U.S. patent application number 13/338420 was filed with the patent office on 2012-06-07 for method and apparatus for microwave depolymerization of hydrocarbon feedstocks.
Invention is credited to John Hemmings, Thomas Pinto, Viktor Sharivker.
Application Number | 20120138601 13/338420 |
Document ID | / |
Family ID | 46161246 |
Filed Date | 2012-06-07 |
United States Patent
Application |
20120138601 |
Kind Code |
A1 |
Hemmings; John ; et
al. |
June 7, 2012 |
Method and Apparatus for Microwave Depolymerization of Hydrocarbon
Feedstocks
Abstract
A method and apparatus is provided for the continuous microwave
depolymerization of high molecular weight organic feedstock
material, such as waste plastics and includes intermittent or
continuous feeding of the processing material on the surface or
into the bulk of the sensitized hot bed located under microwave
irradiation. As a result of the interaction of electromagnetic
field with processed materials, sensitizer is heated by microwave
energy and feedstock material undergoes the depolymerization
reactions. The reaction zone can be localized on the surface of the
hot bed or distributed in the bulk of the reaction mass depending
on the agitation conditions of the reaction mass, such as stirring,
or other agitation means, for example by re-circulated gas.
Products of the reactions are vaporized and transported to the
collection system, which may include a combination of a scrubber, a
condenser and a settler.
Inventors: |
Hemmings; John; (Katy,
TX) ; Pinto; Thomas; (Long Valley, NJ) ;
Sharivker; Viktor; (Ottawa, CA) |
Family ID: |
46161246 |
Appl. No.: |
13/338420 |
Filed: |
December 28, 2011 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13333097 |
Dec 21, 2011 |
|
|
|
13338420 |
|
|
|
|
Current U.S.
Class: |
219/679 ;
219/756 |
Current CPC
Class: |
Y02W 30/62 20150501;
B01J 19/126 20130101; H05B 2206/045 20130101; Y02W 30/703 20150501;
C08J 11/12 20130101; H05B 2214/03 20130101; C10G 1/10 20130101;
H05B 6/701 20130101; C08J 11/10 20130101; Y02W 30/702 20150501 |
Class at
Publication: |
219/679 ;
219/756 |
International
Class: |
H05B 6/64 20060101
H05B006/64 |
Claims
1. Apparatus for the continuous processing of high molecular weight
organic materials, comprising: a reaction vessel constructed and
arranged to receive the high molecular weight organic materials; an
opening in the reaction vessel to receive the high molecular weight
organic materials; a source of microwave energy which is introduced
into the reaction vessel through a waveguide port, constructed and
arranged to impinge upon to heat the materials within the reaction
vessel and cause microwave depolymerization of the materials; the
depolymerization by microwave energy heating the materials to form
liquid portions and vapor portions; the liquid portion migrating to
the bottom portion of the reaction vessel; wherein the temperature
of a portion of the reaction vessel is in the range of about 250
degrees C. to about 425 degrees C.; and a collection apparatus
constructed and arranged to remove one or more of the liquid
portion and the vapor portion of the materials from the reaction
vessel.
2. The apparatus of claim 1, wherein the high molecular weight
organic materials comprises one or more of: waste plastics, waste
oils, petroleum residues, tires, oil sands, oil shale and cellulose
materials.
3. The apparatus of claim 1, wherein the high molecular weight
organic materials are plastics recovered and/or diverted from
municipal solid waste
4. The apparatus of claim 1, wherein the products produced are
synthetic oils used in the production of fuels, waxes and
lubricants
5. The apparatus of claim 1, wherein a scrubber and separator
device downstream of the scrubber, are operatively connected to the
collection apparatus, and wherein the vapor portion removed from
the reaction vessel is condensed by the scrubber, and with the
separator device causing the separation of at least the vapor
portions and the liquid portions of materials exiting the
scrubber.
6. The apparatus of claim 1 further comprising at least one of: (a)
a barrier which is transparent to microwave energy located in the
vicinity of the waveguide port or (b) a port to introduce a gaseous
material into the waveguide to isolate the microwave energy source
from the vapor and liquid portions in the reaction vessel.
7. The apparatus of claim 1, further comprising a source of heating
at least partially contacting the exterior of the reaction
vessel.
8. The apparatus of claim 1, wherein the pressure in the reaction
vessel is in the range of about minus 10 psig to about plus 15
psig.
9. The apparatus of claim 1, further comprising one or more
refining units downstream of the crude wax tank.
10. The apparatus of claim 1, wherein the one or more refining
units comprises one or more of units for: distillation,
hydroprocessing, isomerization and fractionation.
11. A method for the continuous processing of high molecular weight
organic materials, comprising the steps of: introducing the
materials into a reaction vessel constructed and arranged to
receive the high molecular weight organic materials through an
opening in the reactor vessel; using a source of microwave energy
to introduce impinging microwave energy into the reaction vessel
through a waveguide port to cause heating of the materials within
the reaction vessel and causing microwave depolymerization of the
materials; the depolymerization by microwave energy heating the
materials to form liquid portions and vapor portions; the liquid
portion migrating to the bottom portion of the reaction vessel;
maintaining the temperature of one of the portions of the reaction
vessel in the range of about 250 degrees C. to about 425 degrees
C.; providing at least one of a mechanical mixer and a gaseous
material input within the reaction vessel, and mixing the liquid
portion on the bottom portion of the reaction vessel; and removing
one or more of the liquid portion and the vapor portion of the
materials from the reaction vessel.
12. The method of claim 11, wherein the high molecular weight
organic materials comprises one or more of: waste plastics, waste
oils, petroleum residues, tires, oil sands, oil shale and cellulose
materials.
13. The method of claim 11, wherein the high molecular weight
organic materials are plastics recovered and/or diverted from
municipal solid waste
14. The method of claim 11, wherein the products produced are
synthetic oils used in the production of fuels, waxes and
lubricants
15. The method of claim 11, wherein a scrubber and separator device
downstream of the scrubber, are operatively connected to the
collection apparatus, and wherein the vapor portion removed from
the reaction vessel is condensed by the scrubber, and with the
separator device causing the separation of at least the vapor
portions and the liquid portions of materials exiting the
scrubber.
16. The method of claim 11, further comprising providing a source
of heating at least partially contacting the exterior of the
reaction vessel.
17. The method of claim 11, wherein the pressure in the reaction
vessel is maintained in the range of about minus 10 psig to about
plus 15 psig.
18. The method of claim 11, further comprising providing at least
one of: (a) a barrier which is transparent to microwave energy
located in the vicinity of the waveguide port or (b) a port to
introduce a gaseous material into the waveguide to isolate the
microwave energy source from the vapor and liquid portions in the
reactor vessel.
19. The method of claim 11, further comprising the step of refining
the crude wax collected in the crude wax holding tank.
20. The method of claim 11, wherein the steps of refining the crude
wax comprise one or more of the steps of: distillation,
hydroprocessing, isomerization and fractionation.
Description
RELATED APPLICATIONS
[0001] This application is a continuation of and claims the benefit
of U.S. application Ser. No. 13/333,097, filed Dec. 21, 2011, which
is incorporated by reference herein in its entirety.
BACKGROUND OF THE INVENTION
[0002] This application relates to a method and apparatus for the
microwave depolymerization of hydrocarbon feedstocks, including
plastic materials. An earlier effort is embodied in U.S. Pat. No.
6,184,427 entitled "Process and Reactor for Microwave
Depolymerization of Plastic Materials", which is assigned to the
assignee of the present invention. This patent discloses, among
other things, using the interaction of microwave and sensitizers in
order to provide heating and depolymerization of hydrocarbons. The
present invention is an improvement upon such U.S. patent.
SUMMARY OF THE INVENTION
[0003] In general, in one aspect, the invention provides a method
and apparatus for the continuous processing of high molecular
weight organic feedstock material (such as waste plastics, waste
oils, petroleum residues, tires, oil sands, oil shale, cellulose
and other bio material), which includes continuous feeding of the
processing material on the surface or into the bulk of the
sensitized hot bed (reacting mass pool) located under microwave
irradiation. Processed material preferably may be used and may be
fed as a powder, shredded solid, liquid or melted bulk items.
