U.S. patent application number 13/341567 was filed with the patent office on 2012-07-05 for silicon carbide body and method of forming same.
This patent application is currently assigned to SAINT-GOBAIN CERMAICS & PLASTICS, INC.. Invention is credited to Christopher J. Reilly, Yu Zhong.
Application Number | 20120171463 13/341567 |
Document ID | / |
Family ID | 46381017 |
Filed Date | 2012-07-05 |
United States Patent
Application |
20120171463 |
Kind Code |
A1 |
Reilly; Christopher J. ; et
al. |
July 5, 2012 |
SILICON CARBIDE BODY AND METHOD OF FORMING SAME
Abstract
A method of forming a ceramic article including providing a
ceramic body comprising silicon carbide, and treating the ceramic
body in an atmosphere comprising an oxidizing material to remove a
portion of the ceramic body through a chemical reaction between a
portion of the ceramic body and the oxidizing material.
Inventors: |
Reilly; Christopher J.;
(Whitinsville, MA) ; Zhong; Yu; (Shrewsbury,
MA) |
Assignee: |
SAINT-GOBAIN CERMAICS &
PLASTICS, INC.
Worcester
MA
|
Family ID: |
46381017 |
Appl. No.: |
13/341567 |
Filed: |
December 30, 2011 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61428289 |
Dec 30, 2010 |
|
|
|
Current U.S.
Class: |
428/312.6 ;
216/74; 423/324; 428/221 |
Current CPC
Class: |
C04B 2235/3217 20130101;
C04B 2235/405 20130101; C04B 41/5037 20130101; C04B 2235/46
20130101; C04B 41/5037 20130101; C04B 41/87 20130101; C04B 41/5031
20130101; C04B 2235/663 20130101; C04B 41/5022 20130101; Y10T
428/249969 20150401; C04B 2235/658 20130101; C04B 2235/3272
20130101; Y10T 428/249921 20150401; C04B 41/86 20130101; C04B
2235/6586 20130101; C04B 41/009 20130101; C04B 35/6316 20130101;
C04B 35/565 20130101; C04B 41/009 20130101; C04B 2235/428 20130101;
C04B 14/4656 20130101; C04B 35/622 20130101; C04B 2235/3826
20130101; C04B 35/565 20130101; C04B 41/4535 20130101; C04B 41/4535
20130101; C04B 41/4535 20130101; C04B 41/5022 20130101; C04B
41/5031 20130101 |
Class at
Publication: |
428/312.6 ;
423/324; 216/74; 428/221 |
International
Class: |
B32B 3/26 20060101
B32B003/26; B44C 1/22 20060101 B44C001/22; C01B 33/00 20060101
C01B033/00 |
Claims
1. A method of forming a ceramic article comprising: providing a
ceramic body comprising silicon carbide; and treating the ceramic
body in an atmosphere comprising an oxidizing material to remove a
portion of the ceramic body through a chemical reaction between a
portion of the ceramic body and the oxidizing material.
2. The method of claim 1, wherein the oxidizing material comprises
oxygen.
3. The method of claim 1, wherein the oxidizing material comprises
carbon.
4. The method of claim 3, wherein the oxidizing material comprises
carbon dioxide.
5. The method of claim 1, wherein the oxidizing material comprises
a gaseous material.
6. The method of claim 5, wherein treating comprises providing the
oxidizing material into a chamber containing the ceramic body at a
flow rate of at least about 1 standard cubic foot per hour (scfh)
(0.028 cubic meters per hour).
7. The method of claim 6, wherein during treating the oxidizing
material is provided into the chamber at a flow rate of at least
about 2 scfh (0.057 cubic meters per hour).
8. The method of claim 7, wherein during treating the oxidizing
material is provided into the chamber at a flow rate of at least
about 3 scfh (0.085 cubic meters per hour).
9. The method of claim 8, wherein during treating the oxidizing
material is provided into the chamber at a flow rate of at least
about 4 scfh (0.11 cubic meters per hour).
10. The method of claim 6, wherein during treating the oxidizing
material is provided into the chamber at a flow rate of not greater
than about 200 scfh (5.7 cubic meters per hour).
11. The method of claim 1, wherein the oxidizing material comprises
carbon dioxide.
12. The method of claim 11, wherein the oxidizing material consists
essentially of carbon dioxide.
13. The method of claim 1, wherein treating the ceramic body
comprises removing material from an exterior surface of the ceramic
body.
14. The method of claim 1, wherein treating the ceramic body
comprises removing material from pores extending into the ceramic
body.
15. The method of claim 1, wherein treating the ceramic body
comprises removing fibrous material from the ceramic body.
16. The method of claim 1, wherein the chemical reaction includes a
phase transition of the portion of the ceramic body removed.
17. The method of claim 16, wherein the phase transition includes a
change of solid material to gaseous material.
18. The method of claim 1, wherein the chemical reaction includes
oxidation of a portion of the ceramic body by the oxidizing
material to create a reaction product including an oxide
material.
19. The method of claim 18, wherein the oxide material comprises
silicon.
20. The method of claim 19, wherein the oxide material consists
essentially of silicon monoxide.
21. The method of claim 18, wherein the oxide material comprises a
gas.
22. The method of claim 18, wherein the oxide material comprises
carbon.
23. The method of claim 22, wherein the oxide material comprises
carbon monoxide.
