ID | / |
Family ID | 35115877 |
Filed Date | 2012-09-20 |
United States Patent
Application |
20120238640 |
Kind Code |
A9 |
McManus; Samuel P. ; et
al. |
September 20, 2012 |
Polymer Derivatives Comprising an Imide Branching Point
Abstract
The invention provides a water-soluble polymer comprising (i) an
imide group comprising a linking nitrogen atom, a first carbonyl
group covalently attached to the linking nitrogen atom, and a
second carbonyl group covalently attached to the linking nitrogen
atom; (ii) a first water-soluble polymer segment covalently
attached, either directly or through one or more atoms, to the
first carbonyl group of the imide group and (iii) a second
water-soluble polymer segment covalently attached, either directly
or through one or more atoms, to the second carbonyl group of the
imide group. The invention also provides, among other things,
methods for preparing polymers, conjugates, pharmaceutical
compositions and the like.
Inventors: |
McManus; Samuel P.;
(Huntsville, AL) ; Kozlowski; Antoni; (Huntsville,
AL) |
Prior
Publication: |
|
Document Identifier |
Publication Date |
|
US 20080319091 A1 |
December 25, 2008 |
|
|
Family ID: |
35115877 |
Appl. No.: |
11/579475 |
Filed: |
May 3, 2005 |
PCT Filed: |
May 3, 2005 |
PCT NO: |
PCT/US05/15145 PCKC 00 |
371 Date: |
July 11, 2007 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
60567494 |
May 3, 2004 |
|
|
|
Current U.S.
Class: |
514/772.1 ;
525/408 |
Current CPC
Class: |
A61K 47/6903 20170801;
C08G 73/12 20130101; C08G 73/1092 20130101; C08G 73/08 20130101;
C08G 65/33331 20130101; A61K 47/60 20170801 |
Class at
Publication: |
514/772.1 ;
525/408 |
International
Class: |
A61K 47/48 20060101
A61K047/48; C08G 65/333 20060101 C08G065/333 |
Claims
1. A water-soluble polymer comprising (i) an imide group comprising
a linking nitrogen atom, a first carbonyl group covalently attached
to the linking nitrogen atom, and a second carbonyl group
covalently attached to the linking nitrogen atom; (ii) a first
water-soluble polymer segment covalently attached, either directly
or through one or more atoms, to the first carbonyl group of the
imide group; and (iii) a second water-soluble polymer segment
covalently attached, either directly or through one or more atoms,
to the second carbonyl group of the imide group.
2. The water-soluble polymer of claim 1, further comprising (iv) a
reactive group covalently attached, either directly or through one
or more atoms, to the linking nitrogen atom.
3. The water-soluble polymer of claims 1 or 2, wherein the first
and second water-soluble polymer segments are independently
selected from the group consisting of poly(alkylene oxide),
poly(vinyl pyrrolidone), poly(vinyl alcohol), polyoxazoline,
poly(acryloylmorpholine), and poly(oxyethylated polyol).
4. The water-soluble polymer of claims 1 or 2, wherein the first
and second water-soluble polymer segments comprise a poly(alkylene
oxide).
5. The water-soluble polymer of claim 4, wherein the first and
second water-soluble polymer segments comprise poly(ethylene
glycol).
6. The water-soluble polymer of claim 5, wherein each poly(ethylene
glycol) is terminally capped with an end-capping moiety.
7. The water-soluble polymer of claim 6, wherein each end-capping
moiety is independently selected from the group consisting alkoxy,
substituted alkoxy, alkenyloxy, substituted alkenyloxy, alkynyloxy,
substituted alkynyloxy, aryloxy, substituted aryloxy, and
hydroxy.
8. The water-soluble polymer of claim 6, wherein each end-capping
moiety is alkoxy.
9. The water-soluble polymer of claim 8, wherein each alkoxy is
methoxy.
10. The water-soluble polymer of claim 6, wherein the end-capping
moiety is hydroxy.
11. The water-soluble polymer of claim 5, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 100 Daltons to about 100,000 Daltons.
12. The water-soluble polymer of claim 11, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 500 Daltons to about 80,000 Daltons.
13. The water-soluble polymer of claim 12, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 1,000 Daltons to about 50,000 Daltons.
14. The water-soluble polymer of claim 13, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 2,000 Daltons to about 25,000 Daltons.
15. The water-soluble polymer of claim 14, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 5,000 Daltons to about 26,000 Daltons.
16. The water-soluble polymer of claim 2, wherein the reactive
group is selected from the group consisting of hydroxyl (--OH),
ester, orthoester, carbonate, acetal, aldehyde, aldehyde hydrate,
ketone, vinyl ketone, ketone hydrate, thione, thione hydrate,
hemiketal, sulfur-substituted hemiketal, ketal, alkenyl, acrylate,
methacrylate, acrylamide, sulfone, amine, hydrazide, thiol, thiol
hydrate, carboxylic acid, isocyanate, isothiocyanate, maleimide
##STR00026## succinimide ##STR00027## benzotriazole ##STR00028##
vinylsulfone, chloroethylsulfone, dithiopyridine, vinylpyridine,
iodoacetamide, epoxide, glyoxals, diones, mesylates, tosylates,
thiosulfonate, tresylate, and silane.
17. The water-soluble polymer of claim 1 or 2, wherein the first
water-soluble polymer segment is directly attached to the first
carbonyl group of the imide group and the second water-soluble
polymer segment is directly attached to the second carbonyl group
of the imide group.
18. The water-soluble polymer of claim 1 or 2, wherein at least one
of the first and second water-soluble polymer segments is attached
to their respective carbonyl group of the imide group through a
spacer moiety, wherein the spacer moiety is selected from the group
consisting of a bivalent cycloalkyl group comprising 3 to about 20
carbon atoms, an amino acid, a C1-C10 alkylene group,
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein (o) and (p) are
each independently zero to about 10 and Y is selected from the
group consisting of --O--, --S--, --N(R.sub.6)-- wherein R.sub.6 is
H or an organic radical selected from the group consisting of
alkyl, substituted alkyl, alkenyl, substituted alkenyl, alkynyl,
substituted alkynyl, aryl and substituted aryl, --C(O)--, --C(S)--,
--C(O)--O--, --C(O)--NH--, --NH--C(O)--NH--, and --O--C(O)--NH--,
and combinations thereof, wherein the spacer moiety optionally
further includes an ethylene oxide oligomer chain comprising 1 to
20 ethylene oxide monomer units.
19. The water-soluble polymer of claim 2, wherein the reactive
group is covalently attached to the linking nitrogen atom through a
spacer moiety, wherein the spacer moiety is selected from the group
consisting of a bivalent cycloalkyl group comprising 3 to about 20
carbon atoms, an amino acid, a C1-C10 alkylene group,
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein (o) and (p) are
each independently zero to about 10 and Y is selected from the
group consisting of --O--, --S--, --N(R.sub.6)-- wherein R.sub.6 is
H or an organic radical selected from the group consisting of
alkyl, substituted alkyl, alkenyl, substituted alkenyl, alkynyl,
substituted alkynyl, aryl and substituted aryl, --C(O)--, --C(S)--,
--C(O)--O--, --C(O)--NH--, --NH--C(O)--NH--, and --O--C(O)--NH--,
and combinations thereof, wherein the spacer moiety optionally
further includes an ethylene oxide oligomer chain comprising 1 to
20 ethylene oxide monomer units.
20. A water-soluble polymer having one of the following structures:
##STR00029## wherein: POLY.sub.1 is a first water-soluble polymer
segment; POLY.sub.2 is a second water-soluble polymer segment; each
of (a), (b) and (c) is independently either zero or one; X.sub.1,
when present, is a first spacer moiety; X.sub.2, when present, is a
second spacer moiety; X.sub.3, when present, is a third spacer
moiety; and Z is a reactive group.
21. The water-soluble polymer of claim 20, wherein each of
POLY.sub.1 and POLY.sub.2 is independently selected from the group
consisting of poly(alkylene oxide), poly(vinyl pyrrolidone),
poly(vinyl alcohol), polyoxazoline, poly(acryloylmorpholine), and
poly(oxyethylated polyol).
22. The water-soluble polymer of claim 20, wherein POLY.sub.1 and
POLY.sub.2 are the same.
23. The water-soluble polymer of claim 20, wherein POLY.sub.1 and
POLY.sub.2 are different.
24. The water-soluble polymer of claim 20, wherein each of
POLY.sub.1 and POLY.sub.2 is a poly(alkylene oxide).
25. The water-soluble polymer of claim 20, wherein each of
POLY.sub.1 and POLY.sub.2 is a poly(ethylene glycol).
26. The water-soluble polymer of claim 25, wherein each
poly(ethylene glycol) is terminally capped with an end-capping
moiety.
27. The water-soluble polymer of claim 26, wherein each end-capping
moiety is independently selected from the group consisting alkoxy,
substituted alkoxy, alkenyloxy, substituted alkenyloxy, alkynyloxy,
substituted alkynyloxy, aryloxy, substituted aryloxy, and
hydroxy.
28. The water-soluble polymer of claim 27, wherein each end-capping
moiety is alkoxy.
29. The water-soluble polymer of claim 28, wherein each alkoxy is
methoxy.
30. The water-soluble polymer of claim 27, wherein each end-capping
moiety is hydroxy.
31. The water-soluble polymer of claim 25, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 100 Daltons to about 100,000 Daltons.
32. The water-soluble polymer of claim 31, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 1,000 Daltons to about 50,000 Daltons.
33. The water-soluble polymer of claim 32, wherein each
poly(ethylene glycol) has a weight average molecular weight of from
about 5,000 Daltons to about 20,000 Daltons.
34. The water-soluble polymer of claim 20, wherein each of
POLY.sub.1 and POLY.sub.2 independently has a structure selected
from the group consisting of homopolymer, alternating copolymer,
random copolymer, block copolymer, alternating tripolymer, random
tripolymer, and block tripolymer.
35. The water-soluble polymer of claim 20, wherein each of (a) and
(b) is one.
36. The water-soluble polymer of claim 35, wherein each of X.sub.1
and X.sub.2 is the same.
37. The water-soluble polymer of claim 35, wherein each of X.sub.1
and X.sub.2 is different.
38. The water-soluble polymer of claim 35, wherein X.sub.1 and
X.sub.2 are independently selected from the group consisting of a
bivalent cycloalkyl group comprising 3 to about 20 carbon atoms, an
amino acid, a C1-C10 alkylene group,
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein (o) and (p) are
each independently zero to about 10 and Y is selected from the
group consisting of --O--, --S--, --N(R.sub.6)-- wherein R.sub.6 is
H or an organic radical selected from the group consisting of
alkyl, substituted alkyl, alkenyl, substituted alkenyl, alkynyl,
substituted alkynyl, aryl and substituted aryl, --C(O)--, --C(S)--,
--C(O)--O--, --C(O)--NH--, --NH--C(O)--NH--, and --O--C(O)--NH--,
and combinations thereof, wherein X.sub.1 or X.sub.2 may optionally
further include an ethylene oxide oligomer chain comprising 1 to 20
ethylene oxide monomer units.
39. The water-soluble polymer of claim 35, wherein each of X.sub.1
and X.sub.2 is independently selected from the group consisting of
--C(O)--, --C(O)--NH--, --NH--C(O)--NH--, --O--C(O)--NH--,
--C(S)--, --CH.sub.2--, --CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--, --O--CH.sub.2--,
--CH.sub.2--O--, --O--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--, --CH.sub.2--CH.sub.2--O--,
--O--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--O--,
--O--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--O--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--O--,
--C(O)--NH--CH.sub.2--, --C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--, --CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--O--CH.sub.2--, --CH.sub.2--C(O)--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--O--CH.sub.2--,
--C(O)--O--CH.sub.2--CH.sub.2--, --NH--C(O)--CH.sub.2--,
--CH.sub.2--NH--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--NH--C(O)--CH.sub.2--,
--NH--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--NH--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--NH--C(O)--CH.sub.2--CH.sub.2--,
--C(O)--NH--CH.sub.2--, --C(O)--NH--CH.sub.2--CH.sub.2--,
--O--C(O)--NH--CH.sub.2--, --O--C(O)--NH--CH.sub.2--CH.sub.2--,
--NH--CH.sub.2--, --NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--NH--CH.sub.2--, --CH.sub.2--CH.sub.2--NH--CH.sub.2--,
--C(O)--CH.sub.2--, --C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--C(O)--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--C(O)--C-
H.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--N-
H--C(O)--CH.sub.2--CH.sub.2--,
--O--C(O)--NH--(CH.sub.2).sub.h--(OCH.sub.2CH.sub.2).sub.j--,
--NH--C(O)--O--(CH.sub.2).sub.h--(OCH.sub.2CH.sub.2).sub.j--,
--C(O)--NH--(CH.sub.2).sub.h--NH--C(O)--,
--NH--C(O)--NH--(CH.sub.2).sub.h--NH--C(O)--,
--O--C(O)--NH--(CH.sub.2).sub.h--NH--C(O)--, --O--, --S--,
--N(R.sub.6)--, and combinations of two or more of any of the
foregoing, wherein (h) is zero to six, (j) is zero to 20, and
R.sub.6 is H or an organic radical selected from the group
consisting of alkyl, substituted alkyl, alkenyl, substituted
alkenyl, alkynyl, substituted alkynyl, aryl and substituted
aryl.
40. The water-soluble polymer of claim 20, wherein (c) is one.
41. The water-soluble polymer of claim 40, wherein X.sub.3 is
selected from the group consisting of a bivalent cycloalkyl group
comprising 3 to about 20 carbon atoms, an amino acid, a C1-C10
alkylene group, --(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein
(o) and (p) are each independently zero to about 10 and Y is
selected from the group consisting of --O--, --S--, --N(R.sub.6)--
wherein R.sub.6 is H or an organic radical selected from the group
consisting of alkyl, substituted alkyl, alkenyl, substituted
alkenyl, alkynyl, substituted alkynyl, aryl and substituted aryl,
--C(O)--, --C(S)--, --C(O)--O--, --C(O)--NH--, --NH--C(O)--NH--,
and --O--C(O)--NH--, and combinations thereof, wherein X.sub.3 may
optionally further include an ethylene oxide oligomer chain
comprising 1 to 20 ethylene oxide monomer units.
