U.S. patent application number 12/419742 was filed with the patent office on 2010-10-07 for fiber ribbon and fiber ribbon attached to connector for wiring in equipment.
Invention is credited to Tetsuya Haruna, Tomoyuki Hattori, Kazumasa Oishi, Kazuto Saito, Wataru Sakurai, Mitsuaki Tamura, Kazunori Tanaka.
Application Number | 20100254658 12/419742 |
Document ID | / |
Family ID | 42826247 |
Filed Date | 2010-10-07 |
United States Patent
Application |
20100254658 |
Kind Code |
A1 |
Tanaka; Kazunori ; et
al. |
October 7, 2010 |
FIBER RIBBON AND FIBER RIBBON ATTACHED TO CONNECTOR FOR WIRING IN
EQUIPMENT
Abstract
When a glass fiber and an inner fiber coating layer are to be
attached to a connector by removing an outer fiber coating layer
while leaving the inner fiber coating layer as it is, a collective
coating and the outer fiber coating layer can be removed at a
stretch so that the inner fiber coating layer can easily and
satisfactorily be exposed. In the ultraviolet curable resin coating
layer of a coated optical fiber 17 of an optical fiber ribbon 11
for wiring of equipment, the inner fiber coating layer 15 has a
Young's modulus of 600 MPa to 1000 MPa, and the outer fiber coating
layer 16 has a Young's modulus of 10 MPa to 300 MPa. The material
of the outer fiber coating layer 16 is made by mixing 100 weight
parts of base resin, 1-30 weight parts of silicone-based additive,
and 0.5 to 40 weight parts of long chain fatty acid ester compound,
wherein the base resin is a material made of a urethane metha
acrylate oligomer, a mono-functional or multi-functional reactive
dilution monomer, and an optical initiator.
Inventors: |
Tanaka; Kazunori;
(Yokohama-city, JP) ; Oishi; Kazumasa;
(Yokohama-city, JP) ; Hattori; Tomoyuki;
(Yokohama-city, JP) ; Haruna; Tetsuya;
(Yokohama-city, JP) ; Sakurai; Wataru;
(Yokohama-city, JP) ; Tamura; Mitsuaki;
(Yokohama-city, JP) ; Saito; Kazuto;
(Yokohama-city, JP) |
Correspondence
Address: |
MCDERMOTT WILL & EMERY LLP
600 13TH STREET, N.W.
WASHINGTON
DC
20005-3096
US
|
Family ID: |
42826247 |
Appl. No.: |
12/419742 |
Filed: |
April 7, 2009 |
Current U.S.
Class: |
385/54 ;
385/114 |
Current CPC
Class: |
G02B 6/443 20130101;
G02B 6/4403 20130101 |
Class at
Publication: |
385/54 ;
385/114 |
International
Class: |
G02B 6/40 20060101
G02B006/40; G02B 6/44 20060101 G02B006/44 |
Claims
1. An optical fiber ribbon for wiring of equipment, the optical
fiber ribbon being formed in a ribbon-like shape such that a
plurality of coated optical fibers are arranged in parallel and
coated as a whole with a collective coating made of ultraviolet
curable resin, wherein each coated optical fiber has an inner fiber
coating layer and an outer fiber coating layer, each made of
ultraviolet curable resin, the Young's modulus of the inner fiber
coating layer being in the range of 600 MPa to 1000 MPa, the
Young's modulus of the outer fiber coating layer being in the range
of 10 MPa to 300 MPa; and wherein the outer fiber coating layer is
a material made by mixing 100 weight parts of base resin, 1-30
weight parts of silicone-based additive, and 0.5 to 40 weight parts
of long chain fatty acid ester compound.
2. An optical fiber ribbon according to claim 1, wherein the
silicone-based additive is polyorganosiloxiane and the long chain
fatty acid ester compound is a long chain fatty acid ester compound
selected from the group of octyl epoxystearate, epoxisized linseed
oil fatty acid butyl ester, glycerine acetic fatty acid ester, and
citrate ester.
