U.S. patent application number 12/118557 was filed with the patent office on 2009-12-31 for dye-sensitized solar cell and method of fabricating the same.
This patent application is currently assigned to Electronics and Telecommunications Research Institute. Invention is credited to Yong-Seok JUN, Man-Gu KANG, Jong-Dae KIM, Seung-Yup LEE, Hunkyun PAK, Jong-Hyeok PARK, Ho-Gyeong YUN.
Application Number | 20090320914 12/118557 |
Document ID | / |
Family ID | 40762757 |
Filed Date | 2009-12-31 |
United States Patent
Application |
20090320914 |
Kind Code |
A1 |
YUN; Ho-Gyeong ; et
al. |
December 31, 2009 |
DYE-SENSITIZED SOLAR CELL AND METHOD OF FABRICATING THE SAME
Abstract
Provided are a dye-sensitized solar cell and a method of
fabricating the same. The dye-sensitized solar cell includes an
electrode structure including a conductive layer having pores that
are regularly arranged, a semiconductor oxide layer disposed on a
surface of the conductive layer, and a dye layer disposed on a
surface of the semiconductor oxide layer.
Inventors: |
YUN; Ho-Gyeong; (Seoul,
KR) ; JUN; Yong-Seok; (Daejeon, KR) ; KANG;
Man-Gu; (Daejeon, KR) ; LEE; Seung-Yup;
(Gyeongsan-si, KR) ; PAK; Hunkyun; (Daejeon,
KR) ; PARK; Jong-Hyeok; (Daejeon, KR) ; KIM;
Jong-Dae; (Daejeon, KR) |
Correspondence
Address: |
RABIN & Berdo, PC
1101 14TH STREET, NW, SUITE 500
WASHINGTON
DC
20005
US
|
Assignee: |
Electronics and Telecommunications
Research Institute
Daejeon
KR
|
Family ID: |
40762757 |
Appl. No.: |
12/118557 |
Filed: |
May 9, 2008 |
Current U.S.
Class: |
136/255 ;
136/256; 257/E21.461; 257/E31.015; 438/85 |
Current CPC
Class: |
Y02E 10/542 20130101;
H01G 9/209 20130101; H01L 31/18 20130101; H01G 9/2031 20130101;
Y02P 70/50 20151101; H01G 9/2059 20130101; Y02P 70/521
20151101 |
Class at
Publication: |
136/255 ;
136/256; 438/85; 257/E21.461; 257/E31.015 |
International
Class: |
H01L 31/00 20060101
H01L031/00; H01L 31/18 20060101 H01L031/18 |
Foreign Application Data
Date |
Code |
Application Number |
Oct 16, 2007 |
KR |
10-2007-0104023 |
Claims
1. A dye-sensitized solar cell comprising: an electrode structure
including: a conductive layer including pores which are regularly
arranged; a semiconductor oxide layer disposed on a surface of the
conductive layer; and a dye layer disposed on a surface of the
semiconductor oxide layer.
2. The dye-sensitized solar cell of claim 1, wherein the conductive
layer comprises at least one selected from the group consisting of
tin oxide, indium doped tin oxide, antimony doped tin oxide,
fluorine doped tin oxide, metal, conductive polymer and a nano
carbon material.
3. The dye-sensitized solar cell of claim 1, wherein the
semiconductor oxide layer comprises at least one selected from the
group consisting of zinc oxide, tin oxide and titanium oxide.
4. A method of fabricating a dye-sensitized solar cell, the method
comprising: forming an electrode structure including: preparing a
template having pores that are regularly arranged; forming a
conductive layer on a surface of the template; forming a
semiconductor oxide layer on a surface of the conductive layer; and
forming a dye layer on a surface of the semiconductor oxide
layer.
5. The method of claim 4, further comprising removing the
template.
6. The method of claim 5, wherein the template is formed of at
least one material selected from the group consisting of
polystyrene, poly methyl methacrylate (PMMA) and block
co-polymer.
