U.S. patent application number 13/037725 was filed with the patent office on 2011-09-15 for insulative products having bio-based binders.
Invention is credited to Jacob Chacko, Liang Chen, Christopher M. Hawkins, Jesus Manuel Hernandez-Torres, Edward Alan Martine.
Application Number | 20110223364 13/037725 |
Document ID | / |
Family ID | 46729624 |
Filed Date | 2011-09-15 |
United States Patent
Application |
20110223364 |
Kind Code |
A1 |
Hawkins; Christopher M. ; et
al. |
September 15, 2011 |
INSULATIVE PRODUCTS HAVING BIO-BASED BINDERS
Abstract
Fibrous insulation products have an aqueous binder composition
that includes a carbohydrate and a crosslinking agent. In exemplary
embodiments, the carbohydrate-based binder composition may also
include a catalyst, a coupling agent, a process aid, a crosslinking
density enhancer, an extender, a moisture resistant agent, a
dedusting oil, a colorant, a corrosion inhibitor, a surfactant, a
pH adjuster, and combinations thereof. The carbohydrate may be
natural in origin and derived from renewable resources.
Additionally, the carbohydrate polymer may have a dextrose
equivalent (DE) number from 2 to 20. In at least one exemplary
embodiment, the carbohydrate is a water-soluble polysaccharide such
as dextrin or maltodextrin and the crosslinking agent is citric
acid. Advantageously, the carbohydrates have a low viscosity and
cure at moderate temperatures. The environmentally friendly,
formaldehyde-free binder may be used in the formation of insulation
materials and non-woven chopped strand mats. A method of making
fibrous insulation products is also provided.
Inventors: |
Hawkins; Christopher M.;
(Alexandria, OH) ; Hernandez-Torres; Jesus Manuel;
(Pataskala, OH) ; Chen; Liang; (New Albany,
OH) ; Martine; Edward Alan; (Newark, OH) ;
Chacko; Jacob; (Pickerington, OH) |
Family ID: |
46729624 |
Appl. No.: |
13/037725 |
Filed: |
March 1, 2011 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12900540 |
Oct 8, 2010 |
|
|
|
13037725 |
|
|
|
|
61250187 |
Oct 9, 2009 |
|
|
|
Current U.S.
Class: |
428/34.5 ;
428/292.1; 442/176; 442/327; 501/32 |
Current CPC
Class: |
Y10T 442/2959 20150401;
C09J 103/02 20130101; C09J 103/04 20130101; C03C 25/1095 20130101;
C08L 2312/00 20130101; C08L 2666/44 20130101; C09D 189/00 20130101;
C03C 25/20 20130101; C09D 105/00 20130101; C09J 105/06 20130101;
Y10T 442/2992 20150401; C03C 25/32 20130101; C03C 25/321 20130101;
C09D 133/02 20130101; D06N 2209/065 20130101; D06N 2201/082
20130101; Y10T 442/60 20150401; Y10T 428/249924 20150401; C09D
191/00 20130101; Y10T 428/1314 20150115 |
Class at
Publication: |
428/34.5 ;
501/32; 442/176; 442/327; 442/327; 428/292.1 |
International
Class: |
D04H 1/58 20060101
D04H001/58; C03C 14/00 20060101 C03C014/00; B32B 1/08 20060101
B32B001/08; B32B 27/42 20060101 B32B027/42; B32B 27/04 20060101
B32B027/04 |
Claims
1-26. (canceled)
27. A fibrous product comprising: a plurality of randomly oriented
glass fibers; and a formaldehyde-free, thermosetting, bio-based
binder composition applied to at least a portion of said fibers,
said binder composition comprising the reaction product of: at
least one carbohydrate having reactive hydroxyl groups; and at
least one crosslinking agent having reactive carboxylic acid
groups.
28. The fibrous product of claim 27, wherein said product is a
flexible, low-density product having a density of from about 0.3 to
about 4 pcf.
29. The fibrous product of claim 28, wherein said binder
composition is present in an amount from about 2% to about 13%.
30. The fibrous product of claim 27, wherein said product is a
rigid product having a density of from about 1.5 to about 10
pcf.
31. The fibrous product of claim 30, wherein said binder
composition is present in an amount from about 2% to about 20%.
32. The fibrous product of claim 27, wherein said product has a
density of from about 3 to about 8 pcf.
33. The fibrous product of claim 32, wherein said binder
composition is present in an amount from about 3% to about 15%.
34. The fibrous product of claim 27, wherein said product is a
rigid product having a density of from about 1.5 to about 10 pcf,
and is shaped cylindrically to fit around a section of pipe.
35. The fibrous product of claim 27, wherein said product is made
by a rotary fiberization process.
36. The fibrous product of claim 27, wherein said product is a
non-woven product made by an air-laid process, said product having
a density of from about 0.8 to about 4 pcf.
37. The fibrous product of claim 36, wherein said binder
composition is present in an amount from about 5% to about 20%.
38. The fibrous product of claim 27 wherein said at least one
carbohydrate is a carbohydrate having a dextrose equivalent number
from 2 to 20.
39. The fibrous product of claim 38, wherein said at least one
carbohydrate is a water-soluble polysaccharide selected from the
group consisting of pectin, dextrin, maltodextrin, starch, modified
starch, starch derivatives and combinations thereof.
40. The fibrous product of claim 27, wherein said binder
composition in a cured state comprises at least one polyester.
41. The fibrous product of claim 40, wherein said crosslinking
agent is selected from the group consisting of polycarboxylic
acids, salts of polycarboxylic acid, anhydrides, monomeric
carboxylic acid with anhydride, polycarboxylic acid with anhydride,
citric acid, salts of citric acid, adipic acid, salts of adipic
acid, polyacrylic acid, salts of polyacrylic acid, polyacrylic acid
based resins and combinations thereof.
42. The fibrous product of claim 27, wherein said product is free
of added formaldehyde.
43. The fibrous product of claim 27, wherein said fibrous product
is an insulation product.
44. The fibrous product of claim 27, wherein said fibrous product
is a non-woven fibrous mat product having a first major surface and
a second major surface; and having the binder composition at least
partially coating the first major surface.
45. The non-woven mat of claim 44, wherein said binder composition
in a cured state comprises at least one polyester.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation in part of U.S. patent
application Ser. No. 12/900,540, filed Oct. 8, 2010, which claims
priority benefits from U.S. Provisional Patent Application Ser. No.
61/250,187 entitled "Bio-Based Binders For Insulation And Non-Woven
Mats" filed Oct. 9, 2009, the entire contents of which are
expressly incorporated herein by reference.
TECHNICAL FIELD AND INDUSTRIAL APPLICABILITY OF THE INVENTION
[0002] The present invention relates generally to fibrous
insulation products and non-woven mats, and more particularly, to
fibrous insulation products that contain a bio-based binder that
contains no added formaldehyde and is environmentally friendly.
BACKGROUND OF THE INVENTION
[0003] Conventional fibers are useful in a variety of applications
including reinforcements, textiles, and acoustical and thermal
insulation materials. Although mineral fibers (e.g., glass fibers)
are typically used in insulation products and non-woven mats,
depending on the particular application, organic fibers such as
polypropylene, polyester, and multi-component fibers may be used
alone or in combination with mineral fibers in forming the
insulation product or non-woven mat.
[0004] Fibrous insulation is typically manufactured by fiberizing a
molten composition of polymer, glass, or other mineral and spinning
fine fibers from a fiberizing apparatus, such as a rotating
spinner. To form an insulation product, fibers produced by the
rotating spinner are drawn downwardly from the spinner towards a
conveyor by a blower. As the fibers move downward, a binder
material is sprayed onto the fibers and the fibers are collected
into a high loft, continuous blanket on the conveyor. The binder
material gives the insulation product resiliency for recovery after
packaging and provides stiffness and handleability so that the
insulation product can be handled and applied as needed in the
insulation cavities of buildings. The binder composition also
provides protection to the fibers from interfilament abrasion and
promotes compatibility between the individual fibers.
[0005] The blanket containing the binder-coated fibers is then
passed through a curing oven and the binder is cured to set the
blanket to a desired thickness. After the binder has cured, the
fiber insulation may be cut into lengths to form individual
insulation products, and the insulation products may be packaged
for shipping to customer locations. One typical insulation product
produced is a flexible insulation batt or blanket, which is
suitable for use as wall insulation in residential dwellings or as
insulation in the attic and floor insulation cavities in buildings.
Another common insulation product is air-blown or loose-fill
insulation, which is suitable for use as sidewall and attic
insulation in residential and commercial buildings as well as in
any hard-to-reach locations. Loose-fill insulation is formed of
small cubes that are cut from insulation blankets, compressed, and
packaged in bags.
[0006] Non-woven mats may be formed by conventional wet-laid
processes. For example, wet chopped fibers are dispersed in a water
slurry that contains surfactants, viscosity modifiers, defoaming
agents, and/or other chemical agents. The slurry containing the
chopped fibers is then agitated so that the fibers become dispersed
throughout the slurry. The slurry containing the fibers is
deposited onto a moving screen where a substantial portion of the
water is removed to form a web. A binder is then applied, and the
resulting mat is dried to remove any remaining water and cure the
binder. The formed non-woven mat is an assembly of dispersed,
individual glass filaments. An air-laid process is similar except
that glass fibers are dispersed in a stream of air rather than in a
water slurry.
[0007] Various attempts have been made to reduce undesirable
formaldehyde emissions from formaldehyde-based resins. For example,
various formaldehyde scavengers such as ammonia and urea have been
added to the formaldehyde-based resin in an attempt to reduce
formaldehyde emission from the insulation product. Because of its
low cost, urea is added directly to the uncured resin system to act
as a formaldehyde scavenger. The addition of urea to the resin
system produces urea-extended phenol-formaldehyde resole resins.
These resole resins can be further treated or applied as a coating
or binder and then cured. Unfortunately, the urea-extended resoles
are unstable, and because of this instability, the urea-extended
resoles must be prepared on site. In addition, the binder inventory
must be carefully monitored to avoid processing problems caused by
undesired crystalline precipitates of dimer species that may form
during storage Ammonia is not a particularly desirable alternative
to urea as a formaldehyde scavenger because ammonia generates an
unpleasant odor and may cause throat and nose irritation to
workers. Further, the use of a formaldehyde scavenger in general is
undesirable due to its potential adverse affects to the properties
of the insulation product, such as lower recovery and lower
stiffness.
[0008] In addition, previous arts have focused on the use of
polyacrylic acid with a polyhydroxy crosslinking agent or
carbohydrate-based chemistry that is linked to the Maillard
reaction. Polyacrylic acid binders, however, have several
drawbacks. For example, polyacrylic acid binders use petroleum
based materials and costs typically at least two times that of
current phenolic binder systems. In addition, the high viscosity
and different cure characteristics pose process difficulties. Also,
Maillard reaction-based products have an undesirable dark brown
color after curing. Further, the use of large amounts of ammonia
needed to make the binder presents a safety risk and possible
emission problems.
[0009] In view of the existing problems with current binders, there
remains a need in the art for a binder system that is not petroleum
dependent, has no added formaldehyde, is bio-based and
environmentally friendly, and is cost competitive.
SUMMARY OF THE INVENTION
[0010] It is an object of the present invention to provide a binder
composition for use in the formation of fiberglass insulation and
non-woven chopped strand mats that includes at least one
carbohydrate that is natural in origin and at least one
crosslinking agent. The carbohydrate and crosslinking agent form a
polyester thermoset resin. The carbohydrate may have a dextrose
equivalent (DE) from 2 to 20. Additionally, the carbohydrate may be
a water-soluble polysaccharide selected from pectin, dextrin,
maltodextrin, starch, modified starch, starch derivatives and
combinations thereof. The crosslinking agent may be selected from
polycarboxylic acids, salts of polycarboxylic acid, anhydrides,
monomeric and polymeric polycarboxylic acid with anhydride, citric
acid, salts of citric acid, adipic acid, salts of adipic acid,
polyacrylic acid, salts of polyacrylic acid, polyacrylic acid based
resins, and combinations thereof. In one or more embodiments, the
crosslinking agent may be citric acid or any monomeric or polymeric
polycarboxylic acid and their corresponding salts. In some
exemplary embodiments, the binder composition may include a
moisture resistant agent and a pH adjuster. The binder composition
is free of added formaldehyde and is environmentally friendly.
