U.S. patent application number 12/401292 was filed with the patent office on 2009-09-24 for stretchable laminated sheet.
This patent application is currently assigned to Chisso Corporation. Invention is credited to Junji Iwata, Yasushi Matsuda.
Application Number | 20090238849 12/401292 |
Document ID | / |
Family ID | 40675476 |
Filed Date | 2009-09-24 |
United States Patent
Application |
20090238849 |
Kind Code |
A1 |
Iwata; Junji ; et
al. |
September 24, 2009 |
STRETCHABLE LAMINATED SHEET
Abstract
A stretchable laminated sheet with hydrophilic properties, which
particularly has an excellent feeling and stability in wearing and
is capable of efficiently enhancing the effect and efficacy brought
about by a liquid component on a skin or other object, when the
stretchable laminated sheet is impregnated with the liquid
component and wet and then used on the skin or other object. A
stretchable laminated sheet, which is obtained by partially
thermocompression-bonding and laminating a hydrophilic short fiber
layer extensible in at least one direction and an microfiber layer
having a elastomer long fiber of a fiber diameter of 15 .mu.m or
less at 50% or more by weight, wherein discontinuous and regular
concave and convex parts caused by the partial thermocompression
bonding are formed on a surface of the hydrophilic short fiber
layer that is exposed on one surface of the stretchable laminated
sheet, the total area of the concave parts is in a range of 3 to
40% of the area of the surface of the hydrophilic short fiber
layer, and at least the elastomer long fiber of the microfiber
layer is softened and consequently joined to a fiber constituting
the hydrophilic short fiber layer in a sheet thickness direction of
a section where the concave parts exist, whereby the hydrophilic
short fiber layer and the microfiber layer are integrated with each
other.
Inventors: |
Iwata; Junji; (Moriyama-shi,
JP) ; Matsuda; Yasushi; (Moriyama-shi, JP) |
Correspondence
Address: |
HAMRE, SCHUMANN, MUELLER & LARSON, P.C.
P.O. BOX 2902
MINNEAPOLIS
MN
55402-0902
US
|
Assignee: |
Chisso Corporation
Osaka-shi
JP
Chisso Polypro Fiber Co., Ltd.
Tokyo
JP
|
Family ID: |
40675476 |
Appl. No.: |
12/401292 |
Filed: |
March 10, 2009 |
Current U.S.
Class: |
424/401 ;
424/443; 428/138 |
Current CPC
Class: |
B32B 2262/0261 20130101;
A61Q 19/00 20130101; Y10T 428/24331 20150115; B32B 5/06 20130101;
A45D 44/002 20130101; B32B 2262/14 20130101; B32B 2262/08 20130101;
B32B 5/04 20130101; B32B 2262/062 20130101; B32B 2262/065 20130101;
B32B 2307/726 20130101; A61K 8/0208 20130101; B32B 2555/00
20130101; B32B 2307/50 20130101; B32B 2262/0276 20130101; A61M
2210/0606 20130101; B32B 2307/728 20130101; B32B 5/022 20130101;
B32B 5/26 20130101; B32B 2262/0253 20130101; B32B 2262/04 20130101;
D04H 1/559 20130101; D04H 1/4374 20130101 |
Class at
Publication: |
424/401 ;
428/138; 424/443 |
International
Class: |
A61K 9/70 20060101
A61K009/70; B32B 3/10 20060101 B32B003/10 |
Foreign Application Data
Date |
Code |
Application Number |
Mar 19, 2008 |
JP |
2008-072186 |
Nov 5, 2008 |
JP |
2008-284724 |
Claims
1. A stretchable laminated sheet, which is obtained by partially
thermocompression-bonding to laminate a hydrophilic short fiber
layer extensible in at least one direction and a microfiber layer
having an elastomer long fiber of a fiber diameter of 15 .mu.m or
less at 50% or more by weight based on the microfiber layer,
wherein discontinuous and regular concave and convex parts caused
by the partial thermocompression bonding are formed on a surface of
the hydrophilic short fiber layer that is exposed on one surface of
the stretchable laminated sheet, the total area of the concave
parts is in a range of 3 to 40% of the area of the surface of the
hydrophilic short fiber layer, and at least the elastomer long
fiber of the microfiber layer is softened and consequently joined
to a fiber constituting the hydrophilic short fiber layer in a
sheet thickness direction of a section where the concave parts
exist, whereby the hydrophilic short fiber layer and the microfiber
layer are integrated with each other.
2. The stretchable laminated sheet according to claim 1, wherein a
surface of the microfiber layer that is exposed on the other
surface of the stretchable laminated sheet is smooth.
3. The stretchable laminated sheet according to claim 1, wherein
when 100 parts by weight of the stretchable laminated sheet is
impregnated with 100 to 1500 parts by weight of a liquid component
an elongation recovery ratio is in a range of 30 to 100% after the
stretchable laminated sheet is extended by 30% in the at least one
direction.
4. The stretchable laminated sheet according to claim 1, wherein
the hydrophilic short fiber layer has at least 30% by weight of a
short fiber comprising cotton, rayon, cuprammonium, pulp, or two or
more of them.
5. The stretchable laminated sheet according to claim 1, wherein
the hydrophilic short fiber layer is a spunlace non-woven fabric or
a wetlaid web.
6. The stretchable laminated sheet according to claim 1, wherein
the microfiber layer is a fiber layer obtained by randomly
accumulating long fibers produced by a melt blow method.
7. A stretchable laminated sheet, wherein 100 parts by weight of
the stretchable laminated sheet described in claim 1 is impregnated
with 100 to 1500 parts by weight of drug solution or cosmetics.
8. A product, which is obtained by using the stretchable laminated
sheet described in claim 1.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present invention relates to a stretchable laminated
sheet having a hydrophilic layer, and to a product obtained using
the stretchable laminated sheet.
[0003] 2. Description of the Related Art
[0004] Various types of fibers including cellulosic fiber have
conventionally been known as hydrophilic fibers. Because of their
hydrophilic properties, these fibers have been used in absorbent
articles, cleaning supplies, cosmetic sheets, and the like.
Especially when used on a human skin, the important required
performance is the texture and the fitting feeling of a product
obtained using such hydrophilic fibers. However, a conventionally
used cellulosic non-woven fiber has rough and hard feeling and
lacks in texture and fitting feeling.
[0005] As an example of a sheet applied onto a skin, there is
proposed a face mask in which a hydrophilic fiber layer is
practically interlaced by water flow with a microfiber layer
obtained by dividing a splittable type conjugate fiber consisting
of a non-elastomer, and the microfiber layer is taken as a contact
surface contacting with a skin, reducing the stimulation to the
skin and improving the wearability for the skin (see International
Publication WO 2006/016601 pamphlet, for example).
DISCLOSURE OF THE INVENTION
Problem to be solved by the Invention
[0006] An object of the present invention is to provide a
stretchable laminated sheet having hydrophilic properties.
Particularly, an object of the present invention is to provide a
stretchable laminated sheet which has an excellent feeling and
stability in wearing and is capable of efficiently enhancing the
effect and efficacy brought about by a liquid component on a skin
or other object, when the stretchable laminated sheet is
impregnated with the liquid component and then used on the skin or
other object. Another object of the present invention is to provide
a product obtained using this stretchable laminated sheet.
Means to Solve the Problem
[0007] As a result of many keen studies conducted by the inventors
in order to solve the above problems, the inventors have found out
that the problems could be solved by a stretchable laminated sheet
that is obtained by partially integrating a hydrophilic short fiber
layer extensible in at least one direction with a microfiber layer
having at least a certain amount of elastomer long fiber having a
fiber diameter of 15 .mu.m or less, by thermally
compression-bonding them. The inventors therefore have completed
this invention.
[0008] Therefore, the present invention has the following
configurations:
(1) A stretchable laminated sheet, which is obtained by partially
thermocompression-bonding to laminate a hydrophilic short fiber
layer extensible in at least one direction and an microfiber layer
having an elastomer long fiber of 15 .mu.m or less at 50% or more
by weight based on the microfiber layer, wherein discontinuous and
regular concave and convex parts caused by the partial
thermocompression bonding are formed on a surface of the
hydrophilic short fiber layer that is exposed on one surface of the
stretchable laminated sheet, the total area of the concave parts is
in a range of 3 to 40% of the area of the surface of the
hydrophilic short fiber layer, and at least the elastomer long
fiber of the microfiber layer is softened and consequently joined
to a fiber constituting the hydrophilic short fiber layer in a
sheet thickness direction of a section where the concave parts
exist, whereby the hydrophilic short fiber layer and the microfiber
layer are integrated with each other. (2) The stretchable laminated
sheet described in (1) above, wherein a surface of the microfiber
layer exposed on another surface of the stretchable laminated sheet
is smooth. (3) The stretchable laminated sheet described in (1) or
(2) above, wherein when 100 parts by weight of the stretchable
laminated sheet is impregnated with 100 to 1500 parts by weight of
the liquid component, an elongation recovery ratio is in a range of
30 to 100% after the stretchable laminated sheet is extended in the
at least one direction by 30%. (4) The stretchable laminated sheet
described in any of (1) to (3) above, wherein the hydrophilic short
fiber layer has at least 30% by weight of the short fiber
comprising cotton, rayon, cuprammonium, pulp, or two or more of
them. (5) The stretchable laminated sheet described in any of (1)
to (4) above, wherein the hydrophilic short fiber is a spunlace
non-woven fabric or a wetlaid web. (6) The stretchable laminated
sheet described in any of (1) to (5) above, wherein the microfiber
layer is a fiber layer obtained by randomly accumulating long
fibers produced by a melt blow method. (7) The stretchable
laminated sheet, wherein 100 parts by weight of the stretchable
laminated sheet described in any of (1) to (6) above is impregnated
with 100 to 1500 parts by weight of drug solution or cosmetics. (8)
A product, which is obtained by using the stretchable laminated
sheet described in any of (1) to (7) above.
[0009] The stretchable laminated sheet of the present invention
brings an excellent feeling and stability in wearing on a skin and
the like, especially when impregnated with a liquid component and
then used on the skin or other object.
