U.S. patent application number 11/529839 was filed with the patent office on 2010-07-15 for propylene copolymers for adhesive applications.
Invention is credited to Chad E. Bernard, Patrick Brant, Peijun Jiang, David R. Johnsrud, Charles L. Sims.
Application Number | 20100179268 11/529839 |
Document ID | / |
Family ID | 37776894 |
Filed Date | 2010-07-15 |
United States Patent
Application |
20100179268 |
Kind Code |
A9 |
Jiang; Peijun ; et
al. |
July 15, 2010 |
Propylene copolymers for adhesive applications
Abstract
Disclosed herein are adhesives comprising a copolymer comprising
at least 80 wt % of units derived from propylene and from about 1
to about 20 wt % of units derived from at least one C.sub.6 to
C.sub.10 alpha-olefin. The copolymer has a molecular weight of less
than 100,000 and a heat of fusion between about 10 and about 70
J/g. An adhesive containing the copolymer preferably exhibits at
least 50% fiber tear at -18.degree. C. and at least 50% fiber tear
at +25.degree. C. using Inland paper board as a substrate; a
viscosity of less than 50,000 mPa sec at 190.degree. C., a set time
of less than 4 seconds and a toughness of at least 3.4
megajoule/m.sup.3.
Inventors: |
Jiang; Peijun; (League City,
TX) ; Brant; Patrick; (Seabrook, TX) ;
Bernard; Chad E.; (Baytowa, TX) ; Johnsrud; David
R.; (Humble, TX) ; Sims; Charles L.; (Houston,
TX) |
Correspondence
Address: |
EXXONMOBIL CHEMICAL COMPANY
5200 BAYWAY DRIVE, P.O. BOX 2149
BAYTOWN
TX
77522-2149
US
|
Prior
Publication: |
|
Document Identifier |
Publication Date |
|
US 20080081868 A1 |
|
|
US 20100029829 A9 |
February 4, 2010 |
|
|
Family ID: |
37776894 |
Appl. No.: |
11/529839 |
Filed: |
September 29, 2006 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10687508 |
Oct 15, 2003 |
7294681 |
|
|
11529839 |
|
|
|
|
10825380 |
Apr 15, 2004 |
7223822 |
|
|
10687508 |
|
|
|
|
10686951 |
Oct 15, 2003 |
7524910 |
|
|
10825380 |
|
|
|
|
10825635 |
Apr 15, 2004 |
7541402 |
|
|
10686951 |
|
|
|
|
10686951 |
Oct 15, 2003 |
7524910 |
|
|
10825635 |
|
|
|
|
10825349 |
Apr 15, 2004 |
7550528 |
|
|
10686951 |
|
|
|
|
10686951 |
Oct 15, 2003 |
7524910 |
|
|
10825349 |
|
|
|
|
10825348 |
Apr 15, 2004 |
7700707 |
|
|
10686951 |
|
|
|
|
10686951 |
Oct 15, 2003 |
7524910 |
|
|
10825348 |
|
|
|
|
60418482 |
Oct 15, 2002 |
|
|
|
60460714 |
Apr 4, 2003 |
|
|
|
60418482 |
Oct 15, 2002 |
|
|
|
60460714 |
Apr 4, 2003 |
|
|
|
60418482 |
Oct 15, 2002 |
|
|
|
60460714 |
Apr 4, 2003 |
|
|
|
60418482 |
Oct 15, 2002 |
|
|
|
60460714 |
Apr 4, 2003 |
|
|
|
60418482 |
Oct 15, 2002 |
|
|
|
60460714 |
Apr 4, 2003 |
|
|
|
Current U.S.
Class: |
524/487 ;
524/543; 525/70 |
Current CPC
Class: |
C09J 123/142 20130101;
C09J 123/142 20130101; C09J 123/142 20130101; C08L 2666/24
20130101; C08L 51/003 20130101; C08L 2666/24 20130101; C08L 91/06
20130101; C08L 91/06 20130101 |
Class at
Publication: |
524/487 ; 525/70;
524/543 |
International
Class: |
C08L 91/08 20060101
C08L091/08 |
Claims
1. An adhesive comprising a copolymer comprising at least 80 wt %
of units derived from propylene and from about 1 to about 20 wt %
of units derived from at least one C.sub.6 to C.sub.10
alpha-olefin, wherein the copolymer has a molecular weight of less
than 100,000 and a heat of fusion between about 10 and about 70 J/g
and wherein the adhesive has the following properties: (a) at least
50% fiber tear at -18.degree. C. using Inland paper board as a
substrate; (c) at least 50% fiber tear at 25.degree. C. using
Inland paper board as a substrate; (d) a viscosity of less than
50,000 mPa sec at 190.degree. C.; (e) a set time of less than 4
seconds; and (f) a toughness of at least 3.4 megajoule/m.sup.3.
2. The adhesive of claim 1 wherein the copolymer comprises about 2
wt % to about 15 wt % of units derived from said at least one
C.sub.6 to C.sub.10 alpha-olefin.
3. The adhesive of claim 1 wherein the copolymer comprises about 5
wt % to about 15 wt % of units derived from said at least one
C.sub.6 to C.sub.10 alpha-olefin.
4. The adhesive of claim 1 wherein the copolymer consists
essentially of units derived from propylene and said at least one
C.sub.6 to C.sub.10 alpha-olefin.
5. The adhesive of claim 1 wherein said alpha-olefin has 6 to 8
carbon atoms.
6. The adhesive of claim 1 wherein said alpha-olefin comprises
hexene-1.
7. The adhesive of claim 1 wherein said copolymer has a weight
averaged molecular weight of less than 80,000.
8. The adhesive of claim 1 wherein said copolymer has a weight
averaged molecular weight of less than 50,000.
9. The adhesive of claim 1 wherein said copolymer has a weight
averaged molecular weight of at least 10,000.
10. The adhesive of claim 1 wherein the ratio of the weight
averaged molecular weight of the copolyner to the number averaged
molecular weight of the copolyner is between about 4 and about
9.
11. The adhesive of claim 1 said copolymer has a heat of fusion
between about 10 and about 60 J/g.
12. The adhesive of claim 1 said copolymer has a heat of fusion
between about 20 and about 50 J/g.
13. The adhesive of claim 1 further comprising at least 80 wt % of
said copolymer and up to 20 wt % of at least one additive selected
from waxes and functionalized polyolefins.
14. The adhesive of claim 13 wherein said at least one additive
comprises a functionalized polyolefin and said functionalized
polyolefin comprises up to 15 wt % of the adhesive.
15. The adhesive of claim 14 wherein said functionalized polyolefin
comprises from 1 to 10 wt % of the adhesive.
16. The adhesive of claim 14 wherein said functionalized polyolefin
comprises maleated polypropylene.
17. The adhesive of claim 13 wherein said at least one additive
comprises a wax and said wax comprises up to 10 wt % of the
adhesive.
18. The adhesive of claim 17 wherein said wax comprises from 2 to 8
wt % of the adhesive.
19. The adhesive of claim 1 wherein said adhesive has a Shear
Adhesion Fail Temperature (SAFT) of at least 100.degree. C.
20. The adhesive of claim 1 wherein said adhesive has a Shear
Adhesion Fail Temperature (SAFT) of at least 110.degree. C.
21. The adhesive of claim 1 wherein said copolymer has a viscosity
at 190.degree. C. of less than 25,000 mPa sec.
22. The adhesive of claim 1 wherein said copolymer has a viscosity
at 190.degree. C. of greater than 10,000 mPa sec and the adhesive
has a toughness of at least 14 megajoule/m.sup.3 and an elongation
of at least 400%.
23. The adhesive of claim 1 wherein said copolymer has a viscosity
at 190.degree. C. of less than 10,000 mPa sec.
24. The adhesive of claim 1 wherein said copolymer has a viscosity
at 190.degree. C. in the range from 1000 to 10,000 mPa sec and the
adhesive has a toughness of at least 7 megajoule/m.sup.3 and an
elongation of at least 100%.
25. The adhesive of claim 1 wherein said adhesive has a viscosity
at 190.degree. C. of less than 5,000 mPa sec.
26. The adhesive of claim 1 wherein said adhesive has a viscosity
at 190.degree. C. of less than 1,000 mPa sec.
27. The adhesive of claim 1 wherein said adhesive has a set time of
less than 3 seconds.
28. The adhesive of claim 1 wherein said adhesive has a set time of
less than 2 seconds.
29. An adhesive comprising a copolymer comprising at least 80 wt %
of units derived from propylene and from about 1 to about 20 wt %
of units derived from at least one C.sub.6 to C.sub.10
alpha-olefin, wherein the copolymer has a molecular weight of less
than 50,000 and a heat of fusion between about 10 and about 70 J/g
and wherein the adhesive has a Dot T-Peel adhesion of 8 newton or
more for adhesion between a fiber board and a fabric substrate at
room temperature (25.degree. C.) and a Dot T-Peel adhesion of 8
newton or more for adhesion between two polyethylene terephthalate
(PET) films at room temperature (25.degree. C.) and at 40.degree.
C.
Description
BACKGROUND
[0001] One type of adhesive that finds extensive commercial
utility, particularly in packaging applications, is the hot-melt
adhesive, which is a material that can be heated to a melt and then
applied to various substrates such that a bond is formed upon
cooling and resolidification. A wide variety of thermoplastic
polymers, particularly ethylene-based polymers, such as
ethylene-vinyl acetate copolymers ("EVA") have been proposed for
use in hot-melt adhesives but often the adhesive formulation
requires substantial use of low molecular weight ingredients such
as wax and tackifier to adjust the viscosity and glass transition
temperature to useful ranges for hot melt adhesive applications.
Where the polymers have substantial crystallinity and hence a poor
compliance to substrates, this can significantly reduce their
potential for use in low temperature applications. On the contrary,
amorphous polymers often have poor cohesive strength and so require
the presence of large concentrations of high molecular weight
materials to improve cohesive strength but this leads to high melt
viscosity and poor processability. Also desirable in packaging is
to have adhesive compositions that exhibit a sufficiently long time
before hardening to preserve sufficient adhesion (known in industry
as "open time") in assembly operations such as box closures, yet a
quick enough setting speed to allow shortest time application of
adhering pressure (known in industry as "setting time").
[0002] Although many of the alpha-olefin copolymers currently used
in adhesive compositions are derived predominantly from ethylene
(see, for example, International Patent Publication Nos. WO98/03603
and WO99/24516), copolymers derived predominantly from propylene
have also been proposed for use in adhesive compositions. For
example, U.S. Pat. No. 3,954,697 discloses a single component,
hot-melt, pressure-sensitive adhesive based on propylene/higher
1-olefin copolymers containing 40-60 mole % of the higher 1-olefin.
Suitable comonomers include 1-hexene, 1-heptene, 1-octene, 1-nonene
and 1-decene. The copolymer has a melt viscosity range at
190.degree. C. of 10,000 cp to 75,000 cp, a density of 0.85 to
0.86, a glass transition temperature of -30 to -45.degree. C., and
has no melting point measurable by Differential Scanning
Calorimetry. Thus the copolymer is amorphous with no residual
crystallinity or crystallinity of a very low order. The copolymer
is produced using a Ziegler-Natta catalyst. It is to be appreciated
that a hot melt pressure sensitive adhesive (HMPSA) is an adhesive
that is applied hot to a substrate to form an article, such as a
tape or label, which is subsequently used at ambient temperature to
initiate adhesion.
[0003] U.S. Pat. No. 6,627,723 discloses a poly-alpha olefin
copolymer comprising (a) from 60 to 94 mol % of units derived from
one alpha mono-olefin having from 3 to 6 carbon atoms, preferably
propylene; (b) from 6 to 40 mol % of units derived from one or more
other mono-olefins having from 4 to 10 carbon atoms and at least
one carbon atom more than (a), preferably butene-1, hexene-1 or
octene-1; and (c) optionally from 0 to 10 mol % of units derived
from another copolymerizable unsaturated hydrocarbon, different
from (a) and (b), preferably ethylene; wherein the diad
distribution of component A in the inter-polymer as determined by
.sup.13C NMR divided by the calculated Bernoullian diad
distribution is less than 1.07; and wherein the storage modulus G'
of the copolymer determined on cooling, measured at 1 Hz,
intersects 3.times.10.sup.5 Pa at an intersection temperature of
less than 85.degree. C. The copolymer is produced by copolymerizing
the monomers in the presence of a single site metallocene catalyst,
preferably a bridged chiral bis-indenyl metallocene catalyst. The
copolymer is largely amorphous and is said to be useful as a hot
melt adhesive, both with and without the addition of tackifying
resins.
[0004] U.S. Pat. No. 6,747,114 discloses an adhesive composition
comprising a semi-crystalline copolymer of propylene and at least
one comonomer selected ethylene and C.sub.4 to C.sub.20
.alpha.-olefins having a propylene content of greater than 65 mole
percent; wherein the copolymer has a weight average molecular
weight (Mw) from about 15,000 to about 200,000; a melt index (MI)
from about 7 dg/min to about 3000 dg/min as measured by ASTM D
1238(B); and a weight average molecular weight/number average
molecular weight ratio (Mw/Mn) of approximately 2. In Example 4,
propylene is copolymerized with between 11 and 19 wt % 1-hexene at
a temperature of 76.degree. C. to 90.degree. C. over a catalyst
comprising
dimethylsilandiylbis(2-methyl-4-phenyl-1-indenyl)zirconium dimethyl
activated with dimethylanilinium-tetrakis(pentafluorophenyl)borate
to produce semi-crystalline copolymers having a melting
temperature, T.sub.m, between 93.degree. C. and 107.degree. C., a
heat of fusion, .DELTA.H, between 58.5 and 96.6 J/g and a melt
viscosity at 190.degree. C. of between 2230 and 66,000 cps.
Pressure sensitive hot melt adhesives are formed by blending 30 wt
% of each copolymer with 50 wt % of Escorez.RTM. 5380 tackifier and
20 wt % of Kaydol Oil and the resulting adhesives exhibit a tensile
strength in excess of 127 psi, an elongation in excess of 368% and
a Shear Adhesion Failure Temperature (SAFT) to Kraft paper of
74.degree. C. to 83.degree. C. In addition, for the copolymer
formed from 19 wt % 1-hexene, a hot melt adhesive is formed by
blending 80 wt % of the copolymer with 15 wt % of Escorez.RTM. 5380
tackifier and 5 wt % of Kaydol Oil. The resulting adhesive exhibits
a tensile strength of 1452 psi, an elongation of 768% and a Shear
Adhesion Failure Temperature (SAFT) to Kraft paper of 102.5.degree.
