U.S. patent application number 13/284032 was filed with the patent office on 2012-02-23 for antimicrobial coating system.
This patent application is currently assigned to 3M Innovative Properties Company. Invention is credited to Duane Douglas Fansler, Gerald R.A. Hofmann, Mitchell T. Johnson, Linda K.M. Olson, Caroline M. Ylitalo.
Application Number | 20120045498 13/284032 |
Document ID | / |
Family ID | 38024179 |
Filed Date | 2012-02-23 |
United States Patent
Application |
20120045498 |
Kind Code |
A1 |
Ylitalo; Caroline M. ; et
al. |
February 23, 2012 |
ANTIMICROBIAL COATING SYSTEM
Abstract
An antimicrobial coating system, a film-forming composition, and
an antimicrobial film. In some embodiments, the antimicrobial
coating system can include a film-forming composition comprising a
polymer having an effective molecular weight, and an effective
amount of an antimicrobial agent dispersed within the polymer. The
film-forming composition can form a water-insoluble, biocidal
antimicrobial film when applied to a surface.
Inventors: |
Ylitalo; Caroline M.;
(Stillwater, MN) ; Hofmann; Gerald R.A.; (Oakdale,
MN) ; Johnson; Mitchell T.; (Gig Harbor, WA) ;
Olson; Linda K.M.; (Saint Paul, MN) ; Fansler; Duane
Douglas; (Dresser, WI) |
Assignee: |
3M Innovative Properties
Company
|
Family ID: |
38024179 |
Appl. No.: |
13/284032 |
Filed: |
October 28, 2011 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12097334 |
Nov 10, 2008 |
|
|
|
PCT/US2006/047779 |
Dec 14, 2006 |
|
|
|
13284032 |
|
|
|
|
60743037 |
Dec 14, 2005 |
|
|
|
60743038 |
Dec 14, 2005 |
|
|
|
Current U.S.
Class: |
424/407 ; 436/5;
514/558 |
Current CPC
Class: |
A01N 25/10 20130101;
A01N 25/34 20130101; A01N 25/34 20130101; C09D 5/14 20130101; A01N
37/02 20130101; A01N 59/16 20130101; A01N 47/44 20130101; A01N
25/10 20130101; A01N 37/06 20130101; A01N 37/06 20130101; A01N
31/16 20130101; A01N 59/16 20130101; A01N 33/12 20130101; A01N
59/00 20130101; A01N 25/34 20130101; A01N 59/12 20130101; A01N
25/34 20130101; A01N 59/20 20130101; A01N 47/44 20130101; A01N
37/02 20130101; A01N 59/12 20130101; A01N 59/00 20130101; A01N
31/16 20130101; A01N 59/20 20130101; A01N 33/12 20130101 |
Class at
Publication: |
424/407 ;
514/558; 436/5 |
International
Class: |
A01N 25/24 20060101
A01N025/24; A01P 1/00 20060101 A01P001/00; G01N 31/00 20060101
G01N031/00; A01N 37/00 20060101 A01N037/00 |
Claims
1. A film-forming composition comprising: a polymer comprising at
least one of polyvinyl alcohol having an effective molecular
weight, acrylic, urethane, and a combination thereof; an effective
amount of an antimicrobial agent dispersed within the polymer, the
antimicrobial agent comprising at least one of a fatty acid
monoester, a fatty acid monoether, and a combination thereof; and a
solvent, wherein the film-forming composition includes a solid
concentration of no greater than about 50% by weight, the
film-forming composition forming a water-insoluble, biocidal
antimicrobial film when applied to a surface.
2. The film-forming composition of claim 1, wherein the
antimicrobial agent constitutes about 0.1% by weight to about 20%
by weight of the film-forming composition.
3. The film-forming composition of claim 1, wherein the
antimicrobial agent constitutes about 1% by weight to about 10% by
weight of the film-forming composition.
4. The film-forming composition of claim 1, wherein the
film-forming composition further comprises a fast-acting
antimicrobial agent selected from the group consisting of
quaternary ammonium salts, benzalkonium chlorides, biguanide
compounds, alcohols, bleach, hydrogen peroxide, urea hydrogen
peroxide, hydrogen peroxide stabilized in a sodium pyrophosphate
matrix, hydrogen peroxide chelated in polyvinylpyrrolidone, and
combinations thereof.
5. An antimicrobial film comprising: a polymer having an effective
molecular weight, such that the antimicrobial film is
water-insoluble; and an effective amount of an antimicrobial agent,
such that the antimicrobial film is biocidal, the antimicrobial
agent comprising at least one of a fatty acid monoester, a fatty
acid monoether, and a combination thereof, wherein the
antimicrobial film includes about 70% by weight to about 99.9% by
weight of the polymer.
6. The antimicrobial film of claim 5, wherein the antimicrobial
film exhibits microbial load reductions of at least about 99% for
gram positive pathogens and gram negative pathogens, when tested
pursuant to ASTM E2180-01.
7. The antimicrobial film of claim 5, wherein the antimicrobial
film comprises a cross-linked polymer.
8. The antimicrobial film of claim 5, wherein the antimicrobial
film comprises an end-of-service indicator.
9. A method of verifying the presence of an antimicrobial film, the
method comprising: providing the antimicrobial film of claim 5
applied to a surface; wetting the surface; and based on whether a
color change occurred upon wetting the surface, determining whether
the antimicrobial film is still intact on the surface.
10. The antimicrobial film of claim 5, wherein the antimicrobial
film includes about 90% by weight to about 99% by weight of the
polymer.
Description
CROSS-REFERENCE TO RELATED APPLICATION(S)
[0001] This is a continuation of U.S. patent application Ser. No.
12/097,334, filed Dec. 14, 2006, which is a national stage filing
under 35 U.S.C. .sctn.371 of PCT Application No. PCT/US2006/047779,
which claims priority to U.S. Provisional Patent Application No.
60/743,037, filed Dec. 14, 2005, and U.S. Provisional Patent
Application No. 60/743,038, filed Dec. 14, 2005, the disclosures of
all of which are incorporated herein by reference in their
entirety.
FIELD OF THE INVENTION
[0002] The present invention relates to antimicrobial coatings. In
particular, the present invention relates to removable
antimicrobial coatings for use on surfaces to reduce the risk of
contamination by microorganisms.
BACKGROUND
[0003] Contamination by microorganisms can have dramatic impact on
human life and health.
[0004] During everyday routines, people continuously come into
contact with a variety of surfaces that are contaminated with one
or more types of microorganisms, some of which may be pathogens.
Such surfaces may include countertops, tables, and food preparation
surfaces in restaurants, splash guards and conveyor belts in food
processing plants, public facilities, display applications, and a
variety of surfaces in healthcare settings. Contamination with
pathogenic microorganisms in such locations may result in the
spread of disease and infections to people, which correspondingly
endangers human lives and increases health care costs.
[0005] To counter the spread of undesired microorganisms,
frequently touched, potentially contaminated surfaces are typically
cleaned and sanitized on a regular basis. While this provides an
immediate reduction in concentration of microorganisms on given
surfaces, the surfaces must be repeatedly cleaned and sanitized on
a frequent basis to continue to prevent contamination by
microorganisms. One reason for this is because many antimicrobial
materials used for cleaning and sanitation become deactivated when
the surface is dried. In addition, many articles used to wipe
visible dirt from surfaces may recontaminate the wiped surface with
microorganisms that will grow and cause a cross-contamination
hazard. For example, tables and food preparation surfaces at
restaurants are continuously wiped with a sponge or towel to remove
excess consumables and garbage. The article used for wiping
frequently harbors pathogenic microorganisms that are transferred
to the wiped surface.
SUMMARY
[0006] Some aspects of the present invention provide an
antimicrobial coating system. The antimicrobial coating system can
include a film-forming composition comprising a polymer having an
effective molecular weight, and an effective amount of an
antimicrobial agent dispersed within the polymer. The film-forming
composition can form a water-insoluble, biocidal antimicrobial film
when applied to a surface.
[0007] In some aspects of the present invention, a film-forming
composition is provided. The film-forming composition can include a
polymer and an effective amount of an antimicrobial agent dispersed
within the polymer. The polymer can include at least one of
acrylic, urethane, polyvinyl alcohol having an effective molecular
weight, and combinations thereof. The antimicrobial agent can
include at least one of a fatty acid monoester, a fatty acid
monoether, a transition metal ion-containing compound, a quaternary
ammonium-containing compound, a biguanide, and combinations
thereof.
[0008] Some aspects of the present invention provide an
antimicrobial film comprising a polymer having an effective
molecular weight, and an effective amount of an antimicrobial
agent. The antimicrobial film can be water-insoluble and
biocidal.
BRIEF DESCRIPTION OF THE DRAWINGS
[0009] FIG. 1 is a side sectional view of an antimicrobial film of
the present invention disposed on a surface.
[0010] FIG. 2 is a side sectional view of the antimicrobial film
disposed on the surface, with a remover composition of the present
invention being deposited on the antimicrobial film.
[0011] FIG. 3 is a top perspective view of a hand of a user
removing the antimicrobial film from the surface with a wipe
article.
[0012] FIG. 4 is a top perspective view of an article in use for
applying an antimicrobial coating system of the present invention
to a surface to form an antimicrobial film of the present
invention.
[0013] While the above-identified drawings set forth several
embodiments of the invention, other embodiments are also
contemplated, as noted in the discussion. In all cases, this
disclosure presents the invention by way of representation and not
limitation. It should be understood that numerous other
modifications and embodiments can be devised by those skilled in
the art, which fall within the scope and spirit of the principles
of the invention. The figures may not be drawn to scale. Like
reference numbers have been used throughout the figures to denote
like parts.
