U.S. patent application number 12/719138 was filed with the patent office on 2010-06-24 for electrolyte for lithium secondary battery comprising chelating agent and lithium secondary battery using the same.
This patent application is currently assigned to LG CHEM LTD.. Invention is credited to Soon Ho AHN, Seung Tae HONG, Jong Mo JUNG, Hyo Shik KIL, Jeong Min KIM, Jae Hyun LEE, Sung Hyup LEE, Jong Hoa OK.
Application Number | 20100159321 12/719138 |
Document ID | / |
Family ID | 38092460 |
Filed Date | 2010-06-24 |
United States Patent
Application |
20100159321 |
Kind Code |
A1 |
LEE; Jae Hyun ; et
al. |
June 24, 2010 |
ELECTROLYTE FOR LITHIUM SECONDARY BATTERY COMPRISING CHELATING
AGENT AND LITHIUM SECONDARY BATTERY USING THE SAME
Abstract
Disclosed herein is an electrolyte for lithium secondary
batteries comprising: a chelating agent, which forms complexes with
transition metal ions in the battery, and at the same time does not
react and coordinate with lithium ions; a non-aqueous solvent; and
an electrolyte salt, as well as a lithium secondary battery
comprising the electrolyte. The chelating agent, which is contained
in the electrolyte for lithium secondary batteries, can suppress a
side reaction in which transition metal ions are reduced and
deposited as transition metals on the anode. Also, the chelating
agent can suppress internal short-circuits in the battery and the
resulting voltage drop of the battery and a reduction in the safety
and performance of the battery, which can occur when transition
metals are deposited on the anode.
Inventors: |
LEE; Jae Hyun; (Daejeon,
KR) ; AHN; Soon Ho; (Daejeon, KR) ; OK; Jong
Hoa; (Daejeon, KR) ; HONG; Seung Tae;
(Daejeon, KR) ; KIM; Jeong Min; (Daejeon, KR)
; JUNG; Jong Mo; (Daejeon, KR) ; KIL; Hyo
Shik; (Daejeon, KR) ; LEE; Sung Hyup;
(Daejeon, KR) |
Correspondence
Address: |
CANTOR COLBURN, LLP
20 Church Street, 22nd Floor
Hartford
CT
06103
US
|
Assignee: |
LG CHEM LTD.
Seoul
KR
|
Family ID: |
38092460 |
Appl. No.: |
12/719138 |
Filed: |
March 8, 2010 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
12095845 |
Jun 2, 2008 |
|
|
|
PCT/KR2006/005152 |
Dec 1, 2006 |
|
|
|
12719138 |
|
|
|
|
Current U.S.
Class: |
429/207 |
Current CPC
Class: |
H01M 10/4235 20130101;
H01M 10/0565 20130101; H01M 10/0567 20130101; Y02E 60/10 20130101;
H01M 10/052 20130101 |
Class at
Publication: |
429/207 |
International
Class: |
H01M 10/26 20060101
H01M010/26 |
Foreign Application Data
Date |
Code |
Application Number |
Dec 2, 2005 |
KR |
10-2005-0116827 |
Claims
1. An electrolyte for lithium secondary batteries comprising: a
chelating agent, which forms complexes with transition metal ions
in the battery, and at the same time does not react and coordinate
with lithium ions; a non-aqueous solvent; and an electrolyte salt,
wherein the chelating agent comprises EDTA (ethylene diamine
tetraacetic acid), and wherein the chelating agent is contained in
an amount of 2 to 200 mM relative to the electrolyte.
2. The electrolyte of claim 1, wherein the complexes are insoluble
in the electrolyte.
3. A lithium secondary battery comprising an electrolyte for
lithium secondary batteries, wherein the electrolyte comprises: a
chelating agent, which forms complexes with transition metal ions
in the battery, and at the same time does not react and coordinate
with lithium ions; a non-aqueous solvent; and an electrolyte salt,
wherein the chelating agent comprises EDTA (ethylene diamine
tetraacetic acid), and wherein the chelating agent is contained in
an amount of 2 to 200 mM relative to the electrolyte.
