U.S. patent application number 12/888871 was filed with the patent office on 2011-03-31 for coated water soluble nanoparticles.
This patent application is currently assigned to Agency for Science, Technology and Research. Invention is credited to Subramanian T. Selvan, Timothy T. Tan, Jackie Y. Ying.
Application Number | 20110073811 12/888871 |
Document ID | / |
Family ID | 35757751 |
Filed Date | 2011-03-31 |
United States Patent
Application |
20110073811 |
Kind Code |
A1 |
Ying; Jackie Y. ; et
al. |
March 31, 2011 |
COATED WATER SOLUBLE NANOPARTICLES
Abstract
Nanoparticles and methods of making nanoparticles are provided.
The nanoparticles may include semiconductor nanocrystals. A shell
may encapsulate a nanoparticle core, and the shell may include
non-organic material and may be silica. The shell may also include
additional species such as PEG. In some embodiments, a passivation
layer is in contact with the core.
Inventors: |
Ying; Jackie Y.; (Singapore,
SG) ; Selvan; Subramanian T.; (Singapore, SG)
; Tan; Timothy T.; (Singapore, SG) |
Assignee: |
Agency for Science, Technology and
Research
Connexis
SG
|
Family ID: |
35757751 |
Appl. No.: |
12/888871 |
Filed: |
September 23, 2010 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12144070 |
Jun 23, 2008 |
7824731 |
|
|
12888871 |
|
|
|
|
10911402 |
Aug 4, 2004 |
7405002 |
|
|
12144070 |
|
|
|
|
Current U.S.
Class: |
252/500 |
Current CPC
Class: |
Y10T 428/2993 20150115;
Y10S 977/777 20130101; C30B 29/60 20130101; Y10T 428/2998 20150115;
Y10S 977/773 20130101; Y10T 428/2991 20150115 |
Class at
Publication: |
252/500 |
International
Class: |
H01B 1/12 20060101
H01B001/12 |
Claims
1. A semiconductor nanocrystal solution comprising: an aqueous
solution having a pH of less than about 8.0; a plurality of
semiconductor nanocrystals dissolved in the aqueous solution
wherein at least 90% of the semiconductor nanocrystals, by weight,
remain dissolved for greater than 6 hours.
2. The semiconductor nanocrystal solution of claim 1 wherein the
aqueous solution is a biological fluid.
3. The semiconductor nanocrystal solution of claim 1 wherein the
aqueous solution is mammalian blood.
4. The semiconductor nanocrystal solution of claim 1 wherein the
aqueous solution has a pH of less than equal to 7.0.
5. The semiconductor nanocrystal solution of claim 1 wherein the
semiconductor nanocrystals comprise polyethylene glycol.
6. A semiconductor nanocrystal wherein the nanocrystal is soluble
in water at a pH of less than about 8.0.
7. The semiconductor nanocrystal of claim 6 wherein the nanocrystal
comprises a shell comprising silica.
8. The semiconductor nanocrystal of claim 7 wherein the shell
includes a polyethylene glycol.
9. The semiconductor nanocrystal of claim 8 wherein the
polyethylene glycol has a molecular weight of about 5,000 to
10,000.
10. A nanoparticle comprising a silica shell encapsulating a core,
the silica shell including polyethylene glycol, or a derivative
thereof.
11. The nanoparticle of claim 10 wherein the polyethylene glycol
has a molecular weight of about 5,000 to about 10,000.
Description
RELATED APPLICATIONS
[0001] This application is a divisional of U.S. patent application
Ser. No. 12/144,070, entitled "Method of Forming Coated
Water-Soluble Nanoparticles by Inverse Emulsion" and having a
filing date of Jun. 23, 2008, which is a divisional of U.S. patent
application Ser. No. 10/911,402, entitled "Coated Water Soluble
Nanoparticles" and having a filing date of Aug. 4, 2004, which are
incorporated herein by reference in their entirety for all
purposes.
BACKGROUND OF INVENTION
[0002] 1. Field of the Invention
[0003] The invention relates to nanoparticles and methods for
making nanoparticles, and in particular, to semiconductor
nanocrystals that exhibit improved hydrophilicity.
[0004] 2. Discussion of Related Art
[0005] Nanoparticles are microscopic particles of matter having
dimensions on the nanometer scale. Of particular interest are a
class of nanoparticles known as semiconductor nanocrystals, or
quantum dots, that exhibit properties that make them particularly
useful in a variety of applications. Because of quantum confinement
effects, semiconductor nanocrystals can exhibit size-dependent
optical properties. The particles give rise to a class of materials
whose properties include those of both molecular and bulk forms of
matter. When these nanoparticles are irradiated, more energy is
required to promote the electrons to a higher state, leading to an
increase in energy release in the form of photons and light
emission in a color that is characteristic of the material. The
resulting photons that are released typically exhibit a shorter
wavelength than those released from a bulk form of the same
material. The quantum confinement of electrons and holes in three
dimensions contributes to an increasing effective band gap with
decreasing nanocrystal size. Therefore, smaller nanocrystals
typically exhibit shorter emitted photon wavelength. For example,
nanocrystals of cadmium selenide (CdSe) can emit across the entire
visible spectrum when the size of the crystal is varied over the
range of from two to six nanometers.
[0006] Another aspect of semiconductor nanocrystals is that
crystals of a uniform size typically are capable of a narrow and
symmetric emission spectrum regardless of excitation wavelength.
Thus, if nanocrystals of different sizes are employed, different
emission colors may be simultaneously obtained from a common
excitation source. These capabilities contribute to the
nanocrystals' potential as diagnostic tools, for example, as
fluorescent probes in biological labeling and diagnostics. These
nanocrystals, or quantum dots, exhibit high emission stability over
long periods of time, thus providing advantages over conventional
biological probing dyes. One class of semiconductor nanocrystals
are the cadmium chalcogenides. These include, for example, cadmium
selenide and cadmium telluride nanoparticles.
