U.S. patent application number 12/490586 was filed with the patent office on 2010-07-22 for environmentally robust liquid crystal polymer coated optical fiber cable and its use in hermetic packaging.
This patent application is currently assigned to LINDEN PHOTONICS, INC.. Invention is credited to Amaresh Mahapatra, Robert J. Mansfield.
Application Number | 20100183269 12/490586 |
Document ID | / |
Family ID | 46329863 |
Filed Date | 2010-07-22 |
United States Patent
Application |
20100183269 |
Kind Code |
A1 |
Mahapatra; Amaresh ; et
al. |
July 22, 2010 |
ENVIRONMENTALLY ROBUST LIQUID CRYSTAL POLYMER COATED OPTICAL FIBER
CABLE AND ITS USE IN HERMETIC PACKAGING
Abstract
The invention relates to high-strength, abrasion-resistant
optical fiber cable having a supplemental layer consisting
essentially of a liquid crystal polymer (LCP) to enhance the
cable's tensile strength and hermetically seal it, and an outermost
encasing layer to protect the LCP supplemental layer from damage
that could otherwise diminish the tensile strength or destroy the
moisture barrier properties of the cable gained by adding the
supplemental liquid crystal polymer layer. The encasing layer is
preferably a thin layer of a smooth, non-crystalline thermoplastic
that can be easily removed with chemicals that do not affect the
properties of the supplemental layer so that the supplemental layer
can be made accessible for promoting the formation of hermetically
sealed interfaces between the cable and other structures.
Cross-head extrusion methods for coating optical fibers with LCP
and encasing layers are described along with laser and ultrasonic
bonding techniques for fabricating hermetic packages.
Inventors: |
Mahapatra; Amaresh; (Acton,
MA) ; Mansfield; Robert J.; (Sterling, MA) |
Correspondence
Address: |
FRANCIS J. CAUFIELD
6 APOLLO CIRCLE
LEXINGTON
MA
02421-7025
US
|
Assignee: |
LINDEN PHOTONICS, INC.
Westford
MA
|
Family ID: |
46329863 |
Appl. No.: |
12/490586 |
Filed: |
June 24, 2009 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11986815 |
Nov 27, 2007 |
7570853 |
|
|
12490586 |
|
|
|
|
Current U.S.
Class: |
385/94 ;
385/100 |
Current CPC
Class: |
G02B 6/4432 20130101;
G02B 6/4201 20130101; G02B 6/02395 20130101; C03C 25/1065
20130101 |
Class at
Publication: |
385/94 ;
385/100 |
International
Class: |
G02B 6/36 20060101
G02B006/36; G02B 6/44 20060101 G02B006/44 |
Claims
1. A packaging system for hermetically sealing opto-electronic
components while providing a port for exchanging signals with
components outside of said system, said packaging system
comprising: a housing for holding at least one opto-electronic
component in place within said housing and including a port for
receiving and holding at least one optical fiber cable adapted to
optically connect with said opto-electronic component to provide a
conduit for exchanging signals with said opto-electronic component,
said housing being composed of a material for at least in part
hermetically sealing said opto-electronic component within said
housing; and an optical fiber cable having at least one
supplemental layer comprising a liquid crystal polymer material to
enhance the strength of said optical fiber cable and promote the
formation of a final hermetic seal through said housing port where
said supplemental layer of said optical fiber cable interfaces with
said housing to complete the hermetic seal of said opto-electronic
component within said housing.
2. The packaging system of 1 wherein said housing includes
electrical feedthroughs for connecting electrical conductors to
said opto-electronic device.
3. The packaging system of claim 1 further including an encasing
layer surrounding said supplemental layer to protect it from damage
that could otherwise diminish the tensile strength and hermetic
seal of said optical fiber cable gained by adding said supplemental
layer of said liquid crystal polymer material, said encasing layer
comprising a-smooth, non-crystalline thermoplastic.
4. The optical fiber cable of claim 1 wherein said encasing layer
is selected from the group comprising polyamides and
polyesters.
5. The optical fiber cable of claim 1 wherein said polyamide is
Nylon 12.
6. The optical fiber cable of claim 4 wherein said polyamide is
chemically removable with a softening agent selected from the group
comprising dichloromethane, combined with trifluoroacetic
anhydride, benzyl alcohol at 130.degree. C., and HFIP+potassium
trifluoroacetate (mass fraction 0.2%).
1,1,1,3,3,3-Hexafluoropropan-2-ol (HFIP).
7. The optical fiber cable of claim 4 wherein said polyesters are
chemically removable with a softening agent selected from the group
comprising methylene chloride, acetone, methanol, and ethanol.
8. The optical fiber cable of claim 1 wherein said encasing layer
can be easily removed with chemicals that do not affect the
properties of said supplemental LCP layer so that said supplemental
layer can be made accessible to form hermetically sealed interfaces
between said optical fiber cable and other structures.
9. The optical fiber cable of claim 1 wherein said liquid crystal
polymer material comprises a thermotropic thermoplastic.
10. The packaging system of claim 1 wherein said housing comprises:
a substrate for fixturing said at least one opto-electronic
component; a liquid crystal polymer gasket hermetically sealed to
said substrate and having formed therein at least one recess
adapted to define said port for said optical fiber cable; and a
liquid crystal polymer cap hermetically sealed to said gasket.
11. The packaging system of claim 10 wherein a liquid crystal
polymer gasket is ultrasonically welded to said substrate.
12. The packaging system of claim 10 wherein the liquid crystal
polymer cap is ultrasonically welded to said gasket.
13. The packaging system of claim 10 wherein said liquid crystal
polymer cap is laser bonded to said substrate.
14. The packaging system of claim 10 wherein said liquid crystal
polymer cap is laser bonded to said substrate within the wavelength
range from 1.5 to 4.0 microns.
15. The packaging system of claim 10 wherein said substrate is a
material selected from the group consisting of liquid crystal
polymer, silica, silicon, ceramic, silicon carbide, and metal.
16. The packaging system of claim 10 wherein said gasket further
includes electrical feedthroughs for connecting electrical
conductors to said opto-electronic device.
17. The packaging system of claim 16 wherein said gasket is
injection molded.
18. The packaging system of claim 17 wherein said substrate and
said gasket are formed as a single LCP piece by injection
molding.
19. The packaging system of claim 1 wherein said opto-electronic
component is selected from the group comprising MEMS and OMEMS
devices.
Description
CROSS REFERENCE TO RELATED APPLICATION
[0001] This application is divisional application claiming benefit
from co-pending U.S. patent application Ser. No. 11/986,815 filed
on Nov. 27, 2007 in the name of Amaresh Mahapatra, et al. and
entitled "Environmentally Robust Liquid Crystal Polymer Coated
Optical Fiber And Its Use In Hermetic Packaging", the entire
contents of which are incorporated herein by reference.