[0011] It is another object of the present invention to provide a
fibrous insulation product that includes a plurality of randomly
oriented fibers and a binder composition applied to at least a
portion of the fibers and interconnecting the fibers. The binder
includes at least one carbohydrate that is natural in origin and at
least one crosslinking agent. Typically the carbohydrate will have
reactive hydroxyl groups and the crosslinking agent will have
reactive carboxyl groups. The carbohydrate may have a dextrose
equivalent (DE) from 2 to 20. In exemplary embodiments, the
carbohydrate is a water-soluble polysaccharide selected from
pectin, dextrin, maltodextrin, starch, modified starch, starch
derivatives, and combinations thereof. The binder composition may
also include one or more members selected from a catalyst, a
coupling agent, a process aid, a crosslinking density enhancer, an
extender, a moisture resistant agent, a dedusting oil, a colorant,
a corrosion inhibitor, a surfactant, and a pH adjuster. The process
aid agent includes a polyol such as glycerol, triethanolamine,
polyethylene glycol, and pentaerythritol. In one or more
embodiment, the crosslinking agent may be citric acid or any
monomeric or polymeric polycarboxylic acid and their corresponding
salts. Additionally, in low density products (e.g., residential
insulation products), the binder has a light (e.g., white or tan)
color after it has been cured.
[0012] It is yet another object of the present invention to provide
a non-woven chopped strand mat formed of a plurality of randomly
oriented glass fibers having a discrete length enmeshed in the form
of a mat having a first major surface and a second major surface
and a binder composition at least partially coating the first major
surface of the mat. The binder includes (1) at least one
carbohydrate that is natural in origin and has a dextrose
equivalent from 2 to 20 and (2) at least one crosslinking agent.
The binder composition may also include one or more members
selected from a catalyst, a moisture resistant agent, and a pH
adjuster. In at least one exemplary embodiment, the carbohydrate is
a water-soluble polysaccharide selected from pectin, dextrin,
maltodextrin, starch, modified starch, starch derivatives and
combinations thereof. In addition, the crosslinking agent may be
selected from polycarboxylic acids, salts of polycarboxylic acid,
anhydrides, monomeric and polymeric polycarboxylic acid with
anhydride, citric acid, salts of citric acid, adipic acid, salts of
adipic acid, polyacrylic acid, salts of polyacrylic acid,
polyacrylic acid based resins, amino alcohols, sodium metaborate,
polyoxyalkyleneamines, polyamines, polyols, and combinations
thereof. The binder has a light color upon curing, is
environmentally friendly, and is free of added formaldehyde.
[0013] It is an advantage of the present invention that the
carbohydrate is natural in origin and derived from renewable
resources.
[0014] It is yet another advantage of the present invention that
maltodextrin is readily available and is low in cost.
[0015] It is a further advantage of the present invention that
insulation products and non-woven mats utilizing the inventive
binder composition can be manufactured using current manufacturing
lines, to make a variety of product shapes, densities and uses,
thereby saving time and money.
[0016] It is another advantage of the present invention that the
binder composition has no added formaldehyde.
[0017] It is also an advantage of the present invention that the
final product has a light color that allows the use of dyes,
pigments, or other colorants to yield a variety of colors for the
insulation product. Additionally, when finishing the surface of a
board product with paint or a veil of woven or non-woven fabric, it
takes less paint or fabric weight to cover these lighter colored
boards than prior boards.
[0018] It is a further advantage of the present invention that the
binder composition has a reduction in particulate emission compared
to conventional phenol/urea/formaldehyde binder compositions.
[0019] It is a feature of the present invention that the
carbohydrate polymer may have a dextrose equivalent (DE) number
from 2 to 20.
[0020] It is a feature of the present invention that the
maltodextrin can form an aqueous mixture that can be applied by
conventional binder applicators, including spray applicators.
[0021] It is a further feature of the present invention that the
binder can be acidic, neutral, or basic.
[0022] It is another feature of the present invention that the
inventive insulation products and non-woven mats have no added
formaldehyde.
[0023] It is a further advantage of the present invention that the
binder composition produces fibrous products, especially in lighter
density products, that have a softer feel to the touch, which is
advantageous to the installer or user of these fibrous
products.
[0024] It is also a feature of the invention that the inventive
binder composition can be useful for composite reinforcements, such
as chopped strands, for use in thermoplastics, thermosets, and
roofing applications. In addition, the inventive binders may be
used in both single and multi-end rovings.
[0025] The foregoing and other objects, features, and advantages of
the invention will appear more fully hereinafter from a
consideration of the detailed description that follows. It is to be
expressly understood, however, that the drawings are for
illustrative purposes and are not to be construed as defining the
limits of the invention.
BRIEF DESCRIPTION OF THE DRAWINGS
[0026] The advantages of this invention will be apparent upon
consideration of the following detailed disclosure of the
invention, especially when taken in conjunction with the
accompanying drawings wherein:
[0027] FIG. 1 is a schematic illustration of the formation of a
faced insulation product with the inventive binder composition
according to one exemplary embodiment;
[0028] FIG. 2 is a is an elevational view of a manufacturing line
for producing a fiberglass insulation product with the inventive
binder composition where the insulation product does not contain a
facing material according to another exemplary embodiment of the
present invention; and
[0029] FIG. 3 is a schematic illustration of a wet-laid processing
line for forming a chopped strand mat utilizing the inventive
binder composition according a further exemplary embodiment of the
present invention.
DETAILED DESCRIPTION AND PREFERRED EMBODIMENTS OF THE INVENTION
[0030] Unless defined otherwise, all technical and scientific terms
used herein have the same meaning as commonly understood by one of
ordinary skill in the art to which the invention belongs. Although
any methods and materials similar or equivalent to those described
herein can be used in the practice or testing of the present
invention, the preferred methods and materials are described
herein. All references cited herein, including published or
corresponding U.S. or foreign patent applications, issued U.S. or
foreign patents, and any other references, are each incorporated by
reference in their entireties, including all data, tables, figures,
and text presented in the cited references.
[0031] In the drawings, the thickness of the lines, layers, and
regions may be exaggerated for clarity. It will be understood that
when an element such as a layer, region, substrate, or panel is
referred to as being "on" another element, it can be directly on
the other element or intervening elements may also be present.
Also, when an element is referred to as being "adjacent" to another
element, the element may be directly adjacent to the other element
or intervening elements may be present. The terms "top", "bottom",
"side", and the like are used herein for the purpose of explanation
only. Like numbers found throughout the figures denote like
elements. It is to be noted that the phrase "binder", "bio-based
binder", "binder composition", and "binder formulation" may be used
interchangeably herein.
Bio-Based Binder Compositions
[0032] The present invention relates to environmentally friendly,
aqueous polyester binder compositions that contain at least one
bio-based component. In one exemplary embodiment, the bio-based
component is a carbohydrate and the binder and includes a
carbohydrate and a crosslinking agent. Typically the carbohydrate
has reactive hydroxyl groups and the crosslinking agent has
reactive carboxyl groups. In some exemplary embodiments, the
carbohydrate-based binder composition also includes a coupling
agent, a process aid agent, an extender, a pH adjuster, a catalyst,
a crosslinking density enhancer, a deodorant, an antioxidant, a
dust suppressing agent, a biocide, a moisture resistant agent, or
combinations thereof. The binder may be used in the formation of
insulation materials and non-woven chopped strand mats. In
addition, the binder is free of added formaldehyde. Further, the
binder composition has a reduction in particulate emission compared
to conventional phenol/urea/formaldehyde binder compositions. The
inventive binder may also be useful in forming particleboard,
plywood, and/or hardboards.
[0033] In one or more exemplary embodiment, the binder includes at
least one carbohydrate that is natural in origin and derived from
renewable resources. For instance, the carbohydrate may be derived
from plant sources such as legumes, maize, corn, waxy corn, sugar
cane, milo, white milo, potatoes, sweet potatoes, tapioca, rice,
waxy rice, peas, sago, wheat, oat, barley, rye, amaranth, and/or
cassava, as well as other plants that have a high starch content.
The carbohydrate polymer may also be derived from crude
starch-containing products derived from plants that contain
residues of proteins, polypeptides, lipids, and low molecular
weight carbohydrates. The carbohydrate may be selected from
monosaccharides (e.g., xylose, glucose, and fructose),
disaccharides (e.g., sucrose, maltose, and lactose),
oligosaccharides (e.g., glucose syrup and fructose syrup), and
polysaccharides and water-soluble polysaccharides (e.g., pectin,
dextrin, maltodextrin, starch, modified starch, and starch
derivatives).
[0034] The carbohydrate polymer may have a number average molecular
weight from about 1,000 to about 8,000. Additionally, the
carbohydrate polymer may have a dextrose equivalent (DE) number
from 2 to 20, from 7 to 11, or from 9 to 14. The carbohydrates
beneficially have a low viscosity and cure at moderate temperatures
(e.g., 80-250.degree. C.) alone or with additives. The low
viscosity enables the carbohydrate to be utilized in a binder
composition. In exemplary embodiments, the viscosity of the
carbohydrate may be lower than 500 cps at 50% concentration and
between 20 and 30.degree. C. The use of a carbohydrate in the
inventive binder composition is advantageous in that carbohydrates
are readily available or easily obtainable and are low in cost.
[0035] In at least one exemplary embodiment, the carbohydrate is a
water-soluble polysaccharide such as dextrin or maltodextrin. The
carbohydrate polymer may be present in the binder composition in an
amount from about 40% to about 95% by weight of the total solids in
the binder composition, from about 50% to about 95% by weight of
the total solids in the binder composition, from about 60% to about
90%, or from about 70% to about 85%. As used herein, % by weight
indicates % by weight of the total solids in the binder
composition.
[0036] In addition, the binder composition contains a crosslinking
agent. The crosslinking agent may be any compound suitable for
crosslinking the carbohydrate. In exemplary embodiments, the
crosslinking agent has a number average molecular weight greater
than 90, from about 90 to about 10,000, or from about 190 to about
4,000. In some exemplary embodiments, the crosslinking agent has a
number average molecular weight less than about 1000. Non-limiting
examples of suitable crosslinking agents include polycarboxylic
acids (and salts thereof), anhydrides, monomeric and polymeric
polycarboxylic acid with anhydride (i.e., mixed anhydrides), citric
acid (and salts thereof, such as ammonium citrate), 1,2,3,4-butane
tetracarboxylic acid, adipic acid (and salts thereof), polyacrylic
acid (and salts thereof), and polyacrylic acid based resins such as
QXRP 1734 and Acumer 9932, both commercially available from The Dow
Chemical Company. In exemplary embodiments, the crosslinking agent
may be any monomeric or polymeric polycarboxylic acid, citric acid,
and their corresponding salts. The crosslinking agent may be
present in the binder composition in an amount up to about 50% by
weight of the binder composition. In exemplary embodiments, the
crosslinking agent may be present in the binder composition in an
amount from about 5.0% to about 40% by weight of the total solids
in the binder composition or from about 10% to about 30% by
weight.
[0037] Optionally, the binder composition may include a catalyst to
assist in the crosslinking. The catalyst may include inorganic
salts, Lewis acids (i.e., aluminum chloride or boron trifluoride),
Bronsted acids (i.e., sulfuric acid, p-toluenesulfonic acid and
boric acid) organometallic complexes (i.e., lithium carboxylates,
sodium carboxylates), and/or Lewis bases (i.e., polyethyleneimine,
diethylamine, or triethylamine). Additionally, the catalyst may
include an alkali metal salt of a phosphorous-containing organic
acid; in particular, alkali metal salts of phosphorus acid,
hypophosphorus acid, or polyphosphoric acids. Examples of such
phosphorus catalysts include, but are not limited to, sodium
hypophosphite, sodium phosphate, potassium phosphate, disodium
pyrophosphate, tetrasodium pyrophosphate, sodium tripolyphosphate,
sodium hexamethaphosphate, potassium phosphate, potassium
tripolyphosphate, sodium trimetaphosphate, sodium
tetramethaphosphate, and mixtures thereof. In addition, the
catalyst or cure accelerator may be a fluoroborate compound such as
fluoroboric acid, sodium tetrafluoroborate, potassium
tetrafluoroborate, calcium tetrafluoroborate, magnesium
tetrafluoroborate, zinc tetrafluoroborate, ammonium
tetrafluoroborate, and mixtures thereof. Further, the catalyst may
be a mixture of phosphorus and fluoroborate compounds. Other sodium
salts such as, sodium sulfate, sodium nitrate, sodium carbonate may
also or alternatively be used as the catalyst/accelerator. The
catalyst or cure accelerator may be present in the binder
composition in an amount from about 0% to about 10% by weight of
the total solids in the binder composition, or from about 1.0% to
about 5.0% by weight, or from about 3.0% to about 5.0% by
weight.
[0038] The binder composition may optionally contain at least one
coupling agent. In at least one exemplary embodiment, the coupling
agent is a silane coupling agent. The coupling agent(s) may be
present in the binder composition in an amount from about 0.01% to
about 5.0% by weight of the total solids in the binder composition,
from about 0.01% to about 2.5% by weight, or from about 0.1% to
about 0.5% by weight.
