U.S. patent application number 13/341828 was filed with the patent office on 2012-04-26 for flexible circuit chemistry.
This patent application is currently assigned to SRI INTERNATIONAL. Invention is credited to Jaspreet Singh Dhau, Sunity Sharma.
Application Number | 20120100286 13/341828 |
Document ID | / |
Family ID | 45532224 |
Filed Date | 2012-04-26 |
United States Patent
Application |
20120100286 |
Kind Code |
A1 |
Sharma; Sunity ; et
al. |
April 26, 2012 |
FLEXIBLE CIRCUIT CHEMISTRY
Abstract
The present invention provides a circuit creation technology
that improves conductive line manufacture by adding active and
elemental palladium onto the surface of a substrate. The palladium
is disposed in minute amounts on the surface and does not form a
conductive layer by itself, but facilitates subsequent deposition
of a metal onto the surface, according to the pattern of the
palladium, to form the conductive lines.
Inventors: |
Sharma; Sunity; (Fremont,
CA) ; Dhau; Jaspreet Singh; (Menlo Park, CA) |
Assignee: |
SRI INTERNATIONAL
Menlo Park
CA
|
Family ID: |
45532224 |
Appl. No.: |
13/341828 |
Filed: |
December 30, 2011 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11854271 |
Sep 12, 2007 |
8110254 |
|
|
13341828 |
|
|
|
|
60999732 |
Sep 12, 2006 |
|
|
|
Current U.S.
Class: |
427/125 |
Current CPC
Class: |
H05K 2203/0709 20130101;
Y10T 428/2857 20150115; H05K 1/0393 20130101; H05K 3/182 20130101;
H05K 3/1283 20130101; Y10S 428/901 20130101; Y10T 428/24917
20150115 |
Class at
Publication: |
427/125 |
International
Class: |
B05D 5/12 20060101
B05D005/12 |
Claims
1. A method for producing active palladium on a substrate, the
method comprising: depositing a palladium precursor solution onto
the substrate, wherein the palladium precursor solution includes a
palladium compound in a solvent; exposing the palladium precursor
solution to conditions that promote evaporation of the solvent from
the palladium precursor solution to leave a palladium precursor on
the substrate; and decomposing the palladium precursor on the
substrate to produce active palladium, wherein the active palladium
is monatomically disposed on the substrate in the form of single
isolated atoms.
2. The method of claim 1, wherein the active palladium does not by
itself form a conductive layer on the substrate.
3. The method of claim 1, wherein the active palladium has a
concentration of less than about 6.times.10.sup.-10 gram atoms of
palladium per square millimeter.
4. The method of claim 1, wherein depositing the palladium
precursor solution onto the substrate includes patterning the
palladium precursor solution to substantially define an active
palladium pattern.
5. The method of claim 1, wherein decomposing the palladium
precursor includes transferring heat to the substrate.
6. The method of claim 1, wherein decomposing the palladium
precursor includes transferring electromagnetic radiation to the
substrate or the palladium precursor.
7. The method of claim 1, wherein the substrate is flexible.
8. The method of claim 1, wherein the substrate has a thickness
less than about 2 millimeters.
9. The method of claim 1, wherein the palladium precursor solution
includes at least palladium propionate, amyl acetate and
cyclopentylamine
10. The method of claim 1, wherein said resulting palladium
precursor disposed on the substrate has a valence of about
zero.
11. A method for producing active palladium on a substrate, the
method comprising: providing a solution comprising palladium
propionate, amyl acetate and cyclopentylamine; depositing at least
a portion of the solution onto the substrate; removing all solvent
from the solution to leave a palladium precursor on the substrate;
and decomposing the palladium precursor to leave active palladium
on the substrate.
12. The method of claim 11, wherein the active palladium is
monatomically disposed on the substrate in the form of single
isolated atoms.
13. The method of claim 11, wherein the active palladium does not
by itself form a conductive layer on the substrate.
14. The method of claim 11, wherein said depositing includes
patterning the solution to result in a substantially defined
pattern of palladium.
15. The method of claim 1, wherein said depositing includes the use
of a printing apparatus.
16. A method for producing a metallic precursor on a substrate, the
method comprising: depositing a metallic precursor solution onto
the substrate, wherein the metallic precursor solution includes a
metal compound in a solvent; exposing the metallic precursor
solution to conditions that promote evaporation of the solvent from
the metallic precursor solution to leave a metallic precursor on
the substrate; and decomposing the metallic precursor on the
substrate to produce an active metal, wherein the active metal is
monatomically disposed on the substrate in the form of single
isolated atoms.
17. The method of claim 16, wherein said active metal comprises
palladium.
18. The method of claim 16, wherein the active metal does not by
itself form a conductive layer on the substrate.
19. The method of claim 16, wherein said depositing includes
patterning the solution to result in a substantially defined
pattern of metal.
20. The method of claim 16, wherein said depositing includes the
use of a printing apparatus.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of and claims priority
from co-pending and commonly owned U.S. patent application Ser. No.
11/854,271, entitled "FLEXIBLE CIRCUIT CHEMISTRY," filed Sep. 12,
2007, which in turn claims priority from U.S. Provisional
Application No. 60/999,732, entitled "FLEXIBLE CIRCUITS," filed
Sep. 12, 2006, both of which name Sunity Sharma et al. as
inventors, and both of which are incorporated by reference herein
in their entirety and for all purposes.
[0002] This application also relates to U.S. patent application
Ser. No. 11/854,274, which was filed on Sep. 12, 2007, naming S.
Sharma et al. as inventors, and which is also incorporated by
reference herein in its entirety and for all purposes.
BACKGROUND
[0003] This invention relates to precursors used to facilitate the
deposition of a metal onto a surface, such as metal used to form
conductive lines in a circuit. In particular, the invention relates
to printing circuit precursors on a wide variety of substrates
including flexible and non-flat substrates.
[0004] Circuit manufacturers employ numerous techniques to deposit
a conductive pattern on a substrate. One technique applies a
conductive seed layer to the substrate to facilitate subsequent
electro/electroless plating of a metal that forms conductive lines
in the conductive pattern. The conductive seed layer alone is
insufficient to reliably serve as the conductive lines in a
circuit, but uses large amounts of the seed material to maintain
conductivity for subsequent metal addition. Another technique uses
an adhesive layer to attach a conductive layer to the substrate.
The adhesive layer, however, adds thickness to the final circuit,
which is undesirable for circuits employed in portable and small
form factor applications. Circuit manufacturers have also developed
etching processes that apply a photoresist, etch the photoresist to
form a pattern, add metal to form conductive lines according to the
pattern, along with other process steps such as washes to cleanse
byproducts from each stage. These numerous etch steps increase
manufacturing complexity, add disposal requirements for etch
by-products, lengthen manufacturing time, and the pattern and etch
equipment raises capital cost for circuit manufacture. All these
downsides burden circuit manufacturers by adding to manufacturing
complexity and circuit cost.
[0005] Also, most conductive pattern manufacturing processes limit
their circuits to rigid substrates. For example, a seed conductive
layer needs an inflexible substrate to physically support the
continuous seed layer. If the substrate bends, then the continuous
and conductive seed lines crack and break, which compromises
subsequent metal deposition.
[0006] The ability to manufacture a conductive pattern without
these undue complexities and limitations would be desirable.
SUMMARY
[0007] The present invention improves conductive pattern formation
and adds active and elemental palladium onto the surface of a
substrate. Active palladium is palladium metal that has two
desirable properties: it is catalytic for subsequent addition of a
metal onto the palladium, and it is strongly anchored to the
underlying substrate. The active palladium is disposed in minute
amounts on the surface and does not form a conductive layer by
itself, but facilitates subsequent deposition of a metal onto the
surface, according to the pattern of the palladium, to form a
conductive pattern. The conductive pattern may include one or more
conductive lines, or a block deposition of metal according to other
shapes that do not resemble lines.
[0008] This conductive pattern formation is well suited for use in
circuit manufacture, and find wide use to create both existing and
new products. For example, the present invention enables and eases
printing of conductive lines onto flexible substrates and
substrates with custom shapes.
[0009] In one embodiment, the active palladium is disposed on the
surface by first depositing palladium precursor solution onto the
substrate; evaporating solvent from the solution, and then
decomposing a palladium precursor (left after the evaporation) to
produce active palladium on the substrate surface. The active
palladium may or may not be patterned to regulate subsequent
deposition of a metal according to the pattern. Active palladium
patterning may be accomplished during solution deposition on the
surface or during decomposition, for example.
[0010] In one aspect, the present invention relates to a method for
producing active palladium on a substrate. The method includes
depositing a palladium precursor solution onto the substrate; the
palladium precursor solution includes a Lewis base ligand and a
palladium compound in a solvent. The method also includes exposing
the palladium precursor solution to conditions that promote
evaporation of the solvent from the palladium precursor solution to
leave a palladium precursor on the substrate. The method further
includes decomposing the palladium precursor to produce a pattern
of active palladium on a surface of the substrate, wherein the
active palladium approximately has a zero valence.
[0011] In another aspect, the present invention relates to another
method for producing active palladium on a substrate. The method
includes providing a solution comprising a) a Lewis base ligand and
b) a palladium carboxylate having three to five carbon atoms in c)
a solvent. A suitable organic solvent may include an aprotic and
polar solvent. The method also includes depositing a portion of the
palladium precursor solution onto the substrate. The method further
includes removing the solvent to leave a palladium precursor on the
substrate. The method additionally includes decomposing the
palladium precursor to leave active palladium on the substrate.
[0012] In yet another aspect, the present invention relates to a
circuit precursor that includes a substrate and a pattern of active
palladium on a surface of the substrate. The active palladium does
not form a conductive layer on the substrate and has a surface
concentration of less than about 6.times.10.sup.-10 gram atoms of
palladium per square millimeter.
[0013] In still another aspect, the present invention relates to a
method for providing a palladium precursor solution for use with a
printer. The method comprises adding a Lewis base ligand and a
palladium carboxylate to a solvent to create a palladium precursor
solution. The method also comprises storing the palladium precursor
solution in a printing reservoir for use with the printer, which is
configured to transfer the palladium precursor solution from the
reservoir onto a substrate.
[0014] In another aspect, the present invention relates to a
circuit that includes a substrate, a pattern of active palladium on
a surface of the substrate, and a set of conductive lines that
include a metal and are disposed on the substrate according to the
active palladium pattern. The active palladium does not form a
conductive layer on the substrate and has a surface concentration
of less than about 6.times.10.sup.-10 gram atoms of palladium per
square millimeter.
[0015] In yet another aspect, the present invention relates to a
method for producing one or more conductive lines on a substrate.
