U.S. patent application number 12/336839 was filed with the patent office on 2009-10-01 for photovoltaics with interferometric back side masks.
This patent application is currently assigned to QUALCOMM MEMS Technologies, Inc.. Invention is credited to Kasra Khazeni, Manish Kothari.
Application Number | 20090242024 12/336839 |
Document ID | / |
Family ID | 40673151 |
Filed Date | 2009-10-01 |
United States Patent
Application |
20090242024 |
Kind Code |
A1 |
Kothari; Manish ; et
al. |
October 1, 2009 |
PHOTOVOLTAICS WITH INTERFEROMETRIC BACK SIDE MASKS
Abstract
An interferometric mask covers reflective conductors on the back
side of a photovoltaic device. Such an interferometric mask may
reduce reflections of incident light from the conductors. In
various embodiments, the mask reduces reflections, so that a front
and back electrode pattern appears black or similar in color to
surrounding features of the device. In other embodiments, the mask
may modulate reflections of light such that the electrode pattern
matches a color in the visible spectrum.
Inventors: |
Kothari; Manish; (Cupertino,
CA) ; Khazeni; Kasra; (San Jose, CA) |
Correspondence
Address: |
KNOBBE, MARTENS, OLSON & BEAR, LLP
2040 MAIN STREET, FOURTEENTH FLOOR
IRVINE
CA
92614
US
|
Assignee: |
QUALCOMM MEMS Technologies,
Inc.
San Diego
CA
|
Family ID: |
40673151 |
Appl. No.: |
12/336839 |
Filed: |
December 17, 2008 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61014405 |
Dec 17, 2007 |
|
|
|
Current U.S.
Class: |
136/256 ;
257/E31.127; 438/69 |
Current CPC
Class: |
H01L 31/022425 20130101;
Y02E 10/50 20130101; G02B 26/001 20130101; G02B 5/284 20130101;
H01L 31/02168 20130101 |
Class at
Publication: |
136/256 ; 438/69;
257/E31.127 |
International
Class: |
H01L 31/0232 20060101
H01L031/0232; H01L 31/18 20060101 H01L031/18 |
Claims
1. A photovoltaic device defining a front side on which light is
incident and a back side opposite the front side, the photovoltaic
device comprising: a photovoltaic active material; a conductor on
the back side of the photovoltaic material; and an optical
interferometric mask over the back side of the conductor.
2. The photovoltaic device of claim 1, wherein the optical
interferometric mask is configured such that a color of light
reflected from the mask substantially matches a color of
surrounding features on the back side of the photovoltaic
device.
3. The photovoltaic device of claim 2, wherein the optical
interferometric mask is configured such that the color of light
reflected from the mask substantially matches a color in the
visible spectrum.
4. The photovoltaic device of claim 1, wherein the light reflected
from the optical interferometric mask falls within the wavelengths
associated with the visible spectrum.
5. The photovoltaic device of claim 1, wherein the optical
interferometric mask is configured such that little or no incident
visible light is reflected from the back side of the
interferometric mask such that the interferometric mask appears
black from a normal viewing angle.
6. The photovoltaic device of claim 1, wherein the optical
interferometric mask is configured such that the reflectivity in
the visible range from the mask is less than 10%.
7. The photovoltaic device of claim 1, wherein the optical
interferometric mask comprises: a reflective surface; an optical
resonant cavity over the back of the reflective surface; and an
absorber over the back of the optical resonant cavity.
8. The photovoltaic device of claim 7, wherein the reflective
surface is defined by a separate metallic reflector layer between
the conductor and the optical resonant cavity.
9. The photovoltaic device of claim 7, wherein the reflective
surface is defined by the back surface of the conductor.
10. The device of claim 1, wherein the photovoltaic device is
incorporated into a window.
11. The photovoltaic device of claim 1, further comprising: a
display; a processor that is configured to communicate with said
display, said processor being configured to process image data; and
a memory device that is configured to communicate with said
processor.
12. The photovoltaic device as recited in claim 11, further
comprising: a driver circuit configured to send at least one signal
to said display.
13. The photovoltaic device as recited in claim 12, further
comprising: a controller configured to send at least a portion of
said image data to said driver circuit.
14. A photovoltaic device comprising: means for generating an
electrical current from incident light on a side of said means;
front side means and back side means for conducting the generated
electrical current; and means for interferometrically masking said
back side conducting means from the incident side of the
photovoltaic device.
15. A method of manufacturing a photovoltaic device, comprising
providing a photovoltaic generator with a photovoltaic active
layer, a front side conductor and a back side conductor, the front
side conductor configured to allow light through the front side to
the photovoltaic active layer; and forming a plurality of layers
over the back side conductor of the photovoltaic generator to
define an interferometric modulator configured to mask the back
side conductor.
16. The method of claim 15, wherein the interferometric modulator
is integrated with the back side of the photovoltaic device.
17. The method of claim 16, wherein the interferometric modulator
is deposited across the back side conductor.
18. The method of claim 17, wherein the interferometric modulator
extends beyond the surface of the back side conductor by less than
about 10%.
19. The method of claim 18, wherein the interferometric modulator
extends beyond the surface of the back side conductor by less than
about 5%.
20. The method of claim 15, wherein the interferometric modulator
is patterned across the back side conductor.
21. The method of claim 20, wherein the interferometric modulator
comprises an absorber, an optical resonant cavity, and a conductor,
wherein the absorber is patterned to follow a pattern of the back
side conductor.
22. The method of claim 21, wherein the optical resonant cavity is
patterned to follow a pattern of the back side conductor.
23. The method of claim 21, wherein the absorber and optical
resonant cavity are configured to reflect visible light
substantially matching a visible spectrum reflected by exposed
portions of the photovoltaic device.
24. A method of manufacturing a photovoltaic device having a front
side on which light is incident and a back side opposite the front
side, the method comprising forming an interferometric modulator
configured to reduce visible reflections from the back side of the
photovoltaic device.
25. The method of claim 24, wherein the interferometric modulator
interferometrically produces a black appearance.
26. The method of claim 24, wherein the interferometric modulator
interferometrically produces a coherent color in the visible
spectrum.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application claims the benefit of U.S. Provisional
Patent Application No. 61/014,405, filed on Dec. 17, 2007, the
entire contents of which are incorporated by reference and should
be considered a part of this specification.
[0002] The present application is related to U.S. patent
application Ser. No. 11/950,392, filed Dec. 4, 2007 (Atty. Docket
No. QMRC.007A/080171), to U.S. Provisional Application No.
61/002,198, filed on Nov. 7, 2007 (Atty. Docket No.
QMRC.007PR/080171P1), and to U.S. patent application Ser. No.
Unknown, filed on even date herewith (Atty. Docket No.
QMRC.008A2/080419U2).
BACKGROUND
[0003] 1. Field of the Invention
[0004] The present invention relates generally to the field of
optoelectronic transducers that convert optical energy into
electrical energy, such as for example photovoltaic cells.
[0005] 2. Description of the Related Technology
[0006] For over a century fossil fuel such as coal, oil, and
natural gas has provided the main source of energy in the United
States. The need for alternative sources of energy is increasing.
Fossil fuels are a non-renewable source of energy that are
depleting rapidly. The large scale industrialization of developing
nations such as India and China has placed a considerable burden on
the available fossil fuels. In addition, geopolitical issues can
quickly affect the supply of such fuels. Global warming is also of
greater concern in recent years. A number of factors are thought to
contribute to global warming; however, widespread use of fossil
fuels is presumed to be a main cause of global warming. Thus there
is an urgent need to find a renewable and economically viable
source of energy that is also environmentally safe. Solar energy is
an environmentally safe renewable source of energy that can be
converted into other forms of energy such as heat and
electricity.
[0007] Photovoltaic (PV) cells convert optical energy to electrical
energy and thus can be used to convert solar energy into electrical
power. Photovoltaic solar cells can be made very thin and modular.
PV cells can range in size from a few millimeters to 10's of
centimeters. The individual electrical output from one PV cell may
range from a few milliwatts to a few watts. Several PV cells may be
connected electrically and packaged in arrays to produce sufficient
amount of electricity. PV cells can be used in a wide range of
applications such as providing power to satellites and other
spacecraft, providing electricity to residential and commercial
properties, charging automobile batteries, etc.
[0008] While PV devices have the potential to reduce reliance upon
hydrocarbon fuels, the widespread use of PV devices has been
hindered by inefficiency and aesthetic concerns. Accordingly,
improvements in either of these aspects could increase usage of PV
devices.
SUMMARY OF CERTAIN INVENTIVE ASPECTS
[0009] In one embodiment, a photovoltaic device, defining a front
side on which light is incident and a back side opposite the front
side, includes a photovoltaic active material. A conductor is
positioned on the back side of the photovoltaic material. An
optical interferometric mask is positioned over the back side of
the conductor.
[0010] In another embodiment, a photovoltaic device includes a
means for generating an electrical current from incident light on a
side of said means. The device also includes a front side means and
a back side means for conducting the generated electrical current,
as well as a means for interferometrically masking the back side
conducting means from the incident side of the photovoltaic
device.
[0011] In another embodiment, a method of manufacturing a
photovoltaic device includes providing a photovoltaic generator
with a photovoltaic active layer, a front side conductor and a back
side conductor. The front side conductor is configured to allow
light through the front side to the photovoltaic active layer. A
plurality of layers is formed over the back side conductor of the
photovoltaic generator to define an interferometric modulator
configured to mask the back side conductor.
