U.S. patent application number 11/917632 was filed with the patent office on 2011-06-16 for radioactive ray-curable liquid resin composition for use in optical stereolithography, and optically shaped article produced by curing the composition.
This patent application is currently assigned to JSR CORPORATION. Invention is credited to Noriyasu Shinohara, Katsuyuki Takase, Takayoshi Tanabe.
Application Number | 20110144271 11/917632 |
Document ID | / |
Family ID | 37532407 |
Filed Date | 2011-06-16 |
United States Patent
Application |
20110144271 |
Kind Code |
A1 |
Takase; Katsuyuki ; et
al. |
June 16, 2011 |
RADIOACTIVE RAY-CURABLE LIQUID RESIN COMPOSITION FOR USE IN OPTICAL
STEREOLITHOGRAPHY, AND OPTICALLY SHAPED ARTICLE PRODUCED BY CURING
THE COMPOSITION
Abstract
The present invention aims to provide a radiation-curing liquid
resin composition for optical tridimensional modeling having good
storage stability. The suitable radiation-curing liquid resin
composition for optical tridimensional modeling of the present
invention includes a compound represented by the below general
formula (1), a compound having phenolic hydroxyl group, a cationic
polymerizable compound, a radical polymerization initiator, a
radical polymerizable compound, one or more sulfur compound
selected from the group consisting of 2-mercaptobenzothiazole,
2-(4-morpholinodithiobenzothiazole, diisopropylxantogendisulfide
and diphenyldisulfide, a polyether polyol compound.
##STR00001##
Inventors: |
Takase; Katsuyuki; (Chuo-ku,
JP) ; Tanabe; Takayoshi; (Chuo-ku, JP) ;
Shinohara; Noriyasu; (Chuo-ku, JP) |
Assignee: |
JSR CORPORATION
TOKYO
JP
|
Family ID: |
37532407 |
Appl. No.: |
11/917632 |
Filed: |
June 16, 2006 |
PCT Filed: |
June 16, 2006 |
PCT NO: |
PCT/JP2006/312147 |
371 Date: |
March 12, 2009 |
Current U.S.
Class: |
524/710 ;
524/719; 524/736; 524/741; 524/742 |
Current CPC
Class: |
B33Y 70/00 20141201;
C08G 59/687 20130101; C08L 63/00 20130101 |
Class at
Publication: |
524/710 ;
524/719; 524/742; 524/736; 524/741 |
International
Class: |
C08K 5/47 20060101
C08K005/47; C08K 5/372 20060101 C08K005/372; C08K 5/13 20060101
C08K005/13; C08K 5/51 20060101 C08K005/51 |
Foreign Application Data
Date |
Code |
Application Number |
Jun 16, 2005 |
JP |
2005-176080 |
Jun 16, 2005 |
JP |
2005-176236 |
Oct 21, 2005 |
JP |
2005-306855 |
Dec 21, 2005 |
JP |
2005-368066 |
Claims
1. A radiation-curing liquid resin composition for optical
tridimensional modeling comprising: a compound represented by the
general formula (1) described below; ##STR00019## a compound having
phenolic hydroxyl group; a cationic polymerizable compound; a
radical polymerization initiator; a radical polymerizable compound;
one or more sulfur compound selected from the group consisting of
2-mercaptobenzothiazole, 2-(4-morpholinodithio)benzothiazole,
diisopropylxantogendisulfide and diphenyldisulfide; and a polyether
polyol compound.
2. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 1, wherein, per total
content of the composition, the content rate of the compound
represented by the formula (1) is 0.1 to 10% by weight, the content
rate of the compound having phenolic hydroxyl group is 0.1 to 10%
by weight, the content rate of the cationic poiymerizable compound
is 15 to 85% by weight, the content rate of the radical
polymerization initiator is 0.01 to 10% by weight, the content rate
of the radical polymerizable compound is 0.1 to 25% by weight, the
content rate of the sulfur compound is 0.2 to 3% by weight, and the
content rate of the polyether polyol compound is 1 to 35% by
weight.
3. A radiation-curing liquid resin composition for optical
tridimensional modeling comprising: a compound represented by
general formula (1) described below; ##STR00020## a compound having
phenolic hydroxyl group and/or phosphorous ester group; a cationic
polymerizable compound; a radical polymerization initiator; a
radical polymerizable compound; and water; wherein the content of
the compound represented by the following formula (2) is 5% or less
by weight per weight of the compound represented by the
aforementioned formula (1). ##STR00021##
4. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 3, wherein, per total
content of the composition, the content rate of the compound
represented by the formula (1) is 0.1 to 10% by weight, the content
rate of the compound having phenolic hydroxyl group and/or
phosphorous ester group is 0.1 to 10% by weight, the content rate
of the cationic polymerizable compound is 15 to 85% by weight, the
content rate of the radical polymerization initiator is 0.01 to 10%
by weight, the content of the radical polymerizable compound is 0.1
to 25% by weight, and the content rate of the water is 0.1 to 2% by
weight.
5. A radiation-curing liquid resin composition for optical
tridimensional modeling comprising: a compound represented by the
general formula (3) described below; ##STR00022## wherein R.sup.3,
if plural, is a monovalent organic group independently and at least
one thereof is a monovalent aromatic group and n is an integer of 1
to 5; a compound having phenolic hydroxyl group and/or phosphorous
ester group; a cationic polymerizable compound; a radical
polymerization initiator; a radical polymerizable compound; and a
polyether polyol compound.
6. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 5, wherein, the content
of the compound represented by the following formula (4) is 1/20 or
less (weight ratio) of the content of the compound represented by
the aforementioned formula (3): ##STR00023## wherein R.sup.4 is a
monovalent organic group independently and at least one thereof is
a monovalent aromatic group, and n is an integer of 1 to 5.
7. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 5, wherein, per total
content of the composition, the content rate of the compound
represented by the formula (3) is 0.1 to 10% by weight, the content
rate of the compound having phenolic hydroxyl group and/or
phosphorous ester group is 0.1 to 10% by weight, the content rate
of the cationic polymerizable compound is 15 to 85% by weight, the
content rate of the radical polymerization initiator is 0.01 to 10%
by weight, the content rate of the radical polymerizable compound
is 0.1 to 25% by weight, and the content rate of the a polyether
polyol compound is 1 to 35% by weight.
8. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 5, further containing 1
to 35% by weight of elastomer particles having number average
particle sizes of 10 to 1000 nm measured by electron microscope
method, per total content of the composition.
9. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 1, wherein the compound
having phenolic hydroxyl group is at least one compound selected
from the group consisting of the compounds represented by the (5)
to (7) described below: ##STR00024## wherein R.sup.51 and R.sup.52
are independently alkyl groups having a carbon number of 1 to 4,
which may be branched; m and n are independently 1 or 2, p is 1 to
4; and A is an organic group; ##STR00025## wherein R.sup.61 and
R.sup.62 are independently alkyl groups having a carbon number of 6
to 10, which may be branched; ##STR00026## wherein R.sup.71 is
hydrogen atom, methyl group or single bond combining two aromatic
rings; and R.sup.72 is an organic group.
10. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 1, wherein the compound
having phenolic hydroxyl group is
pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]-
.
11. The radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 1, wherein the cationic
polymerization compound contains 40% or more by weight of compound
having two or more alicyclic epoxy groups in a single molecule, per
total content of the cationic polymerization compound.
12. An optically modeled article obtained by irradiating light to
the radiation-curing liquid resin composition for optical
tridimensional modeling according to claim 1.
Description
TECHNICAL FIELD
[0001] The present invention relates to a radiation-curing liquid
resin composition for optical tridimensional modeling and an
optically modeled article obtained by curing the composition.
BACKGROUND ART
[0002] There is a known optical tridimensional modeling method to
form a tridimensional object having a structure of an integrally
laminated cured resin layer, being formed by repeating the step of
forming the cured resin layer through the selective irradiation of
light to a radiation-curing liquid substance (a liquid resin
composition) (refer to Patent Documents 1 to 4). A typical example
of this optical tridimensional modeling method is explained as
follows.
[0003] First, a cured resin layer having a specified pattern is
formed by selectively irradiating light such as ultraviolet laser
to the liquid surface of a radiation-curing liquid resin
composition held in a container. Then, by supplying a
radiation-curing liquid resin composition in a quantity of a single
layer thereof onto the cured resin layer and selectively
irradiating light onto the liquid surface, a new cured resin layer
is formed integrally onto the previously formed cured resin layer
in a continuous fashion with each other. And, by repeating the
above steps for the prescribed number of cycles with or without
changing the light-irradiation pattern, an integrally laminated
tridimensional object by a plurality of cured resin layers is
formed.
[0004] According to this optical tridimensional modeling method,
the target tridimensional object can be provided easily in a short
time no matter how complicated its shape is. Such technology is
extremely useful at the experimental stage in developing new
products in the automobile industry and the consumer-electronics
industry, and is becoming an essential means for shortening the
development period and for reducing costs.
[0005] Conventionally, as radiation-curing liquid resin
compositions used in the optical tridimensional modeling method,
the resin compositions represented by [1] to [3] as described below
have been introduced: [0006] [1] a resin composition containing
radical polymerizable organic compounds such as
urethane(meth)acrylate, oligoester(meth)acrylate,
epoxy(meth)acrylate, thiol, en compound, and photosensitive
polyimide (refer to Patent Documents 5 to 7); [0007] [2] a resin
composition containing cationic polymerizable organic compounds
such as epoxy compound, cyclic ether compound, cyclic lactone
compound, cyclic acetal compound, cyclic thioether compound,
spiro-ortho-ester compound, and vinylether compound (refer to
Patent Documents 8); and [0008] [3] a resin composition containing
radical polymerizable organic compounds and cationic polymerizable
organic compounds (refer to Patent Documents 9 to 14).
[0009] In Patent Documents 15 and 16, there are described
antioxidants as components, which can be added to a
radiation-curing liquid resin composition used for optical
tridimensional modeling.
[0010] In the compositions of the above-mentioned [2] and [3], a
cationic polymerization initiator of triaryl sulfonium salt type is
generally used.
##STR00002##
[0011] Commercially available products of this compound comprise
UVI-6974, UVI-6976 (manufactured by D.A.W. CHEMICAL CO., INC.),
CPI-6976 (manufactured by Aceto Corporation), and the like. [0012]
Patent Document 1: JP-A-60-247515 [0013] Patent Document 2:
JP-A-62-35966 [0014] Patent Document 3: JP-A-62-101408 [0015]
Patent Document 4: JP-A-5-24119 [0016] Patent Document 5:
JP-A-1-204915 [0017] Patent Document 6: JP-A-2-208305 [0018] Patent
Document 7: JP-A-3-160013 [0019] Patent Document 8: JP-A-1-213304
[0020] Patent Document 9: JP-A-2-28261 [0021] Patent Document 10:
JP-A-2-75618 [0022] Patent Document 11: JP-A-6-228413 [0023] Patent
Document 12: JP-A-11-310626 [0024] Patent Document 13:
JP-A-11-228610 [0025] Patent Document 14: JP-A-11-240939 [0026]
Patent Document 15: JP-A-8-256062 [0027] Patent Document 16:
JP-A-2003-240939
DISCLOSURE OF THE INVENTION
Problem to be Solved by the Invention
[0028] Tridimensional objects obtained through those tridimensional
modeling methods using the above-mentioned radiation-curing liquid
resin composition have been widely used in the past as the
shape-confirmation models for investigating the design. It is
required that such a radiation-curing liquid resin composition has
superior storage stability. A composition having inferior storage
stability tends to be inferior in its handling because possible
storage duration from the formulation to the fabrication of a
tridimensional object is short. However, the above-mentioned
traditional compositions still leave room for improvement in view
of the storage stability.
[0029] An object of the present invention is to provide a
radiation-curing liquid resin composition for optical
tridimensional modeling, which has good storage stability.
Means to Solve the Problem
[0030] As the result of wholehearted study and research to achieve
the above-mentioned object, the inventors found that the compound
represented by the aforementioned formula (1) could exhibit
especially superior storage stability when included in a
radiation-curing liquid resin composition for optical
tridimensional modeling, having a specific component composition
and achieved the present invention.
