U.S. patent application number 12/813541 was filed with the patent office on 2010-09-30 for semiconductor device and fabrication method of the semiconductor device.
This patent application is currently assigned to KABUSHIKI KAISHA TOSHIBA. Invention is credited to Ken ONODERA, Kazutaka Takagi.
Application Number | 20100244202 12/813541 |
Document ID | / |
Family ID | 39467849 |
Filed Date | 2010-09-30 |
United States Patent
Application |
20100244202 |
Kind Code |
A1 |
ONODERA; Ken ; et
al. |
September 30, 2010 |
SEMICONDUCTOR DEVICE AND FABRICATION METHOD OF THE SEMICONDUCTOR
DEVICE
Abstract
A semiconductor device and its manufacturing method, the
semiconductor device comprising: a semi-insulating substrate 11 in
which an electrode (12) is formed on a surface (11a) of one side
and in which an aperture (11c) passed through from the surface 11a
of one side to a surface (11b) of another side is formed; and a
conductive layer (17) formed in an inner surface of the aperture
(11c), and electrically connected with the electrode (12); wherein
the aperture (11c) has a tapered region (11d) where an inside
diameter of a part located in the surface (11b) of another side is
larger than an inside diameter of a part located in the surface
(11a) of one side.
Inventors: |
ONODERA; Ken; (Kawasaki-shi,
JP) ; Takagi; Kazutaka; (Kawasaki-shi, JP) |
Correspondence
Address: |
OBLON, SPIVAK, MCCLELLAND MAIER & NEUSTADT, L.L.P.
1940 DUKE STREET
ALEXANDRIA
VA
22314
US
|
Assignee: |
KABUSHIKI KAISHA TOSHIBA
Minato-ku
JP
|
Family ID: |
39467849 |
Appl. No.: |
12/813541 |
Filed: |
June 11, 2010 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12300793 |
Nov 14, 2008 |
7749901 |
|
|
PCT/JP07/72899 |
Nov 28, 2007 |
|
|
|
12813541 |
|
|
|
|
Current U.S.
Class: |
257/621 ;
257/774; 257/E23.011 |
Current CPC
Class: |
H01L 2924/0002 20130101;
H01L 2924/0002 20130101; H01L 2924/00 20130101; H01L 21/76898
20130101; H01L 21/3086 20130101 |
Class at
Publication: |
257/621 ;
257/E23.011; 257/774 |
International
Class: |
H01L 23/48 20060101
H01L023/48 |
Foreign Application Data
Date |
Code |
Application Number |
Nov 30, 2006 |
JP |
2006 323751 |
Claims
1. A semiconductor device comprising: a semi-insulating substrate
composed of GaN or SiC in which an electrode is formed on a surface
of one side and in which a VIA hole passed through from the surface
of one side to a surface of another side is formed; and a
conductive layer formed in an inner surface of the VIA hole, and
electrically connected with the electrode, wherein an inside
diameter of a part located in the surface of the another side of
the VIA hole is larger than an inside diameter of a part located in
the surface of one side.
Description
CROSS-REFERENCE TO PRIOR APPLICATION
[0001] This application is a divisional of and claims the benefit
of priority under 35 U.S.C. .sctn.120 from U.S. Ser. No. 12/300,793
filed Nov. 14, 2008, the entire contents of which is incorporated
herein by reference. U.S. Ser. No. 12/300,793 is a National Stage
of PCT/JP07/72899 filed Nov. 28, 2007, which was not published
under PCT Article 21 (2) in English, and claims the benefit of
priority from Japanese Patent Application No. 2006-323751 filed
Nov. 30, 2006.
TECHNICAL FIELD
[0002] The present invention relates to a semiconductor device used
with a high frequency band, and a fabrication method of the
semiconductor device.
BACKGROUND ART
[0003] A semiconductor device, for example, a microwave
amplification device, which are used with a high frequency band,
composed of active elements, such as a field effect type
transistor, passive elements, such as a resistance and a capacitor,
and circuit elements, such as a microstrip line for transmitting a
high frequency signal, and these circuit elements are formed for
example, on a semi-insulating substrate. Aground conductor is
formed on an opposite surface of the semi-insulating substrate.