[0007] It is known that improved quantum yields of semiconductor
nanocrystals can be obtained by passivating the nanocrystals by
reducing the incident of surface non-radiative recombination sites.
Surface passivation can be achieved, for example, by coating a
material around the nanocrystals. See, e.g., Alivisatos et al.,
U.S. Pat. No. 6,255,198. The coatings can be inorganic or organic
although inorganically coated quantum dots are typically more
robust and exhibit less degradation of photo luminescence quantum
yield in solution than do organically passivated quantum dots.
[0008] For semiconductor nanocrystals to be useful in biological
applications, it is preferred that the crystals are water soluble,
photo-stable and non-toxic. Some quantum dots may exhibit water
solubility but are typically not photo-stable and are toxic. Other
nanocrystals have been coated, for example, with short chain water
soluble molecules, such as thiols, to render the nanocrystals
soluble. However, these organically coated quantum dots have been
shown to be unstable and exhibit deteriorating photo-luminescent
properties. Others, such as Bawendi et al. in U.S. Pat. Nos.
6,319,426 and 6,444,143, hereby incorporated by reference, have
synthesized semiconductive nanocrystals having an organic layer
that also includes linking groups for the attachment of hydrophilic
groups that can provide improved water solubility.
[0009] Some have proposed coating nanocrystals using silicate as a
precursor. These methods use silane as a surface primer to deposit
a thin shell of silica in water. The silica shell can then be
thickened using the Stober method. These procedures, however, are
complicated and time-consuming. Others have used microemulsions as
a technique for silica coating. In particular, using reverse
microemulsions, monodispersed silica particles can be synthesized.
Encapsulation of nanoparticles within silica can lead to an
enhancement in chemical stability and photo-stability. This has
been done in nanoparticles having a zinc sulfide (ZnS) core/two
photon dye/silica particles and the encapsulated dye within the
silica shell has exhibited enhanced luminescence and lifetime.
However, synthesized TOPO semiconductor nanocrystals are water
insoluble and thus silica cannot be precipitated with the
nanocrystals within the aqueous domains of the microemulsion.
SUMMARY OF INVENTION
[0010] The invention is directed, in part, to nanoparticles,
soluble nanoparticles and methods for making nanoparticles.
[0011] In one aspect, a coated nanoparticle is provided, the
nanoparticle comprising a core comprising a semiconductor material,
a non-semi-conductor passivation layer contacting at least a
portion of the core, and a non-organic shell encapsulating at least
partially the core and the passivation layer.
[0012] In another aspect, a method of making a water-soluble
nanoparticle is provided, the method comprising contacting an amine
with a nanoparticle to modify the nanoparticle surface, suspending
the nanoparticle in an aqueous-in-nonaqueous emulsion, introducing
a silica precursor to the emulsion, and polymerizing the silica
precursor to form a silica shell that at least partially
encapsulates the nanoparticle.
[0013] In another aspect, a semiconductor nanocrystal solution is
provided, the solution comprising an aqueous solution having a pH
of less than about 8.0, a plurality of semiconductor nanocrystals
dissolved in the aqueous solution wherein at least 90% of the
semiconductor nanocrystals, by weight, remain dissolved for greater
than 6 hours.
[0014] In another aspect, a semiconductor nanocrystal is provided
wherein the nanocrystal is soluble in water at a pH of less than
about 8.0.
[0015] In another aspect, a nanoparticle is provided, the
nanoparticle comprising a silica shell encapsulating a core, the
silica shell including polyethylene glycol, or a derivative
thereof.
BRIEF DESCRIPTION OF DRAWINGS
[0016] The accompanying drawings, are not intended to be drawn to
scale. In the drawings, each identical or nearly identical
component that is illustrated in various figures is represented by
a like numeral. For purposes of clarity, not every component may be
labeled in every drawing. In the drawings:
[0017] FIG. 1 is a schematic illustration of a silica-coated CdSe
semiconductor nanocrystal.
[0018] FIG. 2 is a schematic illustration of a coated nanocrystal
with a shell including long chain hydrophilic species.
[0019] FIG. 3 is a schematic illustration of a nanoparticle
including a shell and a passivation layer.
[0020] FIG. 4 illustrates a nanoparticle core in contact with an
amino silane surface cap and a surfactant.
[0021] FIG. 5 illustrates a nanoparticle core with exchanging
surfactants and a silica shell.
[0022] FIGS. 6a-6c provide a schematic diagram describing the
encapsulation of hydrophobic semiconductor nanocrystals within the
aqueous domains of a reverse microemulsion, using the interaction
of hydrophilic groups (polar ends) of two different surfactants,
TOPO and IGEPAL.
[0023] FIGS. 7a-7c provide a schematic diagram describing steps
that can result in the encapsulation of hydrophobic semiconductor
nanocrystals (QDs) within a silica shell. The steps include
micellar collisions, nucleation and polymeric growth of
monomers.
[0024] FIG. 8 is a photocopy of a transmission electron micrograph
(TEM) of CdSe/ZnS QD-silica core-shell structures having a diameter
of about 6 nm encapsulated within an approximately 22 nm silica
shell using a microemulsion technique. The majority of single QDs
are encapsulated within a single silica shell.
[0025] FIG. 9 is a photocopy of a transmission electron micrograph
(TEM) of CdSe/ZnS QD-silica core-shell structures having a diameter
of about 6 nm encapsulated within an approximately 100 nm silica in
the microemulsion.
[0026] FIG. 10 illustrates graphically the effect of TEOS
concentration on silica shell thickness and also on the quantum
yield (QY) relative to uncoated CdSe/ZnS nanoparticles.
[0027] FIG. 11 shows the absorption and emission spectra of
CdSe/ZnS semiconductor nanoparticles with and without silica
coating.
[0028] FIG. 12 graphically compares the photo-stability of
silica-coated CdSe/ZnS semiconductor nanocrystals with
organic-coated semiconductor nanoparticles.
[0029] FIGS. 13a-c illustrate the changes of emission intensity of
core semiconductor nanocrystals with various silica coating times.