The method includes depositing a palladium precursor solution onto
the substrate, wherein the palladium precursor solution includes a
Lewis base ligand and a palladium compound in a solvent. The method
also includes exposing the palladium precursor solution to
conditions that promote evaporation of the solvent to leave a
palladium precursor on the substrate. The method further includes
decomposing the palladium precursor to leave active palladium on
the substrate, wherein the active palladium approximately has a
zero valance. The method additionally includes depositing a metal
on the substrate according to a pattern of the active palladium on
the substrate to form one or more conductive lines.
[0016] In still another aspect, the present invention relates to a
structure including a substrate, a conductive layer disposed on the
substrate, and a layer of active palladium disposed between the
substrate and the conductive layer. The active palladium does not
form a conductive layer on the substrate without depositing a metal
or conductive material layer and has a surface concentration of
less than about 6.times.10.sup.-10 gram atoms of palladium per
square millimeter.
[0017] In another aspect, the present invention relates to a method
for printing a palladium precursor on a flexible substrate. The
method includes printing a palladium precursor solution onto the
substrate using a printer. The palladium precursor solution
includes a Lewis base ligand and a palladium compound in a solvent.
The method also includes exposing the palladium precursor solution
to conditions that promote evaporation of the solvent from the
palladium precursor solution to leave a palladium precursor on the
substrate.
[0018] In yet another aspect, the present invention relates to a
printing apparatus for printing a circuit or a circuit precursor.
The printing apparatus comprises a reservoir configured to contain
a palladium precursor solution. The solution includes a solvent, a
Lewis base ligand in the solvent, and a palladium carboxylate in
the solvent, wherein the palladium carboxylate has six carbon atoms
or less. The printing apparatus also comprises a dispensing
mechanism configured to transfer the palladium precursor solution
from the reservoir to a substrate.
[0019] In still another aspect, the present invention relates to a
liquid for use with a printer to produce a metal precursor pattern
on a substrate. The liquid includes a palladium precursor solution
suitable for printing in the printer onto the substrate. The
solution includes a solvent, a Lewis base ligand in the solvent,
and a palladium carboxylate in the solvent.
[0020] In another aspect, the present invention relates to a liquid
for use with a printing apparatus to produce a metal precursor
pattern on a substrate. The liquid includes a palladium precursor
solution suitable for printing in the printing apparatus onto the
substrate. The solution includes a solvent, a Lewis base ligand in
the solvent, and a palladium carboxylate in the solvent. The
palladium precursor solution is adapted to a rheological property
of a fluidic dispensing requirement of the printing apparatus.
[0021] In yet another aspect, the liquid includes an additive that
adjusts a rheological property of the palladium precursor solution
to a rheological property of a fluidic dispensing requirement of
the printing apparatus
[0022] These and other features and advantages of the invention
will be described in more detail below with reference to the
associated figures.
BRIEF DESCRIPTION OF THE DRAWINGS
[0023] FIG. 1 shows a method for producing active palladium on a
substrate in accordance with one embodiment of the present
invention.
[0024] FIG. 2 shows a method for manufacturing a printed circuit on
a substrate in accordance with one embodiment of the present
invention.
[0025] FIG. 3 shows simplified cross sections of exemplary
manufactured components obtained using the manufacturing of FIG. 2
in accordance with one embodiment of the present invention.
[0026] FIG. 4A illustrates an exemplary active palladium pattern on
a surface of a circuit in accordance with a specific embodiment of
the present invention.
[0027] FIG. 4B shows an illustrative microscopic view of a single
palladium line from FIG. 4A.
[0028] FIG. 4C illustrates initial radial growth of copper from the
palladium atoms on a surface of a substrate, according to growth
that might be witnessed in an electroless plating process for
example.
[0029] FIG. 4D illustrates a circuit produced according to the
exemplary active palladium pattern of FIG. 4A.
[0030] FIG. 5 shows the production of a printing reservoir that
stores palladium ink in accordance with one embodiment of the
present invention.
[0031] FIG. 6A shows the printing reservoir used with a printing
apparatus in accordance with one embodiment of the present
invention.
[0032] FIG. 6B shows a printing reservoir that includes palladium
precursor solution in accordance with a specific embodiment of the
present invention.
[0033] FIG. 7 shows an expanded cross section of a structure in
accordance with a specific embodiment of the present invention.
[0034] FIG. 8 illustrates a continuous throughput manufacturing
process in accordance with one embodiment of the present
invention.
[0035] FIG. 9A illustrates an exemplary RFID device in accordance
with a specific embodiment of the present invention.
[0036] FIG. 9B illustrates the automated manufacturing process of
the RFID device of FIG. 9A according to techniques of the present
invention.
[0037] FIG. 9C shows exemplary printed output of the manufacturing
process of FIG. 9B, which includes numerous RFID devices on a roll
material, in accordance with a specific embodiment of the present
invention.
[0038] FIG. 10A shows a tracking label that includes a layered
design in accordance with a specific embodiment of the present
invention.
[0039] FIG. 10B shows an inner surface of a housing used in a cell
phone that includes a conformal surface and circuit printed thereon
in accordance with a specific embodiment of the present
invention.
DETAILED DESCRIPTION
[0040] The present invention will now be described in detail with
reference to a few preferred embodiments thereof as illustrated in
the accompanying drawings. In the following description, numerous
specific details are set forth in order to provide a thorough
understanding of the present invention. It will be apparent,
however, to one skilled in the art, that the present invention may
be practiced without some or all of these specific details. In
other instances, well known process steps and/or structures have
not been described in detail in order to not unnecessarily obscure
the present invention.
[0041] Circuit manufacturing methods described herein deposit a
metal precursor to a substrate, before adding one or more
conductive lines. The metal precursor refers to a metal, typically
in elemental form, that catalyzes the deposition of another metal
onto a surface. Copper is a common metal that is added to form
conductive lines. Numerous established metal plating processes,
such as electro/electroless plating, are used in circuit
manufacturing to deposit copper onto a surface to form the
conductive lines, and benefit from a metal precursor as described
herein. High-resolution circuits and circuit boards may be printed
in this manner--on flexible substrates and custom shaped surfaces.
Metallic and non-metallic substrates may also be used in the
circuits, including thermoplastic substrates, thermosetting resins,
glass, ceramics, semiconductor materials including silicon,
etc.
[0042] Active palladium is a metal precursor that works well with
many substrates and copper deposition techniques. The active
palladium has two desirable properties: (1) it is catalytic for
subsequent addition of a metal onto the palladium (such as
electroless deposition), and (2) it is strongly anchored to the
underlying substrate. In one embodiment, the active palladium
approximately has a zero valance. The active palladium is also
ideally disposed monoatomically onto the substrate. One of skill in
the art will appreciate that elemental palladium does not readily
bind to a surface monoatomically or with an approximately zero
valance, and needs to be deliberately processed to achieve such a
state. Described below are processing techniques to accomplish
this.
[0043] FIG. 1 shows a method 50 for producing a metal precursor
such as active palladium on a substrate in accordance with one
embodiment of the present invention. Although the present invention
will now be described as a method, those of skill in the art will
recognize that description provided for the following steps and
method may also apply to one or more apparatus used to implement
the methods and/or a device produced by the steps and method.
[0044] FIG. 2 shows a method 70 for manufacturing a printed circuit
on a substrate in accordance with one embodiment of the present
invention, which includes the metal precursor patterning steps
52-56 of FIG. 1 in addition to several steps related to circuit
design and manufacture. FIG. 3 shows simplified cross sections of
exemplary manufactured components obtained using the manufacturing
of FIG. 2 in accordance with one embodiment of the present
invention.
[0045] Beginning with FIG. 1, metal precursor patterning method 50
begins by depositing a palladium precursor solution onto a
substrate 20. In one embodiment, the palladium precursor solution
includes a Lewis base ligand and a palladium compound in a solvent.
Further description of palladium precursor solutions and chemical
constituents included therein are described in further detail
below.
[0046] The palladium precursor solution is exposed to conditions
that promote evaporation of the solvent from the palladium
precursor solution, to leave a palladium precursor on the substrate
(54). Typically this includes supplying heat to the substrate
and/or solution via conduction, convection and/or radiation. For
example, a field evaporation using convection is suitable for many
printing applications. While the goal of this evaporation step is
generally to remove as much as the solvent as possible, it is
understood that incomplete solvent evaporation is suitable for many
embodiments. In this case, additional heat or energy supplied in
the next step may complete the evaporation process.
[0047] In one embodiment, evaporation at least partially occurs
before the droplets of palladium precursor solution settle on the
substrate. In some cases, the method expedites evaporation by
pre-heating the palladium precursor solution while it is being
deposited on to the substrate. Depending on the substrate,
evaporating the solvent before or during decomposition reduces
local inaccuracies that may result from the active palladium (which
is so reactive that it may bind to the solvent) attaching to the
solvent residue.
[0048] Method 50 then decomposes the palladium precursor to produce
a pattern of active and elemental palladium on a surface of the
substrate (56). The decomposition adds energy to the palladium
precursor to separate and remove the ligand from the elemental
palladium, thereby leaving the elemental palladium on the surface.
As will be described in further detail below, the decomposition
facilitates the deposition of monoatomic and elemental palladium
with approximately zero valence on the substrate. In one
embodiment, the decomposition converts the palladium precursor from
a palladium cation to active palladium atoms with approximately
zero valence on the substrate.
[0049] Decomposition and de-ligation may be accomplished in various
manners. Generally speaking, the decomposition apparatus provides
electromagnetic radiation and energy to the substrate and/or
palladium precursor. Suitable energy sources may include thermal
sources, light sources such as a laser, infrared and ultraviolet
heaters, ion beams, e-beams, microwave sources, and combinations
thereof. The radiation source may be coherent or non-coherent. In
one embodiment, electromagnetic radiation tuned to a particular
wavelength is employed to minimize thermal energy transfer and
emphasize chemical reaction. For example, ultraviolet radiation may
be employed to promote many different chemical decomposition
reactions. Further, microwave energy may be employed for palladium
inks where the anion or ligand has hydroxyl groups, as the hydroxyl
absorbs radiation in the microwave range. Decomposing a palladium
precursor may be performed in the same chamber as the evaporation
process, or a different one.
[0050] Spatial control for the decomposition is useful when a
pattern has not already been established, e.g., during deposition
of the solution onto the substrate. In a specific embodiment, a
guided laser, ion beam or e-beam, is employed to provide a pattern
on the surface by locally decomposing the palladium precursor
according to the beam movement.