[0039] Non-limiting examples of silane coupling agents that may be
used in the binder composition may be characterized by the
functional groups alkyl, aryl, amino, epoxy, vinyl, methacryloxy,
ureido, isocyanato, and mercapto. In exemplary embodiments, the
silane coupling agent(s) include silanes containing one or more
nitrogen atoms that have one or more functional groups such as
amine (primary, secondary, tertiary, and quaternary), amino, imino,
amido, imido, ureido, or isocyanato. Specific, non-limiting
examples of suitable silane coupling agents include, but are not
limited to, aminosilanes (e.g., 3-aminopropyl-triethoxysilane and
3-aminopropyl-trihydroxysilane), epoxy trialkoxysilanes (e.g.,
3-glycidoxypropyltrimethoxysilane and
3-glycidoxypropyltriethoxysilane), methacryl trialkoxysilanes
(e.g., 3-methacryloxypropyltrimethoxysilane and
3-methacryloxypropyltriethoxysilane), hydrocarbon trialkoxysilanes,
amino trihydroxysilanes, epoxy trihydroxysilanes, methacryl
trihydroxy silanes, and/or hydrocarbon trihydroxysilanes. In one or
more exemplary embodiment, the silane is an aminosilane, such as
.gamma.-aminopropyltriethoxysilane.
[0040] Further exemplary coupling agents (including silane coupling
agents) suitable for use in the binder composition are set forth
below: [0041] Acryl: 3-acryloxypropyltrimethoxysilane;
3-acryloxypropyltriethoxysilane;
3-acryloxypropylmethyldimethoxysilane;
3-acryloxypropylmethyldiethoxysilane;
3-methacryloxypropyltrimethoxysilane;
3-methacryloxypropyltriethoxysilane [0042] Amino:
aminopropylmethyldimethoxysilane; aminopropyltriethoxysilane;
aminopropyltrimethoxysilane/EtOH; aminopropyltrimethoxysilane;
N-(2-aminoethyl)-3-aminopropyltrimethoxysilane;
N-(2-aminoethyl)-3-aminopropylmethyldimethoxysilane;
(2-aminoethyl)-(2-aminoethyl) 3-aminopropyltrimethoxysilane;
N-phenylaminopropyltrimethoxysilane [0043] Epoxy:
3-Glycidoxypropylmethyldiethoxysilane;
3-glycidoxypropylmethyldimethoxysilane;
3-glycidoxypropyltriethoxysilane;
2-(3,4-epoxycyclohexyl)ethylmethyldimethoxysilane;
2-(3,4-epoxycyclohexyl)ethylmethyldiethoxysilane;
2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane;
2-(3,4-Epoxycyclohexyl)ethyltriethoxysilane [0044] Mercapto:
3-mercaptopropyltrimethoxysilane; 3-Mercaptopropyltriethoxysilane;
3-mercaptopropylmethyldimethoxysilane;
3-Mercaptopropylmethyldiethoxysilane [0045] Sulfide:
bis[3-(triethoxysilyl)propyl]-tetrasulfide;
bis[3-(triethoxysilyl)propyl]-disulfide [0046] Vinyl:
vinyltrimethoxysilane; vinyltriethoxysilane; vinyl
tris(2-methoxyethoxy)silane; vinyltrichlorosilane;
trimethylvinylsilane [0047] Alkyl: methyltrimethoxysilane;
methyltriethoxysilane; dimethyldimethoxysilane;
dimethyldiethoxysilane; tetramethoxysilane; tetraethoxysilane;
ethyltriethoxysilane; n-propyltrimethoxysilane;
n-propyltriethoxysilane; isobutyltrimethoxysilane;
hexyltrimethoxysilane; hexyltriethoxysilane; octyltrimethoxysilane;
decyltrimethoxysilane; decyltriethoxysilane; octyltriethoxysilane;
tert-butyldimethylchlorosilane; cyclohexylmethyldimethoxysilane;
dicylohexyldimethoxysilane; cyclohexylethyldimethoxysilane;
t-butylmethyldimethoxysilane [0048] Chloroalkyl:
3-chloropropyltriethoxysilane; 3-chloropropyltrimethoxysilane;
3-chloropropylmethyldimethoxysilane [0049] Perfluoro:
decafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane;
((heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane [0050]
Phenyl: phenyltrimethoxysilane; phenyltriethoxysilane;
diphenyldiethoxysilane; diphenyldimethoxysilane;
diphenyldichlorosilane [0051] Hydrolyzates of the silanes listed
above [0052] Zirconates: zirconium acetylacetonate; zirconium
methacrylate [0053] Titanates: tetra-methyl titanate; tetra-ethyl
titanate; tetra-n-propyl titanate; tetra-isopropyl titanate;
tetra-isobutyl titanate; tetra-sec-butyl titanate; tetra-tert-butyl
titanate; mono n-butyl, trimethyl titanate; mono ethyl
tricyclohexyl titanate; tetra-n-amyl titanate; tetra-n-hexyl
titanate; tetra-cyclopentyl titanate; tetra-cyclohexyl titanate;
tetra-n-decyl titanate; tetra n-dodecyl titanate; tetra (2-ethyl
hexyl) titanate; tetra octylene glycol titanate ester;
tetrapropylene glycol titanate ester; tetra benzyl titanate;
tetra-p-chloro benzyl titanate; tetra 2-chloroethyl titanate; tetra
2-bromoethyl titanate; tetra 2-methoxyethyl titanate; tetra
2-ethoxyethyl titanate.
[0054] Especially suitable titanate ester stabilizers of the
invention are proprietary titanate ester compositions manufactured
under the trade name Tyzor.RTM. by DuPont de Nemours & Co.,
Inc. Non-limiting examples include Tyzor.RTM. titanate esters sold
in the 100% form rather than as solutions, e.g., in a lower
aliphatic alcohol, such as Tyzor.RTM. TBT (tetrabutyl titanate),
Tyzor.RTM. TPT (tetraisopropyl titanate), and Tyzor.RTM. OG
(tetraoctylene glycol titanate ester).
[0055] In addition, the binder composition may include a process
aid (e.g., polyol) in addition to the carbohydrates described
above. The process aid is not particularly limiting so long as the
process aid functions to facilitate the processing of the fibers
formation and orientation. The process aid can be used to improve
binder application distribution uniformity, to reduce binder
viscosity, to increase ramp height after forming, to improve the
vertical weight distribution uniformity, and/or to accelerate
binder de-watering in both forming and oven curing process. The
process aid may be present in the binder composition in an amount
from about 0% to about 25.0% by weight, from about 1.0% to about
20.0% by weight, or from about 5.0% to about 15.0% by weight.
[0056] Examples of processing aids include viscosity modifiers
(e.g., glycerol, 1,2,4-butanetriol, 1,4-butanediol,
1,2-propanediol, 1,3-propanediol, poly(ethylene glycol) and
defoaming agents (e.g., emulsions and/or dispersions of mineral,
paraffin, or vegetable oils, dispersions of polydimethylsiloxane
(PDMS) fluids and silica which has been hydrophobized with
polydimethylsiloxane or other materials, and particles made of
amide waxes such as ethylenebis-stearamide (EBS) or hydrophobized
silica). A further process aid that may be utilized in the binder
composition is a surfactant. One or more surfactant may be included
in the binder composition to assist in binder atomization, wetting,
and interfacial adhesion.
[0057] The surfactant is not particularly limited, and includes
surfactants such as, but not limited to, ionic surfactants (e.g.,
sulfate, sulfonate, phosphate, and carboxylate); sulfates (e.g.,
alkyl sulfates, ammonium lauryl sulfate, sodium lauryl sulfate
(SDS), alkyl ether sulfates, sodium laureth sulfate, and sodium
myreth sulfate); amphoteric surfactants (e.g., alkylbetaines such
as lauryl-betaine); sulfonates (e.g., dioctyl sodium
sulfosuccinate, perfluorooctanesulfonate, perfluorobutanesulfonate,
and alkyl benzene sulfonates); phosphates (e.g., alkyl aryl ether
phosphate and alkyl ether phosphate); carboxylates (e.g., alkyl
carboxylates, fatty acid salts (soaps), sodium stearate, sodium
lauroyl sarcosinate, carboxylate fluorosurfactants,
perfluoronanoate, and perfluorooctanoate); cationic (alkylamine
salts such as laurylamine acetate); pH dependent surfactants
(primary, secondary or tertiary amines); permanently charged
quaternary ammonium cations (e.g., alkyltrimethylammonium salts,
cetyl trimethylammonium bromide, cetyl trimethylammonium chloride,
cetylpyridinium chloride, and benzethonium chloride); and
zwitterionic surfactants, quaternary ammonium salts (e.g., lauryl
trimethyl ammonium chloride and alkyl benzyl dimethylammonium
chloride), and polyoxyethylenealkylamines.
[0058] Suitable nonionic surfactants that can be used in
conjunction with this invention include polyethers (e.g., ethylene
oxide and propylene oxide condensates, which include straight and
branched chain alkyl and alkaryl polyethylene glycol and
polypropylene glycol ethers and thioethers);
alkylphenoxypoly(ethyleneoxy)ethanols having alkyl groups
containing from about 7 to about 18 carbon atoms and having from
about 4 to about 240 ethyleneoxy units (e.g.,
heptylphenoxypoly(ethyleneoxy) ethanols, and
nonylphenoxypoly(ethyleneoxy) ethanols); polyoxyalkylene
derivatives of hexitol including sorbitans, sorbides, mannitans,
and mannides; partial long-chain fatty acids esters (e.g.,
polyoxyalkylene derivatives of sorbitan monolaurate, sorbitan
monopalmitate, sorbitan monostearate, sorbitan tristearate,
sorbitan monooleate, and sorbitan trioleate); condensates of
ethylene oxide with a hydrophobic base, the base being formed by
condensing propylene oxide with propylene glycol; sulfur containing
condensates (e.g., those condensates prepared by condensing
ethylene oxide with higher alkyl mercaptans, such as nonyl,
dodecyl, or tetradecyl mercaptan, or with alkylthiophenols where
the alkyl group contains from about 6 to about 15 carbon atoms);
ethylene oxide derivatives of long-chain carboxylic acids (e.g.,
lauric, myristic, palmitic, and oleic acids, such as tall oil fatty
acids); ethylene oxide derivatives of long-chain alcohols (e.g.,
octyl, decyl, lauryl, or cetyl alcohols); and ethylene
oxide/propylene oxide copolymers.
[0059] In at least one exemplary embodiment, the surfactants are
SURFONYL.RTM. 420, SURFONYL.RTM. 440, and SURFONYL.RTM. 465, which
are ethoxylated 2,4,7,9-tetramethyl-5-decyn-4,7-diol surfactants
(commercially available from Air Products and Chemicals, Inc.
(Allentown, Pa.)), Stanfax (a sodium lauryl sulfate), Surfynol 465
(an ethoxylated 2,4,7,9-tetramethyl 5 decyn-4,7-diol), Triton.TM.
GR-PG70 (1,4-bis(2-ethylhexyl) sodium sulfosuccinate), and
Triton.TM. CF-10 (poly(oxy-1,2-ethanediyl),
alpha-(phenylmethyl)-omega-(1,1,3,3-tetramethylbutyl)phenoxy). The
surfactant may be present in the binder composition in an amount
from 0.0% to about 10% by weight of the total solids in the binder
composition, from about 0.01% to about 10% by weight, or from about
0.2% to about 5.0% by weight.
[0060] The binder composition may optionally include a corrosion
inhibitor to reduce or eliminate any potential corrosion to the
process equipment. The corrosion inhibitor can be chosen from a
variety of agents, such as, for example, hexamine, benzotriazole,
phenylenediamine, dimethylethanolamine, polyaniline, sodium
nitrite, benzotriazole, dimethylethanolamine, polyaniline, sodium
nitrite, cinnamaldehyde, condensation products of aldehydes and
amines (imines), chromates, nitrites, phosphates, hydrazine,
ascorbic acid, tin oxalate, tin chloride, tin sulfate, thiourea,
zinc oxide, and nitrile. Alternatively, the corrosion can be
reduced or eliminated by process control abatement, such as process
water neutralization, removal of corrosive ingredients, and process
water treatment to minimize the corrosivity. The corrosion
inhibitor may be present in the binder composition in an amount
from about 0% to about 15.0% by weight, from about 1.0% to about
5.0% by weight, or from about 0.2% to about 1.0% by weight.
[0061] Also, the binder composition may also contain one or more
biocide such as 3-iodo-2propyl-n-butylcarbamate, carbamic acid,
butyl-, 3-iodo-2-propynyl ester (IPBC),
2-bromo-2-nitropropane-1,3-diol, magnesium nitrate,
5-chloro-2-methyl-4-isothiazolin-3-one, magnesium chloride,
sulfamic acid, N-bromo, sodium salt, diiodomethyl-p-tolysulfone,
dibromoacetonitrile, and 2,2-dibromo-3-nitrilopropionamide to
reduce or eliminate mold and fungal growth on the fiberglass
product. The biocide may be present in the binder composition in an
amount from about 0% to about 10.0% by weight, from about 0.05% to
about 1.0% by weight, or from 0.1% to about 0.5% by weight.