[0031] The first radiation-curing liquid resin composition for
optical tridimensional modeling according to the present invention
(referred to as "liquid resin composition" hereinafter) is
characterized in that the composition includes: [0032] a compound
represented by the general formula (1) described below;
[0032] ##STR00003## [0033] a compound having phenolic hydroxyl
group; [0034] a cationic polymerizable compound; [0035] a radical
polymerization initiator; [0036] a radical polymerizable compound;
[0037] one or more sulfur compound selected from the group
consisting of 2-mercaptobenzothiazole,
2-(4-morpholinodithio)benzothiazole, diisopropylxantogendisulfide
and diphenyldisulfide; and [0038] a polyether polyol compound.
[0039] This liquid resin composition of the present invention
includes the compound having phenolic hydroxyl group, which
functions as primary antioxidant, and the sulfur compound, which
functions as secondary antioxidant, in addition to the cationic
polymerization initiator having a structure of the aforementioned
formula (1). Therefore, the liquid resin composition is superior in
storage stability.
[0040] Further, in recent years, there has been a demand for
transparent objects such as optical parts, as the tridimensional
objects obtained through the tridimensional modeling methods. It is
required that the transparent objects should not turn yellow over
time even in high temperature environments. In this point,
tridimensional modeled articles, which are less turned to yellow
even under a high temperature environment, can be obtained with a
high degree of accuracy, because the above liquid resin composition
of the present invention includes each of the above components in
combination.
[0041] In the above-mentioned liquid resin composition of the
present invention, it is preferred that, per total content of the
composition, [0042] the content rate of the compound represented by
the formula (1) is 0.1 to 10% by weight, [0043] the content rate of
the compound having phenolic hydroxyl group is 0.1 to 10% by
weight, [0044] the content rate of the cationic polymerizable
compound is 1.5 to 85% by weight, [0045] the content rate of the
radical polymerization initiator is 0.01 to 10% by weight, [0046]
the content rate of the radical polymerizable compound is 0.1 to
25% by weight, [0047] the content rate of the sulfur compound is
0.2 to 3% by weight, and [0048] the content rate of the polyether
polyol compound is 1 to 35% by weight.
[0049] Then, the second liquid resin composition of the present
invention is characterized in that the composition includes: [0050]
a compound represented by the general formula (1) described
below;
[0050] ##STR00004## [0051] a compound having phenolic hydroxyl
group and/or phosphorous ester group; [0052] a cationic
polymerizable compound; [0053] a radical polymerization initiator;
[0054] a radical polymerizable compound; and [0055] water; [0056]
the content rate of the compound represented by the following
formula (2) is 5% or less by weight per weight of the compound
represented by the aforementioned formula (1).
##STR00005##
[0057] Such a configured liquid resin composition can exhibit
superior storage stability, because the cationic polymerization
initiator having a structure of the aforementioned formula (1) is
included in combination with the other specific respective
components as described above.
[0058] Most of commercially available cationic polymerization
initiators having a structure of the aforementioned formula (1)
generally include a compound having a structure represented by the
aforementioned formula (2) at over a certain content rate. It was
found, however, that such a compound of the formula (2) lowered
storage stability of the liquid resin composition. Contrary
thereto, even the liquid resin composition of the present invention
can exhibit superior storage stability, because the content of the
compound of the aforementioned formula (2) is decreased.
[0059] Further, in recent years, concerning the models and the like
for transparent objects such as optical parts, there has been a
demand for high transparency in addition to high tridimensional
modeling accuracy. In this relation, the liquid resin composition
of the present invention includes a specific antioxidant, which is
a compound having phenolic hydroxyl group and/or phosphorous ester
group. Therefore, if optically modeled articles are made from such
a liquid resin composition, optically modeled articles obtained can
maintain superior transparency for a long time.
[0060] In the above liquid resin composition of the present
invention, it is characterized that, the content rate of the
compound represented by the formula (1) per total content of the
composition is 0.1 to 10% by weight, [0061] the content rate of the
compound having phenolic hydroxyl group and/or phosphorous ester
group is 0.1 to 10% by weight, [0062] the content rate of the
cationic polymerizable compound is 15 to 85% by weight, [0063] the
content rate of the radical polymerization initiator is 0.01 to 10%
by weight, [0064] the content rate of the radical polymerizable
compound is 0.1 to 25% by weight, and [0065] the content rate of
the water is 0.1 to 2% by weight.
[0066] Further, the third liquid resin composition of the present
invention is characterized in that the composition includes: a
compound represented by the general formula (3) described
below;
##STR00006##
wherein R.sup.3, if plural, is a monovalent organic group
independently and at least one thereof is a monovalent aromatic
group and n is an integer of 1 to 5; [0067] a compound having
phenolic hydroxyl group and/or phosphorous ester group; [0068] a
cationic polymerizable compound; [0069] a radical polymerization
initiator; [0070] a radical polymerizable compound; and [0071] a
polyether polyol compound.
[0072] The above liquid resin composition of the present invention
has superior storage stability, because the cationic polymerization
initiator of triaryl sulfonium salt type represented by the
aforementioned formula (3) is included in a specific
composition.
[0073] In recent years, concerning tridimensional objects obtained
through the tridimensional modeling methods, there has been a
demand for high tridimensional modeling accuracy and, in
particular, for the improvement of the surface smoothness caused by
the side-face step between the respective lamination layers on the
modeled article.
[0074] The composition of [1] in the above prior art is, however,
very difficult to attain high modeling accuracy owing to the large
curing shrinkage. Although the composition of [2] provides high
modeling accuracy in some degree, it tends to provide a brittle
cured article of low resistance. Furthermore, the composition of
[2] is inferior in initial strength (green strength) after
photo-curing and in curing rate to the composition of [1], thus
being difficult to attain high modeling rate. The composition of
[3] achieves high modeling accuracy and excellent mechanical
characteristics compensating the drawbacks of above two methods.
Compared with general-use resins, however, the composition of [3]
is inferior in a part of mechanical and thermal characteristics. In
particular, concerning resistance to fracture the composition of
[3] is inferior to the general-use resins. Thus, it tends to be
difficult to sufficiently satisfy both of modeling accuracy and
other important characteristics in a conventional radiation-curing
liquid resin composition.
[0075] The improvement in the tridimensional modeling accuracy
needs to decrease the dimensional deformation after the
photo-curing. Accordingly, increase in initial strength (green
strength) after photo-curing needs to increase the radiation-curing
property. Nevertheless, a radiation-curing liquid resin composition
having high photo-curing rate almost completes the curing reaction
within a short time after an irradiation of light, or has a small
contribution of the delayed curing reaction so that a step on the
side face between the respective laminated layers often appears. As
a result, sufficient smoothness is difficult to attain on the
surface of the optically modeled article, in particular on the side
face thereof.
[0076] Contrary thereto, the third liquid resin composition of the
above present invention, as described above, is difficult to attain
a step on the side face between the respective laminated layers
while having high photo-curing property, because the cationic
polymerization initiator of triaryl sulfonate type represented by
the aforementioned formula (3) is included in a specific
composition. Therefore, optically modeled article obtained by using
such a liquid resin composition is remarkably superior in surface
smoothness.
[0077] In the third liquid resin composition, it is preferred that
the content of the compound represented by the following formula
(4) is not more than 1/20 (weight ratio) of the content of the
compound represented by the aforementioned formula (3). The
compound of the following formula (4) decreased storage stability
of the composition similarly to the compound of the aforementioned
formula (2). Therefore, decrease in the content of the compound of
the following formula (4) as described above makes storage
stability of the liquid resin composition more improved,
##STR00007##
wherein R.sup.4 is a monovalent organic group independently and at
least one thereof is a monovalent aromatic group, and n is an
integer of 1 to 5.
[0078] In the third liquid resin composition of the present
invention, it is preferred that, per total content of the
composition, [0079] the content of the compound represented by the
formula (3) is 0.1 to 10% by weight, [0080] the content of the
compound having phenolic hydroxyl group and/or phosphorous ester
group is 0.1 to 10% by weight, [0081] the content of the cationic
polymerizable compound is 15 to 85% by weight, [0082] the content
of the radical polymerization initiator is 0.01 to 10% by weight,
[0083] the content of the radical polymerizable compound is 0.1 to
25% by weight, and [0084] the content of the polyether polyol
compound is 1 to 35% by weight.
[0085] Further, it is more preferred that the third liquid resin
composition includes additionally elastomer particles having a
number average particle size of 10 to 1000 nm, which is measured by
an electronically microscope method, at 1 to 35% by weight per
total content of the composition. With the arrangement inclusion,
impact strength and breaking toughness of a cured article of the
liquid resin composition.
[0086] In the first, second and third liquid resin compositions
mentioned above, it is preferred that the above compound having
phenolic hydroxyl group is at least one compound selected from the
group consisting of the compounds represented by the below (5) to
(7):
##STR00008##
wherein R.sup.51 and R.sup.52 are independently an alkyl group
having a carbon number of 1 to 4, which may be branched, m and n
are independently 1 or 2, is an integer of 1 to 5, p is 1 to 4, A
is an organic group;
##STR00009##
wherein R.sup.61 and R.sup.62 are independently an alkyl group
having a carbon number of 6 to 10, which may be branched;
##STR00010##
wherein R.sup.71 is hydrogen atom, methyl group or single bond
combining two aromatic rings, and R.sup.72 is an organic group.
[0087] Of these, it is suitable that the compound having phenolic
hydroxyl group is
pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)pr-
opionate].
[0088] In the first, second and third liquid resin compositions,
the above cationic polymerizable compound includes a compound
having two or more alicyclic epoxy groups in a single molecule at
40% or more by weight per total content of the cationic
polymerizable compound.
[0089] Further, the present invention provides modeled articles
obtained by irradiating light to the first, second and third liquid
resin compositions mentioned above. These optically modeled
articles have characteristics, according to the liquid resin
composition, which is a raw material, such that they turn less
yellow even under high temperature environment, superior
transparency is maintained for a long time, and surface smoothness
is superior.
Effect of the Invention
[0090] The liquid resin composition of the present invention can
provides a high-precision, optically modeled article, which has
excellent characteristics in that they turn less yellow in high
temperature environments, good transparency is maintained for a
long time, and surface smoothness is good.
BEST MODES FOR CARRYING OUT THE INVENTION
[0091] Hereinafter, best modes for carrying out the invention are
explained.
[First Liquid Resin Composition]
[0092] First, preferred embodiment of the first liquid resin
composition according to the present invention is explained.
[0093] The first liquid resin composition includes at least (A1) a
compound represented by the general formula (1) described below,
(B1) a compound having phenolic hydroxyl group, (C1) a cationic
polymerizable compound, (D1) a radical polymerization initiator,
(E1) a radical polymerizable compound, (F1) one or more sulfur
compound selected from the group consisting of
2-mercaptobenzothiazole, 2-(4-morpholinodithio)benzothiazole,
diisopropylxantogendisulfide and diphenyldisulfide, and (G1) a
polyether polyol compound. The components (A1) to (G1) and other
optional components, which may be blended if necessary, are
explained below.
[0094] (The (A1) Component)
[0095] The (A1) component included in the first liquid resin
composition is a compound represented by the following formula (1)
and functions as a photo-cationic polymerization initiator for the
below-described (C1) component (cationic polymerizable compound).
Usually, the compound having a structure represented by the formula
(1) can be used in the form of salt as
diphenyl(phenylthiophenyl)sulfonium hexafluoroantimonate
represented by the following formula (1a).
##STR00011##
[0096] In a commercially available compound represented by the
aforementioned formula (1), a compound represented by the following
formula (2) is usually included as an impurity.
[0097] The content of the compound represented by the following
formula (2) in the first liquid resin composition is preferably
less than 1/20 by weight ratio per the content of the compound
represented by the aforementioned formula (1). Thus, storage
stability of the liquid resin composition is further improved and
increase in viscosity over time is inhibited.
[0098] The compound represented by the following formula (2) is
mostly in the form of salt as
bis[4-(diphenylsulfonio)phenyl]sulfidebishexafluoroantimonate.