[0010] According to the configuration of the stretchable laminated
sheet of the present invention, the hydrophilic short fiber layer
and the microfiber layer having an elastomer fiber are integrated
by being partially thermocompression-bonded, so that interlayer
peeling resistance or other strength that is required in the
laminated sheet can be secured. Therefore, the wet laminated sheet
that is impregnated with the liquid component can realize an
excellent stretchability. In addition, the effect and efficacy
brought about by the liquid component on the skin or other object
can be improved efficiently.
[0011] Therefore, the stretchable laminated sheet of the present
invention can be suitably used in a face mask or the like that is
impregnated with drug solution or cosmetics.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0012] The present invention is now described hereinafter in detail
based on the embodiments of the present invention.
[0013] The stretchable laminated sheet of the present invention has
a hydrophilic short fiber layer and a microfiber layer.
[0014] The hydrophilic short fiber layer used in the present
invention is extensible in at least one direction. Examples of this
fiber layer include a card web having unidirectionally-aligned
short webs, an air laid web or wetlaid web having randomly
accumulated short webs, and a non-woven fabric that is obtained
three-dimensionally interlacing these fibers by means of a needle
punch or spunlace (interlacing by water flow) method. The wetlaid
web or a spunlace non-woven fabric is preferred. In the present
invention, the spunlace non-woven fabric is particularly preferred
in terms of realizing an excellent stretchability that is obtained
especially when the spunlace non-woven fabric is laminated with
microfiber layer defined in the present invention and is in a wet
state, the spunlace non-woven fabric being obtained by means of
interlacing by water fluid a card web having
unidirectionally-aligned short webs and then three-dimensionally
interlacing these fibers.
[0015] Although not particularly limited, the length of the short
fibers constituting the hydrophilic short fiber layer is preferably
2 to 100 mm. As the fibers constituting the hydrophilic short fiber
layer, short fibers with the typically used length can be used in
accordance with a specific method for preparing a fiber layer or in
accordance with, for example, a card web, air laid web, wetlaid
web, and the like.
[0016] In the present invention, if the hydrophilic fiber layer is
constituted by long fibers or continuous fibers, the fibers
interfere or get entangled with each other, which limits the
degrees of freedom of the fibers. As a result, it becomes difficult
to produce extensibility that can follow the shrinkability caused
by the elastomer fibers of the microfiber layer integrated with the
hydrophilic fiber layer. Constituting the hydrophilic fiber layer
with the short fibers reduce the interference between the fibers
and increases the degrees of freedom of the fibers. As a result,
the hydrophilic fiber layer can realize the followability
(extensibility) that can sufficiently reflect the stretchability of
the microfiber layer to the laminated sheet.
[0017] Examples of the short fibers constituting the hydrophilic
short fiber layer include cellulose fibers such as cotton and hemp,
wool, silk, rayon, cuprammonium, pulp, semisynthetic fibers
obtained by using cellulose, and hydrophilized synthetic fibers.
Two or more types of these fibers may be used. Cotton, rayon,
cuprammonium, and pulp are preferred in terms of hydrophilic
properties. It is preferred that the hydrophilic short fiber layer
have 30% or more of these hydrophilic short fibers by weight in
order to retain a sufficient amount of drug solution or cosmetics
or to secure an appropriate penetration speed of the drug solution
or cosmetics. It is preferred that the hydrophilic short fiber
layer particularly have cotton, rayon, cuprammonium, pulp, or a
combination of at least two of these fibers at 30% or more by
weight of the hydrophilic short fiber layer.
[0018] It is particularly preferred that the hydrophilic short
fiber layer be constituted by these hydrophilic short fibers only,
in order to be able to retain the higher amount of drug solution or
cosmetics in the laminated sheet or to increase the penetration
speed of the drug solution or cosmetics. Fibers other than the
abovementioned hydrophilic short fibers may be mixed in the
hydrophilic short fiber layer at no more than 70% by weight of the
hydrophilic short fiber layer, in order to appropriately and
efficiently adjust the retention capability or penetration speed of
the drug solution or cosmetics within the laminated sheet, as well
as the mechanical strength or the degree of extensibility of the
hydrophilic short fiber layer. Especially when the hydrophilic
short fiber layer contains the fibers other than the hydrophilic
short fibers at a range of 30 to 50%, by weight of the hydrophilic
short fiber layer, the retention capability or penetration speed of
the drug solution or cosmetics within the laminated sheet can be
increased significantly, while keeping the mechanical strength or
the degree of extensibility of the hydrophilic short fiber layer at
a proper level. On the other hand, when increasing the mechanical
strength and the degree of extensibility of the hydrophilic short
fiber layer or laminated sheet while keeping the retention
capability or penetration speed of the drug solution or cosmetics
within the laminated sheet, it is preferred that the hydrophilic
short fiber layer contain the fibers other than the hydrophilic
short fibers at a range of 50% to 70% by weight of the hydrophilic
short fiber layer. Examples of the fibers to be mixed include
water-repellent synthetic fibers such as fibers obtained using
polyester, polyolefin, polyamide, or conjugate fibers obtained by
combining at least two types of these polymers.
[0019] Although not particularly limited, the cross-sectional shape
of each of the fibers contained in the hydrophilic short fiber
layer can be round, flat, non-circular, or hollow. When each of the
fibers of the hydrophilic fiber layer has a round cross-sectional
shape, the fiber diameter is preferably larger than 15 .mu.m but
less than or equal to 50 .mu.m.
[0020] It is preferred that the mass per unit area of the
hydrophilic short fiber layer be 5 to 95 g/m.sup.2 in terms of the
strength of the stretchable laminated sheet, the impregnated amount
(retaining amount) of the liquid component, and the stretchability
obtained when the stretchable laminated sheet is impregnated with
the liquid component. The mass per unit area of the hydrophilic
short fiber layer is preferably in a range of 10 to 70 g/m.sup.2.
The thickness of the hydrophilic short fiber layer is preferably at
least 20% on the basis of the thickness of the stretchable
laminated sheet, and is more preferably 30 to 95% in order to
secure a sufficient impregnated amount and sufficient
stretchability in the stretchable laminated sheet when impregnating
it with the liquid component.
[0021] In addition, the degree of extensibility of the hydrophilic
short fiber layer in the dry state is preferably 20 to 250% and
more preferably 20 to 200%, in order to secure the extensibility of
the stretchable laminated sheet.
[0022] The microfiber layer of the stretchable laminated sheet of
the present invention has an elastomer long fiber having a fiber
diameter of 15 .mu.m or less. It is more preferred that the fiber
diameter of the elastomer long fiber be 10 .mu.m or less, because
the stretchable laminated sheet having the microfiber layer becomes
more flexible and more excellent wearing feeling is obtained on a
skin or the like especially when the stretchable laminated sheet is
impregnated with the liquid component.
[0023] Examples of an elastomer material to be used in the
elastomer long fiber include styrene elastomer, olefinic elastomer,
ester elastomer, urethane elastomer, and a mixture thereof. Styrene
elastomer, olefinic elastomer, and urethane elastomer are
particularly preferred in terms of the wearing feeling associated
with the flexibility and stretchability of the stretchable
laminated sheet impregnated with the liquid component, and the
wearing stability associated with the stretchability or the like of
this stretchable laminated sheet.
[0024] Two or more types of these elastomer long fibers may be
mixed together within the microfiber layer. Examples of such a
mixture include a mixture of 1 to 99 wt % of a styrene elastomer
long fiber and 99 to 1 wt % of an olefinic elastomer long fiber, a
mixture of 1 to 99 wt % of an urethane elastomer long fiber and 99
to 1 wt % of an olefinic elastomer long fiber, and a mixture of 1
to 99 wt % of an olefinic elastomer long fiber and 99 to 1 wt % of
another olefinic elastomer long fiber. Of these mixtures, examples
of a specific mixture of two olefinic elastomer long fibers include
a mixture of a polypropylene elastomer long fiber and another
polypropylene elastomer long fiber, a mixture of a polypropylene
elastomer long fiber and a polyethylene elastomer long fiber, and a
mixture of a polyethylene elastomer long fiber and another
polyethylene elastomer long fiber. Especially the wearing feeling
associated with the flexibility and stretchability of the
stretchable laminated sheet impregnated with the liquid component,
and the wearing stability associated with the stretchability or the
like of this stretchable laminated sheet can be adjusted within a
desired range at a high level, depending on the types and weight
ratio of the elastomer long fibers to be mixed.
[0025] The wearing feeling associated with the flexibility and
stretchability of the stretchable laminated sheet impregnated with
the liquid component, and the wearing stability associated with the
stretchability or the like of this stretchable laminated sheet can
be adjusted/controlled at a high level by selecting and mixing, as
the fibers constituting the microfiber layer, a styrene elastomer
long fiber and olefinic elastomer long fiber having a fiber
diameter of 15 .mu.m or lower or preferably 10 .mu.m or lower. It
is preferred that the styrene elastomer long fiber and the olefinic
elastomer long fiber be mixed evenly and randomly. Specifically,
the wearing feeling associated with the flexibility and
stretchability of the stretchable laminated sheet impregnated with
the liquid component, and the wearing stability associated with the
stretchability or the like of this stretchable laminated sheet can
be adjusted/controlled at a higher level by using the microfiber
layer in which a mixing ratio between 30 to 70 wt % of the styrene
elastomer long fiber and 70 to 30 wt % of the olefinic elastomer
long fiber is appropriately set at a desired value.
[0026] Compared to a conventional stretchable laminated sheet, the
stretchable laminated sheet of the present invention exerts an
excellent flexibility and particularly a excellent stretch
performance when it is wet. Due to such performances, the
stretchable laminated sheet of the present invention is suitably
used in, for example, a face mask to be impregnated with drug
solutions or cosmetics and applied onto a skin. A certain section
of the skin on which the face mask is applied is moisturized or
moistened by the drug solution or cosmetics. As a result, the
surface of the skin becomes sensitive and delicate.