[0051] Decomposition proceeds sensitive to the substrate. For
example, melting temperature of the substrate--relative to the
decomposition temperature of the palladium precursor--will affect
temperatures used during decomposition. If the substrate melting
temperature is higher than the decomposition temperature for the
palladium precursor, then decomposition may use heat at a
temperature between the two without compromising the substrate. In
another embodiment where the substrate melting temperature is less
than or near the decomposition temperature of the palladium
precursor, the decomposition provides heat (or another form of
energy) to the palladium precursor at short bursts or pulses to
overcome the decomposition threshold of the palladium precursor,
while avoiding damage to the substrate. This is also useful for any
relationship between the substrate melting (or softening)
temperature and the decomposition temperature for the palladium
precursor (e.g., when the substrate melting temperature is greater
than the decomposition temperature of the palladium precursor) to
save energy for the decomposition.
[0052] In one embodiment, a pattern of active palladium is formed
when the palladium precursor solution is deposited on the
substrate. This permits evaporation and decomposition to be
spatially imprecise. Subsequent evaporation and decomposition of
the palladium precursor then occurs spatially on the substrate
according to the established pattern of solution and palladium
precursor. For example, various liquid printing technologies such
as conventional inkjet printers may be used to pattern the
palladium precursor solution at desired locations on a flat or
non-flat substrate. Resolution of the active palladium pattern then
relates to the spatial resolution of the printing technology used
to dispense the solution.
[0053] In a specific embodiment, decomposition (56) only occurs
after evaporation (54) in order to avoid smudging of a deposited
palladium precursor solution pattern and compromise of a spatially
precise pattern. Further discussion of palladium precursor solution
printing is described with respect to FIG. 6A.
[0054] In another embodiment, the palladium precursor solution is
deposited without a pattern, and localized decomposition forms a
pattern of active palladium from a blanket layer of palladium
precursor. For example, a guided laser, ion beam or e-beam may be
used to scribe specific locations on a blanket sheet of palladium
precursor on a surface, according to a desired pattern. 2-D or 3-D
beam control then permits the active palladium pattern to be
produced on custom shaped 2-D or 3-D surfaces, with a pattern
resolution determined by beam actuation and guidance.
[0055] Output of method 50 of FIG. 1 is a circuit precursor that
includes active palladium on a surface of the substrate (patterned
or not patterned). FIG. 2 expands active palladium production of
method 50 for the production of a circuit.
[0056] Method 70 begins by selecting a suitable substrate (72). The
choice of substrate is typically driven by a particular application
for the palladium ink pattern. At a high level, the substrate may
be conductive, semi conductive, or insulating. Thus, the dielectric
constant of the material may be of any value. The substrate may be
homogeneous or heterogeneous in terms of the material it is made
from. As an example of a heterogeneous substrate, packaging for a
semiconductor chip includes a dielectric substrate on which
conductive vias are formed. Line traces defined by a palladium ink
pattern may be patterned to connect one conductive via to another
or a conductive via to an external lead or pin.
[0057] The substrate can be flat or topologically varying. An
example of a non-flat substrate is the inner casing of a cell phone
that has a convex and custom shape. As another example, pins on a
connector may be printed with palladium ink The connector may also
include a custom or non-flat shape.
[0058] Also, the substrate may be rigid, flexible or semi rigid.
There are multiple ways to characterize a flexible substrate,
including elastic modulus and/or thickness. In one embodiment, a
flexible substrate includes an elastic modulus less than about 1
GPa. In a more specific embodiment, a flexible substrate includes
an elastic modulus less than about 100 MPa. In one embodiment, a
flexible substrate includes a thickness less than about 1
centimeter. In a more specific embodiment, the thickness is less
about 1 millimeter. A higher modulus of elasticity and/or thickness
may also be used.
[0059] One substrate of particular interest is polyimid. Polyimid
(also sold as Kapton.RTM.) is commercially available in thin
sheets, is suitable for printing using many printers such as
commercially available ink jet printers, and is also suitable for
circuit applications that include a flexible substrate. Polyimid
also includes a robust thermal stability that can withstand
dual-stage heating as described in FIG. 1. Conventionally,
adhesives are used to attach palladium to polyimid. The adhesives
remain in the finished circuit but do not survive elevated circuit
temperatures and thus compromise the thermal stability of polyimid
circuits (in addition to adding thickness as described above). The
present invention, however, maintains thermal stability of circuits
constructed with high temperature substrates such as polyimid, in a
thinner profile.
[0060] Other exemplary substrates may include polyester,
polypropylene, polyethylene, ceramic materials, or any other good
dielectric material. The substrate onto which the palladium
precursor is deposited, and subsequently a palladium layer and
conductive lines formed, can also be a metallic material. Also, the
substrate can be plastic, ceramic, glass, silicon wafer, cellulose,
graphite, and paper substrates. Paper readily permits printing
using commercially available and general-purpose printers. In
general, substrate selection is driven by an application. Many
rigid circuit board applications use silicon wafers and Fr4
substrates.
[0061] The present invention may also use fibrous materials as a
substrate, such as those used in a weave. For example, Kevlar
strands may be dipped in a palladium precursor solution and further
processed according to FIG. 1 to leave active palladium on the
individual strands. The strains may then be woven according to
conventional weaving techniques before or after copper or
conductive lines are disposed on the strands (e.g. by electroless
and electroplating).
[0062] Returning back to FIG. 2, the substrate may be pre-treated
or cleaned, before the palladium precursor solution is added, to
facilitate subsequent processing. Various cleaning processes are
suitable for use, as one of skill in the art will appreciate. For
example, a bath in isopropanol simply and inexpensively cleans many
polymer surfaces. Cleaning is not necessary. One advantage of the
invention is that the substrate requires relatively little or
sometimes no treatment prior to deposition of the palladium
precursor solution and forming of copper lines.
[0063] The palladium precursor solution is then provided for
printing (74). More detail on solution chemistry is provided below,
in addition to examples of reservoirs for storing and shipping the
palladium precursor solution (FIGS. 5, 6A and 6B).
[0064] Palladium deposition then proceeds according to FIG. 1
(steps 52-56). Output of method 50 is a pattern of palladium on a
surface of the substrate, where the pattern substantially resembles
a desired conductive line or circuit pattern.
[0065] A pattern of active palladium refers to one or more surface
areas on a substrate that the active palladium occupies after
decomposition. As will be described further below, the pattern may
be established at a number of stages, e.g., during deposition using
a printer or during decomposition using a spatially controlled
decomposition beam. In one embodiment, the pattern includes a set
of active palladium lines disposed on one or more surfaces of the
substrate. Often, the pattern resembles a set of conductive lines
to be subsequently produced using the pattern of active palladium.
FIG. 4A illustrates an exemplary active palladium pattern 105 on a
surface 21 of a circuit 100 in accordance with a specific
embodiment of the present invention. Exemplary patterns also
include circles, rectangles, sets of concentric circles or
rectangles used for an antenna, etc. In general, the present
invention is not limited to any specific pattern, and contemplates
that the pattern may take any geometric arrangement.
[0066] In another embodiment, the pattern is a field deposition
that covers a large portion of the substrate surface. Thus, an
active palladium and conductive layer may also be field deposited
on a substrate using methods described herein. FIG. 7 shows an
expanded cross section of a substrate structure with a field
deposition, without patterning of the active palladium 22, in
accordance with a specific embodiment of the present invention.
[0067] The field deposition can be considered a blanket pattern,
and has many uses. For example, a field coating is well suited for
electromagnetic shielding or antenna manufacture. A field coating
is also well suited for irregular shaped objects. In this case, the
irregular shaped object--such as a strip of hook and loop
fasteners, a brush, or a sponge--is dipped in a palladium precursor
solution to apply a field deposition to the many and minute
features (and the solution decomposed using an oven for example).
An antenna can be made from oddly shaped objects in this manner
Thus, the present invention is also not limited by the shape of the
substrate.
[0068] Returning to FIG. 4A, circuit 100 is disposed on a flexible
tape of polyimid. Pattern 105 includes a series of palladium lines
102 that are shaped to facilitate the subsequent formation of
conductive lines 112 (FIG. 4D). Production of lines 102 and pattern
105 will be described in further detail below.
[0069] FIG. 4B shows an illustrative microscopic view of a single
palladium line 102. The palladium line 102 includes a series of
separate and disconnected active palladium atoms 104 on the surface
21 of substrate 20. Since the metal ions 104 are not connected,
palladium line 102 is not conductive.
[0070] Collectively, the palladium atoms 104 on surface 21
approximately have a zero valence. It is understood that some atoms
may have a slightly different valence due to processing
disturbances and imperfections.
[0071] Borderlines 107 are dotted to illustrate that they
approximate boundaries for the deposition of active palladium ions
104. As will be described with respect to FIG. 4C, copper initially
accumulates on surface 21 according to the atomic locations of
palladium 104. In some instances, depending on the how much metal
is added the metal deposition process, copper accumulation may
extend outside of borderlines 107.
[0072] Palladium deposition according to the present invention uses
low surface concentrations of active palladium. At a minimum,
deposition generates enough palladium on the surface to form metal
conductive lines according to a subsequent metal deposition
technique. For example, for electroless copper deposition, the
palladium surface concentration is high enough to initiate
electroless plating. In one embodiment, palladium line 102 has a
surface concentration of less than about 6.times.10.sup.-10 gram
atoms of palladium per square millimeter. In this case, the active
and elemental palladium 104 surface concentration is so low that
the palladium 104 does not form a conductive layer on substrate 20.
In other words, while some atoms may contact, palladium 104
generally does not leave a high enough surface density to have
consistent contact to permit conductivity of electrons along
palladium lines 102. In a specific embodiment, palladium line 102
has a surface concentration of less than about 3.times.10.sup.-7
gram atoms of palladium per square millimeter. It is understood
that some of these concentrations may not be visible to a human eye
without magnification.
[0073] Referring to FIGS. 2 and 4C-4D, conductive line formation
(76) uses one or more metal deposition techniques that benefit from
the presence of active palladium atoms on a surface of the
substrate. Metals suitable for use for the conductive lines may
include copper, gold, nickel silver and cobalt alloys. For example,
the conductive line may include palladium atoms disposed under a
copper layer with a thin outer layer of gold deposited over the
copper. Other metals may be used for conductive line formation.
[0074] As one of skill in the art will appreciate, a wide variety
of conductive line formation techniques are suitable for use with
the present invention. Plating is the general name of
surface-covering techniques in which a metal is coated onto a solid
surface. Numerous plating methods conventionally used today may
benefit from active palladium. Such techniques include: vapor
deposition under vacuum, sputtering, chemical vapour deposition
with or without a vaccum, and other methods using vacuum or gas
conditions. Thin film deposition plating techniques have
accomplished plating on scales as small as the width of an atom.
Metallizing refers to the process of coating metal on non-metallic
objects. One metallizing technique suitable for use herein applies
a two step process that: a) deposits copper on a seed layer
palladium pattern by electroless deposition (using a conventional
copper electroless deposition process); and b) uses electroplating
to add more copper on top of the electroless copper to produce
thicker copper lines. Other conductive line formation techniques
are also suitable for use herein, and in general, the present
invention is not limited to any particular manufacturing technique
for creating conductive lines on a surface that already includes a
palladium precursor.