##STR00012##
[0099] As the commercially available (A1) component to be used
preferably, in which the content of the compound having a structure
represented by the aforementioned formula (2) is enough small
within the above range, there are CPI-110, CPI-101A, CPI-110A
(manufactured by SAN-APRO LIMITED), for example.
[0100] The content of the (A1) component in the first liquid resin
composition is, per total content of the composition, preferably
0.1 to 10% by weight, more preferably 0.2 to 8% by weight, further
preferably 1 to 8% by weight. If the content of the (A1) component
is less than 0.1% by weight, radiation-curing property of the
liquid resin composition tends to decrease and a tridimensional
having sufficient mechanical strength cannot be modeled. On the
other hands, if the content of the (A1) component is over 10% by
weight and when the liquid resin composition is subjected to an
optical tridimensional modeling method, it tends to be difficult to
attain suitable optical transparency and to control curing depth,
and thus modeling accuracy of a tridimensional object to be
obtained tends to decrease.
[0101] (The (B1) Component)
[0102] The (B1) component included in the first liquid resin
composition is a compound having phenolic hydroxide group.
Applicable (B1) component includes a known antioxidant. Preferred
one is hindered phenol-based compound in the first liquid resin
composition. Through the addition of the (B1) component in
combination with the after-mentioned (F1) component, a
tridimensional modeled article, which turns less yellow even in
high temperature environments, can be obtained with a high degree
of accuracy.
[0103] Specific examples of the (B1) component comprise the
following compounds. It is noted that the name described in
parenthesis after the compound name is an example for a trade name.
The hindered phenolic compound includes,
pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]
(Irganox 1010),
thiodiethylene-bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]
(Irganox 1035FF), 3,5-bis(1,1-dimethylethyl)-4-hydroxy-benzene
propanate,
ethylenebis(oxyethylene)bis[3-(5-tertert-butyl-4-hydroxy-m-tolyl)propiona-
te] (Irganox 245),
octadecyl-3-(3,5-tert-butyl-4-hydroxyphenyl)propionate (Irganox
1076),
3,3',3'',5,5',5''-hexa-tert-butyl-a,a',a''-(mesitylene-2,4,6-triyl)tri-p--
cresol (Irganox 1330),
1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-1,3,5-triazine-2,4,6(1H,3H,-
5H)-trione (Irganox 3114), 4,6-bis(octylthiomethyl)-o-cresol
(Irganox 1520L),
9-bis[2-{3-(3-tertert-butyl-4-hydroxy-5-methylphenyl)propionyloxy-
}-1,1-dimet-hylethyl]-2,4,8,10-tetraoxaspiro[5,5]undecane
(Sumilizer GA-80), and 2,6-tert-butyl-4-methylphenol (Sumilizer
BHT): (Irganox is a trade mark of Ciba Specialty Chemicals K.K.,
and Sumilizer is a trade mark of Sumitomo Chemical Co., Ltd.).
[0104] Of these, it is preferred to use
pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]
because its inhibiting effect to prevent a tridimensional modeled
article from turning yellow over time in high temperature
environments is high.
[0105] Examples of the commercially available hindered phenol-based
(B1) component comprise Irganox 1010, 103 5FF, 245, 1076, 1330,
3114, 1520L, and 3125 (manufactured by Ciba Specialty Chemicals
K.K.), Sumilizer BHT, and GA-80, (manufactured by Sumitomo Chemical
Co., Ltd.), and Cyanox 1790 (manufactured by Cytec Co., Ltd.).
[0106] The content of the (B1) component in the first liquid resin
composition is, per total content of the composition, preferably
0.1 to 10% by weight, more preferably 0.1 to 5% by weight, further
preferably 1.0 to 5.0% by weight. If the content of the (B1)
component is less than 0.1% by weight or more than 10% by weight,
there may be defect in that inhibiting effect to prevent a
tridimensional modeled article from turning yellow over time in
high temperature environments becomes insufficient, for
example.
[0107] (The (C1) Component)
[0108] The (C1) component included in the first liquid resin
composition is a cationic polymerizable compound. This (C1)
component is a compound that initiates polymerization reaction and
cross-linking reaction under light irradiation in the presence of a
cationic photo-polymerization initiator.
[0109] Although the (C1) component is not specifically limited, a
preferable one is a compound having two or more alicyclic epoxy
groups in a single molecule. With the presence of over 40% by
weight of the compound having two or more alicyclic epoxy groups in
a single molecule per total content (100%) of the (C1) component,
good curing rate, mechanical strength and heat resistance can be
attained.
[0110] Examples of the (C1) component comprise: bisphenol A
diglycidyl ether, bisphenol F diglycidyl ether, bisphenol S
diglycidyl ether, brominated bisphenol A diglycidyl ether,
brominated bisphenol F diglycidyl ether, brominated bisphenol S
diglycidyl ether, epoxy novolak resin, hydrogenated bisphenol A
diglycidyl ether, hydrogenated bisphenol F diglycidyl ether,
hydrogenated bisphenol S diglycidyl ether, 3,4-epoxy cyclohexyl
methyl-3',4'-epoxycyclohexylcarboxylate,
2-(3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy)cyclohexane-metha-dioxane,
bis(3,4-epoxycyclohexylmethyl)adipate,
bis(3,4-epoxy-6-methylcyclohexylmethyl)adipate,
3,4-epoxy-6-methylcyclohexyl-3',4'-epoxy-6'-methylcyclohexane
carboxylate, .epsilon.-caprolactone modified
3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate,
trimethylcaprolactone modified
3,4-epoxycylohexylmethyl-3',4'-epoxycyclohexane carboxylate,
-methyl-.beta.-valerolactone modified
3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate,
methylenebis(3,4-epoxycyclohexane),
di(3,4-epoxycyclohexylmethyl)ether of ethyleneglycol,
ethylenebis(3,4-epoxycyclohexane carboxylate),
epoxycyclohexadioctyl hydrophthalate,
epoxycyclohexa-di-2-ethylhexyl hydrophthalate, 1,4-butanediol
diglycidylether, 1,6-hexanediol diglycidylether, neopentylglycol
diglycidylether, trimethylolpropane triglycidylether,
polyethyleneglycol digrycidylether, glycerin triglycidylether, and
polypropyleneglycol diglycidylether; polyglycidylether of polyether
polyol prepared by adding one or more alkylene oxide to aliphatic
polyhydric alcohol such as ethyleneglycol, propyleneglycol, and
glycerin; diglycidylester of long chain aliphatic dibasic acid;
monoglycidylether of higher aliphatic alcohol; monoglycidylether of
polyether alcohol prepared by adding phenol, cresol, butylphenol,
or alkyleneoxide; grycidylester of higher fatty acid; epoxylated
soybean oil; epoxybutylstearate; epoxyoctylstearate; epoxylated
linseed oil; and oxetane compounds such as epoxylated polybutadiene
and 1,4-bis[(3-ethyl-3-oxetanylmethoxy)methyl]benzene. The above
cationic polymerizable compounds can comprise the (C1) component
independently or in combination of two or more of them.
[0111] Of these cationic polymerizable compounds, preferred ones
are 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexyl carboxylate,
bis(3,4-epoxycyclohexylmethyl)adipate, .epsilon.-caprolactone
modified 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexyl
carboxylate, trimethylcaprolactone modified
3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate,
.beta.-methyl-.delta.-valerolactone modified
3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate,
bisphenol A diglycidyl ether, bisphenol F diglycidyl ether,
hydrogenated bisphenol A diglycidyl ether, hydrogenated bisphenol F
diglycidyl ether, 1,4-butanediol diglycidylether, 1,6-hexanediol
diglycidylether, trimethylolpropane triglycidylether, glycerin
triglycidylether, polyethyleneglycol digrycidylether,
polypropyleneglycol diglycidylether, and
1,4-bis[(3-ethyl-3-oxetanylmethoxy)methyl]benzene.
[0112] In view of attaining good curing rate, mechanical strength
and heat resistance as described above, more preferred ones are
compounds having two or more alicyclic epoxy groups in a single
molecule, such as 3,4-epoxycyclohexylmethyl-3',4'-epoxycylcohexyl
carboxylate and bis(3,4-epoxycyclohexylmethyl)adipate.
[0113] Examples of commercially available (C1) can comprise
UVR-6100, UVR-6105, UVR-6110, UVR-6128, UVR-6200, and UVR-6216,
(manufactured by Union Carbide Corporation), CELOXIDE 2021,
CELOXIDE 2021P, CELOXIDE 2081, CELOXIDE 2083, CELOXIDE 2085,
Epolead GT-300, Epolead GT-301, Epolead GT-302, Epolead GT-400,
Epolead 401, and Epolead 403, (manufactured by DAICEL CHEMICAL
INDUSTRIES, LTD.), KRM-2100, KRM-2110, KRM-2199, KRM-2400,
KRM-2410, KRM-2408, KRM-2490, KRM-2200, KRM-2720, and KRM-2750,
(manufactured by ADECA Corporation), Rapi-cure DVE-3, CHVE, PEPC,
(manufactured by ISP Co., Ltd.), Epicoat 828, Epicoat 812, Epicoat
1031, Epicoat 872, and Epicoat CT508, (manufactured by Japan Epoxy
Resin Co., Ltd.), XDO (manufactured by TOA GOSEI CO., TTD.), and
VECOMER 2010, 2020, 4010, and 4020, (manufactured by Allied Signal,
Inc.).
[0114] The content of the (C1) component in the first liquid resin
composition is, per total content of the composition, preferably 15
to 85% by weight, more preferably 30 to 80% by weight, further
preferably 40 to 75% by weight. If the content of the (C1)
component is over 85% by weight, deformation such as warp of a
tridimensional modeled article tends to become greater. On the
other hands, if the content of the (C1) component is less than 15%
by weight, mechanical strength and thermal characteristics tend to
be lowered.
[0115] (The (D1) Component)
[0116] The (D1) component included in the first liquid resin
composition is a radical polymerization initiator. This (D1)
component is a compound which decomposes under radiation rays such
as light and the like to generate radicals, which then initiate the
radical polymerization of the after-mentioned (E1) component
(radical polymerizable compound).
[0117] Examples of the (D1) component comprise, acetophenone,
acetophenonebenzylketal, anthraquinone,
1-(4-isopropylphenyl)-2-hydroxy-2-methylpropane-1-one, carbazole,
xanthone, 4-chlorobenzophenone, 4,4'-diaminobenzophenone,
1,1-dimethoxydeoxybenzoin, 3,3'-dimethyl-4-methoxybenzophenone,
thioxanthone-based compound,
2-methyl-1-[4-(methylthio)phenyl]-2-morphorino-propane-2-one,
2-benzyl-2-dimethylamino-1-(4-morphorinophenyl)-butane-1-one,
triphenyl amine, 2,4,6-trimethylbenzoyldiphenylphosphine oxide,
bis(2,6-dimethoxybenzoyl)-2,4,4-tri-methylpentylphosphine oxide,
benzyldimethylketal, 1-hydroxycyclohexylphenylketone,
2-hydroxy-2-methyl-1-phenylpropane-1-one, fluorenone, fluorene,
benzaldehyde, benzoin methyl ether, benzoin propyl ether,
benzophenone, Michler's ketone, 3-methylacetophenone,
3,3',4,4'-tetra(tert-butylperoxycarbonyl)benzophenone (BTTB), and a
combination of BTTB with dye sensitizer such as xanthene,
thioxanthene, coumalin, and ketocoumalin.
[0118] Of these, specifically preferred ones are
benzyldimethylketal, 1-hydroxycyclohexylphenylketone,
2,4,6-trimethylbenzoyldiphenylphosphine oxide, and
2-benzyl-2-dimethylamino-1-(4-morphorinophenyl)-butane-1-one. These
above radical polymerization initiators can structure the (D1)
component independently or in combination with two or more of
them.
[0119] The content of the (D1) component in the first liquid resin
composition is, per total content of the composition, preferably
0.01 to 10% by weight, more preferably 0.1 to 5% by weight. If the
content of the (D1) component is less than 0.01% by weight, radical
polymerization reaction rate (curing rate) of a liquid resin
composition tends to decrease so that modeling tends to require
longer time and resolution tend to decrease. On the other hands, if
the content of the (D1) component is over 10% by weight, excess
content of the polymerization initiator may decrease curing
characteristics of the liquid resin composition and have adverse
effects on humidity resistance and heat resistance of a
tridimensional modeled article.