C. All of the adhesives formed had at least 20% of the other
ingredients due to the high molecular weight of the starting
copolymers, and had a long set time.
[0005] International Patent Publication No. WO 2004/046214,
published Jun. 3, 2004, discloses a polyolefin adhesive comprising
a polymer having a Dot T-Peel of 1 N or more on Kraft paper, an Mw
of 10,000 to 100,000, a branching index (g') of 0.95 or less
measured at the Mz of the polymer and a heat of fusion of 1 to 70
J/g, wherein the polymer comprises 50 weight % or more of an
alpha-olefin having 3 to 30 carbon atoms, and optionally up to 50
weight % of a comonomer selected from the group consisting of
ethylene, butene, hexene, octene, decene, dodecene, pentene,
heptene, nonene, 4-methyl-pentene-1,3-methyl pentene-1,
3,5,5-trimethyl-hexene-1, and 5-ethyl-1-nonene, and up to 10 weight
% of a diene. The polymer is preferably produced using a mixed
catalyst system comprising a first transition metal compound
capable of producing a crystalline poly-alpha-olefin, preferably
isotactic or syndiotactic polypropylene, having a crystallinity of
20% or more, and a second transition metal compound capable of
producing an amorphous poly-alpha-olefin, preferably atactic
polypropylene, having a crystallinity of 5% or less.
[0006] In particular, Example 71 of WO 2004/046214 discloses the
production of a copolymer of propylene, hexene and 1,9-decadiene by
feeding propylene (14 g/minute or 81 wt %), hexene (3.29 ml/minute
or 15.8 wt %) and 1,9-decadiene (0.206 ml/min) to a liquid filled,
single-stage continuous reactor using a mixed metallocene solution
catalyst system comprising dimethylsilylbis
(2-methyl-4-phenylindenyl)zirconium dimethyl and
dimethylsilyl-(tetramethylcyclopentadienyl) (cyclododecylamido)
titanium dimethyl at a temperature of 115.degree. C. The product,
comprising both amorphous and semi-crystalline propylene
copolymers, had a Tm of 89.8.degree. C., a Tc of 42.6.degree. C., a
glass transition temperature, Tg, of -15.2.degree. C., a heat of
fusion of 27.0 J/g and a viscosity of 524 cp at 190.degree. C. and,
when used as an adhesive without additives, exhibited a set time of
3.5 seconds and 80% fiber tear at 20-25.degree. C. using a file
folder as a substrate. When formulated with 2 wt % of Escorez.RTM.
5637 tackifier and 5 wt % of Paraflint H1 wax, the copolymer of
Example 71 provided an adhesive with a set time of 2 seconds and
90% fiber tear at 20-25.degree. C. on a file folder substrate.
However, the formulated adhesive would have no fiber tear and poor
adhesion at low temperature (-18.degree. C.) on difficult
substrates such as Inland paper board.
[0007] As illustrated by the prior art cited above, the copolymers
derived from either ethylene or propylene currently used in hot
melt adhesives are of high molecular weight. However, high
molecular weight copolymers exhibit poor processability and require
high concentrations (>20%) of other low molecular weight
additives, such as wax and tackifier, to reduce the adhesive
viscosity to the applicable range as well as to improve other
adhesive properties. It would therefore be desirable to develop
adhesives using low molecular weight copolymers having the desired
end-use viscosity. However, low molecular weight polymers often
have poor cohesive strength. There is therefore a need for
copolymers which exhibit low viscosity together with a combination
of good adhesion at low and high temperatures and acceptable
mechanical strength.
[0008] Certain novel propylene copolymers have been produced that,
when combined with small quantities of wax and/or a functionalized
polyolefin, exhibit an excellent balance of adhesive properties,
including a good low temperature (-18.degree. C.) adhesion
performance, short set time and a high toughness at relatively low
application viscosity.
SUMMARY
[0009] Accordingly, disclosed herein is an adhesive comprising a
copolymer comprising at least 80 wt % of units derived from
propylene and from about 1 to about 20 wt % of units derived from
at least one C.sub.6 to C.sub.10 alpha-olefin, wherein the
copolymer has a molecular weight of less than 100,000 and a heat of
fusion between about 10 and about 70 J/g and wherein the adhesive
has the following properties: [0010] (a) at least 50% fiber tear at
-18.degree. C. using Inland paper board as a substrate; [0011] (b)
at least 50% fiber tear at 25.degree. C. using Inland paper board
as a substrate; [0012] (c) a viscosity of less than 50,000 mPa sec
at 190.degree. C.; [0013] (d) a set time of less than 4 seconds;
and [0014] (e) a toughness of at least 3.4 megajoule/m.sup.3.
[0015] Preferably, the copolymer comprises about 2 wt % to about 15
wt %, more preferably about 2 wt % to about 12 wt %, of units
derived from said at least one C.sub.6 to C.sub.10
alpha-olefin.
[0016] Preferably, said at least one alpha-olefin has 6 to 8 carbon
atoms and more preferably comprises hexene-1.
[0017] Preferably, said copolymer has a molecular weight of less
than 80,000, such as less than 50,000.
[0018] Preferably, said copolymer has a heat of fusion between
about 10 and about 60 J/g, such as between about 20 and about 50
J/g.
[0019] Preferably, said copolymer has an Mw/Mn of between 4 and
9.
[0020] Preferably, said adhesive is a hot melt adhesive.
[0021] Preferably, said adhesive comprises at least 80 wt % of said
copolymer and up to 20 wt % of at least one additive selected from
waxes and functionalized polyolefins. In one embodiment, said at
least one additive comprises a functionalized polyolefin and said
functionalized polyolefin comprises up to 15 wt %, for example from
1 to 10 wt %, of the adhesive. In another embodiment, said at least
one additive comprises a wax and said wax comprises up to 10 wt %,
for example from 2 to 8 wt %, of the adhesive.
[0022] Preferably, said adhesive has a Shear Adhesion Fail
Temperature (SAFT) of at least 100.degree. C.
[0023] Preferably, said adhesive has a viscosity of less than
25,000 mPa sec, such as less than 10,000 mPa sec, for example less
than 5,000 mPa sec, typically less than 1,000 mPa sec at
190.degree. C.
[0024] Preferably, said adhesive has a toughness of at least 3.4
megajoule/m.sup.3 when the viscosity at 190.degree. C. is less than
1000 mPa sec; a toughness of at least 7 megajoule/m.sup.3 and an
elongation of at least 100% when viscosity at 190.degree. C. is in
a range from 1000 to 10,000 mPa sec; and a toughness greater than
14 megajoule/m.sup.3 and an elongation of at least 400% when the
viscosity at 190.degree. C. is greater than 10,000 mPa sec.
[0025] Preferably, said adhesive has a set time of less than 3
seconds, typically less than 2 seconds.
[0026] In other embodiments, the adhesive has a Dot T-Peel adhesion
of at least 8 newton for adhesion between a fiber board and a
fabric substrate at room temperature and a Dot T-Peel adhesion of
at least 8 newton for adhesion between two polyethylene
terephthalate (PET) films at room temperature (25.degree. C.) and
at 40.degree. C.
DETAILED DESCRIPTION
[0027] For purposes of disclosure when a polymer or oligomer is
referred to as comprising an olefin, the olefin present in the
polymer or oligomer is the polymerized or oligomerized form of the
olefin, respectively. Likewise, the use of the term "polymer" is
meant to encompass homopolymers and copolymers. The term
"copolymer" is used herein to include any polymer having two or
more monomers. That is, in the case of a propylene copolymer, at
least one other comonomer is polymerized with the propylene to make
the copolymer.
[0028] Disclosed herein is a copolymer of propylene with at least
one C.sub.6 to C.sub.10 alpha-olefin, wherein the copolymer has a
molecular weight of less than 100,000 and a heat of fusion between
about 10 and about 70 J/g. When used as an adhesive, and in
particular as a hot melt adhesive, the present copolymer exhibits a
novel and advantageous combination of properties including at least
50% fiber tear at -18.degree. C. and at least 50% fiber tear at
25.degree. C. using Inland paper board as a substrate, a viscosity
of less than 50,000 mPa sec at 190.degree. C., a set time of less
than 4 seconds and improved mechanical properties such as a
toughness of at least 3.4 megajoule/m.sup.3 or more when the
viscosity at 190.degree. C. is less than 1000 mPa sec; a toughness
of 7 megajoule/m.sup.3 or more and an elongation of 100% or more
when viscosity at 190.degree. C. is in a range from 1000 to 10,000
mPa sec; and a toughness greater than 14 megajoule/m.sup.3 and an
elongation of 400% or more when the viscosity at 190.degree. C. is
greater than 10,000 mPa sec.
Copolymer
[0029] The presently disclosed copolymer comprises at least 80%,
preferably at least 85% by weight of units derived from propylene.
Generally, the maximum concentration of propylene-derived units in
the copolymer is 98%, preferably 95%, more preferably 90% by weight
of the copolymer. In addition to propylene-derived units, the
present copolymer contains from 1 to 20% by weight, preferably from
about 2% to about 15% by weight, more preferably about 2% to about
12% by weight, and most preferably about 2% to about 10% by weight
of units derived from at least one C.sub.6 to C.sub.10
alpha-olefin. In one preferred embodiment, the copolymer comprises
about 90 wt % of propylene-derived units and about 10 wt % of units
derived from said at least one C.sub.6 to C.sub.10
alpha-olefin.
[0030] Preferred C.sub.6 to C.sub.10 alpha-olefins are those having
6 to 8 carbon atoms, with the most preferred alpha-olefin being
hexene-1.
[0031] The copolymer can contain small amounts, generally less than
10% by weight of units derived from other comonomers, such as
ethylene, C.sub.4 and C.sub.5 alpha-olefins and C.sub.11 to
C.sub.20 alpha-olefins, but preferably the copolymer consists
essentially of units derived from propylene and one or more C.sub.6
to C.sub.10 alpha-olefins. In particular, the copolymer is
preferably free of diolefins.
[0032] The present copolymer has a heat of fusion as determined by
differential scanning calorimetry (DSC) between about 10 and about
70 J/g, for example between about 10 and about 60 J/g, such as
about 20 and about 50 J/g, such as between about 20 and about 40
J/g. The copolymer typically has a melting point of less than
130.degree. C., or preferably less than 120.degree. C. This melting
point is due to crystallizable propylene sequences, preferably of
isotactic polypropylene. The semi-crystalline copolymer has
stereoregular propylene sequences long enough to crystallize,
preferably predominately isotactic polypropylene. The length and
distribution of stereoregular propylene sequences is consistent
with the substantially random statistical copolymerization. It is
well known that sequence length and distribution are related to the
copolymerization reactivity ratios. By substantially random, we
mean copolymer for which the product of the reactivity ratios is 2
or less. In stereoblock structures, the average length of
polypropylene sequences is greater than that of substantially
random copolymers with a similar composition. Prior art polymers
with stereoblock structure have a distribution of polypropylene
sequences consistent with these blocky structures rather than a
random substantially statistical distribution. The reactivity
ratios and sequence distribution of the polymer can be determined
by C-13 NMR which locates the comonomer residues in relation to the
neighboring propylene residues. This is according to the procedures
described in the article by H. Kakugo, Y Naito, K. Mizunama and T.
Miyatake in Macromolecules (1982), pages 1150-1152.
[0033] The weight averaged molecular weight (Mw) of the copolymer
is preferably less than 100,000 and typically less than 80,000,
such as less than 50,000. In general, the weight averaged molecular
weight of the copolymer is at least 5,000, such as at least 10,000.
Typically, the ratio of the weight averaged molecular weight (Mw)
of the copolymer to the number averaged molecular weight (Mn) of
the copolymer is between 4 and 9, such as between 5 and 7.
Generally, the semi-crystalline copolymer has a viscosity of less
than 50,000 mPa sec, for example less than 25,000 mPa sec, such as
less than 10,000 mPa sec, for example less than 5,000 mPa sec,
typically less than 1,000 mPa sec measured at 190.degree. C. using
a Brookfield viscometer.
Process for Producing the Copolymer
[0034] Propylene copolymers described herein may be produced in any
known polymerization process. Polymerization methods include high
pressure, slurry, gas, bulk, suspension, supercritical, or solution
phase, or a combination thereof, using a single-site metallocene
catalyst system. The catalysts can be in the form of a homogeneous
solution, supported, or a combination thereof. Polymerization may
be carried out by a continuous, a semi-continuous or batch process
and may include use of chain transfer agents, scavengers, or other
such additives as deemed applicable. By continuous is meant a
system that operates (or is intended to operate) without
interruption or cessation. For example a continuous process to
produce a polymer would be one where the reactants are continually
introduced into one or more reactors and polymer product is
continually withdrawn. In general, the propylene copolymer
described herein is produced in a single polymerization zone using
a single polymerization catalyst.
[0035] Preferably the copolymer is made with a polymerization
catalyst which forms essentially or substantially isotactic
propylene sequences. Nonetheless, the polymerization catalyst used
for the production of the propylene copolymer will introduce
stereo- and regio-errors in the incorporation of propylene. Stereo
errors are those where the propylene inserts in the chain with a
tacticity that is not isotactic. A regio error is one where the
propylene inserts with the methylene group or the methyldiene group
adjacent to a similar group in the propylene inserted immediately
prior to it. Such errors are more prevalent after the introduction
of comonomer such as 1-hexene in the semi-crystalline propylene
copolymer. Notwithstanding the presence of these errors, the
semi-crystalline propylene copolymer is statistically random in the
distribution of comonomer.
[0036] Preferably the semi-crystalline propylene copolymer is made
with a single site metallocene catalyst which allows only a single
statistical mode of addition of propylene and comonomer in a
well-mixed, continuous monomer feed stirred tank polymerization
reactor and which allows only a single polymerization environment
for all of the polymer chains of the semi-crystalline propylene
copolymer.