FIELD OF THE INVENTION
[0002] This invention generally relates to fiber optical component
packaging structured to provide a hermetically sealed and moisture
resistant barrier that passes standard industry hermeticity and
damp heat qualification tests. More particularly, it relates
high-strength, abrasion resistant optical fiber cable that makes
use of a supplemental layer of a liquid crystal polymer to enhance
the tensile strength of the fiber cable, hermetically seal it, and
promote the formation of hermetically sealed interfaces between
such coated fiber and other structures and an encasing layer to
preserve the cable properties provided by the LCP supplemental
layer.
BACKGROUND OF THE INVENTION
[0003] Most electronic components, such as integrated circuits
(ICs) for example, are sealed within plastic packages. The plastic
material is simply molded directly over the IC and a metal lead
frame to which it is attached. However, this type of packaging is
not particularly well suited for use with MEMS devices, where there
is generally a need for an open space within the package to
accommodate motion of the mechanical device within. In addition,
effective packaging for MEMS and other electro-optical devices
often needs to be comprised of hermetically sealed housings to
prevent the ingress of corrosive elements such as water vapor and
oxygen, isolate internal components from shock and vibration,
shield the component from potentially harmful radiation, and
provide a means of conducting heat away from power dissipating
components. In the case of electro-optic devices, the packaging
must also provide a stable platform for the positioning and
interconnection of optical components, such as laser diodes,
modulators, input and output fibers, and the like.
[0004] One of the most important features of a hermetic package is
its ability to withstand extended periods of "damp heat" and remain
"dry" inside. A typical hermetic test for telecom packages measures
the package's ability to withstand 2000 hours in an environment of
85.degree. C. at 85% relative humidity and remain "dry" inside; dry
being defined as less than 5000 ppm internal moisture at the end of
the test. Materials conventionally used to achieve a hermetic seal
are few: metal, glass, and ceramics. Packages sealed properly with
these materials are considered truly hermetic. Common hermetic seal
interfaces are metal-to-metal seals, made via welding, brazing, or
soldering; glass-to-metal seals; ceramic-to-metal seals; and
glass-to-glass seals.
[0005] An example of a typical hermetic fiberoptic component
package is a Kovar box with a Kovar lid that is resistance welded
in place via a seam sealer. Light passes in and out of the package
via hermetic optical paths. Current methods of passing light
through hermetic photonic packages can be categorized as freespace
or fiber feedthroughs. Freespace employs hermetic windows having
metallized edges that are soldered or brazed into the package wall,
sometimes via an intermediate metal ferrule or subcell. A hermetic
collimator lens assembly is soldered to a metal package.
Telecommunication grade optical fiber typically has a polymer
cladding made of UV curable acrylate or Teflon. Hermetic seals
cannot be made to these claddings since their moisture barrier
properties are inherently low. Hence, wherever optical fiber exits
a hermetic package, the cladding layer must be stripped, and the
bare silica fiber metallized. Afterwards, a hermetic seal is made
to the metallization. Because bare silica fiber is fragile and
often breaks, this process is inherently expensive. Hermetic fiber
feedthroughs are made using metallized glass fibers that are
soldered to the package, typically via a cylindrical sleeve or
support that protrudes from the package wall. The ferrule can then
be hermetically attached to the package wall, typically
soldered.
[0006] Fiber feedthrough ferrules with glass frits feature fibers
sealed into a metal sleeve via a glass-to-metal seal using a glass
frit between the glass fiber and metal sleeve (in this case the
fiber is not metallized but its polymer cladding must be stripped).
The ferrule can then be soldered to the package wall, or it may be
part of the package wall.
[0007] Thus, there is a continuing requirement in the industry for
low-cost hermetic packages. Polymer packaging would be inherently
low-cost; however, adhesives, epoxies, and polymers have not been
shown to keep moisture out of packages in extended damp heat tests.
Some polymer-based sealing methods and packages may satisfy limited
test requirements, but moisture diffuses through these materials
over time. Nonhermetic and quasi-hermetic packages are suitable for
certain applications. The component end-customer usually determines
test requirements.
[0008] Recently, a new class of polymers, Liquid Crystal Polymers
(LCP), has been shown to have excellent moisture and oxygen barrier
properties. Silicon Bandwidth, Inc., (Fremont, Calif.) and Foster
Miller, Inc. (U.S. Pat. No. 6,320,257), have both proposed a
liquid-crystal polymer package that can be metallized and soldered
or welded to suitable lids to produce packages that may not be
strictly hermetic but may pass the Telecordia "damp heat"
qualification test. Even with an LCP package, the problems of
producing an optical port remain; namely, stripping and metallizing
the fiber and soldering to the metallization. A need, therefore,
exists for an improved technique to implement an optical port to be
incorporated into metal, ceramic or LCP packages, and it is a
primary object of this invention to satisfy this need.
[0009] Additionally, it is known (See U.S. Pat. No. 4,778,244 to
Ryan) to overcoat optical fiber with LCPs to provide an optical
cable with enhanced strength which, in turn, may be over coated
with scuff resistant coatings. However, the scuff resistant
coatings described are difficult to remove to allow ready access to
the LCP coating for other purposes.
[0010] It is another object of this invention to provide optical
fiber cable with enhanced strength and easily removable encasing
coatings to protect against environmental effects such as moisture
and chafing forces.
[0011] It is yet another object of this invention to provide
optical fiber structures having properties for promoting the
formation of hermetic seals when combined with other
structures.
[0012] It is still another object of the present invention to
provide hermetically sealed packaging for optical and
electro-optical components.
[0013] Yet another object of the present invention is to provide
manufacturing processes for fabricating optical fibers coated with
LCP and chemically removable encasing layers.
[0014] Still another object of the present invention is to provide
manufacturing processes by which hermetically sealed devices can be
fabricated with LCP materials and optical fibers having
supplemental LCP and encasing layers to protect against
environmental effects such as moisture and mechanical forces.
[0015] Other objects of the invention will, in part, appear
hereinafter and will, in part, be obvious when the following
detailed description is read in connection with the drawings.
SUMMARY OF THE INVENTION
[0016] The invention relates to high-strength, environmentally
robust optical fiber cables having a supplemental layer consisting
essentially of a liquid crystal polymer (LCP) to enhance the
cable's tensile strength and hermetically seal it and an outermost
encasing layer to protect the LCP supplemental layer from damage
that could otherwise diminish the tensile strength and moisture
resistant properties of the cable gained by adding the supplemental
liquid crystal polymer layer. The encasing layer is preferably a
thin layer of a smooth, non-crystalline thermoplastic that can be
easily removed with chemicals that will not affect the properties
of the LCP supplemental layer so that the supplemental layer can be
made accessible for promoting the formation of hermetically sealed
interfaces between the cable and other structures. Crosshead
extrusion methods for coating optical fibers with LCP and
chemically removable layers are described along with laser and
ultrasonic bonding techniques for fabricating hermetic
packages.