[0120] (The (E1) Component)
[0121] The (E1) component included in the first liquid resin
composition is a radical polymerizable compound. Specifically, the
compound is a compound having ethylenic unsaturated bond (C.dbd.C),
and examples of that kind of compound are a monofunctional monomer
having one ethylenic unsaturated bond in a single molecule, and a
polyfunctional monomer having two or more ethylenic unsaturated
bonds in a single molecule.
[0122] The monofunctional and the polyfunctional monomers can
comprise the (E1) component independently or in combination of two
or more of them, or in combination of at least one monofunctional
monomer with at least one polyfunctional monomer.
[0123] It is preferable that the (E1) component contains 60% by
weight or more of tri- or higher functional monomer, i.e. a
polyfunctional monomer having three or more of ethylenic
unsaturated bonds in a single molecule, per total content (100% by
weight) of the (E1) component. More preferable content of the tri-
or higher functional monomer is 70% by weight or more, further more
preferable content is 80% by weight or more, and most preferable
content is 100% by weight. If the content is 60% by weight or more,
the radiation-curing property of the obtained resin composition
further improves, and the deformation over time of a tridimensional
modeled article tends not to occur.
[0124] Examples of the monofunctional monomer of the (E1) component
can comprise compounds such as acrylamide, (meth)acryloyl
morpholine, 7-amino-3,7-dimethyloctyl(meth)acrylate,
isobutoxymethyl(meth)acrylamide, isobornyloxyethyl(meth)acrylate,
isobornyl(meth)acrylate, 2-ethylhexyl(meth)acrylate,
ethyldiethyleneglycol(meth)acrylate, t-octyl(meth)acrylamide,
diacetone(meth)acrylamide, dimethylaminoethyl(meth)acrylate,
diethylaminoethyl(meth)acrylate, lauryl(meth)acryl ate,
dicyclopentadiene(meth)acrylate,
dicyclopentenyloxyethyl(meth)acrylate,
dicyclopentenyl(meth)acrylate,
N,N-dimethyl(meth)acrylamidetetrachlorophenyl(meth)acrylate,
2-tetrachlorophenoxyethyl(meth)acrylate,
tetrahydrofulfuryl(meth)acrylate, tetrabromophenyl(meth)acrylate,
2-tetrabromophenoxyethyl(meth)acrylate,
2-trichlorophenoxyethyl(meth)acrylate,
tribromophenyl(meth)acrylate, 2-tribromophenoxyethyl(meth)acrylate,
2-hydroxyethyl(meth)acrylate, 2-hydroxypropyl(meth)acrylate,
vinylcaprolactam, N-vinylpyrrolidone, phenoxyethyl(meth)acrylate,
butoxyethyl(meth)acrylate, pentachlorophenyl(meth)acrylate,
pentabromophenyl(meth)acrylate,
polyethyleneglycolmono(meth)acrylate,
polypropyleneglycolmono(meth)acrylate, bomyl(meth)acrylate, and
methyltriethylenediglycol(meth)acrylate.
[0125] Examples of the polyfunctional monomer of the (E1) component
can comprise ethyleneglycoldi(meth)acrylate,
dicyclopentenyldi(meth)acrylate, triethyleneglycoldiacrylate,
tetraethyleneglycoldi(meth)acrylate,
tricyclodecanediyldimethylenedi(meth)acrylate,
tris(2-hydroxyethyl)isocyanuratedi(meth)acrylate,
tris(2-hydroxyethyl)isocyanuratetri(meth)acrylate, caprolactone
modified tris(2-hydroxyethyl)isocyanuratetri(meth)acrylate,
trimethylolpropanetri(meth)acrylate, ethylene oxide, (hereinafter
referred to as "EO"), modified trimethylolpropanetri(meth)acrylate,
propylene oxide, (hereinafter referred to as "PO"), modified
trimethylolpropanetri(meth)acrylate,
tripropyleneglycoldi(meth)acrylate,
neopentylglycoldi(meth)acrylate, (meth)acrylic acid additive on
both terminals of bisphenol A diglycidylether,
1,4-butanedioldi(meth)acrylate, 1,6-hexanedioldi(meth)acrylate,
pentaerythritoltri(meth)acrylate,
pentaerithritoltetra(meth)acrylate, polyesterdi(meth)acrylate,
polyethyleneglycoldi(meth)acrylate,
dipentaerithritolhexa(meth)acrylate,
dipentaerithritolpenta(meth)acrylate,
dipentaerithritoltetra(meth)acrylate, caprolactone modified
dipentaerithritolhexa(meth)acrylate, caprolactone modified
dipentaerithritolpenta(meth)acrylate,
ditrimethylolpropanetetra(meth)acrylate, EO modified bisphenol A
di(meth)acrylate, PO modified bisphenol A di(meth)acrylate, EO
modified hydrogenated bisphenol A di(meth)acrylate, PO modified
hydrogenated bisphenol A di(meth)acrylate, EO modified bisphenol F
di(meth)acrylate, and (meth)acrylate of phenol novolak
polyglycidylether.
[0126] Of these, the (E1) component preferably includes those
corresponding to the tri- or higher functional monomer, such as
tri(meth)acrylate compound, tetra(meth)acrylate compound,
penta(meth)acrylate compound, and hexa(meth)acrylate compound.
[0127] More specifically, particularly preferred ones are,
trimethylolpropanetri(meth)acrylate,
neopentylglycoldi(meth)acrylate, EO modified
trimethylolpropanetri(meth)acrylate,
dipentaerithritolhexa(meth)acrylate,
dipentaerithritolpenta(meth)acrylate,
ditrimethylolpropanetetra(meth)acrylate, and
dipentaerithritolmonohydroxypenta(meth)acrylate. Examples of
commercially available monofunctional monomer in the (E1) component
can comprise Aronix M-101, M-102, M-111, M-113, M-117, M-152, and
TO-1210 (manufactured by TOA GOSEJ CO., LTD.), KAYARAD TC-110S,
R-564, and R-128H (manufactured by NIPPON KAYAKU CO., LTD.),
Biscoat 192, Biscoat 220, Biscoat 2311HP, Biscoat 2000, Biscoat
2100,Biscoat 2150, Biscoat 8F, and Biscoat 17F (manufactured by
Osaka Organic Chemical Industry Ltd.).
[0128] Examples of commercially available polyfunctional monomer in
the (E1) component can comprise SA 1002 (manufactured by Mitsubishi
Chemical Corporation), Biscoat 195, Biscoat 230, Biscoat 260,
Biscoat 215, Biscoat 310, Biscoat 214HP, Biscoat 295, Biscoat 300,
Biscoat 360, Biscoat GPT, Biscoat 400, Biscoat 700, Biscoat 540,
Biscoat 3000, and Biscoat 3700 (manufactured by Osaka Organic
Chemical Industry Ltd.), KARAYAD R-526, HDDA, NPGDA, TPGDA, MANDA,
R-551, R-712, R-604, R-684, PET-30, GPO-303, TMPTA, THE-330, DPHA,
DPHA-2H, DPHA-2C, DPHA-21, D-310, D-330, DPCA-20, DPCA-30, DPCA-60,
DPCA-120, DN-0075, DN-2475, T-1420, T-2020, T-2040, TPA-320,
TPA-330, RP-1040, RP-2040, R-011, R-300, and R-205 (manufactured by
NIPPON KAYAKU CO., LTD.), Aronix M-210, M-220, M-233, M-240, M-215,
M-305, M-309, M-310, M-315, M-325, M-400, M-6200, and M-6400
(manufactured by TOA GOSEI CO., LTD.), Light Acrylate BP-4EA,
BP-4PA, BP-2EA, BP-2PA, and DCP-A (manufactured by KYOEISHA
CHEMICAL CO., LTD.), New Frontier BPE-4, BR-42M, and GX-8345
(manufactured by DAI-ICHI KOGYO SEIYAKU Co., LTD.), ASF-400
(manufactured by Nippon Steel Chemical Co, Ltd.), Lipoxy SP-1506,
SP-1507, SP-1509, VR-77, SP-4010, and SP-4060 (manufactured by
SHOWA HIGHPOLYMER CO., LTD.), and NK Ester A-BPE-4 (manufactured by
Shin-Nakamura Chemical Co., Ltd.).
[0129] The content of the (E1) component in the first liquid resin
composition is, per total content of the composition, preferably
0.1 to 25% by weight, more preferably 0.1 to 15% by weight. If the
(E1) component is included as above, radiation-curing property of
the liquid resin composition tends to improve and deformation over
time of the tridimensional modeled article tends not to occur. If
the content of the (E1) component is over 25% by weight, impact
resistance and resistance to fracture of the tridimensional modeled
article tend to decrease.
[0130] (The (F1) Component)
[0131] The (F1) component included in the first liquid resin
composition is one or more sulfur compound selected from the group
consisting of 2-mercaptobenzothiazole,
2-(4-morpholinodithiobenzothinzole, diisopropylxantogendisulfide
and diphenyldisulfide.
[0132] With the inclusion of the (F1) component, change (yellowing)
over time of transparency of the cured article (tridimensional
modeled article) obtained by irradiation of light to the liquid
resin composition, can be sufficiently inhibited even in a
high-temperature environment of 80.degree. C. and 2 hours, for
example.
[0133] Here, 2-(4-morphlinodithio)benzothiazol of the (F1)
component is a compound represented by the formula (8).
Isopropylxantgendisulfide is a compound represented by the formula
(9). Diphenyldisulfide is a compound represented by the formula
(10).
##STR00013##
[0134] The content of the (F1) component in the first liquid resin
composition is, per total content of the composition, preferably 2
to 3% by weight. It is noted that the especially preferred content
of the (F1) component varies within the above range as follows,
depending on the kind of the (F1) component. In case of
2-mercaptobenzothiazole, 0.2 to 1.5% by weight is preferable and
0.2 to 0.7% by weight is more preferable. In case of
2-(4-morpholinodithiobenzothiazole or diisopropylxantogendisulfide,
0.2 to 3% by weight is preferable. Further, in case of
diphenyldisulfide, 1 to 3% by weight is preferable.
[0135] If the content of the (F1) component is less than 0.1% by
weight, inhibiting effect to prevent the tridimensional modeled
article from turning yellow sometimes cannot be attained
sufficiently. On the other hands, if the (F1) component is over 3%
by weight, polymerization is inhibited and therefore a liquid resin
composition is not sufficiently cured so that elastic modulus of
the tridimensional modeled article to be obtained by the
tridimensional modeling method tends to decrease.
[0136] (The (G1) Component)
[0137] The (G1) component included in the first liquid resin
composition is polyether polyol. Through the addition of this (G1)
component, radiation-curing property of the liquid resin
composition is improved, mechanical characteristics, specifically
the elastic modulus of the cured product, is improved, and change
over time of shape and mechanical characteristics of the
tridimensional modeled article obtained by the tridimensional
modeling method can be inhibited.
[0138] A preferred (G1) component is one having three or more
hydroxyl groups in a single molecule, and specifically preferred
one has three to six hydroxyl groups in a single molecule. By using
a polyether polyol having three or more hydroxyl groups in a single
molecule, sufficiently improved effect of radiation-curing property
can be attained, and mechanical characteristics, specifically
elastic modulus, of the tridimensional modeled article to be
obtained can be stabilized.
[0139] Examples of the (G1) component can comprise ones prepared by
modifying trivalent or more, polyvalent alcohols, such as
trimethylolpropane, glycerin, pentaerythritol, sorbitol, sucrose,
and quadrol by cyclic ether compounds such as ethylene oxide (EO),
propylene oxide (PO), butylene oxide, and tetrahydrofuran.
[0140] Specific examples can comprise EO modified
trimethylolpropane, PO modified trimethylolpropane, tetrahydrofuran
modified trimethylol propane, EO modified glycerin, PO modified
glycerin, tetrahydrofuran modified glycerin, EO modified
pentaerythritol, PO modified pentaerythritol, tetrahydrofuran
modified pentaerythritol, EO modified sorbitol, PO modified
sorbitol, EO modified sucrose, PO modified sucrose, and EO modified
quodol. The above polyether polyols can structure the (G1)
component separately or in combination of two or more of them.
