U.S. patent application number 12/764843 was filed with the patent office on 2011-10-27 for process for preparation of calcium thiosulfate liquid solution from lime, sulfur, and sulfur dioxide.
This patent application is currently assigned to TESSENDERLO KERLEY, INC.. Invention is credited to Yelena Feinstein, Michael Massoud Hojjatie, Constance Lynn Frank Lockhart.
Application Number | 20110262343 12/764843 |
Document ID | / |
Family ID | 44729927 |
Filed Date | 2011-10-27 |
United States Patent
Application |
20110262343 |
Kind Code |
A1 |
Hojjatie; Michael Massoud ;
et al. |
October 27, 2011 |
PROCESS FOR PREPARATION OF CALCIUM THIOSULFATE LIQUID SOLUTION FROM
LIME, SULFUR, AND SULFUR DIOXIDE
Abstract
An efficient batch or semi-continuous method of production of
relative high concentration, low byproduct-containing, calcium
thiosulfate (CaS.sub.2O.sub.3) from lime, sulfur or calcium
polysulfide, and sulfur dioxide under elevated reaction temperature
conditions is described. The product is an emulsion of liquid
calcium thiosulfate and solid byproducts. Under the conditions of
the art, including the mole ratios of lime to sulfur, the
temperature of the reaction process and the sulfur dioxide reaction
conditions, including rate and duration, the byproducts are reduced
to about 2% by weight.
Inventors: |
Hojjatie; Michael Massoud;
(Tucson, AZ) ; Feinstein; Yelena; (Tucson, AZ)
; Lockhart; Constance Lynn Frank; (Tucson, AZ) |
Assignee: |
TESSENDERLO KERLEY, INC.
Phoenix
AZ
|
Family ID: |
44729927 |
Appl. No.: |
12/764843 |
Filed: |
April 21, 2010 |
Current U.S.
Class: |
423/514 |
Current CPC
Class: |
C01B 17/64 20130101;
C01P 2006/10 20130101; C01P 2006/60 20130101 |
Class at
Publication: |
423/514 |
International
Class: |
C01B 17/64 20060101
C01B017/64 |
Claims
1. A process for preparing calcium thiosulfate comprising the
following steps: (a) providing a calcium hydroxide slurry; (b)
adding sulfur to the slurry; (c) reacting the slurry to form a
calcium polysulfide reaction mixture by consuming substantially all
the calcium hydroxide; (d) adding sulfur dioxide to the reaction
mixture that is substantially free of calcium hydroxide, and
reacting at about atmospheric pressure under conditions sufficient
to form a calcium thiosulfate solution; and (e) recovering the
calcium thiosulfate.
2. The process of claim 1 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide mole ratio of from about
1:1 to about 6:1.
3. The process of claim 2 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide mole ratio of from about
3.5:1 to about 6:1.
4. The process of claim 2 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide mole ratio of from about
3.4:1 to about 3.8:1.
5. The process of claim 3 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide mole ratio of about
3.6:1.
6. The process of claim 1 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide to water mole ratio of at
least about 2:6:30.
7. The process of claim 6 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide to water mole ratio of
about 3.6 to 4.9:1:25.5.
8. The process of claim 7 wherein step (b) further comprises adding
sulfur at a sulfur to calcium hydroxide to water mole ratio of
about 3.6:1:25.5.
9. The process of claim 1 wherein step (c) further comprises
reacting the slurry at a temperature of least about 70.degree. C.
to form a calcium polysulfide reaction mixture.
10. The process of claim 9 wherein step (c) further comprises
reacting the slurry at a temperature of about 85.degree. C. to
about 99.degree. C. to form a calcium polysulfide reaction
mixture.
11. The process of claim 10 wherein step (c) further comprises
reacting the slurry at a temperature of about 90.degree. C. to
about 92.degree. C. to form a calcium polysulfide reaction
mixture.
12. The process of claim 1 wherein step (c) further comprises
cooling the polysulfide reaction mixture to a temperature of about
55.degree. C. to about 75.degree. C.
13. The process of claim 1 wherein step (a) further comprises a
step of forming said calcium hydroxide slurry by combining calcium
oxide and water.
14. The process of claim 1, wherein the calcium oxide is about 96%
to about 99% pure.
15. The process of claim 1 wherein step (d) further comprises
reacting at a temperature of about 82.degree. C. to about
95.degree. C.
16. The process of claim 15 wherein step (d) further comprises
reacting at a temperature of about 85.degree. C. to about
88.degree. C.
17. The process of claim 1 wherein step (d) further comprises
dropping pH to about 3 to about 6.
18. The process of claim 17 wherein step (d) further comprises
dropping pH to about 3.5 to about 4.
19. The process of claim 1 wherein step (d) further comprises
stopping addition of further sulfur dioxide and agitating until pH
is in the range of about 7 to about 7.5.
20. The process of claim 1 wherein step (e) further comprises using
a flocculent to recover the calcium thiosulfate.
21. A process for preparing calcium thiosulfate comprising the
following steps: (a) providing a calcium hydroxide slurry; (b)
adding sulfur to the slurry at a sulfur to calcium hydroxide to
water mole ratio of at least about 2:6:30; (c) reacting the slurry
at a temperature of at least about 70.degree. C. to consume
substantially all the calcium hydroxide and to form a calcium
polysulfide reaction mixture; (d) cooling the calcium polysulfide
reaction mixture to a temperature of about 55.degree. C. to about
75.degree. C.; (e) adding sulfur dioxide to the reaction mixture
and reacting at about atmospheric pressure, a temperature of about
82.degree. C. to about 95.degree. C., and a pH of about 3 to about
6, to form a calcium thiosulfate solution; and (f) recovering the
calcium thiosulfate.
22. The process of claim 21 wherein the process is carried out in
gas/liquid contacting process equipment selected from group
consisting of bubble columns, packed columns, tray columns, spray
columns, mechanically agitated tanks, jet loops, venturi
ejector/eductor/pipes/tubes, and static mixers.
23. A process for preparing calcium thiosulfate comprising the
following steps: (a) providing a lime-sulfur slurry that is
substantially free of calcium hydroxide; (b) adding sulfur dioxide
to the slurry and reacting the slurry at about atmospheric pressure
under conditions sufficient to form a calcium thiosulfate solution;
and (c) recovering the calcium thiosulfate.
24. The process of claim 23, wherein step (b) further comprises
reacting at a temperature of about 82.degree. C. to about
95.degree. C.
25. The process of claim 24 wherein step (b) further comprises
reacting at a temperature of about 85.degree. C. to about
88.degree. C.
26. The process of claim 23 wherein step (b) further comprises
dropping pH to about 3 to about 6.
27. The process of claim 26 wherein step (b) further comprises
dropping pH to about 3.5 to about 4.
28. The process of claim 23 wherein step (b) further comprises
stopping addition of further sulfur dioxide and agitating until pH
rises to about 7 to about 7.5.
29. The process of claim 23 wherein step (c) further comprises
using a flocculent to recover the calcium thiosulfate.
30. A process for preparing calcium thiosulfate comprising the
following steps: (a) providing a lime-sulfur slurry that is
substantially free of calcium hydroxide; (b) adding sulfur dioxide
to the slurry and reacting at about atmospheric pressure, at a
temperature of about 82.degree. C. to about 95.degree. C., and a pH
of about 3 to about 6, to form a calcium thiosulfate solution; and
(c) recovering the calcium thiosulfate.
31. The process of claim 30 wherein the process is carried out in
gas/liquid contacting process equipment selected from group
consisting of bubble columns, packed columns, tray columns, spray
columns, mechanically agitated tanks, jet loops, venturi
ejector/eductor/pipes/tubes, and static mixers.
32. A process for preparing calcium thiosulfate comprising the
following steps: (a) providing a calcium polysulfide slurry; (b)
adding sulfur dioxide to the slurry; (c) reacting the slurry at
about atmospheric pressure under conditions sufficient to form a
calcium thiosulfate solution; and (d) recovering the calcium
thiosulfate.
33. The process of claim 32, wherein step (b) further comprises
reacting at a temperature of about 82.degree. C. to about
95.degree. C.