[0017] In one aspect, the invention comprises an optical fiber
cable having a core with a given index of refraction. The core is
surrounded with a cladding layer having an index of refraction
lower than that of the core so that the two in combination are
capable of propagating light along the length of the fiber cable.
At least one other layer surrounds the cladding and comprises a
liquid crystal polymer material to enhance the strength of the
fiber cable, hermetically seal it, and promote the formation of
hermetically sealed interfaces between the optical fiber cable and
other structures. The core and cladding are preferably of pure
fused silica with the core slightly doped with an index raising
material. LCP coatings may also be applied to optical fiber cables
having acrylate buffer layers over pure fused silica cladding and
inner core. Surrounding the LCP supplemental layer is a thin
chemically removable encasing coating to maintain the strength
enhancing, moisture barrier, and interfacing benefits gained by the
presence of the LCP layer, but is otherwise easily removable under
field conditions via chemicals that do not destroy the properties
of the LCP layer, especially its ability to form hermetic seals
with other structures fabricated of LCP.
[0018] It is preferred to use a vertical drawing process with a
crosshead extruder to apply the LCP and encasing layers over fibers
formed of pure fused silica claddings and inner cores. Use of a
horizontal crosshead extrusion process may be made for applying the
LCP and encasing layers over fibers that already have exterior
polymer buffers such as acrylate or the like.
[0019] Packaging systems for hermetically sealing opto-electronic
components, while providing ports for exchanging signals with
components outside of the system, are also provided. Such systems
comprise a housing for holding at least one opto-electronic
component in place within the housing and include means for
providing a port for receiving and holding at least one optical
fiber cable adapted to optically connect with an opto-electronic
component to provide a conduit for exchanging signals with the
opto-electronic component. The housing is composed of a material
for at least in part hermetically sealing the opto-electronic
component within it. An optical fiber cable having a liquid crystal
polymer layer and an exterior chemically removable encasing layer
is provided to enhance the strength of said optical fiber cable,
hermetically seal it, and promote the formation of a final hermetic
seal at the housing port where the LCP layer of said optical fiber
cable, upon the selective local removal of the encasing layer,
interfaces with the housing to complete the hermetic seal of the
opto-electronic component within the housing.
[0020] Housings comprise substrate bases, shallow casings or
gaskets, and caps that are provided with materials and features
making them amenable to fabrication using laser bonding and
ultrasonic welding to provide hermetic ports and seals.
BRIEF DESCRIPTION OF THE DRAWINGS
[0021] The structure, operation, and methodology of the invention,
together with other objects and advantages thereof, may best be
understood by reading the detailed description in connection with
the drawings in which each part has an assigned a label and/or
numeral that identifies it wherever it appears throughout the
various drawings and wherein:
[0022] FIG. 1 is a diagrammatic cross-sectional view of the
structure of an optical fiber cable in accordance with the
invention;
[0023] FIG. 2 is a diagrammatic perspective view of a vertically
oriented drawing apparatus with a crosshead extruder for applying
LCP and encasing layers over a fiber shortly after being drawn from
a preform;
[0024] FIG. 3 is a diagrammatic illustration showing how LCP
material becomes aligned as it passes through an extrusion head
during coating;
[0025] FIG. 4A is a diagrammatic cross-sectional view of the
structure of another optical fiber cable in accordance with the
invention;
[0026] FIG. 4B is a flow chart of a process for applying the outer
layers on the optical fiber cable shown in FIG. 1
[0027] FIG. 5 is an exploded diagrammatic perspective view of
components used to hermetically seal a device in accordance with
the invention;
[0028] FIG. 6 is a diagrammatic elevational view illustrating an
arrangement optionally employing a small ridge molded into an LCP
cap to further increase the localized pressure in forming a joint
between an LCP cap and a transparent substrate;
[0029] FIG. 7 is a diagrammatic perspective view of a hermetically
sealed packaging arrangement with an LCP cap and substrate along
with a cut away pressure plate and a scanning laser beam used for
bonding purposes to form hermetic seals;
[0030] FIG. 8A is a graph of the absorption spectra of silicon
illustrating that it is essentially transmissive to radiation with
wavelength above about 1 .mu.m;
[0031] FIG. 8B is a graph of the transmission of silica showing
that it is transmissive to radiation in the wavelength range from
0.2 .mu.m to 4 .mu.m;
[0032] FIG. 9A is an exploded diagrammatic perspective view, with
parts broken away, of a well-known hermetically packaged
electro-optical device;
[0033] FIG. 9B is an exploded diagrammatic perspective view, with
parts broken away, of an LCP packaged device in accordance with the
invention;
[0034] FIG. 10 is a diagrammatic perspective view, with parts
broken away, of a substrate machined with a small dovetail shaped
lip over which LCP is molded, along with an enlarged view of a the
detail of the dovetail;
[0035] FIG. 11 is a diagrammatic perspective view along with a
detailed enlargement for a design for over molding electrical
feedthroughs in LCP packaging in accordance with the invention;
[0036] FIG. 12 is a diagrammatic perspective view, with parts
broken away, showing an ultrasonic horn welding the components of
an LCP package in accordance with another aspect of the
invention;
[0037] FIG. 13 is a diagrammatic elevational view showing specially
configured components to be ultrasonically welded in an LCP
arrangement using energy directors in accordance with another
aspect of the invention; and
[0038] FIG. 14 is a diagrammatic perspective view, with parts
broken away, of an ultrasonic horn configured to form hermetic
seals in accordance with the invention, along with an enlarged view
of an energy director.
DETAILED DESCRIPTION
[0039] The invention relates to high-strength, abrasion-resistant
optical fiber cable having a supplemental layer consisting
essentially of a liquid crystal polymer (LCP) to enhance the
cable's tensile strength, hermetically seal it, and provide
interfacing and an outermost encasing layer to protect the
supplemental layer from damage that could otherwise diminish the
properties of the cable gained by adding the supplemental liquid
crystal polymer layer. The encasing layer is preferably a thin
layer of a smooth, non-crystalline thermoplastic that can be easily
removed with chemicals that will not affect the properties of the
supplemental layer so that the supplemental layer can be made
accessible for promoting the formation of hermetically sealed
interfaces between the cable and other structures. Methods for
hermetically sealing packaging are also provided.