[0141] Examples of commercially available (G1) component can
comprise Sunnix TP-400, Sunnix GP-600, Sunnix GP-1000, Sunnix
SP-750, Sunnix GP-250, Sunnix GP-400, and Sunnix GP-600
(manufactured by Sanyo Chemical Industries, Ltd.), TMP-3Glycol,
PNT-4 Glycol, EDA-P-4, and EDA-P-8 (manufactured by Nippon Nyukazai
Co., Ltd.), G-300, G-400, G-700, T-400, EDP-450, SP-600, and SC-800
(manufactured by ADECA Corporation), SCP-400, SCP-1000, and SP-1600
(manufactured by Sakamoto Yakuhin Kogyo Co., Ltd.).
[0142] The content of the (G1) component in the first liquid resin
composition is, per total content of the composition, preferably 1
to 35% by weight, more preferably 1 to 25% by weight, most
preferably 3 to 15% by weight.
[0143] If the (G1) component is less than 1% by weight,
delaying-curing property of the radiation-curing composition
deteriorate, improved effect of radiation-curing property cannot be
attained sufficiently, and possibly the tridimensional modeled
article having good shape-stability and property-stability cannot
be obtained.
[0144] On the other hand, if the content of the (G1) component is
over 35% by weight, radiation-curing property of the liquid resin
composition decreases and elastic modulus of the tridimensional
modeled article obtained by the optical modeling method tends to
decrease.
[0145] (Other Components)
[0146] The first liquid resin composition preferably includes water
as the (H1) component in addition to the above (A1) to (G1)
components. With the inclusion of this (H1) component,
radiation-curing property of the liquid resin composition can be
improved. Further, mechanical characteristics, especially elastic
modulus of the cured article obtained by irradiation of light to
the liquid resin composition is improved and, thus, change over
time of shape and mechanical characteristics of the tridimensional
modeled article by the optical modeling method can be
inhibited.
[0147] The content of the (H1) component in the first liquid resin
composition is, per total content of the composition, preferably
0.1 to 2% by weight, more preferably 0.2 to 1% by weight. If the
(H1) component is less than 0.1% by weight, sensitivity of the
liquid resin composition is likely to change over time and it tends
to be difficult to attain stable modeling. On the other hands, if
more than 2% by weight, elastic modulus of the tridimensional
modeled article obtained by the optical modeling method tends to
decrease.
[0148] The first liquid resin composition may further include a
component other than the (H1) component to improve physical
property and the like of the tridimensional modeled article
produced by the composition. The other component, which can be
arbitrarily added, may comprise a photo-sensitizer (polymerization
accelerator) and reactive diluent, for example.
[0149] Examples of the photo-sensitizer comprise: amine-based
compound such as triethanolamine, methyldiethanolamine,
diethylamine, and diethylamine; thioxanthone; a derivative of
thioxanthone; anthraquinone; a derivative of anthraquinone;
anthracene; a derivative of anthracene; perylene; a derivative of
perylene; benzophenone; and benzoin isopropylether.
[0150] Furthermore, the first liquid resin may further include
various additives as other arbitrary components within a range not
adversely affecting the object and the effect of the present
invention. Examples of these other additives can comprise: polymers
or oligomers such as epoxy resin, polyamide, polyamideimide,
polyurethane, polybutadiene, polychloroprene, polyether, polyester,
styrene-butadiene block copolymer, petroleum resin, xylene resin,
ketone resin, cellulose resin, fluorine-based oligorner,
silicone-based oligomer, and polysulfide-based oligomer;
polymerization inhibitors such as phenothyazine and
2,6-di-tert-butyl-4-methylphenol; polymerization initiator
assistant; leveling agent; wettability improving agent; surface
active agent; plasticizer; ultraviolet light absorber; silane
coupling agent; inorganic filler; elastomer particles; pigment; and
dye.
[0151] (Preparation of the First Liquid Resin Composition)
[0152] The liquid resin composition including the above-mentioned
respective components can be prepared by charging adequate content
of the above respective (A1) to (H1) components, and other
additives into an agitation vessel, and by agitating the contents
normally at temperatures of 30 to 70.degree. C., preferably50 to
60.degree. C. for a period of normally 1 to 6 hours, preferably 1
to 2 hours.
[0153] [Second Liquid Resin Composition]
[0154] Then, preferred embodiment of the second liquid resin
composition according to the present invention is explained.
[0155] The second liquid resin composition includes at least (A2) a
compound represented by the above general formula (1), (B2) a
compound having phenolic hydroxyl group and/or phosphorous ester
group, (C2) a cationic polymerizable compound, (D2) a radical
polymerization initiator, (E2) a radical polymerizable compound,
and (F2) water. Components (A2) to (F2) and other optional
components, which are blended, if necessary, are explained
below
[0156] (The (A2), (C2), (D2), (E2), and (F2) Components)
[0157] The (A2) component included in the second liquid resin
composition is the same as the (A1) component included in the first
liquid resin composition. The second liquid resin composition
includes the compound represented by the aforementioned formula (1)
and, therefore, has superior storage stability and can be converted
into the optically modeled article having superior transparency
after curing. Similarly, in such a (A2) component, the compound
represented by the aforementioned formula (2), which is an impurity
of the compound represented by the aforementioned formula (1), is
included in many cases. The content of the compound represented by
the formula (2) in the second liquid resin composition is, per the
weight of the compound represented by the formula (1), 5% by weight
or less (0 to 5% by weight), preferably 0 to 4% by weight, more
preferably 0 to 3% by weight. In the case where such a condition is
satisfied, storage stability of the liquid resin composition is
good and viscosity increase over time tends to be inhibited.
[0158] The (C2) component is the same as the (C1) component in the
first liquid resin composition. In this (C2) component, it is
preferred that 50% by weight and more of the compound having two or
more alicyclic epoxy groups in a single molecule is included per
total content of the (C2) component. Thus, good curing rate and
mechanical strength can be attained.
[0159] Further, the (D2), (E2), and (F2) components are the same as
the (D1), (E1), and (H1) components in the first liquid resin
composition, respectively.
[0160] (The (B2) Component)
[0161] The (B2) component included in the second liquid resin
composition of the present invention is a compound having phenolic
hydroxide group and/or phosphorous ester group. As such a (B2)
component, there are known antioxidants, and specifically preferred
ones are hindered phenol-based compound and phosphorus-based
compound. With the inclusion of the (B2) component, coloring
(yellowing) over time of the tridimensional modeled article is
effectively reduced. As a result, it becomes possible to maintain
high transparency of the tridimensional modeled article for a long
time after modeling. Examples of the (B2) component can comprise
the following compounds. It is noted that the name described in
parenthesis after the compound name is an example for a trade
name.
[0162] First, as the hindered phenolic compound, the same hindered
phenolic compounds as that in the above (B1) component can be
exemplified.
[0163] The phosphorus-based compounds comprise
tris(2,4-di-tert-butylphenyl)phosphite (Irgafos 168),
bis[2,4-bis(1,1-dimethylethyl)-6-methylphenyl]ethyl ester phosphate
(Irgafos 38), and
6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)-propoxy]-2,4,8,10-tetr-a-ben-
z[d,f][1,3,2]-dioxaphosphepin (Sumilizer GP): (Irgafos is a trade
mark of Ciba Specialty Chemicals K.K., and Sumilizer is a trade
mark of Sumitomo Chemical Co. Ltd.).
[0164] Examples of the commercially available phosphorus-based
compound, which is the (B2) component, comprise Irgafos 168, 12,
and 38 (manufactured by Ciba Specialty Chemicals K.K.), ADK, STAB,
329K, PEP36, and PEP-8 (manufactured by ADECA Corporation),
Sandstab P-EPQ (manufactured by Clariant Inc.), Weston 618, 619G,
and Ultranox 626, (manufactured by General Electric Company), and
Sumilizer GP (manufactured by Sumitomo Chemical Co., Ltd.).
[0165] Of the above-mentioned (B2) components, preferred ones are
pent aerythrityl
-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate],
3,5-bis(1,1-dimethylethyl)-4-hydroxy-benzene propanate,
ethylenebis(oxyethylene)bis[3-(5-tert-butyl-4-hydroxy-m-tolyl)propionate]-
, 4,6-bis(octylthiomethyl)-o-cresol,
bis[2,4-bis(1,1-dimethylethyl)-6-methylphenyl]ethyl ester
phosphite, and
6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)-propoxy]-2,4,8,10-tetra-tert-
-butyl-benz[d,f][1,3,2]-dioxaphosphepin because transparency of the
tridimensional object after modeling can be maintained for a long
time. Of these, pentaerythrityl -tetrakis
[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] is effective.
[0166] Specifically preferred (B2) compound in the second liquid
resin composition is one or more compounds selected from the group
consisting of compounds represented by the formula (5), the formula
(6), and the formula (7) given below:
##STR00014##
wherein R.sup.51 and R.sup.52 are each independently alkyl group
having a carbon number of 1 to 4, which may be branched, in and n
are each independently 1 or 2, p is 1 to 4, and A is hydrogen atom
or an organic group.
[0167] Examples of the A in the formula (5) include a carbon atom,
in which p is 4, and a group represented by
--O--(CH.sub.2).sub.2--O--, in which p is 2, for example. Examples
of commercially available compound having the structure represented
by the formula (5) comprise above-mentioned Irganox 1010, 1035, and
245, and Sumilizer GA-80:
##STR00015##
wherein R.sup.61 and R.sup.62 are each independently an alkyl group
having a carbon number of 6 to 10, which may be branched.
[0168] Commercially available compound represented by the formula
(6) is, for example, Irganox 1520L:
##STR00016##
wherein R.sup.71 is a hydrogen atom, a methyl group, a single bond
combining two aromatic rings, and R.sup.72 is an organic group.
[0169] Examples of commercially available compound represented by
the formula (7) are Irganox 38 and Sumilizer C. P.
[0170] The content of the (B2) component in the second liquid resin
composition is, per total content of the composition, preferably
0.1 to 10% by weight, more preferably 0.1 to 5% by weight, most
preferably 1.0 to 5.0% by weight. If the content of the (B2)
component is less than 0.1% by weight or over 10% by weight, it is
not preferred because transparency of the optically modeled article
decreases over time.
[0171] (Other Components)
[0172] In the second liquid resin composition, various additives as
other arbitrary components can be included within a range not
adversely affecting the object and the effect of the present
invention. Examples of these other additives can comprise: polymers
or oligomers such as epoxy resin, polyamide, polyamideimide,
polyurethane, polybutadiene, polychloroprene, polyether, polyester,
styrene-butadiene block copolymer, petroleum resin, xylene resin,
ketone resin, cellulose resin, fluorine-based oligomer,
silicone-based oligomer, and polysulfide-based oligomer;
polymerization inhibitors such as phenothyazine and
2,6-di-tert-butyl-4-methylphenol; polymerization initiator
assistant; leveling agent; wettability improving agent; surface
active agent; plasticizer; ultraviolet light absorber; silane
coupling agent; inorganic filler; elastomer particles; pigment; and
dye.
[0173] (Preparation of the Second Liquid Resin Composition)
[0174] The second liquid resin composition can be prepared by
charging adequate content of the above respective (A2) to (F2)
components, and other additives into an agitation vessel, and by
agitating the contents normally at temperatures of 30 to 70.degree.
C., preferably 50 to 60.degree. C. for a period of normally 1 to 6
hours, preferably 1 to 2 hours.
[0175] [Third Liquid Resin Composition]
[0176] The third liquid resin composition includes at least (A3) a
compound represented by the aforementioned formula (3), (B3) a
compound having phenolic hydroxyl group and/or phosphorous ester
group, (C3) a cationic polymerizable compound, (D3) a radical
polymerization initiator, (E3) a radical polymerizable compound,
and (F3) polyether polyol compound. Components (A3) to (F3) and
other arbitrary components, which are blended, if necessary, are
explained below.
