U.S. patent application number 12/080647 was filed with the patent office on 2009-10-08 for methods for placement of sealant in subterranean intervals.
This patent application is currently assigned to Halliburton Energy Services, Inc.. Invention is credited to Eldon D. Dalrymple, Larry S. Eoff, Julio E. Vasquez.
Application Number | 20090253594 12/080647 |
Document ID | / |
Family ID | 40957807 |
Filed Date | 2009-10-08 |
United States Patent
Application |
20090253594 |
Kind Code |
A1 |
Dalrymple; Eldon D. ; et
al. |
October 8, 2009 |
Methods for placement of sealant in subterranean intervals
Abstract
Of the many methods provided herein, one method includes a
method of treating an interval of a subterranean formation having a
permeability that varies comprising: identifying the interval to be
treated; introducing a relative-permeability modifier into the
interval, wherein the relative-permeability modifier modifies the
interval to have a more uniform effective permeability to water,
wherein the relative permeability modifier comprises a
water-soluble polymer; and introducing a sealant into the interval,
wherein the more uniform effective permeability of the interval
allows for a more uniform treatment of the interval by the than
would be allowed without treatment of the interval with the
relative-permeability modifier.
Inventors: |
Dalrymple; Eldon D.;
(Duncan, OK) ; Vasquez; Julio E.; (Norman, OK)
; Eoff; Larry S.; (Duncan, OK) |
Correspondence
Address: |
ROBERT A. KENT
P.O. BOX 1431
DUNCAN
OK
73536
US
|
Assignee: |
Halliburton Energy Services,
Inc.
|
Family ID: |
40957807 |
Appl. No.: |
12/080647 |
Filed: |
April 4, 2008 |
Current U.S.
Class: |
507/222 |
Current CPC
Class: |
C09K 8/514 20130101;
C09K 8/512 20130101; E21B 33/138 20130101 |
Class at
Publication: |
507/222 |
International
Class: |
C09K 8/58 20060101
C09K008/58 |
Claims
1. A method of treating an interval of a subterranean formation
having a permeability that varies, the method comprising:
identifying the interval to be treated and introducing a sealant
composition that comprises a relative-permeability modifier into
the interval, wherein the relative-permeability modifier modifies
the interval to have a more uniform effective permeability to
water-based fluids, wherein the relative-permeability modifier
comprises a water-soluble polymer, and wherein the more uniform
effective permeability of the interval allows for a more uniform
treatment of the interval by the sealant composition than would be
allowed without treatment of the interval with the
relative-permeability modifier.
2. The method of claim 1, wherein the interval comprises a first
portion and a second portion; wherein, prior to contacting the
interval with the relative-permeability modifier, the first portion
has a first water permeability and the second portion has a second
water permeability; and wherein, after contacting the interval with
the relative-permeability modifier, the first portion and the
second portion have about the same permeability.
3. The method of claim 1, wherein, after contacting the interval
with the relative-permeability modifier, the effective permeability
of the interval to water varies by up to about 40%.
4. The method of claim 1, wherein the water-soluble polymer
comprises a polymer containing a backbone, the backbone comprising
polar heteroatoms.
5. The method of claim 1, wherein the water-soluble polymer
comprises a polymer that has been hydrophobically modified with an
alkyl group with 4 carbons to 22 carbons present on an amino group
in quaternized form.
6. The method of claim 5, wherein the alkyl group has from 12
carbons to 18 carbons.
7. The method of claim 5, wherein the amino group comprises a
dialkyl amino pendant group.
8. The method of claim 5, wherein the amino group comprises a
dimethyl amino pendant group.
9. The method of claim 1, wherein the water-soluble polymer
comprises a polydimethylaminoethylmethacrylate or
polydimethylaminopropylmethacrylamide, wherein either the
polydimethylaminoethylmethacrylate or
polydimethylaminopropylmethacrylamide has been hydrophobically
modified with an alkyl group with 4 carbons to 22 carbons on a
dimethylamino group present therein.
10. The method of claim 1, wherein the water-soluble polymer
comprises an amino methacrylate/alkyl amino methacrylate
copolymer.
11. The method of claim 1, wherein the water-soluble polymer
comprises a hydrophobically modified polymer, the hydrophobically
modified polymer comprises a polymer backbone and a hydrophobic
branch, the hydrophobic branch comprising an alkyl chain of from
about 4 to about 22 carbons.
12. The method of claim 1, wherein the water-soluble polymer
comprises a hydrophobically modified polymer.
13. The method of claim 1, wherein the water-soluble polymer
comprises a hydrophilically modified polymer.
14. The method of claim 1, wherein the sealant composition
comprises a gelable aqueous silicate composition, wherein the
gelable aqueous silicate composition comprises water, an alkali
metal silicate solution, and a catalyst.
15. The method of claim 1, wherein the sealant composition
comprises a crosslinkable aqueous polymer composition, wherein the
crosslinkable aqueous polymer composition comprises water, a
crosslinkable polymer, and a crosslinking agent.
16. The method of claim 1, wherein the sealant composition
comprises a polymerizable organic monomer composition, wherein the
polymerizable organic monomer composition comprises water, a
water-soluble polymerizable organic monomer, an oxygen scavenger,
and a primary initiator.
17. The method of claim 1, wherein the sealant composition
comprises a resin.
18. The method of claim 1, comprising shutting in a well bore
penetrating the subterranean formation, after the step of
introducing the sealant composition into the interval.
19. The method of claim 1, wherein an elbow or a junction of a
multi-lateral well bore is present in the interval.
20. The method of claim 1, wherein the interval comprises a
water-producing interval of the subterranean formation.
21. (canceled)
22. A method of treating an interval of a subterranean formation
having a permeability that varies, the method comprising:
identifying the interval to be treated; introducing a
relative-permeability modifier into the interval, wherein the
relative-permeability modifier modifies the interval to have a more
uniform effective permeability to water-based fluids, wherein the
relative-permeability modifier is water soluble and comprises a
polymer that has been hydrophobically modified with an alkyl group
with 4 carbons to 22 carbons present on an amino group in
quaternized form; monitoring the pressure of the interval;
adjusting the introducing of the relative permeability modifier
into the interval based at least partially on the monitored
pressure so that the interval retains a water permeability
sufficient to allow injection of water at a rate of about 1/4
barrel per minute at a differential pressure no more than 90% of a
fracture gradient of the interval; and introducing an aqueous-based
sealant into the interval, wherein the more uniform effective
permeability of the interval allows for a more uniform treatment of
the interval by the aqueous-based sealant than would be allowed
without treatment of the interval with the relative-permeability
modifier.
23. The method of claim 22, wherein the alkyl group has from 12
carbons to 18 carbons.
24. The method of claim 22, wherein the amino group comprises a
dialkyl amino pendant group.
25. The method of claim 22, wherein the polymer that has been
hydrophobically modified present in the relative permeability
modified comprises a polydimethylaminoethylmethacrylate or
polydimethylaminopropylmethacrylamide.
Description
BACKGROUND
[0001] The present invention relates to subterranean treatments
and, more particularly, in one or more embodiments, to introducing
a relative-permeability modifier into a subterranean interval ahead
of, or in conjunction with, a sealant.
[0002] In subterranean treatments, it is often desired to treat an
interval of a subterranean formation having sections of varying
permeability. Consequently, it may be difficult to obtain a uniform
distribution of the treatment fluid throughout the entire interval.
For instance, the treatment fluid may preferentially enter portions
of the interval with high permeability at the expense of portions
of the interval with lesser permeability. In some instances, these
intervals with variable permeability may be water-producing
intervals. In other instance, the portion of an interval with high
permeability may be an elbow or turn in a well bore, into which the
treatment fluid may preferentially enter. In yet another
embodiment, the portion of an interval with high permeability may
be a junction of a multi-lateral well, into which the treatment
fluid may preferentially enter.
[0003] In an attempt to facilitate the uniform distribution of
sealants throughout an entire interval, a variety of techniques
have been used to divert the sealant to less permeable portions of
the interval. For example, when the goal is to seal inflow from a
long interval with multiple sections of varying permeability,
sealants may be placed using packers or other such devices to focus
the sealant into target intervals to help insure that the sealant
does not travel into only the sections with relatively high
permeability. Other such techniques may have involved, among other
things, the injection of particulates, foams, or blocking polymers
(e.g., crosslinked aqueous gels) into the interval so as to plug
off the high-permeability portions of the subterranean formation,
thereby diverting subsequently injected fluids to less permeable
portions of the subterranean formation. While each of these
diversion techniques has been used successfully, there may be
disadvantages. Plugging off the high-permeability sections may not
be suitable for a producing interval, for example, because the
injected solution (or material) may reduce or stop the flow of
hydrocarbons in addition to the achieving a desired diversion of
the treatment fluid. Therefore, to return the interval to
production, expensive and/or time-consuming remedial treatments may
be required to remove the injected solutions (or materials).
Furthermore, techniques geared toward injecting solutions (or
materials) designed to plug off high-permeability intervals of the
formation may require expensive zonal isolation, which may be
inaccurate, leading to inadvertent plugging of and/or damage to the
hydrocarbon-bearing sections.
SUMMARY
[0004] The present invention relates to subterranean treatments
and, more particularly, in one or more embodiments, to introducing
a relative-permeability modifier into a subterranean interval ahead
of, or in conjunction with, a sealant.