3. An optical fiber ribbon according to claim 2, wherein the
adhesion between the outer fiber coating layer 16 and the inner
fiber coating layer 15 is 0.05 kgf or more and 0.20 kgf or
less.
4. A connector-attached optical fiber ribbon, comprising a
connector and an optical fiber ribbon set forth in any one of
claims 1 to 3, wherein the connector has a plurality of
through-holes provided at one end side of the connector and a
fitting part provided at the other end side, the through-holes
having an caliber substantially equal to the outer diameter of the
inner fiber coating layer of the coated optical fiber, the fitting
part being used for fixing an optical fiber ribbon, and wherein the
optical fiber ribbon is fixed to the fitting part by peeling off
the outer fiber coating layer and the collective coating
altogether, and inserting the inner fiber coating layer and the
silica glass fiber of the coated optical fiber integrally in the
respective through-holes.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to an optical fiber ribbon for
wiring of equipment and a connector-attached optical fiber ribbon
for wiring of equipment.
[0003] 2. Description of the Background Art
[0004] The optical fiber ribbon is made by arranging a plurality of
coated optical fibers in parallel and covering them with a
collective coating so as to make an integral ribbon-like form.
Japanese Patent Application Publication No. 2003-95706 describes
coated optical fibers contained in an optical fiber ribbon. The
coated optical fiber is such that the outer circumferential surface
of a glass fiber is coated with two layers made of ultraviolet
curable resin: an inner fiber coating layer and an outer fiber
coating layer. The inner fiber coating layer has Young's modulus of
about 1.2 MPa, and the outer fiber coating layer has Young's
modulus of about 700 to 750 MPa, and the outer fiber coating layer
is harder than the inner fiber coating layer. In this optical fiber
ribbon, the glass fiber can be exposed by removing the inner fiber
coating layer and the outer fiber coating layer together with the
collective coating. When a coated optical fiber is attached to a
connector, generally the glass fiber is bared to be fixed to the
connector.
[0005] Japanese Patent Application Publication No. H 2-151821
discloses an optical fiber that is coated with two layers: an inner
fiber coating layer made of acrylate fluoride and an outer fiber
coating layer made of silicone resin. This optical fiber can be
fixed to a connector in the condition where the outer fiber coating
layer only is removed while the inner fiber coating layer remains
as it is. In this manner, it is possible to prevent the glass fiber
from being damaged, and hence the degradation of the transmission
characteristics and mechanical strength can be avoided.
[0006] However, in the case of an optical fiber ribbon, in which
such a kind of coated optical fibers as disclosed by Japanese
Patent Application Publication No. H 2-151821 are further covered
with a collective coating, the attempt to remove the outer fiber
coating layer together the collective coating will often result in
failure: it is difficult to pull out the outer fiber coating layer
in a clean layer condition, that is, the residues of the silicone
resin might be left on the inner fiber coating layer. This is
because the silicone resin is fragile.
SUMMARY OF THE INVENTION
[0007] The object of the present invention is to provide an optical
fiber ribbon for wiring of equipment and an optical fiber ribbon
attached to connector for wiring of equipment. In the optical fiber
ribbon of the invention, the inner fiber coating layer can easily
and satisfactorily be exposed by removing the collective coating
and the outer fiber coating layer at a stretch.
[0008] To achieve the object, the optical fiber ribbon for wiring
of equipment is formed in a ribbon-like shape such that a plurality
of coated optical fibers are arranged in parallel and coated as a
whole with a collective coating made of ultraviolet curable resin,
wherein each coated optical fiber has an inner fiber coating layer
and an outer fiber coating layer, which are made of ultraviolet
curable resin, and the Young's modulus of the inner fiber coating
layer is 600 MPa or more and 1000 MPa or less, and the Young's
modulus of the outer fiber coating layer is 10 MPa or more and 300
MPa or less; the outer fiber coating layer is a material made by
mixing 100 weight parts of base resin, 1-30 weight parts of
silicone-based additive, and 0.5 to 40 weight parts of long chain
fatty acid ester compound, wherein the base resin is a material
made of urethane acrylate oligomer or urethane metha acrylate
oligomer, a mono-functional or multi-functional reactive dilution
monomer, and an optical initiator.