[0040] Reference is now made to FIG. 1 which shows the
cross-sectional shape of a high-strength, abrasion-resistant
optical fiber cable 10 according to the invention. As seen, optical
fiber cable 10 comprises a core 12, a cladding 14, a supplemental
layer 16 composed of LCP, and a thin, chemically removable encasing
layer 18. Core 12 and cladding 14 are preferably formed of pure
fused silica (SiO.sub.2), but may be beneficially composed of other
suitable materials, as well. In addition, core 12 is slightly doped
with an index raising material, such as Germania (GeO.sub.2), so
that its index of refraction is slightly higher than that of
cladding 14. Core 12 and cladding 14 collectively operate by total
internal reflection to confine radiation in core 12 as it
propagates longitudinally along the fiber's length.
[0041] Generally, core 12 and cladding 14 are fabricated by drawing
down a preform made from a well-known modified inside chemical
vapor deposition process (MCVD) or OVD (outside vapor deposition)
or VAD (vapor phase axial deposition). During the drawing process,
LCP supplemental layer 16 is applied directly to the fiber by means
of a vertically oriented extruder. The liquid crystal polymer layer
16 is applied to enhance the strength of optical fiber cable 10,
hermetically seal it, and facilitate, in a manner to be described
later, the formation of hermetically sealed interfaces between
optical fiber cable 10 and other structures, as for example,
hermetically sealed component packaged devices.
[0042] Extruded LCPs have high tensile strength, a measure of the
force per unit cross-section at which an extruded tube of LCP will
break. However, as we have discovered through extensive
experiments, this does not mean that LCPs are safe from external
environmental effects such as moisture and mechanical forces such
as chafing forces applied over time. For example, abrasion from
chafing forces is a form of damage that results when the surface of
a material is rubbed against the surface of another material. In
many potential applications, optical cables need to have high
tensile strength so that they do not break as a result of the
tension during deployment. They also may need to be abrasion
resistant since deployment may involve pulling through a conduit
where the cable surface will rub against the conduit walls and thus
be exposed to chafing forces.
[0043] We have determined experimentally that extruded LCP layers
on optical fiber do not possess sufficient resistance to
environmental effects such as abrasion, and have developed an
abrasion test method to determine abrasion resistance. A fine grit
(120 grit) rubberized abrasive wheel is used for abrasion. A length
of LCP coated optical cable is securely fastened to a rigid
horizontal surface. The test section is continuously abraded, in a
reciprocating manner for 100 cycles, by a 25 mm square section of
the rubberized abrasive element. The load on the abrasive element
during test is a minimum of 500 gm. Following the test, the sample
is examined under a microscope to determine the extent of surface
damage. The sample passes the test if the breaking strength after
abrasion is no less than 90% of the breaking strength before
abrasion. As a consequence of our testing, we have determined that
it is necessary to provide an encasing layer 18 over the LCP
supplemental layer 16 to preserve the strengthened properties and
hermetic seal of optical fiber cable 10 which otherwise would be
diminished considerably absent the encasing layer 18. Results have
indicated that the enhanced strength made possible by the LCP layer
can be reduced by abrasion by as much as 41.7%, an unacceptably
high level.
[0044] We have found that resistance to environmental effects can
be made acceptable by extruding a thin layer of a smooth,
non-crystalline thermoplastic on top of the supplemental LCP layer.
The polymer for this layer is chosen not for its tensile strength,
but for its ability to produce a smooth, surface resistant to
externally applied mechanical forces tending to abrade or otherwise
mechanically damage the supplemental LCP layer.
[0045] In addition to the protective properties of layer 18, it
must also be easily removable under anticipated conditions of use
in the field so that it can be selectively removed to expose the
underlying LCP layer so that the supplemental LCP layer can be
interfaced (bonded) with other structures to provide hermetically
sealed systems. To this end, the composition of the encasing layer
18 preferably is chemically removable by exposure to softening
agents that permit small, but controllable, lengths to be wiped
away without damaging or changing the underlying properties of the
supplemental LCP layer 16.
[0046] Suitable compositions of the encasing layer 18 include
polyamides such a Nylon 12 and polyesters. Nylon 12 may be rendered
removable (strippable) by exposure to Chromic Acid (50%),
Hydrochloric acid (37%), Nitric Acid (50%), or Sulphuric Acid (50%)
while polyamides, in general, can be softened with dichloromethane,
combined with trifluoroacetic anhydride, which reacts with the
amide groups and leads to a rapid dissolution of polyamides at
ambient temperature. Benzyl alcohol may also be used at 130.degree.
C. Warm benzyl alcohol presents few safety hazards. HFIP+potassium
trifluoroacetate (mass fraction 0.2%).
1,1,1,3,3,3-Hexafluoropropan-2-ol (HFIP) is also a quasi-universal
solvent for polyamides at ambient temperature.
[0047] Polyesters may be rendered strippable by exposure to
Methylene Chloride, acetone, methanol, and ethanol.
[0048] The material composition of encasing layer 18 should also be
extrudable, preferably in the form of a thermoplastic.
[0049] Reference is now made to FIG. 2 which shows apparatus by
which optical fiber cable 10 is fabricated with supplemental LCP
layer 16 and encasing layer 18, both applied serially to cladding
14 that, in turn, surrounds core 12. As seen in FIG. 2,
supplemental LCP layer 16 is applied to cladding 14 during the
fiber drawing process, as it is essential that the fiber (core 12
and cladding 14) be protected from environmental effects
immediately upon being drawn.
[0050] A fiber perform 11, from which core 12 and cladding 14 is
drawn, is fed vertically into the top of a high temperature furnace
13, where the tip of perform 11 is heated until it softens. A thin
glass fiber consisting of core 12 and cladding 14 is then drawn
from the bottom of perform 11 and fed through the remainder of the
coating apparatus. To apply the supplemental LCP layer 16 to
cladding 14, an extruder 15 feeds molten LCP polymer under pressure
into a conical shaped tip 17 surrounding the fiber. The molten
polymer thus forms a tight fitting sleeve around the fiber and is
cooled and solidified by passing it through cold water contained in
a cylindrical water trough 19. The water in trough 19 is circulated
and cooled with fiber 10 passing through it over two pulley wheels,
21 and 23, respectively. Afterwards, the encasing layer 18 is
applied with apparatus (not shown) similar to that used to apply
LCP supplemental layer 16. Finished fiber cable 10 is finally wound
onto a large diameter fiber take-up storage drum 25. This entire
process may be under the supervision and control of a computer with
appropriate software to schedule and monitor the apparatus,
associated activities of the apparatus, and communicating
instructions and data among the components of the apparatus.