Volume of TEOS (V.sub.TEOS) added into the microemulsion is
indicated.
[0030] FIG. 14a shows the relative emission intensity versus
coating time at various TEOS concentrations for core semiconductor
nanocrystals.
[0031] FIG. 14b shows the emission wavelength versus coating time
at various TEOS concentrations for core semiconductor
nanocrystals.
[0032] FIG. 14c shows the relative emission intensity versus TEOS
concentrations at 2 hours coating time for core semiconductor
nanocrystals.
[0033] FIGS. 15a-c illustrate the changes of emission intensity of
APS-modified core semiconductor nanocrystals upon various silica
coating times. Volume of TEOS (V.sub.TEOS) added into the
microemulsion is indicated.
[0034] FIG. 16a shows the relative emission intensity versus
coating time at various TEOS concentrations for APS-modified core
semiconductor nanocrystals.
[0035] FIG. 16b shows the emission wavelength versus coating time
at various TEOS concentrations for APS-modified core semiconductor
nanocrystals.
[0036] FIG. 16c shows the relative emission intensity versus TEOS
concentrations at 8 hours coating time for APS-modified core
semiconductor nanocrystals.
[0037] FIG. 17a is a photocopy of a high-resolution TEM micrograph
of silica-coated CdSe semiconductor nanocrystals in water.
[0038] FIG. 17b shows the EDX mapping of silica-coated CdSe
semiconductor nanocrystals in water.
[0039] FIG. 18a shows the photo-stability of CdSe semiconductor
nanocrystals coated with silica in PBS/H.sub.2O with and without
APS. For comparison, core semiconductor nanocrystals in toluene are
shown.
[0040] FIG. 18b depicts the increase in percentage of Quantum Yield
for silica-coated CdSe Semiconductor nanocrystals relative to the
uncoated CdSe semiconductor nanocrystals in toluene after
irradiation with 365 nm excitation for 24 hours.
[0041] FIG. 19 graphically illustrates silica coating time vs.
quantum yield for CdSe/ZnS semiconductor nanocrystals.
[0042] FIG. 20 is a photocopy of a micrograph illustrating single
cores of CdSe/ZnS encapsulated within single shells of silica
having a diameter of about 25 nm.
[0043] FIG. 21 graphically illustrates coating time vs. quantum
yield for different water concentrations in the microemulsion.
[0044] FIG. 22a is a photocopy of a micrograph showing consistent
shell thickness, improved sphericity and improved monodispersity at
increasing amounts of TEOS.
[0045] FIG. 22b is a bar graph showing improved quantum yield with
greater amounts of TEOS.
DETAILED DESCRIPTION
[0046] The present invention relates to nanoparticles, and methods
of making nanoparticles, that can exhibit improved quantum yield,
and/or improved water solubility, and/or improved photo-stability,
and/or improved photo-luminescence. The nanoparticles may include a
non-semiconductor and/or non-metallic and/or non-inorganic
passivation layer. The passivation layer may be amorphous, i.e., it
lacks a crystalline structure. One preferred form of amorphous
passivation layer is one comprising a material such as an amino
silane. In addition, the nanoparticles may include a silica shell
that partially or totally encapsulates the nanoparticle core. In
some cases, the silica shell may be derivatized with, for example,
polyethylene glycol (PEG) or other materials that provide improved
characteristics, such as water solubility. Nanoparticles of
improved quantum yield, stability, solubility and/or
biocompatibility can lead to improved methods, such as, for
example, medical diagnostics.
[0047] The term "nanoparticle" is used herein as it is known in the
art and typically refers to particles having a dimension of less of
100 nanometers. One class of nanoparticles are the "semiconductor
nanocrystals" or "quantum dots" that can provide unique emission
spectra dependent, in part, on the size of the specific
particle.
[0048] A "passivation" layer is a material associated with the
surface of a semiconductor nanocrystal that serves to eliminate
energy levels at the surface of the crystal that may act as traps
for electrons and holes that degrade the luminescent properties of
the nanocrystal. An example is a ZnS layer surrounding a CdSe
semiconductor nanoparticle. Passivation layers result in improved
quantum yields when compared to untreated particles.
[0049] An "emulsion" is a dispersion of a non-aqueous solvent and
an aqueous solvent. A "reverse emulsion" or "aqueous in non-aqueous
emulsion" is a dispersion of discrete areas of aqueous solvent
(aqueous phase) within a non-aqueous solvent.
[0050] A "shell" is a layer that surrounds or partially surrounds a
nanoparticle core and in some cases may be chemically bound to the
nanoparticle, such as by ionic or covalent bonding, and in other
cases is not bound to the nanoparticle core. The shell forms part
of the nanoparticle.
[0051] A "surfactant" is a material exhibiting amphiphilic
properties and is used herein as it is commonly used in the art,
e.g., for introducing hydrophobic species to hydrophilic
environments.
[0052] The term "water soluble" is used herein as it is commonly
used in the art to refer to the dispersion of a nanoparticle in an
aqueous environment. "Water soluble" does not mean, for instance,
that each material is dispersed at a molecular level. A
nanoparticle can be composed of several different materials and
still be "water soluble" as an integral particle.
[0053] A "biological fluid" is a fluid present in or obtained from
animal or plant and is typically aqueous in nature. Biological
fluids include, for example, blood, urine, lymph, saliva, sweat,
and tears.
[0054] A "precursor" is a substance that can be transformed into a
second substance that exhibits different properties from the first.
For example, a monomer is a polymer precursor if it can be
transformed into a polymer.
[0055] In one aspect, a nanoparticle includes a shell that
encapsulates or partially encapsulates the nanoparticle. In some
embodiments, the shell is not chemically bound to the nanoparticle
and yet may contain the nanoparticle by encapsulation. Thus, the
nanoparticle and shell may be devoid of ionic bonds and/or covalent
bonds between the two. The shell may be non-organic and may be a
silicon polymer such as silica. A non-organic shell is one that is
not based on carbon and polymers of carbon, but nonetheless may, in
some cases, include carbon atoms.