[0009] In addition, provided is a connector-attached optical fiber
ribbon, which is made by attaching a connector to the optical fiber
ribbon of the present invention. In the connector-attached optical
fiber ribbon, a plurality of through-holes having a diameter that
is substantially equal to the outer diameter of the inner fiber
coating layer of the coated optical fiber are provided at one end
side of the connector, and a fitting part for fixing an optical
fiber ribbon is provided at the other end side, wherein the outer
fiber coating layer of each coated optical fiber and the collective
coating that constitutes an optical fiber ribbon are peeled off
altogether, and the inner fiber coating layer and the silica glass
fiber of each coated optical fiber are integrally inserted into the
respective through-holes, and the optical fiber ribbon is fixed to
the fitting part of the connector.
BRIEF DESCRIPTION OF THE DRAWINGS
[0010] FIG. 1 is a partially cut-away perspective view showing the
embodiment of an optical fiber ribbon for wiring of equipment
relating to the present invention.
[0011] FIG. 2 is a sectional view showing an embodiment of the
connector-attached optical fiber ribbon for wiring of equipment
relating to the present invention.
[0012] FIG. 3 is a table showing the mixing ratios of additives
added to base resins in Examples and Comparative Examples, and the
respective evaluation results.
DETAILED DESCRIPTION OF THE INVENTION
[0013] In the following, preferred embodiments of the present
invention will be described in detail with reference to the
accompanying drawings. The same reference numerals denote the same
parts, and a repeated explanation will be omitted. The ratios of
dimensions in the drawings do not always exactly correspond to the
description.
[0014] FIG. 1 is a partially cut-away perspective view showing an
optical fiber ribbon 11, which is an embodiment of the present
invention. The optical fiber ribbon 11 has a plurality (e.g., 12
pieces) of coated optical fibers 17, which are arranged in
parallel, and a collective coating 18, which is made of ultraviolet
curable resin and unites the coated optical fibers 17 altogether in
a ribbon-like form. Each coated optical fiber 17 is formed such
that the outer circumference of a silica glass fiber 14 consisting
of a core 12 and a cladding 13 is coated with an inner fiber
coating layer 15 and an outer fiber coating layer 16, which are
made of ultraviolet curable resins. The optical fiber ribbon 11 is
suitable for wiring of equipment (for inter-connection) as
described later.
[0015] First, a method of manufacturing the optical fiber ribbon 11
will be described. The manufacturing method of the optical fiber
ribbon 11 includes a step of making a resin solution, a coating
step, and a cabling step.
[0016] In the step of making the resin solution, first, an oligomer
(prepolymer) is synthesized. A predetermined amount of isocyanate
(TDI, etc.) and diol (PPG, etc.) are addition polymerized. The
resultant product and an acryloyl group-containing monomer (2-HEA,
etc.) are subjected to polycondensation reaction to complete the
intended oligomer synthesis. Next, the blending of the resin
solution is conducted. The oligomer prepared as described above is
mixed with a plural kinds of monomers (N-VC, isobornyl acrylate,
etc.) and an optical initiator (phosphorus-based optical initiator:
TPO, etc). The resultant mixture is further mixed with various
additive agents (silicone-based additive, silane coupling agent,
long chain fatty acid ester compound, etc.).