[0177] (The (A3) Component)
[0178] The (A3) component included in the third liquid resin
composition is the compound having a structure represented by the
following formula (3) and functions as a photo-cationic
polymerization initiator similarly to the above (A1), (A2)
components:
##STR00017##
wherein R.sup.3, if plural, is a monovalent organic group
independently and at least one thereof is a monovalent aromatic
group and n is an integer of 1 to 5.
[0179] The third liquid resin composition improves storage
stability and inhibits viscosity increase over time through the
inclusion of the compound having the structure represented by the
aforementioned formula (3). Further, in the optically modeled
article obtained from the liquid resin composition, a step on the
side face between the respective laminated layers is reduced and
further smooth surface is obtained. Further, because the compound
having the structure represented by the aforementioned formula (3)
does not include an element such as antimony, the liquid resin
composition has further reduced toxicity. Here, commercially
available compound represented by the aforementioned formula (3)
includes the compound represented by the following formula (4) as
an impurity in many cases. In this case, the content of the
compound represented by the following formula (4) is 1/20 or less
(weight ratio) of the content of the compound represented by the
aforementioned formula (3). With the arrangement, storage stability
of the third liquid resin composition is further improved and
viscosity increase over time can be inhibited. Further, a step on
the side face between the respective laminated layers in an
optically modeled article to be obtained is reduced and an
optically modeled article having smoother surface can be
obtained:
##STR00018##
wherein R.sup.4 is a monovalent organic group independently and at
least one thereof is a monovalent aromatic group, and n is an
integer of 1 to 5.
[0180] The content of the (A3) component in the third liquid resin
composition is, per total content of the composition, preferably
0.1 to 10% by weight, more preferably 0.2 to 8% by weight, most
preferably 1 to 8% by weight. If the content of the (A3) component
is less than 0.1% by weight, radiation-curing property of the
liquid resin composition decreases and a tridimensional object
having sufficient mechanical strength cannot be modeled in some
cases. On the other hands, if the content of the (A3) component is
over 10% by weight, when the liquid resin composition is subjected
to an optical tridimensional modeling method, it tends to be
difficult to attain suitable optical transparency and to control
curing depth, and modeling accuracy of a tridimensional object to
be obtained tends to decrease. If the compound represented by the
aforementioned formula (4) is included, it is preferred that the
total content of the compound represented by the aforementioned
formula (3) and the compound represented by the aforementioned
formula (4) satisfies the content of the above-mentioned (A3)
component.
[0181] (The (B3), (C3), (D3), (E3), and (F3) Components)
[0182] The (B3) component is the same as the (B2) component
included in the second liquid resin composition. Because the (B3)
component is included in the third liquid resin composition, curing
of the (E3) component (radical polymerizable compound) is inhibited
certainly. Accordingly, polymerization of the (C3) component
(cationic polymerizable compound) and the like proceeds gradually
even after irradiation of light (delayed curing property). Thus, a
step on the side face between the respective laminated layers of an
optically modeled article to be obtained is reduced and, therefore,
surface smoothness of the optically modeled article is
improved.
[0183] Further, the (C3), (D3), (E3), and (F3) components in the
third liquid resin composition are as the same as the (C1), (D1),
(E1), and (G1) components included in the first liquid resin
composition.
[0184] (Other Components)
[0185] Further, it is more preferred that the third liquid resin
composition includes additionally elastomer particles having a
number average particle size of 10 to 1000 nm, which is measured by
an electron microscope method, as the (G3) component in addition to
the (A3) to (F3) components. Through the inclusion of the (G3)
component, impact resistance and resistance to fracture of a cured
article obtained by irradiating light to the third liquid resin
composition increase.
[0186] Examples of the (G3) component can comprise elastomer
particles with the base component of polybutadiene, polyisoprene,
butadiene-acrylonitrile copolymer, styrene-butadiene copolymer,
styrene-isoprene copolymer, ethylene-propylene copolymer,
ethylene-alpha-olefin copolymer, ethylene-alpha-olefin-polyene
copolymer, acryl rubber, butadiene-(meth)acrylate copolymer,
styrene-butadiene block copolymer, and styrene-isoprene block
copolymer.
[0187] The (G3) component may be core/shell type particles and, of
these above elastomer particles, specifically preferred ones are
prepared by covering a core prepared by partially cross-linked
polybutadiene, polyisoprene, styrene-butadiene copolymer,
styrene-isoprene copolymer, butadiene-(meth) acrylate copolymer,
styrene-butadiene block copolymer, styrene-isoprene block
copolymer, and the like with methylmethacrylate polymer or
methylmethacrylate-glycidylmethacrylate copolymer. As the
commercially available core/shell type elastomer particles, there
are Resinous Bond RKB (manufactured by Resinous Chemicals, Ltd.)
and Techno MBS-61 and MBS-69, (manufactured by Techno Polymer Co.,
Ltd.).
[0188] The content of the (G3) component in the third liquid resin
composition is, per total content of the composition, preferably 1
to 35% by weight, more preferably 2 to 20% by weight, most
preferably 3 to 15% by weight. If the content of the (G3) component
is less than 1% by weight, impact resistance and breaking toughness
of a cured article tends to decrease. On the other hand, if the
content of the (G3) component is over 35% by weight, viscosity of
the composition tends to increase to generate bubbles during
modeling and modeling accuracy of a tridimensional object to be
obtained tends to decrease.
[0189] The third liquid resin composition may further include an
additive such as a photo-sensitizer (polymerization accelerator) or
a reactive diluent other than the above (G3) component, if
necessary. As the additives such as a photo-sensitizer
(polymerization accelerator) or a reactive diluent, the same ones
as exemplified regarding the first liquid resin composition can be
applied.
[0190] (Preparation of the Third Liquid Resin Composition)
[0191] The third liquid resin composition can be prepared by
charging adequate content of the above respective (A3) to (G3)
components, and other additives into an agitation vessel, and by
agitating the contents normally at temperatures of 30 to 70.degree.
C., preferably 50 to 60.degree. C. for a period of normally 1 to 6
hours, preferably 1 to 2 hours. [Optically Modeled Article]
[0192] Then, preferred embodiments of the optically modeled article
obtained through the above-mentioned liquid resin composition and
the method for producing the same are explained.
[0193] The above liquid resin composition is preferably used as the
liquid resin composition for the optical tridimensional modeling
method. That is, a tridimensional object having a desired shape can
be produced by using the optical tridimensional modeling method, in
which lights such as visible light, ultraviolet light, and infrared
light are selectively irradiated to the liquid resin composition,
thus supplying energy necessary to cure the composition.
[0194] According to the liquid resin composition described above,
good storage stability can be obtained and a tridimensional modeled
article can be produced with a high degree of accuracy. The
optically modeled article obtained has excellent characteristics,
in that good transparency can be maintained for a long time because
the degree of yellowing is less in high temperature environments,
or surface smoothness is good because a step on the side face is
reduced, depending on the kind of the liquid resin composition.
[0195] As described above, the optically modeled article according
to the preferred embodiments is obtained by irradiating light to
the above-mentioned liquid resin composition.
[0196] Means to selectively irradiate light to the liquid resin
composition is not specifically limited, and varieties of means can
be applied. Examples of the means are: (a) the one that irradiates
light such as laser light or a light converged by a lens or a
mirror to the composition while scanning the light; (b) the one
that uses a mask which has a light transmitting section to allow a
specific light pattern to pass through, thus irradiating the
non-converged light to the composition via the mask; and (c) the
one that uses a light-guide member fabricated by bundling
pluralities of optical fibers which respond to a specified light
pattern, thus irradiating the light to the composition via the
light-guide. For the means (b) that uses a mask, it is possible to
electro-optically form a mask image composed of the
light-transmitting zone and the light-nontransmitting zone under a
specified pattern utilizing the same principle as that of the
liquid crystal display apparatus.
[0197] Regarding means described above, if the target
tridimensional object has a fine portion or is requested to have
high dimensional accuracy, the means to selectively irradiate light
to the composition is preferably one that scans laser light having
small spot-diameter.
[0198] The irradiated surface (such as scanning plane of converged
light) on the resin composition held in a vessel may be any of the
liquid surface of the resin composition and the contact surface
with the wall of the light-transmitting vessel. When the liquid
surface of the resin composition or the contact surface with the
wall of the vessel is adopted as the irradiation plane of light,
light can be irradiated directly from the outside the vessel or via
the vessel wall.
[0199] According to the optical tridimensional modeling method, a
specified portion of the resin composition is cured, and then the
light-irradiating position (irradiated surface) is moved
continuously or stepwise from the cured portion to the non-cured
portion, thus laminating the cured portions to form the desired
tridimensional shape. The movement of the irradiating position can
be done by varieties of methods, such as: moving any of the light
sources, the vessel holding the liquid resin composition, and the
cured portion of the resin composition; and successively charging
the resin composition to the vessel.
[0200] In the followings, a typical example of the optical
tridimensional modeling method described above is explained. A
supporting stage located in the vessel in an ascending/descending
mode is lowered (immersed) to a slight depth below the liquid
surface of the liquid resin composition, thus charging the resin
composition onto the supporting stage to form the thin layer (1) of
the resin composition. Then, light is selectively irradiated to the
thin layer (1) to form the solid-state cured resin layer (1).
[0201] Subsequently, the liquid resin composition is charged onto
the cured resin layer (1) to form the thin layer (2) of the
composition. Light is selectively irradiated to the thin layer (2),
thus forming the new cured resin layer (2) on the cured resin layer
(1) so as to continuously and integrally laminate together.
[0202] Then, by repeating the steps for a specified number of
cycles while varying or not varying the pattern of light
irradiation, a tridimensional object having integrally-laminated
cured resin layers (n) is modeled.
[0203] Thus obtained tridimensional object is taken out from the
vessel. After removing the non-reacted resin composition left on
the surface of the shape object, cleaning is applied as needed.
Thus, an optically modeled article having a desired shape can be
obtained.
[0204] Examples of cleaning agent are: alcohol-based organic
solvent represented by alcohols such as isopropyl alcohol and ethyl
alcohol; ketone-based organic solvent such as acetone,
ethylacetate, and methylethylketone; aliphatic organic solvent
represented by terpenes; and low viscosity thermosetting resin and
radiation-curing resin.
[0205] Incidentally, post-curing may be conducted by using heat
irradiation or light irradiation as needed after the cleaning with
the cleaning agent. The post-curing cures a non-reacted resin
composition remained in the surface and the inside of the
tridimensional object, and stickiness of the surface of the modeled
article can be suppressed and, further, initial strength of the
modeled article can be improved.
EXAMPLES
[0206] In the followings, the present invention is explained in
more detail by using Examples but the present invention is not
limited to these Examples.
[Preparation of Liquid Resin Composition]The respective components
were charged to an agitation vessel according to the respective
blending formula given in the Table 1 and agitated at 60.degree. C.
for 3 hours, and thus obtained were the respective liquid resin
compositions according to Examples 1 to 10 and Comparative Examples
1 to 2. The blending formula in Table 1 is expressed by parts by
weight.
[Used Components]
[0207] Respective components in Table 1 are as follows.
(A1) Component
[0208] Highly pure product of the compound represented by the
aforementioned formula (1a): This highly pure product is obtained
by refining of CPI-100A (trade name: manufactured by SAN-AFRO
LIMITED) through recrystallization method using THE
[0209] The CPI-100A is a mixture of (1)
diphenyl(phenylthiophenyl)sulfonium hexafluoroantimonate, which is
a compound represented by the formula (1a), and (2)
bis[4-(diphenylsulfonio)phenyl)sulfidebishexafluoroantimonate,
which is a compound represented by the formula (2a), in which the
weight ratio of (2)1(1) is 1/50. The weight ratio of (2)/(1) of the
highly pure product of CPI-100A was confirmed to be not less than
1/50 from the peak area ratio of HPLC.
(B1) Component
[0210] Irganox1010:
entaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]
(manufactured by Ciba Specialty Chemicals K.K.)
(C1-1) Component
[0211] CELOXIDE 2021 P:
3,4-Epoxycyclohexylmethyl-3',4'-epoxycyclohexyl carboxylate
(manufactured by DAICEL CHEMICAL INDUSTRIES, LTD.)
(C1-2) Component
[0212] Epolite 4000: Hydrogenated bisphenol A diglycidyl ether
(manufactured by KYOEISHA CHEMICAL CO., LTD.)