[0062] Further, the binder composition may optionally include at
least one crosslinking density enhancer to improve the degree of
crosslinking of the carbohydrate based polyester binder.
Crosslinking density enhancement can be achieved by increasing
esterification between the hydroxyl and carboxylic acid groups
and/or introducing free radical linkages to improve the strength of
the thermoset resin. The esterification crosslinking density can be
adjusted by changing the ratio between hydroxyl and carboxylic acid
and/or adding additional esterification functional groups such as
triethanolamine, diethanolamine, mono ethanolamine,
1-amino-2-propanol, 1,1'-aminobis-2-propanol,
1,1,'1''nitrilotri-2-propanol, 2-methylaminoethanol,
2-dimethylaminoethanol, 2-(2-aminoethoxy)ethanol,
2{(2-aminoethyl)amino}ethanol, 2-diethylaminoethanol,
2-butylaminoethanol, 2-dibutylaminoethanol,
2cyclohexylaminoethanol, 2,2'-(methylamino)bis-ethanol,
2,2'-(butylamino)bis-ethanol, 1-methylamino-2propanol,
1-dimethylamino-2-propanol, 1-(2-aminoethylamino)-2-propanol,
1,1'-(methylimino)bis-2-propanol, 3-amino-1-propanol,
3-dimethylamino-1propanol, 2-amino-1-butanol,
1-ethylamino-2-butanol, 4-diethylamino-1-butanol,
1-diethylamino-2-butanol, 3-amino-2,2-dimethyl-1-propanol,
2,2-dimethyl-3-dimethylamino-1-propanol,
4-diethylamino-2-butyn-1-ol, 5-diethylamino-3-pentyne-2-ol, bis
(2-hydroxypropyl)amine, as well as other alkanolamines, their
mixtures, and their polymers. Another method to achieve
crosslinking density enhancement is to use both esterification and
free radical reaction for the crosslinking reactions. Chemicals
that can be used for both reactions include maleic anhydride,
maleic acid, or itaconic acid. The crosslinking density enhancer
may be present in the binder composition in an amount from about 0%
to about 25.0% by weight, from about 1.0.0% to about 20.0% by
weight, or from about 5.0% to about 15.0% by weight.
[0063] The binder may also include organic and/or inorganic acids
and bases in an amount sufficient to adjust the pH to a desired
level. The pH may be adjusted depending on the intended
application, or to facilitate the compatibility of the ingredients
of the binder composition. In exemplary embodiments, the pH
adjuster is utilized to adjust the pH of the binder composition to
an acidic pH. Examples of suitable acidic pH adjusters include
inorganic acids such as, but not limited to sulfuric acid,
phosphoric acid and boric acid and also organic acids like
p-toluenesulfonic acid, mono- or polycarboxylic acids, such as, but
not limited to, citric acid, acetic acid and anhydrides thereof,
adipic acid, oxalic acid, and their corresponding salts. Also,
inorganic salts that can be acid precursors. The acid adjusts the
pH, and in some instances, as discussed above, acts as a
crosslinking agent. Optionally, organic and/or inorganic bases,
such sodium hydroxide, ammonium hydroxide, and diethylamine, and
any kind of primary, secondary, or tertiary amine (including
alkanol amine), can be used for pH adjustment. The pH of the binder
composition, when in an acidic state, may range from about 1 to
about 6, and in some exemplary embodiments, from about 2 to about
5, including all amounts and ranges in between. In at least one
exemplary embodiment, the pH of the binder composition is about
2.5. The pH adjuster in an acidic binder composition may be present
in the binder composition in an amount sufficient to obtain the
desired pH.
[0064] The binder composition may also contain a moisture resistant
agent, such as a alum, aluminum sulfate, latex, a silicone
emulsion, a poly(organosiloxane), a hydrophobic polymer emulsion
(e.g., polyethylene emulsion or polyester emulsion), and mixtures
thereof. For clarity, a poly(organosiloxane) is a polymer of the
form --(--R.sub.1SiR.sub.2--).sub.n-- wherein at least one of
R.sub.1 and R.sub.2 is an organic radical, including, e.g. alkyl or
alkenyl, phenyl, etc. In at least one exemplary embodiment, the
latex system is an aqueous latex emulsion. The latex emulsion
includes latex particles that are typically produced by emulsion
polymerization. In addition to the latex particles, the latex
emulsion may include water, a stabilizer such as ammonia, and a
surfactant. The moisture resistant agent may be present in the
binder composition in an amount from 0% to about 20% by weight of
the total solids in the binder composition, from about 5.0% to
about 10% by weight, or from about 5.0% to about 7.0% by
weight.
[0065] Additionally, the binder may contain a dust suppressing
agent to reduce or eliminate the presence of inorganic and/or
organic particles which may have adverse impact in the subsequent
fabrication and installation of the insulation materials. The dust
suppressing agent can be any conventional mineral oil, mineral oil
emulsion, natural or synthetic oil, bio-based oil, or lubricant,
such as, but not limited to, silicone and silicone emulsions,
polyethylene glycol, as well as any petroleum or non-petroleum oil
with a high flash point to minimize the evaporation of the oil
inside the oven.
[0066] In addition, the binder may optionally include at least one
extender to improve the binder's appearance and/or to lower the
overall manufacturing cost. The extender can be an inorganic
filler, such as tin oxide or calcium carbonate or organic materials
such as lignin, lignin sulfonate, or a protein-based biomass. In
exemplary embodiments, the extender is a protein-containing
biomass. Like the carbohydrate, the protein-containing biomass is
natural in origin and is derived from renewable resources. For
instance, the protein may be derived from plant sources such as soy
(e.g., a soy flour), peanuts, sunflowers, kidney beans, walnuts, or
from other plants that have a high protein content. Alternatively,
the protein may come from animal sources such as, but not limited
to, eggs, blood, and animal tissue (e.g., beef, pork, or chicken,
as well as fish). The protein-containing biomass may contain up to
about 95% protein, and in exemplary embodiments, up to 90%, 75%, or
50% protein. As used herein, the term "protein" may be defined as a
macromolecule composed of one or more polypeptides and includes any
combination of polypeptides regardless its amino acid sequence. In
addition, the term "protein" is intended to include all possible
structures in which a protein can be obtained naturally or a
protein that has been modified to improve its reactivity. It is to
be appreciated that derivatives of natural proteins and synthetic
proteins are also included within the scope of the term "protein".
In one or more exemplary embodiment, the protein-containing biomass
is soy flour. The extender may be present in the binder composition
in an amount from about 0% to about 70.0% by weight of the total
solids in the binder composition, from about 5.0% to about 50.0% by
weight, or from about 10.0% to about 40.0% by weight.
[0067] The binder may optionally contain conventional additives
such as, but not limited to dyes, pigments, fillers, colorants, UV
stabilizers, thermal stabilizers, anti-foaming agents,
anti-oxidants, emulsifiers, preservatives (e.g., sodium benzoate),
corrosion inhibitors, and mixtures thereof. Other additives may be
added to the binder composition for the improvement of process and
product performance. Such additives include lubricants, wetting
agents, surfactants, antistatic agents, and/or water repellent
agents. Additives may be present in the binder composition from
trace amounts (such as <about 0.1% by weight the binder
composition) up to about 10.0% by weight of the total solids in the
binder composition. In some exemplary embodiments, the additives
are present in an amount from about 0.1% to about 5.0% by weight of
the total solids in the binder composition, from about 1.0% to
about 4.0% by weight, or from about 1.5% to about 3.0% by
weight.
[0068] The binder further includes water to dissolve or disperse
the active solids for application onto the reinforcement fibers.
Water may be added in an amount sufficient to dilute the aqueous
binder composition to a viscosity that is suitable for its
application to the reinforcement fibers and to achieve a desired
solids content on the fibers. In particular, the binder composition
may contain water in an amount from about 50% to about 98.0% by
weight of the total solids in the binder composition.
[0069] The binder composition may be made by dissolving or
dispersing the crosslinking agent in water to form a mixture. Next,
the carbohydrate may be mixed with the crosslinking agent in the
mixture to form the binder composition. If desired, a cure
accelerator (i.e., catalyst) may be added to the binder
composition. The binder composition may be further diluted with
water to obtain a desired amount of solids. If necessary, the pH of
the mixture may be adjusted to the desired pH level with organic
and inorganic acids and bases.
[0070] In the broadest aspect of the invention, the
carbohydrate-based binder composition is formed of a carbohydrate
(e.g., maltodextrin) and a crosslinking agent (e.g., polyacrylic
acid or citric acid). The range of components used in the inventive
binder composition according to embodiments of the invention is set
forth in Table 1.
TABLE-US-00001 TABLE 1 % By Weight Component of Total Solids
Carbohydrate 60.0-95.0 Crosslinking Agent 5.0-40.0
[0071] Aqueous binder compositions according to other exemplary
embodiments of the present invention that include a process aid
agent (e.g., glycerol) or low molecular weight carbohydrate are set
forth in Table 2.
TABLE-US-00002 TABLE 2 % By Weight Component of Total Solids
Carbohydrate 5.0-90.0 Process Aid Agent 1.0-40.0 Crosslinking Agent
5.0-40.0
[0072] Aqueous binder compositions according to further exemplary
embodiments of the present invention that include a process aid
agent and a catalyst/cure accelerator are set forth in Table 3.
TABLE-US-00003 TABLE 3 % By Weight Component of Total Solids
Carbohydrate 5.0-90.0 Process Aid Agent 1.0-40.0 Crosslinking Agent
5.0-40.0 Catalyst/Cure 1.0-5.0 Accelerator
Fibrous Products with Bio-Based Binders
[0073] In one exemplary embodiment, the binder composition is used
to form a fibrous product, typically an insulation product. Fibrous
products are generally formed of matted inorganic fibers bonded
together by a cured thermoset polymeric material. Examples of
suitable inorganic fibers include glass fibers, wool glass fibers,
and ceramic fibers. Optionally, other reinforcing fibers such as
natural fibers and/or synthetic fibers such as polyester,
polyethylene, polyethylene terephthalate, polypropylene, polyamide,
aramid, and/or polyaramid fibers may be present in the insulation
product in addition to the glass fibers. The term "natural fiber"
as used in conjunction with the present invention refers to plant
fibers extracted from any part of a plant, including, but not
limited to, the stem, seeds, leaves, roots, or phloem. Examples of
natural fibers suitable for use as the reinforcing fiber material
include basalt, cotton, jute, bamboo, ramie, bagasse, hemp, coir,
linen, kenaf, sisal, flax, henequen, and combinations thereof.
Insulation products may be formed entirely of one type of fiber, or
they may be formed of a combination of types of fibers. For
example, the insulation product may be formed of combinations of
various types of glass fibers or various combinations of different
inorganic fibers and/or natural fibers depending on the desired
application for the insulation. The embodiments described herein
are with reference to insulation products formed primarily of glass
fibers.
[0074] The term "fibrous products" is general and encompasses a
variety of compositions, articles of manufacture, and manufacturing
processes. "Fibrous products" may be characterized and categorized
by many different properties; density for example, which may range
broadly from about 0.2 pounds/cubic foot ("pcf") to as high as
about 10 pcf, depending on the product. Low density flexible
insulation batts and blankets typically have densities between
about 0.2 pcf and about 5 pcf, more commonly from about 0.3 to
about 4 pcf. Fibrous products also include higher density products
having densities from about 1 to about 10 pcf, more typically from
about 2 or 3 pcf to about 8 pcf, such as boards and panels or
formed products. Higher density insulation products may be used in
industrial and/or commercial applications, including but not
limited to metal building insulation, pipe or tank insulation,
insulative ceiling and wall panels, duct boards and HVAC
insulation, appliance and automotive insulation, etc.
[0075] Another property useful for categorization is the rigidity
of the product. Residential insulation batts are typically quite
flexible and they can be compressed into rolls or batts while
recovering their "loft" upon decompression. In contrast, other
fibrous products, such as ceiling tiles, wall panels, foundation
boards and certain pipe insulation to mention a few, are quite
rigid and inflexible by design. These products will flex very
little and are unlikely to be adapted or conformed to a particular
space.
[0076] Shape is another important property. Some fibrous products
are flexible, as noted and can be forced to assume conforming
shapes, while other are formed and shaped for a specific purpose.
In some embodiments, the shape is substantially planar, as in duct
boards, ceiling tiles and some wall insulation. In other
embodiments, the fibrous insulation product is manufactured with a
particular shape (e.g. cylindrical) suitable for a particular size
conduit, pipe or tank. In other cases, specific shapes and cutouts,
often die-cut, are included in certain appliance insulation
products, automotive insulation products and the like. Finally,
other shapes may be created with nonwoven textile insulation
products.