34. The process of claim 33 wherein step (b) further comprises
reacting at a temperature of about 85.degree. C. to about
88.degree. C.
35. The process of claim 32 wherein step (b) further comprises
dropping pH to about 3 to about 6.
36. The process of claim 35 wherein step (b) further comprises
dropping pH to about 3.5 to about 4.
37. The process of claim 32 wherein step (b) further comprises
stopping addition of further sulfur dioxide and agitating until pH
rises to about 7 to about 7.5.
38. The process of claim 32 wherein step (c) further comprises
using a flocculent to recover the calcium thiosulfate.
39. A process for preparing calcium thiosulfate comprising the
following steps: (a) providing a calcium polysulfide slurry that is
substantially free of calcium hydroxide; (b) adding sulfur dioxide
to the slurry and reacting at atmospheric pressure at a temperature
of about 82.degree. C. to about 95.degree. C. and a pH of about 3
to about 6, to form a calcium thiosulfate solution; and (c)
recovering the calcium thiosulfate.
40. The process of claim 39 wherein the process is carried out in
gas/liquid contacting process equipment selected from group
consisting of bubble columns, packed columns, tray columns, spray
columns, mechanically agitated tanks, jet loops, venturi
ejector/eductor/pipes/tubes, and static mixers.
41. The process of claim 1 wherein the sulfur dioxide is obtained
from waste gases.
42. The process of claim 23 wherein the sulfur dioxide is obtained
from waste gases.
43. The process of claim 32 wherein the sulfur dioxide is obtained
from waste gases.
44. The process of claim 23, wherein step (b) comprises reacting
the slurry in a first vessel, then filtering the reacted slurry to
form a filtrate, then transferring the filtrate to a second vessel
and adding additional sulfur dioxide to the filtrate in the second
vessel.
45. The process of claim 1, wherein step (d) further comprises
stopping addition of sulfur dioxide when the reaction mixture's pH
is about 4.
46. The process of claim 45, wherein step (d) further comprises
removing excess SO.sub.2.
47. The process of claim 46, wherein step (d) further comprises
adding calcium hydroxide to adjust the solution's pH to about 7 to
about 7.5.
Description
FIELD OF INVENTION
[0001] The present invention is directed to a process for the
preparation of calcium thiosulfate, a plant nutrient solution.
Another aspect of the present invention is the removal of air
pollutant sulfur dioxide from industrial plants producing it, to
convert the sulfur dioxide to calcium thio sulfate.
DESCRIPTION OF RELATED ART
[0002] The thiosulfate ion, S.sub.2O.sub.3.sup.2-, is a structural
analogue of the SO.sub.4.sup.2- ion in which one oxygen atom is
replaced by one S atom. However, the two sulfur atoms in
S.sub.2O.sub.3.sup.-2 are not equivalent. One of the S atoms is a
sulfide-like sulfur atom that gives the thiosulfate its reducing
properties and complexing abilities.
##STR00001##
[0003] Thiosulfates are used in leather tanning, paper and textile
manufacturing, flue-gas desulfurization, cement additives,
dechlorination, ozone and hydrogen peroxide quenching, coating
stabilizers and so on.
[0004] Due to these complex-forming abilities with metals,
thiosulfate compounds have been used in commercial applications
such as photography, waste treatment and water treatment
applications.
[0005] Thiosulfates readily oxidize to tetrathionates and
sulfates:
S.sub.2O.sub.3.sup.2-+O.sub.2S.sub.4O.sub.6.sup.2-2SO.sub.4.sup.2-
[0006] Due to this transformation, thiosulfates are used as
fertilizers in combinations with cations such as ammonium,
potassium, magnesium and calcium. The ammonium, alkali metal and
alkaline earth thiosulfates are soluble in water. Water
solubilities of thiosulfates decrease from ammonium to alkali
metals to alkaline earth thiosulfates, i.e. ammonium thiosulfate
has the highest relative water solubility and alkaline earth
thiosulfates have relatively the lowest.
[0007] Calcium is an essential plant nutrient. Calcium availability
is essential in the biochemistry of plants and, as recently
discovered, improves the nitrogen fertilizer efficiency of
surface-applied urea. This is not to be confused with the role of
important soil amendments such as lime or gypsum with the need of
soluble calcium by high-value crops. Both are extremely important
in soil fertility and plant nutrition and complement each
other.
[0008] Calcium has been applied as a foliar agent in apple orchards
as a preventive to a physiological problem known as "bitter pit"
which is caused by calcium deficiency. Calcium is also important to
potato, tomato, lettuce, carrot, alfalfa and other fruit and
vegetable production. Tomato plants with calcium deficiency show
severe infection with Fusarium oxysporum, the fungal pathogen that
causes wilt and crown rot in tomatoes.
[0009] Although soluble calcium could be attained from calcium
nitrate, calcium chloride and calcium ammonium nitrate, due to the
NO.sub.3.sup.-, or Cl.sup.- anion presence, a more
environmentally-friendly counter ion such as thiosulfate
(S.sub.2O.sub.3.sup.-2) is desirable in the application of calcium
fertilizer products. Calcium thiosulfate is referred to herein as
"CaTs". CaTs is a registered trademark of Tessenderlo Kerley,
Inc.
[0010] Although calcium thiosulfate has been known for many years
and has many references in the literature, there are not many known
commercial methods that employ inexpensive raw materials to produce
high purity calcium thiosulfate with a low amount of byproducts and
with solid residue of insoluble calcium salts which permit easy
separation from the calcium thiosulfate product.
[0011] "Lime-sulfur" is a commonly used term for a calcium
thiosulfate and calcium polysulfide mixture resulting from reaction
of lime and sulfur. Preparation of "lime-sulfur" via boiling of
sulfur sludge from sulfuric acid plant and lime is described by P.
Sivaprasad (India Pat. No. 163510, May 1987).
[0012] U.S. Pat. No. 4,976,937 (Lee) describes a method for sulfur
dioxide removal from flue gases with sulfite oxidation inhibition.
The presence of a small amount of thiosulfate, 0.008-0.3 wt %, in
the wet scrubber inhibits the oxidation of sulfur dioxide to
sulfates and therefore provides a scrubbing system that is
non-scaling for gypsum, i.e., that does not result in the buildup
of gypsum scale. The '937 patent describes that a calcium
thiosulfate and calcium polysulfide mixture results from the
reaction of lime and emulsified sulfur in the lime-slaking tank. It
is mixed with sulfites and bisulfites that originally formed in the
wet scrubber in the recycling tank. Calcium thiosulfate forms from
the reaction of polysulfide, sulfites, and bisulfites at 82.degree.
C.-88.degree. C. (180.degree. F.-190.degree. F.) during 5-25 minute
intervals. However, the concentration of calcium thiosulfate is
only 0.3 wt %.
[0013] U.S. Pat. No. 3,644,087 (Urban) discloses a process for the
removal of sulfur dioxide (SO.sub.2) from gas streams containing
SO.sub.2 and oxygen (O.sub.2) by converting SO.sub.2 to the
corresponding thiosulfate, whilst preventing the buildup of
undesirable byproducts, e.g. sulfates, which otherwise occurs due
to the reaction of oxygen from the input gas stream with the
water-soluble sulfite that is formed when the SO.sub.2 is absorbed
in the scrubbing solution. Urban's process involves adding a
reducing agent such as hydrogen sulfide, finely divided sulfur or
an alkaline earth polysulfide into the gas scrubbing zone, wherein
the scrubbing solution can be a water-soluble alkaline earth
hydroxide. Calcium hydroxide, which is only slightly water-soluble,
is not listed as an example for the scrubbing solution. This patent
does not relate to the production of calcium thio sulfate.
[0014] EPO 043869A1 (Lee) discloses a process for removing SO.sub.2
from flue gases using an aqueous slurry of alkaline earth metal
compounds, wherein thiosulfates are produced and recycled for use
in the process to inhibit the oxidation of sulfites (which forms
undesirable byproducts that cause buildup). Lee discusses that lime
and emulsified sulfur are reacted to produce calcium thiosulfate
and calcium polysulfide. One of Lee's preferred slurries of the
alkaline earth metal compounds is formed from a mixture of calcium
hydroxide and magnesium hydroxide. Lee is not concerned with
producing calcium thiosulfate for recovery as a product.