DETAILED DESCRIPTION
[0014] FIG. 1 is a side sectional view of antimicrobial film 10
disposed on surface 12, where antimicrobial film 10 is formed by a
film-forming composition that can form a first part of a two-part
antimicrobial coating system of the present invention. As discussed
below, the second part of the antimicrobial coating system is a
remover composition (not shown in FIG. 1) that includes a solvent
suitable for removing antimicrobial film 10 from surface 12.
[0015] Surface 12 may be any surface that may incur contamination
by microorganisms, such as table and counter tops, food preparation
surfaces, surfaces found in publicly used locations and facilities
(e.g., public telephones, public transportation, and public
lavatory facilities), touch-screen displays, door handles, light
switches, and surfaces found in healthcare settings (e.g., bed
rails and side tables). While surface 12 is shown as a flat, planar
surface, antimicrobial film 10 may also be coated on curved and
irregular shaped surfaces. As used herein and in the appended
claims, the term "microorganism," "microbe," or a derivative
thereof, is used to refer to any microscopic organism, including
without limitation, one or more of bacteria, viruses, algae, fungi
and protozoa. In some cases, the microorganisms of particular
interest are those that are pathogenic, and the term "pathogen" is
used herein to refer to any pathogenic microorganism.
[0016] As described above, antimicrobial film 10 is derived from a
film-forming composition that is coated onto surface 12, where the
film-forming composition includes a polymer of an effective
molecular weight to provide a water-insoluble antimicrobial film 10
and an effective amount of one or more antimicrobial agents to
reduce microorganism contamination. In some embodiments, the
antimicrobial agents are dispersed within the polymer in a
releasable manner, which allows the antimicrobial agents to be
released from antimicrobial film 10 at an effective diffusion rate
to reduce microorganism contamination on surface 12. In some
embodiments, reducing microorganism contamination includes
providing biocidal activity. As used herein and in the appended
claims, the term "biocidal" is used to describe an antimicrobial
film 10 that kills microorganisms that come into contact with the
antimicrobial film 10. As a result, biocidal activity is
distinguishable over systems that merely provide inhibition of
microorganism growth, because a film that inhibits growth and/or
reproduction of microorganisms does not necessarily kill the
microorganisms. In some embodiments, as further taught by the
examples, biocidal activity, and particularly, extended biocidal
activity (e.g., after 24 hours) can be demonstrated by the
microbial load reductions exhibited by the antimicrobial film 10,
when tested pursuant to ASTM E2180-01.
[0017] While disposed on surface 12, antimicrobial film 10 is
resistant to removal by moderate frictional forces, such as
frictional forces applied when a user uses a wipe article (e.g., a
cloth towel or sponge) to wipe food or waste from surface 12. This
allows antimicrobial film 10 to provide antimicrobial protection to
surface 12 without the risk of accidentally being removed while
surface 12 is wiped clean. In some embodiments, antimicrobial film
10 is water-insoluble.
[0018] As used herein and in the appended claims, the term
"water-insoluble" is used to refer to an antimicrobial film that
does not dissolve (i.e., form a homogeneous solution) after 30
minutes of being placed in DI water at room temperature with no
stirring. One example of a method for testing water-insolubility is
by forming the antimicrobial film onto a release liner, peeling the
antimicrobial film from the release liner and submerging the
antimicrobial film in DI water at room temperature for 30 minutes
with no stirring. If, after 30 minutes, in these conditions, at
least a portion of the antimicrobial film still remains intact and
has not gone into solution, the antimicrobial film is
"water-insoluble." As a result, if an antimicrobial film swells in
water under these conditions, but does not dissolve to form a
homogeneous solution, the antimicrobial film is
"water-insoluble."
[0019] When desired, antimicrobial film 10 may be removed from
surface 12 with a remover composition, and a fresh coating of
antimicrobial film 10 may be applied to provide continuing
antimicrobial protection to surface 12. When removal of
antimicrobial film 10 is desired, the remover composition may be
applied, and antimicrobial film 10 may then be wiped off from
surface 12 under moderate frictional forces. As a result, the
antimicrobial coating system of the present invention is a
convenient system for applying and removing durable antimicrobial
coatings having biocidal activity to and from a variety of
surfaces.
[0020] Suitable polymers for use in the film-forming composition of
antimicrobial film 10 include water-soluble polymers, organic
solvent-soluble polymers, and water-based polymer dispersions.
Examples of water-soluble polymers include polyvinyl alcohols,
polyvinylpyrrolidones, polyethylene oxides, sulfonated
polyurethanes, copolymers thereof, and combinations thereof.
Suitable commercially available polyvinyl alcohols include those
available from J. T. Baker, Phillipsburg, N.J., and from
Sigma-Aldrich Company, St. Louis, Mo. Suitable commercially
available polyvinylpyrrolidones include those available from J. T.
Baker, and those available under the trade designations "PVP-Kxx"
from Peakchem, ZheJiang, China, where the "xx" number after the
letter K indicates the average molecular weight (in 1,000s of
Daltons) of the polymer (e.g., "PVP-K90" and "PVP-K30").
[0021] Suitable commercially available polyethylene oxide polymers
include those available under the trade designation "POLYOX" from
Dow Chemical Co., Midland, Mich. Suitable water-soluble polymers
may have a wide range of molecular weights, where the molecular
weight generally determines the product performance. For example,
if the polymer molecular weight is too low, the film coating may be
tacky and easily removable (i.e., has poor durability and is
water-soluble). Alternatively, if the molecular weight of the
polymer is too high, the coating solution exhibits poor solubility,
which results in the film being difficult to remove. For
applications in which the antimicrobial film 10 will need to be
removed and replenished from time to time, suitable molecular
weights provide good film durability, water-insolubility, and
relative ease of removal by an appropriate remover composition.
That is, in some embodiments, an effective molecular weight refers
to a molecular weight that allows the resulting antimicrobial film
10 to be water-insoluble. For example, in some embodiments, an
effective molecular weight of polyvinyl alcohol is at least about
100,000 Daltons, particularly, at least about 120,000, and more
particularly, at least about 150,000 Daltons.
[0022] Suitable organic solvent-soluble polymers include
polyurethanes, acrylic polymers, polyamides, copolymers thereof,
and combinations thereof. Commercially available solvent-based
polyurethanes include those available under the trade designation
"PERMUTHANE" from Stahl USA, Peabody, Mass. (e.g., "SU26-248",
which is an aliphatic polyurethane in toluene). Other suitable
polyurethanes include those commercially available under the trade
designations "ESTANE" from B.F. Goodrich, Cleveland, Ohio (e.g.,
"Estane 5715" and "Estane 5778"), and "MORTHANE" from Huntsman
Polyurethanes, Ringwood, Ill. (e.g., "CA118" and "CA237" polyester
polyurethanes). Additional suitable polymers include those
commercially available under the trade designation "U-371" from DSM
NeoResins, Wilmington, Mass.
[0023] Examples of water-based polymer dispersions include
polyurethanes, polyureas, polyacrylics, polyethers, polyester, and
copolymers thereof and combinations thereof. Suitable aqueous
dispersions include urethanes such as those commercially available
under the trade designation "NEOREZ" from DSM NeoResins,
Wilmington, Mass. (e.g., "NEOREZ R-960" and "NEOREZ R-9699");
acrylics such as those commercially available under the trade
designation "NEOCRYL" from DSM NeoResins (e.g., "NEOCRYL XK-90",
"NEOCRYL XK-96", and "NEOCRYL XK-95"); and acrylic urethane
copolymers such as those commercially available under the trade
designation "NEOPAC" from DSM NeoResins. Additional suitable
water-based urethanes include those commercially available under
the trade designations "RU-077" and "RU-075" from Stahl USA,
Peabody, Mass.
[0024] Water-soluble materials can be suitable for use in
situations where antimicrobial film 10 remains dry until the
intended removal with a water-based remover composition. The
above-listed materials may also be partially or fully cross-linked
to improve the mechanical structure of the polymer, and to reduce
the water solubility of such materials. Polymers having reduced
water solubility are beneficial for use on surfaces (e.g., surface
12) that come into contact with water (e.g., surfaces that are
rinsed or soaked with water). To initiate the cross-linking, the
polymer may include curing agents, such as chain extension agents,
chemical cross-linking agents, and radiation cross-linking agents
(e.g., photoinitiators).
[0025] To initiate the cross-linking, the film-forming composition
may include cross-linking agents, such as chain extension agents
and chemical cross-linking agents. Examples of cross-linking agents
include isocyanates such as those commercially available under the
trade designation "DESMODUR" from Bayer AG, Pittsburgh, Pa.;
aziridine crosslinkers such as those commercially available under
the trade designation "CX-100" from DSM NeoResins, Wilmington,
Mass.; and those commercially available under the trade designation
"XR-2500" from Stahl USA, Peabody, Mass. Suitable chain extension
agents include carbodiimides such as those commercially available
under the trade designation "EX62-944", and melamines such as those
commercially available under the trade designation "XR-9174", both
from Stahl USA.
[0026] Examples of particularly suitable cross-linkable polymer
compositions include self cross-linking polymer dispersions, where
the deposited coating self cross-links upon drying to form a
durable, water-insoluble coating layer. Self cross-linking polymer
dispersions typically contain side groups that react to form
chemical bonds via condensation polymerizations, which take place
upon evaporation of water. Self cross-linking polymer dispersions
offer the advantage of forming antimicrobial films (e.g.,
antimicrobial film 10) that are solvent resistant without requiring
cross-linking agents. Various types of cross-linking agents can
pose potential health risks because they are small, solvent-borne,
organic molecules (e.g., isocyanates).