[0077] Other classifications of fibrous insulation products can
include the method of manufacture. The manufacture of glass fiber
insulation may be carried out in a continuous process by rotary
fiberization of molten glass, immediately forming a fibrous glass
pack on a moving conveyor, and curing the binder on the fibrous
glass insulation batt to form an insulation blanket as depicted in
FIG. 1. Glass may be melted in a tank (not shown) and supplied to a
fiber forming device such as a fiberizing spinner 15. The spinners
15 are rotated at high speeds. Centrifugal force causes the molten
glass to pass through holes in the circumferential sidewalls of the
fiberizing spinners 15 to form glass fibers. Glass fibers 30 of
random lengths may be attenuated from the fiberizing spinners 15
and blown generally downwardly, that is, generally perpendicular to
the plane of the spinners 15, by blowers 20 positioned within a
forming chamber 25. It is to be appreciated that the glass fibers
30 may be the same type of glass or they may be formed of different
types of glass. It is also within the purview of the present
invention that at least one of the fibers 30 formed from the
fiberizing spinners 15 is a dual glass fiber where each individual
fiber is formed of two different glass compositions.
[0078] The blowers 20 turn the fibers 30 downward to form a fibrous
batt 40. The glass fibers 30 may have a diameter from about 2 to
about 9 microns, or from about 3 to about 6 microns. The small
diameter of the glass fibers 30 helps to give the final insulation
product a soft feel and flexibility.
[0079] The glass fibers, while in transit in the forming chamber 25
and while still hot from the drawing operation, are sprayed with
the inventive aqueous binder composition by an annular spray ring
35 so as to result in a distribution of the binder composition
throughout the formed insulation pack 40 of fibrous glass. Water
may also be applied to the glass fibers 30 in the forming chamber
25, such as by spraying, prior to the application of the aqueous
binder composition to at least partially cool the glass fibers 30.
The binder may be present in an amount from about 1% to 30% by
weight of the total fibrous product, more usually from about 2% to
about 20% or from about 3% to about 14%. Binder content of the
fibrous products is typically measured by loss on ignition or "LOI"
of the cured product.
[0080] The glass fibers 30 having the uncured resinous binder
adhered thereto may be gathered and formed into an uncured
insulation pack 40 on an endless forming conveyor 45 within the
forming chamber 25 with the aid of a vacuum (not shown) drawn
through the fibrous pack 40 from below the forming conveyor 45. The
residual heat from the glass fibers 30 and the flow of air through
the fibrous pack 40 during the forming operation are generally
sufficient to volatilize a majority of the water from the binder
before the glass fibers 30 exit the forming chamber 25, thereby
leaving the remaining components of the binder on the fibers 30 as
a viscous or semi-viscous high-solids liquid.
[0081] The coated fibrous pack 40, which is in a compressed state
due to the flow of air through the pack 40 in the forming chamber
25, is then transferred out of the forming chamber 25 under exit
roller 50 to a transfer zone 55 where the pack 40 vertically
expands due to the resiliency of the glass fibers. The expanded
insulation pack 40 is then heated, such as by conveying the pack 40
through a curing oven 60 where heated air is blown through the
insulation pack 40 to evaporate any remaining water in the binder,
cure the binder, and rigidly bond the fibers together. Heated air
is forced though a fan 75 through the lower oven conveyor 70, the
insulation pack 40, the upper oven conveyor 65, and out of the
curing oven 60 through an exhaust apparatus 80. The cured binder
imparts strength and resiliency to the insulation blanket 10. It is
to be appreciated that the drying and curing of the binder may be
carried out in either one or two different steps. The two stage
(two-step) process is commonly known as B-staging.
[0082] Also, in the curing oven 60, the insulation pack 40 may be
compressed by upper and lower foraminous oven conveyors 65, 70 to
form a fibrous insulation blanket 10. It is to be appreciated that
the insulation blanket 10 has an upper surface and a lower surface.
In particular, the insulation blanket 10 has two major surfaces,
typically a top and bottom surface, and two minor or side surfaces
with fiber blanket 10 oriented so that the major surfaces have a
substantially horizontal orientation. The upper and lower oven
conveyors 65, 70 may be used to compress the insulation pack 40 to
give the insulation blanket 10 a predetermined thickness. It is to
be appreciated that although FIG. 1 depicts the conveyors 65, 70 as
being in a substantially parallel orientation, they may
alternatively be positioned at an angle relative to each other (not
illustrated).
[0083] The curing oven 60 may be operated at a temperature from
about 100.degree. C. to about 325.degree. C., or from about
250.degree. C. to about 300.degree. C. The insulation pack 40 may
remain within the oven for a period of time sufficient to crosslink
(cure) the binder and form the insulation blanket 10. The inventive
binder composition cures at a temperature that is lower than the
curing temperature of conventional formaldehyde binders. This lower
curing temperature requires less energy to heat the insulation
pack, and non-woven chopped strand mat described in detail below,
which results in lower manufacturing costs.
[0084] A facing material 93 may then be placed on the insulation
blanket 10 to form a facing layer 95. Non-limiting examples of
suitable facing materials 93 include Kraft paper, a
foil-scrim-Kraft paper laminate, recycled paper, and calendared
paper. The facing material 93 may be adhered to the surface of the
insulation blanket 10 by a bonding agent (not shown) to form a
faced insulation product 97. Suitable bonding agents include
adhesives, polymeric resins, asphalt, and bituminous materials that
can be coated or otherwise applied to the facing material 93. The
faced fibrous insulation 97 may subsequently be rolled for storage
and/or shipment or cut into predetermined lengths by a cutting
device (not illustrated). Such faced insulation products may be
used, for example, as panels in basement finishing systems, as
ductwrap, ductboard, as faced residential insulation, and as pipe
insulation. It is to be appreciated that, in some exemplary
embodiments, the insulation blanket 10 that emerges from the oven
60 is rolled onto a take-up roll or cut into sections having a
desired length and is not faced with a facing material 94.
Optionally, the insulation blanket 10 may be slit into layers and
by a slitting device and then cut to a desired length (not
illustrated).
[0085] A significant portion of the insulation placed in the
insulation cavities of buildings is in the form of insulation
blankets rolled from insulation products such as is described
above. Faced insulation products are installed with the facing
placed flat on the edge of the insulation cavity, typically on the
interior side of the insulation cavity. Insulation products where
the facing is a vapor retarder are commonly used to insulate wall,
floor, or ceiling cavities that separate a warm interior space from
a cold exterior space. The vapor retarder is placed on one side of
the insulation product to retard or prohibit the movement of water
vapor through the insulation product.
[0086] The presence of water, dust, and/or other microbial
nutrients in the insulation product 10 may support the growth and
proliferation of microbial organisms. Bacterial and/or mold growth
in the insulation product may cause odor, discoloration, and
deterioration of the insulation product 10, such as, for example,
deterioration of the vapor barrier properties of the Kraft paper
facing. To inhibit the growth of unwanted microorganisms such as
bacteria, fungi, and/or mold in the insulation product 10, the
insulation pack 40 may be treated with one or more anti-microbial
agents, fungicides, and/or biocides. The anti-microbial agents,
fungicides, and/or biocides may be added during manufacture or in a
post manufacture process of the insulation product 10. It is to be
appreciated that the insulation product using the inventive binder
composition can be a fiberglass batt as depicted, or as loosefill
insulation, ductboard, ductliner, or pipe wrap (not depicted in the
Figures).
[0087] Formed or shaped products may include a further step,
optionally during cure, that molds or shapes the product to its
specific final shape. Rigid boards are a type of shaped product,
the shape being planar. Other shaped products may be formed by dies
or molds or other forming apparatus. Rigidity may be imparted by
the use of higher density of fibers and/or by higher levels of
binder application. As an alternative to rotary fiberizing, some
fibrous insulation products, particularly higher density, non-woven
insulation products, may be manufactured by an air-laid or wet-laid
process using premade fibers of glass, other minerals or polymers
that are scattered into a random orientation and contacted with
binder to form the product.
[0088] In another embodiment of manufacture, the binder composition
may be used in combination with pre-manufactured fibers to form a
non-woven chopped strand mat. In particular, binder is added during
the formation of the chopped strand mat in a wet-laid or air-laid
mat processing line, where the fibers are dispersed by a water (or
air) fluid. One exemplary process of separately adding the coupling
agent to the chopped strand mat is depicted in FIG. 3. It is to be
appreciated that reference is made herein to glass fibers, although
the chopped strand mat could be formed of, or include, non-glass
fibers. Chopped glass fibers 100 may be provided to a conveying
apparatus such as a conveyor 112 by a storage container 114 for
conveyance to a mixing tank 116 that contains various surfactants,
viscosity modifiers, defoaming agents, and/or other chemical agents
with agitation to disperse the fibers and form a chopped glass
fiber slurry (not shown). The glass fiber slurry may be transferred
to a head box 118 where the slurry is deposited onto a conveying
apparatus such as a moving screen or foraminous conveyor 120 and a
substantial portion of the water from the slurry is removed to form
a web (mat) 122 of enmeshed fibers. The water may be removed from
the web 122 by a conventional vacuum or air suction system (not
shown).
[0089] The inventive binder 124 is applied to the web 122 by a
suitable binder applicator, such as the spray applicator 126 or a
curtain coater (not illustrated). Once the binder 124 has been
applied to the mat 122, the binder coated mat 128 is passed through
at least one drying oven 130 to remove any remaining water and cure
the binder composition 124. The formed non-woven chopped strand mat
132 that emerges from the oven 130 is an assembly of randomly
oriented, dispersed, individual glass fibers. The chopped strand
mat 132 may be rolled onto a take-up roll 134 for storage for later
use as illustrated. The non-woven mat can be use in roofing,
flooring, ceiling, wall applications, as filters, in ground based
vehicles, and in aircraft.
[0090] In some cases, it is even possible to use scraps of
continuous fibers, such as E-glass, and cut them to lengths
suitable for fluid-dispersed manufacturing processes. In one
embodiment of textile pipe insulation, lengths of scrap E-glass are
cut ranging from about 0.5 to about 6 inches, nominally about 2
inches in length. These are dispersed by a fluid (water or air),
the fluid is removed, and the fibers are sprayed with a bio-based
binder which is cured as before.
[0091] Some exemplary fibrous products that can be manufactured
using the bio-based binders according to the invention include
those illustrated in Table A below.
TABLE-US-00004 TABLE A Bio-based binder formulations for
representative products* Flexible Metal Warm Duct Building &
Dry Ceiling Tile boards Media Insulation boards A B C Maltodextrin
65-70 65-70 65-70 65-70 45-50 55-60 Citric Acid 25-30 25-30 25-30
25-30 30-35 25-30 Sodium 2-5 2-5 2-5 2-5 2-5 2-5 hypophosphite
Glycerol 10-15 Polyglycol 7-10 Surfactant (e.g. 0.1- 0.1- 0.1- 0.1-
SURFYNOL 465) 0.3% 0.3% 0.3% 0.3% Organopolysiloxane Up to Up to
0.4- Up to Up to Up to moisture resistance 0.5% 0.5% 0.5% 0.5% 0.5%
0.5% additive (e.g. Polon MR) *In Table A above, each ingredient of
the binder composition is given as a range of typical values of
percentage of dry weight of the binder composition.
[0092] Whereas examples 4, 5, 7, and 12 relate to flexible, light
density residential insulation, examples 8, 9 and 10 further
illustrate commercial fibrous products other than the typical
flexible residential insulation. A more complete listing of
non-residential insulation fibrous products that can be
manufactured using a bio-based binder composition according to the
invention is set forth in Table B, below.
TABLE-US-00005 TABLE B Selected Commercial and Industrial Fibrous
Products which may use a Bio-Based Binder Flexible, Light Density
Rigid Pipe Insulation Textile E-glass Rigid Boards Insulation and
pipe rolls Nonwoven Density Wide range of densities- Light density
- Ranging Ranging from 3-6 pcf Ranging from 0.8 to 4 pcf from 1.5
to 10 pcf from 0.3 to 4.0 pcf Binder content about 2 to about 20%
LOI about 2 to about 13% LOI about 3 to about 15% LOI about 5 to
about 20% LOI Manufacturing Rotary fiber forming Rotary fiber
forming Rotary fiber forming Air-laid nonwoven process method
process process process plus on or offline molding/pipe formation
process Exemplary QUIET R Duct Board Certified R Metal Building
EVOLUTION Paper-Free QUIET R Textile Duct Owens Corning QUIET R
Duct Liner Insulation ASJ Liner Products Board ELAMINATOR .RTM.