[0005] In one embodiment, the present invention provides a method
of treating an interval of a subterranean formation having a
permeability that varies comprising: identifying the interval to be
treated; introducing a relative-permeability modifier into the
interval, wherein the relative-permeability modifier modifies the
interval to have a more uniform effective permeability to
water-based fluids, wherein the relative-permeability modified
comprises a water-soluble polymer; and introducing a sealant into
the interval, wherein the more uniform effective permeability of
the interval allows for a more uniform treatment of the interval by
the sealant than would be allowed without treatment of the interval
with the relative-permeability modifier.
[0006] In one embodiment, the present invention provides a method
of treating an interval of a subterranean formation having a
permeability that varies, the method comprising: identifying the
interval to be treated; introducing a relative-permeability
modifier into the interval, wherein the relative-permeability
modifier modifies the interval to have a more uniform effective
permeability to water-based fluids, wherein the
relative-permeability modifier is water soluble and comprises a
polymer that has been hydrophobically modified with an alkyl group
with 4 carbons to 22 carbons present on an amino group in
quaternized form; monitoring the pressure of the interval;
adjusting the introducing of the relative permeability modifier
into the interval based at least partially on the monitored
pressure so that the interval retains a water permeability
sufficient to allow injection of water at a rate of about 1/4
barrel per minute at a differential pressure no more than 90% of a
fracture gradient of the interval; and introducing an aqueous-based
sealant into the interval, wherein the more uniform effective
permeability of the interval allows for a more uniform treatment of
the interval by the aqueous-based sealant than would be allowed
without treatment of the interval with the relative-permeability
modifier.
[0007] The features and advantages of the present invention will be
readily apparent to those skilled in the art. While numerous
changes may be made by those skilled in the art, such changes are
within the spirit of the invention.
BRIEF DESCRIPTION OF THE DRAWINGS
[0008] These drawings illustrate certain aspects of some of the
embodiments of the present invention, and should not be used to
limit or define the invention.
[0009] FIG. 1 is a cross-sectional, side view of a well bore
penetrating an interval of a subterranean formation.
[0010] FIG. 2 is a cross-sectional, side view of a well bore
penetrating an interval of a subterranean formation showing the
introduction of a fluid comprising a relative-permeability modifier
into the well bore of FIG. 1, in accordance with one embodiment of
the present invention.
[0011] FIG. 3 is a cross-sectional, side view of a well bore
penetrating an interval of a subterranean formation showing the
introduction of an aqueous-based sealant into the well bore of FIG.
1, in accordance with one embodiment of the present invention.
DESCRIPTION OF PREFERRED EMBODIMENTS
[0012] The present invention relates to subterranean treatments
and, more particularly, in one or more embodiments, to introducing
a relative-permeability modifier into a subterranean interval ahead
of, or in conjunction with, a sealant.
[0013] Embodiments of the present invention relate to using a
relative-permeability modifier (e.g., water-soluble hydrophobically
modified polymers) as a pre-flush to treat an interval of a
subterranean formation having variable permeabilities prior to
injection of a sealant. As used in this disclosure, the term
"relative-permeability modifier" refers to a polymer that
selectively reduces the effective permeability of a subterranean
formation to water-based fluids. In general, the
relative-permeability modifier should be used to modify the
interval to have a more uniform effective permeability than prior
to the treatment. Modification of the interval to have a more
uniform effective permeability should facilitate uniform treatment
of the interval with the sealant. As the interval has been modified
to have a more uniform effective permeability, a more uniform
distribution of sealant introduced into the interval should be
obtained than would otherwise be achieved without this permeability
modification. Otherwise, the sealant may preferentially enter
portions of the interval with high permeability at the expense of
portions of the interval with lesser permeability. As desired,
embodiments of the present inventions use of the
relative-permeability modifiers generally may, for example,
alleviate the necessity of using packers or other such mechanisms
to focus the sealant into target areas.
I. Example Methods
Treatment of Formation Interval
[0014] Turning to the drawings and referring first to FIG. 1, a
well bore 10 is shown that penetrates an interval 12 of a
subterranean formation. The interval 12 represents an interval that
has been identified for treatment with a sealant in accordance with
present embodiments. As will be appreciated by those of ordinary
skill in the art, with the benefit of this disclosure, the interval
12 may be any interval of a subterranean formation suitable for
treatment. For example, a water-producing interval of a
subterranean formation may be identified for treatment with the
aqueous-based sealant. By way of further example, an elbow or turn
in the well bore 10 may be identified as an interval for treatment
with a sealant. By way of further example, a junction of a
multi-lateral well bore the interval 12 may be identified as an
interval for treatment with a sealant. Even though FIG. 1 depicts
the well bore 10 as a vertical well bore, the methods of certain
embodiments may be suitable for use in generally horizontal,
generally vertical, or otherwise formed portions of wells.
Moreover, as those of ordinary skill in the art will appreciate,
with the benefit of this disclosure, embodiments of the present
invention may be applicable for the treatment of both production
and injection wells. Additionally, while the well bore 10 is
illustrated as an openhole well bore, embodiments of the present
invention also may be suitable for cased well bores.
[0015] In the illustrated embodiment, the interval 12 has a
permeability that varies. As those of ordinary skill in the art
will appreciate, intervals of a subterranean formation often have
multiple portions along the well bore of varying permeability. For
example, a water-producing portion of the interval 12 may have a
higher permeability than other portions of the interval 12. As will
be appreciated, permeability is generally a function of formation
sand particle size, porosity of the matrix, and consolidation
strength of formation sand. By way of example, formations with
large particle sand size, high porosity, and low consolidation
strength often have higher permeability than those with small
particle sand size, low porosity, and high consolidation strength.
As illustrated, the interval 12 includes multiple portions along
the well bore 10, including a first portion 14, a second portion
16, and a third portion 18. Each portion of the interval may have a
different effective permeability. It should be noted that, while
FIG. 1 illustrates the interval 12 as having three portions along
the well bore 10 with different effective permeabilities,
embodiments of the present invention may be applied to any interval
of a subterranean formation having an effective permeability that
varies one area to another.
[0016] Referring now to FIG. 2, in accordance embodiments of the
present invention, the interval 12 may be contacted with a
relative-permeability modifier (e.g., a water-soluble
hydrophobically modified polymer). In some embodiments, for
contacting the interval 12 with the relative-permeability modifier,
the relative-permeability modifier may be present in a permeability
modifying fluid 20 introduced into the interval 12. Treatment
fluids comprising the relative-permeability modifier will be
referred to herein as "permeability modifying fluids." In some
embodiments, the near well bore portion of the interval 12 is
contacted with the relative-permeability modifier. Those of
ordinary skill in the art will understand that the "near well bore
portion" of a formation generally refers to the portion of a
subterranean formation surrounding a well bore. For example, the
"near well bore portion" may refer to the portion of the formation
surrounding a well bore and having a depth of penetration of from
about 1 to about 3 well bore diameters.
[0017] In general, the relative-permeability modifier should modify
the permeability of the interval 12 to be more uniform. It is
believed that the relative-permeability modifier should attach to
surfaces of particulates within the interval 12 of the formation,
thereby selectively reducing the effective permeability of the
interval 12 to water without a comparable reduction of the
formation's permeability to hydrocarbons. Accordingly, the
effective permeability of the interval 12 of the formation to water
may be modified to be generally uniform. In certain embodiments, it
is believed that the effective permeability of the interval 12 to
water may vary up to about 40% after treatment with the
relative-permeability modifier. While the effective permeability of
the interval 12 to water is selectively reduced, the interval 12
may also have some reduction in its effective permeability to
hydrocarbons.
[0018] In certain embodiments, the contact of the interval 12 with
the relative-permeability modifier should be controlled so that the
flow of fluids (e.g., aqueous fluids) through the interval 12 is
not substantially prevented after the treatment with the
relative-permeability modifier. To prevent substantially reducing
the flow of fluids through the interval 12 after treatment, contact
of the interval 12 with the relative-permeability modifier may be
halted, if the injection pressure rises to 90% of the anticipated
fracture gradient, and any subsequent fluid to be injected may be
"spotted" to the interval 12 before continuing injection into the
interval 12. In certain embodiments, to allow for subsequent
treatments with the sealant, the effective permeability of the
interval to water should be at least about 1% to about 80% of its
pre-treatment injectivity index (injection rate divided by
injection pressure), alternatively, about 30% to about 40%. In
certain embodiments, the interval 12 may retain a water
permeability sufficient to allow injection of water at a rate of
about 1/4 barrel per minute (about 10 gallons/minute) at a
differential injection pressure no more than 90% of the fracture
gradient of the interval 12. Examples of a relative-permeability
modifier suitable for use embodiments of the present invention are
described in more detail below.
[0019] By way of example, Table 1 below illustrates a hypothetical
example of an injection profile into the interval 12 both prior to,
and after, treatment with the relative-permeability modifier. As
will be appreciated, the injection profile indicates the
distribution into the different portions of the interval 12 of an
aqueous fluid bullheaded into the interval 12. As illustrated by
Table 1, the injection profile into the interval 12 should be more
uniform after the treatment, indicating a more uniform water
permeability.