[0027] Examples of self cross-linking urethane dispersions include
polyester-urethanes that are terminated by hydrolysable silyl
groups and contain solubilizing sulfonic acid functional groups.
Such polyester-urethanes are described in Krepski, et al., U.S.
Pat. No. 5,929,160, which is incorporated by reference in its
entirety. Additional examples of suitable self cross-linking
urethane dispersions include polyurethane water-based dispersions
containing hydroxyl groups to accomplish the self cross-linking
function. Suitable hydroxyl group-based polyurethanes include those
prepared pursuant to the process described in Mazanek et al., U.S.
Pat. No. 7,049,367, which is incorporated by reference in its
entirety. Even further additional examples of suitable self
cross-linking urethane dispersions include polyurethane polymer
hybrid dispersions based on oxidatively drying polyols, such as
those disclosed in Ingrisch et al., U.S. Pat. No. 6,462,127, which
is incorporated by reference in its entirety.
[0028] Examples of commercially available self cross-linking
polymers include dispersions sold under the trade designations
"RHEOPLEX" and "ROVACE" available from Rohm and Haas Company,
Philadelphia, Pa., which are typically used as binders for textile
and non-woven substrates for the protection of color dyes applied
to the substrates. Exemplary compositions include the trade
designated "RHEOPLEX HA-12" (non-ionic dispersion with glass
transition temperature of about 19.degree. C.) and "RHEOPLEX
TR-407" (anionic dispersion with glass transition temperature of
34.degree. C.), both of which exhibit good wash durability and
chemical resistance. Additional examples of commercially available
self cross-linking polymers include the trade designated "NEOREZ
R-551" polyether-based polymers and "NEOCRYL XK-98" acrylic
emulsion polymers, both of which are available from DSM NeoResins,
Wilmington, Mass. The "NEOCRYL XK-98" acrylic emulsion polymers are
particularly suitable because they provide good adhesion to most
substrates and exhibit high gloss and block resistance.
[0029] Suitable concentrations of the polymer in the film-forming
composition of antimicrobial film 10, after application and drying
of the film, include any concentration that is effective for
dispersing and containing the antimicrobial agents. Examples of
suitable concentrations of the polymer in the film-forming
composition of antimicrobial film 10 range from about 50% by weight
to about 99.9% by weight, with particularly suitable concentrations
ranging from about 70% by weight to about 99% by weight, and with
even more particularly suitable concentrations ranging from about
90% by weight to about 95% by weight.
[0030] Suitable antimicrobial agents for use in the film-forming
composition of antimicrobial film 10 include any inorganic or
organic antimicrobial agent that is effective for reducing
microbial contamination. Examples of suitable antimicrobial agents
include transition metal ion-containing compounds, (e.g., silver,
zinc, copper, gold, tin and platinum-based compounds), fatty acid
monoesters/monoethers, triclosan, peroxides, iodines, quaternary
ammonium-containing compounds, biguanides, complexes thereof (e.g.,
iodophores), derivatives thereof, and combinations thereof.
[0031] Examples of suitable silver-containing compounds include
silver sulfate, silver acetate, silver chloride, silver lactate,
silver phosphate, silver stearate, silver thiocyanate, silver
proteinate, silver carbonate, silver nitrate, silver sulfadiazine,
silver alginate, silver nanoparticles, silver-substituted ceramic
zeolites, silver complexed with calcium phosphates, silver-copper
complexed with calcium phosphates, silver dihydrogen citrates,
silver iodines, silver oxides, silver zirconium phosphates,
silver-substituted glass, and combinations thereof.
[0032] Suitable commercially available silver zeolite-containing
compounds include those sold under the trade designation "AGION"
from AgION Technologies Inc., Wakefield, Mass.; those available
under the trade designations "IRGAGUARD B5000" and "IRGAGUARD
B8000", which are based on AgZn zeolites supplied by Ciba Specialty
Chemicals, Tarrytown, N.Y.; as well as those available under the
trade designation "ALPHASAN", which are silver sodium hydrogen
zirconium phosphates, supplied by Milliken Chemicals, Spartanburg,
S.C. Suitable commercially available silver chloride-containing
compounds include those available under the trade designation
"JMAC" from Clariant Corporation, Charlotte, N.C.
[0033] Examples of suitable commercially available organic
antimicrobial agents include polymeric quaternary ammonium salts
such as 2-butenyldimethyl ammonium chloride polymers commercially
available under the trade designation "POLYQUAT" from Arch
Chemicals, Inc., Norwalk, Conn.; phenolic compounds such as phenol
and its derivatives, parabens, and triclosan, which has the
chemical formula 2,4,4'-trichloro-2'-hydroxy diphenyl ether, and is
commercially available from Ciba Specialty Chemicals, Tarrytown,
N.Y.; poly(iminoimidocarbonylimidocarbonyliminohexamethylene
hydrochlorides), commercially available under the trade designation
"VANTOCIL P" from Arch Chemicals, Inc., Norwalk, Conn.;
polyhexamethylene biguanides, antimicrobial lipids such as those
disclosed in Scholz et al., U.S. Publication No. 2005/0089539,
which is incorporated herein by reference, antimicrobial acids
(e.g., fatty acids, benzoic acids, and salicylic acids),
antimicrobial natural oils (e.g., tea tree oils, and grape fruit
seed extracts), and combinations thereof. Additional suitable
organic antimicrobial agents include organic salts of transition
metals (i.e., organometallic antimicrobial agents), such as silver
salts (e.g., silver lactate), copper salts (e.g., copper
napthenate), zinc salts, and tin salts (e.g., trialkyl tin
hydroxides and triaryl tin hydroxides).
[0034] Suitable antimicrobial lipids include, for example, fatty
acid monoesters/monoethers. In some embodiments, the fatty acid
monoesters/monoethers suitable for the antimicrobial agent are
considered food grade and recognized as safe (GRAS) by the U.S.
Food and Drug Administration (FDA). Such fatty acid
monoesters/monoethers may be derived from C8 to C12 fatty acids
such as glycerol monoesters of caprylic acid, capric acid, and
lauric acid; propylene glycol monoesters of caprylic acid, capric
acid, and lauric acid; and combinations thereof. Examples of
suitable fatty acid monoesters include, but are not limited to,
glycerol monolaurate commercially available under the trade
designation "LAURICIDIN" from Med-Chem Laboratories, East Lansing,
Mich.; glycerol monocaprylate commercially available under the
trade designation "POEM M-100" from Riken Vitamin Ltd., Tokyo,
Japan; glycerol monocaprate commercially available under the trade
designation "POEM M-200" from Riken Vitamin Ltd.; propylene glycol
monolaurate, propylene glycol monocaprylate, and propylene glycol
monocaprate, all commercially available from Uniquema
International, Chicago, Ill.; and combinations thereof.
[0035] Examples of suitable concentrations of the fatty acid
monoesters/monoethers range from about 1.0% to about 30.0% by
weight. Examples of particularly suitable concentrations of the
fatty acid monoesters/monoethers in the composition range from
about 5.0% to about 20.0% by weight.
[0036] The antimicrobial agent may also include an enhancer and/or
a surfactant for use with the fatty acid monoesters/monoethers, as
discussed in Andrew et al., PCT application No. WO 00/71183,
entitled "Antimicrobial Articles," and in Andrews et al., PCT
Application No. WO01/43549, entitled "Fruit, Vegetable, and Seed
Disinfectants," both of which are incorporated herein by reference
in their entireties.
[0037] Suitable concentrations of the antimicrobial agents in the
film-forming composition of antimicrobial film 10 include any
concentration that is effective for providing biocidal activity.
This may vary depending on the type of antimicrobial agent used.
Examples of suitable concentrations of the antimicrobial agents in
the film-forming composition of antimicrobial film 10 range from
about 0.1% by weight to about 20% by weight, with particularly
suitable concentrations ranging from about 1% by weight to about
10% by weight.
[0038] In some embodiments, the antimicrobial agent may at least
partially interact with the polymer (i.e., form non-covalent bonds
(e.g., ionic bonds, hydrogen bonds, matrix interactions, etc.) or
covalent bonds with the polymer) so as not to be sufficiently
available to provide biocidal activity to microorganisms that come
into contact with the antimicrobial film 10. In other words, the
resulting antimicrobial film may not have a sufficient surface
concentration of the antimicrobial agent to provide biocidal
activity. In such embodiments, a higher concentration of
antimicrobial agent may be needed to provide biocidal activity. As
a result, in some embodiments, an effective amount of antimicrobial
agent is an amount that provides biocidal activity to
microorganisms that come into contact with the antimicrobial film
10.
[0039] A "sufficiently available" antimicrobial agent or a
"sufficient surface concentration" of the antimicrobial agent in
the antimicrobial film 10 is sometimes used to refer to an
antimicrobial film having microbial load reductions of at least 90%
against gram positive or gram negative pathogens when tested
pursuant to ASTM E2180-01, particularly, microbial load reductions
of at least 90% against gram positive and gram negative pathogens
when tested pursuant to ASTM E2180-01, particularly, microbial load
reductions of at least 99% against gram positive or gram negative
pathogens when tested pursuant to ASTM E2180-01, and more
particularly, microbial load reductions of at least 99% against
gram positive and gram negative pathogens when tested pursuant to
ASTM E2180-01.