[0012] In another embodiment, a method of manufacturing a
photovoltaic device, having a front side on which light is incident
and a back side opposite the front side, includes forming an
interferometric modulator configured to reduce visible reflections
from the back side of the photovoltaic device.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] Example embodiments disclosed herein are illustrated in the
accompanying schematic drawings, which are for illustrative
purposes only.
[0014] FIG. 1 schematically illustrates a theoretical optical
interferometric cavity.
[0015] FIG. 2 schematically illustrates a plurality of layers
forming one implementation of an optical interferometric
modulator.
[0016] FIG. 3A is a block diagram of an interferometric modulator
("IMOD") stack, similar to that of FIG. 2, comprising an absorber
layer, an optical resonant cavity and a reflector.
[0017] FIG. 3B schematically illustrates an IMOD where the optical
cavity includes an air gap formed by posts or pillars between the
absorber and reflector layers.
[0018] FIG. 3C illustrates an embodiment of an IMOD, wherein the
optical resonant cavity can be adjusted electromechanically, in an
"open" state.
[0019] FIG. 3D illustrates an IMOD, wherein the optical resonant
cavity can be adjusted electromechanically, in a "closed"
state.
[0020] FIG. 4 shows the total reflection versus wavelength of an
interferometric light modulator with an optical cavity configured
to reflect yellow for normally incident broadband white light.
[0021] FIG. 5 shows the total reflection versus wavelength with an
optical cavity configured to minimize visible reflections for
normally incident broadband white light.
[0022] FIG. 6 shows the total reflection versus wavelength of an
interferometric light modulator like that of FIG. 5 when the angle
of incidence or view angle is approximately 30 degrees to
normal.
[0023] FIG. 7 schematically illustrates a photovoltaic cell
comprising a p-n junction.
[0024] FIG. 8 is a block diagram that schematically illustrates a
photocell comprising a deposited thin film or deposited
photovoltaic active material.
[0025] FIGS. 9A and 9B are schematic plan and isometric sectional
views depicting an example of a solar photovoltaic device with
visible reflective electrodes on the front side.
[0026] FIGS. 10A-10G are schematic cross-sectional views
illustrating steps in a process of manufacturing an embodiment of
an interferometric modulator (IMOD) mask integrated with a
photovoltaic device, where the IMOD mask is patterned together with
photovoltaic device front electrodes.
[0027] FIG. 10H is a schematic cross-sectional view of the
photovoltaic device of FIG. 10G after formation of a protective
film over the IMOD mask.
[0028] FIGS. 11A-D are schematic cross-sectional views illustrating
steps of adding an IMOD mask over a photovoltaic device in
accordance with another embodiment, wherein at least one layer
defining a optical resonant cavity for the IMOD mask remains
unpatterned.
[0029] FIG. 12 is a schematic cross-sectional view of a
photovoltaic device with an IMOD mask covering electrodes in
accordance with another embodiment, wherein the IMOD mask comprises
layers that are patterned to be slightly wider than the
photovoltaic device front electrodes.
[0030] FIGS. 13A-13E are schematic cross-sectional views
illustrating steps in a process of manufacturing a thin film
photovoltaic device on a transparent substrate, with an integrated
IMOD mask.
[0031] FIG. 13F is a schematic cross-sectional view of another
embodiment of an IMOD mask integrated with a thin film photovoltaic
device on a transparent substrate, wherein at least one layer
defining a optical resonant cavity for the IMOD mask remains
unpatterned.
[0032] FIG. 13G is a schematic cross-sectional view of another
embodiment of an IMOD mask integrated on a front side of a
transparent substrate, opposite the side of the substrate with
active photovoltaic material.
[0033] FIGS. 14A and 14B are schematic cross-sectional views of a
photovoltaic device formed with a single crystal semiconductor
photovoltaic device, with and without an IMOD mask formed over the
front electrodes.
[0034] FIG. 15 is a schematic cross-sectional view of an embodiment
of an interferometrically-enhanced photovoltaic device with an
integrated IMOD mask.
[0035] FIG. 16 is a schematic cross-sectional view of an embodiment
of an interferometrically-enhanced photovoltaic device in which an
integrated IMOD mask is operatively coupled to the back
electrode.
[0036] FIG. 17A is a schematic cross-sectional view of an
embodiment of a conductive ribbon with an integrated IMOD mask on
one side.
[0037] FIG. 17B is a schematic cross-sectional view of a
photovoltaic device with masked ribbons, like that of FIG. 17A,
attached to electrodes of the photovoltaic device, for
interconnection of multiple photovoltaic devices.
[0038] FIG. 18A is a schematic cross-sectional view of another
embodiment of a conductive ribbon with an integrated IMOD mask
covering both sides of the ribbon conductor.
[0039] FIG. 18B is a schematic cross-sectional view of a
photovoltaic device with masked ribbons, like that of FIG. 18A,
attached to electrodes of the photovoltaic device, for
interconnection of multiple photovoltaic devices.
[0040] FIG. 19 is a schematic cross-sectional view of an embodiment
of an interferometrically-enhanced photovoltaic ribbon in which the
ribbon conductor and the photovoltaic layers are manufactured
separately for integration on a photovoltaic device.
[0041] FIG. 20 is a schematic top-down view of a plurality of
photovoltaic devices, wafers or cells interconnected by a
conductive ribbon.
DETAILED DESCRIPTION OF CERTAIN EMBODIMENTS
[0042] One issue hindering widespread adoption of photovoltaic (PV)
devices on available surfaces for conversion of light energy into
electric energy or current is the undesirable aesthetic appearance
of conductors or electrodes on the PV devices. The high
reflectivity of common front electrode materials contrasts with the
darker appearance of the active PV material itself, and furthermore
hinders the blending of PV devices with surrounding materials.
Embodiments described herein below employ interferometric modulator
(IMOD) constructions designed to darken, hide or blend electrodes,
thus providing an IMOD mask over conductors for PV devices. Light
incident on the IMOD mask results in little or no visible
reflection in the region of the electrodes due to the principles of
optical interference. The interferometric masking effect is
governed by the dimensions and fundamental optical properties of
the materials making up the IMOD mask. Accordingly, the masking
effect is not as susceptible to fading over time, compared to
common dyes or paints.
[0043] Although certain preferred embodiments and examples are
discussed herein, it will be understood that the inventive subject
matter extends beyond the specifically disclosed embodiments to
other alternative embodiments and/or uses of the invention and
obvious modifications and equivalents thereof. It is intended that
the scope of the invention disclosed herein should not be limited
by the particular disclosed embodiments. Thus, for example, in any
method or process disclosed herein, the acts or operations making
up the method/process may be performed in any suitable sequence and
are not necessarily limited to any particular disclosed sequence
unless specifically noted. Various aspects and advantages of the
embodiments have been described where appropriate. It is to be
understood that not necessarily all such aspects or advantages may
be achieved in accordance with any particular embodiment. Thus, for
example, it should be recognized that the various embodiments may
be carried out in a manner that achieves or optimizes one advantage
or group of advantages as taught herein without necessarily
achieving other aspects or advantages as may be taught or suggested
herein. The following detailed description is directed to certain
specific embodiments of the invention. However, the invention can
be embodied in a multitude of different ways. The embodiments
described herein may be implemented in a wide range of devices that
include photovoltaic devices for collection and conversion of
optical energy to electrical energy.
[0044] In this description, reference is made to the drawings
wherein like parts are designated with like numerals throughout. As
will be apparent from the following description, the embodiments
may be implemented in a variety of devices that comprise
photovoltaic active material.
[0045] FIG. 1 illustrates an optical resonant cavity. An example of
such an optical resonant cavity is a soap film which may produce a
spectrum of reflected colors. The optical resonant cavity shown in
FIG. 1 comprises two interfaces or surfaces 101 and 102. The two
surfaces 101 and 102 may be opposing surfaces on the same layer.
For example, the two surfaces 101 and 102 may comprise surfaces on
a glass or plastic plate or sheet or a film of glass, plastic, or
any other transparent material. Air or other media may surround the
plate, sheet, or film. In the illustrated example, light partially
reflects and partially transmits at each of interfaces 101,
102.
[0046] A ray of light 103 that is incident on the front surface 101
of the optical resonant cavity is partially reflected as indicated
by the light path 104 and partially transmitted through the front
surface 101 along light path 105. The transmitted light may be
partially reflected along light path 107 and partially transmitted
out of the resonant cavity along light path 106. The amount of
light transmitted and reflected may depend on the refractive
indices of the material that forms the optical resonant cavity and
of the surrounding medium. The example is simplified by omission of
multiple internal reflections, as will be appreciated by the
skilled artisan.
[0047] For purposes of the discussions provided herein, the total
intensity of light reflected from the optical resonant cavity is a
coherent superposition of the two reflected light rays 104 and 107.
With such coherent superposition, both the amplitude and the phase
of the two reflected beams contribute to the aggregate intensity.
This coherent superposition is referred to as interference. The two
reflected rays 104 and 107 may have a phase difference with respect
to each other. In some embodiments, the phase difference between
the two waves may be 180 degrees and cancel each other out. If the
phase and the amplitude of the two light rays 104 and 107 are
configured so as to reduce the intensity then the two light beams
are referred to as interfering destructively. If on the other hand
the phase and the amplitude of the two light beams 104 and 107 are
configured so as to increase the intensity then the two light rays
are referred to as interfering constructively. The phase difference
depends on the optical path difference of the two paths, which
depends both on the thickness of the optical resonant cavity, the
index of refraction of the material(s) between the two surfaces 101
and 102, and whether the indices of surrounding materials are
higher or lower than the material forming the optical resonant
cavity. The phase difference is also different for different
wavelengths in the incident beam 103. Accordingly, in some
embodiments the optical resonant cavity may reflect a specific set
of wavelengths of the incident light 103 while transmitting other
wavelengths of the incident light 103. Thus some wavelengths may
interfere constructively and some wavelengths may interfere
destructively. In general, the colors and the total intensity
reflected and transmitted by the optical resonant cavity thus
depend on the thickness and the material(s) forming the optical
resonant cavity and surrounding media. The reflected and
transmitted wavelengths also depend on viewing angle, different
wavelengths being reflected and transmitted at different
angles.