[0017] Here, the resin solution to become an inner fiber coating
layer 15 is an ultraviolet curable resin solution which comprises a
base resin material and additives: the base resin material includes
40-65 weight parts of urethane (metha) acrylate oligomer, 34.5-59
weight parts of mono-functional or multi-functional reactive
dilution monomer, and 0.5 to 3 weight parts of optical initiator,
and the additives are 0.1-5 weight parts of silane coupling agent,
and 0.1-10 weight parts of silicone-based additive, respectively
relative to 100 weight parts of the base resin material, wherein
the silane coupling agent contains one or more alcohoxy groups and
one functional group (i.e., any of mercapto group, methacryl group,
epoxy group, and vinyl group), and wherein the silicone-based
additive is composed of mono-functional or bifunctional silicone
acrylate.
[0018] The resin solution to become an outer fiber coating layer 16
is an ultraviolet curable resin solution which comprises a base
resin material including 30-85 weight parts of urethane (metha)
acrylate oligomer, 69.5-12 weight parts of mono-functional or
multi-functional reactive dilution monomer, and 0.5-3 weight parts
of optical initiator, and which includes 1-30 weight parts of
silicone-based additive, and 0.5-40 weight parts of long chain
fatty acid ester compound, respectively relative to 100 weight
parts of the base resin material.
[0019] Here, the silicone-based additive is polyorganosiloxiane.
The polyorganosiloxiane is represented by chemical formula
YCH.sub.3SiO(X.sub.2SiO)nSiCH.sub.3Y, wherein X is a functional
group of either methyl or ethyl, and Y is a compound comprised of
hydrogen atom, alkyl group or alkenyl group. More specifically, the
silicone-based additives used are polyorganosiloxiane having a
vinyl group terminus and polyorganosiloxane having trimethylsilyl
terminus comprised of a methyl group. The polyorganosiloxiane
preferably has an average molecular weight of 1000 to 60000, and
more preferably 5000 to 45000.
[0020] The long chain fatty acid ester compound is comprised of one
or more kinds of long chain fatty acid ester compounds selected out
of octyl epoxystearate, epoxisized linseed oil fatty acid butyl
ester, glycerine acetic fatty acid ester, citrate ester, and the
like. The average molecular weight of these long chain fatty acid
ester compounds is preferably 500 to 100000, and more preferably
1000 to 60000. The silicone-based additive and the long chain fatty
acid ester compound are not necessarily limited to those described
above.
[0021] At the coating step, an inner fiber coating layer 15 and an
outer fiber coating layer 16 are coated around the outer
circumference of a silica glass fiber 14. The glass fiber 14, which
is formed by drawing an optical fiber preform, has a core 12 of 50
.mu.m or less and preferably 30 .mu.m or more in diameter, and a
cladding 13 of 100 .mu.m or less (e.g., 80 .mu.m) in diameter,
wherein fluorine (F) is added to the cladding 13 and the relative
refractive index difference .DELTA.n between the core 12 and the
cladding 13 is equal to or more than 1.2% (typically 1.9%).
[0022] More specifically, first, the resin solution for the inner
fiber coating layer 15 is coated on the outer circumference of the
glass fiber 14 and is UV-cured, and thereby a small-diameter
single-coat optical fiber is formed. Here, the inner fiber coating
layer 15 has a Young's modulus of 600 MPa or more and 1000 MPa or
less in a state of hardened coating film, and the coating diameter
of the inner fiber coating layer 15, that is, the outer diameter of
the small-diameter single-coat optical fiber is 125 .mu.m. Next,
the resin solution for the outer fiber coating layer 16 is coated
on the outer circumference of the inner fiber coating layer 15 and
is UV-cured, and thereby the coated optical fiber 17 is formed.
Here, the outer fiber coating layer 16 has a Young's modulus of 10
MPa or more and 300 MPa or less in a state of hardened coating
film, and the coating diameter of the outer fiber coating layer 16,
i.e., the outer diameter of the coated optical fiber 17 is 250
.mu.m. The resin solution for the inner fiber coating layer 15 and
the resin solution for the outer fiber coating layer 16 may be
applied consecutively, and they may simultaneously be UV-cured
altogether.