[0040] The film-forming composition may also include fast-acting
antimicrobial agents that may not provide antimicrobial activity
over extended periods of time, but which provide fast antimicrobial
activity of a relatively short duration upon application of the
film-forming composition to surface 12. Examples of suitable
fast-acting antimicrobial agents include quaternary ammonium salts,
benzalkonium chlorides, biguanide compounds (e.g., halogenated
hexidines such as chlorhexidine, chlorhexidine gluconate, and
chlorhexidine acetate), alcohols (e.g., low molecular weight
alcohols such as ethyl alcohol and isopropyl alcohol), bleach,
hydrogen peroxide, urea hydrogen peroxide, hydrogen peroxide
stabilized in a sodium pyrophosphate matrix, hydrogen peroxide
chelated in polyvinylpyrrolidone, and combinations thereof.
Examples of suitable commercially available quaternary ammonium
salts include didecyl dimethyl ammonium chlorides available under
the trade designation "BTC 1010" from Stepan Company, Northfield,
Ill., and under the trade designation "BARDAC 2250" from Lonza
Group Ltd., Valais, Switzerland; dialkyl dimethyl ammonium
chlorides available under the trade designation "BARDAC 2050 also
from Lonza Group Ltd.; and alkyl dimethyl benzyl ammonium chloride
available under the trade designation "BARQUAT MB-50" also from
Lonza Group Ltd.
[0041] Suitable concentrations of the fast-acting antimicrobial
agents in the film-forming composition of antimicrobial film 10
include any concentration that is effective for reducing microbial
contamination, and may depend on the type of fast-acting
antimicrobial agent used. For example, when the fast-acting
antimicrobial agent is an alcohol, suitable concentrations of the
alcohol in the film-forming composition range from about 20% by
weight to about 80% by weight, with particularly suitable
concentrations ranging from about 40% by weight to about 60% by
weight. Examples of suitable concentrations of the antimicrobial
agents in the film-forming composition of antimicrobial film 10
when quaternary amines are used range from about 0.001% by weight
to about 10% by weight, with particularly suitable concentrations
ranging from about 0.1% by weight to about 5% by weight.
[0042] The film-forming composition may also include surfactants
and thickeners to modify wetting and flow properties. Examples of
suitable surfactants include the trade designated "SURFONIC L"
series surfactants commercially available from Huntsman
Corporation, Salt Lake City, Utah; and the trade designated "ZONYL"
surfactants commercially available from E. I. du Pont de Nemours
and Company. Examples of suitable thickeners include starch, gum
arabic, guar gum, and carboxymethylcellulose. A particularly
suitable thickening agent is commercially available under the trade
designation "NEOCRYL-A1127" from DSM NeoResins, Wilmington, Mass.
Examples of suitable total concentrations of surfactants and
thickeners in the film-forming composition of antimicrobial film 10
range from about 1% by weight to about 20% by weight, with
particularly suitable total concentrations ranging from about 5% by
weight to about 10% by weight.
[0043] Additional optional components that may be incorporated into
the film-forming composition include buffering agents and pH
adjusting agents, fragrances or perfumes, dyes and/or colorants,
solubilizing materials, defoamers, lotions and/or mineral oils,
essential oils, enzymes, bleaching agents, preservatives, indicator
dyes, and combinations thereof. Examples of suitable total
concentrations of the optional components in the film-forming
composition of antimicrobial film 10 range from about 1% by weight
to about 20% by weight, with particularly suitable total
concentrations ranging from about 1% by weight to about 5% by
weight. The film-forming composition of antimicrobial film 10 may
contain a dye to allow color tinting of antimicrobial film 10 if
desired.
[0044] Tinted films allow the end user to visually verify the film
coverage of surface 12 and, after applying the remover composition,
visually ensure that all of antimicrobial film 10 has been removed
from surface 12. Furthermore, indicator dyes provide color to the
formulation allowing a user to visually verify the film coverage of
surface 12, but the color disappears upon drying (e.g., upon
exposure to air) within a short time period (e.g., few seconds or
minutes) leaving a colorless film. Examples of suitable indicator
dyes include dyes based on phthalein chemistry, such as
phenolphthalein (pink), thymolphthalein (blue), and
o-cresolphthalein (purple), all of which are obtainable from
Sigma-Aldrich Chemical Company, Saint Louis, Mo. Such indicator
dyes also allow a user to check that antimicrobial film 10 is still
intact by wetting the surface 12. For example, in some embodiments,
if antimicrobial film 10 including the indicator dye is still
intact on the surface 12, the surface 12 will change color upon
wetting (e.g., with water, a high pH solution (such as WINDEX-brand
glass cleaner solution), an ammonia solution, or whatever substance
to which the indicator dye is sensitive). This would indicate to
the user, for example, that antimicrobial film 10 is still applied
to the surface 12.
[0045] The film-forming composition of antimicrobial film 10 may be
formed by blending the antimicrobial agent, the polymer, and any
optional components together. This may be performed as a solution
in a solvent, where the solvent is selected to substantially
dissolve or disperse the antimicrobial agent, the polymer, and any
optional components. Examples of suitable solid concentrations in
the solvent for the resulting film-forming composition range from
about 5% by weight to about 50% by weight. For water-based polymer
dispersions, higher concentrations of solids may be achieved
without an increase in the solution viscosity. Accordingly,
particularly suitable solid concentrations in the solvent for
water-based polymer dispersions range from about 10% to about 40%
by weight. For non-dispersion water-based coatings, and for
solvent-based coatings, particularly suitable solid concentrations
in the solvent range from about 5% to about 20% by weight.
[0046] The film-forming composition may then be applied to surface
12 and dried to form antimicrobial film 10. The film-forming
composition may be applied to surface 12 in a variety of manners,
such as by spraying, brushing, rod coating, or by wiping the
film-forming composition onto surface 12 with a wipe article.
[0047] For example, FIG. 4 is a top perspective view of an article
30 being wiped across surface 12 by hand 16 of a user. Article 30
is a wipe article that includes a substrate and a film-forming
composition impregnated within the substrate. As the user wipes
article 30 across surface 12, the film-forming composition is
extracted from the substrate of article 30 and deposits on surface
12. This forms a thin, continuous antimicrobial film 10 on surface
12.
[0048] The substrate of article 30 may be any type of woven,
non-woven, knitted, foam, or sponge substrate, or combinations
thereof, that is capable of being impregnated with the film-forming
composition. The substrate may consist of a single layer or
multiple layers of one or more materials. Non-woven substrates are
particularly suitable because of their utility in the manufacture
of cleaning and scouring articles.
[0049] Because the film-forming composition is extracted from the
substrate during use, article 30 is particularly suitable as a
disposable wipe (i.e., article 30 may be formed from substrate
materials intended to be discarded after use). Examples of suitable
disposable wipe materials for the substrate of article 30 include
spun-bond and spun-lace non-woven materials having a basis weight
ranging from about 15 grams/meter.sup.2 to about 75
grams/meter.sup.2. Such materials are generally made of synthetic
polymers, natural polymers, and combinations thereof. Suitable
synthetic polymers include rayon polyester, polyethylene
terephthalate (PET), polyvinyl chloride, polyacrylamide,
polystyrene, polyethersulfone, acrylics and acrylic copolymers,
rayon, polyolefins (e.g., polypropylene), and combinations thereof.
Suitable natural polymers include wood pulp, cotton, cellulose,
rayon, and combinations thereof.
[0050] In alternative embodiments, article 30 may be formed from
materials used for semi-disposable or reusable wipes. Examples of
suitable semi-disposable wipe materials for the substrate of
article 30 include spun-lace non-woven materials having a basis
weight ranging from about 75 grams/meter.sup.2 to about 250
grams/meter.sup.2. Such materials may be formed from fibers or
microfibers of polyester, polyamide, viscose, or combinations
thereof. Examples of suitable reusable wipe materials for the
substrate of article 30 include knitted, woven, thermo-bonded,
latex-coated, and chamois-type materials having a basis weight
ranging from about 100 grams/meter.sup.2 to about 300
grams/meter.sup.2. Such materials may be formed from fibers or
microfibers of polyester, rayon, viscose, polypropylene, natural
fibers, polyamides, or combinations thereof.
[0051] Examples of suitable commercially available wipe materials
include those sold under the trade designation "SONTARA", non-woven
fabrics available from Du Pont such as SONTARA 8001 (100% polyester
substrate) and SONTARA 8100 (50% polyester/50% Dacron). Other
suitable wipe materials include those designated as M001, M022, and
M017, and are 100% spunlaced polyester materials available from
Polymer Group Inc., Wilmington, Del. Other polyester substrate
materials can be obtained from Jacob Holms Industries under the
designation 350160 and 10203-003.
[0052] In some embodiments, article 30 is glove-shaped to receive
hand 16 of the user. This provides a convenient means for the user
to wipe article 30 across surface 12 to extract the film-forming
composition. In some embodiments, the glove-shaped article 30
includes a barrier layer (e.g., a flexible polymeric layer) between
the substrate containing the film-forming composition and the hand
16 of the user. This can inhibit contact between the film-forming
composition and hand 16 of the user, thereby reducing the risk of
irritating the skin of hand 16.
[0053] The film-forming composition that is impregnated within the
substrate includes a polymer, one or more antimicrobial agents, and
a solvent. In some embodiments, the polymer and the antimicrobial
agent are substantially dissolved in the solvent, and the solvent
is impregnated within the substrate, thereby retaining the polymer
and the antimicrobial agents (and any optional components) within
the substrate. Examples of suitable concentrations of the
film-forming composition in article 10, prior to extraction, range
from about 50% by weight to about 500% by weight of the substrate,
based on a dry weight of the substrate. Examples of particularly
suitable concentrations of the film-forming composition in article
10, prior to extraction, range from about 100% by weight to about
400% by weight of the substrate, based on a dry weight of the
substrate.