TABLE-US-00001 TABLE 1 Injection Profile Injection Profile
Pre-Treatment Post-Treatment First Portion 95 50 Second Portion 5
35 Third Portion 0 15
It should be noted that, in certain embodiments, to achieve a more
uniform effective permeability to water-based fluids, the entire
interval 12 along the well bore 10 need not be contacted with the
relative-permeability modifier. For example, the first portion 14
and the third portion 18 may be treated to modify the permeability
thereof to be about the permeability of the second portion 16.
[0020] Any suitable technique may be used for introduction of the
permeability modifying fluid 20 into the interval 12, for example,
bull heading, coil tubing, jointed pipe (e.g., with straddle
packers, pinpoint injection tools, etc.) or any other suitable
technique may be used. It should be noted that, to reduce the
potential for the undesired fracturing of the interval 12, the
permeability modifying fluid 20 should be introduced into the
interval 12 at matrix flow rates. Example flow rates for the
permeability modifying fluid 20 are in the range of from about 0.25
barrels to about 3 barrels per minute. However, those of ordinary
skill in the art will appreciate that these flow rates are merely
examples, and embodiments of the present invention are applicable
to flow rates outside these ranges. Further, as discussed
previously, contacting the interval 12 with the
relative-permeability modifier should be controlled so that the
effective permeability of the interval 12 is not undesirably
reduced. For example, the pressure of the permeability modifying
fluid 20 may be monitored as it is being introduced into the
interval 12. As the effective permeability to water of the interval
12 decreases, due to the relative-permeability modifier, there
should be an increase in the pressure of the permeability modifying
fluid 20. Therefore, this pressure may be monitored so that the
permeability of the interval 12 is not undesirably reduced to allow
for the subsequent treatment of the interval 12. Other suitable
techniques for monitoring the permeability of the interval 12 also
may be utilized.
[0021] Optionally, an oxidizer may be introduced into the interval
12, after contacting the interval with the relative-permeability
modifier, to restore the original permeability to the interval 12.
In general, the oxidizer should substantially remove the
relative-permeability modifier from the surfaces within the
interval 12. An oxidizer may be used, for example, where the
relative-permeability modifier has undesirably reduced the
permeability, such as by inadvertently preventing the subsequent
introduction of treatment fluids into the interval 12.
[0022] Referring now to FIG. 3, after the interval 12 has been
identified for water shut off (or water blocking) and contacted
with the relative-permeability modifier, a sealant 22 (e.g., an
aqueous-based sealant) may be introduced into the interval 12. As
the relative-permeability modifier has modified the interval 12 to
have a more uniform permeability, a more uniform distribution of
the sealant 22 should be obtained than would otherwise be achieved
without the permeability modification described above with
reference to FIG. 2. As such, a uniform treatment of the interval
12 by the sealant 22 may be obtained, in that the sealant 22 should
generally not undesirably enter portions of the interval 12 with
high permeability at the expense of portions of the interval 12
with lesser permeability. Thus, the interval 12 may be contacted
with the sealant 22 without requiring the use of packers, for
example. Because the relative permeability modifier selectively
reduces the effective permeability of the interval 12 to water,
aqueous-based sealants may be used, in certain embodiments.
However, as noted above, the effective permeability of the interval
12 to hydrocarbons may also be reduced and, thus, sealants that are
not aqueous-based may also be used. Examples of suitable sealants
will be described in more detail below.
[0023] Any suitable technique may be used for introduction of the
sealant 22 into the interval 12 of the subterranean formation, for
example, bull heading, coiled tubing, jointed pipe (e.g., with
straddle packers, pinpoint injection tools, etc.) or any other
suitable technique may be used. It should be noted that, to reduce
the potential for the undesired fracturing of the interval 12, the
sealant 22 should be introduced into the interval 12 at matrix flow
rates. Example flow rates for the sealant 22 are in the range of
from about 0.25 barrels to about 3 barrels per minute. However,
those of ordinary skill in the art will appreciate that these flow
rates are merely examples, and embodiments of the present invention
are applicable to flow rates outside these ranges.
[0024] Additionally, the sealant 22 should achieve sufficient
penetration into the interval 12 for the desired amount of sealing.
In the illustrated embodiment, the sealant 22 penetrates further
into the interval 12 than the permeability modifying fluid 20. This
deeper penetration of the sealant 22 may be desired, for example,
where the control of water production from the interval 12 is
desired. However, as those of ordinary skill in the art will
appreciate, the depth of penetration of the sealant 22 into the
interval 12 will vary based on the particular degree of sealing
desired. For example, the sealant 22 may have the same penetration,
or even less penetration, than the permeability modifying fluid
20.
[0025] While specific reference is made in the above discussion to
sequential treatment of the interval 12 with the
relative-permeability modifier followed by treatment with the
sealant 22, it should be appreciated that this invention is not
limited to such sequential treatments. By way of example,
embodiments of the present invention also encompass treatment of
the interval 12 with a sealant 22 that comprises the
relative-permeability modifier. In such a treatment, the
relative-permeability modifier present in the sealant 22 should
modify the permeability of the interval 12 to water-based fluids to
be more uniform. Because the interval 12 is modified to have a more
uniform permeability, a more uniform distribution of the sealant 22
should be obtained than would otherwise be achieved without this
permeability modification. As such, a uniform treatment of the
interval 12 by the sealant 22 may be obtained, in that the sealant
22 should generally not undesirably enter portions of the interval
12 with high permeability at the expense of portions of the
interval 12 with lesser permeability.
II. Example Relative
Permeability Modifiers
[0026] As described above, a relative-permeability modifier may be
introduced into at least a portion of a subterranean formation, in
accordance with certain embodiments. In general, suitable
relative-permeability modifiers may be any of a variety of
compounds that are capable of selectively reducing the effective
permeability of a formation to water-based fluids without a
comparable reduction of the formation's effective permeability to
hydrocarbons. Suitable relative-permeability modifiers generally
include water-soluble polymers that attach to surfaces within the
formation, reducing the water permeability without a comparable
reduction in hydrocarbon permeability. As used herein, "water
soluble" refers to at least about 0.01 weight percent soluble in
distilled water at room temperature (about 72.degree. F.). In
certain embodiments, the water-soluble polymer is at least about
0.45 weight percent soluble in distilled water at room temperature.
In certain embodiments, the water-soluble polymer is at least about
0.6 weight percent soluble in distilled water at room
temperature.
[0027] Those of ordinary skill in the art, with the benefit of this
disclosure, will appreciate that a variety of different
water-soluble polymers may be suitable for use as the
relative-permeability modifiers. Examples of suitable water-soluble
polymers include, but are not limited to, homo-, co-, and
terpolymers of acrylamide, 2-acrylamido-2-methyl propane sulfonic
acid, N,N-dimethylacrylamide, vinyl pyrrolidone, dimethylaminoethyl
methacrylate, acrylic acid, dimethylaminopropylmethacrylamide,
vinyl amine, vinyl acetate, trimethylammoniumethyl methacrylate
chloride, methacrylamide, hydroxyethyl acrylate, vinyl sulfonic
acid, vinyl phosphonic acid, methacrylic acid, vinyl caprolactam,
N-vinylformamide, N,N-diallylacetamide, dimethyldiallyl ammonium
halide, itaconic acid, styrene sulfonic acid,
methacrylamidoethyltrimethyl ammonium halide, quaternary salt
derivatives of acrylamide, quaternary salt derivatives of acrylic
acid, and combinations thereof.
[0028] In addition, water-soluble polymers suitable for use as
relative-permeability modifiers also may include hydrophobically
modified polymers. As used in this disclosure, the terms
"hydrophobically modified," "hydrophobic modification," and the
like refer to the incorporation into the hydrophilic polymer
structure of hydrophobic groups, wherein the alkyl chain length is
about 4 to about 22 carbons. While these hydrophobically modified
polymers have hydrophobic groups incorporated into the hydrophilic
polymer structure, they should remain water soluble. In some
embodiments, a mole ratio of a hydrophilic monomer to the
hydrophobic compound in the hydrophobically modified polymer is in
the range of from about 99.98:0.02 to about 90:10, wherein the
hydrophilic monomer is a calculated amount present in the
hydrophilic polymer. In certain embodiments, the hydrophobically
modified polymers may comprise a polymer backbone that comprises
polar heteroatoms. Generally, the polar heteroatoms present within
the polymer backbone of the hydrophobically modified polymers
include, but are not limited to, oxygen, nitrogen, sulfur, or
phosphorous.
[0029] Example hydrophobically modified polymers may contain a
hydrophilic polymer backbone and a hydrophobic branch, wherein the
hydrophobic branch includes an alkyl chain of about 4 to about 22
carbons. In certain embodiments, the hydrophobic branch may have an
alkyl chain length of about 7 to about 22 carbons. In certain
embodiments, the hydrophobic branch may have an alkyl chain length
of about 12 to about 18 carbons.
[0030] Additional examples of suitable hydrophobically modified
polymers include a polymer that has been hydrophobically modified
with an alkyl group present on an amino group (in the polymer
backbone or as a pendant group) in quaternized form. For example,
an alkyl group may be present on a dialkyl amino pendant group in
quaternized form. In one embodiment, the dialkyl amino pendant
group comprises a dimethyl amino pendant group. One specific
example of a hydrophobically modified polymer includes a
polydimethylaminoethylmethacrylate or
polydimethylaminopropylmethacrylamide that has been hydrophobically
modified with an alkyl group with 4 carbons to 22 carbons (e.g., 4
carbons, 6, carbons, 8 carbons, 10 carbons, 12 carbons, 14 carbons,
16 carbons, 18 carbons, 20 carbons, 22 carbons, etc.) on a
dimethylamino group. An example of a suitable HM modified polymer
is HPT-1.TM. relative permeability modifying polymer available from
Halliburton Energy Services, Inc., Duncan, Okla.