7. The method of claim 6, wherein the template is burn out and
removed during a thermal treatment of forming the electrode
structure.
8. The method of claim 5, wherein the template is formed of
alumina.
9. The method of claim 4, wherein the conductive layer is formed of
at least one selected from the group consisting of tin oxide,
indium doped tin oxide, antimony doped tin oxide, fluorine doped
tin oxide, metal, conductive polymer and a nano carbon
material.
10. The method of claim 4, wherein the forming of the semiconductor
oxide layer is performed using at least one method selected from
the group consisting of a deep coating method, an electrophoretic
method, and an electroplating method.
11. The method of claim 10, wherein the semiconductor oxide layer
comprises at least one selected from the group consisting of zinc
oxide, tin oxide and titanium oxide.
12. The method of claim 4, wherein the forming of the semiconductor
oxide layer comprises anodizing or thermally oxidizing a metal or a
metal precursor.
13. The method of claim 12, wherein the semiconductor oxide layer
comprises at least one selected from the group consisting of zinc
oxide, tin oxide and titanium oxide.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This U.S. non-provisional patent application claims priority
under 35 U.S.C. .sctn. 119 of Korean Patent Application No.
10-2007-104023, filed on Oct. 16, 2007, the entire contents of
which are hereby incorporated by reference.
BACKGROUND OF THE INVENTION
[0002] The present invention disclosed herein relates to a
dye-sensitized solar cell and a method of fabricating the same, and
more particularly, to a dye-sensitized solar cell including an
electrode structure having a conductor with pores regularly formed,
which is fabricated by the use of a template, and a method of
fabricating the dye-sensitized solar cell.
[0003] The present invention has been derived from research
undertaken as a part of IT R & D program of the Ministry of
Information and Communication and Institution of Information
Technology Association (MIC/IITA) [2006-S-006-02],
Components/Module technology for ubiquitous terminals.
[0004] A dye-sensitized solar cell includes a dye molecule capable
of receiving incident light with a visible wavelength to form
electron-hole pairs, a semiconductor oxide capable of receiving
excited electrons, and an electrolyte reacting with the electrons
after working and returning to the solar cell, which significantly
differs from a compound solar cell or a wafer type silicon solar
cell using p-n junction.
[0005] A dye-sensitized solar cell, which has been well known
hitherto, was published by Michael Gratzel et al. (refer to U.S.
Pat. No. 4,927,721). A photoelectrochemical solar cell published by
Michael Gratzel et al. includes a photosensitive dye molecule
capable of absorbing a visible light to generate electron-hole
pairs, an electrode structure which is a semiconductor oxide formed
of nanoparticle titanium oxide (TiO.sub.2) with dye molecules
adsorbed, an opposite electrode coated with platinum (Pt) or carbon
(C), and an electrolyte filled between the semiconductor oxide and
the opposite electrode. Because such the photoelectrochemical solar
cell can be fabricated with low fabrication cost per electrical
power in comparison with the wafer type silicon solar cell that
utilizes a p-n junction, so the photoelectrochemical solar cell is
being in the limelight recently.
[0006] FIG. 1 is a partial sectional view illustrating a flow of
electrons created by sunlight in a conventional dye-sensitized
solar cell.
[0007] Referring to FIG. 1, dye molecules excited by light emitted
from the sun eject electrons (e-) into a conduction band of a
semiconductor oxide layer 20 formed of nanoparticle titanium oxide.
The electrons ejected into the conduction band pass through the
nanoparticle titanium oxide and arrive at a conductive substrate 10
formed of a glass coated with fluorine doped SnO.sub.2 (FTO).
Thereafter, the electrons are transferred to an external circuit
(not shown). The electrons, which come back after performing an
electrical work in the external circuit, are injected into the
semiconductor oxide layer 20 formed of nanoparticle semiconductor
oxide through an opposite electrode (not shown), e.g., platinum or
carbon electrode, by means of the electron transfer function of an
oxidation/reduction electrolyte 30. Finally, the electrons reduce
the dye molecule 24 deficient in electrons. In this manner, the
conventional dye-sensitized solar cell is operated.