[0054] The film-forming composition may be impregnated within the
substrate in a variety of manners, such as spraying, knife coating,
roll coating, curtain coating, spin coating, immersion coating, and
combinations thereof. After impregnation and prior to use, the
substrate is at least partially saturated with the film-forming
composition. The resulting article 10 may then be packaged in a
sealed environment (individually or with multiple articles) to
prevent the solvent from evaporating. When the user desires to
apply an antimicrobial film on surface 12, the user may wipe
article 10 across surface 12 while applying a moderate amount of
pressure. The applied pressure and the frictional force imposed by
the wiping action causes portions of the film-forming composition
to deposit from the substrate of article 10. In particular, the
polymer, the antimicrobial agent, and the solvent of the
film-forming composition are each deposited from the substrate of
article 10. This is in contrast to conventional antimicrobial
wipes, in which only an antimicrobial (and typically a solvent) are
deposited. By depositing the polymer with the antimicrobial agent
and the solvent, the resulting antimicrobial film coated on surface
12 prevents the antimicrobial agent from being immediately washed
away when surface 12 is cleaned.
[0055] The amount of film-forming composition extracted is
dependent on the pressure applied, the extent of the wiping action,
and the concentration of the film-forming composition impregnated
within the substrate. In some embodiments, the amount of
film-forming composition extracted is enough to form a dried
antimicrobial film having a layer thickness on surface 12 (after
drying) ranging from about 1 micrometers to about 100 micrometers,
and particularly, ranging from about 2 micrometers to about 50
micrometers. This can provide a suitable concentration of
antimicrobial agents to reduce the risk of microorganism
contamination.
[0056] After use, article 30 may be discarded. Alternatively, if
article 30 retains a useable portion of the impregnated
film-forming composition, article 30 may be reused to apply
antimicrobial films to additional surfaces until the reservoir of
film-forming composition impregnated within substrate 12 is
depleted. Accordingly, article 30 may be used as a disposable or
semi-disposable wipe article by consumers. However, article 30 may
also be re-impregnated with an additional supply of the
film-forming composition for subsequent use. This increases the
product life of article 30.
[0057] After being applied to surface 12, the film-forming
composition may be dried to remove the solvent. Suitable drying
techniques include air drying (e.g., forced or passive) at room
temperature or elevated temperatures. The use of volatile solvents
(e.g., isopropanol and acetone) can be useful for increasing the
rate of drying. After drying, the resulting antimicrobial film is a
thin, continuous film that provides antimicrobial protection to
surface 12, as discussed above. In some embodiments, the polymer
matrix may also be fully or partially cross-linked after being
applied to surface 12 and dried. This can increase the mechanical
integrity of the antimicrobial film, thereby allowing the
antimicrobial film to provide abrasion and chemical resistance to
surface 12 in addition to antimicrobial activity.
[0058] Examples of suitable layer thicknesses for antimicrobial
film 10 (after drying) range from about 1 micrometer to about 500
micrometers, with particularly suitable layer thicknesses ranging
from about 2 micrometers to about 50 micrometers. Once applied,
antimicrobial film 10 is a thin, durable film that provides
antimicrobial protection to surface 12, as discussed above. In some
embodiments, antimicrobial film 10 is also a transparent film,
which allows the aesthetic qualities of the underlying surface
(e.g., surface 12) to be visually observed through antimicrobial
film 10.
[0059] As discussed above, after application to surface 12,
antimicrobial film 10 exhibits antimicrobial activity to reduce the
microorganism contamination of surface 12, and particularly,
exhibits biocidal activity. Examples of suitable levels of biocidal
activity include microbial load reductions of at least about 90%
for at least one of S. aureus (gram positive) and Ps. aeruginosa
(gram negative) pathogens. Examples of even more suitable levels of
biocidal activity include microbial load reductions of at least
about 99% for at least one of S. aureus (gram positive) and Ps.
aeruginosa (gram negative) pathogens. Examples of particularly
suitable levels of biocidal activity include microbial load
reductions of at least about 90% for both of S. aureus (gram
positive) and Ps. aeruginosa (gram negative) pathogens. Finally,
examples of even more particularly suitable levels of biocidal
activity include microbial load reductions of at least about 99%
for both of S. aureus (gram positive) and Ps. aeruginosa (gram
negative) pathogens. The "microbial load reductions" herein refer
to microbial load reductions obtained pursuant to ASTM
E2180-01.
[0060] Antimicrobial film 10 may also include an end-of-service
indicator to provide visual indication prompting the user to
replace antimicrobial film 10. Examples of suitable end-of-service
indicators include time-temperature indicators and color changing
dyes. An end-of-service indicator may be applied to antimicrobial
film 10 in the form of a label or paint to the corners of
antimicrobial film 10 after antimicrobial film 10 is formed on
surface 12. In some embodiments, the indicator is calibrated to
indicate a color change at about the time when the corresponding
antimicrobial layer 10 should be replaced (e.g., when the
antimicrobial activity levels have substantially decreased or are
exhausted).
[0061] Time-temperature indicators typically operate by chemical
reaction mechanisms, diffusion mechanisms, and capillary driven,
fluid-wicking mechanisms. Examples of suitable time-temperature
indicators are disclosed in Bommarito, et al., U.S. Pat. No.
6,741,523 (i.e., microstructured time-dependent indicators) and
Arens, et al., U.S. Pat. No. 5,667,303, both of which are
incorporated by reference in their entireties, and in The Wiley
Encyclopedia of Packaging Technology, 400-406 (John Wiley &
Sons, 1986) under the section entitled "Indicating Devices".
Examples of suitable commercially available time-temperature
indicators include those sold under the trade designations "MONITOR
MARK" from 3M Corporation, St. Paul, Minn.; "WARM MARK" from Dry
Pak Industries, Studio City, Calif.; "FRESH CHECK" from Lifelines
Technology Inc., Morris Plains, N.J.; "VISTAB" from Visual
Indicator Tag Systems AB, Malmo, Sweden; and "TT MONITOR" from
Avery Dennison Corporation, Pasadena, Calif.
[0062] FIG. 2 is a side sectional view of antimicrobial film 10
disposed on surface 12, with remover composition 14 being deposited
on antimicrobial film 10. Remover composition 14 is a solvent-based
composition that dissolves and/or swells the film-forming
composition of antimicrobial film 10, as discussed below. Remover
composition 14 may be deposited on antimicrobial film 10 in a spray
form as illustrated in FIG. 2. Alternatively, remover composition
14 may be incorporated in a wipe article that is wiped across
antimicrobial film 10, thereby allowing remover composition 14 to
dissolve and/or swell antimicrobial film 10 during the wiping
process.
[0063] Remover composition 14 may include one or more solvents that
are effective for dissolving the film-forming composition of
antimicrobial film 10. Examples of suitable solvents for use in
remover composition 14 include water, aqueous alkaline solvents,
volatile solvents (e.g., acetone and isopropanol), glycols, and
combinations thereof.
[0064] If the polymer in the film-forming composition of
antimicrobial film 10 is not cross-linked, then the solvent of
remover composition 14 may be selected to dissolve antimicrobial
film 10. In some embodiments, the remover solvent is selected to
closely match the solubility parameter of the polymer used. The
term "solubility parameter" herein refers to the Hildebrand
solubility parameter (.delta.), which is a solubility parameter
represented by the square root of the cohesive energy density of a
material, having units of (pressure).sup.1/2, and being represented
by the following equation:
.delta. = ( .DELTA. H - RT V ) ( 1 ) ##EQU00001##
where .DELTA.H is the molar vaporization enthalpy of the material,
R is the universal gas constant, T is the absolute temperature, and
V is the molar volume of the solvent. Hildebrand solubility
parameters are generally provided in conventional units of
(calories/centimeter.sup.3).sup.1/2 ((cal/cm.sup.3).sup.1/2) and in
SI units of megaPascals.sup.1/2 (MPa.sup.1/2).
[0065] Hildebrand solubility parameters are tabulated for solvents
in Barton, A. F. M., Handbook of Solubility and Other Cohesion
Parameters, 2.sup.nd Ed. CRC Press, Boca Raton, Fla., (1991), for
monomers and representative polymers in Polymer Handbook, 3.sup.rd
Ed., J. Brandrup & E. H. Immergut, Eds. John Wiley, NY pp.
519-557 (1989), and for many commercially available polymers in
Barton, A. F. M., Handbook of Polymer-Liquid Interaction Parameters
and Solubility Parameters, CRC Press, Boca Raton, Fla., (1990).
Examples of suitable differences in Hildebrand solubility
parameters between the polymer in the film-forming composition of
antimicrobial film 10 and the solvent of remover composition 14
include differences of about 5.0 (cal/cm.sup.3).sup.1/2 or less,
with particularly suitable differences in Hildebrand solubility
parameters including differences of about 2.0
(cal/cm.sup.3).sup.1/2 or less, and with even more particularly
suitable differences in Hildebrand solubility parameters including
differences of about 1.0 (cal/cm.sup.3).sup.1/2.