Sensitized hot bed may preferably be melted or a powdered mixture,
which consists from the initial and/or partially processed
feedstock, microwave sensitizer material and catalyst. As result of
the interaction of electromagnetic field with processed feedstock
materials, the sensitizer is heated by microwave energy and the
feedstock material undergoes reactions, such as de-polymerization,
olefin oligomerization, dehydrogenation, isomerization, naphthene
ring formation, aromaticization and chain branching. The reaction
zone can be localized on the surface of the hot bed or distributed
in the bulk of the melt depending on the agitation conditions of
the melt, such as stirring (or other agitation means, for example
by re-circulated gas). The recycling off-gases (or other type of
gases enriched with hydrogen) may be purged through the reaction
zone allowing intensification of the exothermic reactions, such as
olefin hydrogenation and oligomerization. Products of these
reactions may be vaporized and transported to the collection
system, which is preferably a combination of the scrubber,
condenser and settler in one unit device. Process apparatus may
include the integration of thermal and microwave depolymerization
into the hybrid processing equipment. Process equipment can include
a plurality or cascade of reactor chambers in order to separate
depolymerization stages, as well as include post microwave
treatment of products using distillation, hydroprocessing and
isomerization.
[0004] In one aspect of the invention, a reaction vessel, enclosing
a volume, receives the high molecular weight organic materials. A
source of microwave energy is provided to impinge upon to heat the
materials within the reaction vessel and cause microwave
depolymerization of the materials. The depolymerized materials form
liquids and vapors and the liquid migrates to the bottom of the
reaction vessel. There is an opening in the reaction vessel to
receive the high molecular weight organic materials. A collection
apparatus removes one or more of the liquids and the vapors of the
materials from the reaction vessel.
[0005] In another aspect of the invention, materials are introduced
into a reaction vessel through an opening in the vessel. A
microwave source is used to impinge microwave energy on the
materials such that the microwave energy heats and depolymerizes
the materials in the reaction vessel. The depolymerization step
causes the formation of a vapor portion and a liquid portion from
the materials. The liquid portion migrates to a lower portion of
the reaction vessel. The liquid portion and the vapor portion are
removed from the reaction vessel.
[0006] Variations may include one or more of the following
features.
[0007] The apparatus may have an access opening in the top portion
of the reaction vessel for at least one of continuous and
intermittent feeding of the organic materials into the reaction
vessel.
[0008] The source of microwave energy may introduce microwave
energy through a waveguide into the reaction vessel from one or
more entry ports located in the upper portion of the reaction
vessel. The microwave energy may operate in the range from about
300 MHz to about 3 GHz. In one embodiment of the invention, the
microwave energy operates at about 900 MHz.
[0009] The microwave energy may be of sufficient power and duration
to cause microwave depolymerization of the high molecular weight
materials. The impingement of microwave energy on the materials and
the sensitizer may cause further sensitizer to be formed.
Additionally, the sensitizer formed may be in the form of carbon
particles. The sensitizer formed may also be in the form of carbon
dendrites.
[0010] The collection apparatus may comprise at least two access
ports into the reaction vessel, one of the at least two access
ports being located in the liquid portion of the reaction vessel
and another of the at least two access ports being located in the
vapor portion of the reaction vessel. The at least two access ports
remove the liquid and the vapor from the reaction vessel.
[0011] A scrubber may be operatively connected to one of the at
least two access ports and condense the vapor removed from the
reaction vessel.
[0012] The liquid portion or the vapor portion may be removed one
of continuously and intermittently.
[0013] A separator device may be downstream of the scrubber. The
separator device causes the separation of at least the vapor and
the liquid of materials exiting form the scrubber.
[0014] The top portion of the apparatus may have a microwave
cavity. The microwave cavity can be partitioned into at least two
zones comprising an upper zone and a lower zone. The lower zone may
be at a temperature higher than the temperature of the upper zone.
In one embodiment of the invention, the temperature in the bottom
portion of the reaction vessel may be in the range of about 250
degrees C. to about 425 degrees C. and the temperature in the top
portion of the reaction vessel may be in the range of about 50
degrees C. to about 200 degrees C.
[0015] The mechanical mixer of the apparatus may be located in the
bottom portion of the reaction vessel, the bottom portion of the
vessel comprising a flat surface or an inverted truncated cone.
[0016] The apparatus may have a non-microwave source of heating at
least partially contacting the bottom portion of the reaction
vessel. The apparatus may have at least one source of heat to heat
the top portion of the reaction vessel.
[0017] The collection apparatus may include a crude wax tank which
receives the output from the reaction vessel access ports.
[0018] The apparatus may have one or more refining units downstream
of the crude wax tank.
[0019] The refining units may be for short path distillation,
hydroprocessing, isomerization and fractionation.
[0020] One or more refining units may receive the output from the
crude wax holding tank.
[0021] The apparatus may have a barrier which is transparent to
microwave energy located in the vicinity of the waveguide port to
isolate the microwave energy source from the vapor and liquid in
the reaction vessel. Additionally, the apparatus may have a port in
the vicinity of the waveguide to introduce a gaseous material into
the waveguide to isolate the microwave energy source from the vapor
and liquid portions in the reaction vessel.
[0022] The apparatus may have at least one port in the reaction
vessel to introduce high molecular weight materials in liquid form
into the bottom portion of the reaction vessel.
[0023] The apparatus may have at least one port in the reaction
vessel to remove high molecular weight materials in liquid form
from the bottom portion of the reaction vessel.
[0024] The high molecular weight organic materials may be one or
more of: waste plastics, waste oils, petroleum residues, tires, oil
sands, oil shale and cellulose materials.
[0025] The pressure in the reaction vessel may be in the range of
about minus 10 psig to about plus 15 psig.
[0026] The apparatus may have a sensitizer in the reaction vessel,
the sensitizer being subjected to be impinged upon by the source of
microwave energy.
[0027] The apparatus may have at least one port for the
introduction of the gaseous material into the bottom portion of the
reaction vessel for mixing the liquid portion of the materials in
the bottom portion of the reaction vessel.
[0028] The apparatus may have at least one of a mechanical mixer
and a gaseous material input positioned within the reaction vessel,
the at least one of a mechanical mixer and a gaseous material input
mixing the liquid portion of the materials.
[0029] A sensitizer may be introduced into the reaction vessel to
assist in depolymerization the materials.
[0030] The removed vapor portion may be directed to a scrubber to
condense the vapor portion.
[0031] The material from the scrubber may be directed to a
separator device.
[0032] The reaction vessel may be a sealed vessel and the vessel
pressure may be operated with an internal pressure in the range of
about minus 10 psig to about plus 15 psig.
[0033] The temperature of the vessel may be maintained in the range
of 250 degrees C. to about 425 degrees C.
[0034] The microwave depolymerization of the materials may produce
additional sensitizer without the need for further introduction of
further sensitizer into the vessel from outside the vessel.
[0035] The microwave source may be operated in the range of about
300 MHz to about 3 GHz. In one embodiment of the invention, the
microwave source may be operated at about 900 MHz.
[0036] The temperature of the liquid portion may be in the range of
about 350 degrees C. to about 425 degrees C.
[0037] A further source of heating may be provided to the reaction
vessel to heat the materials in the vessel.
[0038] The liquid portion of the materials may utilize at least one
of a mechanical stirrer and a gaseous fluid input for mixing.
[0039] One or more of the liquid portion and the vapor portion may
be removed from the reaction vessel and collected in a crude wax
holding tank.
[0040] The crude wax collected in the crude wax holding tank may be
refined further. [0041] Refining the molten heavy wax may include
short path distillation, hydroprocessing, isomerization and
fractionation.
[0042] These and other capabilities of the inventions, along with
the invention itself will be more fully understood after a review
of the following figures, detailed descriptions and appended
claims.