[0027] Although the styrene elastomer long fiber generally has an
excellent flexibility, it is somewhat excessively viscous. As a
result, there may be a case that the adhering of the sheet to the
skin is felt too strong, depending on the section of the skin to
which the sheet applied or the kind of the liquid component with
which the stretchable laminated sheet is impregnated. Moreover, the
styrene elastomer long fiber has a sufficient high stretchability,
which pulls the skin as the sheet on the skin shrinks after
applying onto the skin and causes skin tightness. Consequently, it
may not be possible to obtain a comfortable wearing feeling,
depending on the section of the skin or the amount of liquid
component to impregnate the stretchable laminated sheet. Therefore,
mixing the olefinic elastomer long fiber at a specific ratio within
the abovementioned range can provide extremely soft and comfortable
wearing feeling to the section of the sensitive and delicate skin
on which the stretchable laminated sheet is applied. The laminated
sheet to be used, and particularly the structure of the microfiber
layer may be appropriately adjusted by the ingredients or
properties of the drug solution or cosmetics for impregnating the
laminated sheet. For example, in the case where there is concern
that the oil content of the drug solution or cosmetics might cause
swelling or the like of the microfiber layer, it is preferred that
the microfiber layer be constituted by fibers having olefinic
elastomer as the main fiber, or particularly a mixture of the
olefinic elastomer long fiber and another olefinic elastomer long
fiber.
[0028] A stabilizer, flame retardant, antibacterial agent,
colorant, lubricant, light-resistant agent, hydrophilic agent,
antistatic agent, charging agent, and the like may be added to the
microfiber used in the present invention, as long as the effects of
the present invention are not impaired.
[0029] The microfiber layer used in the stretchable laminated sheet
of the present invention may include fibers other than "the
elastomer long fibers having a fiber diameter of 15 .mu.m or less."
It is preferred that the elastomer long fibers having a fiber
diameter of 15 .mu.m or less be included at 50% or more by weight
of the microfiber layer, in order to obtain a comfortable wearing
feeling associated with the flexibility and stretchability of the
stretchable laminated sheet, and the wearing stability associated
with the stretchability or the like of the stretchable laminated
sheet. Preferably, the elastomer long fibers are included at 70% or
more by weight of the microfiber layer. It is particularly
preferred to constitute the microfiber layer with such elastomer
long fibers only in order to obtain a stretchable laminated sheet
having high levels of wearing feeling and wearing stability.
[0030] Examples of the fibers other than "the elastomer long fibers
having a fiber diameter of 15 .mu.m or less" include elastomer
fibers having a fiber diameter of larger than 15 .mu.m but less
than or equal to 50 .mu.m, and non-elastomer fibers such as
polyester, polyolefin, and polyamide. Using "the elastomer long
fibers having a fiber diameter of 15 .mu.m or less" along with 1 to
50 wt % of non-elastomer fibers having a fiber diameter of 1 to 15
.mu.m is effective in appropriately and efficiently adjusting the
wearing feeling or wearing stability associated with the
flexibility or stretchability of the stretchable laminated sheet to
be obtained, although the stretchable laminated sheet is not as
excellent as that obtained by combining a different type of
elastomer fibers at a specific ratio. Examples of the non-elastomer
fibers to be used include polyester terephthalate, polypropylene,
polyethylene, nylon 6, and nylon 66. At least some of the fibers
constituting the microfiber layer may have hydrophilic properties,
under the condition that the hydrophilic properties of the
microfiber layer is not greater than the hydrophilic properties of
the hydrophilic short fiber layer. Examples of the hydrophilic
fibers to be used include cellulose fibers such as cotton and hemp,
wool, silk, rayon, cuprammonium, semisynthetic fibers obtained by
using cellulose, and hydrophilized synthetic fibers.
[0031] The method of producing the elastomer long fibers used in
the microfiber layer and having a fiber diameter of 15 .mu.m or
less is not limited, as long as the fiber diameter is 15 .mu.m or
less. More specifically, it is preferred that the elastomer long
fibers be accumulated randomly in the microfiber layer so that the
stretchability of the elastomer long fibers is produced/reflected
not unidirectionally but evenly in the laminated sheet. In the
fiber layer having unidirectionally-aligned elastomer long fibers,
although the stretchability of the fibers is reflected smoothly in
a direction same as the length direction of the fibers, the
stretchability of the fibers is not produced in a direction
perpendicular to the length direction.
[0032] The elastomer long fibers are preferably produced by a melt
blow method, and it is preferred that the microfiber layer have
elastomer long fibers having a fiber diameter of 15 .mu.m or less
which are produced by a melt blow method and accumulated randomly.
Unlike a general production method in which a surfactant is
attached to the surface of each fiber in order to prevent a problem
caused by electrostatic charge on the fiber occurred in the process
of producing the fiber layer, it is not necessary to attach a
surfactant in the melt blow method.
[0033] Therefore, employing the melt blow method can efficiently
produce water-repellent fibers that are suitably used in the
microfiber layer. The method of mixing "the elastomer long fibers
having a fiber diameter of 15 .mu.m or less" used in the microfiber
layer with "other fibers" is not particularly limited. These fibers
may be mixed together after producing them individually.
[0034] It is also preferred to employ a method for using a
so-called nozzle for mixed fibers in which spinning holes for
discharging different types of fibers are aligned alternately, to
spin these different types of fibers simultaneously by means of the
melt blow method. This method can obtain the microfiber layer
having different types of fibers accumulated extremely evenly and
randomly.
[0035] When the microfiber layer has 0 to 10 wt % of non-elastomer
long fibers and 100 to 90 wt % of elastomer long fibers, and
especially when the microfiber layer is constituted by elastomer
long fibers only and the elastomer long fibers are mixed fibers of
two or more types of elastomer long fibers, or particularly mixed
fibers of 30 to 70 wt % of styrene elastomer long fibers and 70 to
30 wt % of olefinic elastomer long fibers, it is preferred that
these two or more types of fibers be spun by the melt blow method
using the nozzle for mixed fibers described above.
[0036] When using such elastomer long fibers that can produce high
degree of delicate performance, such as extremely comfortable
wearing feeling associated with a high degree of flexibility and
stretchability of the stretchable laminated sheet, and high and
appropriate degree of wearing stability associated with the
stretchability, the delicate performance is suitably secured
depending on the elastomer long fibers to be used or on whether the
two or more types of elastomer long fibers are accumulated/mixed in
the microfiber layer evenly and randomly.
[0037] The structure of the nozzle for mixed fibers is not
particularly limited as long as it can spin different types of
fibers simultaneously and accumulate them evenly and randomly. As
the nozzle for mixed fibers, a nozzle in which spinning holes for
letting out different types of fibers are lined up alternately or
in a zigzag manner can be suitably used. In another example, a
device in which a plurality of nozzles with respective spinning
holes for respectively letting out resins are aligned in a moving
direction of an accumulation conveyor can be used to spin the
different resins from the respective nozzles and then interlace
thus obtained web by means of a needle punch or the like in order
to mix the fibers. The nozzle that has spinning holes for letting
out different types of resins and the spinning holes are aligned
alternately therein are used preferably due to needless of
post-processing.
[0038] It is preferred that the mass per unit area of the
microfiber layer be 5 to 100 g/m.sup.2 so that an excellent
elongation recovery ratio can be obtained when the stretchable
laminated sheet is moistened. It is further preferred that the mass
per unit area of the microfiber layer be 10 to 70 g/m.sup.2. The
thickness of the microfiber layer is preferably 80% or less on the
basis of the thickness of the stretchable laminated sheet and more
preferably 5 to 70% so that a suitable flexibility and wearing
feeling can be secured in the stretchable laminated sheet.
[0039] The hydrophilic short fibers used in the hydrophilic short
fiber layer generally absorb the liquid thereinto by themselves.
Therefore, when a non-woven fabric sheet constituted only by
hydrophilic fibers is impregnated with drug solution or cosmetics,
the non-woven fabric needs to be filled with the drug solution or
cosmetics in an amount greater than that required actually on a
skin, because the fibers themselves absorb the liquid thereinto. In
this case, therefore, the use efficiency of the drug solution or
cosmetics becomes low, causing an increase in costs.
[0040] However, because the stretchable laminated sheet of the
present invention is integrated by partially
thermocompression-bonding the hydrophilic short fiber layer and the
microfiber layer having elastomer long fibers 50% or more by
weight, as described hereinafter, interlayer peeling resistance or
other strength required in the laminated sheet can be secured
sufficiently. Therefore, the stretchable laminated sheet can be
thinned in accordance with the strength required by the product.
Consequently, the absolute amount of the drug solution or cosmetics
absorbed by the hydrophilic fibers of the laminated sheet can be
reduced, and the effective amount of the drug solution or cosmetics
can be efficiently supplied to the skin.
[0041] Moreover, the efficient use of the drug solution or
cosmetics can be also achieved by mixing the fibers other than the
hydrophilic fibers into the hydrophilic short fiber layer at no
more than 70 wt %. On the other hand, together with the lamination
of the microfiber layer, the amount of the drug solution or
cosmetics retained in the stretchable laminated sheet itself and
the speed of the drug solution or cosmetics penetrating into the
stretchable laminated sheet tend to decrease. However, the
retaining amount and the penetration speed can be adjusted by
mixing the hydrophilic fibers into the microfiber layer at no more
than 50 wt % under the condition that the hydrophilic properties of
the hydrophilic short fiber layer is greater than the hydrophilic
properties of the microfiber layer. The abovementioned examples of
the hydrophilic can be also used as the hydrophilic fibers to be
mixed into the microfiber layer. According to these methods, the
total amount of the hydrophilic fibers of the stretchable laminated
sheet can be reduced, while maintaining the retaining amount or
penetration speed of the drug solution or cosmetics within a
desired range. Therefore, the drug solution or cosmetics can be
used effectively, contributing to cost reduction.
[0042] In the stretchable laminated sheet of the present invention,
the hydrophilic short fiber layer and the microfiber layer are
laminated by being partially thermocompression-bonded. Examples of
general fiber layer laminating means include a method of using a
heating roll, heating oven method, needle punch method, spunlace
method (interlacing by water flow), method of using ultrasonic
waves, method of fusing an adhesive, and the like.