42. The water-soluble polymer of claim 40, wherein X.sub.3 is
selected from the group consisting of --C(O)--, --C(O)--NH--,
--NH--C(O)--NH--, --O--C(O)--NH--, --C(S)--, --CH.sub.2--,
--CH.sub.2--CH.sub.2--, --CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--, --O--CH.sub.2--,
--CH.sub.2--O--, --O--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--, --CH.sub.2--CH.sub.2--O--,
--O--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--O--,
--O--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--O--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--O--,
--C(O)--NH--CH.sub.2--, --C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--, --CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--O--CH.sub.2--, --CH.sub.2--C(O)--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--O--CH.sub.2--,
--C(O)--O--CH.sub.2--CH.sub.2--, --NH--C(O)--CH.sub.2--,
--CH.sub.2--NH--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--NH--C(O)--CH.sub.2--,
--NH--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--NH--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--NH--C(O)--CH.sub.2--CH.sub.2--,
--C(O)--NH--CH.sub.2--, --C(O)--NH--CH.sub.2--CH.sub.2--,
--O--C(O)--NH--CH.sub.2--, --O--C(O)--NH--CH.sub.2--CH.sub.2--,
--NH--CH.sub.2--, --NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--NH--CH.sub.2--, --CH.sub.2--CH.sub.2--NH--CH.sub.2--,
--C(O)--CH.sub.2--, --C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--C(O)--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--C(O)--C-
H.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--N-
H--C(O)--CH.sub.2--CH.sub.2--,
--O--C(O)--NH--(CH.sub.2).sub.h--(CH.sub.2CH.sub.2).sub.j--,
--NH--C(O)--O--(CH.sub.2).sub.h--(OCH.sub.2CH.sub.2).sub.j--,
--C(O)--NH--(CH.sub.2).sub.h--NH--C(O)--,
--NH--C(O)--NH--(CH.sub.2).sub.h--NH--C(O)--,
--O--C(O)--NH--(CH.sub.2).sub.h--NH--C(O)--, --O--, --S--,
--N(R.sub.6)--, and combinations of two or more of any of the
foregoing, wherein (h) is zero to six, (j) is zero to 20, and
R.sub.6 is H or an organic radical selected from the group
consisting of alkyl, substituted alkyl, alkenyl, substituted
alkenyl, alkynyl, substituted alkynyl, aryl and substituted
aryl.
43. The water-soluble polymer of claim 20, wherein Z comprises an
electrophile.
44. The water-soluble polymer of claim 20, wherein Z comprises a
nucleophile.
45. The water-soluble polymer of claim 20, wherein Z is selected
from the group consisting of hydroxyl (--OH), ester, orthoester,
carbonate, acetal, aldehyde, aldehyde hydrate, ketone, vinyl
ketone, ketone hydrate, thione, thione hydrate, hemiketal,
sulfur-substituted hemiketal, ketal, alkenyl, acrylate,
methacrylate, acrylamide, sulfone, amine, hydrazide, thiol, thiol
hydrate, carboxylic acid, isocyanate, isothiocyanate, maleimide
##STR00030## succinimide ##STR00031## benzotriazole ##STR00032##
vinylsulfone, chloroethylsulfone, dithiopyridine, vinylpyridine,
iodoacetamide, epoxide, glyoxals, diones, mesylates, tosylates,
thiosulfonate, tresylate, and silane.
46. The polymer of claim 20, selected from the group consisting of
##STR00033## ##STR00034## ##STR00035## ##STR00036## wherein each
(m) is independently 2 to 4,000 and R is an organic group,
preferably C1-C6 alkyl.
47. A conjugate comprising: (i) an imide group comprising a linking
nitrogen atom, a first carbonyl group covalently attached to the
linking nitrogen atom, and a second carbonyl group covalently
attached to the linking nitrogen atom; (ii) a first water-soluble
polymer segment covalently attached, either directly or through one
or more atoms, to the first carbonyl group of the imide group;
(iii) a second water-soluble polymer segment covalently attached,
either directly or through one or more atoms, to the second
carbonyl group of the imide group; and (iv) a pharmacologically
active agent covalently attached, either directly or through one or
more atoms, to the linking nitrogen atom.
48. The conjugate of claim 47, having the structure: ##STR00037##
wherein: POLY.sub.1 is a first water-soluble polymer segment;
POLY.sub.2 is a second water-soluble polymer segment; each of (a),
(b) and (c) is independently either zero or one; X.sub.1, when
present, is a first spacer moiety; X.sub.2, when present, is a
second spacer moiety; X.sub.3, when present, is a third spacer
moiety; and Active agent represents a residue of a
pharmacologically active agent.
49. A method of preparing a conjugate comprising the step of
contacting a water-soluble polymer according to any one of claims
1-46 with a pharmacologically active agent under conditions
suitable to form a covalent attachment between the water-soluble
polymer and the pharmacologically active agent.
50. A pharmaceutical preparation comprising a conjugate according
to claim 47 or claim 48 in combination with a pharmaceutical
excipient.
51. The pharmaceutical preparation of claim 50, wherein the
excipient is a sugar.
52. The pharmaceutical preparation of claim 50, in lyophilized
form.
53. The pharmaceutical preparation of claim 50, further comprising
a liquid diluent.
54. The pharmaceutical preparation of claim 53, wherein the liquid
diluent is selected from the group consisting of bacteriostatic
water for injection, dextrose 5% in water, phosphate-buffered
saline, Ringer's solution, saline solution, sterile water,
deionized water, and combinations thereof.
55. The pharmaceutical preparation of claim 50, in unit dosage
form.
56. The pharmaceutical preparation of claim 50, housed in a glass
vial.
57. A method of delivering a conjugate comprising the step of
administering to a patient a therapeutically effective amount of a
conjugate according to claim 47 or claim 48.
58. A gel comprising a water-soluble polymer of any one of claims
1-46.
59. A method of preparing a water-soluble polymer having an imide
branching moiety comprising the steps of: (i) providing a first
water-soluble polymer segment carrying a first reactive group, the
first reactive group comprising a carbonyl group; (ii) reacting the
first water-soluble polymer segment with ammonia to form a
water-soluble polymer intermediate carrying an amide group
(--C(O)--NH.sub.2); (iii) treating the water-soluble polymer
intermediate with a strong base to remove a proton from the
terminal amine of the amide group; (iv) reacting the water-soluble
polymer intermediate with a second water-soluble polymer segment
carrying a second reactive group comprising a carbonyl group to
form an imide-linked water-soluble polymer, the imide linking group
comprising a linking nitrogen atom, a first carbonyl group
covalently attached to the linking nitrogen atom, and a second
carbonyl group covalently attached to the linking nitrogen atom;
and (v) optionally, attaching a reactive group to the linking
nitrogen atom of the imide-linked water-soluble polymer.
60. The method of claim 59, wherein said attaching step (v)
comprises treating the imide-linked water-soluble polymer with a
strong base to remove a proton from the linking nitrogen atom and
reacting the imide-linked water-soluble polymer with a molecule
having the structure Z-(X.sub.3).sub.c-Q, wherein Z is a reactive
group, (c) is either zero or one, X.sub.3, when present, is a
spacer moiety, and Q is a leaving group.
61. The method of claim 60, wherein Z is selected from the group
consisting of hydroxyl (--OH), ester, orthoester, carbonate,
acetal, aldehyde, aldehyde hydrate, ketone, vinyl ketone, ketone
hydrate, thione, thione hydrate, hemiketal, sulfur-substituted
hemiketal, ketal, alkenyl, acrylate, methacrylate, acrylamide,
sulfone, amine, hydrazide, thiol, thiol hydrate, carboxylic acid,
isocyanate, isothiocyanate, maleimide ##STR00038## succinimide
##STR00039## benzotriazole ##STR00040## vinylsulfone,
chloroethylsulfone, dithiopyridine, vinylpyridine, iodoacetamide,
epoxide, glyoxals, diones, mesylates, tosylates, thiosulfonate,
tresylate, and silane.
62. The method of claim 60, wherein Q is halo or a sulfonate
ester.
63. The method of claim 60, wherein Q is mesylate ester or tosylate
ester.
64. The method of claim 60, wherein X.sub.3 is selected from the
group consisting of a bivalent cycloalkyl group comprising 3 to
about 20 carbon atoms, an amino acid, a C1-C10 alkylene group,
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein (o) and (p) are
each independently zero to about 10 and Y is selected from the
group consisting of --O--, --S--, --N(R.sub.6)-- wherein R.sub.6 is
H or an organic radical selected from the group consisting of
alkyl, substituted alkyl, alkenyl, substituted alkenyl, alkynyl,
substituted alkynyl, aryl and substituted aryl, --C(O)--, --C(S)--,
--C(O)--O--, --C(O)--NH--, --NH--C(O)--NH--, and --O--C(O)--NH--,
and combinations thereof, wherein X.sub.3 may optionally further
include an ethylene oxide oligomer chain comprising 1 to 20
ethylene oxide monomer units.
65. The method of claim 59, wherein each of the first and second
water-soluble polymer segments is a poly(ethylene glycol).
66. The method of claim 65, wherein each poly(ethylene glycol)
comprises an alkoxy end-capping moiety.
67. The method of claim 59, wherein the first and second reactive
groups are carbonate containing reactive groups having the
structure --O--C(O)--O--X.sub.r, wherein X.sub.r is aryl,
substituted aryl, heteroaryl, substituted heteroaryl, heterocycle,
or substituted heterocycle.
68. The method of claim 67, wherein X.sub.r is 1-benzotriazolyl,
o-, m-, or p-nitrophenyl, or N-succinimidyl.
69. The method of claim 59, wherein the imide-linked water-soluble
polymer has the structure: ##STR00041## wherein: POLY.sub.1 is a
first water-soluble polymer segment; POLY.sub.2 is a second
water-soluble polymer segment; each of (a) and (b) is independently
either zero or one; X.sub.1, when present, is a first spacer
moiety; and X.sub.2, when present, is a second spacer moiety.
70. The method of claim 59, wherein, following said attaching step
(v), the imide-linked water-soluble polymer has the structure:
##STR00042## wherein: POLY.sub.1 is a first water-soluble polymer
segment; POLY.sub.2 is a second water-soluble polymer segment; each
of (a), (b) and (c) is independently either zero or one; X.sub.1,
when present, is a first spacer moiety; X.sub.2, when present, is a
second spacer moiety; X.sub.3, when present, is a third spacer
moiety; and Z is a reactive group.
71. The method of claim 59, further comprising the step of
recovering the imide-linked water-soluble polymer.
72. The method of claim 71, wherein the recovering step is carried
out by chromatography.
73. The method of claim 59, further comprising the step of
purifying the imide-linked water-soluble polymer.
74. A method of preparing a water-soluble polymer having an imide
branching moiety comprising the steps of: (i) providing a first
water-soluble polymer segment carrying a first reactive group, the
first reactive group comprising a carbonyl group; (ii) reacting the
first water-soluble polymer segment with a molecule comprising a
second reactive group and an amine group, optionally separated by a
spacer moiety, to form a water-soluble polymer intermediate
comprising an amide linkage (--C(O)--NH--) between the
water-soluble polymer segment and the second reactive group; (iii)
treating the water-soluble polymer intermediate with a strong base
to remove a proton from the nitrogen atom of the amide linkage; and
(iv) reacting the water-soluble polymer intermediate with a second
water-soluble polymer segment carrying a third reactive group
comprising a carbonyl group to form an imide-linked water-soluble
polymer, the imide linking group comprising a linking nitrogen
atom, a first carbonyl group covalently attached to the linking
nitrogen atom, and a second carbonyl group covalently attached to
the linking nitrogen atom.
75. The method of claim 74, wherein the molecule comprising a
second reactive group and an amine group has the structure
Z-(X.sub.3).sub.c--NH.sub.2, wherein Z is the second reactive
group, (c) is either zero or one, and X.sub.3, when present, is a
spacer moiety.
76. The method of claim 75, wherein Z is selected from the group
consisting of hydroxyl (--OH), ester, orthoester, carbonate,
acetal, aldehyde, aldehyde hydrate, ketone, vinyl ketone, ketone
hydrate, thione, thione hydrate, hemiketal, sulfur-substituted
hemiketal, ketal, alkenyl, acrylate, methacrylate, acrylamide,
sulfone, amine, hydrazide, thiol, thiol hydrate, carboxylic acid,
isocyanate, isothiocyanate, maleimide ##STR00043## succinimide
##STR00044## benzotriazole ##STR00045## vinylsulfone,
chloroethylsulfone, dithiopyridine, vinylpyridine, iodoacetamide,
epoxide, glyoxals, diones, mesylates, tosylates, thiosulfonate,
tresylate, and silane.
77. The method of claim 75, wherein X.sub.3 is selected from the
group consisting of a bivalent cycloalkyl group comprising 3 to
about 20 carbon atoms, an amino acid, a C1-C10 alkylene group,
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein (o) and (p) are
each independently zero to about 10 and Y is selected from the
group consisting of --O--, --S--, --N(R.sub.6)-- wherein R.sub.6 is
H or an organic radical selected from the group consisting of
alkyl, substituted alkyl, alkenyl, substituted alkenyl, alkynyl,
substituted alkynyl, aryl and substituted aryl, --C(O)--, --C(S)--,
--C(O)--O--, --C(O)--NH--, --NH--C(O)--NH--, and --O--C(O)--NH--,
and combinations thereof, wherein X.sub.3 may optionally further
include an ethylene oxide oligomer chain comprising 1 to 20
ethylene oxide monomer units.
78. The method of claim 74, wherein each of the first and second
water-soluble polymer segments is a poly(ethylene glycol).
79. The method of claim 78, wherein each poly(ethylene glycol)
comprises an alkoxy end-capping moiety.
80. The method of claim 74, wherein the first and third reactive
groups are carbonate containing reactive groups having the
structure --O--C(O)--O--X.sub.r, wherein X.sub.r is aryl,
substituted aryl, heteroaryl, substituted heteroaryl, heterocycle,
or substituted heterocycle.
81. The method of claim 80, wherein X.sub.r is 1-benzotriazolyl,
o-, m-, or p-nitrophenyl, or N-succinimidyl.
82. The method of claim 74, wherein the imide-linked water-soluble
polymer has the structure: ##STR00046## wherein: POLY.sub.1 is a
first water-soluble polymer segment; POLY.sub.2 is a second
water-soluble polymer segment; each of (a), (b) and (c) is
independently either zero or one; X.sub.1, when present, is a first
spacer moiety; X.sub.2, when present, is a second spacer moiety;
X.sub.3, when present, is a third spacer moiety; and Z is a
reactive group.