24. The method of claim 1, wherein the chemical reaction includes
oxidation of a portion of the ceramic body by the oxidizing
material to create a reaction product including a nitrogen
material.
25. The method of claim 24, wherein the nitrogen material comprises
a gas.
26. The method of claim 25, wherein the nitrogen material consists
essentially of nitrogen gas.
27. The method of claim 1, wherein treating includes operating at a
reaction temperature of at least about 800.degree. C.
28. The method of claim 27, wherein the reaction temperature is at
least about 900.degree. C.
29. The method of claim 28, wherein the reaction temperature is at
least about 950.degree. C.
30. The method of claim 29, wherein the reaction temperature is at
least about 1000.degree. C.
31. The method of claim 1, wherein treating includes operating at a
reaction temperature of not greater than about 2000.degree. C.
32. The method of claim 31, wherein the reaction temperature is not
greater than about 1800.degree. C.
33. The method of claim 32, wherein the reaction temperature is not
greater than about 1500.degree. C.
34. The method of claim 33, wherein the reaction temperature is not
greater than about 1300.degree. C.
35. A method of forming a ceramic article comprising: providing a
ceramic body comprising a fibrous material overlying an exterior
surface of the ceramic body; and treating the ceramic body with a
gaseous reactant material to remove the fibrous material from the
ceramic body through a chemical reaction between the gaseous
reactant material and the fibrous material.
36. The method of claim 35, wherein the gaseous reactant material
comprises an oxidizing material.
37. The method of claim 36, wherein the oxidizing material
comprises carbon dioxide.
38. The method of claim 35, wherein treating comprises providing
the gaseous reactant material into a chamber containing the ceramic
body at a flow rate of at least about 1 standard cubic foot per
hour (scfh) (0.028 cubic meters per hour).
39. The method of claim 35, wherein treating the ceramic body
comprises removing the fibrous material from pores within the
ceramic body.
40. The method of claim 35, wherein the chemical reaction includes
a phase transition of the portion of the fibrous material from a
solid phase material to a gas phase material.
41. The method of claim 35, wherein the chemical reaction includes
oxidation of the fibrous material to form a reaction product
comprising an oxide material.
42. The method of claim 41, wherein the oxide material comprises
silicon monoxide.
43. The method of claim 41, wherein the oxide material comprises
carbon monoxide.
44. The method of claim 35, wherein the chemical reaction includes
oxidation of the fibrous material to form a reaction product
comprising a nitrogen material.
45. The method of claim 44, wherein the nitrogen material consists
essentially of nitrogen gas.
46. The method of claim 35, wherein treating includes operating at
a reaction temperature of at least about 800.degree. C.
47. The method of claim 46, wherein treating includes operating at
a reaction temperature of not greater than about 2000.degree.
C.
48. The method of claim 35, further comprising firing the ceramic
body prior to treating.
49. The method of claim 48, wherein firing is conducted at a firing
temperature of at least about 800.degree. C.
50. The method of claim 49, wherein firing is conducted at a firing
temperature of at least about 900.degree. C.
51. The method of claim 50, wherein firing is conducted at a firing
temperature of at least about 1000.degree. C.
52. The method of claim 48, wherein firing is conducted at a firing
temperature of not greater than about 2000.degree. C.
53. The method of claim 52, wherein firing is conducted at a firing
temperature of not greater than about 1800.degree. C.
54. The method of claim 53, wherein firing is conducted at a firing
temperature of not greater than about 1500.degree. C.
55. The method of claim 48, wherein firing is conducted for a
firing duration of at least about 1 hour.
56. The method of claim 55, wherein firing is conducted for a
firing duration of at least about 10 hours.
57. The method of claim 35, wherein treating comprises cooling the
ceramic body after conducting a firing operation.
58. The method of claim 57, wherein cooling comprises reducing a
temperature of a chamber containing the ceramic body from a firing
temperature
59. The method of claim 35, wherein treating is conducted for a
treatment duration of at least about 10 minutes.
60. The method of claim 59, wherein treating is conducted for a
treatment duration of at least about 30 minutes.
61. The method of claim 60, wherein treating is conducted for a
treatment duration of at least about 60 minutes.
62. The method of claim 59, wherein treating is conducted for a
treatment duration of not greater than about 24 hours.
63. The method of claim 62, wherein treating is conducted for a
treatment duration of not greater than about 12 hours.
64. The method of claim 63, wherein treating is conducted for a
treatment duration of not greater than about 8 hours.
65. A method of forming a ceramic article comprising: firing a
ceramic body comprising silicon carbide in a first atmosphere; and
treating the ceramic body in a second atmosphere after firing,
wherein the second atmosphere is different than the first
atmosphere and comprises a reactant material that chemically reacts
with the ceramic body and removes a portion of the ceramic
body.
66. A ceramic article comprising: a body comprising nitride-bonded
silicon carbide, wherein the body comprises pores at an exterior
surface and a majority of the pores are defined by smooth,
non-fibrous surfaces when viewed at a magnification of at least
1000.times. for at least 2 random locations across the exterior
surface of the body.
67. The ceramic article of claim 66, wherein the body comprises an
open porosity within the body of at least about 2 vol % for a total
amount of porosity within the body.
68. The ceramic article of claim 66, wherein the body comprises a
density of at least about 75% of theoretical density.