[0031] Examples of suitable hydrophobically modified polymers that
may be utilized include, but are not limited to,
acrylamide/octadecyldimethylammoniumethyl methacrylate bromide
copolymer, dimethylaminoethyl methacrylate/vinyl
pyrrolidone/hexadecyldimethylammoniumethyl methacrylate bromide
terpolymer, and acrylamide/2-acrylamido-2-methyl propane sulfonic
acid/2-ethylhexyl methacrylate terpolymer. Another example of a
suitable hydrophobically modified polymer comprises an amino
methacrylate/alkyl amino methacrylate copolymer. An example of a
suitable amino methacrylate/alkyl amino methacrylate copolymer
includes a dimethlyaminoethyl
methacrylate/alkyl-dimethylammoniumethyl methacrylate copolymer. An
example of a suitable dimethlyaminoethyl
methacrylate/alkyl-dimethylammoniumethyl methacrylate copolymer
includes a dimethylaminoethyl
methacrylate/hexadecyl-dimethylammoniumethyl methacrylate
copolymer. As discussed in more detail below, these copolymers may
be formed, in embodiments, by reactions with a variety of alkyl
halides. For example, in some embodiments, the hydrophobically
modified polymer may comprise a dimethylaminoethyl
methacrylate/hexadecyl-dimethylammoniumethyl methacrylate bromide
copolymer.
[0032] Example hydrophobically modified polymers may be synthesized
utilizing any suitable technique. For example, the hydrophobically
modified polymers may be a reaction product of one or more
hydrophilic polymers and one or more hydrophobic compounds. By way
of further example, the hydrophobically modified polymers may be
prepared from a polymerization reaction comprising a hydrophilic
monomer and a hydrophobically modified hydrophilic monomer. In
certain embodiments, the hydrophobically modified polymers may be
pre-reacted before they are placed into the well bore.
Alternatively, in some embodiments, the hydrophobically modified
polymers may be prepared by an appropriate in situ reaction.
Suitable hydrophobically modified polymers and methods for their
preparation are described in more detail in U.S. Pat. Nos.
6,476,169 and 7,117,942, the disclosures of which are incorporated
herein by reference. Those of ordinary skill in the art, with the
benefit of this disclosure, will be able to determine other
suitable methods for the synthesis of suitable hydrophobically
modified polymers.
[0033] In certain embodiments, suitable hydrophobically modified
polymers may be synthesized by the hydrophobic modification of a
hydrophilic polymer via reaction with a hydrophobic compound. As
described above, hydrophobic modification refers to incorporation
into the hydrophilic polymer structure of hydrophobic groups,
wherein the alkyl chain length is from about 4 to about 22 carbons.
The hydrophilic polymers suitable for forming the hydrophobically
modified polymers used in the present invention should be capable
of reacting with hydrophobic compounds. Suitable hydrophilic
polymers include, homo-, co-, or terpolymers such as, but not
limited to, polyacrylamides, polyvinylamines,
poly(vinylamines/vinyl alcohols), alkyl acrylate polymers in
general, and combinations thereof. Additional examples of alkyl
acrylate polymers include polydimethylaminoethyl methacrylate,
polydimethylaminopropyl methacrylamide,
poly(acrylamide/dimethylaminoethyl methacrylate), poly(methacrylic
acid/dimethylaminoethyl methacrylate), poly(2-acrylamido-2-methyl
propane sulfonic acid/dimethylaminoethyl methacrylate),
poly(acrylamide/dimethylaminopropyl methacrylamide), poly(acrylic
acid/dimethylaminopropyl methacrylamide), poly(methacrylic
acid/dimethylaminopropyl methacrylamide), and combinations thereof.
In certain embodiments, the hydrophilic polymers comprise a polymer
backbone and reactive amino groups in the polymer backbone or as
pendant groups, the reactive amino groups capable of reacting with
hydrophobic compounds. In some embodiments, the hydrophilic
polymers comprise dialkyl amino pendant groups. In some
embodiments, the hydrophilic polymers comprise a dimethyl amino
pendant group and a monomer comprising dimethylaminoethyl
methacrylate or dimethylaminopropyl methacrylamide. In certain
embodiments, the hydrophilic polymers comprise a polymer backbone
that comprises polar heteroatoms, wherein the polar heteroatoms
present within the polymer backbone of the hydrophilic polymers
include oxygen, nitrogen, sulfur, or phosphorous. Suitable
hydrophilic polymers that comprise polar heteroatoms within the
polymer backbone include homo-, co-, or terpolymers, such as, but
not limited to, celluloses, chitosans, polyamides, polyetheramines,
polyethyleneimines, polyhydroxyetheramines, polylysines,
polysulfones, gums, starches, and combinations thereof. In one
embodiment, the starch is a cationic starch. A suitable cationic
starch may be formed by reacting a starch, such as corn, maize,
waxy maize, potato, tapioca, or the like, with the reaction product
of epichlorohydrin and trialkylamine.
[0034] The hydrophobic compounds that are capable of reacting with
the hydrophilic polymers include alkyl halides, sulfonates,
sulfates, organic acids, and organic acid derivatives. Examples of
suitable organic acids and derivatives thereof include, but are not
limited to, octenyl succinic acid; dodecenyl succinic acid; and
anhydrides, esters, imides, and amides of octenyl succinic acid or
dodecenyl succinic acid. In certain embodiments, the hydrophobic
compounds may have an alkyl chain length of from about 4 to about
22 carbons. In another embodiment, the hydrophobic compounds may
have an alkyl chain length of from about 7 to about 22 carbons. In
another embodiment, the hydrophobic compounds may have an alkyl
chain length of from about 12 to about 18 carbons. For example,
where the hydrophobic compound is an alkyl halide, the reaction
between the hydrophobic compound and hydrophilic polymer may result
in the quaternization of at least some of the hydrophilic polymer
amino groups with an alkyl halide, wherein the alkyl chain length
is from about 4 to about 22 carbons.
[0035] As previously mentioned, in certain embodiments, suitable
hydrophobically modified polymers also may be prepared from a
polymerization reaction comprising a hydrophilic monomer and a
hydrophobically modified hydrophilic monomer. The hydrophobically
modified polymers synthesized from the polymerization reactions may
have estimated molecular weights in the range of from about 100,000
to about 10,000,000 and mole ratios of the hydrophilic monomer(s)
to the hydrophobically modified hydrophilic monomer(s) in the range
of from about 99.98:0.02 to about 90:10.
[0036] A variety of hydrophilic monomers may be used to form the
hydrophobically modified polymers useful in the present invention.
Examples of suitable hydrophilic monomers include, but are not
limited to, acrylamide, 2-acrylamido-2-methyl propane sulfonic
acid, N,N-dimethylacrylamide, vinyl pyrrolidone, dimethylaminoethyl
methacrylate, acrylic acid, dimethylaminopropylmethacrylamide,
vinyl amine, vinyl acetate, trimethylammoniumethyl methacrylate
chloride, methacrylamide, hydroxyethyl acrylate, vinyl sulfonic
acid, vinyl phosphonic acid, methacrylic acid, vinyl caprolactam,
N-vinylformamide, N,N-diallylacetamide, dimethyldiallyl ammonium
halide, itaconic acid, styrene sulfonic acid,
methacrylamidoethyltrimethyl ammonium halide, quaternary salt
derivatives of acrylamide, quaternary salt derivatives of acrylic
acid, and combinations thereof.
[0037] A variety of hydrophobically modified hydrophilic monomers
also may be used to form the hydrophobically modified polymers
useful in certain embodiments. Examples of suitable hydrophobically
modified hydrophilic monomers include, but are not limited to,
alkyl acrylates, alkyl methacrylates, alkyl acrylamides, alkyl
methacrylamides alkyl dimethylammoniumethyl methacrylate halides,
and alkyl dimethylammoniumpropyl methacrylamide halides, wherein
the alkyl groups have from about 4 to about 22 carbon atoms. In
another embodiment, the alkyl groups have from about 7 to about 22
carbons. In another embodiment, the alkyl groups have from about 12
to about 18 carbons. In certain embodiments, the hydrophobically
modified hydrophilic monomer comprises
octadecyldimethylammoniumethyl methacrylate bromide,
hexadecyldimethylammoniumethyl methacrylate bromide,
hexadecyldimethylammoniumpropyl methacrylamide bromide,
2-ethylhexyl methacrylate, or hexadecyl methacrylamide.
[0038] In addition, water-soluble polymers suitable for use as
relative-permeability modifiers also may include hydrophilically
modified polymers. As used in this disclosure, the terms
"hydrophilic modification," "hydrophilically modified," and the
like refer to the incorporation into the hydrophilic polymer
structure of hydrophilic groups, such as to introduce branching or
to increase the degree of branching in the hydrophilic polymer. The
hydrophilically modified polymers of certain embodiments typically
have molecular weights in the range of from about 100,000 to about
10,000,000. In certain embodiments, the hydrophilically modified
polymers comprise a polymer backbone, the polymer backbone
comprising polar heteroatoms. Generally, the polar heteroatoms
present within the polymer backbone of the hydrophilically modified
polymers include, but are not limited to, oxygen, nitrogen, sulfur,
or phosphorous.