DETAILED DESCRIPTION OF THE DRAWING FIGURES
[0043] FIG. 1 is a schematic drawing illustrating in general the
microwave depolymerization process of the present invention.
[0044] FIG. 2 is a graph which illustrates the effect of reaction
extent on pumpability of bulk materials.
[0045] FIG. 3A is a schematic view of one embodiment of a microwave
applicator having an inclined bottom section.
[0046] FIG. 3B is a schematic view of a second embodiment of a
microwave applicator having a flat bottom.
[0047] FIG. 4 is a schematic view of jet scrubber and wax
separators.
[0048] FIG. 5 is a schematic view of the arrangement of a plurality
of jet scrubbers and wax separators.
[0049] FIG. 6 is another embodiment of the microwave applicator of
FIGS. 3A and 3B with the addition of a thermal depolymerization
zone to the applicator.
[0050] FIG. 7 is a schematic view of an arrangement of devices for
hydrocarbon processing.
DETAILED DESCRIPTION
Description of Overall Microwave Depolymerization Process--Single
Stage and Microwave
[0051] FIG. 1 illustrates a schematic view of the overall microwave
depolymerization apparatus of the present invention, designated as
reference numeral 100. In FIG. 1, 101 denotes a vessel which is
capable of being loaded with waste or low value hydrocarbon
feedstocks in solid form, such as shredded waste plastics, or in
liquid form such as waste oils. Other materials which may be used
as hydrocarbon feedstocks include: high boiling point refining
residue, waste coal, naturally occurring heavy hydrocarbons, such
as uintahite and hydrocarbon by-products from manufacturing
processes. The solid hydrocarbon feedstocks are transferred through
flow line 102, using a suitable feeder device 103 which may be a
screw type feeder but (depending on the flow properties of the
material) could be another conventional feed system such as a pair
of knife gate valves or a rotary feeder to feed the feedstock into
the microwave cavity 104. Microwave cavity 104 is an electrically
conductive enclosure (typically metal) which is large enough for
microwaves (operating for example, at about 900 MHz) to propagate,
preferably in several different modes.
[0052] It is understood that while a 900 MHz source is only one
example of a particular frequency useful in the present invention,
other frequencies may be useful, including the range of about 300
MHz to about 30 GHz. The basic principle underlying the application
of microwave energy is the use of dielectric heating, that is, the
conversion of electric energy to heat resulting from dielectric
losses of an electric non-conducting material. Thus, the present
invention may also employ sources in the dielectric heating
frequencies which includes both radio frequency (RF) and
microwaves.
[0053] Microwave cavity 104 contains gases, vapors and a descending
stream of solid or liquid feedstock falling by gravity from flow
line 102 into the lower part of the cavity where it accumulates in
the form of reacting mass 105. In a preferred embodiment, reacting
mass 105 is contained within a microwave cavity 106 which is
smaller than and concentric to main cavity 104 and which has a
dividing wall 107 which protrudes into the main cavity 104. The
diameter of lower cavity 106 is selected relative to that of main
cavity 104 such that 106 is at least large enough for microwaves to
propagate freely. The gap between the dividing wall 107 and the
inside wall of the main cavity 104 is large enough to ensure that
there is no or at least minimal danger of arcing between the top of
dividing wall 107 and the wall of cavity 104. Furthermore, the
height of the dividing wall 107 may be chosen so that reflected
waves from the coaxial part of the cavity effectively cancel out
the incident waves. The reacting mass may be agitated by means of a
mechanical agitator 108, which may include a Rushton-type turbine
(flat blades) affixed to the end of a vertical shaft which may be
rotated, for example by means of an electric motor and gears.
Recycled gas, consisting predominantly of nitrogen, hydrogen and
light hydrocarbons, for stripping depolymerized hydrocarbons from
the molten reaction mass and to provide light olefins which may
participate in oligomerization reactions, may be introduced below
the agitator. In the preferred embodiment this is done by encasing
the shaft in a pipe 109 and attaching a bubble cap 110 to the shaft
below the turbine. The pipe 109 enters the lower cavity 106 from
the bottom and has an internal diameter which may be significantly
greater than the shaft of the agitator. Gas may be fed into the
annulus between the pipe 109 and the shaft by means of flow line
113. The gas fills the annulus, and flows upwards into the agitated
liquid at the rim of the bubble cap 110.
[0054] The circulating gases, the non-condensed gases that result
from the depolymerization process and which exit from mist
eliminator 190 consist mainly of uncondensed vapors and inert gases
which originate from compressor 114. Gases from compressor 114 may
also be used for waveguide inerting and excess gas can be used as
fuel or simply flared. These surplus gases flow through flow line
115.
[0055] Microwave cavity 104 is enclosed in a jacket, which is split
into a lower zone 116 and an upper zone 117. A cooling medium,
typically a commercial heat transfer fluid, circulates
independently through the lower and upper jacket zones by means of
flow lines 118 and 120 for the lower zone, and 119 and 122
respectively for the upper zone. The inner wall of the cavity is
maintained at a suitable temperature, typically in the range of
about 50 to 120 deg C., by means of the coolant flow. The lower
zone may be operated at a higher temperature to ensure that heavy
wax is above its melting point and thus able to flow downwards. The
specific temperatures are chosen having regard to the properties of
hydrocarbons condensed from the gas stream.
[0056] Microwave energy may be fed into the cavity 104 by means of
one or more waveguides 124 from one or more microwave generators.
The waveguides may enter the cavity in one or in a number of paths.
Three alternative ways are: either parallel to the axis of the
cavity, orthogonal to the axis of the cavity, or as circularly
polarized microwave energy parallel to the axis of the cavity. In
one embodiment, at least one but preferably between 2 and 3
parallel circularly polarized waveguides parallel to the axis of
the vessel are utilized. The waveguide may incorporate a vertical
section running upwards. This is relevant in that the waveguide 124
should be filled with a clean gas with relatively high dielectric
strength (such as nitrogen), whereas the main microwave cavity 104
is filled with hydrocarbon vapors and particulate carbon. It is
generally desirable to prevent excessive ingress of hydrocarbon
vapors from the cavity 104 into the waveguide 124. This is done by
a combination of hydrostatic and hydrodynamic means. The waveguide
may incorporate a window 126 made from a material transparent to
microwaves. The waveguide section which runs vertically upwards, as
shown in FIG. 1, downstream of the window 126 should ideally be
filled with a gas which is denser than the hydrocarbon vapor
present in the microwave cavity 104. The maintenance of sealing by
a gas such as nitrogen is maintained by a small flow using flow
line 128. A second flow line 130 is connected at the high point of
the waveguide. A gas lighter than the hydrocarbon vapors will
typically be added at this point (typically recycled light gases
and nitrogen). This creates a situation where the waveguide from
the window to the high point is filled with a gas heavier than the
gas in the microwave cavity 104 while the section of waveguide from
the microwave cavity to the highpoint is filled with gas lighter
than that in the microwave cavity. It is preferable that the gas
added to the top of the waveguide be less dense than that present
in the cavity. A preferred gas to use for this purpose is recycled
light gas from compressor 114. This gas mixture contains
essentially the same chemical components as are present in the
cavity, that is, a mixture of hydrocarbons, hydrogen and inert
gases, however depleted in heavy hydrocarbons (relative to the gas
in the cavity) and lower in temperature. It is also desirable, but
not essential, that the gas from the compressor 114 be lighter than
the gas added to the bottom of the waveguide. Thus the waveguide,
124, will be filled with a mixture of gases which are
hydrostatically stable, and therefore gases containing particulates
which are present in the cavity will not be able to contaminate the
atmosphere in the waveguide. This is significant because the dirty
gases from the cavity have a significantly lower breakdown voltage
than the clean gases in the waveguide, which implies that should
the dirty gases be allowed to accumulate in the waveguide (where
the electric field strength is much higher than in the cavity),
arcing and plasma generation are likely.