69. The ceramic article of claim 66, wherein the body consists
essentially of nitride-bonded silicon carbide.
70. The ceramic article of claim 66, wherein the body comprises a
coating layer overlying the body.
71. The ceramic article of claim 70, wherein the coating layer
comprises an oxide.
72. The ceramic article of claim 70, wherein the coating layer
comprises an amorphous phase.
73. A ceramic article comprising: a body comprising nitrogen-bonded
silicon carbide having a non-fibrous exterior surface, wherein a
non-fibrous exterior surface is defined by a surface having not
greater than 10 fibers per 100 square microns at a magnification of
at least 1000.times. for at least 2 random locations across the
exterior surface of the body.
74. The ceramic article of claim 73, wherein the exterior surface
is defined by a surface having not greater than 5 fibers per 100
square microns at a magnification of at least 1000.times. for at
least 2 random locations across the exterior surface of the
body.
75. The ceramic article of claim 73, wherein the exterior surface
is defined by a surface having not greater than 1 fiber per 100
square microns at a magnification of at least 1000.times. for at
least 2 random locations across the exterior surface of the body.
Description
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application claims priority under 35 U.S.C.
.sctn.119(e) to U.S. Patent Application No. 61/428,289 entitled
"Silicon Carbide Body and Method of Forming Same," by Reilly et
al., filed Dec. 30, 2010, which is assigned to the current assignee
hereof and incorporated herein by reference in its entirety.
BACKGROUND
[0002] 1. Field of the Disclosure
[0003] The following is directed to a method of forming a ceramic
article, and particularly, a method of forming a silicon carbide
body.
[0004] 2. Description of the Related Art
[0005] Silicon carbide-based ceramic materials are utilized in many
applications for their refractory properties and mechanical
properties. Among the types of silicon carbide-based ceramics
available, various types exist based on the particular forming
process, including for example, sintered silicon carbide, hot
pressed silicon carbide, and recrystallized silicon carbide. Each
of the various types of silicon carbide bodies can have distinct
features. For example, sintered silicon carbide (such as
Hexyloy.RTM.) can be a very dense material, but is generally
expensive and complex to produce. On the other hand, more cost
effective but relatively porous silicon carbide materials such as
nitride-bonded silicon carbide (known by acronyms such as NBSC and
NSIC) have found practical use in refractory applications. Such
refractory components include furnace or kiln furniture utilized in
connection with holding or supporting work pieces during firing
operations, as well as refractory lining materials and structural
walls defining the furnace heating area.
[0006] However, certain process limitations still exist for certain
silicon carbide bodies. In particular reference to nitride-bonded
silicon carbide, during formation of the body, fibers of silicon
nitride are formed on the surface body. Such fibers can roughen the
surface, limit the ability to conduct post-forming processes, and
change the appearance of the body, which may be unsuitable for a
customer's intended use. Accordingly, it is common in the industry
to remove the silicon nitride fibers from the material prior to
further processing. The fibers are removed through physical
techniques, such as sandblasting the surface of the silicon carbide
body. Such processes are time consuming and often limited in
efficacy.
SUMMARY
[0007] According to one aspect, a method of forming a ceramic
article includes providing a ceramic body comprising silicon
carbide, and treating the ceramic body in an atmosphere comprising
an oxidizing material to remove a portion of the ceramic body
through a chemical reaction between a portion of the ceramic body
and the oxidizing material.
[0008] In another aspect, a method of forming a ceramic article
includes providing a ceramic body comprising a fibrous material
overlying an exterior surface of the ceramic body and treating the
ceramic body with a gaseous reactant material to remove the fibrous
material from the ceramic body through a chemical reaction between
the gaseous reactant material and the fibrous material.
[0009] Yet another aspect includes a method of forming a ceramic
article comprising firing a ceramic body comprising silicon carbide
in a first atmosphere and treating the ceramic body in a second
atmosphere after firing, wherein the second atmosphere is different
than the first atmosphere and comprises a reactant material that
chemically reacts with the ceramic body and removes a portion of
the ceramic body.
[0010] In still another aspect, a body includes nitride-bonded
silicon carbide, wherein the body comprises pores at an exterior
surface and a majority of the pores are defined by smooth,
non-fibrous surfaces when viewed at a magnification of at least
1000.times. for at least 2 random locations across the exterior
surface of the body.
[0011] According to one aspect, a ceramic article includes a body
having nitrogen-bonded silicon carbide having a non-fibrous
exterior surface, wherein a non-fibrous exterior surface is defined
by a surface having not greater than 10 fibers per 100 square
microns at a magnification of at least 1000.times. for at least 2
random locations across the exterior surface of the body.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] FIG. 1 includes a flow chart describing a process for
forming a ceramic article in accordance with an embodiment.
[0013] FIG. 2 includes a firing schedule of temperature versus
hours for a ceramic body formed according to an embodiment.
[0014] FIG. 3 includes a magnified image of a portion of a ceramic
body in accordance with an embodiment.
[0015] FIG. 4 includes a magnified image of a portion of a ceramic
body in accordance with an embodiment.
[0016] FIG. 5 includes a magnified image of a portion of a
conventional ceramic body.
[0017] FIG. 6 includes a magnified image of a portion of a
conventional ceramic body.