[0015] U.S. Pat. No. 4,105,754 (Swaine, Jr.) describes the
production of calcium thiosulfate by a metathesis reaction of
ammonium thiosulfate and calcium hydroxide or calcium oxide. This
approach requires constant removal of ammonia by air stripping at
below the boiling point of the mixture and capturing the gas.
Further, not all the ammonia can be removed by this process, and as
a result, the resulting calcium thiosulfate tends to have a
lingering ammonia odor and/or contamination with ammonia or
ammonium thiosulfate.
[0016] Japan Patent No. 6,039 issued in 1973 describes preparation
of calcium and magnesium thiosulfate by treating sulfur and the
corresponding sulfite in an alkaline solution. High yields only are
obtained only with magnesium thiosulfate. This patent also
described the formation of calcium thiosulfate from salt exchange
process between magnesium thiosulfate and calcium hydroxide.
[0017] U.S. Pat. No. 4,156,656 (Dannenberg) describes the reaction
of oxides or hydroxides of alkali and alkaline-earth metals with
sulfur in aqueous media at elevated temperature (200.degree.
C.-250.degree. C.) and pressure (210-560 psig) to produce a
hydrosulfide solution.
[0018] Japan Patent No. 48,006,039 discloses a process for the
manufacturing of calcium and magnesium thiosulfate by reacting
calcium and/or magnesium sulfite with sulfur in alkaline solution.
High yield is only obtained in the preparation of magnesium
thiosulfate, and the preparation of calcium thiosulfate requires a
difficult filtration of a slurry containing magnesium
hydroxide.
[0019] Spain Patent No. 245,171 discloses the use of the
salt-exchange process with sodium thiosulfate and calcium chloride.
The byproduct of this approach is a large amount of sodium chloride
that also contaminates the resulting calcium thiosulfate.
[0020] Russia Patent No. 1,773,866 discloses an ion-exchange
technology for preparation of calcium thiosulfate involving
contacting calcium chloride solution with a strong acidic
cation-exchange resin in H.sup.+ form, and unloading the adsorbed
calcium with sodium thiosulfate solution. The calcium thiosulfate
product formed in this way is contaminated with sodium chloride,
calcium chloride and sodium thiosulfate.
[0021] U.S. Pat. No. 7,572,317 (Choi) describes a method for
leaching gold and other precious metals using elemental sulfur to
convert the precious metals to their sulfidic metal bearing
material, and oxidizing this at high pressure and temperature to
form thiosulfate salts of the metals. Calcium thiosulfate of the
precious metals was formed by addition of lime. The thiosulfate of
precious metal is then converted to precious metal cyanide and the
metal is leached.
[0022] U.S. Pat. No. 6,984,368 (Hojjatie) describes the production
of calcium thiosulfate in high yield and with low solid byproducts
from oxidation of calcium polysulfide at elevated temperature.
However, the '368 patent does not utilize sulfur dioxide.
[0023] Sulfur dioxide is a common air pollutant which forms due to
combustion processes and burning of fossil fuels containing sulfur.
Many industries contribute to the emission of sulfur dioxide in the
atmosphere in the United States. Chief among these industries are:
electric power plants (42%), coal (4%), oil (17%), refinery
operations (5%), smelting of ores (12%), coke processing (2%), and
sulfuric acid manufacture (2%). The maximum allowable concentration
of sulfur dioxide (SO.sub.2) in the air is about 5 ppm. However,
sulfur dioxide may be toxic to vegetation in concentrations of
about 2 to 3 ppm and corrosive to materials made of metal.
[0024] The principle methods used to limit sulfur dioxide emissions
are (a) use of low-sulfur fuels, (b) removal of sulfur from fuel
before combustion, (c) removal of sulfur dioxide after chemical
combustion processes, and (d) modification of chemical combustion
processes.
[0025] Numerous methods have been developed to remove sulfur
dioxide for chemical combustion processes involving sulfur dioxide.
The following are examples of such methods: Absorption into
dimethyl sulfoxide (DMSO, U.S. Pat. No. 3,538,681), absorption in
molten alkaline metals carbonate salts such as lithium, sodium, and
potassium carbonate at 1500.degree. F.-2000.degree. F. (U.S. Pat.
No. 3,671,185) and recovery as hydrogen sulfide, absorption into
potassium polyphosphate solution to form potassium polysulfide
(U.S. Pat. No. 3,630,672), absorption into soda caustic or hydrated
lime to form waste sodium sulfate or calcium sulfate (U.S. Pat. No.
3,640,053), absorption into salts such as formate salts of
ammonium, sodium, and potassium at 457.degree. F. to form hydrogen
sulfide, carbon dioxide, and carbonate salts of these metals (U.S.
Pat. No. 3,687,615), and recovery as ammonium sulfate fertilizer
(U.S. Pat. No. 3,615,165).
BRIEF SUMMARY OF THE INVENTION
[0026] The present invention relates to processes for the
production of calcium thiosulfate by (1) reacting sulfur dioxide
(SO.sub.2) with sulfur (S) and hydrated lime [i.e., calcium
hydroxide, Ca(OH).sub.2], or (2) by reacting SO.sub.2 with
lime-sulfur or calcium polysulfide. The invention further relates
to the foregoing reactions being conducted under certain
conditions, to produce a solution of calcium thiosulfate having a
high concentration and with low byproduct formation.
[0027] Liquid solutions containing high concentrations of calcium
thiosulfate can be prepared in accordance with the present
invention, having only minimal quantities of solid byproducts and
unreacted sulfur in the manner of batch reaction, or via a
semi-continuous reaction process. The invention involves the use of
specific conditions for the reaction, for example the use of
certain molar ratios of the raw materials, reaction time and
temperature, which reduces the formation of undesirable calcium
sulfate byproduct and produces CaTs at a high concentration and
high purity level.
[0028] In one embodiment of the invention, calcium hydroxide slurry
is introduced to the process reactor, elemental sulfur is added to
this slurry, and the mixture is heated while agitating. The mixture
is brought to a temperature suitable for reaction with sulfur
dioxide gas under conditions sufficient to produce calcium
thiosulfate.
[0029] In another embodiment of the invention, a contactor/reactor
apparatus is provided for reacting sulfur dioxide with a slurry,
wherein the slurry is a CaO slurry, a Ca(OH).sub.2 slurry, or a
lime-sulfur slurry, to prepare a calcium thiosulfate solution. If
the aforementioned slurry is a CaO or a Ca(OH).sub.2 slurry, then
sulfur is added to the slurry. The apparatus comprises (i) a bubble
column for providing contact between sulfur dioxide gas bubbles and
liquid/slurry; (ii) a mechanical agitator for dispersing the gas
bubbles within the bubble column; (iii) a venturi, having an
ejector/eductor for ejecting accumulated gas at the top portion of
the bubble column and educting the gas through a venturi, wherein
the venturi contacts the gas with a recirculated portion of the
liquid/slurry; and (iv) a pipe/tube contactor in contact with the
venturi for contacting the gas and a recirculated portion of the
liquid/slurry mixture and returning the mixture to the bottom
portion of the bubble column.
[0030] The present invention may use sulfur dioxide that is
obtained as a byproduct of industrial operations such as mining,
coke processing, oil and gas refineries and power generation
plants. For example, the sulfur dioxide used in the present
invention may be obtained via recovery from incineration of
sulfur-bearing gases from oil refineries.
[0031] In yet another aspect of the invention, a semi-continuous
approach is designed for the removal of sulfur dioxide tail gas
from chemical processing units, power generation industries and
mining industries, and using that sulfur dioxide in a process for
producing high concentration liquid calcium thiosulfate product. In
a specific embodiment, the sulfur dioxide is continuously removed
and immediately used in a process as described herein, to produce
the calcium thiosulfate product.