[0039] The hydrophilically modified polymers may be synthesized
using any suitable method. In one example, the hydrophilically
modified polymers may be a reaction product of a hydrophilic
polymer and a hydrophilic compound. In certain embodiments,
suitable hydrophilically modified polymers may be formed by
additional hydrophilic modification, for example, to introduce
branching or to increase the degree of branching, of a hydrophilic
polymer. Those of ordinary skill in the art, with the benefit of
this disclosure, will be able to determine other suitable methods
for the preparation of suitable hydrophilically modified
polymers.
[0040] The hydrophilic polymers suitable for forming the
hydrophilically modified polymers used in certain embodiments
should be capable of reacting with hydrophilic compounds. In
certain embodiments, suitable hydrophilic polymers include, homo-,
co-, or terpolymers, such as, but not limited to, polyacrylamides,
polyvinylamines, poly(vinylamines/vinyl alcohols), and alkyl
acrylate polymers in general. Additional examples of alkyl acrylate
polymers include, but are not limited to, polydimethylaminoethyl
methacrylate, polydimethylaminopropyl methacrylamide,
poly(acrylamide/dimethylaminoethyl methacrylate), poly(methacrylic
acid/dimethylaminoethyl methacrylate), poly(2-acrylamido-2-methyl
propane sulfonic acid/dimethylaminoethyl methacrylate),
poly(acrylamide/dimethylaminopropyl methacrylamide), poly(acrylic
acid/dimethylaminopropyl methacrylamide), and poly(methacrylic
acid/dimethylaminopropyl methacrylamide). In certain embodiments,
the hydrophilic polymers comprise a polymer backbone and reactive
amino groups in the polymer backbone or as pendant groups, the
reactive amino groups capable of reacting with hydrophilic
compounds. In some embodiments, the hydrophilic polymers comprise
dialkyl amino pendant groups. In some embodiments, the hydrophilic
polymers comprise a dimethyl amino pendant group and at least one
monomer comprising dimethylaminoethyl methacrylate or
dimethylaminopropyl methacrylamide. In other embodiments, the
hydrophilic polymers comprise a polymer backbone comprising polar
heteroatoms, wherein the polar heteroatoms present within the
polymer backbone of the hydrophilic polymers include, but are not
limited to, oxygen, nitrogen, sulfur, or phosphorous. Suitable
hydrophilic polymers that comprise polar heteroatoms within the
polymer backbone include homo-, co-, or terpolymers, such as, but
not limited to, celluloses, chitosans, polyamides, polyetheramines,
polyethyleneimines, polyhydroxyetheramines, polylysines,
polysulfones, gums, starches, and derivatives thereof. In one
embodiment, the starch is a cationic starch. A suitable cationic
starch may be formed by reacting a starch, such as corn, maize,
waxy maize, potato, tapioca, and the like, with the reaction
product of epichlorohydrin and trialkylamine.
[0041] Hydrophilic compounds suitable for reaction with the
hydrophilic polymers include, but are not limited to: polyethers
that comprise halogens; sulfonates; sulfates; organic acids; and
organic acid derivatives. Examples of suitable polyethers include,
but are not limited to, polyethylene oxides, polypropylene oxides,
and polybutylene oxides, and copolymers, terpolymers, and mixtures
thereof. In some embodiments, the polyether comprises an
epichlorohydrin-terminated polyethylene oxide methyl ether.
[0042] The hydrophilically modified polymers formed from the
reaction of a hydrophilic polymer with a hydrophilic compound may
have estimated molecular weights in the range of from about 100,000
to about 10,000,000 and may have weight ratios of the hydrophilic
polymers to the polyethers in the range of from about 1:1 to about
10:1. Examples of suitable hydrophilically modified polymers having
molecular weights and weight ratios in the ranges set forth above
include, but are not limited to, the reaction product of
polydimethylaminoethyl methacrylate and epichlorohydrin-terminated
polyethyleneoxide methyl ether; the reaction product of
polydimethylaminopropyl methacrylamide and
epichlorohydrin-terminated polyethyleneoxide methyl ether; and the
reaction product of poly(acrylamide/dimethylaminopropyl
methacrylamide) and epichlorohydrin-terminated polyethyleneoxide
methyl ether. In some embodiments, the hydrophilically modified
polymer comprises the reaction product of a polydimethylaminoethyl
methacrylate and epichlorohydrin-terminated polyethyleneoxide
methyl ether having a weight ratio of polydimethylaminoethyl
methacrylate to epichlorohydrin-terminated polyethyleneoxide methyl
ether of about 3:1.
III. Example Permeability Modifying Fluids
[0043] In accordance with some embodiments, the
relative-permeability modifier may be present in a fluid, referred
to herein as a "permeability modifying fluid," introduced into the
interval 12. Sufficient concentrations of the relative-permeability
modifier should be present in these permeability modifying fluids
to provide the desired level of permeability modification. In some
embodiments, the relative-permeability modifier may be present in
these permeability modifying fluids in an amount in the range of
from about 0.02% to about 10% by weight of the permeability
modifying fluid. In another embodiment, relative-permeability
modifier may be present in these permeability modifying fluids in
an amount in the range of from about 0.05% to about 1.0% by weight
of the permeability modifying fluid. In certain embodiments, the
relative-permeability modifier may be provided in a concentrated
aqueous solution prior to its combination with the other components
necessary to form the permeability modifying fluids.
[0044] In addition to the relative-permeability modifier, the
permeability modifying fluids generally also comprise water. The
water included in the permeability modifying fluid may include
freshwater, saltwater (e.g., water containing one or more salts
dissolved therein), brines (e.g., natural or produced brines),
seawater, or another other aqueous fluid that does not undesirably
effect the other components in the permeability modifying
fluid.
IV. Example Sealants
[0045] The sealants used in certain embodiments may include any
fluids suitable for sealing the interval 12 of the subterranean
formation that, in the absence of the above-described permeability
modification, would typically enter portions of the interval 12
with higher permeabilities at the expense of portions of the
interval 12 with lesser permeabilities. For example, sealants that
may be used in certain embodiments may comprise getable
compositions. In general, suitable gelable compositions should cure
to form a gel that at least substantially plugs the permeability of
the formation. Gelable compositions suitable for use in certain
embodiments include, for example, those compositions that cure to
form a semi-solid, immovable, gel-like substance. Prior to curing,
the gelable compositions should have low viscosities and be capable
of flowing in pipe and into the subterranean formation.
[0046] Examples of suitable gelable compositions include gelable
aqueous silicate compositions, crosslinkable aqueous polymer
compositions, polymerizable organic monomer compositions, and resin
compositions. Other gelable compositions that cure to substantially
plug the permeability of the formation may also be suitable.
[0047] 1. Gelable Aqueous Silicate Compositions
[0048] In certain embodiments, the aqueous-based sealant may
comprise a gelable aqueous silicate composition. Suitable gelable
aqueous silicate compositions for plugging the permeability of a
formation generally comprise aqueous alkali metal silicate solution
and a catalyst (e.g., a temperature-activated catalyst) for gelling
the aqueous alkali metal silicate solution. An example of a
suitable gelable aqueous silicate compositions is INJECTROL.TM.
sealant, which is available from Halliburton Energy Services, Inc.
Examples of suitable gelable aqueous silicate compositions are
described in U.S. Pat. No. 4,466,831, the disclosure of which is
incorporated herein by reference as if fully set forth herein.
[0049] The aqueous alkali metal silicate solution component of the
gelable aqueous silicate compositions generally comprises water and
an alkali metal silicate. The water generally may include
freshwater, saltwater (e.g., water containing one or more salts
dissolved therein), brines (e.g., natural or produced brines),
seawater, or any other aqueous liquid that does not undesirably
react with the other components used in accordance with this
invention or with the subterranean formation. Examples of suitable
alkali metal silicates include, but are not limited to, one or more
of sodium silicate, potassium silicate, lithium silicate, rubidium
silicate, or cesium silicate. While sodium silicate may be present
in many forms, the sodium silicate used in the aqueous alkali metal
silicate solution may have a Na.sub.2O-to-SiO.sub.2 weight ratio in
the range of from about 1:2 to about 1:4. For example, the sodium
silicate may have a Na.sub.2O-to-SiO.sub.2 weight ratio in the
range of about 1:3.2. Generally, the alkali metal silicate may be
present in the aqueous alkali metal silicate solution component in
an amount in the range of from about 0.1% to about 10% by weight of
the aqueous alkali metal silicate solution component.
[0050] The temperature-activated catalyst component of the gelable
aqueous silicate compositions is used, inter alia, to convert the
gelable aqueous silicate compositions into the desired gel
described above. Selection of a temperature-activated catalyst is
related, at least in part, to the temperature of the subterranean
formation to which the gelable aqueous silicate composition will be
introduced. The temperature-activated catalysts that can be used in
the gelable aqueous silicate compositions of some embodiments
include, but are not limited to, ammonium sulfate (e.g., for the
range of from about 60.degree. F. to about 240.degree. F.); sodium
acid pyrophosphate (e.g., for the range of from about 60.degree. F.
to about 240.degree. F.); citric acid (e.g., for the range of from
about 60.degree. F. to about 120.degree. F.); and ethyl acetate
(e.g., for the range of from about 60.degree. F. to about
120.degree. F.). Generally, the temperature-activated catalyst may
be present in the gelable aqueous silicate composition in the range
of from about 0.1% to about 5% by weight of the gelable aqueous
silicate composition.