[0057] Returning now to a description of activity in microwave
cavity 104, as mentioned above, solid feedstock enters the reacting
mixture from flow line 102, and gases enter from the bottom through
flow line 113. The reacting mixture is irradiated from above and is
well mixed by virtue of mechanical stirring by agitator 108 and the
action of the gases. Depolymerized hydrocarbons leave the reacting
mixture in the gas phase through line 138. Condensed reflux also
leaves the microwave cavity through flow line 136.
[0058] A small portion of the feedstock material has been observed
to depolymerize to form carbon. In addition, there may be inorganic
materials present in the feedstock as well as materials which
produce significant amounts of carbon or other solids. The contents
of the reactor can be removed periodically by means of a suitable
valve 111 which leads to a vessel 112 which may be removably
disposed. This arrangement provides a mechanism by which excessive
solids accumulation can be handled.
[0059] Optionally, liquid hydrocarbons can be introduced to the
reacting mixture through flow line 132 and reacting mixture can be
withdrawn through flow line 134. Line 134 may be utilized for
feeding into a cascading reactor arrangement as discussed herein.
It will be clear to those skilled in the art that the reacting
mixture in vessel 106 may be considered to be essentially in a
"continuous stirred tank reactor" ("CSTR"). It will consequently
also be apparent that a plurality of such reactors can be connected
in either a series or parallel arrangement in order to change the
residence time distribution and thus overall throughput. It is not
essential to add solid material to each stage when several reactors
are joined together. For example, solid feedstock may be introduced
to the first reactor only, with the other of the plural reactors
performing the reaction process with the solid feedstock introduced
into the first reactor. In further consideration of combinations of
reactors, it may be useful to think in terms of a reaction
parameter, which is defined to be zero for unprocessed feedstock
and 100% when all feedstock which is able to react has reacted. It
should be apparent that important physical properties, such as
liquid viscosity, will be a strong function of the reaction
parameter. For many of the feedstocks under consideration (such as,
for example molten plastic and high boiling point refinery bottoms
residues), the viscosity may start out at a very high value and
drop when the material is partially depolymerized. Towards the end
of the reaction, the effective viscosity becomes very high again
due to the large amount of residual solid carbon present in the
reacting mixture. Batch processing of mixed waste plastics has
shown that the reacting material starts out as an extremely high
viscosity melt. Then, as reaction starts to take place, the melt
viscosity rapidly drops to a moderate value such that the material
is relatively easy to mix and pump. The material remains easy to
mix and pump until the reaction has proceeded to the point that
formation of solid carbon is significant, and this is when it
essentially becomes a solid mass. This general trend is shown
graphically in FIG. 2. It should be noted that good mixing is
essential to ensure that the microwave energy is effectively
deployed.
[0060] It will be clear to those skilled in the art that a serial
cascade of reactors may provide ideal reaction conditions for a
material with physical properties (such as viscosity) as described.
Each reactor in a cascade of CSTRs operates at a constant "reaction
parameter," discussed above, and it is a relatively simple matter
with a cascade of reactors to ensure that the "reaction parameter"
remains in the range where good mixing is obtained for all reactors
in that cascade, because the typical material viscosities allow for
good pumping and good mixing, and thus good reaction conditions for
microwave depolymerization as well as avoiding solids build-up. The
same holds true for arrangements other than series. In particular,
one arrangement that has been found to be useful with a solid
feedstock such as mixed waste plastic is to feed solids in parallel
into two or more reactors which are arranged in series with regard
to the reacting mixture. This allows the reacting mixture in each
reactor to be maintained at conditions close to optimal (in terms
of reaction parameter). Additional reactors, after addition of all
feedstock, in such a cascade can be designed to operate in the
region where conditions are well mixed with the reactants from the
final stage passing into a volume where the residue is allowed to
continue to depolymerize until solid, with or without additional
microwave energy.
[0061] As described above, the walls of the microwave cavity 104
are maintained at a lower temperature than the reacting mixture
105. There are likely to be very strong convection currents in the
vapor space of a cavity, since the reacting mixture (at the bottom
of the cavity) will be typically at about 350 to about 425 degrees
C. while the cavity walls will be at 50 to 120 degrees C. The
temperature differential creates a driving force for circulation as
follows: hydrocarbons cool, condense and run down the walls of the
cavity and are collected as a heavy wax product, leaving the cavity
through flow line 136, and to crude wax tank 160. The uncondensed,
cooled gases recirculate back from the walls to the center of the
vessel and join the vapors leaving the reaction zone.
[0062] In addition to liquid wax, which may be withdrawn through
flow line 136, materials are also withdrawn from the bulk gas
through flow line 138, which keeps in balance non condensable
fractions of the gases added to waveguide and to the reacting mass.
The material passing through flow line 138 may include uncondensed
gases with some of the entrained droplets and particles that did
not condense into the heavy wax. In a simpler form of the apparatus
of FIG. 1, there is no secondary reaction zone and flow line 138 is
close coupled to a device, such as jet scrubber 140 to be described
below, to condense the hydrocarbons. In principle, the hydrocarbons
could be condensed in an exchanger or by direct contact, however
due to the presence of hydrocarbon components which form solids,
such as terephthalic acid, as well as solid carbon, it is
convenient to use a jet scrubber with warm water as a condenser.
Water is convenient as the circulating cooling medium because it
makes it relatively simple to deal with hydrocarbons that form
solid particles, such as wax. In principle, a light liquid
hydrocarbon could be used, instead of water. In the preferred
embodiment, scrubbing and cooling are carried out in two
stages.
[0063] Reference numeral 140 in FIG. 1 denotes a jet scrubber,
which consists of a section of pipe with a high velocity nozzle by
means of which water is introduced axially flowing downwards by
means of flow line 142. Gas from cavity 104 is introduced through
flow line 138. Line 138 is preferably a short length of pipe and
may be sloped towards the jet scrubber, as illustrated in FIG. 1,
from the microwave cavity 104 so that liquids will nm into the
scrubber.
[0064] The operating temperature of the scrubber preferably is
maintained above the melting point of the wax so that the stream
consists of a multi phase mixture of uncondensed gases, water
droplets, hydrocarbon liquid droplets, sooty solids and possibly
terephthalic acid, (in the case of plastics feedstock), and related
materials (solid) which leave the jet scrubber and pass directly
into a separator/settling vessel 144. The separator/settling vessel
144 includes a horizontal section (as illustrated) in which bulk
separation of the phases occurs. The gas phase then passes up
through a vertical section fitted with a mist eliminator 146 and
leaves the top of the separator vessel through flow line 148. The
aqueous liquid accumulates in a boot 150, which is sized to allow
droplets of wax to disengage from the water. The water then passes
by means of flow line 151 to a neutralization tank 192, which is
designed and operates to allow the addition of neutralizing medium,
such as limestone, and then flows through flow line 152 to pump 154
from which it is recirculated back to the scrubber by means of flow
line 142.
[0065] Certain components of mixed waste plastics decompose to form
acidic compounds. In particular PVC and CPVC decompose to form
hydrochloric acid vapor. Limestone may also be added to the feed to
provide the possibility of capturing the hydrochloric acid as
calcium chloride, as a solid in the residue. This treatment removes
a portion of the hydrogen chloride which forms but leaves some
hydrogen chloride in the vapor phase.
[0066] In general, the hydrogen chloride is extremely soluble in
water and therefore dissolves in the circulating water stream which
is used to cool the vapors and condense the hydrocarbon liquid. The
materials used for construction of this section of the apparatus
are chosen so that dilute hydrochloric acid can be tolerated to a
degree. In some cases, the water circulates through a packed bed of
limestone chips in neutralization tank 192, upstream of the spray
nozzle where the water and the vapors are brought into contact. In
cases where there is carbon dioxide present in the vapors, which
happens when carbon dioxide is used as the inerting gas and also
when polyethylene terephthalate is present in the feedstock, the
carbon dioxide dissolves to a degree in the circulating water
stream and in turn the dissolved carbon dioxide enables the
limestone chips to gradually dissolve since calcium bicarbonate is
fairly soluble in water. So in cases where carbon dioxide is
present, the circulating water is buffered by calcium bicarbonate,
and carbon dioxide is liberated as hydrogen chloride is taken into
solution. When there is no carbon dioxide present, the circulating
water has a significantly lower pH, since calcium carbonate
(limestone) is significantly less soluble than calcium bicarbonate.