[0066] If the polymer in the film-forming composition of
antimicrobial film 10 is cross-linked, then the solvent of remover
composition 14 may be selected to either dissolve (by chemically
disrupting and breaking the cross-links) antimicrobial film 10,
swell (by absorbing into the cross-linked polymer matrix)
antimicrobial film 10, or a combination thereof. Swelling takes
place when the solvent of remover composition 14 penetrates into a
cross-linked polymer network through the surface of antimicrobial
film 10, which acts as a semi-permeable membrane. The solvent
interacts with segments of the polymer network, which increases
their mobility, disrupts the adhesion of the polymer segments to
surface 12, and facilitates the removal of the film-forming
composition. Swelling will take place only if the free energy of
mixing between the solvent and the polymer segments is negative,
where the free energy of mixing is defined as:
.DELTA.G.sub.m=.DELTA.H.sub.m-T.DELTA.S.sub.m=RT(n.sub.1 ln
.phi..sub.1+n.sub.2 ln .phi..sub.2+.chi..sub.1.phi..sub.2n.sub.1)
(2)
where .DELTA.G.sub.m is the Gibbs free energy of mixing,
.DELTA.H.sub.m is the enthalpy of mixing, T is the absolute
temperature, .DELTA.S.sub.m is the entropy of mixing, R is the
universal gas constant, n.sub.1 is the molar fraction of the
solvent in the swollen film, .phi..sub.1 is the weight fraction of
the solvent, n.sub.2 is molar fraction of the polymer in the
swollen film, .phi..sub.2 the weight fraction of the polymer, and
.chi..sub.1 is the Flory-Huggins interaction parameter. Equation
(2) along with more detailed discussion of the theory of polymer
swelling can be found in Richards, E. G., An Introduction to
Physical Properties of Large Molecules in Solution, IUPAB
Biophysics Series, Cambridge University Press, Cambridge,
(1980).
[0067] Examples of suitable solvents for use in remover composition
14 when the polymer of the antimicrobial film is partially or fully
cross-linked (i.e., polymers having reduced water solubility)
include aqueous alkaline solvents (e.g., ammonia-containing
solvents), volatile solvents (e.g., acetone and isopropanol), and
combinations thereof. For example, when the film-forming
composition of antimicrobial film 10 includes an alkali soluble
acrylic copolymer dispersion commercially available under the trade
designation "NEOCRYL BT-9" from DSM NeoResins, Wilmington, Mass.,
remover composition 14 may include a high pH solvent (e.g., an
ammonia solution or soap-containing aqueous solvent) to dissolve
and/or swell the antimicrobial film 10. Examples of suitable
concentrations of the solvent in remover composition 14 range from
about 50% by weight to 100% by weight, with particularly suitable
total concentrations ranging from about 90% by weight to 100% by
weight.
[0068] Remover composition 14 may also include surfactants and
thickeners, and foaming agents to modify wetting and flow
properties. Examples of suitable surfactants and thickeners include
those discussed above for the film-forming composition of
antimicrobial film 10. Examples of suitable total concentrations of
surfactants and thickeners in remover composition 14 range from
about 1% by weight to about 20% by weight, with particularly
suitable total concentrations ranging from about 5% by weight to
about 10% by weight.
[0069] FIG. 3 is a top perspective view of hand 16 of a user
removing antimicrobial film 10 from surface 12 with wipe article
18. Prior to remover composition 14 being deposited, antimicrobial
film 10 is resistant to being removed from surface 12, as discussed
above. As such, antimicrobial film 10 must be subjected to at least
a first minimum frictional force before being removed. The first
minimum frictional force is greater than a moderate frictional
force applied during a surface wiping with a wipe article. This
prevents antimicrobial film 10 from being undesirably removed until
remover composition 14 is deposited.
[0070] Remover composition 14, however, swells the polymer of the
antimicrobial film 10 and/or breaks down the structural integrity
of the polymer (i.e., dissolves the polymer), thereby allowing
antimicrobial film 10 to be readily removed from surface 12. As a
result, after remover composition 14 is deposited, antimicrobial
film 10 may be removed by an application of a second minimum
frictional force that is less than the first minimum frictional
force. In some embodiments, the second minimum frictional force is
equal to or less than a moderate frictional force applied by a
wiping motion with wipe article 18.
[0071] In some embodiments, as shown in FIG. 3, remover composition
14 may be impregnated within wipe article 18. In this embodiment,
the user may forgo a separate step of depositing remover
composition 14 onto antimicrobial film 10. As the user applies
frictional force to antimicrobial film 10 with wipe article 18,
remover composition 14 is extracted from wipe article 18 and
deposits onto antimicrobial film 10. Remover composition 14 then
dissolves and/or swells the polymer in the film-forming composition
of antimicrobial film 10, thereby allowing antimicrobial film 10 to
be wiped away from surface 12 after several strokes with wipe
article 18. Accordingly, wipe article 18 is a disposable article
that reduces time and effort the user must undertake to remove
antimicrobial film 10 from surface 12.
[0072] After antimicrobial film 10 is removed from surface 12, a
fresh coating of antimicrobial film 10 may be coated on surface 12,
pursuant to the coating techniques discussed above in FIG. 1. This
may provide antimicrobial protection to surface 12 for extended
periods of time. For example, when substantially all of the
antimicrobial agents are released from a first coating of
antimicrobial film 10, a user may deposit remover composition 14 on
antimicrobial film 10, and wipe the first coating of antimicrobial
film 10 away. The user may then coat surface 12 with a second
coating of antimicrobial film 10 to provide a renewed source of
protection against microbial contamination.
EXAMPLES
[0073] The present invention is more particularly described in the
following examples that are intended to be illustrative and not
limiting, since numerous modifications and variations within the
scope of the present invention will be apparent to those skilled in
the art. Examples 1-20 are working examples, and Examples 21-27 are
prophetic examples.
[0074] Unless otherwise noted, all parts, percentages, and ratios
reported in the following examples are on a weight basis, and all
reagents used in the examples were obtained, or are available, from
the chemical suppliers described below, or may be synthesized by
conventional techniques.
[0075] The following compositional abbreviations are used in the
following Examples: [0076] "AgION": A silver-containing inorganic
zeolite food-grade antimicrobial agent, type AJ, which contains
2.5% silver, and which is commercially available under the trade
designation "AgION" Antimicrobial from AgION Technologies, Inc.,
Wakefield, Mass. [0077] "Triclosan": Triclosan antimicrobial agent,
commercially available from Ciba Specialty Chemicals., Tarrytown,
N.Y. [0078] "Lauricidin solution": A fluid solution containing
20.0% glycerol monolaurate fatty acid monoester (commercially
available under the trade designation "LAURICIDIN" from Med-Chem
Laboratories, East Lansing, Mich.), 10.0% 2-hydroxybenzoic
(salicylic) acid (HOC.sub.6H.sub.8CO.sub.2H) with a formula weight
of 138.1 (commercially available from Sigma-Aldrich Chemical
Company, Saint Louis, Mo.), and 10.0% dioctylsulfosuccinate (DOSS)
surfactant (commercially available from Alfa Aesar, Ward Hill,
Mass.) in isopropanol. [0079] "Bardac 205M": A quaternary ammonium
compound commercially available under the trade designation "BARDAC
205M" from Lonza Group Ltd., Valais, Switzerland. [0080] "Bardac
208M": A quaternary ammonium compound commercially available under
the trade designation "BARDAC 208M" from Lonza Lonza Group Ltd.,
Valais, Switzerland. [0081] "Zn Pyrithione": Zinc pyrithione, which
is synthesized from 2-mercaptopyridine N-oxide salt and zinc
acetate, both of which are commercially available from
Sigma-Aldrich Chemical Company, Saint Louis, Mo. [0082] "Silver
oxide": Silver oxide (AgO) having a formula weight of 123.9,
commercially available from Alfa Aesar, Ward Hill, Mass. [0083]
"Vantocil P": A
poly(iminoimidocarbonylimidocarbonyliminohexa-methylene
hydrochloride), pH 5-6, 20% by weight active in water, commercially
available under the trade designation "VANTOCIL P" from Arch
Chemicals, Inc., Norwalk, Conn. [0084] "Vantocil IB": A
poly(iminoimidocarbonylimidocarbonyliminohexa-methylene
hydrochloride), pH 4-5, 20% by weight active in water, commercially
available under the trade designation "VANTOCIL IB" from Arch
Chemicals, Inc., Norwalk, Conn. [0085] "Metasol TK 25": A
thiabendazole-based agent, commercially available under the trade
designation "METASOL TK 25" from Lanxess Corporation, Pittsburgh,
Pa. [0086] "AgION SilverClene 24": A silver-containing inorganic
zeolite food-grade antimicrobial agent, which contains 0.003%
silver, 4.8% citric acid, and which is commercially available under
the trade designation "AGION SILVERCLENE 24" Antimicrobial from
AgION Technologies, Inc., Wakefield, Mass. [0087] "CHG": 20%
chlorhexidine gluconate by weight in water, commercially available
from Xttrium Laboratories, Inc., Chicago, Ill. [0088] "Ammonium
Carbonate": Ammonium carbonate salt, commercially available from
Sigma-Aldrich, Milwaukee, Wis. [0089] "PVOH": A polyvinyl alcohol
polymer with molecular weight of 180,000 Daltons, commercially
available from Sigma-Aldrich Chemical Company, Saint Louis, Mo.
[0090] "PVP-K90": A polyvinylpyrrolidone polymer with molecular
weight of 90,000 Daltons, which is commercially available under the
trade designation "PVP-K90" from Peakchem, ZheJiang, China. [0091]
"R-960": A water based urethane dispersion containing 33% solids,
commercially available under the trade designation "NEOREZ R-960"
from DSM-NeoResins, Wilmington, Mass. [0092] "RU21-075": A
water-based polyurethane dispersion containing 40% solids,
commercially available under the trade designation "RU21-075" from
Stahl USA, Peabody, Mass. [0093] "Sancure 815": A water-based
polyurethane dispersion, commercially available under the trade
designation "SANCURE 815" from Noveon, Inc., Cleveland, Ohio.
[0094] "PVP": A polyvinylpyrrolidone (2% solids in water),
commercially available under the trade designation "K-12" from
International Specialty Products, Wayne, N.J. [0095] "Incorez
835/494": A soft aliphatic polyurethane dispersion (5% in water),
commercially available under the trade designation "INCOREZ
835/494" from Industrial Copolymers, Ltd., Lancashire, England.