[0043] Although not particularly limited, the partial
thermocompression bonding that is performed when producing the
stretchable laminated sheet of the present invention can be
suitably performed by using a heating roll (to be sometimes
referred to as "heating emboss roll" hereinafter) having an
embossed roll surface. In the present invention, the partial
thermocompression bonding performed using the emboss roll is
carried out by pressure-bonding the heating emboss roll to a
surface on the hydrophilic short fiber layer side that is exposed
on one of the surfaces of the laminated sheet. At this moment, the
other surface of the laminated sheet, i.e., a surface on the
microfiber layer side that is exposed on the other surface of the
laminated sheet, is in contact with a roll or the like that has a
flat or embossed surface that may be heated. The surface of the
hydrophilic short fiber layer that is exposed on one of the
surfaces of the laminated sheet has regular concave and convex
shape formed discontinuously as a result of the partial
thermocompression bonding. On the other hand, the surface of the
microfiber layer that is exposed on the other surface of the
stretchable laminated sheet preferably has a flat surface that is
formed by coming into contact with a smooth roll.
[0044] In the stretchable laminated sheet of the present invention,
the concave and convex parts formed by the abovementioned partial
thermocompression bonding on the surface of the hydrophilic short
fiber layer that is exposed on one of the surfaces of the sheet are
such that the total area of the concave parts (to be sometimes
referred to as "pressure-bonded area" hereinafter) is within a
range of 3 to 40% of the area of the surface of the hydrophilic
short fiber layer. The pressure-bonded area in this range is
preferred in terms of the interlayer strength and soft touch
feeling of the laminated sheet. It is more preferred that the
pressure-bonded area be within a range of 5 to 30%.
[0045] Moreover, also the discontinuous and regular concave and
convex parts which may be formed by the partial thermocompression
bonding on the surface of the microfiber layer that is exposed on
the other surface of the laminated sheet are such that the area of
the concave parts (pressure-bonded area) may be within a range of 3
to 40% of the area of the surface of the microfiber layer.
[0046] It is preferred that the depth of each concave part on each
surface of the laminated sheet be 0.1 to 1 mm in terms of the
interlayer strength and soft touch feeing of the laminated sheet,
the area of each concave part be 0.15 to 15 mm.sup.2, and the
distance between the concave parts be 0.5 to 20 mm.
[0047] In the stretchable laminated sheet of the present invention,
at least the elastomer long fiber of the microfiber layer is joined
to a fiber constituting the hydrophilic short fiber layer in a
sheet thickness direction of sections where the concave parts
exist, by softening the elastomer long fiber, whereby the
hydrophilic short fiber layer and the microfiber layer are
integrated with each other. The pressure and temperature at the
time of partial thermocompression bonding can be appropriately
selected under the condition that the hydrophilic short fiber layer
and the microfiber layer are integrated by softening the elastomer
long fiber of the microfibers, and the pressure is preferably
within a range of 5 to 100 kg/cm.sup.2 at the time of the partial
thermocompression bonding, and the temperature 50 to 150.degree. C.
at the time of the thermocompression bonding. The pressure and
temperature are not particularly limited as long as the
abovementioned joining is carried out between the microfiber layer
and the hydrophilic short fiber layer and the interlayer strength
can be obtained.
[0048] As described above, according to the present invention, the
hydrophilic layer has to be a short fiber layer, as it can follow
the stretchability of the microfiber layer. The laminated sheet of
the present invention is characterized in that an excellent
stretchability can be exceptionally generated especially in a
direction of the extensibility of the hydrophilic short fiber
layer, when the laminated sheet is in a wet state rather than the
dry state. It is expected that the reason is because
interference/entanglement caused by the hydrophilic short fibers or
between the hydrophilic short fibers is reduced by moistening the
laminated sheet. However, when the interference/entanglement
between the short fibers is reduced, consequently the strength of
the hydrophilic short fiber layer itself is attenuated, which might
rupture the fiber layer easily.
[0049] It is effective to employ "a partial thermocompression
bonding method" as a method for integrating the both layers in the
present invention, in order to maintain the balance between the
followability of the hydrophilic short fiber layer to the
stretchability of the microfiber layer and the strength of the
hydrophilic short fiber layer. According to the partial
thermocompression bonding method, because the fibers are strongly
joined to each other by thermally softening the fibers in the
"pressure-bonding part," peeling resistance between the microfiber
layer and the hydrophilic short fiber layer can be strengthened. On
the other hand, because the individual fibers exist unboundedly in
a "non-pressure-bonding part" formed along with the
"pressure-bonding part" by employing the partial thermocompression
bonding method, the stretchability of an obtained laminated sheet
can be produced mainly by the elongation of the fibers of this
section. The followability based on the extensibility of the
hydroplilic short fiber layer with respect to the stretchability of
the microfiber layer, and the excellent stretchability of the
resulting laminated sheet are secured by reinforcing the interlayer
peeling resistance by means of the "pressure-bonding part."
Specifically, if the integration of the both layers is weak, the
hydrophilic short fiber layer is peeled easily before sufficiently
following the stretchability of the microfiber layer. It is
considered that the laminated sheet of the present invention
generates an excellent stretchability especially when it is wet,
because the interference/entanglement between the hydrophilic short
fibers present in the "non-pressure-bonding part" is reduced and
the followability of the hydrophilic short fiber layer to the
stretchability of the microfiber layer is further enhanced.
[0050] The elastomer long fiber contained in the microfibers is
softened by means of heat pressure bonding and joined to the fibers
constituting the hydrophilic short fiber layer, whereby the both
layers are integrated with each other. At this moment, in addition
to the bonding force generated by softening the elastomer long
fiber, the bonding force between the elastomer long fiber and the
fibers constituting the hydrophilic short fiber layer is reinforced
by the sticking force or adhesion force inherent to the elastomer
long fiber, so that the interlayer peeling resistance is further
strengthened.
[0051] This integration accompanied by the strong joining can
provide a laminated sheet that cannot be ruptured easily even when
highly stretched. As described above, in the present invention, the
fact that at least the hydrophilic fiber layer is constituted by
short fibers, that the microfiber layer has the elastomer fibers,
and that the both layers are integrated by being partially
thermocompression-bonded to each other forms a foundation for
achieving the effects of the present invention.
[0052] In a laminated sheet in which the layers are integrated by
simply three-dimensionally interlacing fibers by the spunlace
method (interlacing by water flow) or needle punch method, it is
considered that interference/entanglement between the short fibers
at the three-dimensional interlacing points can be reduced in wet
state. However, in the laminated sheet in which the layers are
integrated by three-dimensionally interlacing the fibers,
interlacing between the fibers at the interlacing points
integrating the layers is loosened, whereby the layers are peeled
easily before sufficient followability of the hydrophilic short
fiber layer to the stretchability of the microfiber layer is
generated.
[0053] In addition, when the layers are integrated using the
spunlace method (interlacing by water flow) or needle punch method,
high-pressure water or a needle to be used penetrates or passes
through the laminated body, whereby the fibers are shifted toward
the periphery of the penetrated section and rearranged.
[0054] Therefore, the air permeability of the laminated body having
the integrated layers becomes higher than that obtained before the
layer integration, as the distance between the fibers in the
penetrated or passed section increases.
[0055] On the other hand, integrating the layers using the partial
thermocompression bonding method joins the fibers together at the
bonded section by softening the elastomer fibers contained at least
in the microfiber layer. In other words, the space between the
fibers are closed by press and softening the elastomer fibers,
hence the air permeability of the laminated body having the
integrated layers becomes lower than that obtained before the layer
integration.
[0056] In the stretchable laminated sheet of the present invention,
integrating the layers using the partial thermocompression bonding
method effectively reduces the air permeability of the sheet is a
result, in the case where the laminated sheet is impregnated with
the drug solution or cosmetics and applied to a skin or the like
while the laminated sheet is wet, high masking effect or wrapping
effect is produced, efficiently improving the effect and efficacy
brought about by the drug solution or cosmetics on a skin or the
like.
[0057] The air permeability of the stretchable laminated sheet of
the present invention is preferably 10 to 100 cm.sup.3/cm.sup.2sec
and more preferably 20 to 80 cm.sup.3/cm.sup.2sec. In the case
where the air permeability satisfies such ranges, evaporation or
the like of the liquid component with which the stretchable
laminated sheet is impregnated is reduced and the laminated sheet
is prevented from drying. As a result, the durability of the effect
obtainable by the drug solution or cosmetics can be improved.
[0058] According to the present invention, because the surface of
the hydrophilic short fiber layer that is exposed on one of the
surfaces of the stretchable laminated sheet has the concave and
convex parts, stickiness of this sheet surface can be reduced,
hence handleability is improved and excellent peeling property are
obtained when stacking the laminated sheets together.
[0059] In addition, the surface of the microfiber layer that is
exposed on the other surface of the laminated sheet is preferably
flat so that excellent wearing feeling and adhesion property on the
skin or other object can be attained.
[0060] The stretchable laminated sheet of the present invention is
characterized in generating exceptionally excellent degree of
elongation and stretchability, when the stretchable laminated sheet
is used in a wet state rather than in the dry state. The
characteristic that excellent degree of elongation and
stretchability are not generated in the dry state has an
industrially excellent effect in terms of an excellent distortion
resistance against unexpected stress that is added during a
production step prior to a step of impregnating the laminated sheet
with the liquid component. More specifically, in a step of cutting
the laminated sheet into an appropriate shape/size or shearing it
for the purpose of applying the laminated sheet to a part of a body
or face, the shape of the obtained sheet does not become misshapen,
hence a desired shape can be faithfully achieved in the
product.
[0061] When 100 parts by weight of the stretchable laminated sheet
of the present invention is impregnated with 100 to 1500 parts by
weight of the liquid component, an elongation recovery ratio is
preferably in a range of 30 to 100% when the stretchable laminated
sheet is extended in at least one direction by 30%. More
preferably, the elongation recovery ratio is 50 to 100%.
[0062] Therefore, the stretchable laminated sheet of the present
invention can be suitably used by impregnating it with the liquid
component such as drug solution or cosmetics.