BRIEF DESCRIPTION OF THE DRAWINGS
[0032] The present invention will now be described in more detail
with reference to preferred embodiments of the invention, given by
way of examples, and illustrated in the accompanying drawings in
which:
[0033] FIG. 1 is a graphical illustration of the process kinetics
for calcium thiosulfate preparation from a calcium polysulfide
slurry and sulfur dioxide as a function of pH versus time.
[0034] FIG. 2 is a graphical illustration of the process control of
calcium thiosulfate solution preparation.
[0035] FIG. 3 is a graphical illustration of the process flow
diagram for calcium thiosulfate preparation.
[0036] FIG. 4 is a process flow diagram, including a schematic
illustration of a contactor/reactor, in accordance with a preferred
embodiment of the present invention.
DETAILED DESCRIPTION OF THE INVENTION
[0037] The present invention relates to a process for preparing
calcium thiosulfate by reacting sulfur dioxide with a slurry of
calcium hydroxide, lime-sulfur or calcium polysulfide. More
specifically, the invention relates to a process for preparing
calcium thiosulfate utilizing particular reactants and reaction
parameters and conditions. The present invention provides a process
for the preparation of high purity, concentrated calcium
thiosulfate. The calcium thiosulfate produced according to this
invention does not require further concentration by evaporation or
other means, and is useful as an agricultural nutrient.
[0038] The production of calcium thiosulfate according to the
invention is conducted in a single reaction vessel or,
alternatively, in a series of reaction vessels and holding tanks to
facilitate a semi-continuous reaction. The process of the invention
includes a series of process steps, which can be implemented in
equipment designed to provide the desired process conditions.
[0039] The process steps can be accommodated in a single reaction
vessel with the appropriate auxiliary equipment (pumps, piping,
valves, heat exchangers, filters, controls, etc.) to produce one
single batch at a time. Alternatively, the process steps can be
carried out in a series of reaction vessels and holding tanks to
facilitate a semi-continuous production arrangement.
[0040] Advantageously, described herein is a process by which
calcium thiosulfate can be prepared from inexpensive raw materials,
such as lime (calcium oxide, CaO) and sulfur. A further advantage
is that the invention provides a way to utilize sulfur dioxide
recovered from flue gas (tail or waste gas) from power plants, the
mining industry or other industries, to make the non-hazardous
plant nutrient calcium thiosulfate.
[0041] The following equations illustrate alternative processes for
making CaTs according to the invention.
[0042] Using lime (calcium oxide, CaO) as calcium source:
CaO+S+SO.sub.2.fwdarw.CaS.sub.2O.sub.3
[0043] Using hydrated lime (calcium hydroxide, Ca(OH).sub.2) as
calcium source:
Ca(OH).sub.2+S+SO.sub.2.fwdarw.CaS.sub.2O.sub.3+H.sub.2O
[0044] Using lime-sulfur (mixture of calcium polysulfides,
CaS.sub.x, and calcium thiosulfate, CaS.sub.2O.sub.3) as calcium
source:
CaS.sub.x+CaS.sub.2O.sub.3+SO.sub.2+H.sub.2O.fwdarw.2CaS.sub.2O.sub.3+H.-
sub.2S+(x-2)S
[0045] Using calcium polysulfide (CaS.sub.x) as calcium source:
CaS.sub.x+SO.sub.2+H.sub.2O.fwdarw.CaS.sub.2O.sub.3+H.sub.2S+(x-2)S
[0046] The process of the invention may be carried out according to
the following preferred reaction conditions and parameters.
[0047] If either lime (CaO) or hydrated lime [Ca(OH).sub.2] is used
as the calcium source, a slurry of the lime or hydrated lime in
water is first provided, and then sulfur is added to the slurry.
Lime must be converted to hydrated lime by slaking, i.e. by mixing
with water. Either a pre-existing slurry of hydrated lime is used,
or a slurry is formed by mixing lime with water to form hydrated
lime. In a preferred embodiment, the lime is about 96% to about 99%
pure.
[0048] Preferably, the mixture of sulfur and the slurry is heated.
In a preferred embodiment, it is heated to at least about
70.degree. C. (about 158.degree. F.). More preferably, it is heated
to a temperature in the range of about 85.degree. C. to about
99.degree. C. (about 185.degree. F.-210.degree. F.). Even more
preferably, it is heated to a temperature in the range of about
90.degree. C. to about 92.degree. C. (about 195.degree.
F.-198.degree. F.).
[0049] The sulfur is preferably combined with the calcium hydroxide
at a sulfur to calcium hydroxide mole ratio of about 1:1 to about
6:1. More preferably, the mole ratio is about 3.5:1 to about 6:1.
Still more preferably, the mole ratio is about 3.4:1 to about
3.8:1. Even more preferably, the ratio is about 3.6:1.
[0050] In a preferred embodiment, the mole ratio of sulfur to
calcium hydroxide to water is at least about 2:6:30.
[0051] In another preferred embodiment, the mole ratio of sulfur to
calcium hydroxide to water is about 3.6 to about 4.9:1:25.5.
[0052] In still yet another preferred embodiment, the mole ratio of
sulfur to calcium hydroxide to water is about 3.6:1:25.5.
[0053] If the sulfur to calcium hydroxide to water ratio used is
about 3.6:1:25.5, then the reaction takes about 2-6 hours to
complete.
[0054] Sulfur dioxide is then added to the slurry, which now
contains calcium polysulfides as the result of the reaction of
calcium hydroxide and sulfur. Prior to the addition of sulfur
dioxide, the calcium polysulfide reaction mixture slurry typically
will require cooling. Cooling may be by external cooling or other
means known to one of skill in the art. Cooling is used to avoid
decomposition of the calcium thiosulfate that has formed and to
avoid loss of sulfur dioxide due to evaporation or boiling off. In
a preferred embodiment, the calcium polysulfide reaction mixture is
cooled to a temperature of about 55.degree. C. to about 75.degree.
C. (about 131.degree. C.-167.degree. C.) before the addition of
sulfur dioxide.
[0055] The reaction mixture may optionally be subjected to further
cooling during and/or after addition of the sulfur dioxide to
maintain the temperature of the reaction mixture below a certain
temperature, to avoid decomposition of the calcium thiosulfate
formed and to avoid loss of sulfur dioxide by boiling off. For
example, when the sulfur dioxide is added, it is preferable to
maintain the temperature of the reaction mixture at about
82.degree. C. to about 95.degree. C. (about 180.degree.
F.-203.degree. F.). Still more preferably, the reaction mixture is
maintained at about 85.degree. C. to about 88.degree. C. (about
185.degree. F.-190.degree. F.).
[0056] Preferably, when the sulfur dioxide is added, the pH is
adjusted to about 3-6, or still more, preferably to about
3.5-4.
[0057] In the preferred practice of the invention, only minor
quantities of byproducts are formed. These residual byproducts
generated during lime-sulfur production and subsequent reaction
with sulfur dioxide typically contain calcium sulfite, calcium
sulfate, and elemental sulfur. If metal oxides are present in the
lime (calcium oxide) raw material, some metal sulfides could be
present as well after the reaction is complete. Higher purity
calcium oxide typically contains lower amounts of metal oxides.
Calcium carbonate and silica impurities may accompany commercial
grade calcium oxide. These impurities usually amount to less than
2% by weight of the final calcium thiosulfate solution when a high
grade of calcium oxide is utilized and the formulation and reaction
conditions are adequately controlled. Therefore, a preferred
embodiment of the invention uses a high grade lime as a starting
material.
[0058] Residual reaction byproducts, raw material impurities, and
unreacted raw materials in the calcium thiosulfate solution can
form solid particulate byproduct matter, which preferably is
filtered out in order to provide a clear, solid-free calcium
thiosulfate product solution. Particulate materials, such as
calcium sulfate, calcium sulfite, calcium carbonate, metal
sulfides, elemental sulfur, and silicate impurities can be filtered
more efficiently by adjusting pH and by choosing an appropriate
flocculent.