[0096] "Incorez 835/140": A hard aliphatic polyurethane dispersion
(5% in water), commercially available under the trade designation
"INCOREZ 835/140" from Industrial Copolymers, Ltd., Lancashire,
England. [0097] "Cydrothane HP 5035": A hard aromatic polyurethane
dispersion (5% in water), commercially available under the trade
designation "CYDROTHANE HP 5035" from Cytek Industries, Inc., West
Paterson, N.J. [0098] "Cydrothane HP 1035": A soft aromatic
polyurethane dispersion (5% in water), commercially available under
the trade designation "CYDROTHANE HP 1035" from Cytek Industries,
Inc., West Paterson, N.J. [0099] "GlossTek": A reactive aliphatic
polyurethane, commercially available under the trade designation
"GLOSSTEK" from Ecolab, St. Paul, Minn. [0100] "Stance": A zinc
cross-linked acrylic plus polyethylene wax dispersion, commercially
available under the trade designation "STANCE" from 3M Corporation,
St. Paul, Minn. [0101] "Cornerstone": An acrylic floor
sealer/finish (25% in water), commercially available under the
trade designation "CORNERSTONE" from 3M Corporation, St. Paul,
Minn. [0102] "NeoCryl XK-98": A self cross-linking acrylic
dispersion commercially available under the trade designation
"NEOCRYL XK-98" from DSM NeoResins, Wilmington, Mass. [0103] "B66
acrylic resin": An acrylic resin commercially available under the
trade designation "SPEC-CRETE SUPERSEAL B66" from Farfan &
Mendes Ltd., Georgetown, Guyana. [0104] "XK-90": A 40% acrylic
cross-linkable polymer dispersion in water, commercially available
under the trade designation "NEOPAC XK-90" from DSM-NeoResins,
Wilmington, Mass. [0105] "XR-2500": A polyfunctional aziridine
cross-linker commercially available under the trade designation
"XR-2500" from Stahl USA, Peabody, Mass. [0106] "XL-A": A
combination of 76 parts ethanol, 22.8 parts of an aziridine
cross-linker commercially available under the trade designation
"CX-100" from DSM NeoResins, Wilmington, Mass., and 1.2 parts of a
surfactant commercially available under the trade designation
"SURFYNOL 104PA" from Air Products and Chemicals, Inc. Allentown,
Pa. The combined mixture was blended for 20 minutes under high
shear. [0107] "Exxate 800": An oxo-alkyl acetic ester solvent
commercially available under the trade designation "EXXATE 800"
from Exxon Mobil Corporation, Houston, Tex. [0108] "PET film": A
polyethylene terephthalate film with acrylate-primed layer,
commercially available from Mitsubishi, Japan. [0109] "BOPP Film":
A biaxially-oriented, corona-treated, polypropylene film available
from 3M Corporation, St. Paul, Minn.
Examples 1 and 2
[0110] Antimicrobial films of Examples 1 and 2 were each prepared
pursuant to the following procedure. A PVOH solution was prepared
by combining 5 parts of PVOH with 95 parts water, and shaking the
mixture in a warm bath for 24 hours to fully dissolve the PVOH. 30
parts of the PVOH solution were then mixed with 0.2 parts of an
antimicrobial agent (AgION for Example 1, and Triclosan for Example
2). The resulting film-forming composition was then coated onto a
corona-treated BOPP film using a Meyer rod #36, and dried at
55.degree. C. for 5 minutes to form the antimicrobial film.
[0111] The antimicrobial films of Examples 1 and 2 were each tested
for "microbial load reduction" pursuant to ASTM E2180-01, which
involved inoculation of a molten (45.degree. C.) agar slurry with a
standardized culture of bacterial cells. A thin layer of the
inoculated agar slurry (0.5 milliliter) was then pipetted onto the
test material and the untreated control material. Samples were
tested in duplicate using Staphylococcus aureus (ATCC 6538) and
Pseudomonas aeruginosa (ATCC 9027). After 24 hours, surviving
microorganisms were recovered via elution of the agar slurry
inoculum from the test substrate into D/E Neutralizing broth and
extracted by sonication and vortexing. Serial dilutions were then
made, and pour plates were made of each dilution. Agar plates were
incubated for 48 hours at 28.degree. C..+-.1.degree. C. Bacterial
colonies from each dilution series were then counted and recorded.
Calculation of percent reduction of bacteria from treated versus
untreated samples was then made. A percent reduction greater than
99.95% was reported as 100%.
[0112] Table 1 provides the microbial load reduction results for
the antimicrobial films of Examples 1 and 2.
TABLE-US-00001 TABLE 1 % Reduction Antimicrobial % Reduction S.
aureus Ps. aeruginosa Example Agent (Gram Positive) (Gram Negative)
Example 1 AgION 100 100 Example 2 Triclosan 100 0
[0113] The results shown in Table 1 illustrate the good
antimicrobial activity provided by the antimicrobial films of
Examples 1 and 2. The antimicrobial film of Example 2 exhibited
poor gram negative results, which is typical for Triclosan
antimicrobial agents.
[0114] The antimicrobial films of Examples 1 and 2 were also tested
for ease of removal with a remover composition. Synthetic wipes
(commercially available under the trade designation "TX1009
ALPHAWIPE" from ITW Texwipe, Upper Saddle River, N.J.) were used
for the evaluation. For each antimicrobial film, a 4''.times.4''
piece of a synthetic wipe was saturated with water at room
temperature and rubbed over the antimicrobial film. For each
antimicrobial film of Examples 1 and 2, the film was removed from
the BOPP substrate after two strokes with the wet synthetic wipe.
Based on visual observations, the first stroke appeared to wet and
soften the antimicrobial film due to the antimicrobial film
swelling, and the second stroke removed it in a solid form. This
demonstrates that the antimicrobial film was swelled by water but
did not dissolve in water and was durable enough to substantially
withstand dissolution in water due to the relatively high molecular
weight of PVOH that was used.
Examples 3-8
[0115] Antimicrobial films of Examples 3-8 were each prepared
pursuant to the following procedure. A solution was prepared by
dissolving PVP-K90 and an antimicrobial agent in a 50:50 solution
of isopropanol and methyl ethyl ketone. The solution was then
coated on a non-treated polyethylene terephthalate substrate using
a Meyer rod #9. The coated film was dried at room temperature for
20 minutes and then dried at 80.degree. C. for 10 minutes.
[0116] The antimicrobial films of Examples 3-8 were each tested for
"microbial load reduction" pursuant to the procedure discussed
above for Examples 1 and 2. A control coating of PVP-K90 without an
antimicrobial agent was used as a control.
TABLE-US-00002 TABLE 2 % Percent by Reduction % Reduction Weight of
S. aureus Ps. aeruginosa Antimicrobial Antimicrobial (Gram (Gram
Example Agent Agent Positive) Negative) Example 3 Lauricidin 6 100
0 solution Example 4 Bardac 208M 6 100 100 Example 5 Bardac 205M 6
100 100 Example 6 Triclosan 6 100 0 Example 7 AgION 5 100 100
Example 8 Zn Pyrithione 6 83.8 97.7
[0117] The results shown in Table 2 illustrate the good
antimicrobial activity provided by the antimicrobial films of
Examples 3-8. Accordingly, a variety of antimicrobial agents may be
used with the present invention.
Examples 9-15 and Comparative Examples A and B
[0118] Antimicrobial films of Examples 9-15 and Comparative
Examples A and B were each prepared pursuant to the following
procedure. A solution was prepared by combining an antimicrobial
agent, a cross-linking agent, a polymer dispersion, and 5 parts of
water. For the films of Examples 9-11 and Comparative Example A,
the polymer dispersion was 20 parts of R-960, and for the films of
Examples 12-15 and Comparative Example B, the polymer dispersion
was 10 parts of RU21-075. Table 3 provides the antimicrobial agents
and cross-linking agents combined in the solutions for the films of
Examples 9-15 and Comparative Examples A and B.
TABLE-US-00003 TABLE 3 Parts of Antimicrobial Antimicrobial Cross-
Parts of Example Agent Agent Linker Cross-Linker Comparative None
0.0 None 0.0 Example A Example 9 AgION 0.5 XR-2500 0.2 Example 10
AgION 0.5 XL-A 4.0 Example 11 Triclosan 5.0 XL-A 4.0 Comparative
None 0.0 None 0.0 Example B Example 12 AgION 0.5 XL-A 2.0 Example
13 AgION 0.5 XR-2500 0.1 Example 14 Triclosan 1.0 XL-A 2.0 Example
15 Triclosan 1.0 XR-2500 0.1
[0119] The resulting film-forming compositions were then coated
onto a corona-treated BOPP film using a Meyer rod #6, and dried at
55.degree. C. for 5 minutes to form the antimicrobial film. The
antimicrobial films of Examples 9-15 and Comparative Examples A and
B were then each tested for "microbial load reduction" pursuant to
ASTM E2180-01, as discussed above for Examples 1 and 2. Table 4
provides the microbial load reduction results for the antimicrobial
films of Examples 9-15 and Comparative Examples A and B.