[0048] In FIG. 2, an optical resonant cavity is defined between two
layers. In particular, an absorber layer 201 defines the top or
front surface 101 of the optical resonant cavity while a bottom
reflector layer 202 defines the bottom or back surface 102 of the
optical resonant cavity. The thicknesses of the absorber and
reflector layers may be substantially different from each other.
For example, the absorber layer 201 will typically be thinner than
the bottom reflector layer 202 and is designed to be partially
transmissive. The absorber and reflector layers may comprise metal.
As shown in FIG. 2, the ray of light 203 that is incident on the
absorber layer 201 of the optical interference cavity is partially
reflected out of the optical interference cavity along each of the
paths 204 and 207. The illumination field as viewed by an observer
on the front or incident side is a superposition of the two
reflected rays 204 and 207. The amount of light substantially
absorbed by the device or transmitted out of the device through the
bottom reflector 202 can be significantly increased or reduced by
varying the thickness and the composition of the reflector layers
201, 202, whereas the apparent color of reflections is largely
determined by the interference effect governed by the size or
thickness of the optical resonant cavity between them and the
material properties of the absorber layer 201.
[0049] In some embodiments, the optical cavity between the front
and back surfaces 101, 102 is defined by a layer, such as an
optically transparent dielectric layer, or plurality of layers. In
other embodiments, the optical resonant cavity between the front
and back surfaces 101, 102 is defined by an air gap or combination
of optically transparent layer(s) and an air gap. The size of the
optical interference cavity may be tuned to maximize or minimize
the reflection of one or more specific colors of the incident
light. The color or colors reflected by the optical interference
cavity may be changed by changing the thickness of the cavity.
Accordingly, the color or colors reflected by the optical
interference cavity may depend on the thickness of the cavity. When
the cavity height is such that particular wavelength(s) are
maximized or minimized by optical interference, the structure is
referred to herein as an interferometric modulator (IMOD). An IMOD
may be static (fixed) or dynamic (active).
[0050] In certain embodiments, the optical resonant cavity height
between the top absorber and the bottom reflector may be actively
varied for example by microelectromechanical systems (MEMS). MEMS
include micromechanical elements, actuators, and electronics.
Micromechanical elements may be created using deposition, etching,
and/or other micromachining processes that etch away or remove
parts of substrates and/or deposited material layers or that add
layers to form electrical and electromechanical devices. Such MEMS
devices include IMODs having an optical resonant cavity that can be
adjusted electromechanically. An IMOD selectively absorbs and/or
reflects light using the principles of optical interference. In
certain embodiments, an interferometric modulator may comprise a
pair of conductive plates, one of which is partially reflective and
partially transmissive and the other of which is partly or totally
reflective. The conductive plates are capable of relative motion
upon application of an appropriate electrical signal. In a
particular embodiment, one plate may comprise a stationary layer
deposited on a substrate and the other plate may comprise a
metallic membrane separated from the stationary layer by an air
gap. As described herein in more detail, the position of one plate
in relation to another can change the optical interference of light
incident on the interferometric modulator. In this manner, the
color of light output by a MEMS interferometric modulator (IMOD)
can be actively varied.
[0051] Using such a MEMS-adjustable optical interference cavity, or
MEMS IMOD, it is possible to provide at least two states. A first
state comprises an optical interference cavity of a certain
dimension whereby light of a selected color (based upon the size of
the cavity) interferes constructively and is reflected out of the
cavity. A second state comprises a visible black state produced due
to constructive and/or destructive interference of light, such that
visible wavelength are substantially absorbed. Alternatively, the
two states can be colored and broad spectrum (white)
reflective.
[0052] FIG. 3A is a simplified schematic of an IMOD stack 300. As
illustrated, the IMOD stack 300 comprises an absorber layer 301, a
reflector 303, and an optical resonant cavity 302 formed between
the absorber layer 301 and the reflector 303. The reflector 303
may, for example, comprise a metal layer, such as aluminum, and is
typically thick enough to be opaque (e.g., 300 nm). The optical
resonant cavity 302 may comprise an air gap and/or one or more
optically transparent materials. If the optical resonant cavity 302
is defined by a single layer between the reflector 303 and the
absorber layer 301, a transparent conductor or transparent
dielectric may be used. In some embodiments, the optical resonant
cavity 302 can comprise a composite structure comprising multiple
materials that may include two or more of an air gap, a transparent
conducting material, and a transparent dielectric layer. A possible
advantage of multiple layers and/or air gaps is that selected
layers of the stack may serve multiple functions, such as device
passivation or scratch resistance in addition to its optical role
in the IMOD stack 300. In some embodiments, the optical resonant
cavity may comprise one or more partially transparent materials,
whether conductive or dielectric. Exemplary transparent materials
for the optical interference cavity 302 may comprise a transparent
conductive oxide (TCO), such as indium tin oxide (ITO), and/or a
dielectric, such as silicon dioxide (SiO.sub.2).
[0053] In this embodiment light passes through the IMOD stack 300
first by passing into the absorber layer 301. Some light passes
through the partially transmissive absorber layer 301, through the
optical interference cavity 302, and is reflected off the reflector
303 back through the optical resonant cavity 302 and through the
absorber layer 301.
[0054] With reference to FIG. 3B, in other embodiments, the
thickness of the optical resonant cavity 302 may comprise an air
gap 302 supported by spacers 311, such as rails, posts or pillars.
Within the IMOD 300, the optical resonant or interference cavity
302 may be an air gap that is static, or one that is dynamic, i.e.,
variable using, for example, MEMS technology.
[0055] An interferometric modulator (IMOD) structure such as shown
in FIG. 3A or 3B selectively produces a desired reflection output
using optical interference. This reflected output may be
"modulated" by selection of the thickness and optical properties of
the optical resonant cavity 302, as well as the thickness and
optical properties of the absorber 301 and the reflector 303. The
reflected output may also be varied dynamically using a MEMS device
to change the size of the optical resonant cavity 302. The color
observed by a viewer viewing the surface of the absorber 301 will
correspond to those frequencies that are substantially reflected
out of the IMOD and are not substantially absorbed or destructively
interfered by the various layers of the IMOD. The frequencies that
interfere and are not substantially absorbed can be varied by
selecting the thickness of the optical resonant cavity 302.
[0056] FIGS. 3C and 3D show an embodiment of an IMOD wherein the
optical resonant cavity (302 in FIG. 3B) includes an air gap and
can be electromechanically changed using MEMS technology. FIG. 3C
illustrates an IMOD configured to be in the "open" or "relaxed"
state and FIG. 3D illustrates an IMOD configured to be in the
"closed" or "collapsed" state. The IMOD illustrated in FIGS. 3C and
3D comprises a substrate 320, a thin film stack 330 and a
reflective membrane 303. The thin film stack 330 may comprise an
absorber (corresponding to 303 in FIGS. 3A and 3B) as well as other
layers and materials, such as a separate transparent electrode
layer and a dielectric layer to keep the electrodes insulated from
one another. In some embodiments, the thin film stack 330 may be
attached to the substrate 320. In the "open" state, the thin film
stack 330 is separated from the reflective membrane 303 by a gap
340. In some embodiments, for example, as illustrated in FIG. 3C,
the gap 340 may be an air gap, supported by spacers 311, such as
rails, pillars or posts. In the "open" state, the thickness of the
gap 340 can vary, for example, between 120 nm and 400 nm (e.g.,
approximately 260 nm) in some embodiments. Hence, in the "open"
state, the optical resonant cavity of FIGS. 3A and 3B comprises the
air gap together with any transparent layers over the absorber
within the thin film stack 330.
[0057] In certain embodiments, the IMOD can be switched from the
"open" state to the "closed" state by applying a voltage difference
between the thin film stack 330 and the reflective membrane 303 as
illustrated in FIG. 3D. In the "closed" state, the optical cavity
over the absorber between the thin film stack 330 and the
reflective membrane 303 is defined by, e.g., a dielectric layer
overlying the absorber in the thin film stack 330, and is typically
configured to reflect "black" or minimal visible reflections. The
thickness of the air gap in general can vary between approximately
0 nm and approximately 2000 nm, for example, between "open" and
"closed" states in some embodiments.
[0058] In the "open" state, one or more frequencies of the incident
light interfere constructively above the surface of the substrate
320. Accordingly, some frequencies of the incident light are not
substantially absorbed within the IMOD but instead are reflected
from the IMOD. The frequencies that are reflected out of the IMOD
interfere constructively outside the IMOD. The display color
observed by a viewer viewing the surface of the substrate 320 will
correspond to those frequencies that are substantially reflected
out of the IMOD and are not substantially absorbed by the various
layers of the IMOD. The frequencies that interfere constructively
and are not substantially absorbed can be varied by changing the
thickness of the optical cavity (which includes the gap 340),
thereby changing the thickness of the optical resonant cavity.