DETAILED DESCRIPTION
[0018] The following is directed to ceramic articles comprising
silicon carbide and methods of forming such articles. More
particularly, the following is directed to refractory bodies
incorporating silicon carbide, and can include nitride-bonded
silicon carbide compositions. Reference herein to nitride-bonded
silicon carbide can include ceramic bodies that have a majority
content of silicon carbide. The bodies can also include some
content of other materials including nitrides, oxides, carbides,
silicon, oxynitrides, and a combination thereof.
[0019] In reference to the method of forming a ceramic article in
accordance with an embodiment, FIG. 1 provides a flow chart
illustrating a process of forming such articles. As illustrated,
the process of forming a ceramic article can be initiated by
forming a mixture at step 101. The mixture can include a
combination of powder components which may be mixed together in a
dry form. Alternatively, the mixture may be in the form of a
slurry, including a liquid vehicle containing a mixture of powder
material.
[0020] The process of forming a mixture can include blending fine
and coarse silicon carbide powder materials together. The fine
silicon carbide powder can have an average particle size that is
less than an average particle size of the coarse silicon carbide
powder. The difference in the average particle size between the
fine and the coarse silicon carbide powders can be at least about
10% based on the larger of the two particles. The mixture can
include a bimodal distribution of silicon carbide powder material,
such that upon analysis of the mixture, two distinct modes defined
by the distinct fine and coarse particle sizes are evident. Other
mixtures can include more than two modes, such that the mixture can
include a trimodal mixture of silicon carbide powders.
[0021] For example, the coarse silicon carbide particles can have
an average particle size of at least about 40 microns, at least
about 50 microns, at least about 60 microns, at least about 70
microns, or even at least about 80 microns. Still, the coarse
silicon carbide particles can have an average particle size that is
not greater than about 2500 microns, such as less than about 2000
microns, less than about 1500 microns, less than about 1000
microns, less than about 800 microns, less than about 500 microns,
or even less than about 250 microns. The coarse silicon carbide
powder can have an average particle size within a range between any
of the minimum and maximum values noted above.
[0022] The fine silicon carbide powder can have an average particle
size that is significantly less than the average particle size of
the coarse silicon carbide powder. For example, the fine silicon
carbide particles can have an average particle size of not greater
than about 30 microns, such as not greater than about 25 microns,
not greater than about 20 microns, not greater than about 15
microns, or even not greater than about 10 microns. Still, the fine
silicon carbide particles can have an average particle size that is
at least about 0.01 microns, such as at least about 0.05 microns,
at least about 0.1 microns, or even at least about 0.5 microns. The
fine silicon carbide powder can have an average particle size
within a range between any of the minimum and maximum values noted
above.
[0023] The mixture can include a blend of fine and coarse silicon
carbide powders, which can be placed in the mixture in an equal
amount. However, in other instances, a greater or lesser amount of
one of the fine or coarse silicon carbide powder can be used. In
one particular embodiment, the mixture includes between about 30 wt
% and about 50 wt % of each of the fine and coarse silicon carbide
powders.
[0024] Certain other additive powder materials can be provided in
the mixture. The additives can include powder components having a
composition such as silicon, nitrides, carbides, oxides, borides,
oxynitrides, oxyborides, and a combination thereof. Generally, the
additives are present in minor amounts, such as less than about 25
wt %, not greater than about 20 wt %, not greater than about 15 wt
%, not greater than about 10 wt %, or even not greater than about 5
wt % of the total weight of the mixture. For example, particular
compositions incorporating some content of silicon can include at
least about 10 wt %, such as at least about 12 wt %, at least about
14 wt %, or even at least about 16 wt % silicon. Still, in such
embodiments, the amount of silicon can be not greater than about 25
wt %, not greater than about 22 wt %, not greater than about 20 wt
%, or even not greater than about 18 wt %.
[0025] In reference to still other mixtures used in the formation
of nitride-bonded silicon carbide bodies, use of materials such as
oxides, oxynitrides, and nitrides, can be limited. For example, in
particular instances, the presence of such materials may be not
greater than about 12 wt %, such as not greater than about 10 wt %,
not greater than about 8 wt %, or even not greater than about 5 wt
%.
[0026] In one particular embodiment, the additives include
materials such as aluminum oxide, iron oxide, and a combination
thereof. For example, the mixture can include approximately 5 wt %
alumina powder. Moreover, certain mixtures can include a minor
amount of iron oxide, such as approximately 0.5 wt %. Furthermore,
the mixture may include some content of silicon powder, generally
on the order of 1 wt % to about 10 wt %.
[0027] After suitably forming the mixture at step 101, the process
can continue at step 102 by shaping the mixture into a green body.
It will be appreciated that reference to a green body is reference
to an un-sintered body that has not undergone heat treatment to
densify the body. The shaping process can include various
operations including casting, molding, pressing, extruding, and a
combination thereof. In one particular instance, the process of
shaping the mixture into a green body includes a slip casting
process. For a detailed description of techniques for forming a
ceramic body, attention is drawn to U.S. Pat. No. 4,990,469,
incorporated herein by reference. Other suitable shaping methods
can include drip casting, pressing, pressure casting, extrusion,
and other techniques.
[0028] After shaping the mixture into a green body at step 102 the
process can continue at step 103 by firing the green body to form a
sintered ceramic body. Firing can be conducted in a chamber at a
particular firing temperature, such as at least about 800.degree.