83. The method of claim 74, further comprising the step of
recovering the imide-linked water-soluble polymer.
84. The method of claim 83, wherein the recovering step is carried
out by chromatography.
85. The method of claim 74, further comprising the step of
purifying the imide-linked water-soluble polymer.
Description
FIELD OF THE INVENTION
[0001] The present invention relates generally to branched polymer
derivatives wherein branching in the polymer derivative is effected
through an imide moiety. In addition, the invention relates to
conjugates of the polymer derivatives, methods for synthesizing the
polymer derivatives and methods for conjugating the polymer
derivatives to active agents and other substances.
BACKGROUND OF THE INVENTION
[0002] Scientists and clinicians face a number of challenges in
their attempts to develop active agents that are in a form suitable
for delivery to a patient. Active agents that are polypeptides, for
example, are often delivered via injection rather than orally. In
this way, the polypeptide is introduced into the systemic
circulation without exposure to the proteolytic environment of the
stomach. Injection of polypeptides, however, has several drawbacks.
For example, many polypeptides have a relatively short half-life,
thereby necessitating repeated injections, which are often
inconvenient and painful. Moreover, some polypeptides may elicit
one or more immune responses with the consequence that the
patient's immune system may be activated to degrade the
polypeptide. Thus, delivery of active agents such as polypeptides
is often problematic even when these agents are administered by
injection.
[0003] Some success has been achieved in addressing the problems of
delivering active agents via injection. For example, conjugating
the active agent to a water-soluble polymer has resulted in
polymer-active agent conjugates having reduced immunogenicity and
antigenicity. In addition, these polymer-active agent conjugates
often have greatly increased half-lives compared to their
unconjugated counterparts as a result of decreased clearance
through the kidney and/or decreased enzymatic degradation in the
systemic circulation. As a result of having a greater half-life,
the polymer-active agent conjugate requires less frequent dosing,
which in turn reduces the overall number of painful injections and
inconvenient visits with a health care professional. Moreover,
active agents that were only marginally soluble demonstrate a
significant increase in water solubility when conjugated to a
water-soluble polymer.
[0004] Due to its documented safety and approval by the FDA for
both topical and internal use, poly(ethylene glycol) has been
conjugated to active agents. When an active agent is conjugated to
polyethylene glycol or "PEG", the conjugated active agent is
conventionally referred to as "PEGylated." The commercial success
of PEGylated active agents, such as PEGASYS.RTM. PEGylated
interferon alpha-2a (Hoffmann-La Roche, Nutley, N.J.),
PEG-INTRON.RTM. PEGylated interferon alpha-2b (Schering Corp.,
Kennilworth, N.J.), NEULASTA.TM. PEG-filgrastim (Amgen Inc.,
Thousand Oaks, Calif.), demonstrates that administration of a
conjugated form of an active agent can have significant advantages
over the unconjugated counterpart. PEGylated versions of certain
small molecules, such as distearoylphosphatidylethanolamine
(Zalipsky (1993) Bioconjug. Chem. 4(4):296-299) and fluorouracil
(Ouchi et al. (1992) Drug Des. Discov. 2(1):93-105), have also been
prepared. Harris et al. have provided a review of the effects of
PEGylation on pharmaceuticals. Harris et al. (2003) Nat. Rev. Drug
Discov. 2(3):214-221.
[0005] Despite these successes, conjugation of a polymer to an
active agent is often challenging. For example, attaching a
relatively long poly(ethylene glycol) molecule to an active agent
typically imparts greater water solubility than attaching a shorter
poly(ethylene glycol) molecule. However, some conjugates bearing
such long poly(ethylene glycol) moieties have been known to be
substantially inactive in vivo. It has been hypothesized that these
conjugates are inactive due to the length of the poly(ethylene
glycol) chain, which effectively "wraps" itself around the entire
active agent, thereby blocking access to potential ligands required
for activity.
[0006] The problem associated with inactive conjugates bearing
relatively large poly(ethylene glycol) moieties has been solved, in
part, by using "branched" forms of a polymer derivative.
"mPEG2-N-hydroxysuccinimide" and "mPEG2-aldehyde," as shown below,
represent examples of branched versions of a poly(ethylene glycol)
derivative.
##STR00001##
wherein n represents the number of repeating ethylene oxide monomer
units.
[0007] Although solving some of the issues associated with using
relatively large polymers, branched versions of polymer derivatives
also have problems. For example, the increased structurally
complexity of branching often results in a concomitant increase in
synthetic complexity and/or purification difficulties. As a result,
there is an ongoing need in the art for more readily synthesized
and/or purified polymer derivatives that can be conveniently used
in conjugation reactions with active agents.
SUMMARY OF THE INVENTION
[0008] In one or more aspects of the invention, a polymer is
provided comprising a first water-soluble polymer segment and a
second water-soluble polymer segment covalently linked, either
directly or through a spacer moiety, to an imide moiety. The imide
moiety serves as a branching point to which the two polymer
segments are attached. Other groups, such as a reactive group, can
also be attached to the imide moiety. As will be shown in further
detail below, the imide moiety comprises two carbonyl groups, each
of which is linked to a single nitrogen atom, herein referred to as
a "linking nitrogen atom." Typically, the first and second
water-soluble polymer segments are attached to the carbon atoms of
the carbonyl groups, one water-soluble polymer segment per carbonyl
group. In embodiments also comprising a reactive group, the
reactive group is attached to the linking nitrogen atom, either
directly or through one or more atoms. Thus, the various elements
are attached in such as way as to result in a branched
structure.
[0009] Attachment of the first and second water-soluble polymer
segments, as well as the reactive group, to the imide moiety can be
effected directly or indirectly. Direct attachment typically
comprises a linkage--without any intervening atoms--between the
imide moiety and the first or second water-soluble polymer segment
or the reactive group. Indirect attachment comprises attachment of
the polymer segment or reactive group to the imide moiety through a
spacer moiety comprising one or more atoms. In some instances, both
a direct and indirect attachment can be present within a single
polymer.
[0010] Any water-soluble polymer segment and any reactive group can
be used in the polymer and the invention is not limited in this
regard. It is preferred, however, that the water-soluble polymer
segments comprise poly(ethylene glycol). The polymer segments may
include an end-capping moiety, such as alkoxy (e.g., methoxy or
ethoxy), substituted alkoxy, alkenyloxy, substituted alkenyloxy,
alkynyloxy, substituted alkynyloxy, aryloxy, substituted aryloxy,
or hydroxy. In addition, preferred reactive groups include
nucleophiles and electrophiles commonly used in synthetic organic
chemistry. Particularly preferred reactive groups include hydroxyl
(--OH), ester, orthoester, carbonate, acetal, aldehyde, aldehyde
hydrate, ketone, vinyl ketone, ketone hydrate, thione, thione
hydrate, hemiketal, sulfur-substituted hemiketal, ketal, alkenyl,
acrylate, methacrylate, acrylamide, sulfone, amine, hydrazide,
thiol, thiol hydrate, carboxylic acid, isocyanate, isothiocyanate,
maleimide
##STR00002##
succinimide
##STR00003##
benzotriazole
##STR00004##
vinylsulfone, chloroethylsulfone, dithiopyridine, vinylpyridine,
iodoacetamide, epoxide, glyoxals, diones, mesylates, tosylates,
thiosulfonate, tresylate, and silane. Both water-soluble polymer
segments and reactive groups suitable for use in connection with
the present invention are discussed in more detail below.
[0011] In one or more embodiments, the polymer of the invention has
one of the following structures:
##STR00005##
wherein:
[0012] POLY.sub.1 is a first water-soluble polymer segment;
[0013] POLY.sub.2 is a second water-soluble polymer segment;
[0014] each of (a), (b) and (c) is independently either zero or
one;
[0015] X.sub.1, when present, is a first spacer moiety;
[0016] X.sub.2, when present, is a second spacer moiety;
[0017] X.sub.3, when present, is a third spacer moiety; and
[0018] Z is a reactive group.
[0019] When present, each spacer moiety, X.sub.1, X.sub.2, and
X.sub.3, is preferably: a bivalent cycloalkyl group comprising 3 to
about 20 carbon atoms; an amino acid; a C1-C10 alkylene group;
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein o and p are each
independently zero to about 10 and Y is selected from the group
consisting of --O--, --S--, --C(O)--, --C(S)--, --C(O)--O--,
--C(O)--NH--, --NH--C(O)--NH--, --O--C(O)--NH--, and --N(R.sub.6)--
wherein R.sub.6 is H or an organic radical selected from the group
consisting of alkyl, substituted alkyl, alkenyl, substituted
alkenyl, alkynyl, substituted alkynyl, aryl and substituted aryl;
or a combination thereof, wherein the spacer moiety may optionally
further include an ethylene oxide oligomer chain comprising 1 to 20
ethylene oxide monomer units.
[0020] In one or more aspects, the invention provides a method for
preparing the polymers described herein. Briefly, the method
comprises: (i) providing a first water-soluble polymer segment
carrying a first reactive group that comprises a carbonyl group
(C.dbd.O), (ii) reacting the first water-soluble polymer segment
with anhydrous ammonia to form a water-soluble polymer intermediate
carrying a terminal --C(O)--NH.sub.2 group (iii) treating the
water-soluble polymer intermediate with a strong base to remove a
proton from the terminal --C(O)--NH.sub.2 group, (iv) reacting the
water-soluble polymer intermediate with a second water-soluble
polymer segment carrying a second reactive group comprising a
carbonyl group to form an imide-linked (--C(O)--NH--C(O)--)
water-soluble polymer, the imide linking group comprising a linking
nitrogen atom, a first carbonyl group covalently attached to the
linking nitrogen atom, and a second carbonyl group covalently
attached to the linking nitrogen atom, and (v) optionally,
attaching a reactive group to the linking nitrogen atom of the
imide-linked water-soluble polymer.
[0021] In one or more aspects, the invention provides a second
method for preparing the polymers described herein. Briefly, the
method comprises: (i) providing a first water-soluble polymer
segment carrying a first reactive group, the first reactive group
comprising a carbonyl group, (ii) reacting the first water-soluble
polymer segment with a molecule comprising a second reactive group
and an amine group, optionally separated by a spacer moiety, to
form a water-soluble polymer intermediate comprising a --C(O)--NH--
linkage between the water-soluble polymer segment and the second
reactive group, (iii) treating the water-soluble polymer
intermediate with a strong base to remove a proton from the
nitrogen atom of the --C(O)--NH-- linkage, and (iv) reacting the
water-soluble polymer intermediate with a second water-soluble
polymer segment carrying a third reactive group comprising a
carbonyl group to form an imide-linked water-soluble polymer, the
imide linking group comprising a linking nitrogen atom, a first
carbonyl group covalently attached to the linking nitrogen atom,
and a second carbonyl group covalently attached to the linking
nitrogen atom.
[0022] In one or more aspects of the invention, an active
agent-polymer conjugate is provided wherein the conjugate comprises
a polymer as described herein covalently attached to an active
agent. In addition, the invention also provides a method for
forming active-agent conjugates wherein the method comprises the
step of contacting a polymer as described herein to a
pharmacologically active agent under conditions suitable to form a
covalent attachment between the polymer and the pharmacologically
active agent.
[0023] In one or more aspects of the invention, pharmaceutical
compositions are provided comprising a polymer conjugate as
described herein in combination with a pharmaceutically acceptable
carrier. The pharmaceutical compositions encompass all types of
formulations and in particular those that are suited for injection,
e.g., powders that can be reconstituted as well as suspensions and
solutions. Furthermore, the invention provides a method of treating
a patient comprising the step of administering a polymer conjugate
as described herein.
[0024] Additional aspects, advantages, and novel features of the
invention will be set forth in the description that follows, and/or
will become apparent to one having ordinary skill in the art upon
the following, or may be learned by practice of the invention.
DETAILED DESCRIPTION OF THE INVENTION
[0025] Before describing the present invention in detail, it is to
be understood that this invention is not limited to the particular
polymers, synthetic techniques, active agents, and the like as such
may vary.
[0026] It must be noted that, as used in this specification and the
claims, the singular forms "a," "an," and "the" include plural
referents unless the context clearly dictates otherwise. Thus, for
example, reference to a "polymer" includes a single polymer as well
as two or more of the same or different polymers, reference to a
"conjugate" refers to a single conjugate as well as two or more of
the same or different conjugates, reference to an "excipient"
includes a single excipient as well as two or more of the same or
different excipients, and the like.
[0027] In describing and claiming the present invention, the
following terminology will be used in accordance with the
definitions described below.
[0028] "PEG," "polyethylene glycol" and "poly(ethylene glycol)" as
used herein, are meant to encompass any water-soluble poly(ethylene
oxide). Typically, PEGs for use in accordance with the invention
comprise the following structure "--O(CH.sub.2CH.sub.2O).sub.m--"
where (m) is 2 to 4000. As used herein, PEG also includes
"--CH.sub.2CH.sub.2--O(CH.sub.2CH.sub.2O).sub.m--CH.sub.2CH.sub.2--"
and "--(CH.sub.2CH.sub.2O).sub.m--," depending upon whether or not
the terminal oxygens have been displaced. When the PEG further
comprises a spacer moiety (to be described in greater detail
below), the atoms comprising the spacer moiety, when covalently
attached to a water-soluble polymer segment, do not result in the
formation of an oxygen-oxygen bond (i.e., an "--O--O--" or peroxide
linkage). Throughout the specification and claims, it should be
remembered that the term "PEG" includes structures having various
terminal or "end capping" groups and so forth. The term "PEG" also
means a polymer that contains a majority, that is to say, greater
than 50%, of --CH.sub.2CH.sub.2O-- monomeric subunits. With respect
to specific forms, the PEG can take any number of a variety of
molecular weights, as well as structures or geometries such as
"branched," "linear," "forked," "multifunctional," and the like, to
be described in greater detail below.
[0029] The terms "end-capped" or "terminally capped" are
interchangeably used herein to refer to a terminal or endpoint of a
polymer having an end-capping moiety. Typically, although not
necessarily, the end-capping moiety comprises a hydroxy or
C.sub.1-20 alkoxy group. Thus, examples of end-capping moieties
include alkoxy (e.g., methoxy, ethoxy and benzyloxy), as well as
alkenyloxy, alkynyloxy, aryl, heteroaryl, cyclo, heterocyclo, and
the like. In addition, saturated, unsaturated, substituted and
unsubstituted forms of each of the foregoing are envisioned.