[0037] Suitable single site metallocene catalysts for use herein
include those obeying the following general formula (1):
##STR00001##
wherein M is a Group 3, 4, 5 or 6 transition metal atom, or a
lanthanide metal atom, or actinide metal atom, preferably a Group 4
transition metal atom selected from titanium, zirconium or hafnium;
each cyclopentadienyl (Cp) ring is substituted with from zero to
four substituent groups S, each substituent group S being,
independently, a hydrocarbyl, substituted-hydrocarbyl, halocarbyl,
substituted-halocarbyl, hydrocarbyl-substituted organometalloid,
halocarbyl-substituted organometalloid, disubstituted boron,
disubstituted pnictogen, substituted chalcogen or halogen radical,
provided that two adjacent S groups may joined to form a C.sub.4 to
C.sub.20 ring to give a saturated or unsaturated polycyclic ligand;
the subscript "v" denotes the carbon atom on the Cp-ring to which
the substituent is bonded; A is a bridging group; and X.sub.1 and
X.sub.2 are, independently, hydride radicals, hydrocarbyl radicals,
substituted hydrocarbyl radicals, halocarbyl radicals, substituted
halocarbyl radicals, and hydrocarbyl- and halocarbyl-substituted
organometalloid radicals, substituted pnictogen radicals, or
substituted chalcogen radicals; or X.sub.1 and X.sub.2 are joined
and bound to the metal atom to form a metallacycle ring containing
from about 3 to about 20 carbon atoms; or X.sub.1 and X.sub.2
together can be an olefin, diolefin or aryne ligand; or when
Lewis-acid activators, such as methylalumoxane, which are capable
of donating an X.sub.1 ligand as described above to the transition
metal component are used, X.sub.1 and X.sub.2 may independently be
a halogen, alkoxide, aryloxide, amide, phosphide or other univalent
anionic ligand or both X.sub.1 and X.sub.2 can also be joined to
form a anionic chelating ligand and with the proviso that X.sub.1
and X.sub.2 are not a substituted or unsubstituted cyclopentadienyl
ring.
[0038] Preferably, A is a bridging group containing boron or a
Group 14, 15 or 16 element. Examples of suitable bridging groups
include R'.sub.2C, R'.sub.2Si, R'.sub.2Ge, R'.sub.2CCR'.sub.2,
R'.sub.2CCR'.sub.2CR'.sub.2, R'.sub.2CCR'.sub.2CR'.sub.2CR'.sub.2,
R'C.dbd.CR', R'C.dbd.CR'CR'.sub.2, R'.sub.2CCR'.dbd.CR'CR'.sub.2,
R'C.dbd.CR'CR'.dbd.CR', R'C.dbd.CR'CR'.sub.2CR'.sub.2,
R'.sub.2CSiR'.sub.2, R'.sub.2SiSiR'.sub.2,
R'.sub.2CSiR'.sub.2CR'.sub.2, R'.sub.2SiCR'.sub.2SiR'.sub.2,
R'C.dbd.CR'SiR'.sub.2, R'.sub.2CGeR'.sub.2, R'.sub.2GeGeR'.sub.2,
R'.sub.2CGeR'.sub.2CR'.sub.2, R'.sub.2GeCR'.sub.2GeR'.sub.2,
R'.sub.2SiGeR'.sub.2, R'C.dbd.CR'GeR'.sub.2, R'B, R'.sub.2C--BR',
R'.sub.2C--BR'--CR'.sub.2, R'N, R'P, O, S, Se,
R'.sub.2C--O--CR'.sub.2, R'.sub.2CR'.sub.2C--O--CR'.sub.2CR'.sub.2,
R'.sub.2C--O--CR'.sub.2CR'.sub.2, R'.sub.2C--O--CR'.dbd.CR',
R'.sub.2C--S--CR'.sub.2, R'.sub.2CR'.sub.2C--S--CR'.sub.2CR'.sub.2,
R'.sub.2C--S--CR'.sub.2CR'.sub.2, R'.sub.2C--S--CR'.dbd.CR',
R'.sub.2C--Se--CR'.sub.2,
R'.sub.2CR'.sub.2C--Se--CR'.sub.2CR'.sub.2,
R'.sub.2C--Se--CR'.sub.2CR'.sub.2, R'.sub.2C--Se--CR'.dbd.CR',
R'.sub.2C--N.dbd.CR', R'.sub.2C--NR'--CR'.sub.2,
R'.sub.2C--NR'--CR'.sub.2CR'.sub.2, R'.sub.2C--NR'--CR'.dbd.CR',
R'.sub.2CR'.sub.2C--NR'--CR'.sub.2CR'.sub.2, R'.sub.2C--P.dbd.CR',
and R'.sub.2C--PR'--CR'.sub.2 where R' is hydrogen or a
C.sub.1-C.sub.20 containing hydrocarbyl, substituted hydrocarbyl,
halocarbyl, substituted halocarbyl, silylcarbyl or germylcarbyl
substituent and optionally two or more adjacent R' may join to form
a substituted or unsubstituted, saturated, partially unsaturated or
aromatic, cyclic or polycyclic substituent. Preferred examples for
the bridging group Y include CH.sub.2, CH.sub.2CH.sub.2,
CH(CH.sub.3).sub.2, O, S, SiMe.sub.2, SiPh.sub.2, SiMePh,
Si(CH.sub.2).sub.3 and Si(CH.sub.2).sub.4.
[0039] Preferably transition metal compounds for producing
poly-alpha-olefins having enhanced isotactic character are those of
formula 1 where S are independently chosen such that the
metallocene framework 1) has no plane of symmetry containing the
metal center, and 2) has a C.sub.2-axis of symmetry through the
metal center. These complexes, such as
rac-Me.sub.2Si(indenyl).sub.2ZrMe.sub.2 and
rac-Me.sub.2Si(indenyl).sub.2HfMe.sub.2, are well known in the art
and generally produce isotactic polymers with higher degrees of
stereoregularity than the less symmetric chiral systems. Likewise
another preferred class of transition metal compounds that can
produce isotactic polymers useful in this invention are those
monocyclopentadienyl catalysts disclosed in U.S. Pat. No.
5,026,798, which is incorporated by reference herein. A detailed
description of suitable catalyst compounds and catalyst selections
may be found in U.S. Published Patent Application No. 2004/0217614,
published Jul. 1, 2004 which is incorporated by reference
herein.
[0040] Similarly, transition metal compounds providing tacticity
control exist where the S substituents of sufficient steric bulk to
restrict rotation of the cyclopentadienyl ligands such that the
aforementioned symmetry conditions are satisfied. Preferable chiral
racemic metallocenes of this type include
bis(tricyclo[5.2.1.0.sup.2,6]deca-2,5-dienyl)zirconium and hafnium
dimethyl,
bis((1R)-9,9-dimethyltricyclo[6.1.1.0.sup.2,6]deca-2,5-dienyl)z-
irconium dimethyl,
bis(tricyclo[5.2.1.0.sup.2,6]deca-2,5,8-trienyl)zirconium dimethyl,
bis(tricyclo[5.2.2.0.sup.2,6]undeca-2,5,8-trienyl)zirconium and
hafnium dimethyl and
bis((1R,8R)-7,7,9,9-tetramethyl[6.1.1.0.sup.2,6]deca-2,5-dienyl)zirconium
and hafnium dimethyl.
[0041] Preferably transition metal compounds for the production of
poly-alpha-olefins having enhanced syndiotactic character are also
those of formula 1 where S are independently chosen such that the
Cp ligands have substantially different steric bulk. In order to
produce a syndiotactic polymer the pattern of the groups
substituted on the Cp-rings is important. Thus, by steric
difference or sterically different as used herein, it is intended
to imply a difference between the steric characteristics of the A
and E ligands that renders each to be symmetrical with respect to
the Y bridging group but different with respect to each other
thereby controlling the approach of each successive monomer unit
that is added to the polymer chain. The steric difference between
the A and E ligands act to block the approaching monomer from a
random approach such that the monomer is added to the polymer chain
in the syndiotactic configuration.
[0042] Preferable transition metal compounds for the production of
syndiotactic polymers are those of formula 1 where S are
independently chosen such that 1) the steric difference between the
A and E ligands is maximized and 2) there remains a plane of
symmetry through the metal center and the C.sub.1 and C.sub.1'
carbon atoms of the Cp-rings in formula 1. Thus, complexes such as
Me.sub.2C(.eta..sup.5-C.sub.5H.sub.4)(1-fluorenyl)MMe.sub.2 (where
M=Ti, Zr, or Hf) which possess this symmetry are preferred, and
generally produce the syndiotactic polymer with higher degrees of
stereoregularity than similar, but less symmetric, systems.
Additionally, in the above equation, 1-fluorenyl may be substituted
with 3,8-di-t-butylfluorenyl, octahydrofluorenyl or
3,3,6,6,9,9,12,12-octamethyl-4,4,5,5,10,10,11,11-octahydrodibenzo[b,h]flu-
orene. Because pre-catalysts of this type often lose there ability
to control the stereoregularity of the polymer under high
temperature reaction conditions, to insure higher crystallinity in
the material requires using these catalysts at lower reactor
temperatures, preferably at temperatures below 80.degree. C.
[0043] Particularly preferred transition metal compounds for
producing crystalline poly-alpha-olefins are racemic metallocenes,
such as rac-dimethylsiladiyl(2-isopropyl,4-phenylindenyl).sub.2
zirconium dichloride;
rac-dimethylsiladiyl(2-isopropyl,4-[1-naphthyl]indenyl).sub.2
zirconium dichloride;
rac-dimethylsiladiyl(2-isopropyl,4-[3,5-dimethylphenyl]indenyl).sub.2
zirconium dichloride;
rac-dimethylsiladiyl(2-isopropyl,4-[ortho-methyl-phenyl]indenyl).sub.2
zirconium dichloride; rac-dimethylsilyl bis-(2-methyl,
4-phenylindenyl)zirconium dichoride, rac dimethylsiladlyl
bis-(2-methyl, 4-napthylindenyl)zirconium dichloride, rac-dimethyl
siladiyl(2-isopropyl, 4-[3,5 di-t-butyl-phenyl]indenyl).sub.2
zirconium dichloride; rac-dimethyl siladiyl(2-isopropyl,
4-[orthophenyl-phenyl]indenyl).sub.2 zirconium dichloride,
rac-diphenylsiladiyl(2-methyl-4-[1-naphthyl]indenyl).sub.2
zirconium dichloride and rac-biphenyl siladiyl(2-isopropyl, 4-[3,5
di-t-butyl-phenyl]indenyl).sub.2 zirconium dichloride. Alkylated
variants of these metallocenes (e.g. di-methyl instead of
dichloride) are also contemplated, dictated by the choice of
catalyst activation system. These and other metallocene
compositions are described in detail in U.S. Pat. Nos. 6,376,407,
6,376,408, 6,376,409, 6,376,410, 6,376,411, 6,376,412, 6,376,413,
6,376,627, 6,380,120, 6,380,121, 6,380,122, 6,380,123, 6,380,124,
6,380,330, 6,380,331, 6,380,334, 6,399,723 and 6,825,372.
[0044] The transition metal compounds described above are typically
activated in various ways to yield compounds having a vacant
coordination site that will coordinate, insert, and polymerize
olefin(s). For the purposes of this patent specification and
appended claims, the terms "cocatalyst" and "activator" are used
herein interchangeably and are defined to be any compound which can
activate any one of the catalyst compounds described above by
converting the neutral catalyst compound to a catalytically active
catalyst compound cation. Non-limiting activators, for example,
include alumoxanes, aluminum alkyls, ionizing activators, which may
be neutral or ionic, and conventional-type cocatalysts. Preferred
activators typically include alumoxane compounds, modified
alumoxane compounds, and ionizing anion precursor compounds that
abstract one reactive, .sigma.-bound, metal ligand making the metal
complex cationic and providing a charge-balancing noncoordinating
or weakly coordinating anion.
[0045] Alumoxanes are generally oligomeric compounds containing
--Al(R.sup.1)--O-- sub-units, where R.sup.1 is an alkyl group.
Examples of alumoxanes include methylalumoxane (MAO), modified
methylalumoxane (MMAO), ethylalumoxane and isobutylalumoxane.
Alkylalumoxanes and modified alkylalumoxanes are suitable as
catalyst activators, particularly when the abstractable ligand is a
halide, alkoxide or amide. Mixtures of different alumoxanes and
modified alumoxanes may also be used.
[0046] Alumoxanes may be produced by the hydrolysis of the
respective trialkylaluminum compound. MMAO may be produced by the
hydrolysis of trimethylaluminum and a higher trialkylaluminum such
as tri-iso-butylaluminum. MMAO's are generally more soluble in
aliphatic solvents and more stable during storage. There are a
variety of methods for preparing alumoxane and modified alumoxanes,
non-limiting examples of which are described in U.S. Pat. Nos.
4,665,208, 4,952,540, 5,091,352, 5,206,199, 5,204,419, 4,874,734,
4,924,018, 4,908,463, 4,968,827, 5,308,815, 5,329,032, 5,248,801,
5,235,081, 5,157,137, 5,103,031, 5,391,793, 5,391,529, 5,693,838,
5,731,253, 5,731,451, 5,744,656, 5,847,177, 5,854,166, 5,856,256
and 5,939,346 and European publications EP-A-0 561 476, EP-B-0 279
586, EP-A-0 594-218 and EP-B1-0 586 665, and PCT Publication Nos.
WO 94/10180 and WO 99/15534, all of which are herein fully
incorporated by reference. It may be preferable to use a visually
clear methylalumoxane. A cloudy or gelled alumoxane can be filtered
to produce a clear solution or clear alumoxane can be decanted from
the cloudy solution. Another alumoxane is a modified methyl
alumoxane (MMAO) cocatalyst type 3A (commercially available from
Akzo Chemicals, Inc. under the trade name Modified Methylalumoxane
type 3A, and disclosed in U.S. Pat. No. 5,041,584).
[0047] In addition or in place of alumoxanes, the transition metal
compounds described herein can be activated ionizing or
stoichiometric activator, neutral or ionic, such as tri (n-butyl)
ammonium tetrakis (pentafluorophenyl) boron, a trisperfluorophenyl
boron metalloid precursor or a trisperfluoronaphtyl boron metalloid
precursor, polyhalogenated heteroborane anions (WO 98/43983), boric
acid (U.S. Pat. No. 5,942,459) or combination thereof.