[0059] FIG. 4 illustrates a graph of total reflection of an IMOD
(for example, the IMOD 300 of FIG. 3A or 3B) versus wavelength as
seen from a direction normal or perpendicular to the front surface
of the IMOD. The graph of total reflection shows a reflection peak
at approximately 550 nm (yellow). A viewer viewing the IMOD will
observe the IMOD to be yellow. As mentioned previously, the
location of the peak of the total reflection curve can be shifted
by changing either the thickness or material of the optical
resonant cavity 302 or by changing the material and thickness of
one or more layers in the stack.
[0060] FIG. 5 illustrates a graph of total reflection of the IMOD
versus wavelength over a wavelength range of approximately 400 nm
to 800 nm for an IMOD with an optical cavity thickness selected to
minimize reflections in the visible range. It is observed that the
total reflection is uniformly low in the entire visible wavelength
range. Thus very little light is reflected out of the
interferometric modulator. The color observed by a viewer looking
perpendicularly at the front surface of the IMOD may generally be
black, reddish black or purple in some embodiments.
[0061] Generally, an IMOD stack can have a view angle dependency.
However, when an optical resonant cavity is selected to minimize
IMOD reflection in the visible range, the angle dependency tends to
be fairly low. FIG. 6 illustrates total reflection versus
wavelength for an IMOD with an optical resonant cavity, optimized
to minimize visible reflections, when the angle of incidence or
view angle is 30 degrees. It is observed that the total reflection
is uniformly low in the entire visible wavelength range. Thus very
little visible light is reflected out of the interferometric
modulator. A comparison of FIGS. 5 and 6 shows that the spectral
response of the IMOD with a cavity 302 chosen or modulated to
minimize visible reflection is approximately the same for normal
incidence and when the angle of incidence or view angle is 30
degrees. In other words, the spectral response of a "black" IMOD,
with a cavity selected to minimize visible reflections, does not
exhibit a strong dependency on the angle of incidence or the view
angle.
[0062] FIG. 7 shows a typical photovoltaic (PV) cell 700. A typical
photovoltaic cell can convert light energy into electrical energy
or current. A PV cell is an example of a renewable source of energy
that has less impact on the environment, e.g., a small carbon
footprint. Using PV cells can provide possible cost benefits, such
as reducing the cost of energy generation. PV cells can have many
different sizes and shapes, e.g., from smaller than a postage stamp
to several inches across. Several PV cells can often be connected
together to form PV cell modules that may be up to several feet
long and a few feet wide. Modules, in turn, can be combined and
connected to form PV arrays of different sizes and power
output.
[0063] The size of an array can depend on several factors, such as
the amount of sunlight available in a particular location and the
needs of the consumer. The modules of the array can include
electrical connections, mounting hardware, power-conditioning
equipment, and batteries that store solar energy for use when the
sun is not shining. A PV device can be a single cell with its
attendant electrical connections and peripherals, or a PV module or
a PV array. A PV device can also include functionally unrelated
electrical components, e.g., components that are powered by the PV
cell(s).
[0064] A typical PV cell comprises a PV active region disposed
between two electrodes. In some embodiments, the PV cell comprises
a substrate on which a stack of layers is formed. The PV active
layer of a PV cell may comprise a semiconductor material such as
silicon. In some embodiments, the active region may comprise a p-n
junction formed by contacting an n-type semiconductor material 703
and a p-type semiconductor material 704 as shown in FIG. 7. Such a
p-n junction may have diode-like properties and may therefore be
referred to as a photodiode structure as well.
[0065] The PV active layer(s) 703, 704 are sandwiched between two
electrodes that provide an electrical current path. The back
electrode 705 can be formed of aluminum, silver, molybdenum or some
other conducting material. The back electrode can be rough and
unpolished. The front electrode 701 is designed to cover a
significant portion of the front surface of the p-n junction so as
to lower contact resistance and increase collection efficiency. In
embodiments wherein the front electrode 701 is formed of an opaque
material, the front electrode 701 is configured to leave openings
or windows over the front of the PV active layer to allow
illumination to impinge on the PV active layer. In some
embodiments, the front electrodes can include a transparent
conductor, for example, transparent conducting oxide (TCO) such as
tin oxide (SnO.sub.2) or indium tin oxide (ITO). The TCO can
provide good electrical contact and conductivity and simultaneously
be transparent to the incoming light. In some embodiments, the PV
cell can also comprise a layer of anti-reflective (AR) coating 702
disposed over the front electrode 701. The layer of AR coating 702
can reduce the amount of light reflected from the front surface of
the PV active layer(s) 703, 704.
[0066] When the front surface of the active PV material is
illuminated, photons transfer energy to electrons in the active
region. If the energy transferred by the photons is greater than
the band-gap of the semiconducting material, the electrons may have
sufficient energy to enter the conduction band. An internal
electric field is created with the formation of the p-n junction.
The internal electric field operates on the energized electrons to
cause these electrons to move, thereby producing a current flow in
an external circuit 707. The resulting current flow can be used to
store charge or directly power various electrical devices, such as
a light bulb 706 as shown in FIG. 7.
[0067] In some embodiments, the p-n junction shown in FIG. 7 can be
replaced by a p-i-n junction wherein an intrinsic or undoped
semiconducting layer is sandwiched between a p-type and an n-type
semiconductor. A p-i-n junction may have higher efficiency than a
p-n junction. In some other embodiments, the PV cell can comprise
multiple junctions.
[0068] The PV active layer(s) can be formed by any of a variety of
light absorbing, photovoltaic materials such as crystalline silicon
(c-silicon), amorphous silicon (.alpha.-silicon), cadmium telluride
(CdTe), copper indium diselenide (CIS), copper indium gallium
diselenide (CIGS), light absorbing dyes and polymers, polymers
dispersed with light absorbing nanoparticles, III-V semiconductors
such as GaAs, etc. Other materials may also be used. The light
absorbing material(s) where photons are absorbed and energy
transferred to electrical carriers (holes and electrons) is
referred to herein as the PV active layer of the PV cell, and this
term is meant to encompass multiple active sub-layers. The material
for the PV active layer can be chosen depending on the desired
performance and the application of the PV cell.
[0069] In some embodiments, the PV cell can be formed by using thin
film technology. For example, in one embodiment, where optical
energy passes through a transparent substrate, the PV cell may be
formed by depositing a first or front electrode layer of TCO on a
substrate. PV active material is deposited on the first electrode
layer. A second electrode layer can be deposited on the layer of PV
active material. The layers may be deposited using deposition
techniques such as physical vapor deposition techniques, chemical
vapor deposition techniques, electrochemical deposition techniques,
etc. Thin film PV cells may comprise amorphous or polycrystalline
materials such as thin-film silicon, CIS, CdTe or CIGS. Some
advantages of thin film PV cells are small device footprint and
scalability of the manufacturing process, among others.
[0070] FIG. 8 is a block diagram schematically illustrating a
typical thin film PV cell 800. The typical PV cell 800 includes a
glass substrate 801 through which light can pass. Disposed on the
glass substrate 801 are a first electrode layer 802, a PV active
layer 803 (shown as comprising amorphous silicon), and a second
electrode layer 805. The first electrode layer 802 can comprise a
transparent conducting material such as ITO. As illustrated, the
first electrode layer 802 and the second electrode layer 805
sandwich the thin film PV active layer 803 therebetween. The
illustrated PV active layer 803 comprises an amorphous silicon
layer. As is known in the art, amorphous silicon serving as a PV
material may comprise one or more diode junctions. Furthermore, an
amorphous silicon PV layer or layers may comprise a p-i-n junction
wherein a layer of intrinsic silicon is sandwiched between a
p-doped layer and an n-doped layer.
[0071] As illustrated in FIGS. 9A and 9B, many PV devices employ
specular or reflective conductors 910, 911 on a front, or
light-incident, side of the device, as well as on a back side of
the PV device 900. Conductors on the front or light-incident side
can comprise bus electrodes 910 or gridline electrodes 911. When
optical energy is absorbed by the PV active material 903,
electron-hole pairs are generated. These electrons and holes can
generate current by moving to one or the other of the front
electrodes 910, 911 or back electrodes 905, as shown in FIG. 9B.
The front conductors or electrodes 910, 911 are patterned to both
reduce the distance an electron or hole must travel to reach an
electrode while also allowing enough light to pass through to the
PV active layer 903. However, the lines of bright reflections
generated by these electrodes are often considered to be
unattractive, such that PV devices are often not employed in
visible locations.
[0072] Accordingly, some embodiments below describe methods of
covering unsightly electrodes so that the electrode pattern appears
dark or black to better match the appearance of exposed PV active
regions. Furthermore, some embodiments described below provide
photovoltaic devices that are uniform in appearance so that they
can better blend in with surrounding structures (e.g., rooftop
tiles). This may be achieved either by darkening the portion of the
front of the PV device that has patterned electrodes, or by
rendering the entire front surface (electrodes and active regions)
of the photovoltaic device dark.
[0073] One way of darkening or otherwise masking the electrode so
as to suppress reflections from a conducting layer or electrode is
to use an interferometric modulator (IMOD) as a mask, with
reflectance tuned to darken the electrodes and/or blend with the
color appearance of exposed PV active regions. In the IMOD stack,
the function of the IMOD reflector (e.g., reflector 303 of FIG. 3A
or 3B) can be served by the conductor being masked (e.g., front bus
electrodes 910 or grid line electrodes 911 of FIGS. 9A and 9B).
Light incident on the IMOD mask results in little or no visible
reflection in the region of the electrodes due to the principles of
optical interference discussed above. Advantageously, the
interferometric effect is governed by the thickness and material(s)
of the absorber and optical resonant cavity. Accordingly, the
masking effect is not as susceptible to fading over time compared
to common dyes or paints.