TABLE-US-00004 TABLE 4 % % Reduction Reduction Ps. Parts of S.
aureus aeruginosa Antimicrobial Antimicrobial (Gram (Gram Example
Agent Agent Positive) Negative) Comparative None 0.0 0.0 0.0
Example A Example 9 AgION 0.5 99.7 100.0 Example 10 AgION 0.5 99.4
100.0 Example 11 Triclosan 5.0 69.7 0.0 Comparative None 0.0 0.0
0.0 Example B Example 12 AgION 0.5 98.9 100.0 Example 13 AgION 0.5
96.0 100.0 Example 14 Triclosan 1.0 89.0 0.0 Example 15 Triclosan
1.0 41.0 19.0
[0120] The results shown in Table 4 further illustrate the good
antimicrobial activity provided by the antimicrobial films of the
present invention. As discussed above, the antimicrobial films
containing Triclosan (i.e., Examples 11, 14, and 15) exhibited poor
gram negative results, which is typical for Triclosan antimicrobial
agents. In addition, the antimicrobial films containing Triclosan
exhibited relatively poor gram positive results. This could be due
to the triclosan interacting more strongly with the polymer of the
antimicrobial film.
[0121] The antimicrobial films of Examples 9, 10, 12, and 13, and
Comparative Examples A and B were also tested for ease of removal
from the BOPP film with a remover composition pursuant to the
following procedure. Each sample was sprayed with WINDEX-brand
glass cleaner solution, which is commercially available from SC
Johnson & Son, Inc., Racine, Wis. After a 30 second waiting
period, the sample was then wiped three strokes under moderate
force with a paper towel, and the amounts of the film removed were
estimated by visual observation. Table 5 provides the percent
removal for the antimicrobial films of Examples 9, 10, 12, and 13,
and Comparative Examples A and B.
TABLE-US-00005 TABLE 5 Polymer Matrix Example Material Cross-Linker
% Removal Comparative Example A R-960 None 100% Example 9 R-960
XR-2500 10 Example 10 R-960 XL-A 10 Comparative Example B RU21-075
None 100 Example 12 RU21-075 XL-A 100 Example 13 RU21-075 XR-2500
90
[0122] The results shown in Table 5 illustrate the difference in
removal based on the type of cross-linked polymer dispersion used.
This is shown by the films of Examples 9 and 10, which used the
R-960. Accordingly, a stronger solvent is more desirable for use
with the films of Examples 9 and 10. In comparison, however, the
films of Examples 12 and 13 exhibited low resistances to the alkali
environment, and were readily removed. As such, ammonia-based
solvents are suitable as remover compositions for antimicrobial
films containing cross-linked RU21-075 polymer matrix
materials.
Example 16
[0123] An antimicrobial film of Example 16, which is an example of
a self cross-linking polymer, was prepared pursuant to the
following procedure. A mixture was formed by combining 95 parts of
NeoCryl XK-98 with 5 parts AgION. The mixture was then coated onto
BOPP film using a Meyer rod #14 and dried in an oven at 60.degree.
C. for 5 minutes. While drying, the NeoCryl XK-98 polymer self
cross-linked via a condensation reaction. The resulting
antimicrobial film of Example 16 was then tested for "microbial
load reduction" pursuant to ASTM E2180-01, as discussed above for
Examples 1 and 2. The film of Example 16 exhibited a 100% microbial
load reduction for both S. aureus (gram positive) and Ps.
aeruginosa (gram negative).
[0124] The antimicrobial film of Example 16 was also tested for
ease of removal from the BOPP film with remover compositions. A
first sample of the film was sprayed with water and a second sample
of the film was sprayed with WINDEX-brand glass cleaner solution,
which is commercially available from SC Johnson & Son, Inc.,
Racine, Wis. After a 30 second waiting period, the samples were
then wiped three strokes under moderate force with a paper towel,
and the amount of the film removed was observed. For the
water-sprayed sample, the film was unaffected by the water and was
not removed. This is due to the cross-linked structure of the film.
In contrast, for the WINDEX-sprayed sample, the film was readily
removed. As a result, the antimicrobial film of Example 16 is
suitable for use on a variety of surfaces that are treated with
water. The cross-linked polymer matrix prevents the antimicrobial
film of Example 16 from being removed during normal washing
operations (e.g., washing a surface with a wetted towel or sponge),
but is readily removed when a WINDEX-based remover composition is
applied.
Example 17
[0125] An antimicrobial film of Example 17, which is an example of
AgION silver in a solvent-borne formulation, was prepared pursuant
to the following procedure. A mixture was prepared by combining 2
parts by weight of B66 acrylic resin, 0.2 parts AgION, and 8 parts
Exxate 800 solvent. The mixture was stirred for one hour to
dissolve the B66 acrylic resin and disperse the AgION. The
resulting mixture was then coated on a BOPP film using a Meyer rod
#26. The film was then dried in an oven at 55.degree. C. for 5
minutes. The coating appearance was transparent, but non-uniform
with a blotchy surface.
[0126] The resulting antimicrobial film of Example 17 was then
tested for "microbial load reduction" pursuant to ASTM E2180-01, as
discussed above for Examples 1 and 2. The film of Example 17
exhibited a 68.4% microbial load reduction for S. aureus (gram
positive) and a 100.0% microbial load reduction for Ps. aeruginosa
(gram negative). Additionally, a wipe was saturated with MEK
(methyl ethyl ketone) and used to rub the film. After three
strokes, about 80% of the film was removed, as estimated by visual
observation.
Example 18
[0127] An antimicrobial film of Example 18, which is an example of
AgION silver in a water-based formulation, was prepared pursuant to
the following procedure. A mixture was prepared by combining 8.6
parts XK-90 (acrylic cross-linkable polymer dispersion in water),
0.6 parts XL-A cross-linker, and 0.4 parts AgION. The mixture was
stirred for a few minutes until homogeneous in appearance. The
composition was coated onto a BOPP film using a Meyer rod #14. The
film was then dried at 55.degree. C. for 5 minutes. The resulting
film appearance was hazy, but uniform.
[0128] The resulting antimicrobial film of Example 18 was then
tested for "microbial load reduction" pursuant to ASTM E2180-01, as
discussed above for Examples 1 and 2. The film of Example 17
exhibited a 100.0% microbial load reduction for both S. aureus
(gram positive) and Ps. aeruginosa (gram negative).
[0129] To assess the ease of film removal, a spray of water,
WINDEX-brand glass cleaner solution, soapy warm water, and MEK were
applied to the film. After allowing each solvent to interact with
the film for 10 minutes, the film plus solvent was wiped using a
KemWipe and applying moderate force. The film was unaffected under
the areas saturated with water, WINDEX-brand glass cleaner
solution, and soapy warm water. Most of the film was removed under
the area saturated with MEK. This shows that the film-forming
composition in this example exhibits high durability and requires
an aggressive solvent for the remover composition.
Example 19
[0130] An antimicrobial film of Example 19 was prepared pursuant to
the following procedure. A silver oxide solution was initially
prepared by combining 5 parts ammonium carbonate salt with 95 parts
water, and mixing until the salt was dissolved. To this solution, 1
part silver oxide was added. The mixture was stirred at 60.degree.
C. for one hour until the silver oxide was dissolved. A mixture was
then prepared by combining 20 parts by weight of XK-90 binder
material, 1 part silver oxide solution, 2 parts XL-A cross-linker,
and 12 parts water. The mixture was shaken by hand to form a
uniform dispersion, and then coated on a PET film using a Meyer rod
#12. The film was then dried at in an oven at 55.degree. C. for 5
minutes and cured. The resulting film appearance was transparent
and uniform, with a slight brown tint due to the presence of the
silver oxide. This color tint can be beneficial for allowing a user
to visually determine the presence and uniformity of the
coating.
[0131] The resulting antimicrobial film of Example 10 was then
tested for "microbial load reduction" pursuant to ASTM E2180-01, as
discussed above for Examples 1 and 2. The film of Example 28
exhibited a 51.2% microbial load reduction for S. aureus (gram
positive) and a 100.0% microbial load reduction for Ps. aeruginosa
(gram negative).
Example 20
[0132] An antimicrobial film of Example 20, which included a
fast-acting antimicrobial agent, was prepared pursuant to the
following procedure. A solvent of 60 parts ethyl alcohol and 40
parts water was initially prepared. A mixture was then prepared by
adding 6 parts PVOH polymer to the solvent. The mixture was shaken
in warm bath until the PVOH was dissolved, which was about 24
hours. After the shaking process, 1 part AgION was added to the
mixture. The resulting mixture exhibited instant bacterial kill
capabilities due to the high content of ethyl alcohol, while the
coated composition also provided for longer-term antimicrobial
activity after the alcohol evaporates as shown above in Example 1.
This illustrates the versatility of the present invention for
reducing pathogen contamination.
Examples 21-27
[0133] Examples 21-27 illustrate prophetic polymer-antimicrobial
agent combinations that can be used to form water-insoluble,
biocidal antimicrobial films according to the present invention.
Table 6 provides the listing of the polymer-antimicrobial agent
combinations for Examples 21-27. For each of Examples 21-27, a
plurality of antimicrobial agents can be used alone or in
combination and are listed in a comma-delimited manner to signify
this. The following letter codes are used to abbreviate the
antimicrobial agents in Table 6: A=Vantocil IB, B=Triclosan,
C=AgION SilverClene 24, and D=CHG.
TABLE-US-00006 TABLE 6 Antimicrobial Example Polymer Agent Example
21 Cornerstone (25% in water) A, B, C, D Example 22 Incorez 835/494
(5% in water) C, D Example 23 Incorez 835/140 (5% in water) C, D
Example 24 Cydrothane HP 5035 (5% in water) C, D Example 25
Cydrothane HP 1035 (5% in water) C, D Example 26 GlossTek C, D
Example 27 Stance A, B, C, D
[0134] The embodiments described above and illustrated in the
figures are presented by way of example only and are not intended
as a limitation upon the concepts and principles of the present
invention. As such, it will be appreciated by one having ordinary
skill in the art that various changes in form and detail are
possible without departing from the spirit and scope of the present
invention. Various features and aspects of the invention are set
forth in the following claims.
* * * * *