[0059] The invention includes a series of process steps, which can
be implemented in equipment designed to provide the desired process
conditions. The process steps can be accommodated in a single
reaction vessel with the appropriate auxiliary equipment (pumps,
piping, valves, heat exchangers, filters, controls, etc.) to
produce one single batch at a time. The process steps alternatively
can be carried out in a series of continuously stirred reaction
tanks (CSRT) with appropriate auxiliary equipment to facilitate a
continuous production arrangement.
[0060] The process steps for the batch production could be
subdivided into three sections: lime slaking, reaction, and
filtration.
[0061] The process steps for semi-continuous production consist of
repeatable cycles. Each cycle preferably consists of two steps as
described herein.
[0062] As described herein, the present invention utilizes a series
of reactions between lime or slaked lime, sulfur, and sulfur
dioxide (or between lime-sulfur or calcium polysulfide and sulfur
dioxide) using reaction conditions as described herein, such as raw
material, molar ratios, temperature, pH control, reaction time, and
equipment configuration, to produce high purity and concentrated
calcium thio sulfate without further need for concentration by
evaporation. Advantageously, calcium thiosulfate can be prepared
according to the invention from inexpensive raw materials, such as
lime and sulfur, as well as sulfur dioxide, an environmentally
hazardous gas that is often present in industrial flue gases.
[0063] In an embodiment of the invention, color changes in the
reaction mixture are used to observe the progress of the reaction.
For example, lime-sulfur and polysulfide are typically intensely
red colored, and as they react with sulfur dioxide, the reaction
mixture turns to a yellowish color, and then to a grey-green color.
The grey-green color indicates that the calcium thiosulfate product
in high concentration has been achieved.
[0064] The following describes the preparation of calcium
thiosulfate according to one embodiment of the invention, wherein
hydrated lime is used as the calcium source.
3Ca(OH).sub.2+2(x+1)S.fwdarw.2CaS.sub.x+CaS.sub.2O.sub.3+3H.sub.2O
(i) [0065] (for example, if x=4:
3Ca(OH).sub.2+10S.fwdarw.2CaS.sub.4+CaS.sub.2O.sub.3+3H.sub.2O)
[0066] (molar ratio S:Ca(OH).sub.2.about.3.3:1)
[0066]
CaS.sub.x+CaS.sub.2O.sub.3+SO.sub.2+H.sub.2O.fwdarw.2CaS.sub.2O.s-
ub.3+H.sub.2S+(x-2)S
[0067] Reaction (i) describes a way of making calcium polysulfide
with a relatively low content of calcium thiosulfate. The addition
of reaction (ii) provides one of the processes according to the
invention, for making calcium thiosulfate from sulfur dioxide and
lime-sulfur (lime-sulfur being a mixture of calcium polysulfide and
calcium thiosulfate).
[0068] The following is an example illustrating the production of
CaTs according to the aforementioned process. Laboratory
experiments were conducted in three- or four-neck flasks (the
volume varied from 500 mL to 3 L), equipped with a mechanical
agitator, pH probe, and thermometer. The flask was fitted with a
KOH or caustic soda (NaOH) trap as a scrubber to capture vent
gases. Heating was provided by a heating mantle. The SO.sub.2
source was compressed, liquefied 100% SO.sub.2.
[0069] Raw materials: 41.7 g Ca(OH).sub.2, 36.1 g S (S:Ca(OH).sub.2
molar ratio=2:1), and 200 g H.sub.2O.
[0070] Step (i): the maximum expected concentration of Ca=8.1 wt %;
reaction duration=120 min, temperature=80.degree. C.-90.degree. C.
(176.degree. F.-194.degree. F.). The observed drop of pH was from
12.6 to 9.0.
[0071] Intermediate results: 3.96 wt % Ca, pH 11.5, SG -1.24, --all
referred to the lime-sulfur solution.
[0072] Step (ii): duration=90 minutes, temperature range=30.degree.
C.-40.degree. C. (86.degree. F.-104.degree. F.) (SO.sub.2 sparging
was started when the solution cooled down to 104.degree. F.). The
final product was amber yellow solution, specific gravity=1.32,
pH=11.0, C.sub.Ca by EDTA titration=7.0 wt %, C.sub.CaTs by iodine
titration=21.8 wt % (recalculated C.sub.Ca=5.7 wt %; the rest of
calcium was in the calcium polysulfide form). Solids were
greenish-gray and comprised 22 wt % of the total weight of the
final product. Solids contained 18 wt % of CaTs.
[0073] Yet another embodiment involves preparation of calcium
thiosulfate also using hydrated lime, but via the following direct
one-step reaction:
Ca(OH).sub.2+S+SO.sub.2.fwdarw.CaS.sub.2O.sub.3+H.sub.2O (iii)
[0074] As follows from the preceding equation, the molar ratio of
Ca(OH).sub.2:S should be 1:1. SO.sub.2 sparging was started as soon
as the temperature of Ca(OH).sub.2 slurry, mixed with sulfur,
reached 180-190.degree. F. Four hours of SO.sub.2 sparging was
required to bring the pH of the slurry down to 5.8 from pH
11.5.
[0075] The final product: assay=12.25 wt % CaTs by the EDTA
titration, SG=1.12, pH=8.6. The solids, resulting from the vacuum
filtration, comprised 31.4% of the total weight of the final
product, which appeared to be unusually high. The inventors
determined that the formation of CaSO.sub.3 resulted from the
reaction between Ca(OH).sub.2 and SO.sub.2. Therefore, preferably,
if there is any unreacted Ca(OH).sub.2 by the end of the
lime-sulfur preparation, all solids should be removed from the
reaction zone before reacting the lime-sulfur solution with sulfur
dioxide, to avoid the production of CaSO.sub.3. Otherwise, the
amount of final solids will be increased by CaSO.sub.3 byproduct
(i.e., the purity of the CaTs will be lower, due to the presence of
CaSO.sub.3).
[0076] Yet another embodiment of the invention involves preparation
of calcium thiosulfate by reacting calcium polysulfide with sulfur
dioxide, as shown in the following reaction:
CaS.sub.x+SO.sub.2+H.sub.2O.fwdarw.CaS.sub.2O.sub.3+H.sub.2S+(x-2)S
(iv)
[0077] The chemical description of this approach is identical to
reaction (ii). The difference is in the source of CaS.sub.x and in
its composition. As shown above, the process of calcium thiosulfate
preparation from lime-sulfur solution consists of two steps (i) and
(ii). If relatively pure calcium polysulfide (CaS.sub.x) is used as
a starting material as is proposed in reaction (iv) above, rather
than lime-sulfur, the tendency to form byproducts is significantly
reduced.
[0078] Three variations of that process were performed. The
starting material CaS.sub.4.5 (C.sub.Ca=9.66 wt %, SG=1.48) was
used as a starting material. The product contained about 25 wt %
calcium thiosulfate but yield was about 25%. In the next experiment
the calcium polysulfide was diluted to contain about 7 wt % Ca. The
product contained 28 wt % calcium thiosulfate and the yield was
34%. In the third experiment full strength calcium polysulfide
(9.66 wt % Ca) was used but some calcium thiosulfate (about 5 wt %)
was added with the hope that presence of calcium thiosulfate would
accelerate the process. The product contained 25 wt % calcium
thiosulfate and the yield was 49%.
[0079] The kinetics of these three experiments as a function of pH
vs. reaction time is shown in FIG. 1. These plots consist of two
portions, straight line and steep drop of pH. The transition from
straight line to pH drop corresponds to pH values of 7.5-8.0. The
pH appeared to be the most objective monitoring factor and was used
as the control parameter for the endpoint of the process.
[0080] An example of a preferred embodiment of the invention
involves preparation of calcium thiosulfate from lime-sulfur
solution.
[0081] Listed below are the general characteristics of the calcium
thiosulfate preparation process from a lime-sulfur solution, by
reacting the lime-sulfur solution with sulfur-dioxide, as shown in
the following reaction:
CaS.sub.x+CaS.sub.2O.sub.3+SO.sub.2+H.sub.2O.fwdarw.2CaS.sub.2O.sub.3+H.-
sub.2S+(x-2)S [0082] 1. The calculated concentration of calcium
from Ca(OH).sub.2 at the beginning of the (i) step was 8.1 wt %.