[0063] The drug solution or cosmetics with which the stretchable
laminated sheet of the present invention can be impregnated are not
particularly limited. Examples of the drug solution include an
algefacient, deodorant, antibacterial agent, keratin softening
agent, sebum discharge suppressant, keratolytic drug, bactericidal
agent, sedative, antiplilogistic, disinfectant, insect pest
repellent, brightening agent, degloss, healing agent, and protein
remover. Examples of the cosmetics include liquid cosmetics such as
a skin lotion, emulsion, and beauty essence having a moisturizer,
cleansing component, antiperspirant component, aroma component,
whitening ingredient, blood circulation promotion component,
ultraviolet rays protective ingredient, or slimming ingredient.
[0064] Examples of the components of the drug solution or cosmetics
with which the stretchable laminated sheet of the present invention
is impregnated include polypeptide, such as collagenous
polypeptide. Examples of the polypeptide include the ones disclosed
in Japanese Patent Application Publication No. 2003-321500 and
Japanese Patent Application Publication No. 2005-60314. Specific
examples of the polypeptide include polypeptide expressed by a
formula: R1-(X-Hyp-Gly)n-R2 or a formula: R1(Pro-Y-Gly)n-R2 (where
X and Y are amino-acid residues, R1 is an H or other functional
group, R2 is an OR3 or other functional group, R3 is an H or
univalent metal, and n an integer).
[0065] The stretchable laminated sheet of the present invention has
an exceptionally excellent characteristic in terms of the
elongation recovery ratio obtained when impregnated with the liquid
component, and the liquid component that is used for confirming the
elongation recovery ratio may simply be water. Of course, the scope
of the present invention includes a situation where the elongation
recovery ratio is within a range of the values when other liquid
components such as the drug solution or cosmetics are used.
[0066] In the stretchable laminated sheet of the present invention,
regarding the degree of elongation in a direction in which the
integrated hydrophilic short fiber layer produces extensibility,
the ratio of the degree of elongation obtained when the laminated
sheet is wet to the degree of elongation obtained when the
laminated sheet is dry is preferably 1.1 to 2.0 times and more
preferably 1.2 to 2.0 times. Note that "when the laminated sheet is
dry" or "dry state" described in the present invention means that
the laminated sheet is dried at 100.degree. C. for at least 30
minutes. "When the laminated sheet is wet" or "wet state" mean that
the laminated sheet is immersed in the liquid component for at
least 1.0 minutes or that the 100 parts by weight of the sheet is
impregnated with at least 100 parts by weight of the liquid
component.
[0067] When the stretchable laminated sheet of the present
invention is particularly in the wet state, it is slightly extended
when applied to a skin or other object, and is then fitted
moderately onto the skin or other object by the force that causes
the sheet to shrink. Tightening feeling that is generated as the
skin is moderately pulled by this force produces a comfortable
wearing feeling and wearing stability.
[0068] In the stretchable laminated sheet of the present invention,
10% elongation modulus strength in the direction in which the
integrated hydrophilic short fiber layer produces extensibility, or
preferably in a direction perpendicular to the length direction of
the unidirectionally-aligned fibers constituting the spunlace
non-woven fabric contained in the integrated hydrophilic short
fiber layer, is preferably 0.2 to 5.0 N/25 mm and more preferably
0.5 to 3.0 N/25 mm when the laminated sheet is in the dry state.
Moreover, the 10% elongation modulus strength is preferably 0.1 to
4.0 N/25 mm and more preferably 0.2 to 2.5 N/25 mm when the
laminated sheet is in the wet state. The ratio of the 10%
elongation modulus strength in the wet state to the 10% elongation
modulus strength in the dry state is preferably 0.1 to 0.9 times
and more preferably 0.2 to 0.8 times.
[0069] The stretchable laminated sheet of the present invention can
be used such that the microfiber layer is brought into contact with
the skin or other object. In this case, the hydrophilic short fiber
layer holds the drug solution or cosmetics, and the microfiber
layer exudes a necessary amount of the drug solution or cosmetics
to the skin or other object. The exuded amount or exuding speed can
be adjusted. For example, the thickness of the microfiber layer can
be reduced, the hydrophilic fibers can be mixed in the microfiber
layer at an appropriate amount, and a hydrophilic agent can be
added to resins configuring the microfiber layer or hydrophilizing
processing can be performed, whereby the exuded amount and the
exuding speed can be increased.
[0070] According to the present invention, in addition to the
configuration in which the microfiber layer is constituted by
fibers having small diameter, flexibility that is produced by
including elastic elastomer fibers is an important factor that
produces comfortable wearing feeling. Moreover, preferred fitting
feeling, tightness, and wearing stability are obtained due to an
appropriate gripping effect resulted from the viscosity of the
elastomer fibers. The microfiber layer is constituted by fibers
having small diameter to have a relatively high basis weight. In
addition to this, adhesion property to the skin is improved due to
the smooth surface of the microfiber layer brought into contact
with the skin, whereby the masking effect or wrapping effect is
attained, and the effects of the drug solution or cosmetics can be
improved.
[0071] On the other hand, when the amount of drug solution or
cosmetics is excessively high, excessively exuded drug solution or
cosmetics form a layer of liquid between the smooth microfiber
layer surface and the surface of the skin or other object, which
makes the stretchable laminated sheet slippery on the surface of
the skin or other object. As a result, the fitting properties might
be impaired. In this case, the hydrophilic short fiber layer can be
brought into contact with the skin or other object. Because the
hydrophilic short fiber layer absorbs and holds the drug solution
or cosmetics therein, the hydrophilic short fiber layer is capable
of providing the cosmetics or drug solution to the skin or other
object. In addition, the concave and convex parts formed on the
hydrophilic fiber layer surface improve the slip properties of the
sheet, whereby the fitting feeling is secured.
[0072] When the viscosity of the drug solution or cosmetics is
relatively high, it might be beneficial to bring the hydrophilic
fiber layer into contact with the skin or other object.
Specifically, such a drug solution or cosmetics cannot penetrate
through the microfiber layer easily and thus cannot reach the skin
or other object sufficiently when the microfiber layer is brought
into contact with the skin or other object. However, when the
hydrophilic fiber layer is brought into contact with the skin or
other object, the highly viscous of the drug solution or cosmetics
can allow the stretchable laminated sheet to fit to the skin or
other object. Moreover, the stretchable laminated sheet does not
become sticky because the highly viscous drug solution or cosmetics
cannot penetrate through the microfiber layer constituting the
other surface of the laminated sheet. Therefore, good handling
properties are attained.
[0073] The thickness of the stretchable laminated sheet of the
present invention is not particularly limited. However, in terms of
the impregnating ability and permeability of the drug solution or
cosmetics, the thickness of the stretchable laminated sheet is
preferably 0.2 to 0.7 mm when applying a load of 2 kg/cm.sup.2
(0.196 MPa) to the stretchable laminated sheet. Flexibility
required in the laminated sheet is appropriately selected in
accordance with the retaining amount and viscosity of the drug
solution or cosmetics, and the section to which the laminated sheet
is applied.
[0074] According to the stretchable laminated sheet of the present
invention, it is preferred that 100 parts by weight of the
stretchable laminated sheet be impregnated with 100 to 1500 parts
by weight of the drug solution or cosmetics.
[0075] The stretchable laminated sheet of the present invention can
be suitably used in a product that is impregnated with the drug
solution or cosmetics as described above.
[0076] The stretchable laminated sheet of the present invention can
be impregnated with the drug solution or cosmetics and suitably
applied to any part of a human boy, entire face, nose, eyes, lips,
neck, arms, hands, fingers, hip, abdomen, thighs, calves, knees,
and ankles. Specifically, the stretchable laminated sheet can be
suitably used in a face mask, stretchable members for hygienic
products such as a stretchable member for a disposable diaper,
stretchable member for a diaper, stretchable member for a sanitary
product, and stretchable member for a disposable diaper or diaper
cover, a stretchable tape, band-aid, cotton gauze, supporter, sack,
stretchable members for clothing, foundation cloth of a poultice,
foundation cloth of a plaster material, foundation cloth of a slip
stopper and the like.
EXAMPLES
[0077] Hereinafter, the present invention is described with
examples, but the present invention is not limited to these
examples.
[0078] A stretchable laminated sheet produced in each example and
comparative examples was studied on various properties, and the
definitions and method for measuring various properties are
described hereinafter.
[0079] Note in the following description that "MD" means a
direction that matches the length direction of the unidirectionally
aligned fibers constituting a spunlace non-woven fabric of a used
hydrophilic short fiber layer, and "CD" means a direction
perpendicular to this direction.
[0080] (1) Average Fiber Diameter
[0081] A closeup picture of a surface of the non-woven fabric was
taken using a scanning electron microscope (SEM) to measure the
diameter of a hundred fibers, and the calculated average value was
taken as an average fiber diameter.
[0082] (2) Pressure-Bonding Area Ratio
[0083] A closeup picture of a surface of the non-woven fabric was
taken using the scanning electron microscope (SEM) to obtain a
ratio of a pressure-bonding point per unit pressure-bonding pitch
as a pressure-bonding area ratio.
Pressure-bonding area ratio (%)=(Area of pressure-bonding point
occupying unit pitches/area of unit pitch).times.100
[0084] (3) Elongation Recovery Ratio
[0085] The elongation recovery ratio was measured based on JIS
L1096 "General Textile Testing Method." A test piece having a width
of 25 mm and a length of 200 mm was cut out from the sheet such
that the length direction of the test piece matches the direction
perpendicular to the length direction in which the fibers
constituting the spunlace non-woven fabric of the hydrophilic short
fiber layer were aligned unidirectionally (CD direction).
[0086] This test piece was placed in a polyethylene pouch along
with a sufficient amount of moisturizing toner (product name:
Moistage, essence lotion, manufactured by Kracie Holdings Ltd.) in
which the test piece can be immersed, and this pouch was left for
10 minutes. Hands were held over both surfaces of the test piece
through the pouch three times to impregnate the test piece with the
moisturizing toner until the dead weight of the test piece becomes
no less than double, and the test piece was taken out of the pouch.
A tensile tester autograph AG-G (product name, manufactured by
Shimadzu Corporation) was used to set the gap between the zippers
at 100 mm, whereby the test piece was fixed. The test piece was
stretched to 30 mm at a tension rate of 300 mm/min, and thereafter
shrunk back to the original size at the same rate, so that the load
applied to the test piece is 0. Immediately thereafter, the test
piece was stretched 30% at the same rate, and the stretched length
where the load is applied again is taken as Lmm. The elongation
recovery ratio was obtained based on the following equation.