[0051] 2. Crosslinkable Aqueous Polymer Compositions
[0052] In some embodiments, the aqueous-based sealant may comprise
a crosslinkable aqueous polymer composition. Suitable crosslinkable
aqueous polymer compositions for plugging the permeability of the
formation generally comprise water, a crosslinkable polymer, and a
crosslinking agent. Such compositions are similar to those used to
form gelled treatment fluids, such as fracturing fluids, but,
according to the example methods described herein, they are not
exposed to breakers or de-linkers and so they retain their viscous
nature over time. An example of a suitable crosslinkable polymer
composition is used in H2-Zero.TM. conformance control solutions,
which are commercially available from Halliburton Energy Services,
Inc. Examples of suitable crosslinkable aqueous polymer
compositions are described in U.S. Pat. Nos. 5,836,392, 6,192,986,
and 6,196,317, the disclosures of which are incorporated herein by
reference as if fully set forth herein.
[0053] The water may be any suitable water in which the
crosslinkable composition and the crosslinking agent may be
dissolved, mixed, suspended, or dispersed therein to facilitate gel
formation. For example, the water may include freshwater, saltwater
(e.g., water containing one or more salts dissolved therein),
brines (e.g., natural or produced brines), seawater, or any other
aqueous liquid that does not undesirable react with the other
components used in accordance with embodiments or with the
subterranean formation.
[0054] Examples of crosslinkable polymers that can be used in the
crosslinkable aqueous polymer compositions include, but are not
limited to, carboxylate-containing polymers and
acrylamide-containing polymers. Preferred acrylamide-containing
polymers include polyacrylamide, partially hydrolyzed
polyacrylamide, copolymers of acrylamide and acrylate, and
carboxylate-containing terpolymers and tetrapolymers of acrylate.
Additional examples of suitable crosslinkable polymers include
hydratable polymers comprising polysaccharides and derivatives
thereof and that contain one or more of the monosaccharide units
galactose, mannose, glucoside, glucose, xylose, arabinose,
fructose, glucuronic acid, or pyranosyl sulfate. Suitable natural
hydratable polymers include, but are not limited to, guar gum,
locust bean gum, tara, konjak, tamarind, starch, cellulose, karaya,
xanthan, tragacanth, and carrageenan, and derivatives of all of the
above. Suitable hydratable synthetic polymers and copolymers that
may be used in the crosslinkable aqueous polymer compositions
include, but are not limited to, polyacrylates, polymethacrylates,
polyacrylamides, maleic anhydride, methylvinyl ether polymers,
polyvinyl alcohols, and polyvinylpyrrolidone.
[0055] The crosslinkable polymer used should be included in the
crosslinkable aqueous polymer composition in an amount sufficient
to form the desired gelled substance in the subterranean formation.
In some embodiments, the crosslinkable polymer is included in the
crosslinkable aqueous polymer composition in an amount in the range
of from about 1% to about 30% by weight of the aqueous solvent. In
another embodiment, the crosslinkable polymer is included in the
crosslinkable aqueous polymer composition in an amount in the range
of from about 1% to about 20% by weight of the aqueous solvent.
[0056] The crosslinkable aqueous polymer compositions of some
embodiments further comprise a crosslinking agent for crosslinking
the crosslinkable polymers to form the desired gelled substance. In
some embodiments, the crosslinking agent is a molecule or complex
containing a reactive transition metal cation. An example of a
suitable crosslinking agent comprises trivalent chromium cations
complexed or bonded to anions, atomic oxygen, or water. Examples of
suitable crosslinking agents include, but are not limited to,
compounds or complexes containing chromic acetate and/or chromic
chloride. Other suitable transition metal cations include chromium
VI within a redox system, aluminum III, iron II, iron III, and
zirconium IV.
[0057] The crosslinking agent should be present in the
crosslinkable aqueous polymer compositions of some embodiments in
an amount sufficient to provide, inter alia, the desired degree of
crosslinking. In some embodiments, the crosslinking agent is
present in the crosslinkable aqueous polymer compositions in an
amount in the range of from about 0.01% to about 5% by weight of
the crosslinkable aqueous polymer composition. The exact type and
amount of crosslinking agent or agents used depends upon the
specific crosslinkable polymer to be crosslinked, formation
temperature conditions, and other factors known to those
individuals skilled in the art.
[0058] Optionally, the crosslinkable aqueous polymer compositions
may further comprise a crosslinking delaying agent, such as a
polysaccharide crosslinking delaying agent derived from guar, guar
derivatives, or cellulose derivatives. The crosslinking delaying
agent may be included in the crosslinkable aqueous polymer
compositions, inter alia, to delay crosslinking of the
crosslinkable aqueous polymer compositions until desired. One of
ordinary skill in the art, with the benefit of this disclosure,
will know the appropriate amount of the crosslinking delaying agent
to include in the crosslinkable aqueous polymer compositions for a
desired application.
[0059] 3. Polymerizable Organic Monomer Compositions
[0060] In some embodiments, the aqueous-based sealant may comprise
a polymerizable organic monomer composition. Suitable polymerizable
organic monomer compositions for plugging the permeability of a
formation generally comprise water, a water-soluble polymerizable
organic monomer, an oxygen scavenger, and a primary initiator. An
example of a suitable polymerizable organic monomer compositions
used in Perm-Seal.TM. sealant treatment services, which are
commercially available from Halliburton Energy Services, Inc.
Examples of suitable polymerizable organic monomer compositions are
described in U.S. Pat. Nos. 5,358,051 and 5,335,726, the
disclosures of which are incorporated herein by reference as if
fully set forth herein.
[0061] The water in the polymerizable organic monomer composition
generally may include freshwater, saltwater (e.g., water containing
one or more salts dissolved therein), brines (e.g., natural or
produced brines), seawater, or any other aqueous liquid that does
not undesirable react with the other components used in accordance
with embodiments or with the subterranean formation.
[0062] A variety of monomers may be suitable for use as the
water-soluble polymerizable organic monomers. Examples of suitable
monomers include, but are not limited to, acrylic acid, methacrylic
acid, acrylamide, methacrylamide, 2-methacrylamido-2-methylpropane
sulfonic acid, 2-dimethylacrylamide, vinyl sulfonic acid,
N,N-dimethylaminoethylmethacrylate,
2-triethylammoniumethylmethacrylate chloride,
N,N-dimethyl-aminopropylmethacryl-amide,
methacrylamidepropyltriethylammonium chloride, N-vinyl pyrrolidone,
vinyl-phosphonic acid, and methacryloyloxyethyl trimethylammonium
sulfate, and mixtures thereof. In certain embodiments, the
water-soluble polymerizable organic monomer may be
self-crosslinking. Examples of suitable monomers which are self
crosslinking include, but are not limited to, hydroxyethylacrylate,
hydroxymethylacrylate, hydroxyethylmethacrylate,
N-hydroxymethylacrylamide, N-hydroxymethyl-methacrylamide,
polyethylene glycol acrylate, polyethylene glycol methacrylate,
polypropylene gylcol acrylate, polypropylene glycol methacrylate,
and mixtures thereof. An example of one suitable monomer is
hydroxyethylcellulose-vinyl phosphoric acid.
[0063] The water-soluble polymerizable organic monomer (or monomers
where a mixture thereof is used) should be included in the
polymerizable organic monomer composition in an amount sufficient
to form the desired gelled substance after placement of the
polymerizable organic monomer composition into the subterranean
formation. In some embodiments, the water-soluble polymerizable
organic monomer is included in the polymerizable organic monomer
composition in an amount in the range of from about 1% to about 30%
by weight of the water. In another embodiment, the water-soluble
polymerizable organic monomer is included in the polymerizable
organic monomer composition in an amount in the range of from about
1% to about 20% by weight of the water.
[0064] The presence of oxygen in the polymerizable organic monomer
composition may inhibit the polymerization process of the
water-soluble polymerizable organic monomer or monomers. Therefore,
an oxygen scavenger, such as stannous chloride, may be included in
the polymerizable monomer composition. In order to improve the
solubility of stannous chloride so that it may be readily combined
with the polymerizable organic monomer composition on the fly, the
stannous chloride may be pre-dissolved in a hydrochloric acid
solution. For example, the stannous chloride may be dissolved in a
0.1% by weight aqueous hydrochloric acid solution in an amount of
about 10% by weight of the resulting solution. The resulting
stannous chloride-hydrochloric acid solution may be included in the
polymerizable organic monomer composition in an amount in the range
of from about 0.1% to about 10% by weight of the polymerizable
organic monomer composition. Generally, the stannous chloride may
be included in the polymerizable organic monomer composition of an
embodiment in an amount in the range of from about 0.005% to about
0.1% by weight of the polymerizable organic monomer
composition.