[0056] FIG. 1 shows schematically one embodiment of the invention.
Nanoparticle 100 includes a core 110 and a shell 120. Shell 120 can
be chemically bound or unbound to the core 110. The core can be a
semiconductor material such as a semiconductor nanocrystal (quantum
dot). The shell may be generally spherical and may have a mean
diameter that is about 1.5.times., 2.times., 5.times., 10.times. or
>10.times. the diameter of the core. Typically, a single core is
encapsulated by a single shell although in some embodiments, two or
more cores may be contained within a single shell.
[0057] In another aspect of the invention, a semiconductor
nanocrystal includes a passivation layer. In some embodiments, the
passivation layer may be of a material that is non-conductive
and/or non-semiconductive. For example, the passivation layer may
be of a material that does not exhibit a higher band gap than a
nanocrystal which it surrounds. In specific embodiments, the
passivation layer may be non-ionic and non-metallic. A
non-conductive material is a material that does not transport
electrons when an electric potential is applied across the
material.
[0058] FIG. 3 illustrates schematically and not to scale a
nanoparticle 200 including a core 210, a surface passivation layer
230 and a shell 220. The shell may be organic or non-organic and
may comprise a non-organic polymer such as silica. In this
embodiment, passivation layer 230 is a non-semiconductor and is
preferably an amino (NH.sub.2) silane, such as aminopropyl
trimethoxysilane (APS). The inclusion of this passivation layer has
been shown to provide a quantum yield of about 10-30% or 10-20% in
aqueous media.
[0059] FIG. 4 illustrates schematically an amino silane modifying
the surface of a nanocrystal core to form a passivation layer. The
passivation layer can be comprised of, or consist essentially of, a
compound exhibiting a nitrogen-containing functional group, such as
an amine. The amine may be bound directly or indirectly to one or
more silicon atoms such as those present in a silane or other
silicon polymer. The silanes may include any additional functional
group such as, for example, alkyl groups, hydroxyl groups,
sulfur-containing groups, or nitrogen-containing groups. Compounds
comprising the passivation layer may be of any size but typically
have a molecular weight of less than about 500 or less than about
300. The preferred class of compounds are the amino silanes and in
some embodiments, amino propyl trimethoxysilane (APS) can be used.
The use of APS in semiconductor nanocrystals has been shown to
provide passivation and to improve quantum yields to a level
comparable to the improvements obtained by the use of higher band
gap passivation layers such as those made of zinc sulfide
(ZnS).
[0060] Nanoparticles including a silica shell will, of course, be
of greater dimensions than a similar nanoparticle absent the shell.
For example, nanoparticles of the invention may exhibit mean
diameters of less than 100 nm, less than 50 nm, or less than or
equal to about 25 nm. In other embodiments, the mean diameter of
the nanoparticle including the shell may be greater than 5 nm,
greater than 10 nm, greater than 20 nm, or greater than or equal to
about 25 nm.
[0061] In some embodiments, a silica shell can be functionalized or
derivatized to include compounds, atoms, or materials that can
alter or improve properties such as water solubility, water
stability, photo-stability and biocompatibility. For example, a
silica shell can include moieties such as polyethylene glycol (PEG)
and other glycols. These nanoparticles, with and without PEG, have
been shown to be non-toxic to living cells for extended periods,
and it is believed that the nanoparticles are also non-toxic in
vivo due, at least in part, to the isolation of the toxic core
within the polymerized silica shell.
[0062] As shown in FIG. 2, a shell 120, that may be non-organic,
can include hydrophilic species 130 that can provide greater
hydrophilicity to the nanoparticle. Hydrophilic species 130 can be,
for example, a polyethylene glycol (PEG) or a derivative of
polyethylene glycol. Derivatives include, but are not limited to,
functionalized PEGs, such as amine, thiol and carboxyl
functionalized PEG. The hydrophilic species 130 is associated with
the shell 120 and can be chemically bound to the shell 120 or can
be, for example, physically trapped by the shell material.
Preferably, hydrophilic species 130 includes a portion that can be
chemically bonded to the shell and a second portion that provides
hydrophilicity and may extend outwardly from the surface of the
shell.
[0063] Presence of these glycols can impart superior water
solubility characteristics to the nanoparticles while being
biocompatible and nontoxic and can, in some instances, provide for
better dispersion of the nanoparticles in solution. For example, by
integrating PEG into the silica shell, the semiconductor
nanocrystal may be rendered water soluble at pHs of less than 8,
less than or equal to 7.5, less than or equal to 7 or less than or
equal to 6.5. Thus, these nanoparticles may be water soluble at
neutral or below neutral pHs and thus may be biocompatible and
appropriate for use in biological fluids such as blood and in vivo.
In some embodiments, the inclusion of PEG into the silica shell
provides for a nanoparticle that can remain in solution for a
period of greater than 1 hour, greater than 6 hours, greater than
12 hours or greater than 1 day. In addition, the presence of PEG or
related compounds in the silica shell can provide for a
nanoparticle exhibiting a reduced propensity to adsorb protein,
cells, and other biological materials. This means that, for
example, when used in vivo, the particles can stay in solution for
a longer period of time than do similar particles, thus allowing
for increased circulation and improved deliverability to intended
targets.
[0064] One embodiment is shown in FIG. 5 that illustrates
schematically the formation of a silica shell 120 around a CdSe
core 110. Portions of two surfactants, TOPO 140 and IGEPAL 150, are
shown. TOPO includes the hydrophilic group phosphine oxide and
IGEPAL includes the hydrophilic group PEO. The source of the IGEPAL
150 is the reverse microemulsion (aqueous in non-aqueous) and the
source of the TOPO is the TOPO capped semiconductor nanocrystal.
FIGS. 6a-6c illustrate how the reverse micelles can present the
nanocrystal cores for encapsulation at the water/oil interface.