[0023] In the cabling step, the optical fiber ribbon 11 is made by
arranging 12 pieces of the coated optical fibers 17 in parallel and
uniting them into an integral ribbon-like form by applying an
ultraviolet curable resin for the collective coating 18 and
UV-curing it. In this case, the optical fiber ribbon 11 thus made
has a thickness of about 290 .mu.m.
[0024] In the optical fiber ribbon 11, each coated optical fiber 17
has an inner fiber coating layer 15 of 125 .mu.m in outer diameter
and an outer fiber coating layer 16 of 250 .mu.m in outer diameter,
whereas both fiber coating layers are made of ultraviolet curable
resins. In particular, the material that constitutes the outer
fiber coating layer 16 is a material which comprises a base resin
including a urethane (metha) acrylate oligomer, a mono-functional
or multi-functional reactive dilution monomer, and an optical
initiator, and which also comprises 1-30 weight parts of
silicone-based additive, and 0.5-40 weight parts of long chain
fatty acid ester compound, respectively relative to 100 weight
parts of the base resin.
[0025] FIG. 2 is a cross-sectional side view showing a
connector-attached optical fiber ribbon 21, which is an embodiment
of the present invention. Attachment of a connector 24 to the
optical fiber ribbon 11 is conducted as follows. First, the
connector 24 having an opening in which the optical fiber ribbon 11
is inserted is prepared. One end of the opening is structured as a
plurality of through-holes 22 each having a caliber which is
substantially equal to the outer diameter of the inner fiber
coating layer 15 of the coated optical fiber 17, which is a
constituent member of the optical fiber ribbon 11. The other end of
the opening is shaped approximately similar to the external form of
the optical fiber ribbon 11 and functions as a fitting part 23 for
fixing the optical fiber ribbon 11.
[0026] Next, the collective coating 18 of the optical fiber ribbon
11 and the outer fiber coating layer 16 are simultaneously removed
altogether so as to partially expose the inner fiber coating layer
15. Thus, each silica glass fiber 14 covered with the inner fiber
coating layer 15 is inserted from the side of the fitting part 23
to the respective through-hole 22, whereas the optical fiber ribbon
11 is fixed to the fitting part 23 at the part covered with the
collective coating 18. In this way, the connector-attached optical
fiber ribbon 21 is obtained.
[0027] In order to attach a coated optical fiber to the connector
in such a state as covered with the inner fiber coating layer, the
outer fiber coating layer 16 must be capable of allowing easy
removal while the inner fiber coating layer 15 is stuck to the
glass fiber 14. The long chain fatty acid ester compound added to
the outer fiber coating layer of the coated optical fiber 17
exhibits an effect like a plasticizing agent, swelling the outer
fiber coating layer 16 to some degree. Since the quantity of the
long chain fatty acid ester compound thus added is 0.5 to 40 weight
parts relative to 100 weight parts of the base resin, the outer
fiber coating layer 16 will not afford compression force to the
inner fiber coating layer 16, allowing the easy removal of the
outer fiber coating layer 16.
[0028] In that case, if the ratio of the long chain fatty acid
ester compound is less than 0.5 weight parts, the swelling effect
is hardly recognized. In such case, since the outer fiber coating
layer compresses the inner fiber coating layer, the delamination
that is a starting point in the coating removal will not be caused
between the inner fiber coating layer 15 and the outer fiber
coating layer 16. On the other hand, if the amount of the classy
fat acid ester added to the outer fiber coating layer is 40 weight
parts or more, the swelling effect reaches a saturated level.
Moreover, if any part of the long chain fatty acid ester compound
moves from the outer fiber coating layer 16 to the inner fiber
coating layer 15, it will cause a swelling of the inner fiber
coating layer 15, which will result in the decrease of sticking
force between the glass fiber 14 and the inner fiber coating layer
15.