[0065] The primary initiator is used, inter alia, to initiate
polymerization of the water-soluble polymerizable organic
monomer(s) used in an embodiment. Any compound or compounds that
form free radicals in aqueous solution may be used as the primary
initiator. The free radicals act, inter alia, to initiate
polymerization of the water-soluble polymerizable organic monomer
present in the polymerizable organic monomer composition. Compounds
suitable for use as the primary initiator include, but are not
limited to, alkali metal persulfates; peroxides;
oxidation-reduction systems employing reducing agents, such as
sulfites in combination with oxidizers; and azo polymerization
initiators. Examples of suitable azo polymerization initiators
include 2,2'-azobis(2-imidazole-2-hydroxyethyl) propane,
2,2'-azobis(2-aminopropane), 4,4'-azobis(4-cyanovaleric acid), and
2,2'-azobis(2-methyl-N-(2-hydroxyethyl) propionamide. Generally,
the primary initiator should be present in the polymerizable
organic monomer composition in an amount sufficient to initiate
polymerization of the water-soluble polymerizable organic
monomer(s). In certain embodiments, the primary initiator is
present in the polymerizable organic monomer composition in an
amount in the range of from about 0.1% to about 5% by weight of the
water-soluble polymerizable organic monomer(s). One skilled in the
art will recognize that as the polymerization temperature
increases, the required level of activator decreases.
[0066] Optionally, the polymerizable organic monomer compositions
further may comprise a secondary initiator. A secondary initiator
may be used, for example, where the immature aqueous gel is placed
into a subterranean formation that is relatively cool as compared
to the surface mixing, such as when placed below the mud line in
offshore operations. The secondary initiator may be any suitable
water-soluble compound or compounds that may react with the primary
initiator to provide free radicals at a lower temperature. An
example of a suitable secondary initiator is triethanolamine. In
some embodiments, the secondary initiator is present in the
polymerizable organic monomer composition in an amount in the range
of from about 0.1% to about 5% by weight of the water-soluble
polymerizable organic monomer(s).
[0067] Also optionally, the polymerizable organic monomer
compositions of certain embodiments further may comprise a
crosslinking agent for crosslinking the polymerizable organic
monomer compositions in the desired gelled substance. In some
embodiments, the crosslinking agent is a molecule or complex
containing a reactive transition metal cation. An example of a
suitable crosslinking agent comprises trivalent chromium cations
complexed or bonded to anions, atomic oxygen, or water. Examples of
suitable crosslinking agents include, but are not limited to,
compounds or complexes containing chromic acetate and/or chromic
chloride. Other suitable transition metal cations include chromium
VI within a redox system, aluminum III, iron II, iron III, and
zirconium IV. Generally, the crosslinking agent may be present in
polymerizable organic monomer compositions in an amount in the
range of from 0.01% to about 5% by weight of the polymerizable
organic monomer composition.
[0068] 4. Resin Compositions
[0069] In some embodiments, the sealant may comprise a resin. The
term "resin" as used herein refers to any of numerous physically
similar polymerized synthetics or chemically modified natural
resins including thermoplastic materials and thermosetting
materials. Resins that may be suitable for use in the present
invention may include substantially all resins known and used in
the art.
[0070] One type of resin suitable for use in the methods of the
present invention is a two-component epoxy-based resin comprising a
liquid hardenable resin component and a liquid hardening agent
component. The liquid hardenable resin component comprises a
hardenable resin and an optional solvent. The solvent may be added
to the resin to reduce its viscosity for ease of handling, mixing
and transferring. It is within the ability of one skilled in the
art, with the benefit of this disclosure, to determine if and how
much solvent may be needed to achieve a viscosity suitable to the
subterranean conditions. Factors that may affect this decision
include geographic location of the well, the surrounding weather
conditions, and the desired long-term stability of the
consolidating agent. An alternate way to reduce the viscosity of
the hardenable resin is to heat it. The second component is the
liquid hardening agent component, which comprises a hardening
agent, an optional silane coupling agent, a surfactant, an optional
hydrolyzable ester for, among other things, breaking gelled
fracturing fluid films on proppant particulates, and an optional
liquid carrier fluid for, among other things, reducing the
viscosity of the hardening agent component.
[0071] Examples of hardenable resins that can be used in the liquid
hardenable resin component include, but are not limited to, organic
resins such as bisphenol A diglycidyl ether resins, butoxymethyl
butyl glycidyl ether resins, bisphenol A-epichlorohydrin resins,
bisphenol F resins, polyepoxide resins, novolak resins, polyester
resins, phenol-aldehyde resins, urea-aldehyde resins, furan resins,
urethane resins, glycidyl ether resins, other epoxide resins, and
combinations thereof. In some embodiments, the hardenable resin may
comprise a urethane resin. Examples of suitable urethane resins may
comprise a polyisocyanate component and a polyhydroxy component.
Examples of suitable hardenable resins, including urethane resins,
that may be suitable for use in the methods of the present
invention include those described in U.S. Pat. Nos. 6,582,819,
issued to McDaniel, et al.; 4,585,064 issued to Graham, et al.;
6,677,426 issued to Noro, et al.; and 7,153,575 issued to Anderson,
et al., the disclosures of which are herein incorporated by
reference.
[0072] The hardenable resin may be included in the liquid
hardenable resin component in an amount in the range of about 5% to
about 100% by weight of the liquid hardenable resin component. It
is within the ability of one skilled in the art, with the benefit
of this disclosure, to determine how much of the liquid hardenable
resin component may be needed to achieve the desired results.
Factors that may affect this decision include which type of liquid
hardenable resin component and liquid hardening agent component are
used.
[0073] Any solvent that is compatible with the hardenable resin and
achieves the desired viscosity effect may be suitable for use in
the liquid hardenable resin component. Suitable solvents may
include butyl lactate, dipropylene glycol methyl ether, dipropylene
glycol dimethyl ether, dimethyl formamide, diethyleneglycol methyl
ether, ethyleneglycol butyl ether, diethyleneglycol butyl ether,
propylene carbonate, methanol, butyl alcohol, d'limonene, fatty
acid methyl esters, and butylglycidyl ether, and combinations
thereof. Other preferred solvents may include aqueous dissolvable
solvents such as, methanol, isopropanol, butanol, and glycol ether
solvents, and combinations thereof. Suitable glycol ether solvents
include, but are not limited to, diethylene glycol methyl ether,
dipropylene glycol methyl ether, 2-butoxy ethanol, ethers of a
C.sub.2 to C.sub.6 dihydric alkanol containing at least one C.sub.1
to C.sub.6 alkyl group, mono ethers of dihydric alkanols,
methoxypropanol, butoxyethanol, and hexoxyethanol, and isomers
thereof. Selection of an appropriate solvent is dependent on the
resin composition chosen and is within the ability of one skilled
in the art, with the benefit of this disclosure.
[0074] As described above, use of a solvent in the liquid
hardenable resin component is optional but may be desirable to
reduce the viscosity of the hardenable resin component for ease of
handling, mixing, and transferring. However, as previously stated,
it may be desirable in some embodiments to not use such a solvent
for environmental or safety reasons. It is within the ability of
one skilled in the art, with the benefit of this disclosure, to
determine if and how much solvent is needed to achieve a suitable
viscosity. In some embodiments, the amount of the solvent used in
the liquid hardenable resin component may be in the range of about
0.1% to about 30% by weight of the liquid hardenable resin
component. Optionally, the liquid hardenable resin component may be
heated to reduce its viscosity, in place of, or in addition to,
using a solvent.
[0075] Examples of the hardening agents that can be used in the
liquid hardening agent component include, but are not limited to,
cyclo-aliphatic amines, such as piperazine, derivatives of
piperazine (e.g., aminoethylpiperazine) and modified piperazines;
aromatic amines, such as methylene dianiline, derivatives of
methylene dianiline and hydrogenated forms, and
4,4'-diaminodiphenyl sulfone; aliphatic amines, such as ethylene
diamine, diethylene triamine, triethylene tetraamine, and
tetraethylene pentaamine; imidazole; pyrazole; pyrazine;
pyrimidine; pyridazine; 1H-indazole; purine; phthalazine;
naphthyridine; quinoxaline; quinazoline; phenazine; imidazolidine;
cinnoline; imidazoline; 1,3,5-triazine; thiazole; pteridine;
indazole; amines; polyamines; amides; polyamides; and
2-ethyl-4-methyl imidazole; and combinations thereof. The chosen
hardening agent often effects the range of temperatures over which
a hardenable resin is able to cure. By way of example, and not of
limitation, in subterranean formations having a temperature of
about 60.degree. F. to about 250.degree. F., amines and
cyclo-aliphatic amines such as piperidine, triethylamine,
tris(dimethylaminomethyl)phenol, and dimethylaminomethyl)phenol may
be preferred. In subterranean formations having higher
temperatures, 4,4'-diaminodiphenyl sulfone may be a suitable
hardening agent. Hardening agents that comprise piperazine or a
derivative of piperazine have been shown capable of curing various
hardenable resins from temperatures as low as about 50.degree. F.
to as high as about 350.degree. F.
[0076] The hardening agent used may be included in the liquid
hardening agent component in an amount sufficient to at least
partially harden the resin composition. In some embodiments of the
present invention, the hardening agent used is included in the
liquid hardening agent component in the range of about 0.1% to
about 95% by weight of the liquid hardening agent component. In
other embodiments, the hardening agent used may be included in the
liquid hardening agent component in an amount of about 15% to about
85% by weight of the liquid hardening agent component. In other
embodiments, the hardening agent used may be included in the liquid
hardening agent component in an amount of about 15% to about 55% by
weight of the liquid hardening agent component.