[0008] However, before the electrons injected into the
semiconductor oxide layer 20 made of nanoparticle titanium oxide
from the dye molecule 24 are transferred to the external circuit
and perform an electrical work therein, some of the electrons
injected into the conduction band stay in an unoccupied surface
energy level of the semiconductor oxide layer 20 on which the dye
molecule 24 is not adsorbed while passing through the semiconductor
oxide layer 20 and the conductive substrate 10. At this time the
electron and the electrolyte 30 are recombined so that the
electrons do not circulate in a circuit but vanished ineffectively.
Accordingly, there is a loss in photovoltaic energy conversion
efficiency.
[0009] Furthermore, in the dye-sensitized solar cell proposed by
Michael Gratzel et al. where the semiconductor oxide layer is used
as the electrode structure, a moving passage through which the
electrons injected from the dye molecules to the semiconductor
oxide layer move to the conductive substrate is also made of the
nanoparticle titanium oxide. Accordingly, the electron encounters a
strong electrical resistance while the electron moves to a
3-dimensional structured semiconductor oxide layer, leading to a
decrease in short-circuit current density (Jsc). Resultingly, since
the photovoltaic energy conversion efficiency is determined by
multiplication of a current, a voltage and a fill factor of the
solar cell, the current, the voltage and the fill factor should be
improved to increase the photovoltaic energy conversion efficiency.
Particularly, to increase the voltage significantly, there is a
method of increasing the electron density of the nanoparticle
semiconductor oxide by minimizing the recombination with the
electrons.
[0010] Example of a conventional method of minimizing the decrease
of the photovoltaic energy conversion efficiency occurring in the
semiconductor oxide, e.g., the titanium oxide, is as followings. In
the conventional method, the semiconductor oxide formed of the
titanium oxide is used as the electrode structure, and coated with
a semiconductor oxide material having high band gap energy, for
example, niobium oxide (Nb.sub.2O.sub.5) to form an energy barrier
between the semiconductor oxide layer and the electrolyte, thus
preventing the recombination. According to the conventional method,
the photovoltaic energy conversion efficiency was somewhat
enhanced. However, because the titanium oxide is basically used as
a material for the electrode structure, there is a limitation in
electron movement. Therefore, an increase in the photovoltaic
energy conversion efficiency was limited. Adsorptive properties of
the dye molecule on the niobium oxide are poorer than that of the
dye molecule on the titanium oxide.
[0011] As another conventional method, there has been an attempt to
employ a nanowire-shaped semiconductor oxide as the electrode
structure. However, unlike the expectation that the nanowire-shaped
semiconductor oxide could increase the photovoltaic energy
conversion efficiency because the nanowire itself is a single
crystal and thus advantageous for electron diffusion, the electrode
structure made of nanowire-, nanorod- and nanotube-shaped
semiconductor oxide exhibits poorer photovoltaic energy conversion
efficiency compared to the case of using the nanoparticle
semiconductor oxide as the electrode structure. Possibly, this is
ascribed to the fact that the electrode structure made of the
nanowire-, nanorod- and nanotube-shaped semiconductor oxide has a
smaller surface area than the nanoparticle semiconductor oxide. In
addition to the aforesaid conventional methods, there have been
attempts to form the electrode structure using a semiconductor
oxide of zinc oxide (ZnO) or tin oxide instead of the titanium
oxide. However, the solar cell achieved by this conventional method
still exhibits a poorer photovoltaic energy conversion efficiency
compared to the solar cell using the titanium oxide for the
electrode structure.
SUMMARY OF THE INVENTION
[0012] The present invention provides a dye-sensitized solar cell
capable of maximizing photovoltaic energy conversion
efficiency.
[0013] The present invention also provides a method of fabricating
a dye-sensitized solar cell capable of maximizing photovoltaic
energy conversion efficiency.