[0075] FIG. 4C illustrates initial radial growth of copper from
palladium atoms 104 on surface 21 of substrate 20. This
illustration approximates copper growth that might be witnessed in
an electroless plating process, for example. As shown, the active
palladium 104 anchor to the substrate 20 and initiate attachment of
copper on surface 21 according to their location. The newly
attached copper then facilitates further radial copper deposition
(and platelet-like growth). Copper thus accumulates radially from
each palladium ion 104 on surface 21 of substrate 20, as indicated
by temporal growth lines 106.
[0076] As electroless copper deposition proceeds, contact between
adjacent copper growth lines 106 occurs. Continued metal deposition
adds enough metal to form and gain electrical conductivity along
lines 112.
[0077] The copper deposition also occurs normal to surface 21
(normal to the page as shown). Notably, then, as copper deposition
continues, the initial palladium atoms are buried under the
aggregating copper and no longer visible. For the circuit shown in
FIG. 4D, it is most likely that no active palladium ions 104 will
be visible since they are all buried under considerably much more
copper. And given that the amount of active palladium ions 104 is
relatively small compared to the amount of copper, detection of
palladium 104 becomes difficult after conductive lines 112 have
been formed.
[0078] In this manner, the active and elemental palladium 104
disposed on surface 21 acts as a seed to catalyze deposition of a
metal on substrate 20. Controlled spatial patterning of palladium
lines 102 then permits uncontrolled patterning of conductive lines
112, which blindly follows the established spatial pattern and
arrangement of palladium lines 102.
[0079] While FIG. 4A shows one specific active palladium pattern
105, the present invention is not restricted to any specific number
or arrangement of lines. Typically, the active palladium pattern
substantially resembles the conductive line pattern included in
circuit after copper deposition is finished. In some cases,
palladium lines 102 may be slightly thinner than conductive lines
112 to permit for expansion of the conductive lines during copper
deposition in one or more stages, e.g., electroless deposition
followed by electroplating. As will be described in further detail
below, the present invention also permits active palladium patterns
on 3-D and custom shaped surfaces.
[0080] It should be noted that the palladium printed substrate 100
of FIG. 4A can be an end product by itself. In other words, a
manufacturer may be responsible for printing partially manufactured
circuits 100 that do not yet include conductive lines. These
partially manufactured circuits 100 are then provided to a second
manufacturer responsible for adding a metal to form the actual
conductive lines.
[0081] The palladium precursor solution may be delivered to a
substrate in any of a number of different manners. In one
embodiment, the solution is delivered only to selective regions of
the substrate according to a desired pattern. This spatial
selectivity is referred to herein as "printing" the palladium
precursor solution on the substrate. In other embodiments, the
palladium precursor solution coats the entire substrate or a large
portion thereof. This may be accomplished via a printer (where the
entire surface is selected for printing), dip coating, or another
blank printing procedure. In such cases, the blank palladium
precursor solution may or may not be subsequently patterned to
produce the pattern. When dispersed by a printer or automated
printing process, the palladium precursor solution may be
considered, and referred to herein, as an `ink` or a `palladium
ink`.
[0082] FIG. 5 shows the production of a printing reservoir that
stores a palladium ink in accordance with one embodiment of the
present invention. FIG. 6B shows a printing reservoir 200 (the
output of FIG. 5) that includes palladium precursor solution 210 in
accordance with a specific embodiment of the present invention.
FIG. 6A shows the printing reservoir 200 used with a printing
apparatus 180 in accordance with one embodiment of the present
invention. While printing according to FIGS. 6A and 6B will now be
described with respect to an apparatus, those of skill the art will
recognize of the following description also applies to methods and
steps for producing printed circuit precursors.
[0083] Referring initially to FIG. 6A, printing apparatus 180
refers to a mechanized system that delivers palladium precursor
solution 210 onto a substrate to form a circuit precursor 23.
Printing apparatus 180 generally includes: controller 182,
dispensing mechanism 184, and palladium ink reservoir 200.
[0084] The exact structure of printing apparatus 180 and each of
its components will vary with the printing technique employed, as
one of skill in the art will appreciate. Indeed, an advantage of
the present invention is that it may use a commercially available
printing technique or apparatus without the need for special
retooling or reconfiguration for printing palladium precursor
solution 210. In other cases, printing apparatus 180 is specially
manufactured and/or configured for printing circuits according to
techniques described herein.
[0085] The printing apparatus 180 may include a contact or
contact-less printing technology, and/or signal-directed, manual or
mechanical means. For example, printing apparatus 180 may employ
any one, or a combination, of the following printing technologies:
ink-jet printing, screen printing, pad-printing, spray coating,
spin coating, puddle coating, dip coating, Gravure printing,
ultrasonic spray techniques, wire coating, a stencil, rotogravure,
flexographic techniques, brush coating, or various other blank
coating techniques. Monochrome printing is suitable in many
instances. A specific printing technology may be selected according
to its benefits for a particular application. For example,
ultrasonic spray techniques are well suited to deposit uniform
thickness coatings.
[0086] Dispensing mechanism 184 is configured to transfer the
palladium precursor solution 210 from reservoir 200 to a substrate
20. The structure of dispensing mechanism 184 will depend on the
printing technology used. For example, a conventional inkjet
printer often includes a small printing tube with a known
volumetric capacity that the palladium ink fills into. A control
signal causes an actuator, such as a piezoelectric actuator, to
squeeze the tube and dispense ink from the tube onto the substrate.
For 2-D inkjet printing, a linear actuator moves the tube in a
direction orthogonal to a direction of substrate feed, thereby
providing 2-D printing onto a substrate. The tube then expands and
contracts according to an applied waveform or control signal that
matches a known position of the tube relative to a current position
of the substrate. In this manner, any custom pattern 105 (FIG. 4A)
may be disposed on a substrate according to a control signal that
corresponds to the pattern.
[0087] In a specific embodiment, printing apparatus 180 includes a
general-purpose printer. For example, this may include a printer
traditionally used with personal computers and commercially
available from a wide variety of vendors, including retail vendors
and the like. One suitable personal printer is the Epson C66,
available from a wide variety of vendors, reconfigured with an ink
cartridge that includes palladium ink as described herein. The
general-purpose printer may also include any printer used in the
printing industry, such as commercially available models used to
print on banners and large sheets. One suitable larger printer is
the Roland SP300V available from Roland DG Corporation of
Hamamatsu, Japan. These general-purpose printers are generally
configured to print on thin sheets made from substrates such as
commercially available paper or polyimid. One suitable commercially
available printer includes ink-jet printers. The present invention
then stores palladium precursor solution 210 in a printing
cartridge 200 that mechanically interfaces with the general-purpose
printer.
[0088] Printing apparatus 180 may also be configured to interact
with a personal computer, which is used to supply printing patterns
to printer 180. A user interface on the personal computer permits
external control of printing on apparatus 180. The user interface
also permits easy reconfiguration and printing of new patterns and
circuit designs--without special retooling of printing apparatus
180 for each new pattern or circuit. In this manner, new circuits
may be printed as readily as a conventional general-purpose printer
produces new paper documents.
[0089] One suitable class of printing may be broadly characterized
as "drop on demand" printing. In these processes, a drop of
palladium ink is created wherever necessary on a substrate as
regulated by controller 182. Controller 182 may include any
combination of a processor and/or memory suitable configured to
output a signal to control dispensing mechanism 184. In one
embodiment, the signal is digital and corresponds to a pattern for
the palladium precursor. The pattern may be received from an
external computer that controller 182 interfaces with. Controller
182 may include one or more commercially available processors that
interact with a memory that stores instructions and information
suitable for printing patterns on one more substrates. The memory
may include RAM, ROM, hard drive space, tempering memory such as a
memory stick or CD-ROM, etc.
[0090] Spatially controlled printers permit easy and fast circuit
reconfiguration where only the control signal needs to be changed
to produce a new circuit design or layout. Thus, the present
invention contemplates circuit manufacture according to digital
design without mechanical reconfiguration or downtime of a circuit
manufacturing line. For example, some commercially available inkjet
printers are suitable for printing circuit precursors 23 on
flexible polyimid substrates one or two at a time (or more, if
desired). This permits research organizations, universities and
other small businesses to own custom circuit manufacturing
technology, without having to outsource the production of one or
two custom circuits. Thus, the present invention contemplates
business models where printers are sold with the intent of enabling
small organizations to do their own circuit printing and
manufacture.
[0091] Another class of printing may be broadly characterized as
"image" printing. For example, Gravure printing may also be used
for printing apparatus 180. As a dispensing mechanism 184, Gravure
printing employs a depressed or sunken surface for the image that
is etched or engraved into a cylinder; the unetched areas of the
cylinder represent the non-image or unprinted areas. The cylinder
rotates in a bath of ink called the ink pan (in this instance,
reservoir 200 includes a Gravure ink pan that stores palladium
precursor solution 210). As the cylinder turns, the excess ink is
wiped off the cylinder by a doctor blade. The palladium ink
remaining on the cylinder forms a palladium pattern 105 by direct
transfer to the substrate (paper, polyimid or other material) as it
passes between a plate cylinder and an impression cylinder. Gravure
printing is well suited for static image, long run, high quality
printing that produces a sharp, fine image.
[0092] In another embodiment, printing apparatus 180 permits
conformal printing. Conformal printing refers to printing palladium
ink 210 on non-flat and three-dimensional surfaces. For example,
the non-flat surface may include the inner surface of a cell phone
housing or other portable electronics device, which is commonly
curved and custom shaped. In one embodiment, conformal printing
apparatus 180 includes a pen, movable in three dimensions, that
dispenses palladium ink 210 in response to a control signal. Based
on a known position of the controlled pen relative to the non-flat
substrate, ink is released at controlled times and a pattern is
then produced on the conformal surface as desired.
[0093] The conformal printing apparatus 180 may include any robotic
system that tracks: a) the substrate (or part such as a cell phone
housing); b) the dispensing mechanism 184; or c) combinations
thereof, to provide 3-D relative motion between the substrate and
dispensing mechanism 184. For example, dispensing mechanism 184 may
include a 3-D robotic actuator that moves a pen or dispensing
mechanism to the custom shape of a non-flat substrate.