[0048] Examples of neutral stoichiometric activators include
tri-substituted boron, tellurium, aluminum, gallium and indium or
mixtures thereof. The three substituent groups are each
independently selected from alkyls, alkenyls, halogen, substituted
alkyls, aryls, arylhalides, alkoxy and halides. Preferably, the
three groups are independently selected from halogen, mono or
multicyclic (including halosubstituted) aryls, alkyls, and alkenyl
compounds and mixtures thereof, preferred are alkenyl groups having
1 to 20 carbon atoms, alkyl groups having 1 to 20 carbon atoms,
alkoxy groups having 1 to 20 carbon atoms and aryl groups having 3
to 20 carbon atoms (including substituted aryls). More preferably,
the three groups are alkyls having 1 to 4 carbon groups, phenyl,
napthyl or mixtures thereof. Even more preferably, the three groups
are halogenated, preferably fluorinated, aryl groups. Most
preferably, the neutral stoichiometric activator is
trisperfluorophenyl boron or trisperfluoronapthyl boron.
[0049] Examples of neutral stoichiometric activators include
tri-substituted boron, tellurium, aluminum, gallium and indium or
mixtures thereof. The three substituent groups are each
independently selected from alkyls, alkenyls, halogen, substituted
alkyls, aryls, arylhalides, alkoxy and halides. Preferably, the
three groups are independently selected from halogen, mono or
multicyclic (including halosubstituted) aryls, alkyls, and alkenyl
compounds and mixtures thereof, preferred are alkenyl groups having
1 to 20 carbon atoms, alkyl groups having 1 to 20 carbon atoms,
alkoxy groups having 1 to 20 carbon atoms and aryl groups having 3
to 20 carbon atoms (including substituted aryls). More preferably,
the three groups are alkyls having 1 to 4 carbon groups, phenyl,
napthyl or mixtures thereof. Even more preferably, the three groups
are halogenated, preferably fluorinated, aryl groups. Most
preferably, the neutral stoichiometric activator is
trisperfluorophenyl boron or trisperfluoronapthyl boron.
[0050] Ionic stoichiometric activator compounds may contain an
active proton, or some other cation associated with, but not
coordinated to, or only loosely coordinated to, the remaining ion
of the ionizing compound. Such compounds and the like are described
in European publications EP-A-0 570 982, EP-A-0 520 732, EP-A-0 495
375, EP-B1-0 500 944, EP-A-0 277 003 and EP-A-0 277 004, and U.S.
Pat. Nos. 5,153,157, 5,198,401, 5,066,741, 5,206,197, 5,241,025,
5,384,299 and 5,502,124, all of which are herein fully incorporated
by reference. Ionic catalysts can be prepared by reacting a
transition metal compound with a neutral Lewis acid, such as
B(C.sub.6F.sub.6).sub.3, which upon reaction with the hydrolyzable
ligand (X) of the transition metal compound forms an anion, such as
([B(C.sub.6F.sub.5).sub.3(X)].sup.-), which stabilizes the cationic
transition metal species generated by the reaction.
[0051] Compounds useful as an activator component in the
preparation of the ionic catalyst systems used in the process of
this invention comprise a cation, which is preferably a Bronsted
acid capable of donating a proton, and a compatible
non-coordinating anion which anion is relatively large (bulky),
capable of stabilizing the active catalyst species (the Group 4
cation) which is formed when the two compounds are combined and
said anion will be sufficiently labile to be displaced by olefinic
diolefinic and acetylenically unsaturated substrates or other
neutral Lewis bases such as ethers, nitrites and the like. Two
classes of compatible non-coordinating anions have been disclosed
in EPA 277,003 and EPA 277,004 published 1988: 1) anionic
coordination complexes comprising a plurality of lipophilic
radicals covalently coordinated to and shielding a central
charge-bearing metal or metalloid core, and 2) anions comprising a
plurality of boron atoms such as carboranes, metallacarboranes and
boranes.
[0052] In a preferred embodiment, the stoichiometric activators
include a cation and an anion component, and may be represented by
the following formula:
(L-H).sub.d.sup.+(A.sup.d-)
wherein L is an neutral Lewis base; H is hydrogen; (L-H).sup.+ is a
Bronsted acid; A.sup.d- is a non-coordinating anion having the
charge d-; and d is an integer from 1 to 3.
[0053] The cation component, (L-H).sub.d.sup.+ may include Bronsted
acids such as protons or protonated Lewis bases or reducible Lewis
acids capable of protonating or abstracting a moiety, such as an
alkyl or aryl, from the bulky ligand metallocene containing
transition metal catalyst precursor, resulting in a cationic
transition metal species.
[0054] The anion component A.sup.d- include those having the
formula [M.sup.k+Q.sub.n].sup.d- wherein k is an integer from 1 to
3; n is an integer from 2-6; n-k=d; M is an element selected from
Group 13 of the Periodic Table of the Elements, preferably boron or
aluminum, and Q is independently a hydride, bridged or unbridged
dialkylamido, halide, alkoxide, aryloxide, hydrocarbyl, substituted
hydrocarbyl, halocarbyl, substituted halocarbyl, and
halosubstituted-hydrocarbyl radicals, said Q having up to 20 carbon
atoms with the proviso that in not more than 1 occurrence is Q a
halide. Preferably, each Q is a fluorinated hydrocarbyl group
having 1 to 20 carbon atoms, more preferably each Q is a
fluorinated aryl group, and most preferably each Q is a
pentafluoryl aryl group. Examples of suitable A.sup.d- also include
diboron compounds as disclosed in U.S. Pat. No. 5,447,895, which is
fully incorporated herein by reference.
[0055] Illustrative, but not limiting examples of the ionic
stoichiometric activator (L-H).sub.d.sup.+ (A.sup.d-) is
N,N-dimethylanilinium tetra(perfluorophenyl)borate,
N,N-dimethylanilinium tetrakis(perfluoronapthyl)borate,
N,N-dimethylanilinium tetrakis(perfluorobiphenyl)borate,
N,N-dimethylanilinium
tetrakis(3,5-bis(trifluoromethyl)phenyl)borate, triphenylcarbenium
tetrakis(perfluoronapthyl)borate, triphenylcarbenium
tetrakis(perfluorobiphenyl)borate, triphenylcarbenium
tetrakis(3,5-bis(trifluoromethyl)phenyl)borate, or
triphenylcarbenium tetra(perfluorophenyl)borate.
[0056] In one embodiment, an activation method using ionizing ionic
compounds not containing an active proton but capable of producing
a bulky ligand metallocene catalyst cation and their
non-coordinating anion are also contemplated, and are described in
EP-A-0 426 637, EP-A-0 573 403 and U.S. Pat. No. 5,387,568, which
are all herein incorporated by reference. The term
"non-coordinating anion" (NCA) means an anion which either does not
coordinate to said cation or which is only weakly coordinated to
said cation thereby remaining sufficiently labile to be displaced
by a neutral Lewis base. "Compatible" non-coordinating anions are
those which are not degraded to neutrality when the initially
formed complex decomposes. Further, the anion will not transfer an
anionic substituent or fragment to the cation so as to cause it to
form a neutral four coordinate metallocene compound and a neutral
by-product from the anion. Non-coordinating anions useful in
accordance with this invention are those that are compatible,
stabilize the metallocene cation in the sense of balancing its
ionic charge at +1, yet retain sufficient lability to permit
displacement by an ethylenically or acetylenically unsaturated
monomer during polymerization. These types of cocatalysts sometimes
use tri-isobutyl aluminum or tri-octyl aluminum as a scavenger.
[0057] The polymerization process may also employ cocatalyst
compounds or activator compounds that are initially neutral Lewis
acids but form a cationic metal complex and a noncoordinating
anion, or a zwitterionic complex upon reaction with the invention
compounds. For example, tris(pentafluorophenyl) boron or aluminum
act to abstract a hydrocarbyl or hydride ligand to yield an
invention cationic metal complex and stabilizing noncoordinating
anion, see EP-A-0 427 697 and EP-A-0 520 732 for illustrations of
analogous Group-4 metallocene compounds. Also, see the methods and
compounds of EP-A-0 495 375. For formation of zwitterionic
complexes using analogous Group 4 compounds, see U.S. Pat. Nos.
5,624,878; 5,486,632; and 5,527,929.
[0058] The catalyst system used to produce the presently disclosed
copolymers may also include a support material or carrier. For
example, the catalyst component(s) and/or activator(s) may be
deposited on, contacted with, vaporized with, bonded to, or
incorporated within, adsorbed or absorbed in, or on, one or more
supports or carriers. The support material may any of the
conventional support materials. Preferably the support material is
a porous support material, for example, talc, inorganic oxides and
inorganic chlorides. Other support materials include resinous
support materials such as polystyrene, functionalized or
crosslinked organic supports, such as polystyrene divinyl benzene
polyolefins or polymeric compounds, zeolites, clays, or any other
organic or inorganic support material and the like, or mixtures
thereof.
[0059] The polymerization process employed to produce the presently
disclosed copolymers can be conducted as a solution, bulk, gas or
slurry polymerization process or a combination thereof, preferably
solution phase or bulk phase polymerization process.
[0060] Homogeneous solution polymerization generally involves
polymerization in a continuous reactor in which the polymer formed
and the starting monomer and catalyst materials supplied, are
agitated to reduce or avoid concentration gradients. Suitable
processes operate above the melting point of the polymers at high
pressures, from 1 to 3000 bar (0.1-300 MPa), in which the monomer
acts as diluent or in solution polymerization using a solvent.
[0061] Temperature control in the reactor may be obtained by
balancing the heat of polymerization with reactor cooling by
reactor jackets or external heat exchangers or internal cooling
coils to cool the contents of the reactor, auto refrigeration,
pre-chilled feeds, vaporization of liquid medium (diluent, monomers
or solvent) or combinations of all three. Adiabatic reactors with
pre-chilled feeds may also be used. The reactor temperature depends
on the catalyst used. In general, the reactor temperature
preferably can vary between about 30.degree. C. and about
200.degree. C., more preferably from about 90.degree. C. to about
150.degree. C., and most preferably from about 100.degree. C. to
about 140.degree. C. In series operation, the second reactor
temperature is preferably higher than the first reactor
temperature. The pressure can vary from about 1 mm Hg to 2500 bar
(250 MPa), preferably from 0.1 bar to 1600 bar (0.01-160 MPa), most
preferably from 1.0 to 500 bar (0.1-50 MPa).
[0062] In one embodiment 500 ppm or less of hydrogen is added to
the polymerization, or 400 ppm or less or 300 ppm or less. In other
embodiments at least 50 ppm of hydrogen is added to the
polymerization, or 100 ppm or more, or 150 ppm or more.
[0063] The polymerization may be conducted in a single reactor, or
in parallel or series multiple reactor configurations. The liquid
process comprises contacting olefin monomers with the above
described catalyst systems in a suitable diluent or solvent and
allowing said monomers to react for a sufficient time to produce
the desired polymers. Hydrocarbon solvents are suitable, both
aliphatic and aromatic. Alkanes, such as hexane(s), pentane,
isopentane, cyclohexane, and octane, are preferred.
[0064] The process may be carried out in a continuous stirred tank
reactor, batch reactor or plug flow reactor, or more than one
reactor operated in series or parallel. These reactors may have or
may not have internal cooling or heating and the monomer feed may
or may not be refrigerated. See the general disclosure of U.S. Pat.
No. 5,001,205 for general process conditions. See also,
International Patent Publication Nos. WO 96/33227 and WO
97/22639.
Formulation of Adhesives
[0065] The copolymer produced herein can be used directly as an
adhesive or can blended with other components to form an adhesive.
Examples of such other components include waxes and functionalized
polyolefins. However, in view of the low viscosity of the
copolymer, the blends typically contain no more than 20 wt %, such
as no more than 10 wt %, of such other components.
[0066] In one embodiment, the copolymer is blended with a
functionalized polyolefin such that the resulting adhesive
composition comprises up to 15 wt %, for example from 1 to 10 wt %,
of the functionalized polyolefin. By functionalized is meant that
the polymer has been contacted with an unsaturated acid or
anhydride. Preferred unsaturated acids or anhydrides include any
unsaturated organic compound containing at least one double bond
and at least one carbonyl group. Representative acids include
carboxylic acids, anhydrides, esters and their salts, both metallic
and non-metallic. Preferably the organic compound contains an
ethylenic unsaturation conjugated with a carbonyl group
(--C.dbd.O). Examples include maleic, fumaric, acrylic,
methacrylic, itaconic, crotonic, alpha.methyl crotonic, and
cinnamic acids as well as their anhydrides, esters and salt
derivatives. Particularly preferred functional groups include
maleic acid and maleic anhydride. Maleic anhydride is particularly
preferred. The unsaturated acid or anhydride is preferably present
at about 0.1 weight % to about 10 weight %, preferably at about 0.5
weight % to about 7 weight %, even more preferably at about 1 to
about 4 weight %, based upon the weight of the hydrocarbon resin
and the unsaturated acid or anhydride. In one preferred embodiment
the functionalized polyolefin is maleated polypropylene.
[0067] In another embodiment, the copolymer is blended with a wax,
either alone or with a functionalized polyolefin such that the
resulting adhesive composition comprises up to 10 wt %, for example
from 2 to 8 wt %, of the wax. Suitable waxes include polar waxes,
non-polar waxes, Fischer-Tropsch waxes, oxidized Fischer-Tropsch
waxes, hydroxystearamide waxes, functionalized waxes, polypropylene
waxes, polyethylene waxes, wax modifiers, and combinations
thereof,
[0068] In addition, tackifiers may be used with the copolymer of
this invention. Examples of suitable tackifiers, include, but are
not limited to, aliphatic hydrocarbon resins, aromatic modified
aliphatic hydrocarbon resins, hydrogenated polycyclopentadiene
resins, polycyclopentadiene resins, gum rosins, gum rosin esters,
wood rosins, wood rosin esters, tall oil rosins, tall oil rosin
esters, polyterpenes, aromatic modified polyterpenes, terpene
phenolics, aromatic modified hydrogenated polycyclopentadiene
resins, hydrogenated aliphatic resin, hydrogenated aliphatic
aromatic resins, hydrogenated terpenes and modified terpenes,
hydrogenated rosin acids, and hydrogenated rosin esters. In some
embodiments the tackifier is hydrogenated.