C. In other instances, the firing temperature can be greater, such
as at least about 900.degree. C., at least about 1000.degree. C.,
or even at least about 1050.degree. C. In accordance with another
embodiment, the firing temperature can be not greater than about
2000.degree. C., such as not greater than about 1800.degree. C.,
not greater than about 1500.degree. C., or even not greater than
about 1480.degree. C. It will be appreciated that firing can be
conducted at a firing temperature within a range between any of the
minimum and maximum values noted above.
[0029] Firing may be conducted for a duration of at least about 1
hour. In other instances, the process of firing can be longer, such
that the firing duration can be at least about 10 hours, such as at
least about 25 hours, at least about 30 hours, at least about 40
hours, or even at least about 45 hours. In particular instances,
the firing process can have a duration of firing within a range
between about 10 hours and about 80 hours, such as between about 20
hours and about 65 hours. It will be appreciated that firing is
generally considered the time between the increase in temperature
as the green body is placed in the chamber to a time before the
temperature is reduced in the housing and cooling is
undertaken.
[0030] Firing may be conducted in a controlled atmosphere. In
accordance with an embodiment, the atmosphere can be a reducing
atmosphere. More particularly, the atmosphere during firing can
include nitrogen. In certain processes, the atmosphere during
firing can consist essentially of nitrogen. Such atmosphere may be
effective in reacting silicon contained in the body with the
nitrogen in the atmosphere, causing the formation of the silicon
nitride as a secondary phase that bonds the primary silicon carbide
phase and forms a nitride-bonded silicon carbide body.
[0031] Notably, during the firing process, certain fibrous
materials may be formed on the ceramic body. The fibrous material
may include a carbide, nitride, boride, or a combination thereof.
In particular instances, the fibrous material includes silicon
nitride fibers which are formed as a result of the firing process.
Such fibers can have a needle-like shape, extend over substantially
all of the major exterior surfaces of the body, and be microscopic.
In some cases, the fibers may negatively affect post-sintering
processes, particularly those directed to formation of a coating
layer on the body.
[0032] After firing the green body to form a sintered ceramic body
at step 103, the process can continue at step 104, by treating the
ceramic body. In accordance with an embodiment, the process of
treating the ceramic body can include inducing a chemical reaction
that facilitates removal of a portion of the ceramic body through
the chemical reaction between a reactant material within the
chamber and a portion of the ceramic body. Notably, the process of
treating the ceramic body may be conducted in the same chamber as
firing is conducted, such that the ceramic body does not need to be
removed after firing and placed in a different chamber.
Accordingly, the treating process includes an in-situ chemical
reaction to remove a portion of the ceramic body, which may be
formed during the firing process.
[0033] Treating the ceramic body can include changing the
atmosphere within the chamber after firing. Accordingly, the
atmosphere during treating can be different than the atmosphere
utilized during firing. It will be appreciated that reference to a
different atmosphere is reference to two atmospheres, wherein one
of the atmospheres differs from the other atmosphere by at least
one elemental component, which can be in the form of a free
element, composition, compound, and/or complex.
[0034] In accordance with an embodiment, treating the ceramic body
includes utilizing an oxidizing material within the atmosphere to
facilitate removal of a portion of the ceramic body through a
chemical reaction that takes place between the oxidizing material
and the ceramic body. The chemical reaction undertaken during
treating of the ceramic body can facilitate removing material from
an exterior surface of the ceramic body. In more particular
instances, the reaction can facilitate removal of material from
pores that extend into the interior volume of the ceramic body. As
such, the process of treating the ceramic body can facilitate
removal of the fibrous material from the exterior surface of the
body, and pores extending into the interior volume of the body
connected to the exterior surface.
[0035] In accordance with an embodiment, the oxidizing material may
be a gaseous reactant material suitable for oxidizing a portion of
the ceramic body. For example, the oxidizing material can include
oxygen. One process can include an oxidizing material in the form
of a compound including carbon. According to a particular
embodiment, the oxidizing material can include carbon dioxide, and
more particularly, the oxidizing material may consist essentially
of carbon dioxide.
[0036] In certain instances, the process of treating the ceramic
body can include a chemical reaction defining a phase transition of
one or more chemical components involved in the chemical reaction.
That is, for example, a portion of the body can be removed through
a phase transition, such that a portion of the body transforms
phases from a solid phase to a gas phase. In accordance with one
particular reaction, treating of the ceramic body may be conducted
such that an oxidizing material is introduced into the chamber,
wherein the oxidizing material reacts with a portion of the ceramic
body, which as a result, transforms the portion of the ceramic body
from a solid phase material to a gas phase material.
[0037] The chemical reaction between the oxidizing material and a
portion of the ceramic body can form a reaction product that may
include an oxide material. For example, the oxide material can be a
chemical compound including silicon. For instance, the oxide
material that is a reaction product of the chemical reaction
between the oxidizing material and the portion of the ceramic body
can include silicon monoxide, and more particularly, may consist
essentially of silicon monoxide.
[0038] Another, additional oxide material, separate from the one
noted above, may be formed as a reaction product from treating the
ceramic body. Such an oxide material can be in the form of a gas.
More particularly, the reaction product can be a chemical
composition including carbon. In certain instances, a reaction
product of carbon monoxide can be formed as a result of the
reaction between the ceramic body and the oxidizing material.