[0014] Embodiments of the present invention provide dye-sensitized
solar cells including: an electrode structure including a
conductive layer including pores which are regularly arranged; a
semiconductor oxide layer disposed on a surface of the conductive
layer; and a dye layer disposed on a surface of the semiconductor
oxide layer.
[0015] In some embodiments, the conductive layer includes at least
one selected from the group consisting of tin oxide, indium doped
tin oxide, antimony doped tin oxide, fluorine doped tin oxide,
metal, conductive polymer and a nano carbon material.
[0016] In other embodiments, the semiconductor oxide layer includes
at least one selected from the group consisting of zinc oxide, tin
oxide and titanium oxide.
[0017] In still other embodiments, the dye-sensitized solar cells
further include: a bottom electrode structure disposed one side of
the electrode structure, and contacting the electrode structure; a
top electrode structure disposed on the other side of the electrode
structure; and an electrolyte layer interposed between the
electrode structure and the top electrode structure, and filling
the pores.
[0018] In even other embodiments, the dye-sensitized solar cells
further include a catalyst layer interposed between the electrode
structure and the electrolyte layer. Herein, the catalyst layer
includes platinum or carbon.
[0019] In yet other embodiments, the electrolyte has one state of
liquid, solid and gel.
[0020] In further embodiments of the present invention, methods of
fabricating a dye-sensitized solar cell include: forming an
electrode structure including: preparing a template having pores
that are regularly arranged; forming a conductive layer on a
surface of the template; forming a semiconductor oxide layer on a
surface of the conductive layer; and forming a dye layer on a
surface of the semiconductor oxide layer.
[0021] In still further embodiments, the methods further include
removing the template.
[0022] In even further embodiments, the template is formed of at
least one material selected from the group consisting of
polystyrene, poly methyl methacrylate (PMMA) and block co-polymer.
Here, the template is burn out and removed during a thermal
treatment of forming the electrode structure.
[0023] In yet further embodiments, the template is formed of
alumina. In this case, the template is removed after formation of
the electrode structure.
[0024] In other embodiments, the conductive layer is formed of at
least one selected from the group consisting of tin oxide, indium
doped tin oxide, antimony doped tin oxide, fluorine doped tin
oxide, metal, conductive polymer and a nano carbon material.
[0025] In still other embodiments, the forming of the semiconductor
oxide layer is performed using at least one method selected from
the group consisting of a deep coating method, an electrophoretic
method, and an electroplating method.
[0026] In even other embodiments, the forming of the semiconductor
oxide layer includes anodizing or thermally oxidizing a metal or a
metal precursor.
[0027] In yet other embodiments, the semiconductor oxide layer
includes at least one selected from the group consisting of zinc
oxide, tin oxide and titanium oxide.
[0028] According to the present invention, a dye-sensitized solar
cell includes an electrode structure having pores regularly
arranged, thus making it possible to minimize the recombination due
to oxidation/reduction reaction occurring at a boundary between the
electrode structure and an electrolyte. Furthermore, it is possible
to minimize a moving passage of an electron in the electrode
structure. Consequently, the dye-sensitized solar cell can maximize
its photovoltaic energy conversion efficiency.
BRIEF DESCRIPTION OF THE FIGURES
[0029] The accompanying figures are included to provide a further
understanding of the present invention, and are incorporated in and
constitute a part of this specification. The drawings illustrate
exemplary embodiments of the present invention and, together with
the description, serve to explain principles of the present
invention. In the figures:
[0030] FIG. 1 is a partial sectional view illustrating a flow of
electrons created by sunlight in a conventional dye-sensitized
solar cell;
[0031] FIG. 2 is a plan view illustrating an electrode structure of
a dye-sensitized solar cell and a method of fabricating the same
according to an embodiment of the present invention;
[0032] FIG. 3 is a sectional view illustrating a dye-sensitized
solar cell and a method of fabricating the same according to an
embodiment of the present invention; and
[0033] FIG. 4 is a partial sectional view illustrating a flow of
electrons created by sunlight in the dye-sensitized solar cell
according to the embodiment of the present invention.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
[0034] Preferred embodiments of the present invention will be
described below in more detail with reference to the accompanying
drawings. The present invention may, however, be embodied in
different forms and should not be construed as limited to the
embodiments set forth herein. Rather, these embodiments are
provided so that this disclosure will be thorough and complete, and
will fully convey the scope of the present invention to those
skilled in the art. In the figures, the dimensions of layers and
regions are exaggerated for clarity of illustration. It will also
be understood that when a layer (or film) is referred to as being
`on` another layer or substrate, it can be directly on the other
layer or substrate, or intervening layers may also be present.