4. The lithium secondary battery of claim 3, wherein the complexes
are insoluble in the electrolyte.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of U.S. application Ser.
No. 12/095,845, filed Jun. 2, 2008, which is a national stage of
International Application No. PCT/KR2006/005152, filed on Dec. 1,
2006, and which claims priority to Korean Application No.
10-2005-0116827, filed on Dec. 2, 2005, and all the benefits
accruing therefrom under 35 U.S.C. 119, the contents of which are
incorporated herein by reference in their entirety.
BACKGROUND OF THE INVENTION
[0002] (a) Field of the Invention
[0003] The present invention relates to an electrolyte for lithium
secondary batteries containing a chelating agent, and a lithium
secondary battery comprising said electrolyte.
[0004] (b) Description of the Related Art
[0005] Recently, the compact and lightweight construction of
electronic equipment has been realized and the use of portable
electronic devices has been generalized, and thus studies on
secondary batteries having high energy density have been actively
conducted.
[0006] Lithium secondary batteries, which are currently mainly
used, comprise cathode and anode made of materials capable of
intercalating and deintercalating lithium ions, are fabricated by
injecting a non-aqueous electrolyte between the cathode and anode,
and produce electrical energy by oxidation and reduction reactions,
which occur when lithium ions are intercalated into and
deintercalated from the cathode and anode.
[0007] When the secondary battery is charged and discharged,
transition metal ions in the battery can cause side reactions and
can result in a reduction in the performance of the battery. For
example, when the cathode contains Fe impurities, Fe can be
ionized, and deposited on the anode, resulting in voltage drop.
Also, some Co, which is used as the cathode active material, can be
dissolved out and deposited on the anode, and when spinel Mn is
used for the cathode, Mn can be dissolved. In addition, when a Fe
olivine material is used, Fe can be dissolved out. Such side
reactions deteriorate the stability and performance of the
battery.
[0008] In a prior attempt to suppress side reactions, an expensive
apparatus for purifying raw materials is used, the pretreatment of
raw materials is performed, or other alternative materials having
poor performance are used. However, such methods have problems in
that they are expensive and deteriorate the performance of the
battery.
SUMMARY OF THE INVENTION
[0009] It is an object of the present invention to provide an
electrolyte for lithium secondary batteries containing a chelating
agent, which forms complexes with transition metal ions and, at the
same time, does not react and coordinate with lithium ions, and
thus can improve the performance and safety of the battery by
suppressing side reactions, in which some transition metals and
transition metal ions such as Fe impurities, contained in a
cathode, are oxidized and deposited on an anode when the battery is
charged and discharged, as well as a lithium secondary battery
comprising said electrolyte.
[0010] To achieve the above object, the present invention provides
an electrolyte for lithium secondary batteries, comprising: a
chelating agent, which forms complexes with transition metal ions
in the battery and, at the same time, does not react and coordinate
with lithium ions; a non-aqueous solvent; and an electrolyte salt,
as well as a lithium secondary battery comprising said
electrolyte.
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] FIG. 1 is a graphic diagram showing the results of Fe
electroplating experiments for batteries fabricated according to
Example 1 of the present invention and Comparative Examples
1.about.3.
[0012] FIG. 2 is a graphic diagram showing the results of Fe
electroplating experiments for batteries fabricated according to
Examples 1.about.5 of the present invention and Comparative Example
1.
[0013] FIG. 3 is a graphic diagram showing the high-temperature
storage characteristics of batteries fabricated according to
Examples 6 and 7 of the present invention and Comparative Example
4.
[0014] FIG. 4 is a graphic diagram showing the C-rate
characteristics of batteries fabricated according to Examples 6 and
7 of the present invention and Comparative Example 4.
[0015] FIG. 5 is a graphic diagram showing the cycle
characteristics of batteries fabricated according to Examples 6 and
7 of the present invention and Comparative Example 4.
DETAILED DESCRIPTION OF THE INVENTION
[0016] Hereinafter, the present invention will be described in
further detail.