[0039] A reaction product comprising a nitrogen material may also
be formed as a result of the reaction between a portion of the
ceramic body and the gaseous reactant material. In certain
instances, a reaction product of nitrogen gas may be formed, and
more particularly, a reaction product consisting essentially of
nitrogen gas can be the nitrogen reaction product.
[0040] In accordance with one particular embodiment, the reaction
between a portion of the ceramic body comprising the fibrous
silicon nitride material and a gaseous reactant material in the
form of an oxidizing material can result in oxidation of the
silicon nitride fibers, represented by the following chemical
formula:
Si.sub.3N.sub.4+3CO.sub.2.fwdarw.3SiO+3CO+2N.sub.2
[0041] The process of treating the ceramic body may be conducted at
a particular temperature to facilitate the chemical reaction. In
fact, it has been noted that a certain minimum threshold
temperature may be utilized to drive the reaction, and below such a
temperature, the reaction may not necessarily occur. For example,
the process of treating the ceramic body can be conducted at a
reaction temperature that is at least about 800.degree. C. In other
instances, the reaction temperature can be at least about
900.degree. C., such as at least about 950.degree. C., at least
about 1000.degree. C., at least about 1100.degree. C., or even at
least about 1200.degree. C. In other instances, the process of
treating the ceramic body may be conducted at a reaction
temperature that is not greater than about 2000.degree. C., such as
not greater than about 1800.degree. C., not greater than about
1500.degree. C., or even not greater than about 1300.degree. C. It
will be appreciated that the reaction temperature can be within a
range between any of the minimum and maximum value recited
above.
[0042] Notably, the oxidizing material can be flowed through the
processing chamber at a particular rate to facilitate the reaction.
In fact, a certain flow rate may be utilized to ensure the chemical
reaction between the portion of the ceramic body and the oxidizing
material occurs. In one embodiment, the oxidizing material can be
flowed into the chamber at a flow rate of at least 1 standard cubic
foot per hour (scfh) or 0.028 cubic meters per hour. In still other
embodiments, the process of treating the ceramic body can include
flow of an oxidizing material through the chamber at a flow rate of
at least about 2 scfh (0.057 cubic meters per hour), such as at
least about 3 scfh (0.085 cubic meters per hour), at least about 4
scfh (0.11 cubic meters per hour), or even at least about 5 scfh
(0.14 cubic meters per hour). Still, the flow rate of the oxidizing
material into the chamber during the process of treating the
ceramic body can be not greater than about 200 scfh (5.7 cubic
meters per hour), such as not greater than about 175 scfh (5.0
cubic meters per hour), or even not greater than about 150 scfh
(4.2 cubic meters per hour). It will be appreciated that the flow
rate of oxidizing material through the chamber during treating of
the ceramic body can be within a range between any of the minimum
and maximum values noted above.
[0043] A certain amount of the atmosphere of the chamber during
treating may contain the gaseous reactant material. The atmosphere
of the chamber during treating can include at least about 50 vol %
of the gaseous reactant material for the total volume of the
chamber to facilitate the reaction. In more particular embodiments,
at least about 60 vol %, such as at least about 70 vol %, at least
about 80 vol %, at least about 90 vol %, or even essentially the
entire volume of the chamber can be filled with the gaseous
reactant material during the process of treating.
[0044] Treating can be conducted for a treatment duration of at
least about 10 minutes. In other processes, the treatment duration
can be longer, such as at least about 30 minutes, at least about 45
minutes, at least about 60 minutes, at least about 90 minutes, or
at least about 120 minutes. In certain instances, the treatment
duration can be not greater than about 24 hours, such as not
greater than about 18 hours, not greater than about 12 hours, or
even not greater than about 8 hours. It will be appreciated that
the treatment duration can be within a range between any of the
minimum and maximum values noted above.
[0045] In accordance with an embodiment, the process of treating
the ceramic body can further include a cooling process, wherein the
temperature within the chamber is decreased after firing to
initiate the process of treating the ceramic body. Notably, the
cooling process can be controlled such that the temperature is
properly controlled to facilitate treating of the ceramic body. In
one instance, the temperature is reduced after firing to initiate a
cooling process, while maintaining the temperature above a
particular threshold temperature to facilitate a reaction during
the treating process. Upon cooling, the atmosphere within the
chamber can be changed from the firing atmosphere to the treating
atmosphere to initiate the treating process.
[0046] The resulting ceramic body can be a nitride-bonded silicon
carbide body. In accordance with one embodiment, the ceramic body
can have a Knoop hardness of at least about 1500 kg/mm.sup.2. In
other instances, the Knoop hardness can be greater, such as at
least about 1800 kg/mm.sup.2, such as at least about 2000
kg/mm.sup.2, or even at least about 2500 kg/mm.sup.2. In certain
instances, the ceramic body can have a Knoop hardness of less than
about 4000 kg/mm.sup.2, such as less than about 3500 kg/mm.sup.2,
even less than about 3000 kg/mm.sup.2, or even less than about 2700
kg/mm.sup.2.