[0094] Resolution of a printed palladium pattern 105 (and
subsequent conductive line resolution) will vary with the printing
apparatus 180. In general, resolution may be limited to droplet
size for the printing apparatus. In some cases, printing
capabilities of the printing technology may be used to improve
resolution and pattern output. For example, the dots or drops per
inch used in an inkjet printer will affect droplet size and may be
tailored to increase pattern resolution. In addition, for many
conventional and general-purpose inkjet printers, a grayscale level
setting changes the number of passes that the dispensing mechanism
makes across a substrate. Decreasing the grayscale setting then
decreases the number of passes that the dispensing mechanism makes,
and thereby reduces the number of drops and quantity of palladium
deposited onto the substrate. In one embodiment, printing apparatus
180 provides a printing resolution for a printed palladium pattern
105 of about 10 microns. In another specific embodiment, a line
density of greater than about 1 line per millimeter is suitable for
use. A printing resolution of about 100 microns is suitable in many
applications. In another embodiment, printing apparatus 180 outputs
droplets between about 15 and about 20 picoliters.
[0095] Line thickness is another suitable measure of printing
resolution. In one embodiment, the present invention prints lines
with a planar thickness up to about 2 microns. In a specific
embodiment, a palladium pattern includes a line with a surface
width of less than about 250 microns. Thicker lines may be used. As
one of skill in the art will appreciate, the line width and spacing
will depend on the printing technology and desired pattern.
[0096] It is understood that some printers may use multiple passes
to achieve the desired palladium concentration on a surface. For
example, a printing apparatus may print a palladium precursor
solution, having a concentration of palladium of about 0.01, five
times to achieve a desired concentration on the substrate (such as
0.05). This permits lower concentrations of palladium and solution
to be used in a printing reservoir.
[0097] Various processes and printing apparatus for blanket
depositing of palladium ink may also be employed. A blanket
deposition involves coating a large portion or the entire substrate
surface with the palladium ink and without defining a pattern. Dip
coating represents one suitable method for blanket deposition of
palladium ink Dip coating allows substrates in any shape and size
to have palladium precursor solution disposed thereon. For example,
strands and fibers such as those later weaved together may be dip
coated, in addition to non-flat surfaces described above.
[0098] The blanketed palladium precursor is then later altered to
produce a desired pattern. Patterning a palladium pattern 105 onto
a blank ink of deposition is referred to in here as `scribing`. In
one embodiment, scribing occurs during decomposition of the
palladium precursor remaining after the solvent is evaporated off.
As mentioned above, decomposition typically includes adding energy
to the palladium precursor. One suitable scribing process uses a
laser writing process. While the palladium precursor is adhered to
the surface, a laser beam is applied to the surface at positions
where it is desired to have the palladium remain according to a
desired palladium pattern 105. The laser beam has an energy and/or
wavelength chosen to decompose the palladium precursor (e.g.,
palladium carboxylate) to form elemental palladium that adheres to
the surface. After the laser writing process is complete, the
substrate may be washed or otherwise treated in a manner that
removes the unreacted palladium precursor from the surface. At the
end of this process, a pattern of elemental palladium 104 remains
on the surface at desired locations according to the desired
palladium pattern. Spatial resolution of the active palladium
pattern then depends on the spatial resolution of the laser and/or
its actuators.
[0099] As mentioned above, the decomposition of a palladium
precursor may use any combination of heat, an e-beam, an ion beam,
a laser, or the like. An e-beam or an ion beam also permits
actuated control of a small beam that permits patterning of the
palladium precursor. Pattern resolution will depend on the
actuation and size of the beam. Optics may be used to decrease beam
size increase resolution of pattern 104.
[0100] Returning back to FIG. 6A, the output of printing apparatus
180 is a substrate with the palladium precursor solution printed
thereon. As mentioned above, this may be with a specific pattern
that resembles a desired final pattern for conductive lines a
substrate and circuit (FIG. 4A), or a blank patterning that
requires subsequent scribing to achieve the desired circuit
pattern.
[0101] Evaporation apparatus 190 receives the substrate and exposes
the palladium precursor solution to conditions that promote
evaporation of a solvent from the palladium precursor solution to
leave a palladium precursor 22 on the substrate. Evaporation
apparatus 190 may include any system for transferring heat (or
another form of energy) to the substrate and/or solvent. Heat
transfer via conduction, convection, radiation, and combinations
thereof, are suitable for use with apparatus 190. Evaporation
apparatus 190 may vary with printing apparatus 180. For example,
Gravure printers often use a gas fired or electric fired drier to
dry the Gravure ink and drive off any solvents or water, which
essentially replaces most of the solvent, from the substrate. An
inkjet printer may use rollers with an elevated temperature to
transfer heat to the substrate and dry the palladium ink
Evaporation apparatus 190 outputs a circuit precursor 23 that
includes palladium precursor 22 on a substrate 20.
[0102] In one embodiment, the evaporation process is coupled with
palladium ink deposition. For example, the palladium ink 210 may be
partially pre-heated as it is disposed on the substrate. A second
round of heating then evaporates the solvent from the substrate,
albeit with less energy than normal since the ink has already been
pre-heated.
[0103] In another embodiment, solvent evaporation is coupled with
the decomposition process. In this case, evaporation apparatus 190
is part of a larger apparatus that also performs decomposition of
the palladium precursor.
[0104] In yet another embodiment, a separate chamber 190 is
provided solely for evaporation. For example, this may include a
curing oven whose thermal performance is adapted to specifically
evaporate solvent from circuit precursors 23. In many processes in
which a pattern of active palladium is to be formed on the surface
at a high resolution, it may be desirable to first evaporate
solvent from the deposited palladium ink--and only after this to
decompose the palladium precursor to form the palladium metal ink
pattern. To this end, it is desirable to expose the substrate
and/or solution to conditions that promote evaporation and transfer
heat to the solvent prior to conditions that decompose the
palladium precursor (e.g., palladium carboxylate). This reduces the
likelihood of "smudging" the ink pattern that is to remain on the
substrate. This is particularly useful in sub-ten micron
patterning.
[0105] Turning now to FIGS. 5 and 6B, printing reservoir 200 will
now be expanded upon. The manufacture and construction of printing
reservoir 200 will also vary with the type of printing apparatus
180. In general, the function of printing reservoir 200 is to store
a palladium precursor solution 210. For a particular inkjet
printer, printing reservoir 200 will mechanically and electrically
resemble a printer cartridge designed to interface with that
particular inkjet printer. For Gravure printing, printing reservoir
200 will resemble the ink reservoir according to a particular
Gravure apparatus.
[0106] Printing reservoir 200 may often be sealed prior to usage to
extend shelf life of palladium precursor solution 210. Further
description of shelf life and selecting chemical components to
extend shelf life are described below with respect to solution
chemistry.
[0107] FIG. 5 shows a method 150 for manufacturing printing
reservoir 200 in accordance with one embodiment of the present
invention.
[0108] Method 150 begins by adding a Lewis base ligand
(nucleophile) and a palladium compound such as palladium
carboxylate to a solvent to create the palladium precursor solution
210 (152). In a specific embodiment, palladium propionate was
prepared by treating commercially available palladium acetate in
excess propionic acid. The mixture was maintained at about
40.degree. C. for about 24 hours followed by removal of excess
propionic acid under a vacuum at room temperature. The resulting
solid is soluble in amyl acetate. In another specific embodiment
suitable for printing on polyester, a solution of palladium
propionate having 0.05% palladium by weight was prepared in amyl
acetate Aniline was added in a stoichiometric amount that
corresponds to 2 moles of aniline per gram atom of palladium. This
clear solution was then suitable for printing. Another suitable
composition include a 1:1 mole ratio of pyridine and a 1:2 complex
with cyclo pentyl amine (2 moles of cyclo pentyl amine per gram
atom of palladium). The particular Lewis base ligand, palladium
compound, and solvent will depend on an application, and may also
vary with the printing apparatus used. Further description of the
chemistry included in palladium precursor solution 210 is described
below.
[0109] Rheological requirements for ink used in each of the
printing technologies described above may vary. In one embodiment,
palladium precursor solution 210 is adapted during manufacture to
one or more rheological properties of a fluidic dispensing
requirement of a printer (154). The rheological property may
include one or more of: surface tension, density and viscosity (and
combinations thereof) for palladium precursor solution 210 and/or a
rheological fluidic dispensing requirement of a printer. For
example, Gravure inks preferably include a low viscosity that
allows them to be drawn into engraved cells in a cylinder and then
transferred onto a substrate. Many inkjet printers tune the
waveform supplied to their piezoelectric actuator according to
rheological properties of their preferred ink, e.g., for quality
control of printed output Inks with rheological properties that do
not match the tuned waveform often produce lesser quality printed
output. Providing a new or different ink, such as palladium
precursor solution 210, to a commercially available in
general-purpose inkjet printer may then require the ink to conform
to a tuned waveform or other printing apparatus rheological
property.
[0110] The present invention contemplates multiple ways to adapt
palladium precursor solution 210 to a rheological property of a
fluidic dispensing requirement of a printer. In one embodiment, the
palladium precursor solution is adapted to the rheological property
of the fluidic dispensing requirement. In this case, one or more of
the Lewis base ligand, palladium compound, and/or solvent selected
to provide a particular aggregate rheological property for
palladium ink 210. For example, the solvent may be chosen with
particular density or viscosity to match that desired by a
particular printing apparatus 180.
[0111] In another embodiment, the palladium ink includes an
additive that adjusts a rheological property of the palladium
precursor solution to a rheological property of a fluidic
dispensing requirement of printing apparatus 180. For example, the
additive may include a surfactant that changes surface tension
and/or density of palladium ink 210. Surface tension of palladium
ink 210 often affects droplet size for an inkjet printer that
deposits the ink onto a substrate. The particular substrate
material may also affect surface tension for the printer; paper
often has a different droplet size then a smooth surface associated
with a polymer such as polyimid. In either instance, the surfactant
may be selected to achieve a desired droplet size for a particular
inkjet printer and a particular substrate material. Preferably, the
additive is selected to be chemically inert to the active palladium
left on the substrate. In one embodiment, the additive is selected
to also be chemically inert to the printing apparatus.
[0112] Other additives may be included in palladium ink 210. It is
generally desirable for palladium ink 210 to not substantially
corrode one or more components of printing apparatus 180. Since the
palladium precursor solution 210 may be used with off-the-shelf
general-purpose printers and may include chemistries not intended
for these general-purpose printers, corrosion of printing
components may occur. In this sense, corrosion refers to dissolving
of palladium ink 210 into one or more components of the printer,
chemical attachment of palladium ink 210 into one or more printer
components, softening of the printer components due to the presence
of palladium ink 210, or any change in a mechanical or physical
property of a printer component. As the term is used herein,
substantial corrosion refers to functional degredation of one or
more chemical or mechanical properties for components in a printing
apparatus 180. For example, an ink solution should not corrode
plastic components in a printer to the point where the components
soften, are penetrated by the ink, or lose mechanical tolerances.