However, since the water is predominantly a circulating stream with
a small makeup and blowdown, much of the hydrogen chloride is
neutralized as the circulating water (in that case dilute
hydrochloric acid) passes through the limestone bed.
[0067] The waste water from the process in general is therefore a
mixture of calcium bicarbonate and calcium chloride solutions, with
some free hydrochloric acid. The concentration depends on how much
PVC is present in the feed, and the makeup and blowdown ratios.
Since calcium chloride is extremely soluble, it is possible to
operate the process allowing the calcium chloride content of the
waste water to buildup. The waste water can then be further treated
to recover calcium chloride as a byproduct.
[0068] The water temperature of the water in the scrubber is
determined by the high temperature of gas and vapors from the
microwave zone and the cooling effect is due to evaporation of
circulating water. The temperature is preferably set above the wax
melting point. Water flows from a subsequent scrubbing stage by
means of flow line 156 which acts as a balance line and compensates
automatically for evaporative losses. The wax overflows a weir and
leaves by means of flow line 158 which leads to crude wax tank
160.
[0069] Vapors exiting mist eliminator 146 travel in flow line 148
and then pass to a second stage scrubber 162 in which they are
contacted with cool water from flow line 164. The uncondensed gases
as well as condensed water and hydrocarbons together with
circulating water pass into a second separator/settling vessel 166
which may be similar in construction and operation to the first
stage separator/settling vessel 144. Water from the boot 168 of the
second separator/settling vessel 166 passes by means of flow line
170 to a pump 172 with a side stream passing back to the first
settling vessel boot 150 by means of balance line 156. Water from
pump 172 passes through flow line 174 through cooler 176 and thence
back to scrubber 162 by means of flow line 164. Scrubbed vapors
flow through mist eliminator 190 and leave the settling vessel by
means of flow line 178 which passes to the compressor 114 described
above. Wax flows through flow line 188 to crude wax tank 160.
[0070] Water vapor is still present in the gases leaving the second
stage scrubber so that overall there is need for a make-up stream
of water. This is accomplished by means of flow line 184 into
balance tank 182. The vapor space of the balance tank 182 is linked
to flow line 178 by means of balance line 180. The bottom of the
balance tank 182 is linked to the boot 168 of the second stage
separator/settling vessel 166 by means of balance line 186. The
balance tank 182 and the two separator/settling vessels, 144 and
166, are arranged so that gravity suffices to ensure that water
flows between the vessels as needed to maintain the desired levels.
Consequently, overall, there is evaporation of water in the first
stage scrubber and condensation of water in the second stage
scrubber with flow by gravity from second to first stage
separator/settling vessel to compensate for mass loss. The second
stage scrubber 162 will typically condense slightly less water than
the amount evaporated in the first stage, consequently there is a
need for a constant make-up stream. This is handled by means of the
balance line 186 from balance tank 182 with level maintained in
balance tank by adding water through flow line 184.
[0071] Sooty solids will typically be entrained in the wax stream
and will therefore flow to the crude wax tank 160.
[0072] Solids heavier than water, such as terephthalic acid, 4
formyl benzoic acid and similar breakdown products from
polyethylene terephthalate depolymerization will accumulate in the
boots (150,168) of the separator/settling vessels 144, 166 and will
need to be disposed of periodically.
[0073] In summary then, the process takes waste plastic or other
hydrocarbon feedstock solids, recirculated light gases, optionally
liquid waste hydrocarbons (including material from a previous,
similar stage of depolymerization) and produces a stream of heavy
wax, a stream of lighter wax or liquid hydrocarbons, a stream of
surplus gas, intermittently removed heavy solids and a stream of
residue material which may be sent to a subsequent similar stage of
depolymerization or to disposal.
Details of the Microwave Applicator
[0074] Two embodiments of a microwave applicator are illustrated in
FIGS. 3A and 3B, in which reference numeral 300 indicates the
microwave applicator. The microwave applicator of FIG. 3A consists
of a primary cavity 301 which is of sufficient diameter for
microwaves to propagate freely and sufficient length for effective
separation between the entry point of the microwave energy and the
reacting mixture. In the embodiment shown in FIG. 3A, the microwave
applicator includes a pair of circular waveguide ports 302 and
303.
[0075] While two waveguide ports 302 and 303 are shown, it is to be
understood that any number of waveguide ports may be accommodated,
depending on the specific microwave generator(s) used and the
physical dimensions of the reactor vessel.
[0076] Alternatively, a pair of rectangular waveguides entering
from the top could be employed. The applicator, as shown in FIG.
3A, is fed with energy from two microwave generators, (not shown)
simultaneously so it is desirable to ensure that interference is
minimized. Each waveguide may be fitted with a polarizer to induce
one handedness of circular polarization. The same polarizer will
also prevent energy of the opposite handed polarity from
propagating back up the waveguide.
[0077] Commercially available microwave generators are limited in
size, with a typical maximum being approximately 125 kW, but with
75 kW being more typical. The ability of a well constructed cavity
to handle microwave energy may exceed this amount by a significant
margin, and consequently it may be desirable to feed energy from
more than one waveguide at a time. The number of waveguides that
can be accommodated at one time is a matter of the practicality of
accommodating the necessary ports and waveguide. Beyond a certain
point, the economics may favor simply adding additional applicators
rather than additional generators feeding a single applicator.
[0078] Returning now to FIG. 3A, feedstock enters the cavity from
the top through a nozzle 304, which is sized to allow free flow of
solids but to prevent microwave energy from leaving the cavity,
i.e. dimensions suitable to "choke" the microwaves, as is known to
those of skill in the art. In general, the nozzle may be between
4'' and 6'' in diameter to fulfill these requirements.
[0079] An adequately sized nozzle, 305, is provided to act as an
emergency vent in case of over pressurization. Such typically may
be fitted with a bursting disc or similar device and vapors will be
led away to be flared off or safely vented. The size of nozzle 305
is determined by systems engineering considerations and preferably
the nozzle and associated flow line will be small enough that
microwave energy will not propagate along the line. If it is deemed
necessary to use a larger flow line, a suitable microwave choke may
be incorporated into the nozzle.
[0080] The main cavity 301 is surrounded by a jacket for a heat
transfer fluid, and is subdivided into two zones, 306 and 307. The
heat transfer fluid circulates in by means of nozzles 308 and 309
and out through nozzles 318 and 320. This makes it possible to
maintain the upper cavity walls with desired temperature ranges,
which typically may be in the range of about 50 to about 120 deg C.
The design goal is to maintain the cavity wall at a temperature
such that desirable hydrocarbon components are able to condense on
the wall and run out of the cavity. Furthermore, in the event that
there is a significant amount of PVC present, the walls need to be
maintained at a temperature above the acid dew point. Hydrocarbons
which run down the walls flow out of the zone 307 through a wax
outlet 310.
[0081] In operation, feedstock free falls through cavity 301 into
lower cavity 311, which is smaller in diameter than cavity 301 and
attached coaxially to the bottom of cavity 301. The diameter of
lower cavity 311 is such that microwave energy can freely propagate
into the lower cavity. The diameters of the two cavities are such
that arcing does not occur between the top of the inner cavity and
the wall of the outer cavity. The height of protrusion of the inner
cavity into the upper cavity is such that heavy wax does not reflux
into the lower cavity, but rather exits zone 307 through outlet 310
and, ideally, is such that microwave energy in the annular space
between the walls of the two cavities is minimized.
[0082] A pool of reacting mixture is allowed to build up in the
lower cavity 311, but typically does not fill the lower cavity. The
reacting mixture pool is generally in a liquid state and consists
of partially depolymerized feedstock as well as newly-fed
unconverted plastic material and suspended solids. The pool may be
agitated by means of a stirring device 313 or by means of gas added
through bubble cap 314 or similar sparger device, having been
introduced through nozzle 315 or both methods in combination.