[0017] The present invention is characterized in that a chelating
agent, which is not reactive with lithium ions and does not form
coordinate bonds with lithium ions and thus does not form complexes
with lithium ions, is selected and the selected chelating agent is
used in a lithium secondary battery.
[0018] The cathode of the lithium secondary battery generally
contains lithium transition-metal oxides and, in some cases, Fe as
an impurity. When this secondary battery is charged and discharged,
side reactions can occur, in which transition metals such as Co, Mn
and Ni, which can be contained in the cathode, or transition metals
such as Fe impurities, are ionized, dissolved out from the cathode,
and deposited on the anode.
[0019] When the electrolyte of the lithium secondary battery
contains a chelating agent, the chelating agent will form
coordinate bonds with the metal ions such as Co, Mn, Ni and Fe to
form metal-containing cyclic complexes known as chelates. Also, the
chelating agent, which is included in the inventive electrolyte,
does not deteriorate the performance of the battery because it does
not react and coordinate with lithium ions, so that it does not
form complexes with lithium ions.
[0020] Thus, because the chelating agent forms complexes with
transition metal ions except for lithium ions in the battery, it
significantly reduces the reactivity of the transition metal ions,
so that it can suppress side reactions in which the transition
metal ions are reduced and deposited as transition metals on the
anode. Also, the chelating agent can suppress internal
short-circuits in the battery and the resulting voltage drop of the
battery and a reduction in the safety and performance of the
battery, which can occur when transition metals are deposited on
the anode.
[0021] Also, in the present invention, complexes formed between the
chelating agent and the transition metal ions are preferably
insoluble in the electrolyte. When the complexes between the
chelating agent and the transition metal ions are well soluble in
the electrolyte, the complexes can migrate to the anode and can be
reduced and deposited as transition metals on the surface of the
anode.
[0022] The chelating agent, which is contained in the inventive
electrolyte for lithium secondary batteries, can be at least one
selected from the group consisting of EDTA (ethylene diamine
tetraacetic acid), NTA (nitrilotriacetic acid), DCTA
(trans-1,2-diaminocyclohexanetetraacetic acid), DTPA
(diethylene-triaminepentaacetic acid), and EGTA (ethylene glycol
bis(2-aminoethyl ether)-N,N,N',N'-tetraacetic acid).
[0023] The chelating agent can be contained in an amount of 2 to
200 mM relative to the electrolyte. If the chelating agent is
contained in the electrolyte in an amount of less than 2 mM, it
will be insignificant with respect to the effects of forming
complexes by coordinate bonds between the chelating agent and the
transition metal ions and suppressing the side reaction in which
transition metals are deposited in the anode. On the other hand, if
the chelating agent is contained in an amount of more than 200 mM,
it will not have any further effect resulting from an increase in
the amount of use of the chelating agent.
[0024] The non-aqueous solvent, which is contained in the inventive
electrolyte for lithium secondary batteries, is not specifically
limited as long as it is generally used as a non-aqueous solvent
for non-aqueous electrolytes. Examples of the non-aqueous solvent,
which can be used in the present invention, include cyclic
carbonate, linear carbonate, lactone, ether, ester, and ketone.
[0025] Examples of the cyclic carbonate include ethylene carbonate
(EC), propylene carbonate (PC), and butylene carbonate (BC), and
examples of the linear carbonate include diethyl carbonate (DEC),
dimethyl carbonate (DMC), dipropyl carbonate (DPC), ethyl methyl
carbonate (EMC), and methyl propyl carbonate (MPC). Examples of the
lactone include gamma-butyrolactone (GBL), and examples of the
ether include dibutyl ether, tetrahydrofuran, 2-methyl
tetrahydrofuran, 1,4-dioxane, and 1,2-dimethoxyethane. Also,
examples of the ester include methyl acetate, ethyl acetate, methyl
propionate, and methyl pivalate, and examples of the ketone include
polymethylvinyl ketone. These non-aqueous solvents can be used
alone or in a mixture of two or more thereof.