[0083] 2. S:Ca(OH).sub.2 molar ratio was 2:1. [0084] 3. The
reaction temperature during the (i) step was approximately (about)
80.degree. C. (176.degree. F.)+/-2.degree. C. [0085] 4. The
reaction duration of the (i) step was variable (for example, 120
and 153 min), 2.5 hr on the average, but the longer the (i) step,
the higher is C.sub.Ca in the lime-sulfur solution (Table 1,
below). The average duration of the whole process was 3.5-4.0 hr.
[0086] 5. pH was a control parameter of the process.
[0087] The kinetic curves, pH versus time, are shown in FIG. 1.
This shows that during the step (i), pH of the slurry was gradually
decreased to 9.7. The step (ii) corresponded to a wide straight
line preceding a rapid drop of pH which occurred in less than 10
minutes. [0088] 6. pH was also a monitoring factor to determine the
endpoint of SO.sub.2 sparging. Sparging was stopped when pH of the
slurry reached 3.8-4.0. [0089] 7. In addition to pH, the color of
the slurry was another control parameter of the process.
[0090] During step (i), the color of the reaction mixture changed
from the initial whitish to pale yellow, then to an intensive
yellow, and finally to brownish-yellow. This was interpreted as
accumulation of calcium polysulfide. During step (ii), the
brownish-yellow color was converted back to yellow and remained
nearly unchanged, along with stabilized pH. The sudden drop of pH
was accompanied with rapid change of color; the intensity of yellow
gradually disappeared and finally the solution became
whitish-gray.
[0091] The maximum concentration of calcium (C.sub.Ca) in the
lime-sulfur solution by the end of step (i) was 4.82 wt %. Calcium
thiosulfate concentration (C.sub.CaTs) in the final solution was
21.8-25.4 wt % and calcium polysulfide concentration
(C.sub.Cap.sub.s, as CaS.sub.2) was less than 3.7 wt % (later
SO.sub.2 sparging was prolonged to lower the pH to 3.8-4.0).
SG<1.38, pH=10-11. Solids amounted to 14 wt %. Solids contained
about 17 wt % calcium thio sulfate. Kinetic data of the (i) step
are shown in Table 1.
TABLE-US-00001 TABLE 1 Kinetics of the process for lime-sulfur
preparation Time, min 7 40 70 87 96 128 153 SG 1.08 1.08 1.08 1.11
1.14 1.22 1.26 C.sub.Ca, Wt % 0.12 0.22 0.74 1.4 1.82 3.57 4.82
[0092] As mentioned before, the inventors determined that pH is one
of the factors in monitoring the reaction. It was found that if pH
would be allowed to drop as low as possible, but still was above
the critical value (the critical pH is approximately 4, or more
precisely at pH 3.8-4, below which calcium thiosulfate decomposes),
partial dissolving of CaSO.sub.3 (CaS and CaSO.sub.4 if any) could
be obtained, and as a result a further reduction of the amount of
solids could be obtained. The inventors determined that sulfur
dioxide should be purged into the solution until the pH drops to
about 3.8 to about 4.0.
[0093] The inventors also determined that the purity of lime is
also another factor in reducing the amount of solid byproducts.
They determined that the use of higher purity lime resulted in a
reduced amount of byproduct solids. Preferably, the lime is about
96% to about 99% pure. The amount of byproduct solids was decreased
to 6 wt % of the total product with higher purity lime. The
reaction time also decreased when higher purity lime was used.
[0094] The inventors also determined what pH is needed to prevent
calcium thiosulfate decomposition in the acidic medium according to
equation:
S.sub.2O.sub.3.sup.2-+H.sup.+.fwdarw.HSO.sub.3.sup.-+S.sup.o
[0095] Fourier Transform Infrared Spectroscopy (FTIR) studies
proved that even at pH 4 the product is still calcium thiosulfate
and not calcium bisulfite.
[0096] Calcium thiosulfate solution can be distinguished from
Ca(HSO.sub.3).sub.2 solution visually, as well. Calcium thiosulfate
is a colorless, sometimes cloudy and practically odorless solution.
Ca(HSO.sub.3).sub.2 is yellow with the strong SO.sub.2 smell
typical of bisulfite solutions.
[0097] Preferred process parameters according to the invention are
as follows:
[0098] S:Ca(OH).sub.2 molar ratio. The inventors determined
preferred S:Ca(OH).sub.2 molar ratios for the process, in
correlation with the duration of the process and amount of solids
produced, as follows: [0099] The higher the molar ratio, the
shorter the reaction time required (the endpoint attainment of
C.sub.Ca, approximately 6.5 wt % Ca, correlates to 24.7 wt %
calcium thio sulfate); [0100] The molar ratio 5:1 resulted in the
maximum concentration of calcium: C.sub.Ca=6.94 wt % (recalculated
equivalent calcium thiosulfate concentration=26.4 wt %); [0101] The
molar ratio 4:1 resulted in the minimum amount of remaining solids
and still satisfactory C.sub.Ca=6.60 wt % (the predicted calcium
thiosulfate concentration was 25.1 wt %).
[0102] 99% lime purity was chosen for optimization of the
S:Ca(OH).sub.2 molar ratio to exclude formation of solids due to
impurities associated with lower quality lime. The amounts of
Ca(OH).sub.2 and H.sub.2O were constant in all the experiments
(42.56 g Ca(OH).sub.2 and 263.34 g H.sub.2O). The amount of sulfur
was variable. The conditions of the experiment were as follows:
[0103] temperature: about 96.degree. C.-99.degree. C. (205.degree.
F.-210.degree. F.) (near the boiling point); [0104] duration: 40
min after the temperature reached 200.degree. F.; [0105] immediate
vacuum filtration of the hot final product; [0106] weighing solids
immediately after filtration, without air drying.
[0107] The optimization of the molar ratio was judged by the
following parameters: [0108] 1. Relative amount of solids (%)
related to the total amount of the final lime-sulfur product (a sum
of the weight of filtered lime-sulfur solution and solids). Loss
was not included. [0109] 2. Concentration of calcium in the
lime-sulfur solution (wt %). [0110] 3. Recovery of calcium (%) as
the total amount of calcium in the lime-sulfur solution, related to
the amount of calcium in the lime starting material. Calculation
was based on 100% Ca(OH).sub.2.
[0111] Results are shown in Table 2.
TABLE-US-00002 TABLE 2 Optimization of the S:Ca(OH).sub.2 Molar
Ratio. Relative C.sub.Ca in the S:Ca(OH).sub.2 amount of
lime-sulfur Recovery of # molar ratio solids, % solution, wt % Ca,
% Loss, g 1 1.00 10.9 2.66 31.7 16.0 2 1.92 6.5 4.36 58.0 13.7 3
2.87 3.1 5.71 82.5 15.7 4 3.00 2.7 5.83 86.3 11.0 5 3.20 1.7 6.17
91.6 17.1 6 3.40 1.3 6.22 95.9 9.2 7 3.45 1.5 6.50 97.3 19.8 8 3.60
0.5 6.46 100.0 8.1 9 3.80 0 6.59 100.0 9.1 10 3.83 0.1 6.73 100.0
16.4 11 4.02 0.5 6.57 100.0 14.5 12 4.02 0.2 6.50 100.0 18.3 13
5.00 6.0 6.70 100.0 17.0
[0112] The inventors determined that the preferred S:Ca(OH).sub.2
molar ratio is 3.6 to 3.8:1 (Table 2). This resulted in the minimal
amount of solids (0-0.5%), 100% recovery of calcium, and therefore,
the maximum possible C.sub.Ca was 6.46 wt %, which correlates to
C.sub.CaTs=24.5 wt %.
[0113] Solids analysis showed that when the molar ratio was less
than 3.6 to 3.8:1, solids contained unreacted lime. The smaller the
molar ratio, the larger was the percentage of unreacted lime.
[0114] Starting with molar ratio of 4.0, there was a noticeable
amount of unreacted sulfur.