[0047] In accordance with another embodiment, the ceramic body can
have a corrosion resistance, as measured by weight loss in 53%
hydrochloric acid, not greater than 15 mg/cm.sup.2 yr. In other
instances, the corrosion resistance is better, having a weight loss
that is not greater than about 12 mg/cm.sup.2 yr, not greater than
about 10 mg/cm.sup.2 yr. Still, the weight loss can be at least 5
mg/cm.sup.2 yr. It will be appreciated that the corrosion
resistance can be within a range between any of the minimum and
maximum values noted herein.
[0048] After treating, the nitride-bonded silicon carbide ceramic
body can have a porosity of less than about 25 vol % of the total
volume of the body. In other instances, the porosity of the ceramic
body can be less, such as not greater than about 20 vol %, not
greater than about 18 vol %, or even not greater than about 15 vol
% of the total volume of the ceramic body. It will be appreciated
that the porosity may be at least about 1 vol %, such as at least
about 2 vol %, at least about 3 vol %, or even at least about 5 vol
% of the total volume of the ceramic body. It will be appreciated
that the total volume of porosity within the ceramic body can be
within a range between any of the minimum and maximum values noted
above.
[0049] Furthermore, a fraction of the porosity present within the
ceramic body can be open porosity, which may be defined by a
network of interconnected pores within the body that intersect the
exterior surface. The nitride-bonded silicon carbide ceramic body
generally contains at least about 1 vol %, such as at least about 5
vol %, at least about 8 vol %, or even at least about 10 vol % open
porosity for the total volume of porosity within the body.
[0050] In accordance with another embodiment, the ceramic body can
be formed such that it has a density that is at least about 75% of
theoretical density. In other instances, the ceramic body can have
a density that is at least about 80%, such as at least about 90%,
at least about 92%, or even at least about 95% of theoretical
density.
[0051] As further illustrated in FIG. 1, the process of forming a
ceramic body can further include an optional step 105 which
includes coating of the ceramic body. Coating of the ceramic body
can include formation of a coating layer that overlies the exterior
surface of the body. The coating may overlie essentially the entire
exterior surface of the body such that the ceramic body is
encapsulated by the coating layer. In accordance with an
embodiment, the coating layer can include an oxide material. More
particularly, the coating layer can include an alumina oxide
material and/or a mullite material, which is an alumina silicate
material (3Al.sub.2O.sub.3.2SIO.sub.2). In more particular
instances, the coating layer can include an amorphous phase. In
still other instances, the coating layer can include a crystalline
phase. Certain coating layers can include a combination of
amorphous phase and crystalline phase wherein the crystalline phase
may be mainly in the form of needle-shaped crystals comprising the
alumina silicate material.
[0052] The process of forming the coating layer can be affected by
spraying, dipping, brushing, and the like. For example, a spraying
process can include an air sprayer to achieve a thin, uniform
coating on the surface of the ceramic body. In other instances more
complex shapes of ceramic body may include a submersion approach,
such as dipping, wherein the ceramic body is placed in a slurry
containing a mixture of the material components suitable for
forming the coating layer.
[0053] After sufficiently coating the ceramic body with the desired
material, the coating process can further include a heat treatment.
Heat treatment can be conducted in a particular atmosphere, such as
an oxidizing atmosphere, which can include ambient air. The heat
treatment process can be conducted at elevated temperatures, such
as on the order of at least about 1000.degree. C., at least about
1100.degree. C., or even at least about 1200.degree. C. In such an
instance, the material sprayed or otherwise coated on the
nitride-bonded silicon carbide body can be oxidized to form the
coating layer. Further aspects of the process of forming the
coating layer and characteristics of the coating layer are set
forth in U.S. Pat. No. 7,732,026 which is incorporated in its
entirety by reference.
[0054] In particular reference to the nitrogen-bonded silicon
carbide material (i.e., without an optional coating layer), the
process of treating the ceramic body can facilitate the removal of
fibrous material from the exterior surface of the body as well as
pores within the body that may extend into the interior volume of
the body. Such bodies are distinct from conventional
nitrogen-bonded silicon carbide bodies, since conventional
techniques for removing such fibrous growths on the body include
mechanical abrading techniques including, for example, sand
blasting techniques, which simply remove the fibers from the
exterior surface of the body without removing the fibers from
crevices and pores on the surface, and furthermore, can actually
roughen the exterior surface of the body. Accordingly, the ceramic
body of the embodiments herein can be characterized by smooth,
non-fibrous surfaces when the exterior surface is viewed at
magnifications of at least 1000.times. for at least two random
locations across the exterior surface of the body.
[0055] In particular, the ceramic bodies of the embodiments herein
are characterized by a non-fibrous exterior surface having not
greater than 10 fibers per hundred square microns when viewed at a
magnification of at least 1000.times. at two random locations on
the exterior surface of the ceramic body. In fact, in other
embodiments, the existence of fibers is even more scarce, such that
the exterior surface of the ceramic body is characterized by having
not greater than 5 fibers per 100 square microns, not greater than
1 fiber per 100 square microns, not greater than about 1 fiber per
500 square microns, or even not greater than 1 fiber per 1000
square microns when at least 2 random locations on the exterior
surface of the body are viewed at a magnification of at least
1000.times..
Example
[0056] A nitride-bonded silicon carbide body is formed according to
embodiments herein by initially combining the components provided
in Table 1 below in a slurry. The sample of Example 1, formed
according to the embodiments herein, is designated sample S1.