Moreover, the end-capping group can also be a silane. The
end-capping group can also advantageously comprise a detectable
label. When the polymer has an end-capping group comprising a
detectable label, the amount or location of the polymer and/or the
moiety (e.g., active agent) of interest to which the polymer is
coupled to can be determined by using a suitable detector. Such
labels include, without limitation, fluorescers, chemiluminescers,
moieties used in enzyme labeling, colorimetric (e.g., dyes), metal
ions, radioactive moieties, and the like. Suitable detectors
include photometers, films, spectrometers, and the like.
[0030] The term "water soluble" as in a "water-soluble polymer
segment" and "water-soluble polymer" means any segment or polymer
that is soluble in water at room temperature. Typically, a
water-soluble polymer or segment will transmit at least about 75%,
more preferably at least about 95% of light, transmitted by the
same solution after filtering. On a weight basis, a water-soluble
polymer or segment thereof will preferably be at least about 35%
(by weight) soluble in water, more preferably at least about 50%
(by weight) soluble in water, still more preferably about 70% (by
weight) soluble in water, and still more preferably about 85% (by
weight) soluble in water. It is most preferred, however, that the
water-soluble polymer or segment is about 95% (by weight) soluble
in water or completely soluble in water.
[0031] The term "non-peptidic" as in a "non-peptidic polymer"
refers to a polymer substantially free of peptide linkages.
However, the polymer may include a minor number of peptide linkages
such as, for example, no more than about 1 peptide linkage per
about 10 monomeric units.
[0032] Molecular weight in the context of a water-soluble polymer
of the invention, such as PEG, can be expressed as either a number
average molecular weight or a weight average molecular weight. Both
molecular weight determinations, number average and weight average,
can be measured using gel permeation chromatography or other liquid
chromatography techniques. Other methods for measuring molecular
weight values can also be used, such as the use of end-group
analysis or the measurement of colligative properties (e.g.,
freezing-point depression, boiling-point elevation, or osmotic
pressure) to determine number average molecular weight or the use
of light scattering techniques, ultracentrifugation or viscometry
to determine weight average molecular weight. The polymers of the
invention are typically polydisperse (i.e., number average
molecular weight and weight average molecular weight of the
polymers are not equal), possessing low polydispersity values of
preferably less than about 1.2, more preferably less than about
1.15, still more preferably less than about 1.10, yet still more
preferably less than about 1.05, and most preferably less than
about 1.03.
[0033] As used herein, the term "carboxylic acid" as in a
"carboxylic acid" derivative is a moiety having a
##STR00006##
functional group [also represented as a "--COOH" or --C(O)OH].
Unless the context clearly dictates otherwise, the term carboxylic
acid includes not only the acid form, but corresponding esters and
protected forms as well. Exemplary protecting groups for carboxylic
acids can be found in Greene et al., "PROTECTIVE GROUPS IN ORGANIC
SYNTHESIS," 3.sup.rd Edition, John Wiley and Sons, Inc., New York,
1999.
[0034] The term "reactive" or "activated" when used in conjunction
with a particular functional group, refers to a reactive functional
group that reacts readily with an electrophile or a nucleophile on
another molecule. This is in contrast to those groups that require
strong catalysts or highly impractical reaction conditions in order
to react (i.e., a "nonreactive" or "inert" group).
[0035] The terms "protected" or "protecting group" or "protective
group" refer to the presence of a moiety (i.e., the protecting
group) that prevents or blocks reaction of a particular chemically
reactive functional group in a molecule under certain reaction
conditions. The protecting group will vary depending upon the type
of chemically reactive group being protected as well as the
reaction conditions to be employed and the presence of additional
reactive or protecting groups in the molecule, if any. Protecting
groups known in the art can be found in Greene et al., supra.
[0036] As used herein, the term "functional group" or any synonym
thereof is meant to encompass protected forms thereof.
[0037] The term "spacer" or "spacer moiety" is used herein to refer
to an atom or a collection of atoms optionally used to link one
moiety to another, such as a water-soluble polymer segment to a
branching group such as an imide. The spacer moieties of the
invention may be hydrolytically stable or may include a
physiologically hydrolyzable or enzymatically degradable
linkage.
[0038] "Alkyl" refers to a hydrocarbon chain, typically ranging
from about 1 to 20 atoms in length. Such hydrocarbon chains are
preferably but not necessarily saturated and may be branched or
straight chain, although typically straight chain is preferred.
Exemplary alkyl groups include ethyl, propyl, butyl, pentyl,
1-methylbutyl, 1-ethylpropyl, 3-methylpentyl, and the like. As used
herein, "alkyl" includes cycloalkyl when three or more carbon atoms
are referenced.
[0039] "Lower alkyl" refers to an alkyl group containing from 1 to
6 carbon atoms, and may be straight chain or branched, as
exemplified by methyl, ethyl, n-butyl, iso-butyl, and
tert-butyl.
[0040] "Cycloalkyl" refers to a saturated or unsaturated cyclic
hydrocarbon chain, including bridged, fused, or spiro cyclic
compounds, preferably made up of 3 to about 12 carbon atoms, more
preferably 3 to about 8.
[0041] "Non-interfering substituents" are those groups that, when
present in a molecule, are typically non-reactive with other
functional groups contained within the molecule.
[0042] The term "substituted" as in, for example, "substituted
alkyl," refers to a moiety (e.g., an alkyl group) substituted with
one or more non-interfering substituents, such as, but not limited
to: C.sub.3-C.sub.8 cycloalkyl, e.g., cyclopropyl, cyclobutyl, and
the like; halo, e.g., fluoro, chloro, bromo, and iodo; cyano;
alkoxy, lower phenyl (e.g., 0-2 substituted phenyl); substituted
phenyl; and the like. "Substituted aryl" is aryl having one or more
non-interfering groups as a substituent. For substitutions on a
phenyl ring, the substituents may be in any orientation (i.e.,
ortho, meta, or para).
[0043] "Alkoxy" refers to an --O--R group, wherein R is alkyl or
substituted alkyl, preferably C.sub.1-C.sub.20 alkyl (e.g.,
methoxy, ethoxy, propyloxy, benzyl, etc.), preferably
C.sub.1-C.sub.7.
[0044] As used herein, "alkenyl" refers to a branched or unbranched
hydrocarbon group of 1 to 15 atoms in length, containing at least
one double bond, such as ethenyl, n-propenyl, isopropenyl,
n-butenyl, isobutenyl, octenyl, decenyl, tetradecenyl, and the
like.
[0045] The term "alkynyl" as used herein refers to a branched or
unbranched hydrocarbon group of 2 to 15 atoms in length, containing
at least one triple bond, e.g., ethynyl, n-propynyl, n-butynyl,
isopentynyl, octynyl, decynyl, and so forth.
[0046] "Aryl" means one or more aromatic rings, each of 5 or 6 core
carbon atoms. Aryl includes multiple aryl rings that may be fused,
as in naphthyl or unfused, as in biphenyl. Aryl rings may also be
fused or unfused with one or more cyclic hydrocarbon, heteroaryl,
or heterocyclic rings. As used herein, "aryl" includes
heteroaryl.
[0047] "Heteroaryl" is an aryl group containing from one to four
heteroatoms, preferably N, O, or S, or a combination thereof.
Heteroaryl rings may also be fused with one or more cyclic
hydrocarbon, heterocyclic, aryl, or heteroaryl rings.
[0048] "Heterocycle" or "heterocyclic" means one or more rings of
5-12 atoms, preferably 5-7 atoms, with or without unsaturation or
aromatic character and having at least one ring atom which is not a
carbon. Preferred heteroatoms include sulfur, oxygen, and
nitrogen.
[0049] "Substituted heteroaryl" is heteroaryl having one or more
non-interfering groups as substituents.
[0050] "Substituted heterocycle" is a heterocycle having one or
more side chains formed from non-interfering substituents.
[0051] "Electrophile" refers to an ion or atom or collection of
atoms, that may be ionic, having an electrophilic center, i.e., a
center that is electron seeking, or capable of reacting with a
nucleophile.
[0052] "Nucleophile" refers to an ion or atom or collection of
atoms, that may be ionic, having a nucleophilic center, i.e., a
center that is seeking an electrophilic center or capable of
reaction with an electrophile.
[0053] A "physiologically cleavable" or "hydrolyzable" or
"degradable" bond is a relatively weak bond that reacts with water
(i.e., is hydrolyzed) under physiological conditions. The tendency
of a bond to hydrolyze in water will depend not only on the general
type of linkage connecting two central atoms but also on the
substituents attached to these central atoms. Appropriate
hydrolytically unstable or weak linkages include, but are not
limited to, carboxylate ester, phosphate ester, anhydrides,
acetals, ketals, acyloxyalkyl ether, imines, ortho esters, peptides
and oligonucleotides.
[0054] An "enzymatically degradable linkage" means a linkage that
is subject to degradation by one or more enzymes.
[0055] A "hydrolytically stable" linkage or bond refers to a
chemical bond, typically a covalent bond, that is substantially
stable in water, that is to say, does not undergo hydrolysis under
physiological conditions to any appreciable extent over an extended
period of time. Examples of hydrolytically stable linkages include
but are not limited to the following: carbon-carbon bonds (e.g., in
aliphatic chains), ethers, amides, urethanes, and the like.
Generally, a hydrolytically stable linkage is one that exhibits a
rate of hydrolysis of less than about 1-2% per day under
physiological conditions. Hydrolysis rates of representative
chemical bonds can be found in most standard chemistry
textbooks.
[0056] The terms "active agent," "biologically active agent" and
"pharmacologically active agent" are used interchangeably herein
and are defined to include any agent, drug, compound, composition
of matter or mixture that provides some pharmacologic, often
beneficial, effect that can be demonstrated in-vivo or in vitro.
This includes foods, food supplements, nutrients, nutriceuticals,
drugs, proteins, vaccines, antibodies, vitamins, and other
beneficial agents. As used herein, these terms further include any
physiologically or pharmacologically active substance that produces
a localized or systemic effect in a patient.
[0057] "Pharmaceutically acceptable excipient" or "pharmaceutically
acceptable carrier" refers to an excipient that can be included in
the compositions of the invention and that causes no significant
adverse toxicological effects to the patient.
[0058] "Pharmacologically effective amount," "physiologically
effective amount," and "therapeutically effective amount" are used
interchangeably herein to mean the amount of a polymer-active agent
conjugate--typically present in a pharmaceutical preparation--that
is needed to provide a desired level of active agent and/or
conjugate in the bloodstream or in a target tissue. The exact
amount will depend upon numerous factors, e.g., the particular
active agent, the components and physical characteristics of the
pharmaceutical preparation, intended patient population, patient
considerations, and the like, and can readily be determined by one
of ordinary skill in the art, based upon the information provided
herein and available in the relevant literature.
[0059] "Multifunctional" in the context of a polymer of the
invention means a polymer having 3 or more functional groups
contained therein, where the functional groups may be the same or
different. Multifunctional polymers of the invention will typically
contain from about 3-100 functional groups, e.g., from 3-50
functional groups, from 3-25 functional groups, from 3-15
functional groups, and from 3 to 10 functional groups i.e., 3, 4,
5, 6, 7, 8, 9 or 10 functional groups) within the polymer. A
"difunctional" polymer means a polymer having two functional groups
contained therein, either the same (i.e., homodifunctional) or
different (i.e., heterodifunctional).
[0060] "Branched," in reference to the geometry or overall
structure of a polymer, refers to a polymer having 2 or more
polymer "arms." A branched polymer may possess 2 polymer arms, 3
polymer arms, 4 polymer arms, 6 polymer arms, 8 polymer arms or
more. One particular type of highly branched polymer is a dendritic
polymer or dendrimer, which, for the purposes of the invention, is
considered to possess a structure distinct from that of a branched
polymer.
[0061] A "dendrimer" or dendritic polymer is a globular, size
monodisperse polymer in which all bonds emerge radially from a
central focal point or core with a regular branching pattern and
with repeat units that each contribute a branch point. Dendrimers
exhibit certain dendritic state properties such as core
encapsulation, making them unique from other types of polymers.
[0062] A basic or acidic reactant described herein includes
neutral, charged, and any corresponding salt forms thereof.
[0063] The term "patient," refers to a living organism suffering
from or prone to a condition that can be prevented or treated by
administration of a conjugate as provided herein, and includes both
humans and animals.
[0064] "Optional" and "optionally" mean that the subsequently
described circumstance may or may not occur, so that the
description includes instances where the circumstance occurs and
instances where it does not.
[0065] As used herein, the "halo" designator (e.g., fluoro, chloro,
iodo, bromo, and so forth) is generally used when the halogen is
attached to a molecule, while the suffix "ide" (e.g., fluoride,
chloride, iodide, bromide, and so forth) is used when the ionic
form is used when the halogen exists in its independent ionic form
(e.g., such as when a leaving group leaves a molecule).
[0066] In the context of the present discussion, it should be
recognized that the definition of a variable provided with respect
to one structure or formula is applicable to the same variable
repeated in a different structure, unless the context dictates
otherwise. Thus, for example, the definition of "POLY," "a spacer
moiety," and so forth with respect to a polymer can be equally
applicable to a water-soluble polymer conjugate provided
herein.
[0067] Turning to a first aspect of the invention, a polymer is
provided comprising an imide moiety comprising the following
structure:
##STR00007##
As shown, the imide moiety comprises a central linking nitrogen
atom that is covalently bonded to the carbon atoms of two carbonyl
groups.
[0068] In addition to the imide moiety, the polymer of the
invention also comprises a first water-soluble polymer segment and
a second water-soluble polymer segment. Each water-soluble polymer
segment is attached, either directly or through a spacer moiety, to
one of the two carbonyl groups attached to the linking nitrogen
atom in the imide moiety, one water-soluble polymer segment per
carbonyl group. Thus, the first and second water-soluble polymer
segments are attached to the imide moiety as shown below.
##STR00008##
wherein:
[0069] POLY.sub.1 is a first water-soluble polymer segment;
[0070] POLY.sub.2 is a second water-soluble polymer segment;
[0071] each of (a) and (b) is independently either zero or one;
[0072] X.sub.1, when present, is a first spacer moiety; and
[0073] X.sub.2, when present, is a second spacer moiety.
[0074] Each of the first and second water-soluble polymer segments
can comprise any polymer so long as the polymer is water-soluble.