Further, it will be understood that when a layer is referred to as
being `under` another layer, it can be directly under, and one or
more intervening layers may also be present. In addition, it will
also be understood that when a layer is referred to as being
`between` two layers, it can be the only layer between the two
layers, or one or more intervening layers may also be present. Like
reference numerals refer to like elements throughout.
[0035] Hereinafter, an exemplary embodiment of the present
invention will be described with the accompanying drawings.
[0036] FIG. 2 is a plan view illustrating an electrode structure of
a dye-sensitized solar cell and a method of fabricating the same
according to an embodiment of the present invention.
[0037] Referring to FIG. 2, the electrode structure of the
dye-sensitized solar cell may include a conductive layer 120, a
semiconductor oxide layer 122 and a dye layer 124.
[0038] The conductive layer 120 may have pores that are regularly
arranged. The conductive layer 120 may be formed by coating a
surface of a template (not shown) having pores regularly arranged
with a transparent and conductive material. The conductive material
contained in the conductive layer 120 may include at least one
material selected from the group consisting of tin oxide
(SnO.sub.2), indium doped tin oxide (ITO), antimony doped tin oxide
(ATO), fluorine doped tin oxide (FTO), metal, conductive polymer
and a nano carbon material. Preferably, the conductive layer 120
may be formed of tin oxide.
[0039] The template used to form the conductive layer 120 having
pores regularly arranged may have a shape that allows a surface
area of the electrode structure to be maximized, for example, a
honeycomb, nanowire, nanorod, or nanotube shape. The template may
include at least one material selected from the group consisting of
polystyrene, poly methyl methacrylate (PMMA), block co-polymer and
alumina.
[0040] The semiconductor oxide layer 122 may be formed on a surface
of the conductive layer 120. The semiconductor oxide layer 122 may
be formed using one method selected from the group consisting of a
deep coating method, an electrophoretic method, and an
electroplating method. In addition, the semiconductor oxide layer
122 may be formed by anodizing or thermally oxidizing a metal or a
metal precursor. The semiconductor oxide layer 122 may include at
least one selected from the group consisting of zinc oxide, tin
oxide and titanium oxide. Preferably, the semiconductor oxide layer
122 may include titanium oxide.
[0041] The dye layer 124 may be formed on a surface of the
semiconductor oxide layer 122. The dye layer 124 may be formed by
adsorbing dye molecules on the semiconductor oxide layer 122.
Accordingly, it is possible to form the electrode structure having
pores regularly arranged.
[0042] In the case of using an organic-based template such as
polystyrene, PMMA and block co-polymer, the template may be burn
out and removed during a thermal treatment process of forming the
electrode structure. In contrast, in the case of using an
inorganic-based template such as alumina, the template may be
removed after the formation of the electrode structure. This is
because the inorganic-based template is not sintered during the
thermal process of forming the electrode structure.
[0043] The conductive layer 120 has regularly arranged pores and
thus high porosity, which may make it easy to thickly coat the
surface of the conductive layer 120 with the semiconductor oxide
layer 122. Because the conductive layer 120 is spaced apart from
the semiconductor oxide layer 122 by merely several nanometers, the
thickness of the electrode structure may be increased up to a
distance that light can reach. As the thickness of the electrode
structure becomes greater, the short-circuit current density
becomes higher. That is, the semiconductor oxide layer 122 may
serve as an energy barrier prohibiting the recombination of
electrons and holes between the electrolyte 130 and the conductive
layer 120. Therefore, the photovoltaic energy conversion efficiency
of the dye-sensitized solar cell can be remarkably increased.