(C1-3) Component
[0213] Alonoxetane OXT-121:
1,4-Bis[(3-ethyl-3-oxetanylmethoxy)methyl]benzene (manufactured by
TOA GOSEI CO., TTD.)
(D1) Component
[0214] Irgacure 184: 1-Hydroxycyclohexylphenylketone (manufactured
by Ciba Specialty Chemicals K.K.)
(E1-1) Component
[0215] SR399E: Dipentaerithritolmonohydroxypentaacrylate
(manufactured by USA Sartomer Company Inc., TOMOE ENGINEERING
CO.,LTD.)
(E1-2) Component
[0216] SR9003: Neopentylglycoldiacrylate (manufactured by USA
Sartomer Company Inc., TOMOE ENGINEERING CO., LTD.)
(E1-3) Component
[0217] DPHA: Dipentaerithritolhexaacrylate (manufactured by NIPPON
KAYAKU CO., LTD.)
(F1-1) Component
[0218] 2-Mercaptobenzothiazole (manufactured by Tokyo Chemical
Industry Co., Ltd.)
(F1-2) Component
[0219] NOCCELER MDS: 2-(4-Morpholinodithiobenzothiazole
(manufactured by OUCH[ SHINKO CHEMICAL INDUSTRIAL CO., LTD.)
(F1-3) Component
[0220] Sanbit DX: Diisopropylxantogendisulfide (manufactured by
SANSHIN CHEMICAL INDUSTRY CO.,LTD.)
(F1-4) Component
[0221] Diphenyldisulfide (manufactured by Tokyo Chemical Industry
Co., Ltd.)
(F') Component (Alternative Product of F1 Component)
[0222] NOCCELER DM: Dibenzothiadildisulfide (manufactured by OUCHI
SHINKO CHEMICAL INDUSTRIAL CO., LTD.)
(G1) Component
[0223] Sunnix GP-600: Polyether polyol (manufactured by Sanyo
Chemical Industries, Ltd.)
(H1) Component
[0224] Water
[Measurement of Content of the Compound having a Structure
Represented by the Formula (2)]
[0225] The content of the compound having a structure represented
by the formula (2) in the liquid resin composition was, in each of
Examples 1 to 10 and Comparative Examples 1 to 2, 1/796 in weight
ratio to the compound having a structure represented by the
aforementioned formula (1). This measurement method was as
follows.
[0226] The liquid resin composition and methanol were well mixed at
the volumetric ratio of 20:80 and, after being stood still for one
hour, the supernatant liquid was filtrated with a filter of 0.45
.mu.m to obtain a sample liquid. This sample liquid was analyzed
with a High-performance liquid chromatography (Column: Intertsil
Ph-3 type manufactured by GL Sciences, Inc., Carrier:
methanol/water=95/5 (0.1.5% sodium perchlorate)). Then, from an
area ratio (detected by a diode allay, analyzed at a wavelength of
300 nm) of peaks originated from the compound represented by the
formula (1) and the compound represented by the formula (2)
respectively, the content ratio of these compounds was
calculated.
[Physical Property Evaluation]
[0227] By using each liquid resin composition of Examples 1 to 10
and Comparative Examples 1 to 2, storage stability thereof, and
Young's modulus and yellowing inhibition in high temperature
environments of the optically modeled article were evaluated. The
evaluation result obtained was shown in Table 1. Each evaluation
method is as follows.
(a) Storage Stability
[0228] 100 Gram of each liquid resin composition was weighted,
charged into a sample bottle and stood still in a
constant-temperature unit at 80.degree. C. After a lapse of 10
days, if viscosity of the liquid resin composition increased to 1.5
times or more of the initial value, the result was judged as "B",
and if viscosity of the liquid resin composition was less than 1.5
times of the initial value, the result was judged as "A".
(b) Young's Modulus
[0229] Young's modulus of cured liquid resin composition each
obtained in Examples or Comparative Examples was measured as
follows. First, the liquid resin composition was applied onto a PET
substrate by means of an applicator bar having a thickness of 381
.mu.m, and cured by irradiating ultraviolet ray having energy of 1
J/cm.sup.2 thereto to give a test film.
[0230] Next, Using the cured sample, a strip-shaped sample having a
extended portion width of 6 mm and a extended portion length of 25
mm was produced. Then, tensile testing was conducted by means of
tensile testing machine at a temperature of 23.degree. C. and a
humidity of 50% according to HS K7127. The tensile rate was set to
1 mm/min and Young's modulus was calculated through a tensile
strength at a distortion of 2.5%.
(c) Inhibition of Yellowing in High-Temperature Environments
[0231] First, by using the Solid Creator SCS-300P (manufactured by
Sony Manufacturing Systems Corporation) and under the scanning rate
condition of a laser power of 100 mW at an irradiated surface
(liquid surface) and a curing depth of 0.2 mm for each composition,
the laser was irradiated selectively to each liquid resin
composition to form a cured resin layer (thickness: 0.10 mm), and
this step was repeated to produce an optically modeled article.
[0232] Concerning each optically modeled article, YI values (yellow
index) were measured by means of a minute area micro
spetrocolorimeter (manufactured by NIPPON DENSHOKU INDUSTRIES CO.,
LTD.; VSS-300H type) immediately after the modeling and after being
stood still for 2 hours at 80.degree. C. Then, difference
(.DELTA.YI) between the YT values obtained immediately after the
modeling and after being stood still for 2 hours at 80.degree. C.
was measured. If the .DELTA.YI was 5 or less, the result was judged
as "A", and if the .DELTA.YI was over 5, the result was judged as
"B".
TABLE-US-00001 TABLE 1 Example Comparative 1 2 3 4 5 6 7 8 9 10 1 2
Component A1 4 4 4 4 4 4 4 4 4 4 4 4 B1 1.25 1.25 1.25 1.25 1.25
1.25 1.25 1.25 1.25 1.25 1.25 1.25 C1-1 31.45 31.25 30.75 30.25
31.25 31.25 29.75 28.75 30.75 29.75 31.75 31.25 C1-2 22 22 22 22 22
22 22 22 22 22 22 22 C1-3 17 17 17 17 17 17 17 17 17 17 17 17 D 3 3
3 3 3 3 3 3 3 3 3 3 E1-1 8 8 8 8 8 8 8 8 8 8 8 8 E1-2 4 4 -- -- 4 4
4 4 4 4 4 4 E1-3 -- -- 4 4 -- -- -- -- -- -- -- -- F1-1 0.3 0.5 1
1.5 -- -- -- -- -- -- -- -- F1-2 -- -- -- -- 0.5 -- -- -- -- -- --
-- F1-3 -- -- -- -- -- 1 2 3 -- -- -- -- F1-4 -- -- -- -- -- -- --
-- 1 2 -- -- F' -- -- -- -- -- -- -- -- -- -- -- 0.5 G1 9 9 9 9 9 9
9 9 9 9 9 9 H1 1 1 1 1 1 1 1 1 1 1 1 1 Total (parts by weight) 101
101 101 101 101 101.5 101 101 101 101 101 101 Tridimensional
modeled article Young's modulus (MPa) 1800 1780 1600 1100 1800 1750
1700 1700 1800 1750 1700 1700 Inhibition of turning A A A A A A A A
A A B A yellow under high temperature environment Liquid resin
composition Storage stability A A A A A A A A A A A B
[0233] From table 1, in Examples 1 to 10, it was revealed that
excellent storage stability of the liquid resin composition and
yellowing-inhibiting effect of the optically modeled article n
high-temperature environments were obtained.
[0234] On the other hands, it was confirmed that
yellowing-inhibiting effect of the optically modeled article in
high-temperature environments was inferior to the above because the
component (F1) was not included in Comparative Example 1. In
Comparative Example 2, storage stability of the liquid resin
composition was inferior to the above because other antioxidant was
included instead of the component (F1).
[Preparation of Liquid Resin Composition]
[0235] The respective components were charged to an agitation
vessel according to the respective blending formula given in the
Table 2 and agitated at 60.degree. C. for 3 hours, and thus
obtained were the respective liquid resin compositions according to
Examples 11 to 14 and Comparative Examples 11 to 18. The blending
formula in Table 2 is expressed by % by weight
[Used Components]
[0236] Respective components in Table 2 are as follows.
(A2-1) Component
[0237] CPI-100A (manufactured by SAN-APRO LIMITED): A mixture of
diphenyl(phenylthiophenyl)sulfonium hexafluoroantimonate, which is
a compound represented by the formula (1a), and
[4-(diphenylsulfonio)phenyl)sulfidebishexafluoroantimonate, which
is a compound represented by the formula (2a), and the content
ratio of the compound represented by the formula (2a) to weight
(100% by weight) of the compound represented by the formula (1) was
2% by weight.
(A2-2) Component
[0238] UVI-6974 (manufactured by D.A.W. CHEMICAL CO., INC.): A
mixture of (1) diphenyl(phenylthiophenyl)sulfonium
hexafluoroantimonate, which is a compound represented by the
formula (1a), and (2)
[4-(diphenylsulfonio)phenyl)sulfidebishexafluoroantimonate, which
is a compound represented by the formula (2a), and the content
ratio of the compound represented by the formula (2a) to weight
(100% by weight) of the compound represented by the formula (1) was
83% by weight.
(A') Component
[0239] SP-172 (manufactured by ADEKA CORPORATION): Photocationic
polymerization initiator, which is not a compound represented by
the formula (1a).
(B2-1) Component
[0240] Irganox1010 (manufactured by Ciba Specialty Chemicals K.K.):
Pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]
(B2-2) Component
[0241] Irganox245 (manufactured by Ciba Specialty Chemicals K.K.):
Triethyleneglycol-bis-[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl)propionat-
e]
(C2-1) Component
[0242] Hydrogenated bisphenol A diglycidyl ether
(C2-2) Component
[0243] Neopentylglycol diglycidylether
(C2-3) Component
[0244] 1,4-Bis[(3-ethyl-3-oxetanylmethoxy)methyl]benzene
(D2) Component
[0245] Irgacure 184 (manufactured by Ciba Specialty Chemicals
K.K.): 1-Hydroxycyclohexylphenylketone
(E2-1) Component
[0246] Dipentaerithritolmonohydroxypentaacrylate
(E2-2) Component
[0247] Neopentylglycoldiacrylate
(F2) Component
[0248] Water
[Calculation of Rate of the Compound Represented by the Formula (2)
and the Compound Represented by the Formula (1) in the Liquid Resin
Composition]
[0249] Each liquid resin composition of Examples 11 to 14 and
Comparative Examples 11 to 18 and methanol were well mixed at the
volumetric ratio of 20:80 and, after being stood still for one
hour, the supernatant liquid was filtrated with a filter of 0.45
.mu.m to obtain a sample liquid. This sample liquid was analyzed
with a High-performance liquid chromatography (Column: Intertsil
Ph-3 type manufactured by GL Sciences, Inc., Carrier:
methanol/water=95/5 (0.15% sodium perchlorate)). Then, from an area
ratio (detected by a diode allay, analyzed at a wavelength of 300
nm) of peaks originated from the compound represented by the
formula (1) and the compound represented by the formula (2)
respectively, the content ratio of these compounds was calculated.
The results obtained from the liquid resin compositions according
to each Examples and Comparative Examples were shown in Table
2.
[Physical Property Evaluation]
[0250] By using each liquid resin composition of Examples 11 to 14
and Comparative Examples 11 to 18, storage stability of the resin
liquid, transparency of the optically modeled article (immediately
after the modeling and after a lapse of time) were evaluated. The
evaluation result obtained is shown in Table 2. Each evaluation
method is as follows.
[0251] (a) Transparency of Optically Modeled Article
[0252] First, by using the Solid Creator SCS-300P (manufactured by
Sony Manufacturing Systems Corporation) and under the scanning rate
condition of a laser power of 100 mW at an irradiated surface
(liquid surface) and a curing depth of 0.2 mm for each composition,
the laser was irradiated selectively to each liquid resin
composition to form a cured resin layer (thickness: 0.10 mm), and
this step was repeated to model a test piece for evaluation.