And, when grounding a circuit element, the circuit element provided
on the semi-insulating substrate and the ground conductor formed on
the back side of the semi-insulating substrate are electrically
connected through a VIA (via) hole for passing through the
semi-insulating substrate, for example.
[0004] The VIA-hole provides a through hole passed through from one
surface to a surface of another side of the semi-insulating
substrate, and is having structure which forms a conductive layer
in an inner surface of the through hole. The through hole is
formed, for example by etching, and the conductive layer is formed
by plating, vacuum evaporation, etc.
[0005] The VIA-hole of a configuration described above has some
which are described in the Patent Document 1 etc.
[0006] Patent Document 1: Japanese Patent Application Laid-Open
Publication No. H02-288409.
[0007] As the conventional semiconductor device described above,
the VIA-hole is formed, for example by etching, and the conductive
layer formed in the inner surface of the VIA-hole is formed by
methods, such as plating and vacuum evaporation.
[0008] However, when forming the conductive layer in the inner
surface of the VIA-hole, the so-called "disconnection caused by
step", by which metal performing the plating or the vacuum
evaporation is not fully formed and the conductive layer is not
formed in a part of inner surface of the VIA-hole, may occur. As a
result, grounding of the circuit element becomes insufficient and
it becomes a cause by which the electrical characteristics of a
microwave amplification device etc. deteriorate.
[0009] The object of the present invention is to provide a
semiconductor device for solving the above-mentioned fault and
preventing the disconnection caused by step of the VIA-hole, etc.,
and a fabrication method of the semiconductor device.
DISCLOSURE OF INVENTION
[0010] According to one aspect of the present invention for
achieving the above-mentioned object, a fabrication method of a
semiconductor device is provided. The fabrication method of the
semiconductor device includes: a first step of forming a mask layer
which is composed of material whose etching rate is smaller than a
semi-insulating substrate on a surface of another side of the
semi-insulating substrate where an electrode is formed on a surface
of one side; a second step of forming a resist layer on the mask
layer; a third step of illuminating the resist layer through a mask
pattern which provides a region along which light passes, and
forming a first aperture in the resist layer;
[0011] a fourth step of heating the resist layer in which the first
aperture is formed, and forming a first tapered region where a
thickness becomes thin toward the first aperture side around the
first aperture of the resist layer; a fifth step, after the fourth
step, of forming a second aperture that a part of the surface of
the another side of the semi-insulating substrate exposes by
etching the mask layer using the first aperture of the resist
layer, and forming a second tapered region where a thickness
becomes thin toward the second aperture side around the second
aperture; a sixth step, after the fifth step, of removing the
resist layer which remains on the mask layer; a seventh step, after
the sixth step, of forming a third aperture having a third tapered
region where an inside diameter of apart located in the surface of
the another side of the semi-insulating substrate is larger than an
inside diameter of a part located in the surface of one side by
etching the semi-insulating substrate using the second aperture;
and an eighth step of forming a conductive layer in an inner
surface of the third aperture.
[0012] According to other aspects of the present invention, a
semiconductor device is provided. The semiconductor device
includes: a semi-insulating substrate composed of GaN or SiC in
which an electrode is formed on a surface of one side and in which
a VIA-hole passed through from the surface of one side to a surface
of another side is formed; and a conductive layer formed in an
inner surface of the VIA-hole, and electrically connected with the
electrode; wherein an inside diameter of a part located in the
surface of the another side of the VIA-hole is larger than an
inside diameter of apart located in the surface of one side.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] [FIG. 1] It is a schematic section structure for explaining
a formation method of a VIA-hole applied to a part of a fabrication
method of a semiconductor device according to a first embodiment of
the present invention: (a) a photo lithography process chart; (b) a
formation process chart of a first aperture 14a; (c) a formation
process chart of a first tapered region 14b; (d) an etching process
chart of a mask 13; (e) a process chart which uses the mask 13 to
form a third aperture 11c by etching of a semi-insulating substrate
11; and (f) a process chart for forming a grounding electrode 17 to
form a VIA-hole.
[0014] [FIG. 2] A schematic configuration diagram of an etching
apparatus applied to the VIA-hole formation process for a
semi-insulating substrate in a fabrication method of the
semiconductor device according to the first embodiment of the
present invention.