[0077] In some embodiments, the resin composition may comprise a
liquid hardenable resin component emulsified in a liquid hardening
agent component, wherein the liquid hardenable resin component is
the internal phase of the emulsion and the liquid hardening agent
component is the external phase of the emulsion. In other
embodiments, the liquid hardenable resin component may be
emulsified in water and the liquid hardening agent component may be
present in the water. In other embodiments, the liquid hardenable
resin component may be emulsified in water and the liquid hardening
agent component may be provided separately. Similarly, in other
embodiments, both the liquid hardenable resin component and the
liquid hardening agent component may both be emulsified in
water.
[0078] The optional silane coupling agent may be used, among other
things, to act as a mediator to help bond the resin to formation
particulates or proppant particulates. Examples of suitable silane
coupling agents include, but are not limited to,
N-2-(aminoyl)-3-aminopropyltrimethoxysilane, and
3-glycidoxypropyltrimethoxysilane, and combinations thereof. The
silane coupling agent may be included in the resin component or the
liquid hardening agent component (according to the chemistry of the
particular group as determined by one skilled in the art with the
benefit of this disclosure). In some embodiments of the present
invention, the silane coupling agent used is included in the liquid
hardening agent component in the range of about 0.1% to about 3% by
weight of the liquid hardening agent component.
[0079] Any surfactant compatible with the hardening agent and
capable of facilitating the coating of the resin onto particulates
in the subterranean formation may be used in the liquid hardening
agent component. Such surfactants include, but are not limited to,
an alkyl phosphonate surfactant (e.g., a C.sub.12-C.sub.22 alkyl
phosphonate surfactant), an ethoxylated nonyl phenol phosphate
ester, one or more cationic surfactants, and one or more nonionic
surfactants. Mixtures of one or more cationic and nonionic
surfactants also may be suitable. Examples of such surfactant
mixtures are described in U.S. Pat. No. 6,311,773 issued to Todd et
al. on Nov. 6, 2001, the disclosure of which is incorporated herein
by reference. The surfactant or surfactants that may be used are
included in the liquid hardening agent component in an amount in
the range of about 1% to about 10% by weight of the liquid
hardening agent component.
[0080] While not required, examples of hydrolyzable esters that may
be used in the liquid hardening agent component include, but are
not limited to, a mixture of dimethylglutarate, dimethyladipate,
and dimethylsuccinate; dimethylthiolate; methyl salicylate;
dimethyl salicylate; and dimethylsuccinate; and combinations
thereof. When used, a hydrolyzable ester is included in the liquid
hardening agent component in an amount in the range of about 0.1%
to about 3% by weight of the liquid hardening agent component. In
some embodiments a hydrolyzable ester is included in the liquid
hardening agent component in an amount in the range of about 1% to
about 2.5% by weight of the liquid hardening agent component.
[0081] Use of a diluent or liquid carrier fluid in the liquid
hardening agent component is optional and may be used to reduce the
viscosity of the liquid hardening agent component for ease of
handling, mixing, and transferring. As previously stated, it may be
desirable in some embodiments to not use such a solvent for
environmental or safety reasons. Any suitable carrier fluid that is
compatible with the liquid hardening agent component and achieves
the desired viscosity effects is suitable for use in the present
invention. Some suitable liquid carrier fluids are those having
high flash points (e.g., about 125.degree. F.) because of, among
other things, environmental and safety concerns; such solvents
include, but are not limited to, butyl lactate, dipropylene glycol
methyl ether, dipropylene glycol dimethyl ether, dimethyl
formamide, diethyleneglycol methyl ether, ethyleneglycol butyl
ether, diethyleneglycol butyl ether, propylene carbonate, methanol,
butyl alcohol, d'limonene, and fatty acid methyl esters, and
combinations thereof. Other suitable liquid carrier fluids include
aqueous dissolvable solvents such as, for example, methanol,
isopropanol, butanol, glycol ether solvents, and combinations
thereof. Suitable glycol ether liquid carrier fluids include, but
are not limited to, diethylene glycol methyl ether, dipropylene
glycol methyl ether, 2-butoxy ethanol, ethers of a C.sub.2 to
C.sub.6 dihydric alkanol having at least one C.sub.1 to C.sub.6
alkyl group, mono ethers of dihydric alkanols, methoxypropanol,
butoxyethanol, and hexoxyethanol, and isomers thereof. Combinations
of these may be suitable as well. Selection of an appropriate
liquid carrier fluid is dependent on, inter alia, the resin
composition chosen.
[0082] Other resins suitable for use in the present invention are
furan-based resins. Suitable furan-based resins include, but are
not limited to, furfuryl alcohol resins, furfural resins, mixtures
furfuryl alcohol resins and aldehydes, and a mixture of furan
resins and phenolic resins. Of these, furfuryl alcohol resins may
be preferred. A furan-based resin may be combined with a solvent to
control viscosity if desired. Suitable solvents for use in the
furan-based consolidation fluids of the present invention include,
but are not limited to, 2-butoxy ethanol, butyl lactate, butyl
acetate, tetrahydrofurfuryl methacrylate, tetrahydrofurfuryl
acrylate, esters of oxalic, maleic and succinic acids, and furfuryl
acetate. Of these, 2-butoxy ethanol is preferred. In some
embodiments, the furan-based resins suitable for use in the present
invention may be capable of enduring temperatures well in excess of
350.degree. F. without degrading. In some embodiments, the
furan-based resins suitable for use in the present invention are
capable of enduring temperatures up to about 700.degree. F. without
degrading.
[0083] Optionally, the furan-based resins suitable for use in the
present invention may further comprise a curing agent, inter alia,
to facilitate or accelerate curing of the furan-based resin at
lower temperatures. The presence of a curing agent may be
particularly useful in embodiments where the furan-based resin may
be placed within subterranean formations having temperatures below
about 350.degree. F. Examples of suitable curing agents include,
but are not limited to, organic or inorganic acids, such as, inter
alia, maleic acid, fumaric acid, sodium bisulfate, hydrochloric
acid, hydrofluoric acid, acetic acid, formic acid, phosphoric acid,
sulfonic acid, alkyl benzene sulfonic acids such as toluene
sulfonic acid and dodecyl benzene sulfonic acid ("DDBSA"), and
combinations thereof. In those embodiments where a curing agent is
not used, the furan-based resin may cure autocatalytically.
[0084] Still other resins suitable for use in the methods of the
present invention are phenolic-based resins. Suitable
phenolic-based resins include, but are not limited to, terpolymers
of phenol, phenolic formaldehyde resins, and a mixture of phenolic
and furan resins. In some embodiments, a mixture of phenolic and
furan resins may be preferred. A phenolic-based resin may be
combined with a solvent to control viscosity if desired. Suitable
solvents for use in the present invention include, but are not
limited to butyl acetate, butyl lactate, furfuryl acetate, and
2-butoxy ethanol. Of these, 2-butoxy ethanol may be preferred in
some embodiments.
[0085] Yet another resin-type material suitable for use in the
methods of the present invention is a phenol/phenol
formaldehyde/furfuryl alcohol resin comprising of about 5% to about
30% phenol, of about 40% to about 70% phenol formaldehyde, of about
10% to about 40% furfuryl alcohol, of about 0.1% to about 3% of a
silane coupling agent, and of about 1% to about 15% of a
surfactant. In the phenol/phenol formaldehyde/furfuryl alcohol
resins suitable for use in the methods of the present invention,
suitable silane coupling agents include, but are not limited to,
N-2-(aminoethyl)-3-aminopropyltrimethoxysilane, and
3-glycidoxypropyltrimethoxysilane. Suitable surfactants include,
but are not limited to, an ethoxylated nonyl phenol phosphate
ester, mixtures of one or more cationic surfactants, and one or
more nonionic surfactants and an alkyl phosphonate surfactant.
[0086] Therefore, the present invention is well adapted to attain
the ends and advantages mentioned as well as those that are
inherent therein. The particular embodiments disclosed above are
illustrative only, as the present invention may be modified and
practiced in different but equivalent manners apparent to those
skilled in the art having the benefit of the teachings herein.
Furthermore, no limitations are intended to the details of
construction or design herein shown, other than as described in the
claims below. It is therefore evident that the particular
illustrative embodiments disclosed above may be altered or modified
and all such variations are considered within the scope and spirit
of the present invention. All numbers and ranges disclosed above
may vary by any amount (e.g., 1 percent, 2 percent, 5 percent, or,
sometimes, 10 to 20 percent). Whenever a numerical range, R, with a
lower limit, RL, and an upper limit, RU, is disclosed, any number
falling within the range is specifically disclosed. In particular,
the following numbers within the range are specifically disclosed:
R.dbd.RL+k*(RU-RL), wherein k is a variable ranging from 1 percent
to 100 percent with a 1 percent increment, i.e., k is 1 percent, 2
percent, 3 percent, 4 percent, 5 percent, . . . , 50 percent, 51
percent, 52 percent, . . . , 95 percent, 96 percent, 97 percent, 98
percent, 99 percent, or 100 percent. Moreover, any numerical range
defined by two R numbers as defined in the above is also
specifically disclosed. Moreover, the indefinite articles "a" or
"an", as used in the claims, are defined herein to mean one or more
than one of the element that it introduces. Also, the terms in the
claims have their plain, ordinary meaning unless otherwise
explicitly and clearly defined by the patentee.
* * * * *