Thus, while the nanocrystals may be transported to the aqueous
phase, the formation of the silica polymer tends to occur around
the nanocrystals at the aqueous/non-aqueous interface. FIGS. 7a-7c
illustrate the formation of a silica shell around a nanoparticle
core at the oil/water (cyclohexane/water) interface.
[0065] The aqueous in non-aqueous microemulsion can be produced
using a variety of non-polar solvents. Preferably the non-polar
solvent is a hydrocarbon and may be an aliphatic hydrocarbon and in
a more preferred embodiment is a non-aromatic cyclic hydrocarbon
such as cyclopentane, cyclohexane or cycloheptane.
[0066] In one embodiment, a semiconductor nanocrystal including a
core of a cadmium chalcogenide is coated with a passivation layer
comprising an amine. The core, that may include cadmium selenide or
cadmium telluride, for example, can be made using methods known to
those skilled in the art. An aqueous in non-aqueous reverse micro
emulsion can be prepared, using for example, an ionic or non-ionic
surfactant. Non-ionic surfactants include, for example, polyphenyl
ethers, such as IGEPAL CO-520, while ionic surfactants include, for
example, dioctyl sulfosuccinate sodium salt (AOT). As
conventionally prepared, the calcium chalcogenide core is typically
presented with a trioctyl phosphine oxide (TOPO) surfactant. TOPO
includes a hydrophilic end comprising phosphine oxide while IGEPAL
includes a hydrophilic end comprising polyoxyethylene (PEO). After
introduction of the TOPO semiconductor nanocrystals into the
reverse emulsion, the TOPO can be partially or completely exchanged
for IGEPAL due, in part, to the much higher concentration of IGEPAL
in the reverse emulsion.
[0067] Upon the exchange of TOPO for IGEPAL, the semiconductor
nanocrystal cores are amenable to the aqueous domains in the
reverse emulsion and a sol-gel precursor, such as
tetraethylorthosilicate (TEOS) can be polymerized using methods
known to those skilled in the art, around the core to produce a
silica shell. The resulting nanostructure includes a core of a
cadmium chalcogenide, a passivation layer of an amino silane such
as APS and a hydrophilic shell, such as a shell of polymerized
silica. Surfactants other than IGEPAL may be used and may be
varied, in part, depending upon the core material, how the
nanoparticle core is capped and the reverse emulsion that is used.
Preferred surfactants are those that can be exchanged for TOPO or
other surfactants that are used to cap the core and that also
provide enough hydrophilicity to draw the core into aqueous
portions of the micro-emulsion, thus providing an environment for
the formation of the silica shell.
[0068] In another aspect, a method of making a nanoparticle
including a silica shell modified to improve bio compatibility
and/or water solubility is provided. For example, in some
embodiments a PEG modified silica shell can be formed around a
nanoparticle. The nanoparticle core may be a semiconductor
nanocrystal or other nanoparticle. As described above, the
nanoparticle core may be introduced into a reverse micro-emulsion
(aqueous in non-aqueous emulsion) to prepare it for encapsulation.
In another step, a base such as ammonia (NH.sub.4OH) including a
glycol such as polyethyleneglycol monomethylether (PEG-m) can be
dissolved into the microemulsion. The PEG may be of any molecular
weight, but it is preferably of a molecular weight of greater than
1,000 and less than 20,000 and in some embodiments, is in a range
of between 5,000 and 10,000. A sol-gel precursor such as TEOS can
then be added and the mixture can be stirred allowing the PEG to be
incorporated into the forming silica shell. The resulting silica
shell derivatized with PEG can provide for improved quantum yield,
improved water solubility, improved biocompatibility in a reduced
propensity to coagulate.
[0069] In one embodiment, ammonia and PEG are stirred into the
microemulsion before a sol-gel precursor such as TEOS is added.
After addition of the sol-gel precursor, the microemulsion can be
stirred continuously until a preferred amount of silica
polymerization has taken place. During this time, the PEG is
incorporated into the silica shell and can alter the properties of
the silica shell by, for example, increasing hydrophilicity,
altering the nanoparticle's propensity to adsorb materials such as
proteins in cells, and can increase repulsion forces between
particles, providing for an extended period of suspension of the
particles without coalescing.
[0070] The amount of water (29.5% aqueous NH.sub.4OH) in the
aqueous in non-aqueous (reverse) microemulsion can be varied based
upon the specific reaction that is desired. For example, in some
embodiments the amount of water in the reverse microemulsion is
between 0.2 and 0.5 percent by volume. In preferred embodiments,
the amount of water is between 0.3 and 0.4 percent by volume and in
some embodiments it has been found that quantum yield can be
maximized when the amount of water in the reverse microemulsion is
about 0.3 percent by volume.
[0071] The amount of sol-gel precursor added to the microemulsion
can also affect the properties of the nanoparticle. For example,
while an increase in the amount of sol-gel precursor does not
appear to increase the shell thickness, an increase in the amount
of sol-gel precursor does appear to improve this sphericity as well
as the monodispersity of the particles. In some embodiments,
quantum yield is also improved with higher concentrations of
sol-gel precursor. For example, see FIGS. 20A and 20B.
EXAMPLES
Example 1
Preparation of Silica-Coated ZnS-Capped CdSe Nanocrystals
(CdSe/ZnS/SiO.sub.2) in Reverse Microemulsion
Aqueous in Non-Aqueous Emulsion
[0072] CdSe/ZnS semiconductor nanocrystals with excess TOPO without
any surface modification were prepared according to literature
procedures (Hines et al., "Synthesis and Characterization of
Strongly Luminescing ZnS-Capped CdSe Nanocrystals" J. Phys. Chem.
100, 468-471, 1996. Dabbousi et al., "(CdSe)ZnS Core-Shell Quantum
Dots: Synthesis and Characterization of a Size Series of Highly
Luminescent Nanocrystallites" J. Phys. Chem. B 101, 9463-9475,
1997.). The particles had luminescence quantum yields of 10-25% and
emission at 625 nm (FWHM=30 nm). The particles were precipitated
once from methanol to remove excess TOPO and trioctylphosphine
oxide (TOP). Inverse micelles were prepared using a non-ionic
surfactant such as Igepal CO-520 and cyclohexane as solvent.