In one embodiment, one or more of the Lewis base ligand, palladium
compound, and/or solvent are selected to avoid printer component
corrosion. Ideally, there is zero degradation over time. In one
embodiment, a time limit quantifies the substantial corrosion. In
one embodiment, substantial corrosion refers to noticeable
functional or performance degredation of a printing apparatus or a
component after about 6 months of ink use. In a specific
embodiment, substantial corrosion refers to noticeable functional
degredation of the apparatus after about 3 months. In another
specific embodiment, the palladium precursor solution has a shelf
life, where the palladium precursor solution is at least 90 or 95
percent intact, of greater than 1 month when added to the
solvent.
[0113] The present invention then stores the palladium precursor
solution 210 in a printing reservoir 200. The reservoir may
resemble a cartridge that mechanically interfaces with a
general-purpose printer such as an off-the-shelf inkjet printer.
Alternatively, reservoir 200 may physically resemble an ink well
used in Gravure printing.
[0114] The palladium precursor solution 210 may be characterized by
the concentration of palladium included therein. In one embodiment,
solution 210 includes a concentration between about 0.5 percent and
about 0.002 percent palladium by weight. In a specific embodiment,
solution 210 includes a concentration between about 0.05 percent
and about 0.2 percent palladium by weight.
[0115] Having described circuit manufacturing and printing
processes, chemistry suitable for use with the present invention
will now be expanded upon.
[0116] Previous attempts to form structures reliant on palladium
seed layers by decomposing a deposited palladium compound have been
ineffective. While not wishing to be bound by theory, it is
believed that these attempts failed to form isolated palladium
atoms on the substrate and therefore did not provide good adhesion.
The prior palladium deposition techniques typically employed
palladium precursors that would tend to form groups or agglomerates
of associated palladium atoms on the substrate surface. These
groups of palladium atoms do not adhere well to most substrate
surfaces.
[0117] The inventors have identified and developed the concept of
"active" palladium. This is palladium metal that has two desirable
properties: (1) it is catalytic for subsequent addition of a metal
onto the palladium (such electroless deposition), and (2) it
anchors the deposited metal to the underlying substrate. In some
cases, the active palladium may also be characterized as being
disposed monatomically or even sub-monatomically on the substrate.
At some point in the process, the deposited palladium should have
approximately zero valence.
[0118] The estimation of active palladium as generally having a
zero valence recognizes that the deposition process may not be
perfect in forming all palladium with a zero valence, and minor
amounts may stray therefrom. Elemental palladium with a zero
valence is particularly active, and well-suited to initiate
attachment with copper or another metal used in the conductive
lines. As mentioned above, elemental palladium does not readily
bind to a surface monatomically, and needs to be deliberately
processed to achieve such a state.
[0119] Deposition chemistry and processing techniques chosen by the
inventors provide strong active palladium anchoring by leaving
isolated monatomic palladium (rather than clusters of palladium
atoms), and by producing approximately zero valence atoms on the
substrate. For example, palladium carboxylate precursors,
decomposed with suitable input energy, leave isolated palladium
atoms with approximately zero valence on the substrate after
decomposition. The active palladium atoms so deposited can bind to
both the substrate and a metal subsequently deposited thereon. The
palladium atoms then act as individual and separate anchoring
points between the substrate and metal, which promotes better
adhesion of conductive lines. In some ways, the deposited palladium
atoms resemble atoms deposited on a substrate by a physical vapor
deposition technique such as sputtering.
[0120] The palladium chemistry and deposition techniques invented
by the inventors emphasize process conditions and starting products
that are believed to promote formation of isolated palladium atoms
on a substrate surface. This is believed to be in contrast to prior
techniques. In certain embodiments, it is believed that, in
addition careful selection of palladium solution components, the
deposition technique can have a positive impact on the quality of
active palladium deposited. In one example, the process involves
first driving off solvent from a deposited palladium solution, and
then decomposing the remaining material using added energy (e.g.,
using an ultraviolet source or laser for example) to produce the
active palladium.
[0121] It has been recognized by the inventors that palladium
compounds such as palladium carboxylates easily form loose
assemblies such as dimers and trimers in solution. In these
assemblies, the palladium atoms of individual molecules may cluster
head to head. The inventors discovered that without addressing this
phenomenon, the resulting elemental palladium formed after
decomposition does not adhere well to the substrate. Adding a
strong Lewis base (e.g., a stronger electron donor than the
carboxylate or other anion in the palladium precursor) may break
the bridging between palladium compounds and form a solution in
which the palladium precursor compounds remain relatively isolated
from one another. When the palladium precursor from such solution
is decomposed on a substrate surface, it is believed that elemental
palladium tends to deposit as individual atoms rather than as a
cluster. This forms essentially monatomic anchor points for the
palladium itself as well as subsequently deposited copper or other
metal.
[0122] Generally, the palladium precursor solution includes a Lewis
base ligand and a palladium compound in a solvent. The choice of a
particular palladium precursor and solvent may be dependent upon a
particular substrate on which the palladium and subsequent
conductive lines will be deposited, or a particular manufacturing
process, as one of skill in the art will appreciate.
[0123] Before providing an expanded description of particular
components, one or more optional desirable properties of a
palladium precursor solution will first be discussed. Constituents
of the palladium precursor solution may be selected to produce one
or more properties. In one embodiment, the solvent,
palladium-containing compound and Lewis base ligand are all organic
substances. Suitable examples are described below. In another
embodiment, the Lewis base ligand and a palladium compound are
selected such that decomposition products of the palladium
precursor solution decompose relatively easily. For example, the
constituents may be selected to have a certain decomposition
temperature. The Lewis base ligand and a palladium compound may
also be selected such that decomposition products are benign and/or
easily removed. Examples of suitable decomposition products include
carbon monoxide, carbon dioxide, water and a fragmented or an
unfragmented ligand. When the decomposition uses heat or high
energy, the water often releases as a vapor.
[0124] In addition, the decomposition products preferably do not
affect the substrate being printed upon. In one embodiment, none of
the decomposition products are oxidizers or strong reducing agents.
Again, decomposition by-products such as carbon monoxide, carbon
dioxide, and water are suitable in this regard.
[0125] In another embodiment, the palladium-containing compound is
chosen such that the palladium precursor solution has a sufficient
shelf life for a desired application. As the term is used herein,
shelf life refers to the rate of functional decomposition of the
palladium precursor solution. Preferably, the solution does not
decompose at any measurable rate, or has no technical decomposition
by a certain date defined by the shelf life. Decomposition may
appear as metallic deposits or visual precipitation in the solution
in which the palladium decomposes out of the solution onto walls
and other structures. In one embodiment, the shelf life is greater
than three or six months, and more preferably greater than 6 weeks.
Of course if the intent is to use the precursor solution
immediately or very soon after it is created, shorter shelf lives
may be acceptable. In a specific embodiment, the palladium
precursor solution has a shelf life, where at least 95% by weight
of the palladium precursor remains intact, for longer than 3 months
after the solution is formed. Even longer shelf lives may be
desirable in some contexts, particularly those in whch extended
storage may be needed. As described above, the present invention is
well-suited for use with printing technologies where the palladium
precursor solution is stored in a reservoir or ink cartridge used
with a printer. Storage in such a reservoir may occur for months or
years before use, and the ink cartridge may remain in a printer for
months or years once installed. Selection of a palladium-containing
compound to promote solution longevity is thus important in ink
distribution business models and applications such as these.
Selection of an inert material for the ink reservoir, such as glass
or an inert polymer or polymer coating, also extends
shelf-life.
[0126] In another embodiment, constituents of a palladium precursor
solution are chosen to facilitate deposition of the solution. Four
such examples are now provided.
EXAMPLE#1
Preparation of Palladium(II) Propionate
[0127] 5 gm commercial palladium(II) acetate trimer (Aldrich) was
added to 40 g of propionic acid. The mixture was maintained at 40
degrees Celsius for 24 hours. Excess propionic acid was removed
under vacuum at room temperature. The resulting yellow solid was
used for making palladium inks
EXAMPLE#2
[0128] 0.075% palladium (II) solution in amyl acetate was prepared
by dissolving 0.357 g of palladium (II) propionate, prepared as
described in Example#1, in 199.643 g of amyl acetate. The solution
thus formed was filtered through 0.45 .mu.m PTFE acrodics. 0.241 g
of cyclopentylamine (2 equiv. w.r.t. Pd atom) was added to the
clear solution. The solution immediately turned from brownish
yellow to pale yellow. Two polyester coupons of "5.5.times.6" inch
and "5.times.9" inch were dipped in this palladium (II) solution
for three minutes and heated on a hot plate kept at 160 degrees
Celsius. The coupons were dipped in electroless copper solution for
about 1 minute. A uniform copper layer developed on substrate.
EXAMPLE#3
[0129] 0.125% palladium (II) solution in amyl acetate was prepared
by dissolving 0.297 g of palladium (II) propionate (prepared as
described in Example#1 above) in 99.703 g of amyl acetate. 0.337 g
of tripropylamine was added to the clear solution. Polyester
coupons of "9.times.9" inch were coated with this solution using
camel brush at 50 degrees Celsius and kept in oven at 130 degrees
Celsius for 8 minutes. The coupons were dipped in electroless
copper solution. A uniform layer of copper developed on
substrate.
EXAMPLE#4
[0130] 0.125% palladium (II) solution in amyl acetate was prepared
by dissolving 0.297 g of palladium (II) propionate (prepared as
described in Example#1 above) in 99.703 g of amyl acetate. 0.239 g
of Diisopropylamine was added to the clear solution. A polyimide
substrate"5.times.6" was dip-coated in this solution, air dried and
heated at 170 degrees Celsius for 5 min. The coupon was dipped in
electroless copper solution until a uniform copper layer is
deposited on the substrate.
[0131] Palladium precursor solution components may also be tuned to
an application. As described above, solution components may be
selected to adapt one or more rheological properties of the fluid
that are important for printing. Alternatively, solution components
may be selected according to a specific substrate being printed on;
specific examples are provided below.
[0132] The palladium precursor solution components will now be
separately expanded upon.
[0133] The palladium-containing compound in the palladium precursor
solution acts as a palladium carrier. The palladium-containing
compound may be selected according to one or more of the following
properties: a) be soluble in a particular solvent employed in the
palladium precursor solution; b) be compatible with the chosen
Lewis base ligand (e.g., be a weak Lewis acid); and/or c) be
relatively inexpensive.
[0134] Various palladium carboxylates meet most or all of these
criteria. In one embodiment, it is desirable to limit the size of a
carboxylate to ten carbons or less. In another embodiment, it is
desirable to limit the size of a carboxylate to six carbons or
less. In a specific embodiment, the palladium carboxylate has two
to five carbon atoms. In another specific embodiment, the palladium
carboxylate has three to five carbon atoms. One preferred
carboxylate is a propionate. Examples of other palladium
carboxylates that may be employed are in some embodiments are
palladium acetate, palladium oxalate, and palladium iso-butyrate.