BEST MODE FOR CARRYING OUT THE INVENTION
[0015] There will be described embodiments of the present
invention, with reference to the drawings, where like members or
elements are designated by like reference characters to eliminate
redundancy, and some layers and their subsidiary regions are
designated by the same reference characters for simplicity.
Drawings are schematic, not actual, and may be inconsistent in
between in scale, ratio, etc.
[0016] The embodiments to be described are embodiments of a
technical concept or spirit of the present invention that is not
limited to embodied specifics, and may be changed without departing
from the spirit or scope of claims.
First Embodiment
[0017] FIG. 1 is a schematic section structure for explaining a
formation method of a VIA-hole applied to a part of a fabrication
method of a semiconductor device according to a first embodiment of
the present invention: FIG. 1(a) shows a photo lithography process
chart; FIG. 1(b) shows a formation process chart of a first
aperture 14a; FIG. 1(c) shows a formation process chart of a first
tapered region 14b; FIG. 1(d) shows an etching process chart of a
mask 13; FIG. 1(e) shows a process chart which uses the mask 13 to
form a third aperture 11c by etching of a semi-insulating substrate
11; and FIG. 1(f) shows a process chart for forming a grounding
electrode 17 to form a VIA-hole.
[0018] The fabrication method of the semiconductor device according
to the first embodiment of the present invention will be explained
with reference to the process charts shown in the cross section of
FIG. 1. [0019] (a) As shown in FIG. 1(a), an electrode 12, which
has a certain size is formed on, for example, the front side of one
surface 11a of the semi-insulating substrate 11. The
semi-insulating substrate 11 is composed of compound
semiconductors, such as GaN or SiC, for example. The electrode 12
is formed with Ni etc. An earthing terminal etc. of a circuit
element (not shown) formed on the semi-insulating substrate 11, for
example, on one surface 11a, is connected to the electrode 12.
[0020] A mask layer 13 composed of metal, such as Al, is formed on
the surface 11b of another side, for example, the back-side of the
semi-insulating substrate 11. One of characteristics that an
etching rate by etching gas used when performing dry etching of the
semi-insulating substrate 11 is smaller than the semi-insulating
substrate 11 is used for the metal which forms the mask layer 13,
so as to mention later. Moreover, a resist layer 14 is formed on
the mask layer 13.
[0021] A mask pattern 15 is placed on the upper part of the
semi-insulating substrate 11 on which the mask layer 13 and the
resist layer 14 are formed. For example, a transmission hole 15a is
formed in a part of the mask pattern 15 letting light pass through.
The mask pattern 15 is placed so as to become the physical
placement relation, which the transmission hole 15a and the
electrode 12 oppose. A luminous source 16 is placed on the opposite
side of the semi-insulating substrate 11 on an illustrated upper
part of the mask pattern 15, for example, on the basis of the mask
pattern 15. [0022] (b) Next, illuminate the resist layer 14 through
the mask pattern 15 from the luminous source 16. [0023] (c)
Afterward, perform a developing procedure, and as shown in FIG.
1(b), form a first aperture 14a in a part with which the light is
illuminated, for example, a position which opposes the electrode
12. At this time, the mask layer 13 is exposed to a bottom surface
of the first aperture 14a. In addition, area size of the first
aperture 14a is smaller than the area size of the electrode 12. At
this point, the case of a positive resist is explained. However, a
negative resist can also be used. [0024] (d) Next, heat the resist
layer 14. By the heating process, as shown in FIG. 1(c), an edge
corner of marginal upper limit surrounding the first aperture 14a
becomes smooth, and a first tapered region 14b where thickness
becomes thin toward the first aperture 14a side is formed around
the first aperture 14a circularly, for example. [0025] (e) Next,
etch the mask layer 13 using the first aperture 14a of the resist
layer 14. The etching is performed by dry etching using Ar (argon)
gas or halogen related gas, such as F and Cl, for example.
According to the dry etching, as shown in FIG. 1(d), a second
aperture 13a is formed in the mask layer 13, and the surface 11b of
another side of the semi-insulating substrate 11 is exposed to a
bottom of the second aperture 13a.