Typically, the stirring device will be a flat bladed turbine and
accordingly vertical baffles 316 on the inner wall of cavity 311
may be used to promote good mixing. The agitation serves to help
ensure that the mixture is well mixed. The reacting mixture may
contain sensitizer and may contain catalysts depending on the
desired slate of products. The earlier patent, that is, U.S. Pat.
No. 6,184,427, discloses using the interaction of sensitizer and
microwaves in order to provide heating and depolymerization of
hydrocarbons. The disclosure of U.S. Pat. No. 6,184,427 is herein
incorporated by reference in its entirety into this
specification.
[0083] However, it has been discovered that the process of
microwave depolymerization itself produces a type of carbon which
is a good absorber of microwave energy. Consequently, it is only
necessary, in the process of the present invention, to start out
using a "seed" sensitizer, which is typically activated carbon and
then allowing the system to build the sensitizer up naturally as
the process proceeds and additional carbon is generated. The
microwave energy is understood to be absorbed in the top layer of
liquid, at a rate which depends on the concentration of sensitizer,
which in general decays from the surface approximately
exponentially so that it is reasonable to think in terms of a "half
depth" or a depth at which microwave energy has decayed in
intensity to 50% of the incident amount. It is desirable that the
half depth be in the order of about 10 to about 100 mm so that the
energy is absorbed reasonably uniformly throughout the reacting
mixture. Bulk temperature is maintained reasonably uniform by the
stirring action.
[0084] As illustrated in FIG. 3A, the bottom section 322 of lower
cavity 311 in the vicinity of the bubbler 314 is in a shape of an
inverted cone. This shaped vessel has been found to be beneficial
to facilitate solid settling from the reaction mixture. Turning now
to FIG. 3B, this figure shows the applicator of FIG. 3A in which
all of the corresponding features are the same as in FIG. 3A,
except for the region in the lower cavity bottom. In FIG. 3A, as
described above, the bottom section 322 is first conically shaped
before a cylindrical portion 324, followed by flat bottom wall 326,
whereas in FIG. 3B, the bottom wall of cavity 328 is flat below
cylindrical section 330. It has been found that utilizing a flat
surface rather than a conical surface has the benefit of
facilitating solids removal from the lower reactor cavity.
[0085] While the mechanism is not fully understood, it has been
found that the microwave depolymerization of plastics produces a
higher molecular weight product distribution than appears to be the
case with conventional thermal depolymerization processes with
similar process conditions. As is well understood to those skilled
in the art, conventional heating is slow, relying on convection
currents and thermal conductivity; whereas microwave energy
transfer is rapid and occurs on a molecular level, and can be
explained in terms of instantaneous localized high intensity energy
transfer to the reaction mixture. The result is that microwave
promoted chemical reaction times are much shorter than those based
on conventional heating and occur at significantly lower bulk
temperatures. It may be surmised that this may be due to a
microwave effect or may be a consequence of the rapid heating and
quenching which occurs in the microwave reactor vessel of the
present invention. It is already well understood that microwave
energy couples well to particulate sensitizer. It has also been
observed that a highly effective sensitizer is the carbon which
forms from the microwave depolymerization of hydrocarbon. The
carbon is distributed as fine particles in the bulk liquid. Carbon
dendrites can also be formed in the reactor from carbon particles
due to "step-by-step" joining/combining of these small particles in
the gas space on the solid surface substrate. Very small domains
exist within the reaction mixture where the local temperatures can
be 50 to several hundred degrees Centigrade above the bulk
temperature of the mixture. Microwave depolymerization is
understood to be a free radical reaction which typically requires a
temperature significantly higher than the observed bulk
temperature. It is therefore further surmised that free radical
depolymerization occurs in spatially limited domains and is
followed by immediate quenching in the surrounding bulk mixture.
This appears to limit the amount of secondary depolymerization
which occurs and consequently leads to a product which has a higher
molecular weight distribution than that made under typical prior
art thermal depolymerization mixtures with similar process
conditions.
[0086] Utilizing the preferred embodiment of the invention to
process a feedstock of mixed plastics recovered for municipal solid
waste typically produces a wax with a melting point of 60 degrees
to 70 degrees C. Those skilled in the art will recognize this
melting point as being at least 20 degrees C. in excess of the
melting point of the hydrocarbon mixture typically produced by
conventional thermal depolymerization of the same feedstock.
[0087] The reacting mixture includes a variety of random length
hydrocarbons, derived by degradation of polymers, and including
light hydrocarbons, from about C4 to about C100,000, with typically
75% in the range C40 to C100. Lighter products, in the range of
about C4 to about C60 with typically 75% between C18 and C40, are
removed as a consequence of the flow of gases through the reacting
mixture and pass into the upper cavity. In the upper cavity, there
is a large recirculation of vapor due to the high temperature of
the vapors rising from the central pool compared to the low
temperature of the wall region induced by the cooling jacket. As a
consequence, some of the condensable hydrocarbons form a mist as
cool gas is drawn into the flow of hot vapors. Ultimately, the
heavier hydrocarbons, those, for example, in the range of about C20
to about C60, condense on the walls of the vessel and run out of
nozzle 310 as molten heavy wax. The uncondensed hydrocarbons and
non-condensable gases leave by means of nozzle 317, which is sloped
so that any liquids flow away from the upper cavity. Nozzle 317
leads to a jet scrubbing device by a short flow line, as discussed
above.
[0088] Optionally, nozzles may be installed on the lower cavity and
used to introduce pumpable materials into the reacting mixture as
well as to withdraw the reacting mixture. Examples of pumpable
materials which may be introduced are heavy oils or molten plastic
and partially reacted material from a previous stage of reaction.
The reasons to withdraw such materials are, for example, to send
the material to a subsequent stage for thermal or microwave
processing, to discard heavy residue material and to recover crude
ultra heavy waxes as a product. The materials which leave in the
vapor phase are typically in the carbon number range 9 to 60, with
approximately 75% between carbon number 18 and 40. The material
which remains in the condensed phase is in equilibrium with the
vapor phase and consequently is significantly heavier, with 75%
between carbon number 40 and 100. We have found that the precise
carbon numbers of the vapor and liquid fractions depend on the
severity of microwave depolymerization to which the material has
been subjected. Consequently, if it is desirable to produce an
ultra heavy wax with a specific range of carbon number, one way of
accomplishing this is to reduce or increase the severity of
reaction as well as to increase or reduce the ratio of stripping
gas to feedstock (and consequently the split between vapor and
condensed phases). Thus, by varying the operating conditions, it is
possible to tailor the product weight mixture to at least some
extent.
Filtration and Settling
[0089] The wax produced by microwave depolymerization of plastics
under the process and with the apparatus described above may
contain suspended solids, typically fine carbon formed as a
byproduct of depolymerization and inert materials which were part
of the original waste plastics. This material needs to be removed
from the wax to improve the color. In addition, when polyethylene
terephthalate is present in the feedstock, part of the product of
depolymerization consists of terephthalic acid, 4-formylbenzoic
acid and other, related chemicals which are below the triple point
and therefore which desublimate to form a solid phase as the
hydrocarbon vapor is cooled.
[0090] While these materials can be removed in various different
ways, we have found that it may be advantageous to allow the
material to settle for 4 to 24 hours, maintaining the material at a
temperature above the wax melting temperature, but below water
boiling point, typically 70 to 90 degrees Centigrade; and to keep
the molten wax as a hydrocarbon layer on top of water. This
arrangement enables the solid particulate to settle, and heavy
particles such as terephthalic acid and inorganic matter to fall
out of the hydrocarbon and through the water layer. Solid carbon
tends to be present as extremely fine particulate matter, which is
able to flocculate and settle to the bottom of the hydrocarbon
layer. Due to the hydrophobic nature of this material, it typically
does not fall through the water but rather forms a layer in which
carbon is concentrated at the bottom of the hydrocarbon.