[0051] Referring back to FIG. 1 again, core 12 is preferably single
mode having a diameter in the range between 5 to 8 micrometers, the
diameter of cladding 14 extends out to 125 micrometers, and the
thickness of supplemental LCP layer 16 is 75 micrometers, and that
of the encasing layer 18 is about 40 micrometers or less, making
the final diameter of optical fiber cable 10 about 440 micrometers.
Supplemental LCP layer 16 may be increased in thickness to increase
the tensile strength of optical fiber 10.
[0052] Optical fibers are thin filaments of glass typically about
0.005'' in diameter. As described above, they consist of a central
core region surrounded by an optical cladding, the refractive index
of which is slightly lower than that of the core. Light launched
into one end of the fiber is guided, essentially without loss, via
total internal reflection at the core-cladding interface. Optical
fibers are inherently very strong. Indeed, fused silica of which
many fibers are made is one of the strongest materials known, with
a modulus of 10.sup.7 psi. During the high temperature draw
process, the surface of the optical fiber is essentially flame
polished making it very smooth and clean. As the fiber is drawn
from a furnace, a primary buffer coating of a relatively soft
elastomeric material is applied. In commercial optical fiber, the
typical primary coating is UV cured acrylates, or Teflon. This
coating serves to maintain the polished surface of the fiber and
also to prevent the fiber from bending too sharply, which would
cause stress and also lead to increased optical attenuation.
Typically, the primary coating is about 60 .mu.m thick, giving a
final diameter of the primary coated fiber of about 250 .mu.m.
[0053] To create a fiber cable, the optical fiber is further
protected by additional layers of extruded polymer and in many
cases, longitudinal strength members, made from materials such as
Kevlar.
[0054] Apart from the advantages offered in terms of packaging, LCP
coatings also present a means of creating very strong, compact and
lightweight optical fiber cables. For these applications, optical
fiber structures of the type shown in FIG. 4A may be used. Here,
the optical fiber, designated at 50, has a slightly doped SiO.sub.2
core 52 surrounded by an SiO.sub.2 cladding 54, in turn, surrounded
by an acrylate buffer 56. Surrounding the acrylate buffer 56 is a
supplemental LCP layer 58, again 75 or more micrometers in
thickness. Beyond the supplemental LCP layer 58 is an encasing
layer 60, such as that previously described as layer 18 in FIG. 1.
Thus, the use of LCP as a supplemental layer or coating on top of a
conventional primary buffer or coating of commercial optical fiber
is shown. Such cables have applications in precision guided
munitions, such as TOW missiles and "wire" guided torpedoes, local
area optical communications (plenum cables), and optical fiber
sensors. There appear to be no other materials that can be extruded
onto optical fibers that would provide the mechanical strength,
thermal stability, and moisture barrier properties of LCPs.
[0055] Reference is now made to FIGS. 4A and 4B, which show a
method for applying supplemental LCP layer 58 and encasing layer
60. After the basic structure comprising core 52 and cladding 54
and a primary buffer coating 56 consisting typically of acrylate is
formed, it is stored on a feed spool 20 that is mounted for
rotation around a journal. Uncoated fiber leaves feed spool 20 and
is guided by a positioning idler 22 to a well-known crosshead
extruder 24 that is used to raise LCP material above its melt
temperature and deposit it as a layer on buffer coating 56.
[0056] FIG. 3 illustrates in a general way how LCP material is
organized and oriented as it passes thorough crosshead extruder 24,
as will be explained in more detail hereinafter. Afterwards, about
10 cm downstream of crosshead extruder 24, the LCP coated fiber is
sent through a water bath 26 to solidify the supplemental LCP layer
58. Care must be taken to make the water bath free of turbulence to
reduce the possibility of forming a wavy exterior surface on
supplemental LCP layer 58. After solidifying, the diameter of
supplemental LCP layer 58 is measured at test station 28 for
conformity with its intended design specification. Then, another
idler 30 guides the finished fiber structure onto a take-up spool
32 or alternatively, extruder 24, cooling bath 26 and test station
28 are repeated in serial fashion to apply encasing layer 60.
Throughout the coating process, take-up spool 32 places the fiber
under tension to remove it from feed spool 20 and draw it through
all of the other process stations prior to being rolled up for
storage and subsequent use. Process control of all of the
parameters of the various components and materials used in the
coating process are under the control of a process controller 34,
or suitably programmed computer, that passes signals and data among
the various components via network connectors 36-48, or the like.
General housekeeping chores are also under the control of process
controller 34.
[0057] Having described fiber structures employing supplemental LCP
and easily removable encasing layers and their method of
fabrication, LCP materials themselves will now be discussed,
particularly their barrier properties.
[0058] Not only are LCPs highly impervious to moisture, but also,
as a result of their tightly packed crystalline nature, their
interstices allow very little absorption of moisture or other
gasses. Consequently, out-gassing, which is a problem for many
polymers, is reduced to insignificant levels. Further, since LCP is
merely heated to become fluid, there is no need to use solvated
LCP, which eliminates another major source of outgassing. The
moisture absorption and transmission properties of LCPs are
compared with other polymer classes in Table 1 below.
TABLE-US-00001 TABLE 1 Comparison of barrier properties of
different polymer classes Moisture absorption Moisture (%
@73.degree. F., transmission rate Polymer 50% relative
(gm/m.sup.2/day/atm./ class Specific polymer humidity, per day mil
Polyester PET (poly ethylene 0.06 28 terephthalate) (immersion)
Fluorinated PVDF 0.5 5.3 polymer (Polyvinylidene fluoride, Dupont
TTR10AH9) Polyamide Nylon 1.2 Liquid Vectran 200P (made 0.02 0.17
crystal by Tecona) polymer Zenite (made by 0.002 Dupont) 0.05 (6
mth. Immersion)
[0059] From the table, it can clearly be seen that LCPs offer very
significant improvement both in terms of moisture absorption and
transmission.
[0060] Table 2 below shows typical film properties of LCP versus
polyethylene terephthalate (PET) films (Lusignea, R. W., 1997,
"Liquid Crystal Polymers: New Barrier Materials for Packaging,"
Packaging Technology, October, 1997.). The water transmission rate
through a 25 .mu.m LCP film is 0.17 gm/m.sup.2/day for an ambient
pressure of 1 atmosphere.
[0061] A typical electronic package including cap and housing may
be 10 mm.times.10 mm.times.2 mm. Assuming the whole package is made
of LCP, the total surface area is 280 mm.sup.2. The total amount of
moisture that would penetrate such a package in a year, M, is given
by:
M = 0.17 gm m 2 day .times. 365 days .times. 280 .times. 10 - 6 m 2
.apprxeq. 0.017 gm . ##EQU00001##
[0062] If the wall thickness of the housing and cap is 1 mm instead
of 25 .mu.M, the moisture level in the cavity after I year drops to
insignificant levels.