[0069] In other embodiments the tackifier is non-polar, by which is
meant that the tackifier is substantially free of monomers having
polar groups. Preferably the polar groups are not present, however
if present, they comprise not more than 5 weight %, preferably not
more than 2 weight %, even more preferably no more than 0.5 weight
%, of the tackifier. In some embodiments the tackifier has a
softening point (Ring and Ball, as measured by ASTM E-28) of
80.degree. C. to 150.degree. C., preferably 100.degree. C. to
130.degree. C. In another embodiment the resin is liquid and has a
R and B softening point of between 10 and 70.degree. C.
[0070] The tackifier, if present, is typically present at about 1
to about 15 weight %, such as about 2 to about 10 weight %, for
example about 3 to about 5 weight %, based upon the weight of the
blend.
[0071] Preferred hydrocarbon resins for use as tackifiers or
modifiers include:
[0072] (a) Resins such as C5/C6 terpene resins, styrene terpenes,
alpha-methyl styrene terpene resins, C9 terpene resins, aromatic
modified C5/C6, aromatic modified cyclic resins, aromatic modified
dicyclopentadiene based resins or mixtures thereof. Additional
preferred resins include those described in WO 91/07472, U.S. Pat.
No. 5,571,867, U.S. Pat. No. 5,171,793 and U.S. Pat. No. 4,078,132.
Typically these resins are obtained from the cationic
polymerization of compositions containing one or more of the
following monomers: C5 diolefins (such as 1-3 pentadiene, isoprene,
etc); C5 olefins (such as 2-methylbutenes, cyclopentene, etc.); C6
olefins (such as hexene), C9 vinylaromatics (such as styrene, alpha
methyl styrene, vinyltoluene, indene, methyl indene, etc.); cyclics
(such as dicyclopentadiene, methyldicyclopentadiene, etc.); and or
terpenes (such as limonene, carene, etc).
[0073] (b) Resins obtained by the thermal polymerization of
dicyclopentadiene, and/or the thermal polymerization of dimers or
oligomers of cyclopentadiene and/or methylcyclopentadiene,
optionally with vinylaromatics (such as styrene, alpha-methyl
styrene, vinyl toluene, indene, methyl indene).
[0074] In yet another aspect, the adhesive composition can include
15% by weight or less, or 10% by weight or less, or 5% by weight or
less of one or more additives selected from plasticizers, oils,
stabilizers, antioxidants, pigments, dyestuffs, antiblock
additives, polymeric additives, defoamers, preservatives,
thickeners, adhesion promoters, rheology modifiers, humectants,
fillers, surfactants, processing aids, cross-linking agents,
neutralizing agents, flame retardants, fluorescing agents,
compatibilizers, antimicrobial agents, and water.
[0075] Exemplary oils may include aliphatic naphthenic oils, white
oils, and combinations thereof, for example. The phthalates may
include di-iso-undecyl phthalate (DIUP), di-iso-nonylphthalate
(DINP), dioctylphthalates (DOP), combinations thereof, or
derivatives thereof. Exemplary polymeric additives include homo
poly-alpha-olefins, copolymers of alpha-olefins, copolymers and
terpolymers of diolefins, elastomers, polyesters, block copolymers
including diblocks and triblocks, ester polymers, alkyl acrylate
polymers, and acrylate polymers. Exemplary plasticizers may include
mineral oils, polybutenes, phthalates, and combinations thereof.
Exemplary anti-oxidants include alkylated phenols, hindered
phenols, and phenol derivatives, such as t-butyl hydroquinone,
butylated hydroxyanisole, polybutylated bisphenol, butylated
hydroxy toluene (BHT), alkylated hydroquinone,
2,6-di-tert-butyl-paracresol, 2,5-di-tert-aryl hydroquinone,
octadecyl-3-(3,5-di-tert-butyl-4-hydroxy phenyl) etc.
[0076] Exemplary fillers include silica, diatomaceous earth,
calcium carbonate, iron oxide, hydrogenated castor oil, fumed
silica, precipitated calcium carbonate, hydrophobic treated filmed
silicas, hydrophobic precipitated calcium carbonates, talc, zinc
oxides, polyvinyl chloride powders, fungicides, graphite, carbon
black, asphalt, carbon fillers, clay, mica, fibers, titanium
dioxide, cadmium sulfide, asbestos, wood fluor, polyethylene
powder, chopped fibers, bubbles, beads, thixotropes, bentonite,
calcium sulfate, calcium oxide, magnesium oxide, and combinations
or derivates thereof. Exemplary surfactants include
vinyl-containing or mercapto-containing polyorganosiloxanes,
macromonomers with vinyl terminated polydimethyl siloxane, and
combinations or derivatives thereof.
[0077] Exemplary adhesion promoters include silanes, titanates,
organosylane, acrylics, acids, anhydrides, epoxy resins, hardening
agents, polyamides, methylacrylates, epoxies, phenolic resins,
polyisobutylene, aminoalkyl, mercaptoalkyl, epoxyalkyl,
ureidoalkyl, carboxy, acrylate and isocyanurate functional silanes,
mercaptopropyltrimethoxysilane, glycidoxpropyltrimethoxysilane,
aminopropyltriethoxysilane, aminoethylaminopropyltrimethoxysilane,
ureidopropyltrimethyloxysilane,
bis-gamma-trimethoxysilyl-propylurea,
1,3,5-tris-gamma-trimethoxysilylpropylisocyanurate,
bis-gamma-trimethoxysilylpropylmaleate, fumarate and
gamma-methacryloxypropyltrimethoxysilane,
aminopropyltriethoxysilane, and combinations and derivatives
thereof. Exemplary crosslinking agents include oxime crosslinkers,
alkoxysilanes, epoxyalkylalkoxysilanes, amido silanes,
aminosilanes, enoxysilanes, tetraethoxysilanes, methyltrimethoxy
silane, vinyl trimethoxysilane, glycidoxypropyltrimethoxsilane,
vinyl tris-isopropenoxysilane, methyl tris-isopropenoxysilane,
methyl tris-cyclohexylaminosilane, methyl
tris-secondarybutylaminosilane, polyisocyanates, and combinations
or derivatives thereof. Exemplary organic solvents include
aliphatic solvents, cycloaliphatic solvents, mineral spirits,
aromatic solvents, hexane, cyclohexane, benzene, toluene, xylene,
and combinations or derivatives thereof.
[0078] Exemplary stabilizers include hindered phenols, sulfur
phenols, phosphorous-containing phenols,
1,3,5-trimethyl-2,4,6-tris(3-5-di-tert-butyl-4-hydroxybenzyl)benzene,
pentaerythritol
tetrakis-3(3,5-di-tert-butyl-4-hydroxyphenyl)propionate,
n-octadecyl-3(3,5-di-tert-butyl-4-hydroxyphenyl) propionate,
4,4'-methylenebis(4-methyl-6-tert butylphenol),
4,4'-thiobis(6-tertbutyl-o-cresol), 2,6-di-tert-butylphenol,
6-(4-hydroxyphenoxy)-2,4-bis(n-ocytlthio)-1,3,5-triazine,
2,4,6-tris(4-hydroxy-3,5-di-tert-butyl-phenoxy)-1,3,5-triazine,
di-n-octadecyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonate,
2-(n-octylthio)ethyl-3,5-di-tert-butyl-4-hydroxybenzoate, sorbitol
hexa-(3,3,5-di-tertbutyl-4-hydroxy-phenyl) propionate, and
combinations or derivatives thereof. In one aspect, the adhesive
composition includes from 0.1 to 3 percent by weight of the one or
more stabilizers.
[0079] In another embodiment the copolymer produced by this
invention may be blended with one or more additional polymers to
produce a blend in which the present copolymer is present in an
amount of from 10 to 99 weight %, preferably 20 to 95 weight %,
even more preferably at least 30 to 90 weight %, even more
preferably at least 40 to 90 weight %, even more preferably at
least 50 to 90 weight %, even more preferably at least 60 to 90
weight %, even more preferably at least 70 to 90 weight %, based
upon the total weight of the polymers in the blend. Such blends may
be produced by mixing the two or more polymers together, by
connecting reactors together in series to make reactor blends or by
using more than one catalyst in the same reactor to produce
multiple species of polymer. The polymers can be mixed together
prior to being put into the extruder or may be mixed in an
extruder.
[0080] Suitable polymers for producing blends with the present
copolymer include elastomers (preferred elastomers include all
natural and synthetic rubbers, including those defined in ASTM
D1566). In a preferred embodiment elastomers are blended with the
polymer produced by this invention to form rubber toughened
compositions. In a particularly preferred embodiment the rubber
toughened composition is a two (or more) phase system where the
rubber is a discontinuous phase and the polymer is a continuous
phase. Examples of preferred elastomers include one or more of the
following: ethylene propylene rubber, ethylene propylene diene
monomer rubber, neoprene rubber, styrenic block copolymer rubbers
(including SI, SIS, SB, SBS, SIBS, SEBS, SEPS, and the like (S is
styrene, I is isoprene, B is butadiene, EB is ethylenebutylene, EP
is ethylenepropylene), butyl rubber, halobutyl rubber, copolymers
of isobutylene and para-alkylstyrene, halogenated copolymers of
isobutylene and para-alkylstyrene. This blend may be combined with
the tackifiers and/or other additives as described above.
[0081] In another embodiment the copolymer produced by this
invention may be blended with impact copolymers. Impact copolymers
are defined to be a blend of isotactic PP and an elastomer such as
an ethylene-propylene rubber. In a preferred embodiment the blend
is a two (or more) phase system where the impact copolymer is a
discontinuous phase and the polymer is a continuous phase.
[0082] In another embodiment the copolymer produced by this
invention may be blended with ester polymers. In a preferred
embodiment the blend is a two (or more) phase system where the
polyester is a discontinuous phase and the polymer is a continuous
phase.
[0083] In a preferred embodiment the copolymer of the invention
described above are combined with metallocene polyethylenes (mPE's)
or metallocene polypropylenes (mPP's). The mPE and mPP homopolymers
or copolymers are typically produced using mono- or
bis-cyclopentadienyl transition metal catalysts in combination with
an activator of alumoxane and/or a non-coordinating anion in
solution, slurry, high pressure or gas phase. The catalyst and
activator may be supported or unsupported and the cyclopentadienyl
rings may be substituted or unsubstituted. Several commercial
products produced with such catalyst/activator combinations are
commercially available from ExxonMobil Chemical Company in Baytown,
Tex. under the tradenames EXCEED.TM., ACHIEVE.TM. and EXACT.TM..
For more information on the methods and catalysts/activators to
produce such mPE homopolymers and copolymers see WO 94/26816; WO
94/03506; EPA 277,003; EPA 277,004; U.S. Pat. No. 5,153,157; U.S.
Pat. No. 5,198,401; U.S. Pat. No. 5,240,894; U.S. Pat. No.
5,017,714; CA 1,268,753; U.S. Pat. No. 5,324,800; EPA 129,368; U.S.
Pat. No. 5,264,405; EPA 520,732; WO 92 00333; U.S. Pat. No.
5,096,867; U.S. Pat. No. 5,507,475; EPA 426 637; EPA 573 403; EPA
520 732; EPA 495 375; EPA 500 944; EPA 570 982; WO91/09882;
WO94/03506 and U.S. Pat. No. 5,055,438.
[0084] Adhesive compositions containing the copolymers described
herein exhibit a novel and advantageous balance of properties
including: at least 50% fiber tear at -18.degree. C. and at least
50% fiber tear at 25.degree. C. using Inland paper board as a
substrate, a set time of less than 4 seconds, a viscosity of less
than 50,000 mPa sec at 190.degree. C. and a toughness of greater
than 3.4 megajoule/m.sup.3 when the viscosity at 190.degree. C. is
less than 1000 mPa sec; a toughness of greater than 7
megajoule/m.sup.3 and an elongation of 100% or more when viscosity
at 190.degree. C. is in a range from 1000 to 10,000 mPa sec; and a
toughness of greater than 14 megajoule/m.sup.3 and an elongation of
400% or more when the viscosity at 190.degree. C. is greater than
10,000 mPa sec.
[0085] In preferred embodiments, the adhesive compositions have a
Shear Adhesion Fail Temperature (SAFT) of at least 100.degree. C.,
a viscosity of less than 25,000 mPa sec, such as less than 10,000
mPa sec, for example less than 5,000 mPa sec, typically less than
1,000 mPa sec at 190.degree. C., and a set time of less than 3
seconds, typically less than 2 seconds.
[0086] In other embodiments, the adhesive compositions have a Dot
T-Peel adhesion of at least 8 newton for adhesion between a fiber
board and a fabric substrate at room temperature (25.degree. C.)
and a Dot T-Peel adhesion of at least 8 newton for adhesion between
two polyethylene terephthalate (PET) films at room temperature
(25.degree. C.) and at 40.degree. C.
[0087] In order to measure set time, Dot T-Peel and substrate fiber
tear, adhesive test specimens were created by bonding the
substrates together with a dot of about 0.3 grams of molten
adhesive and compressing the bond with a 500-gram weight. The dot
size was controlled by the adhesive volume such that in most cases
the compressed disk which formed gave a uniform circle just inside
the dimensions of the substrates.
[0088] Once a construct has been produced it can be subjected to
various insults in order to assess the effectiveness of the bond.
Once a bond to a substrate fails a simple way to quantify the
effectiveness of the adhesive is to estimate the area of the
adhesive dot that retained substrate fibers as the construct failed
along the bond line. This estimate is called percent substrate
fiber tear. An example of good adhesion, after conditioning a
sample for 15 hours at -12.degree. C. and attempting to destroy the
bond, would be an estimate of 80-100% substrate fiber tear. It is
likely that 0% substrate fiber tear under those conditions would
signal a loss of adhesion.
[0089] Substrate fiber tear: The specimens were prepared using the
same procedure as that described above. For low temperature fiber
tear test, the bond specimens were placed in a freezer or
refrigerator to obtain the desired test temperature. For substrate
fiber tear at room temperature, the specimens were aged at ambient
conditions. The bonds were separated by hand and a determination
made as to the type of failure observed. The amount of substrate
fiber tear is expressed herein as a percentage. All the fiber tear
tests were conducted using inland paper board as the substrate.