[0074] FIGS. 10A-10G illustrate one example of a process for
fabricating a PV device incorporating an IMOD mask on front
electrodes. The example employs a deposited thin film of PV active
material. In one embodiment, such a photovoltaic device may be
formed on a substrate 1010 such as plastic, glass or another
suitable workpiece. As illustrated in FIG. 10A, a method of
manufacturing such a device can comprise forming a back electrode
1020 on a substrate 1010 using known methods. A metal layer may be
deposited to serve as the back electrode 1020 for a photovoltaic
device, but non-metal conducting materials can also be used.
[0075] With reference to FIG. 10B, the method further includes
formation of a photovoltaic active material 1030. In the
illustrated embodiment, the photovoltaic (PV) active material 1030
comprises a deposited thin film, although in other arrangements
portions of single crystal, semiconductor substrates and/or
epitaxial layers thereover are employed. A deposited PV active
material can comprise, for example, an amorphous silicon thin film,
which has recently been gaining in popularity. Amorphous silicon as
thin films can be deposited over large areas by physical vapor
deposition (PVD), chemical vapor deposition (CVD), electrochemical
vapor deposition, or plasma-enhanced chemical vapor deposition
(PECVD), as well as by other methods known to those of skill in the
art. As is known by those with skill in the art, PV active
materials comprising amorphous silicon layers may include one or
more junctions with n-doped and/or p-doped silicon and may further
comprise p-i-n junctions. Other appropriate materials for the PV
active material 1030 include germanium (Ge), Ge alloys, and alloys
like copper indium gallium selenide (CIGS), cadmium telluride
(CdTe), as well as III-V semiconductor materials, or tandem
multi-junction photovoltaic materials and films. III-V
semiconductor materials include such materials as gallium arsenide
(GaAs), indium nitride (InN), gallium nitride (GaN), boron arsenide
(BAs). Semiconductor alloys like indium gallium nitride may also be
used. Other photovoltaic materials and devices are also possible.
Methods of forming these materials are known to those having skill
in the art. As an illustrative example, alloys like CIGS can be
formed by a vacuum-based process where copper, gallium, and indium
are co-evaporated or co-sputtered then annealed with a selenide
vapor to form the final CIGS structure. Non-vacuum-based
alternative processes are also known to those of skill in the
art.
[0076] In FIG. 10C, a transparent conducting oxide (TCO) 1040 is
optionally deposited over the PV active material 1030. TCO layers
are often used with photovoltaic materials, particularly thin film
photovoltaic materials, in order to improve electrode contact to
the PV active layer 1030. Functionally the TCO 1040 forms a part of
the front electrodes completing a circuit for carrying current
generated by the PV active material 1030, but conventionally the
more conductive metal conductors that overlie the TCO 1040 and
connect the PV cell to a wider circuit are referred to as the front
electrodes. As is known to those with skill in the art, a common
TCO is indium tin oxide (ITO). Methods of forming or depositing ITO
are well known in the art and include electron beam evaporation,
physical vapor deposition, or sputter deposition techniques. Other
TCO materials and processes of manufacture may also be used. The
TCO layer can be omitted in other embodiments.
[0077] In FIG. 10D, deposition of the TCO material 1040 is followed
by the forming of a front conductor layer 1050. The front conductor
layer 1050 may comprise a metal or highly conductive material to
serve as a front electrode and connect the PV cell into a circuit
that carries current generated by the PV cell. As noted above, such
conductors tend to be fairly reflective and can spoil the
appearance of the PV device and hinder widespread use of PV
devices. Typical reflective materials for the front conductor layer
1050 include aluminum (Al), molybdenum (Mo), zirconium (Zr),
tungsten (W), iron (Fe), silver (Ag), and chromium (Cr).
[0078] As shown in FIG. 10E, an optical resonant cavity 1060 is
formed over the front conductor 1050. In the illustrated
embodiment, the optical resonant cavity 1060 is a deposited
transparent layer, although, as discussed above with respect to
FIGS. 3A and 3B, in other arrangements the cavity can comprise an
air gap (see FIG. 3B) defined by spacers, such as posts, pillars or
rails; a single transparent conductive or dielectric layer; a
composite formed by multiple conductive or dielectric transparent
layers; or a composite formed by combination of an air gap with one
or more transparent layers. Optical resonant cavities of a single
layer of transparent material can simplify manufacturing and reduce
costs. Composite structures with multiple layers and/or air gaps
can employ multiple layers to serve multiple functions, such as
device passivation or scratch resistance, in addition to its
optical role in the IMOD mask being formed.
[0079] Air gaps or composite optical resonant cavities can also
serve multiple functions, such as device ventilation or providing
the ability to employ MEMS for either reflecting multiple colors
(e.g., a color mode and a black mask mode) or for forming an
actively (electrically) tunable IMOD mask. In the illustrated
embodiments where the reflector 303 of the IMOD mask also serves as
a front electrode for a PV device, the reflector 303 can be used as
a stationary electrode for electrostatic actuation, for example,
when the PV device is not active. The absorber 301 can act as a
movable electrode. The skilled artisan will appreciate that
interconnection and external circuits for handling dual functions
of electrostatic MEMS operation and current collection from a PV
device can be integrated with the active IMOD mask of the PV
device.
[0080] The optical resonant cavity 1060 of one embodiment is formed
by a layer of SiO.sub.2 or other transparent dielectric material. A
suitable thickness for an SiO.sub.2 (or similar index) optical
resonant cavity 1060 is between 300 .ANG. (angstroms) and 1000
.ANG. to produce an interferometric dark or black effect. Methods
of depositing or forming SiO.sub.2 are known in the art, including
CVD as well as other methods. Other suitable transparent materials
for forming the optical resonant cavity 1060 include ITO,
Si.sub.3N.sub.4, and Cr.sub.2O.sub.3. The optical resonant cavity
1060 of another embodiment is formed by an air gap layer and
SiO.sub.2 or another transparent dielectric material. A suitable
thickness for an air gap optical resonant cavity 1060 is between
450 .ANG. and 1600 .ANG. to produce an interferometric dark or
black effect.
[0081] Referring to FIG. 10F, an absorber layer 1070 is formed over
the optical resonant cavity 1060. In the illustrated embodiment,
where the IMOD mask being constructed is designed to
interferometrically darken the appearance of the naturally
reflective front conductor 1050, the absorber layer 1070 may
comprise, for example, semitransparent thicknesses of metallic or
semiconductor layers. The absorber layer may also comprise
materials that have a non-zero n*k, i.e., a non-zero product of the
index of refraction (n) and extinction coefficient (k). In
particular, chromium (Cr), molybdenum (Mo), molybdenum-chromium
alloy (MoCr), titanium (Ti), silicon (Si), tantalum (Ta) and
tungsten (W) all form suitable layers. In one embodiment, the
thickness of the absorber layer 1070 is between 20 .ANG. and 300
.ANG.. The thickness is selected to be less than that which
produces an opaque layer.
[0082] With reference to FIG. 10G, the stack illustrated in FIG.
10F is then patterned using, e.g., photolithographic patterning and
etching or another suitable technique to form a PV device 1000G as
shown in FIG. 10G. The resultant interferometric modulator (IMOD)
mask 300 comprises a reflector 303 (also serving as a front
conductor or electrode for the PV device), an optical resonant
cavity 302 (referred to by reference number 1060 prior to
patterning), and a patterned absorber 301. In the embodiment of
FIG. 10G, the reflector 303, optical resonant cavity 302, and the
absorber 301 are patterned together and hence aligned with one
another. In other arrangements, components of the IMOD mask 300 may
have a pattern that differs in some fashion from the pattern of the
conductor that serves as the IMOD mask reflector 303, as will be
better understood from the discussion of FIG. 12 below. The IMOD
mask 300 thus covers the front electrode or reflector 303.
Alignment of the IMOD mask 300 with the reflectors 303 that serve
as front electrodes for the PV device risks some minimal
reflections from the sides of the reflectors 303 at acute viewing
angles. On the other hand, the absorber 301 is patterned in a
fashion that does not prevent any more light from reaching the PV
active layer than the reflector 303, which is present anyway as a
front electrode, already does. Thus, the absorber 301 is patterned
in a manner that avoids any further reduction in PV efficiency.
[0083] The materials and dimensions of the absorber 301 and the
optical resonant cavity 302 are selected to reduce reflectivity
from the underlying reflector 303. Reflectivity is defined as a
ratio of [the intensity of light reflected from the IMOD mask 300]
to [the intensity of incident light upon the top of the IMOD mask
300] in the direction normal to the upper surface of the mask 300.
Common PV device front electrode materials for the reflector 303
exhibit reflectivity in the range of 30%-90%. The IMOD mask 300,
however, is configured to interferometrically reduce the overall
reflectivity to less than 10%. Thus, the reflectivity observable
above the IMOD mask 300 is for most common front electrode
(reflector 303) materials less than 10% (at which point the
reflections tend to appear "gray"), and more typically less than
5%. The skilled artisan will appreciate, in view of the disclosure
herein, that reflectivity can be reduced to as little as 1%-3%,
thus truly appearing "black," by proper selection of the materials
and dimensions for the layer(s) in the absorber 301 and the optical
resonant cavity 302.