[0026] When etching the mask layer 13, as for the resist layer 14
which functions as a mask, the circumference of the first aperture
14a is the first tapered region 14b (FIG. 1(c)). Therefore, when
etching the mask layer 13, also about the first tapered region 14b,
the etching progresses to outside in order with the passage of time
from an inner side where thickness near the first aperture 14a is
thin, and a diameter of the first aperture 14a is expanded
gradually.
[0027] Therefore, about the etching of the mask layer 13, first of
all, a part exposed to a bottom of the first aperture 14a is
etched. Then, with expansion of the diameter of the first aperture
14a of the resist layer 14, the etching progresses to outside
gradually from an inner side about the mask layer 13, and a
diameter of the second aperture 13a also expands gradually. At this
time, the etching of the inner side of the mask layer 13 progresses
rather than the outside. Therefore, a second tapered region 13b
where thickness becomes thin gradually, for example toward the
second aperture 13a side is formed around the second aperture 13a
circularly, for example. [0028] (f) Next, as shown in FIG. 1(e),
remove the resist layer 14, and then etch the semi-insulating
substrate 11 by using the mask layer 13. The etching of the
semi-insulating substrate 11 is performed by dry etching using Ar
gas or halogen related gas, such as F and Cl, for example.
[0029] First of all, the etching of the semi-insulating substrate
11 starts at a part exposed to a bottom of the second aperture 13a,
for example, a range surrounded by a dotted line d1 vertical to the
surface of the semi-insulating substrate 11. Then, a third aperture
11c that passes through the semi-insulating substrate 11 is formed
according to progress of the etching.
[0030] At this time, the etching goes to the outside where
thickness is thick in order from an inner side where thickness is
thin, and a diameter of the second aperture 13a is expanded in a
second tapered region 13b of the mask layer 13, as well as the case
of the resist layer 14 explained with FIG. 1(d). Therefore, as for
the semi-insulating substrate 11, for example, an illustrated upper
inside diameter of the third aperture 11c becomes gradually large
with expansion of a diameter of the second aperture 13a in parallel
to formation of the third aperture 11c. In this case, progress of
etching of, for example, the illustrated upper part of the third
aperture 11c, for example, a part located in the surface 11b of
another side, becomes early. For this reason, as shown in a dotted
line d2, the side of an inside diameter D2 of an aperture opened to
the surface 11b of another side of the semi-insulating substrate 11
becomes larger than an inside diameter D1 of an aperture opened to
the surface 11a of one side. Therefore, the third aperture 11c that
has a third tapered region 11d where an inside diameter becomes
small gradually toward the surface 11a of one side from the surface
11b of another side is formed. [0031] (g) Next, as shown in FIG.
1(f), remove the mask layer 13. [0032] (h) Then, as shown in FIG.
1(f), by methods, such as vacuum evaporation or electroplating, the
conductive layer 17 which is composed of metal, such as Au, is
formed in the surface 11b of another side of the semi-insulating
substrate 11 and the inner surface 11d of the third aperture 11c,
and the back side of the electrode 12 facing the third aperture
11c, and then a VIA hole is completed.
[0033] At this time, the electrode 12 has a form which fills up an
aperture of the VIA hole which composes the VIA hole, for example.
Moreover, the conductive layer 17 formed in the surface 11b of
another side of the semi-insulating substrate 11 functions, for
example as a ground conductor.
[0034] According to the above-mentioned embodiment, as shown in the
dotted line d2 of FIG. 1(e), the whole of the third aperture 11c is
tapered region 11d in the depth direction. In order to form the
conductive layer 17 securely, it is preferable for the whole of the
depth direction to be a tapered region. However, it may be a
configuration which provides the tapered region in a part of third
aperture 11c, for example, only partial region of the illustrated
upper part of the third aperture 11c continuous from the surface
11b of another side. In this case, although an effect is small
compared with the case where the whole is the tapered region, an
effect which forms a conductive layer securely is obtained.
[0035] Moreover, when forming the conductive layer 17 in the inner
surface of the third aperture 11c, the mask layer 13 is removed.
However, the conductive layer 17 can also be formed from on the
mask layer 13, without removing the mask layer 13.
[0036] FIG. 2 shows a schematic configuration diagram of an etching
apparatus applied to the VIA hole formation process for the
semi-insulating substrate, in the fabrication method of the
semiconductor device according to the first embodiment of the
present invention.