Inland Paper Board is a high performance box board obtained from
Inland Paper Board and Packaging Company of Rome, Ga. It is
characterized as a #56 virgin high performance paper board
stock.
[0090] Set time is defined as the time it takes for a compressed
adhesive substrate construct to fasten together enough to give
substrate fiber tear when pulled apart, and thus the bond is
sufficiently strong to remove the compression. The bond will likely
still strengthen upon further cooling, however, it no longer
requires compression. These set times were measured by placing a
molten dot of adhesive on to a file folder substrate taped to a
flat table. A file folder tab (1 inch by 3 inch (2.5 cm.times.7.6
cm) was placed upon the dot 3 seconds later and compressed with a
500-gram weight. The weight was allowed to sit for about 0.5 to
about 10 seconds. The construct thus formed was pulled apart to
check for a bonding level good enough to produce substrate fiber
tear. The set time was recorded as the minimum time required for
this good bonding to occur. Standards were used to calibrate the
process.
[0091] Dot T-Peel was determined according to ASTM D 1876, except
that the specimen was produced by combining two 1 inch by 3 inch
(2.54 cm.times.7.62 cm) substrate cut outs with a dot of adhesive
with a volume that, when compressed under a 500 gram weight
occupied about 1 square inch of area (1 inch=2.54 cm). Once made
all the specimens were pulled apart in side-by-side testing (at a
rate of 2 inches per minute) by a machine (such as an Instron) that
records the destructive force of the insult being applied. The
maximum force achieved for each sample tested was recorded and
averaged, thus producing the Average Maximum Force, which is
reported as the Dot T-Peel.
[0092] Peel Strength (modified ASTM D1876): Substrates (1.times.3
inches (25.times.76 mm)) were heat sealed with adhesive film (5
mils (130 .mu.m) thickness) at 135.degree. C. for 1 to 2 seconds
and 40 psi (0.28 MPa) pressure. Bond specimens were peeled back in
a tensile tester at a constant crosshead speed of 2 in/min (51
mm/min). The average force required to peel the bond (5 specimens)
apart was recorded.
[0093] Open time is determined according to ASTM D4497
[0094] Shore A hardness was measured according to ASTM 2240. An air
cooled dot of adhesive was subjected to the needle and the
deflection was recorded from the scale.
[0095] Adhesive melt viscosity and viscosity profiles vs.
temperature were measured using a Brookfield digital viscometer and
a number 27 spindle according to ASTM D-3236.
[0096] J SAFT (modified ASTM D 4498-00) measures the ability of a
bond to withstand an elevated temperature rising at 10.degree. F.
(5.5.degree. C.)/15 min., under a constant force that pulls the
bond in the shear mode. Bonds were formed in the manner described
above on Kraft paper (1 inch by 3 inch (2.5 cm.times.7.6 cm)). The
test specimens were suspended vertically in an oven at room
temperature with a 500-gram load attached to the bottom. The
temperatures at which the weight fell were recorded (when the
occasional sample reached temperatures above the oven capacity
>265.degree. F. (129.degree. C.) it was terminated and averaged
in with the other samples at termination temperature).
[0097] Peel Adhesion Failure Temperature (PAFT) was determined
using following procedure modified according to the procedure of
TAPPI T814 PM-77. Two sheets of 6''.times.12'' Kraft paper were
laminated together with a one inch strip of molten adhesive heated
to 177.degree. C. The laminated sheet was trimmed and cut into
1-inch wide strips. These strips were placed in an oven with a
100-gram of weight hanging in a peel mode. The over temperature
increased at a rate of 30.degree. C. per hour. The samples were
hung from a switch that trips when the samples fail to record the
temperature of failure.
[0098] Cloud point is determined by heating the adhesive blends to
121.degree. C. and applying a small bead (approximately 1 gram) of
the molten adhesive to the bulb of an ASTM thermometer. The
temperature at which the molten adhesive clouds over is then noted.
These measures of cloud point provide an indication of a hot melt's
overall compatibility, i.e., the compatibility of the individual
ingredients with each other.
[0099] Plaques suitable for physical property testing were
compression molded on a Carver hydraulic press. 6.5 g of polymer
was molded between brass plates (0.05'' thick) lined with Teflon
coated aluminum foil. A 0.033'' thick chase with a square opening
4''.times.4'' was used to control sample thickness. After one
minute of preheat at 170.degree. C., under minimal pressure, the
hydraulic load was gradually increased to .about.10,000-15,000
lbs., at which it was held for three minutes. Subsequently the
sample and molding plates were cooled for three minutes under
.about.10,000 to 15,000 lbs. load between the water cooled platens
of the press. Plaques were allowed to equilibrate at room
temperature for a minimum of two days prior to physical property
testing.
[0100] Dog bones for tensile testing were cut from compression
molded plaques using a mallet handle die. Specimen dimensions were
those specified in ASTM D 1708 unless otherwise noted. Tensile
properties were measured on an Instron.TM. model 4502 equipped with
a 22.48 lb. load cell and pneumatic jaws fitted with serrated grip
faces. Deformation was performed at a constant crosshead speed of
5.0 in/min with a data sampling rate of 25 points/second. Jaw
separation prior to testing was 0.876'', from which strains were
calculated assuming affine deformation. Initial modulus, stress and
strain at yield (where evident), peak stress, tensile strength at
break, and strain at break were calculated. A minimum of five
specimens from each plaque was tested, the results being reported
as the average value. All stresses quoted were calculated based
upon the original cross-sectional area of the specimen, taking no
account of reduced cross-section as a function of increasing
strain. Tensile strength is defined as the maximum tensile stress.
Toughness is defined as the ability of polymer to absorb applied
energy. The area under the stress-strain curve is used as a measure
of the toughness.
[0101] The color of polymers and their blends was measured using
Gardner index (Gardner color scale) according to ASTM D 1544-04.
Gardner Delta 212 color comparator was used. The samples were
melted at a set temperature and aged for a specified period of time
prior to measurement.
End-Uses
[0102] The adhesives of this invention can be used in any adhesive
application, including but not limited to, disposables, packaging,
laminates, pressure sensitive adhesives, tapes, labels, wood
binding, paper binding, non-wovens, road marking, reflective
coatings, and the like.
[0103] The adhesives described above may be applied to any
substrate. Preferred substrates include wood, paper, cardboard,
plastic, thermoplastic, rubber, metal, metal foil (such as aluminum
foil and tin foil), metallized surfaces, cloth, non-wovens
(particularly polypropylene spun bonded fibers or non-wovens),
spunbonded fibers, cardboard, stone, plaster, glass (including
silicon oxide (SiO.sub.x) coatings applied by evaporating silicon
oxide onto a film surface), foam, rock, ceramics, films, polymer
foams (such as polyurethane foam), substrates coated with inks,
dyes, pigments, PVDC and the like or combinations thereof.
[0104] Additional preferred substrates include polyethylene,
polypropylene, polyacrylates, acrylics, polyethylene terephthalate,
or any of the polymers listed above as suitable for blends. Any of
the above substrates, and/or the polymers of this invention, may be
corona discharge treated, flame treated, electron beam irradiated,
gamma irradiated, microwaved, or silanized.
[0105] In a particular embodiment, the adhesives of this invention
can be used in a packaging article. The packaging article may be
useful as a carton, container, crate, case, corrugated case, or
tray, for example. More particularly, the packaging article may be
useful as a cereal product, cracker product, beer packaging, frozen
food product, paper bag, drinking cup, milk carton, juice carton,
drinking cup, or as a container for shipping produce, just to name
a few exemplary uses.
[0106] The packaging article is formed by applying an adhesive
composition to at least a portion of one or more packaging
elements. The packaging elements may be formed from paper,
paperboard, containerboard, tagboard, corrugated board, chipboard,
kraft, cardboard, fiberboard, plastic resin, metal, metal alloys,
foil, film, plastic film, laminates, sheeting, or any combination
thereof. In one aspect, the adhesive composition may be used to
bind or bond two or more packaging elements together wherein the
packaging elements are formed from the same or different type of
materials. Accordingly, the packaging elements may be individually
formed from paper, paperboard, containerboard, tagboard, corrugated
board, chipboard, kraft, cardboard, fiberboard, plastic resin,
metal, metal alloys, foil, film, plastic film, laminates, sheeting,
or any combination thereof. The one or more packaging elements may
also be individually coated using paper, foil, metal, metal alloys,
polyethylene, polypropylene, polyester, polyethylene terephthalate,
polyvinyl chloride, polyvinylidine chloride, polyvinyl acetate,
polyamides, homopolymers thereof, and combinations and copolymers
thereof.
[0107] When used in a packaging adhesive application, the present
propylene copolymer typically has a viscosity of less than 1500
mPasec at 190.degree. C. as measured using Brookfield digital
viscometer; a tensile strength of at least 200 psi, preferably at
least 400 psi, more preferably at least 600 psi; an elongation of
at least 30%, preferably at least 80%, more preferably at least
120%; and a toughness of 3.4 megajoule/m.sup.3 or more.
[0108] The adhesive composition may also be formulated to have a
viscosity of less than 1000 mPasec at 190.degree. C. as measured
using Brookfield digital viscometer; has tensile strength of at
least 300 psi, preferably at least 500 psi, more preferably at
least 700 psi; has an elongation of at least 30%, preferably at
least 80%, more preferably at least 120%.
[0109] The adhesive composition may also be formulated to have
fiber tear of greater than 80% at room temperature, and have fiber
tear of greater than 80% at -18.degree. C., and have fiber tear of
greater than 80% at 20.degree. C. All the fiber tear should be
tested on inland paper board. The adhesive composition is also
formulated to have a set time of less than 4 seconds, preferably
less than 3 seconds, more preferably less than 2 seconds.
[0110] The formulated adhesive composition may also has a PAFT of
at least 60.degree. C., preferably at least of 80.degree. C. The
adhesive composition also have a SAFT of at least 70.degree. C.,
preferably at least of 100.degree. C. The cloud point of the
adhesive composition is 275.degree. C. or less, preferably
130.degree. C. or less.
[0111] One formulation of the adhesive composition comprises at
least 80 percent by weight of the copolymer of the present
invention, up to 10 percent by weight of one or more tackifiers, up
to 10 percent by weight of one or more waxes, and up to 15 percent
by weight of one or more additives. Another typical formulation of
the adhesive composition comprises at least 85 percent by weight of
the polymer of the present invention, up to 5 percent by weight of
one or more tackifiers, up to 5 percent by weight of one or more
waxes, up to 10 percent by weight of functionalized polyolefin and
up to 15 percent by weight of one or more additives. Yet another
typical formulation of the adhesive composition comprises at least
90 percent by weight of the polymer of the present invention, up to
5 percent by weight of one or more tackifiers, up to 5 percent by
weight of one or more waxes, up to 10 percent by weight of
functionalized polyolefin and up to 10 percent by weight of one or
more additives.
[0112] In a particular embodiment, the adhesives of this invention
can be used in disposable articles. As used herein, "disposable
articles" refer to articles that are not meant for extended use. A
typical life span of a disposable article can be a single use for
any given period of time to multiple uses that last from seconds to
days, to even weeks or longer periods of use. Typically, disposable
articles are formed by attaching a first disposable element to at
least a portion of a second disposable element using an adhesive
composition. Disposable elements may be formed from nonwoven
fabrics, nonwoven webs, non-elastic nonwoven fabrics, elastic
nonwoven fabrics, necked-bonded laminates, stretch-bonded
laminates, spunbond-meltblown-spunbond laminates, polypropylene
spunbonded layers, polyethylene layers, combination polyethylene
and polypropylene spunbonded layers, elastic strands,
styrene-isoprene-styrene, styrene-butadiene-styrene,
styrene-ethylene/propylene-styrene, styrene-co-butadiene-styrene,
polyurethane, woven fabrics, polypropylene, polyester, body fluid
impermeable backsheets, body fluid impermeable layers, body fluid
permeable layers, body fluid permeable covers, absorbents, tissues,
elastomeric materials, superabsorbent polymers, polyolefin films,
polyester films, polyvinylchloride films, polyvinylidine chloride
films, polyvinyl acetate films, elastic attachment tape, frontal
tape backing, wood, paper, barrier films, film laminates, nonwoven
composites, textile materials, woven materials, durable fabrics,
absorbents, elastomeric strands, elastomeric webs, tissues, films,
coverstock materials, nonwoven polyethylene, perforated
polyethylene, superabsorbent polymers, filaments, porous webs,
fibers, loop fastener material, spunbonded nonwovens, liners,
elastic side panels, fastening tape, elastic bands, rayon, nylon,
cellulosic pulp, cellulosic fluff, superabsorbent batts, or
combinations thereof. The disposable elements may have any
thickness and may vary across a cross-section thereof, depending on
its intended uses. In some aspects, the thicknesses may range from
microns to meters. Preferred thicknesses range from microns to
millimeters.
[0113] Exemplary disposable articles may include diapers, training
pants, sanitary napkins, panty liners, incontinent wear, bed pads,
surgical gowns, surgical drapes, rodent traps, hook and loop
fasteners, garments, medical garments, swimwear, or combinations
thereof.
[0114] The propylene copolymer for disposable adhesive applications
preferably has a viscosity of less than 10,000 mPasec at
190.degree. C. as measured using Brookfield digital viscometer; has
tensile strength of at least 800 psi, preferably at least 1,000
psi, more preferably at least 1,200 psi; has an elongation of at
least 100%, preferably at least 200%, more preferably at least
300%; and has a toughness of 3.4 megajoule or more.
[0115] The adhesive composition is preferably also formulated to
have a viscosity of less than 10,000 mPasec at 190.degree. C. as
measured using Brookfield digital viscometer; has tensile strength
of at least 1,000 psi, preferably at least 1,500 psi, more
preferably at least 2,000 psi; have an elongation of at least 100%,
preferably at least 200%, more preferably at least 300%.
[0116] The adhesive composition is preferably formulated to have a
PAFT of 30.degree. C. or more, and preferably a PAFT of from
30.degree. C. to 110.degree. C. The adhesive composition also has a
SAFT of 50.degree. C. or more, and preferably up to 200.degree.
C.
[0117] Furthermore, the adhesive composition used in the disposable
article preferably has a peel strength (as measured according to
ASTM D 1876) of from 90 to 625 g/cm or from 265 to 625 g/cm or from
15 to 450 g/cm. In another embodiment the peel strength of the
adhesive composition is 90 to 1000 g/cm, alternately 200 to 900
g/cm.