[0044] The electrode structure of the dye-sensitized solar cell
having the above-described structure has regularly arranged pores,
thus minimizing the recombination due to oxidation/reduction
reaction occurring at a boundary between the electrode structure
and the electrolyte. Moreover, the moving passage of electrons can
be minimized in the electrode structure.
[0045] FIG. 3 is a sectional view illustrating a dye-sensitized
solar cell and a method of fabricating the same according to an
embodiment of the present invention.
[0046] Referring to FIG. 3, a dye-sensitized solar cell may include
a bottom electrode structure 110, an electrode structure having a
conductive layer 120, a semiconductor oxide layer 122 and a dye
layer 124, an electrolyte layer 130 and a top electrode structure
140.
[0047] The bottom electrode structure 110 may include a transparent
substrate with conductivity or a transparent substrate of which one
side is coated with a conductive material. The electrode structure
may be formed to contact the conductive side of the bottom
electrode structure 110.
[0048] The electrolyte layer 130 is interposed between the
electrode structure and the top electrode structure 140, and fills
the pores of the electrode structure. The electrolyte layer 130 has
one state of liquid, solid and gel. Preferably, the electrolyte
layer 130 may include I.sub.3.sup.-/I.sup.--based electrolyte.
[0049] The top electrode structure 140 may include a transparent
substrate with conductivity or a transparent substrate of which one
side is coated with conductive material. The conductive one side of
the top electrode structure 140 may be formed to contact the
electrolyte layer 130. The dye-sensitized solar cell may further
include a catalyst layer 142 interposed between the electrolyte 130
and the top electrode structure 140. The catalyst layer 142 may
include platinum or carbon. Accordingly, it may be possible to form
the dye-sensitized solar cell including the electrode structure
having the pores regularly arranged.
[0050] Because the dye-sensitized solar cell includes the electrode
structure having the pores regularly arranged, thus making it
possible to minimize the recombination due to oxidation/reduction
reaction occurring at a boundary between the electrode structure
and the electrolyte. Furthermore, it may be possible to minimize a
moving passage of an electron in the electrode structure.
[0051] FIG. 4 is a partial sectional view illustrating a flow of an
electron created by sunlight in the dye-sensitized solar cell
according to the embodiment of the present invention.
[0052] Referring to FIG. 4, because electrons (e-) transferred from
the dye layer 124 to the conductive layer 120 move to the bottom
electrode structure 110 through the honeycombed conductive layer
120 in the electrode structure of the dye-sensitized solar cell,
the moving passage of the electrons may be minimized to a length of
several nanometers to several tens of nanometers. The semiconductor
oxide layer 122 between the dye layer 124 and the conductive layer
120 may serve as an energy barrier prohibiting the electrons
transferred to the conductive layer 120 from reacting with the
electrolyte layer 130 again. Consequently, the photovoltaic energy
conversion efficiency may be maximized.
[0053] As described above, according to the present invention, a
dye-sensitized solar cell includes an electrode structure having
pores regularly arranged, thus making it possible to minimize the
recombination due to oxidation/reduction reaction occurring at a
boundary between the electrode structure and an electrolyte.
Furthermore, it is possible to minimize a moving passage of an
electron in the electrode structure. Consequently, the
dye-sensitized solar cell can maximize its photovoltaic energy
conversion efficiency.
[0054] The above-disclosed subject matter is to be considered
illustrative, and not restrictive, and the appended claims are
intended to cover all such modifications, enhancements, and other
embodiments, which fall within the true spirit and scope of the
present invention. Thus, to the maximum extent allowed by law, the
scope of the present invention is to be determined by the broadest
permissible interpretation of the following claims and their
equivalents, and shall not be restricted or limited by the
foregoing detailed description.
* * * * *