[0115] Table 3 shows the results of three different experiments in
attempts to optimize the yield and minimize the amount of solid
byproducts:
TABLE-US-00003 TABLE 3 Preparation of the Maximum Concentrated
Lime-Sulfur Solution. C.sub.Ca in the Relative Experiment Expected
lime-sulfur amount of Recovery C.sub.caTs, # Ca(OH).sub.2, g S, g
C.sub.ca, wt % * solution, wt % solids, % of Ca, % wt % ** 1 52.0
81.02 7.11 7.26 1.0 99.0 27.45 2 59.7 93.02 7.76 7.99 1.1 97.2 27.0
3 70.0 109.07 8.56 8.17 8.9 70.8 -- * calculation is based on 100%
recovery of Ca from lime in lime-sulfur solution ** real C.sub.caTs
in the final calcium thiosulfate solution, resulting from the
corresponding lime-sulfur solution
[0116] Experiment #3 was not completed due to the low recovery of
calcium in step (i).
[0117] The inventors determined that the higher the C.sub.Ca was in
the lime-sulfur parent solution, the higher the C.sub.Ca was in the
calcium thiosulfate solution. This was true if C.sub.CaTs was less
than about 27 wt %. The further increase of C.sub.Ca in the
lime-sulfur solution did not influence C.sub.CaTs, but resulted in
the growth of the amount of solid.
[0118] The preferred temperature during the step (i) in which
lime-sulfur is produced by reacting calcium hydroxide and sulfur is
about 93.degree. C. to about 99.degree. C. (200.degree.
F.-210.degree. F.) as described in U.S. Pat. No. 6,984,368.
[0119] The inventors determined that the duration of the step (i)
appears to be dependent on molar ratio only (since temperature is
not variable).
[0120] While using pure lime (99% or better) and pure sulfur with
the optimal molar ratio of
S:Ca(OH).sub.2:H.sub.2O=(3.6-3.8):1:25.5, the endpoint of step (i)
could be judged by the appearance of the solution. The endpoint is
when the solution becomes dark reddish-brown and clear (no solid
particles could be observed). Even while using a different kind of
lime, when the reaction is completed, the color of the reacting
mixture reaches a certain point and remains unchanged. While using
recycled sulfur, it becomes more complicated to determine the
endpoint by color, because impurities and contaminants in the
sulfur tend to cause coloration of the solution, which makes
determination of the endpoint more difficult.
[0121] SO.sub.2 flow. Lime-sulfur solutions are absorbing SO.sub.2
completely even at the highest flow rate (no carry over of SO.sub.2
is monitored in the KOH or NaOH trap). Lab experiments utilized
synthetic SO.sub.2 gas. Industrial gas composition will be dilute,
approximately 4-14 vol % of SO.sub.2, with the balance consisting
of nitrogen, oxygen, and other combustion products. SO.sub.2 flow
rate is not a limiting factor in step (ii).
[0122] Raw Materials
[0123] Different lime purities from different sources were tested
and their effects were compared on the overall process. The lime
purities were Source 1: >99 wt % Ca(OH).sub.2; Source 2: 97.40
wt % Ca(OH).sub.2; Source 3: 94.20 wt % Ca(OH).sub.2; and Source 4:
95.80 wt % Ca(OH).sub.2. The comparison was made in the following
series of tests using pure sulfur (start-up operation): [0124] pure
sulfur: (67.0 g); [0125] molar ratio:
S:Ca(OH).sub.2:H.sub.2O=3.8:1:25.5; [0126] duration: 40 min after
temperature reached 93.3.degree. C. (200.degree. F.); [0127]
temperature: 95.degree. C.-96.degree. C. (203.degree.
F.-205.degree. F.). Solution was boiling; [0128] immediate vacuum
filtration of the hot final product; [0129] weighing solids
immediately after filtration, without air drying.
[0130] The following characteristics were chosen for comparison of
applicability of different lime purities: [0131] 1. Relative amount
of solids (%) as absolute amount of solids, related to the total
amount of the final lime-sulfur product (a sum of the weight of the
final solution and solids. Loss, mostly due to evaporation, was not
included. The average loss was approximately 20 g in each
experiment). [0132] 2. Concentration of calcium in the lime-sulfur
solution determined by EDTA titration (wt %). [0133] 3. Recovery of
calcium (%) as the total amount of calcium in the lime-sulfur
solution, related to the total amount of calcium in the lime
starting material. Calculation was based on assumption for 100%
Ca(OH).sub.2.
TABLE-US-00004 [0133] TABLE 4 Preparation of lime-sulfur solutions
step (i) from different sources of lime and pure sulfur. Amount of
Recovery of Source of lime solids, wt % C.sub.Ca, wt % Ca, %
Filtration Source 1 0.295* 6.65 100 fast Source 2 2.7 6.57 96.3
very slow Source 3 4.0 6.45 93.9 very slow Source 4 2.25 6.44 97.0
slow *A second set of tests was performed to verify
reproducibility. The results shown are averages. The conclusion
showed that higher purity lime reacted more quickly and had less
solid byproducts formed during the reaction.
[0134] Real Gas Mixture
[0135] In the commercial process SO.sub.2 was produced by burning
sulfur in air with a resulting gas mixture consisting of 14%
SO.sub.2, 3% O.sub.2, and 83% N.sub.2. The test was performed to
record the effects of substitution of 100% SO.sub.2 with dilute
SO.sub.2 such as: [0136] Carry-through of unreacted SO.sub.2 due to
an increase in the flow rate to compensate for the dilute
concentration of SO.sub.2; [0137] Possible oxidation of calcium
thiosulfate resulting in CaSO.sub.3 and/or CaSO.sub.4.sup.solid,
due to the presence of oxygen and SO.sub.2 in the real gas mixture.
Tests were performed to investigate these possibilities. SO.sub.2
was mixed with the excess amount of air and the mixture was used as
a source of SO.sub.2. Due to the presence of air, the following
oxidation-reduction reaction is possible:
[0137] 2CaS.sub.2O.sub.3+O.sub.2.fwdarw.2CaSO.sub.4+2S
[0138] For the systematic study, compressed SO.sub.2/air gas
mixture (14.56 vol % SO.sub.2) was used and N.sub.2 was
intentionally substituted with air to replicate the commercial
conditions. Observations from the test: [0139] 1. No considerable
excess oxidation of calcium thiosulfate occurred due to presence of
oxygen. [0140] 2. No significant SO.sub.2 carry-through was
observed during the step (ii) of the process.
[0141] The reaction between sulfur dioxide and lime-sulfur can be
performed in a batch manner in the same equipment where the
lime-sulfur is produced, or it can be performed in separate
dedicated equipment. The lime-sulfur or calcium polysulfide slurry
is cooled to the preferred temperature for reaction with sulfur
dioxide. Preferably, the reaction mixture is maintained in the
range of about 55.degree. C.-75.degree. C. during the step of
reacting the slurry with the sulfur dioxide. Reaction temperatures
above 75.degree. C. (167.degree. F.) should be avoided during
conversion of lime-sulfur (or calcium polysulfide) to calcium
thiosulfate because of possible losses due to thermal
decomposition. The reaction of sulfur dioxide with calcium
polysulfide is exothermic and excess heat generated during SO.sub.2
addition is removed to maintain the desired temperature.
[0142] An important consideration in maintaining a good reaction
rate and complete conversion of the lime-sulfur (or calcium
polysulfide) intermediate to calcium thiosulfate is to provide
adequate gas/liquid contacting area and time for the sulfur dioxide
gas and the liquid lime-sulfur (or calcium polysulfide) slurry to
react. Contact area is important because the reaction primarily
takes place at the SO.sub.2 gas/liquid slurry interface. If this
interface area is not adequate, the reaction will be slow, leading
to larger amounts of undesirable byproducts.
[0143] Many common types of gas/liquid contacting process equipment
can be utilized for contacting and reacting the gas and liquid.
These include, but are not limited to bubble columns, packed
columns, tray columns, spray columns, mechanically agitated tanks,
jet loops, venturi ejector/eductor, pipes/tubes and static
mixers.