[0253] Subsequently, the test piece was taken out from the Solid
Creator and washed to remove the liquid resin composition adhered
on the outer surface. Then, the test piece was stood still at a
constant temperature and humidity room at a temperature of
23.degree. C. and a humidity of 50%.
[0254] After the modeling, the transparency was evaluated
concerning the molded article after being stood still for 24 hours
in the constant temperature and humidity room at a temperature of
23.degree. C. and a humidity of 50% (immediately after the
modeling) and the molded article after being stood still for 1
month under luminescent lights (after a lapse of time).
[0255] The evaluation of transparency was conducted by measuring YI
on a surface of the modeled article by means of the minute area
micro spetrocolorimeter (manufactured by NIPPON DENSHOKU INDUSTRIES
CO., LTD.; VSS-300H type). If the YI was 7 or less, the result was
judged as "A", and if the .DELTA.YI was over 7, the result was
judged as "B".
[0256] (b) Storage stability of liquid resin compositions
[0257] 100 Gram of each liquid resin composition was weighted,
charged into a sample bottle and stood still in a
constant-temperature unit at 80.degree. C. After a lapse of 10
days, if viscosity of the liquid resin composition increased to 1.5
times or more of the initial value, the result was judged as "B",
and if viscosity of the liquid resin composition was less than 1.5
times of the initial value, the result was judged as "A",
TABLE-US-00002 TABLE 2 Example Comparative Example 11 12 13 14 11
12 13 14 15 16 17 18 Component A2-1 4.3 4.3 4.3 4.3 4.3 -- -- --
4.3 -- -- -- A2-2 -- -- -- -- -- 4.3 -- -- -- 4.3 -- -- A' -- -- --
-- -- -- 4.3 -- -- -- 4.3 -- B2-1 1.25 -- 1.25 -- -- 1.25 1.25 1.25
-- 1.25 1.25 1.25 B2-2 -- 1.25 -- 1.25 -- -- -- -- -- -- -- -- C2-1
-- -- 52.25 52.25 -- -- -- -- 52.25 52.25 52.25 52.25 C2-2 10 10 10
10 10 10 10 10 10 10 10 10 C2-3 16.5 16.5 16.5 16.5 16.5 16.5 16.5
16.5 16.5 16.5 16.5 16.5 D2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2
3.2 3.2 E2-1 8 8 8 8 8 8 8 8 8 8 8 8 E2-2 4 4 4 4 4 4 4 4 4 4 4 4
F2 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Total (part by
weight) 47.75 47.75 100 100 46.5 47.75 47.75 43.45 98.75 100 100
95.7 Content (% by weight) of the 2 2 2 2 2 83 2 -- 2 83 2 --
compound represented by the formula (2) to the compound represented
by the formula (1) Transparency of tridimensional modeled article
Immediately after the modeling A A A A A A B A A A B A After a
lapse of time A A A A B A B A B A B A Liquid resin composition
Storage stability A A A A A B A B A B A B
[0258] According to the results in table 2, it is found that the
liquid resin compositions of Examples 11 to 14 are superior in
storage stability and transparency of the optically modeled article
(immediately after the modeling and after a lapse of time).
[0259] On the other hands, in Comparative Examples 11 and 15,
transparency of the optically modeled article after a lapse of time
was inferior because the component (B2) was not included, In
Comparative Examples 12 and 16, storage stability of the liquid
resin composition was inferior because the content of the compound
represented by the formula (2a) was over 5% by weight. Further, in
Comparative Examples 13 and 17, transparency of the optically
modeled article (immediately after the modeling and after a lapse
of time) was inferior because other kind of photocationic
polymerization initiator, which is not the (A2) component, was
used. Further, in Comparative Examples 14 and 18, storage stability
of the liquid resin composition was inferior because the (A2)
component was not included.
[Preparation of Liquid Resin Composition]
[0260] The respective components were charged to an agitation
vessel according to the respective blending formula given in the
Table 3 indicated below and agitated at 60.degree. C. for 3 hours,
and thus obtained were the respective liquid resin compositions
according to Examples 21 to 23 and Comparative Examples 21 to 23.
The blending formula in Table 3 is expressed by % by weight.
[Used Components]
[0261] Respective components in Table 3 are as follows.
(A3) Component
[0262] Compound represented by the formula (1): A mixture of the
compound represented by the formula (1) and the compound
represented by the formula (2) but the content of the compound
represented by the formula (2) is 1/20 or less.
(B3-1) Component
[0263] Irganox 1010:
Pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]
(manufactured by Ciba Specialty Chemicals K.K.)
(B3-2) Component
[0264] Irganox1520L: 4,6-Bis(octylthiomethyl)-o-cresol
(manufactured by Ciba Specialty Chemicals K.K.)
(B3-3) Component
[0265] Irganox245:
Triethyleneglycol-bis-[3-(3-tert-butyl-5-methyl-4-hydroxyphenyl)propionat-
e] (manufactured by Ciba Specialty Chemicals K.K.)
(B3-4) Component
[0266] Irgafos38:
Bis[2,4-bis(1,1-dimethylethyl)-6-methylphenyl]ethyl ester phosphite
(manufactured by Ciba Specialty Chemicals K.K.)
(B3-5) Component
[0267] Sumilizer GP:
6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)-propoxy]-2,4,8,10-tetr-a-ter-
t-butylbenz[d,f[1,3,2]-dioxaphosphepin (manufactured by Sumitomo
Chemical Co. Ltd.)
(C3-1) Component
[0268] 3,4-Epoxy cyclohexyl
methyl-3',4'-epoxycyclohexylcarboxylate
(C3-2) Component
[0269] Bis(3,4-epoxycyclohexylmethyl)adipate
(C3-3) Component
[0270] Bisphenol A diglycidyl ether
(C3-4) Component
[0271] 1,6-Hexanediol diglycidylether
(D3) Component
[0272] 1-Hydroxycyclohexylphenylketone
(E3) Component
[0273] Tris (acryloyloxyethyl)isocyanurate
(F3) Component
[0274] PO modified trimethylolpropane
(G3) Component
[0275] Elastomer particles (Resinous Bond RKB manufactured by
Resinous Chemicals, Ltd.)
[Ratio of the Compound Represented by the Formula (2) and the
Compound Represented by the Formula (1) Included in the Liquid
Resin Composition]
[0276] Liquid resin composition of Examples 21 to 25 and
Comparative Examples 21 to 23 and methanol were each well mixed at
the volumetric ratio of 20:80 and, after being stood still for one
hour, the supernatant liquid was filtrated with a filter of 0.45
.mu.m to obtain a sample liquid. This sample liquid was analyzed
with a High-performance liquid chromatography (Column: Intertsil
Ph-3 type manufactured by GL Sciences, Inc., Carrier:
methanol/water=95/5 (0.15% sodium perchlorate)). Then, from an area
ratio (detected by a diode allay, analyzed at a wavelength of 300
nm) of peaks originated from the compound represented by the
formula (1) and the compound represented by the formula (2)
respectively, the content ratio of these compounds was calculated.
The results obtained from the liquid resin compositions according
to each Examples and Comparative Examples were shown in Table
3.
[Physical Property Evaluation]
[0277] By using each liquid resin composition of Examples 21 to 25
and Comparative Examples 21 to 23, storage stability of the resin
liquid, delayed curing property, a step on the side face of the
modeled article were evaluated. The result obtained in each
evaluation is shown in Table 3.
[0278] (Delayed Curing Property)
[0279] For each liquid resin composition, the line image was formed
using the Laser Modeling Machine SCS-300P (D-MEC Ltd.) in which a
single cured line was prepared by drawing a single cycle of 4 cm in
length applying a laser power of 100 mW on the irradiation plane
(liquid surface) under the condition of about 70 mJ/cm.sup.2 of
irradiation amount of light giving 160 .mu.m of curing width at 870
mm/sec of scanning rate. Immediately after the irradiation and
after a lapse of 20 minutes from the irradiation, respectively, the
linear cured product was taken out from the resin liquid to measure
the cured width and the cured depth using an optical
microscope.
[0280] Then the increase of the cured depth D.sub.20-D.sub.0 was
calculated, where D.sub.0 signifies the cured depth immediately
after the irradiation, and D.sub.20 signifies the cured depth at 20
minutes after the irradiation. When the increase in the cured depth
was 40 .mu.m or more, the result was judged as A, when the cured
depth was between 20 and 40 .mu.m, the result was judged as B, and
when the cured depth was not more than 20 .mu.m, the result was
judged as C.
[0281] (Step on the Side Face of the Modeled Article (.mu.m))
[0282] First, by using the Solid Creator SCS-300P (manufactured by
Sony Manufacturing Systems Corporation) and under the scanning rate
condition of a laser power of 100 mW at an irradiated surface
(liquid surface) and a curing depth of 0.2 mm for each composition,
the laser was irradiated selectively to each liquid resin
composition to form a cured resin layer (thickness: 0.10 mm), and
this step was repeated to model a sample for evaluation.
[0283] Subsequently, the sample for evaluation was taken out from
the Solid Creator and washed to remove the liquid resin composition
adhered on the outer surface. Then, the test piece was stood still
for 24 hours at a constant temperature and humidity room at a
temperature of 23.degree. C. and a humidity of 50%. The irregular
portion (step) on the side face of the modeled article was measured
by means of a laser microscope (OPTIPHOT-POL, manufactured by Nikon
Corporation).
[0284] In Comparative Examples 22 and 23, the step on the side face
of the modeled article could not be measured, because no
tridimensional modeled article having sufficient mechanical
strength could be obtained or because the tridimensional modeled
article could not be produced with accuracy due to insufficient
optical transparency, for example.
[0285] (Storage Stability)
[0286] 100 Gram of each liquid resin composition was weighted,
charged into a sample bottle and stood still in a
constant-temperature unit at 80.degree. C. After a lapse of 10
days, if viscosity of the liquid resin composition increased to 1.5
times or more of the initial value, the result was judged as "B",
and if viscosity of the liquid resin composition was less than 1.5
times of the initial value, the result was judged as "A".
TABLE-US-00003 TABLE 3 Example Comparative Example 21 22 23 24 25
21 22 23 Component A3 4.62 4.57 4.57 4.62 4.62 4.67 0.05 12.82 B3-1
1.15 -- -- -- -- -- -- -- B3-2 -- 2.28 -- -- -- -- -- -- B3-3 -- --
2.28 -- -- -- -- -- B3-4 -- -- -- 1.15 -- -- -- -- B3-5 -- -- -- --
1.15 -- -- -- C3-1 23.09 22.83 22.83 23.09 23.09 23.36 24.5 21.37
C3-2 27.71 27.4 27.4 27.71 27.71 28.04 29.4 25.64 C3-3 8.31 8.22
8.22 8.31 8.31 8.41 8.82 7.69 C3-4 3.7 3.65 3.65 3.7 3.7 3.74 3.92
3.42 D3 1.85 1.83 1.83 1.85 1.85 1.87 1.96 1.71 E3 12.01 11.87
11.87 12.01 12.01 12.15 12.74 11.11 F3 8.31 8.22 8.22 8.31 8.31
8.41 8.82 7.69 G3 9.24 9.13 9.13 9.24 9.24 9.35 9.8 8.55 Total 100
100 100 100 100 100 100 100 Content ratio of the 1/50 1/50 1/50
1/50 1/50 1/50 1/50 1/50 compound represented by the formula
(2)/the compound represented by the formula (1) Delayed curing
property A A A A A C C C Step on the side face of 6 7 6 7 6 15
unmeasurable unmeasurable laminated layers of the modeled article
(.mu.m) Storage stability A A A A A A A B
[0287] From table 3, in Examples 21 to 25, good delayed curing
property could be obtained, the step on the side face of laminated
layers of the modeled article was small, and superior storage
property could be obtained. On the other hands, it was found that,
in Comparative Examples 21 to 23 in which the (B3) component was
not included, delayed curing property was inferior and the step on
the side face of laminated layers of the modeled article was large.
In Comparative Examples 22 and 23, the step on the side face of the
laminated layers of the modeled article could not be measured,
because no tridimensional modeled article having sufficient
mechanical strength could be obtained or because the tridimensional
modeled article could not be produced with good accuracy due to
insufficient transparency, for example.
* * * * *