[0029] Also, since at least one or more kinds of silicone-based
additives are added by the amount of 1 weight part or more to the
outer fiber coating layer, the outer fiber coating layer 16 can
slide on the inner fiber coating layer 15 to a suitable degree when
the removal of the outer fiber coating layer 16 is done. The
surface free energy of the outer fiber coating layer is small, and
the silicone-based additive exists in the surface of the outer
fiber coating layer 16 or the boundary between the outer fiber
coating layer 16 and the inner fiber coating layer 15. Therefore,
at the time of simultaneous removal of the collective coating 18
and the outer fiber coating layer 16, the inner fiber coating layer
15 can be prevented from suffering any damage which might otherwise
be caused by such removal, and hence it is possible to prevent such
damage from decreasing the adherence between the optical fiber and
a ferrule or connector. In addition, when the coated optical fiber
as covered with the inner fiber coating layer 15 is inserted into
the through-hole or the ferrule of the connector, the outer fiber
coating layer 16 can be prevented from leaving any residue thereof
on the inner fiber coating layer 15, and hence no difficulty will
arise in the insertion of such single-coat optical fiber into the
through-hole or the ferrule of the connector.
[0030] On the other hand, if the silicone-based additive added is
more than 30 weight parts, the friction between the outer fiber
coating layer 16 and the inner fiber coating layer 15 will be
insufficient such that, depending on the variation of ambient
temperature, the inner fiber coating layer 15 and the glass fiber
14 might protrude from the outer fiber coating layer 16. In
general, there are cases in which the end of the optical fiber
ribbon 11 for wiring of equipment is directly butted against a
photodetector. In such a case, if the small-diameter single-coat
optical fiber part (the 125 .mu.m diameter part) protrudes from the
coated optical fiber, the photodetector might be damaged.
Therefore, occurrence of such protrusion should be prevented. The
optical fiber ribbon 11 of the invention enables restraining such
occurrence.
[0031] Moreover, the ultraviolet curable resin used in the inner
fiber coating layer 15 and the outer fiber coating layer 16 has
excellent hardening property, and hence the productivity can be
improved by enhancing the manufacturing line speed.
[0032] Furthermore, since the Young's modulus of the inner fiber
coating layer 15 is in the range of 600 MPa to 1000 MPa, while the
Young's modulus of the outer fiber coating layer 16 is in the range
of 10 MPa to 300 MPa, the inner fiber coating layer 15 is harder,
whereas the outer fiber coating layer 16 is softer. Accordingly,
sufficient strength can be secured so that the glass fiber 14 may
not be damaged by the hardness of the inner fiber coating layer 15
which is exposed at the time of attachment to the connector.
[0033] Here, if the Young's modulus of the inner fiber coating
layer 15 is as small as 0.5 to 2.0 MPa at the normal temperature,
the splicing loss will increase because of such displacement in the
position of the glass fiber 14 as occurs inside the connector when
the coated optical fibers 17 are butted each other or when the
coated optical fiber 17 is butted against a photodetector. In
contrast, if the Young's modulus of inner fiber coating layer 15 is
sufficiently high at the normal temperature, the deformation of the
coating will not be caused by the butting, and hence satisfactory
splicing loss properties will be obtained. Since a silicone-based
additive is added to the inner fiber coating layer 15, no adhesion
with a connector, ferrule, or the like occurs thanks to the
delamination effect of the silicon additive, and accordingly
optical properties will not be degraded. Also, a cushioning effect
against a lateral pressure can be provided with the comparatively
soft outer fiber coating layer 16.
[0034] As mentioned above, the protrusion of the coated optical
fiber should be prevented. For the purpose of easy removal of the
outer fiber coating layer 16 as well as prevention of the
protrusion of the inner fiber coating layer 15 including the silica
glass fiber 14, it is more preferable to provide a predetermined
mechanical property such that the adhesion between the outer fiber
coating layer 16 and the inner fiber coating layer 15 be made 0.05
kgf or more and 0.20 kgf or less, by using a silicone-based
additive composed of polyorganosiloxiane and an additive consisting
of one or more kinds of long chain fatty acid ester compounds which
are selected from the group of octyl epoxystearate, epoxisized
linseed oil fatty acid butyl ester, glycerine acetic fatty acid
ester, and citrate ester, etc.