TABLE-US-00002 TABLE 2 Typical LCP film properties Biaxially-
oriented PET film LCP Film Tensile strength (kPa) 172,000 240,000
Tensile modulus (106 kPa) 5.2 12.4 Oxygen permeability (cc/m.sup.2-
78 @ 25 .mu.m 0.23 @ 25 .mu.m 24 hr.-atm.) Water vapor transmission
rate 28 @ 25 .mu.m 0.17 @ 25 .mu.m (gm/m.sup.2-24 hr.-atm.)(per
ASTM F-1249) Upper use temp. (.degree. C.) 120 Over 200 Density
(gm/cc) 1.4 1.4 Tear resistance, Initiation, 35 595 kN/m Tear
resistance, 9 to 53 175 to 525 Propagation, kN/m
[0063] From Table 2, the oxygen transmission rate through a 25
.mu.m LCP film is 0.23 cc/m.sup.2-24 hr.-atm. The total amount of
oxygen that would penetrate such a package in a year, O, is given
by:
O = 0.23 cc m 2 day .times. 365 days .times. 280 .times. 10 - 6 m 2
.apprxeq. 0.02 cc . ##EQU00002##
[0064] Given the volume of the cavity, this translates into a
partial pressure of 0.1 atmospheres, which would also become
negligible if the wall thickness of the housing and cap is 1 mm
instead of 25 .mu.m.
[0065] Therefore, the moisture and oxygen barrier properties of LCP
are more than adequate. Coupled with the moisture and oxygen
barrier properties of LCP, the invention provides reliable and
simple bonding techniques for providing hermetically sealed
packaging arrangements as will be described in more detail
hereinafter.
[0066] Having described the barrier properties of LCPs, it is also
important to understand their thermal, mechanical and electrical
properties.
[0067] LCPs are thermoplastic so that there is an intermediate
temperature such that the LCP is made fluid without a break down of
the crystal structure. They typically melt at about 280.degree. C.
and are thermally stable to 350.degree. C. The coefficient of
thermal expansion (CTE) is very low, and highly anisotropic, being
lowest in the direction of molecular alignment. The actual bulk
value of the CTE can therefore be controlled to some extent by
either controlling the degree of orientation, or by laminating
layers with orthogonal orientations (See U.S. Pat. No. 5,529,741
incorporated herein by reference). This is a desirable feature,
since it means that the CTE can be matched to that of the substrate
material, thus significantly reducing stress associated with
thermal cycling.
[0068] LCPs also exhibit very little creep. This means that
microscopic features produced by molding, embossing or other such
processes will retain their sharp edges and dimensional stability.
Complex packaging designs, as those to be described, are therefore
possible, in which finely detailed features can be defined to
locate, align and secure the various optical and opto-electronic
components.
[0069] In the electronic industry, the use of polymers with high
temperature stability is not new. For instance polyimide, which is
stable to 350.degree. C., has been used for fabrication of flexible
circuits in electronic assemblies. But, it has a tendency to absorb
moisture, which interferes with high frequency performance. It has
been found recently that liquid crystal polymers (LCP) have
significantly lower moisture absorption, and transmission while
being stable up to 350.degree. C. and can, therefore, be used in
high frequency flexible circuits.
[0070] LCPs have a low dielectric constant and loss factor from 1
kHz to 45 GHz. For instance copper clad Biac LCP, sold by W. L.
Gore for flex circuit applications, has a dielectric constant of
3.0 and a loss tangent of 0.003 from 3 to 45 GHz.
[0071] The beneficial properties of LCPs make their use as optical
fiber supplemental layers attractive for a variety of reasons.
Liquid Crystal Polymers (LCPs) are aromatic polyesters with rigid
rod like molecular structures. When heated and extruded, these long
crystalline segments tend to align themselves in the direction of
flow, much like logs in a river, see illustration in FIG. 3.
However, extruded LCPs form long polymer chains that are
principally aligned along the direction of extrusion as shown in
FIG. 3. Such structures are built of individual, but parallel,
interlacing strands of, polymer. Each strand has very high tensile
strength. When a tensile force is applied to the structure, it
exhibits high strength since the intertwined strands do not break
easily and do not slip past each other, Rubbing of the structure
surface against another surface, over time, however progressively
tears the individual strands apart. Where this has happened, the
structure loses tensile strength and moisture resistance since, in
these sections, the several strands are no longer interlaced but
become broken. To prevent degradation of tensile and moisture
barrier properties over time and exposure to environmental forces,
the extruded LCP needs to be encased by another material which is
largely amorphous so that there are no individual strands that can
separate one from the other, hence the need for the encasing layer
previously described.
[0072] It is the high rigidity of these long crystalline segments
that give the LCP materials their high modulus and low
permeability. As indicated earlier, this invention advocates the
use of Liquid Crystal Polymers as a supplemental layer or coating
of optical fibers. LCP materials that have been found useful for
the purposes of the invention comprise, for example, certain grades
of the Vectra.RTM. LCP line marketed by Ticona, Summit, N.J. 07901
(See http://www.ticona.com). Vectra.RTM. liquid crystal polymers
(LCP) are highly crystalline, thermotropic (melt-orienting)
thermoplastics that deliver exceptionally precise and stable
dimensions, high temperature performance and chemical resistance in
very thin-walled applications.
[0073] The Vectra series of LCPs are primarily HNA-HBA copolymers
where the fraction of HNA and HBA can be modified to alter LCP
properties (see, for example, p. 375, "An Introduction to Polymer
Physics," David I. Bower, Cambridge University Press 2002). HNA and
HBA are acronyms for hydrobenzoic acid and hydroxynaphthoic acid,
respectively.
[0074] The use of LCP as an accessible coating material in an
optical fiber cable significantly reduces the problems associated
with creating hermetically sealed optical ports in packaged
electro-optical components. It has been demonstrated that, under
the correct conditions of temperature, time, and pressure, a
hermetic bond can be created between glass and LCPs, and it has
been found that the temperature of the substrate to which the LCP
material is to be bonded should be higher than the melt temperature
of the LCP material and be applied under a slight positive
pressure. The use of optical fiber cable having a supplemental LCP
layer made accessible by removing an encasing coating is
illustrated in FIG. 5 in the packaging of an electro-optic
device.