Pre-Engineered VAPORWICK Insulation DURAFLEX 700 Series Insulation
Metal Roof Insulation FIBERGLAS .TM. Pipe and Transportation
Insul-Quick Insulation MBI Plus Tank Insulation rolls SCR
Insulation Board Metal Bldg Utility Blanket Curtainwall Unfaced
Metal Building Insulation QuietZone Shaftwall for Canada Warm -N
-Dri Flexible Duct Media Insulation Energy Board QUIET R Rotary
Duct Liner TremDrain SOFTR Duct Wrap FRK Exterior Foundation TIW
Types I and II Barrier Board FLEX-Wrap for pipes and tanks Ceiling
Board Blanks H2V Series RA Series Select Sound Thermorange
FlameSpread 25 Sonobatts Thermal Batts
[0093] There are numerous advantages provided by the inventive
binder formulations. For example, unlike conventional
urea-formaldehyde binders, inventive binders have a light color
after curing (in low density products). In addition, the
carbohydrate is natural in origin and derived from renewable
resources. By lowering or eliminating formaldehyde emission, the
overall volatile organic compounds (VOCs) emitted in the workplace
are reduced. Additionally, because carbohydrates are relatively
inexpensive, the insulation product or chopped fiber mat can be
manufactured at a lower cost. Further, the binder has low to no
odor, making it more desirable to work with.
[0094] Having generally described this invention, a further
understanding can be obtained by reference to certain specific
examples illustrated below which are provided for purposes of
illustration only and are not intended to be all inclusive or
limiting unless otherwise specified.
EXAMPLES
Example 1
[0095] The binder formulations set forth in Table 4 were utilized
to form handsheets in the manner described in detail below. The
nonwoven fiberglass handsheets were dried and cured for three
minutes at 400.degree. F. The tensile strength, the Loss on
Ignition (LOI), and the tensile strength divided by the LOI
(tensile strength/LOI) for each sample was determined under ambient
and steam conditions. The tensile strength was measured using
Instron. The loss on ignition (LOI) of the reinforcing fibers is
the reduction in weight experienced by the fibers after heating
them to a temperature sufficient to burn or pyrolyze the organic
size from the fibers. The loss on ignition was measured according
to the procedure set forth in TAPPI T-1013 OM06, Loss on Ignition
of Fiberglass Mats (2006). To place the handsheet in a steam
environment, the handsheets were placed in an autoclave at
240.degree. F. at a pressure between 400 and 500 psi for 30
minutes.
[0096] The handsheets were made according to the following
procedure. First water is added to a bucket (approximately 5
liters). To this water, 8 drops of NALCO dispersant 01NM 159 was
added. A pneumatic stirrer was lowered into the bucket and set at a
slow speed so as to stir but not produce foam. To this stirring
mixture, wet chop glass fibers (8 grams) were added and allowed to
stir for 5 minutes. A screen catch was placed in a
12.times.12.times.12 inch 40 liter Williams standard pulp testing
apparatus (a.k.a. a decide box) and the box was closed. The deckle
box was then filled with water to the "3" mark and a plate stirrer
was placed in the deckle box. To the water in the decide box, a
0.5% wt. solution of polyacrylamide, NALCO 7768, (80 grams) was
added and mixed until dissolved using the plate stirrer. After the
glass fiber water had stirred for 5 minutes, a 0.5% wt. solution of
polyacrylamide, NALCO 7768 (80 grams) was added and stirred at low
speed for one minute, after which the stirring speed was set to the
highest setting and allowed to stir for an additional 2 minutes.
The glass fiber solution is then immediately dumped into the deckle
box and stirred with the plate stirrer for 10 rapid strokes. At
this point, the valve on the decide box was depressed until the
deckle box was empty. After the decide box was drained, the box was
opened and the screen with the handsheet was removed from the base
by holding opposite corners of the screen. The screen was then
placed on a wooden frame and the bio-based binder was applied to
the handsheet using a roll coater. Excess binder was then vacuumed
off. The binder-coated handsheet was placed into an oven for curing
and cut into one inch strips. These strips were placed in a
desiccator overnight.
[0097] The results of this experiment are set forth in Table 5. It
is to be noted that the weights in Table 4 are expressed in grams
(g).
TABLE-US-00006 TABLE 4 Sample Sample Sample Sample Sample 1 3 4 5 6
(10% Sample (20% (20% (20% (15% Acumer 2 Acumer Acumer Acumer
Acumer Component 9932) (Control) 9932) 9932) 9932) 9932)
Maltodextrin 79.9 (DE 11.0) Maltodextrin 79.9 (DE 18.0)
Maltodextrin 89.8 79.9 84.9 (DE 7.5) gamma- 13.7 9.1 13.7 13.7 13.7
13.7 aminopropyl- trihydroxy- silane (1.24% solution) Acumer 20.8
41.7 41.7 41.7 31.2 9932/Cross- linking Agent.sup.(1) Acrylic 127.8
Binder QRXP 1734.sup.(2) Water 675.7 663.1 664.8 664.8 664.8 670.2
Total (g) 800 800 800 800 800 800 .sup.(1)Acumer 9932: a
polyacrylic acid resin (46% solids) commercially available from The
Dow Chemical Company. .sup.(2)QXRP 1734: a polyacrylic acid resin
commercially available from The Dow Chemical Company.
TABLE-US-00007 TABLE 5 Sample Sample Sample Sample Sample Sample 1
2 3 4 5 6 Tensile Strength 20.7 30.4 20.9 20.6 29.3 26.1 (lbf) LOI
(%) 9.7 8.4 9.3 9.5 11.0 11.3 Tensile/LOI 2.1 3.6 2.3 2.2 2.7 2.3
After Steam aging 18.9 16.2 19.9 16.2 22.6 26.1 Tensile Strength
(lbf) After Steam 9.9 9.5 9.8 9.4 10.5 11.3 aging LOI (%) After
Steam aging 1.9 1.7 2.0 1.7 2.2 2.3 Tensile/LOI
[0098] From the data set forth in Tables 4 and 5, it was concluded
that the binder formulations demonstrated equal or better tensile
strengths compared to tensile strengths of current commercially
available products.
Example 2
[0099] The binder formulations set forth in Table 6 were utilized
to form handsheets according to the procedure set forth in Example
1. The nonwoven fiberglass handsheets were dried and cured for
three minutes at 400.degree. F. The tensile strength, the loss on
ignition (LOI), and the tensile strength divided by the LOI
(tensile strength/LOI) for each sample was determined under ambient
and steam conditions. The steam conditions were identical to that
set forth in Example 1. In addition, the loss on ignition and
tensile strength of each the samples were measured according to the
procedures described in Example 1. The results are set forth in
Table 7. It is to be noted that the weights in Table 6 are
expressed in grams (g).
TABLE-US-00008 TABLE 6 Sample 1 Sample 3 Sample 4 10% 20% 20%
Citric Acid Sample 2 Citric Acid Citric Acid Component 5% SHP
Control 5% SHP 5% SHP Maltodextrin 79.9 (DE 11.0) Maltodextrin 79.9
(DE 18.0) Maltodextrin 89.8 (DE 7.5) gamma-amino- 13.7 13.7 13.7
13.7 propyltri- hydroxy- silane (1.24% solution) Citric 9.6 19.2
19.2 Acid/Cross- linking Agent Acrylic Binder 191.7 QRXP
1734.sup.(1) Sodium 4.8 4.8 4.8 4.8 Hypophosphite (SHP) Water 682.1
589.9 682.5 682.5 Total (g) 800 800 800 800 .sup.(1)QXRP 1734: a
polyacrylic acid resin commercially available from The Dow Chemical
Company.
TABLE-US-00009 TABLE 7 Sample 2 Sample 1 Control Sample 3 Sample 4
Tensile Strength (lbf) 16.56 23.31 20.40 20.76 LOI (%) 9.12 7.20
7.99 8.69 Tensile/LOI 1.82 3.24 2.55 2.39 After Steam aging 15.67
13.01 13.03 14.86 Tensile Strength (lbf) After Steam aging 9.73
7.54 8.78 9.11 LOI (%) After Steam aging 1.61 1.73 1.48 1.63
Tensile/LOI
[0100] From the data presented in Tables 6 and 7, it was concluded
that binder formulations containing maltodexrin having different
Dextrose Equivalents (DE) achieved tensile strengths, LOIs, and
LOIs after steam aging that were better than or comparable to
commercially available products.
Example 3
[0101] The binder formulations set forth in Table 8 were utilized
to form handsheets according to the procedure set forth in Example
1. The nonwoven fiberglass handsheets were dried and cured for
three minutes at 400.degree. F. The tensile strength, the LOI, and
the tensile strength/LOI for each sample were determined under
ambient and steam conditions. The steam conditions were identical
to that set forth in Example 1. In addition, the loss on ignition
and tensile strength of each the samples were measured according to
the procedures described in Example 1. The results are set forth in
Table 9. It is to be noted that the weights in Table 8 are
expressed in grams (g).
TABLE-US-00010 TABLE 8 Sample 2 70:30 Sample 5 Sample 1 MD-CA
Sample 3 Sample 4 70:30 70:30 w/5% SHP 70:30 70:30 MD-CA MD-CA and
10% MD-CA MD-CA w/3% Li- Component w/5% SHP H.sub.3PO.sub.4 w/4%
H.sub.3PO.sub.2 w/5% AlCl.sub.3 Carboxylate Maltodextrin 45.1 42.6
46.0 45.1 52.0 (DE 11.0) Citric Acid 19.3 14.2 19.2 19.3 23.3
gamma- 10.2 11.2 10.3 10.2 11.5 aminopropyl- trihydroxy- silane
(1.24% solution) Catalyst 4.1 4.5 (Sodium Hypophosphite) Catalyst
8.5 (85% H3PO4) Catalyst 5.2 (50% H3PO2) Catalyst 6.1 (55.2%
AlCl.sub.3) Lithium 4.1 Carboxylate (50% conc.) Water (g) 721.3
719.0 719.3 719.3 710.1 **MD = maltodextrin, CA = citric acid, SHP
= sodium hypophosphite
TABLE-US-00011 TABLE 9 Sample Sample Sample Sample Sample 1 2 3 4 5
Tensile 14.40 11.87 11.08 6.54 15.94 Strength (lbf) LOI (%) 6.27
6.28 6.42 5.31 4.87 Tensile/LOI 2.30 1.89 1.73 1.23 3.28 After
Steam 7.81 5.98 7.84 2.93 10.63 aging Tensile Strength (lbf) After
Steam 6.95 6.27 6.80 5.44 5.33 aging LOI (%) After Steam 1.12 0.95
1.15 0.54 1.99 aging Tensile/LOI
[0102] From the data set forth in Tables 8 and 9, it was concluded
that bio-based binder formulations containing different catalysts
achieved tensile strengths comparable to that of current
commercially available products.
Example 4
[0103] The binder formulations set forth in Table 10 were utilized
to form R-19 fiberglass insulation batts in a manner known by those
of skill in the art. The R-19 fiberglass insulation batts had a
target 6% LOI and were cured at 510.degree. F. The mechanical
properties of the batts at the end of the line were determined
under ambient conditions. The results are set forth in Table
11.
TABLE-US-00012 TABLE 10 Sample 1 Sample 2 Sample 4 90:10 80:20
Sample 3 70:30 MD-CA MD-CA 80:20 MD-CA Component w/5% SHP w/5% SHP
MD-PA w/5% SHP Maltodextrin 76 lbs 37 lbs 66 lbs 32 lbs gamma- 0.6
lbs 0.3 lbs 0.6 lbs 0.3 lbs aminopropyl- trihydroxy-silane (24.8%
solution) Citric Acid 8.5 lbs .sup. 9 lbs -- 14 lbs Acrylic Binder
-- -- 36 lbs -- (Acumer 9932).sup.(1) Sodium 4.2 lbs 2.3 lbs -- 2.3
lbs Hypophosphite Oil Emulsion 31.5 lbs 17 lbs 31 lbs 17 lbs (50%)
Water 1080.2 lbs 583.4 lbs 1040.4 lbs 586.4 lbs Total 1201 lbs.sup.
649 lbs 1174 lbs 652 lbs .sup.(1)Acumer 9932: a polyacrylic acid
resin (46% solids) commercially available from The Dow Chemical
Company. **MD = maltodextrin, CA = citric acid, PA = polyacrylic
acid, SHP = sodium hypophosphite
TABLE-US-00013 TABLE 11 Phenol/Urea/ Sample Sample Sample Sample
Formaldehyde 1 2 3 4 (Control) Thickness 6.4 6.3 6.3 6.2 6.2
Recovery (in) Stiffness/Sag 23 19 35 15 18 (degree)
[0104] From the data presented in Tables 10 and 11, it was
concluded that binder formulations containing maltodextrin with
polyacrylic acid or different ratios of maltodextrin and citric
acid could be cured under typical manufacturing conditions and
achieved product performance comparable to that of current
commercially available products.