[0073] FIGS. 6 and 7 depict the schemes of the transformation of
hydrophobic semiconductor nanocrystal into aqueous domains of the
reverse microemulsion and silica coating, respectively. Typically,
core-shell semiconductor nanocrystals passivated with TOPO and
dissolved either in butanol or n-hexane were injected into the
reverse micelles. This was followed by the addition of TEOS and was
allowed to stir for 1 hour. Addition of ammonia resulted in a
stable water-in-oil reverse microemulsion. The resulting solution
was stirred for 24 hours, which resulted in homogeneous silica
deposition. Due to the large excess of Igepal, the TOPO ligand was
exchanged for Igepal in cyclohexane and the semiconductor
nanocrystals became more hydrophilic. The nanocrystals were then
solubilized by water through exchange of the Igepal-capped
semiconductor nanocrystals with Igepal-capped aqueous domains.
Example 2
TEM Characterization of Silica-Coated ZnS-Capped CdSe Nanocrystals
(CdSe/ZnS/SiO.sub.2) in Reverse Microemulsion
[0074] Electron microscopy revealed that the majority (>90%) of
nanocrystals are encapsulated as single particles within a silica
shell (FIG. 8). The average total diameter of nanocrystal/Silica is
.about.22 nm. FIG. 9 shows the encapsulation of nanocrystals within
ca. 100 nm silica in the reverse microemulsion. Varying the amount
of water and ammonia in the microemulsion also affects the shell
thickness, since this alters the aqueous domain size. The silica
shell thickness can be increased by increasing the TEOS
concentration as shown in FIG. 10. The higher the concentration of
TEOS the larger is the silica diameter. Increase in the size of
silica lowers the emission intensity and QY. The total diameter of
coated nanocrystals affect the QY relative to the uncoated
nanocrystals, which is also shown in FIG. 10.
Example 3
Emission Characteristics of Silica-Coated ZnS-Capped CdSe
Nanocrystals (CdSe/ZnS/SiO.sub.2) in Water
[0075] Silica-coated nanocrystals in the microemulsion were
centrifuged at 18000 rpm for 30 minutes and the pellet was washed
with cyclohexane twice and dispersed in an alkaline aqueous
solution of pH 8-9. The silica-coated nanocrystals in water were
characterized by UV-visible absorption spectroscopy and
fluorescence spectroscopy. FIG. 11 shows the absorption and
fluorescence spectra of the CdSe nanocrystals before and after
silica coating. UV-visible and photoluminescence spectra show that
there is a 5 nm red-shift for CdSe/ZnS/SiO.sub.2 in water, in
comparison to the CdSe/ZnS nanocrystals in the parent solution,
butanol. Silica-coated semiconductor nanocrystals in water showed
remarkable colloidal stability over a period of several months.
[0076] Silica-coated nanocrystals showed remarkable photostability.
The nanocrystals in water and in butanol were exposed to UV
irradiation (335 nm cut-off filter). About 85% of the quantum yield
was retained after 24 hours for the coated particles in water,
where as the parent semiconductor nanocrystal solution virtually
lost all luminescence after 24 hours. We also compared the results
with those dots in water capped by mercaptoundecanoic acid (MUA).
MUA-capped semiconductor nanocrystals in water exhibited initial
photo-brightening and then photo-dissolution over a period of 24
hours. The exciton absorption peak position is plotted against time
of photolysis in FIG. 12. The peak position remains constant at 616
nm for silica-coated semiconductor nanocrystals, indicating that
the dots are photostable over extended periods of photolysis time.
On the contrary, the nanocrystals capped with MUA show
photo-dissolution as exemplified by blue-shifts in the exciton
position over 24 hours of photolysis.
Example 4
Preparation of TOPO-Capped CdSe Semiconductor Nanocrystals and
Interaction of Surfactants in IGEPAL Reverse Micelles
[0077] The following experiment was run to demonstrate that the
TOPO on a TOPO capped nanocrystal could be exchanged for a more
hydrophilic surfactant that can alter the hydrophilicity of the
nanoparticle.
[0078] CdSe semiconductor nanocrystals with excess TOPO without any
surface modification were prepared according to literature
procedures (Peng et al., "Formation of High-Quality CdTe, CdSe, and
CdS Nanocrystals Using CdO as Precursor" J. Am. Chem. Soc. 123,
183-184, 2001). The particles had luminescence quantum yields of
10-20% and emissions at 550-600 nm (FWHM=30-40 nm). The particles
were precipitated once from methanol to remove excess TOPO and
trioctylphosphine oxide (TOP). Inverse micelles were prepared using
the non-ionic surfactant IGEPAL CO-520 (polyoxyethylene nonylphenyl
ether), at 5%, by weight, and cyclohexane as solvent.
[0079] Emission experiments showed that TOPO-capped nanocrystals
were exchanged by IGEPAL. Changes in emission intensity and
emission wavelength for nanocrystals in IGEPAL micelles in
comparison with those nanocrystals in cyclohexane are due to the
surface ligand exchange reactions between TOPO and IGEPAL.
Example 5
Preparation of Silica-Coated Nanocrystals (CdSe/SiO.sub.2) in
IGEPAL Reverse Microemulsion
Aqueous in Non-Aqueous Emulsion
[0080] CdSe nanocrystals passivated with TOPO were precipitated
with methanol once and the precipitate was dried under nitrogen in
order to remove the methanol. To the precipitate, cyclohexane was
added and vortexed until the solution became clear. The
semiconductor nanocrystals were introduced into the reverse
micelles of an aqueous in non-aqueous emulsion made with 0.5 g
IGEPAL and 10 ml cyclohexane, and stirred for 30 minutes. Then 100
.mu.l of 29.5% NH.sub.4OH was added and stirred for another 1 hour.