[0035] As for the silica glass fiber 14, the coupling efficiency
with the light source improves, since the relative refractive index
difference An between the core 12 and the cladding 13 is equal to
or more than 1.2%.
EXAMPLES
[0036] FIG. 3 is a table showing the mixing ratios of additives
added to the base resins of the outer fiber coating layers and the
respective evaluation results in Examples 1 to 7 and Comparative
Examples 1 to 4. The optical fiber ribbons (Examples 1 to 7 and
Comparative Examples 1 to 4) covered with the resins having the
compositions shown in FIG. 3 are prepared and the respective
characteristics are evaluated. In a glass fiber included in an
optical fiber ribbon, the relative refractive index difference
.DELTA.n of the core 12 and the cladding 13 is 1.9%. The resins are
made by adding the additives described in the table to the base
resin, which is made from 84 wt % of oligomer, 5 wt % of monomer 1
(N-vinyl caprolactam), 5 wt % of monomer 2 (isobornyl acrylate), 5
wt % of monomer 3 (2-hydroxypropyl acrylate), and 1 wt % of optical
initiator (Lucirin TPO), whereas the oligomer is prepared by mixing
polypropylene glycol (PPG) having a number average molecular weight
of 3500, toluene-diisocyanate (TDI), and 2-hydroxyl ethyl acrylate
(2-HEA) at the ratio of 1:2:2 by resin synthesis (dehydration
polymerization reaction).
Evaluation of Young's Modulus
[0037] Pulling tests of optical fiber ribbons are conducted
according to JISK7113 at a pulling speed of 1 mm/ minute. The
evaluation samples are prepared by immersing fibers in MEK and
swelling them, and taking out the pipe-like coating parts only,
separating the inner fiber coating layer 15 (single-coat layer) and
the outer fiber coating layer 16 (OVC layer). Thereafter, the
samples thus prepared are pulled with a pulling test machine. Their
Young's modulus values differ depending on the quantities of the
silicone-based additives and the long chain fatty acid ester
compounds which are added to the outer fiber coating layer.
Evaluation by Simultaneous Removal of Coatings from Optical Fiber
Ribbons
[0038] The collective coatings 18 (tape materials) and the outer
fiber coating layers 16 (OVC layers) are removed altogether from
optical fiber ribbons, using a thermal remover JR-5 (a
jacket-remover used for a small-diameter indoor cable) made by
Sumitomo Electric Industries, Ltd. The condition of the coating
removal is 100.degree. C..times.3 seconds. The evaluation is
conducted as follows: the test results are judged to be poor when
the collective coating 18 and the outer fiber coating layer 16
become crumbled or when any delamination occurs inside the inner
fiber coating layer 15 (single-coat layer) at the time of the inner
fiber coating layer 15 being exposed; and the tests results are
judged to be satisfactory when the inner fiber coating layer 15
(single-coat layer) is exposed with a moderate force without
crumbling the collective coating 18 and the outer fiber coating
layer 16.
Evaluation of Pistoning
[0039] The optical fiber ribbons are subjected to heat shock tests
of -40 to 125.degree. C. The time held under -40.degree. C. and
125.degree. C. is 30 minutes, and the temperature switch from
-40.degree. C. to 125.degree. C. is instantaneously accomplished.
Cut samples, which are prepared with their end faces being
sufficiently clean without any burrs, are laid under the respective
test environments. The above heat shock tests are repeated 100
times, and the protrusion of the glass fiber 14 or the single-coat
fiber having the inner fiber coating layer 15 is measured using an
electronic microscope or the like. If the protrusion quantity is
smaller than 30 .mu.m, the pistoning is judged to be acceptable,
and if the protrusion quantity is 30 .mu.m or more, the pistoning
is judged to be unacceptable.