[0026] The electrolyte salt, which is contained in the inventive
electrolyte for lithium secondary batteries, is not specifically
limited as long as it is generally used as an electrolyte salt for
non-aqueous electrolytes. Non-limiting examples of the electrolyte
salt include salts having a structure such as A.sup.+B.sup.-,
wherein A.sup.+ represents an alkali metal cation such as Li.sup.+,
Na.sup.+, K.sup.+, or a combination thereof, and B represents an
anion such as PF.sub.6.sup.-, BF.sub.4.sup.-, Cl.sup.-, Br.sup.-,
I.sup.-, ClO.sub.4.sup.-, AsF.sub.6.sup.-, CH.sub.3CO.sub.2.sup.-,
CF.sub.3SO.sub.3.sup.-, N(CF.sub.3SO.sub.2).sub.2.sup.-,
C(CF.sub.2SO.sub.2).sub.3.sup.-, or a combination thereof.
Particularly, a lithium salt is preferred. These electrolyte salts
can be used alone or in a mixture of two or more thereof.
[0027] The lithium secondary battery according to the present
invention can employ said electrolyte for lithium secondary
batteries. Specifically, the lithium secondary battery according to
the present invention can comprise a cathode; an anode; a
separator; and said electrolyte for lithium secondary
batteries.
[0028] The lithium secondary battery of the present invention can
be fabricated according to a conventional method known in the art
by interposing a porous separator between the cathode and the
anode, and placing said electrolyte into the resulting structure.
However, the method of fabricating the lithium secondary battery,
which can be used in the present invention, is not limited to any
particular method.
[0029] The cathode active material, which is used in the secondary
battery of the present invention, can consist of any one or a
mixture of two or more selected from among a variety of lithium
transition-metal composite oxides (e.g., lithium manganese
composite oxide, lithium nickel oxide, lithium cobalt oxide, and
the foregoing oxides wherein part of manganese, nickel and cobalt
is replaced with other transition metals and the like such as
LiCoO.sub.2, LiNiO.sub.2, LiMnO.sub.2, LiMn.sub.2O.sub.4,
Li(Ni.sub.aCO.sub.bMn.sub.c)O.sub.2 (0<a<1, 0<b<1,
0<c<1, a+b+c=1), LiNi.sub.1-YCO.sub.YO.sub.2,
LiCo.sub.1-YMn.sub.YO.sub.2, LiNi.sub.1-YMn.sub.YO.sub.2
(0.ltoreq.Y<1), Li(Ni.sub.aCo.sub.bMn.sub.c)O.sub.4
(0<a<2, 0<b<2, 0<c<2, a+b+c=2),
LiMn.sub.2-zNi.sub.zO.sub.4, LiMn.sub.2-zCo.sub.zO.sub.4
(0<Z<2), LiCoPO.sub.4 or LiFePO.sub.4, or a
lithium-containing vanadium oxide and the like), and chalcogen
compounds (such as manganese dioxide, titanium disulfide,
molybdenum disulfide and the like).
[0030] The anode active material, which can be used in the present
invention, can consist of a carbon material, a lithium metal or an
alloy thereof, which can absorb and release lithium ions. In
addition, it is possible to use a metal oxide such as TiO.sub.2 or
SnO.sub.2, which can absorb and release lithium ions and has a
potential of less than 2V for lithium. Particularly, a carbon
material such as graphite is preferred.
[0031] Although the porous separator, which can be used in the
present invention, is not limited to any particular separator, a
porous separator can be used, examples of which include
polypropylene-based, polyethylene-based, and polyolefin-based
porous separators.
[0032] In addition, although the shape of the lithium secondary
battery is not limited to any particular shape, it can have a
cylindrical shape, a prismatic shape, a pouch shape or a coin
shape.
[0033] Hereinafter, the present invention will be described in
further detail with reference to examples. It is to be understood,
however, that these examples are illustrative only, and the scope
of the present invention is not limited thereto.