Moreover, a water-soluble polymer segment as used herein is
typically non-peptidic. Although preferably a poly(ethylene
glycol), (i.e., "PEG" or a "PEG polymer") a water-soluble polymer
segment for use herein can be, for example, other poly(alkylene
glycols) [e.g., poly(propylene glycol) ("PPG"), copolymers of
ethylene glycol and propylene glycol and the like], poly(olefinic
alcohol), poly(vinyl pyrrolidone),
poly(hydroxyalkylmethacrylamide), poly(hydroxyalkylmethacrylate),
poly(saccharides), poly(.alpha.-hydroxy acid), poly(vinyl alcohol),
polyphosphazene, polyoxazoline, poly(oxyethylated polyol), and
poly(N-acryloylmorpholine) such as described in U.S. Pat. No.
5,629,384. The polymer segments can be homopolymers of any of the
foregoing polymers, random copolymers, block copolymers,
alternating copolymers, random tripolymers, block tripolymers,
alternating tripolymers and the like. In addition, a water-soluble
polymer segment is often linear, but can be in other forms (e.g.,
branched, forked, and the like) as will be described in further
detail below. In the context of being present within an overall
structure, a water-soluble polymer segment has from 1 to about 300
termini.
[0075] Each water-soluble polymer segment in the overall structure
can be the same or different. It is preferred, however, that all
water-soluble polymer segments in the overall structure are of the
same type. For example, it is preferred that all of the
water-soluble polymer segments within a given structure are
poly(ethylene glycol).
[0076] Although the number average molecular weight and weight
average molecular weight of any individual water-soluble polymer
segment can vary, both molecular weight values will typically be in
one or more of the following ranges: from about 100 Daltons to
about 100,000 Daltons; from about 500 Daltons to about 80,000
Daltons; from about 1,000 Daltons to about 50,000 Daltons; from
about 2,000 Daltons to about 25,000 Daltons; from about 5,000
Daltons to about 20,000 Daltons. Exemplary number average molecular
weights and weight average molecular weights for the water-soluble
polymer segment include about 1,000 Daltons, about 5,000 Daltons,
about 10,000 Daltons, about 15,000 Daltons, about 20,000 Daltons,
about 25,000 Daltons, and about 30,000 Daltons.
[0077] Each water-soluble polymer segment is typically
biocompatible and non-immunogenic. With respect to
biocompatibility, a substance is considered biocompatible if the
beneficial effects associated with use of the substance alone or
with another substance (e.g., an active agent) in connection with
living tissues (e.g., administration to a patient) outweighs any
deleterious effects as evaluated by a clinician, e.g., a physician.
With respect to non-immunogenicity, a substance is considered
non-immunogenic if use of the substance alone or with another
substance in connection with living tissues does not produce an
immune response (e.g., the formation of antibodies) or, if an
immune response is produced, that such a response is not deemed
clinically significant or important as evaluated by a clinician. It
is particularly preferred that the polymers and water-soluble
polymer segments, described herein as well as conjugates of active
agents and the polymers are biocompatible and non-immunogenic.
[0078] In one form useful in the present invention, free or
nonbound PEG is a linear polymer terminated at each end with
hydroxyl groups:
HO--CH.sub.2CH.sub.2O--(CH.sub.2CH.sub.2O).sub.m'--CH.sub.2CH.sub.2--OH
wherein (m') typically ranges from zero to about 4,000, preferably
from about 20 to about 1,000.
[0079] The above polymer, alpha-,omega-dihydroxylpoly(ethylene
glycol), can be represented in brief form as HO-PEG-OH where it is
understood that the -PEG- symbol represents the following
structural unit:
--CH.sub.2CH.sub.2O--(CH.sub.2CH.sub.2O).sub.m'--CH.sub.2CH.sub.2--
where (m') is as defined above.
[0080] Another type of free or nonbound PEG useful in the present
invention is methoxy-PEG-OH, or MPEG in brief, in which one
terminus is the relatively inert methoxy group, while the other
terminus is a hydroxyl group. The structure of MPEG is given
below.
CH.sub.3O--CH.sub.2CH.sub.2O--(CH.sub.2CH.sub.2O).sub.m'--CH.sub.2CH.sub-
.2--OH
where (m') is as described above.
[0081] Multi-armed or branched PEG molecules, such as those
described in U.S. Pat. No. 5,932,462, can also be used as the PEG
polymer. For example, PEG can have the structure:
##STR00009##
wherein:
[0082] poly.sub.a and poly.sub.b are PEG backbones (either the same
or different), such as methoxy poly(ethylene glycol);
[0083] R'' is a nonreactive moiety, such as H, methyl or a PEG
backbone; and
[0084] P and Q are nonreactive linkages. In a preferred embodiment,
the branched PEG polymer is methoxy poly(ethylene glycol)
disubstituted lysine.
[0085] In addition, the PEG can comprise a forked PEG. An example
of a free or nonbound forked PEG is represented by the following
structure:
##STR00010##
[0086] wherein: X is a spacer moiety and each Z is an activated
terminal group linked to CH by a chain of atoms of defined length.
U.S. Pat. No. 6,362,254 discloses various forked PEG structures
capable of use in the present invention. The chain of atoms linking
the Z functional groups to the branching carbon atom serve as a
tethering group and may comprise, for example, alkyl chains, ether
chains, ester chains, amide chains and combinations thereof.
[0087] The PEG polymer may comprise a pendant PEG molecule having
reactive groups, such as carboxyl, covalently attached along the
length of the PEG rather than at the end of the PEG chain. The
pendant reactive groups can be attached to the PEG directly or
through a spacer moiety, such as an alkylene group.
[0088] In addition to the above-described forms of PEG, the polymer
can also be prepared with one or more weak or degradable linkages
in the polymer, including any of the above described polymers. For
example, PEG can be prepared with ester linkages in the polymer
that are subject to hydrolysis. As shown below, this hydrolysis
results in cleavage of the polymer into fragments of lower
molecular weight:
-PEG-CO.sub.2-PEG-+H.sub.2O.fwdarw.-PEG-CO.sub.2H+HO-PEG-
[0089] Other hydrolytically degradable linkages, useful as a
degradable linkage within a polymer backbone, include carbonate
linkages; imine linkages resulting, for example, from reaction of
an amine and an aldehyde (see, e.g., Ouchi et al. (1997) Polymer
Preprints 38(1):582-3); phosphate ester linkages formed, for
example, by reacting an alcohol with a phosphate group; hydrazone
linkages which are typically formed by reaction of a hydrazide and
an aldehyde; acetal linkages that are typically formed by reaction
between an aldehyde and an alcohol; ortho ester linkages that are,
for example, formed by reaction between a formate and an alcohol;
amide linkages formed by an amine group, e.g., at an end of a
polymer such as PEG, and a carboxyl group of another PEG chain;
urethane linkages formed from reaction of, e.g., a PEG with a
terminal isocyanate group and a PEG alcohol; and oligonucleotide
linkages formed by, for example, a phosphoramidite group, e.g., at
the end of a polymer, and a 5' hydroxyl group of an
oligonucleotide.
[0090] It is understood by those of ordinary skill in the art that
the term poly(ethylene glycol) or PEG represents or includes all
the above forms of PEG.
[0091] Those of ordinary skill in the art will recognize that the
foregoing discussion concerning substantially water-soluble
polymers is by no means exhaustive and is merely illustrative, and
that all polymeric materials having the qualities described above
are contemplated. As used herein, the "term water-soluble polymer"
generally refers to an entire molecule, which can comprise
functional groups such as hydroxyl groups, thiol groups, ortho
ester functionalities and so forth. The term water-soluble polymer
segment is generally reserved for use in discussing specific
molecular structures wherein the polymer is but one part of the
overall molecular structure.
[0092] As depicted in the above formula, each water-soluble polymer
segment is optionally attached to the rest of the structure through
a spacer moiety. A spacer moiety is any atom or series of atoms
connecting one part of a molecule to another. For purposes of the
present disclosure, however, a series of atoms is not a spacer
moiety when the series of atoms is immediately adjacent to a
polymer and the series of atoms is but another monomer or oligomer
such that the proposed spacer moiety would represent a mere
extension of the polymer chain. For example, given the partial
structure "POLY-X--," and POLY is defined as
"CH.sub.3O(CH.sub.2CH.sub.2O).sub.m--" wherein (m) is 2 to 4000 and
X is defined as a spacer moiety, the spacer moiety cannot be
defined as "--CH.sub.2CH.sub.2O--" since such a definition would
merely represent an extension of the polymer. In such a case,
however, an acceptable spacer moiety could be defined as
"--CH.sub.2CH.sub.2--."
[0093] Each spacer moiety described herein, such as X.sub.1 and
X.sub.2, is preferably: a bivalent cycloalkyl group comprising 3 to
about 20 carbon atoms; an amino acid; a C1-C10 alkylene group;
--(CH.sub.2).sub.o--Y--(CH.sub.2).sub.p-- wherein o and p are each
independently zero to about 10 and Y is selected from the group
consisting of --O--, --S--, --C(O)--, --C(S)--, --C(O)--O--,
--C(O)--NH--, --NH--C(O)--NH--, --O--C(O)--NH--, and --N(R.sub.6)--
wherein R.sub.6 is H or an organic radical selected from the group
consisting of alkyl, substituted alkyl, alkenyl, substituted
alkenyl, alkynyl, substituted alkynyl, aryl and substituted aryl;
and any combinations of two or more of the above-described spacer
moieties. Additionally, any of the above spacer moieties may
further include an ethylene oxide oligomer chain comprising 1 to 20
ethylene oxide monomer units, although as noted above, the oligomer
chain would not be considered part of the spacer moiety if the
oligomer is adjacent to a polymer segment and merely represents and
extension of the polymer segment. Particularly preferred examples
of spacer moieties include, but are not limited to, --C(O)--,
--C(O)--NH--, --NH--C(O)--NH--, --O--C(O)--NH--, --C(S)--,
--CH.sub.2--, --CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--, --O--CH.sub.2--,
--CH.sub.2--O--, --O--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--, --CH.sub.2--CH.sub.2--O--,
--O--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--O--,
--O--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--O--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--O--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--O--,
--C(O)--NH--CH.sub.2--, --C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--, --CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--,
--C(O)--O--CH.sub.2--, --CH.sub.2--C(O)--O--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--O--CH.sub.2--,
--C(O)--O--CH.sub.2--CH.sub.2--, --NH--C(O)--CH.sub.2--,
--CH.sub.2--NH--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--NH--C(O)--CH.sub.2--,
--NH--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--NH--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--NH--C(O)--CH.sub.2--CH.sub.2--,
--C(O)--NH--CH.sub.2--, --C(O)--NH--CH.sub.2--CH.sub.2--,
--O--C(O)--NH--CH.sub.2--, --O--C(O)--NH--CH.sub.2--CH.sub.2--,
--NH--CH.sub.2--, --NH--CH.sub.2--CH.sub.2--,
--CH.sub.2--NH--CH.sub.2--, --CH.sub.2--CH.sub.2--NH--CH.sub.2--,
--C(O)--CH.sub.2--, --C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--CH.sub.2--CH.sub.2--,
--CH.sub.2--CH.sub.2--C(O)--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--C(O)--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--NH--C(O)--C-
H.sub.2--,
--CH.sub.2--CH.sub.2--CH.sub.2--C(O)--NH--CH.sub.2--CH.sub.2--N-
H--C(O)--CH.sub.2--CH.sub.2--,
--O--C(O)--NH--(CH.sub.2).sub.h--(OCH.sub.2CH.sub.2).sub.j--,
--NH--C(O)--O--(CH.sub.2).sub.h--(OCH.sub.2CH.sub.2).sub.j--,
--O--, --S--, --N(R.sub.6)--, and combinations of two or more of
any of the foregoing, wherein (h) is zero to six, and (j) is zero
to 20. Other specific spacer moieties have the following
structures: --C(O)--NH--(CH.sub.2).sub.1-6--NH--C(O)--,
--NH--C(O)--NH--(CH.sub.2).sub.1-6--NH--C(O)--, and
--O--C(O)--NH--(CH.sub.2).sub.1-6--NH--C(O)--, wherein the
subscript values following each methylene indicate the number of
methylenes contained in the structure, e.g., (CH.sub.2).sub.1-6
means that the structure can contain 1, 2, 3, 4, 5 or 6 methylenes.
Additionally, any of the above spacer moieties may further include
an ethylene oxide oligomer chain comprising 1 to 20 ethylene oxide
monomer units, although as noted above, the oligomer chain would
not be considered part of the spacer moiety if the oligomer is
adjacent to a polymer segment and merely represents and extension
of the polymer segment.
[0094] In the present context of an amino acid being included in
the structures provided herein, it should be remembered that the
amino acid is connected to the rest of the structure via one, two,
three or more sites. For example, a spacer moiety can result when
an amino acid is attached to the rest of the molecule via two
covalent attachments. In addition, a branching structure can result
when an amino acid is attached to the rest of the molecule via
three sites. Thus, the amino acid structure necessarily changes
somewhat due to the presence of one or more covalent attachments
(e.g., removal of a hydrogen atom from the amino acid in order to
accommodate a covalent linkage). Consequently, reference to an
"amino acid" therefore includes the amino acid containing one or
more linkages to other atoms. The amino acid can be selected from
the group consisting of alanine, arginine, asparagines, aspartic
acid, cysteine, glutamic acid, glutamine, glycine, histidine,
isoleucine, leucine, lysine, methionine, phenylalanine, proline,
serine, threonine, tryptophan, tyrosine, and valine. Both the D and
L forms of the amino acids are contemplated.
[0095] Each spacer moiety, when present, in the overall structure
can be the same or different than any other spacer moiety in the
overall structure. With respect to X.sub.1 and X.sub.2, it is
preferred that X.sub.1 and X.sub.2 are the same when both are
present in the polymer. As depicted in the formula, the linking
moiety "X.sub.1" is present when (a) is defined as one and absent
when (a) is defined as zero. Similarly, the linking moiety
"X.sub.2" is present when (b) is defined as one and absent when (b)
is defined as zero. Preferred spacer moieties corresponding to
X.sub.1 and/or X.sub.2 include --CH.sub.2--, --CH.sub.2CH.sub.2--,
and --CH.sub.2CH.sub.2CH.sub.2--.
[0096] In embodiments of the polymer of the invention where the
linking nitrogen atom is not covalently attached to a reactive
group, the polymer typically has the following structure:
##STR00011##
[0097] wherein POLY.sub.1, POLY.sub.2, (a), (b), X.sub.1 (when
present), and X.sub.2 (when present) are as previously defined.