Adhesion Measurement
[0040] The adhesion between the inner fiber coating layer 15 and
the outer fiber coating layer 16 is measured in a similar manner as
the pull-out evaluation of the optical fiber. An optical fiber
ribbon 11 is adhered and fixed to fixing tools of the pulling test
machine using an adhesive at both end portions each of which has a
length of about 10 mm, and a cut gap is provided (to such a degree
as the cut by a knife does not reach the inner fiber coating layer
15) at a part between the fixed points. The fixing tools are moved
to go away from each other such that a small-diameter single-coat
optical fiber (125 .mu.m diameter) is pulled out from the outer
fiber coating layer 16, at a pulling speed of 10 mm per minute.
Splicing Loss
[0041] The splicing loss is measured for optical fibers which are
inserted in a ferrule under the conditions in which both ends
thereof are covered with an inner fiber coating layer. The loss is
measured by continuous monitoring at temperatures of -40 to
125.degree. C. for 100 cycles.
[0042] In Examples 1 to 7, in which the optical fiber ribbon has an
inner fiber coating layer 15 having Young's modulus of 600 MPa to
1000 MPa and which exhibits acceptable pistoning and excellent
simultaneous coating removability as well as low splicing loss, the
Young's modulus of the outer fiber coating layer 16 is 20 to 290
MPa, and the adhesion between the outer fiber coating layer 16 and
the inner fiber coating layer 15 is 0.06 to 0.18 kgf (FIG. 3).
[0043] In contrast, in Comparative examples 1 to 4, there is a
problem with respect to any of the simultaneous coating
removability, pistoning, and splicing loss. In Comparative Example
1, since the quantity of the added silicone-based additive is too
little, the coating removal is difficult. In Comparative example 2,
since the quantity of the added silicone-based additive is too
much, pistoning is unacceptable. Also, the splicing loss is rather
large, presumably due to the protrusion of the coated optical
fiber. In Comparative Example 3, the Young's modulus of the outer
fiber coating layer 16 is too large to be cut by knife, and because
the quantity of the added long chain fatty acid ester compound is
too little, the coating removal is difficult to accomplish. In
Comparative Example 4, since the quantity of the added long chain
fatty acid ester compound is too much, the outer fiber coating
layer becomes crumbled, which results in poor performance of the
simultaneous coating removal. Also, the outer fiber coating layer
and the inner fiber coating layer slide, making the pistoning
unacceptable, and the splicing loss is large.
[0044] From the above, it is understood that the optical fiber
ribbon 11 exhibits not only superior simultaneous removability of
the collective coating 18 and the outer fiber coating layer 16, but
also acceptable pistoning and low splicing loss, if the optical
fiber ribbon 11 has the following characteristics: the core 12 has
a diameter of 50 .mu.m and the cladding 13 has a diameter of 100
.mu.m or less; the cladding 13 is doped with fluorine and the
relative refractive index difference between the core 12 and the
cladding 13 is 1.2% or more; the inner fiber coating layer 15 of
125 .mu.m diameter and the outer fiber coating layer 16 of 250
.mu.m diameter are made of ultraviolet curable resin; the material
that constitutes the outer fiber coating layer 16 is a material
which comprises a base resin including an optical initiator, a
urethane (metha) acrylate oligomer, and a mono-functional or
multi-functional reactive dilution monomer, and which also
comprises 1-30 weight parts of silicone-based additive, and 0.5-40
weight parts of long chain fatty acid ester compound, respectively
relative to 100 weight parts of the base resin; the Young's modulus
of the outer fiber coating layer 16 is 10 MPa or more and 300 MPa
or less; and the adhesion between the outer fiber coating layer 16
and the inner fiber coating layer 15 is 0.05 kgf to 0.20 kgf.
[0045] The present patent application is based on Japanese patent
application No. 2008-011309 filed on Jan. 22, 2008, and its
contents are incorporated herein by reference.
* * * * *