[0037] At this point, the method for etching the semi-insulating
substrate 11 will be explained with reference to the schematic
structural drawing of FIG. 2.
[0038] A cathode 22 is placed, for example, at the lower side in a
chamber 21. An anode 23 is placed at the upper part of the cathode
22 in a position which opposes the cathode 22. For example, a
high-frequency power source 24 is connected to the anode 23, and
the cathode 22 is grounded. And, the semi-insulating substrate 11
to be etched is mounted, for example on the cathode 22. Moreover, a
supply port 25 for supplying etching gas, for example, Ar gas, or
gas including halogen related elements, such as F and Cl, is
provided at the illustrated upper part of the chamber 21. An
exhaust port 26 for exhausting the gas in the chamber 21 is
provided at the illustrated lower part of the chamber 21.
[0039] In the above-mentioned configuration, the etching gas is
supplied into the chamber 21 from the supply port 25. The etching
gas is excited by high frequency which the high frequency power
source 24 generates, and the semi-insulating substrate 11 is etched
by, for example an action of accelerated ion etc.
[0040] According to the above-mentioned configuration, the tapered
region is provided in the inner surface of the VIA hole of the
semi-insulating substrate. In this case, the aperture of one side
of the VIA hole becomes large, and an inclination of the inner
surface of the VIA hole becomes a form where metal forming the
conductive layer is received. Therefore, when forming the
conductive layer by methods, such as vacuum evaporation and
electroplating, the conductive layer is formed securely and the
disconnection caused by step is prevented.
[0041] Moreover, when a GaN substrate, a SiC substrate, a sapphire
substrate, or diamond substrate, etc. are used as the
semi-insulating substrate, these substances are deficient in
reactivity at the time of etching in order to form the VIA hole,
and it is difficult to form the tapered region in the inner surface
of the VIA hole. For example, since chemical etching is difficult
for SiC, it becomes strong physical etching of sputtering nature,
such as dry etching. Therefore, when forming the VIA hole, it is
difficult to form the tapered region and it becomes a vertical VIA
hole easily.
[0042] However, if a mask layer which is composed of Al etc. and
which performed taper machining is used, also for a GaN substrate
or a SiC substrate, the tapered region can be easily formed in the
inner surface of the VIA hole, and the VIA hole without the
disconnection caused by step is obtained.
[0043] Moreover, even if the aperture of one side of the VIA hole
which forms the VIA hole is large, the aperture by the side of the
electrode is small. Therefore, it is not necessary to enlarge the
electrode, and a circuit is prevented from becoming oversize.
Other Embodiments
[0044] The present invention has been described by the first
embodiment and its modification, as a disclosure including
associated description and drawings to be construed as
illustrative, not restrictive. With the disclosure, artisan might
easily think up alternative embodiments, embodiment examples, or
application techniques.
[0045] In addition, it cannot be overemphasized that the amplifying
elements are applicable not only by FET (Field Effect Transistor)
but other amplifying elements, such as HEMT (High Electron Mobility
Transistor), LDMOS (Lateral Doped Metal-Oxide-Semiconductor Field
Effect Transistor), and HBT (Hetero-junction Bipolar
Transistor).
[0046] Such being the case, the present invention covers a variety
of embodiments, whether described or not. Therefore, the technical
scope of the present invention is appointed only by the invention
specific matter related appropriate scope of claims from the
above-mentioned explanation.
[0047] According to the present invention, the tapered region where
the inside diameter changes to the inner surface of the VIA hole
which composes the VIA hole is formed. Therefore, the conductive
layer is securely formed in the inner surface of the VIA hole, and
the semiconductor device which has the VIA hole without the
disconnection caused by step, and the fabrication method for the
same are achieved.
[0048] The semiconductor device and the fabrication method for the
same according to the embodiments of the present invention are
applied to a semiconductor device in which it is difficult for
thinned layer, such as a SiC substrate and a GaN wafer substrate,
and has wide industrial application fields, such as an internal
consistency type power amplification element, an electric power
MMIC (Monolithic Microwave Integrated Circuit), a microwave power
amplifier, and a millimeter wave power amplifier.
* * * * *