[0098] In embodiments of the polymer of the invention that further
comprise a reactive group, the polymer will typically comprise the
following structure:
##STR00012##
wherein:
[0099] POLY.sub.1, POLY.sub.2, (a), (b), X.sub.1 (when present),
and X.sub.2 (when present) are as previously defined;
[0100] X.sup.3, when present, is a third spacer moiety;
[0101] (c) is either zero or one; and
[0102] Z is a reactive group.
[0103] The third spacer moiety, X.sub.3, when present, can be any
atom or series of atoms connecting one part of a molecule to
another. Although the third spacer moiety is typically different
from the first and/or second spacer moieties (when present), the
third spacer moiety can be the same as another spacer moiety
present in the polymer. The third spacer moiety can be selected
from one of the group of spacer moieties provided above with
respect to first and second spacer moieties. The third spacer
moiety is absent when (c) is defined as zero and is present when
(c) is defined as one.
[0104] A preferred polymer of the invention wherein each of
POLY.sub.1 and POLY.sub.2 is defined as an MPEG has the
structure:
##STR00013##
[0105] wherein each (a), (b), (c), X.sub.1 (when present), X.sub.2
(when present), X.sub.3 (when present), and Z are as previously
defined, and each m is from 2 to about 4000. PEG versions other
than those that are end-capped with methoxy (e.g., end-capped with
a hydroxyl or other alkoxy such as benzyloxy) are also
envisioned.
[0106] In one preferred embodiment of the structure of Formula
(III), each of (a) and (b) are defined as zero, resulting in a
polymer comprising the following structure:
##STR00014##
[0107] wherein each of (m), (c), X.sub.3 (when present), and Z are
as previously defined. Again, PEGs having end-capping groups other
than methoxy can be used.
[0108] As noted, the polymer may comprise a reactive moiety
designated as "Z" throughout the formulae. Preferred reactive
moieties are selected from the group of electrophiles and
nucleophiles. Exemplary reactive groups include hydroxyl (--OH),
ester, orthoester, carbonate, acetal, aldehyde, aldehyde hydrate,
ketone, vinyl ketone, ketone hydrate, thione, thione hydrate,
hemiketal, sulfur-substituted hemiketal, ketal, alkenyl, acrylate,
methacrylate, acrylamide, sulfone, amine, hydrazide, thiol,
disulfide, thiol hydrate, carboxylic acid, isocyanate,
isothiocyanate, maleimide
##STR00015##
succinimide
##STR00016##
benzotriazole
##STR00017##
vinylsulfone, chloroethylsulfone, dithiopyridine, vinylpyridine,
iodoacetamide, epoxide, glyoxals, diones, mesylates, tosylates,
thiosulfonate, tresylate, and silane. Specific examples of
preferred reactive groups include amine, carboxylic acid, ester,
aldehyde, acetal, succinimide, and maleimide.
[0109] Illustrative examples of X.sub.3 and Z combinations
include
##STR00018##
wherein r is 1-5, r' is 0-5, and R.sub.7 is aryl or alkyl.
[0110] Thus, the polymers of the invention comprise many forms.
Exemplary versions of the polymers of the present invention include
the following:
##STR00019## ##STR00020## ##STR00021## ##STR00022##
wherein each (m) is as previously defined and R is an organic
group, preferably C1-C6 alkyl. Again, PEGs having end-capping
groups other than methoxy can be used.
[0111] The polymers of the invention can be prepared by one of
ordinary skill in the art based upon reading the present
disclosure. Further, the polymers of the invention can be prepared
in any number of ways. Consequently, the polymers provided herein
are not limited to the specific technique or approach used in their
preparation. Preferred approaches, however, will be discussed in
detail below.
[0112] In one approach for providing the polymers of the invention,
the two polymer segments are linked to the imide group prior to
attachment of a reactive group to the linking nitrogen atom. In
this embodiment, the method comprises the steps of (i) providing a
first water-soluble polymer segment carrying a first reactive group
that comprises a carbonyl group (C.dbd.O), (ii) reacting the first
water-soluble polymer segment with anhydrous ammonia to form a
water-soluble polymer intermediate carrying a terminal
--C(O)--NH.sub.2 group, (iii) treating the water-soluble polymer
intermediate with a strong base to remove a proton from the
terminal --C(O)--NH.sub.2 group, (iv) reacting the water-soluble
polymer intermediate with a second water-soluble polymer segment
carrying a second reactive group comprising a carbonyl group to
form a water-soluble polymer of the invention. As previously
stated, the water-soluble polymer of the invention comprises (i) an
imide group comprising a linking nitrogen atom, a first carbonyl
group covalently attached to the linking nitrogen atom, and a
second carbonyl group covalently attached to the linking nitrogen
atom; (ii) a first water-soluble polymer segment covalently
attached, either directly or through one or more atoms, to the
first carbonyl group of the imide group; and (iii) a second
water-soluble polymer segment covalently attached, either directly
or through one or more atoms, to the second carbonyl group of the
imide group. Optionally, the method further comprises the step of
attaching a reactive group to the linking nitrogen atom of the
imide-linked water-soluble polymer.
[0113] In the method described immediately above, a protected or
derivatized form of ammonia optionally can be used in place of
anhydrous ammonia. When such a protected or derivatized form of
ammonia is used, however, the method further includes performing a
deprotecting or de-derivatizing step prior to carrying out any
further synthetic steps.
[0114] In one embodiment, the first and second carbonyl-containing
reactive groups carried by the water-soluble polymer segments,
which may be the same or different, are each carbonate-containing
reactive groups having the structure --O--C(O)--O--X.sub.r, wherein
X.sub.r is aryl, substituted aryl, heteroaryl, substituted
heteroaryl, heterocycle, or substituted heterocycle. Exemplary
X.sub.r moieties include 1-benzotriazolyl, o-, m-, or
p-nitrophenyl, and N-succinimidyl.
[0115] Preferred water-soluble polymer segments carrying a reactive
group that comprises a carbonyl group (C.dbd.O) include MPEG
terminating in benzotriazole carbonate ("mPEG-BTC"), MPEG
terminating in the succinimidyl ester of propionic acid
("mPEG-SPA"), mPEG terminating in the succinimidyl ester of
butanoic acid ("mPEG-SBA"), mPEG terminating in a thioester
("mPEG-OPTE"), and mPEG terminating in a double ester
("mPEG-CM-HBA-NHS"). Each of these polymers is available from
Nektar Therapeutics (Huntsville, Ala.).
[0116] As noted, the method may include the step of attaching a
reactive group, which is preferably accomplished by treating the
imide-linked water-soluble polymer [from step (iv), above] with a
strong base to remove a proton from the linking nitrogen atom and
reacting the imide-linked water-soluble polymer with a molecule
having the structure Z-(X.sub.3).sub.c-Q, wherein Z is a reactive
group, (c) is either zero or one, X.sub.3, when present, is a
spacer moiety, and Q is a leaving group. Note that X, (c), and
X.sub.3 and correspond to the moieties carrying the same
designation in Formulas (II)-(IV) above. Exemplary leaving groups
include halo and sulfonate esters. Among halo moieties, bromo,
chloro, and iodo are preferred, with bromo and chloro being
particularly preferred. With respect to sulfonate esters,
methanesulfonate (abbreviated "Ms"), trifluoromethanesulfonate,
trichloromethanesulfonate, 2,2,2-trifluoroethanesulfonate,
2,2,2-trichloroethanesulfonate, nonafluorobutanesulfonate,
p-bromobenzenesulfonate, p-nitrobenzenesulfonate, and
p-toluenesulfonate are particularly preferred, although other
sulfonate esters and similarly constituted leaving groups known to
those of ordinary skill in the art can be used as well. The
presence of the leaving group allows the linking nitrogen atom to
react with the molecule in a nucleophilic substitution reaction,
resulting in covalent attachment of the Z reactive group (along
with the X.sub.3 spacer when present) to the imide-linked
polymer.
[0117] An exemplary reaction scheme utilizing the above-described
method is shown below as Reaction Scheme I. As shown, an MPEG
molecule carrying a benzotriazolyl carbonate reactive group is
reacted with anhydrous ammonia to form a polymer intermediate
carrying a terminal --C(O)--NH.sub.2 group. A proton is removed
from the terminal --C(O)--NH.sub.2 group using a strong base and a
second polymer segment carrying a benzotriazolyl carbonate reactive
group is reacted with the polymer intermediate to form an
imide-linked polymer. Following a second treatment with a strong
base, a reactive group is attached to the linking nitrogen atom. In
this case, the terminal reactive group is an ortho ester that can
be readily converted by hydrolysis to the corresponding carboxylic
acid. The specific reactive groups and polymer segments used in
this reaction scheme could be changed without departing from the
invention as explained above.
##STR00023##
[0118] In another approach for providing polymers of the invention,
a reactive group is attached to a first polymer segment prior to
attaching the second polymer segment to form the imide-linked
polymer.
[0119] In this embodiment, the method comprises: (i) providing a
first water-soluble polymer segment carrying a first reactive
group, the first reactive group comprising a carbonyl group, (ii)
reacting the first water-soluble polymer segment with a molecule
comprising a second reactive group and an amine group, optionally
separated by a spacer moiety, to form a water-soluble polymer
intermediate comprising a --C(O)--NH-- linkage between the
water-soluble polymer segment and the second reactive group, (iii)
treating the water-soluble polymer intermediate with a strong base
to remove a proton from the nitrogen atom of the --C(O)--NH--
linkage, and (iv) reacting the water-soluble polymer intermediate
with a second water-soluble polymer segment carrying a third
reactive group comprising a carbonyl group to form an imide-linked
water-soluble polymer, the imide linking group comprising a linking
nitrogen atom, a first carbonyl group covalently attached to the
linking nitrogen atom, and a second carbonyl group covalently
attached to the linking nitrogen atom.
[0120] Preferably, the molecule comprising a second reactive group
and an amine group has the structure Z-(X.sub.3).sub.c--NH.sub.2,
wherein Z is the second reactive group, (c) is either zero or one,
and X.sub.3, when present, is a spacer moiety. Note that X, (c),
and X.sub.3 and correspond to the moieties carrying the same
designation in Formulas (II)-(IV) above.
[0121] An exemplary reaction scheme utilizing the above-described
method is shown below as Reaction Scheme II. As shown, an MPEG
molecule having a terminal benzotriazolyl carbonate group is
reacted with a molecule carrying a terminal amine group and a
second reactive group, which in this case is an acetal group where
R is an organic radical such as alkyl. The resulting polymer is
treated with a strong base and reacted with a second benzotriazolyl
carbonate terminated mPEG to form an imide-linked polymer carrying
an acetal group. The acetal group can then be derivatized as
desired, such as by hydrolysis to form the corresponding
aldehyde.
##STR00024##
[0122] The strong base used in the methods described above can be
any strong base known in the art. Preferably, the base is an alkali
metal hydroxide or alkali metal hydride (e.g., NaOH or NaH).
[0123] For any given polymer, the methods described above
advantageously provide the ability to further transform the polymer
(either prior or subsequent to any deprotection step) so that it
bears a specific reactive group. Thus, using techniques well known
in the art, the polymer can be functionalized to include a reactive
group (e.g., active ester, thiol, maleimide, aldehyde, ketone, and
so forth).
[0124] For example, when the polymer bears a carboxylic acid as the
reactive group, the corresponding ester can be formed using
conventional techniques. For example, the carboxylic acid can
undergo acid-catalyzed condensation with an alcohol, thereby
providing the corresponding ester. One approach to accomplish this
is to use the method commonly referred to as a Fischer
esterification reaction. Other techniques for forming a desired
ester are known by those of ordinary skill in the art.
[0125] In addition, polymers bearing a carboxylic acid can be
modified to form useful reactive groups other than esters. For
example, the carboxylic acid can be further derivatized to form
acyl halides, acyl pseudohalides, such as acyl cyanide, acyl
isocyanate, and acyl azide, neutral salts, such as alkali metal or
alkaline-earth metal salts (e.g. calcium, sodium, and barium
salts), esters, anhydrides, amides, imides, hydrazides, and the
like. In a preferred embodiment, the carboxylic acid is esterified
to form an N-succinimidyl ester, o-, m-, or p-nitrophenyl ester,
1-benzotriazolyl ester, imidazolyl ester, or N-sulfosuccinimidyl
ester. For example, the carboxylic acid can be converted into the
corresponding N-succinimidyl ester by reacting the carboxylic acid
with dicyclohexyl carbodiimide (DCC) or diisopropyl carbodiimide
(DIC) in the presence of a N-hydroxysuccinimide.
[0126] The steps of the synthesis methods described above take
place in an appropriate solvent. One of ordinary skill in the art
can determine whether any specific solvent is appropriate for any
given reaction. Typically, however, the solvent is a nonpolar
solvent or a polar aprotic solvent. Nonlimiting examples of
nonpolar solvents include benzene, xylene, dioxane, tetrahydrofuran
(THF), and toluene. Exemplary polar aprotic solvents include, but
are not limited to, acetonitrile, DMSO (dimethyl sulfoxide), HMPA
(hexamethylphosphoramide), DMF (dimethylformamide), DMA
(dimethylacetamide), and NMP (N-methylpyrrolidinone).
[0127] The method of preparing the polymers optionally comprises an
additional step of isolating and recovering the polymer once it is
formed. Known methods can be used to isolate the polymer, but it is
particularly preferred to use chromatography, e.g., size exclusion
chromatography. Alternately or in addition, the method includes the
step of purifying the polymer once it is formed. Again, standard
art-known purification methods can be used to purify the
polymer.
[0128] The polymers of the invention can be stored under an inert
atmosphere, such as under argon or under nitrogen. In this way,
potentially degradative processes associated with, for example,
atmospheric oxygen, are reduced or avoided entirely. In some cases,
to avoid oxidative degradation, antioxidants, such as butylated
hydroxyl toluene (BHT), can be added to the final product prior to
storage. In addition, it is preferred to minimize the amount of
moisture associated with the storage conditions to reduce
potentially damaging reactions associated with water. Moreover, it
is preferred to keep the storage conditions dark in order to
prevent certain degradative processes that involve light. Thus,
preferred storage conditions include one or more of the following:
storage under dry argon or another dry inert gas; storage at
temperatures below about -15.degree. C.; storage in the absence of
light; and storage with a suitable amount (e.g., about 50 to about
500 parts per million) of an antioxidant such as BHT.