EXAMPLE 1
Preparation of Electrolyte and Battery, Containing EDTA as
Chelating Agent
[0034] An electrolyte was prepared by dissolving LiPF.sub.6 in
ethylene carbonate (EC): ethyl methyl carbonate (EMC)=1:2(v/v) to a
concentration of 1M, and then adding each of Fe ions (FeCl.sub.3)
and EDTA as a chelating agent to a concentration of 50 mM.
[0035] A battery was fabricated by using a nitric acid-treated
silver wire as a reference electrode, a Pt wire as a counter
electrode, a copper foil as a working electrode, and the
above-prepared electrolyte as an electrolyte.
COMPARATIVE EXAMPLE 1
Preparation of Electrolyte and Battery Containing no Chelating
Agent
[0036] An electrolyte and a battery were prepared according to the
same method as Example 1, except that the chelating agent (EDTA)
was not added.
COMPARATIVE EXAMPLE 2
Preparation of Electrolyte and Battery Containing 18-crown-6 as
Chelating Agent
[0037] An electrolyte and a battery were prepared according to the
same method as Example 1, except that 18-crown-6 (crown ether) was
used instead of EDTA as a chelating agent.
COMPARATIVE EXAMPLE 3
Preparation of Electrolyte and Battery Containing
dibenzo-18-crown-6 as Chelating Agent
[0038] An electrolyte and a battery were prepared according to the
same method as Example 1, except that dibenzo-18-crown-6 (crown
ether) was used instead of EDTA as a chelating agent.
[0039] Experiment 1: Test of Fe Electroplating (Reduction of Fe
Ions)
[0040] In order to observe reactions in which Fe ions in the
electrolytes of batteries prepared in Example 1 and Comparative
Examples 1-3 are reduced on the surface of the anode,
electroplating experiments were carried out, and the experimental
results are shown in FIG. 1.
[0041] As can be seen in FIG. 1, in the case where crown ether was
used as the chelating agent, Fe ions reacted well with the crown
ether to form complexes, but it seems that the complexes were
dissolved well in the electrolyte due to the property of the crown
ether soluble in the organic solvent, so that they rather helped
the Fe ions migrate to the anode and were reduced on the surface of
the anode. As a result, this case was not different from the case
where the chelating agent was not used. However, in the case where
EDTA was used as the chelating agent, a reaction of less than 2V
with respect to Li/Li.sup.+ ions did not substantially appear,
suggesting that the EDTA effectively suppressed the reduction of Fe
ions.
EXAMPLES 2.about.5
Preparation of Electrolytes and Batteries Containing EDTA
[0042] Electrolytes and batteries were prepared according to the
same method as Example 1, except that EDTA was added in amounts of
2 mM, 5 mM, 10 mM and 200 mM, respectively.
[0043] Experiment 2: Reduction of Fe Ions at Varying EDTA
Concentrations
[0044] The reduction reactions of the batteries fabricated in
Examples 1-5 and Comparative Example 1 on the surface of a copper
foil and the amount of the resulting Fe electroplating were
measured, and the measurement results are shown in FIG. 2.
[0045] After Fe was electroplated while changing the amount of
EDTA, the amount of Fe on the copper foil was analyzed using ICP.
As a result, it could be seen that an increase in the amount of
EDTA led to a decrease in the amount of the plated Fe. The values
in brackets in FIG. 2 are the analyzed amounts of Fe, and it could
be seen that, even though the amount of EDTA in the electrolytes
was as low as ten times the amount of Fe ions, EDTA was
significantly effective in inhibiting the reduction of Fe ions.
EXAMPLE 6
Preparation of Electrolyte and Polymer Battery Containing EDTA
[0046] An electrolyte was prepared by adding EDTA to an electrolyte
(EC/EMC=1/2(v/v), 1M LiPF.sub.6) for use in cylindrical batteries
to a concentration of 2 mM.