Elongation recovery ratio when the test piece was stretched 30%
(%)={(30*.sup.1-L)/30*.sup.1}.times.100
*.sup.1: Length of the stretched test piece (mm)
[0087] (4) Rupture Strength and Elongation of the Laminated Sheet
(Dry State Before the Sheet is Impregnated with the Drug Solution
or Cosmetics)
[0088] The rupture strength and elongation were measured based on
JIS L1906 "General Long Fiber Non-woven Fabric Testing Method."
Test pieces having a width of 25 mm and a length of 200 mm were
created. The two types of test pieces were obtained by cutting a
sheet such that the length direction of one of the test pieces
matches the length direction in which the fibers constituting the
spunlace non-woven fabric of the hydrophilic short fiber layer are
aligned unidirectionally (MD direction), and such that the length
direction of the other test piece matches a direction perpendicular
to the MD direction (CD direction). The tensile tester autograph
AG-G (product name, manufactured by Shimadzu Corporation) was used
to set the gap between the zippers at 100 mm, whereby the test
pieces were fixed. The maximum strength and maximum elongation that
are obtained until the test pieces were stretched and ruptured at a
tension rate of 300 mm/mm were taken as a rupture strength and a
rupture elongation. The strength obtained when the test pieces were
stretched 10% was taken as the 10% elongation modulus strength.
[0089] (5) Rupture Strength and Elongation of Wet Laminated Sheet
(Wet State After the Sheet is Impregnated with the Drug Solution or
Cosmetics)
[0090] The rupture strength and elongation were measured based on
JIS L1906 "General Long Fiber Non-woven Fabric Testing Method." Two
types of test pieces having a width of 25 mm and a length of 200 mm
were prepared by cutting a sheet such that the length direction of
one of the test pieces matches the MD direction and such that the
length direction of the other test piece matches the CD direction
in the same manner as (4) above. The test pieces were placed in a
polyethylene pouch along with a sufficient amount of moisturizing
toner (product name: Moistage, essence lotion, manufactured by
Kracie Holdings Ltd.) in which the test piece can be immersed, and
this pouch was left for 10 minutes. Hands were held over both
surfaces of each test piece through the pouch three times to
impregnate the test piece with the moisturizing toner until the
dead weight of the test piece becomes no less than double, and the
test pieces were taken out of the pouch. The tensile tester
autograph AG-G (product name, produced by Shimadzu Corporation) was
used to set the gap between the zippers at 100 mm, whereby the test
pieces were fixed. The maximum strength and maximum elongation that
are obtained until the test pieces were stretched and ruptured at a
tension rate of 300 mm/min were taken as a rupture strength and a
rupture elongation. The strength obtained when the test pieces were
stretched 10% was taken as the 10% elongation modulus strength.
[0091] (6) Mass Per Unit Area
[0092] The mass per unit area was measured based on JIS L1906
"General Long Fiber Noon-woven Fabric Testing Method." A test piece
of 20 cm.times.20 cm was cut out from any five sections on the
non-woven fabric. The weight of each of the test pieces was
measured on an electronic balance, and the average weight was
converted into parts by mass per 1 m.sup.2 and taken as the mass
per unit area.
[0093] (7) The Thickness of the Laminated Sheet, Thickness Ratio of
Each Constituent Layer (%)
[0094] The thickness of the laminated sheet, thickness ratio of
each constituent layer were measured based on JIS L1906 "General
Long Fiber Non-woven Fabric Testing Method."
(i) The thickness L1 (mm) of the laminated sheet or of a dried
clothes wearing sheet is measured. (ii) The hydrophilic fiber layer
and the microfiber layer are peeled, and the thickness L2 (mm) of
the microfiber layer is measured. (iii) The thickness L3 (mm) of
the hydrophilic fiber layer is calculated by the following
equation.
L3 (mm)=L1-L2
(iv) The thickness ratio R1 of the microfiber layer and the
thickness R2 of the hydrophilic fiber layer based on the laminated
sheet are calculated by the following equations.
R1 (%)=L2/L1.times.100
R2 (%)=L3/L1.times.100
[0095] (8) Wearing Stability
[0096] The laminated sheet was cut into the shape of a face mask,
which was placed in a polyethylene pouch along with a sufficient
amount of moisturizing toner (product name: Moistage, essence
lotion, manufactured by Kracie Holdings Ltd.) in which the test
piece can be immersed, and this pouch was left for 10 minutes.
Hands were held over both surfaces of the test piece through the
pouch three times to impregnate the test piece with the
moisturizing toner until the dead weight of the test piece becomes
no less than double. As a result, a face mask was created.
[0097] Aside from this, the abovementioned moisturizing toner was
added to a sheet that was cut into the shape of the same face mask
in the same manner, and this sheet was impregnated with a
moisturizing emulsion (product name: Moistage, essence lotion,
manufactured by Kracie Holdings Ltd.) to create a face mask. These
two types of face masks were put on the face of a panelist for 10
minutes, and the results of these two face masks were summed up to
evaluate the adhesion property, the drying property, the skin
tightness on three scales of .largecircle., .DELTA., and x. Note in
the present example that "good" "drying property" means that the
moisturizing toner or the moisturizing emulsion in the laminated
sheet does not evaporate easily off the laminated sheet.
[0098] .largecircle.: Good
[0099] .DELTA.: Somewhat weak
[0100] x: Weak
[0101] (9) Air Permeability
[0102] The air permeability of the laminated sheet or dried clothes
wearing sheet was measured based on the Frazier method, JIS L1906
"General Long Fiber Non-woven Fabric Testing Method." A test piece
of 200 mm.times.200 mm was prepared and the air permeability was
measured using an air permeability tester (manufactured by Toyo
Seiki Seisaku-sho Ltd.).
[0103] The codes and contents of the raw resins described in the
tables below are as follows, the raw resins being used in the
present invention.
A: Styrene-ethylene-butylene-styrene block copolymer, Clayton
MD6705NS ((product name), manufactured by Clayton Polymer Co.,
Ltd.) B: Propylene ethylene copolymer, VM2125 ((product name),
manufactured by Exxon Mobile Corporation) C: Thermoplastic
polyurethane, Pandex T-1180 ((product name), manufactured by
DIC-Bayer) D: Polypropylene Mitsui polypro S119 ((product name),
manufactured by Prime Polymer Co., Ltd.) E: Ethylene octane
copolymer, EG8402 ((product name), manufactured by Dow Chemical
Co.)
Example 1
[0104] A meltblown non-woven fabric using A as the raw resin for
the microfiber layer was used. As a meltblown device, a device
configured by an extruder having a screw (with 30-mm diameter),
heating body and gear pump, a spinneret (with 0.3-mm hole diameter,
501 holes, and 500-mm effective width), compressed-air generator,
air heater, collecting conveyor having a polyester net, and winder
was used. A was thrown into the extruder, heated/melted by the
heating body at 230.degree. C., discharged from the spinneret at a
spinning speed of 0.45 g/min per unit hole. 98 kPa (gauge pressure)
of compressed air that was heated at 400.degree. C. was used to
spray the discharged fiber onto the collecting conveyor having a
polyester net that travels at a speed of 22 m/min. As a result, a
meltblown non-woven fabric with randomly piled up fibers was
obtained. The collecting conveyor was installed 25 cm away from the
spinnerret cap. The sprayed air was removed by a suction device
provided on the back of the collecting conveyor.
[0105] In the process of producing the meltblown non-woven fabric
using the above method, a spunlace non-woven fabric of
rayon/pump/rayon that is constituted by rayon having a fiber length
of 51 mm and pulp having a fiber length of 7 mm, extensible in a
direction perpendicular to the direction in which the fibers are
aligned unidirectionally, and has a mass per unit area of 43
g/m.sup.2 (laminated fiber layer having a weight ratio of 25/50/25)
was inserted as the hydrophilic short fiber layer, and the 20
g/m.sup.2 meltblown non-woven fabric was laminated thereon.
Furthermore, thus obtained non-woven laminated fabric was subjected
to partial thermocompression bonding using a point bond processor
comprising an embossed roll having an concave and convex surface
and a smooth roll, at a temperature of 80.degree. C. and a pressure
of 20 N/cm, such that the embossed roll comes into contact with the
spunlace non-woven fabric. As a result, a laminated sheet in which
a concaved area ratio was 25%, each concave area 0.46 mm.sup.2, the
depth 0.55 mm, and the distance between the concave parts 1.36 mm
in a vertical direction and 2.72 mm in a horizontal direction was
obtained. The thickness of the laminated sheet was 0.465 mm, and
the microfiber layer consisted 25% and the hydrophilic fiber layer
75% of the laminated sheet, based on the thickness thereof. The
properties of this laminated sheet are shown in Table 1.
[0106] The obtained laminated sheet had an excellent stretchability
in the wet state.
Example 2
[0107] A meltblown non-woven fabric using A and B as the raw resins
for the microfiber layer was used. As a meltblown device, a device
configured by two extruders each having a screw (with 30-mm
diameter), heating body and gear pump, a spinneret for mixed fibers
(with 0.3-mm hole diameter, spinning holes for discharging
different types of fibers that are aligned alternately in each row,
501 holes, and 500-mm effective width), compressed-air generator,
air heater, collecting conveyor having a polyester net, and winder
was used. A and B were thrown into the extruders respectively,
heated/melted by the heating body at 230.degree. C., discharged
from the spinneret at a spinning speed of 0.45 g/min per unit hole
A, B by setting the gear pump so that the ratio of A/B (weight %)
becomes 50/50. 98 kPa (gauge pressure) of compressed air that was
heated at 400.degree. C. was used to spray the discharged fibers
onto the collecting conveyor having a polyester net that travels at
a speed of 22 m/min. As a result, a meltblown non-woven fabric with
randomly and evenly piled up A fiber and B fiber was obtained. The
collecting conveyor was installed 25 cm away from the spinneret.
The sprayed air was removed by a suction device provided on the
back of the collecting conveyor.