Example 5
[0105] The binder formulations set forth in Table 12 were utilized
to form R-19 fiberglass insulation batts in a conventional manner
known by those of skill in the art. The R-19 fiberglass insulation
batts had a target loss on ignition (LOI) of 6%. The mechanical
properties of the batts were determined under ambient conditions.
The results are set forth in Table 13.
TABLE-US-00014 TABLE 12 Sample 1 Sample 2 Sample 3 Sample 4
70:20:10 60:20:20 60:30:10 50:30:20 MD-CA-G MD-CA-G MD-CA-G MD-CA-G
Component w/5% SHP w/5% SHP w/5% SHP w/5% SHP Maltodextrin 65.8 lbs
56.4 lbs 56.4 lbs 47.0 lbs (50% Solids) Citric Acid 18.8 lbs 18.8
lbs 28.2 lbs 28.2 lbs (50% Solids) Sodium Hypo- 5.66 lbs 5.66 lbs
5.66 lbs 5.66 lbs phosphite (41.5% Solids) Glycerol 4.70 lbs 9.40
lbs 4.70 lbs 9.40 lbs Oil Emulsion 4.24 lbs 4.24 lbs 4.24 lbs 4.24
lbs (50% Solids) gamma- 0.37 lbs 0.37 lbs 0.37 lbs 0.37 lbs
aminopropyl- trihydroxy- silane (24.8% solution) Water 545.6 lbs
550.3 lbs 545.6 lbs 550.3 lbs ** MD = maltodextrin, G = glycerol,
CA = citric acid, SHP = sodium hypophosphite
TABLE-US-00015 TABLE 13 Sample 1 Sample 2 Sample 3 Sample 4 80:20
70:10:20 60:20:20 60:10:30 50:20:30 MDCA MD-G-CA MD-G-CA MD-G-CA
MD-G-CA w/5% SHP w/5% SHP w/5% SHP w/5% SHP w/5% SHP Thickness 5.86
6.05 5.82 5.56 5.55 Recovery (in) Stiffness/Sag 40 43 43 33 34
(degree) ** MD = maltodextrin, CA = citric acid, G = glycerol, SHP
= sodium hypophosphite
[0106] It was concluded from the data set forth in Tables 12 and 13
that binder formulations containing process aid agents (e.g.,
glycerin) at varying levels achieved product performance comparable
to that of current commercially available products. It was also
observed that the uncured blanket ramp height before entering the
oven was improved proportional to the percent of glycerin present
in the binder composition. For example, the ramp height increased
from 15% to 50% as the percent of glycerin present in the
composition was raised from 5% to 15%.
Example 6
[0107] The binder formulations set forth in Tables 14 and 16 were
utilized to form handsheets according to the procedure set forth in
Example 1. The nonwoven fiberglass handsheets were dried and cured
for three minutes at 400.degree. F. The tensile strength, the LOI,
and the tensile strength/LOI for each sample was determined under
ambient and steam conditions. The steam conditions were identical
to that set forth in Example 1. In addition, the loss on ignition
and tensile strength of each the samples were measured according to
the procedures described in Example 1. The results are set forth in
Tables 15 and 17. It is to be noted that the weights in Tables 15
and 17 are expressed in grams (g).
TABLE-US-00016 TABLE 14 Sample 1 Sample 2 Sample 3 Sample 4 80:20
70:20:10 75:20:5 70:20:10 MD-CA MD-CA-TEOA MD-CA-TEOA MD-CA-DEOA
Component w/5% SHP w/5% SHP w/5% SHP w/5% SHP Maltodextrin 116.14
101.62 108.88 101.62 (50% Solids) Citric Acid 14.52 14.52 14.52
14.52 (100% Solids) Sodium 8.75 8.75 8.75 8.75 Hypophosphite (41.5%
Solids) Triethanolamine 7.26 3.63 (100% Solids) Diethanolamine 7.26
(100% Solids) gamma- 11.47 11.47 11.47 11.47 aminopropyl-
trihydroxy-silane (1.24% solution) Water 749.13 756.39 752.76
756.39 Total (g) 900 900 900 900 ** MD = maltodextrin, CA = citric
acid, TEOA = Triethanolamine, DEOA = Diethanolamine, SHP = sodium
hypophosphite
TABLE-US-00017 TABLE 15 Sample 1 Sample 2 Sample 3 Sample 4 Tensile
15.7 16.5 15.9 14.6 Strength (lbf) LOI (%) 5.74 5.52 5.27 4.79
Tensile/LOI 2.74 3.00 3.03 3.06
TABLE-US-00018 TABLE 16 Sample 7 Sample 8 Sample 6 60:30:10 65:30:5
Sample 9 Sample 10 70:30 MD-CA- MD-CA- 60:30:10 65:30:5 MD-CA TEOA
TEOA MD-CA- MD-CA- Component w/5% SHP w/5% SHP w/5% SHP TEOA TEOA
Maltodextrin 101.62 87.10 94.36 91.46 99.08 (50% Solids) Citric
Acid 21.78 21.78 21.78 22.86 22.86 (100% Solids) Sodium 8.75 8.75
8.75 Hypophosphite (41.5% Solids) Triethanolamine 7.26 3.63 7.62
3.81 (100% Solids) Diethanolamine (100% Solids) gamma- 11.47 11.47
11.47 11.47 11.47 aminopropyl- trihydroxy- silane (1.24% solution)
Water 756.39 763.64 760.01 766.58 762.77 Total (g) 900 900 900 900
900 ** MD = maltodextrin, CA = citric acid, TEOA = Triethanolamine,
DEOA = Diethanolamine, SHP = sodium hypophosphite
TABLE-US-00019 TABLE 17 Sample 6 Sample 7 Sample 8 Sample 9 Sample
10 Tensile 15.5 19.1 18.9 16.3 18.2 Strength (lbf) LOI (%) 5.20
5.11 4.95 6.00 6.55 Tensile/LOI 2.99 3.74 3.83 3.27 2.78
[0108] From the data set forth in Tables 14-17, it was concluded
that binder formulations containing alkanol amine added as a
crosslinking enhancer achieved tensile strengths and LOIs
comparable to or better than that of current commercially available
products.
Example 7
[0109] The binder formulations set forth in Table 18 and Table 20
were utilized to form R-21 fiberglass insulation batts in a
conventional manner known by those of skill in the art. The R-21
fiberglass insulation batts had a target loss on ignition (LOI) of
5.5%. The mechanical properties of the batts at the end of the line
were determined under ambient conditions. The results are set forth
in Tables 19 and 20.
TABLE-US-00020 TABLE 18 Sample 1 Sample 2 Sample 3 Sample 4 Sample
5 80:20 70:30 60:40 60:30:10 60:30:5:5 MD-CA MD-CA MD-CA MD-CA-G
MD-CA-G-TEOA Component w/5% SHP w/5% SHP w/5% SHP w/5% SHP w/5% SHP
Maltodextrin 258.7 lbs 226.4 lbs 194.0 lbs 194.0 lbs 194.0 lbs (68%
Solids) Citric Acid 88.0 lbs 131.9 lbs 175.9 lbs 131.9 lbs 131.9
lbs (50% Solids) Sodium 26.5 lbs 26.5 lbs 26.5 lbs 26.5 lbs 26.5
lbs Hypophosphite (41.5% Solids) Glycerol 22.0 lbs 11.0 lbs (100%
Solids) Triethanolamine 11.0 lbs (100% Solids) Diethanolamine (85%
Solids) Oil Emulsion 68.4 lbs 68.4 lbs 68.4 lbs 68.4 lbs 68.4 lbs
(50% Solids) gamma- 34.6 lbs 34.6 lbs 34.6 lbs 34.6 lbs 34.6 lbs
aminopropyl- trihydroxy- silane (1.24% solution) Water 2228.5 lbs
2218.9 lbs 2209.3 lbs 2227.4 lbs 2227.4 lbs ** MD = maltodextrin,
CA = citric acid, G = glycerol, TEOA = Triethanolamine, DEOA =
Diethanolamine, SHP = sodium hypophosphite
TABLE-US-00021 TABLE 19 Sample 1 Sample 2 Sample 3 Sample 4 Sample
5 Stiffness/Sag 13.60 9.63 9.65 10.68 11.23 (degree)
TABLE-US-00022 TABLE 20 Sample 6 Sample 8 Sample 9 60:30:10 Sample
7 60:30:10 65:30:5 Sample 10 MD-CA-TEOA 60:30:10 MD-CA-DEOA
MD-CA-DEOA 67:33 Component w/5% SHP MD-CA-TEOA w/5% SHP w/5% SHP
MD-CA Maltodextrin 194.0 lbs 203.7 lbs 194.0 lbs 210.2 lbs 226.4
lbs (68% Solids) Citric Acid 131.9 lbs 138.5 lbs 131.9 lbs 131.9
lbs 153.9 lbs (50% Solids) Sodium 26.5 lbs 26.5 lbs 26.5 lbs
Hypophosphite (41.5% Solids) Glycerol (100% Solids) Triethanolamine
22.0 lbs 23.1 lbs (100% Solids) Diethanolamine 25.9 lbs 12.9 lbs
(85% Solids) Oil Emulsion 68.4 lbs 68.4 lbs 68.4 lbs 68.4 lbs 68.4
lbs (50% Solids) gamma- 34.6 lbs 34.6 lbs 34.6 lbs 34.6 lbs 34.6
lbs aminopropyl- trihydroxy-silane (1.24% solution) Water 2227.4
lbs 2234.9 lbs 2224.2 lbs 2221.6 lbs 2224.9 lbs ** MD =
maltodextrin, CA = citric acid, G = glycerol, TEOA =
Triethanolamine, DEOA = Diethanolamine, SHP = sodium
hypophosphite
TABLE-US-00023 TABLE 21 Sample 6 Sample 7 Sample 8 Sample 9 Sample
10 Stiffness/Sag 11.85 12.28 9.82 9.85 12.11 (degree)
[0110] As shown in Tables 18-21, the addition of glycerol,
diethanolamine, and/or triethanolamine to the bio-based binder
yielded fiberglass insulation products having good performance
properties, such as acceptable stiffness/sag. In addition, binder
formulations containing a blend of maltodextrin and citric acid
without the presence of a catalyst cured under typical
manufacturing conditions and produced acceptable stiffness/sag
performance.
Example 8
[0111] The binder formulations set forth in Table 22 were utilized
to form fiberglass 5 pcf, 1 inch thick ceiling boards in a
conventional manner known by those of skill in the art. The ceiling
boards had a target loss on ignition (LOI) of 13%. The mechanical
properties of the ceiling boards were determined under ambient
conditions. The results are set forth in Table 23. Comparative
Samples 1-3 are presented in Table 22 and Sample 4, the Control in
this experiment, although not specifically identified in Table 22,
is an Owens Corning 5 pound-per-cubic-foot (pcf) 1 inch thick
ceiling board, a commercially available product.
TABLE-US-00024 TABLE 22 Bio-Based Binder Formulation for 5
pound-per- cubic-foot (pcf), 1 inch thick ceiling boards Sample 1
Sample 2 Sample 3 70:30 50:35:15 60:30:10 MD-CA MD-CA-G MD-CA-TEOA
Component w/5% SHP w/5% SHP w/5% SHP Maltodextrin 709. lbs 506.5
lbs 607.8 lbs (50% Solids) Citric Acid 303.9 lbs 354.5 lbs 303.9
lbs (50% Solids) Sodium 61.0 lbs 61.0 lbs 61.0 lbs Hypophosphite
(41.5% Solids) Glycerol 76.0 lbs (100% Solids) Triethanolamine 50.6
lbs (100% Solids) Surfynol 465 1.1 lbs 1.1 lbs 1.1 lbs (100%
Solids) Oil Emulsion 56.4 lbs 56.4 lbs 56.4 lbs (50% Solids) gamma-
4.0 lbs 4.0 lbs 4.0 lbs aminopropyl- trihydroxy- silane (24.8%
solution) Water 1384.3 lbs 1447.1 lbs 1426.2 lbs ** MD =
maltodextrin, CA = citric acid, G = glycerol, TEOA =
Triethanolamine, SHP = sodium hypophosphite
TABLE-US-00025 TABLE 23 Product Performance for 5 pcf, 1 inch thick
ceiling boards Sample 1 Sample 2 Sample 3 Sample 4 70:30 50:35:15
60:30:10 Phenol/Urea/ MD-CA MD-CA-G MD-CA-TEOA Formaldehyde w/5%
SHP w/5% SHP w/5% SHP (Control).sup.(1) Flex Modulus (ksi) 1931
2080 2000 1946 Compressive 37.1 32.5 37.1 31.1 Load @ 10%
Deformation (lbs) .sup.(1)Owens Corning 5 pound-per-cubic-foot
(pcf) 1 inch thick ceiling board, a commercially available
product.