[0047] A cathode slurry was prepared by mixing together 90 wt % of
LiCoO.sub.2 as a cathode active material, 5 wt % of acetylene black
as a conductive agent, and 5 wt % of PVDF as a binder, and then
adding the mixture to NMP (N-methyl-2-pyrrolidone). Then, the
cathode slurry was applied on an aluminum (Al) current collector
and dried, thus preparing a cathode.
[0048] An anode slurry was prepared by adding a mixture of 95 wt %
of graphite as an anode active material and 5 wt % of PVDF as a
binder to NMP. Then, the anode slurry was applied on a copper (Cu)
current collector and dried, thus preparing an anode.
[0049] A polyolefin-based separator was interposed between the
prepared cathode and anode, and then the electrolyte was injected
into the resulting structure, thus fabricating an ICP563443 polymer
battery (5.6 mm thick, 34 mm wide and 43 mm long) having a nominal
capacity of 900 mAh.
EXAMPLE 7
Preparation of Electrolyte and Polymer Battery Containing EDTA
[0050] An electrolyte and a polymer battery were prepared according
to the same method as Example 6, except that EDTA was added to a
concentration of 10 mM in the preparation of the electrolyte.
COMPARATIVE EXAMPLE 4
Preparation of Electrolyte and Polymer Battery Containing no
EDTA
[0051] An electrolyte and a polymer battery were prepared according
to Example 6, except that EDTA was not added in the preparation of
the electrolyte.
[0052] Experiment 3: Evaluation of High-Temperature Storage
Characteristics of Battery
[0053] Each of the batteries fabricated in Examples 6 and 7 and
Comparative Example 4 was fully charged to 4.2 V, and placed in a
constant-temperature chamber, in which the batteries were heated to
90.degree. C. over one hour, maintained at 90.degree. C. for 4
hours, cooled over one hour, and then maintained at room
temperature. During this process, a change in the thickness of each
of the batteries was measured, and the measurement results are
shown in FIG. 3.
[0054] The thickness of a battery during high-temperature generally
becomes thicker due to the generation of gas resulting from the
reaction of the electrolyte or the electrolyte additives on the
electrode surface. However, an increase in the generation of gas,
caused by the use of EDTA, could not be seen in the results of this
Experiment. In other words, it could be found that the batteries
containing EDTA and the battery containing no EDTA showed similar
changes in the thickness thereof, and thus deterioration in the
storage characteristics of the batteries caused by the use of EDTA,
did not occur.
[0055] Experiment 4: Evaluation of C-Rate Characteristics of
Batteries
[0056] The rate capabilities of the batteries fabricated in
Examples 6 and 7 and Comparative Example 4 were measured at a
charge condition of 0.5 C and varying discharge currents, and the
measurement results are shown in FIG. 4.
[0057] In the case where EDTA was added, some deterioration in the
performance of the batteries occurred at a high rate of 2 C, but
was insignificant, and also had little variation between the
batteries.
[0058] Experiment 5: Evaluation of Cycle Characteristics of
Batteries
[0059] The cycle characteristics of the batteries fabricated in
Examples 6 and 7 and Comparative Example 4 were tested, and the
experimental results are shown in FIG. 5.
[0060] As can be seen in FIG. 5, the batteries showed substantially
the same behavior regardless of the amount of EDTA in 0.5 C
charge/1 C discharge conditions and also showed good cycle
characteristics.
INDUSTRIAL APPLICABILITY
[0061] As can be seen from the foregoing, the chelating agent,
which is contained in the inventive electrolyte for lithium
secondary batteries, forms complexes with transition metal ions in
the battery and, at the same time, does not react and coordinate
with lithium ions, and thus can suppress a side reaction in which
transition metal ions are reduced and deposited as transition
metals on the anode. Also, the chelating agent can suppress
internal short-circuits in the battery and the resulting voltage
drop of the battery, and a reduction in the safety and performance
of the battery, which can occur when transition metals are
deposited on the anode.
[0062] Although the preferred embodiment of the present invention
has been described for illustrative purposes, those skilled in the
art will appreciate that various modifications, additions and
substitutions are possible, without departing from the scope and
spirit of the invention as disclosed in the accompanying
claims.
* * * * *