[0084] Thus, little or no light is seen reflecting from the front
conductor of the PV device by an observer. Hence the pattern formed
by the IMOD mask 300 covering the electrode may appear dark or
black. Alternatively, the structure of the IMOD mask 300 is
selected to reflect a color substantially matching the color of
visible regions of the photovoltaic active material adjacent the
front conductor. For most PV devices, the PV active area appears
quite dark, such that reducing visible reflection by way of the
IMOD mask 300 effectively blends the conductors in with the
appearance of the PV active area, making it difficult to
distinguish the two regions of the PV device by sight. However, to
the extent the visible regions of PV active material demonstrate
color(s) other than dark or black, either due to unconventional PV
materials or other coatings over the windows over the PV active
material, the IMOD mask 300 may be constructed to reflect other
colors in order to match with the visible regions of the PV active
area and produce a uniform color or appearance for the PV
device.
[0085] In one example, where the optical resonant cavity 302
comprises an air gap defined by spacers, such as posts, pillars or
rails (see FIG. 3B), a suitable height of the air gap for producing
a dark or black IMOD mask 300 is between 450 .ANG. and 1600 .ANG.,
depending in part on the other materials selected for the IMOD mask
300. In another example, where the optical resonant cavity 302
comprises a dielectric with an index of refraction between 1 and 3
(e.g., SiO.sub.2), a dark or black IMOD mask 300 can be produced
with a dielectric thickness between 300 .ANG. and 1000 .ANG..
[0086] With reference to FIG. 10H, the PV device 1000H can comprise
additional layers, such as overlying hard coats, anti-reflection
coatings or passivation layers, without detracting from the masking
function of the IMOD mask. For example, a dielectric layer 1080
overlying the IMOD mask 300 can comprise SiO.sub.2 or silicon
nitride and can serve as a top passivation layer for the PV device.
Furthermore, the dielectric layer 1080 can be provided in a
thickness suitable to serve as an antireflective (AR) layer which
can further enhance the black state of the front electrode regions.
Typical thicknesses for AR layers of silicon oxide or nitride are
between about 300 .ANG. and 1500 .ANG.. To the extent other layers
are positioned between the viewer and the front electrode reflector
303, adjustments may be called for in the choice of materials,
optical properties, and thicknesses of the various layers to ensure
that the interferometric mask 300 produces the desired
reflectivity.
[0087] FIGS. 11A-11D illustrate another embodiment in which an IMOD
black mask is formed after patterning the front electrodes. FIG.
11A illustrates the PV device structure of FIG. 10D after the
conductor layer 1050 of FIG. 10D has been patterned, such as by
photolithography and etching, to leave patterned front electrodes
or reflectors 303. Suitable materials for the front conductor layer
1050 are discussed above with respect to FIG. 10D. Patterning
defines patterned conductors or front electrodes, which will also
serve as the reflector 303 for the IMOD mask to be formed. The
structure of FIG. 11A may represent, for example, a prefabricated
photovoltaic (PV) device prior to packaging. Alternatively, in
another embodiment, the PV device may be packaged and include, for
example, a passivation layer (not shown) over the structure of FIG.
11A prior to conducting the steps of FIGS. 11B-11D. In such an
arrangement, the selection of materials and dimensions for the
subsequently formed optical resonant cavity and absorber should
account for the optical effect of the passivation layer. Put
another way, in such an unpictured embodiment, the passivation
layer (not shown) can be considered a part of a composite optical
resonant cavity being formed.
[0088] FIG. 11B shows the structure of FIG. 11A after forming a
blanket layer or composite structure selected to define the optical
resonant cavity layer 1060 for the IMOD mask. As noted in the
discussion of FIG. 10E, the optical resonant cavity layer 1060 can
be an air gap (see FIG. 3B) defined by spacers, such as posts,
pillars or rails; a single transparent conductive or dielectric
layer; a composite formed by multiple conductive or dielectric
transparent layers; or a composite formed by combination of an air
gap with one or more transparent layers.
[0089] FIG. 11C illustrates the structure of FIG. 11B after
deposition of an absorber layer 1070. Suitable materials and
thicknesses for the semitransparent absorber layer 1070 are
discussed above with respect to FIG. 10F.
[0090] FIG. 11D illustrates the structure of FIG. 11C after
patterning the absorber layer 1070 to leave a patterned absorber
301. In the illustrated embodiment, the optical resonant cavity
layer 1060 is left as a blanket or unpatterned layer. Hence the
optical resonant cavity layer 1060 is blanketed over the PV cell.
The absorber 301 is patterned, such as by photolithographic masking
and etching, to substantially cover the conductor/electrode
303.
[0091] The resultant structure of FIG. 11D is a PV device 1100 that
comprises the interferometric or IMOD mask 300, including the
patterned reflector 303 that also serves as a front conductor or
front electrode for the PV device, a blanket optical resonant
cavity layer 1060, and a patterned absorber 301. The blanket
optical resonant cavity layer 1060, which can represent a single
layer or a composite structure as discussed above, can also serve
other functions across the regions where PV active layer 1030 is
visible or exposed, such as passivation or antireflection for the
PV active layer 1030 or for an optional intervening TCO layer 1040.
The regions of the optical resonant cavity layer 1060 that lie
between patterned reflector 303 and absorber 301 form the optical
resonant cavity 302 for the IMOD mask 300. In the illustrated
embodiment, the absorber 301 is patterned to be substantially
aligned with the reflector 303.
[0092] FIG. 12 shows another embodiment of the invention, in which
the optical resonant cavity layer 1060 and the absorber layer 1070
(see FIG. 11C), overlying the layers of a PV device as discussed
with respect to FIG. 11C, are patterned together to cover the
patterned reflectors 303 yielding a PV device 1200 as shown in FIG.
12. In this embodiment, the absorber 301 and the optical resonant
cavity 302 are both patterned to cover the electrode, but extend
slightly beyond the electrode 303. In such an embodiment, the
patterned absorber 301 could extend laterally beyond the edge of
the electrode by less than 10% of the width of the electrode on
each side, and in one embodiment by less than 5% of the electrode
width and the length of the absorber 301 (not pictured) could
independently be aligned with or longer (by less than 10% or less
than 5%) than the electrode length. The wider absorber 301 better
ensures covering to mask reflections from the front
conductor/reflector 303, and accommodates reasonable levels of mask
misalignment between the reflector 303 pattern and the absorber 301
pattern. On the other hand, by minimizing the extent that the
absorber 301 is wider than the reflector 303 that is being
interferometrically masked, the amount of light reaching the PV
active layer 1030, and thus overall PV device efficiency, can
remain high.
[0093] In other embodiments not illustrated, the absorber layer and
optical resonant cavity structure can extend over all of the PV
device, but in that case the absorber layer should be very thin
(mostly transmissive) in order to minimize the reduction of light
reaching the PV active layer. Thus, the extent of the dark or
"black" effect is somewhat sacrificed when thinning a blanket
absorber layer to maximize transmission. In that case it may also
be desirable to employ an additional semitransparent reflector,
with relatively high transmission, over the PV active layer in
order to better match the reflected color with that of the IMOD in
the front electrode regions.
[0094] As discussed with respect to FIG. 10H, the interferometric
masks 300 of FIGS. 11D and 12 can also be protected or passivated
by further layer(s) formed or deposited over the surface of the
embodiments.
[0095] FIGS. 13A-13E depict a process for manufacturing another
embodiment, wherein layers of the PV device are formed over a
transparent substrate through which light is transmitted into the
PV active region. FIG. 13A begins with an appropriate optically
transparent substrate 1310, such as glass, plastic, or other
appropriate substrate with useful optical properties. An absorber
layer 1320 is formed or deposited on the back side of the
substrate, opposite the light-incident or front side. Hence, in
FIGS. 13A-13E, light is incident from below. Suitable materials and
thicknesses for the semitransparent absorber layer 1320 are
discussed above with respect to the absorber layer 1070 of FIG.
10F.
[0096] FIG. 13B illustrates the structure of FIG. 13A after forming
or depositing an optical resonant cavity layer 1330 over the
absorber layer 1320. As noted in the discussion of FIG. 10E, the
optical resonant cavity layer 1330 can be an air gap (see FIG. 3B)
defined by spacers, such as posts, pillars or rails; a single
transparent conductive or dielectric layer; a composite formed by
multiple conductive or dielectric transparent layers; or a
composite formed by combination of an air gap with one or more
transparent layers.
[0097] FIG. 13C illustrates further formation or deposition of a
conductor layer 1340 over the optical resonant cavity layer 1330.
Suitable materials for the conductor layer 1340 are discussed above
with respect to the conductor layer 1050 of FIG. 10D.
[0098] With reference to FIG. 13D, patterning or etching the layers
1320, 1330, 1340 forms an IMOD mask 300 pattern that is
substantially similar to or covers the reflector 303 pattern.
Patterning the layer stack defines patterned conductors or front
electrodes, which will also serve as the reflector 303 for the IMOD
mask 300. Although formed on the back side of the substrate, the
reflector 303 is still frontward (closer to the light incident
side) relative to the PV active layer, which has yet to be formed,
and so the reflector 303 is said to define "front conductors" for
the PV device.
[0099] FIG. 13E illustrates the result of depositing a thin film
photovoltaic (PV) active layer 1350 behind or opposite a
light-incident side of the interferometric mask 300, followed by
deposition of a back conductor layer 1360. Suitable materials for
thin film PV active layers are discussed above with respect to FIG.
10B, and in general PV active materials include numerous types of
photosensitive semiconducting material, such as amorphous silicon.
While not shown, a transparent conductor layer (TCO) such as ITO
can be deposited prior to depositing the PV active layer 1350 in
order to improve electrical contact between the PV active layer
1350 and the front conductors 303 and thus improve collection
efficiency of the PV device 1300E. The back conductor layer 1360
may comprise a metal conducting layer, and is typically formed to
an opaque thickness.