[0129] The above-described polymers are useful for conjugation to
biologically active agents or surfaces comprising at least one
group suitable for reaction with the reactive group on the polymer.
For example, amino groups (e.g., primary amines), hydrazines,
hydrazides, and alcohols on an active agent or surface will react
with a carboxylic acid group on the polymer. In addition, a more
"activated" version of the carboxylic acid of the polymer can be
prepared in order to enhance reactivity to the biologically active
agent or surface. Methods for activating carboxylic acids are known
in the art and include, for example, the method for forming an
active ester described above. Other approaches for activating a
carboxylic acid are known to those of ordinary skill in the
art.
[0130] A conjugate of the invention comprises: (i) an imide group
comprising a linking nitrogen atom, a first carbonyl group
covalently attached to the linking nitrogen atom, and a second
carbonyl group covalently attached to the linking nitrogen atom;
(ii) a first water-soluble polymer segment covalently attached,
either directly or through one or more atoms, to the first carbonyl
group of the imide group; (iii) a second water-soluble polymer
segment covalently attached, either directly or through one or more
atoms, to the second carbonyl group of the imide group; and (iv) a
pharmacologically active agent covalently attached, either directly
or through one or more atoms, to the linking nitrogen atom.
[0131] In one embodiment, the conjugate of the invention has the
structure:
##STR00025##
[0132] wherein POLY.sub.1, POLY.sub.2, (a), (b), (c), X.sub.1 (when
present), X.sub.2 (when present), and X.sub.3 (when present) are as
defined above, and "Active agent" represents a residue of a
pharmacologically active agent.
[0133] Typically, the polymer is added to the active agent or
surface at an equimolar amount (with respect to the desired number
of groups suitable for reaction with the reactive group) or at a
molar excess. For example, the polymer can be added to the target
active agent at a molar ratio of about 1:1 (polymer:active agent),
1.5:1, 2:1, 3:1, 4:1, 5:1, 6:1, 8:1, or 10:1. The conjugation
reaction is allowed to proceed until substantially no further
conjugation occurs, which can generally be determined by monitoring
the progress of the reaction over time. Progress of the reaction
can be monitored by withdrawing aliquots from the reaction mixture
at various time points and analyzing the reaction mixture by
SDS-PAGE or MALDI-TOF mass spectrometry or any other suitable
analytical method. Once a plateau is reached with respect to the
amount of conjugate formed or the amount of unconjugated polymer
remaining, the reaction is assumed to be complete. Typically, the
conjugation reaction takes anywhere from minutes to several hours
(e.g., from 5 minutes to 24 hours or more). The resulting product
mixture is preferably, but not necessarily, purified to separate
out excess reagents, unconjugated reactants (e.g., active agent),
undesired multi-conjugated species, and free or unreacted polymer.
The resulting conjugates can then be further characterized using
analytical methods such as MALDI, capillary electrophoresis, gel
electrophoresis, and/or chromatography.
[0134] With respect to polymer-active agent conjugates, the
conjugates can be purified to obtain/isolate different conjugated
species. Alternatively, and more preferably for lower molecular
weight (e.g., less than about 20 kiloDaltons, more preferably less
than about 10 kiloDaltons) polymers, the product mixture can be
purified to obtain the distribution of water-soluble polymer
segments per active agent. For example, the product mixture can be
purified to obtain an average of anywhere from one to five PEGs per
active agent (e.g., protein), typically an average of about three
PEGs per active agent (e.g., protein). The strategy for
purification of the final conjugate reaction mixture will depend
upon a number of factors, including, for example, the molecular
weight of the polymer employed, the particular active agent, the
desired dosing regimen, and the residual activity and in vivo
properties of the individual conjugate(s).
[0135] If desired, conjugates having different molecular weights
can be isolated using gel filtration chromatography. That is to
say, gel filtration chromatography is used to fractionate
differently numbered polymer-to-active agent ratios (e.g., 1-mer,
2-mer, 3-mer, and so forth, wherein "1-mer" indicates 1 polymer to
active agent, "2-mer" indicates two polymers to active agent, and
so on) on the basis of their differing molecular weights (where the
difference corresponds essentially to the average molecular weight
of the water-soluble polymer segments). For example, in an
exemplary reaction where a 100 kDa protein is randomly conjugated
to a PEG alkanoic acid having a molecular weight of about 20 kDa,
the resulting reaction mixture will likely contain unmodified
protein (MW 100 kDa), mono-pegylated protein (MW 120 kDa),
di-pegylated protein (MW 140 kDa), and so forth. While this
approach can be used to separate PEG and other polymer conjugates
having different molecular weights, this approach is generally
ineffective for separating positional isomers having different
polymer attachment sites within the protein. For example, gel
filtration chromatography can be used to separate mixtures of PEG
1-mers, 2-mers, 3-mers, and so forth, although each of the
recovered PEG-mer compositions may contain PEGs attached to
different reactive amino groups (e.g., lysine residues) within the
active agent.
[0136] Gel filtration columns suitable for carrying out this type
of separation include Superdex.TM. and Sephadex.TM. columns
available from Amersham Biosciences (Piscataway, N.J.). Selection
of a particular column will depend upon the desired fractionation
range desired. Elution is generally carried out using a suitable
buffer, such as phosphate, acetate, or the like. The collected
fractions may be analyzed by a number of different methods, for
example, (i) optical density (OD) at 280 nm for protein content,
(ii) bovine serum albumin (BSA) protein analysis, (iii) iodine
testing for PEG content [Sims et al. (1980) Anal. Biochem,
107:60-63], and (iv) sodium dodecyl sulfphate polyacrylamide gel
electrophoresis (SDS PAGE), followed by staining with barium
iodide.
[0137] Separation of positional isomers is carried out by reverse
phase chromatography using a reverse phase-high performance liquid
chromatography (RP-HPLC) C18 column (Amersham Biosciences or Vydac)
or by ion exchange chromatography using an ion exchange column,
e.g., a Sepharose.TM. ion exchange column available from Amersham
Biosciences. Either approach can be used to separate polymer-active
agent isomers having the same molecular weight (positional
isomers).
[0138] Following conjugation, and optionally additional separation
steps, the conjugate mixture can be concentrated, sterile filtered,
and stored at low a temperature, typically from about -20.degree.
C. to about -80.degree. C. Alternatively, the conjugate may be
lyophilized, either with or without residual buffer and stored as a
lyophilized powder. In some instances, it is preferable to exchange
a buffer used for conjugation, such as sodium acetate, for a
volatile buffer such as ammonium carbonate or ammonium acetate,
that can be readily removed during lyophilization, so that the
lyophilized powder is absent residual buffer. Alternatively, a
buffer exchange step may be used using a formulation buffer, so
that the lyophilized conjugate is in a form suitable for
reconstitution into a formulation buffer and ultimately for
administration to a mammal.
[0139] The polymers of the invention can be attached, either
covalently or noncovalently, to a number of entities including
films, chemical separation and purification surfaces, solid
supports, metal surfaces such as gold, titanium, tantalum, niobium,
aluminum, steel, and their oxides, silicon oxide, macromolecules
(e.g., proteins, polypeptides, and so forth), and small molecules.
Additionally, the polymers can also be used in biochemical sensors,
bioelectronic switches, and gates. The polymers can also be
employed as carriers for peptide synthesis, for the preparation of
polymer-coated surfaces and polymer grafts, to prepare
polymer-ligand conjugates for affinity partitioning, to prepare
cross-linked or non-cross-linked hydrogels, and to prepare
polymer-cofactor adducts for bioreactors.
[0140] A biologically active agent for use in coupling to a polymer
as presented herein may be any one or more of the following.
Suitable agents can be selected from, for example, hypnotics and
sedatives, psychic energizers, tranquilizers, respiratory drugs,
anticonvulsants, muscle relaxants, antiparkinson agents (dopamine
antagnonists), analgesics, anti-inflammatories, antianxiety drugs
(anxiolytics), appetite suppressants, antimigraine agents, muscle
contractants, anti-infectives (antibiotics, antivirals,
antifungals, vaccines) antiarthritics, antimalarials, antiemetics,
anepileptics, bronchodilators, cytokines, growth factors,
anti-cancer agents, antithrombotic agents, antihypertensives,
cardiovascular drugs, antiarrhythimics, antioxicants, anti-asthma
agents, hormonal agents including contraceptives, sympathomimetics,
diuretics, lipid regulating agents, antiandrogenic agents,
antiparasitics, anticoagulants, neoplastics, antineoplastics,
hypoglycemics, nutritional agents and supplements, growth
supplements, antienteritis agents, vaccines, antibodies, diagnostic
agents, and contrasting agents.
[0141] More particularly, the active agent may fall into one of a
number of structural classes, including but not limited to small
molecules (preferably water insoluble small molecules), peptides,
polypeptides, proteins, polysaccharides, steroids, nucleotides,
oligonucleotides, polynucleotides, fats, electrolytes, and the
like. Preferably, an active agent for coupling to a polymer as
described herein possesses a native amino group, or alternatively,
is modified to contain at least one reactive amino group suitable
for conjugating to a polymer described herein.
[0142] Specific examples of active agents suitable for covalent
attachment include, but are not limited to, aspariginase, amdoxovir
(DAPD), antide, becaplermin, calcitonins, cyanovirin, denileukin
diftitox, erythropoietin (EPO), EPO agonists (e.g., peptides from
about 10-40 amino acids in length and comprising a particular core
sequence as described in WO 96/40749), dornase alpha,
erythropoiesis stimulating protein (NESP), coagulation factors such
as Factor V, Factor VII, Factor VIIa, Factor VIII, Factor IX,
Factor X, Factor XII, Factor XIII, von Willebrand factor; ceredase,
cerezyme, alpha-glucosidase, collagen, cyclosporin, alpha
defensins, beta defensins, exedin-4, granulocyte colony stimulating
factor (GCSF), thrombopoietin (TPO), alpha-1 proteinase inhibitor,
elcatonin, granulocyte macrophage colony stimulating factor
(GMCSF), fibrinogen, filgrastim, growth hormones human growth
hormone (hGH), growth hormone releasing hormone (GHRH), GRO-beta,
GRO-beta antibody, bone morphogenic proteins such as bone
morphogenic protein-2, bone morphogenic protein-6, OP-1; acidic
fibroblast growth factor, basic fibroblast growth factor, CD-40
ligand, heparin, human serum albumin, low molecular weight heparin
(LMWH), interferons such as interferon alpha, interferon beta,
interferon gamma, interferon omega, interferon tau, consensus
interferon; interleukins and interleukin receptors such as
interleukin-1 receptor, interleukin-2, interluekin-2 fusion
proteins, interleukin-1 receptor antagonist, interleukin-3,
interleukin-4, interleukin-4 receptor, interleukin-6,
interleukin-8, interleukin-12, interleukin-13 receptor,
interleukin-17 receptor; lactoferrin and lactoferrin fragments,
luteinizing hormone releasing hormone (FSH), insulin, pro-insulin,
insulin analogues (e.g., mono-acylated insulin as described in U.S.
Pat. No. 5,922,675), amylin, C-peptide, somatostatin, somatostatin
analogs including octreotide, vasopressin, follicle stimulating
hormone (FSH), influenza vaccine, insulin-like growth factor (IGF),
insulintropin, macrophage colony stimulating factor (M-CSF),
plasminogen activators such as alteplase, urokinase, reteplase,
streptokinase, pamiteplase, lanoteplase, and teneteplase; nerve
growth factor (NGF), osteoprotegerin, platelet-derived growth
factor, tissue growth factors, transforming growth factor-1,
vascular endothelial growth factor, leukemia inhibiting factor,
keratinocyte growth factor (KGF), glial growth factor (GGF), T Cell
receptors, CD molecules/antigens, tumor necrosis factor (TNF),
monocyte chemoattractant protein-1, endothelial growth factors,
parathyroid hormone (PTH), glucagon-like peptide, somatotropin,
thymosin alpha 1, rasburicase, thymosin alpha 1 IIb/IIIa inhibitor,
thymosin beta 10, thymosin beta 9, thymosin beta 4, alpha-1
antitrypsin, phosphodiesterase (PDE) compounds, VLA-4 (very late
antigen-4), VLA-4 inhibitors, bisphosphonates, respiratory
syncytial virus antibody, cystic fibrosis transmembrane regulator
(CFTR) gene, deoxyribonuclease (Dnase), bactericidal/permeability
increasing protein (BPI), and anti-CMV antibody. Exemplary
monoclonal antibodies include etanercept (a dimeric fusion protein
consisting of the extracellular ligand-binding portion of the human
75 kD TNF receptor linked to the Fc portion of IgG1), abciximab,
adalimumab, afelimomab, alemtuzumab, antibody to B-lymphocyte
(lymphostat-B.TM.), atlizumab, basiliximab, bevacizumab, biciromab,
CAT-213 or bertilimumab, CDP-571, CDP-870, cetuximab, clenoliximab,
daclizumab, eculizumab, edrecolomab, efalizumab, epratuzumab,
fontolizumab, gavilimomab, gemtuzumab ozogamicin, ibritumomab
tiuxetan, infliximab, inolimomab, keliximab, labetuzumab,
lerdelimumab, radiolabeled lym-1, metelimumab, mepolizumab,
mitumomab, muromonad-CD3, nebacumab, natalizumab, odulimomab,
omalizumab, oregovbmab, palivizumab, pemtumomab, pexelizumab,
rituximab satumomab pendetide, sevirumab, siplizumab, tositumomab
and I.sup.131 tositumomab, olizumab, trastuzumab, tuvirumab, and
visilizumab.