[0144] A special contactor was developed which utilizes elements of
common types of contacting equipment combined into a single
contactor-reactor design. The elements of this arrangement work to
maximize contact time, area, and overall mass-transfer coefficient
of reacting the lime-sulfur slurry (or calcium polysulfide slurry)
and sulfur dioxide gas with recycled liquid/gas. This arrangement
was described in U.S. Pat. No. 6,984,386, the entire disclosure of
which is incorporated herein by reference, and is shown in FIG. 4
in which a contactor/reactor 60 in accordance with an embodiment of
the invention, comprises (i) a bubble column 61, in which gas
bubbles up through the liquid; (ii) a mechanical agitator 58, which
further disperses bubbles within the column 61 to provide
additional contact area time and mass-transfer; (iii) a venturi
ejector/eductor, where accumulated gas at the top portion 61a of
the column is ejected via a line 11 and educed through a venturi
64, where it is contacted with recirculated liquid/slurry 10; and
(iv) a pipe/tube contactor where the gas/liquid mixture exiting the
venturi 64 is further contacted as it is conducted inside a draft
tube, back to the bottom portion 61b of the bubble column 61, where
it is recombined with the liquid/slurry.
[0145] Mass Balance Check
[0146] A series of tests were performed to calculate mass balance
between raw materials and product/byproduct. Results of one test
are shown in Table 5.
TABLE-US-00005 TABLE 5 Mass balance check. Description Incoming
amount, g Final products, g Ca(OH).sub.2 728.1 S 588.9 H.sub.2O
5039.5 SO.sub.2 313.4 CaTs solution 5589.7 Recycled sulfur 146.2
Solids 272.3 Material, accumulated in 42.2 the KOH trap Total
6669.9 6050.4
[0147] The loss of material, as a difference between the total
starting material and the final products, was 619.5 g (9.3%). Most
of the loss occurred during step (i) due to water evaporation and
vacuum filtration.
[0148] A further embodiment of the invention is one for the
semi-continuous process of CaTs preparation, consisting of
repetitive cycle. Each cycle involves two steps, described by the
following equations: [0149] (a) Preparation of the lime-sulfur
solution (mixture of calcium polysulfide and calcium thio
sulfate):
[0149]
3Ca(OH).sub.2+2(x+1)S.fwdarw.2CaS.sub.x+CaS.sub.2O.sub.3+3H.sub.2-
O (i) [0150] (b) SO.sub.2 sparging, resulting in conversion of
calcium polysulfide into calcium thio sulfate:
[0150]
CaS.sub.x+CaS.sub.2O.sub.3+SO.sub.2+H.sub.2O.fwdarw.2CaS.sub.2O.s-
ub.3+H.sub.2S+(x-2)S (ii)
[0151] The flow diagram of the said process is shown in FIG. 3.
Step (i) is the preparation of lime-sulfur from lime, sulfur, and
water in the reactor R-1. By the end of step (i) the lime-sulfur
product is transferred to filtering unit F-1 (this step is not
shown in FIG. 3). Solids are separated. The filtrate is transferred
to the reactor R-2 and reacted with sulfur dioxide [step (ii)]. The
required SO.sub.2 is provided from sulfur burner B-1. The final
product prepared in reactor R-2 is filtered in the filtering unit
F-2 (not shown) and is transferred to the storage tank. The solids
from filtering units F-1, and F-2 are combined and analyzed for
their sulfur and lime content and transferred back to R-1. This
unreacted sulfur that is transferred back to R-1 is referred to
herein as "recycled sulfur". The deficient amount of sulfur and/or
lime is added and the cycle continues.
[0152] H.sub.2S, generated during the step (ii) in the reactor R-2,
is vented to a scrubber containing caustic soda or can be recycled
to the sulfur burner along with unreacted SO.sub.2, if any.
[0153] The process described above eliminates formation of
CaSO.sub.3 (solid) during the step (ii) by limiting the potential
reaction of unreacted Ca(OH).sub.2, remaining after step (i), with
SO.sub.2.
[0154] A preferred embodiment of the process of the invention is as
follows:
[0155] Step (i): [0156] The molar ratio
S:Ca(OH).sub.2:H.sub.2O=3.6:1:25.5, when pure sulfur feed is used;
[0157] The molar ratio S:Ca(OH).sub.2:H.sub.2O=(3.6-4.9):1:25.5,
when recycled sulfur is used; [0158] Pure feed sulfur and recycled
sulfur should be used separately to attain predictable results by
the end of step (i) (C.sub.Ca in the lime-sulfur solution and
relative amount of the unreacted solids); [0159] Duration: 30-35
min.
[0160] When pure sulfur is used, the endpoint of the reaction can
be monitored by color: dark reddish-brown and clear signifies a
complete reaction; [0161] Temperature: 200.degree. F.-210.degree.
F. (210.degree. F. is near the boiling point). [0162] Immediate
filtration of the lime-sulfur product by the end of step (i);
[0163] To determine lime-sulfur concentration for 25 wt % calcium
thiosulfate production, samples are taken and analyzed at the end
of each step (i). In a case where the lime-sulfur solution contains
lower than projected calcium thio sulfate concentration (C.sub.Ca),
the deficient amount of calcium and sulfur are added and additional
step (i) performed.
[0164] Step (ii): [0165] Sparging of the SO.sub.2/N.sub.2/O.sub.2
gas mixture into lime-sulfur until pH drops to approximately 4. The
low pH guarantees the final calcium thiosulfate solution will be
free from H.sub.2S, which is a side-product of the step (ii).
[0166] Filtration of the final product. Solids, termed as "recycled
sulfur", consist mostly of sulfur. The solids are recycled to the
reactor R-1 as a part of the sulfur feed material. [0167] pH of the
final calcium thiosulfate solution is adjusted to 7.0-7.5 via
addition of lime. Continuous agitation is necessary to have a
steady state pH reading. Afterwards the CaTs solution is filtered
again.
[0168] The reason why pure sulfur and recycled sulfur are
preferably used separately is because it is desirable for the user
of the process to be able to predict with some certainty what will
be the concentration of calcium in the lime-sulfur solution and
what will be the concentration of calcium in the unreacted solids
at the end of step (i). Using pure sulfur permits one to predict
with greater certainty what the concentration of calcium will be.
In contrast, when recycled sulfur is used, it is difficult to
predict with certainty how concentrated the aforementioned calcium
levels will be, because with recycled sulfur it is more difficult
to predict how high the level of S is in the recycled sulfur, and
it is also difficult to predict how pure and how wet (i.e., how
much water it contains) the recycled sulfur is.
[0169] Mass balance check for a semi-continuous seven cycle process
is shown in Table 6.
TABLE-US-00006 TABLE 6 Mass Balance Check of the Seven-Cycle
Process. Incoming amount, g Outgoing amount, g Cycle CaTs #
Ca(OH).sub.2, g S, g H.sub.2O, g SO.sub.2, g solution, g Loss, g
H.sub.2S, g I 62.25 54.14 410 not avail. 394.7 12.97 0 II 62.25
27.07 400 III 0 17.96 199 (II + III) (II + III) (II + III) (II +
III) cycles: 19.9 cycles: 607.1 cycles: 72.56 cycles: 0 IV 108.24
14.4 651 32.2 715.9 13.92 0 V 110.46 40.61 550 31.2 674.9 7.84 0 VI
0 69.98 689 43.6 816.8 27.04 0 VII 0 64.36 622 4.9+ 749.5 24.57 0
Total 343.2 288.26 3521 131.8 3958.9 158.9 0
[0170] The total incoming amount: 4284.26 g.
[0171] The total outgoing amount: 4117.8 g+20.53 g (solids from
VII)+87.07 g=4225.4 g.
[0172] Loss as a difference between the incoming and outgoing
amounts: 58.86 g (1.4 wt %).
[0173] Yield: 3958.9:4284.26=92.4%.
[0174] The calcium thiosulfate produced according to the invention
is an emulsion of liquid calcium thiosulfate and solid byproducts.
This emulsion is preferably further treated to produce a solution
that may be readily filtered. For example, the emulsion may be
treated with a flocculent and acidified to a near neutral pH, to
produce a colloidal solution that filters with ease. The resulting
calcium thiosulfate is a clear liquid with a concentration of up to
about 29% by weight.
* * * * *