[0091] The hydrocarbon is therefore decanted from a few inches
above the water/hydrocarbon interface level. The material still
contains significant color bodies and typically varies from light
brown to yellow in color. These color bodies and other residual
solids can be removed by filtration. This step improves the
appearance of the product and is a requirement if the product is to
be further treated using catalysts.
Details of the Jet Scrubber and Wax Separator
[0092] As explained above with reference to FIG. 1, uncondensed
hydrocarbon vapors and non condensable gases are sent to a jet
scrubber where they are contacted with water. The water temperature
is maintained above the wax melting temperature and the process is
repeated in a second stage, operating at a lower temperature.
[0093] In FIG. 4, reference numeral 400 denotes a piece of
equipment which receives hydrocarbon mist, vapors and non
condensable gases, contacts them with water and separates the
materials into a vapor phase, a molten wax phase and an aqueous
phase.
[0094] Hydrocarbon vapors, mist and non-condensable gases enter
from the microwave cavity by means of nozzle 401, which slopes
towards the jet scrubber 403. Water is introduced as a spray by
means of nozzle 402 and enters the jet scrubber 403 co-axially and
flows in a downward direction. The vapor and water are intimately
mixed in the jet scrubber, such that the temperature of the gas is
reduced, hydrocarbons condense to form a mist of hydrocarbon liquid
and some immiscible solids (such as terephthalic acid). The water
temperature is deliberately maintained a few degrees above the wax
melting temperature so that the bulk hydrocarbon stream is liquid,
which simplifies separation of hydrocarbons from water. The water
is largely in the form of droplets, although part of the water
impinges on the wall of the scrubber and therefore flows down the
scrubber as a film.
[0095] The jet scrubber 403 is long compared to its diameter,
typically between about 8 to about 20 diameters long. The liquid
and gases from the jet scrubber 403 pass into a horizontal settling
vessel, 404 which has a boot 405 to collect water and a vertical
extension 406 with demister pad 407 to assist in removal of liquids
from the gas stream. The liquid hydrocarbon (molten wax) leaves
through nozzle 410, which protrudes into the vessel to
approximately the halfway line and therefore acts as an overflow
weir. This causes the horizontal vessel to operate half full of
liquid and half full of gas. The upper half of the horizontal
vessel acts as a conventional horizontal settler and supplies
adequate residence time to allow the droplets (water and
hydrocarbon) to settle. Additional settling takes place in the
vertical extension and mist eliminator to ensure a high level of
liquid removal from the gases leaving the device by nozzle 412.
Under/overflow baffle 409 separates the region of the horizontal
vessel below the jet scrubber (where there is much agitation) from
the region downstream of the baffle, where droplets of water
entrained in the bulk hydrocarbon or of hydrocarbon entrained in
the water are able to settle into their appropriate phases.
Similarly a baffle 408 separates the agitated zone from a calmer
zone within the boot 405 where entrained hydrocarbon droplets are
able to settle out of the water. Water finally leaves through
nozzle 411.
[0096] In one embodiment illustrated in FIG. 5, reference numeral
500 denotes the system which includes two stages of scrubbing and
settling followed by a balance tank and a neutralization tank. The
vapor side pressures are essentially constant throughout the
system: the jet ejectors produce a small amount of head from the
momentum of the circulating water, and there are small losses in
the pipes. The net effect is that the pressures are within a few
inches water column of each other between the vessels. The vessels
are arranged to be at appropriate levels and are connected by a
number of water balance lines, as shown in FIG. 5. Water is fed
into the head vessel, 503 by means of flow line 504 and level is
maintained in 503 by level control. Water flows from head vessel
503 into separator vessel 502 through balance line 505 and from
separator vessel 502 into separator vessel 501 through balance line
506 then to neutralization tank 512 through flow line 511 and
finally to circulation pump (not shown) through flow line 513 to
maintain appropriate levels in the vessels. The intent is that,
with only water in the system, the levels in the two separators
should be slightly below, perhaps approximately 1/2'' below, the
wax overflow pipe, so that with only water present there should be
no overflow of water into the hydrocarbon piping. In addition, the
neutralization tank 512 may be full of water, which permeates the
neutralization agent (limestone chips). Vapors enter the scrubber
attached to separator 501 by flow line 507 and from separator 501
to the scrubber attached to separator 502 by means of flow line
508. Gases from separator 502 leave the system by means of flow
line 509, which is connected to the head tank by means of balance
line 510. The gas side piping ensures that the pressures of the
various vessels are essentially constant and only differ by small
amounts. Water circulation equipment (pumps) and flow lines are not
shown in this view.
Hybrid Thermal Microwave Reactor
[0097] As described above, partially depolymerized pumpable
material may be subjected to additional stages of depolymerization,
including thermal depolymerization. Thermal depolymerization may be
advantageous in the context of integration of the overall flowsheet
since it may be desirable to produce at least part of the
electrical energy required to generate microwaves using a
conventional internal combustion engine generator and incondensable
depolymerization products as fuel. The use of such a generator
implies that the exhaust from such generator is a readily available
source of thermal energy which may be advantageously integrated
into the process. Furthermore the oxygen utilization of internal
combustion engines (and gas turbines) is such that additional heat
may be obtained by using the exhaust as preheated gas for a fired
heater.
[0098] The thermal reactor can take various alternative forms, and
can be integrated with the microwave reactor to a greater or lesser
extent, as may be desirable. In a preferred embodiment shown in
FIG. 6, reference numeral 600 denotes the thermal reactor which is
close coupled to the microwave reactor, by adding a "firebox" with
burners and a draft system to the outside of the lower zone of the
microwave reactor. Heat transfer on the process side is aided by
the agitator and baffles (discussed previously). Thus it is
possible to input somewhere in the range 100 to 200 kW of energy at
reasonable efficiency. This is comparable to the amount of
microwave energy used.
[0099] This arrangement has several advantages. In principle,
liquid hydrocarbons pick up heat by convection in the wall region
(where the microwave intensity is weak) and then circulate back
through the microwave zone. With hydrocarbon depolymerization
reactions, there is a well known tradeoff between temperature and
residence time in the reaction zone. In the present case, the
thermal zone is essentially a thin layer close to the wall, in
which area the microwave energy is weak or absent and the microwave
depolymerization zone is largely concentrated in the central part
of the reaction zone, close to the surface and not too close to the
walls. Loosely speaking, the microwave zone (i.e. where microwave
energy is intense enough to promote reaction) is a disc
approximately 100 mm less in diameter than the reactor and approx
15-50 mm thick (depending, of course on a number of factors, such
as how much sensitizer is present and how intense is the
agitation).
[0100] It is entirely possible that little or no depolymerization
takes place in the thermal zone with the reactions delayed to the
microwave depolymerization zone where the presence of microwaves
causes the reactions to occur much more readily than in a thermal
reactor. Consequently the thermal zone may be seen as simple way to
augment the capacity and efficiency of the microwave
depolymerization zone by adding additional energy from an
inexpensive and non-microwave source, rather than solely using
microwave energy.
[0101] The equipment for accomplishing this goal will be described
with reference to FIG. 6. In FIG. 6, as shown earlier in FIG. 3,
300 denotes the microwave applicator described above and in
particular 311 denotes the lower cavity of such applicator.
Reference numeral 601 denotes a furnace enclosure which surrounds
the lower cavity applicator 311. The furnace enclosure 601 may
preferably be lined with a refractory, insulating material. Air or
hot exhaust gases from a diesel generator acting as an oxidant and
fuel gas are burned in a series of up-firing burners, 602, which
are formed in a circle around the lower microwave reactor. The
number of burners is chosen such that and are arranged so that the
outer wall of the lower microwave reactor receives radiant energy
rather uniformly from the burners. The burners will typically be
located close to the refractory wall so that the wall acts to
stabilize the flame and a large amount of the radiation is between
the refractory wall and the reactor wall.