[0108] In the process of producing the meltblown non-woven fabric
using the above method, a spunlace non-woven fabric used in Example
1 was inserted as the hydrophilic short fiber layer, and the 20
g/m.sup.2 meltblown non-woven fabric was laminated thereon. The
same processing as Example 1 was performed to obtain a laminated
sheet. In thus obtained laminated sheet, the concaved area ratio
was 25%, each concave area 0.46 mm.sup.2, the depth 0.55 mm, and
the distance between the concave parts was 1.36 mm in a vertical
direction and 2.72 mm in a horizontal direction. The thickness of
the laminated sheet was 0.484 mm, and the microfiber layer
consisted 26% and the hydrophilic fiber layer 74% of the laminated
sheet, based on the thickness thereof. The properties of this
laminated sheet are shown in Table 1. The obtained laminated sheet
had an excellent stretchability in the wet state.
Example 3
[0109] Other than the process of using a meltblown non-woven fabric
in which B and C are used as the raw resins for the microfiber
layer, the same processing as Example 2 was performed to obtain a
laminated sheet. In thus obtained laminated sheet, the concaved
area ratio was 25%, each concave area 0.46 mm.sup.2, the depth 0.55
mm, and the distance between the concave parts was 1.36 mm in a
vertical direction and 2.72 mm in a horizontal direction. The
thickness of the laminated sheet was 0.411 mm, and the microfiber
layer consisted 30% and the hydrophilic fiber layer 70% of the
laminated sheet, based on the thickness thereof. The properties of
this laminated sheet are shown in Table 1. The obtained laminated
sheet had an excellent stretchability in the wet state.
Example 4
[0110] A meltblown non-woven fabric using B and E as the raw resins
for the microfiber layer was used. As a meltblown device, a device
configured by two extruders each having a screw (with 30-mm
diameter), heating body and gear pump, a spinneret for mixed fibers
(with 0.3-mm hole diameter, spinning holes for discharging
different types of fibers that are aligned alternately in each row,
501 holes, and 500-mm effective width), compressed-air generator,
air heater, collecting conveyor having a polyester net, and winder
was used. B and E were thrown into the extruders respectively,
heated/melted by the heating body at 230.degree. C., discharged
from the spinneret at a spinning speed of 0.45 g/min per unit hole
B, E by setting the gear pump so that the ratio of B/E (weight %)
becomes 50/50. 98 kPa (gauge pressure) of compressed air that was
heated at 400.degree. C. was used to spray the discharged fibers
onto the collecting conveyor having a polyester net that travels at
a speed of 22 m/min. As a result, a meltblown non-woven fabric with
randomly and evenly piled up B fiber and E fiber was obtained. The
collecting conveyor was installed 25 cm away from the spinneret.
The sprayed air was removed by a suction device provided on the
back of the collecting conveyor.
[0111] In the process of producing the meltblown non-woven fabric
using the above method, a spunlace non-woven fabric used in Example
1 was inserted as the hydrophilic short fiber layer, and the 20
g/m.sup.2 meltblown non-woven fabric was laminated thereon. The
same processing as Example 1 was performed to obtain a laminated
sheet. In thus obtained laminated sheet, the concaved area ratio
was 25%, each concave area 0.46 mm.sup.2, the depth 0.55 mm, and
the distance between the concave parts was 1.36 mm in a vertical
direction and 2.72 mm in a horizontal direction. The thickness of
the laminated sheet was 0.385 mm, and the microfiber layer
consisted 28% and the hydrophilic fiber layer 72% of the laminated
sheet, based on the thickness thereof. The properties of this
laminated sheet are shown in Table 2. The obtained laminated sheet
had an excellent stretchability in the wet state.
Example 5
[0112] A meltblown non-woven fabric was used based on Example
4.
[0113] In the process of producing the meltblown non-woven fabric
using the above method, a spunlace non-woven fabric of
rayon/polyester that is constituted by rayon having a fiber length
of 51 mm and polyester having a fiber length of 51 mm, extensible
in a direction perpendicular to the direction in which the fibers
are aligned unidirectionally, and has a mass per unit area of 43
g/m.sup.2 (mixed cotton having a weight ratio of 40/60) was
inserted as the hydrophilic short fiber layer, and the 20 g/m.sup.2
meltblown non-woven fabric was laminated thereon.
[0114] Furthermore, thus obtained non-woven laminated fabric was
subjected to partial thermocompression bonding using the point bond
processor comprising an embossed roll having an concave and convex
surface and a smooth roll, at a temperature of 80.degree. C. and a
pressure of 20 N/cm, such that the embossed roll comes into contact
with the spunlace non-woven fabric. As a result, a laminated sheet
in which a concaved area ratio was 25%, each concave area 0.46
mm.sup.2, the depth 0.55 mm, and the distance between the concave
parts 1.36 mm in a vertical direction and 2.72 mm in a horizontal
direction was obtained. The thickness of the laminated sheet was
0.324 mm, and the microfiber layer consisted 33% and the
hydrophilic fiber layer 67% of the laminated sheet, based on the
thickness thereof. The properties of this laminated sheet are shown
in Table 2. The obtained laminated sheet had an excellent
stretchability in the wet state.
Example 6
[0115] A meltblown non-woven fabric was used based on Example
2.
[0116] In the process of producing the meltblown non-woven fabric
using the above method, a spunlace non-woven fabric that is
constituted by rayon having a fiber length of 51 mm, extensible in
a direction perpendicular to the direction in which the fibers are
aligned unidirectionally, and having a mass per unit area of 43
g/m.sup.2 was inserted as the hydrophilic short fiber layer, and
the 20 g/m.sup.2 meltblown non-woven fabric was laminated thereon.
Furthermore, thus obtained non-woven laminated fabric was subjected
to partial thermocompression bonding using the point bond processor
comprising an embossed roll having an concave and convex surface
and a smooth roll, at a temperature of 80.degree. C. and a pressure
of 20 N/cm, such that the embossed roll comes into contact with the
spunlace non-woven fabric. As a result, a laminated sheet in which
a concaved area ratio was 25%, each concave area 0.46 mm.sup.2, the
depth 0.55 mm, and the distance between the concave parts 1.36 mm
in a vertical direction and 2.72 mm in a horizontal direction was
obtained. The thickness of the laminated sheet was 0.468 mm, and
the microfiber layer consisted 26% and the hydrophilic fiber layer
74% of the laminated sheet, based on the thickness thereof. The
properties of this laminated sheet are shown in Table 2. The
obtained laminated sheet had an excellent stretchability in the wet
state.
[0117] The laminated sheet obtained in each of Examples 1 to 6 was
impregnated with the moisturizing toner or moisturizing emulsion
and used as a beauty face mask. As a result, the wearing stability
to the face was good when both the hydrophilic short fiber layer
and the microfiber layer were applied to the skin. The results are
shown in Tables 1 and 2.
Comparative Example 1
[0118] The spunlace non-woven fabric used as the hydrophilic short
fiber layer in Example 1 was used as a single layer not laminated
with the microfiber layer. The results are shown in Table 3. This
fabric was weak in stretchability in the wet state.
Comparative Example 2
[0119] A meltblown non-woven fabric using D as the raw material for
the microfiber layer was used. The microfiber layer and the
hydrophilic short fiber layer were subjected to spunlace treatment
on a 100-mesh plain weave conveyor net by means of a nozzle having
an orifice diameter of 0.3 mm and an orifice interval of 0.5 mm
under the condition of 1 MPa water pressure. Other than this
processing, the same processing as Example 1 was performed to
obtain a laminated sheet. The results are shown in Table 3. This
sheet was weak in stretchability and high in air permeability in
the wet state. Therefore, the drug solution or cosmetics with which
the fabric was impregnated evaporated easily.
Comparative Example 3
[0120] A polyethylene/polyethylene terephthalate splittable fibers
(product name: Sepa, manufactured by Daiwabo Co., Ltd.) were used
in the microfiber layer, and the spunlace non-woven fabric used as
the hydrophilic short fiber layer in Example 1 was used to perform
the spunlace treatment on this micro fiber layer and hydrophilic
short fiber layer on a 100-mesh plain weave conveyor net by means
of a nozzle having an orifice diameter of 0.3 mm and an orifice
interval of 0.5 mm under the condition of 1 MPa water pressure.
Consequently, a laminated sheet was obtained. The results are shown
in Table 3. This sheet was weak in stretchability and high in air
permeability in the wet state. Therefore, the drug solution or
cosmetics with which the fabric was impregnated evaporated
easily.
[0121] The laminated sheet obtained in each of Comparative Examples
1 to 3 was impregnated with the moisturizing toner or moisturizing
emulsion and used as a beauty face mask. As a result, weak wearing
stability was obtained because of no stretchability generated in
the non-woven fabric. The results are shown in Table 3.
TABLE-US-00001 TABLE 1 Example 1 Example 2 Example 3 Micro- Raw
material 1 A A B fiber Raw material 2 -- B C layer Weight ratio
(raw 100:0 50:50 50:50 materials 1:2) Configuration of Regular
Mixed fibers Mixed fibers fiber Production method Meltblown
Meltblown Meltblown Fineness .mu.m 10 10 10 Mass per unit area
g/m.sup.2 20 20 20 Hydrophilic Raw material 1 Rayon Rayon Rayon
short Raw material 2 Pulp Pulp Pulp fiber Raw material 3 Rayon
Rayon Rayon layer Weight ratio (raw 25:50:25 25:50:25 25:50:25
materials 1:2:3) Production method Spunlace Spunlace Spunlace
Structure Laminated Laminated Laminated Mass per unit area
g/m.sup.2 43 43 43 Strength in dry N/25 mm 17/9.7 17/9.7 17/9.7
state (MD/CD) Elongation in dry % 21/56 21/56 21/56 state (MD/CD)
10% elongation N/25 mm 2.4/1.3 2.4/1.3 2.4/1.3 modulus strength in
dry state (MD/CD) Strength in wet N/25 mm 7.3/4.4 7.3/4.4 7.3/4.4
state (MD/CD) Elongation in wet % 39/52 39/52 39/52 state (MD/CD)
10% elongation N/25 mm 1.0/0.6 1.0/0.6 1.0/0.6 modulus strength in
wet state (MD/CD) Air permeability 170 170 170
(cm.sup.3/cm.sup.2/sec) Laminated Lamination method Emboss Emboss
Emboss sheet Thickness of mm 0.465 0.484 0.411 laminated sheet
Thickness of mm/% 0.116/25 0.126/26 0.121/30 microfiber layer/
Ratio based on laminated sheet Thickness of mm/% 0.349/75 0.358/74
0.290/70 hydrophilic short fiber layer/Ratio based on laminated
sheet Strength in dry N/25 mm 14/7.2 15/7.6 14/7.8 state (MD/CD)
Elongation in dry % 24/66 23/64 21/61 state (MD/CD) 10% elongation
N/25 mm 3.7/1.9 3.8/1.9 3.8/1.9 modulus strength in dry state
(MD/CD) Strength in wet N/25 mm 6.3/3.8 6.9/4.0 6.5/4.2 state
(MD/CD) Elongation in wet % 39/83 41/79 38/76 state (MD/CD) 10%
elongation N/25 mm 0.9/0.5 1.0/0.5 1.0/0.5 modulus strength in wet
state (MD/CD) 30% elongation % 97 93 93 recovery ratio (CD) in wet
state Air permeability 62 57 59 (cm.sup.3/cm.sup.2/sec) Wearing
Adhesion .largecircle. (skin: .largecircle. (skin: .largecircle.