[0112] As shown in Tables 22 and 23, the bio-based binder produced
ceiling boards having good performance properties, such as improved
(or equivalent) flexural modulus and improved compressive load
deformation.
Example 9
[0113] The binder formulations set forth in Table 24 were utilized
to form R-6 fiberglass flexible duct media (FDM) in a conventional
manner known by those of skill in the art. The flexible duct media
had a target LOI of 6%. The mechanical properties of the flexible
duct media were determined under ambient conditions. The results
are set forth in Table 25.
TABLE-US-00026 TABLE 24 Bio-Based Binder Formulation for Flexible
Duct Media Sample 1 70:30 MD-CA Component w/5% SHP Maltodextrin
(50% Solids) 529.9 lbs Citric Acid (50% Solids) 227. lbs Sodium
Hypophosphite 45.6 lbs (41.5% Solids) Red Dye (35% Solids) 9.2 lbs
Oil Emulsion (50% Solids) 106.9 lbs gamma-aminopropyl-trihydroxy-
59.6 lbs silane (24.8% solution) Water 3567.2 lbs ** MD =
maltodextrin, CA = citric acid, SHP = sodium hypophosphite
TABLE-US-00027 TABLE 25 Product Performance for R-6 Flexible Duct
Media Insulation Sample 1 Owens Corning R-6 Phenol/ 70:30
Urea/Formaldehyde Flexible MD-CA Duct Media Insulation w/5% SHP
(Control) Tensile Strength (lbf) 17 20
[0114] As shown in Tables 24 and 25, the bio-based produced R-6
flexible duct media insulation that possessed a tensile strength
comparable to that of an existing R-6 flexible duct media
insulation commercial product.
Example 10
[0115] The binder formulations set forth in Table 26 were utilized
to form R-13 fiberglass metal building insulation (MBI) in a
conventional manner known by those of skill in the art. The ceiling
boards had a target LOI of 6.5%. The mechanical properties of the
metal building insulation were determined under ambient conditions.
The results are set forth in Table 27.
TABLE-US-00028 TABLE 26 Bio-Based Binder Formulation for Metal
Building Insulation Sample 1 70:30 MD-CA Component w/5% SHP
Maltodextrin (50% Solids) 463.9 lbs Citric Acid (50% Solids) 198.8
lbs Sodium Hypophosphite 39.9 lbs (41.5% Solids) Red Dye (35%
Solids) 7.3 lbs Oil Emulsion (50% Solids) 84.9 lbs
gamma-aminopropyl-trihydroxy- 52.2 lbs silane (24.8% solution)
Water 1806 lbs ** MD = maltodextrin, CA = citric acid, SHP = sodium
hypophosphite
TABLE-US-00029 TABLE 27 Product Performance for R-13 Metal Building
Insulation Sample 1 Owens Corning R-13 Phenol/ 70:30
Urea/Formaldehyde Metal MD-CA Building Insulation w/5% SHP
(Control) Thickness (in) 4.64 4.66
[0116] As shown in Tables 26 and 27, the bio-based binder produced
R-13 metal building insulation that had a thickness comparable to
that of a commercially available R-13 metal building insulation
product.
Example 11
[0117] Surface tensions of the bio-based binders containing
surfactants to lower the binder surface tension, to improve binder
spray atomization, to improve binder distribution uniformity, and
to improve binder wetting and moving of the binder to fiber-fiber
junctions were compared with a phenol/urea/formaldehyde binder
standard. Surface tensions of the inventive bio-based binder
compositions were measured using a Surface Tensionmeter 6000
(manufactured by the SensaDyne Instrument Division of the Chem-Dyne
Research Group). The instrument was calibrated with deionized
water. Data was recorded every 5 seconds. After the system was
stabilized and the testing had begun, the average value over a
one-minute testing period was obtained for each sample. The results
are set forth in Table 28.
TABLE-US-00030 TABLE 28 Surface tension of the bio-based binder and
surfactant addition % on Surface Binder Mixture binder Tension (10%
total solids) Surfactant solids (dyne/cm) phenol/urea/ None None
72.0 formaldehyde (Control) 80:20 MD-CA w/5% SHP None None 77.7
80:20 MD-CA w/5% SHP Stanfax.sup.(1) 0.1 46.0 0.3 41.3 0.5 41.9
80:20 MD-CA w/5% SHP Surfynol 465.sup.(2) 0.1 51.0 0.3 49.4 0.5
46.2 80:20 MD-CA w/5% SHP Triton .TM. 0.1 35.6 GR-PG70.sup.(3) 0.3
31.3 0.5 30.1 80:20 MD-CA w/5% SHP Sodium Dodecyl- 0.1 60 Sulfate
0.3 51.9 0.5 50.8 80:20 MD-CA w/5% SHP Triton .TM. 0.1 39.1 CF-10
0.3 39.3 0.5 40 .sup.(1)Stanfax - sodium lauryl sulfate
.sup.(2)Surfynol 465 - ethoxylated 2,4,7,9-tetramethyl 5
decyn-4,7-diol .sup.(3)Triton .TM. GR-PG70 - 1,4-bis(2-ethylhexyl)
sodium sulfosuccinate .sup.(4)Triton .TM. CF-10 -
poly(oxy-1,2-ethanediyl),
alpha-(phenylmethyl)-omega-(1,1,3,3-tetramethylbutyl)phenoxy ** MD
= maltodextrin, CA = citric acid, SHP = sodium hypophosphite
[0118] It was concluded from observing the results set forth in
Table 28 that the surface tension of the bio-based binder was
reduced by adding surfactants.
TABLE-US-00031 TABLE 29 Coupling agents for the bio-based binder
formulations-Fiberglass Handsheets Sample 2 Sample 3 Sample 4
Sample 5 Sample 6 70:30 70:30 70:30 70:30 70:30 Sample 1 MD-CA
MD-CA MD-CA MD-CA MD-CA 70:30 w/5% SHP w/5% SHP w/5% SHP w/5% SHP
w/5% SHP MD-CA and 0.19% and 0.38% and 0.19% and 0.38% and 0.19%
w/5% Tyzor .RTM. Tyzor .RTM. Tyzor .RTM. Tyzor .RTM. Tyzor .RTM.
Component SHP TE TE AA-75 AA-75 TPT Maltodextrin 90.3 g 90.3 g 90.0
g 90.3 g 90.0 g 90.3 g (50% conc.) (DE 11.0) Citric Acid 19.4 g
19.4 g 19.3 g 19.4 g 19.3 g 19.4 g gamma- 10.2 g aminopropyl-
trihydroxy-silane (1.24% solution) Sodium 3.9 g 3.9 g 3.9 g 3.9 g
3.9 g 3.9 g Hypophosphite (41.5% conc.) Tyzor .RTM. TE 0.16 g 0.32
g (80% Conc.) Tyzor .RTM. AA-75 0.17 g 0.34 g (75% Conc.) Tyzor
.RTM. TPT 0.13 g (100% Conc.) Water 676.2 686.3 686.5 686.3 686.5
686.3 Total 800 g 800 g 800 g 800 g 800 g 800 g MD = maltodextrin,
CA = citric acid, SHP = sodium hypophosphite
TABLE-US-00032 TABLE 30 Mechanical properties for handsheets with
the bio-based binder formulations containing different coupling
agents Sample 2 Sample 3 Sample 4 Sample 5 Sample 6 70:30 70:30
70:30 70:30 70:30 Sample 1 MD-CA MD-CA MD-CA MD-CA MD-CA 70:30 w/5%
SHP w/5% SHP w/5% SHP w/5% SHP w/5% SHP MD-CA and 0.19% and 0.38%
and 0.19% and 0.38% and 0.19% w/5% Tyzor .RTM. Tyzor .RTM. Tyzor
.RTM. Tyzor .RTM. Tyzor .RTM. SHP TE TE AA-75 AA-75 TPT Tensile
Strength 16.13 16.43 15.79 15.2 15.05 20.17 (lbf) LOI (%) 5.85 6.27
6.34 6.33 6.17 6.73 Tensile/LOI 2.76 2.62 2.49 2.4 2.44 3.00 After
Steam 10.66 6.51 6.64 7.30 10.25 10.29 aging Tensile Strength (lbf)
After Steam 5.03 6.06 6.36 6.58 6.46 8.44 aging LOI (%) After Steam
2.12 1.08 1.04 1.11 1.59 1.22 aging Tensile/LOI MD = maltodextrin,
CA = citric acid, SHP = sodium hypophosphite
[0119] From the data set forth in Tables 29 and 30, it was
concluded that the bio-based formulations containing different
coupling agents achieved tensile strengths comparable to that of
current commercially available products.
Example 12
[0120] The bio-based binder may emit an aroma depending upon
product and curing conditions. To minimize the emission of
undesired aromas, various alkanol amines were added to the binder
composition and R-20 products were produced under typical
(conventional) manufacturing conditions. The produced materials
were cut into 8.times.8 (inch.sup.2), placed in zip bags, and
sealed. Ten panelists were provided with a fresh sample bag and the
panelists individually ranked each of the samples from strongest
aroma (higher number) to weakest aroma (lower number). The results
are presented in Table 31.
TABLE-US-00033 TABLE 31 Aroma decrease in insulation made with the
bio-based binder Aroma Ranking (intensity Sample Description
descending order) Sample 1 70:30 MD-CA w/5% SHP 4 Sample 2 60:30:10
MD-CA-TEOA 3 Sample 3 65:30:5 MD-CA-TEOA 2 w/5% SHP Sample 4
65:30:5 MD-CA-DEOA 1 w/5% SHP ** MD = maltodextrin, CA = citric
acid, TEOA = Triethanolamine, DEOA = diethanolamine, SHP = sodium
hypophosphite
[0121] Based upon the data set forth in Table 31, it was concluded
that the aroma generated by the cured insulation product was
reduced using an inventive bio-based binder containing an alkanol
amine.
Example 13
[0122] The binder formulations of Sample 1 and Sample 2 set forth
in Table 18 combined with the moisture resistant additives listed
in Table 32 were utilized to form fiberglass R-13 insulation
products in a conventional manner known by those of skill in the
art. The R-13 products had a target LOI of 6.5%. The mechanical
properties of the moisture resistance additive added bio-binder
were determined under ambient conditions. The results are set forth
in Table 32.
TABLE-US-00034 TABLE 32 Additives added to improve water resistance
of fiberglass insulation made with bio-based binder - R-13 batts
Amount added Stiff- Additive (% on Binder ness/Sag Description
added Solids) (degree) 80:20 MD-CA w/5% SHP 39 70:30 MD-CA w/5% SHP
28 70:30 MD-CA w/5% SHP Polon MF56 0.3 32 70:30 MD-CA w/5% SHP
SVE-148 0.3 30 70:30 MD-CA w/5% SHP LE-743 0.3 31 70:30 MD-CA w/5%
SHP Silres BS-1042 0.3 37 70:30 MD-CA w/5% SHP ICM-2153 0.3 35
70:30 MD-CA w/5% SHP Silquest 0.3 40 Y-9669 ** MD = maltodextrin,
CA = citric acid, SHP = sodium hypophosphite
[0123] Based upon the data set forth in Table 32, it was concluded
that the bio-based binder formulations containing different
moisture resistant additives obtained a fiber glass insulation
product with performance capabilities comparable to that of
commercially available fiber glass insulation products.
Example 14
[0124] An environmental emission test was using the basic
formulation set forth as Sample 1 of Table 18 together with either
alone or with an existing emulsified mineral de-dusting oil. The
test was conducted over a period of at least 5 hours using a
conventional production line to make an R-19 insulation product for
each formulation including a control. A typical emission sampling
analytical procedure was followed and the filtered particulate
emission and formaldehyde emission were listed in the Table 33.
TABLE-US-00035 TABLE 33 Forming Emission Test Results Binder Type
Binder Type Binder Type Phenol/ Compound/Sample MDCA MDCA-Veg.
Urea/Formaldehyde Train lbs/hour Oil lbs/hour (Control) lbs/hour
Filtered Particulate, 5.499 5.064 6.737 M5/202 Formaldehyde M316
0.028 0.023 0.414
[0125] From the data set forth in Table 33, it was concluded that
the bio-based binder, when applied in a conventional fiber glass
insulation manufacturing process, reduced forming particulate
emission by 18% or more and nearly eliminated formaldehyde emission
during the formation of the insulation. It is noted that the small
amount of formaldehyde detected might have been derived from
formaldehyde binder residue or some other contamination.
[0126] The invention of this application has been described above
both generically and with regard to specific embodiments. Although
the invention has been set forth in what is believed to be the
preferred embodiments, a wide variety of alternatives known to
those of skill in the art can be selected within the generic
disclosure. The invention is not otherwise limited, except for the
recitation of the claims set forth below.
* * * * *