TABLE-US-00001 TABLE 1 6521-100F SILICON CARBIDE GREEN 35.5 wt %
7662-30 SILICON CARBIDE GREEN 33.3 wt % C-8774 IRON OX #222 BAYER
0.44 wt % WD DEIONIZED WATER 11.01 wt % C-8770 A-3000FL CALCINED
ALU 4.44 wt % C-8773 ELKEM SI 0.30% FE 15.07 wt %
[0057] After forming the initial mixture in the form of a slurry,
the mixture is slip cast to form a green body. The green body is
placed in a firing chamber wherein the temperature is increased to
700.degree. C. at 100.degree. C./hr and nitrogen gas is introduced
into the chamber. Thereafter, the temperature is increased to
approximately 1350.degree. C. while nitrogen gas continues to flow.
The temperature is increased to 1440.degree. C. and is soaked for 6
hours in a nitrogen gas atmosphere. After 6 hours of firing at
1440.degree. C., the nitrogen gas atmosphere is purged from the
firing chamber and CO.sub.2 is introduced as an oxidizing material
within the chamber to react with a portion the fired silicon
carbide body. CO.sub.2 is flowed through the chamber at 4 scfh for
approximately 5 hours while the temperature in the chamber is
reduced and cooling of the ceramic body is initiated. After 5 hours
of flowing CO.sub.2 into the chamber, the atmosphere is again
changed such that ambient air is flowed into the chamber while the
ceramic body cools to room temperature. FIG. 2 includes a firing
schedule demonstrating the temperature of the chamber during the
process of forming the ceramic body of Example 1.
[0058] A conventional sample (C1) comprising nitride-bonded silicon
carbide is formed according to a conventional process that utilizes
a similar process as noted above with regard to sample S1; however,
no treating process is conducted. The firing process to form sample
C1 is the same as sample S1. However, after firing, no CO.sub.2 is
introduced into the chamber. After cooling to room temperature,
silicon nitride fibers are evident on the sample C1. No silicon
nitride fibers are observable on the sample S1.
[0059] Sample C1 is sandblasted using 10-40 lbs of pressure and 24
mesh size grit of brown, fused alumina.
[0060] FIGS. 3 and 4 include magnified images of a portion of the
ceramic body of sample S1 formed according to the embodiments
herein. FIGS. 3 and 4 include magnified images of pores on the
exterior surface of the Sample S1. As clearly shown, sample S1 is
essentially free of fibrous material on the exterior surface, even
when observed at magnifications of 500.times. and 1000.times..
[0061] By comparison, a portion of the conventional sample is
illustrated in the magnified images of FIGS. 5 and 6. Clearly, as
shown in FIGS. 5 and 6, the conventional sample has fibers
extending over the surface and obstructing the crevices and pores
on the exterior surface of the ceramic body. Considering that the
viewed area in each of FIGS. 5 and 6 is greater than 1000 square
microns, clearly the concentration of fibers of sample C1 is
significantly greater than that of sample S1, and more
particularly, significantly greater than 10 fibers per hundred
square microns.
[0062] The embodiments herein are directed to nitride-bonded
silicon carbide articles and methods of forming such articles. The
embodiments herein are directed to a combination of processing
techniques configured to facilitate the formation of nitride-bonded
silicon carbide bodies using a more efficient, streamlined process.
Such features include a treating process, wherein a chemical
reaction occurs between a portion of the silicon carbide body and a
gaseous reactant material introduced into the firing chamber under
particular conditions (e.g., temperature, pressure, duration, flow
rate, etc.). Accordingly, portions of the body are removed in-situ,
alleviating the need for future, time-consuming processing, which
would otherwise be necessary to remove the undesirable
portions.
[0063] Furthermore, the result of the unique combination of
processing parameters results in an ceramic article having unique,
identifiable features as compared to nitride-bonded silicon carbide
bodies formed through conventional processing pathways. Such
features include, but are not limited to, particularly low
concentrations of fibrous material on the exterior surface, and
mechanical features. The embodiments provide a combination of
features, which can be combined in various manners to describe and
define the refractory bodies of the embodiments. The description is
not intended to set forth a hierarchy of features, but different
features that can be combined in one or more manners to define the
invention.
[0064] In the foregoing, reference to specific embodiments and the
connections of certain components is illustrative. It will be
appreciated that reference to components as being coupled or
connected is intended to disclose either direct connection between
said components or indirect connection through one or more
intervening components, as will be appreciated, to carry out the
methods as discussed herein. As such, the above-disclosed subject
matter is to be considered illustrative, and not restrictive, and
the appended claims are intended to cover all such modifications,
enhancements, and other embodiments, which fall within the true
scope of the present invention. Thus, to the maximum extent allowed
by law, the scope of the present invention is to be determined by
the broadest permissible interpretation of the following claims and
their equivalents, and shall not be restricted or limited by the
foregoing detailed description.
[0065] The disclosure is submitted with the understanding that it
will not be used to interpret or limit the scope or meaning of the
claims. In addition, in the foregoing disclosure, various features
may be grouped together or described in a single embodiment for the
purpose of streamlining the disclosure. This disclosure is not to
be interpreted as reflecting an intention that the embodiments
herein limit the features provided in the claims, and moreover, any
of the features described herein can be combined together to
describe the inventive subject matter. Still, inventive subject
matter may be directed to less than all features of any of the
disclosed embodiments.
* * * * *