[0118] In another embodiment, the adhesive composition has a creep
resistance of from 70% to 95% at 38.degree. C.
[0119] In one embodiment, the disposable article is a diaper having
two different types of adhesive compositions. The first adhesive
composition can be an elastic attachment type adhesive and the
second type of adhesive can be a construction type adhesive,
sometimes referred to as a core and chassis adhesive. It is
advantageous to utilize one adhesive composition for both the
elastic attachment adhesive and the construction adhesive because
the use of two adhesives on the same diaper poses problems for the
diaper manufacturer, which must ensure that the right adhesive is
used in the correct melt tank and is applied to the correct place
on the diaper. Accordingly, an adhesive that is capable of
performing both types of bonding functions is highly desirable.
[0120] Elastic attachment adhesives bond elastic materials to
disposable elements. Diapers have elastic bands on the legs and/or
the waist of the diaper, and typically include a disposable element
such as an elastic band attached to a second disposable element,
which is the portion of the diaper forming the leg opening or
waist. The adhesive composition is used to attach the elastic band
to the second disposable element, which is usually a
fluid-impermeable barrier layer. An elastic attachment adhesive
primarily exhibits high creep resistance to ensure that the
elastic, when under stress, does not move relative to the surface
of the second disposable element or become partially or fully
detached. Should the elastic move or become detached, the resulting
loss of fit could result in inconvenience, waste, embarrassment,
discomfort, and associated health and safety problems.
[0121] In particular, elasticized areas can be formed by adhesively
bonding non-elastic nonwoven fabrics together with at least one
elastic strand disposed in the middle. In such a process, the
elasticized area is a laminated structure including a nonwoven
substrate, at least one elastic strand and a hot-melt adhesive
composition, which binds the nonwoven substrate and the at least
one elastic strand to one another. The nonwoven substrate is
selected from the group consisting of a necked-bonded laminate, a
stretch-bonded laminate, a spunbond-meltblown-spunbond laminate, a
polypropylene spunbonded layer, and a polyethylene layer in
combination with a polypropylene spunbonded layer, or a combination
thereof. The elastic strand is selected from the group comprising
styrene-isoprene-styrene, styrene-butadiene-styrene,
styrene-ethylene/propylene-styrene,
styrene/ethylene-co-butadiene/styrene, polyurethane, and
combinations thereof.
[0122] Another method of forming the elasticized areas includes
adhesively bonding an elastic nonwoven fabric together with a
non-elastic nonwoven fabric. In such a process, a hot-melt adhesive
composition binds a first nonwoven elastic substrate and a second
nonwoven substrate to one another. The first nonwoven elastic
substrate is selected from the group including a necked-bonded
laminate, a stretch-bonded laminate, a polypropylene spunbonded
layer, a polyethylene layer in combination with a polypropylene
spunbonded layer, a styrene-isoprene-styrene strand, a
styrene-butadiene-styrene strand, a
styrene-ethylene/propylene-styrene strand, a
styrene/ethylene-co-butadiene/styrene strand, and a polyurethane
strand. The second nonwoven substrate is selected from the group
including a necked-bonded laminate, a stretch-bonded laminate, a
spunbond-meltblown-spunbond laminate, a polypropylene spunbonded
layer, a polyethylene layer in combination with a polypropylene
spunbonded layer, a styrene-isoprene-styrene strand, a
styrene-butadiene-styrene strand, a
styrene-ethylene/propylene-styrene strand, a
styrene/ethylene-co-butadiene/styrene strand, and a polyurethane
strand.
[0123] Elastic attachment adhesives preferably function at body
temperature under high peel stress or high shear stress for long
periods of time, so that the adhesives should exhibit high peel
strength and high shear strength.
[0124] The propylene copolymer for elastic attachment adhesive
applications preferably has a viscosity in a range of 2000 to
25,000 mPasec at 190.degree. C. as measured using Brookfield
digital viscometer; has tensile strength of at least 800 psi,
preferably at least 1,000 psi, more preferably at least 1,200 psi;
has an elongation of at least 200%, preferably at least 400%, more
preferably at least 600%; and has a toughness of 7 megajoule or
more.
[0125] The adhesive composition is also preferably formulated to
have a viscosity of less than 25,000 mPasec at 190.degree. C. as
measured using Brookfield digital viscometer; has tensile strength
of at least 1,000 psi, preferably at least 1,500 psi, more
preferably at least 2,000 psi; have an elongation of at least 400%,
preferably at least 600%, more preferably at least 800%.
[0126] In a particular embodiment, the adhesives described herein
can be used in woodworking processes. A woodworking process
involves forming a woodworking article by applying an adhesive
composition to at least a portion of a structural element. The
structural element can include a variety of materials, which
include, but are not limited to wood or plywood, or plastic or
veneer. For example, the structural element can also include
lumber, wood, fiberboard, plasterboard, gypsum, wallboard, plywood,
PVC, melamine, polyester, impregnated paper and sheetrock. A
woodworking process can be used to form indoor furniture, outdoor
furniture, trim, molding, doors, sashes, windows, millwork and
cabinetry, for example.
[0127] The propylene copolymer for woodworking adhesive
applications preferably has a viscosity of less than 25,000 mPa sec
at 190.degree. C. as measured using Brookfield digital viscometer;
has tensile strength of at least 800 psi (5520 kPa), preferably at
least 1,000 psi (6.89 MPa), more preferably at least 1,200 psi
(8.27 MPa); has an elongation of at least 200%, preferably at least
400%, more preferably at least 600%, and has a toughness of 7
megajoule or more.
[0128] The adhesive composition is also preferably formulated to
have a viscosity of less than 25,000 mPa sec at 190.degree. C. as
measured using Brookfield digital viscometer; has tensile strength
of at least 1,000 psi (6.89 MPa), preferably at least 1,500 psi
(10.34 MPa), more preferably at least 2,000 psi (13.79 MPa); have
an elongation of at least 200%, preferably at least 400%, more
preferably at least 600%.
[0129] In yet another aspect, the adhesive composition has an open
time of 3 seconds or more. Preferably, the adhesive composition has
an open time of 20 seconds or more. More preferably, the adhesive
composition has an open time of 60 seconds or more. In another
aspect, the adhesive composition has a set time of 5 minute or
less, preferably 3 minutes or less, more preferably 2 minutes or
less.
[0130] One typical formulation of the adhesive composition includes
at least 70 percent by weight of the copolymer of the present
invention, up to 10 percent by weight of one or more functionalized
polyolefins, up to 10 percent by weight of one or more waxes, up to
15 percent by weight of one or more tackifiers, and up to 10
percent by weight of one or more additives.
[0131] The invention will now be more particularly described with
reference to the following non-limiting Examples.
[0132] In the Examples, the hexene-1 content was determined using
C-13 NMR. In preparation of a polymer for C-13 NMR analysis about
0.2-0.3 grams of polymer was dissolved in about 3 ml of deuterated
tetrachloroethane in a 10-mm diameter NMR tube at about 120.degree.
C., then the sample solution was placed into a NMR spectrometer
with the probe temperature set to 120.degree. C. Spectral data was
collected for at least four hours using an observe pulse angle of
less than 90 degrees, ungated proton decoupling and a delay time
long enough to allow adequate quantification of the NMR signals of
interest. Interpretation of the data is based in part on peak
assignments provided by Kissin and Brandolini (Macromolecules, 24,
2632, (1991)), Folini, et al., (Macromol. Chem. Phys., 201, 401
(2000)) and Resconi, et al., (Chem. Rev., 100, 1253, (2000).
Instrument measured integral intensities were used to determine
sample composition.
[0133] Melting point (Tm), peak crystallization temperature (Tc),
heat of fusion (Hf) and percent crystallinity were determined by
differential scanning calorimetry (DSC) by the following procedure
according to ASTM E 794-85 using a TA Instruments model 2910
machine or a Perkin-Elmer DSC 7 machine. Prior to the DSC
measurement, the samples are aged (typically by holding at ambient
temperature for a period up to about 2 days) or annealed to
maximize the level of crystallinity. Samples weighing approximately
5-10 mg are sealed in aluminum sample pans. The DSC data are
recorded by first cooling the sample to -50.degree. C. and then
gradually heating it to 200.degree. C. at a rate of 10.degree.
C./minute. The sample is kept at 200.degree. C. for 5 minutes
before a second cooling-heating cycle is applied. Both the first
and second cycle thermal events are recorded. Areas under the
melting curves are measured and used to determine the heat of
fusion and the degree of crystallinity. The percent crystallinity
(X %) is calculated using the formula, X %=[area under the curve
(Joules/gram)/B (Joules/gram)]*100, where B is the heat of fusion
for the homopolymer of the major monomer component. These values
for B are to be obtained from the Polymer Handbook, Fourth Edition,
published by John Wiley and Sons, New York 1999. A value of 189 J/g
(B) is used as the heat of fusion for 100% crystalline
polypropylene. The melting temperature is measured and reported
during the second heating cycle (or second melt). Typically, a
sample of propylene copolymer will show secondary melting peaks
adjacent to the principal peak, which peaks are considered together
as a single melting point. The highest of these peaks is considered
the melting point.
[0134] Molecular weights (number average molecular weight (Mn),
weight average molecular weight (Mw), and z-average molecular
weight (Mz)) were determined using a Waters 150 Size Exclusion
Chromatograph (SEC) equipped with a differential refractive index
(DRI) detector, an online low angle light scattering (LALLS)
detector and a viscometer (VIS). The details of these detectors as
well as their calibrations have been described by, for example, T.
Sun, P. Brant, R. R. Chance, and W. W. Graessley, in
Macromolecules, Volume 34, Number 19, 6812-6820, (2001),
incorporated herein by reference. Solvent for the SEC experiment
was prepared by adding 6 grams of butylated hydroxy toluene (BHT)
as an antioxidant to a 4 liter bottle of 1,2,4 trichlorobenzene
(TCB) (Aldrich Reagent grade) and waiting for the BHT to
solubilize. The TCB mixture was then filtered through a 0.7 micron
glass pre-filter and subsequently through a 0.1 micron Teflon
filter. There was an additional online 0.7 micron glass
pre-filter/0.22 micron Teflon filter assembly between the high
pressure pump and SEC columns. The TCB was then degassed with an
online degasser (Phenomenex, Model DG-4000) before entering the
SEC. Polymer solutions were prepared by placing dry polymer in a
glass container, adding the desired amount of TCB, then heating the
mixture at 160.degree. C. with continuous agitation for about 2
hours. All quantities were measured gravimetrically. The TCB
densities used to express the polymer concentration in mass/volume
units were 1.463 g/ml at room temperature and 1.324 g/ml at
135.degree. C. The injection concentration ranged from 1.0 to 2.0
mg/ml, with lower concentrations being used for higher molecular
weight samples.
[0135] The branching index in the Examples was measured using SEC
with an on-line viscometer (SEC-VIS) and is reported as g' at each
molecular weight in the SEC trace. The branching index g' is
defined as:
g ' = .eta. b .eta. l ##EQU00001##
where .eta..sub.b is the intrinsic viscosity of the branched
polymer and .eta..sub.1 is the intrinsic viscosity of a linear
polymer of the same viscosity-averaged molecular weight (M.sub.v)
as the branched polymer. .eta..sub.1=KM.sub.v.sup..alpha., K and
.alpha. were measured values for linear polymers and should be
obtained on the same SEC-DRI-LS-VIS instrument as the one used for
branching index measurement. For polypropylene samples presented in
this invention, K=0.0002288 and .alpha.=0.705 were used. The
SEC-DRI-LS-VIS method obviates the need to correct for
polydispersities, since the intrinsic viscosity and the molecular
weight were measured at individual elution volumes, which arguably
contain narrowly dispersed polymer. Linear polymers selected as
standards for comparison should be of the same viscosity average
molecular weight, monomer content and composition distribution.
Linear character for polymer containing C2 to C10 monomers is
confirmed by Carbon-13 NMR using the method of Randall (Rev.
Macromol. Chem. Phys., C29 (2&3), p. 285-297). Linear character
for C11 and above monomers is confirmed by GPC analysis using a
MALLS detector. For example, for a copolymer of propylene, the NMR
should not indicate branching greater than that of the co-monomer
(i.e. if the comonomer is butene, branches of greater than two
carbons should not be present). For a homopolymer of propylene, the
GPC should not show branches of more than one carbon atom. When a
linear standard is desired for a polymer where the comonomer is C9
or more, one can refer to T. Sun, P. Brant, R. R. Chance, and W. W.
Graessley, Macromolecules, Volume 34, Number 19, 6812-6820, (2001)
for protocols on determining standards for those polymers. In the
case of syndiotactic polymers, the standard should have a
comparable amount of syndiotacticty as measured by Carbon 13 NMR.
The viscosity averaged g' was calculated using the following
equation:
g vls ' = C i [ .eta. i ] b C i KM i .alpha. ##EQU00002##
where C.sub.i is the polymer concentration in the slice i in the
polymer peak, and [.eta..sub.i].sub.b is the viscosity of the
branched polymer in slice i of the polymer peak, and M.sub.i is the
weight averaged molecular weight in slice i of the polymer peak
measured by light scattering, K and .alpha. are as defined
above.
EXAMPLE 1
[0136] All polymerizations were performed in a liquid filled,
single-stage continuous reactor using mixed metallocene catalyst
systems. The reactor was a 0.5-liter stainless steel autoclave
reactor and was equipped with a stirrer, a water cooling/steam
heating element with a temperature controller, and a pressure
controller. Solvents, propylene, and comonomers (such as 1-hexene
and 1-octene) were first purified by passing through a three-column
purification system. The purification system consisted of an
Oxiclear column (Model # RGP-R1-500 from Labelear) followed by a 5A
and a 3A molecular sieve columns. Purification columns were
regenerated periodically whenever there was evidence of lower
activity of polymerization. Both the 3A and 5A molecular sieve
columns were regenerated in-house under nitrogen at a set
temperature of 260.degree. C. and 315.degree. C., respectively. The
molecular sieve material was purchased from Aldrich. Oxiclear
column was regenerated in the original manufacture. The purified
solvents and monomers were then chilled to about -15.degree. C. by
passing through a chiller before being fed into the reactor through
a manifold. Solvent and monomers were mixed in the manifold and fed
into reactor through a single tube. All liquid flow rates were
measured using Brooksfield mass flow meters or Micro-Motion
Coriolis-type flow meters.