[0075] Referring now to FIG. 5, there is shown an electro-optic
modulator 102 packaged according to the invention, although the
principals of the invention apply to any such device. The packaging
for electro-optic modulator 102 is indicated generally at 100 and
consists of molded LCP parts, which have features for locating and
securing input and output optical fiber cables, 104 and 106,
respectively. The two halves of the package, LCP cap 108 and gasket
110, are brought together to capture the input and output fibers,
104 and 106, in small molded, generally elongated semicircular,
recesses, 112 and 114, respectively, provided in the adjoining
faces of LCP cap 108 and gasket 110. It will be understood that the
encasing layer of the optical fiber cable will have been removed
over an appropriate length to permit its underlying supplemental
LCP layer to reside in recesses, 112 and 114. The two halves of
package 100 are then fused together by heating. A scanning laser
beam, ultrasonic or RF induction heating, or other functionally
similar technique may perform the heating. In the case of laser
bonding, the LCP materials need to be sufficiently thin to allow
the laser radiation to reach joint areas or the overlapping seal
areas can be melted to fuse the LCP materials to form seals, and
this can be done scanning from the side where an interface exists
or perpendicular to the joint as, for example, from the cap
side.
[0076] Because the fiber cable supplemental layer or coating is
made from the same material as the other packaging components
(LCP), a perfect seal is created when the two materials are fused
together. The package is hermetic since the LCP material has
excellent moisture and oxygen barrier properties. Materials for the
package can be selected from those already identified above.
[0077] With respect to the use of laser bonding, it was first
demonstrated on thermoplastics in the 1970's, but has only recently
found a place in industrial scale situations. The technique,
suitable for joining both sheet film and molded thermoplastics,
uses a laser beam to melt plastic in a joint region. The laser
generates an intense beam of radiation, which is focused onto the
material to be joined. This excites a resonant frequency in the
molecule, resulting in heating of the surrounding material. Three
forms of conventional laser bonding exist; CO2, Nd:YAG, and diode
laser bonding. Table 3 below gives comparative data on laser
bonding with CO2, Nd:YAG and diode lasers.
TABLE-US-00003 TABLE 3 Comparison of commercially available laser
sources for plastics processing Laser Type CO.sub.2 Nd:YAG Diode
Wavelength (.mu.m) 10.6 1.06 0.8-1.0 Max. power 60,000 6,000 6,000
(W) Efficiency 10% 3% 30% Beam Reflection off mirrors Fiber optic
and Fiber optic Transmission mirrors and mirrors Minimum spot
0.2-0.7 diam. 0.1-0.5 diam. 0.5 .times. 0.5 size* (mm)
[0078] Laser radiation is absorbed by polymers in molecular
vibration spectra of covalent bonds such as C--H, C--C, C--O,
C.dbd.O. The vibration spectra of a particular type of bond are
characteristic of that bond. The location of these vibrational
states is determined largely by the spring constant of the bond and
the reduced mass of the two nuclei. Since the vibrational energy is
inversely related to the reduced mass, bonds with low reduced mass
(such as C--H) have high vibrational frequencies. For example, the
C--H, --C.dbd.C--, and --C--O-- bonds have fundamental vibrational
resonance at wavelengths of 2, 3.3 and 10 .mu.m, respectively.
Since C--H is the bond with the lowest reduced mass in polymers,
absorption below 2 .mu.m is minimal. In practice, because of
vibrational overtones, most polymers are transmissive below 1 .mu.m
and highly absorptive above about 1.5 .mu.m. CO.sub.2 radiation
(10.6 .mu.m) is readily absorbed by most polymers in less than a
mm. Nd:YAG (1.06 .mu.m) will penetrate several mm into most
polymers while diode lasers (0.8 .mu.m nominal) will not be
absorbed by polymers unless IR absorbing dyes such as carbon
particles are added. Since there is some risk in degrading the
barrier properties of LCP or generating carbonization by adding
dyes or carbon powder, diode laser bonding is not an option.
[0079] For electronic and opto-electronic packaging, an embodiment
of the invention uses a laser as a means to bond an LCP cap to a
substrate such as silica, silicon or ceramic (See FIG. 5). The
ideal laser wavelength must be transmitted by the substrate and
strongly absorbed by the LCP, in a thickness of a fraction of a
millimeter. This allows laser delivery through the substrate to the
junction that needs to be bonded. Mechanical pressure is applied to
the bond region to ensure a viable bond. The LCP is sufficiently
thick, e.g. 1 mm, so that only the interface layer melts, and thus,
allows pressure to be applied to the unmelted layer of the LCP. To
further increase the localized pressure, a small ridge may
optionally be molded into the LCP cap, as shown in FIG. 6. The
laser energy is absorbed within the raised ridge, causing it to
melt and bond with the substrate.
[0080] To bond an LCP cap to a substrate, the LCP ridge needs to be
melted at all points. A scanning laser beam is employed (See FIG.
7) to accomplish this. The laser wavelength must be such that it is
absorbed strongly by polymers--hence it must be >1.5 .mu.m.
Thus, Nd:YAG is not an option. It must also be transmitted by
silicon, silica and ideally by ceramics such as sapphire. FIG. 7A
shows that silicon is essentially transmissive above about 1 .mu.m.
Silica, on the other hand, is transmissive in the wavelength range
from 0.2 .mu.m to 4 .mu.m as shown in FIG. 7B. Alumina (sapphire)
is transmissive from 0.15 .mu.m to 6.5 .mu.m. Hence, an ideal
wavelength for LCP bonding to all these substrates is in the range
from 1.5 .mu.m to 4 .mu.m.
[0081] An embodiment of the invention uses a thulium fiber laser
(wavelength: 1.8-2 .mu.m) or Er:YAG laser (wavelength: 2.94 .mu.m)
for laser bonding LCP to silicon, silica and sapphire. IPG
Photonics in Oxford, Mass., has developed thulium fiber lasers,
which operate in the wavelength range of 1.8 to 2.0 .mu.m range
with a maximum output power of 100 W. These are CW lasers. CW
lasers are typically better than pulsed lasers for polymer bonding
since high peak power of pulsed lasers may result in local burning
from impurities. Fiber lasers are ideally suited for beam delivery
in a laser bonding application. Erbium in YAG (Er:YAG) lasers which
operate at a wavelength of 2.94 .mu.m and 30 W power have been
developed primarily for dermatology applications. They are
manufactured by companies such as Lynton Lasers in England and
Unitech Corp in Japan. The wavelength is ideal for laser bonding
LCP to silicon, silica or sapphire. Note that Er:YAG is not to be
confused with Er in silica lasers and optical amplifiers (EDFA),
which nominally operate at a wavelength of 1.5 .mu.m.
[0082] Having discussed the structure and fabrication of optical
fiber cables having supplemental LCP and removable encasing layers
and their incorporation into a general form of hermetic package
using laser and/or ultrasonic bonding, more detailed embodiments of
packaging will now be discussed.
[0083] As indicated previously, the primary functions of packaging
are:
[0084] To prevent the ingress of corrosive elements such as water
vapor and oxygen.
[0085] To isolate the internal components from shock and
vibration.
[0086] To shield the component from potentially harmful
radiation.