Finally, TEOS was added at different concentrations and the
stirring continued for 24 hours. Aliquots of samples were taken at
different periods of coating times ranging from 1 to 24 hours, and
emission spectra were recorded.
[0081] FIGS. 13a-13c depict the effect of TEOS concentration and
silica coating time on the emission characteristics. For
comparison, the emission spectra of nanocrystals in IGEPAL micelles
(no silica coating) are shown. It is clear that the full width at
half maximum (FWHM) of the emission peak is increased with an
increase in coating time. In FIG. 14a the relative emission
intensity is plotted against coating time at various TEOS
concentration. Results show that the emission intensity increases
at 2 hours of silica coating after an initial decrease at 1 hour,
and that a further increase in coating time at 4 hours decreases
the emission intensity, which remains saturated with further
increase in coating time. The initial increase in the intensity at
2 hours is apparently due to silica formation when ammonia
adsorption occurs on the surface sites of the nanocrystals. The
decrease in emission intensity is presumably due to the acidity of
the silanol groups that quench ammonia basicity by a desorption
process at higher coating times (FIG. 14a).
[0082] FIG. 14b shows the effect of coating time on the emission
wavelength at different TEOS concentrations and different particles
sizes. In all the cases, silica-coated nanocrystals exhibit a blue
shift in comparison with naked (uncoated) dots. This implies that
IGEPAL-capped nanocrystals are exchanged for silica-coated
nanocrystals. The surface exchange reaction accounts for the blue
shift. The best conditions for silica coating are found to employ 5
.mu.l TEOS in a total volume of 10 ml microemulsion and 2 hours of
coating time (FIG. 14c).
Example 6
Preparation of Silica-Coated Nanocrystals (CdSe/SiO.sub.2) in
IGEPAL Reverse Microemulsion with an Amino Silane, APS, Added
[0083] CdSe semiconductor nanocrystals passivated with TOPO were
precipitated with methanol once and the precipitate was dried under
nitrogen in order to be free from methanol. 2 .mu.L of APS were
added to the precipitate, which was dissolved in 1 ml of
cyclohexane and vortexed until the solution became clear.
APS-modified nanocrystals were introduced into the reverse micelles
and stirred for 30 minutes. 100 .mu.l of 29.5% NH.sub.4OH was the
added and stirred for another 1 hour. Finally, 5-20 .mu.l TEOS was
added and the stirring continued for 24 hours. Aliquots of samples
were taken at different periods of coating times ranging from 1 to
24 hours and emission spectra were recorded for samples from each
aliquot (FIGS. 15a-15c).
[0084] The results show that APS modification provides more surface
passivation than is found in the naked dots. The APS modification
is preferably done before injecting the nanocrystals into IGEPAL
reverse micelles. With silica coating, there is no initial decrease
in the emission intensity at lower TEOS concentrations (FIGS. 15a
and 15b), but there is a decrease at higher concentrations (FIG.
15c). At 8 hours of coating time, the emission intensity remains
higher than all other coating times up to 24 h. The comparison of
the emission intensities at 8 and 24 hours shows a negligible
decrease (FIG. 16a) irrespective of TEOS concentration. This is
believed to occur because the amine groups provide additional
surface passivation for the APS-modified nanocrystals in comparison
to the similar nanocrystals absent the APS modification.
Furthermore, the acidity of the silanol groups that are formed
during extended periods of silica coating does not seem to affect
the emission properties as the amine protects the nanocrystal
surface.
[0085] FIG. 16b illustrates the effect of coating time on the
emission wavelength for different TEOS concentrations and different
particles sizes of APS-modified nanocrystals. Although
silica-coated nanocrystals exhibit a blue shift (5-10 nm) in
comparison with naked (uncoated) nanocrystals at different coating
times and various TEOS concentrations, the observed blue shifts are
small compared to those for unmodified nanocrystals (10-20 nm) as
shown in FIG. 13b. From this data, good conditions for silica
coating are found to be 2 .mu.l TEOS and 8 hours of coating time
(FIG. 16c).
Example 7
TEM Characterization of Silica-Coated Nanocrystals (CdSe/SiO.sub.2)
in Water
[0086] The silica-coated colloidal solution was centrifuged at
12000 rpm for 20 minutes and the resulting pellet was washed with
deionized water twice and dispersed in a mixture of water and
phosphate buffered saline (PBS). FIG. 17a shows the HRTEM image of
silica-coated nanocrystals in water. The lattice fringes of CdSe
are marked by arrows. The energy dispersive analysis of X-rays
(EDX) mapping (FIG. 17b) confirms the presence of all elements that
are predicted: Cd, Se from CdSe semiconductor nanocrystal core, Si,
O from SiO.sub.2 shell and P from TOPO. Sulfur impurity, possibly
from surfactant, is also seen.
Example 8
Photo-Stability of Silica-Coated Nanocrystals (CdSe/SiO.sub.2) in
Water
[0087] FIG. 18a shows the photo-stability of three different
semiconductor nanocrystals. Included are silica-coated nanocrystals
without APS and silica-coated nanocrystals with APS, both in a
mixture of water and phosphate buffered saline (PBS). The third
nanocrystal is an uncoated nanocrystal (no silica) in toluene. As
can be seen, the coated dots exhibited superior photo-stability
than did the uncoated ones. The increase in QY relative to the
uncoated nanocrystals in toluene is believed to be due to the
photo-brightening of silica-coated nanocrystals. This may be caused
by the photo-ionization of the nanocrystals. An approximately
three-fold increase in QY for silica-coated nanocrystals with APS
modification before coating, compared to silica-coated nanocrystals
without APS modification, is clearly seen in FIG. 18b.
Example 9
Preparation of PEG-Silica-Coated Nanocrystals (CdSe/ZnS/SiO.sub.2
and CdSe/SiO.sub.2) in IGEPAL Reverse Microemulsion with No APS
Added
[0088] CdSe/ZnS and CdSe nanocrystals passivated with TOPO were
precipitated with methanol once and the precipitate was dried under
nitrogen in order to be free from methanol. To the precipitate,
cyclohexane was added and vortexed until the solution became clear.