[0137] The catalyst was
rac-dimethylsilylbis(2-methyl-4-phenylindenyl) zirconium dimethyl
(obtained from Albemarle) pre-activated with N,N-dimethylanilinium
tetrakis (pentafluorophenyl) borate (obtained from Albemarle) at a
molar ratio of about 1:1 in toluene. The catalyst solution was kept
in an inert atmosphere with <1.5 ppm water content and was fed
into reactor by a metering pump through a separated line. Catalyst
and monomer contacts took place in the reactor.
[0138] As an impurity scavenger, 250 ml of tri-n-octyl aluminum
(TNOA) (25 wt % in hexane, Sigma Aldrich) was diluted in 22.83
kilogram of hexane. The TNOA solution was stored in a 37.9-liter
cylinder under nitrogen blanket. The solution was used for all
polymerization runs until about 90% of consumption, then a new
batch was prepared. The feed rates of the TNOA solution were
adjusted in a range from 0 (no scavenger) to 4 ml per minute to
achieve a maximum catalyst activity.
[0139] The reactor was first cleaned by continuously pumping
solvent (e.g., hexane) and scavenger through the reactor system for
at least one hour at a maximum allowed temperature (about
150.degree. C.). After cleaning, the reactor was heated/cooled to
the desired temperature using a water/steam mixture flowing through
the reactor jacket and controlled at a set pressure with controlled
solvent flow. Monomers and catalyst solutions were then fed into
the reactor when a steady state of operation was reached. An
automatic temperature control system was used to control and
maintain the reactor at a set temperature. Onset of polymerization
activity was determined by observations of a viscous product and
lower temperature of water-steam mixture. Once the activity was
established and the system reached equilibrium, the reactor was
lined out by continuing operation of the system under the
established condition for a time period of at least five times of
mean residence time prior to sample collection. The resulting
mixture, containing mostly solvent, polymer and unreacted monomers,
was collected in a collection box after the system reached a steady
state operation. The collected samples were first air-dried in a
hood to evaporate most of the solvent, and then dried in a vacuum
oven at a temperature of about 90.degree. C. for about 12 hours.
The vacuum oven dried samples were weighed to obtain yields. All
the reactions were carried out at a pressure of about 2.41 MPa-g.
The detailed polymerization condition and some product properties
are listed in Table 1A and the C-13 NMR data for polymer products
are listed in Table 1B.
TABLE-US-00001 TABLE 1A Run No. 1-1 1-2 Polymerization temperature
(.degree. C.) 100 100 Propylene feed rate (g/min) 14 14 Hexene-1
feed rate (ml/min) 1.5 1.8 Catalyst feed rate (mol/min) 9.45E-07
9.45E-07 Hexane flow rate (ml/min) 80 80 Tm (.degree. C.) 101 104
Tc (.degree. C.) 52 62 Tg (.degree. C.) -13 Heat of fusion (J/g) 49
55.11 Mn (kg/mol) 5 Mw (kg/mol) 30.53 Mz (kg/mol) 63.129 MWD 5.92
Viscosity @190.degree. C. (mPa sec) 628 Tensile strength (MPa) 14.6
Elongation at break (%) 295 Modulus (MPa) 195.2 Toughness
(megajoule/m.sup.3) 34.8 Copolymer hexene content (wt %) 8.1
8.1
TABLE-US-00002 TABLE 1B C-13 NMR Data for polymers produced in
Example 1 Run No. 1-1 1-2 Triad Mole Fraction [HHH] 0.002 0.002
[HHP] 0.006 0.006 [PHP] 0.034 0.034 [HPH] 0.000 0.000 [HPP] 0.101
0.101 [PPP] 0.857 0.857 Regios per 10,000 Units 2,1 erythro 8 9 2,1
threo 0 0 1,3 insertions 28 23 End Groups per 10,000 Units Butyl 3
4 Propyl 29 28 Isobutyl 43 33 Vinylidene 0 28 Trisub. 9 13 Hexene
Composition Wt (%) 8.1 8.1
[0140] A number of hot melt adhesives were prepared by blending the
polymers produced in Runs 1-1 and 1-2 with one or more of
functionalized additives, tackifier, wax, antioxidant, and other
ingredients under low shear mixing at elevated temperatures to form
fluid melts. The mixing temperature varied from about 130 to about
190.degree. C. As examples, Tables 1C and 1D below list the
detailed formulation and the properties of the resulting blends. In
Tables 1C and 1 D, MAPP40 is a maleic anhydride modified
polypropylene, having an acid number of 50, a viscosity of 300 mPa
sec. at 190.degree. C., a softening point of 149.degree. C.,
available from Chusei, USA., and MA-POA is a functionalized
propylene based adhesive composition produced according to the
procedure described in WO2005105868. The prefunctionalized polymer
has Mn/Mw/Mz of 20.7/40.6/72.5 kg/mole, a heat of fusion of 29.5
J/g, and a melting peak temperature of 132.degree. C. The mealated
polymer contains 1.41 wt % of maleic anhydride. Sasol C80 wax is a
Fischer-Tropsch wax obtained from Moore and Munger., and Escomer
H101 is functionalized wax supplied by ExxonMobil Chemicals,
Houston, Tex. All the adhesion tests were conducted at ambient
condition unless otherwise noted. The formulations are listed in
weight percent unless otherwise noted. The fiber tear was tested on
Inland paper board unless otherwise noted. These Examples
demonstrate that adhesives with good adhesion at room temperature
and -18.degree. C., as well as short set time (<3 seconds),
could be achieved using a formulation comprising the present
propylene copolymer with very low viscosity and small quantities
(<20 wt %) of additives.
TABLE-US-00003 TABLE 1C Adhesive performance obtained using Dot
T-Peel test on Inland board Adhesive formulation No. 1-1 1-2 1-3
1-4 Run No. 1-1 polymer (wt %) 85 85 85 85 MAPP40 (wt %) 10 10 0 0
MA-POA (wt %) 0 0 10 10 C80 wax (wt %) 5 0 5 0 Escomer H101 (wt %)
0 5 0 5 Viscosity at 160.degree. C. (mPa sec) 1200 1200 1200 1200
Set time (sec) 1.5 1.5 1 2 Viscosity at 190.degree. C. (mPa sec)
507 515 550 496 Fiber tear at room temperature (%) >90 >90
>90 <70 Fiber tear at -2.degree. C. (%) >90 >90 >90
<70 Fiber tear at -18.degree. C. (%) >90 <70 >90
<70
TABLE-US-00004 TABLE 1D Adhesive performance obtained using Dot
T-Peel on Inland board Adhesive formulation No. 1-5 1-6 1-7 1-8 1-9
1-10 Run No. 1-2 Polymer 90 90 89 88 85 85 (wt %) MAPP40 (wt %) 0 0
0 0 10 0 MA-POA (wt %) 5 4 5 5 0 10 C80 wax (wt %) 5 6 6 7 5 5 Set
time (sec.) 2.5 2.5 3 2 2.5 2 Viscosity at 160.degree. C. na na na
na 1090 1250 (mPa sec) Viscosity at 190.degree. C. 650 605 680 571
na na (mPa sec) Fiber tear at room 85 10 40 0 94 95 temperature (%)
Fiber tear at -2.degree. C. (%) 88 10 0 0 95 95 Fiber tear at
-18.degree. C. (%) 65 5 5 0 90 95
EXAMPLE 2
[0141] Propylene copolymers in Example 2 were produced following
the same procedure as described in Example 1. Detailed conditions
and some properties data are listed in Table 2A. Runs # 2-1 and
2-12 are comparative examples. They were produced under similar
conditions as the other runs in Example 2 except that there was no
1-hexene fed into the reactor for these two runs. Polymer produced
in Run #2-1 was too brittle for tensile testing. The specimen broke
in the grip. Tensile testing for polymer produced in Run # 2-2 and
Run # 2-3 were conducted on a Type V specimen defined in ASTM D
638-03 (0.25 inch wide and 0.146 inch thick). Tensile testing for
polymer produced in Run # 2-11 and 2-12 were conducted on a Type I
specimen defined in ASTM D 638-03 (0.5 inch wide and 0.0745 inch
thick). Significant improvements in mechanical properties such as
elongation and toughness for propylene copolymers with 1-hexene as
compared with polypropylene homopolymer at similar viscosity are
revealed in this table. This is especially true for polymers with
low viscosity (<800 mPasec). Good mechanical properties at this
low viscosity copolymer allow adhesives with less additives to be
made without sacrificing their cohesive strength.
[0142] The copolymers with higher viscosity are good for adhesive
applications where strong mechanical strength is required such as
woodworking, disposables and elastic attachment.
TABLE-US-00005 TABLE 2A Run # 2-1 2-2 2-3 2-4 4-5 2-6
Polymerization 100 100 100 100 100 100 temperature (.degree. C.)
Propylene feed rate 14 14 14 14 14 14 (g/min) Hexene-1 feed rate 0
1 2 3 4 5 (ml/min) Hexane (ml/min) 80 80 80 80 80 80 Catalyst feed
rate 1.18E-06 1.18E-06 1.2E-06 1.18E-06 1.2E-06 1.2E-06 (mol/min)
Yield (g/min.) 14.1 14.6 15.1 15.9 16.4 17.5 Copolymer hexene 0
3.92 11.3 18.7 content (wt %) Tm (.degree. C.) 134.2 120.4 106.9
95.9 84.3 73.9 Tc (.degree. C.) 95.0 75.6 51.3 38.2 16.1 3.9 Tg
(.degree. C.) -10.7 -11.4 -14.3 -21.3 Heat of fusion (J/g) 78.0
68.8 54.2 49.1 33.5 28.6 Viscosity @190.degree. C. 580.0 565.0
775.0 625.0 685.0 732.5 (mPa sec) Elongation at break 1.9 5.57
747.8 723.7 958.9 (%) Tensile strength 0.41 0.744 10.2 14.8 14.7
(MPa) Toughness 1.41 7.41 435.7 817.9 952.5 (megajoule/m.sup.3) Run
# 2-7 2-8 2-9 2-10 2-11 2-12 Polymerization 80 80 80 80 80 80
temperature (.degree. C.) Propylene feed rate 14 14 14 14 14 14
(g/min) Hexene-1 feed rate 5 4 3 2 1 0 (ml/min) Hexane (ml/min) 80
80 80 80 80 80 Catalyst feed rate 9.4E-07 9.4E-07 9.4E-07 9.4E-07
9.4E-07 9.4E-07 (mol/min) Yield (g/min.) 18.2 17.6 16.0 15.5 14.8
14.3 Copolymer hexene 17.9 12.4 3.7 0 content (wt %) Tm (.degree.
C.) 79.0 85.6 99.0 113.2 129.2 146.8 Tc (.degree. C.) 13.9 20.8
44.1 65.5 85.1 105.4 Tg (.degree. C.) -17.1 -19.7 -14.3 -7.3 -4.5
-- Heat of fusion (J/g) 30.8 35.8 50.5 56.3 73.8 90.1 Viscosity
@190.degree. C. 22400.0 15220.0 14300.0 10560.0 8850.0 6000.0 (mPa
sec) Elongation at break 1452.4 1232.2 1053.8 1003.6 6.07 1.93 (%)
Tensile strength 30.0 28.2 29.1 27.8 20.93 6.73 (MPa) Toughness
1520.1 1817.4 1525.6 1664.2 485.5 12.78 (megajoule/m.sup.3)
[0143] A number of hot melt adhesives were prepared by blending the
polymer produced in Example 2 with one or more of functionalized
additives, wax, antioxidant, and other ingredients under low shear
mixing at elevated temperatures to form fluid melt. The mixing
temperature varied from about 130 to about 190.degree. C. As
examples, Tables 2B and 2C below list the detailed formulation and
the properties of blends. All the adhesion tests were conducted at
ambient condition unless otherwise noted. The formulations are
listed in weight percent unlike otherwise noted. The fiber tear was
tested on Inland paper board. All of these adhesives were produced
using 8 wt. % of other ingredients. Adhesive formulations 2-1 and
2-2 are comparative examples and were produced using
homopolypropylene as base polymers. The adhesive properties for
propylene copolymers were significantly improved as compared with
those for the propylene homopolymer. Also good adhesion was
obtained by using copolymers having high 1-hexene content, but the
set time was longer. The desired balance of adhesive properties and
mechanical strength for the present adhesives can be achieved by
varying the 1-hexene content, polymer viscosity (or molecular
weight) as well as by the addition of other ingredients.
TABLE-US-00006 TABLE 2B Adhesive formulation No. 2-1 2-2 2-3 2-4
2-5 2-6 Polymer produced in run run run run run run Example 2 no no
no no no no 2-1 2-1 2-2 2-2 2-3 2-3 Polymer (wt. %) 92 100 92 100
92 100 C80 wax (wt. %) 5 0 5 0 5 0 MAPP 40 (wt. %) 2 0 2 0 2 0
Irganox 1010 (wt. %) 1 0 1 0 1 0 Set time (second) 2.75 3.5 2.5 5.5
2.5 >6 Fiber tear at room 0 0 69 0 98 0 temperature (%) Fiber
tear at 2.degree. C. (%) 0 0 89 0 89 0 Fiber tear at -18.degree. C.
(%) 0 0 73 0 70 0 Hardness (Shore A) 98 98 98 99 99 98
TABLE-US-00007 TABLE 2C Adhesive formulation No. 2-7 2-8 2-9 2-10
2-11 2-12 Polymer produced in run run run run run Run Example 2 no
no no no no no 2-4 2-4 2-5 2-5 2-6 2-6 Polymer (wt. %) 92 100 92
100 92 100 C80 wax (wt. %) 5 0 5 0 5 0 MAPP 40 (wt. %) 2 0 2 0 2 0
Irganox 1010 (wt. %) 1 0 1 0 1 0 Set time (second) 3 >6 4 >6
5 >6 Fiber tear at room 100 0 100 38 98 0 temperature (%) Fiber
tear at 2.degree. C. (%) 97 0 97 5 99 75 Fiber tear at -18.degree.
C. (%) 92 0 28 0 99 40 Hardness (Shore A) 98 97 94 95 87 83
* * * * *