[0087] To provide a means of conducting heat away from power
dissipating components, and
[0088] In the case of electro-optic devices, the packaging must
also provide a stable platform for the positioning and
interconnection of optical components, such as laser diodes,
modulators, input and output fibers, and the like.
[0089] A typical, well-known, packaged electro-optic device is
illustrated in FIG. 9A. This type of configuration, referred to as
a Butterfly package, is used extensively in the packaging of
electronic, electro-optic and micro electro mechanical systems
(MEMS). The casing of the package is metal, and serves as both a
barrier and a heat sink for the device, which is bonded to the
base. Electrical connections to the device are made via electrical
feedthroughs, which are sealed using glass beads, which are bonded
to both the casing and the electrical conductors. Such
glass-to-metal seals are used extensively in many types of
packaging.
[0090] For an electro-optic device, such as the one illustrated, it
is necessary to couple optical signals in and out of the device via
optical cables. Creating a hermetically sealed optical port is a
non trivial task, and typically involves metallizing the optical
fiber cable so that it can soldered into a metallized glass bead
which in turn is soldered into a small hole in the metal casing. To
metallize the fiber, the protective outer buffer coating must first
be removed, rendering the fiber very susceptible to moisture
degradation and breakage. Creating the sealed optical port is
therefore a very delicate, time consuming and expensive operation,
and is one of the major factors contributing to the very high cost
of packaging this type of component.
[0091] In accordance with a further aspect of the invention, the
metal housing, glass beads and metalized fibers are replaced with a
simplified, precision molded package, in which the necessary
integrity is achieved by bonding the LCP directly to various
components. In the case of the optical port, use is made of the LCP
coated optical fiber cable as previously described, which can be
thermally bonded directly into a housing after having had its
encasing layer removed.
Referring to FIG. 9B, there is shown an inventive package
designated generally at 200 comprising a metal substrate 202 to
which an actual device 204 is bonded. Substrate 202 serves
primarily as a thermal heat sink for device 204. For devices with
low power dissipation, the metal substrate is alternatively
replaced by LCP.
[0092] An LCP gasket 206 or shallow casing is bonded to the metal
substrate 202, with electrical feedthroughs 208 (typical) molded
in. One or more optical ports are made using an LCP ferrule 210
that is molded to the outside of an LCP supplemented fiber 212. The
ferrule 210 is designed so that it can be bonded to the LCP gasket
206 using ultrasonic bonding techniques to be described later.
Finally an LCP cap 214 is bonded on to the top of the gasket 206,
which may be accomplished using ultrasonic bonding.
[0093] A method of the invention for assembling an LCP housing can
be summarized in five major steps:
[0094] Bonding an LCP gasket or shallow casing to a metal substrate
or alternatively LCP substrate.
[0095] Producing hermetically sealed electrical feedthroughs.
[0096] Manufacturing supplemental LCP coated optical fiber cable
with removable encasing layers.
[0097] Producing hermetically sealed optical feedthroughs.
[0098] Ultrasonically welding and bonding the LCP cap to the LCP
gasket.
[0099] The first step in the packing process or method is to attach
an LCP gasket to a metal or LCP substrate. LCP films are routinely
bonded to thin copper laminates to produce flexible circuit boards,
and the strength of the bond between the LCP and the copper is
extremely high. However, in this particular situation, both
materials are very thin, and stresses due to thermal expansion
mismatch are relatively low. When more rigid and substantial
components are connected together, the problem of thermally induced
stresses becomes more significant, and it is probable that repeated
thermal cycling could result in a failure of the LCP/metal bond.
For this reason, the LCP gasket 206 is preferably attached to the
metal substrate 202 by "over-molding" using a mechanical keying
feature machined into the substrate 202. Over molding is a process
whereby a polymer material is injection molded in a cavity into
which the mating part (in this case, the substrate) has been
placed. Here, the substrate is machined to produce a small dovetail
shaped lip 216, over which the LCP is molded, as shown in detail in
FIG. 10. The shape of the lip 216 ensures that, as the two
materials expand and contract, the seal between them remains
tight.
[0100] As with the gasket to substrate seal, a major problem to
overcome with the electrical feedthroughs is that of preventing
bond failure as a result of stresses resulting from mismatched
expansion coefficients. As with the LCP to substrate seal, this
problem is overcome by molding the LCP directly over the electrical
output pins, and designing mechanical features into the latter,
such that the two components are essentially locked together.
[0101] An embodiment of the over-molded electrical feedthroughs is
shown in FIG. 11. Electrical pins 220 are manufactured either by
machining or stamping, and are mounted onto a lead frame for
insertion into the injection molding cavity. Ridges 222 (typical)
are preferably provided on the metal conductors to further ensure a
high integrity seal. Pedestals or ledge 224 are located underneath
electrode pads 226 for location and support purposes.
[0102] Another aspect of the invention comprises extensive
ultrasonic welding to bond various components together. Ultrasonic
bonding is a technique widely used in the manufacture of plastic
components. The materials to be welded must be thermoplastic. That
is, they must not change their chemical composition upon melting.
The process relies upon the use of high frequency sound waves to
create localized heating by friction. The heating softens the
thermoplastic material and causes the two parts to be fused
together. In the bonding process, the two parts to be welded are
held together under pressure and are then subjected to ultrasonic
vibrations usually at a frequency of 10 to 40 kHz.
[0103] The ability to weld a component successfully is governed by
the design of the equipment, the mechanical properties of the
material to be welded and the design of the components. In order to
ensure that heat is generated locally, at the joint between the two
parts, the components are designed with small features called
energy directors (See FIG. 13). These energy directors consist of
small (typically 0.1'') ridges with pointed tops, which serve to
focus ultrasonic energy into a relatively small volume of material,
causing rapid heating and subsequent melting.
[0104] A typical ultrasonic bonding system is illustrated generally
at 300 in FIG. 12. It consists of a transducer 302, booster 304,
horn 306 (or sonotrode) and anvil 308. The two parts to be welded
are sandwiched between the horn 306 and the anvil 308, which must
be relatively immoveable. Ultrasonic energy from the transducer 302
is amplified by the booster 304 and coupled to the horn 306, which
in turn transmits it to the upper of the two components (Shown
generally at 310).
[0105] The design of an embodiment of an LCP cap 400 in accordance
with the invention is shown in FIG. 14. An energy director 402 is
provided in LCP cap 400, and an ultrasonic welding horn 404 is
configured to operate in conjunction with the shape of the LCP cap
400.
[0106] While fundamental and novel features of the invention have
been shown and described with respect to preferred embodiments, it
will be understood that those skilled in the art may make various
changes to the described embodiments based on the teachings of the
invention and such changes are intended to be within the scope of
the invention as claimed.
* * * * *