[0102] The radiant section is large enough so that the flames do
not impinge on its walls. Hot gases leave the radiant section
through exhaust nozzle, 605 which can be connected to a stack or
the hot gases can be sucked through a heat recovery device using an
induced draft fan
Additional Processing to Improve Quality of Products
[0103] The typical wax material produced from the process and
apparatus of the present invention is contained after processing in
accordance with the present invention, in crude wax tank 160 shown
in FIG. 1. Crude wax tank 160 is fed by lines 136, 158 and 188, as
described above. It has been found to be a broad boiling range
material, consisting mainly of straight chain paraffinic
hydrocarbons, from pentane through over 100 carbon atoms (with an
average around 18 to 40 depending on processing conditions). The
material also has been found to contain from 5 to 20% olefins,
which are a combination of 1-olefins and internal olefins. The
material has been found to contain from 0 to 2% aromatics and from
0 to 3% branched chain material. The material may also contain
small amounts of nitrogen compounds (<1000 ppm), sulfur
compounds (<100 ppm) and chlorine compounds (<100 ppm).
[0104] The material is typically <5% light ends (<C6), 5%
gasoline range (C6-C8), 20-30% "diesel range" (C9 through C20) and
60-65% "wax" (C21+).
[0105] The material produced by the process and apparatus of FIG. 1
can be further refined by means of the following processing steps,
which can be used singly or in combination, which can be applied at
the same site as the microwave depolymerization unit or in
conjunction with a downstream processing unit and which can be used
to target specific markets: [0106] Short path distillation [0107]
Hydroprocessing [0108] Isomerization [0109] Fractionation These are
described more fully below. Short Path Distillation--gets its name
from the distance in which the vapor stream travels from the
evaporation surface to the condenser. The evaporator wall generates
the vapors as the feed moves by gravity, while being agitated and
distributed evenly, down the evaporator wall. The vapor stream
travels a "short path" directly to the condenser which is located
within the evaporator chamber. It is conventional to operate at a
high vacuum, sometimes an absolute pressure as low as 0.001 mbar.
It is convenient for the microwave depolymerized wax product as
secondary depolymerization is prevented, which is desirable. When
short path distillation is applied, the wax product has greatly
improved properties and can be used directly in certain
applications. The overhead product, obtained by condensing the
volatiles, is suitable for blending with petroleum derived
hydrocarbons which may be used as a diesel product. The material
condensed has desirable properties as a diesel blendstock (high
cetane number), and in blending is limited by either the amount of
olefins (which impacts the bromine number spec), the amount of
sulfur (in the case of ULSD), or the amount of nitrogen.
[0110] In some cases, it may be better to use a Wiped Film
Evaporator, rather than a short path still, but the same
observations apply.
[0111] In still other cases, conventional distillation equipment is
appropriate.
Hydroprocessing--this is understood to encompass several distinct
reactions which in practice often occur together: hydrogenation of
olefin bonds, hydrodesulphurization of organic sulfur compounds,
hydrodenitrogenation of organic nitrogen compounds,
hydrodepolymerization, and to a limited extent, isomerization. With
the microwave wax product, it is useful to distinguish between
commercial situations in which hydrodepolymerization is desirable
and those in which it is not desirable. Thus, in a situation where
a high quality wax product is required, it is useful to have mild
conditions present in which hydrogenation, hydrodesulphurization
and hydrodenitrogenation take place but in which
hydrodepolymerization and isomerization are limited. FIG. 7 depicts
a typical processing arrangement which targets high quality wax. In
FIG. 7, 700 depicts the hydroprocessing unit. Wax product is first
pumped from crude wax tank 160 through a line (not shown) to the
hydroprocessing unit 700. Crude wax is then pumped to pressure
(typically about 300 to about 900 psi) using a charge pump 701,
then preheated in Feed Effluent exchanger 702 and mixed with
recycled hydrogen. The mixture is taken to reaction temperature
(typically about 600 to about 750 deg F.) in fired heater 703. The
mixture is passed across a hydrotreating catalyst (such as a CoMoS
or NiMoS) with a liquid hourly space velocity of between about 0.5
and 5 hours in reactor 704. Recycle hydrogen may be introduced
between packed beds of catalyst in the reactor 704 in order to
control the temperature rise. The reactor is typically a trickle
bed, in which liquid and vapor phases are both present and flow
together through a packed bed of solid catalyst. The reactor
effluent is cooled in Feed Effluent exchanger 702 and a small
amount of process water is added (to dissolve ammonia liberated by
the hydrogenation of nitrogen compounds). The reactor effluent is
cooled further in air cooler 705 and separated into two liquid
phases and a vapor phase in high pressure separator 706. The raw
wax typically contains more nitrogen than sulfur and consequently
the aqueous stream condensed will consist of ammonia and ammonium
sulfide and it may not be necessary to employ a separate H2S
absorber. The vapor from the high pressure separator is circulated
back to the reactor, using compressor 708. A small amount of the
vapor is purged (to control concentration of inerts and low
molecular weight hydrocarbons) and hydrogen is added by means of
make up compressor 707.
[0112] The liquid stream from the high pressure flash drum 706 is
let down into low pressure flash drum, 710, to release dissolved
gases. The drum is designed as a three phase separator and the
aqueous stream, containing ammonia and dissolved hydrogen sulfide,
commonly known in the trade as sour water, is removed separately
from the hydrocarbon liquid stream and the aqueous stream is
treated for disposal (typically by stripping and incinerating the
ammonia and hydrogen sulfide and passing the stripped water to a
waste water treatment plant).
[0113] The vapor stream from flash drum 710 contains a significant
amount of C21+ wax material and the liquid hydrocarbon from flash
drum 710 contains a significant amount of diesel (likely about
C9-C20). Therefore, it is typical to employ some form of
fractionation. In FIG. 7, the vapor and liquid streams pass from
flash drum 710 to a distillation column 711 with reboiler and
condenser, which strips C20-hydrocarbons from the wax and produces
fuel gas as an overhead product, and a distillate stream in the
diesel/kero range as a side draw.
[0114] This processing scheme produces a high quality, highly
parafinnic diesel blendstock and a high quality wax.
Isomerization--can be carried out for different purposes and in
different ways. If the processing objective is to produce high
quality wax and very high quality diesel blendstock (which will not
degrade the cold flow properties of the diesel), an appropriate
processing scheme would incorporate a bed of isomerization catalyst
to treat the vapor phase (only) which leaves the flash downstream
of the hydrotreating reactor in the above described processing
scheme. The distillate and naphtha range materials would therefore
be isomerized and the balance of the processing scheme can be as
before. This will lead to diesel blendstock with improved cold flow
properties and high quality wax as products.
[0115] A second scenario in which isomerization may be desirable is
to produce lube base oil as one of the end products of the process
of the present invention. This processing scheme is similar to that
described above except that the catalyst is different and the
processing conditions are of somewhat higher severity (temperature
and pressure). Essentially in this scenario, the catalyst is a
hydrodepolymerization catalyst, operated under mild conditions.
[0116] A third scenario would use essentially the same
configuration but with more severe hydrodepolymerization
conditions. This would lead to a higher yield of diesel material
and less lube base oil.
[0117] The detailed descriptions above in connection with the
corresponding figures are intended to illustrate the present
invention, and are not intended to represent the only forms in
which the present invention may be constructed and/or utilized.
While the descriptions set forth the structure and the sequence of
steps for practicing the present invention in connection, it is to
be understood, however, that the same or equivalent structures and
steps may be accomplished by different embodiments that are also
intended to be encompassed within the spirit and scope of the
invention. Accordingly, it is not intended that the invention be
limited except by the claims.
[0118] It is noted that one or more references are incorporated
herein. To the extent that any of the incorporated material is
inconsistent with the present disclosure, the present disclosure
shall control. Furthermore, to the extent necessary, material
incorporated by reference herein should be disregarded if necessary
to preserve the validity of the claims.
[0119] Further, while the description above refers to the
invention, the description may include more than one invention.
* * * * *