(skin: stability*.sup.1 property hydrophilic) hydrophilic)
hydrophilic) .DELTA.:(skin: .largecircle. (skin: .largecircle.
(skin: microfiber) microfiber) microfiber) Drying .largecircle.
(skin: .largecircle. (skin: .largecircle. (skin: property
hydrophilic) hydrophilic) hydrophilic) .largecircle. (skin:
.largecircle. (skin: .largecircle. (skin: microfiber) microfiber)
microfiber) Tighteness .largecircle. (skin: .largecircle. (skin:
.largecircle. (skin: hydrophilic) hydrophilic) hydrophilic)
.largecircle. (skin: .largecircle. (skin: .largecircle. (skin:
microfiber) microfiber) microfiber) *.sup.1Skin: Hydrophilic . . .
Hydrophilic short fiber layer is applied to the skin. Skin:
Microfiber . . . Microfiber layer is applied to the skin.
TABLE-US-00002 TABLE 2 Example 4 Example 5 Example 6 Micro- Raw
material 1 B B A fiber Raw material 2 E E B layer Weight ratio (raw
50:50 50:50 50:50 materials 1:2) Configuration of Mixed fibers
Mixed Mixed fibers fiber fibers Production method Meltblown
Meltblown Meltblown Fineness .mu.m 10 10 10 Mass per unit area
g/m.sup.2 20 20 20 Hydrophilic Raw material 1 Rayon Rayon Rayon
short Raw material 2 Pulp Polyester -- fiber Raw material 3 Rayon
-- -- layer Weight ratio (raw 25:50:25 40:60:0 100:0:0 materials
1:2:3) Production method Spunlace Spunlace Spunlace Structure
Laminated Mixed cotton Single layer Mass per unit area g/m.sup.2 43
43 43 Strength in dry N/25 mm 17/9.7 25/8.1 17/9.4 state (MD/CD)
Elongation in dry % 21/56 45/65 25/55 state (MD/CD) 10% elongation
N/25 mm 2.4/1.3 4.0/1.1 2.6/1.5 modulus strength in dry state
(MD/CD) Strength in wet N/25 mm 7.3/4.4 17/5.7 7.0/4.1 state
(MD/CD) Elongation in wet % 39/52 45/63 35/54 state (MD/CD) 10%
elongation N/25 mm 1.0/0.6 2.4/0.6 1.2/0.4 modulus strength in wet
state (MD/CD) Air permeability 170 120 160 (cm.sup.3/cm.sup.2/sec)
Laminated Lamination method Emboss Emboss Emboss sheet Thickness of
mm 0.385 0.324 0.468 laminated sheet Thickness of mm/% 0.108/28
0.107/33 0.125/26 microfiber layer/ Ratio based on laminated sheet
Thickness of mm/% 0.277/72 0.217/67 0.343/74 hydrophilic short
fiber layer/Ratio based on laminated sheet Strength in dry N/25 mm
16/7.1 23/6.1 15/8.5 state (MD/CD) Elongation in dry % 21/68 43/74
20/57 state (MD/CD) 10% elongation N/25 mm 5.2/1.7 4.1/1.2 4.1/1.8
modulus strength in dry state (MD/CD) Strength in wet N/25 mm
7.1/4.6 20/6.0 7.1/4.5 state (MD/CD) Elongation in wet % 37/82
42/81 41/91 state (MD/CD) 10% elongation N/25 mm 2.6/0.5 2.5/0.6
1.4/0.6 modulus strength in wet state (MD/CD) 30% elongation % 92
93 94 recovery ratio (CD) in wet state Air permeability 60 53 51
(cm.sup.3/cm.sup.2/sec) Wearing Adhesion .largecircle. (skin:
.largecircle. (skin: .largecircle. (skin: stability*.sup.1 property
hydrophilic) hydrophilic) hydrophilic) .largecircle. (skin:
.largecircle. (skin: .largecircle. (skin: microfiber) microfiber)
microfiber) Drying .largecircle. (skin: .largecircle. (skin:
.largecircle. (skin: property hydrophilic) hydrophilic)
hydrophilic) .largecircle. (skin: .largecircle. (skin:
.largecircle. (skin: microfiber) microfiber) microfiber) Tighteness
.largecircle. (skin: .largecircle. (skin: .largecircle. (skin:
hydrophilic) hydrophilic) hydrophilic) .largecircle. (skin:
.largecircle. (skin: .largecircle. (skin: microfiber) microfiber)
microfiber) *.sup.1Skin: Hydrophilic . . . Hydrophilic short fiber
layer is applied to the skin. Skin: Microfiber . . . Microfiber
layer is applied to the skin.
TABLE-US-00003 TABLE 3 Comparative Comparative Comparative Example
1 Example 2 Example 3 Micro- Raw material 1 -- D Polyester fiber
Raw material 2 -- -- Polyethylene layer Weight ratio (raw 0 100:0
50:50 materials 1:2) Configuration of -- Regular Splittable fiber
Production method -- Meltblown Card Fineness .mu.m -- 5 16 (8
splits) Mass per unit area g/m.sup.2 -- 20 15 Hydrophilic Raw
material 1 Rayon Rayon Rayon short Raw material 2 Pulp Pulp Pulp
fiber Raw material 3 Rayon Rayon Rayon layer Weight ratio (raw
25:50:25 25:50:25 25:50:25 materials 1:2:3) Production method
Spunlace Spunlace Spunlace Structure Laminated Laminated Laminated
Mass per unit area g/m.sup.2 43 43 43 Strength in dry N/25 mm
17/9.7 17/9.7 17/9.7 state (MD/CD) Elongation in dry % 21/56 21/56
21/56 state (MD/CD) 10% elongation N/25 mm 2.4/1.3 2.4/1.3 2.4/1.3
modulus strength in dry state (MD/CD) Strength in wet N/25 mm
7.3/4.4 7.3/4.4 7.3/4.4 state (MD/CD) Elongation in wet % 39/52
39/52 39/52 state (MD/CD) 10% elongation N/25 mm 1.0/0.6 1.0/0.6
1.0/0.6 modulus strength in wet state (MD/CD) Air permeability 170
170 170 (cm.sup.3/cm.sup.2/sec) Laminated Lamination method --
Spublace Spulace sheet Thickness of mm -- 0.402 0.526 laminated
sheet Thickness of mm/% -- 0.104/26 0.224/42.6 microfiber layer/
Ratio based on laminated sheet Thickness of mm/% 0.453/-- 0.298/74
0.302/57.4 hydrophilic short fiber layer/Ratio based on laminated
sheet Strength in dry N/25 mm -- 14/7.2 15/8.3 state (MD/CD)
Elongation in dry % -- 20/50 22/57 state (MD/CD) 10% elongation
N/25 mm -- 3.7/2.0 4.0/2.1 modulus strength in dry state (MD/CD)
Strength in wet N/25 mm -- 6.0/4.1 6.8/4.2 state (MD/CD) Elongation
in wet % -- 35/51 34/58 state (MD/CD) 10% elongation N/25 mm --
1.1/0.5 1.2/0.6 modulus strength in wet state (MD/CD) 30%
elongation % 3 6 3 recovery ratio (CD) in wet state Air
permeability -- 150 140 (cm.sup.3/cm.sup.2/sec) Wearing Adhesion
.DELTA. .largecircle. (skin: .largecircle. (skin: stability*.sup.1
property hydrophilic) hydrophilic) .DELTA. (skin: .DELTA. (skin:
microfiber) microfiber) Drying X .largecircle. (skin: .largecircle.
(skin: property hydrophilic) hydrophilic) X (skin: X (skin:
microfiber) microfiber) Tighteness X X (skin: X (skin: hydrophilic)
hydrophilic) X (skin: X (skin: microfiber) microfiber) *.sup.1Skin:
Hydrophilic . . . Hydrophilic short fiber layer is applied to the
skin. Skin: Microfiber . . . Microfiber layer is applied to the
skin.
INDUSTRIAL APPLICABILITY
[0122] The stretchable laminated sheet of the present invention can
be impregnated with the drug solution or cosmetics and suitably
applied to any part of a human boy, entire face, nose, skin around
eyes, lips, neck, arms, hands, fingers, hip, abdomen, thighs,
calves, knees, and ankles. Specifically, the stretchable laminated
sheet can be suitably used in, for example, a face mask,
stretchable members for hygienic products such as a stretchable
member for a disposable diaper, stretchable member for a diaper,
stretchable member for a sanitary product, and stretchable member
for a disposable diaper or diaper cover, a stretchable tape,
band-aid, cotton gauze, supporter, sack, stretchable members for
clothing, foundation cloth of a poultice, foundation cloth of a
plaster material, foundation cloth of a slip stopper and the like.
However, the application of the stretchable laminated sheet of the
present invention is not limited to the above applications.
* * * * *