[0143] Additional agents suitable for covalent attachment include,
but are not limited to, adefovir, alosetron, amifostine,
amiodarone, aminocaproic acid, aminohippurate sodium,
aminoglutethimide, aminolevulinic acid, aminosalicylic acid,
amsacrine, anagrelide, anastrozole, aripiprazole, asparaginase,
anthracyclines, bexarotene, bicalutamide, bleomycin, buserelin,
busulfan, cabergoline, capecitabine, carboplatin, carmustine,
chlorambucin, cilastatin sodium, cisplatin, cladribine, clodronate,
cyclophosphamide, cyproterone, cytarabine, camptothecins, 13-cis
retinoic acid, all trans retinoic acid; dacarbazine, dactinomycin,
daunorubicin, deferoxamine, dexamethasone, diclofenac,
diethylstilbestrol, docetaxel, doxorubicin, dutasteride,
epirubicin, estramustine, etoposide, exemestane, ezetimibe,
fexofenadine, fludarabine, fludrocortisone, fluorouracil,
fluoxymesterone, flutamide, fondaparinux, fulvestrant,
gamma-hydroxybutyrate, gemcitabine, epinephrine, L-Dopa,
hydroxyurea, idarubicin, ifosfamide, imatinib, irinotecan,
itraconazole, goserelin, letrozole, leucovorin, levamisole,
lisinopril, lovothyroxine sodium, lomustine, mechlorethamine,
medroxyprogesterone, megestrol, melphalan, mercaptopurine,
metaraminol bitartrate, methotrexate, metoclopramide, mexiletine,
mitomycin, mitotane, mitoxantrone, naloxone, nicotine, nilutamide,
nitisinone, octreotide, oxaliplatin, pamidronate, pentostatin,
pilcamycin, porfimer, prednisone, procarbazine, prochlorperazine,
ondansetron, oxaliplatin, raltitrexed, sirolimus, streptozocin,
tacrolimus, pimecrolimus, tamoxifen, tegaserod, temozolomide,
teniposide, testosterone, tetrahydrocannabinol, thalidomide,
thioguanine, thiotepa, topotecan, treprostinil, tretinoin,
valdecoxib, celecoxib, rofecoxib, valrubicin, vinblastine,
vincristine, vindesine, vinorelbine, voriconazole, dolasetron,
granisetron; formoterol, fluticasone, leuprolide, midazolam,
alprazolam, amphotericin B, podophylotoxins, nucleoside antivirals,
aroyl hydrazones, sumatriptan; macrolides such as erythromycin,
oleandomycin, troleandomycin, roxithromycin, clarithromycin,
davercin, azithromycin, flurithromycin, dirithromycin, josamycin,
spiromycin, midecamycin, loratadine, desloratadine, leucomycin,
miocamycin, rokitamycin, andazithromycin, and swinolide A;
fluoroquinolones such as ciprofloxacin, ofloxacin, levofloxacin,
trovafloxacin, alatrofloxacin, moxifloxicin, norfloxacin, enoxacin,
grepafloxacin, gatifloxacin, lomefloxacin, sparfioxacin,
temafloxacin, pefloxacin, amifloxacin, fleroxacin, tosufloxacin,
prulifloxacin, irloxacin, pazufloxacin, clinafloxacin, and
sitafloxacin; aminoglycosides such as gentamicin, netilmicin,
paramecin, tobramycin, amikacin, kanamycin, neomycin, and
streptomycin, vancomycin, teicoplanin, rampolanin, mideplanin,
colistin, daptomycin, gramicidin, colistimethate; polymixins such
as polymixin B, capreomycin, bacitracin, penems; penicillins
including penicllinase-sensitive agents like penicillin G,
penicillin V; penicllinase-resistant agents like methicillin,
oxacillin, cloxacillin, dicloxacillin, floxacillin, nafcillin; gram
negative microorganism active agents like ampicillin, amoxicillin,
and hetacillin, cillin, and galampicillin; antipseudomonal
penicillins like carbenicillin, ticarcillin, azlocillin,
mezlocillin, and piperacillin; cephalosporins like cefpodoxime,
cefprozil, ceftbuten, ceftizoxime, ceftriaxone, cephalothin,
cephapirin, cephalexin, cephradrine, cefoxitin, cefamandole,
cefazolin, cephaloridine, cefaclor, cefadroxil, cephaloglycin,
cefuroxime, ceforanide, cefotaxime, cefatrizine, cephacetrile,
cefepime, cefixime, cefonicid, cefoperazone, cefotetan,
cefmetazole, ceftazidime, loracarbef, and moxalactam, monobactams
like aztreonam; and carbapenems such as imipenem, meropenem, and
ertapenem, pentamidine isetionate, albuterol sulfate, lidocaine,
metaproterenol sulfate, beclomethasone diprepionate, triamcinolone
acetamide, budesonide acetonide, fluticasone, ipratropium bromide,
flunisolide, cromolyn sodium, and ergotamine tartrate; taxanes such
as paclitaxel; SN-38, and tyrphostines.
[0144] Preferred small molecules for coupling to a polymer as
described herein are those having at least one naturally occurring
amino group. Preferred molecules such as these include
aminohippurate sodium, amphotericin B, doxorubicin, aminocaproic
acid, aminolevulinic acid, aminosalicylic acid, metaraminol
bitartrate, pamidronate disodium, daunorubicin, levothyroxine
sodium, lisinopril, cilastatin sodium, mexiletine, cephalexin,
deferoxamine, and amifostine.
[0145] Preferred peptides or proteins for coupling to a polymer as
described herein include EPO, IFN-.alpha., IFN-.beta., consensus
IFN, Factor VIII, Factor IX, GCSF, GMCSF, hGH, insulin, FSH, and
PTH.
[0146] The above exemplary biologically active agents are meant to
encompass, where applicable, analogues, agonists, antagonists,
inhibitors, isomers, and pharmaceutically acceptable salt forms
thereof. In reference to peptides and proteins, the invention is
intended to encompass synthetic, recombinant, native, glycosylated,
and non-glycosylated forms, as well as biologically active
fragments thereof.
[0147] The present invention also includes pharmaceutical
preparations comprising a conjugate as provided herein in
combination with a pharmaceutical excipient. Generally, the
conjugate itself will be in a solid form (e.g., a precipitate),
which can be combined with a suitable pharmaceutical excipient that
can be in either solid or liquid form. In one embodiment, the
conjugate is formulated with a liquid diluent, such as
bacteriostatic water for injection, dextrose 5% in water,
phosphate-buffered saline, Ringer's solution, saline solution,
sterile water, deionized water, or combinations thereof.
[0148] Exemplary excipients include, without limitation, those
selected from the group consisting of carbohydrates, inorganic
salts, antimicrobial agents, antioxidants, surfactants, buffers,
acids, bases, and combinations thereof.
[0149] A carbohydrate such as a sugar, a derivatized sugar such as
an alditol, aldonic acid, an esterified sugar, and/or a sugar
polymer may be present as an excipient. Specific carbohydrate
excipients include, for example: monosaccharides, such as fructose,
maltose, galactose, glucose, D-mannose, sorbose, and the like;
disaccharides, such as lactose, sucrose, trehalose, cellobiose, and
the like; polysaccharides, such as raffinose, melezitose,
maltodextrins, dextrans, starches, and the like; and alditols, such
as mannitol, xylitol, maltitol, lactitol, xylitol, sorbitol
(glucitol), pyranosyl sorbitol, myoinositol, and the like.
[0150] The excipient can also include an inorganic salt or buffer
such as citric acid, sodium chloride, potassium chloride, sodium
sulfate, potassium nitrate, sodium phosphate monobasic, sodium
phosphate dibasic, and combinations thereof.
[0151] The preparation may also include an antimicrobial agent for
preventing or deterring microbial growth. Nonlimiting examples of
antimicrobial agents suitable for the present invention include
benzalkonium chloride, benzethonium chloride, benzyl alcohol,
cetylpyridinium chloride, chlorobutanol, phenol, phenylethyl
alcohol, phenylmercuric nitrate, thimersol, and combinations
thereof.
[0152] An antioxidant can be present in the preparation as well.
Antioxidants are used to prevent oxidation, thereby preventing the
deterioration of the conjugate or other components of the
preparation. Suitable antioxidants for use in the present invention
include, for example, ascorbyl palmitate, butylated hydroxyanisole,
butylated hydroxytoluene, hypophosphorous acid, monothioglycerol,
propyl gallate, sodium bisulfite, sodium formaldehyde sulfoxylate,
sodium metabisulfite, and combinations thereof.
[0153] A surfactant may be present as an excipient. Exemplary
surfactants include: polysorbates, such as "Tween 20" and "Tween
80," and pluronics such as F68 and F88 (both of which are available
from BASF, Mount Olive, N.J.); sorbitan esters; lipids, such as
phospholipids such as lecithin and other phosphatidylcholines,
phosphatidylethanolamines (although preferably not in liposomal
form), fatty acids and fatty esters; steroids, such as cholesterol;
and chelating agents, such as EDTA, zinc and other such suitable
cations.
[0154] Acids or bases may be present as an excipient in the
preparation. Nonlimiting examples of acids that can be used include
those acids selected from the group consisting of hydrochloric
acid, acetic acid, phosphoric acid, citric acid, malic acid, lactic
acid, formic acid, trichloroacetic acid, nitric acid, perchloric
acid, phosphoric acid, sulfuric acid, fumaric acid, and
combinations thereof. Examples of suitable bases include, without
limitation, bases selected from the group consisting of sodium
hydroxide, sodium acetate, ammonium hydroxide, potassium hydroxide,
ammonium acetate, potassium acetate, sodium phosphate, potassium
phosphate, sodium citrate, sodium formate, sodium sulfate,
potassium sulfate, potassium fumerate, and combinations
thereof.
[0155] The pharmaceutical preparations encompass all types of
formulations and in particular those that are suited for injection,
e.g., powders that can be reconstituted as well as suspensions and
solutions. For example, the pharmaceutical preparation can be in
the form of a lyophilized cake or powder. The amount of the
conjugate (i.e., the conjugate formed between the active agent and
the polymer described herein) in the composition will vary
depending on a number of factors, but will optimally be a
therapeutically effective dose when the composition is stored in a
unit dose container (e.g., a vial). In addition, the pharmaceutical
preparation can be housed in a syringe. A therapeutically effective
dose can be determined experimentally by repeated administration of
increasing amounts of the conjugate in order to determine which
amount produces a clinically desired endpoint.
[0156] The amount of any individual excipient in the composition
will vary depending on the activity of the excipient and particular
needs of the composition. Typically, the optimal amount of any
individual excipient is determined through routine experimentation,
i.e., by preparing compositions containing varying amounts of the
excipient (ranging from low to high), examining the stability and
other parameters, and then determining the range at which optimal
performance is attained with no significant adverse effects.
[0157] Generally, however, the excipient will be present in the
composition in an amount of about 1% to about 99% by weight,
preferably from about 5%-98% by weight, more preferably from about
15-95% by weight of the excipient, with concentrations less than
30% by weight most preferred.
[0158] These foregoing pharmaceutical excipients along with other
excipients are described in "Remington: The Science & Practice
of Pharmacy", 19.sup.th ed., Williams & Williams, (1995), the
"Physician's Desk Reference", 52.sup.nd ed., Medical Economics,
Montvale, N.J. (1998), and Kibbe, A. H., Handbook of Pharmaceutical
Excipients, 3.sup.rd Edition, American Pharmaceutical Association,
Washington, D.C., 2000.
[0159] The pharmaceutical preparations of the present invention are
typically, although not necessarily, administered via injection and
are therefore generally liquid solutions or suspensions immediately
prior to administration. The pharmaceutical preparation can also
take other forms such as syrups, creams, ointments, tablets,
powders, and the like. Other modes of administration are also
included, such as pulmonary, rectal, transdermal, transmucosal,
oral, intrathecal, subcutaneous, intra-arterial, and so forth.
[0160] As previously described, the conjugates can be administered
injected parenterally by intravenous injection, or less preferably
by intramuscular or by subcutaneous injection. Suitable formulation
types for parenteral administration include ready-for-injection
solutions, dry powders for combination with a solvent prior to use,
suspensions ready for injection, dry insoluble compositions for
combination with a vehicle prior to use, and emulsions and liquid
concentrates for dilution prior to administration, among
others.
[0161] The invention also provides a method for administering a
conjugate as provided herein to a patient suffering from a
condition that is responsive to treatment with conjugate. The
method comprises administering, generally via injection, a
therapeutically effective amount of the conjugate (preferably
provided as part of a pharmaceutical preparation). The method of
administering may be used to treat any condition that can be
remedied or prevented by administration of the particular
conjugate. Those of ordinary skill in the art appreciate which
conditions a specific conjugate can effectively treat. The actual
dose to be administered will vary depend upon the age, weight, and
general condition of the subject as well as the severity of the
condition being treated, the judgment of the health care
professional, and conjugate being administered. Therapeutically
effective amounts are known to those skilled in the art and/or are
described in the pertinent reference texts and literature.
Generally, a therapeutically effective amount will range from about
0.001 mg to 100 mg, preferably in doses from 0.01 mg/day to 75
mg/day, and more preferably in doses from 0.10 mg/day to 50
mg/day.
[0162] The unit dosage of any given conjugate (again, preferably
provided as part of a pharmaceutical preparation) can be
administered in a variety of dosing schedules depending on the
judgment of the clinician, needs of the patient, and so forth. The
specific dosing schedule will be known by those of ordinary skill
in the art or can be determined experimentally using routine
methods. Exemplary dosing schedules include, without limitation,
administration five times a day, four times a day, three times a
day, twice daily, once daily, three times weekly, twice weekly,
once weekly, twice monthly, once monthly, and any combination
thereof. Once the clinical endpoint has been achieved, dosing of
the composition is halted.
[0163] One advantage of administering the conjugates of the present
invention is that individual water-soluble polymer portions can be
cleaved off. Such a result is advantageous when clearance from the
body is potentially a problem because of the polymer size.
Optimally, cleavage of each water-soluble polymer portion is
facilitated through the use of physiologically cleavable and/or
enzymatically degradable linkages such as carbonate or
ester-containing linkages. In this way, clearance of the conjugate
(via cleavage of individual water-soluble polymer portions) can be
modulated by selecting the polymer molecular size and the type
functional group that would provide the desired clearance
properties. One of ordinary skill in the art can determine the
proper molecular size of the polymer as well as the cleavable
functional group. For example, one of ordinary skill in the art,
using routine experimentation, can determine a proper molecular
size and cleavable functional group by first preparing a variety of
polymer derivatives with different polymer weights and cleavable
functional groups, and then obtaining the clearance profile (e.g.,
through periodic blood or urine sampling) by administering the
polymer derivative to a patient and taking periodic blood and/or
urine sampling. Once a series of clearance profiles have been
obtained for each tested conjugate, a suitable conjugate can be
identified.
[0164] It is to be understood that while the invention has been
described in conjunction with the preferred specific embodiments
thereof, that the foregoing description as well as the experimental
that follow are intended to illustrate and not limit the scope of
the invention. Other aspects, advantages and modifications within
the scope of the invention will be apparent to those skilled in the
art to which the invention pertains.
[0165] All articles, books, patents, patent publications and other
publications referenced herein are hereby incorporated by reference
in their entireties.
* * * * *