[0100] In the embodiment of FIGS. 13A-13E, the interferometric mask
300 for a PV device is formed on the optical substrate prior to
forming or depositing the PV active material 1350. In this
embodiment, the photovoltaic device and the interferometric mask
300 are formed on a side of the optical substrate that is opposite
the light-incident or front side of the substrate. Accordingly the
sequence of layer formation can be opposite that of FIGS. 10A-10G.
Additional layers (not shown) can include TCO between the PV active
layer 1350 and the substrate 1310, and AR coatings or hard coats on
the front side of the substrate 1310.
[0101] FIG. 13F illustrates another embodiment. FIG. 13F shows the
absorber layer 1320 of FIG. 13A being patterned prior to the
formation of an optical resonant cavity layer 1370, leaving a
patterned absorber 301. Then the optical resonant cavity layer 1370
is deposited or formed over the patterned absorber 301. As noted in
the discussion of FIG. 10E, the optical resonant cavity layer 1370
can be an air gap (see FIG. 3B) defined by spacers, such as posts,
pillars or rails; a single transparent conductive or dielectric
layer; a composite formed by multiple conductive or dielectric
transparent layers; or a composite formed by combination of an air
gap with one or more transparent layers. A layer of conductor
material is deposited over the optical resonant cavity layer 1370.
The conductor layer may then be patterned to form the front
electrodes for the PV device 1300F, also serving as the patterned
reflector 303 for the IMOD mask 300, while leaving the optical
resonant cavity layer 1370 unpatterned over the PV cell.
Subsequently the PV active layer 1350 is formed over the IMOD mask
300 (including the front electrodes) and the back electrode 1360 is
formed over the PV active layer 1350.
[0102] Use of a blanket optical resonant cavity layer 1370 in an
embodiment where light is transmitted through the substrate, as
shown in FIG. 13F, can have several advantages. As mentioned above,
a transparent conductive oxide (TCO) is often used to improve
contact between an electrode and a photovoltaic material. In the
embodiment of FIG. 13F, the optical resonant cavity structure can
include or be formed by a TCO layer in contact with the front
electrodes formed by the reflector 303. As apparent from a
comparison between FIG. 13E and FIG. 13F, the use of a blanket
optical cavity layer 1370 also reduces the profile or topography of
the device, and thus makes subsequent depositions (e.g., of the
thin film PV active layer 1350) easier.
[0103] FIG. 13G illustrates another embodiment in which the
interferometric mask 300 is formed on the light-incident or front
side of the transparent substrate 1310, while the front electrodes
1390 and the photovoltaic (PV) active layer 1350 are on the back
side of the substrate 1310, opposite the light-incident or front
side. In such an embodiment, due to the thickness of the substrate
1310 between the reflective front electrode 1390 and the absorber
301, it is desirable for the front side IMOD mask 300 to include a
separate reflector 303 on the front side of the substrate 1310,
patterned to cover the reflective front electrode 1390 that is on
the other side of the substrate 1310. In this case, the PV device
1300G can have a conventional construction on the back side of the
substrate 1310, including patterned front electrodes 1390, TCO
layer 1380, PV active layer 1350 and back electrode 1360 formed in
sequence over the back surface of the transparent substrate 1310.
The front side of the substrate 1310 includes an IMOD mask 300
stack of a separate reflector 303, optical resonant cavity 302 and
absorber 301, in sequence, formed on the front side of the
light-transmissive substrate 1310. As with the illustrated
embodiments, this IMOD stack would preferably be patterned to cover
the patterned front conductor 1390. Because it has its own
reflector 303 and absorber 301, such an IMOD mask is electrically
separated from the PV active layer 1350 and can accordingly be
separately interconnected to form an electrostatic MEMS IMOD. In
such an embodiment, the IMOD mask 300 would be capable of opening
and closing, as illustrated in FIGS. 3C and 3D. In this case the
optical resonant cavity 302 may include an air gap (340 in FIG. 3C)
through which the movable electrode (303 in FIGS. 3C and 3D) can
move. As will be appreciated by the skilled artisan, in such an
embodiment, dielectric layers and other layers, as well as support
posts for spacing the movable electrode/reflector from the
stationary electrode/absorber, may be formed in front of the
substrate 1310 to implement a movable IMOD mask 300 on the
light-incident side of substrate 1310.
[0104] FIGS. 14A-14B illustrate an embodiment of integrating an
IMOD mask with a PV device 1400A in which photovoltaic material is
a portion of a single crystal semiconductor substrate and/or
epitaxial layer(s) formed over such a single crystal substrate.
FIG. 14A depicts a photovoltaic (PV) device 1400B comprising a back
electrode 1410, a p-type silicon layer 1420, an n-type silicon
layer 1430, front conductors or electrodes 303, and an
anti-reflective coating 1450. As mentioned previously, it is
desirable that the front electrodes 303 (which can be, e.g., bus
lines or grid lines for a PV array) be masked, or that reflections
from them be reduced or minimized. Hence, an interferometric mask
300 may be formed on a light-incident or front side of the
electrodes as shown in FIG. 14B. This can be accomplished in ways
similar to those described above, using similar materials. In one
embodiment, the process may begin with a silicon substrate or a
single crystal silicon material comprising an active region with
conductors 303 already patterned, as in FIG. 14A, and the IMOD mask
300 is formed thereover. In another embodiment, the process may
begin with a silicon substrate or single crystal silicon material
comprising an active region without a front conductor or electrode
pattern, and the front conductors are formed as reflectors 303
along with the optical resonant cavity 302 and absorber 301 using
techniques similar to those discussed above with respect to FIGS.
10A-10G and 11A-11D. As noted previously, the absorber 301 and the
optical resonant cavity 302, or the absorber alone, may be
patterned to be substantially aligned with the front
electrode/reflector 303 so as to cover the reflector 303 as shown
in FIG. 14B. In another embodiment, the absorber 301 and the
optical resonant cavity 302, or the absorber alone, may be
patterned so as to follow the pattern of the front
electrode/reflector 303 but be wider to cover a greater surface
area than the reflector 303. As in FIGS. 11D and 13F, the optical
resonant cavity layer may be left unpatterned or blanketed over the
PV cell, while the front electrode/reflector 303 and absorber 301
are patterned. In yet another embodiment, the absorber 301, the
optical resonant cavity 302, and/or the front electrode/reflector
303 can be screen printed, in which case formation and patterning
are conducted simultaneously. The layers that form the front
electrode/reflector, optical resonant cavity and absorber can be
screen printed together in any grouping or separately. Furthermore
some layer(s) can be patterned by lithography and etch, while other
layer(s) can be screen printed.
[0105] The foregoing embodiments teach IMOD mask constructions that
can be employed to interferometrically mask front electrodes of PV
devices that have a wide variety of constructions. For example, in
addition to the thin film and crystalline silicon PV cells and the
transmissive substrate embodiments discussed above, an
interferometric or IMOD mask may be used to mask reflections from
the front electrodes of a thin film interferometrically enhanced
photovoltaic cell or device.
[0106] FIG. 15 illustrates an embodiment of a PV device 1500 where
an interferometric mask 300 masks reflections from a reflector 303
which may serve as a front conductor or electrode of an
interferometrically enhanced cell formed on a suitable substrate
1510. In the illustrated embodiment, the conductor 303 is in
electrical contact with a PV active layer 1540 through a TCO layer
1550. In other embodiments, the conductor 303 is directly in
electrical contact with the active layer 1540, or is in electrical
contact through other layers and materials not shown. The
illustrated interferometrically tuned photovoltaic cells comprises
a reflector 1520 and an optical resonant cavity 1530 disposed
behind, or opposite a light-incident side, of the PV active layer
1540. The PV active layer 1540 may comprise a thin film
photovoltaic material, such as amorphous silicon, CIGS or other
thin semiconductor film photovoltaic material. The optical
properties (dimensions and material properties) of the reflector
1520 and optical resonant cavity 1530 are selected so that
reflection from interfaces of the layered PV device 1500 coherently
sum to produce an increased field in the PV active layer 1540 of
the photovoltaic cell, where optical energy is converted into
electrical energy. Such interferometrically enhanced photovoltaic
devices increase the absorption of optical energy in the active
region of the interferometric photovoltaic cell and thereby
increase the efficiency of the device 1500. In variations on this
embodiment, multiple optical resonant cavities can be employed to
separately tune different wavelengths of light and maximize
absorption in the PV active layer(s). The buried optical resonant
cavity 1530 may comprise transparent conductive or dielectric
materials, air gaps, or combinations thereof.
[0107] With reference to FIG. 16, in applications where the back
side of the photovoltaic device may be visible, such as for window
applications, the interferometric mask 300 may be integrated with
or formed on the back side of the photovoltaic active layer 1350,
and more particularly over the back side of the back electrode 1660
(see FIG. 16). As with the front electrode 1690, the back electrode
1660 tends to be reflective and unseemly when visible. In some
embodiments, the IMOD mask 300 is configured such that the color of
light reflected from the mask substantially matches a color of the
surrounding features on the back side of the photovoltaic device.
In some embodiments, the IMOD mask 300 is configured such that the
color of light reflected from the mask substantially matches a
color in the visible spectrum. In some embodiments, the light
reflected from the IMOD mask 300 falls within the wavelengths
associated with the visible spectrum. In some embodiments, the IMOD
mask 300 is configured such that little or no incident visible
light is reflected from the back side of the IMOD mask 300 such
that the IMOD mask appears black from a normal viewing angle. The
IMOD mask 300 therefore can greatly reduce the reflectivity from
the back electrodes (normally 30-90%) to less than 10% or less than
5%. If a black appearance is desired, reflectivity can be about
1-3%.