Note that use of relatively short chain carboxylates may help avoid
the undesirable decomposition processes that produce elemental
carbon. In general, while palladium is bivalent it need not have
two separate carboxylate groups. In some examples, the carboxylate
may include 2 or more carboxylic acid groups (e.g, it could be an
acetate and a proprionate). Further, the carboxylate can be fully
saturated or include one or more unsaturated bonds, and it can be
straight chained or branched. For dicarboxylic acid compounds, one
of the carboxylate groups could be separately reacted to form an
ester.
[0135] The palladium-containing compound may be selected to have a
good shelf life when not in a solution, in addition to its shelf
life when in solution. For example, the palladium compound may not
include hygroscopic properties so as to avoid degradation over time
by attracting water. Palladium (ii) acetate is suitable in this
regard.
[0136] As mentioned, decomposition properties of the palladium
compound may also affect selection (along with decomposition
properties of the Lewis base ligand, as described below). For
example, palladium carboxylates having a decomposition temperature
in the range of about 100.degree. C. to 240.degree. C. are
desirable in some embodiments. The choice of corresponding ligand
will sometimes impact the decomposition temperature. Lewis base
ligands that may be used with palladium carboxylates and allow
decomposition in the above temperature range include
cyclopentylamine, triethyl amine, diisopropyl amine, etc. Palladium
proprionate has a decomposition temperature of about 130.degree. C.
(oven temperature) when used with triethylamine as a Lewis base
ligand.
[0137] As mentioned, a Lewis base ligand may be provided in the
palladium precursor solution to facilitate formation of active
palladium. As alluded to above, it is believed that the presence of
a Lewis base interferes with the natural tendency of palladium
carboxylate molecules to bridge with one another in solution.
Therefore, in certain embodiments, a strong Lewis base is provided
to the palladium precursor solution to coordinate with available
spaces on a palladium that are not occupied by carboxylate groups.
In the embodiments described here, the Lewis base acts as a ligand
for the palladium compounds. In a simplistic view of the chemistry,
palladium has four separate coordination sites that may be
occupied. In palladium carboxylates, carboxylic acid moieties
occupy two of these sites (because palladium has a valence of two).
The remaining two sites may be occupied by other palladium
molecules, by complexing groups, etc. In the embodiments described
here, the Lewis base ligand may occupy one or two available sites
on the palladium and sterically hinder access to those sites by
other palladium carboxylate molecules, etc. Thus, introducing these
ligands may minimize bridging between individual palladium
carboxylate molecules and facilitate deposition of the palladium
atoms on the substrate in an isolated fashion. Again, this is
believed to provide better adhesion of the elemental palladium to
the underlying substrate and better shelf life to the palladium
ink.
[0138] The Lewis base ligands may be any material that meets the
various constraints for an application (e.g., for use with a
specific ink jet printer) and interferes with solution phase
bridging between palladium compounds without decomposing them.
Examples include various nitrogen compounds, phosphorous compounds,
sulfur compounds, etc. Nitrogen-containing compounds are
particularly well-suited to stabilize many palladium precursors
such as palladium carboxylates. Examples of nitrogen-containing
compounds include nitrogen donors such as primary, secondary and
tertiary amines with a general formula RNH.sub.2, R.sub.1R.sub.2NH,
or R.sub.1R.sub.2R.sub.3N, whose R=C.sub.nH2.sub.n+1 and n=1 to 15,
(R.sub.1R.sub.2R.sub.3 may be similar or dissimilar), etc. The
amines may be aliphatic or aromatic, straight chain or branched,
and with or without unsaturation. Specific examples include, for
example, cyclopentylamine, tri-ethylamine, pyridine carboxylates,
pyridine, aniline, tetramethylethylenediamine, dimethylamine, and
di-isopropylamine. In certain embodiments, the molecular weight of
the Lewis base is between about 30 and 200, more preferably between
about 45 and 145. However, in some situations, it may be
appropriate to employ larger molecules or even polymers such as
polyimines This may be appropriate when, for example, it is desired
to increase the viscosity of the palladium precursor solution.
[0139] To produce elemental palladium on the substrate, the Lewis
base ligands will, in most embodiments, need to be removed. This
can be accomplished by either volatilization (depending on the
vapor pressure of the base) or decomposition (along with the
palladium precursor). Decomposition of a nitrogen-containing base
may produce a fragmented or an unfragmented amine
[0140] In some embodiments, the Lewis base is a polar species and
may thus require the use of a polar solvent. In certain
embodiments, aqueous solvents may be appropriate; i.e., water may
serve as a solvent, in part or in whole.
[0141] Other factors may enter choosing a Lewis base. Selection of
the Lewis base ligand will also affect shelf life of the palladium
precursor solution and thermal stability in palladium precursor
after the solvent is evaporated away. For example, cyclopentylamine
or diisopropyl amine will generally improve shelf life. Thermal
stability affects shelf life--and the ease of removing the
palladium precursor from the substrate. Thus, the Lewis base ligand
should readily volatilize when decomposed and separated from the
palladium, but not be subject to degradation within handling
temperatures. Smaller molecular-weight ligands, such as pyridine,
diisopropyl amine, and cyclopentyl amine are particularly
well-suited in this regard. In another embodiment, the Lewis base
ligand is selected to give a decomposition temperature for the
palladium precursor that is less than the melting temperature of
the substrate. Choice of the Lewis base ligand will then depend, in
part, on the substrate being used. Diisopropyl amine and triethyl
amine in a molar ratio of 1:1 is suitable for use with polyester
for example.
[0142] The Lewis base ligand will also affect rheological
properties of the solution. Thus, in certain embodiments, the
rheological properties of Lewis base are considered in making a
decision on which compound to use. For example, tri-ethanol-amine
acts as both a suitable Lewis base and as a surfactant.
[0143] The solvent may be selected according to a number of
factors. In one embodiment, the solvent is a polar molecule or a
combination of polar molecules. In some embodiments, the solvent is
aprotic, preferably comprised of one or more polar aprotic
compounds. Thus, the solvent may be a) polar or non-polar, b)
aprotic or protonic, or any combination of a) and b). The solvent
should be chosen so that it does not interfere with the balance
between the Lewis base ligand and the palladium precursor
compound.
[0144] Some suitable solvents include glycol ethers, methanol,
amylacetate, gamma-butyrolactone, water, ethylene glycol,
di-ethylene glycol, propylene glycol, isobutyl acetate, DMF,
tetramethyl urea, toluene hexane, cyclohexanone, terpeneol,
2,2-dimethoxy propane, chloroform, dichloromethane, ethylene
carbonate, ethylene glycol, diethylene glycol dimethyl ether,
propylene glycol monomethyl ether acetate, butyl acetate,
hydrocarbons such as toluene, xylenes, cyclo hexanone, ethylene
glycol dimethyl ether, ethylene glycol diethyl ether, iso amyl
acetate. A mixture of two or more of these solvents may also be
used.
[0145] Choice of the solvent may be influenced by the intended
process for removing it from the deposition substrate. If
evaporation is chosen, the solvent should have a relatively high
vapor pressure at the temperature employed to remove the solvent.
In addition, heat capacity can affect the choice of a solvent. Note
that the evaporation rate strongly influences the speed and spatial
accuracy of pattern manufacture as described above. Mixtures of
solvents may then be varied to achieve a desired evaporation
temperature.
[0146] As mentioned above, rheological properties of the solvent
may also affect solvent selection. Appropriate rheological
properties for solvent selection include density, viscosity, and
surface tension. The solvent rheological properties may also be
selected relative to a particular substrate being used; liquid and
droplet performance on paper is often different than on a plastic
material. A mixture of amyl acetate and glycol ethers is
well-suited as a solvent for use with polyimid. Choice of solvent
rheological properties may also be affected by a printing apparatus
or dispensing mechanism in the printing apparatus, e.g., to reduce
viscosity for Gravure printing as described above. In addition,
since printing resolution is often affected by solvent properties,
surface tension for the solvent may be modified in order to
increase resolution of a printed pattern.
[0147] The palladium ink also may include a solvent that is chosen
for a certain combination of the properties listed above (e.g., it
may dictate the viscosity, evaporation rate, and surface tension of
solution).
[0148] The solvent must also be compatible with any components in
the printing apparatus used to deliver the palladium ink For
example, seals on many commercially available printers may include
an elastomer that corrodes in the presence of certain chemicals.
Plasticizers for example, which may be included in the palladium
precursor solution 210, are commonly known to corrode plastic
materials. Other components in a printing apparatus that may
corrode include plastics, ceramics and metal components such as
those used in a gasket, O-ring or seal. If the printer is known to
have these or other chemical sensitivities, then the solvent may be
selected to avoid corrosion of such parts. Suitable non-corrosive
solvents include diethylene glycol diethyl ether.
[0149] Having described manufacturing processes suitable for use
with the present invention, along with suitable chemistry,
alternative forms of manufacture suitable for use will now be
discussed.
[0150] The present invention also enables roll-to-roll and other
forms of continuous throughput manufacturing. Continuous throughput
manufacturing permits circuit precursors and circuits to be
efficiently produced in high-volume, and reduces the cost of
individual circuits mass-produced in this manner.
[0151] FIG. 8 illustrates a continuous throughput manufacturing
process 300 in accordance with one embodiment the present
invention. FIG. 8 also shows the manufactured product at each
manufacturing stage.
[0152] Manufacturing process 300 begins with providing a substrate
303 off a roll of substrate material 302. For example, roll 302 may
include a roll of thin polyester or polyimid tape.
[0153] Each layer from the roll 302 is provided to a printing
apparatus 180, which deposits a palladium precursor solution onto
the substrate. As one of skill in the manufacturing arts will
appreciate, there are numerous techniques suitable for automated
supply of a substrate between roll 302 and printing apparatus
180.
[0154] Substrate with palladium precursor solution printed thereon
(305) is provided to curing oven 304, which evaporates the solvent
from the palladium precursor solution. Curing oven 304 also
decomposes the palladium precursor to produce elemental and active
palladium on the surface of the substrate. Output of curing oven
304 are circuit precursors 307 that include active and elemental
palladium on a surface of the substrate in a pattern that resembles
a desired pattern for conductive lines to be subsequently added. As
mentioned before, the palladium pattern may be established during
palladium precursor solution deposition in printing apparatus 180
or during selective decomposition in curing oven 304.