The nanocrystals were introduced into an aqueous in non-aqueous
emulsion, as described above, and stirred for 30 minutes. 50 .mu.l
NH.sub.4OH containing polyethylene glycol monomethyl ether (PEG-m)
concentration of 0.05 g/ml NH.sub.4OH, was added and stirred for
another 1 hour. Finally, TEOS was added at different amounts and
the stirring continued for 144 hours. Aliquots of samples were
taken at different periods of coating times ranging from 24 to 144
hours. The samples were then transferred to water, and the
resulting suspensions remained stable, even after 3 weeks. The
enhanced solubility is attributed to the repulsion force and
solvation layer provided by the PEG. The quantum yield associated
with different coating times was also recorded.
[0089] FIG. 19 illustrates the effect of silica coating time of
CdSe/ZnS nanocrystals on the quantum yield of the samples. The
quantum yield is plotted against coating time. The results show
that the emission intensity increases to a maximum after 90 hours
of silica coating. The maximum quantum yield (17%) achieved is
greater than that of the pre-coated CdSe/ZnS (10%). This is
attributed to enhanced surface passivation by the silica coating
layer surface moiety.
[0090] FIG. 20 provides an electron micrograph showing that the
CdSe/ZnS is encapsulated as single particle within a silica shell
of diameter .about.25 nm. Varying the amount of water (0.3% to
0.4%) in the microemulsion does not appear to affect the shell
thickness but does appear to decrease the quantum yield (FIG. 21).
Varying the volume of TEOS added (20-60 .mu.l) does not appear to
affect the shell thickness but does seem to improve the sphericity
and monodispersity of the particles, as well as the quantum yield,
as evidenced by FIGS. 22a and 22b.
[0091] While several embodiments of the present invention have been
described and illustrated herein, those of ordinary skill in the
art will readily envision a variety of other means and/or
structures for performing the functions and/or obtaining the
results and/or one or more of the advantages described herein, and
each of such variations and/or modifications is deemed to be within
the scope of the present invention. More generally, those skilled
in the art will readily appreciate that all parameters, dimensions,
materials, and configurations described herein are meant to be
exemplary and that the actual parameters, dimensions, materials,
and/or configurations will depend upon the specific application or
applications for which the teachings of the present invention
is/are used. Those skilled in the art will recognize, or be able to
ascertain using no more than routine experimentation, many
equivalents to the specific embodiments of the invention described
herein. It is, therefore, to be understood that the foregoing
embodiments are presented by way of example only and that, within
the scope of the appended claims and equivalents thereto, the
invention may be practiced otherwise than as specifically described
and claimed. The present invention is directed to each individual
feature, system, article, material, kit, and/or method described
herein. In addition, any combination of two or more such features,
systems, articles, materials, kits, and/or methods, if such
features, systems, articles, materials, kits, and/or methods are
not mutually inconsistent, is included within the scope of the
present invention.
[0092] All definitions, as defined and used herein, should be
understood to control over dictionary definitions, definitions in
documents incorporated by reference, and/or ordinary meanings of
the defined terms.
[0093] The indefinite articles "a" and "an," as used herein in the
specification and in the claims, unless clearly indicated to the
contrary, should be understood to mean "at least one."
[0094] The phrase "and/or," as used herein in the specification and
in the claims, should be understood to mean "either or both" of the
elements so conjoined, i.e., elements that are conjunctively
present in some cases and disjunctively present in other cases.
Other elements may optionally be present other than the elements
specifically identified by the "and/or" clause, whether related or
unrelated to those elements specifically identified. Thus, as a
non-limiting example, a reference to "A and/or B" can refer, in one
embodiment, to A only (optionally including elements other than B);
in another embodiment, to B only (optionally including elements
other than A); in yet another embodiment, to both A and B
(optionally including other elements); etc.
[0095] As used herein in the specification and in the claims,
unless clearly indicated to the contrary, "or" should be understood
to have the same meaning as "and/or" as defined above. For example,
when separating items in a list, "or" and "and/or" each shall be
interpreted as being inclusive, i.e., the inclusion of at least
one, but also including more than one, of a number or list of
elements, and, optionally, additional unlisted items. In general,
the term "or" as used herein shall only be interpreted as
indicating exclusive alternatives (i.e. "one or the other but not
both") when preceded by terms of exclusivity, such as "only one of"
or "exactly one of."
[0096] As used herein in the specification and in the claims, the
phrase "at least one," in reference to a list of one or more
elements, should be understood to mean at least one element
selected from any one or more of the elements in the list of
elements, but not necessarily including at least one of each and
every element specifically listed within the list of elements and
not excluding any combinations of elements in the list of elements.
This definition also allows that elements may optionally be present
other than the elements specifically identified within the list of
elements that the phrase "at least one" refers to, whether related
or unrelated to those elements specifically identified. Thus, as a
non-limiting example, "at least one of A and B" (or, equivalently,
"at least one of A or B," or, equivalently "at least one of A
and/or B") can refer, in one embodiment, to at least one,
optionally including more than one, A, with no B present (and
optionally including elements other than B); in another embodiment,
to at least one, optionally including more than one, B, with no A
present (and optionally including elements other than A); in yet
another embodiment, to at least one, optionally including more than
one, A, and at least one, optionally including more than one, B
(and optionally including other elements); etc.
[0097] It should also be understood that, unless clearly indicated
to the contrary, in any methods claimed herein that include more
than one act, the order of the acts of the method is not
necessarily limited to the order in which the acts of the method
are recited.
[0098] In the claims, as well as in the specification above, all
transitional phrases such as "comprising," "including," "carrying,"
"having," "containing," "involving," "holding," and the like are to
be understood to be open-ended, i.e., to mean including but not
limited to. Only the transitional phrases "consisting of" and
"consisting essentially of" shall be closed or semi-closed
transitional phrases, respectively, as set forth in the United
States Patent Office Manual of Patent Examining Procedures, Section
2111.03.
* * * * *