[0108] In some embodiments, the back side interferometric mask 300
may be patterned across the wafer or across the cell to cover any
pattern in the back electrode 1660. From the standpoint of PV
functionality, such patterning may not be needed, since the light
to be converted comes through the front side and the back side can
be opaque, such that the back side interferometric mask may blanket
or cover the entire back side of the wafer. However, for
applications where the backside is visible, often parts of the
window or solar panel are translucent, transparent, or
semi-transparent. In that case, patterning the IMOD mask 300 to
follow a pattern of the back electrode 1660 can help maintain
transparency in regions adjacent to the back electrode 1660,
thereby allowing some light through. As discussed above, with
respect to the front electrodes, such IMOD mask patterns may be
aligned with the back electrode patterns or maybe cover and extend
beyond the surface of the back electrode by less than 10% or less
than 5%. Also, similar to front side IMOD masks, the optical
resonant cavity 302 of the back side mask 300 can be formed with
optically transparent films, including conductive or dielectric
layers, an air gap, multiple layers, or combinations of layer(s)
and an air gap.
[0109] With reference to FIGS. 17A-20, an interferometric modulator
(IMOD) mask can mask high reflectivity of a conductive ribbon or
tab. The ribbon connects electrodes or buses across multiple
photovoltaic (PV) devices, cells or wafers to form large solar
panels, which greatly increases the amount of electrical charge
that can be converted into direct current. The introduction of an
IMOD mask over the conductive ribbon masks or blends the appearance
of the reflective ribbon with the surrounding photovoltaic device,
making the device more attractive to the consumer. For the typical
PV device, the IMOD mask reduces reflections from ribbons on the
front or back side of the PV device to darken the bright
reflections from the ribbon. In some embodiments, the IMOD mask is
configured such that the color of light reflected from the mask
substantially matches a color of the surrounding features on the
photovoltaic device. In some embodiments, the IMOD mask is
configured such that the color of light reflected from the mask
substantially matches a color in the visible spectrum. In some
embodiments, the light reflected from the IMOD mask falls within
the wavelengths associated with the visible spectrum. In some
embodiments, the IMOD mask is configured such that little or no
incident visible light is reflected from the IMOD mask such that
the IMOD mask appears black from a normal viewing angle. As
discussed above with respect to front electrodes, the IMOD mask
preferably exhibits reflectivity in the visible range of less than
10% or even less than 5%. If a black appearance is desired, the
IMOD mask can arrange reflectivity in the about 1-3% range. In
other arrangements, "masking" may involve interferometrically
producing a color in the visible spectrum that blends in with
adjacent features on the device. "Color" IMOD masks can reflect a
coherent band or bands of wavelengths to appear, e.g., red, green,
blue, orange, etc.
[0110] With reference to FIG. 17A, in one embodiment, the
conductive ribbon is integrated with the interferometric mask stack
on one side of the ribbon. The illustrated conductive ribbon
comprises an elongated conductor layer 303, an optical resonant
cavity 302, and an absorber layer 301. In some embodiments, a
separate metallic reflector or mirror layer (not shown) is
deposited on the conductor layer 303 before the deposition of the
optical resonant cavity 302 and the absorber layer 301. The mirror
layer may be formed from Al or Mo, or other similar materials. In
the embodiment shown in FIG. 17A, the conductor layer 303 itself
functions as both the reflector for the IMOD mask 300 and the
conductive ribbon material carrying the bulk of current between PV
cells. The conductor layer is generally dimensioned with a length
sufficient to connect a plurality of PV devices, cells or wafers,
and a width 1702 and thickness 1704 sufficient to produce high
conductivity. Typical thicknesses 1704 are between 0.08 mm and 0.3
mm, while typical widths 1702 are between 1.5 mm and 15 mm. The
edges of the conductor layer 303 may be angled or rounded. The
conductor layer 303 generally comprises copper, but may be formed
with other conductive materials. The optical resonant cavity 302
may be formed of an optically transparent dielectric layer, such as
SiO.sub.2, or an optically transparent conductive material, such as
ITO or ZnO. As previously described for front and back side IMOD
masks, the optical resonant cavity 302 may be formed with a single
optically transparent layer, using multiple layers, air gap(s) and
combinations of the same. The optical resonant cavity 302 is
configured in dimension such that it optimizes constructive and/or
destructive interference of select wavelengths of light, for
example selecting certain wavelengths associated with the visible
spectrum for constructive or destructive interference.
[0111] One of the two major sides of the conductor layer 303 may be
coated or laminated with the optical resonant cavity 302 and
absorber layer 301 as shown in FIG. 17A. One way of forming the
embodiment of FIG. 17A is to place the ribbon conductor on a
support layer 1710, such as tape or another substrate, and coat it
with additional materials to form the optical resonant cavity 302
and absorber layer 301 on the exposed surfaces. Another way of
coating the optical resonant cavity 302 and absorber layer 301 onto
the ribbon conductor 303 is to wind the ribbon conductor from roll
to roll while depositing the layers 301, 302 in a sputter tool.
[0112] With reference to FIG. 20, the prefabricated ribbon with the
integrated IMOD mask 300 can then be interconnected with the
contacts, electrodes, or buses of multiple solar cells 2010 to form
a larger solar panel 2000. The wafers are unloaded from a stack and
aligned. The photovoltaic ribbon is cut to length and provided with
stress-relief bends. While FIG. 20 illustrates photovoltaic ribbon
being applied to the back side of the wafers, this process can also
be performed on the front side.
[0113] FIG. 17B illustrates use of solder 1720, or an adhesive
layer of another material, applied to at least a portion of the
conductors to be interconnected. The conductor 303 of the
integrated IMOD mask 300 is then placed onto the solder 1720, which
is disposed on top of the cell contacts 1730 or on the front
electrodes 1790, as illustrated in FIG. 17B. While illustrated with
the solder 1720 contacting the back electrodes 1760 by way of the
cell contacts 1730, it will be understood that solder can also
directly contact back electrodes. This method is useful for
soldering the ribbon conductor 303 to the front electrodes 1790,
back electrodes 1760, and/or on contacts 1730 through insulating
material, in a single step or in a plurality of steps. In some
embodiments, the IMOD mask 300 may also be conductive, to
facilitate electrical contact among the conductive features.
[0114] The skilled artisan will appreciate that the structure of
FIG. 17B can also be obtained by standard formation of ribbon
interconnection of multiple PV devices followed by shadow-masked
deposition or deposition and patterning of IMOD mask layers. While
solder or other conductive adhesive layers can be omitted by such a
process, thin film deposition is in practice difficult on large
interconnected solar panels.
[0115] In another embodiment as illustrated in FIG. 18A, the ribbon
conductor 303 is coated with the interferometric mask stack on both
sides, for greater manufacturing ease, to form an integrated
IMOD-masked ribbon 1800 prior to attaching the ribbon on PV
devices. In this embodiment, the optical resonant cavity 302 is
preferably formed from a transparent conductive material, such as
the transparent conductive oxides (TCOs), e.g., ITO or ZnO. The
absorber layer 301 is also preferably formed from a conductive
material, such as semitransparent thicknesses of Mo, Cr, MoCr, or
Ti, in order to facilitate an electrical contact between the
conductors for the PV device and the ribbon conductor 303 (which in
the illustrated embodiment also serves as the reflector for the
IMOD mask 300). Accordingly, the coated ribbon 1800 can be readily
soldered or otherwise electrically and mechanically connected to
conductors of the PV device. As noted with respect to FIG. 17A, the
IMOD mask 300 of the surrounded ribbon embodiment can also include
a separate reflective mirror layer between the ribbon conductor 303
and the optical resonant cavity 302.
[0116] FIG. 18B illustrates a close-up view of one method of
attaching the integrated IMOD-masked ribbon 1800 with the
photovoltaic device. In this embodiment, an integrated IMOD-masked
ribbon 1800, with an optical resonant cavity 302 and an absorber
layer 301 coated on both sides of the ribbon conductor 303, is
applied to a front electrode 1890 of a PV device and attached by
means of an adhesive layer 1810. In the illustrated embodiment, the
front electrode 1890 electrically communicates with the PV active
layer 1850 by way of a TCO layer 1880. This method is similar to
the soldering method shown in FIG. 17B, except that the ribbon
conductor 303 comes prefabricated with the integrated IMOD mask
300.
[0117] In another embodiment as illustrated in FIG. 19, the IMOD
mask layers (the optical resonant cavity 302 and the absorber layer
301) and the ribbon conductor 303 are prefabricated but provided
separately. For example, the layers forming the optical resonant
cavity 302 and absorber layer 301 are formed on a tape or other
substrate (not shown), optionally with a release layer (not shown).
In this embodiment, the conductor ribbon 303 and photovoltaic
layers can be integrated on the PV device(s), either at the time of
ribbon tabbing or soldering, or subsequently. With reference to
FIGS. 17B and 19, according to one possible sequence, first solder
1720 is placed on the front and back electrodes of the PV device
that are to be interconnected. Next, the ribbon conductor 303 is
aligned with the aforementioned cell contacts, 1730, front
electrodes 1790 and/or back electrodes 1760 and soldered or tabbed
in place. Next, the IMOD mask layers (the optical resonant cavity
302 and the absorber layer 301) are either coated or laminated onto
the ribbon conductor 303.
[0118] While the foregoing detailed description discloses several
embodiments of the present invention, it should be understood that
this disclosure is illustrative only and is not limiting of the
present invention. It should be appreciated that the specific
configurations and operations disclosed can differ from those
described above, and that the methods described herein can be used
in contexts other than fabrication of semiconductor devices.
* * * * *