[0155] The circuit precursors 307 are then provided, by automated
means, to electroless copper deposition station 306. Electroless
plating, also known as chemical or auto-catalytic plating, is a
non-galvaonic type of plating method that involves several
simultaneous reactions in an aqueous solution, which may occur
without the use of external electrical power. The reaction is
accomplished when hydrogen is released by a reducing agent, such as
sodium borohydride, and oxidized thus producing a negative charge
on the surface of the part. The most common electroless plating
methods are electroless nickel and copper platings, where the
chemistry for each may vary significantly. In one embodiment,
electroless copper deposition includes submersing a circuit
precursor in a solution that includes copper ions, a reducing
agent, a buffer to maintain a certain pH and a complexing agent. In
general, manufacturing process 300 may use any commercially
available electroless deposition technique or apparatus. Metals
added via electroless plating include gold, silver, copper, nickel,
rhodium, and palladium, for example. The exact chemistry and steps
will vary with the type metal.
[0156] One suitable electroless copper process consists of four
stages: cleaning, activation, acceleration, and deposition. The
cleaning stage uses a cleaner-conditioner to remove organics and
condition pattern features for the subsequent uptake of a catalyst.
The cleaner-conditioners often include an alkaline solution. An
optional micro etch step may follow the cleaning; the micro etch
processing step can be used in an electroless line, oxide line,
pattern plate line, or with chemical cleaning. Activation, through
use of a catalyst, reduces the positive ion metal being added.
Common activation catalysts include tin chloride, or palladium
chloride. Acceleration removes the remaining positive metal ions
from the pattern. Fluoboric acid is a common accelerator, as is
sulfuric acid with hydrazine.
[0157] Electroless copper deposition and baths can be divided into
two types: heavy deposition baths (designed to produce 75 to 125
micro-inches of copper) and light deposition baths (20 to 40
micro-inches). Electrolytic copper plating commonly follows light
deposition. Heavy deposition can survive the outer layer imaging
process, with copper electroplating occurring thereafter. Common
constituents of electroless copper chemistry are sodium hydroxide,
formaldehyde, EDTA (or other chelater) and a copper salt. In one
specific complex reaction, catalyzed by palladium, formaldehyde
reduces the copper ion to metallic copper. Formaldehyde (which is
oxidized), sodium hydroxide (which is broken down), and copper
(which is deposited) must be replenished frequently. Many heavy
deposition baths have automatic replenishment schemes based on
in-tank colorimeters. Light deposition formulations may be
controlled by analysis. An anti-tarnish bath may be used after
deposition.
[0158] Output of copper deposition station 306 is a circuit 309
with copper disposed over the active and elemental palladium
according to the palladium pattern.
[0159] The circuits 309 then provided, again by automated means, to
electroplating station 308. Electroplating deposits additional
metal used in the conductive lines. Electroplating is the process
by which a metal in its ionic form is supplied with electrons to
form a non-ionic coating on a desired substrate. One common
electroplating system involves a chemical solution which contains
the ionic form of the metal, an anode (positively charged) which
may consist of the metal being plated (a soluble anode) or an
insoluble anode (usually carbon, platinum, titanium, lead, or
steel), and finally, a cathode (negatively charged) where electrons
are supplied to produce a film of non-ionic metal. Electroplating
may not be necessary when enough copper or metal has been deposited
by electroless deposition station 306, but is commonly used after a
light deposition. Electroplating may include a full panel plating,
which adds about 1 mil on the surface, or a "flash" panel plating,
designed only to add small amounts of copper. Flash-plated panels
return to copper electroplating to be plated up to a required
thickness.
[0160] Output of electroplating station 308 is circuits 311 printed
on the substrate 302. In this case, the circuits are provided back
to a roll 310 for easy shipping of the individual circuits 311 in a
common roll.
[0161] Roll-to-roll manufacturing as demonstrated by manufacturing
process 300 permits automated manufacture by pulling a common line
of polyimid (or another rolled and flexible material) substrate
over a number of rollers 314 along the manufacturing process. This
reduces substrate handling, increases manufacturing speed and
efficiency, facilitates high volume manufacturing, and permits for
centralized automated control of each stage in manufacturing
process 300.
[0162] The present invention is thus well-suited for high
throughput manufacture of small circuits. FIGS. 9A and 9B
illustrate automated manufacture of RFID devices in accordance with
a specific embodiment of the present invention.
[0163] FIG. 9A illustrates an exemplary RFID device 350 in
accordance with a specific embodiment of the present invention.
RFID device (or RFID tag) 350 includes a chip 352 and an antenna
354. Chip 352 may be any commercially available RFID chip, such as
those commercially available from a wide variety of vendors such as
Motorola. Antenna 354 permits communication between chip 352 and an
external RFID reader, and includes a pattern 356 of conductive
lines on the surface of a substrate 358.
[0164] FIG. 9B illustrates the automated manufacturing process 360
of RFID device 350 according to techniques of the present
invention. Manufacturing process 360 begins by rolling a polyester
substrate from a spool 362.
[0165] The polyester substrate is then continuously fed through a
Gravure or other rolled printing apparatus 364 that deposits
palladium ink onto one or more surfaces of the polyester substrate.
The Gravure printing apparatus 364 operates at high speeds to
produce a palladium pattern that resembles the final antenna
pattern 356. Since the final RFID device 350 may be quite small and
often in the range of a few millimeters or less in size, while the
roll for Gravure printing apparatus 364 may be substantially larger
and up to a meter in diameter, hundreds or thousands of a palladium
antenna patterns (depending on the width of the polyester material
supplied to the roll) may be produced for each turn of the roll in
printing apparatus 364.
[0166] The printed palladium solution patterns on the polyester
substrate are then provided to decomposition apparatus 366, which
generates active palladium on the surface of the polyester
substrate by supplying energy to a) first evaporate the solvent
from the solution, and then b) to convert the palladium precursor
to active palladium. In this case, decomposition apparatus 366
supplies one of: hot air, ultraviolet energy, or infrared energy to
supply energy for both a) and b). For example, an infrared lamp
disposed proximate to the substrate as it passes by may be suitable
to provide enough energy for both phases of processing.
[0167] Copper is then added to the palladium precursor patterns on
the substrate (according to the location of the patterns on the
substrate) to form the metal antenna 354. As shown, manufacturing
process 360 uses both electroless copper deposition 368 and copper
electroplating 370, which were described above with respect to FIG.
8.
[0168] The automated process then transports the substrate and
antenna to an optional die-attach station 372, which adds chip 352
to each RFID device 350. This may use any robotic or automated
technology suitable for placing small devices on the polyester
substrate.
[0169] FIG. 9C shows the printed output 375 of manufacturing
process 360, which includes numerous RFID devices on the roll
material before being cut, in accordance with a specific embodiment
of the present invention. As shown, the RFID devices 350 remain on
a common polyester substrate and are rolled back onto an RFID
device spool 374. In another embodiment, the substrate is cut to
produce separated RFID devices that are individually packaged as
output of manufacturing process 360.
[0170] The present invention finds wide use. Provided now are
several additional exemplary products and applications; the
following examples are not meant to be exhaustive, and the present
invention finds use in other applications not mentioned herein for
sake of brevity.
[0171] RFID devices as produced above are suitable for use in the
following applications: package and parcel tracking, baggage
handling systems used in airports, animal tracking on farms,
inventory management, libraries, document management, electronic
toll systems, car identity, ski tickets, medical goods,
anti-counterfeiting of monetary currencies, electronic security
surveillance of articles such as clothing goods, access control
such as requiring security personnel to carry on RFID device,
etc.
[0172] Circuits produced according to the present invention find
wide application. Specific circuits include placing a palladium
layer on electrical contacts, multi-chip modules, printed wiring
boards, and PCMCIA (Personal Computer Memory Card International
Association) cards. This includes computer chips, packaging for
chips, and layered circuit designs are also suitable for production
with methods described herein. The present invention also presents
an alternative to electroplating and vacuum and adhesive deposition
techniques currently used for adding conductive lines, and is
applicable in most applications that these conventional fabrication
techniques are employed.
[0173] As mentioned previously, the present invention is well
suited to produce flexible circuits disposed on a flexible
substrate. Since the active palladium patterns do not require rigid
support of the underlying substrate, circuit precursors produced
according to FIG. 1 may be shipped and handled without compromising
subsequent copper deposition. The flexible circuits may also remain
flexible after copper deposition and conductive line formation.
[0174] Flexible conductive circuits made at high throughputs and
low cost enables circuit usage in a variety of new and existing
applications. FIG. 10A shows a tracking label 400 that includes a
layered design in accordance with a specific embodiment of the
present invention. The layered design includes an outer layer 402,
an intermediate layer 404, and a release layer 406. Outer layer 402
provides visual output for tracking label 400 and may be made from
paper or a pressure-sensitive facestock. Intermediate layer 404
includes an RFID antenna and chip that permits wireless
communication and tracking of label 400. Intermediate layer 404 may
be mass produced according to techniques described herein. Release
layer 406 includes a release coated liner, such as those that
include a peal-off adhesive. Tracking label 400 is thus well-suited
for the shipping industry where large number of packages are sent
and tracked on a daily basis. Release layer 406 permits easy of
use, while the RFID antenna in intermediate layer 404 permits
wireless tracking, which simplifies usage relative to conventional
optical tracking technologies that require a shipping employee to
manipulate and optical reader within line of sight of the tracking
label. Alternatively, the present invention permits an RFID reader
to be stored on a truck or delivery vehicle, where the RFID reader
automatically and wirelessly logs every package loaded onto the
truck and every package subsequently delivered from the truck.
[0175] The present invention also enables circuit printing on
conformal surfaces. Exemplary conformal surfaces includes those
found in cell phones, GPS systems, consumer electronics devices,
etc.
[0176] FIG. 10B shows an inner surface of a housing 420 used in a
cell phone that includes a conformal surface and circuit 422
printed thereon in accordance with a specific embodiment of the
present invention. Disposing circuit 422 on housing permits the
cell phone to include one less structure dedicated specifically to
a circuit. This reduces volume of the cell phone, and may lead to
even thinner cell phone profiles.
[0177] The present invention also permits metal deposition onto
non-circuit structures. For example, circuit components, such as
antennae, may be made using techniques described herein. The
substrate may include a fiber. These (and other non-metal coated
fibers) may be used to create a woven structure or fibrous
material. In one embodiment, patterns are not disposed on
individual fibers, however, patterns may be created by weaving in a
process that optionally employs both coated and uncoated fibers. As
mentioned above, oddly shaped substrates may be field coated, such
as brushes and their individual bristles, sponges, hook and loop
fasteners, etc.
[0178] Although the foregoing invention has been described in some
detail for purposes of clarity of understanding, it will be
apparent that certain changes and modifications may be practiced
within the scope of the appended claims. Therefore, the present
examples are to be considered as illustrative and not restrictive,
and the invention is not to be limited to the details given herein,
but may be modified within the scope of the appended claims.
* * * * *